JP2020117837A - 合成繊維用処理剤、合成繊維の処理方法及び合成繊維 - Google Patents
合成繊維用処理剤、合成繊維の処理方法及び合成繊維 Download PDFInfo
- Publication number
- JP2020117837A JP2020117837A JP2019011410A JP2019011410A JP2020117837A JP 2020117837 A JP2020117837 A JP 2020117837A JP 2019011410 A JP2019011410 A JP 2019011410A JP 2019011410 A JP2019011410 A JP 2019011410A JP 2020117837 A JP2020117837 A JP 2020117837A
- Authority
- JP
- Japan
- Prior art keywords
- amide
- modified silicone
- group
- agent
- chemical formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
上記合成繊維用処理剤において、前記アミド変性シリコーンは、化1中のX1、及びX2がメチル基、又は水酸基であり、且つX1、及びX2のうち少なくとも一つは水酸基である場合のものであることが好ましい。
上記合成繊維用処理剤において、前記アミド変性シリコーンは、化1中のpが15〜700の整数であり、R1がメチル基である場合のものであることが好ましい。
上記合成繊維用処理剤において、前記平滑剤と前記アミド変性シリコーンの含有割合の合計を100質量%とすると、前記平滑剤を80〜99.9質量%、及び前記アミド変性シリコーンを0.1〜20質量%の割合で含有することが好ましい。
上記課題を解決する合成繊維の処理方法は、上記合成繊維用処理剤を、合成繊維100質量%に対し0.1〜10質量%の割合となるよう付着させる。
本発明の処理剤に供する特定のアミド変性シリコーンは下記の化3で示されるものである。
具体的に化3で示されるアミド変性シリコーンとしては、側鎖に3−脂肪酸アミドプロピル基、N−(2−脂肪酸アミドエチル)−3−アミノプロピル基を持った両末端水酸基変性アミド変性シリコーン等が挙げられるが、なかでも側鎖にN−(2−脂肪酸アミドエチル)−3−アミノプロピル基を持った両末端水酸基変性アミド変性シリコーンがより好ましい。
本発明の処理剤に供する平滑剤は、化3で示されるアミド変性シリコーン以外のシリコーンオイル、鉱物油、脂肪酸エステル及び液状ポリオレフィンから選ばれる一つ又は二つ以上からなり、且つ25℃における動粘度が5〜50mm2/sのものである。
なかでも、平滑剤としては、ポリジメチルシロキサン等のシリコーンオイルを含有するものが好ましい。かかる平滑剤としては、25℃における動粘度が5〜50mm2/sのものを用いる。本発明において動粘度は、JIS−K2283(石油製品動粘度試験方法)に記載されたキャノンフェンスケ粘度計を用いた方法により求められる値である。
本発明の処理剤には、本発明の効果を損なわない範囲内にて、必要に応じその他の成分を併用することもできる。かかるその他の成分としては、例えば、帯電防止剤、膠着防止剤、つなぎ剤、濡れ性向上剤、紫外線吸収剤、酸化防止剤、防腐剤等、合成繊維用処理剤として公知の成分が挙げられる。
本発明の処理剤は、化3で示されるアミド変性シリコーンを0.08〜20質量%の割合で含有することが好ましく、0.09〜5.0質量%の割合で含有することがより好ましい。本発明の処理剤は、平滑剤を64〜99.9質量%の割合で含有することが好ましく、85.5〜99.9質量%の割合で含有することがより好ましい。
プレポリマの鎖伸長に用いる前記のジオールとしては、エチレングリコール、1,3−プロパンジオール、4−ブタンジオール、ネオペンチルグリコール、1,2−プロピレングリコール、1,4−シクロヘキサンジメタノ一ル、1,4−シクロヘキサンジオール、1,4−ビス(β−ヒドロキシエトキシ)ベンゼン、ビス(β−ヒドロキシエチル)テレフタレート及びパラキシリレンジオール等が挙げられる。以上、ポリウレタン系弾性繊維の原料となる長鎖の重合体について説明したが、本発明において、かかる長鎖の重合体の重合方法は特に制限されない。
