JP2018094419A - Hair material for brushes and brush prepared therewith - Google Patents
Hair material for brushes and brush prepared therewith Download PDFInfo
- Publication number
- JP2018094419A JP2018094419A JP2017238285A JP2017238285A JP2018094419A JP 2018094419 A JP2018094419 A JP 2018094419A JP 2017238285 A JP2017238285 A JP 2017238285A JP 2017238285 A JP2017238285 A JP 2017238285A JP 2018094419 A JP2018094419 A JP 2018094419A
- Authority
- JP
- Japan
- Prior art keywords
- brush
- bristle material
- brushes
- antibacterial agent
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、歯ブラシを含む各種ブラシに好適なブラシ用毛材及びそれを用いたブラシに関する。 The present invention relates to a brush bristle material suitable for various brushes including a toothbrush and a brush using the same.
歯ブラシは日常的に口腔内で使用されるが、使用後も湿った状態にあるため、随所に存在する黄色ブドウ球菌や歯垢等に含まれる細菌やカビが、繁殖しやすく、細菌やカビが増殖した歯ブラシは、特有の不快な臭いがし、口腔を清潔にするどころか、外部から細菌を口腔内に入れることにもなりかねない。 Toothbrushes are routinely used in the oral cavity, but since they are still moist after use, bacteria and molds contained in Staphylococcus aureus and dental plaque that exist everywhere are easy to propagate, and bacteria and molds are Proliferated toothbrushes have a peculiar unpleasant odor, which can cause bacteria to enter the mouth from the outside, rather than clean the mouth.
このような理由から、歯ブラシにおいては、使用後の細菌の繁殖を抑制することが望まれ、さらに、歯ブラシに求められた特性として毛先による清掃効果に優れていることが望まれている。 For these reasons, in a toothbrush, it is desired to suppress the growth of bacteria after use, and further, as a characteristic required for a toothbrush, it is desired to have an excellent cleaning effect by a hair tip.
歯ブラシの様に継続的に湿潤と乾燥および擦過を繰り返す用途には、抗菌剤のコーティングよりも無機系抗菌剤を練り込む方法の方が安定した抗菌性能を発揮することが開示されている（例えば、特許文献１）。 It is disclosed that a method of kneading an inorganic antibacterial agent exhibits more stable antibacterial performance than an antibacterial agent coating for applications such as a toothbrush that continuously wets, dries and rubs (for example, Patent Document 1).
一方で、ブラシ用毛材の毛先をテーパー化して清掃効果を向上させるためには、アルカリ減量処理が必要であり、一般にアルカリ減量処理により銀系抗菌剤は容易に変色、着色するため、変色防止剤等の化学的処理により解決を図っている（例えば、特許文献２）。 On the other hand, in order to taper the bristles of the bristle material for brushes and improve the cleaning effect, alkali weight reduction treatment is necessary. Generally, silver-based antibacterial agents are easily discolored and colored by alkali weight loss treatment. A solution is made by chemical treatment of an inhibitor or the like (for example, Patent Document 2).
しかしながら、ブラシ用毛材をテーパー化するためには非常に濃い濃度のアルカリ処理を実施することに加え、銀系抗菌剤による汚染が非常に多くなること、化学的処理のための薬剤が多量に必要となることや経時的に効果が低下すること等から、実行に困難が伴ったり、生産性が著しく低い等の問題があった。 However, in order to taper brush hair materials, in addition to carrying out a very high concentration of alkali treatment, the contamination by silver antibacterial agents is extremely large, and there are a large amount of chemical treatment chemicals. There are problems such as difficulty in execution and remarkably low productivity due to necessity and decrease in effect over time.
そこで本発明の課題は、抗菌活性に優れながらも、テーパー加工後に着色を生産性良く除去することが可能なブラシ用毛材、および、それを用いたブラシを提供することにある。 Therefore, an object of the present invention is to provide a hair material for a brush that is excellent in antibacterial activity but can remove coloring with high productivity after taper processing, and a brush using the same.
