JP2018059627A - Slide member - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a slide member that can be produced with improved work efficiency and reduced processing cost.SOLUTION: A slide member has a slide face, and at least part of the slide face is constituted by a surface of a lubrication member. The slide member contains a substrate that is a sintered body of a molding containing metal powder and is integral with the lubrication member, and the lubrication member that is an injection molding of a resin composition containing a polyarylene sulfide resin and a carbon material.SELECTED DRAWING: Figure 1

Description

本発明は、摺動面を有する摺動部材に関する。   The present invention relates to a sliding member having a sliding surface.

固体潤滑剤が埋め込まれた摺動部材に求められる機能等は、年々厳しさを増している。そのため、優れた摺動性を長期間維持でき、かつ、低コストで製造が可能な固体潤滑剤の開発が求められている。   The functions and the like required for the sliding member in which the solid lubricant is embedded are becoming stricter year by year. Therefore, development of a solid lubricant that can maintain excellent slidability for a long period of time and can be manufactured at low cost is demanded.

固体潤滑剤が埋め込まれた摺動部材としては、例えば特許文献１において、円筒状の基体に半径方向の貫通孔を形成し、該貫通孔に固体潤滑剤として、人造黒鉛を主成分とした焼成体を埋め込んだ摺動部材が提案されている。   As a sliding member in which a solid lubricant is embedded, for example, in Patent Document 1, a radial through-hole is formed in a cylindrical base body, and a fire containing mainly artificial graphite as a solid lubricant in the through-hole is used. A sliding member in which the body is embedded has been proposed.

特開２０１３−１４６４５号公報JP 2013-14645 A

しかしながら、基体に半径方向の貫通孔を形成し、該貫通孔に固体潤滑剤を埋め込むためには、固体潤滑剤を基体に対して高精度に固定する必要があり、また、基体の貫通孔や、これに嵌合する固体潤滑剤を高精度に加工する必要があるため、作業効率および加工コストの観点から改善の余地がある。特に、固体潤滑剤として炭素系焼成体（焼成された人造黒鉛）を用いた場合、炭素系焼成体は塑性変形しにくいため、寸法精度を高めるためには切削加工等による成形が必要となり、加工コストがさらに増加するという懸念がある。加えて、貫通孔に固体潤滑剤を埋め込む構造では、摺動部材の使用中に、固体潤滑剤が摺動部材の基体から抜け落ちるという懸念がある。   However, in order to form a radial through hole in the base and embed the solid lubricant in the through hole, it is necessary to fix the solid lubricant to the base with high accuracy. Since it is necessary to process the solid lubricant fitted thereto with high accuracy, there is room for improvement from the viewpoint of work efficiency and processing cost. In particular, when a carbon-based fired body (fired artificial graphite) is used as the solid lubricant, the carbon-based fired body is difficult to plastically deform. There is a concern that costs will increase further. In addition, in the structure in which the solid lubricant is embedded in the through hole, there is a concern that the solid lubricant may fall out of the base of the sliding member during use of the sliding member.

そこで本発明は、摺動部材の製造における作業効率および加工コストを改善できる、摺動部材の提供を第一の目的とする。また、本発明は、摺動部材の製造における作業効率および加工コストを改善できるとともに、摺動部材の使用中に、固体潤滑剤が摺動部材の基体から抜け落ちるおそれが低減された、摺動部材の提供を第二の目的とする。   Then, this invention makes it the 1st objective to provide the sliding member which can improve the working efficiency and processing cost in manufacture of a sliding member. In addition, the present invention can improve the working efficiency and processing cost in manufacturing the sliding member, and the sliding member in which the risk of the solid lubricant falling off the base of the sliding member during use of the sliding member is reduced. Is the second purpose.

本発明は、以下に示す摺動部材を提供する。
［１］ 摺動面を有し、前記摺動面の少なくとも一部が潤滑部材の表面で構成される摺動部材であって、金属粉を含む成形体の焼結体であり、前記潤滑部材と一体化される基体と、ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物の射出成形体である前記潤滑部材と、を含む摺動部材。 The present invention provides the following sliding members.
[1] A sliding member having a sliding surface, wherein at least a part of the sliding surface is constituted by a surface of a lubricating member, and is a sintered body of a molded body containing metal powder, and the lubricating member And a lubricating member that is an injection-molded body of a resin composition containing a polyarylene sulfide-based resin and a carbon material.

［２］ 摺動面を有し、前記摺動面の少なくとも一部が潤滑部材の表面で構成される摺動部材であって、金属粉を含む成形体の焼結体である、前記潤滑部材を収容するための収容部を有する基体と、ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物の射出成形体であって、前記収容部内に配置された前記潤滑部材と、を含む摺動部材。   [2] The lubricating member having a sliding surface, wherein at least a part of the sliding surface is formed of a surface of the lubricating member, and is a sintered body of a molded body containing metal powder. A sliding body comprising: a base body having a housing portion for housing a resin; and an injection-molded body of a resin composition comprising a polyarylene sulfide resin and a carbon material, wherein the lubricating member is disposed in the housing portion Element.

［３］ 前記樹脂組成物における前記カーボン材料の含有率が、ほぼ５質量％以上ほぼ７０質量％以下である、［１］または［２］に記載の摺動部材。   [3] The sliding member according to [1] or [2], wherein a content of the carbon material in the resin composition is approximately 5% by mass or more and approximately 70% by mass or less.

［４］ 前記基体は内部空孔を有し、前記内部空孔内に潤滑油が含浸されている、［１］〜［３］のいずれかに記載の摺動部材。   [4] The sliding member according to any one of [1] to [3], wherein the base body has internal holes, and the internal holes are impregnated with a lubricating oil.

［５］ 前記基体は、ほぼ５％以上ほぼ５０％以下の開放気孔率を有する、［１］〜［４］のいずれかに記載の摺動部材。   [5] The sliding member according to any one of [1] to [4], wherein the base body has an open porosity of approximately 5% or more and approximately 50% or less.

［６］ 前記基体は、ほぼ１０％以上ほぼ５０％以下の表面開孔率を有する、［１］〜［５］のいずれかに記載の摺動部材。   [6] The sliding member according to any one of [1] to [5], wherein the base body has a surface porosity of approximately 10% to approximately 50%.

［７］ 前記基体は、前記収容部の内表面においてほぼ１０％以上ほぼ５０％以下の表面開孔率を有する、［２］に記載の摺動部材。   [7] The sliding member according to [2], wherein the base body has a surface area ratio of approximately 10% to approximately 50% on the inner surface of the housing portion.

［８］ 前記カーボン材料は、カーボンナノ繊維、カーボンブラックおよび黒鉛からなる群から選択される少なくとも１つである、［１］〜［７］のいずれかに記載の摺動部材。   [8] The sliding member according to any one of [1] to [7], wherein the carbon material is at least one selected from the group consisting of carbon nanofibers, carbon black, and graphite.

本発明によれば、摺動部材の製造における作業効率および加工コストを改善できる、摺動部材を提供することができる。また、本発明によれば、摺動部材の製造における作業効率および加工コストを改善できるとともに、摺動部材の使用中に、固体潤滑剤が摺動部材の基体から抜け落ちるおそれが低減された、摺動部材を提供することができる。   ADVANTAGE OF THE INVENTION According to this invention, the sliding member which can improve the working efficiency and manufacturing cost in manufacture of a sliding member can be provided. Further, according to the present invention, it is possible to improve the working efficiency and processing cost in manufacturing the sliding member, and reduce the possibility of the solid lubricant falling off from the base of the sliding member during use of the sliding member. A moving member can be provided.

（ａ）図は、本発明の第１の実施形態により製造される摺動部材の正面図であり、（ｂ）図は、（ａ）図のＢ−Ｂ線における断面図である。(A) The figure is a front view of the sliding member manufactured by the 1st Embodiment of this invention, (b) A figure is sectional drawing in the BB line of (a) figure. 基体の正面図である。It is a front view of a base. 基体、潤滑部材のインサート成形状態を示す金型の断面図である。It is sectional drawing of the metal mold | die which shows the insert molding state of a base | substrate and a lubricating member. 上記金型の固定型を、図３のＣ方向から見た平面図である。It is the top view which looked at the fixed type | mold of the said metal mold | die from the C direction of FIG. 本発明に係る他の実施形態により製造される摺動部材の正面図である。It is a front view of the sliding member manufactured by other embodiment which concerns on this invention.

図１（ａ）および（ｂ）を参照して、摺動部材１は円筒状を成し、その内周に相手材としての軸２（鎖線で示す）が挿入される。摺動部材１は、内周面４ａと凹円筒面状の合せ面４ｂとを備える基体４と、基体４の収容部４ｃに配置され、内周面に露出した内側面３ａおよび基体４の合せ面４ｂと密着した外側面３ｂを有する潤滑部材３とを備える。図１（ａ）に示すように、各潤滑部材３の内側面３ａと基体４の内周面４ａとで、例えば断面真円状の軸受面部１１を構成することができる。軸受１の外周面１２は、図示しないハウジングの内周面に圧入や接着等の手段で固定され、軸受１の内周に挿入された軸２が回転自在に支持される。このように軸２を回転側とする他、軸２を静止側とし、軸受１を回転側とすることもできる。なお、図１（ａ）においては潤滑部材３が５つ設けられる構成が例示されているが、潤滑部材３の数はこれに限定されず、摺動面の少なくとも一部が潤滑部材３の表面で構成されていればよい。   Referring to FIGS. 1A and 1B, the sliding member 1 has a cylindrical shape, and a shaft 2 (indicated by a chain line) as a mating member is inserted into the inner periphery thereof. The sliding member 1 includes a base 4 provided with an inner peripheral surface 4a and a concave cylindrical surface 4b, and an alignment of the inner surface 3a and the base 4 that are disposed in the housing 4c of the base 4 and exposed on the inner peripheral surface. And a lubricating member 3 having an outer surface 3b in close contact with the surface 4b. As shown in FIG. 1A, the inner surface 3 a of each lubricating member 3 and the inner peripheral surface 4 a of the base body 4 can constitute, for example, a bearing surface portion 11 having a perfectly circular cross section. An outer peripheral surface 12 of the bearing 1 is fixed to an inner peripheral surface of a housing (not shown) by means such as press fitting or adhesion, and a shaft 2 inserted into the inner periphery of the bearing 1 is rotatably supported. As described above, the shaft 2 can be the rotating side, the shaft 2 can be the stationary side, and the bearing 1 can be the rotating side. FIG. 1A illustrates a configuration in which five lubrication members 3 are provided, but the number of lubrication members 3 is not limited to this, and at least a part of the sliding surface is the surface of the lubrication member 3. It only has to be configured.

