JP2020047561A - Non-halogen flame-retardant insulation wire - Google Patents
Non-halogen flame-retardant insulation wire Download PDFInfo
- Publication number
- JP2020047561A JP2020047561A JP2018177541A JP2018177541A JP2020047561A JP 2020047561 A JP2020047561 A JP 2020047561A JP 2018177541 A JP2018177541 A JP 2018177541A JP 2018177541 A JP2018177541 A JP 2018177541A JP 2020047561 A JP2020047561 A JP 2020047561A
- Authority
- JP
- Japan
- Prior art keywords
- flame
- retardant
- mass
- halogen
- insulated wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本開示はノンハロゲン難燃性絶縁電線に関する。 The present disclosure relates to halogen-free flame-retardant insulated wires.
絶縁電線は、導体と難燃層とを備える。難燃層は導体の外周に配置されている。難燃層は難燃剤を含む。難燃剤として、ハロゲン系元素を含まないノンハロゲンの難燃剤が望まれている。ノンハロゲンの難燃剤として、金属水酸化物、リン系難燃剤が知られている。リン系難燃剤は特許文献1、2に開示されている。 The insulated wire includes a conductor and a flame-retardant layer. The flame retardant layer is disposed on the outer periphery of the conductor. The flame retardant layer contains a flame retardant. As a flame retardant, a non-halogen flame retardant containing no halogen element has been desired. Metal hydroxides and phosphorus-based flame retardants are known as non-halogen flame retardants. Phosphorus-based flame retardants are disclosed in Patent Documents 1 and 2.
難燃剤として金属水酸化物のみを用いる場合、難燃層の難燃性を確保するためには、金属水酸化物の含有量を多くする必要がある。金属水酸化物の含有量が多い場合、難燃層の引張特性や電気特性等が低下する。 When only a metal hydroxide is used as the flame retardant, it is necessary to increase the content of the metal hydroxide in order to ensure the flame retardancy of the flame retardant layer. When the content of the metal hydroxide is large, the tensile properties, electrical properties, and the like of the flame-retardant layer deteriorate.
難燃剤として、金属水酸化物とリン系難燃剤とを併用することにより、金属水酸化物の含有量を抑制しつつ、難燃層の難燃性を確保することが考えられる。しかしながら、リン系難燃剤は、加水分解し易い。また、リン系難燃剤は、有害ガスを発生させることがある。 By using a metal hydroxide and a phosphorus-based flame retardant in combination as the flame retardant, it is conceivable to secure the flame retardancy of the flame retardant layer while suppressing the content of the metal hydroxide. However, phosphorus-based flame retardants are easily hydrolyzed. Further, phosphorus-based flame retardants may generate harmful gases.
本開示の一局面は、難燃層がリン系難燃剤を含まず、かつ金属水酸化物の含有量を極力小さく抑えながらも優れた難燃性を備えるノンハロゲン難燃性絶縁電線を提供することを目的とする。 One aspect of the present disclosure provides a non-halogen flame-retardant insulated wire having a flame-retardant layer that does not contain a phosphorus-based flame retardant and has excellent flame retardancy while keeping the content of metal hydroxide as low as possible. With the goal.
本開示の一局面は、導体と、前記導体の外周に配置された難燃層と、を備えるノンハロゲン難燃性絶縁電線であって、前記難燃層は、オレフィン系樹脂と、金属水酸化物と、メルカプトベンゾチアゾール亜鉛塩とを含むノンハロゲン難燃性絶縁電線である。
[発明の効果]
One aspect of the present disclosure is a non-halogen flame-retardant insulated wire including a conductor and a flame-retardant layer disposed on the outer periphery of the conductor, wherein the flame-retardant layer includes an olefin-based resin and a metal hydroxide. And a non-halogen flame-retardant insulated wire comprising: a zinc salt of mercaptobenzothiazole.
