JP2019097589A - Wiping sheet

Info

Publication number: JP2019097589A
Application number: JP2017228140A
Authority: JP
Inventors: 翔太郎百合野; Shotaro Yurino; 行人成田; Yukito Narita; 金田　学; Manabu Kaneda; 学金田
Original assignee: Kao Corp
Current assignee: Kao Corp
Priority date: 2017-11-28
Filing date: 2017-11-28
Publication date: 2019-06-24

Abstract

To provide a wiping sheet having both of sheet strength and dirt capturing properties by compatibly attaining improvement in the strength when the sheet is used and a degree of freedom of constituent fibers of the sheet.SOLUTION: A wiping sheet 1 according to the present invention, comprises a nonwoven fabric 1A including a modified fiber 2 whose cross-sectional shape is noncircular and formed by interlacing fibers without any fusion. The tensile strength of the nonwoven fabric 1A is not less than 80 N/30 mm and not more than 200 N/30 mm, and an amount of fiber loss representing a degree of freedom of the fibers is not less than 2 mg and not more than 50 mg. The basis weight of the nonwoven fabric 1A is preferably not less than 40 g/mand not more than 140 g/m. It is also preferable that wash solution is supported by the nonwoven fabric 1A.SELECTED DRAWING: Figure 1

Description

本発明は、ワイピングシートに関する。 The present invention relates to a wiping sheet.

熱可塑性樹脂を原料とする繊維は、その繊維を交絡させた不織布の形態で様々な用途に用いられている。例えば特許文献１には、０．６〜３．３ｄｔｅｘの非分割型異形断面捲縮繊維とフィブリル化繊維とを含む湿式不織布が水流交絡処理されたワイパー用不織布が開示されている。この不織布は、拭き取り性、吸液性、嵩高性及び強度に優れたものであるので、ダストワイパーなどの用途に使用できることが同文献に記載されている。 BACKGROUND OF THE INVENTION Fibers made from thermoplastic resins are used in various applications in the form of non-woven fabrics in which the fibers are entangled. For example, Patent Document 1 discloses a wiper non-woven fabric in which a wet non-woven fabric containing non-splittable deformed cross-section crimped fibers of 0.6 to 3.3 dtex and fibrillated fibers is subjected to hydroentanglement. Since this non-woven fabric is excellent in wiping properties, liquid absorbing properties, bulkiness and strength, it is described in the same document that it can be used for applications such as dust wipers.

また特許文献２には、多葉扁平断面ポリエステル系繊維２０〜８０質量％とセルロース系繊維２０〜８０質量％とからなる不織布が開示されている。この不織布は、水や薬液等の液体の高い吸保液力と放出性を持ち、適度な嵩高性と柔軟性を兼ね備えているので、対人清拭用や美容用として用いることができることが同文献に記載されている。 Moreover, the nonwoven fabric which consists of 20-80 mass% of multi-leaf flat cross-section polyester fiber and 20-80 mass% of cellulose fiber is disclosed by patent document 2. FIG. This non-woven fabric has high absorption and releasability of liquid such as water and chemical solution, and has both appropriate bulkiness and flexibility, so that it can be used for cleaning of people and beauty. It is described in.

特開２０１０−８１９８７号公報Unexamined-Japanese-Patent No. 2010-81987 国際公開第２０１４／１３２６９０号パンフレットInternational Publication No. 2014/132690 brochure

一般的に、フローリングや壁、家具等の硬質表面を清拭するワイピングシートに用いられる不織布は、汚れの捕集性と、不織布自体の強度とを兼ね備えている必要がある。汚れの捕集性及び強度は、不織布を構成する繊維の自由度、つまり繊維の動きやすさによって調整することができるが、その効果は両立しないものとなる。例えば、繊維の自由度が高い不織布を用いた場合、毛髪や微粒子などの汚れの捕集性は向上するものの、ワイピングシート自体の強度が低下し、実使用に耐えない場合がある。一方、繊維の自由度が低い不織布を用いた場合、ワイピングシート自体の強度は上昇するものの、汚れの捕集性が低下してしまう。 Generally, the nonwoven fabric used for the wiping sheet which cleans hard surfaces, such as a flooring, a wall, and furniture, needs to have the collection property of dirt, and the intensity | strength of nonwoven fabric itself. The dirt collection property and strength can be adjusted by the degree of freedom of the fibers constituting the non-woven fabric, that is, the easiness of movement of the fibers, but their effects are not compatible. For example, when a non-woven fabric having a high degree of freedom in fibers is used, although the collection of dirt such as hair and fine particles is improved, the strength of the wiping sheet itself may be reduced and it may not withstand practical use. On the other hand, when a non-woven fabric having a low degree of freedom of fibers is used, although the strength of the wiping sheet itself is increased, the dirt collection performance is reduced.

また、特許文献１及び２の不織布は、上述した拭き取り性や嵩高性、強度等を確保するために二種の繊維を組み合わせて製造されているが、原料供給や製造コストの観点から適切ではない。また、これらの文献に記載されている不織布は、熱融着性繊維による繊維どうしの融着によって不織布の強度を高めることが好適であるとされているところ、繊維どうしの融着に起因して不織布の構成繊維の自由度が低下し、その結果、汚れの捕集性を十分に高めることができなかった。 In addition, the non-woven fabrics of Patent Documents 1 and 2 are manufactured by combining two kinds of fibers in order to secure the above-mentioned wiping properties, bulkiness, strength, etc., but they are not appropriate from the viewpoint of raw material supply and manufacturing cost. . Moreover, the non-woven fabrics described in these documents are considered to be suitable to increase the strength of the non-woven fabric by the fusion of the fibers with each other by the heat-fusible fibers, and it is attributed to the fusion of the fibers. The degree of freedom of the constituent fibers of the non-woven fabric was reduced, and as a result, the dirt collection performance could not be sufficiently improved.

したがって本発明の課題は、従来技術の欠点を解決し得るワイピングシートを提供することにある。 Accordingly, the object of the present invention is to provide a wiping sheet which can solve the drawbacks of the prior art.

前記の課題を解決すべく本発明者が鋭意検討した結果、意外にも、ワイピングシートの構成繊維として横断面の形状が非円形である異形繊維を用いることで、ごみの捕集に有利な繊維自由度を有しながら、シートの強度を高め得ることを知見した。
本発明は前記の知見に基づきなされたものであり、横断面の形状が非円形である異形繊維を含み、該繊維どうしが融着せずに交絡してなる不織布を備えるワイピングシートであって、
前記不織布の引張強度が８０Ｎ／３０ｍｍ以上２００Ｎ／３０ｍｍ以下であり、
繊維の自由度を示す繊維抜け落ち量が２ｍｇ以上５０ｍｇ以下である、ワイピングシートを提供することにより前記の課題を解決したものである。 As a result of intensive investigations by the present inventors to solve the above problems, it is surprising that a fiber that is advantageous for collecting dust by using a non-circular shaped fiber whose cross-sectional shape is non-circular as the component fiber of the wiping sheet. It has been found that the strength of the sheet can be increased while having freedom.
The present invention has been made based on the above-mentioned findings, and is a wiping sheet comprising a non-woven fabric comprising irregular shaped fibers whose cross section has a non-circular shape and in which the fibers are entangled without fusion.
The tensile strength of the non-woven fabric is 80 N / 30 mm or more and 200 N / 30 mm or less,
The above problem is solved by providing a wiping sheet having a fiber loss of 2 mg or more and 50 mg or less indicating the degree of freedom of the fiber.

