JP2020165020A - Material for rucksack and rucksack using the material - Google Patents
Material for rucksack and rucksack using the material Download PDFInfo
- Publication number
- JP2020165020A JP2020165020A JP2019065275A JP2019065275A JP2020165020A JP 2020165020 A JP2020165020 A JP 2020165020A JP 2019065275 A JP2019065275 A JP 2019065275A JP 2019065275 A JP2019065275 A JP 2019065275A JP 2020165020 A JP2020165020 A JP 2020165020A
- Authority
- JP
- Japan
- Prior art keywords
- melting point
- rucksack
- mesh
- lining
- point polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明はリュックサック用素材および同素材を用いたリュックサックに関する。 The present invention relates to a material for a rucksack and a rucksack using the same material.
一般的なリュックサックはバッグと一対の肩ベルトとを有し、一方の肩ベルトを右肩に掛けるとともに他方の肩ベルトを左肩に掛けることでバッグを背負うことができるように構成されている（特許文献１）。特許文献１に記載されたリュックサックの肩ベルトは、弾性を有する芯材と、この芯材を被覆する表生地とで構成されている。また、一般的なリュックサックにおいては、バッグは布地にて構成され、このバッグにおける使用者の背中に当たる部分すなわち背当てにクッション材が配置されたものも見受けられる。このクッション材は、肩ベルトの芯材と同様に適当な布地によって被覆されているのが通例である。 A typical rucksack has a bag and a pair of shoulder belts, and is configured so that the bag can be carried on the back by hanging one shoulder belt on the right shoulder and the other shoulder belt on the left shoulder (). Patent Document 1). The shoulder belt of the rucksack described in Patent Document 1 is composed of an elastic core material and a front fabric covering the core material. Further, in a general rucksack, the bag is made of cloth, and a cushioning material is arranged on the part of the bag that hits the back of the user, that is, the backrest. This cushioning material is usually covered with a suitable fabric as well as the core material of the shoulder belt.
しかし、従来の肩ベルトやバッグは、上記のように弾性を有する芯材やクッション材を有しており、これらの部材は衣類を介して使用者の身体に接するものであるものの、通気性に乏しいという問題点がある。このため、使用者にとっては、肩や背中に汗がこもりやすいという課題がある。また上記した芯材やクッション材は、使用者の人体にうまく適合したものでない限り、使用者に良好なクッション感を作用させることが困難であるという課題もある。また、弾性を有する芯材やクッション材を単に用いただけのものでは、柔軟性は得ることができるものの、剛性や緩衝性がなく、より重たい荷物を背負った場合に身体にフィットし過ぎて背負い心地が悪いという課題がある。 However, conventional shoulder belts and bags have elastic core materials and cushioning materials as described above, and although these members come into contact with the user's body through clothing, they are breathable. There is a problem that it is scarce. For this reason, there is a problem that the user tends to accumulate sweat on the shoulders and back. Further, the above-mentioned core material and cushion material have a problem that it is difficult to give a good cushioning feeling to the user unless the core material and the cushion material are well adapted to the human body of the user. In addition, although flexibility can be obtained by simply using an elastic core material or cushioning material, it does not have rigidity or cushioning properties, and it fits too much on the body when carrying a heavier load and is comfortable to carry. There is a problem that it is bad.
そこで本発明は、このような課題を解決して、リュックサックの肩ベルトや背当てに好適に使用することができる通気性とクッション性を有し、さらには緩衝性と剛性とを兼備したリュックサック用素材を得ることを目的とする。 Therefore, the present invention solves such a problem and has a backpack having breathability and cushioning properties that can be suitably used for a shoulder belt or a backrest of a rucksack, and further has cushioning properties and rigidity. The purpose is to obtain materials for backpacks.
この目的を達成するため本発明のリュックサック用素材は、
リュックサックの肩ベルトおよび／またはリュックサックにおける使用者の背中に当たる部分を構成するために使用される素材であって、
表地と裏地とが連結糸で連結されたダブルラッセル編地にて構成され、
前記表地と裏地との内の少なくともいずれか一方が、メッシュ状体にて構成されているとともに、
前記表地と裏地との内の少なくともいずれか一方の編地を形成する糸条が、高融点ポリマーと低融点ポリマーとを有した複合型熱融着繊維であって、低融点ポリマーの溶融再固化によって、繊維形態を保った高融点ポリマーが固着された状態の繊維によって形成されていることを特徴とする。
In order to achieve this object, the rucksack material of the present invention
A material used to form the shoulder belt of a rucksack and / or the part of the rucksack that hits the user's back.
