JP2019031727A - HIGH-STRENGTH Zn-Al-Mg-BASED SURFACE-COATED STEEL SHEET FOR AUTOMOBILE COMPONENTS AND AUTOMOBILE COMPONENTS USING THE SAME - Google Patents

Abstract

To provide a high-strength hot dip Zn-Al-Mg-based plated steel sheet for automobile components, in which the in-steel concentration of hydrogen entering the steel in a plating line is remarkably lowered, and which exhibits the inherent excellent corrosion resistance of a Zn-Al-Mg-based plated layer, and automobile components using the same.SOLUTION: A high strength surface-coated steel sheet for automobile components comprises a Zn-Al-Mg-based coating layer disposed on the surface of a substrate steel sheet containing, in terms of mass%, 0.01%-0.20% of C, 0.01%-0.50% of Si, 0.10%-2.50% of Mn, 0.005%-0.050% of P, 0.0005%-0.010% of B, 0.01%-0.20% of Ti, 0%-0.10% of Nb, 0%-0.50% of Mo, 0%-0.50% of Cr, 0.01%-0.10% of Al, and the balance Fe and inevitable impurities, wherein the diffusible hydrogen concentration in the substrate steel sheet is 0.30 ppm or less, and the time until rust is generated in a salt spray test is 7000 hours or longer. There are also provided automobile components using the same.SELECTED DRAWING: Figure 1

Description

本発明は、高強度鋼板の表面にＺｎ−Ａｌ−Ｍｇ系表面被覆層を形成した表面処理鋼板であって、特に水素脆性の要因となる鋼中水素濃度を低減し、かつ高耐食性を維持した自動車部品用高強度表面被覆鋼板およびそれを用いた自動車部品に関する。   The present invention is a surface-treated steel sheet in which a Zn-Al-Mg-based surface coating layer is formed on the surface of a high-strength steel sheet, particularly reducing the hydrogen concentration in steel, which causes hydrogen embrittlement, and maintaining high corrosion resistance. The present invention relates to a high-strength surface-coated steel sheet for automobile parts and an automobile part using the same.

近年、自動車部品分野では軽量化および省資源化を目的とした高強度高防錆鋼板のニーズが高まっている。その高強度高防錆鋼板は、プレス加工や曲げ加工をはじめ様々な加工が施されるため、高強度および高耐食性であることに加え、加工性に優れることも重要である。昨今、需要が増している防錆効果の高い表面処理鋼板として、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板がある。しかしながら、この種のめっき鋼板では、めっき原板に高張力鋼を使用した場合、めっきラインで不可避的に鋼中に侵入する水素に起因して、いわゆる水素脆化を起こしやすく、用途によっては問題となる。一般的な溶融亜鉛系めっきラインでは、めっき原板である素材鋼板は、めっき浴の直前で、水素ガスを含む還元性雰囲気中での加熱処理を受ける。この加熱雰囲気中の水素が素材鋼板中に侵入し、水素脆化の原因となる。また、めっき前に行われる電解脱脂等の湿式工程でも水素の侵入が考えられ、これも水素脆化の要因となり得る。   In recent years, there has been an increasing need for high-strength, high-rust-proof steel sheets aimed at reducing weight and saving resources in the automotive parts field. Since the high-strength and high-rust-proof steel sheet is subjected to various processes including pressing and bending, it is also important to have excellent workability in addition to high strength and high corrosion resistance. Recently, as a surface-treated steel sheet having a high rust-preventing effect, which is increasing in demand, there is a molten Zn—Al—Mg-based steel sheet. However, with this type of plated steel sheet, when high-strength steel is used as the plating base plate, so-called hydrogen embrittlement is likely to occur due to hydrogen unavoidably entering the steel in the plating line. Become. In a general hot dip galvanizing line, a raw steel plate that is a plating original plate is subjected to a heat treatment in a reducing atmosphere containing hydrogen gas immediately before the plating bath. Hydrogen in this heated atmosphere enters the material steel plate and causes hydrogen embrittlement. In addition, intrusion of hydrogen can be considered even in a wet process such as electrolytic degreasing performed before plating, which can also cause hydrogen embrittlement.

めっき鋼板における水素脆化は、通常、電気めっきやその前処理の酸洗工程での水素吸蔵によって生じることが知られており、特に９８０ＭＰａ級以上の高張力鋼をめっき原板に使用したときに問題となりやすいとされる。ところが溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板では、７８０ＭＰａ級、あるいは更に５９０ＭＰａ級といった比較的低強度レベルの高張力鋼を使用しても、密着曲げ等の非常に厳しい加工を施すと脆性的破壊が生じることがある。発明者らの詳細な調査によれば、この種の脆性的破壊も、めっきラインで侵入した水素に起因する事象であることがわかった。また、溶融Ｚｎ−Ａｌ−Ｍｇめっき鋼板では、他の一般的な溶融亜鉛系めっき鋼板と比べ、めっき層が鋼板からの水素の離脱を妨げる「障壁」となりやすいことがわかってきた。従って、溶融Ｚｎ−Ａｌ−Ｍｇ系めっきを施した高強度鋼板の加工に対する信頼性レベルを向上させるためには、当該鋼板の水素脆化を抑止する技術の確立が望まれる。   It is known that hydrogen embrittlement in a plated steel sheet is usually caused by hydrogen occlusion in the electroplating or pickling process of its pretreatment, and is particularly problematic when high-tensile steel of 980 MPa class or higher is used as a plating base plate. It is said that it is easy to become. However, with a hot-dip Zn-Al-Mg-based plated steel sheet, even if a high strength steel of a relatively low strength level such as a 780 MPa class or a 590 MPa class is used, brittle fracture will occur if extremely severe processing such as contact bending is performed. May occur. According to detailed investigations by the inventors, it has been found that this kind of brittle fracture is also an event caused by hydrogen penetrating the plating line. In addition, it has been found that in a hot-dip Zn—Al—Mg plated steel sheet, the plating layer tends to be a “barrier” that hinders hydrogen from detaching from the steel sheet as compared with other general hot-dip galvanized steel sheets. Therefore, in order to improve the reliability level with respect to the processing of the high-strength steel sheet subjected to hot-dip Zn—Al—Mg plating, it is desired to establish a technique for suppressing hydrogen embrittlement of the steel sheet.

特開平７−１５０２４１号公報Japanese Patent Laid-Open No. 7-150241 特開２０１２−１７２２４７号公報JP 2012-172247 A 特許第５０９７３０５号公報Japanese Patent No. 5097305

神戸製鋼技報 Ｖｏｌ.５０，Ｎｏ.１，ｐ.６５Kobe Steel Engineering Reports Vol.50, No.1, p.65

鋼板の水素脆化対策の手法として、特許文献１には、鋼の化学組成および金属組織を適正化することにより、大気環境下の腐食反応で発生する水素が鋼板中に入ることを抑制する技術が開示されている。特許文献２には表面の孔食深さより深い位置におけるＭｎのミクロ偏析を低減させることにより、環境から侵入した水素に起因する水素脆化を抑制する技術が開示されている。これらの技術は鋼板を腐食環境で使用する際の水素侵入に対する対策であり、溶融めっきラインで既に侵入してしまった水素に対しては有効でない。   As a technique for countermeasures against hydrogen embrittlement of steel sheets, Patent Document 1 discloses a technique for suppressing hydrogen generated by a corrosion reaction in an atmospheric environment from entering steel sheets by optimizing the chemical composition and metal structure of the steel. Is disclosed. Patent Document 2 discloses a technique for suppressing hydrogen embrittlement due to hydrogen that has entered from the environment by reducing microsegregation of Mn at a position deeper than the surface pitting depth. These techniques are measures against hydrogen intrusion when the steel sheet is used in a corrosive environment, and are not effective against hydrogen that has already infiltrated in the hot dipping line.

鋼材中に侵入した水素を、鋼材の外部へ放出させるための処理として、ベーキング処理が知られている。ベーキング処理は、水素が侵入した鋼材を２００℃前後の温度で加熱することにより、鋼材中に侵入した水素を拡散させて鋼材表面から追い出す処理である。非特許文献１には電気亜鉛めっきを施した鋼製ボルトのベーキング処理に関する記載がある。それによると、拡散性水素の放出には１５０℃以上の加熱が有効であり、特に約２００℃での加熱が効果的であるという。しかし、溶融Ｚｎ−Ａｌ−Ｍｇ系めっきを施した鋼材の場合、１５０℃を超える温度域まで加熱するとめっき層の相構造が変化し、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の優れた耐食性が十分に維持できなくなる。そのため、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板において、その優れた耐食性を維持しながら、鋼材中に侵入した水素を効率的に放出させることは容易でなかった。   Baking treatment is known as a treatment for releasing hydrogen that has entered the steel material to the outside of the steel material. The baking process is a process in which hydrogen that has intruded into hydrogen is heated at a temperature of about 200 ° C. to diffuse the hydrogen that has intruded into the steel and expelled from the surface of the steel. Non-Patent Document 1 describes a baking process for steel bolts subjected to electrogalvanization. According to this, heating at 150 ° C. or higher is effective for releasing diffusible hydrogen, and heating at about 200 ° C. is particularly effective. However, in the case of a steel material subjected to hot-dip Zn—Al—Mg plating, the phase structure of the plating layer changes when heated to a temperature range exceeding 150 ° C., and the original excellent corrosion resistance of the hot-dip Zn—Al—Mg plating layer is obtained. It cannot be maintained sufficiently. For this reason, it has been difficult to efficiently release hydrogen that has penetrated into the steel material while maintaining its excellent corrosion resistance in the molten Zn—Al—Mg-based steel sheet.

また、ベーキング処理では一般的に酸化に起因する変色が生じやすい。水素を使用するような還元性雰囲気では鋼中の水素を除去することが困難であることから、ベーキング時の変色を完全に防止しようとすると真空炉での処理が必要となる。そのような処理はコスト増大を招くため、加工後の高強度部品に対する処理としては実用的な面もあるが、加工用素材としてのめっき鋼板に対しては採用し難い。特に鋼板の場合は表面の変色むらが目立ちやすい。そのため、ベーキング処理によって表面外観の均一性に優れる鋼板素材を実現することは一般に容易でない。   Further, in the baking process, discoloration due to oxidation is generally likely to occur. In a reducing atmosphere using hydrogen, it is difficult to remove hydrogen in the steel. Therefore, to completely prevent discoloration during baking, treatment in a vacuum furnace is required. Since such a process causes an increase in cost, there is a practical aspect as a process for a high-strength part after processing, but it is difficult to adopt it for a plated steel sheet as a processing material. In particular, in the case of a steel plate, surface discoloration unevenness is easily noticeable. For this reason, it is generally not easy to realize a steel sheet material having excellent surface appearance uniformity by baking.

