JP2021008572A - Algae breeding coating composition, algae breeding coating film, base material with algae breeding coating film, and manufacturing method of the base material - Google Patents

Abstract

To provide an algae breeding coating composition capable of forming a fishing bank (seaweed bed) or a marine facility capable of sufficiently breeding algae, even in a season where proliferation of marine sessile animals becomes active such as summer.SOLUTION: An algae breeding coating composition contains a resin (A), water-soluble glass containing at least one element selected from the group consisting of iron, phosphorus and potassium (B), and medetomidine (C).SELECTED DRAWING: None

Description

本発明は、藻類増殖塗料組成物、藻類増殖塗膜、藻類増殖塗膜付き基材および該基材の製造方法に関する。 The present invention relates to an algae growth coating composition, an algae growth coating film, a base material with an algae growth coating film, and a method for producing the base material.

近年、日本・世界各地の沿岸域において、「磯焼け」と呼ばれる、海藻（藻場）が著しく減少または消失する現象が深刻化し、水産業に多大な影響を及ぼしている。 In recent years, in coastal areas around Japan and around the world, a phenomenon called "isoyake", in which seaweeds (seaweed beds) are significantly reduced or disappeared, has become serious and has a great impact on the fishing industry.

この問題に対し、藻類等を人工的に増殖させることを目的として、漁礁体（藻場）を海中に投入し、その表面に藻類を繁殖（増殖、繁茂ともいう。）させる方法が行われている。
海中に投入された漁礁体（藻場）には、藻類が速くかつ多く繁殖することが望ましいが、投入された海域によっては、成長速度や繁殖量に差があり、特に海水中の栄養分が少ない海域では、海藻類の付着生育がほとんど期待できない場合があるため、漁礁体（藻場）への藻類の繁殖を促進させる方法が検討されている。 To solve this problem, a method of throwing a fishing reef body (seaweed bed) into the sea and breeding (also referred to as breeding or overgrowth) algae on the surface thereof has been carried out for the purpose of artificially breeding algae or the like. There is.
It is desirable for algae to grow quickly and in large numbers on the fish reefs (seaweed beds) that have been put into the sea, but there are differences in the growth rate and amount of algae depending on the sea area where they are put, and the nutrients in the seawater are particularly low. Since there are cases where the adhesion and growth of algae can hardly be expected in the sea area, a method for promoting the growth of algae on the reef body (seaweed bed) is being studied.

例えば、特許文献１では、窒素含有物質、リン含有物質、アルカリ金属含有物質およびアルカリ土類金属含有物質から選ばれた２種以上を海藻類の栄養成分として含有する海藻類の増殖促進塗料組成物を漁礁体（藻場）に塗装する方法が開示されている。 For example, in Patent Document 1, a seaweed growth promoting coating composition containing two or more selected from a nitrogen-containing substance, a phosphorus-containing substance, an alkali metal-containing substance, and an alkaline earth metal-containing substance as a nutritional component of seaweed. The method of painting the fish reef body (seaweed bed) is disclosed.

特開昭５７−１７７６２８号公報JP-A-57-177628

しかしながら、前記特許文献１に記載された塗料組成物などの従来の塗料組成物を塗装した漁礁体（藻場）では、藻類を十分に繁殖させることができないことがわかった。
また、フジツボなどの海生付着動物の繁殖が活発となる夏季等では、該海生付着動物の影響により、藻類の繁殖が妨げられていることがわかった。さらに、海洋構造物等の没水部にフジツボなどの海生付着動物が付着すると、海生付着動物の成長に伴い、塗装されている塗膜がダメージを受け、鋼板等の海洋構造物の基材の腐食が進行することがあり、海洋構造物等のメンテナンス時に海生付着動物を除去する際にも塗膜がダメージを受けることがある。このため、フジツボなどの海生付着動物が付着せず、藻類のみを選択的に付着させ成長を促進する漁礁用塗料の開発が好ましいと考えられる。 However, it has been found that algae cannot be sufficiently propagated in a fishing reef body (seaweed bed) coated with a conventional paint composition such as the paint composition described in Patent Document 1.
It was also found that in summer, when the breeding of marine-attached animals such as barnacles is active, the breeding of algae is hindered by the influence of the marine-attached animals. Furthermore, when marine-attached animals such as Fujitsubo adhere to submerged parts of marine structures, etc., the coated coating film is damaged as the marine-attached animals grow, and the base of marine structures such as steel plates Corrosion of the material may progress, and the coating film may be damaged when removing marine-attached animals during maintenance of marine structures and the like. For this reason, it is considered preferable to develop a paint for fishing reefs that does not adhere to marine attached animals such as barnacles and selectively adheres only algae to promote growth.

近年、洋上風力発電などの洋上設備が建設されているが、このような洋上設備の没水部や水との接触部を漁礁化させることで、磯焼けの解消および水産資源の保全に繋げることが検討されている。 In recent years, offshore equipment such as offshore wind power generation has been constructed, and by turning the submerged parts and contact parts with water of such offshore equipment into fishing reefs, it will lead to the elimination of shore burning and the conservation of marine resources. Is being considered.

本発明は、前記課題に鑑みてなされたものであり、夏季などの海生付着動物の繁殖が活発となる時期においても、藻類を十分に繁殖させることが可能な漁礁体（藻場）や洋上設備等を形成することができる藻類増殖塗料組成物を提供することを目的とする。 The present invention has been made in view of the above problems, and is capable of breeding algae sufficiently even in a period such as summer when the breeding of marine attached animals is active, such as a reef body (seaweed bed) or offshore. It is an object of the present invention to provide an algae growth coating composition capable of forming equipment and the like.

本発明者らは前記課題を解決すべく鋭意検討した。その結果、下記構成例によれば、前記課題を解決できることを見出し、本発明を完成するに至った。本発明の構成例は、以下の通りである。 The present inventors have diligently studied to solve the above problems. As a result, they have found that the above problems can be solved according to the following configuration example, and have completed the present invention. A configuration example of the present invention is as follows.

＜１＞ 樹脂（Ａ）、鉄、リンおよびカリウムからなる群より選ばれる少なくとも１種の元素を含む水溶性ガラス（Ｂ）、および、メデトミジン（Ｃ）を含有する、藻類増殖塗料組成物。 <1> An algae growth coating composition containing a water-soluble glass (B) containing at least one element selected from the group consisting of resin (A), iron, phosphorus and potassium, and medetomidine (C).

＜２＞ さらに水溶性付与剤（Ｄ）を含有する、＜１＞に記載の藻類増殖塗料組成物。 <2> The algae growth coating composition according to <1>, which further contains a water-soluble imparting agent (D).

