JP2020525379A - 自動車用ガラス組成物、物品およびハイブリッド積層板 - Google Patents
自動車用ガラス組成物、物品およびハイブリッド積層板 Download PDFInfo
- Publication number
- JP2020525379A JP2020525379A JP2019569748A JP2019569748A JP2020525379A JP 2020525379 A JP2020525379 A JP 2020525379A JP 2019569748 A JP2019569748 A JP 2019569748A JP 2019569748 A JP2019569748 A JP 2019569748A JP 2020525379 A JP2020525379 A JP 2020525379A
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass
- less
- poise
- glass article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
実施例1〜67は、本開示の1つ以上の実施の形態による例示のガラス組成物である。実施例1〜67のガラス組成(モル%)が、表1に与えられている。表1には、20℃での密度、歪み点温度(ビーム曲げ粘度計により測定される)、徐冷点温度(ビーム曲げ粘度計により測定される)、軟化点温度(ファイバ伸張により測定される)、CTE、応力光学係数、屈折率、T200、T35000、T200000、液相温度、液相粘度、ジルコン分解温度、ジルコン分解粘度、および他の属性も含まれている。
実施例68〜77は、本開示の1つ以上の実施の形態による例示のガラス組成物である。実施例68〜77のガラス組成(モル%)が、歪み点温度(ビーム曲げ粘度計により測定される)、徐冷点温度(ビーム曲げ粘度計により測定される)、軟化点温度(ファイバ伸張により測定される)、垂下温度、対数11の粘度(ポアズ)での温度、T200、T35000、T200000、密度、CTE、液相粘度、ジルコン分解温度、およびジルコン分解粘度と共に、表3に与えられている。
ガラス組成物を有するガラス物品において、該ガラス組成物が、
約63モル%から約75モル%の範囲の量のSiO2、
約7モル%から約13モル%の範囲の量のAl2O3、
約13モル%から約24モル%の範囲の量のR2O、および
約0モル%から約3モル%の範囲の量のP2O5
を含み、
前記ガラス組成物は、MgOとZnOの一方または両方を含み、MgOの量は、約0モル%から約7モル%の範囲にあり、ZnOは、約0モル%から約7モル%の範囲の量で存在し、
前記ガラス物品は、徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にある、ガラス物品。
前記ガラス物品が、200ポアズの粘度での温度(℃)(T200)および35000ポアズの粘度での温度(℃)(T35000)を有し、T200−T35000は、約400℃から約600℃の範囲にある、実施形態1に記載のガラス物品。
前記ガラス物品が、200ポアズの粘度での温度(℃)(T200)を有し、関係(徐冷点+軟化点)/2とT200との間の差が−800℃未満である、実施形態1または2に記載のガラス物品。
前記ガラス物品が、35000ポアズの粘度での温度(℃)(T35000)を有し、関係(徐冷点+軟化点)/2とT35000との間の差が−300℃未満である、実施形態1から3のいずれか1つに記載のガラス物品。
T200およびT35000のいずれか一方または両方が、約1030℃より大きい、実施形態2から4のいずれか1つに記載のガラス物品。
前記ガラス物品が、約620℃から約720℃の範囲の垂下温度を有する、実施形態1から5のいずれか1つに記載のガラス物品。
Al2O3の量が約8モル%から約11モル%の範囲にあり、Na2Oの量が約12モル%から約18モル%の範囲にあり、K2Oの量が、約1モル%から約3.5モル%の範囲にある、実施形態1から6のいずれか1つに記載のガラス物品。
約0.01モル%から約4モル%の範囲の量のCaOをさらに含む、実施形態1から7のいずれか1つに記載のガラス物品。
MgOが約0モル%から約3モル%の範囲の量で存在する、実施形態1から8のいずれか1つに記載のガラス物品。
ZnOが約0モル%から約5モル%の範囲の量で存在する、実施形態1から9のいずれか1つに記載のガラス物品。
前記関係(徐冷点+軟化点)/2が約700℃未満である、実施形態1から10のいずれか1つに記載のガラス物品。
約100kP超の液相粘度をさらに有する、実施形態1から11のいずれか1つに記載のガラス物品。
約35kP未満のジルコン分解粘度をさらに有する、実施形態1から12のいずれか1つに記載のガラス物品。
前記ガラス物品が強化されている、実施形態1から13のいずれか1つに記載のガラス物品。