一方、特許文献３には、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板の後処理として、水蒸気雰囲気中で加熱することによりＺｎの黒色酸化物に起因する黒色皮膜を形成する技術が開示されている。しかし、高張力鋼をめっき原板に適用した例は示されていない。   On the other hand, Patent Document 3 discloses a technique for forming a black film resulting from Zn black oxide by heating in a steam atmosphere as a post-treatment of a molten Zn—Al—Mg-based steel sheet. However, an example in which high-strength steel is applied to a plating original sheet is not shown.

本発明は、溶融Ｚｎ−Ａｌ−Ｍｇ系めっきを施した高強度鋼板において、めっきラインで鋼中に侵入した水素の鋼中濃度が顕著に低減されており、かつ溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の優れた耐食性を発揮する自動車部品用鋼板およびそれを用いた自動車部品を提供しようというものである。   The present invention provides a high-strength steel sheet that has been subjected to hot-dip Zn-Al-Mg plating, in which the concentration of hydrogen intruding into the steel in the plating line is significantly reduced, and hot-dip Zn-Al-Mg-based plating. It is intended to provide a steel sheet for automobile parts that exhibits the excellent corrosion resistance inherent to the layer and an automobile part using the same.

発明者らは詳細な研究の結果、高張力鋼をめっき原板に用いた溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に、テンションレベラーによる曲げ伸ばし変形やスキンパス圧延などを付与することによってめっき層にクラックを生じさせ、その後にベーキング処理を行うと、ベーキング温度を１５０℃以下の低温域に設定しても、鋼材中に侵入した水素を効率良く放出させることが可能になることを見いだした。この場合、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の高耐食性を十分に維持することができる。また、そのベーキング処理を水蒸気雰囲気中で行うことによって、意匠性の良い黒色外観の被覆層が得られることが確認された。本発明はこのような知見に基づいて完成したものである。   As a result of detailed studies, the inventors have cracked the plating layer by imparting bending extension deformation or skin pass rolling by a tension leveler to a hot-dip Zn-Al-Mg-based plated steel sheet using high-tensile steel as a plating base plate. It was found that if the baking process is performed after that, even if the baking temperature is set to a low temperature range of 150 ° C. or lower, hydrogen that has entered the steel material can be efficiently released. In this case, the original high corrosion resistance of the molten Zn—Al—Mg based plating layer can be sufficiently maintained. Moreover, it was confirmed that the coating layer of the black appearance with the good design property is obtained by performing the baking process in water vapor | steam atmosphere. The present invention has been completed based on such findings.

上記目的は、質量％で、Ｃ：０.０１〜０.２０％、Ｓｉ：０.０１〜０.５０％、Ｍｎ：０.１０〜２.５０％、Ｐ：０.００５〜０.０５０％、Ｂ：０.０００５〜０.０１０％、Ｔｉ：０.０１〜０.２０％、Ｎｂ：０〜０.１０％、Ｍｏ：０〜０.５０％、Ｃｒ：０〜０.５０％、Ａｌ：０.０１〜０.１０％、残部Ｆｅおよび不可避的不純物である鋼組成の素材鋼板の表面に、金属元素の組成比が質量％で、Ａｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部Ｚｎおよび不可避的不純物であるＺｎ−Ａｌ−Ｍｇ系被覆層を有する表面被覆鋼板であって、前記素材鋼板中の拡散性水素濃度が０.３０ｐｐｍ以下であり、ＪＩＳ Ｚ２３７１：２０１５に従う中性塩水噴霧試験（塩濃度：５０ｇ／Ｌ、温度：３５℃、試験片の裏面および端面シール：あり）による赤錆発生までの時間が７０００時間以上である、高強度表面被覆鋼板によって達成される。   The purpose is mass%, C: 0.01 to 0.20%, Si: 0.01 to 0.50%, Mn: 0.10 to 2.50%, P: 0.005 to 0.050. %, B: 0.0005 to 0.010%, Ti: 0.01 to 0.20%, Nb: 0 to 0.10%, Mo: 0 to 0.50%, Cr: 0 to 0.50% , Al: 0.01 to 0.10%, balance Fe and unavoidable impurities on the surface of the steel plate of the steel composition, the composition ratio of the metal element is mass%, Al: 1.0 to 22.0%, Mg: 1.3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to 0.10%, B: 0 to 0.05%, Fe: 2.0% or less, remaining Zn and inevitable Surface coated steel sheet having a Zn—Al—Mg based coating layer which is a general impurity, the diffusible hydrogen concentration in the material steel sheet is 0.30 ppm or less, and neutral salt spray according to JIS Z2371: 2015 It is achieved by a high-strength surface-coated steel sheet in which the time until the occurrence of red rust by the test (salt concentration: 50 g / L, temperature: 35 ° C., test piece back surface and end face seal: yes) is 7000 hours or more.

この自動車部品用高強度表面被覆鋼板の圧延直角方向の引張強さは例えば５９０ＭＰａ以上である。前記Ｚｎ−Ａｌ−Ｍｇ系被覆層の平均厚さは例えば３〜１００μｍである。上記高強度表面被覆鋼板のなかでも意匠性を改善したものとして、被覆層表面の明度Ｌ＊が６０以下の黒色外観を呈する鋼板が提供される。Ｚｎ−Ａｌ−Ｍｇ系被覆層の表面上には、さらに無機系皮膜あるいは有機系皮膜を有することができる。   The tensile strength in the direction perpendicular to the rolling direction of the high strength surface-coated steel sheet for automobile parts is, for example, 590 MPa or more. The average thickness of the Zn—Al—Mg based coating layer is, for example, 3 to 100 μm. Among the high-strength surface-coated steel sheets, a steel sheet exhibiting a black appearance with a lightness L * of the coating layer surface of 60 or less is provided as an improved design. On the surface of the Zn—Al—Mg coating layer, an inorganic coating or an organic coating can be further provided.

上記の自動車部品用高強度表面被覆鋼板の製造方法として、前記鋼組成を有する素材鋼板を水素と窒素の混合ガス中で５５０〜９００℃に加熱した後、大気に触れることなく、質量％でＡｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部がＺｎおよび不可避的不純物である溶融めっき浴に浸漬させる溶融めっき設備を用いて溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を作る工程（溶融めっき工程）、
前記溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に、テンションレベラーおよび圧延機のいずれか一方または双方を用いて合計伸び率０.２〜１.０％の歪を付与することにより、めっき層にクラックを導入する工程（クラック導入工程）、
前記のクラックを導入した溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を、７０〜１５０℃に加熱保持することにより、前記素材鋼板中の拡散性水素濃度を０.３０ｐｐｍ以下、より好ましくは０.２０ｐｐｍ以下に低減させる工程（ベーキング処理工程）、
を有する製造方法が提供される。 As a manufacturing method of the above-mentioned high strength surface coated steel sheet for automobile parts, after heating the material steel sheet having the steel composition to 550 to 900 ° C. in a mixed gas of hydrogen and nitrogen, it is Al in mass% without touching the atmosphere. : 1.0 to 22.0%, Mg: 1.3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to 0.10%, B: 0 to 0.05%, Fe: 2.0% or less, the process of making a hot-dip Zn—Al—Mg-based plated steel sheet using a hot dipping equipment immersed in a hot dipping bath in which the balance is Zn and inevitable impurities (hot dipping process),
By applying a strain with a total elongation of 0.2 to 1.0% to the molten Zn—Al—Mg based plated steel sheet using either one or both of a tension leveler and a rolling mill, cracks are formed in the plated layer. Step to introduce (crack introduction step),
The diffusible hydrogen concentration in the material steel plate is 0.30 ppm or less, more preferably 0.20 ppm or less by heating and maintaining the molten Zn—Al—Mg-based plated steel plate into which the cracks are introduced at 70 to 150 ° C. To reduce the process (baking process),
A manufacturing method is provided.

ベーキング処理工程に供する鋼板として、素材鋼板中の拡散性水素濃度が０.３５ｐｐｍ以上である鋼板を適用すると、特に効果的である。また、上記のベーキング処理を、水蒸気雰囲気中で７０〜１５０℃に加熱保持して、めっき層表面を水蒸気に接触させる方法で行うことにより、明度Ｌ＊が６０以下の黒色外観を呈する自動車部品用鋼板およびそれを用いた自動車部品を得ることができる。   It is particularly effective to apply a steel sheet having a diffusible hydrogen concentration in the raw steel sheet of 0.35 ppm or more as the steel sheet used for the baking process. In addition, the above baking treatment is performed by heating and maintaining at 70 to 150 ° C. in a water vapor atmosphere, and the plating layer surface is brought into contact with water vapor, whereby an automotive part having a black appearance with a lightness L * of 60 or less. A steel plate and an automobile part using the steel plate can be obtained.

本発明によれば、高張力鋼をめっき原板に用いて溶融Ｚｎ−Ａｌ−Ｍｇ系めっきを施した自動車部品用表面処理鋼板およびそれを用いた自動車部品において、めっきラインなどで鋼中に侵入した水素の濃度をベーキング処理により減じたものが提供される。この自動車部品用表面処理鋼板およびそれを用いた自動車部品は、耐水素脆化に対する信頼性が高い。かつ、ベーキング処理を経ているにもかかわらず、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の優れた耐食性が維持されている。さらに、ベーキング処理を利用して意匠性の高い黒色外観に仕上げることも可能である。本発明は、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板が本来有する高い耐食性、高張力鋼による高い強度、耐水素脆化に対する高い信頼性、さらには必要に応じて黒色調の表面外観による高い意匠性を、一挙に実現可能としたものである。   According to the present invention, in a surface-treated steel sheet for automobile parts that has been subjected to hot-dip Zn-Al-Mg plating using a high-strength steel as a plating base plate and an automobile part using the same, the steel has penetrated into the steel at a plating line or the like. A hydrogen concentration reduced by baking is provided. This surface-treated steel sheet for automobile parts and automobile parts using the steel sheet have high reliability against hydrogen embrittlement resistance. Moreover, despite the baking treatment, the original excellent corrosion resistance of the molten Zn—Al—Mg-based plating layer is maintained. Furthermore, it is also possible to finish the black appearance with high designability by using a baking process. The present invention has the high corrosion resistance inherent in the hot-dip Zn-Al-Mg plated steel sheet, the high strength of high-tensile steel, the high reliability against hydrogen embrittlement, and the high designability due to the black-colored surface appearance as required. Can be realized at once.

本発明における自動車部品とは、主に曲げ加工にて形成される自動車部品であり、シート部材、サイドシル、各種フレーム、メンバー、リンク類、カバー類およびブラケットを含む。     The automobile parts in the present invention are automobile parts mainly formed by bending, and include a seat member, a side sill, various frames, members, links, covers, and brackets.

クラックを導入しためっき鋼板Ｅ−２の被覆層表面のＳＥＭ写真。The SEM photograph of the coating layer surface of the plated steel plate E-2 which introduce | transduced the crack. クラックを導入しためっき鋼板Ｈ−２の被覆層表面のＳＥＭ写真。The SEM photograph of the coating layer surface of the plated steel plate H-2 which introduce | transduced the crack.

