JP2018088013A

JP2018088013A - Laminated light-shielding film for optical apparatus, and light-shielding ring for optical apparatus, lens unit, and camera module using the same

Info

Publication number: JP2018088013A
Application number: JP2018039278A
Authority: JP
Inventors: 豪士長濱; Tsuyoshi Nagahama; 靖麿豊島; Yasumaro Toyoshima; 聡上垣; Satoshi Uegaki; 拡輝山本; Hiroki Yamamoto
Original assignee: Kimoto Co Ltd
Current assignee: Kimoto Co Ltd
Priority date: 2018-03-06
Filing date: 2018-03-06
Publication date: 2018-06-07
Anticipated expiration: 2036-10-06
Also published as: JP6814170B2

Abstract

PROBLEM TO BE SOLVED: To provide a laminated light-shielding film in which the front and back sides can be easily identified despite inclusion of black light-shielding layers.SOLUTION: A laminated light-shielding film 100 has a lamination structure including at least a base material film 11, a black light-shielding layer 21 that is provided on one principal surface 11a of the base material film 11, and a black light-shielding layer 31 that is provided on the other principal surface 11b. The black light-shielding layer 21 and a second black light-shielding layer 23 have an optical density of 2.5 or more and a 60-degree glossiness of 5.0% or less, respectively; the black light-shielding layer 21 has a 60-degree glossiness and/or a lightness index Ldifferent from those of the black light-shielding layer 31. It is preferable that the base material film 11, the first black light-shielding layer 21 and/or the second black light-shielding layer 31 have inclined end faces 12, 22, and 32 that increase the film width from the first black light-shielding layer 21 toward the second black light-shielding layer 31.SELECTED DRAWING: Figure 2

Description

本発明は、積層遮光フィルム、並びに、これを用いた光学機器用遮光リング、レンズユニット及びカメラモジュールに関する。 The present invention relates to a laminated light-shielding film, and a light-shielding ring for optical equipment, a lens unit, and a camera module using the same.

例えば携帯電話、スマートフォン等の情報通信端末やデジタルカメラ等の電子機器には、被写体を撮影して画像信号に変換するためのカメラモジュールが内蔵されている。このカメラモジュールは、被写体を撮像する撮像素子と、この撮像素子上に被写体の画像を結像するためのレンズユニットを備えている。レンズユニットは、通常、複数のレンズの組み合わせから構成されている。 For example, information communication terminals such as mobile phones and smartphones, and electronic devices such as digital cameras have built-in camera modules for photographing subjects and converting them into image signals. This camera module includes an image sensor that images a subject and a lens unit that forms an image of the subject on the image sensor. The lens unit is usually composed of a combination of a plurality of lenses.

この種のカメラモジュールでは、不要な入射光や反射光を除去し、ハレーション、レンズフレア、ゴースト等の発生を防ぎ、撮像画像の画質を向上させることが求められている。そのため、不要光をカットするための遮光部材を有するレンズユニットやカメラモジュール等が提案されている。 This type of camera module is required to remove unnecessary incident light and reflected light to prevent the occurrence of halation, lens flare, ghost, and the like and to improve the image quality of the captured image. Therefore, a lens unit, a camera module, and the like having a light shielding member for cutting unnecessary light have been proposed.

このような遮光部材としては、カーボンブラック、滑剤、微粒子及びバインダー樹脂を含有する遮光層を基材フィルムの両面に形成した遮光フィルムが提案されている（特許文献１及び２参照）。 As such a light shielding member, a light shielding film in which a light shielding layer containing carbon black, a lubricant, fine particles, and a binder resin is formed on both surfaces of a base film has been proposed (see Patent Documents 1 and 2).

特開平９−２７４２１８号公報JP-A-9-274218 ＷＯ２００６／０１６５５５号公報WO2006 / 016555

近年、世界横断的なモジュール化が進展しており、複数のレンズと遮光板を光軸方向に積み重ねたレンズユニット、このレンズユニットに撮像素子をさらに組み込んだカメラモジュール等の形態で、世界各国の製造工場にて、それぞれ製造及び管理されるようになってきている。これにともない、各モジュールの一部品となる遮光フィルムや遮光部材も、各所においてそれぞれ搬送及び製造管理されている。 In recent years, modularization across the world has progressed, and in the form of a lens unit in which a plurality of lenses and a light shielding plate are stacked in the optical axis direction, and a camera module in which an image sensor is further incorporated in this lens unit, They are being manufactured and managed at manufacturing plants. In connection with this, the light-shielding film and the light-shielding member which are one component of each module are also conveyed and manufactured management in each place.

ここで、遮光フィルムから所望形状の遮光部材を作製する際に又は遮光部材をモジュールに組み込む際に、遮光フィルムや遮光部材の表裏面の判別がつかないと、組み込み不良等の製造故障の原因となり得る。そして、世界横断的なモジュール化が進展している昨今において、ワールドワイドに遮光フィルムや遮光部材の管理（表裏面の確認）の徹底を図ることは容易ではない。 Here, when making a light shielding member of a desired shape from the light shielding film or incorporating the light shielding member into the module, if the front and back surfaces of the light shielding film and the light shielding member cannot be discriminated, it may cause a manufacturing failure such as a defective assembly. obtain. And nowadays, as modularization is progressing across the world, it is not easy to ensure thorough management of light-shielding films and light-shielding members (confirmation of front and back surfaces) worldwide.

また、カメラモジュールの小型及び薄膜化の進展により、極めて小さなサイズの遮光部材が搭載されるようになってきている。そして、黒色の遮光層を設けた遮光フィルムにおいては、サイズが数センチ四方以下になると、遮光フィルムの表裏判別が極めて困難になる。とりわけ、黒色度の高い（換言すれば、光学濃度が高い）遮光フィルムにおいては、この傾向が顕著になる。 In addition, with the progress of miniaturization and thinning of the camera module, a light shielding member having an extremely small size has been mounted. And in the light shielding film which provided the black light shielding layer, when the size will be several centimeters square or less, the front and back discrimination of the light shielding film becomes extremely difficult. In particular, this tendency becomes remarkable in a light-shielding film having high blackness (in other words, high optical density).

本発明は、上記課題に鑑みてなされたものである。すなわち本発明の目的は、黒色の遮光層を有しながらも表裏面の判別が容易な積層遮光フィルム、並びに、これを用いた光学機器用遮光リング、レンズユニット及びカメラモジュール等を提供することにある。 The present invention has been made in view of the above problems. That is, an object of the present invention is to provide a laminated light-shielding film that has a black light-shielding layer and can easily discriminate between the front and back surfaces, a light-shielding ring for optical equipment, a lens unit, a camera module, and the like using the same. is there.

本発明者らは、上記課題を解決するべく、人間工学的なアプローチから鋭意検討した。その結果、黒色の遮光層の６０度光沢度及び／又は明度指数Ｌ^*を異ならしめることで、さらに必要に応じて端面をメルクマールとして機能させることで、上記課題を解決できることを見出し、本発明を完成するに至った。 The present inventors diligently studied from an ergonomic approach to solve the above problems. As a result, it has been found that the above problem can be solved by making the end face function as a Merck Mar if necessary by making the 60 ° gloss and / or brightness index L ^* of the black light shielding layer different. It came to be completed.

すなわち、本発明は、以下に示す種々の具体的態様を提供する。
（１）第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度及び／又は明度指数Ｌ^*を有することを特徴とする、積層遮光フィルム。
（２）前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している、上記（１）に記載の積層遮光フィルム。 That is, the present invention provides various specific modes shown below.
(1) It has a laminated structure including at least a first black light shielding layer and a second black light shielding layer, and the first black light shielding layer and the second black light shielding layer have an optical density of 2.5 or more and 5.0. %, And the first black light-shielding layer has a 60-degree glossiness and / or a lightness index L ^* different from the second black light-shielding layer. the film.
(2) The first black light-shielding layer and / or the second black light-shielding layer has an inclined end face that widens the film width from the first black light-shielding layer toward the second black light-shielding layer, The laminated light-shielding film according to (1), wherein the inclined end face is exposed in a plan view as viewed from the normal direction of the main surface of the one black light-shielding layer.

（３）前記第一黒色遮光層の前記主面と前記傾斜端面とを結ぶ傾斜角が１０〜８７°である上記（１）又は（２）に記載の積層遮光フィルム。
（４）前記第一黒色遮光層と前記第二黒色遮光層の６０度光沢度の差が、１．０〜４．５％である上記（１）〜（３）のいずれか一項に記載の積層遮光フィルム。
（５）基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する上記（１）〜（４）のいずれか一項に記載の積層遮光フィルム。
（６）前記基材フィルムは、８０．０〜９９．９％の全光線透過率を有する上記（５）に記載の積層遮光フィルム。
（７）前記基材フィルムは、０．５μｍ以上、５０μｍ以下の厚みを有する上記（６）に記載の積層遮光フィルム。 (3) The laminated light-shielding film according to (1) or (2), wherein an inclination angle connecting the main surface of the first black light-shielding layer and the inclined end surface is 10 to 87 °.
(4) The difference in 60 degree glossiness between the first black light shielding layer and the second black light shielding layer is 1.0 to 4.5%, as described in any one of (1) to (3) above. Laminated light shielding film.
(5) At least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The laminated light-shielding film according to any one of (1) to (4), which has a laminated structure.
(6) The laminated light-shielding film according to (5), wherein the base film has a total light transmittance of 80.0 to 99.9%.
(7) The laminated light-shielding film according to (6), wherein the base film has a thickness of 0.5 μm or more and 50 μm or less.

（８）リング状の外形形状を有し、第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度及び／又は明度指数Ｌ^*を有する、光学機器用遮光リング。
（９）前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している上記（８）に記載の光学機器用遮光リング。
（１０）基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する上記（９）に記載の光学機器用遮光リング。 (8) It has a ring-shaped outer shape, has a laminated structure including at least a first black light shielding layer and a second black light shielding layer, and the first black light shielding layer and the second black light shielding layer are The first black light-shielding layer has an optical density of 5 or more and a 60-degree glossiness of 5.0% or less, and the first black light-shielding layer has a 60-degree glossiness and / or lightness index L ^* different from the second black light-shielding layer. A shading ring for optical equipment.
(9) The first black light-shielding layer and / or the second black light-shielding layer has an inclined end face that widens the film width from the first black light-shielding layer toward the second black light-shielding layer, The light shielding ring for an optical device according to (8), wherein the inclined end surface is exposed in a plan view as viewed from the normal direction of the main surface of the one black light shielding layer.
(10) At least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The light-shielding ring for optical devices according to (9), which has a laminated structure.