上記課題を解決するために、本発明に係るブラシ用毛材は、以下の構成を採る。すなわち、
［１］ポリエステルを主成分とし、抗菌活性値が２．０以上である合成繊維からなるブラシ用毛材。
［２］少なくとも１端がテーパー形状を有する前記［１］に記載のブラシ用毛材。
［３］前記合成繊維の明度が６０以上である前記［１］または［２］に記載のブラシ用毛材。
［４］前記合成繊維が抗菌剤を含有する前記［１］〜［３］のいずれかに記載のブラシ用毛材。
［５］前記抗菌剤が銀含有抗菌剤である前記［４］に記載のブラシ用毛材。
［６］前記抗菌剤を１〜１０００００質量ｐｐｍ含有する前記［４］または［５］に記載のブラシ用毛材。
［７］前記抗菌剤を５〜１００質量ｐｐｍ含有する前記［４］〜［６］のいずれかに記載のブラシ用毛材。
［８］前記［１］〜［７］のいずれかに記載のブラシ用毛材を、少なくとも一部に含むブラシ。
In order to solve the above problems, the bristle material for a brush according to the present invention has the following configuration. That is,
[1] A bristle material for a brush comprising a synthetic fiber mainly composed of polyester and having an antibacterial activity value of 2.0 or more.
[2] The brush bristle material according to [1], wherein at least one end has a tapered shape.
[3] The bristle material for brush according to [1] or [2], wherein the lightness of the synthetic fiber is 60 or more.
[4] The brush hair material according to any one of [1] to [3], wherein the synthetic fiber contains an antibacterial agent.
[5] The brush hair material according to [4], wherein the antibacterial agent is a silver-containing antibacterial agent.
[6] The brush bristle material according to [4] or [5], containing 1 to 100,000 ppm by mass of the antibacterial agent.
[7] The bristle material for brush according to any one of the above [4] to [6], containing 5 to 100 mass ppm of the antibacterial agent.
[8] A brush containing at least a part of the brush hair material according to any one of [1] to [7].
本発明によれば、抗菌活性に優れながらも、テーパー加工後に着色を生産性良く除去することが可能なブラシ用毛材、および、それを用いたブラシを提供できる。 ADVANTAGE OF THE INVENTION According to this invention, although it is excellent in antibacterial activity, the bristle material for brushes which can remove coloring with sufficient productivity after a taper process, and a brush using the same can be provided.
本発明のブラシ用毛材は、ポリエステルを主成分とし、抗菌活性値が２．０以上である合成繊維からなる。 The bristle material for brushes of the present invention is made of a synthetic fiber having polyester as a main component and an antibacterial activity value of 2.0 or more.
上記本発明のブラシ用毛材に用いられる繊維は、ポリエステルを主成分とする合成繊維である。ポリエステルとは、ポリマー鎖中の繰り返し構成単位の少なくとも２０％以上にエステル結合を含むポリマーをいい、かかるポリエステル中に、ＰＥＴ、ＰＴＴおよびＰＢＴからなる群より選ばれる１種以上のポリマーを２０％以上含有していることが好ましく、ＰＥＴ、ＰＴＴおよびＰＢＴからなる群より選ばれる１種以上のポリマーを８０％以上含有していることがより好ましい。ポリエステルを主成分とする合成繊維とは、合成繊維に含まれる成分のうち、５０質量％以上が、前記ポリエステルである合成繊維をいい、かかるポリエステルの比率は、７０質量％以上であればより好ましく、９０質量％以上であればさらに好ましい。このような組成の合成繊維とすることにより、アルカリ減量加工が可能な合成繊維となるためである。 The fiber used for the bristle material for brushes of the present invention is a synthetic fiber mainly composed of polyester. Polyester refers to a polymer containing an ester bond in at least 20% or more of repeating structural units in a polymer chain. In such polyester, 20% or more of one or more polymers selected from the group consisting of PET, PTT and PBT are included. It is preferable to contain, and it is more preferable to contain 80% or more of one or more polymers selected from the group consisting of PET, PTT and PBT. The synthetic fiber having polyester as a main component means a synthetic fiber in which 50% by mass or more of the components contained in the synthetic fiber is the polyester, and the ratio of the polyester is more preferably 70% by mass or more. 90 mass% or more is more preferable. It is because it becomes a synthetic fiber which can carry out an alkali weight reduction process by setting it as the synthetic fiber of such a composition.
