JP2021048952A - Rope-like body curing tape and rope-like body curing tape roll - Google Patents
Rope-like body curing tape and rope-like body curing tape roll Download PDFInfo
- Publication number
- JP2021048952A JP2021048952A JP2019172568A JP2019172568A JP2021048952A JP 2021048952 A JP2021048952 A JP 2021048952A JP 2019172568 A JP2019172568 A JP 2019172568A JP 2019172568 A JP2019172568 A JP 2019172568A JP 2021048952 A JP2021048952 A JP 2021048952A
- Authority
- JP
- Japan
- Prior art keywords
- cord
- curing tape
- base material
- adhesive layer
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、安全帯を養生するためのテープとそれを巻回した索状体養生テープロールに関する。 The present invention relates to a tape for curing a safety belt and a cord-like body curing tape roll around which the tape is wound.
作業員がビルの建築現場など高所で作業する際には安全帯が使用される。安全帯には、胴ベルト型、フルハーネス型などがある。いずれの安全帯においても、ロープやワイヤーなどの索状体を安全帯に接続して使用される。 Safety belts are used when workers work in high places such as building construction sites. Safety belts include a body belt type and a full harness type. In any safety belt, a cord-like body such as a rope or a wire is connected to the safety belt and used.
安全帯を着用した状態で作業員が動くため、索状体は摩擦等により損耗し、徐々に強度が低下してしまう。索状体の損耗を防ぐ目的で、例えば、以下の特許文献に示すようなカバーが提案されている。 Since the worker moves while wearing the safety belt, the cord-like body is worn by friction and the like, and the strength gradually decreases. For the purpose of preventing wear of the cord, for example, a cover as shown in the following patent documents has been proposed.
特許文献１には、一端がベルト固定されたＤリングに固定され、他端にフックを有するロープが記載されている。ロープには、アラミド繊維からなる平織のホースなどから構成される保護材を挿通することが記載されている。 Patent Document 1 describes a rope having one end fixed to a belt-fixed D-ring and the other end having a hook. It is stated that a protective material made of a plain weave hose made of aramid fiber or the like is inserted into the rope.
特許文献２には、安全帯に接続されるロープに保護カバーを巻き付けることが記載されている。保護カバーは、ポリエチレン等からなる帯状材をロープの周面に対してらせん状に巻き付けることにより、ロープに対して装着される。 Patent Document 2 describes that a protective cover is wrapped around a rope connected to a safety belt. The protective cover is attached to the rope by spirally winding a band-shaped material made of polyethylene or the like around the peripheral surface of the rope.
特許文献２のように保護カバーをロープに対して螺旋状に巻き付ける構成では、保護カバーに隙間が形成されるため、ロープを保護する効果に懸念がある。また、特許文献１のように、筒状の保護材を挿通する構成では、ロープの端部に取り付けられたフックやＤリングなどの構造物が邪魔になるので、簡単には保護材を取り外すことができない。索状体の状態を確認し安全性を確認するために、安全帯を使用する前に索状体を目視確認することがあるが、特許文献１のような筒状の保護材の場合は、簡単に取り外すことができない。このため、索状体を目視確認する際の妨げとなる。 In the configuration in which the protective cover is spirally wound around the rope as in Patent Document 2, a gap is formed in the protective cover, so that there is a concern about the effect of protecting the rope. Further, in the configuration in which the tubular protective material is inserted as in Patent Document 1, the protective material is easily removed because the structure such as the hook and the D ring attached to the end of the rope becomes an obstacle. I can't. In order to confirm the condition of the cord and confirm the safety, the cord may be visually confirmed before using the safety belt, but in the case of a tubular protective material as in Patent Document 1, the cord is used. It cannot be easily removed. Therefore, it hinders the visual confirmation of the cord-like body.
本発明は、安全帯に接続される索状体に対して簡単に取り付けることが可能であり、簡単に取り外して目視又は触ることにより索状体の状態を確認することが可能であり、索状体を包み込むように被覆して保護することが可能な索状体養生テープと当該養生テープを巻回した索状体養生テープロールを提供することを目的とする。 INDUSTRIAL APPLICABILITY The present invention can be easily attached to a cord-like body connected to a safety band, and the state of the cord-like body can be confirmed by easily removing and visually or touching the cord-like body. It is an object of the present invention to provide a cord-like curing tape that can be covered and protected so as to wrap around the body and a cord-like curing tape roll wound with the curing tape.
帯状の基材と、当該基材の長手方向に沿って配される粘着剤層とを有し、当該粘着剤層は、少なくとも前記基材の一端部に配されており、前記基材の長手方向に沿って安全帯に接続される索状体を配置して、索状体を周方向に包み込むように前記粘着剤層により筒状に固定して索状体を被覆する索状体養生テープ（以下、養生テープと呼ぶ。）により、上記の課題を解決する。この養生テープは、粘着剤層によって、索状体を周方向に包み込むように筒状に固定するので、索状体を摩擦から効果的に保護することが可能になる。また、上記の養生テープは、基材の少なくとも一端部に配される粘着剤層によって固定するため、種々の寸法の索状体に対して簡単に取り付けることができるし、粘着剤層を剥がして索状体の様子を簡単に目視等で確認することができる。 It has a strip-shaped base material and an adhesive layer arranged along the longitudinal direction of the base material, and the pressure-sensitive adhesive layer is arranged at least at one end of the base material, and the length of the base material is long. A cord-like body curing tape in which a cord-like body connected to a safety belt is arranged along the direction and fixed in a tubular shape by the adhesive layer so as to wrap the cord-like body in the circumferential direction to cover the cord-like body. (Hereinafter, referred to as curing tape) solves the above-mentioned problems. Since the curing tape is fixed in a tubular shape so as to wrap the cord-like body in the circumferential direction by the adhesive layer, the cord-like body can be effectively protected from friction. Further, since the above-mentioned curing tape is fixed by an adhesive layer arranged at at least one end of the base material, it can be easily attached to cords of various sizes, and the adhesive layer can be peeled off. The state of the cord can be easily visually confirmed.
また上記の索状体養生テープを巻回した索状体養生テープロール（以下、テープロールと呼ぶ。）により、上記の課題を解決する。 Further, the above-mentioned problem is solved by the cord-like body curing tape roll (hereinafter, referred to as a tape roll) wound with the above-mentioned cord-like body curing tape.
上記の養生テープ及びテープロールは、前記基材の長手方向に沿って索状体を配置して、索状体の外径にあわせて筒状に固定される前記基材の内径を調節して、前記粘着剤層により筒状に固定することができるようにすることが好ましい。これによって、養生テープを索状体に対して、密着させた状態で筒状に固定することが可能となり、養生テープと索状体との間の空間に、鉄粉等の塵芥等が侵入することをより効果的に防ぐことができる。 In the curing tape and tape roll, a cord-like body is arranged along the longitudinal direction of the base material, and the inner diameter of the base material fixed in a tubular shape is adjusted according to the outer diameter of the cord-like body. , It is preferable that the pressure-sensitive adhesive layer can be fixed in a tubular shape. As a result, the curing tape can be fixed in a tubular shape in close contact with the cord, and dust such as iron powder invades the space between the curing tape and the cord. Can be prevented more effectively.
