JP2019091081A - 赤外線反射シート - Google Patents
赤外線反射シート Download PDFInfo
- Publication number
- JP2019091081A JP2019091081A JP2019033048A JP2019033048A JP2019091081A JP 2019091081 A JP2019091081 A JP 2019091081A JP 2019033048 A JP2019033048 A JP 2019033048A JP 2019033048 A JP2019033048 A JP 2019033048A JP 2019091081 A JP2019091081 A JP 2019091081A
- Authority
- JP
- Japan
- Prior art keywords
- infrared
- pigment
- layer
- dark
- reflective sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の赤外線透過性暗色インキは、太陽電池モジュール用の裏面保護シート等を、意匠性の観点から暗色に着色する用途で用いることができる。又、本発明の赤外線透過性暗色インキは、近赤外線の透過率が高いため、近赤外線の吸収に起因する発熱を抑えることができる。例えば、近赤外線を反射することができる反射シートの表面に本発明の赤外線透過性暗色インキにより赤外線透過暗色層60を形成することで、その外観を暗色としながら、近赤外線を反射することのできる赤外線反射シートを製造することができる。
本発明の赤外線透過性暗色インキに含まれる顔料成分は、以下にその詳細を説明する茶色系顔料と、フタロシアニン系顔料と、からなる暗色顔料を含有する。このような暗色顔料を含んでなる顔料成分を含有する本発明の赤外線透過性暗色インキは、外観が暗色であって、赤外線透過率が高い優れたインキである。
樹脂成分の主剤成分は、例えばポリウレタンジオールと脂肪族ポリカーボネートジオールとの混合物を含む、ポリウレタン/ポリカーボネートジオール系を用いることができる。主剤を構成するポリウレタンジオール及び脂肪族ポリカーボネートジオールは、ともに水酸基を有するポリオールであり、イソシアネート基を有する硬化剤と反応して、接着剤層を構成するものである。本実施形態においては、主剤を特定のポリウレタンジオールと脂肪族ポリカーボネートジオールを所定量配合した混合物とすることによって、赤外線透過暗色層60の接着性及び耐候性を向上させることができる。
赤外線透過性暗色インキに用いることができる硬化剤は、例えばポリイソシアネート化合物を主成分とするものが挙げられる。ポリイソシアネート化合物は、1分子中に2以上のイソシアネート基を有する化合物であり、このイソシアネート基が上記主剤のポリウレタンジオール化合物中の水酸基と反応することにより、ポリウレタンジオール化合物を架橋する。このようなポリイソシアネート化合物としては、上記主剤のポリウレタンジオール化合物を架橋することができるものであれば特に限定されるものではないが、例えば、ポリウレタンジイソシアネート、ヘキサメチレンジイソシアネート(以下、「HDI」)、イソシアヌレート変性のイソホロンジイソシアネート(以下、「ヌレート変性IPDI」)等を例示することができる。これらのポリイソシアネート化合物の中でも、HDIとヌレート変性IPDIとを組み合わせた混合物が水酸基に対する反応性を向上させる観点より好ましい。尚、硬化剤をHDIとヌレート変性IPDIとの混合物とする場合、HDIとヌレート変性IPDIは、70:30〜50:50(質量比)の範囲で用いることが好ましい。
