JP2021019816A - Cleaning tool - Google Patents
Cleaning tool Download PDFInfo
- Publication number
- JP2021019816A JP2021019816A JP2019137954A JP2019137954A JP2021019816A JP 2021019816 A JP2021019816 A JP 2021019816A JP 2019137954 A JP2019137954 A JP 2019137954A JP 2019137954 A JP2019137954 A JP 2019137954A JP 2021019816 A JP2021019816 A JP 2021019816A
- Authority
- JP
- Japan
- Prior art keywords
- cleaning
- cleaning tool
- water
- abrasive
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本開示の一側面は、洗浄具に関する。 One aspect of the disclosure relates to cleaning tools.
特許文献１には、洗浄具として不織布研磨材製品が記載されている。不織布研磨材製品は、不織布と、結合剤と、結合剤に接着する研磨粒子とを有する。結合剤は、不織布の繊維の表面に接着する衝撃緩和性粒子を含んでおり、衝撃緩和性粒子は、弾性体材料からなるコア部と、結合剤マトリクスと良好な相溶性を示す樹脂材料からなるシェル部とを含むコア−シェルゴム粒子である。また、衝撃緩和性粒子には結合材層が設けられており、研磨粒子は結合材層に部分的に埋没した状態で結合材層に接着している。 Patent Document 1 describes a non-woven fabric abrasive product as a cleaning tool. The non-woven fabric abrasive product has a non-woven fabric, a binder, and abrasive particles that adhere to the binder. The binder contains impact-absorbing particles that adhere to the surface of the fibers of the non-woven fabric, and the impact-absorbing particles consist of a core made of an elastic material and a resin material that exhibits good compatibility with the binder matrix. Core-shell rubber particles including a shell portion. Further, the impact-absorbing particles are provided with a binder layer, and the abrasive particles are adhered to the binder layer in a state of being partially embedded in the binder layer.
前述した不織布研磨材製品では、粒状の研磨剤が研磨粒子として接着していることにより、洗浄対象物を磨いて当該洗浄対象物の汚れを効果的に落とすことが可能となる。しかしながら、研磨剤は、粒状であることにより、不織布研磨材製品から落下することがある。不織布研磨材製品は袋に封入された状態で流通することがあり、流通する過程で粒状の研磨剤が落下することによって袋の中に研磨剤が溜まることがある。多くの粒状の研磨剤が落下して袋の中に溜まっている場合、食品衛生上の観点から問題となる可能性がある。従って、粒状の研磨剤の落下を低減させること、特に使用前の流通過程における研磨剤の落下を防止することが望まれている。 In the non-woven fabric abrasive product described above, since the granular abrasive is adhered as polishing particles, it is possible to polish the object to be cleaned and effectively remove the dirt on the object to be cleaned. However, since the abrasive is granular, it may fall off the non-woven abrasive product. Non-woven abrasive products may be distributed in a state of being enclosed in a bag, and the abrasive may be accumulated in the bag due to dropping of granular abrasive in the process of distribution. If many granular abrasives fall and collect in the bag, it can be a problem from a food hygiene point of view. Therefore, it is desired to reduce the drop of the granular abrasive, especially to prevent the drop of the abrasive in the distribution process before use.
本開示の一形態に係る洗浄具は、粒状の研磨剤が付着している洗浄基材と、洗浄基材に含まれている水溶性糊と、を備える。 The cleaning tool according to one embodiment of the present disclosure includes a cleaning base material to which a granular abrasive is attached, and a water-soluble glue contained in the cleaning base material.
本開示の一形態によれば、使用前の粒状の研磨剤の落下を低減させることができる。 According to one embodiment of the present disclosure, it is possible to reduce the drop of the granular abrasive before use.
以下では、図面を参照しながら本開示に係る洗浄具の実施形態について説明する。図面の説明において、同一又は相当する要素には同一の符号を付し、重複する説明を適宜省略する。また、図面は、一部を簡略化又は誇張して描いている場合があり、寸法比率等は図面に記載のものに限定されない。 Hereinafter, embodiments of the cleaning tool according to the present disclosure will be described with reference to the drawings. In the description of the drawings, the same or corresponding elements are designated by the same reference numerals, and duplicate description will be omitted as appropriate. In addition, the drawings may be partially simplified or exaggerated, and the dimensional ratios and the like are not limited to those described in the drawings.
本実施形態に係る洗浄具は、洗浄対象物を擦って洗浄対象物に付着した汚れ等を除去するものである。本開示における「洗浄対象物」とは、洗浄の対象となる物を示しており、例えば、調理器具、食器、衣類、機械又は構造物等、種々の物が含まれる。「洗浄」は、汚れを取り除くことを示しており、例えば、洗浄具を洗浄対象物に擦りつけて洗浄対象物の汚れを掻き落とすこと、水又は洗剤を用いて汚れを除去すること、及び錆等の付着物を磨いて除去することを含んでいる。「汚れ」は、付着することが好まれない物を示しており、例えば、油汚れ、食物かす、石けんかす、水アカ及び錆等を含んでいる。 The cleaning tool according to the present embodiment rubs the object to be cleaned to remove dirt and the like adhering to the object to be cleaned. The “object to be washed” in the present disclosure refers to an object to be washed, and includes, for example, various objects such as cooking utensils, tableware, clothes, machines, and structures. "Washing" refers to removing dirt, for example, rubbing a cleaning tool against the object to be cleaned to scrape off the object to be cleaned, removing dirt with water or detergent, and rusting. It includes polishing and removing deposits such as. "Dirt" refers to things that are not preferred to adhere, including, for example, oil stains, food debris, soap scum, water stains and rust.