[The invention's effect]
本開示の一局面であるノンハロゲン難燃性絶縁電線によれば、難燃層がリン系難燃剤を含まず、かつ金属水酸化物の含有量を極力小さく抑えながらも優れた難燃性を備えるノンハロゲン難燃性絶縁電線を提供することができる。 According to the non-halogen flame-retardant insulated wire according to one aspect of the present disclosure, the flame-retardant layer does not contain a phosphorus-based flame retardant, and has excellent flame retardancy while keeping the content of metal hydroxide as low as possible. A halogen-free flame-retardant insulated wire can be provided.
本開示の例示的な実施形態を、図面を参照しながら説明する。
1.ノンハロゲン難燃性絶縁電線の構成
(1−1)ノンハロゲン難燃性絶縁電線の全体構成
本開示のノンハロゲン難燃性絶縁電線は、導体と、難燃層とを備える。難燃層は、導体の外周に配置される。難燃層は、例えば、導体の外周面に接している。また、導体と難燃層との間に他の層が存在してもよい。
Exemplary embodiments of the present disclosure will be described with reference to the drawings.
1. Configuration of non-halogen flame-retardant insulated wire (1-1) Overall configuration of non-halogen flame-retardant insulated wire The non-halogen flame-retardant insulated wire of the present disclosure includes a conductor and a flame-retardant layer. The flame retardant layer is disposed on the outer periphery of the conductor. The flame retardant layer is in contact with, for example, the outer peripheral surface of the conductor. Another layer may be present between the conductor and the flame retardant layer.
本開示のノンハロゲン難燃性絶縁電線は、例えば、図1に示す構成を有する。ノンハロゲン難燃性絶縁電線100は、導体110と、電気絶縁層120と、難燃層130と、を備える。電気絶縁層120は導体110の外周に配置される。難燃層130は導体110及び電気絶縁層120の外周に配置される。 The halogen-free flame-retardant insulated wire of the present disclosure has, for example, the configuration shown in FIG. The halogen-free flame-retardant insulated wire 100 includes a conductor 110, an electric insulating layer 120, and a flame-retardant layer 130. The electric insulating layer 120 is disposed on the outer periphery of the conductor 110. The flame-retardant layer 130 is arranged on the outer periphery of the conductor 110 and the electrical insulating layer 120.
導体110として、通常用いられる金属線を用いることができる。金属線として、例えば、銅線、銅合金線、アルミニウム線、金線、銀線等が挙げられる。導体110は、その外周面に金属めっき層を備えていてもよい。金属めっき層として、例えば、錫、ニッケル等から成る層が挙げられる。導体110は、金属線を撚り合わせた集合撚り導体であってもよい。導体110の断面積や外径は、ノンハロゲン難燃性絶縁電線100に要求される電気特性に応じて適宜設計することができる。 As the conductor 110, a commonly used metal wire can be used. Examples of the metal wire include a copper wire, a copper alloy wire, an aluminum wire, a gold wire, and a silver wire. The conductor 110 may have a metal plating layer on the outer peripheral surface. Examples of the metal plating layer include a layer made of tin, nickel, or the like. The conductor 110 may be a collective twisted conductor obtained by twisting metal wires. The cross-sectional area and outer diameter of the conductor 110 can be appropriately designed according to the electrical characteristics required for the halogen-free flame-retardant insulated wire 100.
難燃層130は、押出機を用い、難燃性樹脂組成物を電気絶縁層120の上に押し出して形成することができる。
本開示のノンハロゲン難燃性絶縁電線は、例えば、図2に示す構成を有する。ノンハロゲン難燃性絶縁電線200は、導体110と、難燃層130と、を備える。難燃層130は導体110の外周に配置される。ノンハロゲン難燃性絶縁電線200の構成は、基本的にはノンハロゲン難燃性絶縁電線100と同様である。ただし、ノンハロゲン難燃性絶縁電線200は電気絶縁層120を備えない。ノンハロゲン難燃性絶縁電線200では、難燃層130が導体110の外周面を被覆している。
The flame-retardant layer 130 can be formed by extruding the flame-retardant resin composition onto the electric insulating layer 120 using an extruder.
