JP2017210724A - Construction method for concrete structure, and concrete structure - Google Patents

Construction method for concrete structure, and concrete structure Download PDF

Info

Publication number
JP2017210724A
JP2017210724A JP2016102400A JP2016102400A JP2017210724A JP 2017210724 A JP2017210724 A JP 2017210724A JP 2016102400 A JP2016102400 A JP 2016102400A JP 2016102400 A JP2016102400 A JP 2016102400A JP 2017210724 A JP2017210724 A JP 2017210724A
Authority
JP
Japan
Prior art keywords
water repellent
concrete structure
hollow path
silane
repellent layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2016102400A
Other languages
Japanese (ja)
Inventor
サンジェイ パリーク
Pareek Sanjay
サンジェイ パリーク
雅人 尾形
Masato Ogata
雅人 尾形
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nihon University
Original Assignee
Nihon University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nihon University filed Critical Nihon University
Priority to JP2016102400A priority Critical patent/JP2017210724A/en
Publication of JP2017210724A publication Critical patent/JP2017210724A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a construction method for a concrete structure, which maintains a repellent layer on a long-term basis.SOLUTION: A construction method for a concrete structure includes: a hollow passage formation step of forming a hollow passage 4, which has an opening 4a on an outer wall surface 1a, in a concrete base 2 inside which a reinforcement 3 is arranged; and a water-repellent layer formation step of forming a water-repellent layer 2a on the periphery of the hollow passage 4 by making a water-repellent impregnation material flow into the hollow passage 4 and holding the water-repellent impregnation material for a defined period of time in a pressurized state.SELECTED DRAWING: Figure 1

Description

本発明は、コンクリート構造物の施工方法及びコンクリート構造物に関するものである。   The present invention relates to a concrete structure construction method and a concrete structure.

鉄筋が内部に配設されたコンクリート構造物は、発生したひび割れ等から侵入する水分や塩化物が鉄筋と接触することにより、鉄筋に錆が発生する。これを防ぐために、コンクリート構造物の外壁面に、撥水剤が塗布されることがある。例えば、特許文献１におけるコンクリート構造物は、外壁面に塗布されたシラン系撥水剤により、外壁面に撥水層が形成されている。   In the concrete structure in which the reinforcing bars are arranged, rust is generated in the reinforcing bars when moisture or chloride entering from the generated cracks or the like comes into contact with the reinforcing bars. In order to prevent this, a water repellent may be applied to the outer wall surface of the concrete structure. For example, in the concrete structure in Patent Document 1, a water repellent layer is formed on the outer wall surface by a silane-based water repellent applied to the outer wall surface.

特開２００９−９１１６７号公報JP 2009-911167 A

しかしながら、このような外壁面に形成された撥水層は、表面が太陽光や雨等の外的な環境変化に直接晒されることとなる。このため、撥水層は、紫外線による劣化やシラン系撥水剤の流出により、長期的に保持すること難しく、シラン系撥水剤の再塗布等のメンテナンスが必要となる。   However, the surface of the water repellent layer formed on such an outer wall surface is directly exposed to external environmental changes such as sunlight and rain. For this reason, the water-repellent layer is difficult to hold for a long time due to deterioration due to ultraviolet rays or silane-based water repellent outflow, and maintenance such as re-application of the silane-based water repellent is required.

本発明は、上述する問題点に鑑みてなされたもので、コンクリート構造物の施工方法であって、撥水層を長期的に保持することを目的とする。   This invention is made | formed in view of the problem mentioned above, Comprising: It is a construction method of a concrete structure, Comprising: It aims at hold | maintaining a water repellent layer for a long term.

上記目的を達成するために、本発明では、コンクリート構造物の施工方法に係る第１の手段として、 鉄筋が内部に配設されたコンクリートに、外壁面に開口部を有する中空路を形成する中空路形成工程と、上記中空路に撥水性含浸材を注入すると共に加圧状態で一定時間上記撥水性含浸材を保持することにより上記中空路の周囲に撥水層を形成する撥水層形成工程とを有する、という構成を採用する。   In order to achieve the above object, in the present invention, as a first means related to a concrete structure construction method, a hollow path having an opening on an outer wall surface is formed in concrete in which reinforcing bars are disposed. An air passage forming step, and a water repellent layer forming step for forming a water repellent layer around the hollow passage by injecting a water repellent impregnation material into the hollow passage and holding the water repellent impregnation material in a pressurized state for a certain time. The structure of having is adopted.