本実施形態に係る洗浄具は、例えば、不織布によって構成されている。本開示において、「不織布」とは、繊維を織らずに、熱若しくは接着剤によって、又は繊維同士を互いに絡ませることによって形成された構造体又は構造体の一部を示している。洗浄具は、熱可塑性樹脂からなるコイル状フィラメントによって形成されていてもよい。 The cleaning tool according to the present embodiment is made of, for example, a non-woven fabric. In the present disclosure, the "nonwoven fabric" refers to a structure or a part of a structure formed by heat or an adhesive without weaving fibers or by entwining fibers with each other. The cleaning tool may be formed of a coiled filament made of a thermoplastic resin.
「熱可塑性樹脂」は、加熱によって軟化し、熱が加えられることによって成形可能な材料を示しており、例えば、熱可塑性弾性樹脂及び熱可塑性樹脂エラストマーを含んでいる。「コイル状フィラメント」は、複数の線状の樹脂部材が互いに絡み合って形成された構造体を示しており、コイルドウェブ、コイル状不織布フィラメントウェブ、立体網状構造体、立体網目構造体。又は三次元樹脂構造体と称することもある。 “Thermoplastic resin” refers to a material that is softened by heating and can be molded by applying heat, and includes, for example, a thermoplastic elastic resin and a thermoplastic resin elastomer. The "coil-like filament" indicates a structure formed by entwining a plurality of linear resin members with each other, and is a coiled web, a coiled non-woven fabric filament web, a three-dimensional network structure, or a three-dimensional network structure. Alternatively, it may be referred to as a three-dimensional resin structure.
図１は、実施形態に係る例示的な洗浄具１を示す斜視図である。図１に示されるように、洗浄具１は、コイル状フィラメントによって形成された洗浄基材２と、洗浄基材２に塗布されている水溶性糊３とを備える。使用前において水溶性糊３は乾いて硬化した状態とされている。 FIG. 1 is a perspective view showing an exemplary cleaning tool 1 according to an embodiment. As shown in FIG. 1, the cleaning tool 1 includes a cleaning base material 2 formed of a coiled filament and a water-soluble glue 3 applied to the cleaning base material 2. Before use, the water-soluble glue 3 is in a dry and cured state.
「洗浄基材」とは、洗浄具を形成するベースとなる部分を示しており、洗浄具の外観を形成する洗浄具の本体、すなわち、洗浄具に付加又は添加される物以外の物を示している。「水溶性糊」とは、水に溶ける性質を有する粘性体を示しており、例えば、ポリビニルアルコール（ＰＶＡ）、澱粉及びメチルセルロースの少なくともいずれかを含む粘性体が挙げられる。 The “cleaning substrate” refers to a portion that forms a base for forming a cleaning tool, and refers to a main body of the cleaning tool that forms the appearance of the cleaning tool, that is, a material other than those added to or added to the cleaning tool. ing. The "water-soluble glue" refers to a viscous substance having a property of being soluble in water, and examples thereof include a viscous substance containing at least one of polyvinyl alcohol (PVA), starch and methyl cellulose.
洗浄具１は、一例として、調理器具の汚れを掻き取って調理器具の洗浄を行うたわしである。洗浄具１は、例えば、食品工場又は飲食店の調理場等で、調理器具又は食器の洗浄を行うときに用いられる。洗浄具１は、洗剤が塗布された状態で調理器具に擦りつけられるものであってもよい。 The cleaning tool 1 is, for example, a scrubbing brush that scrapes off dirt from the cooking utensil to clean the cooking utensil. The cleaning tool 1 is used, for example, when cleaning cooking utensils or tableware in a kitchen of a food factory or a restaurant. The cleaning tool 1 may be one that is rubbed against a cooking utensil with the detergent applied.
一例として、洗浄具１の外観は直方体状とされており、手で握りやすい大きさとされていてもよい。本開示において「直方体状」とは、矩形の面によって構成された立体を示しており、例えば、長手方向、幅方向及び厚さ方向を有する三次元構造体を含んでいる。例えば、洗浄具１の長手方向Ｄ１の長さＬ１は５ｃｍ以上且つ２０ｃｍ以下であり、洗浄具１の幅方向Ｄ２の長さＬ２（幅）は３ｃｍ以上且つ１５ｃｍ以下であり、洗浄具１の厚さ方向Ｄ３の長さＬ３（厚さ）は１ｃｍ以上且つ１０ｃｍ以下である。但し、長さＬ１、長さＬ２及び長さＬ３の各値は、上記の例に限られず適宜変更可能である。更に、洗浄具の形状は、直方体状に限られず、例えば、球形状又は楕円体状であってもよく、適宜変更可能である。 As an example, the appearance of the cleaning tool 1 has a rectangular parallelepiped shape, and may have a size that is easy to hold by hand. In the present disclosure, the term "rectangular parallelepiped" refers to a solid composed of rectangular surfaces, and includes, for example, three-dimensional structures having longitudinal, width, and thickness directions. For example, the length L1 of the cleaning tool 1 in the longitudinal direction D1 is 5 cm or more and 20 cm or less, the length L2 (width) of the width direction D2 of the cleaning tool 1 is 3 cm or more and 15 cm or less, and the thickness of the cleaning tool 1 The length L3 (thickness) of the longitudinal direction D3 is 1 cm or more and 10 cm or less. However, the values of the length L1, the length L2, and the length L3 are not limited to the above examples and can be changed as appropriate. Further, the shape of the cleaning tool is not limited to the rectangular parallelepiped shape, and may be, for example, a spherical shape or an ellipsoidal shape, and can be appropriately changed.
洗浄基材２の材料は、例えば、ポリアミド系、ウレタン系、ポリオレフィン系及びポリエステル系の少なくともいずれかを含んでいてもよい。一例として、洗浄基材２はナイロン系の材料によって構成されている。また、洗浄基材２はバインダーを含んでいてもよく、バインダーはイソシアネート樹脂、イソシアヌクレート樹脂、フェノール樹脂、エポキシ樹脂、尿素−ホルムアルデヒド樹脂、ワニス、アクリル樹脂及びこれらの混合物の少なくともいずれかを含んでいてもよい。 The material of the cleaning base material 2 may contain, for example, at least one of polyamide-based, urethane-based, polyolefin-based and polyester-based. As an example, the cleaning base material 2 is made of a nylon-based material. Further, the cleaning base material 2 may contain a binder, and the binder contains at least one of an isocyanate resin, an isocyanucrate resin, a phenol resin, an epoxy resin, a urea-formaldehyde resin, a varnish, an acrylic resin and a mixture thereof. You may be.