The non-halogen flame-retardant insulated wire of the present disclosure has, for example, the configuration shown in FIG. The non-halogen flame-retardant insulated wire 200 includes a conductor 110 and a flame-retardant layer 130. The flame retardant layer 130 is disposed on the outer periphery of the conductor 110. The configuration of the non-halogen flame-retardant insulated wire 200 is basically the same as that of the non-halogen flame-retardant insulated wire 100. However, the halogen-free flame-retardant insulated wire 200 does not include the electric insulating layer 120. In the non-halogen flame-retardant insulated wire 200, the flame-retardant layer 130 covers the outer peripheral surface of the conductor 110.
難燃層130は、押出機を用い、難燃性樹脂組成物を導体110の上に押し出して形成することができる。
本開示のノンハロゲン難燃性絶縁電線のサイズは特に限定されず、適宜設定することができる。本開示のノンハロゲン難燃性絶縁電線は、例えば、盤内配線用、車両用、自動車用、機器内配線用、電力用等の用途に使用することができる。
The flame-retardant layer 130 can be formed by extruding the flame-retardant resin composition onto the conductor 110 using an extruder.
The size of the halogen-free flame-retardant insulated wire of the present disclosure is not particularly limited, and can be appropriately set. The non-halogen flame-retardant insulated wire of the present disclosure can be used, for example, for wiring in a panel, for a vehicle, for an automobile, for wiring in a device, for power, and the like.
(1−2)難燃層
難燃層は、オレフィン系樹脂と、金属水酸化物と、メルカプトベンゾチアゾール亜鉛塩とを含む。オレフィン系樹脂は、エチレン−酢酸ビニル共重合体(以下ではEVAとする)を主成分とすることが好ましい。主成分とは、オレフィン系樹脂の中で最も含有量が多い成分を意味する。オレフィン系樹脂がEVAを主成分とする場合、難燃層の難燃性が一層高い。
(1-2) Flame retardant layer The flame retardant layer contains an olefin-based resin, a metal hydroxide, and a mercaptobenzothiazole zinc salt. The olefin resin preferably contains an ethylene-vinyl acetate copolymer (hereinafter referred to as EVA) as a main component. The main component means a component having the largest content in the olefin-based resin. When the olefin resin contains EVA as a main component, the flame retardancy of the flame retardant layer is even higher.
難燃層は、本開示のノンハロゲン難燃性絶縁電線の効果を奏する限りにおいて、EVA以外のオレフィン系樹脂を含有していてもよい。難燃層が含有するオレフィン系樹脂100質量部のうち、EVAの含有量は、50質量部以上であることが好ましく、70質量部以上であることがさらに好ましく、80質量部以上であることが一層好ましく、100質量部であることが特に好ましい。 The flame-retardant layer may contain an olefin resin other than EVA as long as the effect of the non-halogen flame-retardant insulated wire of the present disclosure is exerted. The EVA content is preferably 50 parts by mass or more, more preferably 70 parts by mass or more, and preferably 80 parts by mass or more, out of 100 parts by mass of the olefin-based resin contained in the flame-retardant layer. More preferably, it is particularly preferably 100 parts by mass.
EVA以外のオレフィン系樹脂として、例えば、ポリエチレン(PE)、ポリプロピレン等のポリオレフィンや、エチレン−プロピレン共重合体、エチレン−メチルアクリレート共重合体、エチレン−エチルアクリレート共重合体(EEA)、エチレン−メチルメタクリレート共重合体、エチレン−エチルメタクリレート共重合体等のエチレン系共重合体、プロピレン−酢酸ビニル共重合体、プロピレン−アクリル酸エステル共重合体、プロピレン−メタクリル酸エステル共重合体等のプロピレン系共重合体等を例示することができる。 Examples of olefin resins other than EVA include polyolefins such as polyethylene (PE) and polypropylene, ethylene-propylene copolymer, ethylene-methyl acrylate copolymer, ethylene-ethyl acrylate copolymer (EEA), and ethylene-methyl. Propylene copolymers such as methacrylate copolymers, ethylene copolymers such as ethylene-ethyl methacrylate copolymer, propylene-vinyl acetate copolymers, propylene-acrylate copolymers, and propylene-methacrylate copolymers. Polymers and the like can be exemplified.