It is composed of a double Russell knitted fabric in which the outer material and the lining are connected by a connecting thread.
At least one of the outer material and the lining is made of a mesh-like body, and
The thread forming the knitted fabric of at least one of the outer material and the lining is a composite heat-sealing fiber having a high melting point polymer and a low melting point polymer, and melt resolidification of the low melting point polymer. It is characterized in that the high melting point polymer maintaining the fiber morphology is formed by the fibers in a fixed state.
また、本発明のリュックサック用素材は、上記したダブルラッセル編地の表地と裏地との両方がメッシュ状体にて構成されている場合には、そのうちの少なくともいずれか一方のメッシュ状体において、また表地と裏地とのいずれか一方がメッシュ状体にて構成されている場合には、そのメッシュ状体において、当該メッシュ状体を形成する糸条が、高融点ポリマーと低融点ポリマーとを有した複合型熱融着繊維であって、低融点ポリマーの溶融再固化によって、繊維形態を保った高融点ポリマーが固着された状態の繊維によって形成されていることを特徴とする。 Further, in the rucksack material of the present invention, when both the outer material and the lining of the double Russell knitted fabric described above are composed of a mesh-like body, in at least one of the mesh-like bodies, the mesh-like body may be used. When either the outer material or the lining is composed of a mesh-like body, the threads forming the mesh-like body in the mesh-like body have a high melting point polymer and a low melting point polymer. The composite type heat-fused fiber is characterized in that the high melting point polymer maintaining the fiber morphology is formed by the fixed state fiber by melt resolidification of the low melting point polymer.
本発明のリュックサックは、上記したリュックサック用素材を構成部材とするものであることを特徴とする。 The rucksack of the present invention is characterized in that the rucksack material described above is used as a constituent member.
本発明のリュックサック用素材によれば、表地と裏地とが連結糸で連結されたダブルラッセル編地にて構成され、前記表地と裏地との内の、少なくともいずれか一方が、メッシュ状体にて構成されているため、優れた通気性を有し、このためこの素材を用いたリュックサックを着用したときに、使用者の肩や背中の部分に汗がこもることがないうえに、表地と裏地とが連結糸で連結された三次元編物にて素材が構成されているために、着用者の肩や背中に対する適切なクッション性を発揮することができる。また、表地と裏地との内の少なくともいずれか一方の編地を形成する糸条が、高融点ポリマーと低融点ポリマーとを有した複合型熱融着繊維であって、低融点ポリマーの溶融再固化によって、繊維形態を保った高融点ポリマーが固着された状態の繊維によって形成されていることで、リュックサックの肩ベルトや背当てにとって好ましい適度の剛性も兼備することができるため、重たい荷物を入れた場合であっても、その負荷に対してへたり難く厚みを維持し、通気性や緩衝性に優れることから、背負い心地の良好なリュックサックを提供できる。 According to the material for rucksacks of the present invention, the outer material and the lining are made of a double Russell knitted fabric in which the outer material and the lining are connected by a connecting thread, and at least one of the outer material and the lining is formed into a mesh-like body. Because it is constructed with excellent breathability, when wearing a rucksack using this material, sweat does not stay on the shoulders and back of the user, and it is also the outer material. Since the material is made of a three-dimensional knitted fabric in which the lining is connected with a connecting thread, it is possible to exhibit appropriate cushioning properties for the wearer's shoulders and back. Further, the thread forming the knitted fabric of at least one of the outer material and the lining is a composite heat-sealing fiber having a high melting point polymer and a low melting point polymer, and the low melting point polymer is melted and re-melted. By solidification, the refractory polymer that maintains the fiber morphology is formed by the fibers in a fixed state, so that it can also have appropriate rigidity that is preferable for the shoulder belt and backrest of a rucksack, so that heavy luggage can be carried. Even when it is put in, it does not easily settle under the load, maintains its thickness, and has excellent breathability and cushioning properties, so it is possible to provide a rucksack that is comfortable to carry on the back.