（１１）複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットであって、前記遮光板の少なくとも１以上が、上記（１）〜（７）のいずれか一項に記載の積層遮光フィルム、及び／又は、上記（８）〜（１０）のいずれか一項に記載の光学機器用遮光リングからなるレンズユニット。
（１２）複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットと、前記レンズユニットを通して被写体を撮像する撮像素子とを少なくとも有するカメラモジュールであって、前記遮光板の少なくとも１以上が、上記（１）〜（７）のいずれか一項に記載の積層遮光フィルム、及び／又は、上記（８）〜（１０）のいずれか一項に記載の光学機器用遮光リングからなるカメラモジュール。 (11) A lens unit in which a plurality of lenses and at least one light shielding plate are stacked in the optical axis direction of the lens, and at least one of the light shielding plates is any one of the above (1) to (7) A lens unit comprising the laminated light-shielding film according to claim 1 and / or the light-shielding ring for optical equipment according to any one of (8) to (10) above.
(12) A camera module, wherein the plurality of lenses and at least one light shielding plate include at least a lens unit stacked in the optical axis direction of the lens, and an imaging element that images a subject through the lens unit, At least 1 or more of a light-shielding plate is the laminated light-shielding film as described in any one of said (1)-(7), and / or the optical apparatus as described in any one of said (8)-(10). Camera module consisting of a shading ring.

本発明によれば、黒色の遮光層を有しながらも表裏判別が容易な、積層遮光フィルム及び光学機器用遮光リングを提供することができる。そしてこれら積層遮光フィルム及び光学機器用遮光リングを用いることで、モジュール製造現場における取扱性が向上され、部品管理の負担を軽減できる。そのため、組み込み不良等の製造故障の発生を抑制でき、歩留まりを向上させることができる。したがって、これらを用いたレンズユニット及びカメラモジュール等は、生産性及び経済性に優れたものとなる。 According to the present invention, it is possible to provide a laminated light-shielding film and an optical equipment light-shielding ring that have a black light-shielding layer and can be easily discriminated from the front and back. And by using these laminated light-shielding films and light-shielding rings for optical devices, the handleability at the module manufacturing site is improved, and the burden of component management can be reduced. For this reason, it is possible to suppress the occurrence of a manufacturing failure such as a built-in failure and to improve the yield. Accordingly, a lens unit, a camera module, and the like using these are excellent in productivity and economy.

一実施形態の積層遮光フィルム及びそのロール原反を模式的に示す断面図である。It is sectional drawing which shows typically the lamination light shielding film of one Embodiment, and its roll original fabric. 図１のＩＩ−ＩＩ断面図である。It is II-II sectional drawing of FIG. 一実施形態の積層遮光フィルムの平面図である。It is a top view of the lamination light shielding film of one embodiment. 一実施形態の光学機器用遮光リング（積層遮光フィルム）、並びに、これを用いたレンズユニット及びカメラモジュールを模式的に示す分解斜視図である。It is a disassembled perspective view which shows typically the light-shielding ring (laminated light shielding film) for optical devices of one Embodiment, and the lens unit and camera module using the same. 一実施形態の光学機器用遮光リング（積層遮光フィルム）を模式的に示す断面図である。It is sectional drawing which shows typically the light-shielding ring (laminate light-shielding film) for optical devices of one Embodiment.

以下、本発明の実施の形態について、図面を参照して詳細に説明する。なお、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。また、図面の寸法比率は、図示の比率に限定されるものではない。但し、以下の実施の形態は、本発明を説明するための例示であり、本発明はこれらに限定されるものではない。なお、本明細書において、例えば「１〜１００」との数値範囲の表記は、その上限値「１」及び下限値「１００」の双方を包含するものとする。また、他の数値範囲の表記も同様である。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. The positional relationship such as up, down, left, and right is based on the positional relationship shown in the drawings unless otherwise specified. Further, the dimensional ratios in the drawings are not limited to the illustrated ratios. However, the following embodiments are examples for explaining the present invention, and the present invention is not limited to these. In this specification, for example, the description of a numerical range of “1 to 100” includes both the upper limit value “1” and the lower limit value “100”. This also applies to other numerical range notations.

（第一実施形態）
図１は、本発明の第一実施形態の積層遮光フィルム１００及びその原反ロール２００を模式的に示す断面図であり、図２は、積層遮光フィルム１００の要部を示す断面図（図１のＩＩ−ＩＩ断面）である。図３は、積層遮光フィルム１００の平面図である。この積層遮光フィルム１００は、基材フィルム１１と、この基材フィルム１１の一方の主面１１ａ側に設けられた第一の黒色遮光層２１と、他方の主面１１ｂ側に設けられた第二の黒色遮光層３１とを少なくとも備える。そして、積層遮光フィルム１００は、黒色遮光層２１、基材フィルム１１、及び黒色遮光層３１が、少なくともこの順に配列された積層構造（３層構造）を有するものとなっている。そして、この積層遮光フィルム１００が有芯又は無芯のロール状に巻き取られることにより、巻回体たるロール原反２００が構成されている。 (First embodiment)
FIG. 1 is a cross-sectional view schematically showing a laminated light-shielding film 100 and an original fabric roll 200 of the first embodiment of the present invention, and FIG. 2 is a cross-sectional view showing the main part of the laminated light-shielding film 100 (FIG. 1). II-II cross section). FIG. 3 is a plan view of the laminated light shielding film 100. The laminated light-shielding film 100 includes a base film 11, a first black light-shielding layer 21 provided on one main surface 11 a side of the base film 11, and a second provided on the other main surface 11 b side. The black light shielding layer 31 is provided at least. The laminated light-shielding film 100 has a laminated structure (three-layer structure) in which the black light-shielding layer 21, the base film 11, and the black light-shielding layer 31 are arranged at least in this order. And the roll original fabric 200 which is a wound body is comprised by winding this laminated light-shielding film 100 in the shape of a core or uncore roll.

ここで本明細書において、「基材フィルムの一方（他方）の主面側に設けられた」とは、本実施形態のように基材フィルム１１の表面（例えば主面１１ａや主面１１ｂ）に黒色遮光層２１，３１が直接載置された態様のみならず、基材フィルム１１の表面と黒色遮光層２１，３１との間に任意の層（例えばプライマー層、接着層等）が介在した態様を包含する意味である。また、第一黒色遮光層２１、及び第二黒色遮光層３１を少なくとも備える積層構造とは、第一黒色遮光層２１及び第二黒色遮光層３１のみが直接積層した構造のみならず、上述した３層構造、及び、３層構造に任意の層をさらに設けた構造を包含する意味である。 Here, in this specification, “provided on one (other) main surface side of the base film” means the surface of the base film 11 (for example, the main surface 11a or the main surface 11b) as in this embodiment. In addition to the mode in which the black light-shielding layers 21 and 31 are directly mounted, any layer (for example, a primer layer, an adhesive layer, etc.) is interposed between the surface of the base film 11 and the black light-shielding layers 21 and 31. It is the meaning including an aspect. The laminated structure including at least the first black light shielding layer 21 and the second black light shielding layer 31 is not limited to the structure in which only the first black light shielding layer 21 and the second black light shielding layer 31 are directly laminated, The meaning includes a layer structure and a structure in which an arbitrary layer is further provided in a three-layer structure.

基材フィルム１１は、黒色遮光層２１，３１を支持可能なものである限り、その種類は特に限定されない。寸法安定性、機械的強度及び軽量化等の観点から、合成樹脂フィルムが好ましく用いられる。合成樹脂フィルムの具体例としては、ポリエステルフィルム、ＡＢＳ（アクリロニトリル−ブタジエン−スチレン）フィルム、ポリイミドフィルム、ポリスチレンフィルム、ポリカーボネートフィルム等が挙げられる。また、アクリル系、ポリオレフィン系、セルロース系、ポリスルホン系、ポリフェニレンスルフィド系、ポリエーテルスルホン系、ポリエーテルエーテルケトン系のフィルムを用いることもできる。これらの中でも、基材フィルム１１としては、ポリエステルフィルムが好適に用いられる。とりわけ、一軸又は二軸延伸フィルム、特に二軸延伸ポリエステルフィルムは、機械的強度及び寸法安定性に優れるため、特に好ましい。また、耐熱用途には、一軸又は二軸延伸ポリイミドフィルムが特に好ましい。これらは１種を単独で用いることができ、また２種以上を組み合わせて用いることもできる。 The type of the base film 11 is not particularly limited as long as it can support the black light shielding layers 21 and 31. From the viewpoints of dimensional stability, mechanical strength, weight reduction, etc., a synthetic resin film is preferably used. Specific examples of the synthetic resin film include a polyester film, an ABS (acrylonitrile-butadiene-styrene) film, a polyimide film, a polystyrene film, and a polycarbonate film. Acrylic, polyolefin, cellulose, polysulfone, polyphenylene sulfide, polyethersulfone, and polyetheretherketone films can also be used. Among these, a polyester film is preferably used as the base film 11. In particular, a uniaxially or biaxially stretched film, particularly a biaxially stretched polyester film is particularly preferable because of excellent mechanical strength and dimensional stability. For heat resistant applications, a uniaxial or biaxially stretched polyimide film is particularly preferable. These can be used individually by 1 type and can also be used in combination of 2 or more type.

基材フィルム１１の厚みは、要求性能及び用途に応じて適宜設定でき、特に限定されない。軽量化及び薄膜化の観点からは、基材フィルム１１の厚みは、０．５μｍ以上、５０μｍ以下が好ましく、より好ましくは１μｍ以上、２５μｍ以下、さらに好ましくは４μｍ以上、１０μｍ以下、特に好ましくは５μｍ以上、７μｍ以下である。なお、黒色遮光層２１，３１との接着性を向上させる観点から、必要に応じて、基材フィルム１１表面にアンカー処理やコロナ処理等の各種公知の表面処理を行うこともできる。 The thickness of the base film 11 can be appropriately set according to required performance and application, and is not particularly limited. From the viewpoint of weight reduction and thinning, the thickness of the base film 11 is preferably 0.5 μm or more and 50 μm or less, more preferably 1 μm or more and 25 μm or less, further preferably 4 μm or more and 10 μm or less, and particularly preferably 5 μm. As described above, it is 7 μm or less. In addition, from a viewpoint of improving adhesiveness with the black light shielding layers 21 and 31, various well-known surface treatments, such as an anchor process and a corona treatment, can also be performed to the base film 11 surface as needed.

基材フィルム１１の外周側面（外周端面）には、傾斜端面１２が設けられている。この傾斜端面１２によって、基材フィルム１１の断面構造は、下底が上底よりも長い台形状となっており、基材フィルム１１のフィルム幅は、黒色遮光層２１から黒色遮光層３１に向けて拡開された構造となっている（図２参照）。 An inclined end surface 12 is provided on the outer peripheral side surface (outer peripheral end surface) of the base film 11. Due to the inclined end surface 12, the cross-sectional structure of the base film 11 has a trapezoidal shape in which the lower base is longer than the upper base, and the film width of the base film 11 is directed from the black light shielding layer 21 to the black light shielding layer 31. Thus, the structure is expanded (see FIG. 2).