〔素材鋼板の化学組成〕
めっき原板に相当する素材鋼板の成分元素について説明する。本明細書において、素材鋼板の化学組成に関する「％」は特に断らない限り「質量％」を意味する。 [Chemical composition of steel plate]
The component elements of the material steel plate corresponding to the plating original plate will be described. In this specification, “%” relating to the chemical composition of the steel sheet means “mass%” unless otherwise specified.

Ｃは、鋼の高強度化に必要な元素である。引張強さ５９０ＭＰａ以上の強度レベルを得るためには０.０１％以上のＣ含有量を必要とする。Ｃ含有量が過剰になると組織の不均一性が顕著となり、加工性が低下する。Ｃ含有量は０.２０％以下に制限され、０.１６％以下に管理してもよい。   C is an element necessary for increasing the strength of steel. In order to obtain a tensile strength of 590 MPa or more, a C content of 0.01% or more is required. When the C content is excessive, the non-uniformity of the structure becomes remarkable, and the workability decreases. The C content is limited to 0.20% or less, and may be controlled to 0.16% or less.

Ｓｉは、高強度化に有効である他、セメンタイトの析出を抑制する作用を有し、パーライト等の生成を抑制するうえで有効である。これらの作用を十分に発揮させるために０.０１％以上のＳｉ含有量を確保する。多量にＳｉを含有すると、鋼板表面にＳｉ濃化層が生じ、めっき性の低下を招く要因となる。Ｓｉ含有量は０.５０％以下に制限され、０.２５％以下とすることがより好ましい。   In addition to being effective for increasing the strength, Si has the effect of suppressing the precipitation of cementite and is effective in suppressing the formation of pearlite and the like. In order to fully exhibit these actions, an Si content of 0.01% or more is ensured. When Si is contained in a large amount, a Si concentrated layer is formed on the surface of the steel sheet, which causes a decrease in plating properties. The Si content is limited to 0.50% or less, and more preferably 0.25% or less.

Ｍｎは、高強度化に有効である。引張強さ５９０ＭＰａ以上の強度レベルを安定して得るために０.１０％以上のＭｎ含有量を確保する。０.５０％以上とすることがより効果的である。Ｍｎ含有量が過大になると偏析が生じやすくなり加工性が低下する。Ｍｎ含有量は２.５０％以下とする。   Mn is effective for increasing the strength. In order to stably obtain a strength level of a tensile strength of 590 MPa or more, an Mn content of 0.10% or more is ensured. It is more effective to set it to 0.50% or more. If the Mn content is excessive, segregation is likely to occur and workability is reduced. The Mn content is 2.50% or less.

Ｐは、固溶強化に有効である。ここでは０.００５％以上のＰ含有量を確保する。０.０１０％以上に管理してもよい。Ｐ含有量が過大になると偏析が生じやすくなり加工性が低下する。Ｐ含有量は０.０５０％以下に制限される。   P is effective for solid solution strengthening. Here, a P content of 0.005% or more is secured. You may manage to 0.010% or more. When the P content is excessive, segregation is likely to occur and the workability is reduced. The P content is limited to 0.050% or less.

Ｂは、鋼のオーステナイト−フェライト変態を抑制し、変態組織強化に寄与する。また、ＴｉやＮｂを添加した場合には、オーステナイト−フェライト変態の抑制によりＴｉ系炭化物やＮｂ系炭化物の析出温度を低下させ、それらの炭化物を微細化させる効果を有する。上記効果を十分に得るために、０.０００５％以上のＢ含有量を確保する。０.００１％以上とすることがより効果的である。多量のＢ含有は硼化物の生成による加工性低下を招く要因となる。Ｂを添加する場合は０.０１０％以下の範囲で行う必要があり、０.００５％以下に管理してもよい。   B suppresses the austenite-ferrite transformation of steel and contributes to strengthening of the transformation structure. In addition, when Ti or Nb is added, the precipitation temperature of Ti-based carbides and Nb-based carbides is reduced by suppressing the austenite-ferrite transformation, and the carbides are refined. In order to sufficiently obtain the above effect, a B content of 0.0005% or more is ensured. It is more effective to make it 0.001% or more. A large amount of B is a factor that causes a decrease in workability due to the formation of borides. When adding B, it is necessary to carry out in the range of 0.010% or less, and you may manage to 0.005% or less.

Ｔｉは、Ｃと結合して微細なＴｉ系炭化物を形成し、高強度化に寄与する。その作用を十分に発揮させるために０.０１％以上のＴｉ含有量を確保する。過剰のＴｉ含有は加工性の低下を招く。Ｔｉ含有量は０.２０％以下とし、０.１５％以下に管理してもよい。   Ti combines with C to form fine Ti-based carbides, contributing to high strength. A Ti content of 0.01% or more is ensured in order to fully exert its action. Excessive Ti content causes deterioration of workability. Ti content may be 0.20% or less, and may be controlled to 0.15% or less.

Ｎｂは、Ｃと結合して微細なＮｂ系炭化物を形成し、高強度化に寄与する。また、組織の微細化、均一化にも有効である。従って、必要に応じてＮｂを含有させることができる。上記効果を十分に得るためには０.００５％以上のＮｂ含有量を確保することがより効果的である。多量のＮｂ含有は加工性の低下を招く。Ｎｂを添加する場合は０.１０％以下の範囲で行う。   Nb combines with C to form fine Nb-based carbides, contributing to high strength. It is also effective for making the structure finer and uniform. Therefore, Nb can be contained as necessary. In order to sufficiently obtain the above effect, it is more effective to secure an Nb content of 0.005% or more. When a large amount of Nb is contained, the workability is reduced. When adding Nb, it is performed within a range of 0.10% or less.

Ｍｏ、Ｃｒは、いずれも固溶強化によって強度を向上させる作用を有するので、必要に応じてＭｏ、Ｃｒの１種または２種を添加することができる。上記作用を十分に発揮させるためには、Ｍｏについては０.０１％以上、Ｃｒについても０.０１％以上の含有量を確保することがより効果的である。これらの元素を多量に含有すると延性の低下を招く。これらの１種または２種を添加する場合、Ｍｏ含有量は０.５０％以下、Ｃｒ含有量も０.５０％以下の範囲とする。   Since both Mo and Cr have the effect of improving strength by solid solution strengthening, one or two of Mo and Cr can be added as necessary. In order to sufficiently exhibit the above-described action, it is more effective to secure a content of 0.01% or more for Mo and 0.01% or more for Cr. When these elements are contained in a large amount, ductility is reduced. When one or two of these are added, the Mo content is 0.50% or less and the Cr content is 0.50% or less.

Ａｌは、脱酸作用を有する。その作用を十分に発揮させるために、鋼中のＡｌ含有量が０.０１％以上となるようにＡｌを添加することが望ましい。過剰のＡｌ含有は加工性の低下を招く。Ａｌ含有量は０.１０％以下に制限され０.０５％以下に管理してもよい。   Al has a deoxidizing action. In order to fully exhibit the action, it is desirable to add Al so that the Al content in the steel is 0.01% or more. Excessive Al content causes deterioration of workability. The Al content is limited to 0.10% or less and may be controlled to 0.05% or less.

その他、不純物として混入するＳは０.０１０％まで許容されるが、０.００５％以下であることがより好ましい。過剰な低Ｓ化は製鋼負荷の増大を招くので、通常、Ｓ含有量は０.０００５％以上で構わない。   In addition, S mixed as an impurity is allowed up to 0.010%, but more preferably 0.005% or less. Since excessively low S leads to an increase in steelmaking load, the S content is usually 0.0005% or more.

〔Ｚｎ−Ａｌ−Ｍｇ系被覆層〕
上記の化学組成を有する素材鋼板の表面には、Ｚｎ−Ａｌ−Ｍｇ系被覆層を有している必要がある。その被覆層は、溶融Ｚｎ−Ａｌ−Ｍｇ系めっきにより形成されためっき層に由来するものであり、本明細書ではこれを「Ｚｎ−Ａｌ−Ｍｇ系被覆層」と呼んでいる。Ｚｎ−Ａｌ−Ｍｇ系被覆層は、後述するように、クラックが導入された後にベーキング処理を受けたものである。従って、ベーキング処理後のＺｎ−Ａｌ−Ｍｇ系被覆層はクラックを有している。Ｚｎ−Ａｌ−Ｍｇ系被覆層の表面を例えばＳＥＭ（走査型電子顕微鏡）で観察すると、１ｍｍ２当たりに存在するクラックの総延長は例えば３.０〜８.０ｍｍである。このクラックは素材鋼板からの水素の放出に寄与したものであるが、上記の程度の総延長を有するクラックが残存していても、それによる耐食性の低下は問題にならないことが確認された。溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の優れた耐食性が維持されるかどうかに関しては、ベーキング処理での温度が大きく影響する。本発明に従う高強度表面被覆鋼板は、後述のように高温でのベーキングを避けて製造されるので、ＪＩＳ Ｚ２３７１：２０１５に従う中性塩水噴霧試験（塩濃度：５０ｇ／Ｌ、温度：３５℃、試験片の裏面および端面シール：あり）により赤錆が発生するまでの時間が７０００時間以上という、優れた耐食性を呈する。ベーキング処理を水蒸気雰囲気中で行うことによって形成される黒色のＺｎ−Ａｌ−Ｍｇ系被覆層を有する場合でも、同様の優れた耐食性を呈する。 [Zn-Al-Mg-based coating layer]
It is necessary to have a Zn—Al—Mg coating layer on the surface of the material steel plate having the above chemical composition. The coating layer is derived from a plating layer formed by hot-melt Zn—Al—Mg-based plating, and is referred to as “Zn—Al—Mg-based coating layer” in this specification. As will be described later, the Zn—Al—Mg coating layer is subjected to a baking treatment after the cracks are introduced. Therefore, the Zn—Al—Mg-based coating layer after the baking treatment has cracks. When the surface of the Zn—Al—Mg-based coating layer is observed with, for example, an SEM (scanning electron microscope), the total extension of cracks existing per 1 mm 2 is, for example, 3.0 to 8.0 mm. This crack contributed to the release of hydrogen from the steel sheet, but it was confirmed that the deterioration of the corrosion resistance due to the crack having the total extension of the above degree does not become a problem. Whether or not the original excellent corrosion resistance of the molten Zn—Al—Mg plating layer is maintained is greatly affected by the temperature in the baking treatment. Since the high-strength surface-coated steel sheet according to the present invention is manufactured by avoiding baking at a high temperature as described later, a neutral salt spray test (salt concentration: 50 g / L, temperature: 35 ° C., test according to JIS Z2371: 2015) Excellent corrosion resistance of 7000 hours or more until red rust occurs due to the back and end face seals of the piece. Even when a black Zn—Al—Mg-based coating layer is formed by performing the baking treatment in a water vapor atmosphere, the same excellent corrosion resistance is exhibited.