前記ガラス物品がフュージョン成形されている、実施形態1から14のいずれか1つに記載のガラス物品。
アルミノケイ酸塩ガラス物品において、
2モル%超の量のAl2O3を含むガラス組成物、
を有し、
前記ガラス物品が徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にある、ガラス物品。
前記ガラス組成物が、約5モル%以上の総量のアルカリ金属酸化物(R2O)を含む、実施形態16に記載のガラス物品。
前記ガラス組成物が、MgOとZnOの一方または両方を含み、MgOの量は、約0モル%から約7モル%の範囲にあり、ZnOは、約0モル%から約7モル%の範囲の量で存在する、実施形態16または17に記載のガラス物品。
前記アルカリ金属酸化物の量の総量が、約5モル%から約20モル%の範囲にある、実施形態16から18のいずれか1つに記載のガラス物品。
約1000℃超の35キロポアズの粘度での温度をさらに有する、実施形態16から19のいずれか1つに記載のガラス物品。
約900℃超の200キロポアズの粘度での温度をさらに有する、実施形態16から20のいずれか1つに記載のガラス物品。
約580℃未満の徐冷点をさらに有する、実施形態16から21のいずれか1つに記載のガラス物品。
約530℃未満の歪み点をさらに有する、実施形態16から22のいずれか1つに記載のガラス物品。
約2.6g/cm3以下の密度をさらに有する、実施形態16から23のいずれか1つに記載のガラス物品。
約725℃から860℃の範囲の軟化点をさらに有する、実施形態16から24のいずれか1つに記載のガラス物品。
前記ガラス物品が強化されている、実施形態16から25のいずれか1つに記載のガラス物品。
前記ガラス物品がフュージョン成形されている、実施形態16から26のいずれか1つに記載のガラス物品。
内部および該内部と連通する開口を画成する本体と、
前記開口内に配置されたガラス物品であって、2モル%超の量のAl2O3を含むガラス組成物、徐冷点(℃)、軟化点(℃)、および約625℃から約725℃の範囲にある(徐冷点+軟化点)/2の関係を有する、ガラス物品と、
を備えた乗り物。
前記ガラス物品が、約16モル%以上の量の総量のアルカリ金属酸化物を含むガラス組成物、および約600℃から約700℃の範囲の垂下温度を有する、実施形態28に記載の乗り物。
前記ガラス組成物が、4モル%超の量のAl2O3をさらに含む、実施形態28または29に記載の乗り物。
前記ガラス組成物が、Li2O、Na2OおよびK2Oから選択されるアルカリ金属酸化物をさらに含み、該アルカリ金属酸化物が約5モル%超の量で存在する、実施形態28から30のいずれか1つに記載の乗り物。
前記ガラス組成物が、約5モル%から約24モル%の範囲の総量のアルカリ金属酸化物(R2O=Li2O+Na2O+K2O)をさらに含む、実施形態31に記載の乗り物。
前記ガラス物品が、約1000℃超の35キロポアズの粘度での温度をさらに有する、実施形態28から32のいずれか1つに記載の乗り物。
前記ガラス物品が、約900℃超の200キロポアズの粘度での温度をさらに有する、実施形態28から33のいずれか1つに記載の乗り物。
前記ガラス物品が、約600℃未満の徐冷点をさらに有する、実施形態28から34のいずれか1つに記載の乗り物。
前記ガラス物品が、約550℃未満の歪み点をさらに有する、実施形態28から35のいずれか1つに記載の乗り物。
前記ガラス物品が、約2.6g/cm3以下の密度をさらに有する、実施形態28から36のいずれか1つに記載の乗り物。
前記ガラス物品が、約725℃から860℃の範囲の軟化点をさらに有する、実施形態28から37のいずれか1つに記載の乗り物。
前記ガラス物品が強化されている、実施形態28から38のいずれか1つに記載の乗り物。
前記ガラス物品がさらにフュージョン成形されている、実施形態28から39のいずれか1つに記載の乗り物。
第1のガラス層、
前記第1のガラス層上に配置された中間層、および
前記第1のガラス層と反対の前記中間層上に配置された第2のガラス層、
を備えた積層板であって、
前記第1のガラス層および前記第2のガラス層のいずれか一方または両方が、実施形態1から15のいずれか1つに記載のガラス物品から作られている、積層板。
前記第1のガラス層および前記第2のガラス層のいずれか一方または両方が、約1.6mm未満の厚さを有する、実施形態41に記載の積層板。
第1のガラス層、
前記第1のガラス層上に配置された中間層、および
前記第1のガラス層と反対の前記中間層上に配置された第2のガラス層であって、実施形態1から15のいずれか1つに記載のガラス物品から作られているその第2のガラス層、
を備えた積層板。
前記第1のガラス層が1.6mm以上の厚さを有し、前記第2のガラス層が約1.6mm未満の厚さを有する、実施形態43に記載の積層板。
積層板を形成する方法において、
