JP2018505117A - 化学強化可能なガラス板 - Google Patents
化学強化可能なガラス板 Download PDFInfo
- Publication number
- JP2018505117A JP2018505117A JP2017530117A JP2017530117A JP2018505117A JP 2018505117 A JP2018505117 A JP 2018505117A JP 2017530117 A JP2017530117 A JP 2017530117A JP 2017530117 A JP2017530117 A JP 2017530117A JP 2018505117 A JP2018505117 A JP 2018505117A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- composition
- glass plate
- weight
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
−ガラス製造ライン、特にフロートラインは、かなりの出資となり、組成物によって、たとえば耐火物質が損傷しても修復できないため;および
−ある組成から別の組成に変更する移行時間は、この時間が長いと最終ガラスの製造コストに大きな悪影響が生じるので、ガラス製造時の非常に重要なパラメータの1つとなるためである。
65≦SiO2≦78%
5≦Na2O≦20%
1≦K2O<8%
1≦Al2O3<6%
2≦CaO<10%
0≦MgO≦8%;および
0.1〜0.7の範囲のK2O/(K2O+Na2O)比
を含むホウ素フリーおよびストロンチウムフリーおよびリチウムフリーガラス組成を有するガラス板に関する。
65≦SiO2≦78%
8≦Na2O≦15%
1≦K2O<6%
1≦Al2O3<3%
4≦CaO<10%
0≦MgO≦6%;
全鉄:0.06<Fe2O3≦0.2重量%;および
0.1〜0.5の範囲のK2O/(K2O+Na2O)比
を含む。
65≦SiO2≦78%
8≦Na2O≦15%
2≦K2O<6%
1≦Al2O3<3%
6≦CaO<10%
0≦MgO≦6%;
全鉄:0.06<Fe2O3≦0.2重量%;および
0.2〜0.5の範囲のK2O/(K2O+Na2O)比
を含む。
65≦SiO2≦78%
8≦Na2O≦15%
2≦K2O<4%
1≦Al2O3<3%
6≦CaO<10%
0≦MgO≦5%;
全鉄:0.06<Fe2O3≦0.2重量%;および
0.2〜0.4の範囲のK2O/(K2O+Na2O)比
を含む。
前項で作製した試料について、2つの異なる強化条件下で化学強化し、それらのそれぞれについて異なる試料を同時に同じ条件で処理した。異なる組成の試料を1つのカセット中に入れ、予備加熱し、次に溶融KNO3(>99%)浴中に浸漬した。イオン交換後、試料を冷却し、洗浄した。
Fluegelモデル(Glass Technol.:Europ.J.Glass Sci.Technol.A 48(1):13−30(2007);およびJournal of the American Ceramic Society 90(8):2622(2007))を使用して、ガラス組成に基づいた以下の性質の評価を行った:
1200℃および1400℃で評価されるガラス溶融密度;
「融点温度T2」での粘度;
「作用点温度T4」;
失透温度T0。
融点温度T2は、好ましくは最高1550℃、より好ましくは最高1520℃、最も好ましくは最高1500℃である。
−これらの融点温度T2は1500℃未満であり、これらは従来のソーダ石灰ガラス(比較例1.1および2.1)に近い温度である。
−これらの作用点温度T4は1100℃未満であり、これらは従来のソーダ石灰ガラス(比較例.1.1および2.1)に近い温度である。
−これらの失透温度T0は、作用点温度T4よりも低いため適切である;
−これらのガラス密度は、ソーダ石灰ガラス(比較例1.1および2.1)に非常に近く、そのため組成物の変更(移行)中の密度の欠陥が回避/限定される。
Claims (15)
- ガラスの全重量を基準として表した重量パーセント値の単位で:
65≦SiO2≦78%
5≦Na2O≦20%
1≦K2O<8%
1≦Al2O3<6%
2≦CaO<10%
0≦MgO≦8%;
0.1〜0.7のK2O/(K2O+Na2O)比
を含むホウ素フリー、ストロンチウムフリー、およびリチウムフリーのガラス組成を有するガラス板。 - 前記組成が0.002〜1.7重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項1に記載のガラス板。
- 前記組成が0.002〜0.6重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項1または2に記載のガラス板。
- 前記組成が0.002〜0.2重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項1〜3のいずれか一項に記載のガラス板。
- 前記組成が0.06<Fe2O3≦1.7重量%の全鉄を含むことを特徴とする請求項1〜2のいずれか一項に記載のガラス板。
- 前記組成が0.06<Fe2O3≦0.6重量%の全鉄を含むことを特徴とする請求項1〜5のいずれか一項に記載のガラス板。
- 前記組成が0.06<Fe2O3≦0.2重量%の全鉄を含むことを特徴とする請求項1〜6のいずれか一項に記載のガラス板。
- 前記組成が1≦Al2O3≦4重量%となる低アルミナ含有量を含むことを特徴とする請求項1〜7のいずれか一項に記載のガラス板。
- 前記組成が2≦Al2O3≦3重量%を含むことを特徴とする請求項1〜8のいずれか一項に記載のガラス板。
- 前記組成が5≦CaO<10重量%を含むことを特徴とする請求項1〜9のいずれか一項に記載のガラス板。
- 前記組成が1≦K2O<6重量%を含むことを特徴とする請求項1〜10のいずれか一項に記載のガラス板。
- 前記組成が3≦K2O≦6重量%を含むことを特徴とする請求項1〜11のいずれか一項に記載のガラス板。
- 前記組成が0.1〜0.5の範囲のK2O/(K2O+Na2O)比を含むことを特徴とする請求項1〜12のいずれか一項に記載のガラス板。
- 前記組成が0.2〜0.5の範囲のK2O/(K2O+Na2O)比を含むことを特徴とする請求項1〜13のいずれか一項に記載のガラス板。
- 前記組成が0.2〜0.4の範囲のK2O/(K2O+Na2O)比を含むことを特徴とする請求項1〜14のいずれか一項に記載のガラス板。