JP2018071295A

JP2018071295A - Sheet for concrete curing

Info

Publication number: JP2018071295A
Application number: JP2016215761A
Authority: JP
Inventors: 田中　俊治; Toshiharu Tanaka; 俊治田中; 真一豊岡; Shinichi Toyooka; 顕平泉; Akira Hiraizumi; 江崎　孝二; Koji Ezaki; 孝二江崎
Original assignee: Unitika Ltd
Current assignee: Unitika Ltd
Priority date: 2016-11-04
Filing date: 2016-11-04
Publication date: 2018-05-10

Abstract

PROBLEM TO BE SOLVED: To provide a sheet for concrete curing which can prevent drying of a concrete surface over a long period of time and where a weight during hydration is not excessive.SOLUTION: A synthetic resin film 13 and a spunlace non-woven fabric 14 containing more than 50 mass% of a cotton fiber are laminated.SELECTED DRAWING: Figure 1

Description

本発明はコンクリート養生用シートに関する。 The present invention relates to a concrete curing sheet.

コンクリート構造物を養生するために、養生用シートが用いられている（特許文献１〜４）。 Curing sheets are used for curing concrete structures (Patent Documents 1 to 4).

特許文献１に記載の養生用シートは、高吸水性繊維、または／および、高吸水ポリマーすなわち高分子吸収体を含有したものである。特許文献２には、高吸水性ポリマーを含む透水性シートと不透水性のプラスチックシートとを合着した養生用シートが記載されている。特許文献３に記載の養生用シートは、プラスチックフィルムと繊維シートとを積層した構成である。そのうち、プラスチックフィルムは本来の養生の目的つまりコンクリートの乾燥を防止するためのものである。繊維シートは、当該養生用シートをコンクリートに密着させる役目を果たすもの、すなわち繊維の交絡部分にコンクリートを入り込ませることによって打設コンクリートへの密着性を確保するものである。特許文献４には、親水性を有する剤を混入したプラスチック樹脂製の不織シートの片面に、不透水性のプラスチック製のシートを接合した養生用シートが記載されている。 The curing sheet described in Patent Document 1 contains a superabsorbent fiber or / and a superabsorbent polymer, that is, a polymer absorber. Patent Document 2 describes a curing sheet in which a water-permeable sheet containing a superabsorbent polymer and a water-impermeable plastic sheet are bonded together. The curing sheet described in Patent Document 3 has a configuration in which a plastic film and a fiber sheet are laminated. Among them, the plastic film is intended for the purpose of curing, that is, to prevent the concrete from drying. The fiber sheet plays the role of bringing the curing sheet into close contact with the concrete, that is, ensures the adhesion to the cast concrete by allowing the concrete to enter the entangled portion of the fiber. Patent Document 4 describes a curing sheet in which a non-permeable plastic sheet is bonded to one side of a plastic resin nonwoven sheet mixed with a hydrophilic agent.

特開平８−１８８４８６号公報JP-A-8-188486 実開昭６３−２１３６７号公報Japanese Utility Model Publication No. 63-21367 特開２００７−４６２７０号公報JP 2007-46270 A 特開２０１４−２３７９２５号公報JP 2014-237925 A

しかし、フィルムタイプではコンクリート表面の乾燥を長時間にわたって防止することが困難で、フィルムを貼って数時間でコンクリート表面が乾いてしまい、養生用シートに水をかけるなどの対応が必要である。高分子吸収体を含む養生用シートは、養生用シート自体は湿潤状体を保つことができるが、肝心のコンクリートに水分を供給することができないため、十分な養生効果を期待することができない。また高分子吸収体を含んだ養生用シートは、水分を含むと重くなり、このためコンクリートに貼り付けるために特別な器具が必要になってしまう。 However, it is difficult to prevent the concrete surface from drying for a long time with the film type, and the concrete surface is dried within a few hours after the film is applied, and it is necessary to take measures such as applying water to the curing sheet. A curing sheet containing a polymer absorber can maintain a moist state in the curing sheet itself, but cannot provide sufficient curing effect because it cannot supply moisture to the essential concrete. In addition, a curing sheet containing a polymer absorbent becomes heavy when it contains moisture, and thus a special instrument is required to stick it to concrete.