図１に示されるリュックサックにおいて、１１はバッグ、１２、１２は一対の肩ベルトである。バッグ１１は樹脂シートにて袋状に形成され、肩ベルト１２は樹脂材によって厚手の帯状に形成されている。バッグ１１には、使用者が着用したときに使用者の背中に接する背当て１３が形成されている。
In the rucksack shown in FIG. 1, 11 is a bag and 12 and 12 are a pair of shoulder belts. The
肩ベルト１２と背当て１３とには、本発明の実施の形態の素材１４が用いられている。この素材１４は、図２〜図５に示すように、表地１５と裏地１６とを有するとともに、これら表地１５と裏地１６とを連結する多数の連結糸１７を有することで、所要の弾力性を発揮することが可能な、ダブルラッセル編地にて構成されている。表地１５は、メッシュ状体すなわちメッシュ構造の編物布帛である。裏地１６は、図示のように表地と同様のメッシュ構造の編物布帛であることが好適である。あるいは、後述のように、裏地１６は、メッシュ構造であることに代えて、地組織すなわちメッシュ構造ではない一般的な目の詰まった編地にて構成することもできる。連結糸１７は、表地１５の構成糸条と、裏地１６の構成糸条とを繋ぐものである。
The
図示の表地１５と裏地１６とのメッシュ構造について説明する。このメッシュ構造は、多角形状のメッシュ構造であり、図示の例ではメッシュの形状が六角形である。このほかにも四角形のメッシュ構造も容易に実現することができ、その場合のメッシュの形状は、図示を省略するが菱形となる。
The mesh structure of the illustrated
本発明の実施の形態において、表地１５と裏地１６とのメッシュ構造は、多角形の一辺が２〜６０コースの編目により構成されたものである。一辺を構成する編目の個数をこの範囲とするのは、主としてメッシュの立体形状の安定性の観点による。
In the embodiment of the present invention, the mesh structure of the
メッシュ組織にて構成された表地１５の構成糸条と裏地１６の構成糸条とは、上述のように連結糸１７によって繋がれている。図示のように、連結糸１７はダブルラッセル編地の厚み方向に配列され、表地１５の構成糸条と裏地１６の構成糸条との間に編み構造によって多数本の連結糸１７が配置されている。その繊度は、素材１４の形態安定性の観点から、１００デシテックス以上であることが好ましい。
The constituent threads of the
素材１４すなわちダブルラッセル編地を構成する糸条は、このダブルラッセル編地がリュックサックのバッグ１１および肩ベルト１２としての好適な弾性を有することができる適宜の材料にて構成することができる。そのような材料としては、ポリエチレンテレフタレートのようなポリエステルや、ポリアミドや、その他の熱可塑性樹脂を挙げることができる。
The thread constituting the
本発明の実施の形態の素材１４における表地１５と裏地１６との内の少なくともいずれか一方の編地を形成する糸条は、複合型熱融着繊維によって構成される。また、両方がメッシュ状体にて構成されている場合には、そのうちの少なくともいずれか一方のメッシュ状体において、また表地１５と裏地１６とのいずれか一方がメッシュ状体にて構成されている場合には、そのメッシュ状体において、当該メッシュ状体を形成する糸条は、複合型熱融着繊維によって構成されることが好ましい。そのような複合型熱融着繊維としては、鞘部に低融点熱可塑性ポリマーが配され、芯部に、鞘部の低融点熱可塑性ポリマーよりも融点の高い高融点熱可塑性ポリマーが配された芯鞘型熱融着性繊維が挙げられる。ポリマーが融点を有しない場合は、融点に代えて軟化点での高低の対比となる。そのほかにも、低融点熱可塑性ポリマーと高融点熱可塑性ポリマーとが半々に配されたサイドバイサイド型熱融着性繊維などが挙げられる。
The yarn forming at least one of the
図６は、芯鞘型の断面構造を有する複合型熱融着繊維の断面構造を示す。ここで、１８は芯部、１９は鞘部である。芯部１８を構成する高融点ポリマーと、鞘部１９を構成する低融点ポリマーとしては、たとえば、ポリエステル系重合体、ポリアミド系重合体（ナイロン）、ポリオレフィン系重合体、ポリブチラール系重合体、ポリアクリル系重合体、ポリエチレン−酢酸ビニル共重合体、ポリウレタン重合体などなどが挙げられる。素材１４の柔軟性を重視する場合には、両ポリマーがいずれもポリアミド系重合体であることが好ましく、強度や所要の剛性に優れるという点では両ポリマーがいずれもポリエステル系重合体であることが好ましい。
FIG. 6 shows a cross-sectional structure of a composite heat-sealed fiber having a core-sheath type cross-sectional structure. Here, 18 is a core portion and 19 is a sheath portion. Examples of the high melting point polymer constituting the
低融点熱可塑性ポリマーと高融点熱可塑性ポリマーとの具体的な好ましい組み合わせは、両者の相溶性や後述する熱接着時の性能を考慮すると、低融点ポリエステルと高融点ポリエステル、低融点ポリプロピレンと高融点ポリプロピレン、ポリエチレンとポリプロピレン、低融点ナイロンと高融点ナイロン、などが挙げられる。 Specific preferable combinations of the low melting point thermoplastic polymer and the high melting point thermoplastic polymer are low melting point polyester and high melting point polyester, and low melting point polypropylene and high melting point in consideration of compatibility between the two and the performance at the time of thermal bonding described later. Examples include polypropylene, polyethylene and polypropylene, low melting point nylon and high melting point nylon, and the like.
