JP2019162648A - Molten metal supply device and molten metal supply method - Google Patents

Molten metal supply device and molten metal supply method Download PDF

Info

Publication number
JP2019162648A
JP2019162648A JP2018051960A JP2018051960A JP2019162648A JP 2019162648 A JP2019162648 A JP 2019162648A JP 2018051960 A JP2018051960 A JP 2018051960A JP 2018051960 A JP2018051960 A JP 2018051960A JP 2019162648 A JP2019162648 A JP 2019162648A
Authority
JP
Japan
Prior art keywords
molten metal
ladle
holding
holding furnace
container
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2018051960A
Other languages
Japanese (ja)
Other versions
JP6973219B2 (en
Inventor
三吉　博晃
Hiroaki Mitsuyoshi
博晃 三吉
晴生 明本
Haruo Akemoto
晴生 明本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ube Machinery Corp Ltd
Original Assignee
Ube Machinery Corp Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ube Machinery Corp Ltd filed Critical Ube Machinery Corp Ltd
Priority to JP2018051960A priority Critical patent/JP6973219B2/en
Publication of JP2019162648A publication Critical patent/JP2019162648A/en
Application granted granted Critical
Publication of JP6973219B2 publication Critical patent/JP6973219B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

To provide a molten metal supply device, in a ladle fitted with a cover and a pressurization apparatus, capable of reducing the time for opening the cover in a process of molten metal charge, degasification and refining treatment.SOLUTION: Each component constituting a molten metal supply device 1 is fitted to a molten metal holding container 11, and, from the molten metal holding container, only the two components of a suction tube 12 and a molten metal pouring tube 13 are respectively communicated with a ladle 2 and a holding furnace 3. Thus, without remodeling the generally used ladle, it can be easily utilized. Further, in the process of molten metal material charge to the ladle, molten metal charge, degasification and refining treatment, the operation time of cover opening is made needless, and operation time reduction is made possible. Further, molten metal supply amount adjustment to the holding furnace is facilitated, and conveyance with the stable supply amount of a molten metal is made possible.SELECTED DRAWING: Figure 1

Description

本発明は、ダイカストマシン等において使用される溶湯の輸送に関するものである。さらに詳しくは、取鍋から保持炉に溶湯を補給するための溶湯補給装置及び溶湯補給方法に関するものである。   The present invention relates to transportation of molten metal used in a die casting machine or the like. More specifically, the present invention relates to a molten metal replenishing device and a molten metal replenishing method for replenishing molten metal from a ladle to a holding furnace.

従来の技術として、例えば特許文献１の第１図に示す先行技術が開示されている。   As a conventional technique, for example, the prior art shown in FIG.

この技術における注湯炉の主要構成は貯湯容器（取鍋に相当する）とこの貯湯容器に隣接する受湯容器（保持炉に相当する）とこの両者を接続するサイフォンとからなる。   The main structure of the pouring furnace in this technique consists of a hot water storage container (corresponding to a ladle), a hot water receiving container (corresponding to a holding furnace) adjacent to the hot water storage container, and a siphon connecting the two.

貯湯容器は耐圧容器に収納される。この耐圧容器はガスケットを介してカバーで密閉され、このカバーに接続した弁と圧力配管を介して加圧装置が接続され、加圧されたり、大気に開放されたりできる。カバーを開いて溶湯の材料を投入したり、他のるつぼ形誘導炉から溶湯をチャージしたりする。   The hot water storage container is stored in a pressure resistant container. The pressure vessel is sealed with a cover via a gasket, and a pressurizing device is connected via a valve connected to the cover and a pressure pipe, so that it can be pressurized or opened to the atmosphere. Open the cover and charge the molten metal, or charge the molten metal from another crucible induction furnace.

このような貯湯容器に隣接して配置される受湯容器は、底部に出湯ノズル、上方に保温カバーを設けてタンディッシュを形成する。   A hot water receiving container disposed adjacent to such a hot water storage container forms a tundish by providing a hot water discharge nozzle at the bottom and a heat insulating cover above.

サイフォンを逆Ｕ字状に形成するため、両端を閉じた水平な管でサイフォンの上端空間を形成しこの上端空間に連通して一対の垂直な２本の管（１本は貯湯容器に連通し、他の１本は受湯容器に連通している）を前記水平な管の両端部にコ字状に接続する。このように形成されたサイフォンの一端である管（受湯容器に連通している）の下端を受湯容器の底部、他端である管（貯湯容器に連通している）の下端を貯湯容器の底部にそれぞれ開口する。そして上端空間は弁と真空配管を介して真空発生装置に接続され、真空力が加えられたり、大気に開放されたりできる。   In order to form the siphon in an inverted U shape, the upper end space of the siphon is formed by a horizontal tube closed at both ends, and communicates with the upper end space to form a pair of two vertical tubes (one in communication with the hot water storage container). The other one communicates with the hot water receiving container) at both ends of the horizontal pipe. The lower end of the pipe (connected to the hot water receiving container) which is one end of the siphon thus formed is the bottom of the hot water receiving container, and the lower end of the pipe (which is connected to the hot water storing container) is the hot water storage container. Open at the bottom of each. The upper end space is connected to a vacuum generator via a valve and a vacuum pipe, so that a vacuum force can be applied or opened to the atmosphere.

この先行技術のような構造の注湯炉の運転方法について説明する。   The operation method of the pouring furnace having the structure as in the prior art will be described.

始めに、受湯容器内に溶湯がなく、サイフォンが大気に開放されたりしていわゆるサイフォンが成立してないために真空力を利用することができない初期状態を考える。この時、最大許容圧力の範囲内の圧力を貯湯容器に印加すると、溶湯は管（貯湯容器に連通している）をサイフォンの峰（上端空間の下端）まで上昇し、管（受湯容器に連通している）を落下して受湯容器に流出する。そして、受湯容器内に管（受湯容器に連通している）の下端を閉じる以上で充分な溶湯を流出させればよい。   First, consider an initial state in which there is no molten metal in the hot water receiving container and the siphon is opened to the atmosphere, and so-called siphon is not established, so that the vacuum force cannot be used. At this time, when a pressure within the range of the maximum allowable pressure is applied to the hot water storage container, the molten metal rises up the pipe (communicating with the hot water storage container) to the peak of the siphon (the lower end of the upper end space), and the pipe (to the hot water receiving container). Fall down to the hot water container. And sufficient molten metal should just be made to flow out more than closing the lower end of a pipe (communicating with the hot water receiving container) in the hot water receiving container.

次に受湯容器に充分な溶湯があって、サイフォンの一端、管（受湯容器に連通している）の下端が溶湯で大気から閉塞されているいわゆるサイフォンが成立している時に上端空間に真空力を作用させ、必要により貯湯容器に加圧力を加圧すれば、サイフォン作用で溶湯は貯湯容器から受湯容器へ流出する。溶湯の移送高さに対し、サイフォンを利用して加圧力のほかに真空力も利用できるのである。   Next, when there is enough molten metal in the hot water receiving container, so-called siphon in which one end of the siphon and the lower end of the pipe (connected to the hot water receiving container) are closed from the atmosphere with molten metal is formed in the upper end space. If a vacuum force is applied and if necessary a pressurizing force is applied to the hot water storage container, the molten metal flows out from the hot water storage container to the hot water receiving container by siphon action. In addition to the applied pressure, vacuum force can be used for the molten metal transfer height using a siphon.

前記の運転方法の細部について説明する。   Details of the operation method will be described.

まず、サイフォンが成立していないで加圧力のみで溶湯を移送してサイフォンを成立させ、その後に真空力を作用させると、受湯容器内の溶湯が管（受湯容器に連通している）で吸い上げられて上昇して受湯容器内の溶湯レベルが降下する。もし管（受湯容器に連通している）の下端まで降下するとサイフォンが切れるので、受湯容器内には予め、印加する真空力に応じた溶湯レベルが必要である。これは印加真空力に対し、受湯容器及び管（受湯容器に連通している）の水平断面とから容易に算出できる。また初期状態からサイフォンを成立させるために加圧力のみで溶湯を移送する時にも、受湯容器の出湯ノズルから溶湯の出湯がある時には、その分充分な溶湯の量の値は増加するし、運転は速かでなければならない。   First, when the siphon is not formed but the molten metal is transferred only by the applied pressure to form the siphon and then the vacuum force is applied, the molten metal in the hot water receiving container is connected to the pipe (connected to the hot water receiving container). It is sucked up and rises and the molten metal level in the hot water receiving container is lowered. If the pipe (communicating with the hot water receiving container) is lowered to the lower end, the siphon is cut off. Therefore, a molten metal level corresponding to the applied vacuum force is required in the hot water receiving container. This can be easily calculated with respect to the applied vacuum force from the horizontal section of the hot water receiving container and pipe (in communication with the hot water receiving container). In addition, even when the molten metal is transferred only by the applied pressure to establish the siphon from the initial state, if there is a molten metal discharged from the outlet nozzle of the hot water receiving container, the value of the amount of molten metal will increase accordingly, and the operation Must be fast.