コンクリート構造物の施工方法に係る第２の手段として、上記第１の手段において、上記中空路は、上記鉄筋に沿って形成される、という構成を採用する。   As a second means related to the construction method of the concrete structure, a configuration is adopted in which, in the first means, the hollow path is formed along the reinforcing bar.

コンクリート構造物の施工方法に係る第３の手段として、上記第２の手段において、上記中空路は、上記鉄筋よりも外壁面側に形成される、という構成を採用する。   As a third means related to the construction method of the concrete structure, in the second means, a configuration is adopted in which the hollow path is formed on the outer wall surface side with respect to the reinforcing bar.

コンクリート構造物に係る第１の手段として、鉄筋が内部に配設されたコンクリート構造物であって、外壁面に開口部を有する中空路と、上記中空路の周囲に形成された撥水層とを有する、という構成を採用する。   As a first means related to a concrete structure, a concrete structure in which reinforcing bars are disposed inside, a hollow path having an opening on an outer wall surface, and a water repellent layer formed around the hollow path, The structure of having is adopted.

本発明によれば、撥水性含浸材は、コンクリート構造物の外壁面に開口部を有する中空路に注入され、さらに加圧状態で保持される。これにより、撥水性含浸材は、中空路の内壁から周囲へと含浸し、中空路の内壁の周囲に撥水層を形成することができる。このような撥水層は、外部に露出する部分が少ないため、外的環境の影響を受け難く、長期的に保持される。   According to the present invention, the water-repellent impregnating material is injected into a hollow passage having an opening on the outer wall surface of a concrete structure, and is further held in a pressurized state. Thereby, the water-repellent impregnating material can be impregnated from the inner wall of the hollow path to the periphery, and a water-repellent layer can be formed around the inner wall of the hollow path. Since such a water-repellent layer has few exposed parts, it is hardly affected by the external environment and is retained for a long time.

本発明の一実施形態に係るコンクリート構造物の一部を示す模式断面図である。It is a schematic cross section showing a part of a concrete structure according to an embodiment of the present invention. 本発明の一実施形態に係るコンクリート構造物の中空路形成工程の過程を示す模式断面図である。It is a schematic cross section which shows the process of the hollow path formation process of the concrete structure which concerns on one Embodiment of this invention. 本発明の一実施形態に係るコンクリート構造物の撥水層形成工程の過程を示す模式断面図である。It is a schematic cross section which shows the process of the water-repellent layer formation process of the concrete structure concerning one Embodiment of this invention. 本発明に係る施工方法の効果の検証結果であり、（ａ）がシラン系撥水剤の注入時間に対するシラン系撥水剤の浸透深さ及び浸透量の相関を示すグラフであり、（ｂ）がシラン系撥水剤の浸透面積率と浸透量との相関を示すグラフであり、（ｃ）がシラン系撥水剤の浸透量とコンクリートの中性化深さとの相関を示すグラフである。It is a verification result of the effect of the construction method which concerns on this invention, (a) is a graph which shows the correlation of the penetration depth of a silane type water repellent with respect to the injection | pouring time of a silane type water repellent, and the penetration amount, (b) Is a graph showing the correlation between the penetration ratio of the silane water repellent and the penetration amount, and (c) is a graph showing the correlation between the penetration amount of the silane water repellent and the neutralization depth of concrete. 本発明の一実施形態に係るコンクリート構造物の変形例である。It is a modification of the concrete structure which concerns on one Embodiment of this invention.

以下、図面を参照して、本発明に係るコンクリート構造物の施工方法及びコンクリート構造物の一実施形態について説明する。なお、以下の図面において、各部材を認識可能な大きさとするために、各部材の縮尺を適宜変更している。図１は、本実施形態に係るコンクリート構造物１の一部を示す模式断面図である。   Hereinafter, an embodiment of a concrete structure construction method and a concrete structure according to the present invention will be described with reference to the drawings. In the following drawings, the scale of each member is appropriately changed in order to make each member a recognizable size. FIG. 1 is a schematic cross-sectional view showing a part of a concrete structure 1 according to this embodiment.

図１は、本実施形態に係るコンクリート構造物１の一部を示す模式断面図である。本実施形態に係るコンクリート構造物１は、コンクリート基部２と、鉄筋３と、中空路４とを有する鉄筋コンクリート構造物である。また、コンクリート構造物１は、外部に露出している外壁面１ａ、１ｂ、１ｃを有している。このようなコンクリート構造物１には、例えば、梁、柱等の建築構造物や、ダム等の土木構造物が好適である。   FIG. 1 is a schematic cross-sectional view showing a part of a concrete structure 1 according to this embodiment. A concrete structure 1 according to this embodiment is a reinforced concrete structure having a concrete base 2, a reinforcing bar 3, and a hollow path 4. Moreover, the concrete structure 1 has the outer wall surfaces 1a, 1b, and 1c exposed to the outside. As such a concrete structure 1, for example, a building structure such as a beam or a column, or a civil engineering structure such as a dam is suitable.