Ｚｎ−Ａｌ−Ｍｇ系被覆層はベーキング処理を経ているが、その化学組成は元の溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層の組成をほぼ維持している。ベーキング処理を水蒸気雰囲気中で行うことによって形成される黒色のＺｎ−Ａｌ−Ｍｇ系被覆層では、Ｚｎの一部が黒色酸化物に変化しているが、この場合も金属元素の組成比で見ると、元の溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層の組成をほぼ維持している。元の溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層として、ここでは耐食性に優れる溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に適用されている組成範囲のめっき層を利用する。具体的には、金属元素の組成比が質量％で、Ａｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部Ｚｎおよび不可避的不純物であるものを対象とする。   The Zn—Al—Mg-based coating layer has undergone a baking treatment, but its chemical composition substantially maintains the composition of the original molten Zn—Al—Mg-based plating layer. In the black Zn—Al—Mg-based coating layer formed by performing the baking process in a water vapor atmosphere, a part of Zn is changed to a black oxide. And the composition of the original molten Zn—Al—Mg-based plating layer is substantially maintained. Here, as the original molten Zn—Al—Mg-based plating layer, a plating layer having a composition range applied to a molten Zn—Al—Mg-based plated steel sheet having excellent corrosion resistance is used. Specifically, the composition ratio of the metal element is mass%, Al: 1.0 to 22.0%, Mg: 1.3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to The target is 0.10%, B: 0 to 0.05%, Fe: 2.0% or less, the balance Zn and inevitable impurities.

Ｚｎ−Ａｌ−Ｍｇ系被覆層の優れた防錆効果を長期にわたって維持するために、Ｚｎ−Ａｌ−Ｍｇ系被覆層の平均厚さは３μｍ以上であることが好ましい。過剰に厚く形成することは不経済であり、また被覆層自体の加工性低下にもつながる。通常、Ｚｎ−Ａｌ−Ｍｇ系被覆層の平均厚さは１００μｍ以下の範囲とすればよい。ここで、当該被覆層の平均厚さは、板厚方向に平行な断面の観察によって求めることができる。   In order to maintain the excellent antirust effect of the Zn—Al—Mg based coating layer over a long period of time, the average thickness of the Zn—Al—Mg based coating layer is preferably 3 μm or more. Forming an excessively thick film is uneconomical and leads to a decrease in workability of the coating layer itself. Usually, the average thickness of the Zn—Al—Mg based coating layer may be in the range of 100 μm or less. Here, the average thickness of the coating layer can be obtained by observing a cross section parallel to the plate thickness direction.

黒色外観を呈するＺｎ−Ａｌ−Ｍｇ系被覆層は、ベーキング処理時に溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層の表面が水蒸気と接触して、被覆層中にＺｎの黒色酸化物が生成することによって形成される。従って、Ｚｎの黒色酸化物はＺｎ−Ａｌ−Ｍｇ系被覆層の上層部に比較的多く分布し、黒色調の表面外観を与える効果を呈する。種々検討の結果、Ｚｎ−Ａｌ−Ｍｇ系被覆層の表面の明度Ｌ＊が６０以下であるＺｎの黒色酸化物が形成されている場合に、変色むらが目立ちにくい意匠性に優れた黒色外観を呈することがわかった。明度Ｌ＊が４０以下となるように調整すると、より深みのある黒色外観を呈するようになる。Ｚｎの黒色酸化物に起因する黒色外観は、鋼中の拡散性水素濃度を０.３０ｐｐｍ以下に低減させるためのベーキング処理条件範囲内で実現できる。   The Zn-Al-Mg-based coating layer exhibiting a black appearance is formed by the surface of the molten Zn-Al-Mg-based plating layer coming into contact with water vapor during the baking process and the formation of a black oxide of Zn in the coating layer. Is done. Accordingly, the black oxide of Zn is distributed in a relatively large amount in the upper layer portion of the Zn—Al—Mg-based coating layer, and exhibits an effect of giving a black-like surface appearance. As a result of various studies, when a black oxide of Zn whose surface brightness L * of the Zn—Al—Mg-based coating layer is 60 or less is formed, a black appearance excellent in design that makes discoloration unevenness less noticeable I found it to be present. When the brightness L * is adjusted to be 40 or less, a deeper black appearance is exhibited. The black appearance due to the black oxide of Zn can be realized within the baking treatment condition range for reducing the diffusible hydrogen concentration in the steel to 0.30 ppm or less.

〔素材鋼板中の拡散性水素濃度〕
水素脆化の要因となる素材鋼板中の水素濃度は、拡散性水素濃度を測定することによって評価することができる。拡散性水素濃度は、大気圧イオン化質量分析装置で、常温から３００℃まで５℃／ｍｉｎの昇温速度で加熱した際に放出される水素量を測定することによって求めることができる。測定試料としては、Ｚｎ−Ａｌ−Ｍｇ系被覆層を研磨紙により除去した素材鋼板のみからなる試料を使用することができる。 [Diffusion hydrogen concentration in the steel sheet]
The hydrogen concentration in the material steel plate that causes hydrogen embrittlement can be evaluated by measuring the diffusible hydrogen concentration. The diffusible hydrogen concentration can be determined by measuring the amount of hydrogen released when heated from room temperature to 300 ° C. at a heating rate of 5 ° C./min with an atmospheric pressure ionization mass spectrometer. As a measurement sample, a sample made of only a raw steel plate from which the Zn—Al—Mg-based coating layer has been removed with abrasive paper can be used.

通常、上述した組成範囲の高張力鋼をめっき原板に用いて連続溶融めっきラインで製造した溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板の場合、ベーキング処理前の素材鋼板中の拡散性水素濃度は０.３５ｐｐｍ以上となる。発明者らの検討によれば、素材鋼板中の拡散性水素濃度をベーキング処理によって０.３０ｐｐｍ以下に低減すると、９８０ＭＰａ級以上の高張力鋼を素材鋼板とする溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板で問題となりやすい水素脆化の現象のみならず、７８０ＭＰａ級あるいは５９０ＭＰａ級の比較的強度レベルの低い高張力鋼を素材鋼板とする溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板でも、水素脆化の現象が顕著に抑制されることがわかった。従って、本発明では素材鋼板中の拡散性水素濃度を０.３０ｐｐｍ以下に規定する。０.２０ｐｐｍ以下であることがより好ましい。   Usually, in the case of a hot-dip Zn-Al-Mg-based plated steel sheet produced by a continuous hot dipping line using the high-strength steel having the composition range described above as a plating original sheet, the diffusible hydrogen concentration in the raw steel sheet before baking is 0. It becomes 35 ppm or more. According to the study by the inventors, when the diffusible hydrogen concentration in the raw steel plate is reduced to 0.30 ppm or less by baking treatment, a hot-rolled Zn-Al-Mg-based plated steel plate using high-tensile steel of 980 MPa class or higher as the raw steel plate. In addition to the phenomenon of hydrogen embrittlement, which is likely to be a problem, the phenomenon of hydrogen embrittlement also occurs in a hot-dip Zn-Al-Mg-based plated steel sheet made of a high strength steel of a relatively low strength level of 780 MPa class or 590 MPa class. It was found that it was significantly suppressed. Therefore, in the present invention, the diffusible hydrogen concentration in the raw steel plate is regulated to 0.30 ppm or less. More preferably, it is 0.20 ppm or less.

〔素材鋼板の金属組織〕
素材鋼板のマトリックス（鋼素地）は、ベイニティックフェライト相からなる組織、またはフェライト相とマルテンサイト相の混合組織であることが望ましい。後者の組織において、マルテンサイト量は１０〜５０体積％であることが好ましい。 [Metal structure of steel plate]
The matrix (steel substrate) of the material steel plate is desirably a structure composed of bainitic ferrite phase or a mixed structure of ferrite phase and martensite phase. In the latter structure, the amount of martensite is preferably 10 to 50% by volume.

〔機械的特性〕
上記のＺｎ−Ａｌ−Ｍｇ系被覆層を形成した自動車部品用黒色表面被覆高強度鋼板の機械的特性は、圧延直角方向の引張試験（ＪＩＳ Ｚ２２４１：２０１１）において、引張強さ５９０〜１１８０ＭＰａ、破断時全伸び１０％以上であることが望ましい。 (Mechanical properties)
The mechanical properties of the black surface-coated high-strength steel sheet for automobile parts on which the above Zn—Al—Mg-based coating layer is formed are as follows. It is desirable that the total elongation is 10% or more.

〔製造方法〕
素材鋼板中の拡散性水素濃度が上記のように低減された自動車部品用高強度表面被覆鋼板は、上記化学組成を有する鋼板をめっき原板に用いて溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を作り、そのめっき鋼板のめっき層にクラックを導入した後に、比較的低温にコントロールされた温度域でベーキング処理を施すことによって製造することができる。 〔Production method〕
A high-strength surface-coated steel sheet for automobile parts in which the diffusible hydrogen concentration in the material steel sheet is reduced as described above is a molten Zn-Al-Mg-based plated steel sheet using a steel sheet having the above chemical composition as a plating base plate, After the crack is introduced into the plating layer of the plated steel sheet, it can be manufactured by baking in a temperature range controlled to a relatively low temperature.

〔溶融めっき〕
従来一般的な手法で溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を製造ればよい。大量生産現場における連続溶融めっきラインを使用することができる。具体的には、溶融めっき直前に施される表面還元処理を兼ねた熱処理は、水素と窒素の混合ガス中で５５０〜９００℃に加熱することによって行う。上記混合ガスに占める水素ガスの割合は２５〜３５体積％とすることが望ましい。材料温度が上記温度範囲にある時間は例えば２０〜２００秒の範囲で調整することが望ましい。このようにして水素と窒素の混合ガス中で素材鋼板を加熱すると、鋼中に水素が侵入する。その水素の鋼中濃度は、後述のベーキング処理によって大幅に低減することができる。素材鋼板の板厚は例えば０.８〜４.５ｍｍである。この熱処理後は、大気に触れることなく、溶融めっき浴中へ浸漬させる。 [Hot plating]
What is necessary is just to manufacture a fusion | melting Zn-Al-Mg type plated steel plate by the conventional general method. Continuous hot dipping lines in mass production sites can be used. Specifically, the heat treatment that also serves as the surface reduction treatment performed immediately before hot dipping is performed by heating to 550 to 900 ° C. in a mixed gas of hydrogen and nitrogen. The proportion of hydrogen gas in the mixed gas is preferably 25 to 35% by volume. The time during which the material temperature is in the above temperature range is desirably adjusted within a range of 20 to 200 seconds, for example. When the material steel plate is heated in a mixed gas of hydrogen and nitrogen in this way, hydrogen enters the steel. The concentration of hydrogen in the steel can be greatly reduced by a baking process described later. The thickness of the material steel plate is, for example, 0.8 to 4.5 mm. After this heat treatment, it is immersed in a hot dipping bath without exposure to the atmosphere.