特開平４−１１８１６８号公報Japanese Patent Laid-Open No. 4-118168

上述した先行技術においては、貯湯容器（取鍋に相当する）が耐圧容器に収納されており、この耐圧容器はガスケットを介してカバーで密閉され、このカバーには圧力配管と弁を介して加圧装置が接続されている。そのため、一般的に使用される取鍋（貯湯容器）を利用する場合には、カバーや加圧装置等を取付けるといった、取鍋の改造が必要になる、という課題がある。   In the prior art described above, a hot water storage container (corresponding to a ladle) is housed in a pressure-resistant container, and this pressure-resistant container is sealed with a cover via a gasket, and this cover is pressurized via a pressure pipe and a valve. Pressure device is connected. Therefore, when using the ladle (hot water storage container) generally used, there exists a subject that the modification of a ladle becomes necessary, such as attaching a cover and a pressurization apparatus.

また、上述した先行技術においては、貯湯容器（取鍋に相当する）に、溶湯の材料を投入したり、溶湯をチャージしたりする場合には、カバーを開く必要がある。そのため、取鍋への溶湯の材料の投入あるいは溶湯のチャージ、脱ガス及び精錬処理の工程において、カバーを開くための作業時間が必要になる、という課題がある。   In the above-described prior art, when a molten metal material is charged into a hot water storage container (corresponding to a ladle) or when the molten metal is charged, it is necessary to open the cover. Therefore, there is a problem that work time is required to open the cover in the process of charging the molten metal into the ladle or charging the molten metal, degassing and refining treatment.

さらに、上述した先行技術においては、貯湯容器（取鍋に相当する）に接続された加圧装置と、サイフォン作用と、サイフォンの上端空間に接続された真空発生装置と、を利用している。したがって、受湯容器（保持炉に相当する）への溶湯の補給量の調整が困難である。そのため、保持炉に輸送する溶湯の補給量が安定しない、という課題がある。   Furthermore, in the prior art mentioned above, the pressurization apparatus connected to the hot water storage container (equivalent to a ladle), the siphon action, and the vacuum generator connected to the upper end space of the siphon are used. Therefore, it is difficult to adjust the amount of molten metal supplied to the hot water receiving container (corresponding to a holding furnace). Therefore, there is a problem that the replenishment amount of the molten metal transported to the holding furnace is not stable.

請求項１に記載の発明は、
取鍋から保持炉に溶湯を補給する溶湯補給装置において、
取鍋から溶湯保持容器に溶湯を輸送する吸引管と、
溶湯保持容器から保持炉に溶湯を輸送する注湯管と、
溶湯保持容器と吸引管の通路を開閉する吸引弁と、
溶湯保持容器と注湯管の通路を開閉する注湯弁と、
取鍋あるいは保持炉から溶湯保持容器に溶湯を吸引するための真空装置と、
を備え、
取鍋から保持炉に溶湯を補給することを特徴とする溶湯補給装置である。 The invention described in claim 1
In the molten metal replenishing device that replenishes molten metal from the ladle to the holding furnace,
A suction pipe for transporting the molten metal from the ladle to the molten metal holding container;
A pouring pipe for transporting the molten metal from the molten metal holding container to the holding furnace;
A suction valve for opening and closing the passage of the molten metal holding container and the suction pipe;
A pouring valve for opening and closing the passage of the molten metal holding container and the pouring pipe,
A vacuum device for sucking molten metal from a ladle or holding furnace into a molten metal holding container;
With
A molten metal replenishing device that replenishes molten metal from a ladle to a holding furnace.

請求項２に記載の発明は、
請求項１に記載の発明において、
溶湯保持容器から保持炉に溶湯を輸送するための加圧装置と、
溶湯保持容器の中に保持された溶湯のレベルを検知する第１の湯面センサと、
溶湯保持容器と吸引管の接続部に、吸引管内に残留した溶湯を取鍋に戻すために、フィルタを介して不活性ガスを溶湯保持容器と吸引管の接続部内に導入する第１の不活性ガス導入部と、
溶湯保持容器と注湯管の接続部に、注湯管内に残留した溶湯を保持炉に輸送するために、フィルタを介して不活性ガスを溶湯保持容器と注湯管の接続部内に導入する第２の不活性ガス導入部と、
保持炉内に補給される溶湯のレベルを検知する第２の湯面センサと、
を備えたことを特徴とする溶湯補給装置である。 The invention described in claim 2
In the invention of claim 1,
A pressure device for transporting the molten metal from the molten metal holding container to the holding furnace;
A first hot water surface sensor for detecting the level of the molten metal held in the molten metal holding container;
A first inert gas is introduced through the filter into the connecting portion between the molten metal holding container and the suction pipe in order to return the molten metal remaining in the suction pipe to the ladle at the connecting portion between the molten metal holding container and the suction pipe. A gas introduction part;
In order to transport the molten metal remaining in the molten metal holding pipe and the pouring pipe to the holding furnace, an inert gas is introduced into the molten metal holding container and the pouring pipe through the filter. Two inert gas inlets;
A second hot water surface sensor for detecting the level of the molten metal supplied into the holding furnace;
A melt replenishing device characterized by comprising:

請求項３に記載の発明は、
請求項１又は請求項２に記載の発明において、
前記溶湯保持容器及び前記吸引管及び前記注湯管のそれぞれに、ヒータを備えたことを特徴とする溶湯補給装置である。 The invention according to claim 3
In the invention according to claim 1 or claim 2,
A molten metal replenishing device comprising a heater in each of the molten metal holding container, the suction pipe, and the pouring pipe.

請求項４に記載の発明は、
請求項１又は請求項２に記載の発明において、
前記取鍋が溶解炉であることを特徴とする溶湯補給装置である。 The invention according to claim 4
In the invention according to claim 1 or claim 2,
The ladle is a melting furnace, wherein the ladle is a melting furnace.

請求項５に記載の発明は、
取鍋から保持炉に溶湯を補給する溶湯補給装置を具備した溶湯補給方法において、
取鍋から溶湯保持容器に溶湯を輸送する吸引管と、
溶湯保持容器から保持炉に溶湯を輸送する注湯管と、
溶湯保持容器と吸引管の通路を開閉する吸引弁と、
溶湯保持容器と注湯管の通路を開閉する注湯弁と、
取鍋あるいは保持炉から溶湯保持容器に溶湯を吸引するための真空装置と、
を備え、
取鍋から保持炉に溶湯を補給することを特徴とする溶湯補給方法である。 The invention described in claim 5
In the molten metal replenishing method equipped with the molten metal replenishing device for replenishing the molten metal from the ladle to the holding furnace,
A suction pipe for transporting the molten metal from the ladle to the molten metal holding container;
A pouring pipe for transporting the molten metal from the molten metal holding container to the holding furnace;
A suction valve for opening and closing the passage of the molten metal holding container and the suction pipe;
A pouring valve for opening and closing the passage of the molten metal holding container and the pouring pipe,
A vacuum device for sucking molten metal from a ladle or holding furnace into a molten metal holding container;
With
A molten metal replenishing method characterized by replenishing molten metal from a ladle to a holding furnace.