赤外線透過性暗色インキの成分は、硬化剤を含有し基材等同士を接合するものとする場合には、主剤と硬化剤の配合比率は、(ポリイソシアネート化合物由来のイソシアネート基)/(ポリウレタンジオール化合物由来の水酸基)の比が1.0以上3.5以下の範囲であることが好ましく、更に、1.2以上3.0以下の範囲にあることが好ましい。主剤成分のポリウレタンジオール化合物と硬化剤成分のポリイソシアネート化合物との配合比率が上記範囲にあることにより、各基材を強固に接合することができる赤外線透過性暗色インキを得ることができるため好ましい。
上記の他、必要に応じてシランカップリング剤、粘着付与剤、安定化剤、充填剤、可塑剤、軟化点向上剤、触媒等を添加剤として混合することができる。シランカップリング剤としては、例えば、メチルトリメトキシラン、メチルトリエトキシシラン等のシランモノマー、ビニルトリエトキシシラン、ビニルトリメトキシシラン等のビニルシラン、3−メタクリロキシプロピルトリエトキシシラン、3−メタクリロキシプロピルトリメトキシシラン等のメタクリルシラン、3−グリシドキシプロピルトリメトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン等のエポキシシランを挙げることができる。粘着付与剤としては、ロジン系樹脂、テルペン系樹脂等が挙げられる。安定化剤としては、酸化防止剤、紫外線防止剤等が挙げられる。充填剤としては、無機フィラー等が挙げられる。
上記の赤外線透過性暗色インキの組成物として、良好な塗布性及びハンドリング適性を得るために、溶剤成分を添加することが好ましい。このような溶剤成分としては、上記酢酸エチル、酢酸メチル、プロピオン酸メチル等のカルボン酸エステルを挙げることができるがこれに限定されない。尚、主剤と硬化剤の2液タイプとして構成される場合には、主剤で使用される溶剤成分と硬化剤で使用される溶剤成分はそれぞれ独立に選択され、同一でも異なっていても良い。
上記赤外線透過性暗色インキを用いることにより、赤外線反射シートを製造することができる。赤外線反射シートとは、図2の赤外線反射シート6のように、透明密着層62と赤外線透過暗色層60と反射層61とが積層された積層体を例示することができる。尚、図2の赤外線反射シート6は太陽電池モジュール用の裏面保護シートとして用いられているが、本発明の赤外線反射シートの使用用途が太陽電池モジュール用の裏面保護シートに限定されるわけではない。以下、赤外線反射シートを構成する各層について各々説明する。
本実施形態に関する赤外線透過暗色層60は、水酸基を有する主剤樹脂と、イソシアネート基を有する硬化剤と、顔料成分とを、を含有する層である。本実施形態に関する赤外線透過暗色層60は、水酸基を有する主剤樹脂と、イソシアネート基を有する硬化剤と、を含有しており、シート同士を接着する機能を有する。
反射層61は、白色顔料を含む樹脂シート又は白色顔料を含むコート層(塗布膜や印刷膜)を形成した樹脂シートからなり、近赤外線を反射する白色樹脂層である。反射層61は、赤外線透過暗色層60を透過してきた近赤外線を反射する機能を有する。そのため、例えば、本実施形態の赤外線反射シート6が、太陽電池モジュール用の裏面保護シートとして用いられた場合には、本実施形態の赤外線反射シート6は、太陽電池モジュール1の発電効率向上に十分に寄与することのできる赤外線反射シート(裏面保護シート)6となる。尚、本明細書では、樹脂をシート状に加工したものの名称として樹脂シートという用語を使用するが、この用語は、樹脂フィルムも含む概念として使用する。