また、化3で示されるアミド変性シリコーンとして、pが15〜700の整数であり、R1がメチル基であるものを用いた場合には、加工時におけるスカム発生を抑制することによる加工品位を向上させる効果が大きくなる。
2成分以上で構成される場合には、それらを表1に記載の割合(質量比)で混合して、表1に記載の平滑剤を調製した。
S10:25℃における動粘度が10mm2/sであるポリジメチルシロキサン
S20:25℃における動粘度が20mm2/sであるポリジメチルシロキサン
S30:25℃における動粘度が30mm2/sであるポリジメチルシロキサン
S50:25℃における動粘度が50mm2/sであるポリジメチルシロキサン
M6:25℃における動粘度が6mm2/sである鉱物油
M10:25℃における動粘度が10mm2/sである鉱物油
M15:25℃における動粘度が15mm2/sである鉱物油
M21:25℃における動粘度が21mm2/sである鉱物油
M40:25℃における動粘度が40mm2/sである鉱物油
試験区分2(アミド変性シリコーンの合成)
・アミド変性シリコーン(AS−1)の合成
シロキサン部分の繰り返し単位が40である、両末端水酸基変性ポリジメチルシロキサン27000g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206g、水酸化カリウム40%水溶液3.3gをガラス製の反応容器内に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った。その後、水32gを添加し、減圧で脱水操作を行い、セライトを用いて濾過を行い、アミノ変性シリコーン27000gを得た。得られたアミノ変性シリコーン27000gにオレイン酸2814gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(AS−1)27000gを得た。
化3に示す一般式のp、qの数値に応じて、シロキサン部分の繰り返し単位を変更し、両末端水酸基変性ポリジメチルシロキサンに代替、及び併用して使用する他、X3の構造に応じたアミン、脂肪酸を使用し、アミド変性シリコーン(AS−1)と同様に合成を行った。
N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミンを3−(ジメトキシメチルシリル)プロピルアミンに替えて、アミド変性シリコーン(AS−1)と同様に合成を行った。
シロキサン部分の繰り返し単位が40である、両末端シラノール変性ポリジメチルシロキサン30543g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン1032g、水酸化カリウム40%水溶液4.0gをガラス製の反応容器内に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った。その後、水135gを添加し、減圧で脱水操作を行なった後、ジメチルジメトキシシラン60gを添加、撹拌しつつ90℃で2時間反応を行い、減圧で脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン31000gを得た。得られたアミノ変性シリコーン31000gにテレフタル酸85gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(AS−12)31000gを得た。
ヘキサメチルジシロキサン162、水18g、水酸化カリウム40%水溶液10.3g、オクタメチルシクロテトラシロキサン13320g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン(Ras−1)13000gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液0.4g、ジメチルジメトキシシラン361g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン(Ras−2)500gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液5.2g、オクタメチルシクロテトラシロキサン5932g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン413gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン6400gを得た。