JP2017213723A - Composite sheet and camouflage material - Google Patents
Composite sheet and camouflage material Download PDFInfo
- Publication number
- JP2017213723A JP2017213723A JP2016107719A JP2016107719A JP2017213723A JP 2017213723 A JP2017213723 A JP 2017213723A JP 2016107719 A JP2016107719 A JP 2016107719A JP 2016107719 A JP2016107719 A JP 2016107719A JP 2017213723 A JP2017213723 A JP 2017213723A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- flame retardant
- composite sheet
- resin layer
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、基材に様々な特性を付与するための機能性付与層を積層した複合シート、およびそれを用いてなる、例えば航空機、船舶、車輌などを隠蔽する偽装材に関する。 The present invention relates to a composite sheet obtained by laminating a functional layer for imparting various properties to a base material, and a camouflage material using the composite sheet for hiding, for example, an aircraft, a ship, or a vehicle.
従来より、対可視光、対近赤外線偽装効果ならびに対遠赤外線偽装効果を有する上に優れた対レーダー偽装効果を有する偽装材が使用されている。このような偽装材として導電性樹脂層を有する基布の両面に、金属層および迷彩用着色剤含有樹脂層を順に積層した偽装材が提案されている（例えば特許文献１）。 Conventionally, a camouflage material having an anti-radical camouflage effect as well as an anti-radical camouflage effect and a far-infrared camouflage effect has been used. As such a camouflage material, a camouflage material has been proposed in which a metal layer and a camouflage colorant-containing resin layer are sequentially laminated on both surfaces of a base fabric having a conductive resin layer (for example, Patent Document 1).
これら偽装材は、航空機、船舶、車輌などを覆うことにより偵察装置による識別を困難にするために使用されるが、偽装対象物が熱源であるエンジン部を有している場合もあり、偽装材には高い難燃性が要求される。難燃性を付与した従来の偽装材としては、偽装材の表面にある複数の厚い樹脂層の一部に難燃化剤を含ませたものが提案されている（例えば特許文献２、３）。 These camouflaged materials are used to make it difficult for the reconnaissance device to identify them by covering aircraft, ships, vehicles, etc., but the camouflaged object may have an engine part that is a heat source. Requires high flame retardancy. As a conventional camouflaged material imparted with flame retardancy, a material in which a flame retardant is included in a part of a plurality of thick resin layers on the surface of the camouflaged material has been proposed (for example, Patent Documents 2 and 3). .
一方、近年の偵察装置の高性能化に伴い、より一層高い偽装性能、例えば対レーダー偽装性能の向上が求められているが、偽装性能向上のため導電性樹脂層の樹脂を増やして性能向上を図った場合、難燃性が低下する問題があった。また、難燃化剤を増量することで難燃性は向上するが、偽装材が著しく重くなるという問題もあった。 On the other hand, with higher performance of reconnaissance devices in recent years, higher camouflage performance such as anti-radar camouflage performance is required, but to improve camouflage performance, increase the resin of the conductive resin layer to improve performance. In this case, there is a problem that the flame retardancy is lowered. Moreover, although flame retardance improves by increasing a flame retardant, there also existed a problem that a camouflage material became remarkably heavy.
本発明は、かかる従来技術に鑑み、対可視光、対近赤外線、対遠赤外線、対レーダー偽装性能を向上させた場合においても、難燃性能を損なわずに重量増加を極めて少なくできる複合シート、および偽装材を提供せんとするものである。 In view of such conventional technology, the present invention is a composite sheet that can extremely reduce the increase in weight without impairing the flame retardancy even when the anti-visible light, anti-infrared, anti-far infrared, and anti-radar camouflage performance is improved, And disguised materials.
本発明は、かかる課題を解決するために、次のような手段を採用するものである。すなわち本発明の複合シートおよび偽装材は、
（１）基材の表裏面に難燃樹脂層を１層ずつ含み、さらに着色層、金属層および導電樹脂層から選ばれる少なくとも２種を積層してなる複合シートであって、該難燃樹脂層の少なくとも１層は基材に隣接する複合シート。
（２）基材の片面に難燃樹脂層が隣接し、難燃樹脂層が隣接した片面とは反対の他面に着色層または金属層または導電樹脂層が隣接する前記（１）に記載の複合シート。
（３）金属層を複合シートの最外層より内層側に配した前記（１）および（２）のいずれかに記載の複合シート。
（４）前記基材が繊維シートである前記（１）〜（３）のいずれかに記載の複合シート。
（５）前記（１）〜（４）のいずれかに記載の複合シートを配する偽装材。
である。
The present invention employs the following means in order to solve such problems. That is, the composite sheet and fake material of the present invention are:
(1) A composite sheet comprising one layer each of a flame retardant resin layer on the front and back surfaces of a substrate, and further laminating at least two selected from a colored layer, a metal layer, and a conductive resin layer, the flame retardant resin At least one of the layers is a composite sheet adjacent to the substrate.
(2) The flame retardant resin layer is adjacent to one side of the substrate, and the colored layer, the metal layer, or the conductive resin layer is adjacent to the other side opposite to the one side where the flame retardant resin layer is adjacent. Composite sheet.
(3) The composite sheet according to any one of (1) and (2), wherein the metal layer is arranged on the inner layer side from the outermost layer of the composite sheet.
(4) The composite sheet according to any one of (1) to (3), wherein the base material is a fiber sheet.
(5) A camouflage material provided with the composite sheet according to any one of (1) to (4).
It is.