リュックサック用の素材１４としての観点から、複合型熱融着性繊維における高融点熱可塑性ポリマーと低融点熱可塑性ポリマーとの質量比率、すなわち芯部１８と鞘部１９との質量比率は、たとえば、高融点熱可塑性ポリマー／低融点熱可塑性ポリマーの質量比率で、２／８〜８／２がよく、２／１〜３／１がより好ましい。
From the viewpoint of the
素材１４は、肩ベルト１２や背当て１３としてより適した性能を発揮することができるように、熱セット処理されたものにて構成される。熱セット処理することによって、図７に示すように、鞘部１９の低融点熱可塑性ポリマーを融解あるいは軟化させたうえで再固化させることで、図示のように複数の繊維の芯部１８同士を熱接着によって互いに固定一体化することができる。それによって、複合型熱融着性繊維により構成される編地自体が、繊維布帛が有するしなやかさを失って、剛性を有し、形態安定性を有したものとなり、メッシュの目が適切な大きさに開いた状態で固定することができ、その結果、肩ベルト１２や背当て１３の三次元的な形態を安定化させたうえで、所要の通気性を確保することができるとともに、素材１４に、肩ベルト１２や背当て１３に適した程良い弾力性や、バッグ１１の内部の収用物に対する緩衝性や、使用者の身体に対するフィット性や、剛性を付与することができる。
The
熱セット処理の際には、上記のように熱融着成分としての鞘部１９の低融点熱可塑性ポリマーは融解あるいは軟化されて、場合によっては図示のように繊維形態を失ったうえで再固化されるが、そのときに熱セットの処理温度を、鞘部１９の低融点熱可塑性ポリマーの融点または軟化点以上の温度かつ芯部１８の高融点熱可塑性ポリマーの融点または軟化点未満の温度とすることにより、芯部１８の高融点熱可塑性ポリマーは繊維形態を保った状態に維持される。その結果、本発明のリュックサック用素材１４は、繊維状の成分を含んだシート状体となるため、このような繊維状の成分を含まない単なる樹脂シートにて構成された素材に比べて強度的に優れたものとすることができる。
During the heat setting treatment, the low melting point thermoplastic polymer of the
図８および図９は、本発明のリュックサック用素材１４の他の実施の形態を示す。この実施の形態では、前述のように、裏地１６は、メッシュ構造であることに代えて、地組織すなわちメッシュ構造ではない一般的な目の詰まった編地にて構成されている。このような構成であると、例えば、表地１５を着用者の身体側に配置することで優れた通気性を確保することができるうえに、裏地１６を一般的な目の詰まった編地にて構成することで、肩ベルト１２に所要の強度や形態保持性を付与することができるとともに、背当て１３もバッグ１１と一体化されることで、着用者の背中の部分におけるバッグ１１の強度や形態保持性を向上させることができる。また、一般的な目の詰まった編地であることで、バッグ１１への取付け性が良好である。反対に、メッシュ状の表地１５を着用者の身体側とは反対側に配置させ、裏地１６を着用者の身体側に配置した場合でも、優れた通気性確保と形態保持性、緩衝性を奏する。さらには、上述したような、表地１５のみならず裏地１６もがメッシュ構造を呈する素材１１の場合は、格段に優れた通気性を得ることができる。
8 and 9 show other embodiments of the
以上において説明した素材１４を用いて、図１に示されるリュックサックの肩ベルト１２と、バッグ１１の背当て１３とが形成される。肩ベルト１２は、着用者の身体側にメッシュ構造の表地１５または裏地１６を露出させることで、通気性をより発揮させることができる。着用者の身体側以外の部分は、着用性や装飾性を向上させるために、布帛などのシート材２０でカバーすることが好適である。背当て１３も、同様に着用者の身体側にメッシュ構造の表地１５または裏地１６を露出させることで、通気性をより発揮させることができる。図示は省略するが、この背当て１３についても、布帛などのシート材でたとえば縁取りを施すことなどにより、装飾性などを向上させることができる。
場合によっては、上記とは逆に、着用者の身体側とは反対側に、メッシュ構造の表地１５または裏地１６を露出させることもできる。
Using the material 14 described above, the