得られたアミノ変性シリコーン6400gにアジピン酸291gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−3)6655gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液2.4g、オクタメチルシクロテトラシロキサン2225g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン413gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン2700gを得た。得られたアミノ変性シリコーン2700gにトリメリット酸419gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−4)3082gを得た。
メチルハイドロジェンポリジメチルシロキサン(メチルハイドロジェンシロキサン単位2個、ジメチルシロキサン単位30個、トリメチルシロキサン単位1個、トリメチルシリル単位1 個から構成されたもの)2505g、ペンタノイルポリアルキレングリコールモノアリルエーテル( ポリアルキレングリコールがエチレンオキシ単位3 個とプロピレンオキシ単位3 個とがランダム結合したもの)897g、触媒として塩化白金6 水和物0.1g及びトルエン2000mlを反応容器に仕込み、反応系の温度を110℃に保ち、10時間付加反応を行なった。反応系からキシレンを減圧留去した後、触媒を濾別し、中間体としてポリエーテル変性シリコーンを得た。別に、3−アミノプロピルメチルジメトキシシラン490g及び水144gを反応容器に仕込み、反応系の温度を40℃に保ち、2時間重合反応を行なった後、80℃で2時間減圧脱水処理し、中間体としてアミノ基含有ポリシロキサンを得た。かくして得たポリエーテル変性シリコーン1701g及びアミノ基含有ポリシロキサン135gを反応容器に仕込み、均一に混合した後、水酸化カリウム0.1gを加えて、反応系の温度を98℃に保ち、24時間反応を行なった。反応物を酢酸で中和した後、更に無水トリメリット酸193gを加え、反応系の温度を150〜175℃として、6時間アミド化反応を行ない、アミド変性シリコーン(Ras−5)を得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液10.4g、オクタメチルシクロテトラシロキサン11123g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン11000gを得た。得られたアミノ変性シリコーン11000gにテレフタル酸160gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−6)11142gを得た。
・実施例1 表1に記載の平滑剤(L−1)99部、表2に記載のアミド変性シリコーン(AS−1)1部を、20〜35℃の範囲内の温度で均一になるまで混合して実施例1の合成繊維用処理剤を調製した。
実施例1の合成繊維用処理剤と同様にして、実施例2〜17及び比較例1〜3の合成繊維用処理剤を調製した。これらの内容を表3にまとめて示した。
AS−1〜AS−12,Ras−1〜Ras−6:表2に記載のアミノ変性シリコーン及びアミド変性シリコーン
Ras−7:粘度900mm2/s(25℃)、官能基当量2700g/molのアミドポリエーテル変性シリコーン
・試験区分4(合成繊維への合成繊維用処理剤の付着及び評価)
・合成繊維としてのポリウレタン系弾性繊維への合成繊維用処理剤の付着
ビス−(p−イソシアネートフェニル)−メタン/テトラメチレンエーテルグリコール(数平均分子量1800)=1.58/1(モル比)の混合物を常法により90℃で3時間反応させ、キャップドグリコールを得た後、このキャップドグリコールをN,N’−ジメチルアセトアミド(以下、DMAcという)で希釈した。次にエチレンジアミン及びジエチルアミンを含むDMAc溶液を前記のキャップドグリコールのDMAc溶液に加え、室温で高速攪拌装置を用いて混合し、鎖伸長させてポリマを得た。更にDMAcを加えて前記のポリマ濃度が約35%のDMAc溶液とし、このDMAc溶液に、ポリマに対して酸化チタンを4.7%、ヒンダードアミン系耐侯剤を3.0%及びヒンダードフェノール系酸化防止剤を1.2%となるように添加し、混合して均一なポリマ混合溶液とした。