洗浄基材２は、複数の線状の樹脂部材２ｂが互いに絡み合って形成されている。また、洗浄基材２は、着色されていてもよく、これにより色鮮やかな洗浄具１とすることが可能である。洗浄基材２の色彩は、一例として、青、黒又は橙であるが、黄、緑、赤、茶又は桃色であってもよく、適宜変更可能である。 The cleaning base material 2 is formed by entwining a plurality of linear resin members 2b with each other. Further, the cleaning base material 2 may be colored, which makes it possible to obtain a colorful cleaning tool 1. The color of the cleaning base material 2 is, for example, blue, black, or orange, but may be yellow, green, red, brown, or pink, and can be changed as appropriate.
なお、洗浄基材２の色彩が青である場合、青の食品が少ないことにより、万が一洗浄基材２の線状の樹脂部材２ｂが食品に混入しても当該混入を発見しやすくすることができる。上記のように洗浄基材２が着色されている場合、複数の洗浄具１を用途別又は研磨力別に使い分けることが可能となる。 When the color of the cleaning base material 2 is blue, the amount of blue food is small, so that even if the linear resin member 2b of the cleaning base material 2 is mixed in the food, the contamination can be easily detected. it can. When the cleaning base material 2 is colored as described above, it is possible to use a plurality of cleaning tools 1 according to the application or the polishing power.
また、樹脂部材２ｂの線径（繊維径）は、例えば、０．１ｍｍ以上且つ１０ｍｍ以下である。なお、樹脂部材２ｂの線径の下限は０．２ｍｍ、０．３ｍｍ、０．５ｍｍ又は１．０ｍｍであってもよく、樹脂部材２ｂの線径の上限は９ｍｍ、８ｍｍ、７ｍｍ、５ｍｍ、３ｍｍ又は１ｍｍであってもよい。更に、樹脂部材２ｂの線径は、０．３ｍｍ以上且つ１．０ｍｍ以下であってもよく、適宜変更可能である。 The wire diameter (fiber diameter) of the resin member 2b is, for example, 0.1 mm or more and 10 mm or less. The lower limit of the wire diameter of the resin member 2b may be 0.2 mm, 0.3 mm, 0.5 mm or 1.0 mm, and the upper limit of the wire diameter of the resin member 2b is 9 mm, 8 mm, 7 mm, 5 mm and 3 mm. Alternatively, it may be 1 mm. Further, the wire diameter of the resin member 2b may be 0.3 mm or more and 1.0 mm or less, and can be changed as appropriate.
洗浄基材２は、粒状の研磨剤を有する。研磨剤は、洗浄対象物に対する洗浄具１の洗浄力を高めるために洗浄基材２に満遍なく塗布されている。研磨剤の形状は、球形状、楕円体状、直方体状、立方体状、正多面体状、及び不定形のいずれであってもよい。研磨剤の直径又は一辺の長さ（平均値）は、例えば、０．００３ｍｍ以上、０．０１ｍｍ以上又は０．１ｍｍ以上である。研磨剤の直径又は一辺の長さ（平均値）は、３ｍｍ以下、１ｍｍ以下、又は０．５ｍｍ以下である。 The cleaning substrate 2 has a granular abrasive. The abrasive is evenly applied to the cleaning base material 2 in order to enhance the cleaning power of the cleaning tool 1 with respect to the object to be cleaned. The shape of the abrasive may be spherical, ellipsoidal, rectangular parallelepiped, cubic, regular polyhedral, or amorphous. The diameter or the length of one side (average value) of the abrasive is, for example, 0.003 mm or more, 0.01 mm or more, or 0.1 mm or more. The diameter of the abrasive or the length of one side (average value) is 3 mm or less, 1 mm or less, or 0.5 mm or less.
研磨剤は、例えば、洗浄基材２の樹脂部材２ｂに付着した砥粒であって、アクリル又はウレタン樹脂等のバインダー樹脂によって樹脂部材２ｂに固着している。例えば、バインダー樹脂と研磨剤の混合溶液を洗浄基材２にスプレーで塗布することにより、又はバインダー樹脂溶液を洗浄基材２に塗布した後に当該混合溶液又はバインダー溶液が塗布された塗布面に研磨剤を散布することにより、研磨剤を樹脂部材２ｂに固着させている。 The abrasive is, for example, abrasive grains attached to the resin member 2b of the cleaning base material 2, and is fixed to the resin member 2b by a binder resin such as acrylic or urethane resin. For example, by applying a mixed solution of a binder resin and an abrasive to the cleaning base material 2 by spraying, or after applying the binder resin solution to the cleaning base material 2, polishing is performed on the coated surface to which the mixed solution or the binder solution is applied. By spraying the agent, the abrasive is fixed to the resin member 2b.
研磨剤の材料は、一例として、メラミン樹脂を含んでいる。なお、研磨剤の材料は、例えば、ナイロン樹脂等の他の樹脂粒子、アルミナ、炭化ケイ素、ダイヤモンド、酸化セリウム、酸化クロム、エメリ、ガーネット、ザクロ石、コランダム又は珪砂等であってもよい。また、研磨剤は、酸化アルミニウム、シリコンカーバイド等からなる鉱物粒子等であってもよいし、これらの混合物の少なくともいずれかを含んでいてもよい。 The material of the abrasive contains, for example, a melamine resin. The material of the abrasive may be, for example, other resin particles such as nylon resin, alumina, silicon carbide, diamond, cerium oxide, chromium oxide, emery, garnet, garnet, corundum, silica sand, or the like. Further, the abrasive may be mineral particles made of aluminum oxide, silicon carbide or the like, or may contain at least one of a mixture thereof.