本発明のブラシ用毛材は、抗菌活性値が２．０以上である。ここでいう抗菌活性値とは、ＪＩＳ Ｚ ２８０１：２０１０のフィルム密着法によって測定される抗菌活性値であり、これが、２．０以上であれば、黄色ぶどう球菌への抗菌性能が良好となり、かかる観点から３．０以上が好ましく、４．０以上であることがさらに好ましい。かかる抗菌活性値は、高ければ高いほど好ましいが、現状での上限値は５．１である。これは該測定法での計測限界であり、これを超える値を得ることは現在の評価技術では困難である。ただし、今後評価方法が進歩すれば、前記上限値を超える抗菌活性値を有するものを適用することを妨げるものではない。 The brush hair material of the present invention has an antibacterial activity value of 2.0 or more. Here, the antibacterial activity value is an antibacterial activity value measured by the film adhesion method of JIS Z 2801: 2010. If this is 2.0 or more, the antibacterial performance against Staphylococcus aureus will be good, and such From the viewpoint, it is preferably 3.0 or more, and more preferably 4.0 or more. The higher the antibacterial activity value, the better. However, the upper limit value at present is 5.1. This is a measurement limit in the measurement method, and it is difficult to obtain a value exceeding this with the current evaluation technique. However, if the evaluation method advances in the future, it does not preclude applying one having an antibacterial activity value exceeding the upper limit.
前記抗菌活性は、抗菌剤を含有せしめることにより付与することができる。本発明のブラシ用毛材に適用する抗菌剤としては、ポリエステルを主成分とする合成繊維を得る工程として溶融紡糸が好ましいことから、耐熱性の高いものが好ましく、かかる観点から無機系抗菌剤が好ましく、中でも、銀含有抗菌剤がより好ましい。さらに好ましくは銀含有抗菌剤を多孔質担体に担持させるもので、抗菌性能が高く、また、安全性も高いことを特徴としており、銅や亜鉛を使用した抗菌剤に比較して、抗菌作用が１０倍以上であることによる。 The antibacterial activity can be imparted by incorporating an antibacterial agent. As the antibacterial agent applied to the bristle material for brushes of the present invention, melt spinning is preferable as the step of obtaining a synthetic fiber containing polyester as a main component, so that a material having high heat resistance is preferable. Among them, a silver-containing antibacterial agent is more preferable. More preferably, a silver-containing antibacterial agent is supported on a porous carrier, and is characterized by high antibacterial performance and high safety. Compared with antibacterial agents using copper or zinc, the antibacterial action is high. Because it is 10 times or more.
また、抗菌剤のポリエステル繊維中の含有量は１〜１０００００質量ｐｐｍの範囲内であることが好ましく、より好ましくは２〜１０００質量ｐｐｍの範囲内、さらに好ましくは５〜１００質量ｐｐｍの範囲内であることが望ましい。 Moreover, it is preferable that content in the polyester fiber of an antibacterial agent exists in the range of 1-100,000 mass ppm, More preferably, it exists in the range of 2-1000 mass ppm, More preferably, it exists in the range of 5-100 mass ppm. It is desirable to be.
抗菌剤の含有量については、繊維を燃やした灰分中のチタン以外の無機成分を元素分析にて定量化することで算出する。ここで酸化チタンを合成繊維には艶消し剤として用いており、その添加量が灰分中に含まれてしまうことが想定されるため、チタンは測定外とするため、元素分析にてチタン量を測定し、除外する。 About content of an antibacterial agent, it calculates by quantifying the inorganic components other than titanium in the ash which burned the fiber by elemental analysis. Here, titanium oxide is used as a matting agent in synthetic fibers, and since it is assumed that the amount added is included in the ash, titanium is excluded from measurement. Measure and exclude.
さらに、繊維に含有している抗菌剤の状態は、表面付近に局在化していても、全体に存在していてもよい。抗菌剤を含有せしめる方法については、表面に含浸させる方法、紡糸前の原料に練り込んで紡糸する方法等、特に限定されるものではないが、生産性の観点から紡糸前の原料に練り込んで紡糸する方法が好ましい。 Furthermore, the state of the antibacterial agent contained in the fiber may be localized near the surface or may exist throughout. The method of impregnating the antibacterial agent is not particularly limited, such as a method of impregnating the surface, a method of kneading into the raw material before spinning, and spinning, but from the viewpoint of productivity, kneading into the raw material before spinning. A method of spinning is preferred.