溶融めっき浴の組成は、質量％でＡｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部がＺｎおよび不可避的不純物とする。得られるめっき鋼板のめっき層組成は、ほぼめっき浴組成を反映したものとなる。めっき浴から引き上げられた鋼板は、ガスワイピング法などでめっき付着量を調整した後、常法により冷却される。めっき付着量は片面当たりのめっき層平均厚さで３〜１００μｍとすることが好ましい。   The composition of the hot dipping bath is Al: 1.0 to 22.0%, Mg: 1.3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to 0.10% by mass%, B: 0 to 0.05%, Fe: 2.0% or less, the balance being Zn and inevitable impurities. The plating layer composition of the obtained plated steel sheet substantially reflects the plating bath composition. The steel sheet pulled up from the plating bath is cooled by a conventional method after adjusting the plating adhesion amount by a gas wiping method or the like. The plating adhesion amount is preferably 3 to 100 μm in terms of the average thickness of the plating layer per side.

〔クラック導入処理〕
ベーキング処理によって溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の優れた耐食性を劣化させないためには、後述のように低温域でベーキング処理を施す必要がある。しかし、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層は、一般的な亜鉛めっき層と比べ、水素放出の障害となりやいことがわかった。そのため、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に低温域でのベーキング処理を施すと、素材鋼板中の水素を安定して所定濃度以下に低減させることが難しい。そこで、ベーキング処理に供するための前処理として、めっき層にクラックを導入しておく。クラックが導入されたＺｎ−Ａｌ−Ｍｇ系被覆層であっても、雨水に曝される環境下や湿潤環境下で使用された際に、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層に特有の腐食生成物による防錆効果が発揮される。 [Crack introduction processing]
In order not to deteriorate the original excellent corrosion resistance of the molten Zn—Al—Mg-based plating layer by the baking treatment, it is necessary to perform the baking treatment in a low temperature region as described later. However, it has been found that the hot-dip Zn—Al—Mg-based plating layer is likely to be an obstacle to hydrogen release compared to a general galvanized layer. For this reason, when the molten Zn—Al—Mg based plated steel sheet is subjected to a baking process at a low temperature range, it is difficult to stably reduce the hydrogen in the raw steel sheet to a predetermined concentration or less. Therefore, cracks are introduced into the plating layer as pretreatment for the baking treatment. Even when a cracked Zn-Al-Mg coating layer is used in an environment exposed to rainwater or in a wet environment, corrosion generation peculiar to a molten Zn-Al-Mg plating layer The rust prevention effect by a thing is demonstrated.

めっき層へのクラックの導入は、テンションレベラーによる曲げ伸ばし変形や、スキンパス圧延によって行うことができる。テンションレベラー装置やスキンパス圧延機での変形を合計で複数回付与してもよい。種々検討の結果、鋼板に合計伸び率０.２〜１.０％の歪を付与することが望ましい。この合計伸び率の範囲で、めっき層表面に１ｍｍ２当たり総延長３.０〜８.０ｍｍ、より好ましくは３.０〜６.０ｍｍのクラックが導入され、後述する低温域でのベーキング処理で素材鋼板中の拡散性水素濃度を０.３０ｐｐｍ以下、より好ましくは０.２０ｐｐｍ以下に低減させることができる。合計伸び率が小さすぎるとクラックの導入量が不足し、低温域でのベーキング処理で水素を十分に放出させる効果が安定して得られない。合計伸び率が過大になると鋼板の延性を損なう要因となる。
合計伸び率ＲＴＯＴＡＬ（％）は下記（１）式により定まる。
ＲＴＯＴＡＬ（％）＝（Ｌ１−Ｌ０）／Ｌ０×１００ …（１）
ここで、Ｌ０は溶融Ｚｎ−Ａｌ−Ｍｇ系めっき終了時点の鋼板における任意の通板方向区間Ｘの通板方向長さ（ｍ）、Ｌ１はベーキング処理開始直前の鋼板における前記通板方向区間Ｘ由来部分の通板方向長さ（ｍ）である。 Cracks can be introduced into the plating layer by bending and stretching with a tension leveler or skin pass rolling. You may give the deformation | transformation in a tension leveler apparatus or a skin pass rolling mill in multiple times in total. As a result of various studies, it is desirable to impart a strain with a total elongation of 0.2 to 1.0% to the steel sheet. Within this total elongation range, cracks with a total extension of 3.0 to 8.0 mm, more preferably 3.0 to 6.0 mm per mm 2 are introduced on the surface of the plating layer, and the material is subjected to baking treatment in a low temperature range described later. The diffusible hydrogen concentration in the steel sheet can be reduced to 0.30 ppm or less, more preferably 0.20 ppm or less. If the total elongation is too small, the amount of cracks introduced is insufficient, and the effect of sufficiently releasing hydrogen by baking at low temperatures cannot be obtained stably. If the total elongation is excessive, it becomes a factor that impairs the ductility of the steel sheet.
The total elongation RTOTAL (%) is determined by the following equation (1).
RTOTAL (%) = (L1-L0) / L0 × 100 (1)
Here, L0 is the length (m) of the plate passing direction in an arbitrary plate passing direction section X in the steel sheet at the end of the molten Zn—Al—Mg based plating, and L1 is the plate passing direction section X in the steel plate immediately before the start of the baking process. It is the length (m) in the plate passing direction of the origin portion.

〔ベーキング処理〕
ベーキング処理は、鋼材中に侵入した水素を外部に放出させることによって、鋼中水素濃度を減少させるための加熱処理である。また、黒色調の表面外観を得る場合には、その黒色化の処理も兼ねている。発明者らは、ベーキング処理の加熱温度（最高到達材温）と耐食性の関係について検討を重ねてきた。その結果、上述した組成の溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層を１５０℃より高い温度に加熱すると、めっき層中の相構造が変化し、耐食性の劣化が顕在化するようになる。一方、ベーキング処理の加熱温度が７０℃を下回ると水素の放出効果を安定して十分に得ることが難しくなる。従って、ベーキング処理は７０〜１５０℃に加熱保持することによって行う。 [Baking treatment]
The baking treatment is a heat treatment for reducing the hydrogen concentration in the steel by releasing hydrogen that has entered the steel to the outside. Moreover, when obtaining the black-like surface appearance, it also serves as the blackening process. The inventors have repeatedly studied the relationship between the heating temperature (maximum material temperature) of the baking treatment and the corrosion resistance. As a result, when a molten Zn—Al—Mg-based plating layer having the above-described composition is heated to a temperature higher than 150 ° C., the phase structure in the plating layer changes, and deterioration of corrosion resistance becomes apparent. On the other hand, if the heating temperature of the baking process is lower than 70 ° C., it is difficult to obtain a sufficient and stable hydrogen release effect. Therefore, the baking process is performed by heating and maintaining at 70 to 150 ° C.

ベーキング処理の時間、すなわち、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を７０〜１５０℃の範囲内に設定した所定温度に保持する時間は、素材鋼板中の拡散性水素濃度を０.３０ｐｐｍ以下、あるいは０.２０ｐｐｍ以下といった目標レベルに低減可能な時間に設定する。溶融めっき条件、ベーキング処理の雰囲気ガス条件、ベーキング処理温度に応じて、予め予備実験を行うことにより、適正処理時間を定めればよい。通常、１〜５０時間の範囲で良好な結果が得られる処理時間を設定することができる。２〜３６時間の範囲とすることがより好ましい。   The time for the baking treatment, that is, the time for maintaining the molten Zn—Al—Mg-based plated steel sheet at a predetermined temperature set in the range of 70 to 150 ° C. is such that the diffusible hydrogen concentration in the raw steel sheet is 0.30 ppm or less The time that can be reduced to the target level such as 0.20 ppm or less is set. An appropriate processing time may be determined by conducting preliminary experiments in advance in accordance with the hot dip plating conditions, the atmospheric gas conditions of the baking process, and the baking process temperature. Usually, the processing time in which a favorable result is obtained in the range of 1 to 50 hours can be set. More preferably, it is in the range of 2 to 36 hours.

ベーキング処理の加熱雰囲気については、黒色調の表面外観を得る場合は水蒸気雰囲気とする必要があるが、それ以外の場合は、大気、真空、不活性ガスのいずれの雰囲気であってもよい。水蒸気雰囲気下で黒色化を行う場合は、水蒸気雰囲気中における不純物ガス成分（水蒸気以外のガス成分）の含有量を５体積％以下とすることが望ましい。   The heating atmosphere of the baking treatment needs to be a water vapor atmosphere in order to obtain a black-like surface appearance, but in other cases, it may be any atmosphere of air, vacuum, or inert gas. When blackening is performed in a water vapor atmosphere, the content of impurity gas components (gas components other than water vapor) in the water vapor atmosphere is preferably 5% by volume or less.

溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層を上記温度の水蒸気に接触させると、めっき層中のＺｎが優先的に酸化して黒色のＺｎ酸化物が形成され、明度Ｌ＊が６０以下である意匠性の高い黒色調の表面外観を得ることができる。水蒸気の分圧については、相対湿度（その温度における飽和水蒸気圧に対する、実際に雰囲気中に存在する水蒸気の分圧）が７０〜１００％となるように調整すればよい。相対湿度が７０％を下回るとＺｎの黒色酸化物の生成速度が遅く、鋼中水素の放出が十分達成される時間では着色むらが生じやすい。   When the molten Zn—Al—Mg-based plating layer is brought into contact with water vapor at the above temperature, Zn in the plating layer is preferentially oxidized to form a black Zn oxide, and the lightness L * is 60 or less. High black tone surface appearance can be obtained. The partial pressure of water vapor may be adjusted so that the relative humidity (the partial pressure of water vapor actually present in the atmosphere with respect to the saturated water vapor pressure at that temperature) is 70 to 100%. When the relative humidity is less than 70%, the formation rate of the black oxide of Zn is slow, and uneven coloring tends to occur in the time when the release of hydrogen in the steel is sufficiently achieved.

ベーキング処理を大気雰囲気で行う場合は、連続焼鈍炉を通板させる手法を適用することができる。また、鋼板をコイル状に巻いた状態でベーキング処理に供する場合は、例えばベル型バッチ焼鈍炉を利用することができる。この場合、大気以外の所定雰囲気下で処理することが可能となる。   In the case where the baking process is performed in an air atmosphere, a technique of passing through a continuous annealing furnace can be applied. Moreover, when using for a baking process in the state which wound the steel plate in the coil shape, a bell type batch annealing furnace can be utilized, for example. In this case, the treatment can be performed in a predetermined atmosphere other than the atmosphere.