この傾斜端面１２は、基材フィルム１１を図２に示すように平坦状態にしたとき、基材フィルム１１の主面１１ａ側から視認可能となるように、基材フィルム１１の主面１１ａの法線方向からの平面視で露出するように設けられている（図３参照）。具体的には、基材フィルム１１の主面１１ａと傾斜端面１２とを結ぶ傾斜角θ（俯角θ）が１０〜８７°となるように設定されている。主面１１ａ側からの平面視における傾斜端面１２の視認性を向上させ、基材フィルム１１端面の強度を維持し、生産性を維持する等の観点から、傾斜角θは３０〜８５°が好ましく、４０〜８３°がより好ましく、４５〜８０°がさらに好ましい。なお、傾斜端面１２が基材フィルム１１の主面１１ａ側から視認可能である限り、例えばフィルム端面強化のために、傾斜端面１２に透明乃至半透明の保護層等が設けられていてもよい。 The inclined end surface 12 is a method of the main surface 11a of the base film 11 so that the base film 11 is visible from the main surface 11a side of the base film 11 when the base film 11 is made flat as shown in FIG. It is provided so as to be exposed in plan view from the line direction (see FIG. 3). Specifically, the inclination angle θ (the depression angle θ) connecting the main surface 11a of the base film 11 and the inclined end surface 12 is set to be 10 to 87 °. In view of improving the visibility of the inclined end surface 12 in a plan view from the main surface 11a side, maintaining the strength of the end surface of the base film 11 and maintaining productivity, the inclination angle θ is preferably 30 to 85 °. 40 to 83 ° is more preferable, and 45 to 80 ° is more preferable. In addition, as long as the inclined end surface 12 is visible from the main surface 11a side of the base film 11, for example, a transparent or semi-transparent protective layer may be provided on the inclined end surface 12 in order to strengthen the film end surface.

なお、基材フィルム１１の外観は、透明、半透明、不透明のいずれであってもよく、特に限定されない。例えば発泡ポリエステルフィルム等の発泡した合成樹脂フィルムや、カーボンブラック等の黒色顔料や他の顔料を含有させた合成樹脂フィルムを用いることもできる。主面１１ａ側からの平面視における傾斜端面１２の視認性を向上させる観点からは、基材フィルム１１は、８０．０〜９９．９％の全光線透過率を有することが好ましく、より好ましくは８３．０〜９９．０％、さらに好ましくは８５．０〜９９．０％である。 The appearance of the base film 11 may be transparent, translucent, or opaque, and is not particularly limited. For example, a foamed synthetic resin film such as a foamed polyester film, or a synthetic resin film containing a black pigment such as carbon black or other pigments may be used. From the viewpoint of improving the visibility of the inclined end surface 12 in a plan view from the main surface 11a side, the base film 11 preferably has a total light transmittance of 80.0 to 99.9%, more preferably. It is 83.0-99.0%, More preferably, it is 85.0-99.0%.

黒色遮光層２１，３１は、２．５以上の光学濃度（ＯＤ）及び５．０％以下の６０度光沢度（Ｇ６０）を有する遮光膜である。
なお、本明細書において、光学濃度（ＯＤ）は、ＪＩＳ−Ｋ７６５１：１９８８に準拠し、光学濃度計（ＴＤ−９０４：グレタグマクベス社）及びＵＶフィルターを用いて測定して得られた値とする。より高い遮光性を具備させる観点から、黒色遮光層２１，３１は、それぞれ単層で２．７以上の光学濃度（ＯＤ）を有することが好ましい。また、黒色遮光層２１，３１を積層させた場合、その積層体の光学濃度（ＯＤ）は、４．５〜６．０が好ましく、より好ましくは５．０〜６．０である。
また、６０度光沢度は、ＪＩＳ−Ｚ８７４１：１９９７に準拠し、デジタル変角光沢計（UGV-5K：スガ試験機社製）を用い入射受光角６０°における黒色遮光層２１，３１表面の光沢度（鏡面光沢度）（％）を測定して得られた値とする。入射光の反射を抑制し、光吸収性を高める観点から、黒色遮光層２１，３１は、３．０％以下の６０度光沢度を有することが好ましく、より好ましくは１．０％である。 The black light shielding layers 21 and 31 are light shielding films having an optical density (OD) of 2.5 or more and a 60 degree glossiness (G60) of 5.0% or less.
In the present specification, the optical density (OD) is a value obtained by measurement using an optical densitometer (TD-904: Gretag Macbeth) and a UV filter in accordance with JIS-K7651: 1988. . From the viewpoint of providing higher light-shielding properties, the black light-shielding layers 21 and 31 preferably each have a single layer optical density (OD) of 2.7 or higher. Moreover, when the black light shielding layers 21 and 31 are laminated, the optical density (OD) of the laminated body is preferably 4.5 to 6.0, more preferably 5.0 to 6.0.
The 60 degree glossiness is based on JIS-Z8741: 1997, and the gloss of the surfaces of the black light shielding layers 21 and 31 at an incident light receiving angle of 60 ° using a digital variable glossmeter (UGV-5K: manufactured by Suga Test Instruments Co., Ltd.). The value obtained by measuring the degree (specular gloss) (%). From the viewpoint of suppressing reflection of incident light and improving light absorption, the black light shielding layers 21 and 31 preferably have a 60 ° gloss of 3.0% or less, and more preferably 1.0%.

２．５以上の光学濃度及び５．０％以下の６０度光沢度を有する遮光膜としては、当業界で公知のものを用いることができ、その種類は特に限定されない。例えば黒色系の遮光膜としては、バインダー樹脂及び黒色顔料を少なくとも含有する黒色遮光膜が好ましく用いられる。以下、この黒色遮光膜を例に挙げて、詳述する。 As the light-shielding film having an optical density of 2.5 or more and a glossiness of 60 degrees of 5.0% or less, those known in the art can be used, and the kind thereof is not particularly limited. For example, as the black light shielding film, a black light shielding film containing at least a binder resin and a black pigment is preferably used. Hereinafter, the black light shielding film will be described in detail as an example.

バインダー樹脂としては、ポリ（メタ）アクリル酸系樹脂、ポリエステル系樹脂、ポリ酢酸ビニル系樹脂、ポリ塩化ビニル系樹脂、ポリビニルブチラール系樹脂、セルロース系樹脂、ポリスチレン／ポリブタジエン樹脂、ポリウレタン系樹脂、アルキド樹脂、アクリル系樹脂、不飽和ポリエステル系樹脂、エポキシエステル系樹脂、エポキシ系樹脂、エポキシアクリレート系樹脂、ウレタンアクリレート系樹脂、ポリエステルアクリレート系樹脂、ポリエーテルアクリレート系樹脂、フェノール系樹脂、メラミン系樹脂、尿素系樹脂、ジアリルフタレート系樹脂等の熱可塑性樹脂又は熱硬化性樹脂が挙げられるが、これらに特に限定されない。また、熱可塑性エラストマー、熱硬化性エラストマー、紫外線硬化型樹脂、電子線硬化型樹脂等も用いることができる。これらは１種を単独で用いることができ、また２種以上を組み合わせて用いることもできる。なお、バインダー樹脂は、要求性能及び用途に応じて、適宜選択して用いることができる。例えば、耐熱性が求められる用途においては、熱硬化性樹脂が好ましい。 Binder resins include poly (meth) acrylic acid resins, polyester resins, polyvinyl acetate resins, polyvinyl chloride resins, polyvinyl butyral resins, cellulose resins, polystyrene / polybutadiene resins, polyurethane resins, alkyd resins. , Acrylic resins, unsaturated polyester resins, epoxy ester resins, epoxy resins, epoxy acrylate resins, urethane acrylate resins, polyester acrylate resins, polyether acrylate resins, phenol resins, melamine resins, urea Thermoplastic resins or thermosetting resins such as a series resin and a diallyl phthalate series resin are exemplified, but not limited thereto. Further, thermoplastic elastomers, thermosetting elastomers, ultraviolet curable resins, electron beam curable resins, and the like can also be used. These can be used individually by 1 type and can also be used in combination of 2 or more type. In addition, binder resin can be suitably selected and used according to a required performance and a use. For example, in applications where heat resistance is required, thermosetting resins are preferred.

黒色遮光層２１，３１中のバインダー樹脂の含有量（総量）は、特に限定されないが、接着性、遮光性、耐傷付性、摺動性及び艶消し性等の観点から、４０〜９０質量％が好ましく、より好ましくは５０〜８５質量％、さらに好ましくは６０〜８０質量％である。 The content (total amount) of the binder resin in the black light-shielding layers 21 and 31 is not particularly limited, but is 40 to 90% by mass from the viewpoint of adhesiveness, light-shielding properties, scratch resistance, slidability, and matte properties. Is preferable, more preferably 50 to 85% by mass, still more preferably 60 to 80% by mass.

黒色顔料は、バインダー樹脂を黒色に着色して遮光性を付与するものである。黒色顔料の具体例としては、例えば、黒色樹脂粒子、チタンブラック、マグネタイト系ブラック、銅・鉄・マンガン系ブラック、チタンブラック、カーボンブラック等が挙げられるが、これらに特に限定されない。これらの中でも、隠蔽性に優れることから、黒色樹脂粒子、チタンブラック、カーボンブラックが好ましく、より好ましくはカーボンブラックである。これらは１種を単独で用いることができ、また２種以上を組み合わせて用いることもできる。 The black pigment imparts light shielding properties by coloring the binder resin black. Specific examples of the black pigment include, but are not limited to, black resin particles, titanium black, magnetite black, copper / iron / manganese black, titanium black, carbon black, and the like. Among these, black resin particles, titanium black, and carbon black are preferable because of excellent concealability, and carbon black is more preferable. These can be used individually by 1 type and can also be used in combination of 2 or more type.

カーボンブラックとしては、オイルファーネスブラック、ランプブラック、チャンネルブラック、ガスファーネスブラック、アセチレンブラック、サーマルブラック、ケッチェンブラック等、各種公知の製法で作製されたものが知られているが、その種類は特に制限されない。黒色遮光層２１，３１に導電性を付与し静電気による帯電を防止する観点から、導電性カーボンブラックが特に好ましく用いられる。カーボンブラックの歴史は古く、例えば三菱化学株式会社、旭カーボン株式会社、御国色素株式会社、レジノカラー社、Ｃａｂｏｔ社、ＤＥＧＵＳＳＡ社等から、各種グレードのカーボンブラック単体及びカーボンブラック分散液が市販されており、要求性能や用途に応じて、これらの中から適宜選択すればよい。なお、カーボンブラックの粒子サイズは、要求性能等に応じて適宜設定でき、特に限定されない。カーボンブラックの平均粒子径Ｄ₅₀は、０．０１〜２．０μｍであることが好ましく、より好ましくは０．０５〜０．１．０μｍ、さらに好ましくは０．０８〜０．５μｍである。なお、本明細書における平均粒子径とは、レーザー回折式粒度分布測定装置（例えば、島津製作所社：ＳＡＬＤ−７０００等）で測定される、体積基準のメジアン径（Ｄ₅₀）を意味する。 As carbon black, oil furnace black, lamp black, channel black, gas furnace black, acetylene black, thermal black, ketjen black, etc., which are produced by various known production methods are known, but the type is particularly Not limited. From the viewpoint of imparting conductivity to the black light-shielding layers 21 and 31 and preventing electrostatic charging, conductive carbon black is particularly preferably used. Carbon black has a long history, and various grades of carbon black and carbon black dispersions are commercially available from, for example, Mitsubishi Chemical Corporation, Asahi Carbon Corporation, Mikuni Dye Co., Ltd., Resino Color Corporation, Cabot Corporation, DEGUSSA Corporation, etc. Depending on the required performance and application, these may be selected as appropriate. The particle size of carbon black can be set as appropriate according to required performance and is not particularly limited. The average particle diameter D ₅₀ of carbon black is preferably 0.01 to 2.0 μm, more preferably 0.05 to 0.10 μm, and still more preferably 0.08 to _0.5 μm. The average particle diameter in the present specification means a volume-based median diameter (D ₅₀ ) measured by a laser diffraction particle size distribution measuring apparatus (for example, Shimadzu Corporation: SALD-7000).