本発明によれば、シートの使用時における強度と、シートの構成繊維の自由度の向上とが両立し、シート強度及び汚れの捕集性を兼ね備えたワイピングシートを提供できる。 ADVANTAGE OF THE INVENTION According to this invention, the strength at the time of use of a sheet | seat, and the improvement of the freedom degree of the constituent fiber of a sheet make compatible, and it can provide the wiping sheet which has sheet | seat strength and the collection property of dirt.

図１（ａ）ないし（ｅ）は、本発明のワイピングシートに用いられる異形繊維の横断面形状の斜視模式図である。Fig.1 (a) thru | or (e) are perspective schematic diagrams of the cross-sectional shape of the unusual shape fiber used for the wiping sheet of this invention. 図２（ａ）ないし（ｃ）は、図１（ｂ）、（ｄ）及び（ｅ）における異形繊維の横断面形状の平面拡大図である。Fig.2 (a) thru | or (c) are the plane enlarged views of the cross-sectional shape of the deformed fiber in FIG.1 (b), (d) and (e). 図３は、本発明のワイピングシートの製造に用いられる製造装置の模式図である。FIG. 3 is a schematic view of a production apparatus used for producing the wiping sheet of the present invention. 図４は、実施例及び比較例のワイピングシートにおける不織布の引張強度を示すグラフである。FIG. 4 is a graph showing the tensile strength of the nonwoven fabric in the wiping sheet of the example and the comparative example.

以下、本発明のワイピングシートをその好ましい実施形態に基づき説明する。本発明においてワイピングとは、清掃及び清拭の両方の意味を含むものであり、例えば、床面、壁面、天井及び柱等の建物の清掃、建具や備品の清掃、物品の拭き取り、身体及び身体に係る器具の清拭等が含まれる。 Hereinafter, the wiping sheet of the present invention will be described based on its preferred embodiment. In the present invention, wiping includes the meaning of both cleaning and cleaning, for example, cleaning of a building such as a floor surface, a wall surface, a ceiling and a column, cleaning of fittings and fixtures, wiping of articles, body and body Cleaning of the equipment pertaining to

本発明のワイピングシートは、異形繊維を含み、好ましくは異形繊維を主体とする不織布を備えている。異形繊維は、その繊維どうしが、堆積、交絡又は結合して不織布を形成している。繊維の自由度を高めて、汚れの捕集効率を高める観点から、不織布を構成する繊維は、その繊維どうしが融着していないことが好ましい。「主体とする」とは、ワイピングシートを構成する不織布に、異形繊維が５０質量％以上含まれていることをいう。 The wiping sheet of the present invention comprises a non-woven fabric containing deformed fibers, preferably mainly made of deformed fibers. In the deformed fibers, the fibers are deposited, entangled or bonded to form a non-woven fabric. From the viewpoint of enhancing the degree of freedom of the fibers and enhancing the dirt collection efficiency, it is preferable that the fibers constituting the non-woven fabric are not fused together. The term "mainly" means that the non-woven fabric constituting the wiping sheet contains 50% by mass or more of deformed fiber.

本発明のワイピングシートは、異形繊維を含む単層の不織布から構成されていてもよく、あるいは異形繊維を含む層と、異形繊維を含まない層とを備えた多層構造の不織布から構成されていてもよい。また本発明のワイピングシートは、第１の異形繊維を含む層と、第１の異形繊維と異なる第２の異形繊維を含む層とを備えた多層構造の不織布から構成されていてもよい。 The wiping sheet of the present invention may be composed of a single-layer non-woven fabric containing non-uniform fibers, or a non-woven fabric of multi-layer structure comprising a layer containing non-uniform fibers and a layer not containing non-like fibers. It is also good. In addition, the wiping sheet of the present invention may be composed of a nonwoven fabric of a multilayer structure comprising a layer containing a first deformed fiber and a layer containing a second deformed fiber different from the first deformed fiber.

本発明のワイピングシートは、異形繊維を含む不織布（単層及び多層を問わない）のみから構成されていてもよく、あるいは異形繊維を含む不織布と、異形繊維を含まない不織布又は不織布以外の他のシート材料とを重ね合わせたマルチプライの構造を有していてもよい。 The wiping sheet of the present invention may be composed only of non-woven fabric (whether single-layer and multi-layer) containing deformed fibers, or non-woven fabric containing deformed fibers and non-woven fabric containing non-deformed fibers or other non-woven fabrics. It may have a multi-ply structure in which sheet materials are superposed.

本発明のワイピングシートにおける異形繊維の占める割合は、該ワイピングシートが単層構造の不織布からなる場合は、シート強度及び汚れの捕集性を一層両立させる観点から、５０質量％以上であることが好ましく、６０質量％以上であることが更に好ましく、７０質量％以上であることが一層好ましい。本発明のワイピングシートに異形繊維以外に含有させ得る繊維は横断面が真円の繊維である。かかる繊維は、該ワイピングシートが単層構造の不織布からなる場合は、多くても好ましくは５０質量％以下の割合で含有され、更に好ましくは４０質量％以下、一層好ましくは３０質量％以下の割合で含有される。 When the wiping sheet is made of a single-layer non-woven fabric, the ratio of the deformed fiber in the wiping sheet of the present invention is 50% by mass or more from the viewpoint of further achieving both sheet strength and dirt collection performance. The content is preferably 60% by mass or more, and more preferably 70% by mass or more. The fibers which can be contained in the wiping sheet of the present invention other than the deformed fibers are fibers having a perfect circular cross-section. When the wiping sheet is composed of a single layer non-woven fabric, the fiber is contained in a proportion of at most 50% by mass, preferably at most 40% by mass, more preferably at most 30% by mass. Contained in

本発明のワイピングシートに含まれる異形繊維とは、繊維の横断面の形状が非円形である繊維を指す。繊維の横断面が非円形とは、繊維の横断面が真円形以外の形状を有することをいう。このような繊維の横断面の形状を有する異形繊維２としては、例えば図１（ａ）に示す三角形や、四角形、五角形及び六角形などの凸多角形又は正多角形、図１（ｂ）に示す星形多角形、図１（ｃ）に示す楕円形、図１（ｄ）に示すＷ字形、及び図１（ｅ）に示す多葉形などの横断面形状を有するものが挙げられるが、本発明の効果が奏される限り、特に限定されない。異形繊維は、その横断面形状において、尖鋭な頂部を有する凸部を好ましくは少なくとも１つ、更に好ましくは２つ以上、一層好ましくは３つ以上有することが好ましい。尖鋭な頂部とは、異形繊維の横断面形状における凸部の輪郭が、例えば（イ）非平行な２本の直線が交わることで画成される場合、（ロ）１本の直線と１本の曲線とが交わることで画成される場合、及び（ハ）２本の曲線が交わることで画成される場合などが挙げられる。例えば図１（ａ）に示す異形繊維は尖鋭な頂部を３つ有し、図１（ｂ）に示す異形繊維は尖鋭な頂部を６つ有し、図１（ｅ）に示す異形繊維は尖鋭な頂部を８つ有する。本発明においては、１種の異形繊維を単独で用いてもよく、あるいは横断面形状が異なる２種以上の異形繊維を組み合わせて用いてもよい。 The modified fiber contained in the wiping sheet of the present invention refers to a fiber whose cross-sectional shape of the fiber is non-circular. The non-circular cross section of the fiber means that the cross section of the fiber has a shape other than a perfect circle. Examples of deformed fibers 2 having such a cross-sectional shape of the fibers include triangles shown in FIG. 1 (a), convex polygons such as quadrilaterals, pentagons and hexagons, or regular polygons, and FIG. 1 (b) Those having a cross-sectional shape such as a star-shaped polygon shown, an oval shown in FIG. 1 (c), a W-shape shown in FIG. 1 (d), and a multilobe shown in FIG. There is no particular limitation as long as the effects of the present invention are exhibited. The deformed fiber preferably has at least one, more preferably two or more, and more preferably three or more projections having a sharp apex in the cross-sectional shape. For example, when the contour of the convex portion in the cross-sectional shape of the deformed fiber is defined by intersection of two non-parallel straight lines, one sharp line and one straight line And (c) when two curves are crossed. For example, the deformed fiber shown in FIG. 1 (a) has three sharp peaks, the deformed fiber shown in FIG. 1 (b) has six sharp peaks, and the deformed fiber shown in FIG. 1 (e) is sharp Has eight tops. In the present invention, one type of variant fiber may be used alone, or two or more types of variant fibers having different cross-sectional shapes may be used in combination.