本発明によれば、対可視光、対近赤外線、対遠赤外線、対レーダー偽装性能を向上させた場合においても、難燃性能を損なわずに重量増加が極めて少ない複合シートを提供することができる。したがって、本発明の偽装材は、軽量であるため展張性、作業性に優れ航空機、船舶、車両などを偽装するのに好適に使用することができる。 According to the present invention, even when the anti-visible light, anti-infrared ray, anti-infrared ray, and radar camouflage performance is improved, it is possible to provide a composite sheet with a very small increase in weight without impairing the flame retardancy. . Therefore, since the camouflage material of the present invention is lightweight, it has excellent stretchability and workability and can be suitably used for camouflaging aircraft, ships, vehicles, and the like.
本発明は、前記課題、つまり対可視光、対近赤外線、対遠赤外線、対レーダー偽装性能を向上させた場合においても、難燃性能を損なわずに重量増加を極めて少なくできる複合シートについて、鋭意検討し、構成する機能性付与層の積層位置、特に難燃樹脂層を特定の位置に積層させることで、他の機能性付与層を高性能化した場合においても高い難燃性を維持するための難燃樹脂層の重量増加を抑えることが可能で、それにより、偽装材として軽量であるため、展張性、作業性に優れたものを提供することができることを究明し、本発明に到達したものである。 The present invention is earnest about the composite sheet that can significantly reduce the weight increase without impairing the flame retardancy even in the case of improving the above-mentioned problems, that is, the anti-visible light, the near infrared, the far infrared, and the radar disguise performance. In order to maintain high flame retardancy even when the performance of other functional layers is improved by laminating the position of the functional layers to be studied, especially by laminating the flame retardant resin layer at a specific position. It was possible to suppress the increase in the weight of the flame retardant resin layer, and as a result, it was lightweight as a camouflage material, so that it was possible to provide a material with excellent stretchability and workability, and the present invention was achieved. Is.
本発明の基材を構成する素材としては特に限定されないが、ナイロン６、ナイロン６・６、ナイロン１２、ナイロン４・６、ナイロン６成分とナイロン６・６成分を共重合した共重合ポリアミドなどからなるポリアミド樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレートなどのホモポリエステル、ポリエステルの繰り返し単位を構成する酸成分にイソフタル酸、５−ナトリウムスルホイソフタル酸またはアジピン酸などの脂肪族ジカルボン酸などを共重合した共重合ポリエステルなどからなるポリエステル樹脂、ポリパラフェニレンテレフタルアミド、ポリメタフェニレンイソフタルアミドなどに代表されるアラミド樹脂、ポリビニルアルコール系樹脂、ポリフェニレンサルファイド樹脂、超高分子量ポリエチレン樹脂、塩化ビニル樹脂などの合成樹脂が例示できる。また、これら合成樹脂には、製造工程や加工工程での生産性あるいは特性改善のために通常使用されている各種添加剤を含んでいてもよい。例えば、熱安定剤、酸化防止剤、光安定剤、平滑剤、帯電防止剤、可塑剤、難燃剤などを含有せしめることができる。 Although it does not specifically limit as a raw material which comprises the base material of this invention, From nylon 6, nylon 6,6, nylon 12, nylon 4,6, copolymer polyamide which copolymerized nylon 6 component and nylon 6/6 component, etc. Polyamide resin, polyethylene terephthalate, homopolyester such as polybutylene terephthalate, copolymerization of aliphatic dicarboxylic acid such as isophthalic acid, 5-sodiumsulfoisophthalic acid or adipic acid with the acid component constituting the repeating unit of polyester Polyester resin composed of polyester, aramid resin represented by polyparaphenylene terephthalamide, polymetaphenylene isophthalamide, polyvinyl alcohol resin, polyphenylene sulfide resin, ultrahigh molecular weight polyethylene resin, chloride Synthetic resins such as sulfonyl resin can be exemplified. In addition, these synthetic resins may contain various additives that are usually used for improving productivity or characteristics in the manufacturing process and processing process. For example, a heat stabilizer, an antioxidant, a light stabilizer, a smoothing agent, an antistatic agent, a plasticizer, a flame retardant, and the like can be included.
かかる合成樹脂を用いて、繊維、フィルムを得る。本発明の基材は、織物、編物、不織布等の繊維シートやフィルムからなるシートを言うが、これらの中でも引張強さや引裂き強さに優れる繊維シートが好ましく、さらに好ましくは織物を用いるのがよい。 Fibers and films are obtained using such synthetic resins. The substrate of the present invention refers to a sheet made of a fiber sheet or a film such as a woven fabric, a knitted fabric, and a nonwoven fabric. Among them, a fiber sheet excellent in tensile strength and tear strength is preferable, and a woven fabric is more preferably used. .
本発明に用いる織物としては、求められる引張強さや引裂き強さにより、繊維の種類、織組織、織密度等、適宜選択することができる。好ましくは、最終的に得られる複合シートを軽量なものとするため、目付は５０〜３００ｇ／ｍ２の範囲がよく、さらに好ましくは、１００〜２００ｇ／ｍ２がよい。織物に用いる繊維の種類としては、前記合成樹脂からなる繊維や、綿、麻などの天然繊維も使用することができる。 As the woven fabric used in the present invention, the fiber type, woven structure, woven density, and the like can be appropriately selected depending on the required tensile strength and tear strength. Preferably, for the composite sheet finally obtained a light weight, the basis weight may range of 50 to 300 g / m 2, more preferably, it is 100 to 200 g / m 2. As the types of fibers used in the woven fabric, fibers made of the above synthetic resin and natural fibers such as cotton and hemp can be used.