本実施形態に関する透明密着層62は、近赤外光を透過し、赤外線反射シート6の最外層に配置される層である。又、透明密着層62は、他の樹脂層と密着性を有する層であり、例えば、エチレン−酢酸ビニル共重合体樹脂(EVA樹脂)、又はポリエチレン等のポリオレフィンが含有される樹脂層と密着性を有する層である。そのため、図2の透明密着層62のように、背面封止材層5と透明密着層62とを積層させ、密着させることができる。
本実施形態の赤外線反射シート6には、本発明の効果を害さない範囲で、その他の層を設けても良い。例えば、上記の反射層61の透明密着層62の積層面の反対側であって、赤外線反射シート6の最外側にフッ素系樹脂やポリエチレンテレフタレート(PET)等からなる耐候層(図示せず)を更に積層されていても良い。この場合は意匠性向上のために耐候層を暗色としても良い。或いは、反射層61と透明密着層62の間に、例えば裏面保護シート6の強度を増すための他の透明な補強層(図示せず)を設けても良い。
本実施形態の赤外線反射シートの好ましい使用例について説明する。例えば、本実施形態の赤外線反射シート6を、太陽電池モジュールの太陽電池素子の非受光面側に配置することで、太陽電池モジュール用の裏面保護シートとして用いることができる。図1は、太陽電池モジュ−ルについて、その層構成の一例を例示する断面の模式図である。太陽電池を構成する太陽電池モジュール1は、図1に示すように入射光7の受光面側から、透明前面基板2、前面封止材層3、太陽電池素子4、背面封止材層5、裏面保護シート(赤外線反射シート)6が順に積層された構成である。
裏面保護シート6は、反射層61と透明密着層62の間に赤外線透過暗色層60を設けて、ドライラミネート加工により製造することができる。尚、その他の層を設けることにより、接着剤層が複数の層となる場合にも、同様の方法で各層を密着させて積層することができる。
太陽電池を構成する太陽電池モジュール1の製造方法は、太陽電池を構成する各部材を順次積層し、真空熱ラミネート加工により一体化する方法を例示することができる。この際のラミネート温度は、130℃以上190℃以下の範囲内とすることが好ましい。又、ラミネート時間は、5分以上60分以下の範囲内が好ましく、特に8分以上40分以下の範囲内が好ましい。このようにして、太陽電池を構成する各部材を一体成形体として加熱圧着成形して、太陽電池モジュール1を製造することができる。
本発明の赤外線反射シートの他の実施形態について図6を用いて説明する。(尚、必要に応じて、図6の本実施形態の赤外線反射シート6と区別するために、図2の赤外線反射シート6ように赤外線透過暗色層60がシート同士を接着する機能を有する赤外線透過暗色層が積層された赤外線反射シートについて、「上記の実施形態の赤外線反射シート」と表記することがある。)本実施形態の赤外線反射シートの赤外線透過暗色層60は、シート同士を接着する機能を有しない赤外線透過暗色層60であり、透明密着層62と反射層61との間に積層される層のうち2つの層が、赤外線透過暗色層60及び透明接着剤層63である。意匠性の観点からシートの全面を暗色にはせず、例えば、パターニングのような模様等を施すために、部分的に着色された赤外線反射シートが求められる場合がある。このような赤外線反射シートを製造する際には、例えば、予め、赤外線透過性を有する赤外線透過性暗色インキを、透明密着層及び/又は反射層のような樹脂シートに部分的に塗布し、このように部分的に塗布された赤外線透過性暗色インキを硬化させることによって赤外線透過暗色層60を形成し、その後顔料を混入させていない透明接着剤を塗布及び硬化させて透明接着剤層を形成し、反射層と透明密着層とを積層することで、部分的に着色されていることによってパターニングのような模様等を有する赤外線反射シートを製造することができる。
