Abstract

PROBLEM TO BE SOLVED: To propose a re-sealable packaging bag which can be acquired only in a normal bag making step without requiring a conventional complex step, and a package capable of solving problems regarding wet tissues and the like by using the packaging bag as an outer bag of wet tissues and the like.SOLUTION: A packaging bag is constituted by making sealant layers of a surface laminate 6a and a rear laminate 6b having a base material layer 5, an adhesive layer 3 and a sealant layer 2 face each other, and by heat-sealing a peripheral edge. A tip end part of an opening seal part 8 which becomes an opening part has a non-sealed part 7, and by peeling off the opening seal part while gripping the non-sealed part of the surface laminate and the rear laminate, the adhesive layer of the opening seal part is exposed, and the opening part exhibits re-sealability.SELECTED DRAWING: Figure 1

Description

本発明は再封止可能な包装袋に関し、特にウェットティッシュ等を収納した包装袋の外袋として用いる包装袋、及びこれを用いた包装体に関する。   The present invention relates to a resealable packaging bag, and more particularly to a packaging bag used as an outer bag of a packaging bag containing wet tissue and the like, and a package using the same.

再封止可能な包装袋の例として、例えばウェットティッシュは、耐水性の紙や不織布に水や、保湿剤等を含ませたものを再封止可能な包装袋に収納したものが販売されている。このような用途に用いる包装袋としては、内容物を取り出すための取り出し口に、再封止可能な粘着シートを貼り付けた軟包装袋が一般的に用いられている。   As an example of a resealable packaging bag, for example, a wet tissue is sold in which a water-resistant paper or non-woven fabric containing water or a moisturizer is contained in a resealable packaging bag. Yes. As a packaging bag used for such an application, a flexible packaging bag in which a resealable adhesive sheet is attached to a takeout port for taking out contents is generally used.

しかし、このような構成の包装袋は、取り出し口に貼り付ける粘着シートを別途に準備しなければならず、製造に要する手間とコストが問題となっていた。特許文献１に記載された包材および包装体は、これらの問題を解決するためになされたものであり、別体の蓋材を用いることなく、再封することが可能であり、かつ、簡便安価に製造することができる包材を提供することを目的としたものである。   However, the packaging bag having such a configuration has to separately prepare a pressure-sensitive adhesive sheet to be attached to the take-out port, and there is a problem in labor and cost required for manufacturing. The packaging material and package described in Patent Document 1 have been made in order to solve these problems, can be resealed without using a separate lid, and are simple An object of the present invention is to provide a packaging material that can be manufactured at low cost.

特許文献１に記載された包材は、取り出し口とその周囲部分に粘着剤層を設けた積層体を用いて、外面側からは取り出し口より大きな第１の切り込みを設け、内面側からは、取り出し口に相当する第２の切り込みを設けることにより、第１の切り込みと第２の切り込みの間の部分に粘着剤層を露出させ、この粘着剤層によって開口部の再封性を実現したものである。   The packaging material described in Patent Document 1 is provided with a first cut larger than the takeout port from the outer surface side using a laminate in which a pressure-sensitive adhesive layer is provided on the takeout port and the surrounding portion, and from the inner surface side, By providing a second notch corresponding to the outlet, the adhesive layer is exposed in a portion between the first notch and the second notch, and the resealability of the opening is realized by this adhesive layer. It is.

しかし、特許文献１に記載された包材は、製造の際に積層体の特定の部分に粘着剤を塗布し、この塗布部分に位置合わせをしながら切り込みを設ける必要があるが、粘着剤は一般的に無色透明であり、この透明な粘着剤に位置合わせをしながら、表裏両面から切り込みを入れるという非常に煩雑な工程を要するという問題があった。   However, in the packaging material described in Patent Document 1, it is necessary to apply a pressure-sensitive adhesive to a specific part of the laminate during production, and to provide a cut while aligning the applied part. In general, it is colorless and transparent, and there is a problem that it requires a very complicated process of making incisions from both the front and back sides while aligning the transparent adhesive.