＜３＞ 前記樹脂（Ａ）の固形分１００質量部に対して、前記水溶性ガラス（Ｂ）を４０〜３００質量部含有する、＜１＞または＜２＞に記載の藻類増殖塗料組成物。
＜４＞ 前記樹脂（Ａ）の固形分１００質量部に対して、前記メデトミジン（Ｃ）を０．１〜５質量部含有する、＜１＞〜＜３＞のいずれかに記載の藻類増殖塗料組成物。 <3> The algae growth coating composition according to <1> or <2>, which contains 40 to 300 parts by mass of the water-soluble glass (B) with respect to 100 parts by mass of the solid content of the resin (A).
<4> The algae growth coating material according to any one of <1> to <3>, which contains 0.1 to 5 parts by mass of the medetomidine (C) with respect to 100 parts by mass of the solid content of the resin (A). Composition.

＜５＞ ＜１＞〜＜４＞のいずれかに記載の藻類増殖塗料組成物から形成された藻類増殖塗膜。
＜６＞ 水中において少なくとも鉄イオンを放出する、＜５＞に記載の藻類増殖塗膜。 <5> An algae growth coating film formed from the algae growth coating composition according to any one of <1> to <4>.
<6> The algae growth coating film according to <5>, which releases at least iron ions in water.

＜７＞ 基材と＜５＞または＜６＞に記載の藻類増殖塗膜とを含む、藻類増殖塗膜付き基材。 <7> A base material with an algae growth coating film, which comprises a base material and the algae growth coating film according to <5> or <6>.

＜８＞ 下記工程［１］および［２］を含む、藻類増殖塗膜付き基材の製造方法。
［１］基材に、＜１＞〜＜４＞のいずれかに記載の藻類増殖塗料組成物を塗装する工程
［２］塗装された藻類増殖塗料組成物を乾燥させて藻類増殖塗膜を形成する工程 <8> A method for producing a base material with an algae growth coating film, which comprises the following steps [1] and [2].
[1] Step of coating the base material with the algae growth coating composition according to any one of <1> to <4> [2] The coated algae growth coating composition is dried to form an algae growth coating film. Process to do

本発明に係る藻類増殖塗料組成物によれば、夏季などの海生付着動物の繁殖が活発となる時期においても、藻類を十分に繁殖させることが可能な漁礁体（藻場）や洋上設備等を形成することができ、漁獲量等の早期増収に寄与することができ、大気中の二酸化炭素を藻類が取り込むことによる地球温暖化の抑制にも寄与することができる。
特に、海生付着動物の繁殖を抑制しながらも、一方で、藻類の繁殖を促進させることができ、その効果を長期間にわたり持続させることができ、さらには、漁礁効果を有する洋上風力発電などの洋上設備を提供することができる。 According to the algae breeding coating composition according to the present invention, a fish reef body (seaweed bed), offshore equipment, etc. capable of sufficiently breeding algae even in a period such as summer when the breeding of marine attached animals is active. It is possible to contribute to the early increase in yield such as catch, and it is also possible to contribute to the suppression of global warming due to the uptake of carbon dioxide in the atmosphere by algae.
In particular, while suppressing the breeding of marine attached animals, on the other hand, it is possible to promote the breeding of algae, the effect can be sustained for a long period of time, and further, offshore wind power generation having a fishing reef effect, etc. Can provide offshore facilities.

≪藻類増殖塗料組成物≫
本発明に係る藻類増殖塗料組成物（以下「本組成物」ともいう。）は、樹脂（Ａ）（以下「成分（Ａ）」ともいう。他の成分についても同様。）、鉄、リンおよびカリウムからなる群より選ばれる少なくとも１種の元素を含む水溶性ガラス（Ｂ）、および、メデトミジン（Ｃ）を含有する。
前記藻類は特に制限されないが、アオノリ、アサクサノリ、コンブ、ワカメ、ヒジキ、モズク、アオサ、テングサ等の海藻が好ましい。 ≪Algae growth paint composition≫
The algae growth coating composition (hereinafter, also referred to as “the present composition”) according to the present invention includes resin (A) (hereinafter, also referred to as “component (A)”; the same applies to other components), iron, phosphorus and. It contains a water-soluble glass (B) containing at least one element selected from the group consisting of potassium, and medetomidin (C).
The algae are not particularly limited, but seaweeds such as green laver, pyropia tenera, kelp, wakame seaweed, hijiki, mozuku, sea lettuce, and seaweed are preferable.

＜樹脂（Ａ）＞
成分（Ａ）としては特に制限されず、没水環境下で使用される塗膜の樹脂として公知の樹脂を用いることができる。
本組成物に用いる成分（Ａ）は、１種でも２種以上でもよい。 <Resin (A)>
The component (A) is not particularly limited, and a known resin can be used as the resin for the coating film used in a submerged environment.
The component (A) used in this composition may be one kind or two or more kinds.

成分（Ａ）としては、例えば、常温または焼き付け乾燥により塗膜を形成可能な樹脂、具体的には、溶剤蒸発乾燥系樹脂、酸化重合系樹脂、反応硬化系樹脂等が挙げられ、より具体的には、例えば、アミノ樹脂（例：メラミン樹脂）、エポキシ系樹脂（エポキシエステル系樹脂を含む）、ポリウレタン系樹脂、ポリエステル系樹脂、フェノール系樹脂、アルキド系樹脂、ポリオレフィン系樹脂、塩化ビニル系樹脂（例：塩化ビニル・酢酸ビニル・ビニルアルコール共重合体）、塩化ゴム系樹脂、塩素化ポリオレフィン系樹脂、（メタ）アクリル系樹脂、エチレン・酢酸ビニル系樹脂、スチレン・ブタジエン系樹脂、塩化ビニル・ビニルイソブチルエーテル系樹脂、石油系炭化水素樹脂、シリコーン系樹脂、フッ素系樹脂が挙げられる。
これらの中でも、塩化ビニル系樹脂、エポキシ系樹脂、アクリル系樹脂、塩化ゴム系樹脂、塩素化ポリプロピレン系樹脂、塩素化ポリエチレン系樹脂、エチレン・酢酸ビニル系樹脂、スチレン・ブタジエン系樹脂等が好ましい。 Examples of the component (A) include a resin capable of forming a coating film at room temperature or by baking and drying, specifically, a solvent evaporative drying resin, an oxidation polymerization resin, a reaction curing resin and the like, and more specific examples thereof. Examples include amino resins (eg, melamine resins), epoxy resins (including epoxy ester resins), polyurethane resins, polyester resins, phenol resins, alkyd resins, polyolefin resins, vinyl chloride resins. (Example: vinyl chloride / vinyl acetate / vinyl alcohol copolymer), rubber chloride resin, chlorinated polyolefin resin, (meth) acrylic resin, ethylene / vinyl acetate resin, styrene / butadiene resin, vinyl chloride Examples thereof include vinyl isobutyl ether-based resins, petroleum-based hydrocarbon resins, silicone-based resins, and fluorine-based resins.
Among these, vinyl chloride-based resin, epoxy-based resin, acrylic-based resin, rubber chloride-based resin, chlorinated polypropylene-based resin, chlorinated polyethylene-based resin, ethylene / vinyl acetate-based resin, styrene / butadiene-based resin and the like are preferable.