生産効率の向上の観点から、異形繊維は、繊維形成性の樹脂を原料として構成されていることが好ましい。そのような樹脂としては、例えば各種の熱可塑性樹脂が挙げられる。熱可塑性樹脂としては、例えば、ポリエチレンやポリプロピレン等のポリオレフィン樹脂、ポリエチレンテレフタレート等のポリエステル樹脂、ポリアミド樹脂、ポリ塩化ビニルやポリスチレン等のビニル系樹脂、ポリアクリル酸やポリメタクリル酸メチル等のアクリル系樹脂、ポリパーフルオロエチレン等のフッ素樹脂などが挙げられ、これらのうち一種を単独で又は二種以上を組み合わせて用いることができる。 From the viewpoint of improving the production efficiency, it is preferable that the deformed fiber is made of a fiber-forming resin as a raw material. As such resin, various thermoplastic resins are mentioned, for example. Examples of thermoplastic resins include polyolefin resins such as polyethylene and polypropylene, polyester resins such as polyethylene terephthalate, polyamide resins, vinyl resins such as polyvinyl chloride and polystyrene, and acrylic resins such as polyacrylic acid and polymethyl methacrylate. And fluorine resins such as polyperfluoroethylene, etc., and one of these may be used alone or in combination of two or more.

ワイピングシートに含まれる異形繊維の繊度は、ワイピング時における操作性及び汚れの捕集効率の観点から、０．８ｄｔｅｘ以上であることが好ましく、１ｄｔｅｘ以上であることがより好ましく、１．２ｄｔｅｘ以上であることが更に好ましく、またその上限は、４ｄｔｅｘ以下であることが好ましく、３．５ｄｔｅｘ以下であることがより好ましく、３ｄｔｅｘ以下であることが更に好ましい。 The fineness of the deformed fiber contained in the wiping sheet is preferably 0.8 dtex or more, more preferably 1 dtex or more, and more preferably 1.2 dtex or more, from the viewpoint of operability at the time of wiping and dirt collection efficiency. The upper limit is preferably 4 dtex or less, more preferably 3.5 dtex or less, and still more preferably 3 dtex or less.

ワイピングシートに横断面が真円の繊維が含まれる場合、該繊維の繊度は、ワイピング時における操作性及び汚れの捕集効率の観点から、０．６ｄｔｅｘ以上であることが好ましく、１．０ｄｔｅｘ以上であることが更に好ましく、１．２ｄｔｅｘ以上であることが一層好ましい。また、４.０ｄｔｅｘ以下であることが好ましく、３．５ｄｔｅｘ以下であることが更に好ましく、３．０ｄｔｅｘ以下であることが一層好ましい。 When the wiping sheet contains a fiber of which the cross section is a perfect circle, the fineness of the fiber is preferably 0.6 dtex or more from the viewpoint of the operability at the time of wiping and the collection efficiency of the dirt, and 1.0 dtex or more Is more preferably 1.2 dtex or more. Further, it is preferably 4.0 dtex or less, more preferably 3.5 dtex or less, and still more preferably 3.0 dtex or less.

ワイピング時におけるワイピングシートの強度を維持する観点から、ワイピングシートを構成する不織布の引張強度が８０Ｎ／３０ｍｍ以上であることが好ましく、８５Ｎ／３０ｍｍ以上であることがより好ましく、９０Ｎ／３０ｍｍ以上であることが更に好ましく、またその上限は２００Ｎ／３０ｍｍ以下であることが好ましく、１５０Ｎ／３０ｍｍ以下であることがより好ましく、１２０Ｎ／３０ｍｍ以下であることが更に好ましい。具体的には、ワイピングシートを構成する不織布の引張強度が８０Ｎ／３０ｍｍ以上２００Ｎ／３０ｍｍ以下であることが好ましく、８５Ｎ／３０ｍｍ以上１５０Ｎ／３０ｍｍ以下であることがより好ましく、９０Ｎ／３０ｍｍ以上１２０Ｎ／３０ｍｍ以下であることが更に好ましい。この引張強度は、不織布の機械方向（ＭＤ）及び幅方向（ＣＤ）のいずれか一方で満たされていればよく、両方で満たされていることが更に好ましい。不織布の引張強度の測定方法は、後述する実施例にて詳述する。 From the viewpoint of maintaining the strength of the wiping sheet at the time of wiping, the tensile strength of the non-woven fabric constituting the wiping sheet is preferably 80 N / 30 mm or more, more preferably 85 N / 30 mm or more, and 90 N / 30 mm or more The upper limit thereof is preferably 200 N / 30 mm or less, more preferably 150 N / 30 mm or less, and still more preferably 120 N / 30 mm or less. Specifically, the tensile strength of the non-woven fabric constituting the wiping sheet is preferably 80 N / 30 mm or more and 200 N / 30 mm or less, more preferably 85 N / 30 mm or more and 150 N / 30 mm or less, and 90 N / 30 mm or more and 120 N / More preferably, it is 30 mm or less. The tensile strength may be satisfied in any one of the machine direction (MD) and the cross direction (CD) of the nonwoven fabric, and it is more preferable that both are satisfied. The measuring method of the tensile strength of a nonwoven fabric is explained in full detail in the example mentioned below.

ワイピングシートの繊維の自由度を高め、毛髪等の汚れの捕集性を高くする観点から、ワイピングシートを構成する不織布からの繊維抜け落ち量が２ｍｇ以上であることが好ましく、３ｍｇ以上であることがより好ましく、５ｍｇ以上であることが更に好ましく、またその上限は５０ｍｇ以下であることが好ましく、２５ｍｇ以下であることがより好ましく、１０ｍｇ以下であることが更に好ましい。具体的には、繊維抜け落ち量が２ｍｇ以上５０ｍｇ以下であることが好ましく、３ｍｇ以上２５ｍｇ以下であることがより好ましく、５ｍｇ以上１０ｍｇ以下であることが更に好ましい。繊維抜け落ち量の測定方法は、後述する実施例にて詳述する。 From the viewpoint of increasing the degree of freedom of the fibers of the wiping sheet and increasing the collection of dirt such as hair, it is preferable that the amount of fiber loss from the non-woven fabric constituting the wiping sheet is 2 mg or more, and 3 mg or more The upper limit is preferably 50 mg or less, more preferably 25 mg or less, and still more preferably 10 mg or less. Specifically, the amount of fiber loss is preferably 2 mg or more and 50 mg or less, more preferably 3 mg or more and 25 mg or less, and still more preferably 5 mg or more and 10 mg or less. The method of measuring the amount of fiber loss will be described in detail in the examples described later.