また、上記のような問題に加えて、ウェットティッシュを収納した包装袋に関する別の問題点として、何度か使用するうちに開口部の再封性が十分でなくなり、ウェットティッシュが乾燥してしまうという問題があった。   In addition to the above problems, another problem with packaging bags containing wet tissue is that the resealability of the opening becomes insufficient and the wet tissue dries out after several uses. There was a problem.

またさらに別の問題として、しばしば使用済みのウェットティッシュを収納する方法に困る場合があった。   Yet another problem is often the difficulty in storing used wet tissue.

特開２０１４−１３１９１６号公報JP 2014-131916 A

本発明の解決しようとする課題は、従来のような煩雑な工程を必要とせず、通常の製袋工程のみによって得られる、再封止可能な包装袋、およびこの包装袋をウェットティッシュ等の外袋として用いることにより、ウェットティッシュ等に関する上記の問題点を解消することができる包装体を提案するものである。   The problem to be solved by the present invention is that a re-sealable packaging bag obtained by only a normal bag-making process without requiring a complicated process as in the prior art, and the packaging bag outside a wet tissue or the like. The present invention proposes a package that can eliminate the above-mentioned problems relating to wet tissue and the like by using it as a bag.

上記の課題を解決するための手段として、請求項１に記載の発明は、基材層、粘着層、シーラント層を有する表面積層体及び裏面積層体のシーラント層同士が対向されて、周縁が熱シールされてなる包装袋であって、開口部となる開口シール部の先端部に未シール部を有し、表面積層体及び裏面積層体の該未シール部を把持して該開口シール部を引き剥がすことにより、該開口シール部の粘着層が露出し、開口部が再封止性を発現することを特徴とする包装袋である。   As a means for solving the above problems, the invention according to claim 1 is such that the base layer, the adhesive layer, the surface laminate having the sealant layer, and the sealant layers of the back laminate are opposed to each other, and the periphery is heated. A sealed packaging bag having an unsealed portion at the front end portion of the opening seal portion serving as an opening, and gripping the unsealed portion of the front surface laminate and the back surface laminate to pull the opening seal portion. By peeling off, the adhesive layer of the opening seal part is exposed, and the opening part exhibits resealability.

本発明に係る包装袋は、全面に粘着層を有する積層体の周縁部を熱シールしてなる包装袋であるため、シール部を引き剥がすことにより、粘着層が露出し、再封止性を発現する。   Since the packaging bag according to the present invention is a packaging bag formed by heat-sealing the peripheral portion of the laminate having the adhesive layer on the entire surface, the adhesive layer is exposed by peeling off the seal portion, and resealability is achieved. To express.

また、請求項２に記載の発明は、前記開口シール部の先端部の未シール部のさらに先端部が熱シールされており、前記未シール部に開封予定部を有することを特徴とする請求項１に記載の包装袋である。   The invention according to claim 2 is characterized in that the tip of the unsealed portion at the tip of the opening seal portion is further heat sealed, and the unsealed portion has a portion to be opened. 1. The packaging bag according to 1.

また、請求項３に記載の発明は、ウェットティッシュを収納した包装体の外袋であることを特徴とする請求項１または２に記載の包装袋である。   The invention according to claim 3 is the packaging bag according to claim 1 or 2, which is an outer bag of a packaging body containing a wet tissue.

また、請求項４に記載の発明は、前記開口シール部の内側に、使用後のウェットティッシュを収納するための仕切り部を有することを特徴とする請求項３に記載の包装袋である。   The invention according to claim 4 is the packaging bag according to claim 3, further comprising a partition part for storing the wet tissue after use inside the opening seal part.

また、請求項５に記載の発明は、前記表面積層体および裏面積層体が、水蒸気バリア層を有することを特徴とする請求項１〜４のいずれか１項に記載の包装袋である。
請求項６に記載の発明は、請求項１〜５のいずれか１項に記載の包装袋に、ウェットティッシュを収納した包装体を収納した包装体である。 The invention according to claim 5 is the packaging bag according to any one of claims 1 to 4, wherein the front surface laminate and the back surface laminate have a water vapor barrier layer.
Invention of Claim 6 is the package which accommodated the package which accommodated the wet tissue in the packaging bag of any one of Claims 1-5.