第1のガラス物品、および実施形態1から27のいずれか1つに記載の第2のガラス物品を積み重ねて、積層体を形成する工程であって、該第1のガラス物品が、該第2のガラス物品と異なる組成を有し、第一面および該第一面と反対の第二面を有し、該第2のガラス物品は、第三面および該第三面と反対の第四面を有し、前記積層体において、前記第二面が前記第三面と隣接している工程;
前記積層体を成形型上に配置する工程;
前記積層体を、前記第1のガラス物品の徐冷点より高い温度に加熱して、成形積層体を形成する工程;および
前記第1のガラス物品と前記第2のガラス物品との間に中間層を配置する工程;
を有してなる方法。
前記成形積層体が、約10mm以下の最大距離を有する間隙を前記第二面と前記第三面との間に含む、実施形態45に記載の方法。
前記最大距離が約5mm以下である、実施形態46に記載の方法。
前記最大距離が約3mm以下である、実施形態46に記載の方法。
積層板において、
第1の主面、該第1の主面と反対の第2の主面、該第1の主面と該第2の主面との間の距離として規定される第1の厚さ、および約2mm以上の第1の垂下深さを有する第1の湾曲ガラス層であって、第1の粘度(ポアズ)を有する第1の湾曲ガラス層;
第3の主面、該第3の主面と反対の第4の主面、該第3の主面と該第4の主面との間の距離として規定される第2の厚さ、および約2mm以上の第2の垂下深さを有する第2の湾曲ガラス層であって、第2の粘度を有する第2の湾曲ガラス層;および
前記第1の湾曲ガラス層と前記第2の湾曲ガラス層との間であって、前記第2の主面および前記第3の主面に隣接して配置された中間層;
を備え、
630℃での前記第1の粘度が630℃の温度での前記第2の粘度より大きく、
前記第1の垂下深さが前記第2の垂下深さの10%以内であり、前記第1の湾曲ガラス層と前記第2の湾曲ガラス層との間の形状偏差は、光学三次元スキャナで測定して、±5mm以下であり、
前記第1の主面および前記第4の主面の一方または両方は、ASTM1561にしたがう透過光学素子を使用した光学的歪み検出器で測定して、200ミリジオプター未満の光学的歪みを有し、
前記第3の主面または前記第4の主面は、ASTM C1279にしたがって、表面応力計で測定して、7MPa未満の膜引張応力を有する、積層板。
前記第1の湾曲ガラス層が、ガラス組成物を有するガラス物品から作られており、該ガラス組成物が、
約63モル%から約75モル%の範囲の量のSiO2、
約7モル%から約13モル%の範囲の量のAl2O3、
約13モル%から約24モル%の範囲の量のR2O、および
約0モル%から約3モル%の範囲の量のP2O5
を含み、
前記ガラス組成物は、MgOとZnOの一方または両方を含み、MgOの量は、約0モル%から約7モル%の範囲にあり、ZnOは、約0モル%から約7モル%の範囲の量で存在し、
前記ガラス物品は、徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にある、実施形態49に記載の積層板。
前記第1の湾曲ガラス層が、アルミノケイ酸塩ガラス物品から作られており、該ガラス物品が、2モル%超の量のAl2O3を含むガラス組成物を有し、前記ガラス物品が徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にあり、前記ガラス組成物が、必要に応じて、約5モル%以上の総量のアルカリ金属酸化物(R2O)を含む、実施形態49に記載の積層板。
約630℃の温度で、前記第1の粘度が、前記第2の粘度の約10倍から該第2の粘度の約750倍の範囲にある、実施形態50または51に記載の積層板。
前記第1の厚さが前記第2の厚さより小さい、実施形態50から52のいずれか1つに記載の積層板。
前記第1の厚さが、約0.1mmから約1.6mm未満までであり、前記第2の厚さが、約1.6mmから約3mmの範囲にある、実施形態50から53のいずれか1つに記載の積層板。
前記第1の湾曲ガラス層が第1の垂下温度を有し、前記第2の湾曲ガラス層が、該第1の垂下温度と異なる第2の垂下温度を有する、実施形態50から54のいずれか1つに記載の積層板。
前記第1の垂下温度と前記第2の垂下温度との間の差の大きさが、約30℃から約150℃の範囲にある、実施形態55に記載の積層板。
前記形状偏差が約±1mm以下である、実施形態50から56のいずれか1つに記載の積層板。
前記前記形状偏差が約±0.5mm以下である、実施形態50から57のいずれか1つに記載の積層板。
前記光学的歪みが約100ミリジオプター以下である、実施形態50から58のいずれか1つに記載の積層板。
前記膜引張応力が約5MPa以下である、実施形態50から59のいずれか1つに記載の積層板。
前記第1の垂下深さが約5mmから約30mmの範囲にある、実施形態50から60のいずれか1つに記載の積層板。
前記第3の主面または前記第4の主面が、表面応力計で測定して、3MPa未満の表面圧縮応力を有する、実施形態50から61のいずれか1つに記載の積層板。
