JP2020008264A - Water absorption sheet structure - Google Patents
Water absorption sheet structure Download PDFInfo
- Publication number
- JP2020008264A JP2020008264A JP2018132613A JP2018132613A JP2020008264A JP 2020008264 A JP2020008264 A JP 2020008264A JP 2018132613 A JP2018132613 A JP 2018132613A JP 2018132613 A JP2018132613 A JP 2018132613A JP 2020008264 A JP2020008264 A JP 2020008264A
- Authority
- JP
- Japan
- Prior art keywords
- water
- absorbent sheet
- liquid
- sheet structure
- permeable member
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、吸水シート構造体に関する。具体的には、本発明は、吸水性シートを備える吸水シート構造体に関する。 The present invention relates to a water-absorbent sheet structure. Specifically, the present invention relates to a water-absorbent sheet structure provided with a water-absorbent sheet.
従来、夏場の強い日差しを遮蔽するために、日よけスクリーンシートやグリーンカーテンが使用されている。日よけスクリーンシートは、太陽の熱線や紫外線を反射させることで、室内空間の温度の上昇を防ぐ働きをする。また、グリーンカーテンは、日差しを遮蔽するのみならず、植物の葉表面から水蒸気が蒸散することにより、周辺温度を下げることもできる。このように水蒸気の蒸散を利用することで、夏場の暑さを和らげる工夫が行われている。 2. Description of the Related Art Conventionally, a shade screen sheet or a green curtain has been used to shield strong sunlight in summer. The sunshade screen sheet functions to prevent the temperature of the indoor space from rising by reflecting the heat rays and ultraviolet rays of the sun. The green curtain not only shields the sun, but also lowers the ambient temperature by evaporating water vapor from the leaf surface of the plant. By utilizing the evaporation of water vapor as described above, various measures have been taken to reduce the heat in summer.
しかし、このようなグリーンカーテンは、生きた植物により形成されるものであるため、植物が成長するまでに日数を要したり、手入れに労力がかかることがある。このため、植物の葉や茎の形に似せた合成樹脂からなるグリーンカーテンも開発されている。また、吸水性のシートに水を吸水させ、その水分を蒸散させることにより、周辺温度を下げることを目的とした水蒸散シートもグリーンカーテンの代用品として用いられている（例えば、特許文献１）。 However, since such a green curtain is formed by a living plant, it may take many days for the plant to grow or it may take a lot of effort to maintain the plant. For this reason, a green curtain made of a synthetic resin that resembles the shape of a plant leaf or stem has been developed. In addition, a water-evaporating sheet intended to lower ambient temperature by absorbing water in a water-absorbing sheet and evaporating the water is also used as a substitute for a green curtain (for example, Patent Document 1). .
遮光等を目的としたシートは、その目的ゆえにシート面積が大きくなる傾向にある。このため、このようなシートに水分を吸水させた場合、シートの重量が増え、意図しないシートの破損等が生じることがある。また、重量の大きなシートを支えるために、強固な支持部材や保持部材が必要となるため、設置費用がかさむこともある。 A sheet for the purpose of shading or the like tends to have a large sheet area for that purpose. For this reason, when water is absorbed in such a sheet, the weight of the sheet increases, and unintended breakage of the sheet may occur. In addition, since a strong supporting member and a holding member are required to support a heavy sheet, installation cost may be increased.
そこで本発明者らは、このような従来技術の課題を解決するために、吸水性及び水蒸散性を有するシート構造体であって、水を吸水した際に破損等が生じにくいシート構造体を提供することを目的として検討を進めた。 In order to solve the problems of the related art, the present inventors have developed a sheet structure having water absorbency and water transpiration, which is unlikely to be damaged when water is absorbed. The study was conducted for the purpose of providing.
上記の課題を解決するために鋭意検討を行った結果、本発明者らは、吸水性シートを収容し得る収容部を有する液透過性部材に、吸水性シートを収容することで、吸水性と水蒸散性を維持したままで、破損等の発生が抑制されたシート構造体が得られることを見出した。
具体的に、本発明は、以下の構成を有する。
As a result of intensive studies to solve the above-described problems, the present inventors have found that a liquid-permeable member having an accommodation portion capable of accommodating a water-absorbent sheet, by accommodating the water-absorbent sheet, has a water absorbing property. It has been found that a sheet structure in which the occurrence of breakage and the like is suppressed can be obtained while maintaining water transpiration.
Specifically, the present invention has the following configuration.
［１］ 吸水性シートと、
吸水性シートを収容する収容部を有する液透過性部材と、を備える吸水シート構造体。
［２］ 吸水性シートの厚み（ｍｍ）をＴとし、
吸水性シートを蒸留水に５分間浸漬した後に、５０メッシュの金網上に水平となるように１分間静置した場合、
吸水性シートの吸水量は、Ｔ×３００ｇ／ｍ2以上である［１］に記載の吸水シート構造体。
［３］ 吸水性シートの最大面の面積は、１００ｃｍ2以上である［１］又は［２］に記載の吸水シート構造体。
［４］ 吸水シート構造体は、他の構造体と接合可能な接合部材をさらに備える［１］〜［３］のいずれかに記載の吸水シート構造体。
［５］ 接合部材は、懸吊用係合部材である［４］に記載の吸水シート構造体。
［６］ 吸水シート構造体は、吊下式吸水シート構造体である［１］〜［５］のいずれかに記載の吸水シート構造体。
［７］ 吸水性シートは、パルプを主成分として含む不織布である［１］〜［６］のいずれかに記載の吸水シート構造体。
［８］ 吸水性シートは、さらにバインダー成分を含む［７］に記載の吸水シート構造体。
［９］ 液透過性部材は、少なくとも１つの液透過孔を有する［１］〜［８］のいずれかに記載の吸水シート構造体。
［１０］ 液透過性部材は、網目状部材である［１］〜［９］のいずれかに記載の吸水シート構造体。
［１１］ 液透過性部材の引張強度は、３０Ｎ／ｍ以上である［１］〜［１０］のいずれかに記載の吸水シート構造体。
［１２］ 液透過性部材は、ポリエステル、ナイロン及びポリエチレンから選択される樹脂を主成分として含む［１］〜［１１］のいずれかに記載の吸水シート構造体。
［１３］ 液透過性部材は、袋状部材である［１］〜［１２］のいずれかに記載の吸水シート構造体。
［１４］ 吸水シート構造体は、複数の吸水性シートを備え、
液透過性部材は、各吸水性シートを収容する複数の収容部を有するか、もしくは、
液透過性部材は、複数の袋状部材が連結した部材である［１］〜［１３］のいずれかに記載の吸水シート構造体。
[1] a water-absorbing sheet;
A liquid-permeable member having a storage section for storing the water-absorbent sheet.
[2] Let T be the thickness (mm) of the water-absorbent sheet,
When the water-absorbent sheet is immersed in distilled water for 5 minutes, and then left standing for 1 minute on a 50-mesh wire net so as to be horizontal,
The water-absorbent sheet structure according to [1], wherein the water-absorbent sheet has a water absorption of T × 300 g / m 2 or more.
[3] The water-absorbent sheet structure according to [1] or [2], wherein the area of the largest surface of the water-absorbent sheet is 100 cm 2 or more.
[4] The water-absorbent sheet structure according to any one of [1] to [3], wherein the water-absorbent sheet structure further includes a joining member that can be joined to another structure.
[5] The water-absorbent sheet structure according to [4], wherein the joining member is a hanging engagement member.
[6] The water-absorbing sheet structure according to any one of [1] to [5], wherein the water-absorbing sheet structure is a suspension type water-absorbing sheet structure.
[7] The water-absorbent sheet structure according to any one of [1] to [6], wherein the water-absorbent sheet is a nonwoven fabric containing pulp as a main component.