そこで本発明は、このような課題を解決して、コンクリート表面の乾燥を長時間にわたって防止することが可能であるとともに、含水時の重量が過大になることがないコンクリート養生用シートを得ることを目的とする。 Therefore, the present invention solves such problems and can obtain a concrete curing sheet that can prevent drying of the concrete surface over a long period of time and does not have an excessive weight when containing water. Objective.

この目的を達成するため、本発明のコンクリート養生用シートは、下記の特徴を有する。 In order to achieve this object, the concrete curing sheet of the present invention has the following characteristics.

（１）合成樹脂製のフィルムと、コットン繊維を５０質量％を超えて含有するスパンレース不織布とが積層されていることを特徴とするコンクリート養生用シート。 (1) A sheet for concrete curing characterized in that a synthetic resin film and a spunlace nonwoven fabric containing more than 50% by mass of cotton fibers are laminated.

（２）スパンレース不織布は、目付が５０ｇ／ｍ^２以上であることを特徴とする（１）のコンクリート養生用シート。 (2) The concrete curing sheet according to (1), wherein the spunlace nonwoven fabric has a basis weight of 50 g / m ² or more.

（３）引張強力が１００Ｎ／５ｃｍ幅以上であるとともに、ＪＩＳ−Ｌ１９１３に規定される保水率が１５０％以上であることを特徴とする（１）または（２）のコンクリート養生用シート。 (3) The concrete curing sheet according to (1) or (2), wherein the tensile strength is 100 N / 5 cm width or more and the water retention rate specified in JIS-L1913 is 150% or more.

本発明のコンクリート養生用シートによれば、コットン繊維を５０質量％を超えて含有するスパンレース不織布によって優れた保水性を発揮するとともに、合成樹脂製のフィルムによって乾燥防止効果を発揮することができ、このためコンクリート表面の乾燥を長時間にわたって防止することが可能である。しかも、コットン繊維を５０質量％を超えて含有するスパンレース不織布によって保水性を発揮するものであるため、含水時の重量が過大になることがないという利点を有する。 According to the concrete curing sheet of the present invention, the spunlace nonwoven fabric containing more than 50% by mass of cotton fibers exhibits excellent water retention, and the synthetic resin film can exhibit an anti-drying effect. Therefore, it is possible to prevent the concrete surface from drying for a long time. Moreover, since the water retention is exhibited by the spunlace nonwoven fabric containing more than 50% by mass of cotton fibers, there is an advantage that the weight when containing water does not become excessive.

本発明の実施の形態のコンクリート養生用シートをコンクリート構造物の表面に貼り付けた状態を示す断面図である。It is sectional drawing which shows the state which affixed the sheet | seat for concrete curing of embodiment of this invention on the surface of a concrete structure.

図１において、１１はコンクリート構造体、１２は本発明の実施の形態のコンクリート養生用シートである。養生用シート１２は、フィルム１３と不織布１４とが積層されたものであり、不織布１４がコンクリート構造体１１の表面に沿って配置されるとともに、フィルム１３が不織布１４よりもコンクリート構造体１１から離れて位置する状態で配置されている。 In FIG. 1, 11 is a concrete structure, and 12 is a concrete curing sheet according to an embodiment of the present invention. The curing sheet 12 is formed by laminating a film 13 and a nonwoven fabric 14. The nonwoven fabric 14 is arranged along the surface of the concrete structure 11, and the film 13 is separated from the concrete structure 11 more than the nonwoven fabric 14. It is arranged in the state that is located.