本発明のブラシ用毛材は、少なくとも１端がテーパー形状を有することが好ましい。好ましいテーパー形状としては、先端から０．５ｍｍの部分が毛材の長手方向の中央部の横断面の９０％以下の直径であることが好ましく、８０％以下であることがより好ましく、５０％以下であることがさらに好ましい。毛材の長手方向の中央部の横断面の直径についてはブラシ用毛材の用途に応じて設計されればよく、例えば歯ブラシにおいては、特定の太さ以下とすることにより、歯間への侵入性を向上でき、優れた清掃性を発揮できる。 The brush bristle material of the present invention preferably has a tapered shape at least at one end. As a preferable tapered shape, the diameter of 0.5 mm from the tip is preferably 90% or less, more preferably 80% or less, and more preferably 50% or less of the cross section of the central portion in the longitudinal direction of the bristle material. More preferably. The diameter of the cross-section of the central portion in the longitudinal direction of the bristle material may be designed according to the use of the bristle material for the brush. For example, in a toothbrush, by entering a specific thickness or less, penetration between teeth Can be improved, and excellent cleaning properties can be demonstrated.
テーパー形状とするための加工については、一般にメカニカル加工とケミカル加工があるが、先端形状を安定化および上記のような形状を得るためにケミカル加工が好ましい。 As for the processing for obtaining a tapered shape, there are generally mechanical processing and chemical processing, but chemical processing is preferable in order to stabilize the tip shape and obtain the shape as described above.
本発明のブラシ用毛材の明度は６０以上であることが好ましく、６５以上であることがより好ましく、７０以上であることがさらに好ましい。ここでいう明度とは、Ｌａｂ表色系におけるＬ値である。かかる明度は、高ければ高いほど好ましいが、８５あれば十分である。かかるＬ値は、カラーメーターで測定することができる。カラーメーターとしては、市販のものを適用すればよい。例えば、スガ試験機製ＳＭ−Ｔカラーメーター等が挙げられる。なお、Ｌ値は、測定するサンプルの状態によって値が変化するため、本発明においては、後述の図面にて説明する形態に配置して測定した値を採るものとする。 The brightness of the brush hair material of the present invention is preferably 60 or more, more preferably 65 or more, and further preferably 70 or more. The brightness here is an L value in the Lab color system. Such lightness is preferably as high as possible, but 85 is sufficient. Such L value can be measured with a color meter. A commercially available color meter may be used as the color meter. For example, SM-T color meter manufactured by Suga Test Instruments and the like can be mentioned. In addition, since a value changes with the state of the sample to measure, L value shall take the value measured by arrange | positioning to the form demonstrated in the below-mentioned drawing in this invention.
本発明のブラシ用毛材が銀を含有する抗菌剤を含有するものである場合、ケミカル加工することにより、銀を含有する抗菌剤に特有の着色が発生し、加工後の繊維は茶褐色な繊維となる。これは、抗菌剤の金属成分である銀がアルカリ中の金属と交換反応し、茶褐色な水酸化金属塩を発生するためであり、ケミカル加工する際には避けられない。かかる場合、ブラシ用毛材を洗浄して茶褐色な水酸化金属塩を除去し、明度を前記の範囲とすることが好ましい。 When the brush hair material of the present invention contains an antibacterial agent containing silver, the antibacterial agent containing silver is colored by chemical processing, and the processed fiber is a brown fiber It becomes. This is because silver, which is a metal component of the antibacterial agent, exchanges with a metal in an alkali to generate a brown metal hydroxide salt, which is unavoidable during chemical processing. In such a case, it is preferable that the bristle material for the brush is washed to remove the brown metal hydroxide salt and the brightness is in the above range.