以下、実施の形態を示しつつ、本発明に係る摺動部材について詳細に説明する。
［第１の実施形態］
本実施形態に係る摺動部材は、金属粉を含む原料粉を成形型を用いて圧縮成形し、成形体（金属粉成形体）を加熱して焼結させることにより得られた基体４、および、基体４をインサート部品として、ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物を射出成形することにより、基体４の収容部４ｃに射出成形体として配置された樹脂組成物である潤滑部材３を含む。好ましくは、ポリアリーレンスルフィド系樹脂は樹脂組成物の主成分（重量比で最も重い成分）である。 Hereinafter, the sliding member according to the present invention will be described in detail while showing embodiments.
[First Embodiment]
The sliding member according to the present embodiment includes a base 4 obtained by compression-molding raw material powder containing metal powder using a mold, and heating and sintering the molded body (metal powder molded body), and Lubricating member which is a resin composition arranged as an injection-molded body in the accommodating portion 4c of the base body 4 by injection molding a resin composition containing a polyarylene sulfide resin and a carbon material using the base body 4 as an insert part 3 is included. Preferably, the polyarylene sulfide-based resin is the main component (the heaviest component by weight) of the resin composition.

以下、本発明に係る摺動部材として軸受を一例に挙げ、図１〜図４を参照しながら説明する。   Hereinafter, the sliding member according to the present invention will be described with reference to FIGS.

（１）基体４
図１を参照して、基体４は、軸受を製造する際に採用される通常の製造工程に従って、金属粉を含む成形体を焼結することにより得られた焼結体である。基体４は、潤滑部材３を収容するための収容部４ｃを備えている。金属粉を含む成形体は、例えば金属粉を主成分（重量比で最も多い成分）とする原料粉を成形型を用いて圧縮成形することによって得ることができる。圧縮成形により得られた成形体（金属粉成形体）を加熱して焼結させることにより、潤滑部材３を収容するための収容部４ｃを備えた基体４を得ることができる。 (1) Base 4
Referring to FIG. 1, base 4 is a sintered body obtained by sintering a molded body containing metal powder in accordance with a normal manufacturing process employed when manufacturing a bearing. The base body 4 includes a housing portion 4 c for housing the lubricating member 3. A molded body containing metal powder can be obtained, for example, by compression-molding raw material powder containing metal powder as a main component (a component having the largest weight ratio) using a molding die. By heating and sintering a molded body (metal powder molded body) obtained by compression molding, it is possible to obtain a base body 4 having a housing portion 4c for housing the lubricating member 3.

図２を参照して、成形型に原料粉を充填して圧縮することで、基体４に対応した形状の成形体４’（金属粉成形体）が成形される。この金属粉成形体４’には、その成形時に、基体４の収容部４ｃに相当する凹部４ａ’が形成されている。   Referring to FIG. 2, a molded body 4 ′ (metal powder molded body) having a shape corresponding to the substrate 4 is molded by filling the molding die with raw material powder and compressing. The metal powder molded body 4 ′ is formed with a recess 4 a ′ corresponding to the housing portion 4 c of the base body 4 at the time of molding.

次いで、金属粉成形体４’を焼結させるのに必要な焼結温度（例えば金属粉成形体４’が銅鉄系であれば、７５０〜９００℃程度）で加熱することにより、金属粉成形体４’を焼結させる。   Next, metal powder molding is performed by heating at a sintering temperature necessary to sinter the metal powder molded body 4 ′ (for example, about 750 to 900 ° C. if the metal powder molded body 4 ′ is copper iron-based). The body 4 'is sintered.

焼結された金属粉成形体４’は、寸法を矯正するためのサイジング工程に移送され、金型内での再圧縮により表面各部（内周面、外周面、および両端面）の寸法が矯正される。この際、少なくとも軸受面部１１となる内周面４ａの寸法が矯正されることで、高真円度の軸受面部１１を得ることができる。これにより、安定した軸受性能を得ることが可能となる。このように、軸受面部１１は最終的にはサイジング工程で仕上げられ、潤滑部材３を収容するための収容部４ｃを備えた基体４を得ることができる。   The sintered metal powder molded body 4 ′ is transferred to a sizing process for correcting the dimensions, and the dimensions of each surface portion (inner peripheral surface, outer peripheral surface, and both end surfaces) are corrected by recompression in the mold. Is done. Under the present circumstances, the bearing surface part 11 of high roundness can be obtained by correcting the dimension of the internal peripheral surface 4a used as the bearing surface part 11 at least. Thereby, stable bearing performance can be obtained. Thus, the bearing surface portion 11 is finally finished in the sizing process, and the base body 4 including the housing portion 4c for housing the lubricating member 3 can be obtained.

基体４を製造するために用いられる金属粉としては、例えば、銅を主成分（重量比で最も多い成分）とする銅系、鉄を主成分（重量比で最も多い成分）とする鉄系、銅および鉄を主成分（重量比で最も多い成分）とする銅鉄系をはじめとする任意の種類の金属の金属粉を用いることができる。この他、アルミニウム−青銅系等の特殊な金属の金属粉を用いることもできる。   Examples of the metal powder used to manufacture the substrate 4 include a copper-based material having copper as a main component (the most component by weight ratio), an iron-based material having iron as a main component (the most component by weight ratio), Metal powders of any kind of metal including copper-iron-based materials containing copper and iron as main components (the largest component by weight) can be used. In addition, a metal powder of a special metal such as aluminum-bronze can be used.

銅鉄系の金属粉を用いる場合には、鉄粉、銅粉、および低融点金属粉を混合した金属粉を用いることができる。低融点金属は、焼結時にそれ自体が溶融して液相焼結を進行させるための成分であり、銅よりも低融点の金属が使用される。具体的には７００℃以下の融点を有する金属、例えば錫（Ｓｎ）、亜鉛（Ｚｎ）、リン（Ｐ）を含む金属等が使用可能である。この中でも銅との相性の良い錫を用いるのが好ましい。低融点金属は、混合粉中にその単体粉を添加する他、他の金属粉と合金化することで添加することもできる。   When using copper iron-based metal powder, metal powder in which iron powder, copper powder, and low melting point metal powder are mixed can be used. The low-melting point metal is a component for melting itself at the time of sintering to advance liquid phase sintering, and a metal having a lower melting point than copper is used. Specifically, a metal having a melting point of 700 ° C. or lower, for example, a metal containing tin (Sn), zinc (Zn), or phosphorus (P) can be used. Among these, it is preferable to use tin having good compatibility with copper. The low melting point metal can be added by alloying with other metal powders in addition to adding the simple powder to the mixed powder.

上記の金属粉の他に、必要に応じてフッ化カルシウム等の焼結助剤やステアリン酸亜鉛等の潤滑剤を添加し、さらに固体潤滑剤粉としての黒鉛粉を添加することもできる。黒鉛粉を添加することで、焼結後の基体４の焼結組織中に黒鉛粒子を分散させることができる。そのため、軸受面部１１のうち基体４で形成される部分における潤滑性を高めることができる。   In addition to the above metal powder, a sintering aid such as calcium fluoride and a lubricant such as zinc stearate may be added as necessary, and further graphite powder as a solid lubricant powder may be added. By adding graphite powder, graphite particles can be dispersed in the sintered structure of the base 4 after sintering. Therefore, the lubricity in the part formed with the base | substrate 4 among the bearing surface parts 11 can be improved.

ここでは具体的には、基体４を構成する金属（元素）の割合は、例えばＦｅ粉、Ｃｕ粉、Ｓｎ粉の混合粉末であり、本実施形態ではさらに黒鉛粉が混合される。各粉末の配合割合は、例えば、Ｃｕ粉：ほぼ１０〜３０質量％、具体的には１０〜３０質量％（好ましくはほぼ１５〜２０質量％、具体的には１５〜２０質量％）、Ｓｎ粉：ほぼ０．５〜３．０質量％、具体的には０．５〜３．０質量％（好ましくはほぼ１．５〜２．０質量％、具体的には１．５〜２．０質量％）、黒鉛粉：ほぼ０．５〜７．０質量％、具体的には０．５〜７．０質量％（好ましくはほぼ０．５〜３．０質量％、具体的には０．５〜３．０質量％）とし、残りをＦｅ粉とする。Ｃｕ粉の配合割合は、これが少なすぎると摺動面部１１の内周面４ａの摺動性が低下し、多すぎると摺動面部１１の内周面４ａの耐摩耗性に問題が生じるので上記の範囲とする。   Specifically, the ratio of the metal (element) constituting the substrate 4 is, for example, a mixed powder of Fe powder, Cu powder, and Sn powder. In this embodiment, graphite powder is further mixed. The blending ratio of each powder is, for example, Cu powder: approximately 10 to 30% by mass, specifically 10 to 30% by mass (preferably approximately 15 to 20% by mass, specifically 15 to 20% by mass), Sn Powder: about 0.5 to 3.0% by mass, specifically 0.5 to 3.0% by mass (preferably about 1.5 to 2.0% by mass, specifically 1.5 to 2%. 0 mass%), graphite powder: approximately 0.5 to 7.0 mass%, specifically 0.5 to 7.0 mass% (preferably approximately 0.5 to 3.0 mass%, specifically 0.5 to 3.0% by mass), and the remainder is Fe powder. If the amount of Cu powder is too small, the slidability of the inner peripheral surface 4a of the sliding surface portion 11 is lowered, and if it is too large, there is a problem in the wear resistance of the inner peripheral surface 4a of the sliding surface portion 11. The range.