難燃層は、上記のEVA以外のオレフィン系樹脂のうち、1種を含有していてもよいし、2種以上の組み合わせを含有していてもよい。2種以上の組み合わせの中では、エチレン−エチルアクリレート共重合体とエチレン−酢酸ビニル共重合体との組み合わせが好ましい。 The flame-retardant layer may contain one kind or a combination of two or more kinds of the above-mentioned olefin resins other than EVA. Among two or more combinations, a combination of an ethylene-ethyl acrylate copolymer and an ethylene-vinyl acetate copolymer is preferable.
難燃層が、エチレン−エチルアクリレート共重合体とエチレン−酢酸ビニル共重合体とを合計100質量部含有する場合、エチレン−エチルアクリレート共重合体の含有量は、5質量部以上40質量部以下であることが好ましい。また、難燃層は、必要に応じて、相溶化剤や密着性向上剤として機能する他の樹脂を含有してもよい。 When the flame-retardant layer contains a total of 100 parts by mass of the ethylene-ethyl acrylate copolymer and the ethylene-vinyl acetate copolymer, the content of the ethylene-ethyl acrylate copolymer is 5 parts by mass or more and 40 parts by mass or less. It is preferred that In addition, the flame retardant layer may contain another resin that functions as a compatibilizer or an adhesion improver, if necessary.
金属水酸化物として、例えば、水酸化マグネシウム、水酸化アルミニウム、及び水酸化カルシウム等が挙げられる。これらの金属水酸化物を、1種類単独で用いてもよいし、2種類以上を組み合わせて用いてもよい。難燃層は、オレフィン系樹脂100質量部に対して、100質量部以上200質量部以下の金属水酸化物を含むことが好ましい。オレフィン系樹脂100質量部に対して、金属水酸化物の含有量が100質量部以上である場合、難燃層の難燃性が一層高い。オレフィン系樹脂100質量部に対して、金属水酸化物の含有量が200質量部以下である場合、難燃層の機械特性が一層良好である。機械特性として、例えば、引張強度、伸び率等が挙げられる。金属水酸化物の含有量は、より好ましくは、オレフィン系樹脂100質量部に対して、150質量部以上200質量部以下である。 Examples of the metal hydroxide include magnesium hydroxide, aluminum hydroxide, and calcium hydroxide. One of these metal hydroxides may be used alone, or two or more thereof may be used in combination. The flame retardant layer preferably contains 100 to 200 parts by mass of a metal hydroxide based on 100 parts by mass of the olefin-based resin. When the content of the metal hydroxide is 100 parts by mass or more based on 100 parts by mass of the olefin-based resin, the flame retardancy of the flame retardant layer is even higher. When the content of the metal hydroxide is 200 parts by mass or less with respect to 100 parts by mass of the olefin-based resin, the mechanical properties of the flame retardant layer are more excellent. Examples of the mechanical properties include tensile strength and elongation. The content of the metal hydroxide is more preferably 150 parts by mass or more and 200 parts by mass or less based on 100 parts by mass of the olefin-based resin.