本発明の複合シートは、前記基材に難燃樹脂層と、着色層、金属層および導電樹脂層などの機能性付与層を複合シートに求められる特性に応じて、選択し積層してなるものである。該機能性付与層としては、前記３種類の層以外の層を含んでいてもよく、例えば撥水・防水、撥油、抗菌・制菌、防臭、防汚などの他の機能性を付与できる層が含まれても良い。 The composite sheet of the present invention is obtained by selecting and laminating a flame retardant resin layer and a functional layer such as a colored layer, a metal layer and a conductive resin layer on the base material according to the characteristics required for the composite sheet. It is. The functionality-imparting layer may contain layers other than the above-mentioned three types of layers, and can impart other functionality such as water / water repellency, oil repellency, antibacterial / antibacterial, deodorization, and antifouling. Layers may be included.
そして、少なくとも基材の表裏面に難燃樹脂層を１層ずつ含み、さらに着色層、金属層、および導電樹脂層から選ばれる少なくとも２種が積層されてなり、該難燃樹脂層の少なくとも１層が基材に隣接させてなる複合シートであることが必要である。このように基材の両面に難燃樹脂層を配し、かつ少なくとも１層の難燃樹脂層を基材に隣接させることで、高い難燃性を得ることが可能となる。難燃樹脂層を基材の片面のみしか積層しない場合、複合シートが着火した際、難燃樹脂層を積層しない側の機能性付与層が燃焼するか、燃焼を抑えるために多量の難燃樹脂を用いる。一方、難燃樹脂層を基材の両面に配するが少なくとも１層を基材に隣接してない場合、燃焼により加熱された金属層が基材の燃焼を促進する、あるいは加熱され溶融した着色層や導電樹脂層等の樹脂が基材に浸透し、所謂蝋燭が燃焼すると同様の現象が生じ易くなる。したがって、基材の両面に難燃樹脂層を積層し、少なくとも１層を基材に隣接させる。 And at least 1 sort (s) chosen from a colored layer, a metal layer, and a conductive resin layer is laminated | stacked at least 1 layer of a flame retardant resin layer on the front and back of a base material at least, and at least 1 of this flame retardant resin layer It is necessary that the layer is a composite sheet formed adjacent to the substrate. In this way, it is possible to obtain high flame retardancy by arranging the flame retardant resin layers on both surfaces of the base material and making at least one flame retardant resin layer adjacent to the base material. When the flame retardant resin layer is laminated only on one side of the base material, when the composite sheet is ignited, the functionality-imparting layer on the side where the flame retardant resin layer is not laminated burns or a large amount of flame retardant resin is used to suppress combustion. Is used. On the other hand, if the flame retardant resin layer is disposed on both sides of the base material but at least one layer is not adjacent to the base material, the metal layer heated by combustion promotes the combustion of the base material or is heated and melted. When a resin such as a layer or a conductive resin layer penetrates into the base material and a so-called candle burns, the same phenomenon is likely to occur. Therefore, a flame-retardant resin layer is laminated on both sides of the base material, and at least one layer is adjacent to the base material.
かかる難燃樹脂層を形成する樹脂としては、リン系化合物、臭素化ビスフェノール類、ハロゲン化化合物などの有機難燃化剤や三酸化アンチモンや水酸化アルミニウムなどの無機系難燃化剤などの難燃成分をフェノール樹脂、エポキシ樹脂、メラミン樹脂、尿素樹脂、不飽和ポリエステル樹脂、アルキド樹脂、ポリウレタン等の熱硬化性樹脂や、ポリエチレン、ポリ塩化ビニル、ポリスチレン、ポリプロピレン、アクリル、ポリアミド、ポリエステル等の熱可塑性樹脂などの樹脂に混合させたものが挙げられる。そして、基材を形成する素材や難燃樹脂層以外の機能性付与層の構成により、難燃樹脂層に用いる樹脂量は適宜選択できるが、得られる複合シートを軽量なものとする点から、基材の目付を１００とした場合に、基材の両面に積層される難燃樹脂層の目付の合計は２０〜８０が好ましく、さらに好ましくは３０〜５０とすることがよい。また、基材を挟んで表裏面に積層する難燃樹脂層の目付の比率は、基材に隣接する層を１００とした場合に、反対面は３０〜１００とするのがよく、さらに好ましくは５０〜９０である。 Resins that form such a flame retardant resin layer include organic flame retardants such as phosphorus compounds, brominated bisphenols, halogenated compounds, and inorganic flame retardants such as antimony trioxide and aluminum hydroxide. Flame retardant components such as phenol resin, epoxy resin, melamine resin, urea resin, unsaturated polyester resin, alkyd resin, polyurethane, etc., heat such as polyethylene, polyvinyl chloride, polystyrene, polypropylene, acrylic, polyamide, polyester, etc. The thing mixed with resin, such as a plastic resin, is mentioned. And, depending on the composition of the functional layer other than the material forming the base material and the flame retardant resin layer, the amount of resin used for the flame retardant resin layer can be appropriately selected, but from the point that the resulting composite sheet is lightweight, When the basis weight of the substrate is 100, the total basis weight of the flame-retardant resin layer laminated on both surfaces of the substrate is preferably 20 to 80, and more preferably 30 to 50. Further, the basis weight ratio of the flame retardant resin layers laminated on the front and back surfaces with the base material sandwiched therebetween is preferably 30 to 100 when the layer adjacent to the base material is 100, and more preferably 50-90.
かかる難燃樹脂層は、ナイフコーティング、ナイフオーバーロールコーティング、リバースロールコーティング等のコーティング方式、または凸版印刷、グラビア印刷等の印刷方式、またはパディング方式などで基材シート等の上に塗布し、乾燥して形成することができる。 Such a flame retardant resin layer is applied onto a substrate sheet or the like by a coating method such as knife coating, knife over roll coating, reverse roll coating, or printing method such as relief printing, gravure printing, or padding method, and then dried. Can be formed.