成分（Ａ）の形状としては特に制限されず、例えば、液状の樹脂を用いてもよく、固形状の樹脂を用いてもよいが、固形状の樹脂を用いる場合、溶媒に溶解させてワニス状にして使用することが好ましい。 The shape of the component (A) is not particularly limited, and for example, a liquid resin may be used or a solid resin may be used, but when a solid resin is used, it is dissolved in a solvent to form a varnish. It is preferable to use it.

成分（Ａ）のＧＰＣ（ゲルパーミエーションクロマトグラフ）で測定した重量平均分子量は、本組成物の塗装硬化条件などにもより、一概に決定されないが、好ましくは１５，０００〜２００，０００である。 The weight average molecular weight of the component (A) measured by GPC (gel permeation chromatography) is not unconditionally determined depending on the coating curing conditions of the present composition, but is preferably 15,000 to 200,000. ..

成分（Ａ）の含有量は、本組成物の固形分（不揮発分）１００質量％に対し、好ましくは１５〜５０質量％、より好ましくは２０〜４０質量％である。
成分（Ａ）の含有量がこの範囲にあると、成分（Ｂ）や（Ｃ）を十分に保持することができ、さらに、成分（Ｂ）や（Ｃ）の有する効果を十分に発揮させることができる藻類増殖塗膜を容易に得ることができる。 The content of the component (A) is preferably 15 to 50% by mass, more preferably 20 to 40% by mass, based on 100% by mass of the solid content (nonvolatile content) of the present composition.
When the content of the component (A) is in this range, the components (B) and (C) can be sufficiently retained, and the effects of the components (B) and (C) can be sufficiently exerted. It is possible to easily obtain a coating film for growing algae.

なお、本組成物の固形分（不揮発分）とは、該組成物を乾燥（硬化）して得られる藻類増殖塗膜と同義であり、本組成物中の溶剤（各成分に含まれる溶媒を含む）以外の成分である。 The solid content (nonvolatile content) of the present composition is synonymous with the algae growth coating film obtained by drying (curing) the composition, and the solvent (solvent contained in each component) in the present composition is used. Ingredients other than).

＜水溶性ガラス（Ｂ）＞
成分（Ｂ）は、鉄、リンおよびカリウムからなる群より選ばれる少なくとも１種の元素を含む水溶性ガラスであり、藻類の繁殖をより促進させることができる等の点から、水中において少なくとも鉄イオンを放出することが可能な、鉄元素を含む水溶性ガラスであることが好ましい。
このような成分（Ｂ）を用いると、周囲の海水中に微量のイオンを徐々に溶出させることができ、その溶出により藻類の繁殖に有効な漁礁体（藻場）を長期にわたって提供することができる。
本組成物に用いる成分（Ｂ）は、１種でも２種以上でもよい。 <Water-soluble glass (B)>
The component (B) is a water-soluble glass containing at least one element selected from the group consisting of iron, phosphorus and potassium, and at least iron ions in water can be used to further promote the growth of algae. It is preferable that the glass is a water-soluble glass containing an iron element capable of releasing.
By using such a component (B), a small amount of ions can be gradually eluted into the surrounding seawater, and the elution can provide a fishing reef body (seaweed bed) effective for algae breeding for a long period of time. it can.
The component (B) used in this composition may be one kind or two or more kinds.

なお、水溶性ガラスとは、特開平６−３３５３３０号公報の実施例に記載の方法において、２５℃の水１００ｍＬへのケイ素元素の溶出量が、ＳｉＯ₂換算で、１００μｇ／１０ｇ以上であるガラスのことをいう。 The water-soluble glass is a glass in which the amount of silicon element eluted into 100 mL of water at 25 ° C. is 100 μg / 10 g or more in terms of SiO _{2 in} the method described in Examples of JP-A-6-335330. It means that.

成分（Ｂ）は、藻類の繁殖をより促進させることができる等の点から、鉄元素を含むことが好ましく、この場合、成分（Ｂ）中の鉄元素の含有量は、Ｆｅ₂Ｏ₃換算で、好ましくは１〜５０質量％、より好ましくは２〜３５質量％である。
また、成分（Ｂ）は、二価の鉄を含有していることも同様の理由から好ましく、成分（Ｂ）中の該二価の鉄の含有量は、好ましくは１質量％以上、より好ましくは３質量％以上、さらに好ましくは５質量％以上、特に好ましくは８質量％以上、好ましくは３０質量％以下である。
成分（Ｂ）中の鉄元素の含有量は、蛍光Ｘ線（（株）リガク製、Ｓｕｐｅｒｍｉｎｉ２００ 卓上波長分散型蛍光Ｘ線装置）で測定することができる。下記リン元素等の他の元素の含有量も同様の方法で測定することができる。
また、成分（Ｂ）中の二価の鉄の含有量は、メスバウアースペクトル法で測定することができる。 The component (B) preferably contains an iron element from the viewpoint of being able to further promote the growth of algae, and in this case, the content of the iron element in the component (B) is converted to Fe ₂ O _3. It is preferably 1 to 50% by mass, more preferably 2 to 35% by mass.
Further, it is preferable that the component (B) contains divalent iron for the same reason, and the content of the divalent iron in the component (B) is preferably 1% by mass or more, more preferably. Is 3% by mass or more, more preferably 5% by mass or more, particularly preferably 8% by mass or more, and preferably 30% by mass or less.
The content of the iron element in the component (B) can be measured by a fluorescent X-ray (manufactured by Rigaku Co., Ltd., Supermini 200 desktop wavelength dispersive fluorescent X-ray apparatus). The content of other elements such as the following phosphorus element can also be measured by the same method.
Further, the content of divalent iron in the component (B) can be measured by the Mössbauer spectral method.

成分（Ｂ）は、藻類の成長をより促進させることができる等の点から、リン元素を含むことが好ましく、この場合、成分（Ｂ）中のリン元素の含有量は、Ｐ₂Ｏ₅換算で、好ましくは１〜３０質量％、より好ましくは２〜２５質量％である。 The component (B) preferably contains a phosphorus element from the viewpoint of being able to further promote the growth of algae, and in this case, the content of the phosphorus element in the component (B) is converted to P ₂ O _5. It is preferably 1 to 30% by mass, and more preferably 2 to 25% by mass.

成分（Ｂ）は、藻類の成長をより促進させることができる等の点から、カリウム元素を含むことが好ましく、この場合、成分（Ｂ）中のカリウム元素の含有量は、Ｋ₂Ｏ換算で、好ましくは１〜５０質量％、より好ましくは５〜４０質量％である。 The component (B) preferably contains a potassium element from the viewpoint of being able to further promote the growth of algae, and in this case, the content of the potassium element in the component (B) is converted into K ₂ O. , Preferably 1 to 50% by mass, more preferably 5 to 40% by mass.