黒色遮光層２１，３１中の黒色顔料の含有量（総量）は、特に限定されないが、分散性、製膜性、取扱性、接着性、滑り性、艶消し性、耐磨耗性等の観点から、黒色遮光層２１，３１中に含まれる全樹脂成分に対する固形分換算（ｐｈｒ）で、１０〜６０質量％であることが好ましく、より好ましくは１５〜５０質量％であり、さらに好ましくは２０〜４０質量％である。 The content (total amount) of the black pigment in the black light-shielding layers 21 and 31 is not particularly limited. From the viewpoints of dispersibility, film-forming property, handleability, adhesiveness, slipperiness, matteness, abrasion resistance, and the like. Therefore, it is preferably 10 to 60% by mass, more preferably 15 to 50% by mass, and still more preferably 20 in terms of solid content (phr) with respect to all resin components contained in the black light shielding layers 21 and 31. -40 mass%.

黒色遮光層２１，３１の厚みは、要求性能及び用途に応じて適宜設定でき、特に限定されない。高い光学濃度、軽量化及び薄膜化の観点からは、黒色遮光層２１，３１の厚みは、それぞれ０．１μｍ以上が好ましく、より好ましくは０．２μｍ以上、さらに好ましくは０．５μｍ以上、特に好ましくは１μｍ以上であり、上限側は１５μｍ以下が好ましく、より好ましくは１２μｍ以下、さらに好ましくは９μｍ以下、特に好ましくは６μｍ以下である。 The thickness of the black light shielding layers 21 and 31 can be appropriately set according to the required performance and application, and is not particularly limited. From the viewpoint of high optical density, weight reduction, and thinning, the thickness of the black light shielding layers 21 and 31 is preferably 0.1 μm or more, more preferably 0.2 μm or more, still more preferably 0.5 μm or more, and particularly preferably. Is 1 μm or more, and the upper limit is preferably 15 μm or less, more preferably 12 μm or less, still more preferably 9 μm or less, and particularly preferably 6 μm or less.

本実施形態の積層遮光フィルム１００においては、人間工学的なアプローチから、黒色遮光層２１と黒色遮光層３１が異なる６０度光沢度（Ｇ６０）及び／又は明度指数Ｌ^*を有するように構成した点に１つの特徴がある。このように６０度光沢度及び／又は明度指数Ｌ^*を異ならしめることで、その光沢感、艶、又は明度の差に基づいて、非接触すなわち目視で、積層遮光フィルム１００の表裏の判別が可能となる。
このとき、黒色遮光層２１の６０度光沢度と黒色遮光層３１の６０度光沢度との差は、判別性や黒色度（遮光性）のバランスを考慮して適宜設定すればよく、特に限定されないが、１．０〜４．５％であることが好ましく、より好ましくは１．５〜４．０％、さらに好ましくは２．０〜３．０％である。このような６０度光沢度の差を設けるには、例えば、黒色遮光層２１の６０度光沢度を１．０〜５．０とし、黒色遮光層３１の６０度光沢度を０．１〜０．９とすればよい。
また、明度の差は、ＣＩＥ１９７６Ｌ^*ａ^*ｂ^*表色系における明度指数Ｌ^*で表すことができ、明度指数Ｌ^*の差は１〜２０であることが好ましく、より好ましくは２〜１５、さらに好ましくは３〜１０である。 In the laminated light-shielding film 100 of the present embodiment, the black light-shielding layer 21 and the black light-shielding layer 31 are configured to have different 60 degree glossiness (G60) and / or lightness index L ^* from an ergonomic approach. There is one feature. Thus, by making the 60 degree glossiness and / or the brightness index L ^* different, the front and back sides of the laminated light-shielding film 100 can be discriminated in a non-contact manner, that is, visually, based on the difference in glossiness, gloss, or brightness. It becomes.
At this time, the difference between the 60-degree glossiness of the black light-shielding layer 21 and the 60-degree glossiness of the black light-shielding layer 31 may be appropriately set in consideration of the balance between discriminability and blackness (light-shielding property), and is particularly limited. However, it is preferably 1.0 to 4.5%, more preferably 1.5 to 4.0%, and still more preferably 2.0 to 3.0%. In order to provide such a difference in 60 degree glossiness, for example, the 60 degree glossiness of the black light shielding layer 21 is set to 1.0 to 5.0, and the 60 degree glossiness of the black light shielding layer 31 is set to 0.1 to 0. .9.
The lightness difference can be represented by the lightness index L ^* in the CIE 1976 L ^* a ^* b ^* color system, and the lightness index L ^* difference is preferably 1 to 20, more preferably 2 to 2. 15, more preferably 3-10.

黒色遮光層２１と黒色遮光層３１の６０度光沢度及び／又は明度指数Ｌ^*の調整方法としては、例えば、黒色遮光層２１と黒色遮光層３１とで黒色顔料の含有量を相違させる方法、黒色遮光層２１と黒色遮光層３１とで黒色度の異なる黒色顔料を用いる方法、黒色遮光層２１と黒色遮光層３１とで大きさの異なる黒色顔料を用いる方法、黒色遮光層２１と黒色遮光層３１とで表面粗さを相違させる方法、黒色遮光層２１と黒色遮光層３１とで色相の異なるバインダー樹脂を用いる方法等があるが、これらに特に限定されない。また、遮光膜に用いられる各種公知の添加剤を配合することで、明度、色相、及び／又は彩度を調整することも可能である。これらの調整方法は、各種の方法をそれぞれ単独で又は適宜組み合わせて行うことができる。 As a method for adjusting the 60 degree glossiness and / or the lightness index L ^* of the black light shielding layer 21 and the black light shielding layer 31, for example, a method of making the black pigment content different between the black light shielding layer 21 and the black light shielding layer 31, A method using a black pigment having a different blackness between the black light shielding layer 21 and the black light shielding layer 31, a method using a black pigment having a different size between the black light shielding layer 21 and the black light shielding layer 31, and the black light shielding layer 21 and the black light shielding layer. There are a method of making the surface roughness different from that of 31 and a method of using a binder resin having a different hue between the black light shielding layer 21 and the black light shielding layer 31, but are not particularly limited thereto. It is also possible to adjust the brightness, hue, and / or saturation by blending various known additives used for the light-shielding film. These adjustment methods can be carried out by combining various methods individually or in appropriate combination.

黒色遮光層２１，３１の外周側面には、上述した傾斜端面１２に対応する傾斜角θを有する傾斜端面２２，３２（外周端面２２，３２）が両側面（２箇所）に設けられている。これらの傾斜端面２２，３２は、黒色遮光層２１，３１を図２に示すように平坦状態にしたとき、黒色遮光層２１の主面２１ａ側から視認可能となるように、黒色遮光層２１の主面２１ａの法線方向からの平面視で露出するように設けられている（図３参照）。具体的には、黒色遮光層２１の主面２１ａと傾斜端面２２，３２とを結ぶ傾斜角θが１０〜８７°となるように設定されている。なお、傾斜端面２２，３２が黒色遮光層２１の主面２１ａ側から視認可能である限り、例えばフィルム端面強化のために、傾斜端面２２，３２に透明乃至半透明の保護層等が設けられていてもよい。このように構成し、基材フィルム１１と黒色遮光層２１，３１との色相、彩度、明度、透明度、６０度光沢度、全光線透過率等の相違を利用することにより、黒色遮光層２１，３１の判別性がさらに向上する。ここで、傾斜端面２２，３２の傾斜角θは、特に限定されないが、傾斜端面１２と同様に１０〜８７°が好ましく、より好ましくは３５〜８５°、さらに好ましくは４０〜８３°、特に好ましくは４５〜８０°である。傾斜端面１２と同一又は同程度の傾斜角に設定することで、端面強度を高く維持し易い傾向にあり、また、生産性が向上され易い傾向にある。 On the outer peripheral side surfaces of the black light shielding layers 21 and 31, inclined end surfaces 22 and 32 (outer peripheral end surfaces 22 and 32) having an inclination angle θ corresponding to the inclined end surface 12 described above are provided on both side surfaces (two locations). These inclined end faces 22 and 32 are formed on the black light shielding layer 21 so that the black light shielding layers 21 and 31 are visible from the main surface 21a side of the black light shielding layer 21 when the black light shielding layers 21 and 31 are in a flat state as shown in FIG. It is provided so as to be exposed in plan view from the normal direction of the main surface 21a (see FIG. 3). Specifically, the inclination angle θ connecting the main surface 21a of the black light shielding layer 21 and the inclined end faces 22 and 32 is set to be 10 to 87 °. As long as the inclined end surfaces 22 and 32 are visible from the main surface 21a side of the black light-shielding layer 21, for example, a transparent or translucent protective layer is provided on the inclined end surfaces 22 and 32 in order to strengthen the film end surface. May be. The black light-shielding layer 21 is configured as described above and uses the difference in hue, saturation, lightness, transparency, 60-degree glossiness, total light transmittance, and the like between the base film 11 and the black light-shielding layers 21 and 31. , 31 is further improved. Here, the inclination angle θ of the inclined end faces 22 and 32 is not particularly limited, but is preferably 10 to 87 °, more preferably 35 to 85 °, still more preferably 40 to 83 °, particularly preferably the same as the inclined end face 12. Is 45 to 80 °. By setting the inclination angle to be the same as or similar to that of the inclined end face 12, the end face strength tends to be maintained high, and the productivity tends to be improved.

