JP2018172258A - 導電性ハニカム構造体 - Google Patents
導電性ハニカム構造体 Download PDFInfo
- Publication number
- JP2018172258A JP2018172258A JP2017073009A JP2017073009A JP2018172258A JP 2018172258 A JP2018172258 A JP 2018172258A JP 2017073009 A JP2017073009 A JP 2017073009A JP 2017073009 A JP2017073009 A JP 2017073009A JP 2018172258 A JP2018172258 A JP 2018172258A
- Authority
- JP
- Japan
- Prior art keywords
- honeycomb structure
- electrode layer
- metal
- side wall
- peripheral side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】外周側壁と、外周側壁の内側に配設され、一方の底面から他方の底面まで貫通して流路を形成する複数のセルを区画形成する隔壁とを有する柱状のセラミックス製ハニカム構造部、ハニカム構造部の中心軸を挟んで、外周側壁の外面上に配設された一対の電極層、及び、各電極層と一箇所又は二箇所以上の溶接部位を介して接合された一対の金属端子、を備えた導電性ハニカム構造体であって、一箇所又は二箇所以上の溶接部位は、一箇所当たりの溶接部位の溶接面積が2〜50mm2である導電性ハニカム構造体。
【選択図】図1
Description
(1)ハニカム構造体と端子は、電極層を間に挟んで接合する。
(2)端子側から熱エネルギーを加えて溶接する。
(3)溶接は一箇所当たりの溶接部位の大きさに制限を設ける。
外周側壁と、外周側壁の内側に配設され、一方の底面から他方の底面まで貫通して流路を形成する複数のセルを区画形成する隔壁とを有する柱状のセラミックス製ハニカム構造部、
ハニカム構造部の中心軸を挟んで、外周側壁の外面上に配設された一対の電極層、及び、
各電極層と一箇所又は二箇所以上の溶接部位を介して接合された一対の金属端子、
を備えた導電性ハニカム構造体であって、
一箇所又は二箇所以上の溶接部位は、一箇所当たりの溶接部位の溶接面積が2〜50mm2である導電性ハニカム構造体である。
図1には、本発明の一実施形態に係るハニカム構造体100をセルの流路に垂直な方向から観察したときの断面模式図が示されている。図2には、図1に示す実施形態に係るハニカム構造体100を矢印Xの方向から観察したときの側面模式図が示されている。図3には、図1に示す実施形態に係るハニカム構造体100を矢印Yの方向から観察したときの側面模式図が示されている。
ハニカム構造部101の外形は柱状である限り特に限定されず、例えば、底面が円形の柱状(円柱形状)、底面がオーバル形状の柱状、底面が多角形(四角形、五角形、六角形、七角形、八角形等)の柱状等の形状とすることができる。また、ハニカム構造部101の大きさは、耐熱性を高める(外周側壁の周方向に入るクラックを防止する)という理由により、底面の面積が2000〜20000mm2であることが好ましく、5000〜15000mm2であることが更に好ましい。
一対の電極層112a、112bは、ハニカム構造部101の中心軸Oを挟んで、外周側壁102の外面109上に対向して配設される。具体的には、セル108の流路方向に垂直な断面において、一対の電極層112a、112bのそれぞれの周方向中心からハニカム構造部101の中心軸Oまで延ばした二つの線分のなす角度θ(0°≦θ≦180°)は、150°≦θ≦180°であることが好ましく、160°≦θ≦180°であることがより好ましく、170°≦θ≦180°であることが更により好ましく、180°であることが最も好ましい。