上記の養生テープ及びテープロールにおいて、前記基材は、可撓性を備えており、索状体の外形にあわせて追従するように変形させることが可能なものとすることが好ましい。これによって、索状体の外形に合わせて養生テープを変形させて、索状体に対して養生テープをより密着させやすくなる。また、索状体が動いた際に、索状体の変形に合わせて養生テープが追従するように変形させて、テープが固定された状態を維持しやすくすることができる。 In the above-mentioned curing tape and tape roll, it is preferable that the base material has flexibility and can be deformed so as to follow the outer shape of the cord-like body. As a result, the curing tape is deformed according to the outer shape of the cord-like body, and the curing tape can be more easily adhered to the cord-like body. Further, when the cord-like body moves, the curing tape can be deformed so as to follow the deformation of the cord-like body, so that the tape can be easily maintained in a fixed state.
上記の養生テープ及びテープロールにおいて、前記基材は、合成樹脂で目止めした層又は熱可塑性樹脂のラミネート層を有するものとすることが好ましい。これにより、索状体と養生テープとの間に塵芥等が侵入することをより効果的に防止することができる。 In the above-mentioned curing tape and tape roll, it is preferable that the base material has a layer sealed with a synthetic resin or a laminated layer of a thermoplastic resin. As a result, it is possible to more effectively prevent dust and the like from entering between the cord-like body and the curing tape.
上記の養生テープ及びテープロールにおいて、前記基材は、紫外線の透過率を低減可能に構成することが好ましい。索状体が合成樹脂材料で構成されている場合などにおいて、索状体が紫外線により劣化することを防止することができる。 In the above-mentioned curing tape and tape roll, it is preferable that the base material is configured so that the transmittance of ultraviolet rays can be reduced. When the cord is made of a synthetic resin material, it is possible to prevent the cord from being deteriorated by ultraviolet rays.
上記の養生テープ及びテープロールにおいて、粘着剤層は、原油を蒸留する際に分留される留分を原料とする石油樹脂を含有させることが好ましい。揮発した有機溶剤の存在下で索状体が動かされるなど、厳しい条件下で使用されると、粘着剤層から剥離が生じることがある。上記の石油樹脂を粘着性付与剤として配合することにより、上記のような厳しい条件下で使用される場合に粘着剤層から剥離が生じることを防ぐことができる。 In the above-mentioned curing tape and tape roll, the pressure-sensitive adhesive layer preferably contains a petroleum resin made from a fraction fractional distilled when the crude oil is distilled. When used under harsh conditions, such as when the cord is moved in the presence of a volatile organic solvent, peeling may occur from the adhesive layer. By blending the above petroleum resin as a tackifier, it is possible to prevent peeling from the pressure-sensitive adhesive layer when used under the severe conditions as described above.
上記の養生テープ及びテープロールにおいて、基材は、合成樹脂製のフィルム、フラットヤーンクロス、又は不織布で構成することが好ましい。これによって、塵芥や摩擦等から索状体をより効果的に保護することが可能になる。 In the above-mentioned curing tape and tape roll, the base material is preferably composed of a synthetic resin film, flat yarn cloth, or non-woven fabric. This makes it possible to more effectively protect the cord-like body from dust, friction, and the like.
本発明によれば、安全帯に接続される索状体に対して簡単に取り付けることが可能であり、簡単に取り外して目視又は触ることにより索状体の状態を確認することが可能であり、索状体を包み込むように被覆して保護することが可能な索状体養生テープと当該養生テープを巻回した索状体養生テープロールを提供することができる。 According to the present invention, it can be easily attached to the cord-like body connected to the safety belt, and the state of the cord-like body can be confirmed by easily removing it and visually or touching it. It is possible to provide a cord-shaped curing tape that can be covered and protected so as to wrap the cord-shaped body and a cord-shaped body curing tape roll in which the curing tape is wound.
以下、本発明の実施形態について図面を参照して説明する。図１ないし図３に索状体養生テープ（以下、単に養生テープと呼ぶ。）の一実施形態を示す。図４及び図５に養生テープの第二実施形態を示す。図６に索状体養生テープロールの一実施形態を示す。なお、図１及び図４は、養生テープの短手方向に沿って切断した状態を示す断面図ある。図３及び５は、索状体の延在方向に直交する方に切断した状態を示す断面図である。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. 1 to 3 show an embodiment of a cord-shaped body curing tape (hereinafter, simply referred to as a curing tape). 4 and 5 show a second embodiment of the curing tape. FIG. 6 shows an embodiment of the cord-shaped body curing tape roll. 1 and 4 are cross-sectional views showing a state in which the curing tape is cut along the lateral direction. 3 and 5 are cross-sectional views showing a state of being cut in a direction orthogonal to the extending direction of the cord-like body.
図１ないし図３の養生テープ１は、帯状の基材１１と、当該基材１１の長手方向に沿って配される粘着剤層１２とを有する。粘着剤層１２は、前記基材１１の両端部に配されている。
The curing tape 1 of FIGS. 1 to 3 has a strip-
上記の養生テープ１は、図２に示したように、図示を省略する安全帯に接続される索状体４を被覆して保護するのに使用する。具体的には、基材１１の長手方向に沿って索状体４を配置して、索状体４を周方向に包み込むように前記粘着剤層１２により筒状に固定して索状体４を被覆して、使用する。索状体４を周方向に包み込む際には、基材１１の短手方向に基材を曲げていき、基材１１が索状体４の周面に沿うようにして、粘着剤層１２により基材１１の端部を固定する。
As shown in FIG. 2, the above-mentioned curing tape 1 is used to cover and protect the cord-
図２に示した索状体４には、一端部にフック４１が固定されており、他端部にはカン４２が固定されている。フック４１は、揺動可能に構成された開閉部材４１１と、受部４１２とを有する。開閉部材４１１は、棒状であり、受部４１２に基端が固定されており、バネ力によって受部４１２を閉じる方向に付勢されている。受部４１２は、鉤爪状であり、開閉部材４１１と共に輪を形成する。索状体の構成は、これに限定されず、安全帯に索状体を固定する留め具として、他の留め具を使用してもよい。
A
図１に示したように、養生テープ１では、基材１１の両端部に基材１１の幅よりも細い帯状の粘着剤層１２が設けられている。粘着剤層は、養生テープの中央部には設けられていない。基材１１で索状体４を被覆した状態で、基材１１を索状体に対して固定する際には、図３に示したように、一方の粘着剤層１２と他方の粘着剤層１２とを接面させることにより、基材１１が筒状となるようにする。養生テープ１では、一方の粘着剤層１２と他方の粘着剤層１２とを接面させるため、一方の粘着剤層１２と他方の粘着剤層１２とが合わさって、厚みのある単一の粘着剤層が形成される。このため、例えば、一方の粘着剤層１２と他方の粘着剤層１２の厚みを薄くしても、構造上、粘着力が不足しないようになっている。粘着剤層１２の厚みを薄くすることができるので、後述するように、養生テープ１を巻回して索状体養生テープロール５（以下、テープロールと呼ぶ。）を構成した際に、養生テープ１の厚みを薄くすることにより、テープロールが嵩張らないようにすることができる。