なお、黒色遮光層２１，３１は、当業界で公知の各種添加剤を含有していてもよい。その具体例としては、マット剤（艶消し剤）、滑剤、導電剤、難燃剤、抗菌剤、防カビ剤、酸化防止剤、可塑剤、レベリング剤、流動調整剤、消泡剤、分散剤等が挙げられるが、これらに特に限定されない。マット剤としては、架橋ポリメチルメタクリレート粒子、架橋ポリスチレン粒子等の有機系微粒子、シリカ、メタケイ酸アルミン酸マグネシウム、酸化チタン等の無機系微粒子等が挙げられるが、これらに特に限定されない。滑剤としては、ポリエチレン、パラフィン、ワックス等の炭化水素系滑剤；ステアリン酸、１２−ヒドロキシステアリン酸等の脂肪酸系滑剤；ステアリン酸アミド、オレイン酸アミド、エルカ酸アミド等のアミド系滑剤；ステアリン酸ブチル、ステアリン酸モノグリセリド等のエステル系滑剤；アルコール系滑剤；金属石鹸、滑石、二硫化モリブデン等の固体潤滑剤；シリコーン樹脂粒子、ポリテトラフッ化エチレンワックス、ポリフッ化ビニリデン等のフッ素樹脂粒子等が挙げられるが、これらに特に限定されない。これらの中でも、特に有機系滑剤が好ましく用いられる。また、バインダー樹脂として、紫外線硬化型樹脂や電子線硬化型樹脂を用いる場合には、例えばｎ−ブチルアミン、トリエチルアミン、トリ−ｎ−ブチルホスフィン等の増感剤や紫外線吸収剤等を用いてもよい。これらは１種を単独で用いることができ、また２種以上を組み合わせて用いることもできる。これらの含有割合は、特に限定されないが、黒色遮光層２１，３１中に含まれる全樹脂成分に対する固形分換算で、一般的にはそれぞれ０．０１〜５質量％であることが好ましい。 The black light shielding layers 21 and 31 may contain various additives known in the art. Specific examples include matting agents (matting agents), lubricants, conductive agents, flame retardants, antibacterial agents, fungicides, antioxidants, plasticizers, leveling agents, flow regulators, antifoaming agents, dispersing agents, etc. However, it is not particularly limited to these. Examples of the matting agent include organic fine particles such as crosslinked polymethyl methacrylate particles and crosslinked polystyrene particles, inorganic fine particles such as silica, magnesium aluminate metasilicate, and titanium oxide, but are not particularly limited thereto. Lubricants include hydrocarbon lubricants such as polyethylene, paraffin and wax; fatty acid lubricants such as stearic acid and 12-hydroxystearic acid; amide lubricants such as stearic acid amide, oleic acid amide and erucic acid amide; butyl stearate And ester lubricants such as stearic acid monoglyceride; alcohol lubricants; solid lubricants such as metal soaps, talc and molybdenum disulfide; fluororesin particles such as silicone resin particles, polytetrafluoroethylene wax, and polyvinylidene fluoride. However, it is not particularly limited to these. Of these, organic lubricants are particularly preferably used. Further, when an ultraviolet curable resin or an electron beam curable resin is used as the binder resin, for example, a sensitizer such as n-butylamine, triethylamine, or tri-n-butylphosphine, an ultraviolet absorber, or the like may be used. . These can be used individually by 1 type and can also be used in combination of 2 or more type. Although these content rates are not specifically limited, Generally it is preferable that it is 0.01-5 mass% in conversion of solid content with respect to all the resin components contained in the black light shielding layers 21 and 31, respectively.

また、黒色遮光層２１，３１は、１０．０％以下の可視光反射率を有することが好ましい。ここで可視光反射率とは、分光光度計（島津製作所社製、分光光度計SolidSpec-3700等）及び標準板として硫酸バリウムとを用い、黒色遮光層２１，３１に対して入射角８°で光を入射したときの、相対全光線反射率を意味する。より高い遮光性を具備させる等の観点から、黒色遮光層２１，３１の可視光反射率は、８％以下がより好ましく、さらに好ましくは６％以下、特に好ましくは４％以下である。なお、黒色遮光層２１，３１の判別性を高める観点からは、黒色遮光層２１と黒色遮光層３１の可視光反射率の差は１％であることが好ましい。また、積層遮光フィルム１００としては、可視光以外の赤外（８００〜１０００ｎｍ）範囲の拡散反射率が、１０％以下であることが好ましく、より好ましくは８％以下、さらに好ましくは６％以下、特に好ましくは４％以下である。 Moreover, it is preferable that the black light shielding layers 21 and 31 have a visible light reflectance of 10.0% or less. Here, the visible light reflectance is a spectrophotometer (manufactured by Shimadzu Corporation, spectrophotometer SolidSpec-3700, etc.) and barium sulfate as a standard plate, and an incident angle of 8 ° with respect to the black light shielding layers 21 and 31. This means the relative total light reflectance when light is incident. From the viewpoint of providing higher light shielding properties, the visible light reflectance of the black light shielding layers 21 and 31 is more preferably 8% or less, further preferably 6% or less, and particularly preferably 4% or less. In addition, from the viewpoint of improving the discrimination between the black light shielding layers 21 and 31, the difference in visible light reflectance between the black light shielding layer 21 and the black light shielding layer 31 is preferably 1%. The laminated light-shielding film 100 preferably has a diffuse reflectance in the infrared (800 to 1000 nm) range other than visible light of 10% or less, more preferably 8% or less, and even more preferably 6% or less. Particularly preferably, it is 4% or less.

さらに、黒色遮光層２１，３１は、十分な帯電防止性能を具備させる観点から、１．０×１０⁸Ω未満の表面抵抗率を有することが好ましく、より好ましくは１．０×１０⁵Ω未満、さらに好ましくは５．０×１０⁴Ω未満である。なお、本明細書において、表面抵抗率は、ＪＩＳ−Ｋ６９１１：１９９５に準拠して測定される値とする。 Further, the black light shielding layers 21 and 31 preferably have a surface resistivity of less than 1.0 × 10 ⁸ Ω, more preferably less than 1.0 × 10 ⁵ Ω, from the viewpoint of providing sufficient antistatic performance. More preferably, it is less than 5.0 × 10 ⁴ Ω. In this specification, the surface resistivity is a value measured according to JIS-K6911: 1995.

積層遮光フィルム１００の製造方法は、上述した構成のものが得られる限り、特に限定されない。基材フィルム１１上に黒色遮光層２１，３１を再現性よく簡易且つ低コストで製造する観点からは、ドクターコート、ディップコート、ロールコート、バーコート、ダイコート、ブレードコート、エアナイフコート、キスコート、スプレーコート、スピンコート等の従来公知の塗布方法が好適に用いられる。 The manufacturing method of the laminated light-shielding film 100 is not particularly limited as long as the above-described configuration can be obtained. From the viewpoint of manufacturing the black light-shielding layers 21 and 31 on the base film 11 with good reproducibility and at low cost, doctor coat, dip coat, roll coat, bar coat, die coat, blade coat, air knife coat, kiss coat, spray Conventionally known coating methods such as coating and spin coating are preferably used.

例えば、上述したバインダー樹脂及び黒色顔料、並びに必要に応じて配合される任意成分としての添加剤を溶媒中に含有する塗布液を、基材フィルム１１の主面上に塗布し、乾燥させた後、必要に応じて熱処理や加圧処理等を行うことにより、基材フィルム１１上に黒色遮光層２１，３１を製膜できる。ここで使用する塗布液の溶媒としては、水；メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶剤；酢酸メチル、酢酸エチル、酢酸ブチル等のエステル系溶剤；メチルセロソルブ、エチルセロソルブ等のエーテル系溶剤；メチルアルコール、エチルアルコール、イソプロピルアルコール等のアルコール系溶剤、並びにこれらの混合溶媒等を用いることができる。なお、基材フィルム１１と黒色遮光層２１，３１との接着を向上させるため、必要に応じてアンカー処理やコロナ処理等を行うこともできる。さらに、必要に応じて、基材フィルム１１と黒色遮光層２１，３１との間にプライマー層や接着層等の中間層を設けることもできる。なお、圧縮成形、射出成形、ブロー成形、トランスファ成形、押出成形等の各種公知の成形方法により、所望形状を有する積層遮光フィルム１００を簡易に得ることもできる。また、一旦シート状に成形した後、真空成形や圧空成形等を行うこともできる。 For example, after applying the above-described binder resin and black pigment, and a coating solution containing an additive as an optional component blended in if necessary on the main surface of the base film 11 and drying it The black light-shielding layers 21 and 31 can be formed on the base film 11 by performing heat treatment or pressure treatment as necessary. The solvent of the coating solution used here is water; ketone solvents such as methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone; ester solvents such as methyl acetate, ethyl acetate and butyl acetate; ether solvents such as methyl cellosolve and ethyl cellosolve Alcohol solvents such as methyl alcohol, ethyl alcohol, isopropyl alcohol, and mixed solvents thereof can be used. In addition, in order to improve adhesion | attachment with the base film 11 and the black light shielding layers 21 and 31, an anchor process, a corona treatment, etc. can also be performed as needed. Furthermore, an intermediate layer such as a primer layer or an adhesive layer may be provided between the base film 11 and the black light shielding layers 21 and 31 as necessary. The laminated light-shielding film 100 having a desired shape can be easily obtained by various known molding methods such as compression molding, injection molding, blow molding, transfer molding, and extrusion molding. Moreover, after forming into a sheet form once, vacuum forming, pressure forming, etc. can also be performed.

また、傾斜端面１２，２２，３２の形成方法についても、特に限定されない。各種公知の手法を適宜適用して、任意の傾斜角θを有する傾斜端面１２，２２，３２を作成することができる。例えば、基材フィルム１１上に黒色遮光層２１及び黒色遮光層３１を設けた積層遮光フィルムを用意し、その外周側面を上述した傾斜角θで切り落とす（裁断する）ことで、傾斜端面１２，２２，３２を簡易に設けることができる。また、傾斜端面２２，３２が不要な場合は、任意の傾斜角θを有する傾斜端面１２を予め設けた基材フィルム１１を用意し、この基材フィルム１１上に黒色遮光層２１及び黒色遮光層３１を設ければよい。 Also, the method for forming the inclined end faces 12, 22, 32 is not particularly limited. By applying various known methods as appropriate, the inclined end faces 12, 22, and 32 having an arbitrary inclination angle θ can be created. For example, by preparing a laminated light-shielding film in which the black light-shielding layer 21 and the black light-shielding layer 31 are provided on the base film 11, and cutting off (cutting) the outer peripheral side surface at the above-described inclination angle θ, the inclined end surfaces 12, 22 , 32 can be provided easily. When the inclined end surfaces 22 and 32 are unnecessary, a base film 11 provided with the inclined end surface 12 having an arbitrary inclination angle θ is prepared in advance, and the black light shielding layer 21 and the black light shielding layer are provided on the base film 11. 31 may be provided.

（作用）
本実施形態の積層遮光フィルム１００及び原反ロール２００においては、２．５以上の光学濃度及び５．０％以下の６０度光沢度を有する第一黒色遮光層２１と第二黒色遮光層３１を採用している。そのため、これをレンズユニットやカメラモジュール等の光学機器用遮光部材として用いることで、不要な入射光や反射光を除去することができ、ハレーション、レンズフレア、ゴースト等の発生を防止でき、撮像画像の画質を向上させることができる。 (Function)
In the laminated light-shielding film 100 and the original fabric roll 200 of the present embodiment, the first black light-shielding layer 21 and the second black light-shielding layer 31 having an optical density of 2.5 or more and a 60 degree gloss of 5.0% or less are provided. Adopted. Therefore, by using this as a light-shielding member for optical devices such as lens units and camera modules, unnecessary incident light and reflected light can be removed, occurrence of halation, lens flare, ghost, etc. can be prevented, and the captured image Image quality can be improved.