本発明に係る包装袋は、基材層、粘着層、シーラント層を有する表面積層体及び裏面積層体のシーラント層同士が対向されて、周縁が熱シールされてなる包装袋であって、開口部となる開口シール部の先端部に未シール部を有し、表面積層体及び裏面積層体の該未シール部を把持して該開口シール部を引き剥がすことにより、該開口シール部の粘着層が露出し、開口部が再封止性を発現するものであるから、積層体のどの部分を用いて包装袋を作成しても、同様の再封止性が発揮される。このため、製造工程において、再封止部の位置合わせ等の煩雑な手間が不要となり、生産効率が向上する。   The packaging bag according to the present invention is a packaging bag in which a base layer, an adhesive layer, a surface laminate having a sealant layer, and a sealant layer of a back laminate are opposed to each other, and the periphery is heat-sealed. The opening seal portion has an unsealed portion at the tip, and the adhesive layer of the opening seal portion is formed by gripping the unsealed portions of the front surface laminate and the back surface laminate and peeling off the opening seal portion. Since it is exposed and the opening develops resealability, the same resealability is exhibited no matter which part of the laminate is used to create the packaging bag. For this reason, in a manufacturing process, complicated work, such as alignment of a reseal part, becomes unnecessary, and production efficiency improves.

包装袋の熱シール部は、いずれの熱シール部も同様に再封止性を発揮するものであるため、開口シール部に限らず、他のシール部から開封しても、再封止することができる。また、開口シール部のシール形状は、設計の自由度が高く、さまざまな形状を自由に設計できる。また、開口シール部の先端部に未シール部を有するので、開封時に手で持ち易く、開封が容易である。   The heat-sealed part of the packaging bag also exhibits resealability in the same way as any heat-sealed part, so it should be resealed not only from the open-sealed part but also from other sealed parts. Can do. Further, the seal shape of the opening seal portion has a high degree of design freedom, and various shapes can be freely designed. Moreover, since the unsealed portion is provided at the tip of the opening seal portion, it is easy to hold by hand when opening, and opening is easy.

包装袋の再封止性は、粘着層が露出することによって発揮されるものであるため、再封止に当たっては、指で加圧圧着するだけの簡単な操作で容易に再封止することができる。   Since the resealability of the packaging bag is exhibited when the adhesive layer is exposed, it can be easily resealed with a simple operation of pressure-pressing with a finger. it can.

またさらに、包装袋を構成する積層体は、全面に亘って均一なものであるから、包装袋には特に局所的な凹凸がなく、包装袋の厚さが均一であるという特徴を有する。   Furthermore, since the laminated body constituting the packaging bag is uniform over the entire surface, the packaging bag has no particular local unevenness, and the thickness of the packaging bag is uniform.

請求項２に記載の発明のように、前記開口シール部の先端部の未シール部のさらに先端部が熱シールされており、前記未シール部に開封予定部を有する場合には、未開封の状態で、開口シール部が外気に晒されることがなく、保存性に優れ、また衛生的である。   As in the second aspect of the present invention, when the tip of the unsealed portion of the tip of the opening seal portion is heat sealed, and the unsealed portion has a portion to be opened, In this state, the opening seal portion is not exposed to the outside air, is excellent in storage stability, and is hygienic.

請求項３に記載の発明のように、本発明に係る包装袋をウェットティッシュ等を収納した包装体の外袋として使用した場合には、特にその特徴が十分に発揮される。さらに、請求項４に記載したように、前記開口シール部の内側に、使用後のウェットティッシュ等を収納するための仕切り部を有する場合においては、従来その処置に不便を来たしていた、使用後のウェットティッシュ等を収納することができるので、極めて使い勝手が良い。   When the packaging bag according to the present invention is used as an outer bag of a package containing a wet tissue or the like as in the invention described in claim 3, the characteristics are sufficiently exhibited. Furthermore, when it has a partition part for storing the wet tissue etc. after use inside the said opening seal | sticker part as described in Claim 4, after the use which has come to be inconvenient for the treatment conventionally It can be used for storing wet tissue, etc., so it is extremely convenient.