成分（Ｂ）中のケイ素元素の含有量は、ＳｉＯ₂換算で、好ましくは１５〜８０質量％、より好ましくは２５〜６５質量％である。 The content of the silicon element in the component (B) is preferably 15 to 80% by mass, more preferably 25 to 65% by mass in terms of SiO ₂ .

成分（Ｂ）は、ナトリウム元素を含んでいてもよく、この場合、成分（Ｂ）中のナトリウム元素の含有量は、Ｎａ₂Ｏ換算で、好ましくは１〜３０質量％、より好ましくは２〜２０質量％である。 The component (B) may contain a sodium element. In this case, the content of the sodium element in the component (B) is preferably 1 to 30% by mass, more preferably 2 to 30% by mass in terms of Na ₂ O. It is 20% by mass.

成分（Ｂ）は、ホウ素元素を含んでいてもよく、この場合、成分（Ｂ）中のホウ素元素の含有量は、Ｂ₂Ｏ₅換算で、好ましくは０．１〜６０質量％である。 The component (B) may contain a boron element, and in this case, the content of the boron element in the component (B) is preferably 0.1 to 60% by mass in terms of B ₂ O ₅ .

成分（Ｂ）は、マンガン元素を含んでいてもよく、この場合、成分（Ｂ）中のマンガン元素の含有量は、ＭｎＯ換算で、好ましくは０．１〜５質量％である。 The component (B) may contain a manganese element, and in this case, the content of the manganese element in the component (B) is preferably 0.1 to 5% by mass in terms of MnO.

成分（Ｂ）は、具体的には、例えば、非晶質網目構造を形成するケイ素と酸素を中心とする網目形成原子、その網目構造の中に入り込むナトリウム、カリウムなどの網目修飾原子、そして網目形成原子または網目修飾原子として機能する鉄原子を含む。このような水溶性ガラスを水に浸漬すると、水分子が前記網目構造の網目を徐々に切断するため、水溶性ガラスを構成する成分が長期間にわたって徐々に溶出する。
構成元素の種類と量を、その製造時に調整することで、目的の成分を目的の量で溶出させることもできる。
また、水との接触面積を増大させ、構成元素の溶出を促進する等の点から、成分（Ｂ）を多孔質体としてもよい。 Specifically, the component (B) is, for example, a network-forming atom centered on silicon and oxygen forming an amorphous network structure, a network-modifying atom such as sodium or potassium that enters the network structure, and a network. Includes iron atoms that function as forming or network modifying atoms. When such a water-soluble glass is immersed in water, water molecules gradually cut the network of the network structure, so that the components constituting the water-soluble glass are gradually eluted over a long period of time.
By adjusting the type and amount of the constituent elements at the time of production, the desired component can be eluted in the desired amount.
Further, the component (B) may be a porous body from the viewpoint of increasing the contact area with water and promoting the elution of the constituent elements.

成分（Ｂ）は、ケイ素、鉄、リンおよび／またはカリウムなどの元素成分を含む公知の材料を用い、高温に加熱（例：１，３００〜１，５００℃で約１０分間以上加熱）して、溶融させ、次いで冷却させる公知のガラス化法により製造することができる。なお、このガラス化法を行う際に、溶融雰囲気を、コークスなどの還元剤を使用するか、または、一酸化炭素ガスなどの還元性ガスを用いて還元性にすることで、得られる成分（Ｂ）中の二価の鉄の含有量を増加させることができる。
また、成分（Ｂ）は、使用済みの廃ガラス等を破砕し、これに必要な追加元素成分を含む原料を添加した後、前記と同様に加熱溶融する方法でも製造することができる。 The component (B) uses a known material containing elemental components such as silicon, iron, phosphorus and / or potassium, and is heated to a high temperature (eg, heated at 1,300 to 1,500 ° C. for about 10 minutes or more). It can be produced by a known vitrification method of melting and then cooling. When performing this vitrification method, a component obtained by making the molten atmosphere reducible by using a reducing agent such as coke or by using a reducing gas such as carbon monoxide gas ( B) The content of divalent iron in can be increased.
Further, the component (B) can also be produced by a method of crushing used waste glass or the like, adding a raw material containing an additional element component necessary for the crushed glass, and then heating and melting in the same manner as described above.

成分（Ｂ）の平均粒径は特に制限されないが、藻類の繁殖性により優れ、含まれる成分の徐放性に優れ、長期間にわたり藻類の繁殖を促進させることができる等の点から、好ましくは１０〜２，０００μｍ、より好ましくは２０〜６００μｍである。
該平均粒径は、光学顕微鏡観察による粒子１００個の粒径を平均した値である。 The average particle size of the component (B) is not particularly limited, but it is preferable because it is excellent in the reproductive property of algae, is excellent in the sustained release property of the contained component, and can promote the reproductive activity of the algae for a long period of time. It is 10 to 2,000 μm, more preferably 20 to 600 μm.
The average particle size is a value obtained by averaging the particle sizes of 100 particles as observed by an optical microscope.

成分（Ｂ）の含有量は、前記成分（Ａ）の固形分１００質量部に対し、好ましくは４０〜３００質量部、より好ましくは５０〜２５０質量部、特に好ましくは１００〜２４０質量部である。
成分（Ｂ）の含有量がこの範囲にあると、藻類の繁殖および成長をより促進させることができる。 The content of the component (B) is preferably 40 to 300 parts by mass, more preferably 50 to 250 parts by mass, and particularly preferably 100 to 240 parts by mass with respect to 100 parts by mass of the solid content of the component (A). ..
When the content of the component (B) is in this range, the growth and growth of algae can be further promoted.

＜メデトミジン（Ｃ）＞
メデトミジンは、（＋／−）−４−［１−（２，３−ジメチルフェニル）エチル］−１Ｈ−イミダゾールであり、下記式（１）で表される。 <Medetomidine (C)>
Medetomidine is (+/-)-4- [1- (2,3-dimethylphenyl) ethyl] -1H-imidazole and is represented by the following formula (1).

メデトミジンは、光学異性を有するが、本組成物に含まれるメデトミジンは、その一方のみであっても、任意の比率の混合物であってもよく、また、イミダゾリウム塩や金属等への付加物を形成していてもよい。
成分（Ｃ）を含有することで、夏季などの海生付着動物の繁殖が活発となる時期においても、海生付着動物、特にフジツボ類や腔腸動物（ヒドラ等）類の繁殖を抑制しながらも、一方で、藻類の繁殖を促進させることができる。 Medetomidine has optical isomerism, but the medetomidine contained in the present composition may be only one of them or a mixture of any ratio, and may be an adduct to an imidazolium salt, a metal, or the like. It may be formed.
By containing the component (C), even during the period when the breeding of marine attached animals becomes active, such as in summer, while suppressing the breeding of marine attached animals, especially barnacles and cavity animals (hydra, etc.) On the other hand, it can promote the growth of algae.