次に、Ｓｎ粉は、成形体４’（圧粉体）の焼結時にＣｕ粉を溶融させることにより、基体４のＦｅ組織同士を結合するためのＣｕ−Ｓｎ合金組織を形成するために配合されている。そのため、Ｓｎ粉の配合量が少なすぎると基体４の強度を十分に高めることができないが、Ｓｎ粉の配合量が多すぎると、基体４の高コスト化を招来する可能性がある。以上から、Ｃｕ粉およびＳｎ粉の配合割合は上記の範囲とする。   Next, Sn powder is blended to form a Cu-Sn alloy structure for bonding the Fe structures of the substrate 4 by melting the Cu powder during sintering of the compact 4 '(green compact). Has been. Therefore, if the amount of Sn powder is too small, the strength of the substrate 4 cannot be sufficiently increased. However, if the amount of Sn powder is too large, the cost of the substrate 4 may be increased. From the above, the blending ratio of Cu powder and Sn powder is in the above range.

また、黒鉛粉は、基体４に遊離黒鉛として残存させて基体４にて固体潤滑剤として機能させるために配合される。そのため、黒鉛粉の配合割合は、これが少なすぎると固体潤滑剤としての効果が低くなるが、多すぎると、黒鉛は、Ｆｅ、Ｃｕと比較して比重が小さいため、粉末の偏析、流動性の悪化、粉末充填性の悪化を引き起こすので上記の範囲とする。   Further, the graphite powder is blended so as to remain as free graphite in the base 4 and to function as a solid lubricant in the base 4. Therefore, if the blending ratio of the graphite powder is too small, the effect as a solid lubricant will be low. However, if it is too large, the specific gravity of graphite is smaller than that of Fe and Cu. Since the deterioration and deterioration of the powder filling property are caused, the above range is set.

（２）潤滑部材３
潤滑部材３を基体４の収容部４ｃに配置するために、基体４をインサート部品として、ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物が射出成形される。これにより、複数の潤滑部材３が基体４と一体化される。具体的に説明すると、複数の潤滑部材３が基体４の収容部４ｃに射出成形体として配置される（以後、インサート成形工程ともいう）。 (2) Lubricating member 3
In order to arrange the lubricating member 3 in the housing portion 4c of the base body 4, a resin composition containing a polyarylene sulfide-based resin and a carbon material is injection-molded using the base body 4 as an insert part. Thereby, the plurality of lubricating members 3 are integrated with the base body 4. More specifically, a plurality of lubricating members 3 are arranged as injection molded bodies in the accommodating portion 4c of the base 4 (hereinafter also referred to as an insert molding process).

図３を参照して、インサート成形工程は、固定型２１と、可動型２２とを備えた成形金型２０を用いることにより行うことができる。固定型２１には円柱部２１ａが設けられ、円柱部２１ａの外周面で基体４の内周面４ａが成形される。固定型２１のうち、潤滑部材３の端面を形成する成形面２１ｃには、ゲート２１ｂが設けられる。本実施形態では、固定型２１の成形面２１ｃに、複数（図示例では５つ）のゲート２１ｂが円周方向等間隔に配される（図４参照）。尚、ゲートの種類は、図示例のような点状ゲートに限らず、例えば環状のフィルムゲートとしてもよい。   With reference to FIG. 3, the insert molding step can be performed by using a molding die 20 including a fixed die 21 and a movable die 22. The fixed die 21 is provided with a cylindrical portion 21a, and the inner peripheral surface 4a of the base body 4 is formed on the outer peripheral surface of the cylindrical portion 21a. A gate 21 b is provided on a molding surface 21 c that forms an end surface of the lubricating member 3 in the fixed mold 21. In the present embodiment, a plurality (five in the illustrated example) of gates 21b are arranged at equal intervals in the circumferential direction on the molding surface 21c of the fixed die 21 (see FIG. 4). The type of the gate is not limited to the dotted gate as in the illustrated example, and may be, for example, an annular film gate.

インサート成形工程では、まず、固定型２１の円柱部２１ａに、基体４を差し込んで配置する。この状態で、可動型２２と固定型２１とを型締めすることでキャビティ２３が形成される。このとき、基体４は、固定型２１と可動型２２とで軸方向両側から挟持される。このキャビティ２３は、基体４の収容部４ｃに相当する。   In the insert molding step, first, the base body 4 is inserted into the cylindrical portion 21a of the fixed mold 21 and arranged. In this state, the cavity 23 is formed by clamping the movable mold 22 and the fixed mold 21. At this time, the base 4 is sandwiched between the fixed mold 21 and the movable mold 22 from both sides in the axial direction. The cavity 23 corresponds to the accommodating portion 4 c of the base body 4.

次いで、ランナ２１ｄからゲート２１ｂを介してポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物をキャビティ２３に射出する。これにより、キャビティ２３には溶融した樹脂組成物が充填される。キャビティ２３に満たされた樹脂組成物が冷却されて固化することにより、潤滑部材３が基体４の内周面４ａに配置され、軸受１が製造される。   Next, a resin composition containing a polyarylene sulfide-based resin and a carbon material is injected into the cavity 23 from the runner 21d through the gate 21b. As a result, the cavity 23 is filled with the molten resin composition. When the resin composition filled in the cavity 23 is cooled and solidified, the lubricating member 3 is disposed on the inner peripheral surface 4a of the base body 4, and the bearing 1 is manufactured.

上記実施形態によれば、例えば、熱可塑性樹脂であるポリアリーレンスルフィド系樹脂を主成分（重量比で最も多い成分）とし、カーボン材料をさらに含む樹脂組成物が収容部４ｃに射出される。これにより、潤滑部材３が収容部４ｃに配置された軸受１を効率的に、かつ、連続的に大量に製造することが可能となる。軸受１を効率的、かつ、連続的に大量に製造することが可能になるので、一つ一つの軸受１の製造コストを下げることが可能となる。また、潤滑部材３は、基体４の収容部４ｃに配置されている。そのため、潤滑部材３に含まれるポリアリーレンスルフィド系樹脂のアンカー効果により、合せ面４ｂ（収容部４ｃの内表面）において、基体４と潤滑部材３との結合力が高められる。これにより、軸受１の使用中に潤滑部材３が軸受１の基体４から抜け落ちるおそれを低減させることができる。   According to the above-described embodiment, for example, a resin composition containing a polyarylene sulfide-based resin, which is a thermoplastic resin, as a main component (a component having the largest weight ratio) and further containing a carbon material is injected into the housing portion 4c. Thereby, it becomes possible to manufacture the bearing 1 in which the lubricating member 3 is disposed in the housing portion 4c efficiently and continuously in large quantities. Since the bearing 1 can be manufactured efficiently and continuously in large quantities, the manufacturing cost of each bearing 1 can be reduced. Further, the lubricating member 3 is disposed in the housing portion 4 c of the base body 4. Therefore, due to the anchor effect of the polyarylene sulfide resin contained in the lubricating member 3, the bonding force between the base body 4 and the lubricating member 3 is enhanced on the mating surface 4b (inner surface of the accommodating portion 4c). Thereby, the possibility that the lubricating member 3 may fall off from the base 4 of the bearing 1 during use of the bearing 1 can be reduced.

（３）ポリアリーレンスルフィド系樹脂
本願発明に用いるポリアリーレンスルフィド系樹脂（以下、ＰＡＳ樹脂と称する。）は、一般的に下記一般式（１）で示される合成樹脂である。下記一般式（１）中のＡｒはアリーレン基であり、Ａｒとしては、例えば下記一般式（２）〜（７）に示されるものが挙げられる。 (3) Polyarylene sulfide-based resin The polyarylene sulfide-based resin (hereinafter referred to as PAS resin) used in the present invention is a synthetic resin generally represented by the following general formula (1). Ar in the following general formula (1) is an arylene group, and examples of Ar include those represented by the following general formulas (2) to (7).

［ｎは繰り返し単位−Ａｒ−Ｓ−の繰り返し数を表す自然数である。］ [N is a natural number representing the number of repeating units -Ar-S-. ]

［ＱはＦ、ＣｌおよびＢｒから選ばれるハロゲンまたはＣＨ_３を示し、ｍは１〜４の整数を示す。］ [Q represents halogen or CH ₃ selected from F, Cl and Br, and m represents an integer of 1 to 4. ]

本願発明に用いるＰＡＳ樹脂としては、上記一般式（１）中のＡｒが、上記一般式（２）である、ポリフェニレンスルフィド樹脂（以下、ＰＰＳ樹脂と称する。）を好適に用いることができる。   As the PAS resin used in the present invention, a polyphenylene sulfide resin (hereinafter referred to as PPS resin) in which Ar in the general formula (1) is the general formula (2) can be preferably used.

