JP2021011417A - 厚膜抵抗体用組成物、厚膜抵抗体用ペースト、および厚膜抵抗体 - Google Patents
厚膜抵抗体用組成物、厚膜抵抗体用ペースト、および厚膜抵抗体 Download PDFInfo
- Publication number
- JP2021011417A JP2021011417A JP2019127963A JP2019127963A JP2021011417A JP 2021011417 A JP2021011417 A JP 2021011417A JP 2019127963 A JP2019127963 A JP 2019127963A JP 2019127963 A JP2019127963 A JP 2019127963A JP 2021011417 A JP2021011417 A JP 2021011417A
- Authority
- JP
- Japan
- Prior art keywords
- thick film
- film resistor
- mass
- range
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記導電性粉末は、銅、ニッケル、および、ニッケル酸ランタンからなり、
前記銅の含有量は30質量%〜70質量%の範囲にあり、前記ニッケルの含有量は10質量%〜35質量%の範囲にあり、ニッケル酸ランタンの含有量は0質量%を超えて20質量%以下であり、および、前記ガラスフリットの含有量は5質量%〜50質量%の範囲にある、
ことを特徴とする。
前記導電性成分は、銅、ニッケル、および、ニッケル酸ランタンからなり、
前記銅の含有量は30質量%〜70質量%の範囲にあり、前記ニッケルの含有量は10質量%〜35質量%の範囲にあり、ニッケル酸ランタンの含有量は0質量%を超えて20質量%以下であり、および、前記ガラス成分の含有量は5質量%〜50質量%の範囲にある、
ことを特徴とする。
本発明の厚膜抵抗体用組成物は、導電性粉末およびガラスフリットを主成分とする。
本発明の厚膜抵抗体用組成物を構成する導電性粉末は、銅、ニッケル、および、ニッケル酸ランタンからなる。
平均粒径(μm)={6/(理論密度(g/cm3)×比表面積(m2/g))}
本発明の厚膜抵抗体用組成物を構成するガラスフリットは、鉛を実質的に含まないガラスにより構成される。
本発明の厚膜抵抗体用組成物において、導電性粉末とガラスフリットのほかに、他の添加剤を添加することも可能である。たとえば、厚膜抵抗体における、抵抗値や抵抗温度係数などの電気的特性や温度特性の調整、膨張係数の調整、耐電圧性の向上、その他の改質を目的として、本発明の厚膜抵抗体用組成物は、酸化マンガン、酸化銅、酸化ニオブ、酸化スズ、酸化タンタル、酸化チタンなどの無機成分を、適宜含有することができる。
本発明の厚膜抵抗体用ペーストは、厚膜抵抗体用組成物と有機ビヒクルとを含み、該厚膜抵抗体用組成物として、上記の本発明の厚膜抵抗体用組成物が用いられていることを特徴とする。具体的には、本発明の厚膜抵抗体用ペーストは、本発明の厚膜抵抗体用組成物と有機ビヒクルの混練物により構成される。以下、詳細を説明する。
厚膜抵抗体用ペーストを構成する有機ビヒクルは、少なくとも樹脂と溶剤により構成される。
本発明の厚膜抵抗体用ペーストは、厚膜抵抗体用組成物と有機ビヒクルのほかに、添加剤を含むことができる。たとえば、導電性粉末やその他の無機成分などの凝集を防ぐ観点から、分散剤を含むことができる。また、塗布作業性の観点から、レオロジーコントロール剤を含むことができる。
厚膜抵抗体用ペーストの調製は、公知の技術を用いればよく、たとえば、3本ロールミル、ボールミルなどを用いることができる。
本発明の厚膜抵抗体は、導電性成分とガラス成分とを含む焼成体からなる。前記導電性成分は、銅、ニッケル、ニッケル酸ランタンを含む。前記ガラス成分は、鉛を実質的に含まないことを特徴とする。すなわち、本発明の厚膜抵抗体は、本発明の厚膜抵抗体用ペーストを用いて形成され、本発明の厚膜抵抗体用組成物の焼成体により構成される。