以下、この実施形態における赤外線反射シートについて、この実施形態に特有の部分を中心に説明する。赤外線透過暗色層60は、主として、反射層61と透明密着層62の間に積層体として配置される。赤外線透過暗色層60は、透明密着層及び/又は反射層表面の全面に積層されていても良いし、透明密着層及び/又は反射層表面の一部にのみに積層されていても良い。透明密着層及び/又は反射層表面の一部にのみに赤外線透過暗色層60が積層された赤外線反射シートは、意匠性の高い赤外線反射シートである。尚、この赤外線透過暗色層60は、反射層61より受光面側であれば、例えば図6に示すように透明密着層62に接着させても良いし、図6に示すもの以外でも反射層61と接触させる形で反射層61の内側に積層させても良い。
透明接着剤層63は、主として反射層61と透明密着層62を接合するために設けられる接着剤層である。本実施形態において透明接着剤層63は、反射層61の上面、又は、該上面に対向する透明密着層62の下面に塗布された透明接着剤が積層後に硬化することによって形成される。
本実施形態に関する透明密着層は、上記の実施形態の赤外線反射シートに用いられる透明密着層に用いられる層と同様のものを用いることができる。本実施形態に関する透明密着層は、押し出し法、Tダイ法等のフィルム成形法により製造されたフィルムやシートを使用することができる。
又、透明接着剤層及び透明密着層の代わりに、透明易接着剤層が、背面封止材層5と赤外線透過暗色層60との間に形成されていても良い。透明易接着剤層とは、いわゆるプライマー層であり、透明易接着剤層を構成するプライマー組成物を、例えばオレフィン系樹脂と水性媒体を含有してなり、有機溶剤を実質的に含有しないプライマー組成物を用いることができる。透明接着剤層及び透明密着層の代わりに、透明易接着剤層を積層することにより、赤外線反射シートの層を減らすことが可能になるため、生産性の面から好ましい。
本実施形態の赤外線反射シートには、上記の実施形態の赤外線反射シートと同様に本発明の効果を害さない範囲で、その他の層を設けても良い。
本実施形態の赤外線反射シートは、例えば赤外線透過暗色層60を予め積層した反射層61又は透明密着層62を用いてそれらの間に透明接着剤層63を介して、ドライラミネート加工により製造することができる。尚、その他の層を設けることにより、透明接着剤層が複数の層となる場合にも、同様の方法で各層を密着させて積層することができる。
本実施形態の赤外線反射シートは、上記の太陽電池モジュールの製造方法と同様に太陽電池を構成する各部材を順次積層し、例えば真空熱ラミネート加工により一体化することにより製造することができる。
窒素雰囲気下、攪拌機、窒素ガス導入管を備えたフラスコに、エチレングリコール(32.3質量部)、2,2−ジメチル−1,3−プロパンジオール(270.8質量部)、1,6−ヘキサンジオール(122.9質量部)、アジピン酸(228.1質量部)、イソフタル酸(664質量部)を加え、180℃から220℃にて窒素にてバブリングさせ、酸価2mgKOH/gまで反応させ、酢酸エチル(860質量部)を加え、ポリエステルジオールHの50%溶液を得た。得られた樹脂の水酸基価は、32mgKOH/gであり、数平均分子量は約3500であった。
ヘキサメチレンジイソシアネート(HDIアダクト:2官能)とイソシアヌレート変性のイソホロンジイソシアネート(ヌレート変性IPDI)の混合物を使用した。上記アダクト変性HDI及びヌレート変性IPDIの混合比(HDIアダクト)/(ヌレート変性IPDI)を6:4(質量比)とした。
顔料:茶色系顔料(ベンズイミダゾロン系顔料(PigmentBrown25、粒径0.08μm))、フタロシアニン系顔料(非晶質型フタロシアニン系顔料青(PigmentBlue15、粒径0.15〜0.20μm))
溶剤:酢酸エチル