As shown in FIG. 1, in the curing tape 1, strip-shaped
図４及び図５に養生テープの他の実施形態を示す。この養生テープ２は、図４に示したように、基材１１の長手方向に沿って配される細幅かつ帯状の粘着剤層２２が基材１１の一端部にのみ配置される点で、上記の養生テープ１と異なっている。
4 and 5 show other embodiments of the curing tape. As shown in FIG. 4, the curing tape 2 has a narrow and strip-shaped
養生テープ２を索状体４に対して固定する際には、図５に示したように、粘着剤層２２が設けられた基材１１の一端部における面と、粘着剤層２２が設けられたのと反対側の端部に配された面、すなわち基材１１の他端部における面とが重なるようにして、粘着剤層２２で養生テープ２を固定する。この状態において、基材１１の一端部における面に設けられた粘着剤層２２は、基材１１の他端部における面に接面する。これにより、養生テープ２は、索状体４を周方向に包み込むように筒状に固定される。
When fixing the curing tape 2 to the cord-
上記の養生テープ１及び２では、養生テープが索状体４を周方向に包み込むように筒状に固定することより、索状体４を保護する。このため、索状体４が養生テープから露出しにくくなっており、摩擦又は作業現場において飛散する可能性のある鉄粉、砂、小石、若しくはガラス片などの塵芥、又は後述する有機溶剤、塗料の飛沫、若しくは剥がれた塗膜等から、索状体４を保護することができる。
In the above-mentioned curing tapes 1 and 2, the cord-shaped
養生テープ１及び２では、基材１１の少なくとも一端部に粘着剤層が設けられているだけなので、索状体１１に対して養生テープが意図せず貼り付いたり、養生テープ同士が意図せず貼り付いたりしにくくなっている。また、養生が不要になった際には、養生テープを簡単に索状体から取り外すことができるようになっている。
In the curing tapes 1 and 2, since the adhesive layer is only provided at at least one end of the
養生テープ２では、図５において矢印で示したように、索状体４の周方向に対して端部を移動させることによって、筒状に固定される基材の内径を小さくするように絞り込むことができる。このため、索状体４の外径にあわせて筒状に固定される基材の内径を小さくすることができる。外径の異なる種々の索状体に対して、養生テープ２を固定して索状体を養生することが可能になり、従来のように、索状体の外径に適合するように、複数の索状体のカバーを用意する必要がなくなる。
In the curing tape 2, as shown by an arrow in FIG. 5, the inner diameter of the base material fixed in a tubular shape is narrowed down by moving the end portion with respect to the circumferential direction of the cord-
養生テープ２では、筒状に固定される養生テープ２の内径を絞り込んで、索状体４に対して固定することによって、索状体４と養生テープ２との間に鉄粉、砂、小石、若しくはガラス片などの塵芥、又は後述する有機溶剤、塗料の飛沫、若しくは剥がれた塗膜等が侵入することをより効果的に防止することが可能になる。特に索状体４の長手方向における両端部において索状体４と養生テープ２との間に隙間が存在すると、当該隙間から塵芥等が侵入しやすくなる。索状体４の周面に対して養生テープ２が密に接触するように固定することで、塵芥等が侵入することを防止する効果を高めることができる。
In the curing tape 2, the inner diameter of the curing tape 2 fixed in a tubular shape is narrowed down and fixed to the cord-
養生テープ１及び２で被覆し、保護することができる索状体の寸法、構成材料は共に限定されない。安全帯の索状体としては、細い金属繊維を撚り合わせて構成したワイヤーロープ、又は合成繊維をより合わせて構成した合成繊維製のロープが一般的に使用される。上記の養生テープ１及び２は、ワイヤーロープ及び合成繊維製のロープのいずれにも好適に使用することができる。合成繊維製のロープは、ワイヤーロープに比して、後述する有機溶剤、又は塗料の飛沫によって、劣化しやすい。このため、養生テープ１及び２は、合成樹脂製のロープを保護する用途により好適に使用することができる。 The dimensions and constituent materials of the cord-like body that can be covered with the curing tapes 1 and 2 and protected are not limited. As the cord-like body of the safety belt, a wire rope formed by twisting fine metal fibers or a rope made of synthetic fibers formed by twisting synthetic fibers is generally used. The above-mentioned curing tapes 1 and 2 can be suitably used for both wire ropes and ropes made of synthetic fibers. Rope made of synthetic fiber is more likely to be deteriorated by splashes of an organic solvent or paint, which will be described later, than a wire rope. Therefore, the curing tapes 1 and 2 can be more preferably used for the purpose of protecting the rope made of synthetic resin.
上記の養生テープ１及び２を構成する基材１１は、共に可撓性を備えており、索状体４の外形にあわせて追従するように変形させることができる。例えば、索状体の端部に後述する留め具の上に、養生テープ１及び２を被せるように固定する際に、留め具又は索状体の外形にあわせて、養生テープ１及び２を変形させながら固定し、塵芥等が養生テープ１及び２と索状体４との間に侵入にくいようにすることができる。また、作業者の動作によって、索状体４は変形するが、索状体４の外形にあわせて養生テープ１及び２が変形するため、養生テープ１及び２が索状体４から剥がれにくくなる。
The
養生テープに可撓性を付与するには、可撓性を有する素材で基材を構成すればよい。そのような素材としては、例えば、合成樹脂フィルム、フラットヤーンクロス、又は不織布などが挙げられる。 In order to impart flexibility to the curing tape, the base material may be composed of a flexible material. Examples of such a material include synthetic resin films, flat yarn cloths, and non-woven fabrics.
合成樹脂フィルム、又はフラットヤーンクロスを構成する素材としては、例えば、ポリエチレン、ポリエステル、ポリプロピレン、ポリ塩化ビニル、ポリアミド、ポリカーボネート、又はポリウレタンなどの合成樹脂材料が挙げられる。中でも熱可塑性樹脂が成形しやすいので好ましい。また、上記の高分子を構成するモノマーの２種以上を重合してなる共重合体を含有する合成樹脂を使用してもよい。 Examples of the material constituting the synthetic resin film or flat yarn cloth include synthetic resin materials such as polyethylene, polyester, polypropylene, polyvinyl chloride, polyamide, polycarbonate, and polyurethane. Of these, thermoplastic resins are preferable because they are easy to mold. Further, a synthetic resin containing a copolymer obtained by polymerizing two or more kinds of monomers constituting the above polymer may be used.
不織布を構成する繊維としては、例えば、ポリエチレン、ポリエステル、ポリプロピレン、ポリ塩化ビニル、ポリアミド、ポリカーボネート、又はポリウレタンで構成された合成繊維が挙げられる。これらの高分子を構成する２種以上のモノマーを重合してなる共重合体を含有する合成繊維を使用してもよい。合成樹脂のうち特に熱可塑性樹脂を使用すると成形しやすいので好ましい。不織布を構成する繊維は、熱溶着によって、不織布を構成する繊維が拘束されたものを使用すると、不織布を構成する繊維が応力によってずれにくくなり、養生テープに強度を付与することができるので好ましい。 Examples of the fibers constituting the non-woven fabric include synthetic fibers composed of polyethylene, polyester, polypropylene, polyvinyl chloride, polyamide, polycarbonate, or polyurethane. Synthetic fibers containing a copolymer obtained by polymerizing two or more kinds of monomers constituting these polymers may be used. Of the synthetic resins, it is particularly preferable to use a thermoplastic resin because it is easy to mold. It is preferable to use fibers constituting the non-woven fabric in which the fibers constituting the non-woven fabric are restrained by heat welding because the fibers constituting the non-woven fabric are less likely to shift due to stress and strength can be imparted to the curing tape.