請求項６に記載の発明は、
請求項５に記載の発明において、
溶湯保持容器から保持炉に溶湯を輸送するための加圧装置と、
溶湯保持容器の中に保持された溶湯のレベルを検知する第１の湯面センサと、
溶湯保持容器と吸引管の接続部に、吸引管内に残留した溶湯を取鍋に戻すために、フィルタを介して不活性ガスを溶湯保持容器と吸引管の接続部内に導入する第１の不活性ガス導入部と、
溶湯保持容器と注湯管の接続部に、注湯管内に残留した溶湯を保持炉に輸送するために、フィルタを介して不活性ガスを溶湯保持容器と注湯管の接続部内に導入する第２の不活性ガス導入部と、
保持炉内に補給される溶湯のレベルを検知する第２の湯面センサと、
を備えたことを特徴とする溶湯補給方法である。 The invention described in claim 6
In the invention of claim 5,
A pressure device for transporting the molten metal from the molten metal holding container to the holding furnace;
A first hot water surface sensor for detecting the level of the molten metal held in the molten metal holding container;
A first inert gas is introduced through the filter into the connecting portion between the molten metal holding container and the suction pipe in order to return the molten metal remaining in the suction pipe to the ladle at the connecting portion between the molten metal holding container and the suction pipe. A gas introduction part;
In order to transport the molten metal remaining in the molten metal holding pipe and the pouring pipe to the holding furnace, an inert gas is introduced into the molten metal holding container and the pouring pipe through the filter. Two inert gas inlets;
A second hot water surface sensor for detecting the level of the molten metal supplied into the holding furnace;
A molten metal replenishment method characterized by comprising:

請求項７に記載の発明は、
請求項５又は請求項６に記載の発明において、
前記溶湯保持容器及び前記吸引管及び前記注湯管のそれぞれに、ヒータを備えたことを特徴とする溶湯補給方法である。 The invention described in claim 7
In the invention according to claim 5 or claim 6,
A molten metal replenishing method, wherein a heater is provided in each of the molten metal holding container, the suction pipe, and the pouring pipe.

請求項８に記載の発明は、
請求項５又は請求項６に記載の発明において、
前記取鍋が溶解炉であることを特徴とする溶湯補給方法である。 The invention according to claim 8 provides:
In the invention according to claim 5 or claim 6,
A ladle replenishing method, wherein the ladle is a melting furnace.

請求項９に記載の発明は、
請求項５〜８に記載の発明のいずれか１項の発明において、
前記保持炉内に溶湯が無い場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする溶湯補給方法である。 The invention according to claim 9 is:
In the invention according to any one of claims 5 to 8,
In the case where there is no molten metal in the holding furnace, the molten metal is replenished to the holding furnace from the ladle.

請求項１０に記載の発明は、
請求項５〜８に記載の発明のいずれか１項の発明において、
前記保持炉内に溶湯が有る場合であって、前記取鍋内の湯面レベルより前記保持炉内の湯面レベルが低い場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする溶湯補給方法である。 The invention according to claim 10 is:
In the invention according to any one of claims 5 to 8,
When the molten metal is present in the holding furnace and the molten metal level in the holding furnace is lower than the molten metal level in the ladle, the molten metal is replenished from the ladle to the holding furnace. It is a molten metal replenishment method.

請求項１１に記載の発明は、
請求項５〜８に記載の発明のいずれか１項の発明において、
前記保持炉内に溶湯が有る場合であって、前記取鍋内の湯面レベルと前記保持炉内の湯面レベルが同じ場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする溶湯補給方法である。 The invention according to claim 11
In the invention according to any one of claims 5 to 8,
When there is a molten metal in the holding furnace, and the molten metal level in the ladle is the same as the molten metal level in the holding furnace, the molten metal is replenished from the ladle to the holding furnace. It is a molten metal replenishment method.

本発明によれば、溶湯補給装置を構成している真空装置や加圧装置等の各部品は、溶湯保持容器に取付けられており、溶湯保持容器からは、吸引管と注湯管の二つの部品のみが、それぞれ取鍋と保持炉に連通している。したがって、取鍋にカバーや加圧装置等を取付けるといった、取鍋の改造が不要であり、一般的に使用される取鍋を、改造せずに、そのまま容易に利用することが可能となる、という効果がある。   According to the present invention, each component such as a vacuum device and a pressurizing device constituting the molten metal replenishing device is attached to the molten metal holding container, and from the molten metal holding container, there are two suction pipes and a pouring pipe. Only the parts are in communication with the ladle and holding furnace, respectively. Therefore, it is not necessary to modify the ladle, such as attaching a cover or a pressurizing device to the ladle, and it is possible to easily use the ladle that is generally used without modification. There is an effect.

また、本発明によれば、一般的に使用される取鍋を、改造せずに、そのまま容易に利用することができるため、取鍋への溶湯の材料の投入あるいは溶湯のチャージ、脱ガス及び精錬処理の工程において、カバーを開くための作業時間が不要になり、作業時間の短縮が可能となる、という効果がある。   Further, according to the present invention, since a generally used ladle can be easily used as it is without remodeling, charging the molten metal into the ladle or charging the molten metal, degassing and In the refining process, there is an effect that the work time for opening the cover becomes unnecessary and the work time can be shortened.

また、本発明によれば、保持炉内に補給される溶湯のレベルを検知する第２の湯面センサにより、保持炉内の湯面の高さを検知したら、注湯弁により溶湯保持容器と注湯管の通路を閉めるため、注湯管内に残留した溶湯だけが保持炉内に補給される。そのため、保持炉内への溶湯の補給量の調整が容易であり、溶湯の補給量が安定した輸送が可能となる、という効果がある。   Further, according to the present invention, when the height of the molten metal level in the holding furnace is detected by the second molten metal level sensor that detects the level of the molten metal replenished in the holding furnace, In order to close the passage of the pouring pipe, only the molten metal remaining in the pouring pipe is supplied into the holding furnace. Therefore, it is easy to adjust the replenishment amount of the molten metal into the holding furnace, and there is an effect that the stable replenishment amount of the molten metal can be transported.

さらに、本発明によれば、
溶湯保持容器と吸引管の接続部に、吸引管内に残留した溶湯を取鍋に戻すために、フィルタを介して不活性ガスを溶湯保持容器と吸引管の接続部内に導入する第１の不活性ガス導入部と、
溶湯保持容器と注湯管の接続部に、注湯管内に残留した溶湯を保持炉に輸送するために、フィルタを介して不活性ガスを溶湯保持容器と注湯管の接続部内に導入する第２の不活性ガス導入部と、
を備えている。
したがって、吸引管内あるいは注湯管内に残留した溶湯を不活性ガスによって、取鍋あるいは保持炉に直ちに移送することができる。そのため、吸引管内あるいは注湯管内に残留した溶湯が凝固するのを防止することが可能となる、という効果がある。 Furthermore, according to the present invention,
A first inert gas is introduced through the filter into the connecting portion between the molten metal holding container and the suction pipe in order to return the molten metal remaining in the suction pipe to the ladle at the connecting portion between the molten metal holding container and the suction pipe. A gas introduction part;
In order to transport the molten metal remaining in the molten metal holding pipe and the pouring pipe to the holding furnace, an inert gas is introduced into the molten metal holding container and the pouring pipe through the filter. Two inert gas inlets;
It has.
Therefore, the molten metal remaining in the suction pipe or the pouring pipe can be immediately transferred to the ladle or the holding furnace by the inert gas. Therefore, there is an effect that it is possible to prevent the molten metal remaining in the suction pipe or the pouring pipe from solidifying.

本発明の一態様である溶湯補給装置を説明する図である。It is a figure explaining the molten metal supply apparatus which is 1 aspect of this invention. 第１の実施形態に係る溶湯補給方法を説明する図である。It is a figure explaining the molten metal supply method which concerns on 1st Embodiment. 第２の実施形態に係る溶湯補給方法を説明する図である。It is a figure explaining the molten metal supply method which concerns on 2nd Embodiment. 第３の実施形態に係る溶湯補給方法を説明する図である。It is a figure explaining the molten metal supply method which concerns on 3rd Embodiment.

本発明をより詳細に説明するために、以下、本発明を実施するための形態を、好適な例を挙げて、適宜図面を用いて説明する。
ここでは、例えばダイカストマシン（図示せず）において、取鍋と保持炉を設置した場合の、溶湯補給装置を備えた一態様について、図１を用いて説明する。 In order to describe the present invention in more detail, a mode for carrying out the present invention will be described below with reference to the drawings as appropriate with a suitable example.
Here, for example, in a die-casting machine (not shown), an embodiment provided with a molten metal replenishing device when a ladle and a holding furnace are installed will be described with reference to FIG.