このポリマ混合溶液を用いて、公知のスパンデックスで用いられる乾式紡糸方法により、単糸数4本からなる44dtexの弾性糸を紡糸し、巻き取り前のオイリングローラーから各例の合成繊維用処理剤をそのままニートの状態でローラー給油した。かくしてローラー給油したものを、巻き取り速度550m/分で、長さ57mmの円筒状紙管に、巻き幅42mmを与えるトラバースガイドを介して、サーフェイスドライブの巻取機を用いて巻き取り、乾式紡糸ポリウレタン系弾性繊維のパッケージを得た。合成繊維用処理剤の付着量の調節は、オイリングローラーの回転数を調整することで行い、目標値7.0%で付着させた。
前記で得た乾式紡糸ポリウレタン系弾性繊維パッケージを下記の測定及び評価に供し、結果を表3にまとめて示した。
前記のパッケージ(1kg巻き)について、捲き幅の最大値(Wmax)と最小幅(Wmin)を計測し、双方の差(Wmax−Wmin)からバルジを求め、下記の基準で評価した。
○:バルジが4〜10mm。
×:バルジが10mm以上。
前記のパッケージ(1kg巻き)捲糸体をミニチュア整経機に10本仕立て、25℃で65%RHの雰囲気下に糸速度300m/分で1500km巻き取った。このとき、ミニチュア整経機のクシガイドでのスカムの蓄積状態を肉眼観察し、下記の基準で評価した。
○:スカムがやや付着しているが、糸の安定走行に問題はなかった。
×:スカムの付着及び蓄積が多く、糸の安定走行に大きな問題があった。
摩擦測定メーター(エイコー測器社製、SAMPLE FRICTION UNIT MODEL TB−1)を用い、二つのフリーローラー間に直径1cmで表面粗度2Sのクロムメッキ梨地ピンを配置し、このクロムメッキ梨地ピンに対し、前記のパッケージ(500g巻き)から引き出したポリウレタン系弾性繊維の接触角度が90度となるようにした。25℃で60%RHの条件下、入側で初期張力(T1)5gをかけ、100m/分の速度で走行させたときの出側の2次張力(T2)を0.1秒毎に1分間測定した。下記の数1から摩擦係数を求め、下記の基準で評価した。
△:摩擦係数が0.260以上0.300未満。
×:摩擦係数が0.300以上。
試料糸を用いて織物ストレッチ布帛を作製し、染色等の後加工を行い、その外観品位を評価した。先ず、試料糸を、カチオン可染ポリエステル糸(168dtex/48fil)でカバリング加工した。その際のカバリング機での条件を、ヨリ数=450t/m、ドラフト=3.0として得られたカバリング糸をヨコ糸用とし、またヨリ数700T/M、ドラフト=3.5として得られたカバリング糸をタテ糸用とした。次に、得られたカバリング糸をそれぞれヨコ糸、タテ糸として用い、タテ糸を5100本(荒巻整経1100本)で糊付け整経した後、レビアー織機を用いて2/1綾組織で製織した。そして製織で得られた生機を常法に従い精練加工、中間セット(185℃)、減量加工を行ない、更にカチオン染料を用いた染色加工、乾燥、仕上げ剤処理、及び180℃、布帛20m/分、セットゾーン24mの条件で仕上げセットを行った。
◎:波打ちが全くなく、手触りが滑らか。
×:波打ちが気になり、手触りにひっかかりがある。
表3の結果からも明らかなように、本発明の処理剤及び処理方法によると、合成繊維の製造において、優れた捲形状を有するパッケージを得ることができ、また後加工でのスカム発生や擦過による糸切れが少なく、結果として編地の表面が滑らかで加工品位に優れた合成繊維を得ることができるのである。
上記合成繊維用処理剤において、前記アミド変性シリコーン以外のシリコーンオイル、鉱物油、脂肪酸エステル、及び液状ポリオレフィンから選ばれる少なくとも一つを含む平滑剤を含有し、前記平滑剤の25℃における動粘度が5〜50mm2/sであることが好ましい。
上記合成繊維用処理剤において、前記平滑剤と前記アミド変性シリコーンの含有割合の合計を100質量%とすると、前記平滑剤を80〜99.9質量%、及び前記アミド変性シリコーンを0.1〜20質量%の割合で含有することが好ましい。
上記課題を解決する合成繊維の処理方法は、上記合成繊維用処理剤を、合成繊維100質量%に対し0.1〜10質量%の割合となるよう付着させる。
本発明の処理剤に供する特定のアミド変性シリコーンは下記の化3で示されるものである。