基材には、合成樹脂材料により目止めした層又は熱可塑性樹脂のラミネート層を設けることがこのましい。基材を目止め又はラミネートすることによって、基材として強度に優れるフラットヤーンクロスを選択したり、クッション性に優れる不織布を選択した場合において、塗料、有機溶剤、又は粉塵等の透過率を低減して、索状体をより効果的に保護することが可能になる。 The base material is preferably provided with a layer sealed with a synthetic resin material or a laminated layer of a thermoplastic resin. By sealing or laminating the base material, when a flat yarn cloth with excellent strength is selected as the base material or a non-woven fabric with excellent cushioning properties is selected, the transmittance of paint, organic solvent, dust, etc. is reduced. Therefore, it becomes possible to protect the cord-like body more effectively.
目止めに使用する素材は、特に限定されないが、例えば、アクリル樹脂、合成ゴム、ポリ酢酸ビニル、ポリアクリロニトリル、ポリ塩化ビニル樹脂、又はこれらのポリマーを構成するモノマーの２種以上を共重合させてなる共重合体等の合成樹脂を使用することができる。 The material used for sealing is not particularly limited, but for example, acrylic resin, synthetic rubber, polyvinyl acetate, polyacrylonitrile, polyvinyl chloride resin, or two or more kinds of monomers constituting these polymers are copolymerized. A synthetic resin such as a copolymer can be used.
ラミネートに使用する素材は、溶融押し出しが可能な熱可塑性樹脂とすることが好ましい。熱可塑性樹脂としては、ポリエチレン、及びポリプロピレン等のポリオレフィン、又はポリエチレンテレフタレート等のポリエステル等を使用することができる。その他、溶着、接着、又は塗布など、薄膜状の合成樹脂材料を積層する方法によって、ラミネートしてもよい。 The material used for laminating is preferably a thermoplastic resin that can be melt-extruded. As the thermoplastic resin, polyolefins such as polyethylene and polypropylene, polyesters such as polyethylene terephthalate, and the like can be used. In addition, it may be laminated by a method of laminating a thin film synthetic resin material such as welding, adhesion, or coating.
上記の養生テープ１及び２を構成する基材１１は、紫外線の透過率を低減可能に構成することが好ましい。例えば、基材が紫外線を反射するように構成してもよいし、基材が紫外線を吸収するように構成してもよい。例えば、基材又は基材のラミネート層に対してアルミニウムなどの金属粒子を練りこんだり、金属粒子を蒸着したり、白色顔料等の紫外線の高い顔料を練りこんだりすることによって、紫外線の反射率を向上させることができる。また、黒色顔料等の紫外線の吸収率が高い顔料を練り込むことによって、紫外線の吸収率を向上させることができる。
It is preferable that the
上記のように紫外線の吸収率を低下したり、紫外線の反射率を向上させることによって、紫外線の透過率を低減して、索状体を紫外線から保護することができる。なお、紫外線の吸収率を向上させると、赤外線によって、基材の温度が上昇しやすくなることがある。このため、紫外線の反射率を向上させるようにすることがより好ましい。 By lowering the absorption rate of ultraviolet rays and improving the reflectance of ultraviolet rays as described above, the transmittance of ultraviolet rays can be reduced and the cord-like body can be protected from ultraviolet rays. If the absorption rate of ultraviolet rays is improved, the temperature of the base material may easily rise due to infrared rays. Therefore, it is more preferable to improve the reflectance of ultraviolet rays.
上記の基材に設けられる粘着剤層は、例えば、粘着剤を基材に対して塗布、スプレー等するにより適用することで形成することができる。塗布により形成する場合は、例えば、グラビアコータ法、ロールコータ法、リバースコータ法、ドクターブレード法、バーコータ法、コンマコータ法、ファウンテンダイコータ法、リップコータ法、又はナイフコータ法等により粘着剤層を形成することができる。これらのうちグラビアコータ法、コンマコータ法、又はリップコータ法は、粘着性を十分に発揮できる厚みとなる塗布量で粘着剤を略均等に簡単に塗布することができるので好ましい。 The pressure-sensitive adhesive layer provided on the above-mentioned base material can be formed, for example, by applying the pressure-sensitive adhesive to the base material by applying, spraying, or the like. When forming by coating, for example, the adhesive layer is formed by a gravure coater method, a roll coater method, a reverse coater method, a doctor blade method, a bar coater method, a comma coater method, a fountain die coater method, a lip coater method, a knife coater method, or the like. Can be done. Of these, the gravure coater method, the comma coater method, or the lip coater method is preferable because the pressure-sensitive adhesive can be easily and evenly applied in a coating amount having a thickness capable of sufficiently exhibiting the adhesiveness.
粘着剤が分散媒又は溶媒と共に用いられる場合は、粘着剤を塗布した後に熱風、赤外線、近赤外線、又は、高周波などによりエネルギーを与えることにより加熱して、乾燥してもよい。粘着剤層の乾燥後の厚みは、例えば、０．００５〜０．３ｍｍの範囲にすることが可能であり、好ましくは、０．０１〜０．２５ｍｍである。 When the pressure-sensitive adhesive is used together with a dispersion medium or a solvent, the pressure-sensitive adhesive may be applied and then heated by applying energy with hot air, infrared rays, near-infrared rays, high frequency, or the like to dry. The thickness of the pressure-sensitive adhesive layer after drying can be, for example, in the range of 0.005 to 0.3 mm, preferably 0.01 to 0.25 mm.
上記の粘着剤層を形成する際に使用される粘着剤は、特に限定されず、例えば、アクリル系粘着剤、シリコーン系粘着剤、又はウレタン系粘着剤などの合成樹脂系の粘着剤を使用してもよいし、ニトリルゴム系粘着剤、又は合成ゴム系粘着剤などのゴム系の粘着剤を使用してもよい。中でも耐候性に優れるアクリル系粘着剤を好適に使用することができる。粘着剤は、水又は有機溶媒などの適宜の分散媒又は溶媒を添加して使用することができる。 The pressure-sensitive adhesive used when forming the above-mentioned pressure-sensitive adhesive layer is not particularly limited, and for example, a synthetic resin-based pressure-sensitive adhesive such as an acrylic pressure-sensitive adhesive, a silicone-based pressure-sensitive adhesive, or a urethane-based pressure-sensitive adhesive is used. Alternatively, a rubber-based pressure-sensitive adhesive such as a nitrile rubber-based pressure-sensitive adhesive or a synthetic rubber-based pressure-sensitive adhesive may be used. Above all, an acrylic pressure-sensitive adhesive having excellent weather resistance can be preferably used. The pressure-sensitive adhesive can be used by adding an appropriate dispersion medium or solvent such as water or an organic solvent.
使用されるアクリル樹脂系粘着剤は、特に限定されないが、一例を挙げると次のようなものを使用することができる。（Ａ）アルキル基の炭素数が４〜１２のアクリル酸アルキルエステル及び／又はアルキル基の炭素数が４〜１８のメタクリル酸アルキルエステル８５〜９８.９質量％と、（Ｂ）アクリロニトリル、及びメタクリロニトリルのうち１種以上の物質１〜１０質量％と、（Ｃ）α，β−不飽和カルボン酸０.１〜５質量％とを含有するモノマーの混合物を重合したものを使用することができる。 The acrylic resin-based pressure-sensitive adhesive used is not particularly limited, but the following can be used as an example. (A) Acrylic acid alkyl ester having 4 to 12 carbon atoms in the alkyl group and / or methacrylic acid alkyl ester having 4 to 18 carbon atoms in the alkyl group 85 to 98.9% by mass, and (B) acrylonitrile and methacryl A polymerized mixture of monomers containing 1 to 10% by mass of one or more substances of acrylonitrile and 0.1 to 5% by mass of (C) α, β-unsaturated carboxylic acid can be used. it can.