フィルム１３は合成樹脂によって形成されている。合成樹脂としては、ポリオレフィン樹脂、ポリエステル樹脂、ポリアミド樹脂などを挙げることができる。フィルム１３の厚みは、５〜１００μｍが好適である。フィルム１３が５μｍよりも薄いと、取扱い時に破れが生じ易くなるだけでなく、屋外での使用時に紫外線劣化によって簡単に破れる状態となり、機能を維持できなくなるという問題を生じることがある。また１００μｍよりも厚いと、不織布と積層された製品となった際にシートが硬すぎて取り扱いにくい、あるいはコンクリートへの貼り付きが悪い、吸水時の重量が重すぎてはがれ易くなるという問題を生じることがある。 The film 13 is made of a synthetic resin. Examples of the synthetic resin include a polyolefin resin, a polyester resin, and a polyamide resin. The thickness of the film 13 is preferably 5 to 100 μm. If the film 13 is thinner than 5 μm, not only the film tends to be broken during handling, but also a problem that the film 13 can be easily broken due to ultraviolet deterioration when used outdoors, and the function cannot be maintained. On the other hand, if it is thicker than 100 μm, the sheet is too hard to handle when it becomes a product laminated with a non-woven fabric, or the sticking to concrete is bad, or the weight at the time of water absorption is too heavy and it is easy to peel off. Sometimes.

不織布１４は、コットン繊維を５０質量％を超えて含有する。コットン繊維は、吸水性に優れた繊維であり、このコットン繊維を主体とするものであること、すなわちコットン繊維を５０質量％を超えて含有することが必要である。それによって、所要の保水性を得ることができる。 The nonwoven fabric 14 contains more than 50% by mass of cotton fibers. The cotton fiber is a fiber excellent in water absorption, and is mainly composed of the cotton fiber, that is, the cotton fiber needs to be contained in an amount exceeding 50% by mass. Thereby, the required water retention can be obtained.

不織布１４は、スパンレース不織布であることが必要である。スパンレース不織布は短繊維を互いに交絡させることで不織布化されたものであるため、繊維間空隙が良好に確保される。したがって、コットン繊維自体が吸水により保水することに加えて、コットン繊維が親水性であることから、コットン繊維同士の繊維間空隙内にも良好に水分を保持することが可能となり、それらの点から良好な保水性を得ることができる。つまり、本発明によれば、不織布１４がコットン繊維を５０質量％を超えて含有するスパンレース不織布であることによって、きわめて良好な保水性を達成することができる。 The nonwoven fabric 14 needs to be a spunlace nonwoven fabric. Since the spunlace nonwoven fabric is made into a nonwoven fabric by entanglement of short fibers with each other, a good inter-fiber gap is secured. Therefore, in addition to the water retention of the cotton fiber itself by water absorption, the cotton fiber is hydrophilic, so it is possible to hold moisture well in the interfiber space between the cotton fibers. Good water retention can be obtained. In other words, according to the present invention, the nonwoven fabric 14 is a spunlace nonwoven fabric containing more than 50% by mass of cotton fibers, whereby extremely good water retention can be achieved.

良好な保水性を達成するために、不織布１４は、コットン繊維を８０質量％以上含有することがよりいっそう好ましく、また、１００質量％がコットン繊維であることも好ましい。なお、他の繊維と混合させる場合は、強度の点を考慮して、ポリエステル繊維を混合することが好ましい。 In order to achieve good water retention, the nonwoven fabric 14 more preferably contains 80% by mass or more of cotton fibers, and 100% by mass is preferably cotton fibers. In addition, when making it mix with another fiber, it is preferable to mix a polyester fiber in consideration of the point of intensity | strength.

不織布１４の目付は、５０〜１５０ｇ／ｍ^２であることが、保水した状態でコンクリートに貼り付き続けられるという目的のために好ましい。不織布１４の目付が５０ｇ／ｍ^２未満であると、保水量が少なすぎて数日で乾燥してしまい、養生の役目を果たせなくなるという問題を生じやすい。反対に不織布１４の目付が１５０ｇ／ｍ^２を超えると、保水量は問題ないが、シートとしての重量が重すぎるとともに、繊維量が増大することにしたがって保水量も増大することにより重量が増大することが原因して、垂直のコンクリート壁面からはがれ易くなってしまうという問題を生じやすい。 The basis weight of the nonwoven fabric 14 is preferably 50 to 150 g / m ² for the purpose of being able to keep sticking to the concrete while retaining water. If the basis weight of the non-woven fabric 14 is less than 50 g / m ² , the amount of water retention is too small and the fabric dries in a few days, which tends to cause a problem that it cannot perform the curing role. On the contrary, if the basis weight of the nonwoven fabric 14 exceeds 150 g / m ² , the water retention amount is not a problem, but the weight as the sheet is too heavy, and the water retention amount increases as the fiber amount increases, thereby increasing the weight. For this reason, it tends to cause a problem that it is easily peeled off from the vertical concrete wall surface.