コンクリート基部２は、型枠にコンクリートが打設されることにより形成されており、撥水層２ａを有している。撥水層２ａは、図１に示すように、中空路４を中心として、鉄筋３を含む円柱状の領域に形成されている。このような撥水層２ａは、中空路４の内壁面からシラン系撥水剤（撥水性含浸材）を含浸させることにより形成されている。シラン系撥水剤は、コンクリートに含浸することにより、含浸した範囲を疎水化する特性を有している。鉄筋３は、この撥水層２ａにより、近接する外壁面１ｃより侵入した水分及び塩化物イオンと接触することがなく、劣化しにくくなる。   The concrete base 2 is formed by placing concrete on a mold and has a water repellent layer 2a. As shown in FIG. 1, the water repellent layer 2 a is formed in a columnar region including the rebar 3 with the hollow path 4 as the center. Such a water repellent layer 2 a is formed by impregnating a silane water repellent (water repellent impregnating material) from the inner wall surface of the hollow path 4. Silane-based water repellents have the property of making the impregnated region hydrophobic by impregnating concrete. The water repellent layer 2a does not come into contact with moisture and chloride ions that have entered from the adjacent outer wall surface 1c, and the rebar 3 is not easily deteriorated.

鉄筋３は、コンクリート基部２の引張強度を補強するため、コンクリート基部２に配設されている細長状の鋼材である。このような鉄筋３は、コンクリート構造物１において、外壁面１ｃから所定のかぶり厚さが確保された位置に内設されている。この中空路４は、鉄筋３よりも外側、すなわち、鉄筋３と、鉄筋３と近接する外壁面１ｃとの間において、鉄筋３に沿ってコンクリート基部２に形成されている。この中空路４は、円柱状の空洞とされ、一方の外壁面１ｂに第１中空路開口４ａを有し、他方の外壁面１ａに第２中空路開口４ｂが形成されている。なお、この中空路４の体積は、コンクリート構造物１の体積に対して、コンクリート構造物１の強度を損なわないように十分小さく設定されている。   The reinforcing bar 3 is an elongated steel material disposed on the concrete base 2 in order to reinforce the tensile strength of the concrete base 2. Such a reinforcing bar 3 is provided in the concrete structure 1 at a position where a predetermined cover thickness is secured from the outer wall surface 1c. The hollow path 4 is formed on the concrete base 2 along the reinforcing bar 3 outside the reinforcing bar 3, that is, between the reinforcing bar 3 and the outer wall surface 1 c adjacent to the reinforcing bar 3. The hollow path 4 is a cylindrical cavity, and has a first hollow path opening 4a on one outer wall surface 1b and a second hollow path opening 4b formed on the other outer wall surface 1a. The volume of the hollow passage 4 is set to be sufficiently smaller than the volume of the concrete structure 1 so as not to impair the strength of the concrete structure 1.

このようなコンクリート構造物１の施工方法を図２及び図３を参照して説明する。図２は、本実施形態に係るコンクリート構造物１の中空路形成工程の過程を示す模式断面図である。図３は、本実施形態に係るコンクリート構造物１の撥水層形成工程の過程を示す模式断面図である。   The construction method of such a concrete structure 1 is demonstrated with reference to FIG.2 and FIG.3. FIG. 2 is a schematic cross-sectional view illustrating a process of forming a hollow path of the concrete structure 1 according to the present embodiment. FIG. 3 is a schematic cross-sectional view showing the process of the water repellent layer forming step of the concrete structure 1 according to this embodiment.