粘着剤層には、充填剤、改質剤、顔料、又は硬化剤などの添加剤を添加してもよい。充填剤としては、例えば、ガラス、タルク、シリカ若しくは炭酸カルシムなどの無機系充填材、又はシリカゲル、若しくはセルロースなどの有機系充填材が挙げられる。充填剤は、例えば、粒状又はビーズ状のものであってもよい。 Additives such as fillers, modifiers, pigments, or hardeners may be added to the pressure-sensitive adhesive layer. Examples of the filler include an inorganic filler such as glass, talc, silica or calcium carbonate, or an organic filler such as silica gel or cellulose. The filler may be, for example, granular or beaded.
改質剤としては、例えば、粘着性付与樹脂、可塑剤、老化防止剤、紫外線防止剤、含浸剤、非粘着性のアクリル樹脂、界面活性剤、又は鉱物油等が挙げられる。顔料としては、紫外線を吸収又は反射させるものが挙げられ、例えば、金属粉、酸化チタン、カーボンブラックなどが挙げられる。 Examples of the modifier include an adhesive resin, a plasticizer, an antiaging agent, an ultraviolet inhibitor, an impregnating agent, a non-adhesive acrylic resin, a surfactant, a mineral oil and the like. Examples of the pigment include those that absorb or reflect ultraviolet rays, and examples thereof include metal powder, titanium oxide, and carbon black.
上記の粘着性付与樹脂としては、例えば、原油を蒸留する際に分留される留分を原料とする石油樹脂を使用することができる。石油樹脂としては、脂肪族系の石油樹脂、芳香族系の石油樹脂、脂環族系の石油樹脂、又は液状石油系樹脂などが挙げられる。これらのうちＣ９留分を原料とするＣ９系石油樹脂、又はＣ５留分を原料とするＣ５系石油樹脂と上記のＣ９系石油樹脂との混合物を好適に使用することができる。粘着性付与樹脂を配合することによって、粘着剤層同士を貼り合わせた際、又は粘着剤層と基材とを貼り合わせた際に、高い粘着力を保持することができる。 As the adhesive-imparting resin, for example, a petroleum resin made from a fraction fractional distillation when distilling crude oil can be used. Examples of the petroleum resin include aliphatic petroleum resins, aromatic petroleum resins, alicyclic petroleum resins, and liquid petroleum resins. Of these, a C9-based petroleum resin using the C9 fraction as a raw material, or a mixture of a C5-based petroleum resin using the C5 fraction as a raw material and the above-mentioned C9-based petroleum resin can be preferably used. By blending the tackifier resin, high adhesive strength can be maintained when the pressure-sensitive adhesive layers are bonded to each other or when the pressure-sensitive adhesive layer and the base material are bonded to each other.
合成石油系樹脂を配合する場合、その配合量は、例えば、粘着剤のベースポリマー１００重量部に対して、通常５〜１００重量部の範囲にすることができる。Ｃ９系石油樹脂の場合は、前記ベースポリマー１００重量部に対して、５〜６０重量部配合することが好ましい。また、Ｃ９系石油樹脂とＣ５系石油樹脂を含有する場合は、Ｃ９系石油樹脂の含有量は前記ベースポリマー１００重量部に対して５〜６０重量部とし、Ｃ５系石油樹脂の含有量は前記ベースポリマー１００重量部に対して２〜１５重量部とすることが好ましい。 When the synthetic petroleum-based resin is blended, the blending amount can be, for example, usually in the range of 5 to 100 parts by weight with respect to 100 parts by weight of the base polymer of the pressure-sensitive adhesive. In the case of C9 petroleum resin, it is preferable to add 5 to 60 parts by weight with respect to 100 parts by weight of the base polymer. When the C9 petroleum resin and the C5 petroleum resin are contained, the content of the C9 petroleum resin is 5 to 60 parts by weight with respect to 100 parts by weight of the base polymer, and the content of the C5 petroleum resin is the above. It is preferably 2 to 15 parts by weight with respect to 100 parts by weight of the base polymer.
上記の可塑剤としては、特に限定されないが、例えば、プロセスオイル、液状ポリブタジエン、液状ポリイソブチレン、液状ポリイソプレン、液状テルペン系樹脂、液状テルペンフェノール系樹脂、液状ロジン系樹脂、液状シリコーン系樹脂、液状クマロン−インデン樹脂、液状キシレン樹脂、液状スチレン樹脂、流動パラフィン、塩化パラフィン、パラフィンワックス、エチレンとα−オレフィンのコオリゴマー、ホワイトオイル、ペトロラタム、石油スルホン酸塩、ギルソナイト、石油アスファルト、フタル酸エステル誘導体、イソフタル酸誘導体、テトラヒドロフタル酸誘導体、アジピン酸誘導体、アゼライン酸誘導体、セバシン酸誘導体、ドデカン−２−酸誘導体、マレイン酸誘導体、フマル酸誘導体、トリメリット酸誘導体、クエン酸誘導体、イタコン酸誘導体、オレイン酸誘導体、リシノール酸誘導体、ステアリン酸誘導体、その他脂肪酸誘導体、スルホン酸誘導体、リン酸誘導体、グルタール酸誘導体、その他のモノエステル系可塑剤、グリコール誘導体、グリセリン誘導体、パラフィン誘導体、エポキシ誘導体、重合形可塑剤、又は動植物油脂系可塑剤等が挙げられる。 The above-mentioned plasticizer is not particularly limited, and is, for example, process oil, liquid polybutadiene, liquid polyisobutylene, liquid polyisoprene, liquid terpene resin, liquid terpenphenol resin, liquid rosin resin, liquid silicone resin, liquid. Kumaron-inden resin, liquid xylene resin, liquid styrene resin, liquid paraffin, chloride paraffin, paraffin wax, co-oligomers of ethylene and α-olefin, white oil, petrolatum, petroleum sulfonate, gilsonite, petroleum asphalt, phthalate ester derivative , Isophthalic acid derivative, tetrahydrophthalic acid derivative, adipic acid derivative, azelaic acid derivative, sebacic acid derivative, dodecane-2-ic acid derivative, maleic acid derivative, fumaric acid derivative, trimellitic acid derivative, citrate derivative, itaconic acid derivative, Oleic acid derivative, ricinolic acid derivative, stearic acid derivative, other fatty acid derivative, sulfonic acid derivative, phosphoric acid derivative, glutaric acid derivative, other monoester plasticizer, glycol derivative, glycerin derivative, paraffin derivative, epoxy derivative, polymerized form Examples thereof include plasticizers, animal and vegetable oil-based plasticizers, and the like.
可塑剤を配合する場合、その配合量は、ベースポリマー１００質量部に対して、通常５〜１００質量部の範囲で選択される。 When the plasticizer is blended, the blending amount is usually selected in the range of 5 to 100 parts by mass with respect to 100 parts by mass of the base polymer.