ＰＡＳ樹脂は、繰り返し単位（−Ａｒ−Ｓ−）の含有率が７０モル％以上であることが好ましく、９０〜１００モル％であることがより好ましい。ここでいう繰り返し単位の含有率とは、ＰＡＳ樹脂を構成する全モノマー１００％に占める繰り返し単位の割合をいう。繰り返し単位の含有率が７０モル％未満のＰＡＳ樹脂を用いた際には、潤滑部材３を形成した際に、低い吸水性に基づく、潤滑部材３における寸法変化の低減等の安定性を得にくい傾向にある。   The PAS resin preferably has a repeating unit (—Ar—S—) content of 70 mol% or more, and more preferably 90 to 100 mol%. The content rate of a repeating unit here means the ratio of the repeating unit which occupies for 100% of all the monomers which comprise PAS resin. When a PAS resin having a repeating unit content of less than 70 mol% is used, it is difficult to obtain stability such as reduction in dimensional change in the lubricating member 3 based on low water absorption when the lubricating member 3 is formed. There is a tendency.

ＰＡＳ樹脂を得るには既に良く知られた方法を用いることができ、例えば、特公昭４４−２７６７１号公報や特公昭４５−３３６８号公報に開示されているようなハロゲン置換芳香族化合物と硫化アルカリとの反応、特公昭４６−２７２５５号公報に開示されているような、ルイス酸触媒共存下における芳香族化合物と塩化硫黄との縮合反応、または米国特許第３２７４１６５号公報に開示されているような、アルカリ触媒もしくは銅塩等の共存下におけるチオフェノール類の縮合反応等によって合成されるが、目的に応じて具体的な方法を任意に選択することができる。   In order to obtain the PAS resin, a well-known method can be used. For example, halogen-substituted aromatic compounds and alkali sulfides disclosed in Japanese Patent Publication Nos. 44-27671 and 45-3368 are disclosed. A reaction with an aromatic compound and sulfur chloride in the presence of a Lewis acid catalyst, as disclosed in Japanese Patent Publication No. 46-27255, or as disclosed in US Pat. No. 3,274,165. Although it is synthesized by a condensation reaction of thiophenols in the presence of an alkali catalyst or a copper salt, a specific method can be arbitrarily selected according to the purpose.

具体的な方法としては、硫化ナトリウムとｐ−ジクロロベンゼンとをＮ−メチルピロリドン、ジメチルアセトアミド等のアミド系溶媒若しくはスルホラン等のスルホン系溶媒中で反応させることが挙げられる。なお、ＰＡＳ樹脂の結晶性に影響を与えない範囲で、例えば、下記一般式（８）〜（１２）に示される成分をＰＡＳ樹脂に含ませ、共重合成分とすることができる。下記一般式（８）〜（１２）に示される成分の添加量は、ＰＡＳ樹脂を構成する全モノマー１００％に対して３０モル％未満、好ましくは１０モル％未満で１モル％以上とすることができる。   As a specific method, sodium sulfide and p-dichlorobenzene are reacted in an amide solvent such as N-methylpyrrolidone and dimethylacetamide or a sulfone solvent such as sulfolane. In addition, in the range which does not affect the crystallinity of PAS resin, the component shown by following General formula (8)-(12) can be included in PAS resin and can be used as a copolymerization component, for example. The addition amount of the components represented by the following general formulas (8) to (12) is less than 30 mol%, preferably less than 10 mol% and 1 mol% or more with respect to 100% of all monomers constituting the PAS resin. Can do.

［Ｒはメチル基以外のアルキル基、ニトロ基、フェニル基、アルコキシ基等を示す。］ [R represents an alkyl group other than a methyl group, a nitro group, a phenyl group, an alkoxy group, or the like. ]

また、ＰＡＳ樹脂は、架橋型のものであるか、または部分的交差結合、すなわち、部分架橋を有するものであることが好ましい。部分的交差結合を有するＰＡＳ樹脂は、半架橋型またはセミリニア型のＰＡＳとも呼ばれる。架橋型ＰＡＳ樹脂は、ポリマの製造工程中に酸素存在下で熱処理を行うことによってポリマの分子量を必要な水準に高める。架橋型ＰＡＳ樹脂は、ポリマ分子の一部がお互いに酸素を介して二次元または三次元の架橋構造を有する。そのため、次に述べるリニア型ＰＡＳ樹脂に比較して高温環境下においても高い剛性を保持し、クリープ変形が少ない点や、応力緩和されにくい点で優れる。このように、架橋型または半架橋型のＰＡＳ樹脂は、リニア型（架橋のないもの）のＰＡＳ樹脂に比べて耐熱性、耐クリープ性および耐摩耗性に優れている。そのため、リニア型ＰＡＳ樹脂に比べて射出成形した成形品にバリの発生が少ない利点がある。   The PAS resin is preferably a cross-linked type or has a partial cross-linkage, that is, a partial cross-link. A PAS resin having a partial cross-linking is also called a semi-crosslinked or semi-linear PAS. The cross-linked PAS resin increases the molecular weight of the polymer to a necessary level by performing a heat treatment in the presence of oxygen during the production process of the polymer. In the crosslinked PAS resin, some polymer molecules have a two-dimensional or three-dimensional crosslinked structure through oxygen to each other. For this reason, it is excellent in that it maintains high rigidity even under a high temperature environment as compared with the linear PAS resin described below, and has little creep deformation and resistance to stress relaxation. As described above, the cross-linked or semi-cross-linked PAS resin is superior in heat resistance, creep resistance and wear resistance as compared with a linear (non-cross-linked) PAS resin. Therefore, there is an advantage that the occurrence of burrs is less in the injection-molded molded product than in the linear PAS resin.

一方、リニア型ＰＡＳ樹脂は、ポリマの製造工程において熱処理工程が無いためにポリマ分子中には架橋構造は含まれず、分子は一次元の直鎖状とされている。一般的にはリニア型ＰＡＳ樹脂は架橋型ＰＡＳ樹脂に比較して剛性が低く、靭性や伸びが多少高いのが特長とされている。また、リニア型ＰＡＳ樹脂は、特定方向からの機械的強度に優れたものである。さらにリニア型ＰＡＳ樹脂は、ポリマの純度が高く、吸湿が少ないために高温多湿雰囲気でもさらに寸法変化が少なく電気絶縁性の低下も少ないという利点がある。また、リニア型ＰＡＳ樹脂は、例えば分子量を調整して溶融粘度を低くすることが可能なことから、リニア型ＰＡＳ樹脂にカーボン材料等を多量に混合させた樹脂組成物の流動性が低下して射出成形時における歩留り率が低下する他、射出成形を行うこと自体が困難となることは回避される。   On the other hand, since the linear PAS resin does not include a heat treatment step in the production process of the polymer, the polymer molecule does not include a crosslinked structure, and the molecule is a one-dimensional linear chain. In general, linear PAS resins are characterized by low rigidity and somewhat higher toughness and elongation than cross-linked PAS resins. The linear PAS resin is excellent in mechanical strength from a specific direction. Further, the linear PAS resin has an advantage that since the polymer has high purity and low moisture absorption, the dimensional change is small and the electrical insulation is not deteriorated even in a high temperature and high humidity atmosphere. In addition, since the linear PAS resin can reduce the melt viscosity by adjusting the molecular weight, for example, the fluidity of the resin composition in which a large amount of a carbon material or the like is mixed with the linear PAS resin is reduced. In addition to a decrease in yield during injection molding, it is avoided that injection molding itself is difficult.

ＰＡＳ樹脂に架橋を形成するか、または部分的交差結合を形成する方法としては、例えば、低重合度のポリマを重合した後、空気が存在する雰囲気で加熱する方法や、架橋剤や分岐剤を添加する方法がある。   Examples of a method of forming a crosslink in the PAS resin or forming a partial crosslink include, for example, a method in which a polymer having a low polymerization degree is polymerized and then heated in an atmosphere in which air exists, a crosslinker or a branching agent is used. There is a method of adding.

ＰＡＳ樹脂の見かけの溶融粘度は、１０００ポアズ以上１００００ポアズ以下の範囲とするのが好ましい。見かけの溶融粘度が低すぎると、潤滑部材３の強度が低下しうる。一方、見かけの溶融粘度が高くなり過ぎると、成形性が低下しうると共に、基体４表面の開放気孔に溶融状態の樹脂材料が入り込みにくくなる。そのため、アンカー効果が低下する可能性がある。   The apparent melt viscosity of the PAS resin is preferably in the range of 1000 poise to 10,000 poise. If the apparent melt viscosity is too low, the strength of the lubricating member 3 can be reduced. On the other hand, if the apparent melt viscosity becomes too high, the moldability may be lowered and the molten resin material will not easily enter the open pores on the surface of the substrate 4. Therefore, the anchor effect may be reduced.

架橋性のＰＡＳ樹脂の溶融粘度は１０００〜５０００ポイズとすることができ、好ましくは２０００〜４０００ポイズである。溶融粘度が低すぎると、１５０℃以上の高温域で耐クリープ特性などの機械的特性が低下しうる。また、溶融粘度が大きすぎると成形性が劣る可能性がある。なお、溶融粘度の測定は、測定温度３００℃、オリフィスが穴径１ｍｍ、長さ１０ｍｍ、測定荷重２０ｋｇ／ｃｍ^２、予熱時間６分の条件下で、高化式フローテスタにて行うことができる。 The melt viscosity of the crosslinkable PAS resin can be 1000 to 5000 poise, and preferably 2000 to 4000 poise. If the melt viscosity is too low, mechanical properties such as creep resistance can be lowered at a high temperature of 150 ° C. or higher. Moreover, when melt viscosity is too large, moldability may be inferior. The melt viscosity can be measured with a Koka flow tester under the conditions of a measurement temperature of 300 ° C., an orifice having a hole diameter of 1 mm, a length of 10 mm, a measurement load of 20 kg / cm ² , and a preheating time of 6 minutes. .