一対の金属端子103a、103bは一箇所又は二箇所以上の溶接部位120を介して各電極層112a、112bに接合されている(図2参照)。一箇所当たりの溶接部位120の溶接面積を小さくすることで、熱膨張差による割れや剥離を抑制することができる。具体的には、一箇所当たりの溶接部位120の溶接面積は50mm2以下とすることが好ましく、45mm2以下とすることがより好ましく、40mm2以下とすることが更に好ましく、30mm2以下とすることが更により好ましい。但し、一箇所当たりの溶接部位120の溶接面積が過度に小さいと接合強度が確保できないため、2mm2以上とすることが好ましく、3mm2以上とすることがより好ましく、4mm2以上とすることが更により好ましい。
次に、本発明に係る導電性ハニカム構造体を製造する方法について例示的に説明する。本発明のハニカム構造体の製造方法は一実施形態において、電極層形成ペースト付き未焼成ハニカム構造部を得るA1工程と、電極層形成ペースト付き未焼成ハニカム構造部を焼成してハニカム構造体を得る工程A2と、ハニカム構造体に金属端子を溶接する工程A3とを含む。
(1.円柱状の坏土の作製)
炭化珪素(SiC)粉末と金属珪素(Si)粉末とを80:20の質量割合で混合してセラミック原料を調製した。そして、セラミック原料に、バインダとしてヒドロキシプロピルメチルセルロース、造孔材として吸水性樹脂を添加すると共に、水を添加して成形原料とした。そして、成形原料を真空土練機により混練し、円柱状の坏土を作製した。バインダの含有量は炭化珪素(SiC)粉末と金属珪素(Si)粉末の合計を100質量部としたときに7質量部とした。造孔材の含有量は炭化珪素(SiC)粉末と金属珪素(Si)粉末の合計を100質量部としたときに3質量部とした。水の含有量は炭化珪素(SiC)粉末と金属珪素(Si)粉末の合計を100質量部としたときに42質量部とした。炭化珪素粉末の平均粒子径は20μmであり、金属珪素粉末の平均粒子径は6μmであった。また、造孔材の平均粒子径は20μmであった。炭化珪素粉末、金属珪素粉末及び造孔材の平均粒子径は、レーザー回折法で粒度の頻度分布を測定したときの、体積基準による算術平均径を指す。
得られた円柱状の坏土を碁盤目状の口金構造を有する押出成形機を用いて成形し、セルの流路方向に垂直な断面における各セル形状が正方形である円柱状ハニカム成形体を得た。このハニカム成形体を高周波誘電加熱乾燥した後、熱風乾燥機を用いて120℃で2時間乾燥し、両底面を所定量切断して、ハニカム乾燥体を作製した。
珪化タンタル(TaSi2)粉末、金属珪素(Si)粉末、炭化珪素(SiC)粉末、メチルセルロース、グリセリン、及び水を、自転公転攪拌機で混合して、第一の電極層形成ペーストを調製した。TaSi2粉末、Si粉末、及びSiC粉末は体積比で、TaSi2粉末:Si粉末:SiC粉末=50:30:20となるように配合した。また、TaSi2粉末、Si粉末、及びSiC粉末の合計を100質量部としたときに、メチルセルロースは0.5質量部であり、グリセリンは10質量部であり、水は38質量部であった。珪化タンタル粉末の平均粒子径は7μmであった。金属珪素粉末の平均粒子径は6μmであった。炭化珪素粉末の平均粒子径は35μmであった。これらの平均粒子径はレーザー回折法で粒度の頻度分布を測定したときの、体積基準による算術平均径を指す。
珪化クロム(CrSi2)粉末、金属珪素(Si)粉末、メチルセルロース、グリセリン、及び水を、自転公転攪拌機で混合して、第二の電極層形成ペーストを調製した。ここでは、CrSi2粉末及びSi粉末は体積比で、CrSi2粉末:Si粉末=90:10となるように配合した。また、CrSi2粉末及びSi粉末の合計を100質量部としたときに、メチルセルロースは0.5質量部であり、グリセリンは10質量部であり、水は38質量部であった。珪化クロム粉末の平均粒子径は7μmであった。金属珪素粉末の平均粒子径は6μmであった。
上記の第一の電極層形成ペーストを上記ハニカム乾燥体の外周側壁の外面上に中心軸を挟んで対向するように二箇所塗布した(図1のθ=0°とした。)。各塗布部は、セルの流路方向に垂直な断面において中心角αが90°になるようにして、ハニカム乾燥体の両底面間の全長に亘って帯状に形成した。次いで、第一の電極層形成ペーストの塗布部を部分的に被覆するようにして金属端子の溶接に必要な領域だけ第二の電極層形成ペーストを塗布した。第一及び第二の電極層形成ペーストを塗布後のハニカム乾燥体を120℃で乾燥して、電極層形成ペースト付き未焼成ハニカム構造部を得た。