金属水酸化物の表面は、脂肪酸やシラン化合物で処理されていることが好ましい。金属水酸化物の表面が脂肪酸やシラン化合物で処理されている場合、難燃層の引張特性が一層良好である。金属水酸化物にあらかじめ表面処理する場合に使用するシラン化合物として、例えば、ビニルトリメトキシシラン、ビニルトリエトキシシラン、メタクリロキシプロピル、トリメトキシシラン、アミノプロピルトリメトキシシラン、アミノプロピルトリエトキシシラン等がある。これらを1種類単独で使用してもよいし、2種類以上を併用してもよい。
メルカプトベンゾチアゾール亜鉛塩は、金属水酸化物と同様に、難燃剤として機能する。難燃層が、難燃剤として、金属水酸化物とメルカプトベンゾチアゾール亜鉛塩とを含有することにより、難燃層の難燃性を確保しつつ、難燃層における金属水酸化物の含有量を抑制しつつ、難燃層の難燃性を確保できる。
The surface of the metal hydroxide is preferably treated with a fatty acid or a silane compound. When the surface of the metal hydroxide is treated with a fatty acid or a silane compound, the tensile properties of the flame retardant layer are more excellent. Examples of the silane compound used when the metal hydroxide is subjected to surface treatment in advance include, for example, vinyltrimethoxysilane, vinyltriethoxysilane, methacryloxypropyl, trimethoxysilane, aminopropyltrimethoxysilane, aminopropyltriethoxysilane, and the like. is there. These may be used alone or in combination of two or more.
Mercaptobenzothiazole zinc salt, like metal hydroxide, functions as a flame retardant. The flame retardant layer contains a metal hydroxide and a zinc mercaptobenzothiazole as a flame retardant, thereby ensuring the flame retardancy of the flame retardant layer and reducing the content of the metal hydroxide in the flame retardant layer. The flame retardancy of the flame-retardant layer can be ensured while suppressing.
難燃層は、オレフィン系樹脂100質量部に対して、1質量部以上40質量部以下のメルカプトベンゾチアゾール亜鉛塩を含むことが好ましい。オレフィン系樹脂100質量部に対して、メルカプトベンゾチアゾール亜鉛塩の含有量が1質量部以上である場合、難燃層の難燃性が一層高い。オレフィン系樹脂100質量部に対して、メルカプトベンゾチアゾール亜鉛塩の含有量が40質量部を超える場合、メルカプトベンゾチアゾール亜鉛塩の含有量が40質量部である場合に比べて、難燃層の難燃性はそれ以上向上し難い。 The flame retardant layer preferably contains 1 to 40 parts by mass of a mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin. When the content of the mercaptobenzothiazole zinc salt is 1 part by mass or more with respect to 100 parts by mass of the olefin-based resin, the flame retardancy of the flame retardant layer is even higher. When the content of the mercaptobenzothiazole zinc salt exceeds 40 parts by mass with respect to 100 parts by mass of the olefin-based resin, the flame-retardant layer is more difficult than when the content of the mercaptobenzothiazole zinc salt is 40 parts by mass. Flammability is hard to further improve.
難燃層は、リン系難燃剤を含まない。リン系難燃剤として、例えば、赤リン、ポリリン酸アンモニウム等が挙げられる。難燃層は、ハロゲン元素含有難燃剤を含まない。つまり、本開示の絶縁電線は、ノンハロゲン難燃性絶縁電線である。 The flame retardant layer does not contain a phosphorus-based flame retardant. Examples of the phosphorus-based flame retardant include red phosphorus, ammonium polyphosphate and the like. The flame retardant layer does not contain a halogen element-containing flame retardant. That is, the insulated wire of the present disclosure is a non-halogen flame-retardant insulated wire.
難燃層は、他の難燃剤又は難燃助剤(ただし、リン系難燃剤及びハロゲン元素含有難燃剤ではない)をさらに含んでいてもよい。難燃層は、架橋剤、滑剤、カーボンブラック、着色剤、酸化防止剤等をさらに含んでいてもよい。難燃層は、架橋剤、架橋促進剤、電子線等を使用して架橋されていてもよい。 The flame retardant layer may further contain other flame retardants or flame retardant auxiliaries (but not phosphorus-based flame retardants and halogen element-containing flame retardants). The flame retardant layer may further contain a crosslinking agent, a lubricant, carbon black, a coloring agent, an antioxidant, and the like. The flame retardant layer may be cross-linked using a cross-linking agent, a cross-linking accelerator, an electron beam, or the like.