また、部分的交差結合を有するＰＡＳ樹脂の熱安定性は、上記の溶融粘度測定条件にて、予熱６分後と３０分後の溶融粘度の変化率が−５０％〜１５０％の範囲であることが好ましい。なお、変化率は下記の式で表される。
［変化率＝（Ｐ３０−Ｐ６）／Ｐ６×１００（Ｐ６：予熱６分後の測定値、Ｐ３０：予熱３０分後の測定値）］。 Moreover, the thermal stability of the PAS resin having a partial cross-linking is such that the change rate of the melt viscosity after 6 minutes and 30 minutes after the preheating is in the range of −50% to 150% under the above-described melt viscosity measurement conditions. It is preferable. The rate of change is expressed by the following formula.
[Change rate = (P30−P6) / P6 × 100 (P6: measured value after 6 minutes of preheating, P30: measured value after 30 minutes of preheating)].

以上のような条件を満足する部分的交差結合を有するＰＡＳ樹脂としては、例えば、トープレン社製：Ｔ４、Ｔ４ＡＧ、ＴＸ−００７等をあげることができる。ＰＡＳ樹脂の重量平均分子量としては、２００００〜４５０００が好ましく、２５０００〜４００００がより好ましい。重量平均分子量が２００００より小さいときは、耐熱性が劣る傾向にあり、また、重量平均分子量が４５０００より大きいときは、複雑な精密な寸法精度に対する成形性が劣る傾向にある。なお、本発明における重量平均分子量とは、ＰＡＳ樹脂を溶媒に溶解させた後、ゲル・パーミエーション・クロマトグラフ（ＧＰＣ法）で測定されるポリスチレン換算での重量平均分子量を示し、該測定は後記の実施例にて示される条件で実施される。   Examples of the PAS resin having a partial cross bond that satisfies the above-described conditions include, for example, T4, T4AG, TX-007, etc. manufactured by Toprene. As a weight average molecular weight of PAS resin, 20000-45000 are preferable and 25000-40000 are more preferable. When the weight average molecular weight is smaller than 20000, the heat resistance tends to be inferior, and when the weight average molecular weight is larger than 45,000, the moldability for complicated precise dimensional accuracy tends to be inferior. The weight average molecular weight in the present invention indicates a weight average molecular weight in terms of polystyrene measured by gel permeation chromatograph (GPC method) after dissolving the PAS resin in a solvent. It implements on the conditions shown in the Example of this.

また、ＰＡＳ樹脂の分子量は、射出成形性を考慮すると、数平均分子量で１３０００〜３００００が好ましく、更に耐疲労性、高成形精度を考慮すると、数平均分子量で１８０００〜２５０００がより好ましい。数平均分子量が１３０００未満の場合には、分子量が低すぎて、耐疲労性が劣る傾向にある。一方、数平均分子量が３００００を越える場合には耐疲労性は向上するものの、必要な衝撃強度等の機械的強度を達成するために、例えば炭素繊維を含有させることが必要な場合がある。例えば１０〜５０質量％の炭素繊維を含有させると、成形時の溶融粘度が上記の上限値（１００００ポアズ）を超える。そのため、射出成形時に潤滑部材３の成形精度を確保することが困難になる傾向にある。なお、本発明における数平均分子量とは、ＰＡＳ樹脂を溶媒に溶解させた後、ゲル・パーミエーション・クロマトグラフ（ＧＰＣ法）で測定されるポリスチレン換算での数平均分子量を示し、該測定は後記の実施例にて示される条件で実施される。   The molecular weight of the PAS resin is preferably 13,000 to 30000 in terms of number average molecular weight in view of injection moldability, and more preferably 18000 to 25000 in terms of number average molecular weight in consideration of fatigue resistance and high molding accuracy. When the number average molecular weight is less than 13,000, the molecular weight is too low and the fatigue resistance tends to be inferior. On the other hand, when the number average molecular weight exceeds 30000, although fatigue resistance is improved, it may be necessary to contain, for example, carbon fiber in order to achieve necessary mechanical strength such as impact strength. For example, when 10-50 mass% carbon fiber is contained, the melt viscosity at the time of shaping | molding exceeds said upper limit (10000 poise). Therefore, it tends to be difficult to ensure the molding accuracy of the lubricating member 3 during injection molding. The number average molecular weight in the present invention indicates the number average molecular weight in terms of polystyrene measured by gel permeation chromatograph (GPC method) after dissolving the PAS resin in a solvent. It implements on the conditions shown in the Example of this.

ＰＡＳ樹脂の融点は、例えば約２２０〜２９０℃、好ましくは２８０〜２９０℃である。一般にＰＰＳ樹脂の融点は、約２８５℃であるため、ＰＡＳ樹脂としてＰＰＳ樹脂を用いることが好ましい。また、ＰＡＳ樹脂は吸水性が低いため、ＰＡＳ樹脂が含まれた潤滑部材３は吸水による寸法変化が低減される傾向にある。したがって、ＰＡＳ樹脂が含まれた潤滑部材３を有する軸受１は、潤滑部材３における焼き付きが生じにくく、かつ、吸水による寸法変化が低減されるという優れた安定性を有する傾向にある。   The melting point of the PAS resin is, for example, about 220 to 290 ° C, preferably 280 to 290 ° C. In general, since the melting point of the PPS resin is about 285 ° C., it is preferable to use the PPS resin as the PAS resin. Further, since the PAS resin has low water absorption, the lubricating member 3 containing the PAS resin tends to reduce dimensional changes due to water absorption. Therefore, the bearing 1 having the lubrication member 3 containing the PAS resin tends to have excellent stability that the seizure in the lubrication member 3 hardly occurs and the dimensional change due to water absorption is reduced.

（４）カーボン材料
樹脂組成物に配合されるカーボン材料としては、例えば、黒鉛、カーボンナノ繊維およびカーボンブラック等が挙げられる。カーボン材料の形態としては粉末状を挙げることができる。カーボン材料粉末としては、例えば黒鉛粉を用いることができ、具体的には、天然黒鉛粉および人造黒鉛粉の何れもが使用可能である。天然黒鉛粉は鱗片状を成しているため潤滑性に優れるという特徴を有する。一方、人造黒鉛粉は塊状を成しているため成形性に優れるという特徴を有する。尚、カーボン材料粉末は、結晶質粉である黒鉛粉に限らず、ピッチ粉やコークス粉等の非晶質粉を用いることもできる。カーボン材料としてカーボンナノ繊維を用いた場合には、潤滑部材３の曲げ弾性率などの機械的強度の向上を図ることができる。カーボンナノ繊維は、ピッチ系とＰＡＮ系とに大別されるが、何れも使用可能である。カーボンナノ繊維は、例えば、平均繊維径２０μｍ以下、平均繊維長０．０２〜０．２ｍｍのものを用いることができる。 (4) Carbon material As a carbon material mix | blended with a resin composition, graphite, carbon nanofiber, carbon black, etc. are mentioned, for example. Examples of the form of the carbon material include powder. As the carbon material powder, for example, graphite powder can be used, and specifically, any of natural graphite powder and artificial graphite powder can be used. Natural graphite powder has a feature of excellent lubricity because it is in the form of scales. On the other hand, artificial graphite powder has a feature that it is excellent in formability because it is in a lump shape. The carbon material powder is not limited to the graphite powder, which is a crystalline powder, but may be an amorphous powder such as pitch powder or coke powder. When carbon nanofibers are used as the carbon material, the mechanical strength such as the bending elastic modulus of the lubricating member 3 can be improved. Carbon nanofibers are broadly classified into pitch systems and PAN systems, and any of them can be used. For example, carbon nanofibers having an average fiber diameter of 20 μm or less and an average fiber length of 0.02 to 0.2 mm can be used.

カーボン材料粉末（例えば、黒鉛粉）にバインダを含めることもできる。バインダとしては樹脂バインダ粉を用いることができ、樹脂バインダ粉としては、例えばフェノール樹脂粉を用いることができる。必要に応じて成形助剤や潤滑剤、または改質剤等を添加して、カーボン材料粉末とバインダを均一に混合することが好ましい。   A binder can also be included in the carbon material powder (for example, graphite powder). As the binder, resin binder powder can be used, and as the resin binder powder, for example, phenol resin powder can be used. It is preferable to add a molding aid, a lubricant, a modifier, or the like as necessary to uniformly mix the carbon material powder and the binder.

潤滑部材３を構成する原料粉末として、上記のようにカーボン材料粉末および樹脂バインダ粉の混合粉末を用いる他、樹脂バインダの介在下でカーボン材料粉末を造粒した造粒粉を用いることもできる。造粒粉は、単体の樹脂バインダ粉やカーボン材料粉末と比べて比重が大きく、流動性が高い。そのため、造粒粉を含む樹脂組成物の成形型への供給がしやすくなり、所定形状に精度良く成形することが可能となる。   As the raw material powder constituting the lubricating member 3, in addition to using the mixed powder of the carbon material powder and the resin binder powder as described above, a granulated powder obtained by granulating the carbon material powder in the presence of the resin binder can also be used. The granulated powder has a larger specific gravity and higher fluidity than a single resin binder powder or carbon material powder. Therefore, it becomes easy to supply the resin composition containing the granulated powder to the molding die, and it becomes possible to accurately mold into a predetermined shape.

軸受１では、軸受面部１１の一部を構成する潤滑部材３がカーボン材料の供給源となる。潤滑部材３から供給されたカーボン材料が、軸受面部１１と軸２との相対移動によって軸受面部１１全体に行き渡る。これにより、軸受面部１１全体でカーボン材料による潤滑効果を得ることができる。   In the bearing 1, the lubricating member 3 constituting a part of the bearing surface portion 11 serves as a carbon material supply source. The carbon material supplied from the lubricating member 3 spreads over the entire bearing surface portion 11 by the relative movement of the bearing surface portion 11 and the shaft 2. Thereby, the lubrication effect by a carbon material can be acquired in the bearing surface part 11 whole.

