JP2020132608A - Adhesive sheet - Google Patents
Adhesive sheet Download PDFInfo
- Publication number
- JP2020132608A JP2020132608A JP2019032301A JP2019032301A JP2020132608A JP 2020132608 A JP2020132608 A JP 2020132608A JP 2019032301 A JP2019032301 A JP 2019032301A JP 2019032301 A JP2019032301 A JP 2019032301A JP 2020132608 A JP2020132608 A JP 2020132608A
- Authority
- JP
- Japan
- Prior art keywords
- particles
- adhesive
- nanosilk
- adhesive sheet
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、肌表面に対して着脱可能な粘着シート、特に粘着性エラストマーシート、親水性高分子ゲルに関する。 The present invention relates to an adhesive sheet that can be attached to and detached from the skin surface, particularly an adhesive elastomer sheet and a hydrophilic polymer gel.
加齢などが原因による肌のカサつきや、老廃物の蓄積によるニキビ、肌荒れなどを防止し、アンチエイジング効果を肌にもたらすための肌に貼る美容シートが開発されている。 Beauty sheets have been developed to be applied to the skin to prevent dryness of the skin due to aging, acne due to accumulation of waste products, rough skin, etc., and to bring an anti-aging effect to the skin.
しかし、従来技術によれば、有効成分が含有された領域は、美容シートを肌に貼って固定するための粘着部とは別に製造されている。そのため、美容シートの粘着部の全面積を有効成分による効果を発揮する領域として使用することができず、製品の大きさに対して有効成分面積が小さくなるという問題があった。 However, according to the prior art, the region containing the active ingredient is manufactured separately from the adhesive portion for attaching and fixing the beauty sheet to the skin. Therefore, the entire area of the adhesive portion of the beauty sheet cannot be used as an area where the effect of the active ingredient is exerted, and there is a problem that the area of the active ingredient becomes smaller than the size of the product.
また、従来の美容シートに含まれる有効成分は、不織布などにあらかじめ染み込ませてあり、有効成分が肌と接触する部分には粘着性がないものも多い。有効成分含有量を増量するために、このような不織布部分の面積を大きくすると、有効成分が肌に充分密着しない場合も生ずる。そうすると、十分な美容シートから肌への有効成分の受け渡しが実現できないという問題もあった。 In addition, the active ingredient contained in the conventional beauty sheet is pre-impregnated into a non-woven fabric or the like, and in many cases, the portion where the active ingredient comes into contact with the skin is not sticky. If the area of such a non-woven fabric portion is increased in order to increase the content of the active ingredient, the active ingredient may not sufficiently adhere to the skin. Then, there is also a problem that it is not possible to deliver the active ingredient from a sufficient beauty sheet to the skin.
そこで、上記課題を解決するための手段として本発明に係る粘着シートは、肌表面に対して着脱可能な粘着性を備え、薄板状に形成されてなる粘着性素材にナノシルク粒子、若しくはナノプラチナ粒子、又は、ナノシルク粒子及びナノプラチナ粒子が付着されてなるものを粘着剤として備えることを特徴とする。 Therefore, as a means for solving the above-mentioned problems, the adhesive sheet according to the present invention has adhesiveness that can be attached to and detached from the skin surface, and nanosilk particles or nanoplatinum particles are used as an adhesive material formed in a thin plate shape. Alternatively, the adhesive is provided with nanosilk particles and nanoplatinum particles attached thereto.
前記粘着性素材は、エラストマー若しくは親水性高分子ゲルであることが好ましい。エラストマー若しくは親水性高分子ゲルとしては、アクリル酸共重合体によって構成されてなるアクリル系粘着剤、天然ゴムを含むゴム系粘着剤、ＳＩＳ系粘着剤、シリコーンゴム等からなるシリコーン系粘着剤、ウレタン樹脂によって構成されてなるウレタン系粘着剤、粘着性を保持したエラストマー樹脂（シリコンゲル・ポリエチレンゲル・ウレタンゲル等）、粘着性を有する親水性高分子ゲルのうちから選択された１または２以上の粘着剤、エラストマー樹脂、親水性高分子ゲルを用いることができる。 The adhesive material is preferably an elastomer or a hydrophilic polymer gel. Examples of the elastomer or hydrophilic polymer gel include an acrylic pressure-sensitive adhesive composed of an acrylic acid copolymer, a rubber-based pressure-sensitive adhesive containing natural rubber, a SIS-based pressure-sensitive adhesive, a silicone-based pressure-sensitive adhesive made of silicone rubber, and urethane. One or more selected from urethane-based adhesives composed of resins, elastomer resins with adhesiveness (silicon gel, polyethylene gel, urethane gel, etc.), and hydrophilic polymer gels with adhesiveness. Adhesives, elastomer resins, and hydrophilic polymer gels can be used.