請求項５に記載の発明のように、表裏面の積層体が、水蒸気バリア層を含む場合には、仮にウェットティッシュを収納した包装体の密封性が十分でない場合であってもウェットティッシュが乾燥することがなく、保存性、保湿性が十分に発揮される。   When the laminate on the front and back surfaces includes a water vapor barrier layer as in the invention described in claim 5, the wet tissue is dried even if the sealing property of the package containing the wet tissue is not sufficient. This ensures that the storage and moisture retention are fully demonstrated.

図１は、本発明に係る包装袋の一実施態様を示した平面説明図である。FIG. 1 is an explanatory plan view showing one embodiment of a packaging bag according to the present invention. 図２は、本発明の請求項２に係る包装袋の一実施態様を示した平面説明図である。FIG. 2 is an explanatory plan view showing an embodiment of a packaging bag according to claim 2 of the present invention. 図３は、本発明の請求項４に係る包装袋に、ウェットティッシュを収納した包装体を収納した包装体を示した平面説明図である。FIG. 3 is an explanatory plan view showing a package in which a package containing wet tissue is stored in a packaging bag according to claim 4 of the present invention. 図４は、図３に示した包装体のＸ−Ｘ´断面を示した断面模式図である。FIG. 4 is a schematic cross-sectional view showing the XX ′ cross-section of the package shown in FIG. 3. 図５は、図３に示した包装体のＹ−Ｙ´断面を示した断面模式図である。FIG. 5 is a schematic cross-sectional view showing the YY ′ cross section of the package shown in FIG. 3. 図６は、本発明に係る包装袋を構成する積層体の一例を示した断面模式図である。FIG. 6 is a schematic cross-sectional view showing an example of a laminate constituting the packaging bag according to the present invention.

以下、図面を参照しながら、本発明に係る包装袋１ならびにこれを用いた包装体２０について詳細に説明する。図１は、本発明に係る包装袋１の一実施態様を示した平面説明図である。また図６は、本発明に係る包装袋１を構成する積層体６の一例を示した断面模式図である。本発明に係る包装袋１は、基材層５、粘着層３、シーラント層２を有する表面積層体６ａ及び裏面積層体６ｂのシーラント層２同士が対向されて、周縁が熱シールされてなる包装袋である。開口部となる開口シール部８の先端部には、未シール部７を有し、表面積層体６ａ及び裏面積層体６ｂの未シール部７を把持して開口シール部８を引き剥がすことにより、開口シール部８の粘着層３が露出し、開口部が再封止性を発現することを特徴とする。   Hereinafter, the packaging bag 1 according to the present invention and the package 20 using the same will be described in detail with reference to the drawings. FIG. 1 is an explanatory plan view showing an embodiment of a packaging bag 1 according to the present invention. FIG. 6 is a schematic cross-sectional view showing an example of a laminated body 6 constituting the packaging bag 1 according to the present invention. The packaging bag 1 according to the present invention is a packaging in which the surface layer 6a having the base material layer 5, the adhesive layer 3, and the sealant layer 2 and the sealant layer 2 of the back surface laminate 6b are opposed to each other and the periphery is heat-sealed. It is a bag. By having an unsealed portion 7 at the tip of the opening seal portion 8 to be an opening, grasping the unsealed portion 7 of the front surface laminate 6a and the back surface laminate 6b, and peeling off the open seal portion 8; The adhesive layer 3 of the opening seal portion 8 is exposed, and the opening portion exhibits resealability.

図６において、図の左側は、表裏面の積層体が熱シールされた状態を示したものであり、図の右側は、シール部を引き剥がした状態をそれぞれ模式的に示したものである。この例では、表面積層体６ａのシーラント層２と粘着層３との間で剥離が生じ、表面積層体６ａの粘着層３が露出している。   In FIG. 6, the left side of the figure shows a state where the laminate on the front and back surfaces is heat-sealed, and the right side of the figure schematically shows a state where the seal portion is peeled off. In this example, peeling occurs between the sealant layer 2 and the adhesive layer 3 of the surface laminate 6a, and the adhesive layer 3 of the surface laminate 6a is exposed.