本明細書における「繊維抜け落ち量」とは、ワイピングシート内における繊維の自由度を示す値である。つまり、繊維抜け落ち量は、外力に対する繊維の動きやすさを定量的に示したものであり、繊維抜け落ち量が多いほど、繊維の自由度が高いことを意味する。繊維の抜け落ち量が上述の範囲の下限値未満であると、繊維間での摩擦や結合が強くなっているので、ワイピングシート自体の強度は高くなるが、繊維の自由度は低下し、汚れの捕集性が低下する。一方、繊維の抜け落ち量が上述の範囲の上限値を超えると、繊維間での摩擦や結合が弱くなっているので、繊維の自由度は高く、汚れの捕集性は高くなるものの、ワイピングシート自体の強度が低下する。このような範囲の繊維抜け落ち量は、例えば後述するワイピングシートの製造方法において、異形繊維の種類を適切に選択したり、水流交絡の条件を変更したりすることによって、適宜調整することができる。 In the present specification, “the amount of fiber loss” is a value indicating the degree of freedom of fibers in the wiping sheet. That is, the amount of fiber dropout quantitatively indicates the ease of movement of the fiber to an external force, and it means that the greater the amount of fiber dropout, the higher the degree of freedom of the fiber. If the amount of fiber dropout is less than the lower limit value of the above range, the friction and bonding between the fibers become strong, so the strength of the wiping sheet itself becomes high, but the degree of freedom of the fibers decreases and the dirt Collection performance decreases. On the other hand, if the amount of fiber dropout exceeds the upper limit value of the above range, the friction and bond between the fibers become weak, so the degree of freedom of the fibers is high and the dirt collection property is high, but the wiping sheet The strength of itself decreases. The amount of fiber loss in such a range can be appropriately adjusted, for example, by appropriately selecting the type of deformed fiber or changing the hydroentanglement condition in the method of manufacturing a wiping sheet described later.

異形繊維の横断面を横切る線分のうち、最長の線分の長さをＡとし、該線分と直交し且つ該横断面と横切る線分のうち最長の線分の長さをＢとしたときに（図２（ａ）ないし（ｃ）参照）、Ａ／Ｂの値が１．２以上であることが好ましく、１．５以上であることがより好ましく、２以上であることが更に好ましく、またその上限は５以下であることが好ましく、４以下であることがより好ましく、３以下であることが更に好ましい。具体的には、Ａ／Ｂの値が１．２以上５以下であることが好ましく、１．５以上４以下であることがより好ましく、２以上３以下であることが更に好ましい。このような構成を有していることによって、ワイピングシートを構成する繊維が毛髪等の汚れに絡みやすく、且つこれらの汚れを該繊維に引っかけてワイピング対象面から除去することができる。 Among the line segments crossing the cross section of the irregular fiber, the length of the longest line segment is A, and the length of the longest line segment orthogonal to the line segment and of the line segment intersecting with the cross section is B. Sometimes (see FIGS. 2A to 2C), the value of A / B is preferably 1.2 or more, more preferably 1.5 or more, and still more preferably 2 or more. The upper limit thereof is preferably 5 or less, more preferably 4 or less, and still more preferably 3 or less. Specifically, the value of A / B is preferably 1.2 or more and 5 or less, more preferably 1.5 or more and 4 or less, and still more preferably 2 or more and 3 or less. By having such a configuration, the fibers constituting the wiping sheet are easily entangled with stains such as hair, and these stains can be hooked to the fibers to be removed from the surface to be wiped.

上述の長さＡ及び長さＢについて、図２（ａ）ないし（ｃ）に示す形状以外の横断面形状について例を挙げると、繊維の横断面形状が正三角形である異形繊維では、長さＡは正三角形の一辺の長さであり、長さＢはある頂点から一辺に下ろした垂線の長さとなる。また、繊維の横断面形状が楕円である異形繊維では、長さＡは楕円の長径であり、長さＢは楕円の短径である。 As for the lengths A and B described above, for example, with respect to cross-sectional shapes other than the shapes shown in FIGS. 2A to 2C, in the case of deformed fibers in which the cross-sectional shape of the fibers is an equilateral triangle, the lengths A is the length of one side of an equilateral triangle, and the length B is the length of a perpendicular drawn from one vertex to one side. Moreover, in the deformed fiber whose cross-sectional shape of the fiber is an ellipse, the length A is the major axis of the ellipse and the length B is the minor axis of the ellipse.

ワイピングシートに、横断面形状が異なる２種以上の異形繊維が含まれている場合、前記のＡ及びＢは、すべての種類の異形繊維について測定したＡの平均値及びＢの平均値のことである。 When the wiping sheet contains two or more types of deformed fibers different in cross-sectional shape, the above A and B refer to the average value of A and the average value of B measured for all types of deformed fibers. is there.

ワイピング時における操作性と汚れの捕集性とを兼ね備える観点から、長さＡは、上述のＡ／Ｂの範囲を満たすことを条件として、１μｍ以上であることが好ましく、５μｍ以上であることがより好ましく、１０μｍ以上であることが更に好ましく、またその上限は８０μｍ以下であることが好ましく、５０μｍ以下であることが好ましく、２５μｍ以下であることが好ましい。 From the viewpoint of combining the operability at the time of wiping and the dirt collection property, the length A is preferably 1 μm or more, and preferably 5 μm or more, provided that the range of A / B described above is satisfied. The upper limit is preferably 80 μm or less, more preferably 50 μm or less, and preferably 25 μm or less.

同様の観点から、長さＢは、上述のＡ／Ｂの範囲を満たすことを条件として、０．２μｍ以上であることが好ましく、１μｍ以上であることがより好ましく、２μｍ以上であることが更に好ましく、またその上限は４０μｍ以下であることが好ましく、２０μｍ以下であることが好ましく、１５μｍ以下であることが好ましい。 From the same viewpoint, the length B is preferably 0.2 μm or more, more preferably 1 μm or more, and further preferably 2 μm or more, as long as the above-mentioned range of A / B is satisfied. The upper limit is preferably 40 μm or less, more preferably 20 μm or less, and preferably 15 μm or less.

図２（ａ）ないし（ｃ）に示すように、異形繊維の横断面における輪郭線を周方向に沿って見たときに、複数の凸部Ｐと、隣り合う凸部Ｐ間に位置する凹部Ｒとを有する形状である場合、隣り合う凸部Ｐの頂点間を結ぶ線分の長さをＣとし、その線分から凹部Ｒの最底位置に下した垂線の長さをＤとしたときに（図２（ａ）ないし（ｃ）参照）、Ｃ／Ｄの値が０．１以上であることが好ましく、１以上であることがより好ましく、２以上であることが更に好ましく、またその上限は５以下であることが好ましく、４以下であることがより好ましく、３以下であることが更に好ましい。このような構成を有していることによって、繊維単体での表面積が増加し汚れとの接触面積が増えるため、汚れの捕集性を一層高めることができる。 As shown in FIGS. 2 (a) to 2 (c), when the contour line in the cross section of the deformed fiber is viewed along the circumferential direction, the concave portions located between the plurality of convex portions P and the adjacent convex portions P In the case of a shape having R, when the length of a line segment connecting the apexes of adjacent convex portions P is C, and the length of a perpendicular from the line segment to the lowest position of the recess R is D The value of C / D is preferably 0.1 or more, more preferably 1 or more, still more preferably 2 or more, and the upper limit thereof (see FIGS. 2A to 2C). Is preferably 5 or less, more preferably 4 or less, and still more preferably 3 or less. By having such a configuration, the surface area of the fiber alone increases and the contact area with the dirt increases, so the dirt collection performance can be further enhanced.