本発明の複合シートを構成する金属層は、該複合シートが車輌等から発せられる熱放射を遮蔽し、サーモグラフィーなどの遠赤外線画像装置に対し、優れた遠赤外線偽装効果を該偽装シートに付与するものである。 The metal layer constituting the composite sheet of the present invention shields thermal radiation emitted from a vehicle or the like, and imparts an excellent far-infrared disguise effect to the disguise sheet for far-infrared imaging devices such as thermography. Is.
かかる金属層を形成する金属としては、チタン、ステンレス、ニッケル、クロム、金、銀、銅、鉄、亜鉛、アルミニウムなどや、これらの合金などを採用することができる。その中でも、加工性および遠赤外線偽装性の面から、チタン、ステンレス、アルミニウム、ニッケル、銀から選ばれる少なくとも１種類が好ましく使用される。 As a metal forming such a metal layer, titanium, stainless steel, nickel, chromium, gold, silver, copper, iron, zinc, aluminum, or an alloy thereof can be employed. Among them, at least one selected from titanium, stainless steel, aluminum, nickel, and silver is preferably used in terms of workability and far-infrared disguise.
かかる金属層は、真空蒸着法、スパッタリング法、イオンプレーティング法などにより形成することができる。この中でも、薄膜形成が容易であることから、スパッタリング法が好ましく採用される。 Such a metal layer can be formed by a vacuum deposition method, a sputtering method, an ion plating method, or the like. Among these, since the thin film formation is easy, the sputtering method is preferably employed.
かかる金属層の厚さは、０．００３〜０．０９μｍであることが好ましい。すなわち、かかる金属層の厚さが、０．００３μｍ以上とすることで、遠赤外線偽装性向上の実効を得ることができる。一方、０．０９μｍ以下とすることで、複合シートの柔軟性が阻害されるのを防ぐことができ、かつ、金属特有の光沢を抑制することができる。 The thickness of the metal layer is preferably 0.003 to 0.09 μm. That is, when the thickness of the metal layer is 0.003 μm or more, the effect of improving far-infrared disguise can be obtained. On the other hand, by setting it as 0.09 micrometer or less, it can prevent that the softness | flexibility of a composite sheet is inhibited, and can suppress the glossiness peculiar to a metal.
またこの時、厚みの異なる金属層を部分的に形成してもよい。そうすることで、複合シートの熱放射を多段階に分布させることができ、さらに遠赤外線偽装効果を向上させることができる。ここでいう、多段階に分布するとは、複合シート表面に、相異なる熱放射を有する領域が、多数分布して存在することを意味するものである。 At this time, metal layers having different thicknesses may be partially formed. By doing so, the thermal radiation of the composite sheet can be distributed in multiple stages, and the far infrared disguise effect can be further improved. Here, “distributed in multiple stages” means that a large number of regions having different heat radiation are present on the surface of the composite sheet.
金属層は、基材上に直接形成してもよいし、他の機能性付与層の上に形成してもよい。ただし、着色層による可視光偽装性の実効を得るために、この着色層より下層に形成するのが好ましい。なお、基材に隣接しない難燃樹脂層は、該金属層と該着色層の層間に形成されていてもよい。 The metal layer may be formed directly on the substrate, or may be formed on another functional layer. However, in order to obtain the effect of visible light disguise by the colored layer, it is preferable to form the colored layer below the colored layer. In addition, the flame retardant resin layer not adjacent to the substrate may be formed between the metal layer and the colored layer.
本発明の複合シートにおいて、その表面の平均熱放射率は０．３５〜０．７０の範囲に制御されていることが好ましい。平均熱放射率が０．３５未満になると自然環境（背景）より低温側に傾き、また０．７０を超えると高温側に傾くため、赤外線カメラによる撮影において、周囲から偽装対象物が識別され難くするためにも表面の平均熱放射率は０．３５〜０．７０とすることが好ましい。 In the composite sheet of the present invention, the average thermal emissivity of the surface is preferably controlled in the range of 0.35 to 0.70. When the average thermal emissivity is less than 0.35, it tilts to the lower temperature side than the natural environment (background), and when it exceeds 0.70, it tilts to the higher temperature side. In order to achieve this, the average thermal emissivity of the surface is preferably 0.35 to 0.70.
本発明でいう着色層は、該複合シートの可視光線や近赤外線に対する偽装性能を、着色剤により向上させるものである。近赤外線カメラに対する偽装効果を得られるようにするには、偽装シートとしての近赤外線反射率が遮蔽対象物の周囲の環境に混和するような着色剤を使用することが好ましい。 The colored layer referred to in the present invention is to improve the camouflage performance of the composite sheet with respect to visible light and near infrared light with a colorant. In order to obtain the camouflage effect for the near-infrared camera, it is preferable to use a colorant whose near-infrared reflectance as the camouflaged sheet is mixed with the environment around the shielding object.
かかる着色層に使用される着色剤としては、顔料、染料が挙げられ、中でも無機顔料、有機顔料が好ましい。かかる無機顔料としては、例えば、酸化チタン、炭酸カルシウム、ベンガラなどを主成分とする顔料などを挙げることができ、有機顔料としては例えば、アゾ顔料、フタロシアニン顔料、スレン顔料、イソインドリン顔料などを挙げることができる。 Examples of the colorant used in the colored layer include pigments and dyes. Among these, inorganic pigments and organic pigments are preferable. Examples of such inorganic pigments include pigments mainly composed of titanium oxide, calcium carbonate, bengara, and the like. Examples of organic pigments include azo pigments, phthalocyanine pigments, selenium pigments, and isoindoline pigments. be able to.