上記主剤(固形分率50質量%)、上記硬化剤(固形分率10質量%)、上記茶色系顔料(ベンズイミダゾロン系顔料)、上記フタロシアニン系顔料(非晶質型フタロシアニン系顔料)(ベンズイミダゾロン系顔料とフタロシアニン系顔料との含有量比が52.5:47.5、樹脂成分100質量部に対して顔料成分が35質量部)を、上記溶剤に溶解させて調製した。
有機顔料を以下のようにし、固形分塗布量10g/m2以上20g/m2以下(硬化後厚さ10μm以上20μm以下)となるように調製した以外はインキ1同様に調製した。
顔料:ジオキサジン化合物16.7質量%(樹脂成分100質量部に対して顔料成分が20質量部)
本実施形態に係る赤外線透過性暗色インキの近赤外線の反射性(透過性)を評価するために、実施例及び比較例として、以下に示す方法で、透過性測定用試料を作製した。
反射層:東レ製、白色PET、188μm
透明密着層となる樹脂基材として下記の樹脂を用いた。
透明密着層:ポリエチレン、60μm
[実施例1]:上記反射層からなるシート上に、インキ1をグラビアコートし(塗布量は5g/m2)、厚さ5μm(乾燥状態)の接着剤層を、その上に上記透明密着層を積層し、45℃以上55℃以下、168時間のエージング処理をして加熱硬化させることにより赤外線反射シートを作成した。
分光光度計(株式会社日立ハイテクノロジーズ製、「U−4100」)を用いて、実施例1及び比較例1の赤外線反射シート試料について光を入射したときの、波長300nm〜1200nmの光の反射率(%)を評価した。評価結果を図3に示した。
<サンプル作成>
[実施例2〜4]:実施例1と同様にインキ1を各塗布量によりグラビアコートすることで赤外線反射シートを作成した。その後、各赤外線反射シートを裏面保護シートとして疑似モジュールを新たに作成した。
JIS Z8722に準拠し、D65光源、10°視野角の条件によって、KONICA MINOLTA分光測色計CM−700dを用いて各サンプルを透明樹脂層側から光源を当てることで測定を行った。本試験により得られた色座標の結果を表1、図4及び図5に示す。
インキ1の茶色系顔料(ベンズイミダゾロン系顔料(表2中、茶と表記))とフタロシアニン系顔料(表2中、青と表記)との含有量比を表2になるように配合比(質量比)を変更したインキを、塗布量を5g/m2として上記色座標−塗布量依存性試験1同様に疑似モジュールを作成し、JIS Z8722に準拠し、D65光源、10°視野角の条件によって、KONICA MINOLTA分光測色計CM−700dを用いて各サンプルを透明樹脂層側から光源を当てることで測定を行った。又、測定結果からカーボンブラックとの色差(ΔE*ab)をそれぞれ求めた。本試験により得られた色座標の測定結果及びカーボンブラックとの色差(ΔE*ab)を表2に示す。尚、表2中の「茶色系顔料の含有量」の記載は、フタロシアニン系顔料100質量部に対する茶色系顔料の含有量を意味する。
<サンプル作成>
[実施例10]:実施例1と同様にインキ1の塗布量を7g/m2とし、グラビアコートすることで赤外線反射シートを作成した。その後、各赤外線反射シートを裏面保護シートとして疑似モジュールを実施例2〜4同様に新たに作成した。
上記サンプルを170℃14時間保管し、保管後の色調を測定した。色調は、JIS Z8722に準拠し、D65光源、10°視野角の条件によって、実施例、及び比較例の各試料の色座標を測定することにより行った。各試料測定には、KONICA MINOLTA分光測色計CM−700dを用いて測定を行った。
<サンプル作成>
インキ1、及びインキ2により接着して、実施例11、及び参考例の接着性測定用試料をそれぞれ作成した。試料作成は、実施例11は、実施例1と同様にインキ1をグラビアコートすることで赤外線反射シートを作成した(インキ1の塗布量は5g/m2、厚さ5μm(乾燥状態))。参考例は、比較例1と同様にインキ2をグラビアコートすることで赤外線反射シートを作成した(インキ2の塗布量は10g/m2、厚さ10μm(乾燥状態))。