成分（Ｃ）の含有量は、前記成分（Ａ）の固形分１００質量部に対し、好ましくは０．１〜５質量部、より好ましくは０．２〜３質量部、特に好ましくは０．５〜２質量部である。
成分（Ｃ）の含有量がこの範囲にあると、夏季などの海生付着動物の繁殖が活発となる時期においても、海生付着動物、特にフジツボ類や腔腸動物（ヒドラ等）類の繁殖の抑制と、藻類の繁殖の促進によりバランスよく優れる藻類増殖塗膜を容易に得ることができる。 The content of the component (C) is preferably 0.1 to 5 parts by mass, more preferably 0.2 to 3 parts by mass, and particularly preferably 0.5, with respect to 100 parts by mass of the solid content of the component (A). ~ 2 parts by mass.
When the content of the component (C) is within this range, the breeding of marine sessile animals, especially fujitsubo and luminal animals (hydra, etc.), even during the period when the breeding of marine sessile animals is active, such as in summer. A well-balanced and excellent algae growth coating film can be easily obtained by suppressing the above-mentioned conditions and promoting the growth of algae.

＜水溶性付与剤（Ｄ）＞
本組成物が成分（Ｄ）を含有することで、藻類増殖塗膜の水中での表面からの更新性を向上させ、成分（Ｂ）に含まれる鉄、リンおよび／またはカリウムの放出や成分（Ｃ）の水中への放出を促進させることができる。
成分（Ｄ）を用いる場合、用いる成分（Ｄ）は、１種でも２種以上でもよい。 <Water-soluble imparting agent (D)>
When this composition contains the component (D), the renewability of the algae growth coating film from the surface in water is improved, and the release of iron, phosphorus and / or potassium contained in the component (B) and the component ( The release of C) into water can be promoted.
When the component (D) is used, the component (D) to be used may be one kind or two or more kinds.

成分（Ｄ）としては、得られる藻類増殖塗膜に水溶性を付与できる成分であれば特に制限されないが、モノカルボン酸化合物が好ましい。
前記モノカルボン酸化合物としては、例えば、ガムロジン、ウッドロジン、トール油ロジン等のロジン、水添ロジン、不均化ロジン等のロジン誘導体、トリメチルイソブテニルシクロヘキセンカルボン酸、ナフテン酸、バーサチック酸、ステアリン酸、サリチル酸等の脂肪族、脂環式または芳香族のモノカルボン酸が挙げられる。 The component (D) is not particularly limited as long as it can impart water solubility to the obtained algae growth coating film, but a monocarboxylic acid compound is preferable.
Examples of the monocarboxylic acid compound include rosins such as gum rosin, wood rosin and tall oil rosin, rosin derivatives such as hydrogenated rosin and disproportionate rosin, trimethylisobutenyl cyclohexene carboxylic acid, naphthenic acid, versatic acid and stearic acid. , Salicylic acid and other aliphatic, alicyclic or aromatic monocarboxylic acids.

本組成物が成分（Ｄ）を含有する場合、該成分（Ｄ）の含有量は、前記成分（Ａ）の固形分１００質量部に対し、好ましくは２〜３０質量部、より好ましくは５〜２０質量部である。
成分（Ｄ）の含有量がこの範囲にあると、成分（Ｂ）に含まれる鉄、リンおよび／またはカリウムの放出や成分（Ｃ）の水中への放出量を適切に調整することができ、長期間にわたり藻類の繁殖を促進させることができる。 When the present composition contains the component (D), the content of the component (D) is preferably 2 to 30 parts by mass, more preferably 5 to 5 parts by mass with respect to 100 parts by mass of the solid content of the component (A). It is 20 parts by mass.
When the content of the component (D) is in this range, the release of iron, phosphorus and / or potassium contained in the component (B) and the release amount of the component (C) into water can be appropriately adjusted. It can promote the growth of algae over a long period of time.

＜その他の成分＞
本組成物は、前述した成分の他に、所望により、本発明の効果を損なわない範囲で、タレ止め・沈降防止剤（搖変剤）、可塑剤、顔料、溶剤、海生付着動物に対する防汚（忌避）剤、消泡剤、レベリング剤等の、従来の塗料組成物に用いられている各種成分を含有していてもよい。
これらの成分はそれぞれ、１種単独で用いてもよく、２種以上を用いてもよい。 <Other ingredients>
In addition to the above-mentioned components, the present composition can be used to prevent sagging / sedimentation (defoaming agents), plasticizers, pigments, solvents, and marine-attached animals, if desired, as long as the effects of the present invention are not impaired. It may contain various components used in conventional coating compositions, such as a stain (repellent) agent, an antifoaming agent, and a leveling agent.
Each of these components may be used alone or in combination of two or more.

〈タレ止め・沈降防止剤（搖変剤）〉
本組成物は、塗装時の厚塗り性、タレ止め性の向上や、成分（Ｂ）、（Ｃ）および必要により用いられる溶剤不溶分（顔料等）の沈降防止のため、各種タレ止め・沈降防止剤（搖変剤）を含有していてもよい。 <Sauce prevention / sedimentation inhibitor (stiffening agent)>
This composition has various anti-sagging and sedimentation properties in order to improve the thick coating property and anti-sagging property at the time of coating and to prevent the sedimentation of components (B) and (C) and solvent-insoluble components (pigments, etc.) used as necessary. It may contain an inhibitor (stiffening agent).

タレ止め・沈降防止剤としては、例えば、Ａｌ、Ｃａ、Ｚｎのステアレート塩、レシチン塩、アルキルスルホン酸塩などの有機粘土系塩類、酸化ポリエチレン系ワックス、アマイドワックス、水添ヒマシ油系ワックス、ポリアマイド系ワックス、合成微粉シリカが挙げられ、好ましくは、ポリアマイドワックス、合成微粉シリカ、酸化ポリエチレン系ワックス、有機粘土系塩類が挙げられる。 Examples of the anti-sag / sedimentation preventive agent include organic clay salts such as stearate salts of Al, Ca and Zn, lecithin salts and alkyl sulfonates, polyethylene oxide waxes, amido waxes and hydrogenated castor oil waxes. Examples thereof include polyamide wax and synthetic fine powder silica, and preferable examples thereof include polyamide wax, synthetic fine powder silica, polyethylene oxide wax and organic clay salts.

本組成物がタレ止め・沈降防止剤を含有する場合、その含有量は、本組成物の固形分１００質量％に対し、好ましくは０．１〜２質量％である。 When the present composition contains a sagging preventive / sedimentation inhibitor, the content thereof is preferably 0.1 to 2% by mass with respect to 100% by mass of the solid content of the present composition.