テーパー形成の際に生じる水酸化金属塩等（以下、付着物と記す場合もある）を除去する洗浄方法は、特に限定されるものではないが、ブラシ用毛材を直径０．１ｍｍ程度の酸素微泡を分散せしめた液体（以下、浸漬液と記すこともある）に浸漬することで、水酸化金属塩等の汚れが浮き上がり、除去が容易となる。浸漬時間は０．５ｈｒ以上が好ましく、より好ましくは１．５ｈｒ以上、さらに好ましくは２．０ｈｒ以上である。浸漬時間の上限については、生産性を考慮して設定すれば良いが、２．５ｈｒ浸漬すれば十分である場合が多い。付着物の除去は洗浄液を０．２ＭＰａ〜３．０ＭＰａの高圧にて噴射し洗浄することが好ましい。噴射する圧力は０．５ＭＰａ〜１．５ＭＰａがより好ましい。３．０ＭＰａ以上では毛材の剛性を上回るため、水圧により毛先が折れ曲がってしまい、製品品位が低下してしまう場合がある。酸素微泡を分散せしめた液体へ浸漬する工程、洗浄液の噴射による洗浄の工程、において用いる浸漬液や洗浄液には水道水を用いることができ、酸、アルカリ、界面活性剤等が含まれていても構わない。 The cleaning method for removing metal hydroxide salt or the like (hereinafter sometimes referred to as deposits) generated during the taper formation is not particularly limited, but the brush hair material is oxygen having a diameter of about 0.1 mm. By immersing in a liquid in which fine bubbles are dispersed (hereinafter also referred to as an immersion liquid), dirt such as a metal hydroxide salt rises and is easily removed. The immersion time is preferably 0.5 hr or more, more preferably 1.5 hr or more, and further preferably 2.0 hr or more. The upper limit of the immersion time may be set in consideration of productivity, but it is often sufficient to immerse for 2.5 hours. The removal of deposits is preferably performed by spraying the cleaning liquid at a high pressure of 0.2 MPa to 3.0 MPa. The pressure to be injected is more preferably 0.5 MPa to 1.5 MPa. Since the rigidity of the hair material is exceeded at 3.0 MPa or more, the hair tip may be bent by water pressure, and the product quality may be lowered. The immersion liquid and the cleaning liquid used in the step of immersing in the liquid in which fine oxygen bubbles are dispersed and the cleaning step by spraying the cleaning liquid can use tap water, and include acid, alkali, surfactant and the like. It doesn't matter.
本発明のブラシ用毛材は、直径としては、５０〜１，０００μｍの範囲にあることが好ましく、８０〜５００μｍの範囲であることがより好ましい。ブラシ用毛材の直径が５０μｍ未満であると、ブラシ用毛材自身の腰が弱くなりすぎ、用途によっては清掃効果が低下するおそれがある。ブラシ用毛材の直径が１，０００μｍを超えると、ブラシ用毛材自身の腰が強くなりすぎ、先端部の露出状態にもよるが、ブラシ用毛材が被清掃物側に強く押し付けられて被清掃物を傷つけやすくなるおそれがある。ここで直径とは繊維断面の外接円の径のことである。 The diameter of the brush hair material of the present invention is preferably in the range of 50 to 1,000 μm, and more preferably in the range of 80 to 500 μm. If the diameter of the brush bristle material is less than 50 μm, the brush bristle material itself becomes too weak and the cleaning effect may be reduced depending on the application. If the diameter of the brush bristle material exceeds 1,000 μm, the brush bristle material itself becomes too strong, and depending on the exposed state of the tip, the brush bristle material is strongly pressed against the object to be cleaned. The object to be cleaned may be easily damaged. Here, the diameter is a diameter of a circumscribed circle of the fiber cross section.
また、本発明に係るブラシ用毛材においては、繊維形状は円形に形成されている形態、円形以外の三角、四角、星型等の異形断面に形成されている形態、いずれの形状でも構わず、また、複数が連なった形も採り得る。用途や使用形態、使用条件等に応じて適宜決定すればよい。 Moreover, in the bristle material for brushes according to the present invention, the shape of the fiber may be any shape, such as a shape formed in a circular shape, a shape formed in a non-circular triangle, square, star shape, or the like. In addition, a form in which a plurality are connected may be employed. What is necessary is just to determine suitably according to a use, a use form, use conditions, etc.
また、本発明のブラシ用毛材は、芯鞘状等の複合繊維になっていても構わないが、かかる場合、表面に抗菌剤を含有する部分が露出していることが好ましい。例えば、芯鞘形状の複合繊維となっている場合、少なくとも、鞘の部分に抗菌剤が含有されている態様が挙げられる。 Moreover, although the bristle material for brushes of the present invention may be a core-sheath-like composite fiber, in such a case, it is preferable that a portion containing an antibacterial agent is exposed on the surface. For example, when it is a core-sheath-shaped composite fiber, an embodiment in which an antibacterial agent is contained at least in the sheath portion is exemplified.