2.ノンハロゲン難燃性絶縁電線の製造方法
二軸押出機、二軸ロール、ミキシングロール、ミキサー、ダンブラ、ニーダ等を用いて各成分を混合し、難燃層の材料である難燃性樹脂組成物を製造する。ノンハロゲン難燃性絶縁電線が図1に示す構成を有する場合は、押出機を用いて電気絶縁層を難燃性樹脂組成物で被覆し、難燃層を形成する。ノンハロゲン難燃性絶縁電線が図2に示す構成を有する場合は、押出機を用いて導体を難燃性樹脂組成物で被覆し、難燃層を形成する。
2. Method for producing non-halogen flame-retardant insulated wire Mixing each component using a twin-screw extruder, twin-screw roll, mixing roll, mixer, damper, kneader, etc. To manufacture. When the halogen-free flame-retardant insulated wire has the configuration shown in FIG. 1, the electric insulation layer is coated with a flame-retardant resin composition using an extruder to form a flame-retardant layer. When the halogen-free flame-retardant insulated wire has the configuration shown in FIG. 2, the conductor is coated with a flame-retardant resin composition using an extruder to form a flame-retardant layer.
3.実施例
(3−1)難燃性樹脂組成物の製造
表1及び表2に示す配合成分を、それらの表に示す配合量で混練し、実施例1〜7及び比較例1〜4の難燃性樹脂組成物を製造した。混練にはバンバリーミキサを使用した。混練は、160℃にて15分間行った。なお、表1及び表2における配合量の単位は質量部である。
3. Example (3-1) Production of Flame-Retardant Resin Composition The blending components shown in Tables 1 and 2 were kneaded in the blending amounts shown in the tables, and the difficulties in Examples 1 to 7 and Comparative Examples 1 to 4 were obtained. A flammable resin composition was produced. A Banbury mixer was used for kneading. The kneading was performed at 160 ° C. for 15 minutes. The unit of the compounding amount in Tables 1 and 2 is parts by mass.
(3−2)難燃性樹脂組成物の評価
各実施例及び各比較例の難燃性樹脂組成物について、難燃性を評価した。評価方法は以下のとおりである。JIS K 7201−2に準拠して、難燃性樹脂組成物から成る試験用シートを作成した。試験用シートの厚みは3mmである。試験用シートを用いて酸素指数を測定した。酸素指数の測定値を上記表1及び表2に示す。酸素指数の単位は容量%である。酸素指数は、材料が燃焼を持続するために必要な最低酸素濃度を示す。材料の酸素指数が高いほど、その材料の難燃性は高い。
(3-2) Evaluation of Flame Retardant Resin Composition The flame retardant properties of the flame retardant resin compositions of the respective examples and comparative examples were evaluated. The evaluation method is as follows. A test sheet made of the flame-retardant resin composition was prepared according to JIS K7201-2. The thickness of the test sheet is 3 mm. The oxygen index was measured using the test sheet. The measured values of the oxygen index are shown in Tables 1 and 2 above. The unit of the oxygen index is% by volume. The oxygen index indicates the minimum oxygen concentration required for the material to sustain combustion. The higher the oxygen index of a material, the higher the flame retardancy of the material.
実施例1の難燃性樹脂組成物は、メルカプトベンゾチアゾール亜鉛塩を含有する点を除いて比較例1の難燃性樹脂組成物と一致する。実施例1の難燃性樹脂組成物は、比較例1の難燃性樹脂組成物よりも酸素指数が大きい。 The flame retardant resin composition of Example 1 is identical to the flame retardant resin composition of Comparative Example 1 except that it contains a mercaptobenzothiazole zinc salt. The flame retardant resin composition of Example 1 has a larger oxygen index than the flame retardant resin composition of Comparative Example 1.