プレッシャークッカー試験機(平山製作所製:HASTTEST)にて120℃、85%RH、1.6atmの条件に設定し、上記各試料を一定時間(表4中、投入前を0h、24時間投入後を24h等と表記)投入した。その後、上記剥離試験を3回行った。投入前及び一定時間投入後の各測定結果の平均値を表4に示す。
本実施形態に係る裏面保護シートの接着性、接着耐久性、耐ブロッキング性、密着性、色座標−塗布量依存性を評価するために、以下に示す方法で接着剤を製造し、該接着剤を用いた接着性測定用試料を作成した。
[主剤]
攪拌機、温度計、窒素ガス導入管を備えた丸底フラスコに数平均分子量1000の脂肪族ポリカーボネートジオール(50質量部)と、1,6−ヘキサンジオール(70質量部)と、1,8−オクタンジオール(30質量部)と、イソホロンジイソシアネート(IPDI)(176.6質量部)、イソホロンジイソシアネート(IPDI)のトリメチロールプロパン(TMP)アダクト変性物(10質量部)と、酢酸エチル(333.6質量部)を仕込み、窒素ガス導入下にて、赤外線吸収スペクトルにて2270cm−1のイソシアネートの吸収が消失するまで加熱環流させ、グリコール変性量:10%、IPDI変性量:2%の実施例1の主剤樹脂を調製した。尚、本実施例において、グリコール変性量とは、上記の主剤樹脂成分の全成分質量に対するアルキレンジオール化合物(本実施例においては、1,6−ヘキサンジオールと1,8−オクタンジオールの混合物)の質量(質量比%)をいい、IPDI変性量とは、上記の主剤樹脂成分の全成分質量に対する変性イソシアネート化合物(本実施例においては、イソホロンジイソシアネート(IPDI)のトリメチロールプロパン(TMP)アダクト変性物)の質量(質量比%)をいう。
ヘキサメチレンジイソシアネート(HDI)のヌレート体(40質量部)とイソホロンジイソシアネート(IPDI)のトリメチロールプロパン(TMP)アダクト変性物(60質量部)とからなる硬化剤を調製した。又、ポリイソシアネート化合物のNCO価と架橋性主剤樹脂のOH価の比であるNCO/OH比がそれぞれ表5になるようにそれぞれ配合した。
顔料:茶色系顔料(ベンズイミダゾロン系顔料(PigmentBrown25、粒径0.08μm))、フタロシアニン系顔料(非晶質型フタロシアニン系顔料青(PigmentBlue15、粒径0.15〜0.20μm))
溶剤:酢酸エチル
上記主剤、上記硬化剤、上記茶色系顔料(ベンズイミダゾロン系顔料)及び上記フタロシアニン系顔料(茶色系顔料とフタロシアニン系顔料との含有量比が52.5:47.5、主剤樹脂成分100質量部に対して顔料成分が40質量部)を、上記溶剤に溶解させてそれをインキ3とした。
[主剤]
窒素雰囲気下、攪拌機、窒素導入管を備えたフラスコに、エチレングリコール(32.3質量部)、2,2−ジメチル−1,3−プロパンジオール(270.8質量部)、1,6−ヘキサンジオール(122.9質量部)、アジピン酸(228.1質量部)、イソフタル酸(664質量部)を加え、180℃から220℃にて窒素にてバブリングさせ、酸価2mgKOH/gまで反応させ、酢酸エチル(860質量部)を加え、ポリエステルジオールHの50%溶液を得た。得られた樹脂のOH価は、32mgKOH/gであり、数平均分子量は約3500であった。
溶剤:酢酸エチル
上記主剤(固形分率50質量%)、上記硬化剤(固形分率10質量%)、ジオキサジン化合物16.7質量%(主剤樹脂成分100質量部に対して顔料成分が20質量部)