この露出した粘着層３が、開口部に再封止性をもたらす。表裏どちらの粘着層が剥離するかは特定されず、どちらか凝集力の弱い方が剥離する。どちらの粘着層が露出しても再封止性の機能としては同様である。この事は、製袋工程における製造条件に過度の厳密さが要求されないことを示しており、生産性が向上することに繋がる。   This exposed adhesive layer 3 provides resealability to the opening. It is not specified which of the front and back adhesive layers is peeled off, and the one with weaker cohesive strength peels off. Whichever adhesive layer is exposed, the resealability function is the same. This indicates that excessive strictness is not required for the manufacturing conditions in the bag making process, which leads to an improvement in productivity.

なお、図６に示した例では、表面積層体６ａ、裏面積層体６ｂは、それぞれ基材層５と粘着層３の間に、水蒸気バリア層４を有している。水蒸気バリア層４を備えた積層体は、水蒸気の透過性が小さくなるので、ウェットティッシュを収納した包装体の外袋として、
好都合である。 In the example shown in FIG. 6, the front surface laminate 6 a and the back surface laminate 6 b have the water vapor barrier layer 4 between the base material layer 5 and the adhesive layer 3, respectively. Since the laminated body provided with the water vapor barrier layer 4 has low water vapor permeability, as an outer bag of a package containing a wet tissue,
Convenient.

図２は、本発明の請求項２に係る包装袋の一実施態様を示した平面説明図である。この例では、開口シール部８の先端部の未シール部７のさらに先端部が熱シールされてトップシール部１１を形成しており、未シール部７に開封予定部９を有することを特徴とする。開封予定部９の両端には開封ノッチ１０が設けられている。   FIG. 2 is an explanatory plan view showing an embodiment of a packaging bag according to claim 2 of the present invention. In this example, the tip of the unsealed portion 7 at the tip of the opening seal portion 8 is further heat-sealed to form a top seal portion 11, and the unsealed portion 7 has a scheduled opening portion 9. To do. Opening notches 10 are provided at both ends of the planned opening portion 9.

包装袋１をこのように構成することにより、開封するまでの間、開口シール部８の外側が清潔に保たれる。開封予定部９に沿って開封した後は、図１に示した例と同様になる。   By configuring the packaging bag 1 in this manner, the outside of the opening seal portion 8 is kept clean until it is opened. After opening along the planned opening portion 9, the example is the same as that shown in FIG.

開封予定部９は、開封位置を示した仮想的なものであり、実際には何もなくても良いが、印刷などにより開封する位置を示しても良いし、実際に積層体に例えばハーフカット線を施して開封し易くしても良い。   The unscheduled opening portion 9 is a virtual one that indicates the opening position, and may actually be nothing, but may indicate the position to be opened by printing or the like, and may actually be, for example, half-cut into the laminate. You may make it easy to open with a line.

図３は、本発明の請求項４に係る包装袋１に、ウェットティッシュを収納した包装体１９を収納した包装体２０を示した平面説明図である。また図４、図５は、それぞれ図３のＸ−Ｘ´断面、Ｙ−Ｙ´断面を示した断面模式図である。   FIG. 3 is an explanatory plan view showing a package 20 containing a package 19 containing a wet tissue in the packaging bag 1 according to claim 4 of the present invention. 4 and 5 are cross-sectional schematic views showing the XX ′ cross section and the YY ′ cross section of FIG. 3, respectively.

この例は、本発明に係る包装袋１をウェットティッシュ包装体１９の外袋として利用したものである。この例では、さらに開口シール部８の内側に、使用済みのウェットティッシュ１６を収納するための仕切り部１５が設けられている。   In this example, the packaging bag 1 according to the present invention is used as an outer bag of the wet tissue package 19. In this example, a partition part 15 for storing the used wet tissue 16 is further provided inside the opening seal part 8.