（５）その他の材料
樹脂組成物は、ポリアリーレンスルフィド系樹脂およびカーボン材料に加えて、他の充填剤を含んでもよい。他の充填剤としては、例えば、ガラス繊維、アラミド繊維、アルミナ繊維、芳香族ポリアミド繊維、ポリエステル繊維、ボロン繊維、炭化珪素繊維、窒化硼素繊維、窒化珪素繊維、金属繊維等の繊維類やこれらを布状に編んだもの、炭酸カルシウムやタルク、シリカ、クレー、マイカ等の鉱物類、硼酸アルミニウムウィスカー、チタン酸カリウムウィスカー等の無機ウィスカー類、ポリイミド樹脂やポリベンゾイミダゾール等の各種耐熱性樹脂等を用いることができる。これらの充填剤を含むことにより、潤滑部材３の摩擦摩耗特性の改善や、線膨張係数を小さくすることができる。必要に応じて、離型剤、難燃剤、耐候性改良剤、酸化防止剤、顔料などの添加剤を適宜添加してもよい。 (5) Other materials The resin composition may include other fillers in addition to the polyarylene sulfide-based resin and the carbon material. Examples of other fillers include fibers such as glass fiber, aramid fiber, alumina fiber, aromatic polyamide fiber, polyester fiber, boron fiber, silicon carbide fiber, boron nitride fiber, silicon nitride fiber, metal fiber, and the like. Knitted fabric, minerals such as calcium carbonate, talc, silica, clay, mica, inorganic whiskers such as aluminum borate whisker and potassium titanate whisker, various heat resistant resins such as polyimide resin and polybenzimidazole Can be used. By including these fillers, the friction and wear characteristics of the lubricating member 3 can be improved and the linear expansion coefficient can be reduced. If necessary, additives such as a mold release agent, a flame retardant, a weather resistance improver, an antioxidant, and a pigment may be appropriately added.

（６）カーボン材料の含有量
樹脂組成物に配合されるカーボン材料の含有量は、潤滑部材３の摺動面の摺動特性を確保するために好適な範囲に設定され、ほぼ５質量％以上ほぼ７０質量％以下、具体的には５質量％以上７０質量％以下、好ましくはほぼ１０質量％以上ほぼ６０質量％以下、具体的には１０質量％以上６０質量％以下、より好ましくはほぼ４０質量％以下、具体的には４０質量％以下である。樹脂組成物中におけるカーボン材料の配合量がほぼ５質量％未満の場合、具体的にはほぼ１０質量％未満の場合、より具体的には１０質量％未満の場合、カーボン材料の配合量が少ないためにカーボン材料による摺動面の摺動特性向上効果が現れ難くなる傾向にある。樹脂組成物中におけるカーボン材料の配合量がほぼ７０質量％を超える場合、具体的にはほぼ６０質量％を超える場合、より具体的には６０質量％を超える場合、樹脂組成物の流動性が低下して射出成形時における歩留り率が低下する他、射出成形を行うこと自体が困難となる傾向にある。摺動特性を確保しつつ、射出成形時における歩留り率の低下を避けるために、樹脂組成物中に配合されるカーボン材料の含有量は、上記範囲内であることが好ましく、ほぼ４０質量％以下、具体的には４０質量％以下であることがより好ましい。 (6) Content of carbon material The content of the carbon material blended in the resin composition is set in a suitable range in order to ensure the sliding characteristics of the sliding surface of the lubricating member 3, and is approximately 5% by mass or more. Approximately 70% by mass or less, specifically 5% by mass or more and 70% by mass or less, preferably approximately 10% by mass or more and approximately 60% by mass or less, specifically 10% by mass or more and 60% by mass or less, more preferably approximately 40% by mass. It is not more than mass%, specifically not more than 40 mass%. When the compounding amount of the carbon material in the resin composition is less than about 5% by mass, specifically when it is less than about 10% by mass, more specifically when it is less than 10% by mass, the compounding amount of the carbon material is small. Therefore, the effect of improving the sliding characteristics of the sliding surface by the carbon material tends to hardly appear. When the compounding amount of the carbon material in the resin composition exceeds approximately 70% by mass, specifically exceeds approximately 60% by mass, more specifically exceeds 60% by mass, the fluidity of the resin composition is increased. In addition to a decrease in yield rate during injection molding, it tends to be difficult to perform injection molding itself. The content of the carbon material blended in the resin composition is preferably within the above range in order to avoid a decrease in the yield rate during injection molding while ensuring sliding characteristics, and is approximately 40% by mass or less. Specifically, it is more preferably 40% by mass or less.

（７）潤滑油の含浸
軸受１は、無数の内部空孔を有しているため、インサート成形工程を経た軸受１の内部空孔に、潤滑油を含浸させることもできる。例えば、インサート成形工程を経た軸受１を、減圧環境下において潤滑油中に浸漬させた後、大気圧に戻すことにより、軸受１の内部空孔に潤滑油を含浸させることができる。潤滑油としては、軸受用として汎用されているものであれば特に制限されず、例えば、スピンドル油、冷凍機油、タービン油、マシン油、ダイナモ油などの鉱油、ポリブテン、ポリ-α-オレフィン、アルキルナフタレン、脂環式化合物などの炭化水素系合成油、または、天然油脂とポリオールとのエステル油、リン酸エステル、ジエステル油などのエステル、ポリグリコール油、シリコーン油、ポリフェニルエーテル油、アルキルジフェニルエーテル油、アルキルベンゼン、フッ素化油などの非炭化水素系合成油、液状グリース等を用いてもよい。 (7) Impregnation of lubricating oil Since the bearing 1 has innumerable internal holes, the internal holes of the bearing 1 that have undergone the insert molding process can be impregnated with lubricating oil. For example, after the bearing 1 that has undergone the insert molding process is immersed in lubricating oil in a reduced pressure environment, the internal holes of the bearing 1 can be impregnated with lubricating oil by returning to atmospheric pressure. The lubricating oil is not particularly limited as long as it is widely used for bearings. For example, mineral oil such as spindle oil, refrigerator oil, turbine oil, machine oil, dynamo oil, polybutene, poly-α-olefin, alkyl, etc. Hydrocarbon synthetic oils such as naphthalene and alicyclic compounds, or ester oils of natural oils and polyols, esters such as phosphate esters and diester oils, polyglycol oils, silicone oils, polyphenyl ether oils, alkyl diphenyl ether oils In addition, non-hydrocarbon synthetic oils such as alkylbenzene and fluorinated oil, liquid grease, and the like may be used.

（８）基体４の開放気孔率
基体４の開放気孔率は、インサート成形工程を経た軸受１の内部空孔に潤滑油を含浸する場合において、当該潤滑油が潤滑性付与剤として機能し軸受１の摺動特性を向上させるために好適な範囲に設定される。基体４の開放気孔率は、ほぼ５％以上、具体的には５％以上、好ましくはほぼ１０％以上、具体的には１０％以上、より好ましくはほぼ１５％以上、具体的には１５％以上である。また、基体４の開放気孔率は、ほぼ５０％以下、具体的には５０％以下、好ましくはほぼ４０％以下、具体的には４０％以下、より好ましくはほぼ３０％以下、具体的には３０％以下、さらに好ましくはほぼ２５％以下、具体的には２５％以下である。開放気孔率がほぼ５％（具体的には５％）未満の場合、基体４の内部空孔に含浸される潤滑油の総量が少ない。そのため、軸受１に長期に亘って潤滑油に基づく優れた潤滑性能を発揮させることが困難な傾向にある。また、開放気孔率がほぼ５０％（具体的には５０％）を超える場合、基体４の成形が困難となって基体４の成形性が低下する。その結果、生産性よく基体４を成形することが困難となり、基体４を備えた軸受１を低コストで生産することが困難となる傾向にある。基体４に潤滑油に基づく優れた潤滑性能を発揮させつつ、生産性よく軸受１を成形するために、基体４の開放気孔率は、上記範囲内であることが好ましい。なお、「開放気孔率」は、基体４の体積に対する含浸可能な内部空孔を百分率で表したもので、完全含浸後の油の体積を基体４の体積で除し、１００を乗じて求められる。開放気孔率は、日本工業規格の「焼結金属材料−密度，含油率及び開放気孔率試験方法（ＪＩＳ Ｚ ２５０１：２０００）」により測定する事ができる。 (8) Open porosity of the base 4 The open porosity of the base 4 is determined by the fact that the lubricating oil functions as a lubricity imparting agent when the internal pores of the bearing 1 subjected to the insert molding process are impregnated with the lubricating oil. In order to improve the sliding characteristics, it is set within a suitable range. The open porosity of the substrate 4 is approximately 5% or more, specifically 5% or more, preferably approximately 10% or more, specifically 10% or more, more preferably approximately 15% or more, specifically 15%. That's it. The open porosity of the substrate 4 is approximately 50% or less, specifically 50% or less, preferably approximately 40% or less, specifically 40% or less, more preferably approximately 30% or less, specifically. 30% or less, more preferably about 25% or less, specifically 25% or less. When the open porosity is less than about 5% (specifically, 5%), the total amount of lubricating oil impregnated in the internal pores of the substrate 4 is small. Therefore, it tends to be difficult for the bearing 1 to exhibit excellent lubricating performance based on the lubricating oil over a long period of time. Further, when the open porosity exceeds approximately 50% (specifically, 50%), it becomes difficult to form the base 4 and the formability of the base 4 is lowered. As a result, it is difficult to form the base body 4 with high productivity, and it tends to be difficult to produce the bearing 1 including the base body 4 at low cost. In order to form the bearing 1 with high productivity while allowing the base 4 to exhibit excellent lubricating performance based on the lubricating oil, the open porosity of the base 4 is preferably within the above range. The “open porosity” is expressed as a percentage of the internal pores that can be impregnated with respect to the volume of the substrate 4, and is obtained by dividing the volume of oil after complete impregnation by the volume of the substrate 4 and multiplying by 100. . The open porosity can be measured by the Japanese Industrial Standard “Sintered Metal Material—Density, Oil Content and Open Porosity Test Method (JIS Z 2501: 2000)”.