養生用シート１２を得るためにフィルム１３と不織布１４とを積層一体化させるための手法は、適宜のものを採用することができる。たとえば、フィルム１３と不織布１４との間に、熱接着用のたとえばポリエチレンシートを押出ラミネートにより介在させることができる。あるいはホットメルト接着により積層一体化を達成することもできる。 As a method for laminating and integrating the film 13 and the nonwoven fabric 14 in order to obtain the curing sheet 12, an appropriate one can be adopted. For example, a polyethylene sheet for heat bonding can be interposed between the film 13 and the nonwoven fabric 14 by extrusion lamination. Or lamination integration can also be achieved by hot melt bonding.

養生用シート１２の全体において、その目付は、上述したフィルムの厚みの好適な範囲と、不織布の目付の好適な範囲と、積層一体化のための材料を必要に応じて用いることとにもとづき、６０〜２００ｇ／ｍ^２であることが好ましい。 In the entire curing sheet 12, the basis weight is based on the above-described preferred range of the thickness of the film, the preferred range of the basis weight of the nonwoven fabric, and the use of materials for lamination and integration as necessary. It is preferable that it is 60-200 g / m < ² >.

養生用シート１２は、ＪＩＳＬ１９０８の２ｋＰａという条件で測定したときの厚みが３００〜２０００μｍであることが好ましい。 As for the sheet | seat 12 for curing, it is preferable that the thickness when it measures on the conditions of 2 kPa of JISL1908 is 300-2000 micrometers.

養生用シート１２は、実用上の強力として、引張強力が１００Ｎ／５ｃｍ幅以上であることが好ましい。引張強力が１００Ｎ／５ｃｍ幅に満たないと、コンクリート養生用シートとしての所要強力を有さないことになって、保水させた状態でコンクリートへ貼り付ける際に、破れが生じる場合があるという不都合が生じやすくなる。かつ、養生用シート１２は、ＪＩＳ−Ｌ１９１３に規定される保水率が１５０％以上であることが好ましい。すなわち養生用シート１３は、上述の好適な目付の範囲から理解されるようにシート自体の重量が軽く、したがって保水時の重量も軽くできるため、その保水率を１５０％以上まで高めることができ、これにより十分な保水量を得られることで、コンクリートの表面を長期にわたって湿潤状態に保つことができる。反対に保水率が１５０％未満であると、十分な保水量が得られず、短期間に乾燥してしまい、コンクリート養生の機能を果たせなくなるという不都合が生じやすい。 The curing sheet 12 preferably has a tensile strength of 100 N / 5 cm width or more as a practical strength. If the tensile strength is less than 100 N / 5 cm width, it will not have the required strength as a concrete curing sheet, and there is the inconvenience that tearing may occur when affixed to concrete with water retained. It tends to occur. And it is preferable that the water retention of prescription | regulation sheet | seat 12 prescribed | regulated to JIS-L1913 is 150% or more. That is, the sheet 13 for curing is light in weight of the sheet itself as understood from the above-mentioned preferred basis weight range, and thus can also reduce the weight during water retention, so that the water retention rate can be increased to 150% or more, As a result, a sufficient amount of water can be obtained, so that the surface of the concrete can be kept wet for a long time. On the other hand, when the water retention rate is less than 150%, a sufficient amount of water retention cannot be obtained, and the inconvenience of drying in a short time and being unable to perform the function of concrete curing is likely to occur.

以下の実施例、比較例における各種の評価は、下記の手法によって行った。 Various evaluations in the following examples and comparative examples were performed by the following methods.

（１）目付［ｇ／ｍ^２］
標準状態の試料から試料長１０ｃｍ、試料幅５ｃｍの試料片を１０点採取した。各試料片の質量［ｇ］を評量し、得られた値の平均値を単位面積あたりに換算して、目付とした。 (1) Weight per unit [g / m ² ]
Ten sample pieces having a sample length of 10 cm and a sample width of 5 cm were collected from the standard sample. The mass [g] of each sample piece was weighed, and the average value obtained was converted per unit area to obtain the basis weight.