[8] The water-absorbent sheet structure according to [7], wherein the water-absorbent sheet further contains a binder component.
[9] The water-absorbent sheet structure according to any one of [1] to [8], wherein the liquid-permeable member has at least one liquid-permeable hole.
[10] The water-absorbent sheet structure according to any one of [1] to [9], wherein the liquid-permeable member is a mesh member.
[11] The water-absorbent sheet structure according to any one of [1] to [10], wherein the liquid-permeable member has a tensile strength of 30 N / m or more.
[12] The water-absorbent sheet structure according to any one of [1] to [11], wherein the liquid-permeable member contains a resin selected from polyester, nylon and polyethylene as a main component.
[13] The water-absorbent sheet structure according to any one of [1] to [12], wherein the liquid-permeable member is a bag-shaped member.
[14] The water-absorbent sheet structure includes a plurality of water-absorbent sheets,
The liquid-permeable member has a plurality of storage sections for storing each water-absorbent sheet, or
The water-absorbent sheet structure according to any one of [1] to [13], wherein the liquid-permeable member is a member in which a plurality of bag-shaped members are connected.
本発明によれば、吸水性及び水蒸散性を有するシート構造体であって、水を吸水した際に破損等が生じにくいシート構造体を得ることができる。 ADVANTAGE OF THE INVENTION According to this invention, it is a sheet structure which has water absorbency and water transpiration, and it is hard to produce breakage etc. when absorbing water.
以下において、本発明について詳細に説明する。以下に記載する構成要件の説明は、代表的な実施形態や具体例に基づいてなされることがあるが、本発明はそのような実施形態に限定されるものではない。なお、本明細書において「〜」を用いて表される数値範囲は「〜」前後に記載される数値を下限値及び上限値として含む範囲を意味する。 Hereinafter, the present invention will be described in detail. The description of the components described below may be made based on representative embodiments or specific examples, but the present invention is not limited to such embodiments. In this specification, a numerical range represented by using “to” means a range including numerical values described before and after “to” as a lower limit and an upper limit.
（吸水シート構造体）
本発明は、吸水性シートと、吸水性シートを収容する収容部を有する液透過性部材と、を備える吸水シート構造体に関する。本発明の吸水シート構造体は、吸水性シートを備えるため、水分を十分に吸水することができ、かつ水蒸散性能を発揮することができる。また、本発明の吸水シート構造体は上記構成を有するものであるため、吸水性シートが水を吸水した際においても吸水性シートが破断することが抑制される。このように、本発明の吸水シート構造体は、吸水性及び水蒸散性に加え、湿潤時の耐破断性も兼ね備えている。
(Water absorbing sheet structure)
The present invention relates to a water-absorbent sheet structure including a water-absorbent sheet and a liquid-permeable member having a storage section for storing the water-absorbent sheet. Since the water-absorbing sheet structure of the present invention includes the water-absorbing sheet, it can sufficiently absorb water and exhibit water transpiration performance. Further, since the water-absorbing sheet structure of the present invention has the above-described configuration, even when the water-absorbing sheet absorbs water, the breakage of the water-absorbing sheet is suppressed. As described above, the water-absorbent sheet structure of the present invention has not only water absorbency and water transpiration but also rupture resistance when wet.
図１は、本発明の吸水シート構造体の構成を説明する斜視図である。図１に示されるように、本発明の吸水シート構造体１００において、吸水性シート１０は、液透過性部材２０に収容される。液透過性部材２０は、例えば、上端部に開口部を有する構造とすることができ、この開口部から吸水性シート１０を挿入することで、液透過性部材２０に吸水性シート１０を収容することができる。
FIG. 1 is a perspective view illustrating the configuration of the water-absorbent sheet structure of the present invention. As shown in FIG. 1, in the water-
図２は、本発明の吸水シート構造体の構成を説明する正面図である。図２に示されるように、吸水性シート１０は、その全部が液透過性部材２０の収容部に収容されることが好ましい。但し、吸水性シート１０の一部が液透過性部材２０の収容部に収容された状態で保持されてもよい。
FIG. 2 is a front view illustrating the configuration of the water-absorbent sheet structure of the present invention. As shown in FIG. 2, it is preferable that the water-
図２に示されるように、本発明の吸水シート構造体１００は、他の構造体と接合可能な接合部材３０をさらに備えることが好ましい。接合部材３０は１つのみ設けられてもよいが、２つ以上設けられることが好ましい。吸水シート構造体１００が接合部材３０を有することにより、吸水シート構造体１００と他の構造体との係合や連結が容易となる。
As shown in FIG. 2, it is preferable that the water-
本発明の吸水シート構造体は、吊下式吸水シート構造体であることが好ましい。すなわち、本発明の吸水シート構造体は、他の構造体や部材に吊り下げられた状態で使用される構造体であることが好ましい。吊下式吸水シート構造体は、後述するような接合部材を有することが好ましく、このような接合部材を他の構造体や部材に係合することで吸水シート構造体を吊下式とすることができる。吸水シート構造体を吊下式吸水シート構造体とすることにより、水蒸散性能をより効果的に高めることができる。 The water-absorbing sheet structure of the present invention is preferably a suspension-type water-absorbing sheet structure. That is, the water-absorbing sheet structure of the present invention is preferably a structure that is used while being suspended from another structure or member. The suspended water-absorbing sheet structure preferably has a joining member as described below, and the water-absorbing sheet structure is suspended by engaging such a joining member with another structure or member. Can be. By making the water-absorbing sheet structure a suspension-type water-absorbing sheet structure, the water transpiration performance can be more effectively improved.
本発明の吸水シート構造体は、１つの吸水性シートと、１つの収容部を有する液透過性部材２０からなるものであってもよい。また、本発明の吸水シート構造体は、複数の吸水性シートを備えるものであってもよい。吸水シート構造体が複数の吸水性シートを備えるものである場合、液透過性部材は、各吸水性シートを収容する複数の収容部を有するものであるか、もしくは、液透過性部材は、複数の袋状部材が連結した部材であることが好ましい。
The water-absorbent sheet structure of the present invention may be composed of one water-absorbent sheet and the liquid-
図３及び４は、複数の吸水性シートを備える吸水シート構造体の構成を説明する正面図である。図３では、１つの液透過性部材が各吸水性シートを収容する複数の収容部を有している。この場合、１つの液透過性部材が複数のポケット状の収容部を有することが好ましい。なお、図３では、１つの液透過性部材が２つの収容部を有している例を示しているが、収容部の数は特に限定されるものではない。例えば、１つの液透過性部材に設けられる収容部の数は、２つ以上であることが好ましく、３つ以上であることがより好ましく、５つ以上であることがさらに好ましい。また、１つの液透過性部材に設けられる収容部の数は、１００個以下であることが好ましく、５０個以下であることがより好ましい。 3 and 4 are front views illustrating the configuration of a water-absorbent sheet structure including a plurality of water-absorbent sheets. In FIG. 3, one liquid permeable member has a plurality of storage sections for storing the respective water absorbent sheets. In this case, it is preferable that one liquid permeable member has a plurality of pocket-shaped accommodation portions. Although FIG. 3 shows an example in which one liquid-permeable member has two storage sections, the number of storage sections is not particularly limited. For example, the number of storage portions provided in one liquid-permeable member is preferably two or more, more preferably three or more, and still more preferably five or more. In addition, the number of storage portions provided in one liquid permeable member is preferably 100 or less, and more preferably 50 or less.