水蒸気雰囲気で黒色化を行う場合は、大気から遮断された炉内で行う。密閉性の高い容器を炉体に用いることが望ましい。炉内に溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を収容する際、めっき層表面が雰囲気ガスと接触するように配慮する。窒素置換や真空引きなどによって炉内の空気を排除し、その後、水蒸気を導入して、炉内雰囲気を水蒸気雰囲気とし、所定の温度まで昇温し、その温度で保持することによりベーキング処理を行う。ベーキング処理中も所定のガス組成が維持されるように炉内雰囲気を管理する。   When blackening is performed in a steam atmosphere, it is performed in a furnace cut off from the atmosphere. It is desirable to use a highly airtight container for the furnace body. When accommodating the molten Zn—Al—Mg-based plated steel sheet in the furnace, consideration is given so that the surface of the plating layer comes into contact with the atmospheric gas. Exclude air in the furnace by nitrogen replacement or evacuation, and then introduce water vapor to make the atmosphere in the furnace a water vapor atmosphere, raise the temperature to a predetermined temperature, and perform the baking process by holding at that temperature . The furnace atmosphere is managed so that a predetermined gas composition is maintained even during the baking process.

〔無機系皮膜の形成〕
上記のベーキング処理によって改質されたＺｎ−Ａｌ−Ｍｇ系被覆層の表面上に、無機系皮膜を形成させることができる。無機系皮膜としては溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に従来から適用されている公知のものが種々適用可能である。なかでも、バルブメタルの酸化物、バルブメタルの酸素酸塩、バルブメタルの水酸化物、バルブメタルのリン酸塩およびバルブメタルのフッ化物からなる群から選ばれる１種類または２種類以上の化合物（以下「バルブメタル化合物」ともいう）を含むものが好適な対象として挙げられる。バルブメタルとしては、Ｔｉ、Ｚｒ、Ｈｆ、Ｖ、Ｎｂ、Ｔａ、Ｗ、Ｓｉ、Ａｌなどが例示できる。上記バルブメタル化合物は、これらのバルブメタルの１種以上を含有するものを適用することが望ましい。無機系皮膜は、公知の方法で形成させることができる。例えば、バルブメタル化合物などを含有する無機系塗料を、Ｚｎ−Ａｌ−Ｍｇ系被覆層の表面上にロールコート法、スピンコート法、スプレー法などで塗布する方法が採用できる。 [Formation of inorganic film]
An inorganic coating can be formed on the surface of the Zn—Al—Mg coating layer modified by the baking treatment. As the inorganic coating, various known coatings conventionally applied to hot-dip Zn—Al—Mg plated steel sheets can be applied. Among them, one or more compounds selected from the group consisting of valve metal oxides, valve metal oxyacid salts, valve metal hydroxides, valve metal phosphates and valve metal fluorides ( Those containing a “valve metal compound”) are also suitable objects. Examples of the valve metal include Ti, Zr, Hf, V, Nb, Ta, W, Si, and Al. It is desirable to apply the valve metal compound containing at least one of these valve metals. The inorganic film can be formed by a known method. For example, a method of applying an inorganic coating material containing a valve metal compound or the like on the surface of the Zn—Al—Mg coating layer by a roll coating method, a spin coating method, a spray method or the like can be employed.

〔有機系皮膜の形成〕
上記のベーキング処理によって改質されたＺｎ−Ａｌ−Ｍｇ系被覆層の表面上に、有機系皮膜を形成させることもできる。有機系樹脂皮膜も、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板に従来から適用されている公知のものが種々適用可能である。例えば、ウレタン系樹脂、エポキシ系樹脂、オレフィン系樹脂、スチレン系樹脂、ポリエステル系樹脂、アクリル系樹脂、フッ素系樹脂、またはこれらの樹脂の組み合わせ、あるいはこれらの樹脂の共重合体または変性物などを含有する皮膜が挙げられる。有機系皮膜も、公知の方法で形成させることができる。例えば、上記の樹脂成分を含有する有機系塗料を、Ｚｎ−Ａｌ−Ｍｇ系被覆層の表面上にロールコート法、スピンコート法、スプレー法などで塗布する方法が採用できる。 [Formation of organic film]
An organic coating can also be formed on the surface of the Zn—Al—Mg coating layer modified by the baking process. Various known organic resin coatings conventionally applied to hot-dip Zn—Al—Mg-based plated steel sheets can also be applied. For example, urethane resins, epoxy resins, olefin resins, styrene resins, polyester resins, acrylic resins, fluorine resins, combinations of these resins, copolymers or modified products of these resins, etc. The film to contain is mentioned. The organic film can also be formed by a known method. For example, a method of applying the organic paint containing the resin component to the surface of the Zn—Al—Mg coating layer by a roll coating method, a spin coating method, a spray method, or the like can be employed.

表１に示す化学組成の鋳造スラブを１２５０℃に加熱した後、熱間圧延して、熱延めっき原板用または冷延めっき原板用の熱延鋼板とした。熱延条件は、熱延めっき原板用では仕上圧延温度８８０℃、巻取温度６００℃、板厚３.２ｍｍとし、冷延めっき原板用では仕上圧延温度８８０℃、巻取温度４６０℃、板厚２ｍｍとした。ここで、仕上圧延温度は熱間圧延最終パス直後の板表面温度によって表される。熱延めっき原板用の熱延鋼板は、酸洗を施してそのまま熱延めっき原板とした。冷延めっき原板用の熱延鋼板は、酸洗を施したのち、表２中に示す冷間圧延率で冷間圧延を施し、冷延めっき原板とした。
なお、表１に示す鋼はいずれも本発明で規定する化学組成を満たす「発明対象鋼」である。また、表２の冷間圧延率０％のものが熱延めっき原板を使用した例である。 A cast slab having a chemical composition shown in Table 1 was heated to 1250 ° C., and then hot-rolled to obtain a hot-rolled steel sheet for a hot-rolled plated original sheet or a cold-rolled plated original sheet. The hot rolling conditions are a finish rolling temperature of 880 ° C., a coiling temperature of 600 ° C., and a sheet thickness of 3.2 mm for a hot rolled plate, and a finish rolling temperature of 880 ° C., a coiling temperature of 460 ° C. It was 2 mm. Here, the finish rolling temperature is represented by the plate surface temperature immediately after the final hot rolling pass. The hot-rolled steel sheet for the hot-rolled plating sheet was pickled and used as the hot-rolled sheet. The hot-rolled steel sheet for cold-rolled plating sheet was pickled and then cold-rolled at the cold rolling rate shown in Table 2 to obtain a cold-rolled sheet sheet.
In addition, all the steels shown in Table 1 are “invention steels” that satisfy the chemical composition defined in the present invention. Moreover, the thing of the cold rolling rate 0% of Table 2 is an example which used the hot-rolling plating original plate.

（溶融めっき工程）
各めっき原板を用いて、連続溶融めっきラインにて溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を製造した。めっき原板（素材鋼板）を水素と窒素の混合ガス中で加熱して焼鈍したのち、大気に接触させることなく、溶融めっき浴に浸漬させ、その後めっき浴から引き上げてガスワイピング法でめっき付着量を調整し、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板を得た。めっき浴組成は、質量％で、Ａｌ：６.０％、Ｍｇ：３.０％、Ｓｉ：０.０１％、Ｔｉ：０.００２％、Ｂ：０.０００５％、Ｆｅ：０.１％、残部Ｚｎとした。上記の焼鈍における雰囲気および温度は表２中に記載してある。めっき付着量は、鋼板片面当たりのめっき層厚さが１０μｍとなるように調整した。 (Hot plating process)
Using each plating original plate, a hot-dip Zn—Al—Mg-based plated steel plate was produced in a continuous hot dipping line. After heating and annealing the plating original plate (material steel plate) in a mixed gas of hydrogen and nitrogen, it is immersed in a hot dipping bath without contacting it with the atmosphere, and then pulled up from the plating bath to increase the amount of coating by gas wiping. It adjusted and obtained the hot-dip Zn-Al-Mg system plating steel plate. The plating bath composition is mass%, Al: 6.0%, Mg: 3.0%, Si: 0.01%, Ti: 0.002%, B: 0.0005%, Fe: 0.1% The balance was Zn. The atmosphere and temperature in the above annealing are described in Table 2. The plating adhesion amount was adjusted so that the plating layer thickness per one surface of the steel sheet was 10 μm.

（クラック導入工程）
使用した連続溶融めっきラインは、めっき装置より後段（通板方向の下流側）に、テンションレベラー（Ｔ.Ｌｖ）と、スキンパス圧延機（ＳＫＰ）を備えている。溶融めっきを終えた鋼帯に、
（i）テンションレベラーやスキンパス圧延機による伸び変形を全く加えていない部分、
（ii）テンションレベラーおよびスキンパス圧延機のいずれか一方あるいは両方を使用して合計伸び率０.２〜１.０％の伸び変形を加えた部分、
（iii）テンションレベラーおよびスキンパス圧延機の両方を使用して合計伸び率１.２％の伸び変形を加えた部分、
をそれぞれ形成した。 (Crack introduction process)
The continuous hot dipping line used is equipped with a tension leveler (T.Lv) and a skin pass rolling mill (SKP) at a stage subsequent to the plating apparatus (downstream in the sheet passing direction). To the steel strip after hot dipping,
(I) A portion where no elongation deformation by a tension leveler or a skin pass rolling mill is applied.
(Ii) A portion subjected to elongation deformation with a total elongation of 0.2 to 1.0% using one or both of a tension leveler and a skin pass rolling mill,
(Iii) A portion subjected to elongation deformation with a total elongation of 1.2% using both a tension leveler and a skin pass rolling mill,
Formed respectively.