図１に示すように、溶湯補給装置１は、取鍋２と保持炉３の間を連通するように配置されており、取鍋２から保持炉３に溶湯４を輸送する装置である。   As shown in FIG. 1, the molten metal replenishing device 1 is arranged to communicate between the ladle 2 and the holding furnace 3, and is an apparatus that transports the molten metal 4 from the ladle 2 to the holding furnace 3.

溶湯補給装置１本体の構成は、
（１）取鍋２から溶湯保持容器１１に溶湯４を輸送する吸引管１２
（２）溶湯保持容器１１から保持炉３に溶湯４を輸送する注湯管１３
（３）溶湯保持容器１１と吸引管１２の通路を開閉する吸引弁１４
（４）溶湯保持容器１１と注湯管１３の通路を開閉する注湯弁１５
（５）取鍋２あるいは保持炉３から溶湯保持容器１１に溶湯４を吸引するための真空装置１６
（６）溶湯保持容器１１から保持炉３に溶湯４を輸送するための加圧装置１７
（７）溶湯保持容器１１の中に保持された溶湯４のレベルを検知する第１の湯面センサ１８
（８）溶湯保持容器１１と吸引管１２の接続部に、吸引管１２内に残留した溶湯４を取鍋２に戻すために、フィルタを介して不活性ガスを溶湯保持容器１１と吸引管１２の接続部内に導入する第１の不活性ガス導入部１９
（９）溶湯保持容器１１と注湯管１３の接続部に、注湯管１３内に残留した溶湯４を保持炉３に輸送するために、フィルタを介して不活性ガスを溶湯保持容器１１と注湯管１３の接続部内に導入する第２の不活性ガス導入部２０
（１０）保持炉３内に補給される溶湯４のレベルを検知する第２の湯面センサ２１
から成っている。 The configuration of the melt replenishing device 1 main body is as follows:
(1) Suction tube 12 for transporting the molten metal 4 from the ladle 2 to the molten metal holding container 11
(2) Pouring pipe 13 for transporting the molten metal 4 from the molten metal holding container 11 to the holding furnace 3
(3) Suction valve 14 for opening and closing the passage between the molten metal holding container 11 and the suction pipe 12
(4) A pouring valve 15 for opening and closing the passage between the molten metal holding container 11 and the pouring pipe 13
(5) Vacuum device 16 for sucking molten metal 4 from ladle 2 or holding furnace 3 into molten metal holding container 11
(6) Pressurizing device 17 for transporting the molten metal 4 from the molten metal holding container 11 to the holding furnace 3
(7) A first hot water level sensor 18 for detecting the level of the molten metal 4 held in the molten metal holding container 11.
(8) In order to return the molten metal 4 remaining in the suction pipe 12 to the ladle 2 at the connection portion between the molten metal holding container 11 and the suction pipe 12, inert gas is passed through the filter to the molten metal holding container 11 and the suction pipe 12. 1st inert gas introduction part 19 introduced in the connection part of
(9) In order to transport the molten metal 4 remaining in the molten metal pipe 13 to the holding furnace 3 at the connection portion between the molten metal holding container 11 and the molten metal pipe 13, an inert gas is passed through the filter with the molten metal holding container 11. Second inert gas introduction part 20 introduced into the connection part of the pouring pipe 13
(10) Second molten metal level sensor 21 for detecting the level of the molten metal 4 supplied into the holding furnace 3
Consists of.

吸引弁１４と注湯弁１５は、例えば、電磁弁の切換えを利用して、シリンダを駆動させ、上下方向に沿って進退可能となっており、それぞれ吸引管１２と注湯管１３の上側開口端を開閉させるようになっている。
なお、吸引弁１４と注湯弁１５の進退駆動については、それぞれ吸引管１２と注湯管１３の上側開口端を開閉させることが可能であれば、適宜、好適な機構を選定することができる。 The suction valve 14 and the pouring valve 15 can move forward and backward along the vertical direction by driving a cylinder by using, for example, switching of an electromagnetic valve. The upper openings of the suction pipe 12 and the pouring pipe 13 respectively. The end is opened and closed.
For the advance / retreat drive of the suction valve 14 and the pouring valve 15, a suitable mechanism can be selected as appropriate as long as the upper open ends of the suction pipe 12 and the pouring pipe 13 can be opened and closed, respectively. .

第１の不活性ガス導入部１９と第２の不活性ガス導入部２０には、溶湯４は通過させず、不活性ガスのみを通過させる、フィルタが備えられている。
フィルタとしては、例えば、セラミック又は対溶損性の高い金属から成る多孔質フィルタ、無数の穴が施された焼結フィルタ、等を使用する。フィルタの隙間、穴径等については、０.０１〜０.１ｍｍ程度が好ましい。
なお、フィルタの種類については、溶湯４は通過させず、不活性ガスのみを通過させることが可能であれば、適宜、好適なものを選定することができる。 The first inert gas introduction part 19 and the second inert gas introduction part 20 are provided with a filter that does not allow the molten metal 4 to pass therethrough but allows only the inert gas to pass therethrough.
As the filter, for example, a porous filter made of ceramic or a metal having a high resistance to fusing, a sintered filter provided with countless holes, and the like are used. About the clearance of a filter, a hole diameter, etc., about 0.01-0.1 mm is preferable.
In addition, about the kind of filter, if the molten metal 4 is not allowed to pass through and only an inert gas can be passed, a suitable thing can be selected suitably.

溶湯保持容器１１及び吸引管１２及び注湯管１３は、溶湯保持容器１１内及び吸引管１２内及び注湯管１３内の溶湯４の温度の低下を抑制する目的で、
それぞれにヒータ（図示せず）を備えている。
なお、ヒータの種類については、溶湯保持容器１１内の溶湯４の温度の低下を抑制することが可能であれば、適宜、好適なものを選定することができる。
また、溶湯保持容器１１には、溶湯保持容器１１内の溶湯４の温度を検知するために、温度センサを設置することが好ましい。
なお、温度センサの種類については、溶湯保持容器１１内の溶湯４の温度を検知することが可能であれば、適宜、好適なものを選定することができる。 The molten metal holding container 11, the suction pipe 12 and the pouring pipe 13 are for the purpose of suppressing a decrease in the temperature of the molten metal 4 in the molten metal holding container 11, the suction pipe 12 and the pouring pipe 13.
Each is provided with a heater (not shown).
In addition, about the kind of heater, if it can suppress the fall of the temperature of the molten metal 4 in the molten metal holding | maintenance container 11, a suitable thing can be selected suitably.
The molten metal holding container 11 is preferably provided with a temperature sensor in order to detect the temperature of the molten metal 4 in the molten metal holding container 11.
In addition, about the kind of temperature sensor, if the temperature of the molten metal 4 in the molten metal holding | maintenance container 11 can be detected, a suitable thing can be selected suitably.

取鍋２については、溶湯４の材料（インゴットなど）を加熱して溶かすための溶解炉を使用することも可能である。
なお、溶解炉の種類については、溶湯４の材料（インゴットなど）を加熱して溶かすことが可能であれば、適宜、好適なものを選定することができる。 For the ladle 2, it is also possible to use a melting furnace for heating and melting the material of the molten metal 4 (such as an ingot).
In addition, about the kind of melting furnace, if the material (ingot etc.) of the molten metal 4 can be heated and melted, a suitable thing can be selected suitably.

溶湯補給装置１によれば、溶湯補給装置１を構成している真空装置１６や加圧装置１７等の各部品は、溶湯保持容器１１に取付けられており、溶湯保持容器１１からは、吸引管１２と注湯管１３の二つの部品のみが、それぞれ取鍋２と保持炉３に連通している。したがって、取鍋２にカバーや加圧装置１７等を取付けるといった、取鍋の改造が不要であり、一般的に使用される取鍋を、改造せずに、そのまま容易に利用することが可能となる、という作用効果がある。   According to the molten metal replenishing device 1, each component such as the vacuum device 16 and the pressurizing device 17 constituting the molten metal replenishing device 1 is attached to the molten metal holding container 11. Only two parts 12 and the pouring pipe 13 communicate with the ladle 2 and the holding furnace 3, respectively. Therefore, there is no need to modify the ladle such as attaching a cover, a pressure device 17 or the like to the ladle 2, and a generally used ladle can be easily used without modification. It has the effect of becoming.