仕切り部１５は、仕切りフィルム１４によってウェットティッシュ包装体１９の収納部と区画されており、開口シール部８を開くことにより、ここに使用済みのウェットティッシュ１６を収納できるようになっている。そのため、仕切りフィルム１４の上端は、開口シール部８より下の位置にあることが必要である。   The partition portion 15 is partitioned from the storage portion of the wet tissue package 19 by the partition film 14, and the used wet tissue 16 can be stored therein by opening the opening seal portion 8. Therefore, the upper end of the partition film 14 needs to be at a position below the opening seal portion 8.

このように、仕切り部１５が存在することにより、使用済みのウェットティッシュを安全に収納することができ、また開口部は、再封止できるため、バッグの中を濡らしたりすることもない。   As described above, the presence of the partition portion 15 allows the used wet tissue to be safely stored, and the opening portion can be resealed, so that the bag does not get wet.

次に、表裏面の積層体６ａ、６ｂを構成する各層について説明する。基材層５としては、一般的に軟包装材に用いられる各種合成樹脂フィルムが使用できる。具体的には、ポリプロピレン樹脂（ＰＰ）、ポリエチレンテレフタレート樹脂（ＰＥＴ）、ナイロン−６、ナイロン−６６等のポリアミド樹脂、ポリ塩化ビニル樹脂（ＰＶＣ）、ポリ塩化ビニリデン樹脂（ＰＶＤＣ）、ポリカーボネート樹脂（ＰＣ）等の各種合成樹脂フィルムが用いられる。   Next, each layer which comprises the laminated bodies 6a and 6b of front and back is demonstrated. As the base material layer 5, various synthetic resin films generally used for soft packaging materials can be used. Specifically, polyamide resins such as polypropylene resin (PP), polyethylene terephthalate resin (PET), nylon-6, nylon-66, polyvinyl chloride resin (PVC), polyvinylidene chloride resin (PVDC), polycarbonate resin (PC ) And other synthetic resin films are used.

水蒸気バリア層４としては、ポリ塩化ビニリデンフィルム、ポリビニルアルコールフィルム、エチレンビニルアルコール共重合体フィルム、ガスバリア性ナイロンフィルム、ガスバリア性ポリエチレンテレフタレート（ＰＥＴ）フィルム等のガスバリア性フィルムや、ＰＥＴフィルム等にアルミニウム等の金属を蒸着した金属蒸着フィルムや、ＰＥＴフィルムに酸化アルミニウムや酸化珪素等の無機酸化物を蒸着させた無機酸化物蒸着フィルム、あるいは、ポリ塩化ビニリデンコーティング等のガスバリアコーティング層、あるいはアルミニウム箔等の金属箔などを用いることができる。   Examples of the water vapor barrier layer 4 include a polyvinylidene chloride film, a polyvinyl alcohol film, an ethylene vinyl alcohol copolymer film, a gas barrier nylon film, a gas barrier polyethylene terephthalate (PET) film and the like, a PET film and the like such as aluminum. Metal vapor deposition film obtained by vapor deposition of metal, inorganic oxide vapor deposition film obtained by depositing inorganic oxide such as aluminum oxide and silicon oxide on PET film, gas barrier coating layer such as polyvinylidene chloride coating, aluminum foil, etc. A metal foil or the like can be used.

粘着層３としては、アクリル系粘着剤、ウレタン系粘着剤、シリコーン系粘着剤などの粘着剤や、各種粘着性樹脂を用いることができる。   As the pressure-sensitive adhesive layer 3, pressure-sensitive adhesives such as acrylic pressure-sensitive adhesives, urethane pressure-sensitive adhesives, and silicone pressure-sensitive adhesives, and various pressure-sensitive adhesive resins can be used.

粘着層３としては、ホットメルト系粘着樹脂をシーラント層と共押出した粘着シーラン
トフィルムなどを利用しても良い。このような粘着シーラントフィルムは、粘着層が片面に露出していると、巻き取ることができないので、シーラント層／粘着層／シーラント層のように、３層で押し出して用いられることが多い。 As the adhesive layer 3, an adhesive sealant film obtained by co-extruding a hot-melt adhesive resin with a sealant layer may be used. Since such an adhesive sealant film cannot be wound up when the adhesive layer is exposed on one side, it is often used by extruding in three layers like sealant layer / adhesive layer / sealant layer.