また、前記粘着性素材に前記ナノシルク粒子が付着されている場合においては、前記ナノシルク粒子の粒子径が１００〜１０００ｎｍであることが好ましい。 When the nanosilk particles are attached to the adhesive material, the particle size of the nanosilk particles is preferably 100 to 1000 nm.
前記粘着性素材に前記ナノシルク粒子が付着されている場合においては、前記ナノシルク粒子は、前記粘着性素材への練り込みにより付着されてなることが好ましい。また、前記粘着性素材に前記ナノプラチナ粒子が付着されている場合においては、前記ナノプラチナ粒子は、前記粘着性素材への練り込みにより付着されてなることが好ましい。 When the nanosilk particles are attached to the adhesive material, it is preferable that the nanosilk particles are attached by kneading into the adhesive material. When the nano-platinum particles are attached to the adhesive material, it is preferable that the nano-platinum particles are attached by kneading into the adhesive material.
前記粘着剤はシート状の基材に貼着されてなることが好ましく、また、前記粘着剤は、前記基材の両面に貼着されてなるものであっても好ましい。 The pressure-sensitive adhesive is preferably adhered to a sheet-shaped base material, and the pressure-sensitive adhesive may be adhered to both sides of the base material.
前記基材には、ポリプロピレン樹脂、ポリエチレン樹脂、ポリエチレンテレフタレート樹脂、ポリ塩化ビニル樹脂、シリコーン、天然繊維、合成繊維、Ｆａｂｒｉｃ織布、及び紙から選択される１または２以上の素材によって構成されたものを用いることができる。 The base material is composed of one or more materials selected from polypropylene resin, polyethylene resin, polyethylene terephthalate resin, polyvinyl chloride resin, silicone, natural fiber, synthetic fiber, Fabric woven fabric, and paper. Can be used.
本発明に係る粘着シートは、スポーツテープ、顔や体の肌表面に貼る美容シート、二重まぶた形成用テープ、シミ隠しテープ、顔のたるみなどをリフトアップするためのリフトアップテープ、フットケア用テープ等に使用することができる。また、傷テープ、医療用テープの粘着部を本発明に係る粘着シートによって構成しても好ましい。 The adhesive sheet according to the present invention is a sports tape, a beauty sheet to be attached to the skin surface of the face or body, a double eyelid forming tape, a stain concealing tape, a lift-up tape for lifting up sagging face, and a foot care product. It can be used for tapes and the like. Further, it is also preferable that the adhesive portion of the scratch tape or the medical tape is composed of the adhesive sheet according to the present invention.
本発明に係る粘着シートは、人体の肌表面に貼り付けることにより、粘着性素材に付着してなるナノシルク粒子及び／又はナノプラチナ粒子が有する抗酸化能により粘着シートの粘着部全体から肌へのアンチエイジング効果を発揮させることができる。 The adhesive sheet according to the present invention is attached to the skin surface of the human body to attach the nanosilk particles and / or nanoplatinum particles to the adhesive material, and the antioxidant ability of the adhesive sheet is applied to the entire adhesive portion of the adhesive sheet to the skin. It can exert an anti-aging effect.
また、粘着性素材にナノシルク粒子を付着させることにより、粘着シートの粘着部全体から肌への保湿効果・抗菌効果を発揮させることができる。前記アンチエイジング効果と保湿効果は、それぞれによっても肌弾力を向上させる効果もあるだけでなく、前記アンチエイジング効果と保湿効果とを合わせて発揮することによって、肌弾力の向上効果をより強く発揮させることができる。 Further, by adhering the nanosilk particles to the adhesive material, it is possible to exert a moisturizing effect and an antibacterial effect on the skin from the entire adhesive portion of the adhesive sheet. The anti-aging effect and the moisturizing effect not only have the effect of improving the skin elasticity, but also exert the skin elasticity improving effect more strongly by exerting the anti-aging effect and the moisturizing effect together. be able to.