また、溶湯補給装置１によれば、一般的に使用される取鍋を、改造せずに、そのまま容易に利用することができるため、取鍋２への溶湯の材料の投入あるいは溶湯のチャージ、脱ガス及び精錬処理の工程において、カバーを開くための作業時間が不要になり、作業時間の短縮が可能となる、という作用効果がある。   In addition, according to the molten metal replenishing device 1, a generally used ladle can be easily used as it is without remodeling. Therefore, charging of molten material into the ladle 2 or charging of the molten metal, In the degassing and refining process, there is an effect that the work time for opening the cover is not required and the work time can be shortened.

＜第１の実施形態＞
以下、本発明の第１の実施形態を図に基づいて説明する。
図２は、図１にて説明した溶湯補給装置１を適用しており、保持炉３内に溶湯４が無い場合において、取鍋２から保持炉３に溶湯４を補給する際の溶湯補給方法の詳細を説明する図である。 <First Embodiment>
DESCRIPTION OF EXEMPLARY EMBODIMENTS Hereinafter, a first embodiment of the invention will be described with reference to the drawings.
FIG. 2 applies the molten metal replenishing device 1 described in FIG. 1, and when there is no molten metal 4 in the holding furnace 3, a molten metal replenishing method for replenishing the molten metal 4 from the ladle 2 to the holding furnace 3. FIG.

図２において、溶湯補給装置１により、取鍋２から保持炉３に溶湯４を補給する工程については、（ａ）、（ｂ）、（ｃ）、（ｄ）、（ｅ）の順番で、順に移行するようになっている。   In FIG. 2, about the process of replenishing the molten metal 4 from the ladle 2 to the holding furnace 3 by the molten metal replenishment apparatus 1, in order of (a), (b), (c), (d), (e), It is designed to move in order.

図２（ａ）は、溶湯補給装置１の初期状態の工程を示しており、吸引弁１４は開き、注湯弁１５は閉じ、の状態になっている。この工程では、取鍋２内の溶湯４を溶湯保持容器１１内に輸送するための準備をする。   FIG. 2A shows a process in an initial state of the molten metal replenishing device 1, in which the suction valve 14 is open and the pouring valve 15 is closed. In this step, preparation is made for transporting the molten metal 4 in the ladle 2 into the molten metal holding container 11.

次に、吸引弁１４は開き、注湯弁１５は閉じ、の状態を保持して、図２（ｂ）に示す真空吸引の工程に移行する。この工程では、真空装置１６が駆動され、溶湯保持容器１１内を真空吸引する。そのため、取鍋２内の溶湯４が、吸引管１２を介して溶湯保持容器１１内に輸送される。   Next, the suction valve 14 is opened and the pouring valve 15 is closed, and the process proceeds to the vacuum suction process shown in FIG. In this step, the vacuum device 16 is driven and the inside of the molten metal holding container 11 is vacuumed. Therefore, the molten metal 4 in the ladle 2 is transported into the molten metal holding container 11 through the suction pipe 12.

溶湯保持容器１１内に輸送される溶湯４の湯面レベルは徐々に上昇し、第１の湯面センサ１８によって、湯面が検知されると、図２（ｃ）に示す溶湯戻しの工程に移行する。この工程では、吸引弁１４は閉じ、注湯弁１５は閉じ、の状態になり、溶湯保持容器１１内に一定量の溶湯４が保持される。   When the molten metal level of the molten metal 4 transported into the molten metal holding container 11 gradually rises and the molten metal level is detected by the first molten metal level sensor 18, the molten metal returning process shown in FIG. Transition. In this step, the suction valve 14 is closed and the pouring valve 15 is closed, and a certain amount of the molten metal 4 is held in the molten metal holding container 11.

図２（ｃ）に示す溶湯戻しの工程では、第１の不活性ガス導入部１９において、溶湯保持容器１１と吸引管１２の接続部内に不活性ガスが導入される。そのため、吸引管１２内に残留した溶湯４は、取鍋２に戻される。   In the step of returning the molten metal shown in FIG. 2C, the inert gas is introduced into the connection portion between the molten metal holding container 11 and the suction pipe 12 in the first inert gas introduction unit 19. Therefore, the molten metal 4 remaining in the suction pipe 12 is returned to the ladle 2.

次に、図２（ｄ）に示す加圧補給の工程に移行する。この工程では、吸引弁１４は閉じ、注湯弁１５は開き、の状態になり、加圧装置１７が駆動され、溶湯保持容器１１内を加圧する。そのため、溶湯保持容器１１内の溶湯４が、注湯管１３を介して保持炉３に輸送される。
ここでは、加圧装置１７が駆動されることを例に挙げて説明しているが、溶湯保持容器１１内を大気に開放することによって、溶湯保持容器１１内の溶湯４を、注湯管１３を介して保持炉３に輸送することも可能である。 Next, the process proceeds to the pressurizing process shown in FIG. In this step, the suction valve 14 is closed and the pouring valve 15 is opened, and the pressurizing device 17 is driven to pressurize the molten metal holding container 11. Therefore, the molten metal 4 in the molten metal holding container 11 is transported to the holding furnace 3 through the pouring pipe 13.
Here, the case where the pressurizing device 17 is driven is described as an example. However, by opening the inside of the molten metal holding container 11 to the atmosphere, the molten metal 4 in the molten metal holding container 11 is replaced with the pouring pipe 13. It is also possible to transport to the holding furnace 3 via

溶湯保持容器１１内及び注湯管１３内の溶湯４が、全て保持炉３に輸送されると、図２（ｅ）に示す補給完了の工程に移行する。この工程では、吸引弁１４は開き、注湯弁１５は閉じ、の状態になり、溶湯補給装置１は、次の溶湯補給動作の待機をする。   When all the molten metal 4 in the molten metal holding container 11 and the pouring pipe 13 is transported to the holding furnace 3, the process proceeds to the replenishment completion step shown in FIG. In this step, the suction valve 14 is opened and the pouring valve 15 is closed, and the molten metal replenishing device 1 waits for the next molten metal replenishing operation.

＜第２の実施形態＞
以下、本発明の第２の実施形態を図に基づいて説明する。
図３は、図１にて説明した溶湯補給装置１を適用しており、保持炉３内に溶湯４が有る場合であって、取鍋２内の湯面レベルより保持炉３内の湯面レベルが低い場合において、取鍋２から保持炉３に溶湯４を補給する際の溶湯補給方法の詳細を説明する図である。 <Second Embodiment>
Hereinafter, a second embodiment of the present invention will be described with reference to the drawings.
FIG. 3 is a case where the molten metal replenishing device 1 described in FIG. 1 is applied and the molten metal 4 is present in the holding furnace 3, and the molten metal level in the holding furnace 3 from the molten metal level in the ladle 2. It is a figure explaining the detail of the molten metal replenishment method at the time of replenishing the molten metal 4 from the ladle 2 to the holding furnace 3 when a level is low.

図３において、溶湯補給装置１により、取鍋２から保持炉３に溶湯４を補給する工程については、（ａ）、（ｂ）、（ｃ）、（ｄ）の順番で、順に移行するようになっている。   In FIG. 3, the process of replenishing the molten metal 4 from the ladle 2 to the holding furnace 3 by the molten metal replenishing device 1 is performed in order of (a), (b), (c), (d). It has become.

図３（ａ）は、溶湯補給装置１の初期状態の工程を示しており、吸引弁１４は開き、注湯弁１５は閉じ、の状態になっている。この工程では、取鍋２内の溶湯４を溶湯保持容器１１内に輸送するための準備をする。   FIG. 3A shows a process in an initial state of the molten metal replenishing device 1, in which the suction valve 14 is open and the pouring valve 15 is closed. In this step, preparation is made for transporting the molten metal 4 in the ladle 2 into the molten metal holding container 11.

次に、吸引弁１４は開き、注湯弁１５は開き、の状態になり、図３（ｂ）に示す真空吸引の工程に移行する。この工程では、真空装置１６が駆動され、溶湯保持容器１１内を真空吸引する。そのため、取鍋２内の溶湯４と保持炉３内の溶湯４が、それぞれ吸引管１２と注湯管１３を介して溶湯保持容器１１内に輸送される。   Next, the suction valve 14 is opened, the pouring valve 15 is opened, and the process proceeds to the vacuum suction process shown in FIG. In this step, the vacuum device 16 is driven and the inside of the molten metal holding container 11 is vacuumed. Therefore, the molten metal 4 in the ladle 2 and the molten metal 4 in the holding furnace 3 are transported into the molten metal holding container 11 through the suction pipe 12 and the pouring pipe 13, respectively.