得られた溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板のコイルから、上記各（i）〜（iii）の部分のめっき鋼板を採取し、圧延方向および板厚方向に平行な断面（Ｌ断面）の金属組織を光学顕微鏡で調べた。また、圧延直角方向の引張試験片（ＪＩＳ ５号）を作製し、ＪＩＳ Ｚ２２４１：２０１１に規定の引張試験を行って引張強さＴＳ（ＭＰａ）、破断時全伸びＴ.Ｅｌ（％）を求めた。さらに、上記（ii）および（iii）の部分のめっき鋼板について、被覆層（めっき層）の表面をＳＥＭにより倍率５００倍で１０視野観察して、被覆層表面に形成されたクラックの長さを測定し、面積１ｍｍ２当たりのクラックの総延長（ｍｍ）を求めた。参考のため、図１に表２のめっき鋼板Ｅ−２（クラック導入工程での合計伸び率０.２％、被覆層１ｍｍ２当たりのクラック総延長３.２ｍｍ）、図２に表２のめっき鋼板Ｈ−２（クラック導入工程での合計伸び率１.０％、被覆層１ｍｍ２当たりのクラック総延長６.８ｍｍ）について、それぞれ被覆層表面のＳＥＭ写真を示す。図１、図２とも、（ａ）はＳＥＭ画像の一例、（ｂ）はそれらのＳＥＭ画像上に、クラック導入工程で導入されたクラックであることが明らかである部分を黒のラインで表示したものである。このクラックは、後述のベーキング処理後にほぼそのまま残存することが確かめられている。各めっき鋼板における面積１ｍｍ２当たりのクラックの総延長は、クラック導入工程で導入されたクラックであることが明らかである部分の総延長を測定して定めた。表２に、これらの結果を示す。   From the obtained coil of the molten Zn-Al-Mg-based plated steel sheet, the plated steel sheets of the parts (i) to (iii) are collected, and a metal having a cross section (L cross section) parallel to the rolling direction and the plate thickness direction. The tissue was examined with a light microscope. In addition, a tensile test piece (JIS No. 5) in the direction perpendicular to the rolling direction was prepared, and the tensile test specified in JIS Z2241: 2011 was performed to obtain the tensile strength TS (MPa) and the total elongation at break T.El (%). It was. Further, with respect to the plated steel sheets of the above parts (ii) and (iii), the surface of the coating layer (plating layer) was observed with 10 fields of view at 500 times magnification by SEM, and the length of cracks formed on the surface of the coating layer was determined. The total extension (mm) of cracks per area of 1 mm 2 was measured. For reference, FIG. 1 shows a plated steel sheet E-2 shown in Table 2 (total elongation 0.2% in the crack introduction process, total crack extension 3.2 mm per 1 mm 2 coating layer), and FIG. 2 shows a plated steel sheet shown in Table 2. SEM photographs of the surface of the coating layer are shown for H-2 (total elongation of 1.0% in the crack introduction step, total crack extension of 6.8 mm per 1 mm2 of coating layer). 1 and 2, (a) is an example of an SEM image, and (b) is a black line on the SEM image, which is clearly a crack introduced in the crack introduction process. Is. It has been confirmed that this crack remains almost as it is after the baking process described later. The total extension of cracks per area of 1 mm 2 in each plated steel sheet was determined by measuring the total extension of the portions that are clearly cracks introduced in the crack introduction step. Table 2 shows these results.

表２に見られるように、クラック導入工程で合計伸び率が０.２％以上の伸び変形を付与することによって、被覆層（めっき層）に１ｍｍ２当たり総延長３.０ｍｍ以上のクラックを導入することができる。また、合計伸び率１.２％の伸び変形を付与した場合には、合計伸び率０.２〜１.０％の場合に比べ、破断時全伸びＴ.Ｅｌが低くなり、鋼板の延性低下が生じている。鋼板の加工性を重視する場合にはクラック導入工程での合計伸び率を１.０％以下の範囲で設定することが望ましい。   As seen in Table 2, cracks having a total elongation of 3.0 mm or more per 1 mm 2 are introduced into the coating layer (plating layer) by imparting an elongation deformation with a total elongation of 0.2% or more in the crack introduction step. be able to. In addition, when elongation deformation having a total elongation of 1.2% is applied, the total elongation at break T.E1 is lower than in the case of a total elongation of 0.2 to 1.0%, and the ductility of the steel sheet is lowered. Has occurred. When emphasizing the workability of the steel sheet, it is desirable to set the total elongation in the crack introduction process within a range of 1.0% or less.

（ベーキング処理工程）
次に、上記（i）の部分（クラック導入なし）および（ii）の部分（クラック導入あり）のめっき鋼板を用いて、ベーキング処理の効果を調べた。ベーキング処理条件は表３〜５に掲載してある。（i）のめっき鋼板については大気雰囲気（表３）、（ii）のめっき鋼板については大気雰囲気（表４）および水蒸気雰囲気（表５）にてベーキング処理を施した。このうち、水蒸気雰囲気でのベーキング処理は以下のようにして行った。すなわち、クラック導入工程を終えためっき鋼板を加熱炉内に入れ、めっき層表面が雰囲気ガスに接触するように置いた。その後、炉内を密閉し、真空ポンプにて真空引き後、ガス導入管から水蒸気を導入し、相対湿度が１００％となるように炉内圧力をコントロールしながら炉内温度を所定のベーキング処理温度まで昇温し、その温度で所定時間の保持を行ったのち降温し、炉内を大気に開放した。ベーキング処理中の雰囲気ガスは、水蒸気１００体積％、相対湿度１００％とした（表５の各例共通）。 (Baking process)
Next, the effect of the baking treatment was examined using the plated steel sheet of the part (i) (without crack introduction) and the part (ii) (with crack introduction). Baking conditions are listed in Tables 3-5. The plated steel sheet (i) was baked in an air atmosphere (Table 3), and the plated steel sheet (ii) was baked in an air atmosphere (Table 4) and a steam atmosphere (Table 5). Among these, the baking process in water vapor | steam atmosphere was performed as follows. That is, the plated steel sheet after the crack introduction process was placed in a heating furnace and placed so that the surface of the plating layer was in contact with the atmospheric gas. Then, the inside of the furnace is sealed, evacuated with a vacuum pump, steam is introduced from the gas introduction pipe, and the furnace temperature is controlled to a predetermined baking temperature while controlling the furnace pressure so that the relative humidity becomes 100%. The temperature was raised to 1, and kept at that temperature for a predetermined time, then the temperature was lowered, and the inside of the furnace was opened to the atmosphere. The atmosphere gas during the baking treatment was 100% by volume of water vapor and 100% of relative humidity (common to each example in Table 5).

ベーキング処理後の鋼板からサンプルを採取し、素材鋼板中の拡散性水素濃度および塩水噴霧試験による赤錆発生時間を測定した。さらに、水蒸気雰囲気でベーキング処理を行ったもの（表５に記載のもの）についてはＺｎ−Ａｌ−Ｍｇ系被覆層表面の明度Ｌ＊を測定した。試験方法は以下の通りである。   A sample was taken from the steel plate after the baking treatment, and the diffusible hydrogen concentration in the raw steel plate and the red rust occurrence time by a salt spray test were measured. Furthermore, the lightness L * of the Zn—Al—Mg-based coating layer surface was measured for those subjected to the baking treatment in a steam atmosphere (shown in Table 5). The test method is as follows.

（拡散性水素濃度の測定）
鋼板サンプル表層のＺｎ−Ａｌ−Ｍｇ系被覆層を研磨紙で除去することによって、素材鋼板のみからなる試料を作製した。拡散性水素濃度の測定条件を以下に示す。
・試料加熱部：赤外線ゴールドイメージ炉（アルバック理工社製 ＲＨＬ−Ｅ４１０Ｐ）
・分析計：ＡＰＳ−ＭＳ／大気圧イオン化質量分析装置（日本エイピーアイ社製 ＦＬＥＸ−ＭＳ４００）
・分析試料：１０ｍｍ×３ｍｍ寸法に切断したもの３枚を分析
・測定温度：常温〜３００℃
・昇温速度：５℃／ｍｉｎ
・測定雰囲気：Ａｒ（１０００ｍＬ／ｍｉｎ） (Measurement of diffusible hydrogen concentration)
By removing the Zn—Al—Mg-based coating layer on the surface layer of the steel plate sample with abrasive paper, a sample consisting only of the raw steel plate was produced. The measurement conditions for the diffusible hydrogen concentration are shown below.
Sample heating unit: Infrared gold image furnace (RHL-E410P manufactured by ULVAC-RIKO)
Analyzer: APS-MS / atmospheric pressure ionization mass spectrometer (FLEX-MS400 manufactured by Japan API Corporation)
・ Analytical sample: Analyzed three pieces cut into 10 mm × 3 mm dimensions.
・ Raising rate: 5 ° C / min
Measurement atmosphere: Ar (1000 mL / min)

（塩水噴霧試験での赤錆発生時間の測定）
ＪＩＳ Ｚ２３７１：２０１５に従う中性塩水噴霧試験（塩濃度：５０ｇ／Ｌ、温度：３５℃、試験片の裏面および端面シール：あり）を行い、塩水噴霧試験開始から４０００時間経過後は１００時間毎に噴霧を停止して試験片表面の赤錆発生の有無を目視にて観察した。赤錆の発生が最初に認められた塩水噴霧累積時間をその試料の赤錆発生時間とした。ここでは１００時間毎に観察を行ったので、例えば、赤錆発生時間が７１００時間である試料は少なくとも「赤錆発生までの時間が７０００時間以上」という耐食性を満たしていると評価できる。 (Measurement of red rust occurrence time in salt spray test)
A neutral salt spray test according to JIS Z2371: 2015 (salt concentration: 50 g / L, temperature: 35 ° C., back and end face seals of test piece: yes), every 4000 hours after the start of the salt spray test Spraying was stopped and the presence or absence of red rust on the surface of the test piece was visually observed. The accumulated salt spray time at which red rust was first observed was taken as the red rust generation time for the sample. Here, since observation was performed every 100 hours, for example, it can be evaluated that a sample having a red rust occurrence time of 7100 hours satisfies at least the corrosion resistance of “the time until red rust occurrence is 7000 hours or more”.

（明度Ｌ＊値の測定）
分光型色差計（有限会社東京電色製；ＴＣ−１８００）を用いて、ＪＩＳ Ｋ５６００に準拠した分光反射測定法で明度Ｌ＊値を測定した。測定条件を以下に示す。
・光学条件：ｄ／８°法（ダブルビーム光学系）
・視野：２度視野
・測定方法：反射光測定
・標準光：Ｃ
・表色系：ＣＩＥＬＡＢ
・測定波長：３８０〜７８０ｎｍ
・測定波長間隔：５ｎｍ
・分光器：回折格子 １２００／ｍｍ
・照明：ハロゲンランプ（電圧１２Ｖ、電力５０Ｗ、定格寿命２０００時間）
・測定面積：７.２５ｍｍφ
・検出素子：光電子増倍管（Ｒ９２８；浜松ホトニクス株式会社）
・反射率：０−１５０％
・測定温度：２３℃
・標準板：白色
これらの結果を表３、表４、表５に示す。 (Measurement of lightness L * value)
Using a spectroscopic color difference meter (manufactured by Tokyo Denshoku Co., Ltd .; TC-1800), the lightness L * value was measured by a spectral reflection measurement method based on JIS K5600. The measurement conditions are shown below.
・ Optical conditions: d / 8 ° method (double beam optical system)
-Field of view: 2 degree field of view-Measuring method: Reflected light measurement-Standard light: C
-Color system: CIELAB
・ Measurement wavelength: 380 to 780 nm
・ Measurement wavelength interval: 5 nm
-Spectroscope: diffraction grating 1200 / mm
・ Lighting: Halogen lamp (voltage 12V, power 50W, rated life 2000 hours)
・ Measurement area: 7.25mmφ
-Detection element: Photomultiplier tube (R928; Hamamatsu Photonics Co., Ltd.)
-Reflectance: 0-150%
・ Measurement temperature: 23 ℃
Standard plate: white These results are shown in Table 3, Table 4, and Table 5.