さらに、粘着性素材にナノシルク粒子及びナノプラチナ粒子の両方が付着されてなることによって、粘着シートの粘着部全体から、ナノプラチナ粒子がナノシルク粒子自体の酸化による劣化を防止する効果を発揮させることができる。これにより、ナノシルク粒子のみが粘着性素材に付着されてなる粘着シートよりも上記抗酸化能や保湿効果の持続時間をより長く保つことができる粘着シートを提供することができる。 Further, by adhering both the nanosilk particles and the nanoplatinum particles to the adhesive material, the nanoplatinum particles can exert the effect of preventing deterioration due to oxidation of the nanosilk particles themselves from the entire adhesive portion of the adhesive sheet. it can. This makes it possible to provide an adhesive sheet capable of maintaining the duration of the antioxidant ability and the moisturizing effect longer than that of the adhesive sheet in which only nanosilk particles are attached to the adhesive material.
また、ナノシルク粒子の粒子径が１００〜１０００ｎｍであることによって、シルク由来の保湿機能を効率的に発揮し得る粘着シートを提供することができる。 Further, when the particle size of the nanosilk particles is 100 to 1000 nm, it is possible to provide an adhesive sheet capable of efficiently exerting the moisturizing function derived from silk.
ナノシルク粒子及びナノプラチナ粒子が粘着性素材に練り込まれてなることにより、粘着性素材に付着されたナノ粒子の脱落を抑制できるだけでなく、粘着性素材の減損によっても粘着性素材内部から新たなナノ粒子を粘着性素材表面に露出させることができるため、上記ナノシルク粒子やナノプラチナ粒子の有する効果を長期にわたって維持させることができる。 By kneading the nanoparticles and nanoplatinum particles into the adhesive material, not only can the nanoparticles adhering to the adhesive material be suppressed from falling off, but also the deterioration of the adhesive material causes new new particles from inside the adhesive material. Since the nanoparticles can be exposed on the surface of the adhesive material, the effects of the nanosilk particles and nanoplatinum particles can be maintained for a long period of time.
本発明に係る粘着シートは、粘着性素材に有効成分であるナノシルク粒子やナノプラチナ粒子が非常に微細な粒子として直接付着しているので、シートの粘着性を犠牲にすることない。そして、ナノシルク粒子やナノプラチナ粒子が付着された粘着性素材全体が肌に密着するので、粘着シート全体で抗酸化能等の上記効能を肌に及ぼすことができる。 In the adhesive sheet according to the present invention, nanosilk particles and nanoplatinum particles, which are active ingredients, are directly attached to the adhesive material as very fine particles, so that the adhesiveness of the sheet is not sacrificed. Then, since the entire adhesive material to which the nanosilk particles and nanoplatinum particles are attached adheres to the skin, the above-mentioned effects such as antioxidant ability can be exerted on the skin by the entire adhesive sheet.
以下、本発明に係る実施の形態を、図を参照しながら詳しく説明する。なお、本明細書及び図面において、実質的に同一の機能構成を有する構成要素については、同一の符号を付することにより重複説明を省略する。 Hereinafter, embodiments according to the present invention will be described in detail with reference to the drawings. In the present specification and the drawings, components having substantially the same functional configuration are designated by the same reference numerals, so that duplicate description will be omitted.