その結果として、取鍋２側と保持炉３側のそれぞれから溶湯保持容器１１内に輸送される溶湯４は、溶湯保持容器１１内で合流し、取鍋２内の溶湯４と保持炉３内の溶湯４が連通した状態になる。この状態になると、サイフォンの原理により、湯面レベルが高い取鍋２側から、湯面レベルが低い保持炉３側に、溶湯４が輸送される。   As a result, the molten metal 4 transported into the molten metal holding container 11 from each of the ladle 2 side and the holding furnace 3 side merges in the molten metal holding container 11, and the molten metal 4 in the ladle 2 and the holding furnace 3 The molten metal 4 is in a communication state. If it will be in this state, the molten metal 4 will be conveyed from the ladle 2 side with a high hot-water surface level to the holding furnace 3 side with a low hot-water surface level by the principle of siphon.

なお、溶湯補給装置１は、サイフォンの原理による溶湯４の輸送の間、真空装置１６の駆動によって、溶湯保持容器１１内の湯面レベルは徐々に上昇するが、第１の湯面センサ１８によって、湯面が検知されると、真空装置１６の駆動を制御し、それ以上の湯面レベルの上昇を抑制するように構成されている。   In the molten metal replenishing device 1, the level of the molten metal in the molten metal holding container 11 is gradually increased by the driving of the vacuum device 16 during the transportation of the molten metal 4 according to the siphon principle. When the molten metal level is detected, the driving of the vacuum device 16 is controlled to prevent further increase of the molten metal level.

サイフォンの原理によって、保持炉３内に輸送される溶湯４の湯面レベルは徐々に上昇し、第２の湯面センサ２１によって、湯面が検知されると、図３（ｃ）に示す給湯完了の工程に移行する。この工程では、吸引弁１４は開き、注湯弁１５は閉じ、の状態になる。   Due to the principle of siphon, the level of the molten metal 4 transported into the holding furnace 3 gradually rises. When the molten metal level is detected by the second molten metal level sensor 21, the hot water supply shown in FIG. Move to the completion process. In this step, the suction valve 14 is opened and the pouring valve 15 is closed.

次に、吸引弁１４は開き、注湯弁１５は閉じ、の状態を保持して、図３（ｄ）に示す溶湯戻しの工程に移行する。この工程では、加圧装置１７が駆動され、溶湯保持容器１１内を加圧する。そのため、溶湯保持容器１１内の溶湯４が、吸引管１２を介して取鍋２に輸送される。
ここでは、加圧装置１７が駆動されることを例に挙げて説明しているが、溶湯保持容器１１内を大気に開放することによって、溶湯保持容器１１内の溶湯４を、吸引管１２を介して取鍋２に輸送することも可能である。 Next, the state where the suction valve 14 is opened and the pouring valve 15 is closed is maintained, and the process proceeds to the molten metal returning process shown in FIG. In this step, the pressurizing device 17 is driven to pressurize the molten metal holding container 11. Therefore, the molten metal 4 in the molten metal holding container 11 is transported to the ladle 2 via the suction pipe 12.
Here, although the case where the pressurizing device 17 is driven is described as an example, the molten metal 4 in the molten metal holding container 11 is removed from the suction pipe 12 by opening the molten metal holding container 11 to the atmosphere. It is also possible to transport to ladle 2 via.

図３（ｄ）に示す溶湯戻しの工程では、第２の不活性ガス導入部２０において、溶湯保持容器１１と注湯管１３の接続部内に不活性ガスが導入される。そのため、注湯管１３内に残留した溶湯４は、保持炉３に輸送される。   In the molten metal returning step shown in FIG. 3 (d), the inert gas is introduced into the connection portion between the molten metal holding container 11 and the pouring pipe 13 in the second inert gas introduction unit 20. Therefore, the molten metal 4 remaining in the pouring pipe 13 is transported to the holding furnace 3.

不活性ガスによる保持炉３への、注湯管１３内に残留した溶湯４の輸送を終えると、補給完了となり、溶湯補給装置１は、次の溶湯補給動作の待機をする。   When the transport of the molten metal 4 remaining in the pouring pipe 13 to the holding furnace 3 by the inert gas is completed, the replenishment is completed, and the molten metal replenishing device 1 stands by for the next molten metal replenishment operation.

＜第３の実施形態＞
以下、本発明の第３の実施形態を図に基づいて説明する。
図４は、図１にて説明した溶湯補給装置１を適用しており、保持炉３内に溶湯４が有る場合であって、取鍋２内の湯面レベルと保持炉３内の湯面レベルが同じ場合において、取鍋２から保持炉３に溶湯４を補給する際の溶湯補給方法の詳細を説明する図である。 <Third Embodiment>
Hereinafter, a third embodiment of the present invention will be described with reference to the drawings.
FIG. 4 is a case where the molten metal replenishing device 1 described in FIG. 1 is applied and the molten metal 4 is present in the holding furnace 3, and the molten metal level in the ladle 2 and the molten metal level in the holding furnace 3. It is a figure explaining the detail of the molten metal replenishment method at the time of replenishing the molten metal 4 from the ladle 2 to the holding furnace 3 in the case where the level is the same.

図４において、溶湯補給装置１により、取鍋２から保持炉３に溶湯４を補給する工程については、（ａ）、（ｂ）、（ｃ）、（ｄ）、（ｅ）の順番で、順に移行するようになっている。   In FIG. 4, about the process of replenishing the molten metal 4 from the ladle 2 to the holding furnace 3 by the molten metal replenishing device 1, in the order of (a), (b), (c), (d), (e), It is designed to move in order.

図４（ａ）は、溶湯補給装置１の初期状態の工程を示しており、吸引弁１４は開き、注湯弁１５は閉じ、の状態になっている。この工程では、取鍋２内の溶湯４を溶湯保持容器１１内に輸送するための準備をする。   FIG. 4A shows a process in an initial state of the molten metal replenishing device 1, in which the suction valve 14 is opened and the pouring valve 15 is closed. In this step, preparation is made for transporting the molten metal 4 in the ladle 2 into the molten metal holding container 11.

次に、吸引弁１４は開き、注湯弁１５は閉じ、の状態を保持して、図４（ｂ）に示す真空吸引の工程に移行する。この工程では、真空装置１６が駆動され、溶湯保持容器１１内を真空吸引する。そのため、取鍋２内の溶湯４が、吸引管１２を介して溶湯保持容器１１内に輸送される。   Next, the suction valve 14 is opened and the pouring valve 15 is closed, and the process proceeds to the vacuum suction process shown in FIG. In this step, the vacuum device 16 is driven and the inside of the molten metal holding container 11 is vacuumed. Therefore, the molten metal 4 in the ladle 2 is transported into the molten metal holding container 11 through the suction pipe 12.

溶湯保持容器１１内に輸送される溶湯４の湯面レベルは徐々に上昇し、第１の湯面センサ１８によって、湯面が検知されると、図４（ｃ）に示す溶湯戻しの工程に移行する。この工程では、吸引弁１４は閉じ、注湯弁１５は閉じ、の状態になり、溶湯保持容器１１内に一定量の溶湯４が保持される。   The molten metal level of the molten metal 4 transported into the molten metal holding container 11 gradually rises, and when the molten metal level is detected by the first molten metal level sensor 18, the molten metal returning process shown in FIG. Transition. In this step, the suction valve 14 is closed and the pouring valve 15 is closed, and a certain amount of the molten metal 4 is held in the molten metal holding container 11.

図４（ｃ）に示す溶湯戻しの工程では、第１の不活性ガス導入部１９において、溶湯保持容器１１と吸引管１２の接続部内に不活性ガスが導入される。そのため、吸引管１２内に残留した溶湯４は、取鍋２に戻される。   In the molten metal returning step shown in FIG. 4C, the first inert gas introduction unit 19 introduces the inert gas into the connection portion between the molten metal holding container 11 and the suction pipe 12. Therefore, the molten metal 4 remaining in the suction pipe 12 is returned to the ladle 2.