〈可塑剤〉
可塑剤としては成分（Ａ）以外の成分であれば特に限定されないが、例えば、塩素化パラフィン、フタル酸エステル、アジピン酸エステル、トリメリット酸エステル、リン酸エステル、クエン酸エステル、セバシン酸エステル、アゼライン酸エステル、マレイン酸エステル、安息香酸エステルが挙げられる。 <Plasticizer>
The plasticizer is not particularly limited as long as it is a component other than the component (A), and for example, chlorinated paraffin, phthalate ester, adipic acid ester, trimellitic acid ester, phosphoric acid ester, citric acid ester, sebacic acid ester, etc. Azelaic acid ester, maleic acid ester, benzoic acid ester can be mentioned.

本組成物が可塑剤を含有する場合、その含有量は、本組成物の固形分１００質量％に対し、好ましくは３〜１５質量％である。 When the present composition contains a plasticizer, the content thereof is preferably 3 to 15% by mass with respect to 100% by mass of the solid content of the present composition.

〈顔料〉
顔料としては、前記成分（Ｂ）と成分（Ｃ）以外の成分であれば特に制限されず、従来公知の有機系、無機系の各種着色または体質顔料を用いることができる。
有機系顔料としては、例えば、ナフトールレッド、フタロシアニンブルー、フタロシアニングリーン、紺青が挙げられる。
無機系顔料としては、例えば、カーボンブラック、チタン白、ベンガラ、バライト粉、シリカ、炭酸カルシウム、タルク、硫酸バリウム、亜鉛華（ＺｎＯ、酸化亜鉛）、鉛白、鉛丹、亜鉛末が挙げられる。 <Pigment>
The pigment is not particularly limited as long as it is a component other than the component (B) and the component (C), and various conventionally known organic and inorganic coloring or extender pigments can be used.
Examples of the organic pigment include naphthol red, phthalocyanine blue, phthalocyanine green, and prussian blue.
Examples of the inorganic pigment include carbon black, titanium white, red iron oxide, barite powder, silica, calcium carbonate, talc, barium sulfate, zinc oxide (ZnO, zinc oxide), lead white, lead tan, and zinc powder.

本組成物が顔料を含有する場合、その含有量は、本組成物の固形分１００質量％に対し、好ましくは５〜６０質量％、より好ましくは１０〜３０質量％である。 When the present composition contains a pigment, the content thereof is preferably 5 to 60% by mass, more preferably 10 to 30% by mass, based on 100% by mass of the solid content of the present composition.

海生付着動物の繁殖を抑制しながらも、一方で、藻類の繁殖をより促進させることができ、その効果を長期間にわたり容易に持続させることができる等の点から、本組成物中の顔料体積濃度（ＰＶＣ）は、好ましくは２８〜５５％、より好ましくは３８〜５２％である。 Pigments in the present composition from the viewpoints that while suppressing the reproduction of marine-attached animals, on the other hand, the reproduction of algae can be further promoted and the effect can be easily maintained for a long period of time. The volume concentration (PVC) is preferably 28-55%, more preferably 38-52%.

前記ＰＶＣは、前記成分（Ｂ）と成分（Ｃ）を含むすべての顔料の合計の体積濃度のことをいい、具体的には下記式より求めることができる。
ＰＶＣ［％］＝本組成物中の全ての顔料の体積の合計×１００／本組成物中の固形分の体積 The PVC refers to the total volume concentration of all the pigments including the component (B) and the component (C), and can be specifically calculated by the following formula.
PVC [%] = total volume of all pigments in the composition x 100 / volume of solids in the composition

前記本組成物中の固形分の体積は、本組成物の固形分の質量および真密度から算出することができる。前記固形分の質量および真密度は、測定値でも、用いる原料から算出した値でも構わない。 The volume of the solid content in the present composition can be calculated from the mass and the true density of the solid content of the present composition. The mass and true density of the solid content may be measured values or values calculated from the raw materials used.

前記顔料の体積は、用いた顔料の質量および真密度から算出することができる。前記顔料の質量および真密度は、測定値でも、用いる原料から算出した値でも構わない。測定値としては、例えば、本組成物の固形分より顔料と他の成分とを分離し、分離された顔料の質量および真密度を測定することで算出することができる。 The volume of the pigment can be calculated from the mass and true density of the pigment used. The mass and true density of the pigment may be measured values or values calculated from the raw materials used. The measured value can be calculated, for example, by separating the pigment and other components from the solid content of the present composition and measuring the mass and true density of the separated pigment.

〈溶剤〉
藻類の繁殖をより長期間にわたり持続させることができる等の点から、本組成物に配合する各種成分は、溶剤に溶解または分散していることが好ましい。
該溶剤としては、本組成物に配合する各成分の種類に応じて適宜選択すればよいが、例えば、脂肪族系、芳香族系、ケトン系、エステル系、エーテル系など、通常の塗料組成物に配合されるような各種溶剤が挙げられる。
前記芳香族系溶剤としては、例えば、キシレン、トルエンが挙げられ、ケトン系溶剤としては、例えば、メチルイソブチルケトン（ＭＩＢＫ）が挙げられ、エステル系溶剤としては、例えば、酢酸ブチルが挙げられ、エーテル系溶剤としては、例えば、プロピレングリコールモノメチルエーテル（ＰＧＭ）、プロピレングリコールモノメチルエーテルアセテート（ＰＭＡＣ）が挙げられる。 <solvent>
It is preferable that the various components to be blended in the present composition are dissolved or dispersed in a solvent from the viewpoint that the growth of algae can be sustained for a longer period of time.
The solvent may be appropriately selected according to the type of each component to be blended in the present composition, and for example, an ordinary coating composition such as an aliphatic type, an aromatic type, a ketone type, an ester type, or an ether type. Examples include various solvents such as those blended in.
Examples of the aromatic solvent include xylene and toluene, examples of the ketone solvent include methyl isobutyl ketone (MIBK), and examples of the ester solvent include butyl acetate and ether. Examples of the solvent include propylene glycol monomethyl ether (PGM) and propylene glycol monomethyl ether acetate (PMAC).

本組成物に用いる溶剤の使用量は特に制限されず、前記各種成分を溶解または分散できる量であることが好ましい。 The amount of the solvent used in the composition is not particularly limited, and is preferably an amount capable of dissolving or dispersing the various components.

＜藻類増殖塗料組成物の製造＞
本組成物は、前記各種成分を混合すればよく、この混合の際には、公知の混合機、攪拌機等を用いることができる。
前記各種成分は、所定の量となるように、一度にまたは分割して混合すればよく、この際には、任意の順序で加えればよいが、成分（Ａ）を溶剤に溶解したワニス、または、ワニス状の市販の成分（Ａ）に、成分（Ｂ）、（Ｃ）および必要により顔料を加えて攪拌することが好ましい。 <Manufacturing of algae growth paint composition>
In this composition, the various components may be mixed, and a known mixer, stirrer or the like can be used for this mixing.
The various components may be mixed at once or in divided portions so as to have a predetermined amount, and in this case, they may be added in any order, but a varnish in which the component (A) is dissolved in a solvent, or , It is preferable to add the components (B) and (C) and, if necessary, a pigment to the commercially available varnish-like component (A) and stir.