図１は、第一の実施形態に係る粘着シート１の概要を示す図である。本実施形態に係る粘着シート１は図４に示すように目の下の肌５に貼れるように、長尺方向が３ｃｍ程度、短尺方向が１ｃｍ程度の大きさに形成されてなる。但し、粘着シート１は、対象とする体の部位に応じて形状や大きさを任意のものとすることができる。
FIG. 1 is a diagram showing an outline of the pressure-sensitive
本実施の形態に係る粘着シート１は、シート状の基材２と、基材２の表面に貼着されてなる薄板状のエラストマー３によって構成されてなる。エラストマー３は、肌表面に対して着脱可能な粘着性を備えるので、粘着シート１を肌に貼り付けた後、一定時間経過後に容易に肌から剥がすことができる。
The pressure-sensitive
本実施の形態において、エラストマー３には、図１（ｂ）の拡大円に示すように、ナノシルク粒子Ｓ及びナノプラチナ粒子Ｐが練り込まれることによってこれらのナノ粒子をエラストマー３に付着させてなる。
In the present embodiment, as shown in the enlarged circle of FIG. 1 (b), the nanoparticles S and the nanoparticles P are kneaded into the
ナノシルク粒子Ｓは、粒径１００〜１０００ｎｍの粒子であることが好ましい。ナノシルク粒子Ｓを、粒子径数百ｎｍとすることで、シルク中に含まれるセリシン、フィブロイン、またはグリシンという機能性成分を分解させずに残存させることができるからである。特に、生体適合性が高く、通気機能と保湿機能を兼ね備えたフィブロイン、高い保湿機能、抗酸化機能、抗菌機能、紫外線吸収作用を備えたセリシンを分解させずに残存させることにより、アクリル酸共重合体によって構成されてなるアクリル系粘着剤、天然ゴムを含むゴム系粘着剤、ＳＩＳ系粘着剤、シリコーンゴム等からなるシリコーン系粘着剤、ウレタン樹脂によって構成されてなるウレタン系粘着剤、粘着性を保持したエラストマー樹脂のうちから選択された１または２以上の粘着剤、粘着性を保持したエラストマー樹脂などによって構成されるエラストマー３にシルク由来の特性を付加させることが可能となる。
The nanosilk particles S are preferably particles having a particle size of 100 to 1000 nm. By setting the nanosilk particles S to have a particle diameter of several hundred nm, the functional components such as sericin, fibroin, and glycine contained in the silk can be left without being decomposed. In particular, fibroin, which has high biocompatibility and has both aeration function and moisturizing function, and sericin, which has high moisturizing function, antioxidant function, antibacterial function, and ultraviolet absorbing function, are retained without being decomposed, so that the same weight of acrylic acid is used. Acrylic adhesive composed of coalescence, rubber adhesive containing natural rubber, SIS adhesive, silicone adhesive composed of silicone rubber, urethane adhesive composed of urethane resin, adhesiveness It is possible to add silk-derived properties to the
また、ナノプラチナ粒子Ｐは、粒径１〜５０ｎｍであって、有機物の保護膜で覆われていない状態のナノプラチナ粒子であることが好ましい。さらにナノプラチナ粒子Ｐは、１〜５ｎｍの粒径であるのがより好ましい。この範囲であると、ナノプラチナ粒子の抗酸化作用、除菌作用等の効果を十分発現させ、エラストマー３に付着したナノシルク粒子Ｓの酸化による劣化を抑制することができるからである。以下、ナノシルク粒子Ｓ及びナノプラチナ粒子Ｐを包括してナノ粒子ということがある。
Further, the nanoplatinum particles P are preferably nanoplatinum particles having a particle size of 1 to 50 nm and not covered with a protective film of an organic substance. Further, the nanoplatinum particles P preferably have a particle size of 1 to 5 nm. This is because within this range, the effects such as the antioxidant action and the sterilizing action of the nanoplatinum particles can be sufficiently exhibited, and the deterioration of the nanosilk particles S attached to the
＜レーザー微細化によるナノ粒子＞
上記のようなナノ粒子は、シルクもしくはプラチナを水中に浸漬した状態でレーザー光照射により微細化し、そのまま水中に分散させたナノ粒子水（ナノ粒子分散水）の状態で保存しておくことが望ましい。ナノ粒子の凝集を抑制することができるからである。
<Nanoparticles by laser miniaturization>
It is desirable that the above nanoparticles are made finer by irradiating laser light with silk or platinum immersed in water, and then stored in the state of nanoparticle water (nanoparticle dispersed water) dispersed in water as it is. .. This is because the aggregation of nanoparticles can be suppressed.