実施例12〜15、比較例8〜10の試料に対して下記の方法で耐ブロッキング性に関する試験を行い、測定結果により耐ブロッキング性を評価した。試験片は全て15mm幅である。
○:暗色インキ層の転移なく、自然にシート同士が剥離する
△:暗色インキ層の転移なく、シート同士の剥離時の若干の密着手ごたえ有り
×:暗色インキ層の転移あり、及び/又は、シート同士の剥離時に密着手ごたえ有り
実施例12〜15、比較例8〜10の試料に対して下記の方法で耐ブロッキング性に関する試験を行い、測定結果により耐ブロッキング性を評価した。試験片は全て15mm幅である。
○:0%のコーティング剥離
△:0%超15%以下のコーティング剥離
×:15%超のコーティング剥離
<サンプル作成>
[実施例13〜15]:白PET(東レ社製白PET厚さ188μm)フィルムの表面に、赤外線透過性暗色インキ液をバーコーターにて塗工し(塗布量は表6に記載)、塗工されたインキ液を120℃で2分間乾燥させて基材表面に暗色インキ層を形成した。そして乾燥直後の暗色インキ層表面に透明接着剤をグラビアコートし(塗布量は5.0g/m2)、厚さ5.0μm(乾燥状態)の接着剤層を、その上にポリエチレン樹脂(厚さ60μm)を積層し、45℃〜55℃、168時間のエージング処理をして加熱硬化させることにより裏面保護シートを作成し、裏面保護シートから疑似モジュールを新たに作成した。
JIS−Z8722に準拠し、D65光源、10°視野角の条件によって、KONICA MINOLTA分光測色計CM−700dを用いて各サンプルを透明樹脂層側から光源を当てることで測定を行った。本試験により得られた色座標の結果を表6に示す。
<サンプル作成>
白PET(東レ社製白PET、188μm)フィルムの表面に、赤外線透過性暗色インキ液をバーコーターにて塗工し(塗布量は4g/m2)、塗工されたインキ液を120℃で2分間乾燥させて基材表面に赤外線透過暗色層を形成した。そして、赤外線透過暗色層の表面に上記透明接着剤をグラビアコートし(塗布量は5.0g/m2)、厚さ5.0μm(乾燥状態)の透明接着剤層を、その上にポリエチレン樹脂(60μm)を積層し、45℃以上55℃以下、168時間のエージング処理をして加熱硬化させることにより赤外線反射シートのサンプルを作成した。
2 透明前面基板
3 前面封止材層
4 太陽電池素子
5 背面封止材層
6 赤外線反射シート(裏面保護シート)
7 入射光
60 赤外線透過暗色層
61 反射層
62 透明密着層
63 透明接着剤層
Claims (11)
- 赤外線反射シートであって、
前記赤外線反射シートは、反射層と赤外線透過暗色層とが積層されてなり、
前記赤外線透過暗色層は、第1の顔料と、第2の顔料と、を含有し、
前記第1の顔料は、ベンズイミダゾロン系顔料、4−[(2,5−ジクロロフェニル)アゾ]−3−ヒドロキシ−N−(2,5−ジメトキシフェニル)−2−ナフタレンカルボキサミド、1−[(4−ニトロフェニル)アゾ]−2−ナフタレノール、ビス[3−ヒドロキシ−4−(フェニルアゾ)−2−ナフタレンカルボン酸]銅塩、C.I.PigmentBrown7、N,N’−ビス(2,4−ジニトロフェニル)−3,3’−ジメトキシ−1,1’−ビフェニル−4,4’−ジアミン、3,4,9,10−ペリレンテトラカルボン酸ジイミド、Δ2,2’(1H,1’H)−ビナフト[2,1−b]チオフェン−1,1’−ジオン及びN、N’−(10,15,16,17−テトラヒドロ−5,10,15,17−テトラオキソ−5H−ジナフト[2,3−a:2’,3’−i]カルバゾール−4,9−ジイル)ビス(ベンズアミド)からなる群より選ばれた少なくとも一種以上の顔料であり、
前記第2の顔料は、フタロシアニン系顔料であり、