粘着剤層には、粘着剤の性質を調節するために、例えば、テルペン系樹脂、テルペンフェノール系樹脂、フェノール系樹脂、芳香族炭化水素変性テルペン樹脂、ロジン系樹脂、変性ロジン系樹脂、クマロン−インデン樹脂、キシレン樹脂、スチレン系樹脂、又はジシクロペンタジエン樹脂等を添加してもよい。 In the pressure-sensitive adhesive layer, for example, terpene-based resin, terpene-phenol-based resin, phenol-based resin, aromatic hydrocarbon-modified terpene resin, rosin-based resin, modified rosin-based resin, kumaron- Inden resin, xylene resin, styrene resin, dicyclopentadiene resin and the like may be added.
上記の養生テープを構成する基材の厚みは、例えば０．０３〜１．０ｍｍにすることができる。粘着剤層に厚みは、例えば、０．０１〜０．２５ｍｍにすることができる。粘着剤層の幅は、例えば、５．０〜１００ｍｍにすることができる。粘着剤層を、基材の両端部にその長手方向に沿って設ける場合は、例えば、粘着剤層の間隔が１０〜１０００ｍｍにすることができる。 The thickness of the base material constituting the above-mentioned curing tape can be, for example, 0.03 to 1.0 mm. The thickness of the pressure-sensitive adhesive layer can be, for example, 0.01 to 0.25 mm. The width of the pressure-sensitive adhesive layer can be, for example, 5.0 to 100 mm. When the pressure-sensitive adhesive layers are provided on both ends of the base material along the longitudinal direction thereof, for example, the distance between the pressure-sensitive adhesive layers can be 10 to 1000 mm.
安全帯に接続される索状体は、上述のように摩擦や鉄粉等の塵芥によって損耗する。これに加えて、例えば、高所において塗装作業や劣化した塗膜の剥離作業を行う際には、塗料、有機溶剤、又は塗膜が剥離して生じる塵芥が発生する。また、例えば、塗膜を剥離させる際には、塗膜に有機溶剤を塗布又は散布して、塗膜を剥離させやすくすることがある。また、近隣へ、作業音が漏れたり、塗料、有機溶剤、又は粉塵などが飛散することを防止する目的で作業現場をブルーシートなどの幕で囲んで作業を行うことがある。こうした場合、塗料、有機溶剤、粉塵などが幕内に滞留して濃度が上昇するため、索状体に影響が及びやすくなる。 As described above, the cord-like body connected to the safety belt is worn by friction and dust such as iron powder. In addition to this, for example, when a painting operation or a peeling operation of a deteriorated coating film is performed at a high place, dust generated by peeling the paint, an organic solvent, or the coating film is generated. Further, for example, when the coating film is peeled off, an organic solvent may be applied or sprayed on the coating film to facilitate the peeling of the coating film. In addition, the work site may be surrounded by a curtain such as a blue sheet for the purpose of preventing the work sound from leaking to the neighborhood and the paint, organic solvent, dust, etc. from scattering. In such a case, paint, organic solvent, dust, etc. stay in the curtain and the concentration increases, so that the cord-like body is easily affected.
索状体に塗料が付着すると索状体が硬化する原因となる。また、索状体に有機溶剤が付着すると索状体が劣化して、強度が低下する原因となる。索状体に有機溶剤が付着すると索状体の内部に有機溶剤が浸透する。索状体が一見汚れていないようでも、有機溶剤によって強度が低下している場合がある。索状体に粉塵が付着すると粉塵、索状体が動いた際に粉塵によって索状体に傷が入る原因となる。このため、索状体の強度を担保するために、索状体を頻繁に交換したり、頻繁に索状体の確認を行う必要がある。 Adhesion of paint to the cord causes the cord to harden. Further, if an organic solvent adheres to the cord-like body, the cord-like body deteriorates, which causes a decrease in strength. When the organic solvent adheres to the cord, the organic solvent permeates the inside of the cord. Even if the cords do not seem to be dirty at first glance, the strength may be reduced by the organic solvent. If dust adheres to the cord-like body, the dust may cause damage to the cord-like body due to the dust when the cord-like body moves. Therefore, in order to ensure the strength of the cords, it is necessary to replace the cords frequently and to check the cords frequently.
高所において塗装作業や塗膜の剥離作業を行う際には、上述のように、有機溶剤が飛散する環境となる。有機溶剤は、粘着剤層に作用して養生テープを剥がれやすくすることがある。また、有機溶剤が基材に浸透して、索状体に染み込むことがある。養生テープを、有機溶剤が存在する環境下で使用する場合は、養生テープの粘着剤層に粘着性付与樹脂を含有させることが好ましい。また、養生テープの基材は、ポリエチレン、ポリエステル、ポリプロピレン、ポリ塩化ビニル、ポリアミド、ポリカーボネート、ポリウレタン、又はこれらの高分子の原料となる２種以上のモノマーの共重合体等の合成樹脂材料で構成し、有機溶剤が浸透するのを防止することが好ましい。 As described above, when the painting work or the peeling work of the coating film is performed at a high place, the environment is such that the organic solvent is scattered. The organic solvent may act on the pressure-sensitive adhesive layer to facilitate the peeling of the curing tape. In addition, the organic solvent may permeate the base material and soak into the cord-like body. When the curing tape is used in an environment in which an organic solvent is present, it is preferable that the adhesive layer of the curing tape contains a tackifying resin. The base material of the curing tape is composed of a synthetic resin material such as polyethylene, polyester, polypropylene, polyvinyl chloride, polyamide, polycarbonate, polyurethane, or a copolymer of two or more monomers which are raw materials for these polymers. However, it is preferable to prevent the organic solvent from penetrating.
上記の養生テープ１及び２は、例えば、円筒状の芯に巻回することによって、図６に示したように、索状体養生テープロール５とすることができる。粘着剤層は、テープロールの内側及び外側のいずれの向きに配置されるようにしてもよい。図６の例では、粘着剤層１２を破線で示したように、内側に配置している。粘着剤層１２を外側に向けて配置する際には、離型紙を使用すればよい。
The curing tapes 1 and 2 can be formed into a cord-shaped curing tape roll 5 as shown in FIG. 6 by winding the curing tapes 1 and 2 around a cylindrical core, for example. The pressure-sensitive adhesive layer may be arranged either inside or outside the tape roll. In the example of FIG. 6, the pressure-
以下、養生テープの実施例を挙げて、具体的に説明する。 Hereinafter, a specific description will be given with reference to examples of curing tape.
〔実施例１〕
帯状の基材と、当該基材の長手方向に沿って配される粘着剤層とを有し、粘着剤層は前記基材の両端部に配配される図１と同様の構成を有する養生テープを製造し、当該養生テープを巻回してテープロールを製造した。
[Example 1]
It has a strip-shaped base material and a pressure-sensitive adhesive layer arranged along the longitudinal direction of the base material, and the pressure-sensitive adhesive layer has a curing structure similar to that in FIG. 1 arranged at both ends of the base material. A tape was manufactured, and the curing tape was wound around to manufacture a tape roll.