In some cases, contrary to the above, the
このような、本発明の実施の形態の素材１４を用いて構成した肩ベルト１２や背当て１３は、上記のように良好な通気性を有することで、着用時に汗がこもったりすることが無いという利点がある。のみならず、ダブルラッセル編地にて構成されているために、適度なクッション性を有し、このために着用時における使用者への負荷を軽減することができる。さらに、熱セット処理が施されたものであることで、適度な剛性や形態安定性を発揮することができて、過度に柔軟であることで着用時に身体にフィットし過ぎるということがないうえに、圧縮時には点でなく面の全体で負荷を受け止めて圧縮することになり、このため圧縮時にもある程度以上の厚みを維持することができて、それにもとづくクッション性を確保することもでき、通気性を維持し、緩衝性に優れる。したがって、リュックサックの肩ベルト１２や背当て１３としてより適したものとなる。
The
以下の実施例・比較例において、各物性の評価や性能試験は、次のようにして行った。 In the following Examples and Comparative Examples, evaluation of each physical property and performance test were carried out as follows.
（ａ）３点曲げ応力
試料を長さ７０ｍｍ、幅５０ｍｍにカットし、ＪＩＳＫ−７１７１に従い、試料のウェール方向に圧子が沿うように試料の中央部の３点曲げ試験を行った。試験速度は２ｍｍ／分、支点間距離は３２ｍｍとした。試料に荷重がかかり始めた点を始点とし圧子が７ｍｍ変位した時の応力を測定した。５回測定しその平均値を算出して３点曲げ応力とした。
(A) Three-point bending stress The sample was cut to a length of 70 mm and a width of 50 mm, and a three-point bending test was performed at the center of the sample so that the indenter would follow the wale direction of the sample according to JISK-7171. The test speed was 2 mm / min and the distance between the fulcrums was 32 mm. The stress when the indenter was displaced by 7 mm was measured starting from the point where the load began to be applied to the sample. It was measured 5 times and the average value was calculated to obtain a 3-point bending stress.
（ｂ）圧縮応力
試料を長さ７０ｍｍ、幅５０ｍｍにカットし、平らな金属板の上に設置した。ＪＩＳＫ−７１７１に従い、試料のウェール方向に圧子が沿うように試料の中央部を圧子で圧縮し、圧子が２ｍｍ変位した時の応力を測定した。５回測定しその平均値を算出して圧縮応力とした。
(B) Compressive stress The sample was cut to a length of 70 mm and a width of 50 mm and placed on a flat metal plate. According to JISK-7171, the central part of the sample was compressed with an indenter so that the indenter was aligned in the wale direction of the sample, and the stress when the indenter was displaced by 2 mm was measured. It was measured 5 times and the average value was calculated to obtain the compressive stress.