（９）基体４の含油率
この基体４の内部気孔には、潤滑剤として、例えば鉱物油や合成油等の潤滑油が含浸される。そのため、基体４が軸２に対して回転すると、基体４の内部気孔に保持された潤滑油が基体４の内周面４ａの表面開孔から滲み出し、内周面４ａ（摺動面部１１）と軸２の外周面との間に潤滑油の油膜が形成される。これにより、摺動面部１１の摩耗が抑制または防止される。基体４全体の含油率は、ほぼ５ｖｏｌ％以上、具体的には５ｖｏｌ％以上、好ましくはほぼ１０ｖｏｌ％以上、具体的には１０ｖｏｌ％以上、より好ましくはほぼ１５ｖｏｌ％以上、具体的には１５ｖｏｌ％以上とする。また、基体４全体の含油率は、ほぼ５０ｖｏｌ％以下、具体的には５０ｖｏｌ％以下、好ましくはほぼ４０ｖｏｌ％以下、具体的には４０ｖｏｌ％以下、より好ましくはほぼ３０ｖｏｌ％以下、具体的には３０ｖｏｌ％以下、さらに好ましくはほぼ２５ｖｏｌ％以下、具体的には２５ｖｏｌ％以下とする。含油率がほぼ５ｖｏｌ％、具体的にはほぼ１０ｖｏｌ％、より具体的にはほぼ１５ｖｏｌ％、さらに具体的には１５ｖｏｌ％を下回ると、所望の潤滑特性を長期間に亘って安定的に維持・発揮することができない。含油率がほぼ５０ｖｏｌ％、具体的にはほぼ４０ｖｏｌ％、より具体的にはほぼ３０ｖｏｌ％、さらに具体的にはほぼ２５ｖｏｌ％、特に具体的には２５ｖｏｌ％を上回ると、内部気孔率が高まる関係上、基体４に全体として必要とされる機械的強度を確保することができない可能性があるからである。 (9) Oil content of base 4 The internal pores of the base 4 are impregnated with a lubricating oil such as mineral oil or synthetic oil as a lubricant. Therefore, when the base 4 rotates with respect to the shaft 2, the lubricating oil held in the internal pores of the base 4 oozes out from the surface opening of the inner peripheral surface 4a of the base 4, and the inner peripheral surface 4a (sliding surface portion 11). And an oil film of lubricating oil is formed between the outer peripheral surface of the shaft 2. Thereby, wear of the sliding surface portion 11 is suppressed or prevented. The oil content of the entire substrate 4 is about 5 vol% or more, specifically 5 vol% or more, preferably about 10 vol% or more, specifically 10 vol% or more, more preferably about 15 vol% or more, specifically 15 vol%. That's it. Further, the oil content of the whole substrate 4 is about 50 vol% or less, specifically 50 vol% or less, preferably about 40 vol% or less, specifically 40 vol% or less, more preferably about 30 vol% or less, specifically 30 vol% or less, more preferably about 25 vol% or less, specifically 25 vol% or less. When the oil content is about 5 vol%, specifically about 10 vol%, more specifically about 15 vol%, and more specifically below 15 vol%, the desired lubrication characteristics can be stably maintained over a long period of time. I can't demonstrate it. When the oil content is about 50 vol%, specifically about 40 vol%, more specifically about 30 vol%, more specifically about 25 vol%, more specifically about 25 vol%, the internal porosity is increased. Furthermore, there is a possibility that the mechanical strength required for the substrate 4 as a whole cannot be ensured.

また、基体４の内部気孔に含浸させる潤滑油があまりに低粘度であると、潤滑油が外部に流出し易くなる他、油膜剛性が低くなって摺動面部１１の摩耗抑制効果が不十分になる可能性がある。一方、潤滑油があまりに高粘度であると、摺動面部１１の表面開孔からの潤滑油の滲み出し量が不足し、所定厚さ・剛性の油膜を形成できない可能性がある。かかる観点から、潤滑油としては、４０℃における動粘度が、ほぼ５ｍｍ^２／ｓ以上、具体的には５ｍｍ^２／ｓ以上、好ましくはほぼ３０ｍｍ^２／ｓ以上、具体的には３０ｍｍ^２／ｓ以上、より好ましくはほぼ５０ｍｍ^２／ｓ以上、具体的には５０ｍｍ^２／ｓ以上とする。また、潤滑油としては、４０℃における動粘度が、ほぼ６００ｍｍ^２／ｓ以下、具体的には６００ｍｍ^２／ｓ以下、好ましくはほぼ５５０ｍｍ^２／ｓ以下、具体的には５５０ｍｍ^２／ｓ以下、より好ましくはほぼ５００ｍｍ^２／ｓ以下、具体的には５００ｍｍ^２／ｓ以下とする。 Further, if the lubricating oil impregnated in the internal pores of the base body 4 is too low in viscosity, the lubricating oil will easily flow out to the outside, and the oil film rigidity will be low and the wear suppressing effect of the sliding surface portion 11 will be insufficient. there is a possibility. On the other hand, if the lubricating oil is too viscous, there is a possibility that the amount of lubricating oil oozing out from the surface opening of the sliding surface portion 11 will be insufficient, and an oil film having a predetermined thickness and rigidity may not be formed. From this point of view, the lubricating oil has a kinematic viscosity at 40 ° C. of about 5 mm ² / s or more, specifically 5 mm ² / s or more, preferably about 30 mm ² / s or more, specifically 30 mm ² / s. More preferably, it is about 50 mm ² / s or more, more specifically 50 mm ² / s or more. The lubricating oil has a kinematic viscosity at 40 ° C. of about 600 mm ² / s or less, specifically 600 mm ² / s or less, preferably about 550 mm ² / s or less, specifically 550 mm ² / s or less, More preferably, it is about 500 mm ² / s or less, specifically 500 mm ² / s or less.

なお、基体４の内部気孔には、上記の潤滑油に替えて液状グリースを含浸させても構わない。液状グリースとしては、例えば、４０℃における動粘度が上記範囲内にある潤滑油を基油とし、これにリチウム石けん等の石けん系増ちょう剤、またはウレア等の非石けん系増ちょう剤を添加したものを使用することができる。   Note that the internal pores of the base 4 may be impregnated with liquid grease instead of the above lubricating oil. As the liquid grease, for example, a lubricating oil having a kinematic viscosity at 40 ° C. within the above range is used as a base oil, and a soap-based thickener such as lithium soap or a non-soap-based thickener such as urea is added thereto. Things can be used.

（１０）基体４の表面開孔率
基体４の、収容部４ｃの内表面である合せ面４ｂにおける表面開孔率は、基体４の収容部４ｃに配置された潤滑部材３に含まれるポリアリーレンスルフィド系樹脂のアンカー効果により、基体４と潤滑部材３との結合力を高めるために好適な範囲に設定される。係る表面開孔率は、好ましくは１０％以上５０％以下である。表面開孔率が１０％未満の場合、合せ面４ｂの表面気孔に入り込む潤滑部材３に含まれるポリアリーレンスルフィド系樹脂の量が減る。そのため、ポリアリーレンスルフィド系樹脂のアンカー効果が減少する傾向にある。また、表面開孔率が５０％を超える場合、収容部４ｃの成形が困難となる傾向にある。基体４と潤滑部材３との結合力を高めつつ、生産性よく軸受１を成形するために、基体４の表面開孔率は、上記範囲内であることが好ましい。なお、「表面開孔率」とは、表面の単位面積当りに占める表面開孔の総面積の割合（面積比）である。また、ここでいう表面開孔率は、便宜的には例えば、Nikon社製：ECLIPSE ME600等の金属顕微鏡で撮影した画像（例えば５００倍）を画像データとしてコンピュータに取り込み、気孔部分の面積を演算することで求めることができる。 (10) Surface Opening Ratio of Base 4 The surface opening ratio of the base 4 on the mating surface 4b, which is the inner surface of the housing portion 4c, is the polyarylene contained in the lubricating member 3 disposed in the housing portion 4c of the base 4. Due to the anchor effect of the sulfide-based resin, the range is set within a suitable range in order to increase the bonding force between the base 4 and the lubricating member 3. The surface area ratio is preferably 10% or more and 50% or less. When the surface open area ratio is less than 10%, the amount of the polyarylene sulfide resin contained in the lubricating member 3 entering the surface pores of the mating surface 4b is reduced. Therefore, the anchor effect of polyarylene sulfide resin tends to decrease. Moreover, when the surface area ratio exceeds 50%, it tends to be difficult to mold the housing portion 4c. In order to form the bearing 1 with high productivity while increasing the bonding force between the base 4 and the lubricating member 3, the surface porosity of the base 4 is preferably within the above range. The “surface aperture ratio” is the ratio (area ratio) of the total area of surface apertures per unit area of the surface. In addition, for the sake of convenience, the surface area ratio here is calculated, for example, by taking an image (for example, 500 times) taken with a metal microscope such as Nikon Corporation: ECLIPSE ME600 as image data and calculating the area of the pore portion. You can ask for it.

（１１）軸２の材質
軸の材質は特に限定されず、ＳＳ鋼、Ｓ−Ｃ鋼、ＳＣＭ鋼、ＳＵＪ鋼、ＳＵＳ鋼など種々の材料を用いることができる。鋼の硬度は、ＨＲＣ３０〜６０（ＨＢ２８６〜６５４）程度、または、ＨＢ１４０〜２２０程度で良く、また、焼き入れ処理後の硬度はＨＲＣ５５〜７０程度好ましくはＨＲＣ５５〜６０、または、ＨＲＣ６０〜６５程度とすると良い。このように、摺動部材１および軸２を備えるすべり軸受装置を構成させてもよい。 (11) Material of shaft 2 The material of the shaft is not particularly limited, and various materials such as SS steel, SC steel, SCM steel, SUJ steel, and SUS steel can be used. The hardness of the steel may be about HRC 30 to 60 (HB 286 to 654) or about HB 140 to 220, and the hardness after quenching is about HRC 55 to 70, preferably HRC 55 to 60, or HRC 60 to 65. Good. In this way, a slide bearing device including the sliding member 1 and the shaft 2 may be configured.