・粘着剤の調製
固形分が５０質量％であり、残部が液分であるアクリル系粘着剤と、Ｃ９系石油樹脂を含有する市販の粘着性付与樹脂と、テルペンフェノール樹脂と、硬化剤であるイソシアネートとを混合して、樹脂粒がなくなるまで撹拌した。なお、Ｃ９系石油樹脂は、ベースポリマーであるアクリル樹脂１００重量部に対して４０重部添加した。テルペンフェノール樹脂は、アクリル樹脂１００重量部に対して１０重量部添加して、粘着剤を調製した。
-Preparation of adhesive A acrylic adhesive having a solid content of 50% by mass and the balance being a liquid, a commercially available tackifying resin containing a C9 petroleum resin, a terpenphenol resin, and a curing agent. It was mixed with isocyanate and stirred until there were no resin particles. In addition, 40 parts by weight of C9 petroleum resin was added with respect to 100 parts by weight of acrylic resin which is a base polymer. The terpene phenol resin was added in an amount of 10 parts by weight to 100 parts by weight of the acrylic resin to prepare a pressure-sensitive adhesive.
・基材の作製
アルミニウム粉を練り込んだポリエチレン製のフラットヤーンクロスの片面に、ポリエチレンを溶融押し出しして、ラミネートした。
-Preparation of base material Polyethylene was melt-extruded and laminated on one side of a polyethylene flat yarn cloth kneaded with aluminum powder.
・粘着剤層の形成
上記のようにして作製した基材のラミネート層に対して、０．６Ｋｗ・ｍｉｎ/ｍ２でコロナ処理を施した。そして、基材の両端部にその長手方向に沿って、幅７．５ｍｍ、厚さ０．０５ｍｍとなるように、上記の粘着剤をコンマーター法によって塗布した。これを熱により乾燥して、ロール状に巻き取った。ラミネート層を備える基材の厚みは０．１１ｍｍであり、基材の幅は１２５０ｍｍである。
-Formation of Adhesive Layer The laminated layer of the base material prepared as described above was subjected to corona treatment at 0.6 Kw · min / m 2. Then, the above-mentioned adhesive was applied to both ends of the base material by the commuter method so as to have a width of 7.5 mm and a thickness of 0.05 mm along the longitudinal direction thereof. This was dried by heat and wound into a roll. The thickness of the base material provided with the laminated layer is 0.11 mm, and the width of the base material is 1250 mm.
〔実施例２〕
ポリエチレン製の不織布を、黒色顔料とＴｇ−２０℃のアクリル樹脂とを含有する含浸剤に浸漬して目止め処理を行い、片面に剥離剤を塗布したものを基材として使用したこと以外は、実施例１の養生テープと同様にして、実施例２に係る養生テープを製造した。
[Example 2]
Except for the fact that a polyethylene non-woven fabric was dipped in an impregnating agent containing a black pigment and an acrylic resin at Tg-20 ° C to perform a sealing treatment, and a release agent was applied to one side as a base material. The curing tape according to Example 2 was produced in the same manner as the curing tape of Example 1.
〔実施例３〕
基材として、厚さ０．６６ｍｍの紙製の基材に対して、実施例２で使用したのと同様の黒色の含浸剤で目止め処理を行い、実施例２と同様の方法により剥離処理を行ったものを使用した点以外は、実施例２と同様にして、実施例３に係る養生テープを製造した。
[Example 3]
As the base material, a paper base material having a thickness of 0.66 mm was sealed with the same black impregnating agent used in Example 2, and peeled off by the same method as in Example 2. The curing tape according to Example 3 was produced in the same manner as in Example 2 except that the same as in Example 2 was used.
〔実施例４〕
Ｃ９系石油樹脂を含有しない粘着剤を使用して、養生テープを構成した点以外は、実施例１と同様にして、実施例４に係る養生テープを製造した。実施例４の養生テープに使用した粘着剤は、Ｃ９石油樹脂を含有しない点を除けば、実施例１で使用した粘着剤と同じである。
[Example 4]
The curing tape according to Example 4 was produced in the same manner as in Example 1 except that the curing tape was formed by using an adhesive containing no C9 petroleum resin. The pressure-sensitive adhesive used for the curing tape of Example 4 is the same as the pressure-sensitive adhesive used in Example 1 except that it does not contain C9 petroleum resin.
〔比較例１〕
粘着剤を基材の全面に塗布した点以外は、実施例２と同様にして比較例１に係る養生テープを製造した。
[Comparative Example 1]
The curing tape according to Comparative Example 1 was produced in the same manner as in Example 2 except that the adhesive was applied to the entire surface of the base material.
図３に示したように、実施例１ないし４の養生テープの粘着剤層同士が接面するようにして、索状体の周方向に包み込むように筒状に実施例１ないし４の養生テープを索状体である合成繊維製のロープに対して固定した。実施例１ないし４の養生テープは、いずれも索状体に対して簡単に筒状に固定することが可能であり、作業性に優れていた。 As shown in FIG. 3, the curing tapes of Examples 1 to 4 are formed in a tubular shape so that the adhesive layers of the curing tapes of Examples 1 to 4 are in contact with each other and are wrapped in the circumferential direction of the cord-like body. Was fixed to a rope made of synthetic fiber, which is a cord-like body. All of the curing tapes of Examples 1 to 4 could be easily fixed to the cord-like body in a tubular shape, and were excellent in workability.
上記のように、実施例１ないし４の養生テープを固定した索状体を高所における安全帯として使用した。作業現場では、塗装作業を行っており、遮蔽用の膜内に塗料と有機溶剤が飛散する環境であった。実施例１ないし４の養生テープは、いずれも、索状体から養生テープをずらした状態としたり、養生テープの一部を剥がすことにより、索状体の様子を観察したり触って確認することが可能であった。作業後には、実施例１から４の養生テープを索状体から剥がして、索状体から完全に養生テープを取り去る作業も簡単に行うことができた。 As described above, the cord-like body to which the curing tape of Examples 1 to 4 was fixed was used as a safety belt at a high place. At the work site, painting work was being carried out, and the environment was such that the paint and organic solvent were scattered inside the shielding film. In each of the curing tapes of Examples 1 to 4, the state of the cord-like body is observed or touched by shifting the curing tape from the cord-like body or by peeling off a part of the curing tape. Was possible. After the work, the curing tapes of Examples 1 to 4 could be easily peeled off from the cord-like body to completely remove the curing tape from the cord-like body.
一方、比較例１の養生テープでは、粘着剤が基材の全面に塗布されていることから、索状体に対して養生テープを筒状に固定しようとした際に、粘着剤層同士が貼り付いたり、索状体に対して養生テープの粘着剤層が意図せず貼り付いたりして、作業性がよくなかった。比較例１の養生テープをずらしたり、養生テープの一部を剥がして索状体の様子を確認しようとした際には、索状体に養生テープの全体が貼り付いているため、簡単にずらしたり一部を剥がしたりすることができなかった。なお、比較例１の養生テープで養生した索状体を、高所での塗装作業が終わった後に確認したところ、索状体は、塗料や有機溶剤で汚れておらず、きれいな状態であった。 On the other hand, in the curing tape of Comparative Example 1, since the adhesive is applied to the entire surface of the base material, the adhesive layers are stuck to each other when the curing tape is fixed to the cord-like body in a tubular shape. The workability was not good because the adhesive layer of the curing tape was unintentionally attached to the cord-like body. When the curing tape of Comparative Example 1 is shifted or a part of the curing tape is peeled off to check the state of the cord-like body, the entire curing tape is attached to the cord-like body, so that the curing tape can be easily shifted. I couldn't peel off a part of it. When the cord-like body cured with the curing tape of Comparative Example 1 was confirmed after the painting work at a high place was completed, the cord-like body was not contaminated with paint or an organic solvent and was in a clean state. ..