まず、本実施形態に係るコンクリート構造物１の施工過程では、中空路形成工程が行われる。
図２（ａ）に示すように、不図示の型枠に鉄筋３と、鋼棒Ｓとが配置され、さらに、コンクリート原料が型枠に打設され、所定の期間養生されることにより、鉄筋３及び鋼棒Ｓを内設した状態でコンクリート基部２が硬化する。また、鋼棒Ｓは、事前に外周面全体に剥離剤等が塗布されており、コンクリート基部２が硬化した後に抜去可能とされている。所定期間後に、コンクリートの硬化が完了すると、図２（ｂ）及び（ｃ）に示すように、鋼棒Ｓが引き抜かれ、鋼棒Ｓが配置されていた空間が中空路４となる。 First, in the construction process of the concrete structure 1 according to the present embodiment, a hollow path forming step is performed.
As shown in FIG. 2 (a), a reinforcing bar 3 and a steel rod S are arranged in a mold (not shown), and further, a concrete raw material is placed on the mold and cured for a predetermined period. The concrete base 2 is hardened in a state in which 3 and the steel rod S are installed. Further, the steel rod S is previously coated with a release agent or the like on the entire outer peripheral surface, and can be removed after the concrete base 2 is cured. When the hardening of the concrete is completed after a predetermined period, as shown in FIGS. 2B and 2C, the steel bar S is pulled out, and the space where the steel bar S is arranged becomes the hollow path 4.

中空路形成工程が行われた後に、撥水層形成工程が行われる。
撥水層形成工程では、まず、第１中空路開口４ａに、一端がポンプＰと接続されたホースＨがシラン系撥水剤注入用プラグｐ１を介して接続される。また、第２中空路開口４ｂには、シラン系撥水剤吐出用プラグｐ２が取り付けられる。このポンプＰは、中空路４内にシラン系撥水剤を加圧状態で注入する装置である。このようなポンプＰにより、第１中空路開口４ａから、中空路４内にシラン系撥水剤が加圧注入される。このときのポンプＰの注入圧力は、例えば５ＭＰａ〜１０ＭＰａ程度とされる。 After the hollow path forming step is performed, the water repellent layer forming step is performed.
In the water repellent layer forming step, first, a hose H having one end connected to the pump P is connected to the first hollow passage opening 4a via a silane-based water repellent injection plug p1. A silane water repellent discharge plug p2 is attached to the second hollow passage opening 4b. The pump P is a device that injects a silane water repellent into the hollow path 4 in a pressurized state. With such a pump P, a silane water repellent is pressurized and injected into the hollow path 4 from the first hollow path opening 4a. The injection pressure of the pump P at this time is about 5 MPa to 10 MPa, for example.

さらに、ポンプＰによりシラン系撥水剤の加圧注入が継続されることにより、中空路４内が一定期間にわたり加圧状態で保持される。これにより、中空路４内のシラン系撥水剤は、内壁面より徐々にコンクリート基部２へと含浸することにより撥水層２ａを形成する。なお、この撥水層２ａは、シラン系撥水剤の注入圧力及び加圧時間を増大させることにより、より広範囲に含浸する特性を有している。このため、シラン系撥水剤の注入圧力及び加圧時間を適宜調節することにより、鉄筋３を含む範囲に撥水層２ａを形成することができる。このようにして形成された撥水層２ａは、外的影響を受けにくくシラン系撥水剤の再注入の必要がない。したがって、撥水層形成工程は、コンクリート構造物１の建設時に一度実施するのみで良い。   Furthermore, by continuing the pressure injection of the silane-based water repellent by the pump P, the inside of the hollow path 4 is maintained in a pressurized state for a certain period. Thereby, the silane water repellent in the hollow path 4 gradually impregnates the concrete base 2 from the inner wall surface to form the water repellent layer 2a. The water repellent layer 2a has a characteristic of being impregnated in a wider range by increasing the injection pressure and pressurizing time of the silane water repellent. For this reason, the water repellent layer 2a can be formed in the range including the reinforcing bar 3 by appropriately adjusting the injection pressure and pressurizing time of the silane water repellent. The water repellent layer 2a formed in this manner is not easily affected by external influences and does not require reinjection of a silane water repellent. Therefore, the water repellent layer forming step only needs to be performed once when the concrete structure 1 is constructed.

このような撥水層２ａを形成するためのシラン系撥水剤の注入条件についての検証結果を以下に示す。
検証においては、鉄筋３が内設されると共に中空路４が形成されたコンクリート供試体が作成された。このコンクリート供試体は、水セメント比５７．９％であり、水３１８ｋｇ／ｍ３に対して、セメント１８４ｋｇ／ｍ３、細骨材８５５ｋｇ／ｍ３、粗骨材９３６ｋｇ／ｍ３、ＡＥ減水剤３．１８０ｋｇ／ｍ３を混合したコンクリート材である。また、検証に用いたシラン系撥水剤は、主成分として、シラン・シロキサンを含有し、活性成分が９０％以下であり、粘度が５００ｍＰａ・Ｓ／２５℃である。 The verification results of the injection conditions of the silane-based water repellent for forming such a water repellent layer 2a are shown below.
In the verification, a concrete specimen in which the reinforcing bar 3 was installed and the hollow path 4 was formed was created. This concrete specimen has a water cement ratio of 57.9%, with respect to water 318 kg / m 3 , cement 184 kg / m 3 , fine aggregate 855 kg / m 3 , coarse aggregate 936 kg / m 3 , AE water reducing agent 3. A concrete material mixed with 180 kg / m 3 . The silane-based water repellent used for verification contains silane / siloxane as a main component, has an active component of 90% or less, and a viscosity of 500 mPa · S / 25 ° C.