（ｃ）リュックサック用緩衝材としての性能試験
容量２２Ｌ、タテ４８ｃｍ×ヨコ２５ｃｍ×奥行き２２ｃｍのリュックサックの背当て材として、タテ３０ｃｍ×ヨコ２０ｃｍにカットした試料を１枚使用した。また、同リュックサックの左右の肩ベルトとして、タテ４０ｃｍ×ヨコ５ｃｍにカットした同試料を左右に１枚ずつ使用した。リュックサックの内部に１０ｋｇの錘を入れて、実際に人がリュックサックを背負った時の背当ておよび肩ベルトとしての剛性、フィット性、通気性、緩衝性について官能評価を行った。
(C) Performance test as a cushioning material for a rucksack As a backpack material for a rucksack having a capacity of 22 L and a length of 48 cm × width of 25 cm × depth of 22 cm, one sample cut into a length of 30 cm × width of 20 cm was used. Further, as the left and right shoulder belts of the rucksack, the same sample cut into a length of 40 cm and a width of 5 cm was used one by one on the left and right. A 10 kg weight was placed inside the rucksack, and sensory evaluation was performed on the rigidity, fit, breathability, and cushioning properties of the backpack and shoulder belt when a person actually carried the rucksack on his back.
実施例１
６枚筬を具備したダブルラッセル編機を用いて、Ｌ１〜Ｌ６筬に下記原糸を供給し、図１０に示す組織にて編成した。図１０に示す組織を４テンポ表示すると、以下の通りである。
Ｌ１：２１１１／１２２２／１０１１／１２１１／１０１１／１２１１／１０１１／
１２２２／２１２２／２３２２／２１２２／２３２２／２１２２／２３２２
Ｌ２：１２２２／２１２２／２３２２／２１２２／２３２２／２１２２／２３２２／２１１１／１２１１／１０１１／１２１１／１０１１／１２１１／１０１１
Ｌ３：２１１０／１２１０／１２１０／１２１０／１２１０／１２１０／１２１０／
１２２３／１２２３／２１２３／２１２３／２１２３／２１２３／２１２３
Ｌ４：１２２３／２１２３／２１２３／２１２３／２１２３／２１２３／２１２３／
２１１０／１２１０／１２１０／１２１０／１２１０／１２１０／１２１０
Ｌ５：１１１２／１１１０／１１１２／１１１０／１１１２／１１０１／１１１２／
２２２１／２２２３／２２２１／２２２３／２２２１／２２２３／２２２１
Ｌ６：２２２１／２２２３／２２２１／２２２３／２２２１／２２２３／２２２１／
１１１２／１１１０／１１１２／１１１０／１１１２／１１１０／１１１２
ここで、
Example 1
Using a double Russell knitting machine equipped with 6 reeds, the following yarns were supplied to L1 to L6 reeds and knitted with the structure shown in FIG. The organization shown in FIG. 10 is displayed at four tempos as follows.
L1: 2111/1222/12101/1211/1011/1211/1011 /
1222/2122/2322/2122/2322/2122/2322
L2: 1222/2122/2322/2122/2322/2122/2322/2111/1211/111/1211/1011/1211/1011
L3: 2110/1210/1210/1210/1210/1210/1210 /
1223/1223/2123/2123/2123/2123/2123
L4: 1223/2123/2123/2123/2123/2123/2123 /
2110/1210/1210/1210/1210/1210/1210
L5: 1112/1110/1112/1110/1112/1101/1112 /
2221/2223/2221/2223/2221/2223/2221
L6: 2221/2223/2221/2223/2221/2223/2221/
1112/1110/1112/1110/1112/1110/1112
here,
Ｌ１：ユニチカ社製 商品名「メルセット ＣＭ２７」２８０ｄｔｅｘ４８フィラメント（芯鞘複合型熱融着繊維からなるマルチフィラメント糸 芯：ポリエチレンテレフタレート（ＰＥＴ）、鞘：共重合ポリエステル、芯鞘比（質量比）は芯：鞘＝２．７：１）を３本
Ｌ２：ユニチカ社製 商品名「メルセット ＣＭ２７」２８０ｄｔｅｘ４８フィラメント糸を３本（Ｌ１と同じもの）
Ｌ３：ユニチカ社製ＰＥＴモノフィラメント糸（品番 ＰＶ２１） ２８０ｄｔｅｘを２本
Ｌ４：ユニチカ社製ＰＥＴモノフィラメント糸（品番 ＰＶ２１）２８０ｄｔｅｘを２本（Ｌ３と同じもの）
Ｌ５：ユニチカ社製 商品名「メルセット ＣＭ２７」２８０ｄｔｅｘ４８フィラメントを３本（Ｌ１と同じもの）
Ｌ６：ユニチカ社製 商品名「メルセット ＣＭ２７」２８０ｄｔｅｘ４８フィラメントを３本（Ｌ５と同じもの）とした。
L1: Made by Unitika Co., Ltd. Product name "Melset CM27" 280dtex48 filament (multifilament yarn made of core-sheath composite heat-sealing fiber Core: polyethylene terephthalate (PET), sheath: copolymerized polyester, core-sheath ratio (mass ratio) Core: Sheath = 2.7: 1) 3 pieces L2: Unitika Co., Ltd. Product name "Melset CM27" 280dtex48 3 filament threads (same as L1)
L3: Two Unitika PET monofilament yarns (part number PV21) 280dtex L4: Two Unitika PET monofilament yarns (part number PV21) 280dtex (same as L3)
L5: Unitika Ltd. product name "Melset CM27" 3 280dtex48 filaments (same as L1)
L6: Unitika Ltd. trade name "Melset CM27" 280dtex48 filaments were set to 3 (same as L5).