ところで、洗浄基材２から研磨剤が落下しやすいという問題に対しては、例えば、研磨剤を固着させた洗浄基材２にスプレーによる樹脂コーティングを行うことが考えられる。しかしながら、樹脂コーティングの場合、洗浄基材２の使用中も研磨剤が樹脂に覆われているので研磨剤による洗浄力が低下しうる。 By the way, to solve the problem that the abrasive is easily dropped from the cleaning base material 2, for example, it is conceivable to apply a resin coating by spraying to the cleaning base material 2 to which the abrasive is fixed. However, in the case of the resin coating, since the abrasive is covered with the resin even during the use of the cleaning base material 2, the cleaning power of the abrasive can be reduced.
そこで、本実施形態に係る洗浄具１では、洗浄基材２に水溶性糊３を含ませることによって洗浄基材２からの研磨剤の落下を抑制している。すなわち、研磨剤が固着している洗浄基材２に更に水溶性糊３を後述する方法で含ませる。水溶性糊３は、研磨剤を洗浄基材２の樹脂部材２ｂに更に強固に固着させることができる。水溶性糊３は、例えば、洗浄基材２からの研磨剤の脱落を抑制する液体糊である。水溶性糊３は、研磨剤を一時的に（例えば、洗浄具１の使用前、又は洗浄具１が袋から取り出されるまでの間）覆うものであって、洗浄具１を使用しているうちに水と共に溶けて流れていく。従って、洗浄具１の使用中には、研磨剤の研磨面が露出するため、研磨剤による研磨力の低下を抑制できる。なお、「研磨剤の研磨面」とは、研磨剤の表面のうち、洗浄対象物に擦り付けられて洗浄対象物の研磨に寄与する面を示している。例えば、洗浄具１の使用前において、水溶性糊３は、研磨剤の表面の２０％以上、５０％以上、又は８０％以上を被覆している。 Therefore, in the cleaning tool 1 according to the present embodiment, the cleaning base material 2 is impregnated with the water-soluble glue 3 to prevent the abrasive from falling from the cleaning base material 2. That is, the cleaning base material 2 to which the abrasive is adhered is further contained with the water-soluble glue 3 by the method described later. The water-soluble glue 3 can further firmly fix the abrasive to the resin member 2b of the cleaning base material 2. The water-soluble glue 3 is, for example, a liquid glue that suppresses the removal of the abrasive from the cleaning base material 2. The water-soluble glue 3 temporarily covers the abrasive (for example, before the cleaning tool 1 is used or until the cleaning tool 1 is taken out of the bag), and the cleaning tool 1 is used. It melts with water and flows. Therefore, since the polished surface of the abrasive is exposed during the use of the cleaning tool 1, it is possible to suppress a decrease in the polishing power due to the abrasive. The "polished surface of the abrasive" refers to the surface of the abrasive that is rubbed against the object to be cleaned and contributes to the polishing of the object to be cleaned. For example, before using the cleaning tool 1, the water-soluble glue 3 covers 20% or more, 50% or more, or 80% or more of the surface of the abrasive.
水溶性糊３のけん化度は、例えば、９６ｍｏｌ％以上且つ１００ｍｏｌ％以下、又は９７ｍｏｌ％以上且つ１００ｍｏｌ％以下である。水溶性糊３は完全けん化のＰＶＡであってもよい。また、水溶性糊３の平均重合度は、一例として、９００以上且つ１１００以下である。しかしながら、水溶性糊３のけん化度及び平均重合度は前述の例に限られず適宜変更可能である。 The saponification degree of the water-soluble glue 3 is, for example, 96 mol% or more and 100 mol% or less, or 97 mol% or more and 100 mol% or less. The water-soluble glue 3 may be a completely saponified PVA. Further, the average degree of polymerization of the water-soluble glue 3 is, for example, 900 or more and 1100 or less. However, the saponification degree and the average degree of polymerization of the water-soluble glue 3 are not limited to the above-mentioned examples and can be appropriately changed.
また、水溶性糊３の材料は、ポリ酢酸ビニル（ＰＶＡｃ）、耐熱性ポリマー及びカルボキシメチルセルロース（ＣＭＣ）の少なくともいずれかを含むものであってもよい。更に、水溶性糊３の材料は、小麦、タピオカ及びコーンスターチの少なくともいずれかを含むものであってもよい。 Further, the material of the water-soluble glue 3 may contain at least one of polyvinyl acetate (PVAc), a heat-resistant polymer and carboxymethyl cellulose (CMC). Further, the material of the water-soluble glue 3 may contain at least one of wheat, tapioca and cornstarch.
水溶性糊３は、一例として、洗濯糊である。しかしながら、水溶性糊３は、水糊、澱粉糊、粒糊、又はケイコ−糊等の天然糊であってもよい。このように、水溶性糊３の材料及び種類は適宜変更可能である。また、水溶性糊３には、水溶性糊３の腐食を抑制するために、防腐剤が添加されていてもよい。 The water-soluble glue 3 is, for example, a laundry starch. However, the water-soluble glue 3 may be a natural glue such as water glue, starch glue, grain glue, or Keiko-glue. As described above, the material and type of the water-soluble glue 3 can be changed as appropriate. Further, a preservative may be added to the water-soluble glue 3 in order to suppress the corrosion of the water-soluble glue 3.