本発明のブラシ用毛材は、それを少なくとも一部に含むブラシとして好ましく用いられる。かかるブラシは、ブラシ用の毛材が特に上述したような特性を有するので、歯ブラシや舌ブラシ、歯間ブラシ、化粧ブラシ、フェイシャル用ブラシとして好適であり、塗布用ブラシや液晶洗浄用ブラシ等の工業用途にも好ましく用いられる。 The brush bristle material of the present invention is preferably used as a brush containing at least a part thereof. Such brushes are suitable as toothbrushes, tongue brushes, interdental brushes, cosmetic brushes, facial brushes, and the like because the bristle material for brushes has the characteristics described above, such as application brushes and liquid crystal cleaning brushes. It is also preferably used for industrial applications.
本発明のブラシにおいて、ブラシ用毛材の植毛方法は特には限定されず、その用途に適した方法で植毛されていればよい。一般に歯ブラシ用途においては、平線植毛および無平線植毛があるが、いずれの植毛方法においても対応可能である。 In the brush of the present invention, the method of planting the bristle material for the brush is not particularly limited as long as it is planted by a method suitable for the application. In general, for toothbrush applications, there are flat line flocking and non-flat line flocking, but any flocking method can be used.
また、本発明に係るブラシにおいては、その用途にもよるが、好ましいブラシの毛丈（ブラシ根元から毛先までの長さ）の範囲として、１〜１００ｍｍの範囲が例示され、より好ましくは、５〜３５ｍｍの範囲である。 Moreover, in the brush according to the present invention, although it depends on its use, a range of 1 to 100 mm is exemplified as a preferable brush bristle length (length from the brush root to the hair tip), more preferably, The range is 5 to 35 mm.
以下に、本発明の実施の形態について、図面を参照しながら説明する。 Embodiments of the present invention will be described below with reference to the drawings.
図１は、本発明の一実施形態（実施形態１）に係るブラシ用毛材１を示しており、図１（Ａ）は該毛材１の一方の端部を示している。ブラシ用毛材１は、図１（Ｂ）に示すように、ポリエステルを主成分とする合成樹脂で形成された合成繊維２の長手方向の一方の端または両方の端には（図１（Ａ）は該ブラシ用毛材１の一方の端部のみを示している。）、テーパー部３が形成されている。
FIG. 1 shows a
本発明のブラシ用毛材を上記ポリエステル樹脂としてポリブチレンテレフタレート（ＰＢＴ）で形成し、アルカリ減量加工でテーパー形状を形成させることが好ましい。これにより図１（Ａ）に示すようなテーパー部３が形成されるため、テーパー部３が形成されていないブラシ用毛材よりも細く、汚れの掻き取りに際し、歯間への侵入性が向上し、高い清掃効果を発揮でき、優れた清掃性を発現する。
It is preferable that the bristle material for brushes of the present invention is formed of polybutylene terephthalate (PBT) as the above-mentioned polyester resin, and a tapered shape is formed by alkali weight reduction processing. As a result, a tapered
上記のように構成されたブラシ用毛材１が、各種ブラシの作製のために少なくとも一部に使用される。一般に、ブラシ用毛材をブラシ構成部材に植毛する際の方法として、代表的に二種の方法が知られているが、これら二種の方法を、歯ブラシへの使用の場合を例にとって、図２を参照しながら説明する。
The brush bristle
図２（Ａ）は、ブラシ用毛材１１が歯ブラシ構成部材１２のヘッド部に植毛された歯ブラシ１３を示しており、このブラシ用毛材１１の植毛方法として、図２（Ａ）のａ−ａ’線に沿う拡大断面図である図２（Ｂ）、（Ｃ）に示すような二種の方法がある。図２（Ｂ）に示す方法では、植毛穴１４に二つ折りにしたブラシ用毛材１１を差し込み、平線１５と称されている固定具でブラシ用毛材１１を歯ブラシ構成部材１２に固定する。完成された歯ブラシは、通常、平線歯ブラシと呼ばれている。このような平線歯ブラシでは、予め作製されたブラシ用毛材１１の両方の端部がブラシの毛先となる。図２（Ｃ）に示す方法では、歯ブラシ構成部材１２のヘッド部表面側部材１２ａの貫通穴１６にブラシ用毛材１１の一方の端部を挿通させ、挿通されたブラシ用毛材１１のもう一方の端部に加熱装置(図示略)を当てて焼玉１７と称されている抜け防止あるいは固定用の塊を形成し、しかる後に、ヘッド部裏面側部材１２ｂを接合し焼玉１７を隠して歯ブラシ商品を完成させる。完成された歯ブラシは、通常、無平線歯ブラシと呼ばれている。このような無平線歯ブラシでは、予め作製されたブラシ用毛材１１の一方の端部がブラシの毛先となる。したがって、本発明に係るブラシ用毛材１が平線歯ブラシに使用される場合には、上述したテーパー部３はブラシ用毛材１の両方の端部に形成されることになり、無平線歯ブラシに使用される場合には、テーパー端部４はブラシ用毛材１の一方の端部のみに形成されることになる。
FIG. 2 (A) shows a
本発明のブラシ用毛材２１のＬ値は、測定するサンプルの状態によって値が変化するため、本発明において適用する測定方法について図３を参照しながら説明する。
Since the L value of the
まず、試験条件として、反射光、Φ５、Ｎ＝３の平均とする。 First, the test conditions are the average of reflected light, Φ5, and N = 3.