≪藻類増殖塗膜、藻類増殖塗膜付き基材≫
本発明に係る藻類増殖塗膜（以下「本塗膜」ともいう。）は、本組成物から形成され、本発明に係る藻類増殖塗膜付き基材は、基材と本塗膜とを含む。 ≪Algae growth coating film, base material with algae growth coating film≫
The algae growth coating film according to the present invention (hereinafter, also referred to as “the main coating film”) is formed from the present composition, and the base material with the algae growth coating film according to the present invention includes the base material and the present coating film. ..

本塗膜は、藻類の繁殖をより促進させることができる等の点から、水中において少なくとも鉄イオン（鉄含有イオン）を放出する、好ましくは、鉄イオン（鉄含有イオン）と、リンイオン（リン含有イオン）および／またはカリウムイオン（カリウム含有イオン）とを放出する塗膜であることが望ましい。 This coating film releases at least iron ions (iron-containing ions) in water from the viewpoint of further promoting the growth of algae, preferably iron ions (iron-containing ions) and phosphorus ions (phosphorus-containing ions). It is desirable that the coating film releases ions) and / or potassium ions (potassium-containing ions).

本塗膜の厚みは特に制限されないが、藻類の繁殖を長期間にわたり持続させることができる等の点から、好ましくは３０μｍ〜３ｍｍ、より好ましくは５０μｍ〜１ｍｍである。 The thickness of the present coating film is not particularly limited, but is preferably 30 μm to 3 mm, more preferably 50 μm to 1 mm from the viewpoint of being able to sustain the growth of algae for a long period of time.

本塗膜は、本組成物を乾燥（硬化）することで製造でき、本塗膜は、基材上に形成すること、つまり本塗膜付き基材を製造することが好ましい。
本塗膜付き基材は、下記工程［１］および［２］を含むことが好ましい。
［１］基材に、本組成物を塗装する工程
［２］塗装された本組成物を乾燥させて本塗膜を形成する工程 The present coating film can be produced by drying (curing) the present composition, and it is preferable that the present coating film is formed on a substrate, that is, a substrate with the present coating film is produced.
The base material with a coating film preferably includes the following steps [1] and [2].
[1] Step of coating the present composition on a base material [2] Step of drying the applied present composition to form the present coating film

前記基材としては、例えば、人工漁礁体や人工藻場として利用されてきた基材、具体的には、テトラポッド、消波ブロック等のブロック；兵器、車両、船舶等の海没処分される人工物；木材；石材；貝殻等の水酸廃棄物；網；ロープが挙げられる。
また、前記基材として、橋梁、港湾設備、海上ブイ、海中パイプライン、ＦＰＳＯ（浮体式海洋石油・ガス生産貯蔵積出設備）、ＦＬＮＧ（浮体式洋上天然ガス液化設備）、石油掘削リグ、石油備蓄基地、メガフロート、洋上風力発電設備、潮力発電設備等における水中構造物も挙げられる。
本組成物は、これらの基材の中でも、大型構造物に本塗膜を形成するのに適している。 As the base material, for example, a base material used as an artificial reef body or an artificial seashell field, specifically, a block such as a tetrapod or a wave-dissipating block; a weapon, a vehicle, a ship or the like is submerged in the sea. Artificial reefs; wood; stones; hydroxides such as shells; nets; ropes.
In addition, as the base material, bridges, port equipment, offshore buoys, underwater pipelines, FPSO (floating offshore oil and gas production storage and shipping equipment), FLNG (floating offshore natural gas liquefaction equipment), oil drilling rigs, oil Underwater structures in storage bases, mega floats, offshore wind power generation equipment, tidal power generation equipment, etc. can also be mentioned.
Among these base materials, the present composition is suitable for forming the present coating film on a large structure.

前記基材の材質としては特に制限されず、コンクリート、木、石、金属（例：鉄鋼（鉄、鋼、合金鉄、炭素鋼、合金鋼など）、非鉄金属（亜鉛、アルミニウムなど）、ステンレス）、樹脂等が挙げられる。 The material of the base material is not particularly limited, and is concrete, wood, stone, metal (eg, steel (iron, steel, alloy iron, carbon steel, alloy steel, etc.), non-ferrous metal (zinc, aluminum, etc.), stainless steel). , Resin and the like.

本組成物を基材に塗装する方法としては特に制限されず、従来公知の方法を制限なく使用できる。例えば、エアレススプレー、エアースプレー、刷毛塗り、ローラー塗り、静電塗装等の塗布方法、基材を本組成物に浸漬する方法が挙げられる。
なお、塗装の際には、必要に応じて、塗装方法に合わせて本組成物の粘度を調整してもよい。 The method for coating the composition on the substrate is not particularly limited, and conventionally known methods can be used without limitation. For example, a coating method such as airless spray, air spray, brush coating, roller coating, electrostatic coating, and a method of immersing the base material in the present composition can be mentioned.
At the time of painting, the viscosity of the present composition may be adjusted according to the painting method, if necessary.

また、前記塗装は、１回の塗装（１回塗り）で、所望の厚みの本塗膜を形成してもよいし、２回（必要によりそれ以上）の塗装で、所望の厚みの本塗膜を形成してもよい。 Further, in the coating, the main coating film having a desired thickness may be formed by one coating (one coating), or the main coating film having a desired thickness may be formed by two coatings (more than necessary). A film may be formed.

本組成物と基材との良好な付着性を確保するため、本組成物を基材に塗装する前に、錆、油脂、水分、塵埃、スライム、塩分などの基材表面付着物を清掃、除去することが好ましい。
特に、基材として金属製基材を採用する場合には、基材に予め防食塗膜などを形成しておくことが好ましく、具体的には、エポキシ樹脂系防食塗膜が好ましい。また、基材としてコンクリート製基材を採用する場合には、耐アルカリ性を有する塗膜などを形成しておくことが好ましく、具体的には、エポキシ樹脂系塗膜が好ましい。
本組成物は、その効果がより発揮される等の点から、通常、上塗り塗料として、基材の最表面（基材とは反対側の表面）に塗装することが好ましい。 In order to ensure good adhesion between the composition and the substrate, clean the surface deposits on the substrate such as rust, oil, moisture, dust, slime, and salt before applying the composition to the substrate. It is preferable to remove it.
In particular, when a metal base material is used as the base material, it is preferable to form an anticorrosion coating film or the like on the base material in advance, and specifically, an epoxy resin-based anticorrosion coating film is preferable. When a concrete base material is used as the base material, it is preferable to form a coating film having alkali resistance, and specifically, an epoxy resin-based coating film is preferable.
The present composition is usually preferably coated on the outermost surface of the base material (the surface opposite to the base material) as a topcoat paint from the viewpoint of exerting its effect more.