かかる着色層を形成する樹脂としては、例えば、ビニル系、アクリル系、ウレタン系、ポリアミド系、ポリエステル系、エポキシ系、アルキッド系、ポリスチレン系、フッ素系などの樹脂が挙げられる。これらの中でも、柔軟性および金属層への接着性の面からウレタン系樹脂が好ましく使用される。 Examples of the resin forming the colored layer include vinyl-based, acrylic-based, urethane-based, polyamide-based, polyester-based, epoxy-based, alkyd-based, polystyrene-based, and fluorine-based resins. Among these, urethane-based resins are preferably used in terms of flexibility and adhesion to the metal layer.
かかる着色層は、着色剤を含む水系樹脂、有機溶剤系樹脂またはエマルジョンを、コーティング方式、プリント（顔料捺染）方式、噴霧方式、印刷方式などで基材シート等の上に塗布し、乾燥して形成することができる。 Such a colored layer is formed by applying a water-based resin, an organic solvent-based resin or an emulsion containing a colorant onto a substrate sheet or the like by a coating method, a printing (pigment printing) method, a spraying method, a printing method, or the like, and then drying. Can be formed.
着色層単独の厚さとしては、０．５〜１０μｍであることが好ましい。０．５μｍ以上とすることで、着色剤含有樹脂層の下にある基材シートやあるいは層の色が透けて見えるのを防ぎ、着色による色を呈することができる。一方、１０μｍ以下とすることで、柔軟性や収納性が低下するのを防ぐとともに、着色剤含有樹脂層から発せられる熱放射が高くなることによる遠赤外線偽装効果の低下を防ぐことができる。 The thickness of the colored layer alone is preferably 0.5 to 10 μm. By setting it as 0.5 micrometer or more, it can prevent that the color of the base material sheet or layer under a colorant containing resin layer sees through, and can exhibit the color by coloring. On the other hand, by setting it as 10 micrometers or less, while preventing a softness | flexibility and storage property falling, the fall of the far-infrared camouflage effect by the thermal radiation emitted from a colorant containing resin layer becoming high can be prevented.
また、着色層は、迷彩模様を呈してもよい。そのようにすることで、可視光偽装性能および近赤外線偽装性能をさらに高めることができる。迷彩模様は、自然環境、すなわち樹木、草、土などに調和した複数色の色相からなる規則的あるいは不規則的な形状の柄模様である。迷彩模様を形成する色は、着色剤含有樹脂における着色剤の選択により得ることができる。また、迷彩模様を呈する各色の着色剤含有樹脂層の厚さを異ならせることで、熱放射を多段階に分布させることができる。 The colored layer may exhibit a camouflage pattern. By doing so, visible light camouflage performance and near infrared camouflage performance can be further enhanced. The camouflage pattern is a regular or irregular pattern having a plurality of hues in harmony with the natural environment, that is, trees, grass, soil, and the like. The color forming the camouflage pattern can be obtained by selecting a colorant in the colorant-containing resin. Moreover, thermal radiation can be distributed in multiple stages by varying the thickness of the colorant-containing resin layer of each color that exhibits a camouflage pattern.
着色層は、難燃樹脂層の下層および上層のいずれに形成してもよい。ただし、着色層による可視光偽装性の実効を得るために、最外層部分に形成するのが好ましい。 The colored layer may be formed on either the lower layer or the upper layer of the flame retardant resin layer. However, in order to obtain the effect of visible light disguise by the colored layer, it is preferably formed in the outermost layer portion.
また、必要に応じて、着色層または／および難燃樹脂層に近赤外線反射調整剤を添加してもよい。工程を少なくできる点では、着色層または難燃樹脂層のいずれかに近赤外線反射調整剤を添加するのが好ましい。近赤外線反射調整剤を添加することで、周囲の環境が有する近赤外線反射率に同化しやすくなり、該偽装シートに高い近赤外線偽装効果を付与することができる。 Moreover, you may add a near-infrared reflection regulator to a colored layer or / and a flame-retardant resin layer as needed. In terms of reducing the number of steps, it is preferable to add a near-infrared reflection modifier to either the colored layer or the flame retardant resin layer. By adding a near-infrared reflection adjusting agent, it becomes easy to assimilate to the near-infrared reflectance of the surrounding environment, and a high near-infrared camouflaging effect can be imparted to the camouflaged sheet.
かかる近赤外線反射調整剤とは、近赤外線反射剤や近赤外線吸収剤を言う。近赤外線反射剤としては、特に限定されるものではないが、酸化チタン、酸化アルミニウム、アルミン酸亜鉛、硫酸バリウム等を挙げることができる。また、近赤外線吸収剤としては、特に限定されるものではないが、カーボンブラック、フタロシアニン系化合物、アントラキノン系化合物等を挙げることができる。 Such near-infrared reflection modifiers refer to near-infrared reflectors and near-infrared absorbers. Although it does not specifically limit as a near-infrared reflector, Titanium oxide, aluminum oxide, zinc aluminate, barium sulfate etc. can be mentioned. Moreover, as a near-infrared absorber, although it does not specifically limit, carbon black, a phthalocyanine type compound, an anthraquinone type compound, etc. can be mentioned.
近赤外線反射量は、前記金属層の厚み、または金属の種類によって変化するため、かかる近赤外線反射調整剤の着色層あるいは難燃樹脂層に対する添加量は、金属層の厚み、または金属の種類にあわせて、周囲の環境が有する近赤外線反射率に同化するように、適宜調整するとよい。 Since the amount of near-infrared reflection varies depending on the thickness of the metal layer or the type of metal, the amount of the near-infrared reflection modifier added to the colored layer or the flame-retardant resin layer depends on the thickness of the metal layer or the type of metal. In addition, it may be adjusted as appropriate so as to assimilate the near infrared reflectance of the surrounding environment.