本発明の厚膜抵抗体の製造方法は、以下の内容に限定されるものではなく、処理条件などについては、公知の手段および方法を用いて、適宜変更することができる。
本発明の厚膜抵抗体の抵抗値は、抵抗体幅と抵抗体長さの比を1:100とした抵抗値から計算した面積抵抗値で評価される。本発明の厚膜抵抗体は、100mΩ/□〜15Ω/□の範囲にある面積抵抗値を有する。
抵抗温度係数(TCR)は、厚膜抵抗体の熱的安定性(温度特性)の指標となる。抵抗温度係数は次のように計算される。なお、抵抗温度係数のは単位は、ppm/℃である。
低温抵抗温度係数(CTCR)=[(R−55−R25)/R25(−55−25)]×106
負荷特性は、厚膜抵抗体の電流負荷に対する安定性(電気的特性の安定性)の指標となる。本発明においては、負荷特性として、200pFのコンデンサに2kVで充電した電荷を抵抗体に5回放電したときの抵抗値変化率の測定値(ΔR)を採用している。
[厚膜抵抗体用組成物]
〔導電性粉末〕
導電性粉末として、銅粉末、ニッケル粉末、ニッケル酸ランタン粉末を使用した。
ガラスフリットには、37重量%BaO−43重量%SiO2−7重量%B2O3−13重量%Al2O3の組成のガラスフリットを用いた。このガラスフリットは、通常の手段である、混合、溶融、急冷、および粉砕の工程を経ることによって作製した。なお、粉砕工程後のガラスフリットのレーザー式粒度分布測定器を用いた測定により得られた平均粒径D50は、2.0μmであった。
厚膜抵抗体用組成物:70質量%、および、アクリルとターピネオールを主成分とする有機ビヒクル(アクリル:ターピネオールは、1:4):30質量%を混合し、三本ロ−ルミルで混練して抵抗ペーストを作製した。
次に、得られた厚膜抵抗体の特性(面積抵抗値、抵抗温度係数(TCR)、負荷特性)を測定した。
低温抵抗温度係数(CTCR)=[(R−55−R25)/R25(−55−25)]×106
Claims (6)
- 導電性粉末と、鉛を実質的に含まないガラスフリットとを含み、
前記導電性粉末は、銅、ニッケル、および、ニッケル酸ランタンからなり、
前記銅の含有量は30質量%〜70質量%の範囲にあり、前記ニッケルの含有量は10質量%〜35質量%の範囲にあり、ニッケル酸ランタンの含有量は0質量%を超えて20質量%以下であり、および、前記ガラスフリットの含有量は5質量%〜50質量%の範囲にある、厚膜抵抗体用組成物。 - 前記導電性粉末は、銅およびニッケルからなる粉末と、ニッケル酸ランタン粉末とからなり、前記銅およびニッケルからなる粉末は、0.1μm〜3.0μmの範囲にあるBET法による平均粒径を有し、前記ニッケル酸ランタン粉末は、0.01μm〜0.2μmの範囲にあるBET法による平均粒径を有する、請求項1に記載の厚膜抵抗体用組成物。
- 前記ガラスフリットは、5μm以下のレーザー式粒度分布測定による平均粒径D50を有する、請求項1または2に記載の厚膜抵抗体用組成物。
- 厚膜抵抗体用組成物と有機ビヒクルとを含み、前記厚膜抵抗体用組成物として、請求項1〜3のいずれかに記載の厚膜抵抗体用組成物が用いられている、厚膜抵抗体用ペースト。
- 前記有機ビヒクルの含有量は、前記厚膜抵抗体用ペースト全体に対して、20質量%〜50質量%の範囲にある、請求項4に記載の厚膜抵抗体用ペースト。
- 導電性成分と、鉛を実質的に含まないガラス成分とを含む焼成体からなり、
前記導電性成分は、銅、ニッケル、および、ニッケル酸ランタンからなり、
前記銅の含有量は30質量%〜70質量%の範囲にあり、前記ニッケルの含有量は10質量%〜35質量%の範囲にあり、ニッケル酸ランタンの含有量は0質量%を超えて20質量%以下であり、および、前記ガラス成分の含有量は5質量%〜50質量%の範囲にある、
厚膜抵抗体。