図３（Ａ）は、測定するブラシ用毛材２１を透明なガラス板２２にセットしたサンプル２３を上から見た状態を示しており、このサンプル２３をｃ−ｃ’線でカットした横断面を図３（Ｂ）に示す。測定は図３（Ｂ）のサンプル２３のガラス板２２の側から行う。ブラシ用毛材２１をガラス板２２に並べる際には、０．０６２５ｇ／ｃｍ２かつ上部から見て発光部が見えないように並べる。また、実際の測定時にはブラシ用毛材２１を固定するために、図３（Ｃ）に示す用にブラシ用毛材２１のブラシ用毛材２１と接する面が明度６５の白色板２４を置いて測定する。
FIG. 3A shows a state in which a
本発明に係るブラシ用毛材は、上述の実施形態１以外にも、種々の形態を採り得る。図４に各種形態を、繊維の横断面にて例示する。複合断面３１、４１、異形断面５１、６１、７１、８１等様々な形態を採るこができ、抗菌剤を含有している部分を網掛けで表記した。
The bristle material for brushes according to the present invention can take various forms other than the first embodiment described above. Various forms are illustrated in FIG. 4 in the cross section of a fiber. Various forms such as
また、本発明に係るブラシ用毛材は、高い抗菌性能を有した白色繊維を得ることができ、種々の横断面形態を採り得、用途や使用目的に応じて、最適な設計をすることが可能である。 Further, the bristle material for brushes according to the present invention can obtain white fibers having high antibacterial performance, can take various cross-sectional forms, and can be optimally designed according to the use and purpose of use. Is possible.
以下に、本発明の実施例について、図面を参照しながら説明するが、本願発明は、これらに限定されるものではない。 Examples of the present invention will be described below with reference to the drawings. However, the present invention is not limited to these examples.
各特性の測定は、以下の様に行った。 Each characteristic was measured as follows.
（１）ブラシ用毛材の直径
繊維断面の外接円の径をＮ＝４０測定し、平均値を直径とした。
(1) Diameter of brush bristle material The diameter of the circumscribed circle of the fiber cross section was measured at N = 40, and the average value was taken as the diameter.
（２）明度
スガ試験機製ＳＭ−Ｔカラーメーターを用いて行った。ブラシ用毛材２１をガラス板２２に並べる際には、０．０６２５ｇ／ｃｍ２かつ発光部が見えないように並べ、その上に白色板６４を置き、反射光、Φ５、Ｎ＝３の設定で測定し、平均値を明度とした。
(2) Lightness It was performed using a SM-T color meter manufactured by Suga Test Instruments. When arranging the brush bristle
（３）抗菌活性値
ＪＩＳ Ｚ ２８０１：２０１０のフィルム密着法によって測定した。
(3) Antibacterial activity value It measured by the film contact | adherence method of JISZ2801: 2010.