＜ナノ粒子分散水の製造方法＞
このようなナノ粒子分散水は、以下のような方法によって製造される。すなわち、ナノ粒子化しようとするシルク原料もしくはプラチナ原料を溶媒（本実施形態では水）の中に浸漬した状態で、プラチナ原料もしくはシルク原料をターゲットとして、レーザー光源によるレーザー光照射と、超音波振動子による超音波照射とを同時に行う。ここで、シルク原料は、シルク片若しくは粒状シルクを用いることが好ましい。また、プラチナ原料は、板状のプラチナ板若しくは粒状プラチナを用いることが好ましい。
<Manufacturing method of nanoparticle dispersed water>
Such nanoparticle dispersed water is produced by the following method. That is, in a state where the silk raw material or the platinum raw material to be made into nanoparticles is immersed in a solvent (water in this embodiment), the platinum raw material or the silk raw material is targeted, laser light irradiation by a laser light source, and ultrasonic vibration. Ultrasonic irradiation by the child is performed at the same time. Here, it is preferable to use silk pieces or granular silk as the silk raw material. Further, as the platinum raw material, it is preferable to use a plate-shaped platinum plate or granular platinum.
シルク原料に粒状シルクを用いる場合には、粒状シルクの粒径が１〜１００μｍ程度のものが好ましいが、ナノシルク粒子Ｓよりも大きなものであればその大きさは限定しない。また、シルク原料にシルク片を用いる場合には、数ｍｍ角の布状片を用いることができる。 When granular silk is used as the silk raw material, the particle size of the granular silk is preferably about 1 to 100 μm, but the size is not limited as long as it is larger than the nanosilk particles S. When a silk piece is used as a silk raw material, a cloth-like piece of several mm square can be used.
プラチナ原料に粒状プラチナを用いる場合には、粒状プラチナの粒径が１〜１００μｍ程度のものが好ましいが、ナノプラチナ粒子よりも大きなものであればその大きさは限定しない。プラチナ原料にプラチナ板を用いる場合には、板の厚みが０．５ｍｍ〜２．０ｍｍ程度のものが好ましい。以下、本実施の形態においては、プラチナ原料に前記プラチナ板を用いるものとする。 When granular platinum is used as the platinum raw material, the particle size of the granular platinum is preferably about 1 to 100 μm, but the size is not limited as long as it is larger than the nanoplatinum particles. When a platinum plate is used as the platinum raw material, the thickness of the plate is preferably about 0.5 mm to 2.0 mm. Hereinafter, in the present embodiment, the platinum plate will be used as the platinum raw material.
これにより、水中に浸漬されて分散状態のシルク原料若しくはプラチナ原料に対してレーザーを照射することによって微細化してナノ粒子化させるとともに、微細化したナノ粒子の凝集を超音波照射で抑制し、水中にナノ粒子が分散して浮遊した状態（ナノ粒子分散水）を生成することができる。このような水中におけるレーザーを用いたナノ粒子化は、液相レーザアブレーションの原理に基づく。シルク原料をナノ粒子化して、ナノシルク粒子Ｓを水中に分散させたものをナノシルク粒子分散水といい、プラチナ原料をナノ粒子化して、プラチナナノ粒子Ｐを水中に分散させたものをナノプラチナ粒子分散水という。 As a result, the silk raw material or the platinum raw material that is immersed in water and dispersed is irradiated with a laser to make it finer and nanoparticles, and the aggregation of the finer nanoparticles is suppressed by ultrasonic irradiation in water. It is possible to generate a floating state (nanoparticle-dispersed water) in which nanoparticles are dispersed. Such laser-based nanoparticle formation in water is based on the principle of liquid-phase laser ablation. Nanoparticles of silk raw material and dispersion of nanosilk particles S in water are called nanosilk particle dispersion water, and those of platinum raw material made into nanoparticles and platinum nanoparticles P dispersed in water are nanoplatinum particle dispersion. It's called water.