図４は、（ａ）がシラン系撥水剤の注入時間に対するシラン系撥水剤の浸透深さ及び浸透量の相関を示すグラフであり、（ｂ）がシラン系撥水剤の浸透面積率と浸透量との相関を示すグラフであり、（ｃ）がシラン系撥水剤の浸透量とコンクリートの中性化深さとの相関を示すグラフである。   4A is a graph showing the correlation between the penetration depth and penetration amount of the silane water repellent with respect to the injection time of the silane water repellent, and FIG. 4B is the penetration area ratio of the silane water repellent. And (c) is a graph showing the correlation between the penetration amount of the silane water repellent and the neutralization depth of concrete.

図４（ａ）に示すグラフは、シラン系撥水剤の注入圧力を２ＭＰａ及び５ＭＰａとして、それぞれにおいて、シラン系撥水剤の浸透深さ及び浸透量を注入時間ごとに比較している。このグラフに示すように、注入圧力２ＭＰａ及び注入圧力５ＭＰａのいずれの場合においても、シラン系撥水剤の注入時間を増加させることにより、浸透深さ及び浸透量が増加していることがわかる。また、注入圧力を上昇させることにより、より短時間で、シラン系撥水剤を深くまで浸透させることができることがわかる。すなわち、高い圧力を加えることにより、シラン系撥水材の時間当たりの浸透深さ及び浸透量が増加すると考えられる。   The graph shown in FIG. 4A compares the penetration depth and penetration amount of the silane-based water repellent with each injection time, assuming that the injection pressure of the silane-based water repellent is 2 MPa and 5 MPa. As shown in this graph, it can be understood that the penetration depth and the penetration amount are increased by increasing the injection time of the silane-based water repellent at both injection pressures of 2 MPa and 5 MPa. It can also be seen that by increasing the injection pressure, the silane water repellent can be deeply penetrated in a shorter time. That is, it is considered that the penetration depth and penetration amount per hour of the silane-based water repellent material is increased by applying a high pressure.

図４（ｂ）に示すグラフは、横軸にシラン系撥水剤の浸透量、縦軸にシラン系撥水剤の浸透面積率を取っている。このグラフに示すように、浸透面積率は、シラン系撥水剤の浸透量を増加させることにより、上昇する傾向があることがわかる。すなわち、シラン系撥水剤の浸透量を増加させることにより、撥水層２ａの形成範囲が大きくなると考えられる。   In the graph shown in FIG. 4B, the horizontal axis represents the penetration amount of the silane-based water repellent, and the vertical axis represents the penetration area ratio of the silane-based water repellent. As shown in this graph, it can be seen that the penetration area ratio tends to increase by increasing the penetration amount of the silane water repellent. That is, it is considered that the formation range of the water repellent layer 2a is increased by increasing the penetration amount of the silane water repellent.

図４（ｃ）のグラフは、横軸に注入時間、縦軸に中性化深さを取っている。コンクリートの中性化は、内部の鉄筋３の腐食の要因となる現象である。図４（ｃ）に示すように、注入圧力が２ＭＰａの場合、５ＭＰａの場合共に、注入時間を増加させることにより、中性化深さを抑制できることがわかる。さらに、注入圧力が５ＭＰａの場合は、注入圧力が２ＭＰａの場合と比較して、中性化をより抑制できると考えられる。   In the graph of FIG. 4C, the horizontal axis represents the injection time, and the vertical axis represents the neutralization depth. The neutralization of concrete is a phenomenon that causes corrosion of the internal reinforcing bars 3. As shown in FIG. 4C, it can be seen that the neutralization depth can be suppressed by increasing the injection time in both cases where the injection pressure is 2 MPa and 5 MPa. Furthermore, when the injection pressure is 5 MPa, it is considered that neutralization can be further suppressed as compared with the case where the injection pressure is 2 MPa.