図４では、液透過性部材は複数の袋状部材が連結した部材である。この場合、液透過性部材は、複数の液透過性部材の集合体であると言える。複数の液透過性部材は、各々、接合部材３０によって連結していることが好ましい。連結した液透過性部材の数は特に限定されるものではないが、例えば、２つ以上であることが好ましく、３つ以上であることがより好ましく、５つ以上であることがさらに好ましい。また、連結した液透過性部材の数は、１００個以下であることが好ましく、５０個以下であることがより好ましい。
In FIG. 4, the liquid-permeable member is a member in which a plurality of bag-shaped members are connected. In this case, it can be said that the liquid-permeable member is an aggregate of a plurality of liquid-permeable members. It is preferable that the plurality of liquid-permeable members are connected to each other by the joining
本発明では、吸水シート構造体が複数の吸水性シートを備える場合において、吸水性シート同士を直接的に連結せずに、液透過性部材に複数の収容部を設けたり、また、複数の液透過性部材を連結することとしている。これにより、吸水性シートが十分量の水分を吸水した場合であっても、自重や他重により、吸水性シートが破断することがない。また、吸水シート構造体が複数の吸水性シートを備えることにより、吸水性シートの合計表面積を大きくすることができ、大面積化が可能となる。このため、本発明の吸水シート構造体は、高い吸水性を発揮することができ、結果として、優れた水蒸散性を発揮することができる。 In the present invention, when the water-absorbent sheet structure includes a plurality of water-absorbent sheets, the liquid-absorbent sheets are not directly connected to each other, and a plurality of storage portions are provided in the liquid-permeable member, or a plurality of liquid-absorbent sheets are provided. The transmissive member is connected. Thereby, even when the water-absorbent sheet absorbs a sufficient amount of water, the water-absorbent sheet does not break due to its own weight or other weight. In addition, since the water-absorbent sheet structure includes a plurality of water-absorbent sheets, the total surface area of the water-absorbent sheet can be increased, and the area can be increased. Therefore, the water-absorbing sheet structure of the present invention can exhibit high water absorption, and as a result, can exhibit excellent water transpiration.
（吸水性シート）
本発明の吸水シート構造体においては、吸水性シートが十分な量の水分を吸水し、その水分を徐放することで、水蒸散性能を発揮することができる。このため、吸水性シートはある程度の大きさを有し、かつ十分な吸水性能を有することが好ましい。具体的には、１つの吸水性シートの最大面の面積は、１００ｃｍ2以上であることが好ましく、１５０ｃｍ2以上であることがより好ましく、２００ｃｍ2以上であることがさらに好ましい。なお、吸水性シートの最大面の面積は、１０ｍ2以下であることが好ましい。吸水性シートの最大面の面積を上記範囲内とすることにより、十分量の水分を吸水することができ、吸水した水を徐放することで、優れた水蒸散性能を発揮し得る。
(Water absorbent sheet)
In the water-absorbent sheet structure of the present invention, the water-absorbent sheet absorbs a sufficient amount of water and gradually releases the water, thereby exhibiting water transpiration performance. For this reason, the water absorbing sheet preferably has a certain size and sufficient water absorbing performance. Specifically, the area of the largest surface of one water-absorbent sheet is preferably 100 cm 2 or more, more preferably 150 cm 2 or more, and even more preferably 200 cm 2 or more. The area of the largest surface of the water-absorbent sheet is preferably 10 m 2 or less. By setting the area of the largest surface of the water-absorbent sheet within the above range, a sufficient amount of water can be absorbed, and excellent water transpiration performance can be exhibited by releasing the absorbed water gradually.
吸水性シートはシート状体であり、その厚みは特に限定されるものではないが、例えば、１ｍｍ以上であることが好ましく、２ｍｍ以上であることがより好ましい。また、吸水性シートの厚みは、１００ｍｍ以下であることが好ましく、５０ｍｍ以下であることがより好ましい。吸水性シートの厚みを上記範囲内とすることにより、水分の吸水と放出がスムーズになる。 The water-absorbent sheet is a sheet-like body, and its thickness is not particularly limited, but is, for example, preferably 1 mm or more, and more preferably 2 mm or more. Further, the thickness of the water-absorbent sheet is preferably 100 mm or less, more preferably 50 mm or less. By setting the thickness of the water-absorbent sheet within the above range, water absorption and release of water become smooth.
厚みがＴ（ｍｍ）の吸水性シートを蒸留水に５分間浸漬した後に、５０メッシュの金網上に水平となるように１分間静置した場合、吸水性シートの吸水量は、Ｔ×３００ｇ／ｍ2以上であることが好ましく、Ｔ×４００ｇ／ｍ2以上であることがより好ましく、
Ｔ×５００ｇ／ｍ2以上であることがさらに好ましく、Ｔ×６００ｇ／ｍ2以上であることが特に好ましい。なお、吸水性シートの吸水量の上限値は特に限定されるものではない。ここで、吸水性シートの吸水量はシートの単位面積（１ｍ2）あたりの吸水質量であり、以下の式により算出される。
吸水量（ｇ／ｍ2）＝（浸漬・静置後の吸水性シートの質量−浸漬前の吸水性シートの質量）／吸水性シートの面積（ｍ2）
なお、吸水性シートを蒸留水に浸漬する際には、吸水性シートのすべての面が水面下に存在するように浸漬を行う。
When a water-absorbent sheet having a thickness of T (mm) is immersed in distilled water for 5 minutes and then left standing on a 50-mesh wire net for 1 minute, the water-absorbent sheet has a water absorption of T × 300 g / m 2 or more, more preferably T × 400 g / m 2 or more,
It is more preferably at least T × 500 g / m 2 , particularly preferably at least T × 600 g / m 2 . The upper limit of the water absorption of the water-absorbent sheet is not particularly limited. Here, the water absorption of the water-absorbent sheet is the mass of water absorbed per unit area (1 m 2 ) of the sheet, and is calculated by the following equation.
Water absorption (g / m 2 ) = (mass of water-absorbent sheet after immersion and standing−mass of water-absorbent sheet before immersion) / area of water-absorbent sheet (m 2 )
When immersing the water-absorbent sheet in distilled water, immersion is performed so that all surfaces of the water-absorbent sheet are below the water surface.
吸水性シートの坪量は、５０ｇ／ｍ2以上であることが好ましく、１００ｇ／ｍ2以上であることがより好ましく、１５０ｇ／ｍ2以上であることがさらに好ましい。吸水性シートの坪量を上記範囲内とすることにより、吸水性及び水蒸散性に加え、湿潤時の耐破断性を高めることができる。 The basis weight of the water-absorbent sheet is preferably at least 50 g / m 2, more preferably at least 100 g / m 2 , even more preferably at least 150 g / m 2 . By setting the basis weight of the water-absorbent sheet within the above range, the water-absorbing property and the water transpiration property as well as the rupture resistance when wet can be enhanced.
吸水性シートは、不織布であることが好ましく、パルプ（パルプ繊維）を主成分として含む不織布であることがより好ましい。ここで、主成分とは、該成分を５０質量％以上含むことをいう。吸水性シートにおけるパルプの含有量は、吸水性シートの全質量に対して、５０質量％以上であることが好ましく、６０質量％以上であることがより好ましく、７０質量％以上であることがさらに好ましく、８０質量％以上であることが特に好ましい。なお、吸水性シートはパルプからなる不織布であってもよい。 The water-absorbent sheet is preferably a nonwoven fabric, and more preferably a nonwoven fabric containing pulp (pulp fiber) as a main component. Here, the main component means that the component is contained at 50% by mass or more. The content of pulp in the water-absorbent sheet is preferably 50% by mass or more, more preferably 60% by mass or more, and further preferably 70% by mass or more, based on the total mass of the water-absorbent sheet. It is particularly preferably at least 80% by mass. Note that the water-absorbent sheet may be a nonwoven fabric made of pulp.