異形繊維の横断面を観察したとき、任意に選択した隣り合う凸部Ｐの頂点間を結ぶ線分の長さＣが異なる場合、Ｃ／Ｄの値を算出するためのＣの値はすべてのＣの値の平均値とする。同様に、任意に選択した凹部Ｒにおける垂線の長さをＤが異なる場合、Ｃ／Ｄの値を算出するためのＤの値はすべてのＤの値の平均値とする。以下の説明において、Ｃ及びＤの値に言及する場合には、当該値はＣ及びＤの平均値のことである。 If the length C of the line connecting the vertices of the arbitrarily selected adjacent convex portions P is different when observing the cross section of the deformed fiber, the value of C for calculating the value of C / D is all It is an average value of C values. Similarly, in the case where the lengths of perpendicular lines in arbitrarily selected concave portions R are different, the value of D for calculating the value of C / D is taken as the average value of all the values of D. In the following description, when referring to the values of C and D, the value is the average value of C and D.

ワイピング時における操作性及び汚れの捕集効率を高める観点から、長さＣは、上述のＣ／Ｄの範囲を満たすことを条件として、０．１μｍ以上であることが好ましく、０．５μｍ以上であることがより好ましく、１μｍ以上であることが更に好ましく、またその上限は２０μｍ以下であることが好ましく、１０μｍ以下であることが好ましく、５μｍ以下であることが好ましい。 From the viewpoint of enhancing the operability at the time of wiping and the collection efficiency of the dirt, the length C is preferably 0.1 μm or more on condition that the range of C / D described above is satisfied. And the upper limit thereof is preferably 20 μm or less, preferably 10 μm or less, and more preferably 5 μm or less.

同様の観点から、長さＤは、上述のＣ／Ｄの範囲を満たすことを条件として、０．１μｍ以上であることが好ましく、０．５μｍ以上であることがより好ましく、１μｍ以上であることが更に好ましく、またその上限は２０μｍ以下であることが好ましく、１０μｍ以下であることが好ましく、５μｍ以下であることが好ましい。 From the same point of view, the length D is preferably 0.1 μm or more, more preferably 0.5 μm or more, and 1 μm or more, provided that the range of C / D described above is satisfied. Is more preferably 20 μm or less, preferably 10 μm or less, and more preferably 5 μm or less.

上述の長さＡないしＤは、以下の測定方法によって測定することができる。すなわち、作製した不織布をかみそり等を用いて繊維の断面形状を維持した状態で切断した後、該断面をＰｔで真空蒸着した。走査電子顕微鏡（日本電子株式会社製、ＪＳＭ−ＩＴ１００）を用いて、Ｐｔ蒸着した不織布の断面を倍率５００〜１０００倍で観察し、付属ソフトの長さ計測ツールを用いて繊維断面における上記長さＡないしＤをそれぞれ測定した。 The above-mentioned lengths A to D can be measured by the following measurement method. That is, the produced non-woven fabric was cut using a razor or the like while maintaining the cross-sectional shape of the fiber, and then the cross-section was vacuum-deposited with Pt. The cross section of the Pt-deposited non-woven fabric is observed at a magnification of 500 to 1000 times using a scanning electron microscope (JSM-IT100 manufactured by Nippon Denshi Co., Ltd.), and the length in the fiber cross section using the attached software length measurement tool A to D were measured respectively.

ワイピングシートの剛性及び強度を発現させる観点から、ワイピングシートを構成する不織布の坪量は、４０ｇ／ｍ^２以上が好ましく、４５ｇ／ｍ^２以上がより好ましく、５０ｇ／ｍ^２以上が更に好ましく、またその上限は、１４０ｇ／ｍ^２以下が好ましく、１００ｇ／ｍ^２以下がより好ましく、８０ｇ／ｍ^２以下が更に好ましい。具体的には、ワイピングシートを構成する不織布の坪量は、４０ｇ／ｍ^２以上１４０ｇ／ｍ^２以下が好ましく、４５ｇ／ｍ^２以上１００ｇ／ｍ^２以下がより好ましく、５０ｇ／ｍ^２以上８０ｇ／ｍ^２以下が更に好ましい。 From the viewpoint of developing the rigidity and strength of the wiping sheet, the basis weight of the nonwoven fabric constituting the wiping sheet is preferably 40 g / m ² or more, more preferably 45 g / m ² or more, and still more preferably 50 g / m ² or more. the upper limit is preferably 140 g / ^{m 2} or less, more preferably 100 g / ^{m 2} or less, 80 g / ^{m 2} or less is more preferable. Specifically, the basis weight of the non-woven fabric constituting the wiping sheet is preferably 40 g / m ² or more and 140 g / m ² or less, more preferably 45 g / m ² or more and 100 g / m ² or less, and 50 g / m ² or more and 80 g / m ² or more. m ² or less is more preferable.

また同様の観点から、ワイピングシートの厚みは、４０Ｎ／ｍ^２荷重下において０．５ｍｍ以上であることが好ましく、１．０ｍｍ以上であることが更に好ましく、またその上限は、同荷重下において２．５ｍｍ以下であることが好ましく、３ｍｍ以下であることが更に好ましい。 From the same viewpoint, the thickness of the wiping sheet is preferably 0.5 mm or more under a load of 40 N / m ² , more preferably 1.0 mm or more, and the upper limit thereof is 2 under the same load. It is preferably not more than 0.5 mm, and more preferably not more than 3 mm.

ワイピングシートは、ワイピング時において、不織布をそのまま（いわゆる乾式の態様）で使用してもよく、不織布に洗浄液を塗布、噴霧、担持又は含浸させた態様（いわゆる湿式の態様）で使用してもよい。これらの態様は、ワイピング対象面に付着している汚れの種類や、ワイピング対象物の物性に応じて選択することができる。ワイピング対象面における洗浄効率を高める観点からは、ワイピングシートを構成する不織布には洗浄液が担持されていることが好ましい。不織布には異形繊維が含まれているので、繊維間の空隙を大きくすることができ、その結果、ワイピングシート中の洗浄液の保液性が向上するという利点も奏される。 The wiping sheet may use the non-woven fabric as it is (so-called dry mode) at the time of wiping, or may use the non-woven fabric in the mode (so-called wet mode) in which the cleaning liquid is applied, sprayed, supported or impregnated . These modes can be selected according to the type of stain attached to the surface to be wiped and the physical properties of the object to be wiped. From the viewpoint of enhancing the cleaning efficiency on the surface to be wiped, it is preferable that the cleaning liquid be carried on the non-woven fabric constituting the wiping sheet. Since the non-woven fabric contains deformed fibers, the space between the fibers can be increased, and as a result, the advantage of improving the retention of the cleaning liquid in the wiping sheet is also exhibited.