同様に高所での塗装作業が終わった後に、実施例１及び実施例２の養生テープで養生した索状体を確認したところ、索状体は、塗料や有機溶剤で汚れておらず、きれいな状態であった。 Similarly, after the painting work at a high place was completed, the cords cured with the curing tapes of Examples 1 and 2 were confirmed, and the cords were not contaminated with paint or organic solvent and were clean. It was in a state.
同様に高所での塗装作業が終わった後に、実施例３及び実施例４の養生テープで養生した索状体を確認した。実施例３の養生テープでは、高所における塗装作業終了後において養生テープに剥がれは見られなかったものの、索状体に対して塗料に含まれる有機溶剤が染み込んだような汚れが確認された。実施例３の養生テープを構成する基材を確認すると、溶剤が基材に染み込んでいた。 Similarly, after the painting work at a high place was completed, the cords cured with the curing tapes of Examples 3 and 4 were confirmed. In the curing tape of Example 3, although the curing tape was not peeled off after the completion of the painting work at a high place, it was confirmed that the cord-like body was stained with the organic solvent contained in the paint. When the base material constituting the curing tape of Example 3 was confirmed, the solvent had permeated into the base material.
実施例４の養生テープでは、高所における塗装作業終了後において、養生テープが部分的に数か所剥がれており、索状体が塗料で汚れていた。養生テープが剥離した部分から塗料が侵入し、索状体が塗料で汚れたものと推測される。 In the curing tape of Example 4, after the painting work at a high place was completed, the curing tape was partially peeled off in several places, and the cord-like body was contaminated with paint. It is presumed that the paint invaded from the part where the curing tape was peeled off and the cord was soiled with the paint.
なお、実施例３及び４の養生テープは、塗装作業を行わない高所の現場で使用した際には、剥がれや塗料又は有機溶剤による汚れの問題は生じなかった。 When the curing tapes of Examples 3 and 4 were used at a high place where painting work was not performed, there was no problem of peeling or stains due to paint or an organic solvent.
以上のように、実施例１ないし４の養生テープは、索状体に対して簡単に取り付けたり取り外すことが容易であり、索状体の状態を確認する必要がある際には、一部を剥がしたり、位置をずらしたりして、索状体の様子を簡単に確認することができた。実施例３及び４の養生テープは、鉄粉などの塵芥や摩擦から索状体を保護する効果に優れていた。実施例１及び２の養生テープは、これに加えて、有機溶剤や塗料が存在する環境下における使用においても、剥がれや有機溶剤の浸潤や侵入がみられず、索状体を適切に保護できるものであった。 As described above, the curing tapes of Examples 1 to 4 can be easily attached to and detached from the cord-like body, and when it is necessary to check the state of the cord-like body, a part of the curing tape is used. By peeling it off or shifting its position, it was possible to easily check the state of the cord. The curing tapes of Examples 3 and 4 were excellent in the effect of protecting the cord-like body from dust such as iron powder and friction. In addition to this, the curing tapes of Examples 1 and 2 are not peeled off or infiltrated or invaded by the organic solvent even when used in an environment in which an organic solvent or paint is present, and can appropriately protect the cord. It was a thing.
次に、粘着性付与剤について検討した。実施例１の養生テープでは、粘着性付与剤として、Ｃ９系石油樹脂を使用した。この粘着性付与樹脂に替えて、ロジンを含有する粘着性付与樹脂、テルペンを含有する粘着性付与樹脂、エチレン酢酸ビニル共重合体を含有する粘着性付与樹脂、Ｃ５系石油樹脂を含有する市販の粘着性付与樹脂、又は、市販のＣ５系石油樹脂と市販のＣ９系石油樹脂とを混合した粘着性付与樹脂をそれぞれ使用して、養生テープを作製した。 Next, the tackifier was examined. In the curing tape of Example 1, a C9-based petroleum resin was used as the tackifier. Instead of this tackifier resin, a commercially available tackifier resin containing rosin, a tackiness-imparting resin containing terpene, a tackiness-imparting resin containing an ethylene-vinyl acetate copolymer, and a C5 petroleum resin are commercially available. A curing tape was prepared by using an adhesive-imparting resin or an adhesive-imparting resin in which a commercially available C5 petroleum resin and a commercially available C9 petroleum resin were mixed.
ロジンを含有する粘着性付与剤を使用した養生テープと、テルペンを含有する粘着性付与剤を使用した養生テープでは、粘着力は向上したものの、有機溶剤が存在する環境下で使用すると、養生テープが剥がれてしまった。エチレン酢酸ビニル共重合体を含有する粘着性付与剤を使用した養生テープと、Ｃ５系石油樹脂を含有する粘着性付与剤を使用した養生テープでは、アクリル系粘着剤と粘着性付与樹脂とが互いに溶け合わず、ゲル状の析出物が生じた。Ｃ５系石油樹脂とＣ９系石油樹脂とを含有する粘着性付与剤については、Ｃ５系石油樹脂の含有量が、粘着剤のベースポリマーであるアクリル樹脂１００重量部に対して、Ｃ５系石油樹脂が１０重量部であれば、析出物が生じず、有機溶剤の存在下で粘着剤層から剥がれることはなかった。Ｃ５系石油樹脂の含有量がアクリル樹脂１００重量部に対して１６重量部を超えると、析出物が生じた。 Although the adhesive strength of the curing tape using the rosin-containing adhesive-imparting agent and the curing tape using the terpene-containing adhesive-imparting agent was improved, the curing tape was used in an environment in which an organic solvent was present. Has peeled off. In the curing tape using the tackifier containing ethylene-vinyl acetate copolymer and the curing tape using the tackifier containing C5 petroleum resin, the acrylic pressure-sensitive adhesive and the tack-imparting resin are mutually exclusive. It did not dissolve and a gel-like precipitate was formed. Regarding the tackifier containing the C5 type petroleum resin and the C9 type petroleum resin, the content of the C5 type petroleum resin is 100 parts by weight of the acrylic resin which is the base polymer of the pressure-sensitive adhesive. When it was 10 parts by weight, no precipitate was formed and it did not peel off from the pressure-sensitive adhesive layer in the presence of the organic solvent. When the content of the C5 petroleum resin exceeded 16 parts by weight with respect to 100 parts by weight of the acrylic resin, precipitates were formed.
１ 索状体養生テープ
１１ 基材
１２ 粘着剤層
４ 索状体
２ 索状体養生テープ
1 Cord-shaped
Claims (8)
当該粘着剤層は、少なくとも前記基材の一端部に配されており、
前記基材の長手方向に沿って安全帯に接続される索状体を配置して、索状体を周方向に包み込むように前記粘着剤層により筒状に固定して索状体を被覆する索状体養生テープ。 It has a strip-shaped base material and an adhesive layer arranged along the longitudinal direction of the base material.
The pressure-sensitive adhesive layer is arranged at least at one end of the base material.
A cord-like body connected to the safety belt is arranged along the longitudinal direction of the base material, and the cord-like body is fixed in a tubular shape by the adhesive layer so as to wrap the cord-like body in the circumferential direction to cover the cord-like body. Cord-shaped body curing tape.