パルプとしては、木材パルプ（針葉樹、広葉樹）、ラグパルプ、リンターパルプ、リネンパルプ、楮・三椏・雁皮パルプなどの非木材パルプ、古紙パルプなどの原料パルプから得られたものが例示できる。原料パルプとしては、機械パルプ（ＧＰ、ＲＧＰ、ＴＭＰ）、化学パルプ（亜硫酸パルプ、クラフトパルプ）を挙げることができる。中でも、パルプとしては、木材パルプを用いることが好ましい。 Examples of the pulp include those obtained from raw pulp such as wood pulp (coniferous and hardwood), rug pulp, linter pulp, linen pulp, non-wood pulp such as mulberry, mitsumata, and goose pulp, and waste paper pulp. Examples of the raw pulp include mechanical pulp (GP, RGP, TMP) and chemical pulp (sulfite pulp, kraft pulp). Among them, wood pulp is preferably used as pulp.
パルプ繊維の繊維幅は特に限定されるものではないが、繊維幅が１μｍ以上のパルプ繊維であることが好ましい。また、吸水性シートは、繊維幅が１μｍ未満の微細繊維状セルロース（ナノセルロースファイバー）を含むものであってもよい。吸水性シートに繊維幅が１μｍ未満の微細繊維状セルロースを含有させることで、吸水性シートの水分保持力を高めることもできる。 The fiber width of the pulp fiber is not particularly limited, but is preferably a pulp fiber having a fiber width of 1 μm or more. Further, the water-absorbent sheet may contain fine fibrous cellulose (nanocellulose fiber) having a fiber width of less than 1 μm. By including fine fibrous cellulose having a fiber width of less than 1 μm in the water-absorbent sheet, the water-retaining ability of the water-absorbent sheet can be increased.
パルプ繊維の質量平均繊維長は、特に限定されないが、０．０５〜５ｍｍであることが好ましい。パルプ繊維の繊維長を上記範囲内とすることにより、パルプ繊維が吸水性シートから脱落することが抑制され、吸水率を高めることができる。 The mass average fiber length of the pulp fiber is not particularly limited, but is preferably 0.05 to 5 mm. By setting the fiber length of the pulp fiber within the above range, the pulp fiber is prevented from falling off the water-absorbent sheet, and the water absorption can be increased.
また、吸水性シートは、さらにバインダー成分を含むものであることが好ましい。バインダー成分は、パルプ繊維を結着させる働きをすることが好ましい。これにより、吸水性シートからパルプ繊維が意図せずに脱落することをより効果的に抑制することができる。 Further, it is preferable that the water-absorbing sheet further contains a binder component. The binder component preferably functions to bind pulp fibers. This makes it possible to more effectively prevent the pulp fibers from unintentionally falling off the water-absorbent sheet.
バインダー成分は熱融着性樹脂であることが好ましい。熱融着性樹脂は、加熱により少なくとも一部の熱融着性樹脂が溶融した後に、溶融樹脂が固まることで、各繊維を結着させる。このような熱融着性樹脂としては、例えば、ポリエチレン（共重合ポリエチレンを包含する）、ポリプロピレン（変性ポリプロピレン、及び共重合ポリプロピレンを包含する）、低融点ポリエステル（例えば低融点ポリエチレンテレフタレート）、低融点ポリアミド、低融点ポリ乳酸、ポリブチレンサクシネート、アクリル樹脂、ウレタン樹脂、スチレンブタジエン共重合体、ポリビニルアルコール（ＰＶＡ）、エチレン−酢酸ビニル共重合体（ＥＶＡ）等からなる合成繊維を挙げることができる。 The binder component is preferably a heat-fusible resin. The heat fusible resin binds each fiber by solidifying the molten resin after at least a part of the heat fusible resin is melted by heating. Examples of such a heat-fusible resin include polyethylene (including copolymerized polyethylene), polypropylene (including modified polypropylene and copolymerized polypropylene), low-melting polyester (eg, low-melting polyethylene terephthalate), and low-melting polyester. Synthetic fibers composed of polyamide, low melting point polylactic acid, polybutylene succinate, acrylic resin, urethane resin, styrene butadiene copolymer, polyvinyl alcohol (PVA), ethylene-vinyl acetate copolymer (EVA), and the like can be given. .
熱融着性樹脂は、単一の樹脂からなる単一繊維であってもよいが、二種以上の樹脂を組み合わせた複合樹脂であってもよい。例えば、融点の高い樹脂からなる芯部と、芯部の外周を被覆し、融点の低い樹脂からなる鞘を有する芯鞘型複合樹脂を用いてもよい。融点が異なる２種の樹脂を組み合わせた形態としては、ＰＥＴ／ＰＥＴ複合樹脂、ＰＥ／ＰＥ複合樹脂、ＰＰ／ＰＰ複合樹脂、ＥＶＡ／ＰＰ複合樹脂、ＰＥ／ＰＥＴ複合樹脂、ＰＰ／ＰＥＴ複合樹脂、ＰＥ／ＰＰ複合樹脂を挙げることができる。中でも、芯部にポリプロピレン繊維（融点１６０℃）を用い、被覆層にポリエチレン層（融点１３０℃）を用いた芯鞘型複合樹脂（ＰＥ／ＰＰ複合樹脂）は好ましく用いられる。このような芯鞘型複合樹脂を使用する場合には、外側の被覆層が溶融し芯部は溶融しない温度（一例として１４０℃）の熱風を加えて被覆層のみを溶融することが好ましい。また、本発明では、二種の融点の異なる樹脂を隣接して配置させた、サイドバイサイド型などの複合樹脂も使用することができる。 The heat-fusible resin may be a single fiber made of a single resin, or may be a composite resin in which two or more resins are combined. For example, a core-sheath composite resin having a core made of a resin having a high melting point and a sheath covering the outer periphery of the core and having a sheath made of a resin having a low melting point may be used. Examples of the combination of two resins having different melting points include PET / PET composite resin, PE / PE composite resin, PP / PP composite resin, EVA / PP composite resin, PE / PET composite resin, PP / PET composite resin, PE / PP composite resin can be mentioned. Among them, a core-sheath type composite resin (PE / PP composite resin) using a polypropylene fiber (melting point 160 ° C.) for the core and a polyethylene layer (melting point 130 ° C.) for the coating layer is preferably used. When such a core-sheath type composite resin is used, it is preferable that only the coating layer is melted by applying hot air at a temperature at which the outer coating layer melts and the core does not melt (for example, 140 ° C.). Further, in the present invention, a composite resin such as a side-by-side type resin in which two kinds of resins having different melting points are arranged adjacent to each other can also be used.
熱融着性樹脂の形状は特に限定されず、粉末状、粒状、繊維状、及びそれらを任意に組み合わせた形状とすることができる。熱融着性樹脂繊維は、捲縮（クリンプ、カール、スパイラル）していてもよく、パルプ繊維のようにフィブリル化されていてもよい。 The shape of the heat-fusible resin is not particularly limited, and may be powdery, granular, fibrous, or any combination thereof. The heat-fusible resin fiber may be crimped (crimp, curl, spiral) or fibrillated like pulp fiber.
吸水性シートに含まれるバインダー成分の含有量は、吸水性シートの全質量に対して、４９質量％以下であることが好ましく、３０質量％以下であることがより好ましく、２０質量％以下であることがさらに好ましい。 The content of the binder component contained in the water-absorbent sheet is preferably 49% by mass or less, more preferably 30% by mass or less, and more preferably 20% by mass or less based on the total mass of the water-absorbent sheet. Is more preferable.