例えばナノシルク粒子分散水とナノプラチナ粒子分散水とを混合したナノ粒子分散水に、エラストマー３を配合させたあと、乾燥させることによって、エラストマー３の表面にナノシルク粒子Ｓ及びナノプラチナ粒子Ｐが付着した構造を実現することができる。粘着シート１は、図４に示すように、肌に貼り付けることができる。図１中の拡大円は、エラストマー３の内部及び表面に付着したナノシルク粒子Ｓ及びナノプラチナ粒子Ｐの様子を拡大して示す概略図である。
For example, the nanosilk particles S and the nanoplatinum particles P adhered to the surface of the
また、ナノシルク粒子Ｓ及びナノプラチナ粒子Ｐの付着は、ナノプラチナ粒子分散水若しくはナノシルク粒子分散水、又はナノプラチナ粒子分散水とナノシルク粒子分散水との混合液を、エラストマー３への練り込みによって行われても好ましい。また、あらかじめナノ粒子分散水をスプレー法などによりシリカに担持させることによって乾燥状態として取得した粒子を、エラストマー３へ練り込んでおくこととしてもよい。粒子が練り込まれたエラストマー３は、その後成形されて薄板状に形成される。ナノプラチナ粒子、ナノシルク粒子をシリカに担持させ、エラストマーシートの原料に混錬し射出成型・押出成形・圧縮成形などで薄板状に成型することも可能となる。
Further, the nanosilk particles S and the nanoplatinum particles P are attached by kneading nanoplatinum particle-dispersed water or nanosilk particle-dispersed water, or a mixed solution of nanoplatinum particle-dispersed water and nanosilk particle-dispersed water into the
ナノ粒子がエラストマー３に練り込まれてなることにより、エラストマー３に付着されたナノ粒子の脱落を抑制できるだけでなく、エラストマー３表面の減損によってもエラストマー３内部から新たなナノ粒子をエラストマー３表面に露出させることができるため、ナノシルク粒子Ｓやナノプラチナ粒子Ｐの有する抗酸化能や保湿効果を、長期にわたって維持させることができる。
By kneading the nanoparticles into the
以下にナノプラチナ粒子Ｐが発揮しうる抗酸化能について示す。検証試料としてナノプラチナ粒子Ｐ３０ｍｇを１５ｍＬの蒸留水中に分散させたナノプラチナ粒子Ｐ分散水を用意した。比較試料として蒸留水１５ｍＬ、及びクエン酸などのアミノ酸などによって粒子の周囲がコーティングされコロイド状に形成されたプラチナナノコロイド３０ｍｇを１５ｍＬの蒸留水中に分散させたプラチナナノコロイド分散水を用意した。以下、上記検証試料及び比較試料を包括して試料液という。ここで、ナノプラチナ粒子Ｐは、アミノ酸などによって粒子がコーティングされていないプラチナ単独の粒子である。 The antioxidant capacity that the nanoplatinum particles P can exert is shown below. As a verification sample, nanoplatinum particle P-dispersed water in which 30 mg of nanoplatinum particles P was dispersed in 15 mL of distilled water was prepared. As comparative samples, 15 mL of distilled water and 30 mg of platinum nanocolloids formed in a colloidal form by coating the periphery of particles with amino acids such as citric acid were dispersed in 15 mL of distilled water to prepare platinum nanocolloid-dispersed water. Hereinafter, the above-mentioned verification sample and comparative sample are collectively referred to as a sample solution. Here, the nano-platinum particles P are platinum-only particles whose particles are not coated with amino acids or the like.
〔測定方法〕
フェントン法に従って、試料液３０μＬ、ＦｅＳＯ４水溶液（０．２ｍＭ）３７．５μＬ、ＤＭＰＯ（１／１０希釈溶液）２０μＬ、及び過酸化水素水溶液（１ｍＭ）７５μＬをサンプル管に順次添加した。サンプル管への添加後３０秒経過後に、毛細管に試料液をサンプリングした。次に、サンプリングした毛細管５ｍｍφのＥＳＲ試料管に入れ、電子スピン共鳴（ＥＳＲ）装置（日本電子製 ＪＥＳ ＦＡ２００型）を用いて試料液中のDMPO-OHラジカルの電子スピン共鳴を測定した。DMPO-OHラジカルの電子スピン共鳴が蒸留水の場合と比較して減少するほど活性酸素消去能が高く（表２参照）、抗酸化能が高いと判断できる。電子スピン共鳴の測定条件は以下のとおりである。
〔Measuring method〕
According to the Fenton method, 30 μL of the sample solution, 37.5 μL of the FeSO4 aqueous solution (0.2 mM), 20 μL of the DMPO (1/10 diluted solution), and 75 μL of the hydrogen peroxide aqueous solution (1 mM) were sequentially added to the sample tube. Thirty seconds after the addition to the sample tube, the sample solution was sampled in the capillary tube. Next, the sampled capillary tube was placed in an ESR sample tube having a diameter of 5 mm, and the electron spin resonance of DMPO-OH radicals in the sample solution was measured using an electron spin resonance (ESR) device (JES FA200 type manufactured by JEOL Ltd.). It can be judged that the more the electron spin resonance of the DMPO-OH radical decreases as compared with the case of distilled water, the higher the active oxygen scavenging ability (see Table 2) and the higher the antioxidant ability. The measurement conditions for electron spin resonance are as follows.