また、近赤外線反射調整剤を着色層に添加する場合、それぞれの色に対する添加量を異ならせることで、該複合シートの近赤外線反射率を多段階に分布させることができる点で好ましい。 Moreover, when adding a near-infrared reflection control agent to a colored layer, it is preferable at the point which can distribute the near-infrared reflectance of this composite sheet in multiple steps by varying the addition amount with respect to each color.
本発明の複合シートは、導電樹脂層を形成していることが好ましい。かかる導電樹脂としては、電子伝導性フィラー等の導電性材料を含有する樹脂が挙げられ、導電樹脂層を形成することで、レーダー波に対する反射特性を周囲の環境の反射特性に近似させる実効を得ることができる。 The composite sheet of the present invention preferably has a conductive resin layer. Examples of such a conductive resin include a resin containing a conductive material such as an electron conductive filler. By forming a conductive resin layer, the effect of approximating the reflection characteristics with respect to the radar wave to the reflection characteristics of the surrounding environment is obtained. be able to.
電子伝導性フィラーとしては例えば、カーボンブラック、グラファイト、カーボンナノチューブなどの炭素質粒子や、炭素繊維や、銀、ニッケルなどの金属粉や、酸化スズ、酸化チタン、酸化亜鉛などの導電性金属酸化物の単体や、硫酸バリウムなどの絶縁性粒子を芯体にして前記導電性金属酸化物を湿式的に被覆したものや、導電性金属炭化物や、導電性金属窒化物や、導電性金属ホウ化物を挙げることができる。また、電子伝導性フィラーは、一種を単独で用いてもよいし、複数種を組み合わせて用いてもよい。 Examples of the electron conductive filler include carbonaceous particles such as carbon black, graphite, and carbon nanotubes, carbon fibers, metal powders such as silver and nickel, and conductive metal oxides such as tin oxide, titanium oxide, and zinc oxide. Or a conductive metal oxide wet-coated with insulating particles such as barium sulfate as a core, conductive metal carbide, conductive metal nitride, and conductive metal boride. Can be mentioned. Moreover, an electron conductive filler may be used individually by 1 type, and may be used in combination of multiple types.
導電樹脂を形成する樹脂としては例えば、ビニル系、アクリル系、ウレタン系、ポリアミド系、ポリエステル系、エポキシ系、アルキッド系、ポリスチレン系、フッ素系などの樹脂を挙げることができる。 Examples of the resin forming the conductive resin include vinyl resins, acrylic resins, urethane resins, polyamide resins, polyester resins, epoxy resins, alkyd resins, polystyrene resins, fluorine resins, and the like.
導電樹脂層は、導電性材料を混合した樹脂液を、コーティング方式、ディッピング方式、プリント（顔料捺染）方式、噴霧方式、印刷方式などでシートに塗布し、乾燥して形成することができる。 The conductive resin layer can be formed by applying a resin liquid mixed with a conductive material to a sheet by a coating method, a dipping method, a printing (pigment printing) method, a spraying method, a printing method, and the like, and then drying.
導電樹脂層は、基材に隣接してもよいし、金属層とその他の機能性付与層との間、もしくはその他の機能性付与層の層間やその上に形成してもよい。ただし、基材シートに隣接しない場合は、各機能性付与層の性能を阻害しない厚みや色でなければならない。導電樹脂層も金属層の上部に形成する場合は、複合シートの熱放射率に影響を与え得るので、平均熱放射率が所望の範囲に制御されるよう留意するのが望ましい。基材の片面に形成する難燃樹脂層と導電樹脂層を含む機能性付与層をあわせた厚みは１〜２０μｍであることが好ましい。各層の性能向上の実効を得るためには、導電樹脂層は、基材シートに隣接するのが好ましい。 The conductive resin layer may be adjacent to the substrate, or may be formed between the metal layer and the other functional layer, or between or on the other functional layer. However, when it is not adjacent to the base sheet, it must have a thickness and color that do not impair the performance of each functional layer. When the conductive resin layer is also formed on the metal layer, it may affect the thermal emissivity of the composite sheet. Therefore, it is desirable to take care that the average thermal emissivity is controlled within a desired range. The combined thickness of the flame retardant resin layer formed on one side of the substrate and the functional layer including the conductive resin layer is preferably 1 to 20 μm. In order to obtain the effect of improving the performance of each layer, the conductive resin layer is preferably adjacent to the base sheet.
本発明の複合シートは、難燃性がＪＩＳ Ａ １３２２（１９６６）に規定される防炎１級、２級を満足することが好ましい。当該基準を満足することで、使用の際、万一偽装シートに炎が着火しても、炎はすぐに鎮火し、燃え広がりを防ぐことができる。 It is preferable that the composite sheet of the present invention satisfies the flameproof grades 1 and 2 defined by JIS A 1322 (1966). By satisfying the standard, in the event of use, even if a flame is ignited in the camouflaged sheet, the flame is immediately extinguished and the spread of the flame can be prevented.