吸水性シートは、さらに吸水性ポリマー（ＳＡＰ）を含んでもよい。また、吸水性シートは、吸水性ポリマー（ＳＡＰ）を繊維化した吸収性繊維（ＳＡＦ）を含んでもよい。ここで、吸水性ポリマー（ＳＡＰ）は、高吸水性ポリマーであり、「高吸水性」とは自重の２０倍以上の水分を吸収可能なことをいう。吸水性ポリマー（ＳＡＰ）としては、澱粉系、セルロース系、合成樹脂系等のものがあり、澱粉−アクリル酸（塩）グラフト共重合体、イソブチレン−マレイン酸共重合体、澱粉−アクリル酸エチルグラフト共重合体のケン化物、澱粉−メタクリル酸メチルグラフト共重合体のケン化物、澱粉−アクリロニトリル共重合体のケン化物、澱粉−アクリルアミドグラフト共重合体のケン化物、アクリル酸（塩）重合体、アクリル酸で架橋されたポリエチレンオキサイド、ナトリウムカルボキシメチルセルロースの架橋物、ポリビニルアルコール−無水マレイン酸共重合体の架橋物、生分解性のあるポリアスパラギン酸のアミノ酸架橋物、Ａｌｃａｌｉｇｅｎｅｓ Ｌａｔｕｓからの培養生成物等を挙げることができる。中でも、アクリル酸（塩）重合体は好ましく用いられ、特にポリアクリル酸ナトリウム系樹脂が好ましく用いられる。 The water absorbing sheet may further include a water absorbing polymer (SAP). Further, the water-absorbent sheet may include absorbent fibers (SAF) obtained by fibrillating a water-absorbent polymer (SAP). Here, the water-absorbing polymer (SAP) is a super-water-absorbing polymer, and “highly water-absorbing” means that it can absorb water at least 20 times its own weight. Examples of the water-absorbing polymer (SAP) include starch-based, cellulose-based, and synthetic resin-based polymers, such as starch-acrylic acid (salt) graft copolymer, isobutylene-maleic acid copolymer, starch-ethyl acrylate graft. Saponified copolymer, saponified starch-methyl methacrylate graft copolymer, saponified starch-acrylonitrile copolymer, saponified starch-acrylamide graft copolymer, acrylic acid (salt) polymer, acrylic Acid-crosslinked polyethylene oxide, sodium carboxymethylcellulose crosslinked product, polyvinyl alcohol-maleic anhydride copolymer crosslinked product, biodegradable polyaspartic acid amino acid crosslinked product, culture product from Alcaligenes Latus, etc. Can be mentioned. Among them, an acrylic acid (salt) polymer is preferably used, and a sodium polyacrylate resin is particularly preferably used.
吸水性シートは、上記成分の他に任意成分を含んでもよい。任意成分としては、例えば、難燃剤、紫外線吸収剤、光拡散剤、消臭剤、香料、着色剤、抗菌剤、防カビ剤等を挙げることができる。また、吸水性シートには、水分含有率を指標となる発色剤を添加することも好ましい。例えば、吸水性シートの水分含有率が一定値以下となった際に発色する発色剤を添加することで、給水のタイミングを容易に把握することができる。なお、吸水性シートにおける任意成分の含有量は、吸水性シートの全質量に対して、２０質量％以下であることが好ましく、１０質量％以下であることがより好ましい。 The water-absorbent sheet may contain optional components in addition to the above components. Examples of the optional component include a flame retardant, an ultraviolet absorber, a light diffusing agent, a deodorant, a fragrance, a coloring agent, an antibacterial agent, and a fungicide. Further, it is also preferable to add a color former having a water content as an index to the water absorbent sheet. For example, the timing of water supply can be easily grasped by adding a coloring agent which develops a color when the water content of the water-absorbent sheet becomes a certain value or less. The content of the optional component in the water-absorbent sheet is preferably 20% by mass or less, more preferably 10% by mass or less, based on the total mass of the water-absorbent sheet.
吸水性シートは、エアレイド法により形成されたシートであることが好ましい。エアレイド法とは、乾式不織布の形成方法の一つである。具体的には、上述したパルプ繊維を乾式で解繊し、解繊した繊維と、必要に応じて各種成分を混合しつつ空気を媒体として走行する金網上に堆積させることでウェブ（不織布シート）を形成する方法である。なお、ウェブを構成する繊維間はバインダー成分によって結着されることが好ましい。このように、吸水性シートは、エアレイド法によって形成された不織布（エアレイド不織布シート）であることが好ましい。 The water-absorbing sheet is preferably a sheet formed by an airlaid method. The airlaid method is one of the methods for forming a dry nonwoven fabric. Specifically, a web (nonwoven fabric sheet) is obtained by defibrating the above-mentioned pulp fiber in a dry manner and mixing the defibrated fiber and various components as necessary and depositing it on a wire mesh that travels using air as a medium. It is a method of forming. Preferably, the fibers constituting the web are bound by a binder component. Thus, the water-absorbent sheet is preferably a nonwoven fabric (airlaid nonwoven fabric sheet) formed by the airlaid method.
（液透過性部材）
本発明の吸水シート構造体は、吸水性シートを収容する収容部を有する液透過性部材を備える。液透過性部材は、水分を透過させる性質を有しているものであれば特に限定されるものではない。本発明の吸水シート構造体においては、上述したように吸水性シートが十分な量の水分を吸水し、その水分を徐放することで、水蒸散性能を発揮することができる。液透過性部材は、吸水性シートが吸水する水分及び徐放する水分の往来を阻害することがなく、高いレベルの液透過性を有している。
(Liquid permeable member)
The water-absorbent sheet structure of the present invention includes a liquid-permeable member having a storage section for storing the water-absorbent sheet. The liquid-permeable member is not particularly limited as long as it has a property of transmitting moisture. In the water-absorbent sheet structure of the present invention, as described above, the water-absorbent sheet absorbs a sufficient amount of water and gradually releases the water, thereby exhibiting water transpiration performance. The liquid-permeable member has a high level of liquid permeability without hindering the movement of the water absorbed by the water-absorbent sheet and the water gradually released.
液透過性部材は、袋状部材であることが好ましい。液透過性部材は、袋状部材の少なくともいずれか一辺に開口部を有することが好ましく、この開口部から吸水性シートの出し入れが行われる。開口部には、開閉自在な係止部材が設けられていてもよい。例えば、ボタンやファスナー、面ファスナーといった係止部材が設けられていてもよい。これにより、液透過性部材から吸水性シートが意図せずに脱落することを抑制することができる。 The liquid-permeable member is preferably a bag-like member. The liquid-permeable member preferably has an opening on at least one side of the bag-like member, and the water-absorbent sheet is taken in and out from this opening. The opening may be provided with a locking member that can be opened and closed. For example, a locking member such as a button, a fastener, or a hook-and-loop fastener may be provided. This can prevent the water-absorbent sheet from unintentionally falling off the liquid-permeable member.
液透過性部材は、水分の透過性をより高めるという観点から、少なくとも１つの液透過孔を有するものであることが好ましい。液透過孔は、貫通孔であることが好ましく、吸水性シートが吸水する水分及び徐放する水分の往来を阻害することのない大きさを有することが好ましい。具体的には、貫通孔の開口部面積は１ｍｍ2以上５０ｍｍ2以下であることが好ましい。なお、液透過性部材に貫通孔が多数設けられる場合は、貫通孔は、微細孔であってもよい。 It is preferable that the liquid permeable member has at least one liquid permeable hole from the viewpoint of further increasing the water permeability. The liquid permeation hole is preferably a through hole, and preferably has a size that does not hinder the flow of water absorbed by the water-absorbent sheet and water released gradually. Specifically, the opening area of the through hole is preferably 1 mm 2 or more and 50 mm 2 or less. When a large number of through holes are provided in the liquid permeable member, the through holes may be fine holes.
液透過性部材は、多数の液透過孔を有するものであることが好ましく、液透過性部材は網目状部材であることが好ましい。液透過性部材が網目状部材である場合、液透過性部材は、ネット状シートやメッシュ状シートから構成される部材であることが好ましい。 The liquid permeable member preferably has a large number of liquid permeable holes, and the liquid permeable member is preferably a mesh member. When the liquid-permeable member is a mesh member, the liquid-permeable member is preferably a member composed of a net-like sheet or a mesh-like sheet.