次に、洗浄基材２、水溶性糊３及び研磨剤を備える洗浄具１の製造方法の例について説明する。まず、複数の線状の樹脂部材２ｂを絡ませてコイルドウェブを形成し、一対のローラ間にコイルドウェブを通過させ、例えば、液状のバインダーと粒状の研磨剤とを含有するスラリーをコイルドウェブに塗布する。そして、バインダーを硬化してコイルドウェブを加熱することによって研磨剤が付着している洗浄基材２を作製する（洗浄基材を用意する工程）。 Next, an example of a method for manufacturing a cleaning tool 1 including a cleaning base material 2, a water-soluble glue 3, and an abrasive will be described. First, a plurality of linear resin members 2b are entwined to form a coiled web, and the coiled web is passed between a pair of rollers. For example, a slurry containing a liquid binder and a granular abrasive is coiled. Apply to the web. Then, the binder is cured and the coiled web is heated to prepare the cleaning base material 2 to which the abrasive is attached (step of preparing the cleaning base material).
次に、洗浄基材２に水溶性糊３を塗布する。具体的には、例えば、ＰＶＡの粉末を水に溶融して重量パーセント濃度が１％以上且つ１０％以下であるＰＶＡ溶液を水溶性糊３として作製する。そして、図２に示されるように、洗浄基材２に完全に浸るまで水溶性糊３を洗浄基材２に満遍なく注ぎかけることにより塗布する（水溶性糊を塗布する工程）。 Next, the water-soluble glue 3 is applied to the cleaning base material 2. Specifically, for example, a PVA powder having a weight percent concentration of 1% or more and 10% or less is prepared as a water-soluble glue 3 by melting PVA powder in water. Then, as shown in FIG. 2, the water-soluble glue 3 is evenly poured onto the cleaning base material 2 until it is completely immersed in the cleaning base material 2 (step of applying the water-soluble glue).
続いて、水溶性糊３が十分に塗布された洗浄基材２を乾燥させる。例えば、オーブンに洗浄基材２を入れて水溶性糊３を乾燥させる。一例として、水溶性糊３を乾燥させる温度は５０℃、水溶性糊３を乾燥させる時間は３０分である（水溶性糊を乾燥させる工程）。その後、洗浄基材２を所定の大きさに裁断した後に、洗浄具１が完成する。 Subsequently, the cleaning base material 2 to which the water-soluble glue 3 is sufficiently applied is dried. For example, the cleaning base material 2 is placed in an oven to dry the water-soluble glue 3. As an example, the temperature at which the water-soluble glue 3 is dried is 50 ° C., and the time for drying the water-soluble glue 3 is 30 minutes (step of drying the water-soluble glue). Then, after cutting the cleaning base material 2 to a predetermined size, the cleaning tool 1 is completed.
次に、本実施形態に係る洗浄具１の作用効果について説明する。 Next, the action and effect of the cleaning tool 1 according to the present embodiment will be described.
洗浄具１では、粒状の研磨剤が付着している洗浄基材２に水溶性糊３が含まれている。洗浄基材２に水溶性糊３が含まれていることによって、洗浄基材２に対する粒状の研磨剤の付着力を高めることができるので、洗浄基材２からの研磨剤の落下を低減させることができる。従って、使用前に袋に封入された状態で洗浄具１が流通する場合であっても、袋の内部における粒状の研磨剤の落下を抑制できるので、袋の中に多くの研磨剤が溜まる問題を回避することができる。 In the cleaning tool 1, the water-soluble glue 3 is contained in the cleaning base material 2 to which the granular abrasive is attached. Since the cleaning base material 2 contains the water-soluble glue 3, the adhesive force of the granular abrasive to the cleaning base material 2 can be increased, so that the falling of the abrasive from the cleaning base material 2 can be reduced. Can be done. Therefore, even when the cleaning tool 1 is distributed in a state of being enclosed in a bag before use, it is possible to suppress the fall of granular abrasives inside the bag, so that a large amount of abrasives accumulate in the bag. Can be avoided.
水溶性糊３は、ポリビニルアルコール（ＰＶＡ）を含んでいてもよい。この場合、ポリビニルアルコールが水溶性であって且つ生分解性があり更に無害であることにより、安全で環境に優しい水溶性糊とすることができる。水溶性糊３がポリビニルアルコールである場合、防腐性が高い水溶性糊３とすることができるため、衛生面の点においても優れた水溶性糊３とすることができる。 The water-soluble glue 3 may contain polyvinyl alcohol (PVA). In this case, since polyvinyl alcohol is water-soluble, biodegradable, and harmless, it can be a safe and environmentally friendly water-soluble paste. When the water-soluble glue 3 is polyvinyl alcohol, it can be a water-soluble glue 3 having high antiseptic properties, so that it can be an excellent water-soluble glue 3 in terms of hygiene.
また、水溶性糊３は、水溶性であって洗浄具１の使用中に水と共に流れるもの、すなわち、洗浄具１の使用前に研磨剤を一時的に覆うものであってもよい。この場合、ポリビニルアルコールを含む水溶性糊３は、生分解性が高いため環境への影響を低減させることができると共に、水溶性糊３を有しない場合と同等の洗浄力を発揮させることができる。研磨剤を被覆する水溶性糊３は、使用中に水と共に流れるため、使用中には研磨剤の研磨面が露出する。このため、水溶性糊３で被覆しない場合と同等の高い研磨性能を維持することができる。 Further, the water-soluble glue 3 may be water-soluble and flow with water during the use of the cleaning tool 1, that is, a material that temporarily covers the abrasive before the cleaning tool 1 is used. In this case, since the water-soluble glue 3 containing polyvinyl alcohol has high biodegradability, the influence on the environment can be reduced, and the detergency equivalent to that in the case without the water-soluble glue 3 can be exhibited. .. Since the water-soluble glue 3 that coats the abrasive flows with water during use, the polished surface of the abrasive is exposed during use. Therefore, high polishing performance equivalent to that in the case of not coating with the water-soluble glue 3 can be maintained.
洗浄基材２は、不織布によって構成されていてもよい。この場合、洗浄基材２の材料として不織布を用いることができる。 The cleaning base material 2 may be made of a non-woven fabric. In this case, a non-woven fabric can be used as the material of the cleaning base material 2.