（１）複合シートの難燃性
ＪＩＳ Ａ １３２２−１９６６に拠って測定した。
（試験体）
試験体の形状は約３０ｃｍ×２０ｃｍとした。
試験体の前処理にはＡ法を採用し、およそ気乾状態の試験体を５０±２℃で４８時間乾燥し、ついでこれを乾燥用シリカゲルを入れたデシケータ中に２４時間放置してから加熱試験を行った。
（加熱試験装置）
加熱試験は、本規定に則った加熱試験装置を用い、容器内で行った。
加熱試験に用いるバーナは、高さ１６０ｍｍ、内径２０ｍｍのメッケルバーナを用い、１次空気を混入しないでガスだけを送入した。
加熱試験に用いる燃料は、ＪＩＳ Ｋ ２２４０（２０１３）に規定された液化石油ガス５号を用いた。
（加熱試験）
加熱試験装置の所定の位置にバーナを置き、支持わくを取り付けない状態で、炎の長さが６５ｍｍになるように調整した。
試験体は本規定に則った支持わくにはさみ、たるみのないようにして、加熱試験装置に取り付けた。
バーナの点火には感応コイルを使用し、加熱の終了時には燃料コックを閉じた。
加熱時間は１０秒とした。
測定項目として、残炎は、加熱終了時から試験体が炎をあげて燃え続ける時間を測定した。
測定項目として、残じんは、加熱終了時から１分後に無炎燃焼している状態を観察によって判定した。
測定項目として、炭化長は、試験体の加熱面の炭化部分について、支持わくの長手方向の最大長さを測定した。
試験の回数は、複合シートの表裏面、タテ／ヨコについて各３回とし、上記の各測定項目について、最大の値を採用し、次の基準にて難燃性の区分付けを行った。
・防炎１級：炭化長が５ｃｍ以下であり、残炎がなく（大体１秒以下）、かつ、残じんが１分後に存していなかった。
・防炎２級：炭化長が１０ｃｍ以下であり、残炎が５秒以下であり、かつ、残じんが１分後に存していなかった。
・防炎３級：炭化長が１５ｃｍ以下であり、残炎が５秒以下であり、かつ、残じんが１分後に存していなかった。
(1) Flame retardancy of composite sheet: Measured according to JIS A 1322-1966.
(Test specimen)
The shape of the test body was about 30 cm × 20 cm.
Method A was used for pretreatment of the test specimen. The test specimen in an air-dried state was dried at 50 ± 2 ° C. for 48 hours, and then left in a desiccator containing silica gel for drying for 24 hours and then heated. A test was conducted.
(Heating test equipment)
The heating test was carried out in a container using a heating test apparatus according to this rule.
As the burner used for the heating test, a Meckel burner having a height of 160 mm and an inner diameter of 20 mm was used, and only gas was fed without mixing primary air.
As the fuel used for the heating test, liquefied petroleum gas No. 5 defined in JIS K 2240 (2013) was used.
(Heating test)
A burner was placed at a predetermined position of the heating test apparatus, and the length of the flame was adjusted to 65 mm with no support frame attached.
The test body was attached to the heating test apparatus so as not to sag and to be held between support frames according to this rule.
A sensitive coil was used to ignite the burner, and the fuel cock was closed at the end of heating.
The heating time was 10 seconds.
As a measurement item, the after flame was measured for the time that the specimen continued to burn with flames from the end of heating.
As a measurement item, the residual dust was determined by observation of a state of flameless combustion 1 minute after the end of heating.
As a measurement item, the carbonization length was determined by measuring the maximum length in the longitudinal direction of the support frame for the carbonized portion of the heating surface of the test specimen.
The number of tests was 3 times for each of the front and back surfaces of the composite sheet and the length / width, and the maximum value was adopted for each of the above measurement items, and the flame retardancy was classified according to the following criteria.
Flameproof grade 1: The carbonization length was 5 cm or less, there was no afterflame (approximately 1 second or less), and no residual dust was present after 1 minute.
Flameproof grade 2: Carbonization length was 10 cm or less, afterflame was 5 seconds or less, and no residual dust was present after 1 minute.
Flameproof third grade: carbonization length was 15 cm or less, afterflame was 5 seconds or less, and no residual dust was present after 1 minute.
（２）複合シートの偽装性
大きさ１ｍ×１ｍの試料を、周囲に植生が存在する環境下におき、周波数９．８ＧＨｚのレーダー波測定装置（アジレントテクノロジー（株）製）にて偽装性をレーダー偽装性として確認した。また、目視で周囲との混和を目視偽装性として確認した。それぞれ周囲の植生と混和している場合を○、混和していない場合を×とした。試験は、試料の表（Ａ）面、裏（Ｂ）面のそれぞれについて実施した。
(2) Impersonation of composite sheet A sample with a size of 1m x 1m is placed in an environment where vegetation is present in the surrounding area, and impersonation is performed with a radar wave measuring device (manufactured by Agilent Technologies) with a frequency of 9.8 GHz. Confirmed as radar disguise. Moreover, mixing with the surroundings was confirmed visually as visual disguise. The case where each was mixed with the surrounding vegetation was marked as ◯, and the case where it was not mixed was marked as x. The test was performed on each of the front (A) surface and the back (B) surface of the sample.
［実施例１］
総繊度５６０ｄｔｅｘ、フィラメント数９６本のポリエチレンテレフタレート（ＰＥＴ）繊維を使用して、織密度：経３５本／２５ｍｍ、緯３５本／２５ｍｍの平織を得た。
得られた織物を常法により精錬し、１８０℃で熱セットした。この織物を基材シートとした。
[Example 1]
Using a polyethylene terephthalate (PET) fiber having a total fineness of 560 dtex and 96 filaments, a plain weave having a weaving density of warp 35/25 mm and weft 35/25 mm was obtained.
The obtained woven fabric was refined by a conventional method and heat-set at 180 ° C. This fabric was used as a base sheet.