液透過性部材の引張強度は、３０Ｎ／ｍ以上であることが好ましく、５０Ｎ／ｍ以上であることがより好ましい。液透過性部材の引張強度を上記下限値以上とすることにより、吸水性シートが多量の水を吸水した場合であっても、液透過性部材が破断することなく、吸水性シートを安定的に保持することができる。また、液透過性部材の引張強度を上記下限値以上とすることにより、吸水シート構造体が複数の吸水性シートを備える場合においても、多数の吸水性シートを保持することが可能となる。例えば、複数の吸水性シートが吸水して、最上端にかかる重量が１００ｋｇを超えた場合であっても、液透過性部材は破断することなく、吸水性シートを保持することができる。
ここで、液透過性部材の引張強度を算出する際には、まず、紙及び板紙の引張特性の試験方法（定速伸張法）ＪＩＳ Ｐ ８１１３：２００６に準じて、液透過性部材の最大引張荷重を測定する。その後、以下の式を用いて、液透過性部材の引張強度を算出する。なお、液透過性部材の引張強度は、液透過性部材１枚の引張強度である。
Ｓ（引張強度）＝Ｆ（最大引張荷重）／Ｗ（試験片の初期幅）
The tensile strength of the liquid-permeable member is preferably 30 N / m or more, more preferably 50 N / m or more. By setting the tensile strength of the liquid-permeable member to be equal to or more than the lower limit, even when the water-absorbent sheet absorbs a large amount of water, the liquid-permeable member does not break and the water-absorbent sheet can be stably formed. Can be held. Further, by setting the tensile strength of the liquid-permeable member to be equal to or more than the lower limit, even when the water-absorbent sheet structure includes a plurality of water-absorbent sheets, it is possible to hold a large number of water-absorbent sheets. For example, even when a plurality of water-absorbent sheets absorb water and the weight applied to the uppermost end exceeds 100 kg, the liquid-permeable member can hold the water-absorbent sheet without breaking.
Here, when calculating the tensile strength of the liquid-permeable member, first, the maximum tensile strength of the liquid-permeable member is determined in accordance with JIS P 8113: 2006, a method for testing the tensile properties of paper and paperboard (constant speed extension method). Measure the load. Thereafter, the tensile strength of the liquid-permeable member is calculated using the following equation. In addition, the tensile strength of the liquid-permeable member is the tensile strength of one liquid-permeable member.
S (tensile strength) = F (maximum tensile load) / W (initial width of test piece)
液透過性部材は、ポリエステル、ナイロン及びポリエチレンから選択される樹脂を主成分として含む部材であることが好ましい。中でも、液透過性部材は、ナイロンを主成分として含む部材であることが好ましい。ここで、主成分とは、該成分を５０質量％以上含むことをいう。なお、液透過性部材を構成する樹脂は、非吸水性であることが好ましく、撥水性を有していてもよい。 The liquid-permeable member is preferably a member containing a resin selected from polyester, nylon and polyethylene as a main component. In particular, the liquid-permeable member is preferably a member containing nylon as a main component. Here, the main component means that the component is contained at 50% by mass or more. The resin constituting the liquid permeable member is preferably non-water-absorbing, and may have water repellency.
液透過性部材には加飾が施されてもよい。例えば、色付きの液透過性部材を用いたり、必要に応じて他の加飾部材を付設してもよい。液透過性部材が複数の袋状部材が連結した部材である場合は、各袋状部材を異なる色にしたり、装飾を施したりすることで、吸水シート構造体の意匠性や利便性を高めることもできる。 The liquid-permeable member may be decorated. For example, a colored liquid-permeable member may be used, or another decorative member may be provided as needed. When the liquid-permeable member is a member in which a plurality of bag-shaped members are connected, each bag-shaped member is made to have a different color or decorated to enhance the design and convenience of the water-absorbing sheet structure. Can also.
（接合部材）
図２に示されるように、本発明の吸水シート構造体１００は、他の構造体と接合可能な接合部材３０をさらに備えることが好ましい。接合部材３０は、他の吸水シート構造体１００と接合可能な部材であってもよく、吸水シート構造体ではない、他の構造体と接合可能な部材であってもよい。この場合、他の構造体としては、吸水シート構造体１００を吊り下げるための構造体や、吸水シート構造体１００を係合するための構造体が挙げられる。なお、吸水シート構造体１００に複数の接合部材３０が備え付けられている場合は、各々の接合部材３０の形状や構造は異なっていてもよく、同一であってもよい。
(Joining members)
As shown in FIG. 2, it is preferable that the water-
図２においては、接合部材３０は、液透過性部材２０に取り付けられた別個の部材として描画されているが、接合部材３０は、液透過性部材２０と一体となった部材であってもよい。例えば、液透過性部材２０の左右側端部に帯状部材を設け、この帯状部材を延出させることで接合部材３０を形成してもよい。この場合、接合部材３０と液透過性部材２０を構成する材料が共通していてもよい。接合部材３０が液透過性部材２０に取り付けられた別個の部材である場合、接合部材３０は液透過性部材２０を他の部材に緊結し得る部材であればよい。例えば、結束バンド、フック、紐、針金等の部材を挙げることができる。また、接合部材３０の材質としては、金属、合成樹脂、繊維等を挙げることができる。なお、接合部材３０を磁石から構成した部材や、接合箇所に磁石を配設した部材としてもよい。この場合、磁力により、接合部材の接合箇所を係合することがきできる。
In FIG. 2, the joining
接合部材が液透過性部材に取り付けられている場合、接合部材は、液透過性部材の上端側に係合されていることが好ましい。また、係合箇所は、２箇所以上であることが好ましく、例えば、液透過性部材の上端側の角部近傍であることが好ましい。この場合、接合部材の取り付け箇所は、液透過性部材の上端縁から、１０ｍｍ以上内側であって、１００ｍｍまでの距離の間にある好ましい。また、接合部材の取り付け箇所は、液透過性部材の左右端縁から、１０ｍｍ以上内側であって、１５０ｍｍまでの距離の間にあることが好ましい。これにより、液透過性部材が吸水性シートの重みにより破損することを抑制することができる。また、吸水シート構造体を他の部材に係合した際に、その安定性を高めることができる。 When the joining member is attached to the liquid-permeable member, it is preferable that the joining member is engaged with the upper end side of the liquid-permeable member. In addition, it is preferable that the number of engagement portions is two or more, for example, it is preferable that the engagement portion is near a corner on the upper end side of the liquid permeable member. In this case, it is preferable that the attachment portion of the joining member be located 10 mm or more inside the upper end edge of the liquid-permeable member and at a distance of up to 100 mm. Further, it is preferable that the attachment portion of the joining member is located at least 10 mm inside and at a distance of up to 150 mm from the left and right edges of the liquid-permeable member. This can prevent the liquid-permeable member from being damaged by the weight of the water-absorbent sheet. Further, when the water-absorbing sheet structure is engaged with another member, the stability can be improved.
液透過性部材が、複数の袋状部材が連結した部材である場合は、液透過性部材の下端側の角部近傍には、接合受け部材が設けられていてもよい。接合受け部材としては、液透過性部材に環装されたリングホルダー等を挙げることができる。これにより、ある一つの液透過性部材の接合部材を、他の液透過性部材の接合受け部材に係合することで、複数の液透過性部材が連結した吸水シート構造体を容易に形成することができる。また、接合受け部材を設けることにより、接合強度を高めることができ、液透過性部材の破断等を抑制することができる。 When the liquid-permeable member is a member in which a plurality of bag-shaped members are connected, a joint receiving member may be provided near a corner on the lower end side of the liquid-permeable member. As the joining receiving member, a ring holder or the like mounted around a liquid-permeable member can be used. Thereby, the joining member of one liquid permeable member is engaged with the joining receiving member of another liquid permeable member, so that a water absorbing sheet structure in which a plurality of liquid permeable members are connected can be easily formed. be able to. Further, by providing the joining receiving member, the joining strength can be increased, and breakage of the liquid-permeable member can be suppressed.