洗浄基材２は、熱可塑性樹脂からなるコイル状フィラメントによって形成されていてもよい。この場合、コイル状フィラメントにおいて熱可塑性樹脂からなる線状の樹脂部材２ｂが絡み合って洗浄基材２が形成されているため、洗浄基材２を洗浄対象物に擦りつけることによって洗浄対象物の汚れを効果的に掻き落とすことができ、高い洗浄力を発揮する。 The cleaning base material 2 may be formed of a coiled filament made of a thermoplastic resin. In this case, since the linear resin member 2b made of a thermoplastic resin is entangled in the coiled filament to form the cleaning base material 2, the cleaning base material 2 is rubbed against the cleaning target object to stain the cleaning target object. Can be effectively scraped off and exerts high detergency.
本実施形態に係る洗浄具１の製造方法では、粒状の研磨剤が付着している洗浄基材２を用意する。そして、洗浄基材２に、前述したような図２に示される方法（洗浄基材２に注ぎかける方法）で水溶性糊３を塗布し、水溶性糊３を乾燥させる。従って、洗浄基材２に水溶性糊３が含まれていることによって洗浄基材２に対する研磨剤の付着力を高めることができるので、洗浄基材２からの研磨剤の落下を低減させることができる。また、研磨剤付きの洗浄基材２に水溶性糊３を塗布して乾燥させることにより、洗浄具１を容易に製造することができる。従って、研磨剤の落下が低減された洗浄具１の製造を容易に行うことができる。 In the method for manufacturing the cleaning tool 1 according to the present embodiment, the cleaning base material 2 to which the granular abrasive is attached is prepared. Then, the water-soluble glue 3 is applied to the cleaning base material 2 by the method shown in FIG. 2 (a method of pouring onto the cleaning base material 2) as described above, and the water-soluble glue 3 is dried. Therefore, since the cleaning base material 2 contains the water-soluble glue 3, the adhesive force of the abrasive to the cleaning base material 2 can be increased, so that the dropping of the abrasive from the cleaning base material 2 can be reduced. it can. Further, the cleaning tool 1 can be easily manufactured by applying the water-soluble glue 3 to the cleaning base material 2 with an abrasive and drying it. Therefore, it is possible to easily manufacture the cleaning tool 1 in which the drop of the abrasive is reduced.
以上、本開示に係る洗浄具の実施形態について説明した。しかしながら、本開示は前述した実施形態に限定されるものではない。例えば、洗浄基材の形状、大きさ及び材料は適宜変更可能である。また、洗浄具によって洗浄される洗浄対象物の種類も適宜変更可能である。一例として、洗浄対象物は構造物であってもよい。構造物としては、例えば、建物、機械及び車両等が挙げられる。建物は、壁、柱、窓、及び建物の内部設備等を含んでいてもよいし、機械は工作機械、搬送機械、及びその他のロボット等を含んでいてもよいし、車両は自動車及び自転車等を含んでいてもよい。これらの洗浄対象物に対しても本開示に係る洗浄具を適用させることが可能である。 The embodiment of the cleaning tool according to the present disclosure has been described above. However, the present disclosure is not limited to the embodiments described above. For example, the shape, size and material of the cleaning substrate can be changed as appropriate. Further, the type of the object to be cleaned to be cleaned by the cleaning tool can be changed as appropriate. As an example, the object to be cleaned may be a structure. Examples of the structure include buildings, machines, vehicles and the like. The building may include walls, pillars, windows, internal equipment of the building, etc., the machine may include machine tools, transport machines, other robots, etc., and the vehicle may include automobiles, bicycles, etc. May include. It is possible to apply the cleaning tool according to the present disclosure to these cleaning objects.
（実施例）
次に、本開示に係る洗浄具の実施例について説明する。本開示は、以下の実施例に限定されない。実施例では、後述する種々の実験を行い、実施例に係る洗浄具の有効性を確認した。
(Example)
Next, an example of the cleaning tool according to the present disclosure will be described. The present disclosure is not limited to the following examples. In the examples, various experiments described later were carried out to confirm the effectiveness of the cleaning tool according to the examples.
（粒状の研磨剤の落下状況を確認する実験）
本実験では、水溶性糊３を塗布した実施例１〜４に係る洗浄具１、及び水溶性糊３を塗布しない比較例１に係る洗浄具、のそれぞれに対して、研磨剤の落下状況を確認する実験を行った。実施例１〜４に係る洗浄具１、及び比較例１に係る洗浄具の詳細は以下のとおりである。
(Experiment to confirm the falling condition of granular abrasive)
In this experiment, the dropping state of the abrasive was determined for each of the cleaning tool 1 according to Examples 1 to 4 to which the water-soluble glue 3 was applied and the cleaning tool 1 according to Comparative Example 1 to which the water-soluble glue 3 was not applied. An experiment was conducted to confirm. The details of the cleaning tool 1 according to Examples 1 to 4 and the cleaning tool according to Comparative Example 1 are as follows.
（実施例１）
実施例１に係る洗浄具１は、コイルドウェブであって縦１１５ｍｍ×横１７０ｍｍ×厚さ３５ｍｍの直方体状たわしである３Ｍ（スリーエム）社製、“スコッチ・ブライト（登録商標）がんこたわし荒目”を研磨剤が固着した洗浄基材２として用意した。そして、重量パーセント濃度が１％であるＰＶＡ溶液を水溶性糊３として洗浄基材２に満遍なく注ぎかけることによって塗布し、オーブンに洗浄基材２を入れて５０℃で３０分間乾燥させて６０ｍｍ×１２５ｍｍに裁断し、実施例１の洗浄具１とした。
(Example 1)
The cleaning tool 1 according to the first embodiment is a coiled web, which is a rectangular scrubbing brush of 115 mm in length × 170 mm in width × 35 mm in thickness, manufactured by 3M Ltd., “Scotch-Brite® Gankowashi Coarse”. Was prepared as the cleaning base material 2 to which the abrasive was adhered. Then, a PVA solution having a weight percent concentration of 1% is applied as a water-soluble glue 3 by evenly pouring it onto the cleaning base material 2, and the cleaning base material 2 is placed in an oven and dried at 50 ° C. for 30 minutes to achieve 60 mm ×. It was cut to 125 mm and used as the cleaning tool 1 of Example 1.