編成した網地は、表地および裏地ともに略六角形状の網目を有し、表地および裏地がＰＥＴモノフィラメント糸によって連結されたものであった。全巾１２７０ｍｍ、厚み５．９ｍｍ、コース密度２６．２本／インチ、ウェール密度１４．０本／インチ、目付け１０００ｇ／ｍ２であった。この網地をピンテンターを用いて１８０℃で２分間熱処理し、全巾９８５ｍｍ、厚み５．５ｍｍ、コース密度２５．４本／インチ、ウェール密度９．１本／インチ、目付け６２２ｇ／ｍ２の網地構造の素材を得た。 The knitted net had a substantially hexagonal mesh on both the outer and lining, and the outer and lining were connected by PET monofilament yarn. The total width was 1270 mm, the thickness was 5.9 mm, the course density was 26.2 lines / inch, the wale density was 14.0 lines / inch, and the basis weight was 1000 g / m 2 . This net is heat-treated at 180 ° C. for 2 minutes using a pin tenter, and has a total width of 985 mm, a thickness of 5.5 mm, a course density of 25.4 lines / inch, a wale density of 9.1 lines / inch, and a basis weight of 622 g / m 2 . Obtained the material of the ground structure.
実施例２
実施例１と比べて、６枚筬のうちのＬ１筬およびＬ２筬に下記原糸用いた点を変化させた。そして、それ以外は実施例１と同様にして網地構造の素材を得た。
Ｌ１：ユニチカ社製 ＰＥＴマルチフィラメント糸（品番 Ｅ８１４）２８０ｄｔｅｘ４８フィラメントを３本
Ｌ２：ユニチカ社製 ＰＥＴマルチフィラメント糸（品番 Ｅ８１４）２８０ｄｔｅｘ４８フィラメントを３本（Ｌ１と同じもの）
Example 2
Compared with Example 1, the point that the following raw yarn was used for L1 reed and L2 reed out of 6 reeds was changed. Then, a material having a net structure was obtained in the same manner as in Example 1 except for the above.
L1: Three Unitika PET multifilament yarns (part number E814) 280dtex48 filaments L2: Unitika PET multifilament yarns (part number E814) 280dtex48 filaments three (same as L1)
実施例２の網地構造の素材は、片面が熱融着性複合繊維のみから構成され熱融着により硬化して形態安定性を向上させるものであり、他面は熱による影響を受けずに柔軟な繊維形態を維持するものであるため、剛性・形態安定性と柔軟性とを併せ持ち、実施例１と比較して、より身体へのフィット感を有するものであった。リュックサックに適用する際に、熱融着性複合繊維のみから構成される面を身体側ではない方に位置させることにより、身体へのフィット感がより良好となった。なお、その逆の使用方法であっても、当然ながら、本発明の効果を良好に奏することができるものであった。 The material of the mesh structure of Example 2 is composed of only heat-sealing composite fibers on one side and is cured by heat-sealing to improve morphological stability, and the other side is not affected by heat. Since it maintains a flexible fiber morphology, it has both rigidity / morphological stability and flexibility, and has a better fit to the body as compared with Example 1. When applied to a rucksack, the fit to the body was improved by locating the surface composed only of the heat-sealing composite fibers on the side other than the body side. As a matter of course, the effect of the present invention can be satisfactorily exhibited even in the reverse usage method.