しかも、第一黒色遮光層２１と第二黒色遮光層３１とが、異なる６０度光沢度及び／又は明度指数Ｌ^*を有するため、その光沢感、艶、又は明度の差に基づいて、非接触すなわち目視で、表裏面の判別を容易に行うことができる。また、平面視で視認可能に露出した傾斜端面１２は、フィルム外周縁において、光沢感のある輝部として認知可能であるため、非接触すなわち目視で積層遮光フィルム１００の表裏面の判別を、格別容易に行うことができる。これは、第一黒色遮光層２１や第二黒色遮光層３１と傾斜端面１２（基材フィルム１１）との、色相、彩度、明度、透明度、６０度光沢度、全光線透過率等の相違に起因する。 In addition, since the first black light-shielding layer 21 and the second black light-shielding layer 31 have different 60 degree glossiness and / or brightness index L ^* , non-contact based on the difference in glossiness, gloss, or brightness. That is, the front and back surfaces can be easily discriminated visually. Further, since the inclined end surface 12 exposed so as to be visible in a plan view can be recognized as a bright portion having a glossy feeling at the outer peripheral edge of the film, the discrimination between the front and back surfaces of the laminated light-shielding film 100 can be performed without contact, that is, visually. It can be done easily. This is the difference in hue, saturation, lightness, transparency, 60-degree glossiness, total light transmittance, etc. between the first black light-shielding layer 21 and the second black light-shielding layer 31 and the inclined end surface 12 (base film 11). caused by.

また、本実施形態の積層遮光フィルム１００及び原反ロール２００を暗所で取り扱う場合にも、傾斜端面１２は有効に機能する。すなわち、傾斜端面１２（基材フィルム１１）は、第一黒色遮光層２１や第二黒色遮光層３１との相違に起因して、僅かな光であっても光沢感のある輝部として明瞭に認知可能である。また、傾斜端面１２を指等で直接触れ、その傾斜方向を確認することで、表裏面の判別を行うこともできる。 Moreover, the inclined end surface 12 functions effectively also when handling the laminated light shielding film 100 and the original fabric roll 200 of this embodiment in a dark place. That is, the inclined end face 12 (base film 11) is clearly a glossy bright part even with a small amount of light due to the difference from the first black light shielding layer 21 and the second black light shielding layer 31. Recognizable. Further, the front and back surfaces can be discriminated by directly touching the inclined end surface 12 with a finger or the like and confirming the inclination direction.

（変形例）
なお、本発明は、その要旨を逸脱しない範囲内で、任意に変更して実施することができる。例えば、傾斜端面２２，３２を設けずに、傾斜端面１２のみを設けてもよい。また、傾斜端面１２の形成箇所は、基材フィルム１１の外周側面の少なくとも一部に設けられていればよい。さらに、本実施形態のように積層遮光フィルム１００のＭＤ方向に延在するように基材フィルム１１の両側面（２箇所）に設けても、基材フィルム１１のＴＤ方向に延在するように基材フィルム１１の一側面（１箇所）又は両側面（２箇所）に設けてもよい。或いは、基材フィルム１１の外周側面の全面（全周）にわたって傾斜端面１２を設けてもよい。また、ＭＤ方向及び／又はＴＤ方向に延在する傾斜端面１２は、本実施形態のように連続的に形成されていてもよく、また、断続的に形成されていてもよい。 (Modification)
In addition, this invention can be changed arbitrarily and implemented within the range which does not deviate from the summary. For example, only the inclined end surface 12 may be provided without providing the inclined end surfaces 22 and 32. Moreover, the formation location of the inclined end surface 12 should just be provided in at least one part of the outer peripheral side surface of the base film 11. FIG. Furthermore, even if it provides in the both sides | surfaces (2 places) of the base film 11 so that it may extend in MD direction of the laminated light shielding film 100 like this embodiment, it may extend in the TD direction of the base film 11 You may provide in the one side surface (one place) or both side surfaces (two places) of the base film 11. FIG. Alternatively, the inclined end surface 12 may be provided over the entire outer peripheral side surface (the entire circumference) of the base film 11. Further, the inclined end surface 12 extending in the MD direction and / or the TD direction may be formed continuously as in the present embodiment, or may be formed intermittently.

（第二実施形態）
図４は、本発明の第二実施形態のレンズユニット４１及びカメラモジュール５１を模式的に示す分解斜視図である。レンズユニット４１は、レンズ群４２（レンズ４２Ａ，４２Ｂ，４２Ｃ，４２Ｄ，４２Ｅ）と、多段円筒状のホルダー４３と、遮光性スペーサーとしての光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃ（積層遮光フィルム１００）とから構成されている。ホルダー４３の内周部には複数の段差部４３ａ，４３ｂ，４３ｃが設けられている。そして、この段差部４３ａ，４３ｂ，４３ｃを利用して、レンズ群４２及び光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃが、同軸上（同一光軸上）に配置して積み重ねられた状態で、ホルダー４３内の所定位置に収納配置されている。ここで、レンズ４２Ａ，４２Ｂ，４２Ｃ，４２Ｄ，４２Ｅとしては、凸レンズや凹レンズ等、種々のレンズを用いることができ、その曲面は、球面であっても、非球面であってもよい。一方、カメラモジュール５１は、上述したレンズユニット４１と、このレンズユニット４１の光軸上に配置され、レンズユニット４１を通して被写体を撮像する、ＣＣＤイメージセンサやＣＭＯＳイメージセンサ等の撮像素子４４とから構成されている。 (Second embodiment)
FIG. 4 is an exploded perspective view schematically showing the lens unit 41 and the camera module 51 of the second embodiment of the present invention. The lens unit 41 includes a lens group 42 (lenses 42A, 42B, 42C, 42D, and 42E), a multistage cylindrical holder 43, and light shielding rings 100A, 100B, and 100C for optical devices as light shielding spacers (laminated light shielding film 100). ). A plurality of step portions 43 a, 43 b, 43 c are provided on the inner peripheral portion of the holder 43. Then, using the stepped portions 43a, 43b, and 43c, the lens group 42 and the light shielding rings for optical equipment 100A, 100B, and 100C are arranged coaxially (on the same optical axis) and stacked. It is stored and arranged at a predetermined position in 43. Here, as the lenses 42A, 42B, 42C, 42D, and 42E, various lenses such as a convex lens and a concave lens can be used, and the curved surface may be spherical or aspherical. On the other hand, the camera module 51 includes the lens unit 41 described above and an imaging element 44 such as a CCD image sensor or a CMOS image sensor that is disposed on the optical axis of the lens unit 41 and images a subject through the lens unit 41. Has been.

図５は、光学機器用遮光リング１００Ａを模式的に示す断面図である。光学機器用遮光リング１００Ａは、上述した第一実施形態の積層遮光フィルム１００をリング状（中空筒状）に打ち抜き加工して得られたものである。そのため、光学機器用遮光リング１００Ａは、上述した第一実施形態の積層遮光フィルム１００と同様の積層構造を有する。 FIG. 5 is a cross-sectional view schematically showing a light shielding ring 100A for an optical device. The light shielding ring 100A for an optical device is obtained by punching the laminated light shielding film 100 of the first embodiment described above into a ring shape (hollow cylindrical shape). Therefore, the light shielding ring 100A for an optical device has the same laminated structure as the laminated light shielding film 100 of the first embodiment described above.

光学機器用遮光リング１００Ａは、平面視で略中央位置に円筒状の中空部Ｓが設けられた、外形がリング状（中空筒状）の遮光板である。本実施形態において、光学機器用遮光リング１００Ａの外周側面には、上述した傾斜端面１２，２２，３２）が設けられておらず、これらの外周側面は断面視で矩形状に形成されている。すなわち、本実施形態の光学機器用遮光リング１００Ａにおいて、外周端面の傾斜角θは９０°となっている。一方、本実施形態の光学機器用遮光リング１００Ａにおいて、内周端面には、上述した傾斜端面１２，２２，３２に対応する、傾斜端面１３，２３，３３が設けられている。なお、光学機器用遮光リング１００Ｂ，１００Ｃは、外径のサイズ及び中空部Ｓの外径のサイズがそれぞれ相違すること以外は、光学機器用遮光リング１００Ａと同様の構成を有するものであり、ここでの重複した説明は省略する。 The light shielding ring 100A for an optical device is a light shielding plate having a ring shape (hollow cylindrical shape) in which a cylindrical hollow portion S is provided at a substantially central position in plan view. In the present embodiment, the above-described inclined end faces 12, 22, and 32) are not provided on the outer peripheral side surface of the light shielding ring 100A for optical equipment, and these outer peripheral side surfaces are formed in a rectangular shape in a sectional view. That is, in the light shielding ring 100A for an optical device according to this embodiment, the inclination angle θ of the outer peripheral end face is 90 °. On the other hand, in the light shielding ring for optical equipment 100A of the present embodiment, inclined end surfaces 13, 23, 33 corresponding to the above-described inclined end surfaces 12, 22, 32 are provided on the inner peripheral end surface. The optical device shading rings 100B and 100C have the same configuration as the optical device shading ring 100A except that the outer diameter and the hollow portion S have different outer diameters. The duplicate description in is omitted.

（作用）
本実施形態の光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃにおいても、２．５以上の光学濃度及び５．０％以下の６０度光沢度を有する第一黒色遮光層２１と第二黒色遮光層３１を採用している。そのため、これをレンズユニットやカメラモジュール等の光学機器用遮光部材として用いることで、不要な入射光や反射光を除去することができ、ハレーション、レンズフレア、ゴースト等の発生を防止でき、撮像画像の画質を向上させることができる。 (Function)
Also in the light-shielding rings 100A, 100B, and 100C for the optical device of the present embodiment, the first black light-shielding layer 21 and the second black light-shielding layer 31 having an optical density of 2.5 or more and a glossiness of 60 degrees of 5.0% or less. Is adopted. Therefore, by using this as a light-shielding member for optical devices such as lens units and camera modules, unnecessary incident light and reflected light can be removed, occurrence of halation, lens flare, ghost, etc. can be prevented, and the captured image Image quality can be improved.

しかも、第一黒色遮光層２１と第二黒色遮光層３１とが、異なる６０度光沢度及び／又は明度指数Ｌ^*を有するため、その光沢感、艶、又は明度の差に基づいて、非接触すなわち目視で、光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃの表裏面の判別を容易に行うことができる。そのため、これら光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃを用いたレンズユニット４１及びカメラモジュール５１は、その保管時や組み込み時においても、表裏面の誤認に基づく組み込み不良等の製造故障が抑止される。 In addition, since the first black light-shielding layer 21 and the second black light-shielding layer 31 have different 60 degree glossiness and / or brightness index L ^* , non-contact based on the difference in glossiness, gloss, or brightness. That is, it is possible to easily distinguish the front and back surfaces of the light shielding rings 100A, 100B, and 100C for optical devices by visual observation. For this reason, the lens unit 41 and the camera module 51 using the light shielding rings 100A, 100B, and 100C for optical devices are prevented from being manufactured and malfunctioned due to misidentification of the front and back surfaces during storage or assembly. .