次に、電極層形成ペースト付き未焼成ハニカム構造部を、大気雰囲気において、550℃で3時間、脱脂した。次に、脱脂した電極層形成ペースト付き未焼成ハニカム構造部を、焼成し、酸化処理して、ハニカム構造体を作製した。焼成は、1450℃のアルゴン雰囲気中で2時間行った。酸化処理は、1300℃の大気中で1時間行った。
上記製造条件により得られたハニカム構造体の各電極層の第二の電極層上にSUS製の板状金属端子(寸法:30mm×50mm×0.5mmt)をファイバーレーザー溶接機を用いて、試験番号に応じて表1に記載の条件で金属端子側から点状又は線状にレーザー照射した。線状にレーザー照射する場合、線幅は2mmとした。金属端子はハニカム構造体の外周側壁の曲面に沿って予め曲げ加工してから使用した。レーザー照射条件はレーザー出力を1kWとし、レーザー出力/ビーム面積≒0.6kW/mm2とした。各電極層に対する金属端子の溶接条件は同一とした。
上記条件による金属端子の溶接時に、ハニカム構造体の溶接部位近傍部分にクラックが発生するか否かを拡大鏡で40倍の倍率で調査した。クラックが発生しなかった場合を「なし」、クラックが発生した場合を「クラックあり」とした。結果を表1に示す。
上記条件により溶接した金属端子をJIS Z3144:2013のピール試験に準拠して引き剥がしたときの剥離箇所を全ての溶接部位について調査した。各試験例について、全ての溶接部位の剥離がハニカム構造部又は電極層の破壊を伴う場合には、金属端子と電極層の間の界面の接合強度が高いと判断し、「OK」とした。一方、剥離がハニカム構造部又は電極層の破壊を伴わず、金属端子と電極層の界面で生じた溶接部位が一つでもあった場合には、金属端子と電極層の間の界面の接合強度が低いと判断し、「NG」とした。結果を表1に示す。
上記製造条件により得られた金属端子付きハニカム構造体について、「ハニカム構造体を収納する金属ケースと、当該金属ケース内に加熱ガスを供給することができるプロパンガスバーナーと、を備えたプロパンガスバーナー試験機」を用いて加熱冷却試験を実施した。上記加熱ガスは、ガスバーナー(プロパンガスバーナー)でプロパンガスを燃焼させることにより発生する燃焼ガスとした。そして、上記加熱冷却試験によって、ハニカム構造体にクラックが発生するか否かを確認することにより、耐熱衝撃性を評価した。具体的には、まず、プロパンガスバーナー試験機の金属ケースに、得られたハニカム構造体を収納(キャニング)した。そして、金属ケース内に、プロパンガスバーナーにより加熱されたガス(燃焼ガス)を供給し、ハニカム構造体内を通過するようにした。金属ケースに流入する加熱ガスの温度条件(入口ガス温度条件)を以下のようにした。まず、5分で900℃まで昇温し、900℃で10分間保持し、その後、5分で100℃まで冷却し、100℃で10分間保持し、その後、室温まで冷却した。その後、ハニカム構造体の外周側壁のクラックを目視により確認した。クラックが確認されなかった場合、耐熱衝撃性試験合格とした。結果を表1に示す。5個のうち4個以上においてクラックが見られない場合を「OK」とし、5個のうち2個以上においてクラックが見られた場合を「NG」とした。
第一の電極層及び第二の電極層の線膨張率(CTE)を以下の方法により測定した。上記製造条件により得られた金属端子付きハニカム構造体から、線膨張率を測定するための第一の電極層及び第二の電極層の測定試料を切り出して作製した。測定試料の大きさは、縦0.2mm×横4mm×長さ50mmとした。作製した測定試料について、BrukerAXS社製の熱膨張率測定装置「TD5000S(商品名)」を用いて、JIS R1618:2004に準拠して、25℃から800℃までの線膨張率を測定した。測定された値を、第一の電極層及び第二の電極層のそれぞれの線膨張率(×10-6(1/K))とした。結果を表1に示す。また、ハニカム構造体から外周側壁の一部を切り出して線膨張率を同様の手順で測定したところ、4.5×10-6(1/K)であった。
第一の電極層及び第二の電極層のヤング率は以下の手順により測定した。第一の電極層及び第二の電極層電極層と同一材質の試験片を用意し、当該試験片について、JIS R1601:2008に示される4点曲げ強さ試験法に準拠することにより曲げ強さ測定し、この測定結果から「応力−歪曲線」を作成した。このようにして得られた「応力−歪曲線」の傾きを算出し、この「応力−歪曲線」の傾きをヤング率とした。