上記の検証結果から、シラン系撥水剤の注入圧力が高いほど、または、注入時間が長いほど撥水層２ａの形成範囲が大きくなる。また、このような撥水層２ａには、中性化を抑制する効果があると認められる。   From the above verification results, the higher the injection pressure of the silane-based water repellent or the longer the injection time, the larger the formation range of the water repellent layer 2a. Moreover, it is recognized that such a water repellent layer 2a has an effect of suppressing neutralization.

このような本実施形態においてシラン系撥水剤は、第１中空路開口４ａを有する中空路４に注入され、さらに加圧状態で保持される。これにより、シラン系撥水剤は、中空路４の内壁面から周囲へと含浸し、中空路４の内壁面の周囲に撥水層２ａを形成することができる。このような撥水層２ａは、外部に露出する部分が少ないため、外的環境により流出または劣化しづらく、長期的に保持される。   In such an embodiment, the silane-based water repellent is injected into the hollow path 4 having the first hollow path opening 4a, and is held in a pressurized state. Accordingly, the silane-based water repellent can be impregnated from the inner wall surface of the hollow path 4 to the periphery, and the water repellent layer 2 a can be formed around the inner wall surface of the hollow path 4. Since such a water repellent layer 2a has few exposed parts, it is difficult to flow out or deteriorate due to the external environment, and is retained for a long time.

また、シラン系撥水剤は、中空路４に加圧注入されることにより、コンクリート基部２への浸透量が、コンクリート構造物１の外壁に塗布される場合と比較して増加する。したがって、一度のシラン系撥水剤注入作業により、十分な浸透深さを得ることができる。また、シラン系撥水剤の注入圧力及び注入時間を適宜変更ことにより、コンクリート基部２への浸透量を調節することが可能である。これにより、所定の浸透量となるまでシラン系撥水剤を複数回塗布する等の作業の必要がなく、一度の作業で必要な浸透量を確保できるため、作業工程を簡略化することができる。したがって、従来工法と比較して、本実施形態に係る施工方法は、時間的なコストを削減することができる。   Further, when the silane-based water repellent is injected into the hollow passage 4 under pressure, the amount of penetration into the concrete base 2 is increased as compared with the case where it is applied to the outer wall of the concrete structure 1. Therefore, a sufficient penetration depth can be obtained by a single silane-based water repellent injection operation. Moreover, it is possible to adjust the amount of penetration into the concrete base 2 by appropriately changing the injection pressure and the injection time of the silane water repellent. As a result, there is no need for work such as applying the silane-based water repellent multiple times until a predetermined amount of penetration is achieved, and the necessary amount of penetration can be ensured in a single operation, thus simplifying the work process. . Therefore, compared with the conventional construction method, the construction method according to the present embodiment can reduce the time cost.

さらに、本実施形態に係るコンクリート構造物１の中空路４は、鉄筋３に沿って形成されている。これにより、撥水層２ａは、鉄筋３を含む範囲に形成可能であり、鉄筋３に水分または塩化物イオンが接触することを効果的に防止でき、鉄筋の劣化を効果的に抑止することができる。   Furthermore, the hollow path 4 of the concrete structure 1 according to the present embodiment is formed along the reinforcing bar 3. Thereby, the water-repellent layer 2a can be formed in a range including the reinforcing bar 3, can effectively prevent moisture or chloride ions from coming into contact with the reinforcing bar 3, and effectively suppress the deterioration of the reinforcing bar. it can.

また、本実施形態に係るコンクリート構造物１の中空路４は、鉄筋３よりも外壁面１ｃに近い位置に形成されている。したがって、撥水層２ａは、鉄筋３から外壁面１ｃの近傍にかけて形成されることとなる。これにより、撥水層２ａは、外壁面１ｃから浸透する水分及び塩化物イオンが鉄筋３に到達することを、より確実に阻止することができる。   Moreover, the hollow path 4 of the concrete structure 1 according to the present embodiment is formed at a position closer to the outer wall surface 1 c than to the reinforcing bar 3. Therefore, the water repellent layer 2a is formed from the reinforcing bar 3 to the vicinity of the outer wall surface 1c. Thereby, the water-repellent layer 2a can more reliably prevent moisture and chloride ions penetrating from the outer wall surface 1c from reaching the rebar 3.