接合部材は、懸吊用係合部材であることが好ましい。すなわち、接合部材は、吸水シート構造体を他の構造体や部材に吊り下げ可能とする部材であることが好ましい。また、接合部材は脱着可能な部材であることが好ましく、これにより必要に応じて接合様式を変更することもできる。 The joining member is preferably a suspension engaging member. That is, the joining member is preferably a member that allows the water-absorbing sheet structure to be hung by another structure or member. Further, the joining member is preferably a detachable member, so that the joining mode can be changed as needed.
また、接合部材は、吸水シート構造体の連結方向に伸びる一連の紐状部材であってもよい。例えば、１本のロープ状部材もしくは１組のロープ状部材に複数の吸水シート構造体を固定することで複数の吸水性シートを備えた吸水シート構造体を形成してもよい。 Further, the joining member may be a series of string-like members extending in the connection direction of the water-absorbing sheet structure. For example, a plurality of water-absorbing sheet structures may be fixed to one rope-shaped member or a set of rope-shaped members to form a water-absorbing sheet structure provided with a plurality of water-absorbing sheets.
（吸水シート構造体の使用方法）
吸水シート構造体の使用する際には、吸水シート構造体を水分に浸漬する工程を含むことが好ましい。浸漬する工程では、吸水シート構造体を水に浸漬してもよく、また、吸水シート構造体に水を給水してもよい。給水の方法としては、水分を流入させる方法や、塗布や噴霧による方法が挙げられる。なお、吸水シート構造体の使用する際には、予め水分を含浸させた吸水性シートを液透過性部材に収容することで、水分を吸水した吸水シート構造体を得てもよい。
(How to use the water-absorbing sheet structure)
When using the water-absorbing sheet structure, it is preferable to include a step of immersing the water-absorbing sheet structure in moisture. In the immersion step, the water-absorbent sheet structure may be immersed in water, or water may be supplied to the water-absorbent sheet structure. Examples of the water supply method include a method of flowing in water, a method of applying and spraying. When using the water-absorbent sheet structure, the water-absorbent sheet structure impregnated with moisture may be stored in a liquid-permeable member to obtain a water-absorbent sheet structure that has absorbed water.
図３及び４に示されたように、吸水シート構造体が複数の吸水性シートを備える場合、最上位にある吸水性シートに水分を給水することとしてもよい。本発明の吸水シート構造体においては、液透過性部材は水分を透過させるものであるため、吸水シート構造体を懸吊することで、上流側で給水された水分が下流の吸水性シートにも行き渡ることとなる。例えば、懸吊状態の吸水シート構造体の最上位の吸水性シートに水分を給水することで、複数の吸水性シートに水分を行き渡らせることができるため、給水を容易に行うことができる。 As shown in FIGS. 3 and 4, when the water-absorbent sheet structure includes a plurality of water-absorbent sheets, water may be supplied to the uppermost water-absorbent sheet. In the water-absorbent sheet structure of the present invention, since the liquid-permeable member is permeable to moisture, by suspending the water-absorbent sheet structure, the water supplied on the upstream side allows the water supplied on the downstream side also to the water-absorbent sheet. Will go around. For example, by supplying water to the uppermost water-absorbent sheet of the suspended water-absorbent sheet structure, water can be distributed to a plurality of water-absorbent sheets, so that water can be supplied easily.
吸水シート構造体から、水分が蒸散した後には、再度給水を行うことで、吸水性シートに水分を含浸させてもよい。このように、本発明の吸水シート構造体は繰り返しの利用が可能である。 After water evaporates from the water-absorbent sheet structure, water may be supplied again to impregnate the water-absorbent sheet with water. Thus, the water-absorbing sheet structure of the present invention can be used repeatedly.
（用途）
本発明の吸水シート構造体は、吸水性と水蒸散性能に優れているため、例えば、熱遮蔽用シート、光遮蔽用シート、冷却用シート、加湿用シートとして用いることができる。また、吸水性シートに各種薬剤や香料等を含浸させることにより、本発明の吸水シート構造体は、芳香性シートや防虫シート、殺虫シートとして用いることもできる。
(Application)
Since the water-absorbing sheet structure of the present invention is excellent in water absorption and water transpiration performance, it can be used as, for example, a heat shielding sheet, a light shielding sheet, a cooling sheet, and a humidifying sheet. Further, by impregnating the water-absorbing sheet with various chemicals, fragrances, and the like, the water-absorbing sheet structure of the present invention can be used as an aromatic sheet, an insect repellent sheet, and an insecticidal sheet.
以下に実施例と比較例を挙げて本発明の特徴をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す具体例により限定的に解釈されるべきものではない。 Hereinafter, features of the present invention will be described more specifically with reference to examples and comparative examples. Materials, usage amounts, ratios, processing contents, processing procedures, and the like shown in the following examples can be appropriately changed without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be construed as being limited by the specific examples described below.
＜製造例１＞
（吸水性シートの作製）
針葉樹晒クラフトパルプ（ＮＢＫＰ）を気流中で解繊して解繊ＮＢＫＰ繊維とした。これにポリエチレン／ポリプロピレン複合繊維（繊維長５ｍｍ、繊度１．７ｄｔｅｘ）を混合して、ＮＢＫＰ７５質量部とポリエチレン／ポリプロピレン複合繊維２５質量部からなるエアレイド用ウェブ原料を得た。
<Production Example 1>
(Preparation of water-absorbent sheet)
Softwood bleached kraft pulp (NBKP) was defibrated in an air stream to obtain defibrated NBKP fibers. A polyethylene / polypropylene composite fiber (fiber length 5 mm, fineness 1.7 dtex) was mixed with the mixture to obtain an airlaid web raw material composed of NBKP 75 parts by mass and polyethylene / polypropylene composite fiber 25 parts by mass.
サクションボックスを有するメッシュコンベヤ上に、キャリアシートとして、坪量５５ｇ／ｍ2のエアレイド不織布（商品名：難燃性キノクロスＫＦＲ５５、王子キノクロス株式会社製）を繰り出し、その上に、粉体フィーダーを利用し、１０ｇ／ｍ2となるように熱融着性樹脂（ポリエチレンパウダー）を散布した。次いで、マットフォーマーを使用して、上記で得たエアレイド用ウェブ原料を、坪量が１３３３ｇ／ｍ2になるように落下堆積させた。さらに、その上に、粉体フィーダーを利用し、７ｇ／ｍ2となるように熱融着性樹脂（ポリエチレンパウダー）を散布し、キャリアシートとして用いたものと同じエアレイド不織布を積層して、合計坪量１６００ｇ／ｍ2のエアレイドウェブを得た。 An air-laid nonwoven fabric having a basis weight of 55 g / m 2 (trade name: Flame Retardant Kino Cloth KFR55, manufactured by Oji Kino Cloth Co., Ltd.) is fed out as a carrier sheet on a mesh conveyor having a suction box, and a powder feeder is used thereon. Then, a heat-fusible resin (polyethylene powder) was sprayed so as to be 10 g / m 2 . Then, using a mat former, the web material for airlaid obtained above was dropped and deposited so that the basis weight was 1333 g / m 2 . Further, a heat-fusible resin (polyethylene powder) was sprayed thereon at 7 g / m 2 using a powder feeder, and the same air-laid non-woven fabric as that used as the carrier sheet was laminated thereon. An airlaid web having a basis weight of 1600 g / m 2 was obtained.