その上さらに、本実施形態の光学機器用遮光リング１００Ａにおいては、傾斜端面１３，２３，３３が設けられており、黒色遮光層２１，３１の判別性がさらに高められている。このように光軸側の端面（内周端面）に傾斜端面１３，２３，３３を設けることで、不要な反射光を除去することができ、ハレーション、レンズフレア、ゴースト等の発生を防ぎ、撮像画像の画質を向上させることができる。 In addition, in the light shielding ring 100A for an optical device according to the present embodiment, inclined end surfaces 13, 23, and 33 are provided, and the distinguishability of the black light shielding layers 21 and 31 is further enhanced. By providing the inclined end faces 13, 23, 33 on the end face (inner peripheral end face) on the optical axis side in this way, unnecessary reflected light can be removed, and the occurrence of halation, lens flare, ghost, etc. can be prevented and imaging can be performed. The image quality can be improved.

（変形例）
なお、本発明は、その要旨を逸脱しない範囲内で、任意に変更して実施することができる。例えば、積層遮光フィルム１００（光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃ）の外形形状は、例えば平面視で長方形状、正方形状、六角形状等の多角形状、楕円形状、不定形状等の任意の形状を採用することができる。また、光学機器用遮光リング１００Ａ，１００Ｂ，１００Ｃの中空部Ｓの形状も、本実施形態では平面視で円状に形成されているが、その外形は特に限定されない。例えば平面視で長方形状、正方形状、六角形状等の多角形状、楕円形状、不定形状等の任意の形状を採用することができる。さらに、本実施形態では、上述した傾斜端面１２，２２，３２を設けていないが、必要に応じて、傾斜端面１２、及び傾斜端面２２，３２のいずれか一方或いは双方を適宜設けることができる。 (Modification)
In addition, this invention can be changed arbitrarily and implemented within the range which does not deviate from the summary. For example, the outer shape of the laminated light-shielding film 100 (light-shielding rings 100A, 100B, and 100C for optical devices) is, for example, an arbitrary shape such as a rectangular shape, a square shape, a hexagonal shape such as a hexagonal shape, an elliptical shape, and an indefinite shape in plan view. Can be adopted. Moreover, although the shape of the hollow part S of the light shielding rings 100A, 100B, and 100C for optical devices is also formed in a circular shape in plan view in this embodiment, the outer shape is not particularly limited. For example, an arbitrary shape such as a rectangular shape, a square shape, a polygonal shape such as a hexagonal shape, an elliptical shape, or an indefinite shape can be adopted in plan view. Furthermore, in this embodiment, although the inclined end surfaces 12, 22, and 32 described above are not provided, either one or both of the inclined end surfaces 12 and the inclined end surfaces 22, 32 can be appropriately provided as necessary.

本発明は、精密機械分野、半導体分野、光学機器分野、電子機器等における高性能な遮光部材として広く且つ有効に利用可能である。とりわけ、高性能一眼レフカメラ、コンパクトカメラ、ビデオカメラ、携帯電話、プロジェクタ等に搭載されるレンズユニットやカメラモジュール等に用いる遮光部材として、殊に有効に利用可能である。 The present invention can be widely and effectively used as a high-performance light-shielding member in the precision machinery field, semiconductor field, optical field, electronic device, and the like. In particular, it can be used particularly effectively as a light-shielding member used in lens units and camera modules mounted on high-performance single-lens reflex cameras, compact cameras, video cameras, mobile phones, projectors, and the like.

１１・・・基材フィルム
１１ａ・・・表面（主面）
１１ｂ・・・表面（主面）
１２・・・傾斜端面
１３・・・傾斜端面
２１・・・黒色遮光層
２１ａ・・・表面（主面）
２２・・・傾斜端面
２３・・・傾斜端面
３１・・・黒色遮光層
３１ａ・・・表面（主面）
３２・・・傾斜端面
３３・・・傾斜端面
４１・・・レンズユニット
４２・・・レンズ群
４２Ａ・・・レンズ
４２Ｂ・・・レンズ
４２Ｃ・・・レンズ
４２Ｄ・・・レンズ
４２Ｅ・・・レンズ
４３・・・ホルダー
４３ａ・・・段差部
４３ｂ・・・段差部
４３ｃ・・・段差部
４４・・・撮像素子
５１・・・カメラモジュール
１００・・・積層遮光フィルム
１００Ａ・・・光学機器用遮光リング（積層遮光フィルム）
１００Ｂ・・・光学機器用遮光リング（積層遮光フィルム）
１００Ｃ・・・光学機器用遮光リング（積層遮光フィルム）
２００・・・原反ロール
θ ・・・傾斜角
Ｓ・・・中空部
ＭＤ・・・流れ方向
ＴＤ・・・垂直方向 11: Base film 11a: Surface (main surface)
11b ... surface (main surface)
DESCRIPTION OF SYMBOLS 12 ... Inclined end surface 13 ... Inclined end surface 21 ... Black light-shielding layer 21a ... Surface (main surface)
22 ... Inclined end face 23 ... Inclined end face 31 ... Black shading layer 31a ... Surface (main surface)
32 ... Inclined end face 33 ... Inclined end face 41 ... Lens unit 42 ... Lens group 42A ... Lens 42B ... Lens 42C ... Lens 42D ... Lens 42E ... Lens 43・・・ Holder 43a ・・・ Step part 43b ・・・ Step part 43c ・・・ Step part 44 ・・・ Imaging element 51 ・・・ Camera module 100 ・・・ Laminated light shielding film 100A ・・・ Light shielding ring for optical device (Laminated light shielding film)
100B ... Light shielding ring for optical equipment (laminated light shielding film)
100C ... Light-shielding ring for optical equipment (laminated light-shielding film)
200: Raw material roll θ: Inclination angle S: Hollow part MD: Flow direction TD: Vertical direction

本発明は、上記課題に鑑みてなされたものである。すなわち本発明の目的は、黒色の遮光層を有しながらも表裏面の判別が容易な光学機器用積層遮光フィルム、並びに、これを用いた光学機器用遮光リング、レンズユニット及びカメラモジュール等を提供することにある。
The present invention has been made in view of the above problems. That is, an object of the present invention is to provide a laminated light-shielding film for optical equipment that has a black light-shielding layer and can easily discriminate between the front and back surfaces, a light-shielding ring for optical equipment, a lens unit, a camera module, and the like using the same There is to do.

すなわち、本発明は、以下に示す種々の具体的態様を提供する。
（１）第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、前記第一黒色遮光層は前記積層構造の表側の最表面に配置され、前記第二黒色遮光層は前記積層構造の裏側の最表面に配置され、前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、前記第一黒色遮光層は、前記第二黒色遮光層とは異なる明度指数Ｌ^*を有することを特徴とする、光学機器用積層遮光フィルム。
（２）前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している、上記（１）に記載の光学機器用積層遮光フィルム。
That is, the present invention provides various specific modes shown below.
(1) It has a laminated structure including at least a first black light-shielding layer and a second black light-shielding layer, the first black light-shielding layer is disposed on the outermost surface of the laminated structure, and the second black light-shielding layer is Arranged on the outermost surface of the back side of the laminated structure, the first black light shielding layer and the second black light shielding layer have an optical density of 2.5 or more and a 60 degree gloss of 5.0% or less, wherein the first light shielding layer is characterized by having a bright index L ^* that is different from said second light shielding layer, laminated shielding film for optical instruments.
(2) The first black light-shielding layer and / or the second black light-shielding layer has an inclined end face that widens the film width from the first black light-shielding layer toward the second black light-shielding layer, The laminated light-shielding film for optical equipment according to (1), wherein the inclined end face is exposed in a plan view as viewed from the normal direction of the main surface of the one black light-shielding layer.

（３）前記第一黒色遮光層及び／又は前記第二黒色遮光層には、中空部が設けられており、前記中空部の内周に傾斜端面を有する（１）又は（２）に記載の光学機器用積層遮光フィルム。
（４）前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度を有し、前記第一黒色遮光層と前記第二黒色遮光層の６０度光沢度の差が、１．０〜４．５％である上記（１）〜（３）のいずれか一項に記載の光学機器用積層遮光フィルム。
（５）基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する上記（１）〜（４）のいずれか一項に記載の光学機器用積層遮光フィルム。
(3) The first black light-shielding layer and / or the second black light-shielding layer is provided with a hollow portion, and has an inclined end surface on the inner periphery of the hollow portion. Laminated light shielding film for optical equipment.
(4) The first black light-shielding layer has a 60 degree glossiness different from that of the second black light-shielding layer, and the difference in 60-degree glossiness between the first black light-shielding layer and the second black light-shielding layer is The laminated light-shielding film for optical equipment according to any one of (1) to (3), which is 1.0 to 4.5%.
(5) At least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The laminated light-shielding film for optical equipment according to any one of (1) to (4), having a laminated structure.

（６）リング状の外形形状を有し、第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、前記第一黒色遮光層は前記積層構造の表側の最表面に配置され、前記第二黒色遮光層は前記積層構造の裏側の最表面に配置され、前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、前記第一黒色遮光層は、前記第二黒色遮光層とは異なる明度指数Ｌ^*を有する、光学機器用遮光リング。
（７）前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している上記（６）に記載の光学機器用遮光リング。
（８）前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度を有し、前記第一黒色遮光層と前記第二黒色遮光層の６０度光沢度の差が、１．０〜４．５％である上記（６）又は（７）に記載の光学機器用遮光リング。
（９）基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する上記（６）〜（８）のいずれか一項に記載の光学機器用遮光リング。
（１０）リング状の外形形状を有し、基材フィルム、前記基材フィルムの一方の主面側に設けられた第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有し、前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、前記第一黒色遮光層は、前記第二黒色遮光層とは異なる明度指数Ｌ ^* を有する、光学機器用遮光リング。ここで、この（１０）に記載の光学機器用遮光リングは、上記（６）〜（９）のいずれか１以上の特徴をさらに有していることが好ましい。
( 6 ) It has a ring-shaped outer shape and has a laminated structure including at least a first black light-shielding layer and a second black light-shielding layer, and the first black light-shielding layer is disposed on the outermost surface of the laminated structure. The second black light shielding layer is disposed on the outermost surface on the back side of the laminated structure, and the first black light shielding layer and the second black light shielding layer have an optical density of 2.5 or more and 5.0% or less. a 60 degree gloss, respectively, the first light shielding layer, said has a bright index L ^* that is different from the second light shielding layer, the light shielding ring for optical instruments.
( 7 ) The first black light-shielding layer and / or the second black light-shielding layer has an inclined end face that widens the film width from the first black light-shielding layer toward the second black light-shielding layer, The light shielding ring for an optical device according to ( 6 ), wherein the inclined end surface is exposed in a plan view as viewed from the normal direction of the main surface of the one black light shielding layer.
(8) The first black light-shielding layer has a 60-degree glossiness different from that of the second black light-shielding layer, and a difference in 60-degree glossiness between the first black light-shielding layer and the second black light-shielding layer is The light-shielding ring for optical devices according to (6) or (7), which is 1.0 to 4.5%.
( 9 ) At least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The light-shielding ring for optical devices according to any one of (6) to (8) , having a laminated structure.
(10) It has a ring-shaped outer shape, and is provided on the base film, the first black light shielding layer provided on one main surface side of the base film, and the other main surface side of the base film. The first black light-shielding layer and the second black light-shielding layer each have an optical density of 2.5 or more and a 60 degree gloss of 5.0% or less. And the first black light-shielding layer has a lightness index L ^* different from that of the second black light-shielding layer . Here, it is preferable that the light-shielding ring for an optical device described in (10) further includes any one or more of the features (6) to (9).