［実施例１〜１０］
ポリテトラメチレンテレフタレート（ＰＢＴ）からなり、直径１２０〜１８０μｍ、抗菌剤を１〜１０００質量ｐｐｍ含有する合成樹脂からなる図１に示すブラシ用毛材を、図２に示す歯ブラシに適用した場合の代表的な特性を表１にまとめた。
[Examples 1 to 10]
Representative of the brush hair material shown in FIG. 1 made of polytetramethylene terephthalate (PBT) having a diameter of 120 to 180 μm and a synthetic resin containing 1 to 1000 mass ppm of antibacterial agent applied to the toothbrush shown in FIG. The typical characteristics are summarized in Table 1.
［実施例１１〜１９］
ポリトリメチレンテレフタレート（ＰＴＴ）からなり、直径１２０〜１８０μｍ、抗菌剤を１〜１０００質量ｐｐｍ含有する合成樹脂からなる図１に示すブラシ用毛材を、図２に示す歯ブラシに適用した場合の代表的な特性を表２にまとめた。
［比較例１］
未洗浄のＰＢＴ抗菌繊維からなる図１に示すブラシ用毛材を、図２に示す歯ブラシに適用した場合の代表的な特性を表２にまとめた。
［比較例２］
弱洗浄のＰＢＴ抗菌繊維からなる図１に示すブラシ用毛材を、図２に示す歯ブラシに適用した場合の代表的な特性を表２にまとめた。
[Examples 11 to 19]
Representative of the brush hair material shown in FIG. 1 made of a synthetic resin made of polytrimethylene terephthalate (PTT) and having a diameter of 120 to 180 μm and an antibacterial agent of 1 to 1000 ppm by mass applied to the toothbrush shown in FIG. The typical characteristics are summarized in Table 2.
[Comparative Example 1]
Table 2 summarizes typical characteristics when the brush bristle material shown in FIG. 1 made of unwashed PBT antibacterial fibers is applied to the toothbrush shown in FIG.
[Comparative Example 2]
Table 2 summarizes typical characteristics when the bristle material for brushes shown in FIG. 1 made of weakly washed PBT antibacterial fibers is applied to the toothbrush shown in FIG.
［実施例２０〜２２］
ポリテトラメチレンテレフタレート（ＰＢＴ）からなり、直径５０〜１００μｍ、抗菌剤を５０質量ｐｐｍ含有する合成樹脂からなる図１に示すブラシ用毛材を、フェイシャル用ブラシに適用した場合の代表的な特性を表３にまとめた。
［実施例２３〜２５］
ポリトリメチレンテレフタレート（ＰＴＴ）からなり、直径５０〜１００μｍ、抗菌剤を５０質量ｐｐｍ含有する合成樹脂からなる図１に示すブラシ用毛材を、フェイシャル用ブラシに適用した場合の代表的な特性を表３にまとめた。
[Examples 20 to 22]
Typical characteristics when the hair material for brushes shown in FIG. 1 made of synthetic resin containing polytetramethylene terephthalate (PBT) and having a diameter of 50 to 100 μm and containing 50 mass ppm of antibacterial agent is applied to a facial brush. The results are summarized in Table 3.
[Examples 23 to 25]
Typical characteristics when the brush hair material shown in FIG. 1 made of polytrimethylene terephthalate (PTT), made of synthetic resin containing 50 to 100 μm in diameter and 50 mass ppm of antibacterial agent is applied to a facial brush. The results are summarized in Table 3.
本発明は、あらゆるブラシに適用でき、特に、歯ブラシ、舌ブラシ、化粧ブラシ、フェイシャル用ブラシ、塗布用ブラシ、液晶洗浄用ブラシ等に好適なものである。 The present invention can be applied to any brush, and is particularly suitable for toothbrushes, tongue brushes, makeup brushes, facial brushes, application brushes, liquid crystal cleaning brushes, and the like.
１、１１、２１ ブラシ用毛材
２ 合成繊維３ テーパー部
１２ 歯ブラシ構成部材
１２ａ ヘッド部表面側部材
１２ｂ ヘッド部裏面側部材
１３ 歯ブラシ
１４ 植毛穴
１５ 平線
１６ 貫通穴
１７ 焼玉
２２ ガラス板
２３ サンプル
２４ 白色板
３１、４１ ブラシ用毛材（複合繊維）
５１、６１、７１、８１ ブラシ用毛材（異形断面繊維）
1, 11, 21 Brush bristle
51, 61, 71, 81 Hair material for brushes (irregular cross-section fiber)
Claims (8)