具体的に化3で示されるアミド変性シリコーンとしては、側鎖に3−脂肪酸アミドプロピル基、N−(2−脂肪酸アミドエチル)−3−アミノプロピル基を持った両末端水酸基変性アミド変性シリコーン等が挙げられるが、なかでも側鎖にN−(2−脂肪酸アミドエチル)−3−アミノプロピル基を持った両末端水酸基変性アミド変性シリコーンがより好ましい。
本発明の処理剤に供する平滑剤は、化3で示されるアミド変性シリコーン以外のシリコーンオイル、鉱物油、脂肪酸エステル及び液状ポリオレフィンから選ばれる一つ又は二つ以上からなり、且つ25℃における動粘度が5〜50mm2/sのものである。
なかでも、平滑剤としては、ポリジメチルシロキサン等のシリコーンオイルを含有するものが好ましい。かかる平滑剤としては、25℃における動粘度が5〜50mm2/sのものを用いる。本発明において動粘度は、JIS−K2283(石油製品動粘度試験方法)に記載されたキャノンフェンスケ粘度計を用いた方法により求められる値である。
本発明の処理剤には、本発明の効果を損なわない範囲内にて、必要に応じその他の成分を併用することもできる。かかるその他の成分としては、例えば、帯電防止剤、膠着防止剤、つなぎ剤、濡れ性向上剤、紫外線吸収剤、酸化防止剤、防腐剤等、合成繊維用処理剤として公知の成分が挙げられる。
本発明の処理剤は、化3で示されるアミド変性シリコーンを0.08〜20質量%の割合で含有することが好ましく、0.09〜5.0質量%の割合で含有することがより好ましい。本発明の処理剤は、平滑剤を64〜99.9質量%の割合で含有することが好ましく、85.5〜99.9質量%の割合で含有することがより好ましい。
プレポリマの鎖伸長に用いる前記のジオールとしては、エチレングリコール、1,3−プロパンジオール、4−ブタンジオール、ネオペンチルグリコール、1,2−プロピレングリコール、1,4−シクロヘキサンジメタノ一ル、1,4−シクロヘキサンジオール、1,4−ビス(β−ヒドロキシエトキシ)ベンゼン、ビス(β−ヒドロキシエチル)テレフタレート及びパラキシリレンジオール等が挙げられる。以上、ポリウレタン系弾性繊維の原料となる長鎖の重合体について説明したが、本発明において、かかる長鎖の重合体の重合方法は特に制限されない。
また、化3で示されるアミド変性シリコーンとして、pが15〜700の整数であり、R1がメチル基であるものを用いた場合には、加工時におけるスカム発生を抑制することによる加工品位を向上させる効果が大きくなる。
2成分以上で構成される場合には、それらを表1に記載の割合(質量比)で混合して、表1に記載の平滑剤を調製した。
S10:25℃における動粘度が10mm2/sであるポリジメチルシロキサン
S20:25℃における動粘度が20mm2/sであるポリジメチルシロキサン
S30:25℃における動粘度が30mm2/sであるポリジメチルシロキサン
S50:25℃における動粘度が50mm2/sであるポリジメチルシロキサン
M6:25℃における動粘度が6mm2/sである鉱物油
M10:25℃における動粘度が10mm2/sである鉱物油
M15:25℃における動粘度が15mm2/sである鉱物油
M21:25℃における動粘度が21mm2/sである鉱物油
M40:25℃における動粘度が40mm2/sである鉱物油
試験区分2(アミド変性シリコーンの合成)
・アミド変性シリコーン(AS−1)の合成
シロキサン部分の繰り返し単位が40である、両末端水酸基変性ポリジメチルシロキサン27000g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206g、水酸化カリウム40%水溶液3.3gをガラス製の反応容器内に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った。その後、水32gを添加し、減圧で脱水操作を行い、セライトを用いて濾過を行い、アミノ変性シリコーン27000gを得た。得られたアミノ変性シリコーン27000gにオレイン酸2814gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(AS−1)27000gを得た。
化3に示す一般式のp、qの数値に応じて、シロキサン部分の繰り返し単位を変更し、両末端水酸基変性ポリジメチルシロキサンに代替、及び併用して使用する他、X3の構造に応じたアミン、脂肪酸を使用し、アミド変性シリコーン(AS−1)と同様に合成を行った。