（１１）複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットであって、前記遮光板の少なくとも１以上が、上記（１）〜（５）のいずれか一項に記載の光学機器用積層遮光フィルム、及び／又は、上記（６）〜（１０）のいずれか一項に記載の光学機器用遮光リングからなるレンズユニット。
（１２）複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットと、前記レンズユニットを通して被写体を撮像する撮像素子とを少なくとも有するカメラモジュールであって、前記遮光板の少なくとも１以上が、上記（１）〜（５）のいずれか一項に記載の光学機器用積層遮光フィルム、及び／又は、上記（６）〜（１０）のいずれか一項に記載の光学機器用遮光リングからなるカメラモジュール。
( 11 ) A lens unit in which a plurality of lenses and at least one light shielding plate are stacked in the optical axis direction of the lens, and at least one of the light shielding plates is any one of the above (1) to ( 5 ). A lens unit comprising the laminated light-shielding film for optical equipment according to claim 1 and / or the light-shielding ring for optical equipment according to any one of ( 6 ) to ( 10 ) above.
( 12 ) A camera module, wherein the plurality of lenses and at least one or more light shielding plates include at least a lens unit stacked in the optical axis direction of the lens, and an imaging element that images a subject through the lens unit, At least 1 or more of a light-shielding plate is a laminated light-shielding film for optical devices as described in any one of said (1)-( 5 ), and / or as described in any one of ( 6 )-( 10 ) above. Camera module consisting of a shading ring for optical equipment.

黒色顔料は、バインダー樹脂を黒色に着色して遮光性を付与するものである。黒色顔料の具体例としては、例えば、黒色樹脂粒子、マグネタイト系ブラック、銅・鉄・マンガン系ブラック、チタンブラック、カーボンブラック等が挙げられるが、これらに特に限定されない。これらの中でも、隠蔽性に優れることから、黒色樹脂粒子、チタンブラック、カーボンブラックが好ましく、より好ましくはカーボンブラックである。これらは１種を単独で用いることができ、また２種以上を組み合わせて用いることもできる。
The black pigment imparts light shielding properties by coloring the binder resin black. Specific examples of the black pigment, for example, black resin particle, Ma Gunetaito based black, copper-iron-manganese black, titanium black, carbon black and the like, not particularly limited thereto. Among these, black resin particles, titanium black, and carbon black are preferable because of excellent concealability, and carbon black is more preferable. These can be used individually by 1 type and can also be used in combination of 2 or more type.

カーボンブラックとしては、オイルファーネスブラック、ランプブラック、チャンネルブラック、ガスファーネスブラック、アセチレンブラック、サーマルブラック、ケッチェンブラック等、各種公知の製法で作製されたものが知られているが、その種類は特に制限されない。黒色遮光層２１，３１に導電性を付与し静電気による帯電を防止する観点から、導電性カーボンブラックが特に好ましく用いられる。カーボンブラックの歴史は古く、例えば三菱化学株式会社、旭カーボン株式会社、御国色素株式会社、レジノカラー工業株式会社、Ｃａｂｏｔ社、ＤＥＧＵＳＳＡ社等から、各種グレードのカーボンブラック単体及びカーボンブラック分散液が市販されており、要求性能や用途に応じて、これらの中から適宜選択すればよい。なお、カーボンブラックの粒子サイズは、要求性能等に応じて適宜設定でき、特に限定されない。カーボンブラックの平均粒子径Ｄ₅₀は、０．０１〜２．０μｍであることが好ましく、より好ましくは０．０５〜０．１．０μｍ、さらに好ましくは０．０８〜０．５μｍである。なお、本明細書における平均粒子径とは、レーザー回折式粒度分布測定装置（例えば、島津製作所社：ＳＡＬＤ−７０００等）で測定される、体積基準のメジアン径（Ｄ₅₀）を意味する。
As carbon black, oil furnace black, lamp black, channel black, gas furnace black, acetylene black, thermal black, ketjen black, etc., which are produced by various known production methods are known, but the type is particularly Not limited. From the viewpoint of imparting conductivity to the black light-shielding layers 21 and 31 and preventing electrostatic charging, conductive carbon black is particularly preferably used. Carbon black has a long history, for example by Mitsubishi Chemical Co., Ltd., Asahi Carbon Co., Ltd., Mikuni Color Ltd., Rejinokara industrial stock company, Cabot Corporation, from DEGUSSA companies, etc., carbon black alone and carbon black dispersion of various grades are commercially available It may be selected appropriately from these according to the required performance and application. The particle size of carbon black can be set as appropriate according to required performance and is not particularly limited. The average particle diameter D ₅₀ of carbon black is preferably 0.01 to 2.0 μm, more preferably 0.05 to 0.10 μm, and still more preferably 0.08 to _0.5 μm. The average particle diameter in the present specification means a volume-based median diameter (D ₅₀ ) measured by a laser diffraction particle size distribution measuring apparatus (for example, Shimadzu Corporation: SALD-7000).

Claims

第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、
前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、
前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度及び／又は明度指数Ｌ^*を有する
ことを特徴とする、積層遮光フィルム。 Having a laminated structure comprising at least a first black light shielding layer and a second black light shielding layer;
The first black light-shielding layer and the second black light-shielding layer each have an optical density of 2.5 or more and a 60 degree gloss of 5.0% or less,
The first black light-shielding layer has a 60-degree glossiness and / or lightness index L ^* different from that of the second black light-shielding layer.

前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、
前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している
請求項１に記載の積層遮光フィルム。 The first black light shielding layer and / or the second black light shielding layer has an inclined end face that widens the film width from the first black light shielding layer toward the second black light shielding layer,
The laminated light-shielding film according to claim 1, wherein the inclined end surface is exposed in a plan view as viewed from the normal direction of the main surface of the first black light-shielding layer.

前記第一黒色遮光層の前記主面と前記傾斜端面とを結ぶ傾斜角が１０〜８７°である
請求項１又は２に記載の積層遮光フィルム。 The laminated light-shielding film according to claim 1 or 2, wherein an inclination angle connecting the main surface of the first black light-shielding layer and the inclined end surface is 10 to 87 °.

前記第一黒色遮光層と前記第二黒色遮光層の６０度光沢度の差が、１．０〜４．５％である
請求項１〜３のいずれか一項に記載の積層遮光フィルム。 The laminated light-shielding film according to any one of claims 1 to 3, wherein a difference in 60-degree glossiness between the first black light-shielding layer and the second black light-shielding layer is 1.0 to 4.5%.

基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する
請求項１〜４のいずれか一項に記載の積層遮光フィルム。 Laminated structure comprising at least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The laminated light-shielding film according to any one of claims 1 to 4, comprising:

前記基材フィルムは、８０．０〜９９．９％の全光線透過率を有する
請求項５のいずれか一項に記載の積層遮光フィルム。 The said base film is a laminated light shielding film as described in any one of Claims 5 which has the total light transmittance of 80.0-99.9%.

前記基材フィルムは、０．５μｍ以上、５０μｍ以下の厚みを有する
請求項６に記載の積層遮光フィルム。 The laminated light-shielding film according to claim 6, wherein the base film has a thickness of 0.5 μm or more and 50 μm or less.

リング状の外形形状を有し、
第一黒色遮光層、及び第二黒色遮光層を少なくとも備える積層構造を有し、
前記第一黒色遮光層及び前記第二黒色遮光層は、２．５以上の光学濃度及び５．０％以下の６０度光沢度をそれぞれ有し、
前記第一黒色遮光層は、前記第二黒色遮光層とは異なる６０度光沢度及び／又は明度指数Ｌ^*を有する、
光学機器用遮光リング。 It has a ring-shaped outer shape,
Having a laminated structure comprising at least a first black light shielding layer and a second black light shielding layer;
The first black light-shielding layer and the second black light-shielding layer each have an optical density of 2.5 or more and a 60 degree gloss of 5.0% or less,
The first black light shielding layer has a 60 degree glossiness and / or a lightness index L ^* different from the second black light shielding layer,
Shading ring for optical equipment.

前記第一黒色遮光層及び／又は前記第二黒色遮光層は、前記第一黒色遮光層から前記第二黒色遮光層に向けてフィルム幅を拡開させる傾斜端面を有し、
前記第一黒色遮光層の主面の法線方向から見た平面視で、前記傾斜端面が露出している
請求項８に記載の光学機器用遮光リング。 The first black light shielding layer and / or the second black light shielding layer has an inclined end face that widens the film width from the first black light shielding layer toward the second black light shielding layer,
The light shielding ring for an optical device according to claim 8, wherein the inclined end surface is exposed in a plan view as viewed from the normal direction of the main surface of the first black light shielding layer.

基材フィルム、前記基材フィルムの一方の主面側に設けられた前記第一黒色遮光層、及び前記基材フィルムの他方の主面側に設けられた第二黒色遮光層を少なくとも備える積層構造を有する
請求項９に記載の光学機器用遮光リング。 Laminated structure comprising at least a base film, the first black light shielding layer provided on one main surface side of the base film, and a second black light shielding layer provided on the other main surface side of the base film The light-shielding ring for optical devices according to claim 9, comprising:

複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットであって、
前記遮光板の少なくとも１以上が、請求項１〜７のいずれか一項に記載の積層遮光フィルム、及び／又は、請求項８〜１０のいずれか一項に記載の光学機器用遮光リングからなる
レンズユニット。 A plurality of lenses and at least one light shielding plate are lens units stacked in the optical axis direction of the lens,
At least 1 or more of the said light-shielding plates consists of the laminated light-shielding film as described in any one of Claims 1-7, and / or the light-shielding ring for optical apparatuses as described in any one of Claims 8-10. Lens unit.

複数のレンズ及び少なくとも１以上の遮光板が、前記レンズの光軸方向に積み重ねられたレンズユニットと、前記レンズユニットを通して被写体を撮像する撮像素子とを少なくとも有するカメラモジュールであって、
前記遮光板の少なくとも１以上が、請求項１〜７のいずれか一項に記載の積層遮光フィルム、及び／又は、請求項８〜１０のいずれか一項に記載の光学機器用遮光リングからなる
カメラモジュール。 A plurality of lenses and at least one light shielding plate having at least a lens unit stacked in an optical axis direction of the lens, and an image pickup device that images a subject through the lens unit;
At least 1 or more of the said light-shielding plates consists of the laminated light-shielding film as described in any one of Claims 1-7, and / or the light-shielding ring for optical apparatuses as described in any one of Claims 8-10. The camera module.