（２）厚み［μｍ］
ＪＩＳＬ１９０８に従い、標準状態の試料から、プレッサーフットの直径の１．７５倍以上の大きさの試験片を１０点採取し、２ｋＰａの荷重で測定を行い、その平均値を示した。 (2) Thickness [μm]
In accordance with JIS L1908, 10 test pieces having a size of 1.75 times the diameter of the presser foot were collected from the standard state sample, measured at a load of 2 kPa, and the average value was shown.

（３）引張強力［Ｎ／５ｃｍ幅］
ＪＩＳＬ１９０８に従い、標準状態の試料から、幅５ｃｍ×長さ２０ｃｍの試験片を縦横それぞれ５個採取し、つかみ間隔１０ｃｍ，引張速度２ｃｍ／ｍｉｎの条件で測定し、各々その平均値を示した。 (3) Tensile strength [N / 5cm width]
In accordance with JIS L1908, 5 specimens each having a width of 5 cm and a length of 20 cm were taken from a sample in a standard state and measured under the conditions of a gripping interval of 10 cm and a tensile speed of 2 cm / min, and the average value was shown for each.

（４）伸度［％］
引張強力の測定時に、最大強度を示した時点の伸び率を算出し、縦横それぞれ５個の値の平均値を示した。 (4) Elongation [%]
At the time of measuring the tensile strength, the elongation at the time when the maximum strength was shown was calculated, and the average value of 5 values in the vertical and horizontal directions was shown.

（５）引裂強力［Ｎ］
ＪＩＳＬ１９１３のペンジュラム法に従い、縦横それぞれ５個の試験を行い、各々その平均値を示した。 (5) Tear strength [N]
According to the JIS L1913 pendulum method, five tests were conducted in each of the vertical and horizontal directions, and the average value was shown.

（６）保水率［％］
ＪＩＳＬ−１９１３に基づき測定した。 (6) Water retention rate [%]
It measured based on JIS L-1913.

（７）貼り付け後１週間の様子
５０ｃｍ角の大きさの試料を水に浸した後に持ち上げ、フィルム面を上側とした水平姿勢で３０秒間保持することで余分な水分を落とした。そして、表面が平滑な鉛直方向のコンクリート壁に、しわや浮きが発生しないように貼り付けて、その後の１週間の様子を観察した。そのときに、試料がコンクリート壁に貼り付いているか否かの状態は、目視にて観察した。試料が水分を保持しているか否かは、試料の一部分をコンクリート壁から剥離させて、指先の触感およびコンクリート表面の濡れ状態の目視の確認により、判定した。 (7) State of one week after pasting A sample having a size of 50 cm square was dipped in water, then lifted, and held for 30 seconds in a horizontal posture with the film surface on the upper side to remove excess water. And it affixed on the concrete wall of the perpendicular direction with the smooth surface so that a wrinkle and a float may not generate | occur | produce, and observed the mode for the following one week. At that time, whether or not the sample was stuck on the concrete wall was visually observed. Whether or not the sample retained moisture was determined by peeling a part of the sample from the concrete wall and visually confirming the touch feeling of the fingertip and the wet state of the concrete surface.

（実施例１）
コットン繊維のみを用い、＃１００メッシュのネット状のウェブ支持体を用いた公知のスパンレース法により、目付６０ｇ／ｍ^２で表面が平滑なコットンスパンレース不織布を得た。この不織布に、ポリエチレンテレフタレート（ＰＥＴ）製の厚さ１６μｍのフィルムを貼り合わせた。貼り合わせは、ポリエチレンを用いた押し出しラミネートの手法により行った。ポリエチレン層の厚さは１５μｍとした。これにより、実施例１のコンクリート養生用シートを得た。このシートの各特性の測定結果を表１に示す。 Example 1
A cotton spunlace nonwoven fabric with a basis weight of 60 g / m ² and a smooth surface was obtained by a known spunlace method using only a cotton fiber and a # 100 mesh net-like web support. A 16 μm thick film made of polyethylene terephthalate (PET) was bonded to this nonwoven fabric. Bonding was performed by an extrusion laminating method using polyethylene. The thickness of the polyethylene layer was 15 μm. This obtained the concrete curing sheet of Example 1. Table 1 shows the measurement results of the characteristics of this sheet.