N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミンを3−(ジメトキシメチルシリル)プロピルアミンに替えて、アミド変性シリコーン(AS−1)と同様に合成を行った。
シロキサン部分の繰り返し単位が40である、両末端シラノール変性ポリジメチルシロキサン30543g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン1032g、水酸化カリウム40%水溶液4.0gをガラス製の反応容器内に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った。その後、水135gを添加し、減圧で脱水操作を行なった後、ジメチルジメトキシシラン60gを添加、撹拌しつつ90℃で2時間反応を行い、減圧で脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン31000gを得た。得られたアミノ変性シリコーン31000gにテレフタル酸85gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(AS−12)31000gを得た。
ヘキサメチルジシロキサン162、水18g、水酸化カリウム40%水溶液10.3g、オクタメチルシクロテトラシロキサン13320g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン(Ras−1)13000gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液0.4g、ジメチルジメトキシシラン361g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン(Ras−2)500gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液5.2g、オクタメチルシクロテトラシロキサン5932g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン413gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン6400gを得た。得られたアミノ変性シリコーン6400gにアジピン酸291gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−3)6655gを得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液2.4g、オクタメチルシクロテトラシロキサン2225g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン413gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン2700gを得た。得られたアミノ変性シリコーン2700gにトリメリット酸419gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−4)3082gを得た。
メチルハイドロジェンポリジメチルシロキサン(メチルハイドロジェンシロキサン単位2個、ジメチルシロキサン単位30個、トリメチルシロキサン単位1個、トリメチルシリル単位1個から構成されたもの)2505g、ペンタノイルポリアルキレングリコールモノアリルエーテル(ポリアルキレングリコールがエチレンオキシ単位3 個とプロピレンオキシ単位3 個とがランダム結合したもの)897g、触媒として塩化白金6水和物0.1g及びトルエン2000mlを反応容器に仕込み、反応系の温度を110℃に保ち、10時間付加反応を行なった。反応系からキシレンを減圧留去した後、触媒を濾別し、中間体としてポリエーテル変性シリコーンを得た。別に、3−アミノプロピルメチルジメトキシシラン490g及び水144gを反応容器に仕込み、反応系の温度を40℃に保ち、2時間重合反応を行なった後、80℃で2時間減圧脱水処理し、中間体としてアミノ基含有ポリシロキサンを得た。かくして得たポリエーテル変性シリコーン1701g及びアミノ基含有ポリシロキサン135gを反応容器に仕込み、均一に混合した後、水酸化カリウム0.1gを加えて、反応系の温度を98℃に保ち、24時間反応を行なった。反応物を酢酸で中和した後、更に無水トリメリット酸193gを加え、反応系の温度を150〜175℃として、6時間アミド化反応を行ない、アミド変性シリコーン(Ras−5)を得た。