前記積層板が、ASTM C1652/C1652Mにより測定して、視覚歪みを実質的に含まない、実施形態50から62のいずれか1つに記載の積層板。
前記第1の湾曲ガラス層が強化されている、実施形態50から63のいずれか1つに記載の積層板。
前記第1の湾曲ガラス層が、化学強化されている、機械的に強化されている、または熱強化されている、実施形態64に記載の積層板。
前記第2の湾曲ガラス層が強化されていない、実施形態64または65に記載の積層板。
前記第2の湾曲ガラス層が強化されている、実施形態64または65に記載の積層板。
前記第2の湾曲ガラス層がソーダ石灰ケイ酸塩ガラスから作られている、実施形態50から67のいずれか1つに記載の積層板。
前記第1の湾曲ガラス層が、第1の長さおよび第1の幅を有し、該第1の長さおよび該第1の幅のいずれか一方または両方は、約0.25メートル以上である、実施形態50から68のいずれか1つに記載の積層板。
前記第1の湾曲ガラス層が、第1の長さおよび第1の幅を有し、前記第2の湾曲ガラス層が、該第1の長さの5%以内の第2の長さ、および該第1の幅の5%以内の第2の幅を有する、実施形態50から69のいずれか1つに記載の積層板。
前記積層板が複雑に湾曲している、実施形態50から70のいずれか1つに記載の積層板。
前記積層板が、自動車用板ガラスまたは建築用板ガラスを構成する、実施形態50から71のいずれか1つに記載の積層板。
内部および該内部と連通する開口を画成する本体と、
前記開口内に配置された実施形態50から72のいずれか1つに記載の積層板と、
を備えた乗り物。
前記積層板が複雑に湾曲している、実施形態73に記載の乗り物。
102、412 第1の主面
104、414 第2の主面
106、108 副面
110 厚さt
200、300、400、500 積層板
210、310、510 第1のガラス層
220、330、530 第2のガラス層
320、430、520 中間層
410 第1の湾曲ガラス層
416 第1の厚さ
418 第1の垂下深さ
420 第2の湾曲ガラス層
422 第3の主面
424 第4の主面
426 第2の厚さ
428 第2の垂下深さ
512 第三面
514 第四面
532 第一面
534 第二面
600 車両
610 車体
620 開口
630 ガラス物品
Claims (10)
- ガラス組成物を有するガラス物品において、該ガラス組成物が、
約63モル%から約75モル%の範囲の量のSiO2、
約7モル%から約13モル%の範囲の量のAl2O3、
約13モル%から約24モル%の範囲の量のR2O、および
約0モル%から約3モル%の範囲の量のP2O5
を含み、
前記ガラス組成物は、MgOとZnOの一方または両方を含み、MgOの量は、約0モル%から約7モル%の範囲にあり、ZnOは、約0モル%から約7モル%の範囲の量で存在し、
前記ガラス物品は、徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にある、ガラス物品。 - 前記ガラス物品が、200ポアズの粘度での温度(℃)(T200)および35000ポアズの粘度での温度(℃)(T35000)を有し、T200−T35000は、約400℃から約600℃の範囲にある、請求項1記載のガラス物品。
- 前記ガラス物品が、200ポアズの粘度での温度(℃)(T200)を有し、関係(徐冷点+軟化点)/2とT200との間の差が−800℃未満である、請求項1または2記載のガラス物品。
- 前記ガラス物品が、35000ポアズの粘度での温度(℃)(T35000)を有し、関係(徐冷点+軟化点)/2とT35000との間の差が−300℃未満である、請求項1から3いずれか1項記載のガラス物品。
- T200およびT35000のいずれか一方または両方が、約1030℃より大きい、請求項2から4いずれか1項記載のガラス物品。
- 前記ガラス物品が、約620℃から約720℃の範囲の垂下温度を有する、請求項1から5いずれか1項記載のガラス物品。
- Al2O3の量が約8モル%から約11モル%の範囲にあり、Na2Oの量が約12モル%から約18モル%の範囲にあり、K2Oの量が、約1モル%から約3.5モル%の範囲にある、請求項1から6いずれか1項記載のガラス物品。
- 約0.01モル%から約4モル%の範囲の量のCaO、
約0モル%から約3モル%の範囲の量で存在するMgO、および
約0モル%から約5モル%の範囲の量で存在するZnO、
の少なくとも1つをさらに含む、請求項1から7いずれか1項記載のガラス物品。 - 前記ガラス物品が、強化されている、およびフュージョン成形されている、の少なくとも一方である、請求項1から8いずれか1項記載のガラス物品。
- アルミノケイ酸塩ガラス物品において、
2モル%超の量のAl2O3を含むガラス組成物、
を有し、
前記ガラス物品が徐冷点(℃)および軟化点(℃)を有し、(徐冷点+軟化点)/2の関係が約625℃から約725℃の範囲にある、ガラス物品。