次に、図４（ｄ）に示す加圧補給の工程に移行する。この工程では、吸引弁１４は閉じ、注湯弁１５は開き、の状態になり、加圧装置１７が駆動され、溶湯保持容器１１内を加圧する。そのため、溶湯保持容器１１内の溶湯４が、注湯管１３を介して保持炉３に輸送される。
ここでは、加圧装置１７が駆動されることを例に挙げて説明しているが、溶湯保持容器１１内を大気に開放することによって、溶湯保持容器１１内の溶湯４を、注湯管１３を介して保持炉３に輸送することも可能である。 Next, the process proceeds to the pressurization process shown in FIG. In this step, the suction valve 14 is closed and the pouring valve 15 is opened, and the pressurizing device 17 is driven to pressurize the molten metal holding container 11. Therefore, the molten metal 4 in the molten metal holding container 11 is transported to the holding furnace 3 through the pouring pipe 13.
Here, the case where the pressurizing device 17 is driven is described as an example. However, by opening the inside of the molten metal holding container 11 to the atmosphere, the molten metal 4 in the molten metal holding container 11 is replaced with the pouring pipe 13. It is also possible to transport to the holding furnace 3 via

溶湯保持容器１１内及び注湯管１３内の溶湯４が、全て保持炉３に輸送されると、図４（ｅ）に示す補給完了の工程に移行する。この工程では、吸引弁１４は開き、注湯弁１５は閉じ、の状態になり、溶湯補給装置１は、次の溶湯補給動作の待機をする。   When all the molten metal 4 in the molten metal holding container 11 and the pouring pipe 13 is transported to the holding furnace 3, the process proceeds to the replenishment completion step shown in FIG. In this step, the suction valve 14 is opened and the pouring valve 15 is closed, and the molten metal replenishing device 1 waits for the next molten metal replenishing operation.

以上、第１の実施形態、第２の実施形態、第３の実施形態について説明したが、取鍋２内の溶湯４の湯面レベルと保持炉３内の溶湯４の湯面レベルの高さの関係に応じて、第１の実施形態、第２の実施形態、第３の実施形態の中から、適宜、好適な溶湯補給方法を選択すれば良い。   As mentioned above, although 1st Embodiment, 2nd Embodiment, and 3rd Embodiment were demonstrated, the height of the hot_water | molten_metal surface level of the molten metal 4 in the ladle 2 and the hot_water | molten_metal surface level of the molten metal 4 in the holding furnace 3 was demonstrated. According to the relationship, a suitable molten metal replenishing method may be selected as appropriate from the first embodiment, the second embodiment, and the third embodiment.

なお、第１の実施形態、第２の実施形態、第３の実施形態の、どの実施形態の場合においても、保持炉３内に輸送される溶湯４の湯面レベルが徐々に上昇し、第２の湯面センサ２１によって、湯面が検知されると、給湯補給完了となる。   In any of the first embodiment, the second embodiment, and the third embodiment, the level of the molten metal 4 transported into the holding furnace 3 gradually increases, When the hot water level is detected by the second hot water level sensor 21, the hot water supply is completed.

ここでは、保持炉３内に溶湯４が有る場合であって、取鍋２内の湯面レベルより保持炉３内の湯面レベルが高い場合において、取鍋２から保持炉３に溶湯４を補給する際の溶湯補給方法の詳細な説明は省略した。この場合は、第３の実施形態による溶湯補給方法を選択すれば良い。   Here, when the molten metal 4 is present in the holding furnace 3 and the molten metal level in the holding furnace 3 is higher than the molten metal level in the ladle 2, the molten metal 4 is transferred from the ladle 2 to the holding furnace 3. A detailed description of the molten metal replenishment method when replenishing was omitted. In this case, the molten metal supply method according to the third embodiment may be selected.

第１の実施形態、第２の実施形態、第３の実施形態によれば、保持炉３内に補給される溶湯４のレベルを検知する第２の湯面センサ２１により、保持炉３内の湯面の高さを検知したら、注湯弁１５により溶湯保持容器１１と注湯管１３の通路を閉めるため、注湯管１３内に残留した溶湯４だけが保持炉３内に補給される。そのため、保持炉３内への溶湯４の補給量の調整が容易であり、溶湯の補給量が安定した輸送が可能となる、という作用効果がある。   According to the first embodiment, the second embodiment, and the third embodiment, the second molten metal level sensor 21 that detects the level of the molten metal 4 that is replenished in the holding furnace 3 is used to adjust the inside of the holding furnace 3. When the height of the molten metal surface is detected, the molten metal holding container 11 and the molten metal pipe 13 are closed by the molten metal valve 15, so that only the molten metal 4 remaining in the molten metal pipe 13 is supplied into the holding furnace 3. Therefore, the adjustment of the replenishment amount of the molten metal 4 into the holding furnace 3 is easy, and there is an effect that the stable replenishment amount of the molten metal can be transported.

また、第１の実施形態、第２の実施形態、第３の実施形態によれば、
溶湯保持容器１１と吸引管１２の接続部に、吸引管１２内に残留した溶湯４を取鍋２に戻すために、フィルタを介して不活性ガスを溶湯保持容器１１と吸引管１２の接続部内に導入する第１の不活性ガス導入部１９と、
溶湯保持容器１１と注湯管１３の接続部に、注湯管１３内に残留した溶湯４を保持炉３に輸送するために、フィルタを介して不活性ガスを溶湯保持容器１１と注湯管１３の接続部内に導入する第２の不活性ガス導入部２０と、
を備えている。
したがって、吸引管１２内あるいは注湯管１３内に残留した溶湯４を不活性ガスによって、取鍋２あるいは保持炉３に直ちに移送することができる。そのため、吸引管１２内あるいは注湯管１３内に残留した溶湯が凝固するのを防止することが可能となる、という作用効果がある。 Further, according to the first embodiment, the second embodiment, and the third embodiment,
In order to return the molten metal 4 remaining in the suction pipe 12 to the ladle 2 at the connection part between the molten metal holding container 11 and the suction pipe 12, inert gas is passed through the filter in the connection part between the molten metal holding container 11 and the suction pipe 12. A first inert gas introduction part 19 to be introduced into
In order to transport the molten metal 4 remaining in the molten metal pipe 13 to the holding furnace 3 at the connecting portion between the molten metal holding container 11 and the molten metal pipe 13, an inert gas is passed through the filter to the molten metal holding container 11 and the molten metal pipe. A second inert gas introduction part 20 to be introduced into the 13 connection parts;
It has.
Therefore, the molten metal 4 remaining in the suction pipe 12 or the pouring pipe 13 can be immediately transferred to the ladle 2 or the holding furnace 3 by the inert gas. Therefore, there is an effect that it is possible to prevent the molten metal remaining in the suction pipe 12 or the pouring pipe 13 from solidifying.

第１の実施形態、第３の実施形態によれば、
加圧装置１７、あるいは、大気開放による溶湯保持容器１１内の加圧力を調整することにより、溶湯４の輸送速度を制御し、保持炉３内での溶湯４の泡立ちを抑えて、酸化物の発生を抑制することが可能となる、という作用効果がある。 According to the first embodiment and the third embodiment,
By adjusting the pressurizing device 17 or the pressure in the molten metal holding container 11 that is released to the atmosphere, the transport speed of the molten metal 4 is controlled, and the bubbling of the molten metal 4 in the holding furnace 3 is suppressed. There is an effect that generation | occurrence | production can be suppressed.

第２の実施形態によれば、
大気に直接晒されることなく、取鍋２から保持炉３に溶湯４を補給できるため、酸化物の発生を抑制することが可能となる、という作用効果がある。 According to the second embodiment,
Since the molten metal 4 can be replenished from the ladle 2 to the holding furnace 3 without being directly exposed to the atmosphere, there is an effect that generation of oxides can be suppressed.

以上のように、本発明によれば、優れた作用効果がある溶湯補給装置及び溶湯補給方法を提供でき、ダイカストマシン等において、取鍋から保持炉に溶湯を補給する際の技術に関わる分野で、利用、貢献することができるものである。   As described above, according to the present invention, it is possible to provide a molten metal replenishing apparatus and a molten metal replenishing method that have excellent operational effects, and in a field related to a technique for replenishing molten metal from a ladle to a holding furnace in a die casting machine or the like. Can use, contribute.