ヘキサメチルジシロキサン162g、水54g、水酸化カリウム40%水溶液10.4g、オクタメチルシクロテトラシロキサン11123g、N−[3−(ジメトキシメチルシリル)プロピル]エチレンジアミン206gをガラス製の反応容器に入れ、撹拌しつつ90℃まで昇温し、4時間反応を行った後、減圧で脱水、脱メタノールを行い、セライトを用いて濾過を行い、アミノ変性シリコーン11000gを得た。得られたアミノ変性シリコーン11000gにテレフタル酸160gをガラス製の反応容器内に入れ、撹拌しつつ120℃まで昇温し、窒素気流下で4時間反応を行った。その後反応物を冷却し、アミド変性シリコーン(Ras−6)11142gを得た。
・実施例1 表1に記載の平滑剤(L−1)99部、表2に記載のアミド変性シリコーン(AS−1)1部を、20〜35℃の範囲内の温度で均一になるまで混合して実施例1の合成繊維用処理剤を調製した。
実施例1の合成繊維用処理剤と同様にして、実施例2〜6、参考例1〜11及び比較例1〜3の合成繊維用処理剤を調製した。これらの内容を表3にまとめて示した。
AS−1〜AS−12,Ras−1〜Ras−6:表2に記載のアミノ変性シリコーン及びアミド変性シリコーン
Ras−7:粘度900mm2/s(25℃)、官能基当量2700g/molのアミドポリエーテル変性シリコーン
・試験区分4(合成繊維への合成繊維用処理剤の付着及び評価)
・合成繊維としてのポリウレタン系弾性繊維への合成繊維用処理剤の付着
ビス−(p−イソシアネートフェニル)−メタン/テトラメチレンエーテルグリコール(数平均分子量1800)=1.58/1(モル比)の混合物を常法により90℃で3時間反応させ、キャップドグリコールを得た後、このキャップドグリコールをN,N’−ジメチルアセトアミド(以下、DMAcという)で希釈した。次にエチレンジアミン及びジエチルアミンを含むDMAc溶液を前記のキャップドグリコールのDMAc溶液に加え、室温で高速攪拌装置を用いて混合し、鎖伸長させてポリマを得た。更にDMAcを加えて前記のポリマ濃度が約35%のDMAc溶液とし、このDMAc溶液に、ポリマに対して酸化チタンを4.7%、ヒンダードアミン系耐侯剤を3.0%及びヒンダードフェノール系酸化防止剤を1.2%となるように添加し、混合して均一なポリマ混合溶液とした。このポリマ混合溶液を用いて、公知のスパンデックスで用いられる乾式紡糸方法により、単糸数4本からなる44dtexの弾性糸を紡糸し、巻き取り前のオイリングローラーから各例の合成繊維用処理剤をそのままニートの状態でローラー給油した。かくしてローラー給油したものを、巻き取り速度550m/分で、長さ57mmの円筒状紙管に、巻き幅42mmを与えるトラバースガイドを介して、サーフェイスドライブの巻取機を用いて巻き取り、乾式紡糸ポリウレタン系弾性繊維のパッケージを得た。合成繊維用処理剤の付着量の調節は、オイリングローラーの回転数を調整することで行い、目標値7.0%で付着させた。
前記で得た乾式紡糸ポリウレタン系弾性繊維パッケージを下記の測定及び評価に供し、結果を表3にまとめて示した。
前記のパッケージ(1kg巻き)について、捲き幅の最大値(Wmax)と最小幅(Wmin)を計測し、双方の差(Wmax−Wmin)からバルジを求め、下記の基準で評価した。
○:バルジが4〜10mm。
×:バルジが10mm以上。
前記のパッケージ(1kg巻き)捲糸体をミニチュア整経機に10本仕立て、25℃で65%RHの雰囲気下に糸速度300m/分で1500km巻き取った。このとき、ミニチュア整経機のクシガイドでのスカムの蓄積状態を肉眼観察し、下記の基準で評価した。
○:スカムがやや付着しているが、糸の安定走行に問題はなかった。
×:スカムの付着及び蓄積が多く、糸の安定走行に大きな問題があった。
摩擦測定メーター(エイコー測器社製、SAMPLE FRICTION UNIT MODEL TB−1)を用い、二つのフリーローラー間に直径1cmで表面粗度2Sのクロムメッキ梨地ピンを配置し、このクロムメッキ梨地ピンに対し、前記のパッケージ(500g巻き)から引き出したポリウレタン系弾性繊維の接触角度が90度となるようにした。25℃で60%RHの条件下、入側で初期張力(T1)5gをかけ、100m/分の速度で走行させたときの出側の2次張力(T2)を0.1秒毎に1分間測定した。下記の数1から摩擦係数を求め、下記の基準で評価した。