塗装された本組成物を乾燥させる方法としては特に制限されず、乾燥（硬化）時間を短縮させるために５〜６０℃程度に加熱して乾燥させることもできるが、通常は、常温、大気下で１〜１４日程度放置することで乾燥させる。 The method for drying the coated composition is not particularly limited, and it can be dried by heating it to about 5 to 60 ° C. in order to shorten the drying (curing) time, but it is usually at room temperature and in the air. Let it dry for 1 to 14 days.

以下、実施例に基づいて本発明をさらに具体的に説明するが、本発明の実施態様はこれらの実施例により何ら限定されるものではない。 Hereinafter, the present invention will be described in more detail based on Examples, but the embodiments of the present invention are not limited to these Examples.

［実施例１〜５および比較例１〜２］
＜藻類増殖塗料組成物の調製＞
溶剤（キシレン、ＭＩＢＫ、ＰＧＭ）に、成分（Ａ）を撹拌しながら加え、成分（Ａ）を溶剤に溶解させた樹脂ワニスを作製した。作製した樹脂ワニスに、残りのその他成分を撹拌しながら加えて均一にした後、成分（Ｂ）および成分（Ｃ）を順に加えて均一になるまで攪拌することで、藻類増殖塗料組成物を調製した。
藻類増殖塗料組成物を調製するのに用いた各成分の種類と量を表１に示す。なお、表１中の各成分の欄の数値は質量部を示す。また、各成分の詳細を表２に示す。 [Examples 1 to 5 and Comparative Examples 1 to 2]
<Preparation of algae growth paint composition>
The component (A) was added to a solvent (xylene, MIBK, PGM) with stirring to prepare a resin varnish in which the component (A) was dissolved in the solvent. The remaining other components are added to the prepared resin varnish with stirring to make it uniform, and then the component (B) and the component (C) are added in order and stirred until uniform to prepare an algae growth coating composition. did.
Table 1 shows the types and amounts of each component used to prepare the algae growth coating composition. The numerical values in the columns of each component in Table 1 indicate parts by mass. The details of each component are shown in Table 2.

＜試験板の作成＞
サンドブラスト鋼板（３００ｍｍ×１００ｍｍ×厚さ２．３ｍｍ）に、エポキシ樹脂系防食塗料であるバンノー５００（中国塗料（株）製）を乾燥膜厚が２００μｍになるように塗装して、一晩乾燥させた。
その後、調製した藻類増殖塗料組成物を乾燥膜厚が２００μｍになるように塗装して、２４時間常温乾燥させることで、試験板を作製した。 <Creation of test board>
A sandblasted steel sheet (300 mm x 100 mm x 2.3 mm thick) is coated with Vanno 500 (manufactured by China Paint Co., Ltd.), which is an epoxy resin anticorrosive paint, so that the dry film thickness is 200 μm, and dried overnight. It was.
Then, the prepared algae growth coating composition was coated so as to have a dry film thickness of 200 μm, and dried at room temperature for 24 hours to prepare a test plate.

＜試験方法＞
前記試験板を、夏季（５月開始）および冬季（１１月開始）の広島県の広島湾に静置浸漬し、５月および１１月に浸漬してから２ヶ月後および４カ月後の藻類付着面積を目視により計測し、下記評価基準に基づき評価を行った。なお、藻類付着面積と藻類付着量とは比例関係にあった。結果を表１に示す。
（評価基準）
◎：藻類付着面積が８０％以上
○：藻類付着面積が５０％以上８０％未満
△：藻類付着面積が３０％以上５０％未満
×：藻類付着面積が３０％未満 <Test method>
The test plate was statically immersed in Hiroshima Bay in Hiroshima Prefecture in the summer (starting in May) and winter (starting in November), and algae adhered 2 months and 4 months after being immersed in May and November. The area was visually measured and evaluated based on the following evaluation criteria. The algae adhesion area and the algae adhesion amount were in a proportional relationship. The results are shown in Table 1.
(Evaluation criteria)
⊚: Algae adhesion area is 80% or more ○: Algae adhesion area is 50% or more and less than 80% Δ: Algae adhesion area is 30% or more and less than 50% ×: Algae adhesion area is less than 30%

Claims (8)

樹脂（Ａ）、鉄、リンおよびカリウムからなる群より選ばれる少なくとも１種の元素を含む水溶性ガラス（Ｂ）、および、メデトミジン（Ｃ）を含有する、藻類増殖塗料組成物。 An algae growth coating composition containing a water-soluble glass (B) containing at least one element selected from the group consisting of resin (A), iron, phosphorus and potassium, and medetomidine (C). さらに水溶性付与剤（Ｄ）を含有する、請求項１に記載の藻類増殖塗料組成物。 The algae growth coating composition according to claim 1, further comprising a water-soluble imparting agent (D). 前記樹脂（Ａ）の固形分１００質量部に対して、前記水溶性ガラス（Ｂ）を４０〜３００質量部含有する、請求項１または２に記載の藻類増殖塗料組成物。 The algae growth coating composition according to claim 1 or 2, which contains 40 to 300 parts by mass of the water-soluble glass (B) with respect to 100 parts by mass of the solid content of the resin (A). 前記樹脂（Ａ）の固形分１００質量部に対して、前記メデトミジン（Ｃ）を０．１〜５質量部含有する、請求項１〜３のいずれか１項に記載の藻類増殖塗料組成物。 The algae growth coating composition according to any one of claims 1 to 3, which contains 0.1 to 5 parts by mass of the medetomidine (C) with respect to 100 parts by mass of the solid content of the resin (A). 請求項１〜４のいずれか１項に記載の藻類増殖塗料組成物から形成された藻類増殖塗膜。 An algae growth coating film formed from the algae growth coating composition according to any one of claims 1 to 4. 水中において少なくとも鉄イオンを放出する、請求項５に記載の藻類増殖塗膜。 The algae growth coating film according to claim 5, which releases at least iron ions in water. 基材と請求項５または６に記載の藻類増殖塗膜とを含む、藻類増殖塗膜付き基材。 A base material with an algae growth coating film, which comprises the base material and the algae growth coating film according to claim 5 or 6. 下記工程［１］および［２］を含む、藻類増殖塗膜付き基材の製造方法。
［１］基材に、請求項１〜４のいずれか１項に記載の藻類増殖塗料組成物を塗装する工程
［２］塗装された藻類増殖塗料組成物を乾燥させて藻類増殖塗膜を形成する工程 A method for producing a base material with an algae growth coating film, which comprises the following steps [1] and [2].
[1] Step of coating the base material with the algae growth coating composition according to any one of claims 1 to 4 [2] The coated algae growth coating composition is dried to form an algae growth coating film. Process to do