（実施例２）
実施例２〜５に係る洗浄具１のそれぞれは、水溶性糊３のＰＶＡの重量パーセントが実施例１の洗浄具１と異なっており、その他の仕様は実施例１に係る洗浄具１と同一である。実施例２に係る洗浄具１では、水溶性糊３のＰＶＡの重量パーセントを２％とした。
(Example 2)
Each of the cleaning tools 1 according to Examples 2 to 5 has a different weight percentage of PVA of the water-soluble glue 3 from the cleaning tool 1 of Example 1, and other specifications are the same as those of the cleaning tool 1 according to Example 1. Is. In the cleaning tool 1 according to Example 2, the weight percentage of PVA of the water-soluble glue 3 was set to 2%.
（実施例３）
実施例３に係る洗浄具１では、水溶性糊３のＰＶＡの重量パーセントを５％とした。
(Example 3)
In the cleaning tool 1 according to Example 3, the weight percentage of PVA of the water-soluble glue 3 was set to 5%.
（実施例４）
実施例４に係る洗浄具１では、水溶性糊３のＰＶＡの重量パーセントを１０％とした。
(Example 4)
In the cleaning tool 1 according to Example 4, the weight percentage of PVA of the water-soluble glue 3 was set to 10%.
（比較例１）
比較例１に係る洗浄具は、水溶性糊３を塗布しないコイルドウェブであって縦１１５ｍｍ×横１７０ｍｍ×厚さ３５ｍｍの直方体状たわしである３Ｍ（スリーエム）社製、“スコッチ・ブライト（登録商標）がんこたわし荒目”とした。
(Comparative Example 1)
The cleaning tool according to Comparative Example 1 is a coiled web to which the water-soluble glue 3 is not applied, and is a rectangular parallelepiped scrubbing brush having a length of 115 mm, a width of 170 mm, and a thickness of 35 mm, manufactured by 3M Ltd. Trademark) "Gankowashi Rough".
以上の実施例１〜４及び比較例１に係る洗浄具を３個ずつ用意して、それぞれの洗浄具の重量を測定した。そして、それぞれの洗浄具をテーブルに５回衝突させ、各洗浄具を手で握って片手で１０回絞って洗浄具を捻り研磨剤を落下させた後、再度各洗浄具の重量を測定した。その後、研磨剤を落下させる前後における洗浄具の重量の差を算出し、算出した値を落下した研磨剤の重量とした。その算出の結果（平均値）を図３のグラフに示す。 Three cleaning tools according to Examples 1 to 4 and Comparative Example 1 were prepared, and the weight of each cleaning tool was measured. Then, each cleaning tool was made to collide with the table 5 times, each cleaning tool was grasped by hand, squeezed 10 times with one hand, the cleaning tool was twisted to drop the abrasive, and then the weight of each cleaning tool was measured again. Then, the difference in the weight of the cleaning tool before and after dropping the abrasive was calculated, and the calculated value was taken as the weight of the dropped abrasive. The result of the calculation (mean value) is shown in the graph of FIG.
図３に示されるように、水溶性糊３が塗布されていない比較例１の洗浄具では、落下した研磨剤の重量は３２．７ｍｇであった。これに対し、ＰＶＡの重量パーセントを１％とした水溶性糊３が塗布された実施例１に係る洗浄具１では、落下した研磨剤の重量は２５．７ｍｇ、実施例２，３，４に係る洗浄具１では、落下した研磨剤の重量はそれぞれ２２．３ｍｇ、１６．７ｍｇ、１．０ｍｇであった。 As shown in FIG. 3, in the cleaning tool of Comparative Example 1 to which the water-soluble glue 3 was not applied, the weight of the dropped abrasive was 32.7 mg. On the other hand, in the cleaning tool 1 according to Example 1 to which the water-soluble glue 3 having a weight percentage of PVA of 1% was applied, the weight of the dropped abrasive was 25.7 mg, and in Examples 2, 3 and 4. In the cleaning tool 1, the weights of the dropped abrasive were 22.3 mg, 16.7 mg, and 1.0 mg, respectively.
以上より、水溶性糊３が塗布された実施例１〜４の洗浄具１では、比較例１の洗浄具よりも、落下した研磨剤の重量を低減できることが分かった。具体的には、落下した研磨剤の重量を、ＰＶＡの濃度が１％の実施例１では２１％、ＰＶＡの濃度が２％の実施例２では３２％、ＰＶＡの濃度が５％の実施例３では４９％減らせることが分かった。更に、ＰＶＡの濃度が１０％である実施例４では、研磨剤の落下量を９７％も低減できることが分かった。このように、ＰＶＡを塗布した実施例１〜４に係る洗浄具１では、研磨剤の落下を効果的に抑制できることが分かった。 From the above, it was found that the cleaning tool 1 of Examples 1 to 4 coated with the water-soluble glue 3 can reduce the weight of the dropped abrasive as compared with the cleaning tool of Comparative Example 1. Specifically, the weight of the dropped abrasive is 21% in Example 1 having a PVA concentration of 1%, 32% in Example 2 having a PVA concentration of 2%, and 5% in PVA concentration. It was found that 3 can reduce 49%. Furthermore, it was found that in Example 4 in which the concentration of PVA was 10%, the amount of falling abrasive was reduced by 97%. As described above, it was found that the cleaning tool 1 according to Examples 1 to 4 coated with PVA can effectively suppress the falling of the abrasive.