以上の実施形態では、潤滑部材３の内側面３ａと基体４の内周面４ａとを同一円筒面状に配し、これらで軸受面部１１を構成した場合を示したが、これに限られない。以下、本発明の他の実施形態を説明するが、上記の実施形態と重複する点については説明を省略する。   In the above embodiment, the case where the inner surface 3a of the lubricating member 3 and the inner peripheral surface 4a of the base body 4 are arranged in the same cylindrical surface and the bearing surface portion 11 is configured by these is shown, but the present invention is not limited thereto. . Hereinafter, although other embodiment of this invention is described, description is abbreviate | omitted about the point which overlaps with said embodiment.

［その他の実施形態］
図５を参照して、潤滑部材３の内側面３ａを基体４の内周面４ａよりも内径側に配し、潤滑部材３の内側面３ａのみで軸受面部１１を構成するように軸受１を製造してもよい。この場合、複数の潤滑部材３の内側面３ａは、同一円筒面上に配されることが好ましい。 [Other Embodiments]
Referring to FIG. 5, the bearing 1 is arranged such that the inner side surface 3 a of the lubricating member 3 is arranged on the inner diameter side with respect to the inner peripheral surface 4 a of the base body 4 and the bearing surface portion 11 is configured only by the inner side surface 3 a of the lubricating member 3. It may be manufactured. In this case, the inner side surfaces 3a of the plurality of lubricating members 3 are preferably arranged on the same cylindrical surface.

また、潤滑部材３は、図１（ｂ）に示すように軸受１の軸方向全長にわたって配置する他、軸方向の一部領域に限って配置してもよく、例えば軸方向に離隔した複数箇所に配置してもよい。   Further, the lubricating member 3 may be disposed only in a partial region in the axial direction in addition to the entire axial length of the bearing 1 as shown in FIG. 1B, for example, a plurality of locations separated in the axial direction. You may arrange in.

また、軸受１においては、必ずしも軸受面部１１の全体に対して軸２が摺動するわけではなく、例えば、軸受面部１１の限定された一部領域が軸２と摺動する場合がある。具体的には、軸２を水平姿勢とした場合、軸２は重力によって落ち込んで軸受面部１１の下側領域で軸受面部１１と摺動する場合がある。その場合、軸２との摺動領域に潤滑部材３が位置するように、軸受１における潤滑部材３の位置や形状を設計し、または軸受１の円周方向の位相を調整することで、軸２を潤滑部材３と常に摺動させることが可能となる。これにより高い潤滑効果を得ることができるため、例えば軸受面部１１との間に潤滑油を介在させないオイルレスの状態で軸２を支持することが可能となる。もちろん、軸受面部１１と軸２との間に潤滑油を介在させた状態で用いることもでき、この場合さらに潤滑効果が高められる。本実施形態では、軸受面部１１と軸２との間に潤滑油を介在させると共に、基板４の内部空孔に油を含浸させている。この場合、軸２の回転に伴う温度上昇により基板４の表面（内側面３ａ）から油が滲み出し、この油が軸受面部１１と軸２との摺動領域に供給されることで、摺動領域における油膜切れを確実に回避して優れた摺動性が維持される。   In the bearing 1, the shaft 2 does not necessarily slide with respect to the entire bearing surface portion 11. For example, a limited partial region of the bearing surface portion 11 may slide with the shaft 2. Specifically, when the shaft 2 is in a horizontal posture, the shaft 2 may drop due to gravity and slide with the bearing surface portion 11 in the lower region of the bearing surface portion 11. In that case, the position and shape of the lubricating member 3 in the bearing 1 are designed so that the lubricating member 3 is located in the sliding region with the shaft 2, or the circumferential phase of the bearing 1 is adjusted so that the shaft 2 can always slide with the lubricating member 3. As a result, a high lubrication effect can be obtained, so that the shaft 2 can be supported in an oilless state in which no lubricating oil is interposed between the bearing surface portion 11 and the like, for example. Of course, it can also be used in a state where lubricating oil is interposed between the bearing surface portion 11 and the shaft 2, and in this case, the lubricating effect is further enhanced. In the present embodiment, lubricating oil is interposed between the bearing surface portion 11 and the shaft 2, and the internal holes of the substrate 4 are impregnated with oil. In this case, the oil rises from the surface (inner side surface 3a) of the substrate 4 due to the temperature rise accompanying the rotation of the shaft 2, and this oil is supplied to the sliding region between the bearing surface portion 11 and the shaft 2 to slide. An excellent slidability is maintained by reliably avoiding oil film breakage in the region.

また、本発明は、軸の相対回転を支持する軸受に限らず、軸の軸方向移動を支持する軸受に適用することもできる。また、本発明は、円筒形状の摺動部材に限らず、他の形状（例えば、半円筒状や直方体状）の摺動部材に適用することもできる。   The present invention is not limited to a bearing that supports the relative rotation of the shaft, but can also be applied to a bearing that supports the axial movement of the shaft. Further, the present invention is not limited to a cylindrical sliding member, and can be applied to a sliding member having another shape (for example, a semi-cylindrical shape or a rectangular parallelepiped shape).

１ 摺動部材（軸受）、２ 軸、３ 潤滑部材、３ａ 内側面、３ｂ 外側面、４ 基体、４’ 成形体、４ａ 内周面、４ａ’ 凹部、４ｂ 合せ面、４ｃ 収容部、１１ 軸受面部（摺動面部）、１２ 外周面、２０ 成形金型、２１ 固定型、２１ａ 円柱部、２１ｂ ゲート、２１ｃ 成形面、２１ｄ ランナ、２２ 可動型、２３ キャビティ。   DESCRIPTION OF SYMBOLS 1 Sliding member (bearing), 2 axis | shaft, 3 lubrication member, 3a inner surface, 3b outer surface, 4 base | substrate, 4 'molded object, 4a inner peripheral surface, 4a' recessed part, 4b mating surface, 4c accommodating part, 11 bearing Surface portion (sliding surface portion), 12 outer peripheral surface, 20 molding die, 21 fixed mold, 21a cylindrical portion, 21b gate, 21c molding surface, 21d runner, 22 movable mold, 23 cavity.

Claims (8)

摺動面を有し、前記摺動面の少なくとも一部が潤滑部材の表面で構成される摺動部材であって、
金属粉を含む成形体の焼結体であり、前記潤滑部材と一体化される基体と、
ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物の射出成形体である前記潤滑部材と、
を含む摺動部材。 A sliding member having a sliding surface, wherein at least a part of the sliding surface is constituted by a surface of a lubricating member;
A sintered body of a molded body containing metal powder, and a base body integrated with the lubricating member;
The lubricating member which is an injection-molded article of a resin composition comprising a polyarylene sulfide-based resin and a carbon material;
A sliding member. 摺動面を有し、前記摺動面の少なくとも一部が潤滑部材の表面で構成される摺動部材であって、
金属粉を含む成形体の焼結体である、前記潤滑部材を収容するための収容部を有する基体と、
ポリアリーレンスルフィド系樹脂とカーボン材料とを含む樹脂組成物の射出成形体であって、前記収容部内に配置された前記潤滑部材と、
を含む摺動部材。 A sliding member having a sliding surface, wherein at least a part of the sliding surface is constituted by a surface of a lubricating member;
A base body having a housing portion for housing the lubricating member, which is a sintered body of a molded body containing metal powder;
An injection molded body of a resin composition comprising a polyarylene sulfide-based resin and a carbon material, the lubricating member disposed in the housing portion,
A sliding member. 前記樹脂組成物における前記カーボン材料の含有率が、ほぼ５質量％以上ほぼ７０質量％以下である、請求項１または２に記載の摺動部材。   The sliding member according to claim 1 or 2, wherein a content of the carbon material in the resin composition is approximately 5% by mass or more and approximately 70% by mass or less. 前記基体は内部空孔を有し、
前記内部空孔内に潤滑油が含浸されている、請求項１から３のいずれか１項に記載の摺動部材。 The substrate has internal voids;
The sliding member according to any one of claims 1 to 3, wherein the internal hole is impregnated with a lubricating oil. 前記基体は、ほぼ５％以上ほぼ５０％以下の開放気孔率を有する、請求項１から４のいずれか１項に記載の摺動部材。   The sliding member according to any one of claims 1 to 4, wherein the base body has an open porosity of approximately 5% or more and approximately 50% or less. 前記基体は、ほぼ１０％以上ほぼ５０％以下の表面開孔率を有する、請求項１から５のいずれか１項に記載の摺動部材。   The sliding member according to any one of claims 1 to 5, wherein the base body has a surface area ratio of approximately 10% to approximately 50%. 前記基体は、前記収容部の内表面においてほぼ１０％以上ほぼ５０％以下の表面開孔率を有する、請求項２に記載の摺動部材。   The sliding member according to claim 2, wherein the base has a surface area ratio of approximately 10% or more and approximately 50% or less on the inner surface of the housing portion. 前記カーボン材料は、カーボンナノ繊維、カーボンブラックおよび黒鉛からなる群から選択される少なくとも１つである、請求項１から７のいずれか１項に記載の摺動部材。   The sliding member according to any one of claims 1 to 7, wherein the carbon material is at least one selected from the group consisting of carbon nanofibers, carbon black, and graphite.