ワイピング時において、ワイピングシートを湿式の態様で用いる場合、該シートに担持される洗浄液としては、水単独や、添加剤を含む水溶液など、湿式ワイピングシートに用いられる一般的な組成のものを用いることができる。洗浄液に用いられる添加剤としては、界面活性剤、殺菌剤、香料、芳香剤、消臭剤、ｐＨ調整剤、アルコール、研磨粒子などが挙げられる。 When using a wiping sheet in a wet mode at the time of wiping, as the cleaning liquid carried on the sheet, use is made of one having a general composition used for a wet wiping sheet, such as water alone or an aqueous solution containing additives. Can. As an additive used for a washing | cleaning liquid, surfactant, a disinfectant | microbicide, a fragrance | flavor, an aromatic agent, a deodorizer, a pH adjuster, alcohol, abrasive particles etc. are mentioned.

異形繊維の繊維長は、繊維の製造方法によるが、一般に１ｍｍ以上１００ｍｍ以下が好ましく、１０ｍｍ以上９０ｍｍ以下がより好ましく、２０ｍｍ以上６０ｍｍ以下が更に好ましい。 The fiber length of the deformed fiber is generally 1 mm to 100 mm, preferably 10 mm to 90 mm, and more preferably 20 mm to 60 mm, although it depends on the method of producing the fiber.

以上は本発明のワイピングシートの一実施形態に関する説明であったところ、以下にワイピングシートの好適な製造方法を、図３を参照しながら説明する。図３には、ワイピングシートの製造に好適に用いられる製造装置１０が示されている。製造装置１０は、搬送方向（ＭＤ方向）に沿って、ウェブ形成部２０と、水流交絡部３０とをこの順で備えている。なお、以下に示す製造装置１０の構成は、スパンレース法による不織布の一般的な製造装置と同様である。 The above description is about the embodiment of the wiping sheet according to the present invention. Hereinafter, a preferred method for manufacturing the wiping sheet will be described with reference to FIG. The manufacturing apparatus 10 suitably used for manufacture of a wiping sheet is shown by FIG. The manufacturing apparatus 10 includes a web forming unit 20 and a water flow interlaced unit 30 in this order along the transport direction (MD direction). In addition, the structure of the manufacturing apparatus 10 shown below is the same as that of the general manufacturing apparatus of the nonwoven fabric by a spunlace method.

ウェブ形成部２０は、異形繊維２のウェブを形成するものである。ウェブ形成部２０は、ワイピングシートの原料である異形繊維２からウェブを形成するカード機２１を備えている。カード機２１によって形成された異形繊維２のウェブは、水流交絡部３０へ搬送される。 The web forming unit 20 forms a web of the deformed fiber 2. The web formation part 20 is equipped with the card machine 21 which forms a web from the deformed fiber 2 which is a raw material of a wiping sheet. The web of deformed fibers 2 formed by the carding machine 21 is conveyed to the water flow entanglement unit 30.

水流交絡部３０は、異形繊維２のウェブを水流によって交絡させ、異形繊維２を含む不織布１Ａを形成するものである。水流交絡部３０は、異形繊維２のウェブに水流を吹き付ける水流ノズル３１と、無端ベルトからなる支持ベルト３２とを備えている。水流ノズル３１は、異形繊維２のウェブ及び支持ベルト３２の上方に位置しており、異形繊維２のウェブの幅方向（ＣＤ方向）全域にわたって高圧水流を吹き付けることができるようになっている。支持ベルト３２は、水流ノズル３１と対向して配されており、吹き付けられた水を透過させるために、格子状などの各種パターンで穴が空いた構造となっている（図示せず）。水流ノズル３１からの水流の吹き付けによって交絡された異形繊維２を含む不織布１Ａは、支持ベルト３２によって下流の工程へ搬送される。 The water entanglement portion 30 entangles the web of deformed fibers 2 by a water flow to form a nonwoven fabric 1A including the deformed fibers 2. The water flow entangled portion 30 includes a water flow nozzle 31 for blowing a water flow to the web of the deformed fiber 2 and a support belt 32 made of an endless belt. The water flow nozzle 31 is located above the web of the deformed fiber 2 and the support belt 32 so that high-pressure water flow can be sprayed over the entire width direction (CD direction) of the web of the deformed fiber 2. The support belt 32 is disposed to face the water flow nozzle 31, and has a structure in which holes are formed in various patterns such as a grid shape (not shown) in order to transmit sprayed water. The nonwoven fabric 1A including the deformed fiber 2 entangled by the spray of the water flow from the water flow nozzle 31 is conveyed by the support belt 32 to the downstream process.

特に、上述の引張強度及び繊維抜け落ち量を有する不織布は、水流交絡の条件を調整して製造することができる。具体的には、異形繊維２のウェブに対して、水流ノズル３１から吹き付ける水圧を好ましくは３０ｋｇ／ｃｍ^２以上８０ｋｇ／ｃｍ^２以下、更に好ましくは４０ｋｇ／ｃｍ^２以上６０ｋｇ／ｃｍ^２以下とし、且つ異形繊維２のウェブのＭＤ方向における搬送速度を好ましくは２ｍ／ｍｉｎ以上１０ｍ／ｍｉｎ以下、更に好ましくは４ｍ／ｍｉｎ以上８ｍ／ｍｉｎ以下とすることで製造することができる。 In particular, the non-woven fabric having the above-described tensile strength and the amount of fiber loss can be manufactured by adjusting the conditions of hydroentanglement. Specifically, the water pressure sprayed from the water flow nozzle 31 is preferably 30 kg / cm ² or more and 80 kg / cm ² or less, more preferably 40 kg / cm ² or more and 60 kg / cm ² or less, with respect to the web of deformed fiber 2 It can manufacture by setting the conveyance speed in MD direction of the web of deformed fiber 2 to preferably 2 m / min to 10 m / min, more preferably 4 m / min to 8 m / min.

このような工程を経て、異形繊維２どうしが融着せずに交絡している不織布１Ａを形成することができる。不織布１Ａを形成した後、必要に応じて、ヒーター等を用いて不織布１Ａを乾燥してもよい（図示せず）。 Through such a process, it is possible to form the non-woven fabric 1A in which the different shaped fibers 2 are entangled without fusion. After forming the non-woven fabric 1A, if necessary, the non-woven fabric 1A may be dried using a heater or the like (not shown).

最後に、製造された不織布１Ａは、該不織布１Ａをそのままで乾式のワイピングシート１としてもよく、該不織布１Ａに更に洗浄液を担持させて、湿式のワイピングシート１とすることができる。 Finally, the non-woven fabric 1A produced may be used as the dry-type wiping sheet 1 as it is, and the non-woven fabric 1A may further carry a cleaning liquid to form the wet-type wiping sheet 1.

このようにして製造されたワイピングシートは、該ワイピングシート単体で、又はワイパーなどの清掃用具に付着させて、床面、壁面等の建物、戸棚、窓ガラス、鏡、ドア、ドアノブ等の建具、ラグ、カーペット、机食卓等の家具、キッチン、トイレ、身体の清拭や、衛生用品、包装などにも使用できる。 The wiping sheet manufactured in this manner may be a single piece of the wiping sheet or attached to a cleaning tool such as a wiper to build a floor surface, a wall surface, a building, a cupboard, a window glass, a mirror, a door, a door knob, etc. It can also be used for rugs, carpets, furniture such as desks, kitchens, toilets, cleaning the body, hygiene products, packaging, etc.