シーラント層２としては、ポリオレフィン系樹脂が一般的に使用され、具体的には、低密度ポリエチレン樹脂（ＬＤＰＥ）、中密度ポリエチレン樹脂（ＭＤＰＥ）、直鎖状低密度ポリエチレン樹脂（ＬＬＤＰＥ）、エチレン−酢酸ビニル共重合体（ＥＶＡ）、エチレン−αオレフィン共重合体、エチレン−メタアクリル酸樹脂共重合体などのエチレン系樹脂や、ポリエチレンとポリブテンのブレンド樹脂や、ホモポリプロピレン樹脂（ＰＰ）、プロピレン−エチレンランダム共重合体、プロピレン−エチレンブロック共重合体、プロピレン−αオレフィン共重合体などのポリプロピレン系樹脂等が使用される。   As the sealant layer 2, a polyolefin resin is generally used. Specifically, a low density polyethylene resin (LDPE), a medium density polyethylene resin (MDPE), a linear low density polyethylene resin (LLDPE), ethylene- Ethylene resins such as vinyl acetate copolymer (EVA), ethylene-α olefin copolymer, ethylene-methacrylic acid resin copolymer, blend resin of polyethylene and polybutene, homopolypropylene resin (PP), propylene- Polypropylene resins such as ethylene random copolymer, propylene-ethylene block copolymer, and propylene-α olefin copolymer are used.

仕切りフィルム１４としては、シーラント層２に用いた材料と同様の材料を用いた単体フィルムが使用できる。仕切り部１５を備えた本発明に係る包装袋は、ウェットティッシュを収納した包装体の外袋として最適であるが、一般的なティッシュペーパーを収納した包装体の外袋としても利用できる。以下実施例に基づいて本発明に係る包装袋について具体的に説明する。   As the partition film 14, a single film using the same material as that used for the sealant layer 2 can be used. The packaging bag according to the present invention provided with the partition portion 15 is optimal as an outer bag of a package containing wet tissue, but can also be used as an outer bag of a package containing general tissue paper. Hereinafter, based on an Example, the packaging bag concerning this invention is demonstrated concretely.

＜実施例１＞
基材層として厚さ１２μｍのＰＥＴ樹脂フィルムを用いた。水蒸気バリア層として、厚さ１５μｍの延伸ナイロンフィルムを用いた。粘着層及びシーラント層として、内層及び外層がＬＬＤＰＥで、中間層にウレタン系粘着剤層を有する３層構成のフィルムを共押出インフレーション法を用いて成膜したものを用いた。各層の厚さは、内層１５μｍ、粘着層１０μｍ、外層２５μｍとした。上記の各層をウレタン系接着剤を用いてドライラミネート法により積層し、表面積層体、裏面積層体とした。仕切りフィルムとしては、厚さ４０μｍのＬＬＤＰＥフィルムを用いた。 <Example 1>
A PET resin film having a thickness of 12 μm was used as the base material layer. As the water vapor barrier layer, a stretched nylon film having a thickness of 15 μm was used. As the pressure-sensitive adhesive layer and the sealant layer, a film having a three-layer structure in which an inner layer and an outer layer are LLDPE and a urethane-based pressure-sensitive adhesive layer is formed as an intermediate layer by using a coextrusion inflation method was used. The thickness of each layer was 15 μm for the inner layer, 10 μm for the adhesive layer, and 25 μm for the outer layer. Each of the above layers was laminated by a dry laminating method using a urethane-based adhesive to obtain a surface laminate and a back laminate. As the partition film, an LLDPE film having a thickness of 40 μm was used.