実施例2〜6の難燃性樹脂組成物は、メルカプトベンゾチアゾール亜鉛塩を含有する点を除いて比較例2の難燃性樹脂組成物と一致する。実施例2〜6の難燃性樹脂組成物は、比較例2の難燃性樹脂組成物よりも酸素指数が大きい。 The flame-retardant resin compositions of Examples 2 to 6 correspond to the flame-retardant resin compositions of Comparative Example 2 except that they contain a mercaptobenzothiazole zinc salt. The flame retardant resin compositions of Examples 2 to 6 have a larger oxygen index than the flame retardant resin composition of Comparative Example 2.
実施例7の難燃性樹脂組成物は、メルカプトベンゾチアゾール亜鉛塩を含有する点を除いて比較例3の難燃性樹脂組成物と一致する。実施例7の難燃性樹脂組成物は、比較例3の難燃性樹脂組成物よりも酸素指数が大きい。 The flame retardant resin composition of Example 7 is identical to the flame retardant resin composition of Comparative Example 3 except that it contains a zinc mercaptobenzothiazole salt. The flame retardant resin composition of Example 7 has a larger oxygen index than the flame retardant resin composition of Comparative Example 3.
実施例2〜5の難燃性樹脂組成物は、比較例3、4の難燃性樹脂組成物よりも金属水酸化物の配合量が少ない。しかしながら、実施例2〜5の難燃性樹脂組成物は、比較例3、4の難燃性樹脂組成物よりも酸素指数が大きい。また、実施例7の難燃性樹脂組成物は、比較例4の難燃性樹脂組成物よりも金属水酸化物の配合量が少ない。しかしながら、実施例7の難燃性樹脂組成物は、比較例4の難燃性樹脂組成物よりも酸素指数が大きい。よって、実施例2〜5、7の難燃性樹脂組成物では、金属水酸化物の含有量を抑えつつ、優れた難燃性を備えている。 The flame-retardant resin compositions of Examples 2 to 5 have a smaller amount of metal hydroxide than the flame-retardant resin compositions of Comparative Examples 3 and 4. However, the flame retardant resin compositions of Examples 2 to 5 have a larger oxygen index than the flame retardant resin compositions of Comparative Examples 3 and 4. Further, the flame retardant resin composition of Example 7 has a smaller amount of the metal hydroxide than the flame retardant resin composition of Comparative Example 4. However, the flame retardant resin composition of Example 7 has a larger oxygen index than the flame retardant resin composition of Comparative Example 4. Therefore, the flame-retardant resin compositions of Examples 2 to 5, and 7 have excellent flame retardancy while suppressing the content of the metal hydroxide.
オレフィン系樹脂100質量部に対して、3質量部以上40質量部以下のメルカプトベンゾチアゾール亜鉛塩を含む実施例2〜6の難燃性樹脂組成物は、金属水酸化物の含有量を抑えつつ、優れた難燃性を備えている。オレフィン系樹脂100質量部に対して、3質量部以上20質量部以下のメルカプトベンゾチアゾール亜鉛塩を含む実施例2〜5の難燃性樹脂組成物は、難燃性が一層高い。オレフィン系樹脂100質量部に対して、3質量部以上10質量部以下のメルカプトベンゾチアゾール亜鉛塩を含む実施例2〜4の難燃性樹脂組成物は、難燃性がさらに高い。オレフィン系樹脂100質量部に対して、3質量部以上5質量部以下のメルカプトベンゾチアゾール亜鉛塩を含む実施例2〜3の難燃性樹脂組成物は、難燃性が特に高い。 The flame-retardant resin compositions of Examples 2 to 6 containing from 3 parts by mass to 40 parts by mass of mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin, while suppressing the content of the metal hydroxide. Has excellent flame retardancy. The flame-retardant resin compositions of Examples 2 to 5 containing 3 to 20 parts by mass of a mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin have higher flame retardancy. The flame-retardant resin compositions of Examples 2 to 4 containing 3 to 10 parts by mass of mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin have even higher flame retardancy. The flame-retardant resin compositions of Examples 2 to 3 containing 3 to 5 parts by mass of mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin have particularly high flame retardancy.