以上、本発明をその好ましい実施形態に基づき説明したが、本発明は前記実施形態に制限されない。例えば本発明のワイピングシートは、先に述べたとおり、異形繊維を含む不織布のみから構成されていてもよく、あるいは該不織布に加えて他の層を有していてもよい。不織布と他の層とが積層されてワイピングシートが構成されている場合には、異形繊維を含む不織布が外方を向く面がワイピング面として供される。 Although the present invention has been described above based on its preferred embodiments, the present invention is not limited to the embodiments. For example, as described above, the wiping sheet of the present invention may be composed solely of a non-woven fabric containing deformed fibers, or may have other layers in addition to the non-woven fabric. When the non-woven fabric and the other layer are laminated to constitute the wiping sheet, the surface of the non-woven fabric containing the deformed fiber facing outward serves as the wiping surface.

以下、実施例により本発明を更に詳細に説明する。しかしながら本発明の範囲は、かかる実施例に制限されない。 Hereinafter, the present invention will be described in more detail by way of examples. However, the scope of the present invention is not limited to such embodiments.

〔実施例１〕
図１（ａ）に示すように、繊維の横断面の形状が三角形である異形繊維を用いて、水流交絡を行って不織布を製造した。水流交絡の条件は、水流ノズル３１から吹き付けられる水圧を５０ｋｇ／ｃｍ^２とし、異形繊維ウェブの搬送速度を５ｍ／ｍｉｎとした。不織布の寸法を２８５ｍｍ×２０５ｍｍに成形した後、そのままの状態（すなわち乾式の状態）として、目的とするワイピングシートとした。異形繊維の原料樹脂としてポリプロピレン（ＰＰ）を用いた。この異形繊維の繊度は１．４５ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 Example 1
As shown in FIG. 1 (a), hydroentangling was carried out using a modified fiber in which the shape of the cross section of the fiber is a triangle to produce a non-woven fabric. The water flow entanglement conditions were such that the water pressure sprayed from the water flow nozzle 31 was 50 kg / cm ^2, and the conveyance speed of the deformed fiber web was 5 m / min. After forming the dimensions of the non-woven fabric to 285 mm × 205 mm, the non-woven fabric was used as it was (that is, in the dry state) to obtain a target wiping sheet. Polypropylene (PP) was used as a raw material resin of the deformed fiber. The fineness of this deformed fiber was 1.45 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔実施例２〕
図１（ｂ）に示すように、繊維の横断面の形状が星形六角形である異形繊維を用いて不織布を製造したほかは、実施例１と同様にワイピングシートを得た。この異形繊維の繊度は１．３ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 Example 2
As shown in FIG. 1 (b), a wiping sheet was obtained in the same manner as in Example 1 except that non-woven fabric was manufactured using deformed fibers in which the shape of the cross section of the fiber is a star-shaped hexagon. The fineness of this deformed fiber was 1.3 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔実施例３〕
図１（ｃ）に示すように、繊維の横断面の形状が楕円形である異形繊維を用いて不織布を製造したほかは、実施例１と同様にワイピングシートを得た。この異形繊維の繊度は２．２ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 [Example 3]
As shown in FIG. 1 (c), a wiping sheet was obtained in the same manner as in Example 1 except that a non-woven fabric was produced using a modified fiber in which the shape of the cross section of the fiber is elliptical. The fineness of this deformed fiber was 2.2 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔実施例４〕
図１（ｄ）に示すように、繊維の横断面の形状がＷ形である異形繊維を用いて不織布を製造したほかは、実施例１と同様にワイピングシートを得た。この異形繊維の繊度は２．８５ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 Example 4
As shown in FIG. 1 (d), a wiping sheet was obtained in the same manner as in Example 1 except that a non-woven fabric was produced using a modified fiber in which the shape of the cross section of the fiber is W-shaped. The fineness of this deformed fiber was 2.85 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔実施例５〕
図１（ｅ）に示すように、繊維の横断面の形状が多葉形である異形繊維を用いて不織布を製造したほかは、実施例１と同様にワイピングシートを得た。この異形繊維の繊度は１．７ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 [Example 5]
As shown in FIG. 1 (e), a wiping sheet was obtained in the same manner as in Example 1 except that a non-woven fabric was produced using a modified fiber in which the shape of the cross section of the fiber is multi-leaf. The fineness of this deformed fiber was 1.7 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔比較例１〕
繊維の横断面の形状が真円形である繊維を用いて不織布を製造したほかは、実施例１と同様にワイピングシートを得た。この繊維の繊度は１．４５ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 Comparative Example 1
A wiping sheet was obtained in the same manner as in Example 1 except that a non-woven fabric was produced using fibers of which the cross-sectional shape of the fibers is a perfect circle. The fineness of this fiber was 1.45 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔比較例２〕
水流交絡の条件を水流ノズル３１から吹き付けられる水圧を５０ｋｇ／ｃｍ^２とし、異形繊維ウェブの搬送速度を１ｍ／ｍｉｎとしたほかは、実施例５と同様にワイピングシートを得た。 Comparative Example 2
A wiping sheet was obtained in the same manner as in Example 5 except that the water flow entanglement condition was that the water pressure sprayed from the water flow nozzle 31 was 50 kg / cm ^2, and the conveyance speed of the deformed fiber web was 1 m / min.

〔比較例３〕
繊維の原料としてパルプ及びポリエステル繊維を用いて、湿式スパンレース法によって製造した不織布を用いて、乾式のワイピングシートを得た。この繊維の繊度は２．５ｄｔｅｘであった。不織布の坪量は７５ｇ／ｍ^２であった。 Comparative Example 3
A dry wiping sheet was obtained using a nonwoven fabric produced by a wet spunlace method using pulp and polyester fibers as raw materials of fibers. The fineness of this fiber was 2.5 dtex. The basis weight of the non-woven fabric was 75 g / m ² .

〔比較例４〕
繊維ウェブの搬送速度を１ｍ／ｍｉｎとして不織布を製造したほかは、比較例１と同様にワイピングシートを得た。この繊維の繊度は１．４５ｄｔｅｘであった。不織布の坪量は６０ｇ／ｍ^２であった。 Comparative Example 4
A wiping sheet was obtained in the same manner as Comparative Example 1 except that the nonwoven fabric was manufactured at a fiber web conveyance speed of 1 m / min. The fineness of this fiber was 1.45 dtex. The basis weight of the non-woven fabric was 60 g / m ² .

〔引張強度の測定〕
実施例及び比較例のワイピングシートについて、引張強度の測定を行った。詳細には、引張強度試験機（株式会社島津製作所社製、ＡＧ−ＩＳ１００Ｎ）を用いて、長さ１５０ｍｍ×幅３０ｍｍの試料を、スパン１００ｍｍ、速度３００ｍｍ／分で試料を引っ張ったときの、試料が破断するまでの最大荷重値（Ｎ）を測定した。搬送方向（ＭＤ方向）及びＭＤ方向に直交する幅方向（ＣＤ方向）の引張強度（Ｎ／３０ｍｍ）をそれぞれ６回測定し、引張強度の測定値の平均値及び標準偏差を算出した。結果を図４及び表１に示す。 [Measurement of tensile strength]
The tensile strength was measured about the wiping sheet of an Example and a comparative example. Specifically, when a sample of 150 mm long × 30 mm wide is pulled at a span of 100 mm and a speed of 300 mm / min using a tensile strength tester (AG-IS 100N manufactured by Shimadzu Corporation), The maximum load value (N) until the sample broke was measured. The tensile strength (N / 30 mm) in the width direction (CD direction) orthogonal to the transport direction (MD direction) and the MD direction was measured six times each, and the average value and the standard deviation of the measured values of tensile strength were calculated. The results are shown in FIG. 4 and Table 1.