△:摩擦係数が0.260以上0.300未満。
×:摩擦係数が0.300以上。
試料糸を用いて織物ストレッチ布帛を作製し、染色等の後加工を行い、その外観品位を評価した。先ず、試料糸を、カチオン可染ポリエステル糸(168dtex/48fil)でカバリング加工した。その際のカバリング機での条件を、ヨリ数=450t/m、ドラフト=3.0として得られたカバリング糸をヨコ糸用とし、またヨリ数700T/M、ドラフト=3.5として得られたカバリング糸をタテ糸用とした。次に、得られたカバリング糸をそれぞれヨコ糸、タテ糸として用い、タテ糸を5100本(荒巻整経1100本)で糊付け整経した後、レビアー織機を用いて2/1綾組織で製織した。そして製織で得られた生機を常法に従い精練加工、中間セット(185℃)、減量加工を行ない、更にカチオン染料を用いた染色加工、乾燥、仕上げ剤処理、及び180℃、布帛20m/分、セットゾーン24mの条件で仕上げセットを行った。
◎:波打ちが全くなく、手触りが滑らか。
×:波打ちが気になり、手触りにひっかかりがある。
表3の結果からも明らかなように、本発明の処理剤及び処理方法によると、合成繊維の製造において、優れた捲形状を有するパッケージを得ることができ、また後加工でのスカム発生や擦過による糸切れが少なく、結果として編地の表面が滑らかで加工品位に優れた合成繊維を得ることができるのである。
Claims (12)
- 合成繊維に付着させて用いられる合成繊維用処理剤であって、
下記の化1で示されるアミド変性シリコーンを含有して成ることを特徴とする合成繊維用処理剤。
X1,X2:メチル基、炭素数1〜4のアルコキシ基、又は水酸基であり、且つX1、及びX2のうち少なくとも一つは炭素数1〜4のアルコキシ基又は水酸基
X3:下記の化2で示されるアミド変性基
R1:炭素数1〜5のアルキル基
p:4〜1200の整数
q:1〜100の整数)
R2,R3:それぞれ独立して、炭素数2〜5のアルキレン基
R4:1〜4価のカルボン酸から一つの水酸基を除いた残基
r:0又は1) - 前記アミド変性シリコーンは、化1中のX1、及びX2がメチル基、又は水酸基であり、且つX1、又はX2のうち少なくとも一つは水酸基である場合のものである請求項1に記載の合成繊維用処理剤。
- 前記アミド変性シリコーンは、化1中のX1、及びX2が水酸基である場合のものである請求項1又は2に記載の合成繊維用処理剤。
- 前記アミド変性シリコーンは、化1中のpが15〜700の整数であり、R1がメチル基である場合のものである請求項1〜3のいずれか一項に記載の合成繊維用処理剤。
- 前記アミド変性シリコーンは、化1中のpが100〜500の整数であり、qが1〜10の整数であり、アミド当量が3000〜30000g/molである場合のものである請求項1〜4のいずれか一項に記載の合成繊維用処理剤。
- 前記アミド変性シリコーン以外のシリコーンオイル、鉱物油、脂肪酸エステル、及び液状ポリオレフィンから選ばれる少なくとも一つを含む平滑剤を含有し、前記平滑剤の25℃における動粘度が5〜50mm2/sである請求項1〜5のいずれか一項に記載の合成繊維用処理剤。
- 前記平滑剤は、前記アミド変性シリコーン以外のシリコーンオイルを含むものである請求項6に記載の合成繊維用処理剤。
- 前記平滑剤と前記アミド変性シリコーンの含有割合の合計を100質量%とすると、前記平滑剤を80〜99.9質量%、及び前記アミド変性シリコーンを0.1〜20質量%の割合で含有する請求項6又は7に記載の合成繊維用処理剤。
- 前記平滑剤と前記アミド変性シリコーンの含有割合の合計を100質量%とすると、前記平滑剤を95〜99.9質量%、及び前記アミド変性シリコーンを0.1〜5質量%の割合で含有する請求項7又は8に記載の合成繊維用処理剤。
- 前記合成繊維は、ポリウレタン系弾性繊維である請求項1〜9のいずれか一項に記載の合成繊維用処理剤。
- 請求項1〜10のいずれか一項に記載の合成繊維用処理剤を、合成繊維100質量%に対し0.1〜10質量%の割合となるよう付着させることを特徴とする合成繊維の処理方法。
- 請求項1〜10のいずれか一項に記載の合成繊維用処理剤が付着していることを特徴とする合成繊維。