このような本実施形態に係る施工方法では、中空路４にシラン系撥水剤を注入しているため、外壁面１ｃにシラン系撥水剤を塗布する従来工法と比較して、表面の凹凸や表面の付着物を除去する必要がなく、施工が容易である。また、本実施形態に係る施工方法は、温度変化によるシラン系撥水剤の粘度の低下の影響を受けず、実施可能である。さらに、本実施形態に係る施工方法は、外壁面が濡れている場合等にも実施することができる。したがって、本実施形態に係るコンクリート構造物１の施工は、天候の変化に左右されずに実施可能である。   In such a construction method according to this embodiment, since a silane-based water repellent is injected into the hollow path 4, the surface irregularities are compared with the conventional method of applying a silane-based water repellent to the outer wall surface 1c. And it is not necessary to remove the deposits on the surface, and construction is easy. Moreover, the construction method according to the present embodiment can be carried out without being affected by the decrease in the viscosity of the silane water repellent due to temperature change. Furthermore, the construction method according to the present embodiment can also be implemented when the outer wall surface is wet. Therefore, the construction of the concrete structure 1 according to the present embodiment can be performed without being influenced by changes in the weather.

また、シラン系撥水剤は臭気があるため、外壁面１ｃに塗布する場合には近隣居住者に悪臭被害が発生する可能性がある。しかしながら、中空路４にシラン系撥水剤を注入する本実施形態に係る施工方法では、外気に触れるシラン系撥水剤の量が少ないため、空気中に揮発するシラン系撥水剤の成分の量が少なく、臭気が発生しづらい。   In addition, since the silane water repellent has an odor, when it is applied to the outer wall surface 1c, there is a possibility that bad odor damage may occur in neighboring residents. However, in the construction method according to this embodiment in which the silane-based water repellent is injected into the hollow path 4, the amount of the silane-based water repellent that comes into contact with the outside air is small. The amount is small and it is hard to generate odor.

また、本実施形態に係る施工方法は、コンクリート構造物１の外壁面１ｃに影響を与えないため、施工後にコンクリート構造物１の外壁面に塗料などを塗布することも容易である。   Moreover, since the construction method according to the present embodiment does not affect the outer wall surface 1c of the concrete structure 1, it is easy to apply paint or the like to the outer wall surface of the concrete structure 1 after construction.

なお、本発明は上記実施形態に限定されるものではなく、例えば以下のような変形例が考えられる。
（１）上記実施形態においては、中空路４は、１本のみを図示しているが、本発明はこれに限定されない。中空路４は複数形成されるものとしてもよい。また、中空路４同士が接続されるものとしてもよい。中空路４を複数形成することにより、コンクリート基部２に対してより広範囲に撥水層２ａを形成することが可能である。 In addition, this invention is not limited to the said embodiment, For example, the following modifications can be considered.
(1) In the above embodiment, only one hollow path 4 is illustrated, but the present invention is not limited to this. A plurality of hollow paths 4 may be formed. Further, the hollow paths 4 may be connected to each other. By forming a plurality of hollow passages 4, it is possible to form the water repellent layer 2 a in a wider range with respect to the concrete base 2.

（２）また、コンクリート構造物１の内部に亀裂等が発生した場合には、中空路４の周囲に撥水層２ａが形成されていても、中空路４から補修剤や再アルカリ化剤を注入することが可能である。中空路４から補修剤や再アルカリ化剤を注入することにより、コンクリート構造物１内部の亀裂を補修することができる。
さらに、シラン系撥水剤に対して、鉄筋３の防錆剤や、コンクリート基部２の中性化抑止剤等を混合して撥水層２ａを形成することも可能である。この場合、鉄筋３の防錆や、鉄筋３の周囲におけるコンクリート強度低下防止を撥水と同時に行うことができる。 (2) Further, when a crack or the like occurs in the concrete structure 1, a repair agent or a realkalizing agent is removed from the hollow path 4 even if the water repellent layer 2 a is formed around the hollow path 4. It is possible to inject. By injecting a repairing agent or a realkalizing agent from the hollow passage 4, it is possible to repair a crack in the concrete structure 1.
Furthermore, it is possible to form the water repellent layer 2a by mixing a rust-based water repellent with a rust preventive agent for the reinforcing bars 3, a neutralization inhibitor for the concrete base 2, and the like. In this case, rust prevention of the reinforcing bar 3 and prevention of concrete strength reduction around the reinforcing bar 3 can be performed simultaneously with water repellency.