前記赤外線反射シートは、JIS−Z8722に準拠して、D65光源、10°視野角の条件によって測定した前記赤外線透過暗色層の色調とカーボンブラックの色調との色差ΔE*abが10以下である、赤外線反射シート。 - 前記赤外線透過暗色層は、水酸基を有する主剤樹脂と、顔料成分とを含み、
前記主剤樹脂100質量部に対する前記顔料成分の含有量が20質量部以上40質量部以下であり、
前記顔料成分は、前記第1の顔料と、前記第2の顔料と、を含んでいる、請求項1に記載の赤外線反射シート。 - 前記赤外線透過暗色層を形成する赤外線透過性暗色インキの固形分換算の塗布量が5g/m2以上15g/m2以下である請求項2に記載の赤外線反射シート。
- 透明密着層と、反射層と、を少なくとも含む複数の層が積層されてなる赤外線反射シートであって、
前記透明密着層と前記反射層との間に積層される層のうち2つの層が、赤外線透過暗色層及び透明接着剤層であり、
前記赤外線透過暗色層は、第1の顔料と、第2の顔料と、を含有し、
前記第1の顔料は、ベンズイミダゾロン系顔料、4−[(2,5−ジクロロフェニル)アゾ]−3−ヒドロキシ−N−(2,5−ジメトキシフェニル)−2−ナフタレンカルボキサミド、1−[(4−ニトロフェニル)アゾ]−2−ナフタレノール、ビス[3−ヒドロキシ−4−(フェニルアゾ)−2−ナフタレンカルボン酸]銅塩、C.I.PigmentBrown7、N,N’−ビス(2,4−ジニトロフェニル)−3,3’−ジメトキシ−1,1’−ビフェニル−4,4’−ジアミン、3,4,9,10−ペリレンテトラカルボン酸ジイミド、Δ2,2’(1H,1’H)−ビナフト[2,1−b]チオフェン−1,1’−ジオン及びN、N’−(10,15,16,17−テトラヒドロ−5,10,15,17−テトラオキソ−5H−ジナフト[2,3−a:2’,3’−i]カルバゾール−4,9−ジイル)ビス(ベンズアミド)からなる群より選ばれた少なくとも一種以上の顔料であり、
前記第2の顔料は、フタロシアニン系顔料であり、
前記赤外線反射シートは、JIS−Z8722に準拠して、D65光源、10°視野角の条件によって測定した前記赤外線透過暗色層の色調とカーボンブラックの色調との色差ΔE*abが10以下である、赤外線反射シート。 - 前記赤外線透過暗色層は、水酸基を有する主剤樹脂と、硬化剤と、顔料成分とを含み、
前記主剤樹脂100質量部に対する前記顔料成分の含有量が20質量部以上50質量部以下であり、
前記主剤樹脂のOH価に対する前記硬化剤のNCO価の比であるNCO/OH比が1.0以上2.0以下であって、
前記顔料成分は、前記第1の顔料と、前記第2の顔料と、を含んでいる、請求項4に記載の赤外線反射シート。 - 前記赤外線透過暗色層を形成する赤外線透過性暗色インキの固形分換算の塗布量が、3g/m2以上7g/m2以下である請求項5に記載の赤外線反射シート。
- 前記赤外線透過暗色層は、硬化剤を含有し、
前記硬化剤が、ジイソシアネート化合物である請求項5又は6に記載の赤外線反射シート。 - 前記赤外線透過暗色層が、前記透明密着層及び/又は前記反射層の一部のみに積層されている請求項4から7のいずれかに記載の赤外線反射シート。
- 前記赤外線反射シートの前記赤外線透過暗色層の積層側の表面に、更に透明易接着剤層が積層されてなる請求項1から8のいずれかに記載の赤外線反射シート。
- 前記反射層における前記赤外線透過暗色層の積層面の反対側の面には、赤外線透過コート層が積層されていて、
前記赤外線透過コート層は、暗色系の有機顔料を含んでなり、750nm以上1500nm以下の近赤外線を透過する層である、請求項1から9のいずれかに記載の赤外線反射シート。 - 請求項1から10のいずれかに記載の赤外線反射シートと、
太陽電池素子と、を有し、
前記赤外線反射シートは、前記太陽電池素子の非受光面側に配置されている太陽電池モジュール。