これらの材料を用いて、周縁を熱シールし、開口シール部を設け、開封予定部として、レーザーによるハーフカット線を設け、さらにＵ字型の開封ノッチを設けた。以上により図３に示したようなウェットッティッシュ包装体の外袋を作成した。得られた包装袋は、仕切り部を備えているため、使用済みのウェットティッシュを収納することができ、利便性が高いものであった。また、未使用のウェットティッシュの保存性についても良好であった。   Using these materials, the periphery was heat-sealed, an opening seal part was provided, a laser-cut half-cut line was provided as a planned opening part, and a U-shaped opening notch was further provided. Thus, an outer bag of a wet tissue package as shown in FIG. 3 was prepared. Since the obtained packaging bag was provided with the partition part, the used wet tissue could be accommodated and it was highly convenient. Moreover, the preservability of the unused wet tissue was also good.

１・・・包装袋
２・・・シーラント層
３・・・粘着層
４・・・水蒸気バリア層
５・・・基材層
６ａ・・・表面積層体
６ｂ・・・裏面積層体
７・・・未シール層
８・・・開口シール部
９・・・開封予定部
１０・・・開封ノッチ
１１・・・トップシール部
１２・・・サイドシール部
１３・・・ボトムシール部
１４・・・仕切りフィルム
１５・・・仕切り部
１６・・・使用済みのウェットティッシュ
１９・・・ウェットティッシュ包装体
２０・・・包装体 DESCRIPTION OF SYMBOLS 1 ... Packaging bag 2 ... Sealant layer 3 ... Adhesive layer 4 ... Water vapor barrier layer 5 ... Base material layer 6a ... Front surface laminated body 6b ... Back surface laminated body 7 ... Unsealed layer 8 ... opening seal part 9 ... planned opening part 10 ... opening notch 11 ... top seal part 12 ... side seal part 13 ... bottom seal part 14 ... partition film 15 ... partition 16 ... used wet tissue 19 ... wet tissue package 20 ... package

Claims (6)

基材層、粘着層、シーラント層を有する表面積層体及び裏面積層体のシーラント層同士が対向されて、周縁が熱シールされてなる包装袋であって、開口部となる開口シール部の先端部に未シール部を有し、表面積層体及び裏面積層体の該未シール部を把持して該開口シール部を引き剥がすことにより、該開口シール部の粘着層が露出し、開口部が再封止性を発現することを特徴とする包装袋。   It is a packaging bag in which the sealant layers of the front surface laminate and the back surface laminate having the base material layer, the adhesive layer, and the sealant layer are opposed to each other, and the peripheral edge is heat sealed, and the front end portion of the opening seal portion that becomes the opening portion Has an unsealed portion, grips the unsealed portions of the front surface laminate and the back surface laminated body and peels off the opening seal portion, thereby exposing the adhesive layer of the opening seal portion and resealing the opening portion. A packaging bag characterized by exhibiting a sealing property. 前記開口シール部の先端部の未シール部のさらに先端部が熱シールされており、前記未シール部に開封予定部を有することを特徴とする請求項１に記載の包装袋。   The packaging bag according to claim 1, wherein a distal end portion of an unsealed portion at a distal end portion of the opening seal portion is heat-sealed, and the unsealed portion has a planned opening portion. ウェットティッシュを収納した包装体の外袋であることを特徴とする請求項１または２に記載の包装袋。   The packaging bag according to claim 1 or 2, wherein the packaging bag is an outer bag of a packaging body containing a wet tissue. 前記開口シール部の内側に、使用後のウェットティッシュを収納するための仕切り部を有することを特徴とする請求項３に記載の包装袋。   The packaging bag according to claim 3, further comprising a partition part for storing the wet tissue after use inside the opening seal part. 前記表面積層体および裏面積層体は、水蒸気バリア層を有することを特徴とする請求項１〜４のいずれか１項に記載の包装袋。   The said surface laminated body and back surface laminated body have a water vapor | steam barrier layer, The packaging bag of any one of Claims 1-4 characterized by the above-mentioned. 請求項１〜５のいずれか１項に記載の包装袋に、ウェットティッシュを収納した包装体を収納した包装体。   The package which accommodated the package which stored the wet tissue in the packaging bag of any one of Claims 1-5.

Images