測定結果として、蒸留水及びナノプラチナ粒子Ｐ分散水のＥＳＲスペクトル変化を図５に示す。また、蒸留水及びプラチナナノコロイド分散水のＥＳＲスペクトル変化を図６に示す。そして、図５及び図６のスペクトル図からそれぞれ低磁場側のＭｎマーカーとDMPO-OHラジカルの低磁場側から２番目のピーク（334.5磁場/T付近のピーク）面積の比をDMPO-OHの相対生成量として表２に示した。 As a measurement result, changes in the ESR spectrum of distilled water and nanoplatinum particle P dispersed water are shown in FIG. In addition, the ESR spectral changes of distilled water and platinum nanocolloidally dispersed water are shown in FIG. Then, from the spectrum diagrams of FIGS. 5 and 6, the ratio of the Mn marker on the low magnetic field side and the second peak (peak near 334.5 magnetic field / T) area of the DMPO-OH radical from the low magnetic field side is the relative DMPO-OH. Table 2 shows the amount of production.
図５によれば、蒸留水のＥＳＲスペクトル（破線）には明確なDMPO-OHラジカルの電子スピン共鳴に基づくピークが現れている。この蒸留水から得られた相対生成量は１．９１０であった。これに対して、ナノプラチナ粒子Ｐ分散水のＥＳＲスペクトル（実線）はほとんど平坦であり、相対生成量を計量すると０．００４という非常に小さい値を示すことが分かった。 According to FIG. 5, a clear peak based on electron spin resonance of DMPO-OH radical appears in the ESR spectrum (broken line) of distilled water. The relative production amount obtained from this distilled water was 1.910. On the other hand, it was found that the ESR spectrum (solid line) of the nano-platinum particle P dispersed water was almost flat, and when the relative production amount was measured, it showed a very small value of 0.004.
一方、図６によれば、蒸留水のＥＳＲスペクトル（破線）には図５と同じく明確なDMPO-OHラジカルの電子スピン共鳴に基づくピークが見られる。これに対して、プラチナナノコロイド分散水のＥＳＲスペクトルにおいてもDMPO-OHラジカルの電子スピン共鳴に基づくピークが現れた。ただし、プラチナナノコロイド分散水のＥＳＲスペクトルに現れたDMPO-OHラジカルの電子スピン共鳴に基づくピークは蒸留水のＥＳＲスペクトルに見られるピークよりも小さく、相対生成量としては１．４００であった。 On the other hand, according to FIG. 6, the ESR spectrum (broken line) of distilled water shows a clear peak based on electron spin resonance of DMPO-OH radical as in FIG. On the other hand, a peak based on electron spin resonance of DMPO-OH radical appeared in the ESR spectrum of platinum nanocolloidally dispersed water. However, the peak based on the electron spin resonance of DMPO-OH radicals appearing in the ESR spectrum of platinum nanocolloidally dispersed water was smaller than the peak seen in the ESR spectrum of distilled water, and the relative production amount was 1.400.
また表２に示した結果から、蒸留水のDMPO-OHの相対生成量と比較して、プラチナナノコロイドは相対生成量が約２７％の減少（（１．９１０−１．４００）／１．９１０×１００）であったのに対して、ナノプラチナ粒子Ｐでは約９８％減少（（１．９１０−０．００４）／１．９１０×１００）させることができることがわかった。このようにプラチナナノコロイドを使用しても一定の抗酸化能が発揮していることがわかるが、アミノ酸などによって粒子の周囲がコーティングされていないナノプラチナ粒子Ｐを用いると、より大きな抗酸化能を発揮することが示された。 In addition, from the results shown in Table 2, the relative production amount of platinum nanocolloid was reduced by about 27% compared to the relative production amount of DMPO-OH in distilled water ((1.910-1.400) / 1. It was found that the nanoplatinum particles P could be reduced by about 98% ((1.910-0.004) /1.910 × 100), whereas it was 910 × 100). In this way, it can be seen that a certain level of antioxidant capacity is exhibited even when platinum nanocolloids are used, but when nanoplatinum particles P whose surroundings are not coated with amino acids or the like are used, a larger antioxidant capacity is exhibited. It was shown to exert.