実施例1と同様の手順でハニカム乾燥体を作製した。その後、試験番号に応じて表1の記載の電極層条件及び溶接条件に変更した他は、実施例1と同様の手順で、電極層形成ペーストの調製、電極層形成ペーストの塗布、焼成及び金属端子の溶接を行って金属端子付きハニカム構造体を製造した。
第一の電極層形成ペースト中のTaSi2粉末、Si粉末、及びSiC粉末の体積比を、TaSi2粉末:Si粉末:SiC粉末=40:40:20に変更し、第一の電極層の厚みを表1に記載のように変更し、第二電極層を形成しなかった他は、実施例1と同様の方法で、電極層形成ペースト付き未焼成ハニカム構造部を得た。次いで、電極層形成ペースト付き未焼成ハニカム構造部を実施例1と同じ条件で脱脂、焼成及び酸化処理してハニカム構造体を得た。その後、金属端子の材質をインバー(Fe−Ni合金)製に変更した他は実施例1と同じ手順で、表1の記載の条件で、第一の電極層上にレーザー溶接を行って金属端子付きハニカム構造体を製造した。
一箇所当たりの溶接部位の溶接面積が適切であった実施例1〜20においては、溶接時に端子の剥離やハニカム構造体にクラックが発生しなかった。特に、端子毎の合計溶接面積、溶接部位の間隔及び線膨張率が適切であった実施例1〜13及び20については耐熱衝撃性についても優れていた。
例えば、実施例8はP≧{(A1+A2)/2}/10の関係が成立したことで、一箇所当たりの溶接面積及び端子毎の合計溶接面積が同じ実施例14よりも耐熱衝撃性が向上した。実施例9及び実施例10はP≧{(A1+A2)/2}/10の関係が成立したことで、一箇所当たりの溶接面積及び端子毎の合計溶接面積が同じ実施例15よりも耐熱衝撃性が向上した。
実施例16に対して実施例8は端子毎の合計溶接面積が適切化されていたことで、耐熱衝撃性が向上した。実施例17に対して実施例10は端子毎の合計溶接面積が適切化されていたことで、耐熱衝撃性が向上した。
実施例7では、第一の電極層の線膨張率をAとし、第二の電極層の線膨張率をBとし、金属端子の線膨張率をCとすると、A<B<Cの関係式が成立したことで、実施例18及び実施例19よりも耐熱衝撃性が向上した。
一方、比較例1及び比較例2では一箇所当たりの溶接部位の溶接面積が小さすぎたため、溶接時に端子が剥離した。比較例3では逆に一箇所当たりの溶接部位の溶接面積が大きすぎたため、溶接時にハニカム構造体にクラックが発生した。
101 ハニカム構造部
102 外周側壁
103a、103b 金属端子
104 第一底面
106 第二底面
108 セル
109 外面
110 隔壁
112a、112b 電極層
116 突出部
117 突出部の上面
120 溶接部位
Claims (6)
- 外周側壁と、外周側壁の内側に配設され、一方の底面から他方の底面まで貫通して流路を形成する複数のセルを区画形成する隔壁とを有する柱状のセラミックス製ハニカム構造部、
ハニカム構造部の中心軸を挟んで、外周側壁の外面上に配設された一対の電極層、及び、
各電極層と一箇所又は二箇所以上の溶接部位を介して接合された一対の金属端子、
を備えた導電性ハニカム構造体であって、
一箇所又は二箇所以上の溶接部位は、一箇所当たりの溶接部位の溶接面積が2〜50mm2である導電性ハニカム構造体。 - 金属端子毎に二箇所以上の溶接部位が存在する場合、隣接する溶接部位の溶接面積をそれぞれA1及びA2とし、隣接する溶接部位の間隔をPとすると、P≧{(A1+A2)/2}/10の関係が成立する請求項1に記載の導電性ハニカム構造体。
- 一箇所又は二箇所以上の溶接部位の金属端子毎の合計溶接面積が2mm2以上120mm2以下である請求項1又は2に記載の導電性ハニカム構造体。
- 各電極層は、ハニカム構造部の外周側壁の外面に接する第一の電極層と、金属端子に接する第二の電極層を備えた積層構造を有しており、第二の電極層は応力緩和層である請求項1〜3の何れか一項に記載の導電性ハニカム構造体。
- 第一の電極層の線膨張率をAとし、第二の電極層の線膨張率をBとし、金属端子の線膨張率をCとすると、A<B<Cの関係式が成立する請求項4に記載の導電性ハニカム構造体。
- 第二の電極層のヤング率は2〜50GPaである請求項4又は5に記載の導電性ハニカム構造体。