めっき層にクラックを導入せずにベーキング処理を施した場合（表３）、ベーキング処理温度を１５０℃より高温で行った例（試料Ｎｏ.１７、１８、２４）を除き、素材鋼板中の拡散性水素濃度を０.３０ｐｐｍ以下に低減することはできなかった。ただし、高温でベーキング処理を行った上記の例では、塩水噴霧試験での赤錆発生までの時間が７０００時間未満であり、ベーキング処理による耐食性低下が生じた。クラック導入工程を適用しない場合は、素材鋼板中の拡散性水素濃度の顕著な低減と、溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層本来の耐食性を安定して両立させることは困難である。   Diffusion in the raw steel plate, except for cases where the baking treatment temperature was higher than 150 ° C. (sample Nos. 17, 18, and 24) when baking treatment was performed without introducing cracks in the plating layer (Table 3). The neutral hydrogen concentration could not be reduced to 0.30 ppm or less. However, in the above example where the baking treatment was performed at a high temperature, the time until the occurrence of red rust in the salt spray test was less than 7000 hours, and the corrosion resistance decreased due to the baking treatment. When the crack introduction process is not applied, it is difficult to stably achieve both a remarkable reduction of the diffusible hydrogen concentration in the raw steel sheet and the original corrosion resistance of the molten Zn—Al—Mg-based plating layer.

めっき層にクラックを導入した後にベーキング処理を施した場合（表４、表５）、ベーキング処理温度が１５０℃以下であっても、素材鋼板中の拡散性水素濃度を安定して０.３０ｐｐｍ以下に低減することが可能であった。これらはいずれも塩水噴霧試験での赤錆発生までの時間が７０００時間以上であり、ベーキング処理後の被覆層は通常の溶融Ｚｎ−Ａｌ−Ｍｇ系めっき層と同様に優れた防錆効果を呈することが確認された。ただし、試験Ｎｏ.３９、６９はベーキング処理温度が５０℃と低すぎたので、拡散性水素濃度の低減効果が不十分であった。ベーキング処理温度を１５０℃より高温に設定した例（試料Ｎｏ.４７、４８、５４、７７、７８、８４）では、耐食性低下が認められた。表３と、表４との対比から、被覆層におけるクラックの有無によって、耐食性（防錆性能）に差は認められなかった。水蒸気雰囲気でのベーキング処理を行ったものでは、ベーキング処理温度が５０℃と低すぎた例（試料Ｎｏ.６９）を除き、明度Ｌ＊が６０以下の黒色調の外観が得られ、明度Ｌ＊が４０以下の深みのある黒色外観に調整することも可能であることが確認された。   When the baking treatment is performed after introducing cracks in the plating layer (Tables 4 and 5), the diffusible hydrogen concentration in the material steel plate is stably 0.30 ppm or less even when the baking treatment temperature is 150 ° C. or less. It was possible to reduce it. All of these have a time of 7000 hours or more until the occurrence of red rust in the salt spray test, and the coating layer after the baking treatment should exhibit an excellent rust prevention effect in the same manner as a normal molten Zn-Al-Mg plating layer. Was confirmed. However, in Test Nos. 39 and 69, since the baking temperature was too low at 50 ° C., the effect of reducing the diffusible hydrogen concentration was insufficient. In the examples (sample Nos. 47, 48, 54, 77, 78, 84) in which the baking temperature was set higher than 150 ° C., a decrease in corrosion resistance was observed. From the comparison between Table 3 and Table 4, there was no difference in corrosion resistance (rust prevention performance) depending on the presence or absence of cracks in the coating layer. In the case where the baking treatment was performed in a steam atmosphere, a blackish appearance having a lightness L * of 60 or less was obtained except for the case where the baking treatment temperature was too low (50 ° C.) (Sample No. 69). It was confirmed that it was possible to adjust to a black appearance with a depth of 40 or less.

（曲げ試験）
次に、鋼Ｎｏ.Ｄのめっき鋼板（板厚１.０ｍｍ）を用いて、曲げ加工性に及ぼす素材鋼板中の拡散性水素濃度の影響を調べた実験例を示す。表３〜５に記載した試料Ｎｏ.１０、４０、７０のＺｎ−Ａｌ−Ｍｇ系被覆鋼板サンプルに、ＪＩＳ Ｚ２２４８：２００６のＶブロック法に従い、４５°の押金具を用いて、曲げ軸が試料の圧延方向に対して平行となるように常温での１３５°Ｖ曲げ試験を施した。先端の曲率半径が異なる種々の押金具を使用してＶ曲げ試験を行い、試験後の曲げ加工部表面を目視で観察し、割れが発生しない最小曲げ半径ＭＢＲ（ｍｍ）を求めた。結果を表６に示す。 (Bending test)
Next, an experimental example in which the influence of the diffusible hydrogen concentration in the material steel plate on the bending workability is shown using a steel No. D plated steel plate (plate thickness: 1.0 mm). According to the V-block method of JIS Z2248: 2006, the bending axis was set to the sample according to JIS Z2248: 2006 for the sample Nos. 10, 40 and 70 of the sample Nos. 10, 40 and 70 described in Tables 3 to 5. A 135 ° V bending test at normal temperature was performed so as to be parallel to the rolling direction. A V-bending test was performed using various metal fittings having different curvature radii at the tip, and the surface of the bent portion after the test was visually observed to obtain a minimum bending radius MBR (mm) at which no cracks occurred. The results are shown in Table 6.

素材鋼板中の拡散性水素濃度を低減した本発明例では、比較例に対し、曲げ加工性が顕著に向上している。被覆層にクラックを導入した後にベーキング処理を施す手法により、水素脆化を解消して加工性を顕著に向上させ、実際の自動車部品への加工が可能となる。   In the present invention example in which the diffusible hydrogen concentration in the raw steel plate is reduced, the bending workability is remarkably improved as compared with the comparative example. By introducing a crack after the crack is introduced into the coating layer, the hydrogen embrittlement is eliminated and the workability is remarkably improved, and the actual automobile part can be processed.

Claims (4)

質量％で、Ｃ：０.０１〜０.２０％、Ｓｉ：０.０１〜０.５０％、Ｍｎ：０.１０〜２.５０％、Ｐ：０.００５〜０.０５０％、Ｂ：０.０００５〜０.０１０％、Ｔｉ：０.０１〜０.２０％、Ｎｂ：０〜０.１０％、Ｍｏ：０〜０.５０％、Ｃｒ：０〜０.５０％、Ａｌ：０.０１〜０.１０％、残部Ｆｅおよび不可避的不純物である鋼組成の素材鋼板の表面に、金属元素の組成比が質量％で、Ａｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部Ｚｎおよび不可避的不純物であるＺｎ−Ａｌ−Ｍｇ系被覆層を有する表面被覆鋼板であって、前記素材鋼板中の拡散性水素濃度が０.３０ｐｐｍ以下であり、ＪＩＳ Ｚ２３７１：２０１５に従う中性塩水噴霧試験（塩濃度：５０ｇ／Ｌ、温度：３５℃、試験片の裏面および端面シール：あり）による赤錆発生までの時間が７０００時間以上である、自動車部品用高強度表面被覆鋼板。   By mass%, C: 0.01 to 0.20%, Si: 0.01 to 0.50%, Mn: 0.10 to 2.50%, P: 0.005 to 0.050%, B: 0.0005 to 0.010%, Ti: 0.01 to 0.20%, Nb: 0 to 0.10%, Mo: 0 to 0.50%, Cr: 0 to 0.50%, Al: 0 0.01% to 0.10%, balance Fe and inevitable impurities steel composition material steel plate surface, the composition ratio of metal elements is mass%, Al: 1.0-22.0%, Mg: 1. 3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to 0.10%, B: 0 to 0.05%, Fe: 2.0% or less, remaining Zn and inevitable impurities A surface-coated steel sheet having a Zn—Al—Mg-based coating layer, wherein the diffusible hydrogen concentration in the material steel sheet is 0.30 ppm or less, and a neutral salt spray test according to JIS Z2371: 2015 (salt concentration) : High-strength surface-coated steel sheet for automobile parts, in which the time until red rust is generated by 50 g / L, temperature: 35 ° C., and the back and end face seals of the test piece is 7000 hours or more. 圧延方向の引張強さが５９０ＭＰａ以上である請求項１に記載の自動車部品用高強度表面被覆鋼板。   The high-strength surface-coated steel sheet for automobile parts according to claim 1, wherein the tensile strength in the rolling direction is 590 MPa or more. 素材鋼板が、質量％で、Ｃ：０.０１〜０.２０％、Ｓｉ：０.０１〜０.５０％、Ｍｎ：０.１０〜２.５０％、Ｐ：０.００５〜０.０５０％、Ｂ：０.０００５〜０.０１０％、Ｔｉ：０.０１〜０.２０％、Ｎｂ：０〜０.１０％、Ｍｏ：０〜０.５０％、Ｃｒ：０〜０.５０％、Ａｌ：０.０１〜０.１０％、残部Ｆｅおよび不可避的不純物である鋼組成の素材鋼板の表面に、金属元素の組成比が質量％で、Ａｌ：１.０〜２２.０％、Ｍｇ：１.３〜１０.０％、Ｓｉ：０〜２.０％、Ｔｉ：０〜０.１０％、Ｂ：０〜０.０５％、Ｆｅ：２.０％以下、残部Ｚｎおよび不可避的不純物であるＺｎ−Ａｌ−Ｍｇ系被覆層を有する自動車部品であって、前記素材鋼板中の拡散性水素濃度が０.３０ｐｐｍ以下であり、ＪＩＳ Ｚ２３７１：２０１５に従う中性塩水噴霧試験（塩濃度：５０ｇ／Ｌ、温度：３５℃、試験片の裏面および端面シール：あり）による赤錆発生までの時間が７０００時間以上である、自動車部品用。   The material steel plate is in mass%, C: 0.01 to 0.20%, Si: 0.01 to 0.50%, Mn: 0.10 to 2.50%, P: 0.005 to 0.050. %, B: 0.0005 to 0.010%, Ti: 0.01 to 0.20%, Nb: 0 to 0.10%, Mo: 0 to 0.50%, Cr: 0 to 0.50% , Al: 0.01 to 0.10%, balance Fe and unavoidable impurities on the surface of the steel plate of the steel composition, the composition ratio of the metal element is mass%, Al: 1.0 to 22.0%, Mg: 1.3 to 10.0%, Si: 0 to 2.0%, Ti: 0 to 0.10%, B: 0 to 0.05%, Fe: 2.0% or less, remaining Zn and inevitable Part having a Zn—Al—Mg-based coating layer, which is a typical impurity, wherein the diffusible hydrogen concentration in the material steel plate is 0.30 ppm or less, and a neutral salt spray test according to JIS Z2371: 2015 For automobile parts in which the time until the occurrence of red rust by the test (salt concentration: 50 g / L, temperature: 35 ° C., test piece back and end face seals: yes) is 7000 hours or more. 素材鋼板の圧延方向の引張強さが５９０ＭＰａ以上である請求項３に記載の自動車部品用。

The automobile part according to claim 3, wherein the tensile strength in the rolling direction of the raw steel plate is 590 MPa or more.