〔繊維抜け落ち量の測定〕
実施例及び比較例の不織布について、繊維抜け落ち量の測定を行った。詳細には、評価対象の不織布に５．５Ｎ／ｍ^２の荷重を負荷した状態で、回転速度２．３ｍ／ｓで回転する円形のウレタン発泡体に当接させて、１．５分間摩擦をかけた。その後、ウレタン発泡体に付着した繊維を粘着テープで捕集し、その繊維の質量（ｍｇ）を測定した。繊維抜け落ち量が多いほど、繊維の自由度が高いことを示す。結果を表１に示す。 [Measurement of fiber loss amount]
The amount of fiber loss was measured for the non-woven fabrics of the example and the comparative example. In detail, with a load of 5.5 N / m ² applied to the non-woven fabric to be evaluated, contact the circular urethane foam rotating at a rotational speed of 2.3 m / s for 1.5 minutes. I took it. Thereafter, the fiber attached to the urethane foam was collected with an adhesive tape, and the mass (mg) of the fiber was measured. The greater the amount of fiber loss, the higher the degree of freedom of the fibers. The results are shown in Table 1.

〔毛髪捕集性の評価〕
実施例及び比較例のワイピングシートについて、毛髪捕集性の評価を行った。詳細には、毛髪を１０本散布したフローリング（コンビットニューアドバンス１０１、ウッドワン社製）をワイピング対象面として、０．１６ｋＮ／ｍ^２の圧力をかけて、０．２７ｍ^２の面積をワイピングを行い、そのときの毛髪捕集性を以下の基準で評価した。結果を表１に示す。
Ａ：毛髪が７０％以上捕集でき、捕集性は非常に良好であった。
Ｂ：毛髪が５０％以上７０％未満捕集でき、捕集性は良好であった。
Ｃ：毛髪が０％以上５０％未満捕集でき、捕集性は不良であった。 [Evaluation of hair collection property]
The hair collecting properties of the wiping sheets of the examples and comparative examples were evaluated. Specifically, flooring (Con-bit New Advance 101, Woodone Co.) were dispersed hair 10 present as a wiping subject surface, by applying a pressure of 0.16kN / ^{m 2,} subjected to wiping an area of 0.27 m ² The hair collection property at that time was evaluated based on the following criteria. The results are shown in Table 1.
A: 70% or more of the hair could be collected, and the collection performance was very good.
B: Hair can be collected at 50% or more and less than 70%, and the collection property is good.
C: The hair could be collected at 0% or more and less than 50%, and the collection performance was poor.

図４及び表１に示すように、異形繊維を用いた実施例１ないし５のワイピングシートは、異形繊維を用いていない比較例１のワイピングシートと比較して、ＭＤ方向及びＣＤ方向の引張強度が高いものであることが判る。また表１に示すように、実施例１ないし５のワイピングシートは、比較例２及び比較例３のワイピングシートと比較して、繊維抜け落ち量が多く、すなわち繊維の自由度が高く、毛髪捕集性が高いものであることが判る。特に、同一の繊維を使用した実施例５と比較例２とを比較すると、水流交絡の条件を弱めることによって、シートの引張強度と毛髪捕集性とが両立できるシートを製造できることが判る。 As shown in FIG. 4 and Table 1, the wiping sheets of Examples 1 to 5 using deformed fibers have tensile strengths in the MD direction and the CD direction as compared with the wiping sheet of Comparative Example 1 not using deformed fibers. Is found to be high. Further, as shown in Table 1, the wiping sheets of Examples 1 to 5 have a greater amount of fiber loss, that is, a higher degree of freedom of fibers, as compared with the wiping sheets of Comparative Examples 2 and 3. It can be seen that it is highly sexual. In particular, when Example 5 using the same fiber and Comparative Example 2 are compared, it can be seen that a sheet in which the tensile strength and the hair collecting property of the sheet can be compatible can be manufactured by weakening the conditions of water entanglement.

以上より、本発明のワイピングシートは、シートの使用時における強度と、シートの構成繊維の自由度の向上とを両立しており、ワイピング時の実使用に耐え、且つ毛髪等の汚れの捕集性を高めることができるものであることが判る。 As mentioned above, the wiping sheet of this invention is compatible in the strength at the time of use of a sheet | seat, and the improvement of the freedom degree of the constituent fiber of a sheet, endures actual use at the time of wiping, and collection of stains, such as hair. It turns out that it is what can improve sex.

１ワイピングシート
１Ａ不織布
２異形繊維
１０製造装置
２０ウェブ形成部
３０水流交絡部
ＭＤ搬送方向 1 Wiping sheet 1A Non-woven fabric 2 Modified fiber 10 Manufacturing device 20 Web forming part 30 Water flow entangled part MD Conveying direction

Claims

横断面の形状が非円形である異形繊維を含み、該繊維どうしが融着せずに交絡してなる不織布を備えるワイピングシートであって、
前記不織布の引張強度が８０Ｎ／３０ｍｍ以上２００Ｎ／３０ｍｍ以下であり、
繊維の自由度を示す繊維抜け落ち量が２ｍｇ以上５０ｍｇ以下である、ワイピングシート。 What is claimed is: 1. A wiping sheet comprising a non-circular fiber comprising non-circular shaped fibers whose cross-sectional shape is non-circular, wherein the fibers are entangled without fusion.
The tensile strength of the non-woven fabric is 80 N / 30 mm or more and 200 N / 30 mm or less,
A wiping sheet having a fiber loss of 2 mg to 50 mg, which indicates the degree of freedom of fibers.

前記不織布の坪量が４０ｇ／ｍ^２以上１４０ｇ／ｍ^２以下である、請求項１に記載のワイピングシート。 The wiping sheet according to claim 1, wherein the basis weight of the non-woven fabric is 40 g / m ² or more and 140 g / m ² or less.

前記繊維の横断面を横切る線分のうち、最長の線分の長さをＡとし、該線分と直交し且つ該横断面と横切る線分のうち最長の線分の長さをＢとしたときに、Ａ／Ｂの値が１．０以上３．０以下である、請求項１又は２に記載のワイピングシート。 The length of the longest line segment among the line segments crossing the cross section of the fiber is A, and the length of the longest line segment orthogonal to the line segment and across the cross section is B. The wiping sheet according to claim 1, wherein sometimes the value of A / B is 1.0 or more and 3.0 or less.

前記繊維は、その横断面における輪郭線を周方向に沿って見たときに、複数の凸部と、隣り合う凸部間に位置する凹部とを有する形状をしており、
隣り合う前記凸部の頂点間を結ぶ線分の長さをＣとし、該線分から前記凸部の最底位置に下した垂線の長さをＤとしたときに、Ｃ／Ｄの値が０．１以上５．０以下である、請求項１ないし３のいずれか一項に記載のワイピングシート。 The fiber has a shape having a plurality of convex portions and a concave portion located between adjacent convex portions when the contour line in the cross section is viewed along the circumferential direction,
Assuming that the length of a line segment connecting the apexes of adjacent convex portions is C, and the length of a perpendicular from the line segment to the bottom of the convex portion is D, the value of C / D is 0. The wiping sheet according to any one of claims 1 to 3, which is 1 or more and 5.0 or less.

前記繊維の横断面の形状が凸多角形である、請求項１又は２に記載のワイピングシート。 The wiping sheet according to claim 1, wherein the shape of the cross section of the fiber is a convex polygon.

洗浄液が前記不織布に担持されている、請求項１ないし５のいずれか一項に記載のワイピングシート。 The wiping sheet according to any one of claims 1 to 5, wherein a cleaning solution is carried by the non-woven fabric.