比較例１
実施例２と比べて、６枚筬のうちのＬ５筬およびＬ６筬に下記原糸用いた点を変化させた。そして、それ以外は実施例２と同様にして網地構造の素材を得た。
Ｌ５：ユニチカ社製ＰＥＴマルチフィラメント糸（品番 Ｅ８１４）２８０ｄｔｅｘ４８フィラメントを３本（Ｌ１と同じもの）
Ｌ６：ユニチカ社製ＰＥＴマルチフィラメント糸（品番 Ｅ８１４）２８０ｄｔｅｘ４８フィラメントを３本（Ｌ５と同じもの）
Comparative Example 1
Compared with Example 2, the point that the following raw yarn was used for L5 reed and L6 reed out of 6 reeds was changed. Then, a material having a net structure was obtained in the same manner as in Example 2 except for the above.
L5: Unitika PET multifilament yarn (product number E814) 3 280dtex48 filaments (same as L1)
L6: Unitika PET multifilament yarn (product number E814) 3 280dtex48 filaments (same as L5)
実施例１、２および比較例１の素材についての測定・評価結果を表１に示す。 Table 1 shows the measurement / evaluation results of the materials of Examples 1 and 2 and Comparative Example 1.
実施例１および２の網地構造の素材は、３点曲げおよび圧縮のいずれの応力も高い値であり、圧縮されにくく、圧力に対して立体構造を良好に維持し、形態安定性に優れ、通気性を維持し得るものであった。なお、実施例２において、３点曲げ応力および圧縮応力を測定する際に、熱融着性複合繊維のみから構成される編地側ではない面側を上面として測定した。また、リュックサックの肩ベルトおよび背当て部分に、実施例１および２の網地構造の素材を適用したリュックサックを作成し、１０ｋｇの錘を入れて背負った場合であっても、背負い心地が良好であった。一方、比較例１の網地構造の素材は、実施例と比較して応力が小さく、圧力に対して立体構造を維持しにくいものであった。すなわち比較例１は、表地も裏地も両方とも熱の影響を受けていない繊維を用いたことから、剛性を有さず、本発明の効果を奏しない網地構造の素材であった。 The materials of the mesh structure of Examples 1 and 2 have high stresses of both three-point bending and compression, are difficult to be compressed, maintain a good three-dimensional structure against pressure, and have excellent morphological stability. It was able to maintain breathability. In Example 2, when measuring the three-point bending stress and the compressive stress, the surface side, which is not the knitted fabric side composed of only the heat-sealing composite fiber, was measured as the upper surface. Further, even when a rucksack is prepared by applying the material of the mesh structure of Examples 1 and 2 to the shoulder belt and the backrest portion of the rucksack and a weight of 10 kg is put on the backpack, the backpack is comfortable to carry. It was good. On the other hand, the material of the net structure of Comparative Example 1 had a smaller stress than that of the example, and it was difficult to maintain the three-dimensional structure against pressure. That is, in Comparative Example 1, since both the outer material and the lining used fibers that were not affected by heat, they were materials having a net structure that did not have rigidity and did not exhibit the effects of the present invention.
Claims (3)
表地と裏地とが連結糸で連結されたダブルラッセル編地にて構成され、
前記表地と裏地との内の少なくともいずれか一方がメッシュ状体にて構成されているとともに、
前記表地と裏地との内の少なくともいずれか一方の編地を形成する糸条が、高融点ポリマーと低融点ポリマーとを有した複合型熱融着繊維であって、低融点ポリマーの溶融再固化によって、繊維形態を保った高融点ポリマーが固着された状態の繊維によって形成されていることを特徴とするリュックサック用素材。 A material used to form the shoulder belt of a rucksack and / or the part of the rucksack that hits the user's back.
It is composed of a double Russell knitted fabric in which the outer material and the lining are connected by a connecting thread.
At least one of the outer material and the lining is made of a mesh-like body, and
The thread forming the knitted fabric of at least one of the outer material and the lining is a composite heat-sealing fiber having a high melting point polymer and a low melting point polymer, and melt resolidification of the low melting point polymer. A material for rucksacks, characterized in that a high melting point polymer that retains its fiber morphology is formed by fibers in a fixed state.