（洗浄力を確認する実験）
前述したＰＶＡの濃度が５％の実施例３に係る洗浄具１、水溶性糊３を塗布しない比較例１に係る洗浄具、及び洗浄基材２に合成樹脂による樹脂コーティングを行った比較例２に係る洗浄具、のそれぞれに対して、洗浄力を確認する実験を行った。比較例２に係る洗浄具の詳細は以下のとおりである。
(Experiment to confirm detergency)
The cleaning tool 1 according to Example 3 having a PVA concentration of 5%, the cleaning tool according to Comparative Example 1 to which the water-soluble glue 3 is not applied, and Comparative Example 2 in which the cleaning base material 2 is coated with a synthetic resin. An experiment was conducted to confirm the detergency of each of the cleaning tools according to the above. The details of the cleaning tool according to Comparative Example 2 are as follows.
（比較例２）
比較例２に係る洗浄具は、水溶性糊３を塗布しないコイルドウェブであって縦１１５ｍｍ×横１７０ｍｍ×厚さ３５ｍｍの直方体状たわしである３Ｍ（スリーエム）社製、“スコッチ・ブライト（登録商標）がんこたわし荒目”にスプレーによって合成樹脂を塗布した。合成樹脂としては、ウレタン樹脂を含む合成樹脂を洗浄基材２に塗布した。
(Comparative Example 2)
The cleaning tool according to Comparative Example 2 is a coiled web to which the water-soluble glue 3 is not applied, and is a rectangular parallelepiped scrubbing brush having a length of 115 mm, a width of 170 mm, and a thickness of 35 mm, manufactured by 3M Ltd. Synthetic resin was applied by spraying to "Gankowashi Coarse". As the synthetic resin, a synthetic resin containing a urethane resin was applied to the cleaning base material 2.
以上の比較例２、並びに、前述した実施例３及び比較例１のそれぞれの洗浄具を用いて金属板を擦って洗浄する実験を行った。金属板には茶色の擬似的な焦げ汚れを塗布して付着させ、この模擬的な焦げ汚れを洗浄具で複数回擦って焦げ汚れの下の金属板が見えたときまでに擦っている回数（摺動回数）を測定した。金属板は長方形状とされており、金属板に洗浄具を一定の強さで押し当てて洗浄具を金属板の長手方向に沿って一定の強さで擦ることにより、洗浄具の摺動回数を測定して各洗浄具の洗浄力を検証した。その結果を以下の表１に示す。 An experiment was conducted in which the metal plate was rubbed and washed using the cleaning tools of Comparative Example 2 and the above-mentioned Examples 3 and 1 described above. Apply brown pseudo-burnt stains to the metal plate and attach it, and rub this simulated burnt stains multiple times with a cleaning tool until the metal plate under the burnt stains is visible. The number of slides) was measured. The metal plate has a rectangular shape, and the number of times the cleaning tool is slid by pressing the cleaning tool against the metal plate with a constant strength and rubbing the cleaning tool with a constant strength along the longitudinal direction of the metal plate. Was measured to verify the detergency of each cleaning tool. The results are shown in Table 1 below.
表１の「水洗い前」は、洗浄具を水洗いする前（初期状態）に洗浄具で金属板を擦って洗浄を行ったときの金属板に対する摺動回数を示しており、「水洗い後」は、洗浄具を水洗いした後に洗浄具で金属板を擦って洗浄を行ったときの金属板に対する摺動回数を示している。 "Before washing with water" in Table 1 shows the number of times the metal plate is rubbed with the washing tool before washing with water (initial state), and "after washing with water" is It shows the number of times of sliding on the metal plate when the metal plate is rubbed with the cleaning tool after washing the cleaning tool with water.
表１に示されるように、合成樹脂のコーティングを施した比較例２の洗浄具では、実施例３及び比較例１の洗浄具と比較して、金属板に対する摺動回数が多く、洗浄力が低いことが分かった。一方、実施例３の洗浄具１は、水洗い前の金属板に対する摺動回数は１８回で比較例１よりも３回多かったが、水洗い後の金属板に対する摺動回数は比較例１と同一の１５回だった。以上の結果より、水溶性糊３を含む実施例３の洗浄具１では、研磨剤の落下を抑制することができると共に、水溶性糊３を含まない比較例１の洗浄具と同等の洗浄力を発揮できることが分かった。 As shown in Table 1, the cleaning tool of Comparative Example 2 coated with a synthetic resin has a larger number of slides on the metal plate and has a higher cleaning power than the cleaning tools of Example 3 and Comparative Example 1. It turned out to be low. On the other hand, the cleaning tool 1 of Example 3 had 18 slides on the metal plate before washing with water, which was 3 times more than that of Comparative Example 1, but the number of slides on the metal plate after washing with water was the same as that of Comparative Example 1. It was 15 times. From the above results, the cleaning tool 1 of Example 3 containing the water-soluble glue 3 can suppress the falling of the abrasive and has the same cleaning power as the cleaning tool of Comparative Example 1 containing no water-soluble glue 3. It turned out that it can demonstrate.
１…洗浄具、２…洗浄基材、３…水溶性糊。 1 ... Cleaning tool, 2 ... Cleaning base material, 3 ... Water-soluble glue.
Claims (4)
前記洗浄基材に含まれている水溶性糊と、
を備える洗浄具。 A cleaning base material with granular abrasives attached,
The water-soluble glue contained in the cleaning substrate and
Cleaning tool equipped with.
請求項１に記載の洗浄具。 The water-soluble glue contains polyvinyl alcohol (PVA).
The cleaning tool according to claim 1.
請求項１又は２に記載の洗浄具。 The cleaning base material is made of a non-woven fabric.
The cleaning tool according to claim 1 or 2.
請求項１〜３のいずれか一項に記載の洗浄具。 The cleaning substrate is formed of a coiled filament made of a thermoplastic resin.
The cleaning tool according to any one of claims 1 to 3.