（実施例２）
コットン繊維とＰＥＴ短繊維とを、質量比で、（コットン繊維）／（ＰＥＴ短繊維）＝６０／４０で混綿したものを用い、＃２５メッシュのネット状のウェブ支持体を用いた公知のスパンレース法により、目付７５ｇ／ｍ^２で表面に上記メッシュに対応した凹凸を有するスパンレース不織布を得た。そして、それ以外は実施例１と同じとして、実施例２のコンクリート養生用シートを得た。このシートの各特性の測定結果を表１に示す。 (Example 2)
A known span using a # 25 mesh net-like web support using a mixture of cotton fibers and PET short fibers in a mass ratio of (cotton fibers) / (PET short fibers) = 60/40 By a lace method, a spunlace nonwoven fabric having a surface area of 75 g / m ² and having irregularities corresponding to the mesh on the surface was obtained. And otherwise, it was the same as that of Example 1, and the concrete curing sheet of Example 2 was obtained. Table 1 shows the measurement results of the characteristics of this sheet.

（比較例１）
不織布として、ＰＥＴ長繊維９０質量％、アクリル系水性樹脂１０質量％、目付が７０ｇ／ｍ^２で熱圧接タイプの、長繊維スパンボンド不織布（ユニチカ社製製品名「マリックス１０７０６／ＷＴＤ」）を用いた。そして、それ以外は実施例１と同じとして、比較例１のコンクリート養生用シートを得た。このシートの各特性の測定結果を表１に示す。 (Comparative Example 1)
As the non-woven fabric, a long-fiber spunbonded non-woven fabric (product name “Marix 10706 / WTD” manufactured by Unitika Co., Ltd.) of 90% by mass of PET long fiber, 10% by mass of acrylic water-based resin, and a basis weight of 70 g / m ² is used. It was. Other than that, the concrete curing sheet of Comparative Example 1 was obtained in the same manner as Example 1. Table 1 shows the measurement results of the characteristics of this sheet.

（比較例２）
不織布として、ＰＥＴ長繊維９９質量％、親水性界面活性剤１質量％で、目付が１４０ｇ／ｍ^２の、ニードルパンチ不織布（ユニチカ社製製品名「アピールＡＮ１２０」）を用いた。そして、それ以外は実施例１と同じとして、比較例２のコンクリート養生用シートを得た。このシートの各特性の測定結果を表１に示す。 (Comparative Example 2)
As the non-woven fabric, a needle punch non-woven fabric (product name “Appeal AN120” manufactured by Unitika Ltd.) having 99% by mass of PET long fibers, 1% by mass of a hydrophilic surfactant and having a basis weight of 140 g / m ² was used. And other than that was the same as Example 1, and obtained the concrete curing sheet of Comparative Example 2. Table 1 shows the measurement results of the characteristics of this sheet.

１２コンクリート養生用シート
１３フィルム
１４不織布 12 Concrete curing sheet 13 Film 14 Non-woven fabric

Claims

合成樹脂製のフィルムと、コットン繊維を５０質量％を超えて含有するスパンレース不織布とが積層されていることを特徴とするコンクリート養生用シート。 A concrete curing sheet, characterized in that a synthetic resin film and a spunlace nonwoven fabric containing more than 50 mass% of cotton fibers are laminated.

スパンレース不織布は、目付が５０ｇ／ｍ^２以上であることを特徴とする請求項１記載のコンクリート養生用シート。 ^2. The concrete curing sheet according to claim 1, wherein the spunlace nonwoven fabric has a basis weight of 50 g / m ² or more.

引張強力が１００Ｎ／５ｃｍ幅以上であるとともに、ＪＩＳ−Ｌ１９１３に規定される保水率が１５０％以上であることを特徴とする請求項１または２項記載のコンクリート養生用シート。 The concrete curing sheet according to claim 1 or 2, wherein the tensile strength is 100 N / 5 cm width or more and the water retention rate specified in JIS-L1913 is 150% or more.