上記基材シートの片面（Ｂ面）に、ブロモ系難燃化剤を１５質量％含有するウレタン樹脂からなる難燃樹脂を質量４０ｇ／ｍ２になるように、コーティングにて塗布して難燃層を形成した。次に、該難燃層をコートした面と反対面（Ａ面）に導電樹脂を質量１５ｇ／ｍ２になるようにコーティングにて塗布して導電層を形成し、更にその上に前記ブロモ系難燃化剤を１５質量％含有するウレタン樹脂からなる難燃樹脂を質量２０ｇ／ｍ２になるように、コーティングにて塗布して難燃層を形成した。該シートの両面に、片面の厚みが０．０１μｍの金属薄膜を積層して金属層を形成し、更にその上に片面の質量が１０ｇ／ｍ２となるようにコーティングにて塗布して着色層を形成して偽装シートとした。 A flame retardant resin made of urethane resin containing 15% by mass of a bromo flame retardant is applied to one side (B side) of the base sheet by coating so that the mass becomes 40 g / m 2. A layer was formed. Next, a conductive resin is applied to the surface opposite to the surface coated with the flame retardant layer (A surface) by coating so that the mass becomes 15 g / m 2 , and a conductive layer is further formed thereon, and the bromo series is further formed thereon. A flame retardant layer was formed by coating a flame retardant resin composed of a urethane resin containing 15% by mass of a flame retardant so as to have a mass of 20 g / m 2 . A metal layer is formed on both sides of the sheet by laminating a metal thin film having a thickness of 0.01 μm on one side, and further, a colored layer is applied thereon by coating so that the mass on one side is 10 g / m 2. To form a camouflaged sheet.
上記基材シートの両面に形成した金属層は、アルゴン雰囲気中でアルミのスパッタリング加工を施して、厚さが基材シートの片面につき０．０１μｍの金属薄膜層を形成したものを用いた。 The metal layer formed on both surfaces of the base material sheet was formed by performing aluminum sputtering in an argon atmosphere to form a metal thin film layer having a thickness of 0.01 μm on one surface of the base material sheet.
なお、上記基材シートの両面に形成した着色層は、淡緑色顔料を水系アクリル系樹脂に混合した着色剤含有樹脂を用いたが、淡緑色に限定されるものではなく、必要に応じ濃緑色、茶色、黒色等の他の顔料も用いることができ、単色でも多色で形成してもよく、多色で形成する場合には、コーティングによる塗布以外に、凸版印刷機（フレキソ印刷）にて塗布して形成することが可能である。 In addition, although the coloring layer formed on both surfaces of the said base material sheet used the colorant containing resin which mixed the light green pigment with water-based acrylic resin, it is not limited to light green, dark green as needed Other pigments such as brown and black can also be used, and may be formed in a single color or multiple colors. When forming in multiple colors, in addition to coating by coating, a letterpress printing machine (flexographic printing) It can be formed by coating.
［実施例２］
実施例１と同様の基材を用い、該基材の両面に難燃層を隣接し、その片面（Ａ面）に導電層を形成した以外は、実施例１と同様の構成として偽装シートとした。
[Example 2]
A camouflaged sheet having the same structure as in Example 1 except that a base material similar to that in Example 1 was used, a flame retardant layer was adjacent to both surfaces of the base material, and a conductive layer was formed on one surface (A surface). did.
［実施例３］
実施例１と同様の基材を用い、実施例１と同様の方法で、基材の片面（Ｂ面）側に難燃層、反対（Ａ面）側に導電層を形成して、その両面に金属層形成し、Ｂ面側に導電層、Ａ面側に難燃層を形成し、さらに両面に着色層を形成して偽装シートとした。
[Example 3]
Using the same base material as in Example 1, a flame retardant layer is formed on one side (B side) side of the base material, and a conductive layer is formed on the opposite side (A side) in the same manner as in Example 1. A metal layer was formed, a conductive layer was formed on the B surface side, a flame retardant layer was formed on the A surface side, and a colored layer was further formed on both surfaces to obtain a camouflaged sheet.
［実施例４］
実施例３のＢ面側の着色層を形成せずに偽装シートとした。
[Example 4]
A camouflaged sheet was formed without forming the colored layer on the B-side of Example 3.
［比較例１］
実施例１の基材に隣接する難燃層の質量を６０ｇ／ｍ２とし、導電層の上の難燃層を形成させない（Ａ面に難燃層が含まれない）構成とした。
[Comparative Example 1]
The mass of the flame retardant layer adjacent to the base material of Example 1 was set to 60 g / m 2 , so that the flame retardant layer on the conductive layer was not formed (the A surface does not include the flame retardant layer).
［比較例２］
難燃層の質量を１２０ｇ／ｍ２とした他は、比較例１と同様の構成とした。
[Comparative Example 2]
The configuration was the same as that of Comparative Example 1 except that the mass of the flame retardant layer was 120 g / m 2 .
［比較例３］
実施例１で用いたのと同様の基材を用い、実施例１と同様の方法で、基材の片面（Ａ面）側に導電層、反対（Ｂ面）側に金属層を形成して、その上のＡ面側に金属層、難燃層を、Ｂ面側に難燃層を形成し、さらに両面に着色層を形成して偽装シートとした。
[Comparative Example 3]
Using a substrate similar to that used in Example 1, a conductive layer is formed on one side (A surface) side of the substrate and a metal layer is formed on the opposite (B surface) side in the same manner as in Example 1. The camouflaged sheet was formed by forming a metal layer and a flame retardant layer on the A surface side, a flame retardant layer on the B surface side, and further forming a colored layer on both surfaces.
［比較例４］
比較例３のＢ面側に形成した難燃層を取り除いた構成とした。
[Comparative Example 4]
The flame retardant layer formed on the B surface side of Comparative Example 3 was removed.
実施例、比較例の各シートの性能を表１に示す。表１に示すとおり、実施例は、比較例と同じ偽装性を有するにも関わらず、難燃性に優れ、軽量なものである。 Table 1 shows the performance of each sheet of Examples and Comparative Examples. As shown in Table 1, the examples are excellent in flame retardancy and light weight despite having the same disguise as the comparative example.
Claims (5)