１ 溶湯補給装置
２ 取鍋
３ 保持炉
４ 溶湯
１１ 溶湯保持容器
１２ 吸引管
１３ 注湯管
１４ 吸引弁
１５ 注湯弁
１６ 真空装置
１７ 加圧装置
１８ 第１の湯面センサ
１９ 第１の不活性ガス導入部
２０ 第２の不活性ガス導入部
２１ 第２の湯面センサ DESCRIPTION OF SYMBOLS 1 Molten replenishment apparatus 2 Ladle 3 Holding furnace 4 Molten metal 11 Molten metal holding container 12 Suction pipe 13 Pouring pipe 14 Suction valve 15 Pouring valve 16 Vacuum apparatus 17 Pressurization apparatus 18 1st hot_water | molten_metal sensor 19 1st inertness Gas introduction part 20 Second inert gas introduction part 21 Second hot water surface sensor

Claims (11)

取鍋から保持炉に溶湯を補給する溶湯補給装置において、
取鍋から溶湯保持容器に溶湯を輸送する吸引管と、
溶湯保持容器から保持炉に溶湯を輸送する注湯管と、
溶湯保持容器と吸引管の通路を開閉する吸引弁と、
溶湯保持容器と注湯管の通路を開閉する注湯弁と、
取鍋あるいは保持炉から溶湯保持容器に溶湯を吸引するための真空装置と、
を備え、
取鍋から保持炉に溶湯を補給することを特徴とする溶湯補給装置。 In the molten metal replenishing device that replenishes molten metal from the ladle to the holding furnace,
A suction pipe for transporting the molten metal from the ladle to the molten metal holding container;
A pouring pipe for transporting the molten metal from the molten metal holding container to the holding furnace;
A suction valve for opening and closing the passage of the molten metal holding container and the suction pipe;
A pouring valve for opening and closing the passage of the molten metal holding container and the pouring pipe,
A vacuum device for sucking molten metal from a ladle or holding furnace into a molten metal holding container;
With
A molten metal replenishing device that replenishes molten metal from a ladle to a holding furnace. 溶湯保持容器から保持炉に溶湯を輸送するための加圧装置と、
溶湯保持容器の中に保持された溶湯のレベルを検知する第１の湯面センサと、
溶湯保持容器と吸引管の接続部に、吸引管内に残留した溶湯を取鍋に戻すために、フィルタを介して不活性ガスを溶湯保持容器と吸引管の接続部内に導入する第１の不活性ガス導入部と、
溶湯保持容器と注湯管の接続部に、注湯管内に残留した溶湯を保持炉に輸送するために、フィルタを介して不活性ガスを溶湯保持容器と注湯管の接続部内に導入する第２の不活性ガス導入部と、
保持炉内に補給される溶湯のレベルを検知する第２の湯面センサと、
を備えたことを特徴とする請求項１に記載の溶湯補給装置。 A pressure device for transporting the molten metal from the molten metal holding container to the holding furnace;
A first hot water surface sensor for detecting the level of the molten metal held in the molten metal holding container;
A first inert gas is introduced through the filter into the connecting portion between the molten metal holding container and the suction pipe in order to return the molten metal remaining in the suction pipe to the ladle at the connecting portion between the molten metal holding container and the suction pipe. A gas introduction part;
In order to transport the molten metal remaining in the molten metal holding pipe and the pouring pipe to the holding furnace, an inert gas is introduced into the molten metal holding container and the pouring pipe through the filter. Two inert gas inlets;
A second hot water surface sensor for detecting the level of the molten metal supplied into the holding furnace;
The melt replenishing device according to claim 1, comprising: 前記溶湯保持容器及び前記吸引管及び前記注湯管のそれぞれに、ヒータを備えたことを特徴とする請求項１又は請求項２に記載の溶湯補給装置。   The molten metal replenishing device according to claim 1, wherein each of the molten metal holding container, the suction pipe, and the pouring pipe is provided with a heater. 前記取鍋が溶解炉であることを特徴とする請求項１又は請求項２に記載の溶湯補給装置。   The molten metal supply device according to claim 1 or 2, wherein the ladle is a melting furnace. 取鍋から保持炉に溶湯を補給する溶湯補給装置を具備した溶湯補給方法において、
取鍋から溶湯保持容器に溶湯を輸送する吸引管と、
溶湯保持容器から保持炉に溶湯を輸送する注湯管と、
溶湯保持容器と吸引管の通路を開閉する吸引弁と、
溶湯保持容器と注湯管の通路を開閉する注湯弁と、
取鍋あるいは保持炉から溶湯保持容器に溶湯を吸引するための真空装置と、
を備え、
取鍋から保持炉に溶湯を補給することを特徴とする溶湯補給方法。 In the molten metal replenishing method equipped with the molten metal replenishing device for replenishing the molten metal from the ladle to the holding furnace,
A suction pipe for transporting the molten metal from the ladle to the molten metal holding container;
A pouring pipe for transporting the molten metal from the molten metal holding container to the holding furnace;
A suction valve for opening and closing the passage of the molten metal holding container and the suction pipe;
A pouring valve for opening and closing the passage of the molten metal holding container and the pouring pipe,
A vacuum device for sucking molten metal from a ladle or holding furnace into a molten metal holding container;
With
A molten metal replenishing method characterized by replenishing molten metal from a ladle to a holding furnace. 溶湯保持容器から保持炉に溶湯を輸送するための加圧装置と、
溶湯保持容器の中に保持された溶湯のレベルを検知する第１の湯面センサと、
溶湯保持容器と吸引管の接続部に、吸引管内に残留した溶湯を取鍋に戻すために、フィルタを介して不活性ガスを溶湯保持容器と吸引管の接続部内に導入する第１の不活性ガス導入部と、
溶湯保持容器と注湯管の接続部に、注湯管内に残留した溶湯を保持炉に輸送するために、フィルタを介して不活性ガスを溶湯保持容器と注湯管の接続部内に導入する第２の不活性ガス導入部と、
保持炉内に補給される溶湯のレベルを検知する第２の湯面センサと、
を備えたことを特徴とする請求項５に記載の溶湯補給方法。 A pressure device for transporting the molten metal from the molten metal holding container to the holding furnace;
A first hot water surface sensor for detecting the level of the molten metal held in the molten metal holding container;
A first inert gas is introduced through the filter into the connecting portion between the molten metal holding container and the suction pipe in order to return the molten metal remaining in the suction pipe to the ladle at the connecting portion between the molten metal holding container and the suction pipe. A gas introduction part;
In order to transport the molten metal remaining in the molten metal holding pipe and the pouring pipe to the holding furnace, an inert gas is introduced into the molten metal holding container and the pouring pipe through the filter. Two inert gas inlets;
A second hot water surface sensor for detecting the level of the molten metal supplied into the holding furnace;
The melt replenishing method according to claim 5, comprising: 前記溶湯保持容器及び前記吸引管及び前記注湯管のそれぞれに、ヒータを備えたことを特徴とする請求項５又は請求項６に記載の溶湯補給方法。   The molten metal replenishing method according to claim 5 or 6, wherein a heater is provided in each of the molten metal holding container, the suction pipe, and the pouring pipe. 前記取鍋が溶解炉であることを特徴とする請求項５又は請求項６に記載の溶湯補給方法。   The molten metal supply method according to claim 5 or 6, wherein the ladle is a melting furnace. 前記保持炉内に溶湯が無い場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする請求項５〜８項のいずれか１項に記載の溶湯補給方法。   The molten metal replenishing method according to any one of claims 5 to 8, wherein when there is no molten metal in the holding furnace, the molten metal is replenished from the ladle to the holding furnace. 前記保持炉内に溶湯が有る場合であって、前記取鍋内の湯面レベルより前記保持炉内の湯面レベルが低い場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする請求項５〜８項のいずれか１項に記載の溶湯補給方法。   When the molten metal is present in the holding furnace and the molten metal level in the holding furnace is lower than the molten metal level in the ladle, the molten metal is replenished from the ladle to the holding furnace. The melt replenishing method according to any one of claims 5 to 8. 前記保持炉内に溶湯が有る場合であって、前記取鍋内の湯面レベルと前記保持炉内の湯面レベルが同じ場合において、前記取鍋から前記保持炉に溶湯を補給することを特徴とする請求項５〜８項のいずれか１項に記載の溶湯補給方法。   When there is a molten metal in the holding furnace, and the molten metal level in the ladle is the same as the molten metal level in the holding furnace, the molten metal is replenished from the ladle to the holding furnace. The melt replenishing method according to any one of claims 5 to 8.
JP2018051960A 2018-03-20 2018-03-20 Molten metal replenishment device and molten metal replenishment method Active JP6973219B2 (en)