このようにして得たエアレイドウェブを加熱炉で１４０℃に加熱し、熱加圧ロールで処理して、坪量１６００ｇ／ｍ2、厚さ２０ｍｍの吸水性シート用不織布を得た。得られた吸水性シート用不織布の水平吸水量は２００００ｇ／ｍ2であった。この吸水性シート用不織布を、６０ｃｍ四方の正方形に裁断し、吸水性シートを得た。 The air-laid web thus obtained was heated to 140 ° C. in a heating furnace and treated with a hot press roll to obtain a nonwoven fabric for a water-absorbent sheet having a basis weight of 1600 g / m 2 and a thickness of 20 mm. The horizontal water absorption of the obtained nonwoven fabric for a water absorbent sheet was 20,000 g / m 2 . This nonwoven fabric for a water-absorbent sheet was cut into a square of 60 cm square to obtain a water-absorbent sheet.
（液透過性部材の作製）
市販のナイロンメッシュ（商品名：＃３０１０ナイロンメッシュ、富士ニツティング製）を、幅７０ｃｍ、長さ１５０ｃｍに裁断した。断裁したナイロンメッシュ生地を、半分の長さで二つ折りにし、市販の結束バンド（商品名：ＴＲＪ１００ナイロン結束バンド、トラスコ中山製）を用いて、断裁したナイロンメッシュの幅方向両端をかがる形で、両端から５ｍｍのところを１０ｃｍ間隔で結束した。このようにして、上端部の幅方向に開口部を有する、幅６９ｃｍ、深さ７５ｃｍの袋状に加工し、液透過性部材とした。このようにして、複数個の液透過性部材を作製した。
(Production of liquid permeable member)
A commercially available nylon mesh (trade name: # 3010 nylon mesh, manufactured by Fuji Nitting) was cut into a width of 70 cm and a length of 150 cm. The cut nylon mesh fabric is folded in half at half length, and both ends in the width direction of the cut nylon mesh are bent using a commercially available binding band (trade name: TRJ100 nylon binding band, manufactured by Trusco Nakayama). Then, the portion 5 mm from both ends was bound at 10 cm intervals. In this way, a bag having a width of 69 cm and a depth of 75 cm having an opening in the width direction of the upper end was processed into a liquid-permeable member. Thus, a plurality of liquid-permeable members were produced.
（液透過性部材の支持部材への固定）
シート構造体を適用する支持部材（接合部材）として、市販の６ｍｍナイロンロープ５ｍを水平に張った。このナイロンロープの長さ方向に沿って、複数の液透過性部材が連続して固定されるように、液透過性部材の開口部端辺を固定した。各液透過性部材をナイロンロープに固定する際には、開口部の片側のナイロンメッシュ生地をナイロンロープ上に重ね、１０ｃｍおきに市販の結束バンドを用いて固定した。固定した液透過性部材の開口部から、６０ｃｍ四方の吸水性シートを挿入し、吸水シート構造体１を作製した。
(Fixing of liquid permeable member to support member)
As a support member (joining member) to which the sheet structure was applied, a commercially available 6 mm nylon rope 5 m was stretched horizontally. The edge of the opening of the liquid permeable member was fixed so that the plurality of liquid permeable members were continuously fixed along the length direction of the nylon rope. When fixing each liquid permeable member to the nylon rope, the nylon mesh cloth on one side of the opening was placed on the nylon rope, and fixed every 10 cm using a commercially available binding band. A water-absorbing sheet of 60 cm square was inserted from the opening of the fixed liquid-permeable member to produce a water-absorbing sheet structure 1.
＜製造例２＞
市販の不織布（商品名：ハトシートＸＣＡ６、王子キノクロス株式会社製、坪量８００ｇ／ｍ2、厚さ６ｍｍ）を吸水性シート用不織布として使用した以外は製造例１と同様にして、吸水シート構造体２を作製した。なお、ハトシートＸＣＡ６の水平吸水量は、１００００ｇ／ｍ2であった。
<Production Example 2>
A water-absorbent sheet structure was produced in the same manner as in Production Example 1 except that a commercially available nonwoven fabric (trade name: Pigeon Sheet XCA6, manufactured by Oji Kinocross Co., Ltd., basis weight 800 g / m 2 , thickness 6 mm) was used as the nonwoven fabric for the water-absorbent sheet. 2 was produced. In addition, the horizontal water absorption of the pigeon sheet XCA6 was 10,000 g / m 2 .
（評価）
＜吸水量＞
吸水性シートを蒸留水に５分間浸漬した後に、１分間、５０メッシュの金網上に水平となるように静置した。その後、吸水量を以下の式により算出した。
吸水量（ｇ／ｍ2）＝（浸漬・静置後の吸水性シートの質量−浸漬前の吸水性シートの質量）／吸水性シートの面積（ｍ2）
(Evaluation)
<Water absorption>
After the water-absorbent sheet was immersed in distilled water for 5 minutes, it was allowed to stand on a 50-mesh wire net for 1 minute so as to be horizontal. Thereafter, the water absorption was calculated by the following equation.
Water absorption (g / m 2 ) = (mass of water-absorbent sheet after immersion and standing−mass of water-absorbent sheet before immersion) / area of water-absorbent sheet (m 2 )
＜引張強度＞
紙及び板紙の引張特性の試験方法（定速伸張法）ＪＩＳ Ｐ ８１１３：２００６に準じて、液透過性部材の最大引張荷重を測定した。液透過性部材の引張強度は、以下の式で算出される値である。なお、液透過性部材の引張強度は、液透過性部材１枚の引張強度である。
Ｓ（引張強度）＝Ｆ（最大引張荷重）／Ｗ（試験片の初期幅）
<Tensile strength>
Test method for tensile properties of paper and paperboard (constant speed extension method) The maximum tensile load of the liquid-permeable member was measured according to JIS P 8113: 2006. The tensile strength of the liquid-permeable member is a value calculated by the following equation. In addition, the tensile strength of the liquid-permeable member is the tensile strength of one liquid-permeable member.
S (tensile strength) = F (maximum tensile load) / W (initial width of test piece)
（評価結果）
製造例で得られた吸水シート構造体は、いずれも優れた吸水性を有し、かつ優れた水蒸散性を発揮した。また、湿潤時の耐破断性も兼ね備えていた。
(Evaluation results)
Each of the water-absorbing sheet structures obtained in the production examples had excellent water absorption and exhibited excellent water transpiration. In addition, it also had rupture resistance when wet.
１０ 吸水性シート
２０ 液透過性部材
３０ 接合部材
１００ 吸水シート構造体
Claims (14)
前記吸水性シートを収容する収容部を有する液透過性部材と、を備える吸水シート構造体。 A water-absorbent sheet,
A liquid-permeable member having a storage section for storing the water-absorbent sheet.
前記吸水性シートを蒸留水に５分間浸漬した後に、５０メッシュの金網上に水平となるように１分間静置した場合、
前記吸水性シートの吸水量は、Ｔ×３００ｇ／ｍ2以上である請求項１に記載の吸水シート構造体。 T is the thickness (mm) of the water-absorbent sheet,
When the water-absorbent sheet is immersed in distilled water for 5 minutes, and then left standing for 1 minute on a 50-mesh wire net so as to be horizontal,
The water absorption of the absorbent sheet is water sheet structure according to claim 1 is T × 300g / m 2 or more.
前記液透過性部材は、各吸水性シートを収容する複数の収容部を有するか、もしくは、
前記液透過性部材は、複数の袋状部材が連結した部材である請求項１〜１３のいずれか１項に記載の吸水シート構造体。 The water-absorbent sheet structure includes a plurality of water-absorbent sheets,
The liquid-permeable member has a plurality of storage sections for storing each water-absorbent sheet, or
The water-absorbent sheet structure according to any one of claims 1 to 13, wherein the liquid-permeable member is a member in which a plurality of bag-shaped members are connected.