4.他の実施形態
以上、本開示の実施形態について説明したが、本開示は上述の実施形態に限定されることなく、種々変形して実施することができる。
4. Other embodiments
Although the embodiments of the present disclosure have been described above, the present disclosure is not limited to the above embodiments, and can be implemented with various modifications.
(1)上記各実施形態における1つの構成要素が有する機能を複数の構成要素に分担させたり、複数の構成要素が有する機能を1つの構成要素に発揮させたりしてもよい。また、上記各実施形態の構成の一部を省略してもよい。また、上記各実施形態の構成の少なくとも一部を、他の上記実施形態の構成に対して付加、置換等してもよい。なお、特許請求の範囲に記載の文言から特定される技術思想に含まれるあらゆる態様が本開示の実施形態である。 (1) The function of one component in each of the above embodiments may be shared by a plurality of components, or the function of a plurality of components may be exhibited by one component. Further, a part of the configuration of each of the above embodiments may be omitted. Further, at least a part of the configuration of each of the above embodiments may be added to, replaced with, or the like with respect to the configuration of the other above embodiment. Note that all aspects included in the technical idea specified by the language described in the claims are embodiments of the present disclosure.
(2)上述したノンハロゲン難燃性絶縁電線の他、当該ノンハロゲン難燃性絶縁電線を構成要素とするケーブル、難燃性樹脂組成物、ノンハロゲン難燃性絶縁電線の製造方法、難燃性樹脂組成物の製造方法等、種々の形態で本開示を実現することもできる。 (2) In addition to the non-halogen flame-retardant insulated wire described above, a cable, a flame-retardant resin composition, a method for producing a halogen-free flame-retardant insulated wire, and a flame-retardant resin composition The present disclosure can be realized in various forms such as a method of manufacturing a product.
100、200…ノンハロゲン難燃性絶縁電線、110…導体、120…電気絶縁層、130…難燃層 100, 200: halogen-free flame-retardant insulated wire, 110: conductor, 120: electric insulating layer, 130: flame-retardant layer
Claims (4)
前記導体の外周に配置された難燃層と、
を備えるノンハロゲン難燃性絶縁電線であって、
前記難燃層は、オレフィン系樹脂と、金属水酸化物と、メルカプトベンゾチアゾール亜鉛塩とを含むノンハロゲン難燃性絶縁電線。 Conductor and
A flame-retardant layer arranged on the outer periphery of the conductor,
A non-halogen flame-retardant insulated wire comprising:
The flame-retardant layer is a halogen-free flame-retardant insulated wire containing an olefin-based resin, a metal hydroxide, and a mercaptobenzothiazole zinc salt.
前記難燃層は、前記オレフィン系樹脂100質量部に対して、100質量部以上200質量部以下の前記金属水酸化物を含むノンハロゲン難燃性絶縁電線。 The non-halogen flame-retardant insulated wire according to claim 1,
The flame-retardant layer is a non-halogen flame-retardant insulated wire including 100 to 200 parts by mass of the metal hydroxide based on 100 parts by mass of the olefin-based resin.
前記難燃層は、前記オレフィン系樹脂100質量部に対して、1質量部以上40質量部以下の前記メルカプトベンゾチアゾール亜鉛塩を含むノンハロゲン難燃性絶縁電線。 The non-halogen flame-retardant insulated wire according to claim 1 or 2,
The non-halogen flame-retardant insulated wire, wherein the flame-retardant layer contains 1 to 40 parts by mass of the mercaptobenzothiazole zinc salt with respect to 100 parts by mass of the olefin-based resin.
前記オレフィン系樹脂は、エチレン−酢酸ビニル共重合体を主成分とするノンハロゲン難燃性絶縁電線。 It is a halogen-free flame-retardant insulated wire according to any one of claims 1 to 3,
The olefin-based resin is a non-halogen flame-retardant insulated wire mainly containing an ethylene-vinyl acetate copolymer.