粘着シート１のエラストマー３の表面に付着されたナノプラチナ粒子Ｐは、粘着シート１が貼り付けられた肌表面に対して上記抗酸化能を発揮することができる。また、ナノシルク粒子Ｓもナノプラチナ粒子Ｐと同様に、粘着シート１が貼り付けられた肌表面に対して上記抗酸化能を発揮することができる。
The nanoplatinum particles P attached to the surface of the
図２は、粘着シート１の第二の実施形態の概要を示す図である。本実施の形態においては、エラストマー３が基材２の両面に貼着されてなる。本実施の形態においても、図１（ｂ）の拡大円に示す場合と同様に、エラストマー３の内部及び表面にナノシルク粒子Ｓ及びナノプラチナ粒子Ｐが練り込みによって付着されてなる。
FIG. 2 is a diagram showing an outline of a second embodiment of the
図３は、粘着シート１の第三の実施形態の概要を示す図である。本実施の形態においては、エラストマー３が単独で粘着シート１を構成してなる。本実施の形態においても、図１（ｂ）の拡大円に示す場合と同様に、エラストマー３の内部及び表面にナノシルク粒子Ｓ及びナノプラチナ粒子Ｐが練り込みによって付着されてなる。
FIG. 3 is a diagram showing an outline of a third embodiment of the
第二若しくは第三の実施形態における粘着シート１は、例えば二重まぶた形成シートなど、肌と肌の間に挿し入れて、肌の形状を補正するような用途に使用されるシートとして用いることが好ましい。
The
図４には、第一の実施の形態に係る粘着シート１の使用例を示す。図４において、使用者４は、目の下の肌５に粘着シート１を貼っている。粘着シート１のエラストマー３にはナノシルク粒子Ｓやナノプラチナ粒子Ｐが練り込まれているため、粘着シート１が貼られている部分の肌にアンチエイジング効果や保湿効果を与えることができる。また、エラストマー３には他の美容成分を含有させてもよい。粘着シート１の使用後は、肌から粘着シート１を容易に剥がすことができる。また、エラストマー３を親水性高分子ゲルに代えても同様の効果を備える粘着シート１を実現することができる。
FIG. 4 shows an example of using the
１ 粘着シート
２ 基材
３ エラストマー、親水性高分子ゲル
1
Claims (7)
ことを特徴とする粘着シート。 Adhesives are made of nanosilk particles, nanoplatinum particles, or nanosilk particles and nanoplatinum particles attached to an adhesive material that has adhesiveness that can be attached to and detached from the skin surface and is formed in the shape of a thin plate. Adhesive sheet characterized by being prepared as.
ことを特徴とする請求項１に記載の粘着シート。 The pressure-sensitive adhesive sheet according to claim 1, wherein the nano-silk particles are attached to the adhesive material, and the particle size of the nano-silk particles is 100 to 1000 nm.
ことを特徴とする請求項１または２に記載の粘着シート。 The adhesive according to claim 1 or 2, wherein the nanosilk particles are attached to the adhesive material, and the nanosilk particles are attached by kneading into the adhesive material. Sheet.
ことを特徴とする粘着シート。 An adhesive sheet having adhesiveness that can be attached to and detached from the skin surface, and having nanoplatinum particles attached to an adhesive material formed in a thin plate shape as an adhesive.
ことを特徴とする請求項４に記載の粘着シート。 The pressure-sensitive adhesive sheet according to claim 4, wherein the nano-platinum particles are adhered by kneading into the pressure-sensitive adhesive material.
ことを特徴とする請求項１〜５のいずれか１つに記載の粘着シート。 The pressure-sensitive adhesive sheet according to any one of claims 1 to 5, wherein the pressure-sensitive adhesive is adhered to a sheet-like base material.
ことを特徴とする請求項６に記載の粘着シート。
The pressure-sensitive adhesive sheet according to claim 6, wherein the pressure-sensitive adhesive is adhered to both surfaces of the base material.