（３）また、上記実施形態においては、中空路４は、鉄筋３と外壁面１ｃとの間に形成されるものとしたが、本発明はこれに限定されない。
図５は、上記実施形態に係るコンクリート構造物１の変形例である。図５（ａ）に示すように、中空路４は、外壁面１ｃから見て鉄筋３よりも内側に形成されるものとしてもよい。例えば、鉄筋３におけるかぶり厚さが少ない場合等に、中空路４を外壁面１ｃから見て鉄筋３よりも内側に形成することにより、コンクリート構造物１の強度を確保することができる。 (3) Moreover, in the said embodiment, although the hollow path 4 shall be formed between the reinforcing bar 3 and the outer wall surface 1c, this invention is not limited to this.
FIG. 5 is a modification of the concrete structure 1 according to the embodiment. As shown in FIG. 5A, the hollow path 4 may be formed inside the reinforcing bar 3 when viewed from the outer wall surface 1c. For example, when the cover thickness in the reinforcing bar 3 is small, the strength of the concrete structure 1 can be ensured by forming the hollow path 4 inside the reinforcing bar 3 when viewed from the outer wall surface 1c.

（４）さらに、上記実施形態においては、撥水層２ａは、鉄筋３を含む範囲に形成されていることとしたが、本発明はこれに限定されない。撥水層２ａは、図５（ｂ）に示すように、鉄筋３を含まない範囲に形成されているものとしてもよい。なお、このような場合には、鉄筋３と、外壁面１ｃとの間に撥水層２ａを形成することが好ましい。 (4) Furthermore, in the said embodiment, although the water repellent layer 2a was formed in the range containing the reinforcing bar 3, this invention is not limited to this. The water repellent layer 2a may be formed in a range not including the reinforcing bars 3, as shown in FIG. In such a case, it is preferable to form a water repellent layer 2a between the reinforcing bar 3 and the outer wall surface 1c.

（５）また、中空路４が複数形成されている場合、隣接する撥水層２ａ同士が、図５（ｃ）に示すように、互いに重複するように形成されているものとしてもよい。この場合、隣接する撥水層２ａ同士の間に隙間ができず、より確実に鉄筋３の周囲を撥水することができる。 (5) When a plurality of hollow paths 4 are formed, adjacent water repellent layers 2a may be formed so as to overlap each other as shown in FIG. 5 (c). In this case, there is no gap between the adjacent water repellent layers 2a, and the periphery of the reinforcing bar 3 can be repelled more reliably.

（６）さらに、撥水層２ａは、図５（ｃ）に示すように、外壁面１ｃに到達するように形成されているものとしてもよい。この場合、撥水層２ａが外壁面１ｃを保護することができ、コンクリート構造物１の美観を保持することができる。 (6) Further, the water repellent layer 2a may be formed so as to reach the outer wall surface 1c as shown in FIG. 5 (c). In this case, the water repellent layer 2a can protect the outer wall surface 1c, and the aesthetic appearance of the concrete structure 1 can be maintained.

１……コンクリート構造物
１ｃ……外壁面
２……コンクリート基部
２ａ……撥水層
３……鉄筋
４……中空路
４ａ……第１中空路開口 DESCRIPTION OF SYMBOLS 1 ... Concrete structure 1c ...... Outer wall surface 2 ... Concrete base 2a ... Water-repellent layer 3 ... Reinforcement 4 ... Hollow path 4a ... 1st hollow path opening

Claims (4)

鉄筋が内部に配設されたコンクリートに、外壁面に開口部を有する中空路を形成する中空路形成工程と、
前記中空路に撥水性含浸材を注入すると共に加圧状態で一定時間前記撥水性含浸材を保持することにより前記中空路の周囲に撥水層を形成する撥水層形成工程と
を有することを特徴とするコンクリート構造物の施工方法。 A hollow path forming step for forming a hollow path having an opening on the outer wall surface in the concrete in which the reinforcing bars are disposed,
And a water repellent layer forming step of forming a water repellent layer around the hollow path by injecting the water repellent impregnant into the hollow path and holding the water repellent impregnant for a predetermined time in a pressurized state. The construction method of the concrete structure which is characterized. 前記中空路は、前記鉄筋に沿って形成されることを特徴とする請求項１記載の施工方法。   The construction method according to claim 1, wherein the hollow path is formed along the reinforcing bar. 前記中空路は、前記鉄筋よりも外壁面側に形成されることを特徴とする請求項２記載の施工方法。   The construction method according to claim 2, wherein the hollow path is formed closer to the outer wall surface than the reinforcing bar. 鉄筋が内部に配設されたコンクリート構造物であって、
外壁面に開口部を有する中空路と、
前記中空路の周囲に形成された撥水層と
を有することを特徴とするコンクリート構造物。 It is a concrete structure with reinforcing bars arranged inside,
A hollow path having an opening on the outer wall;
And a water repellent layer formed around the hollow path.
JP2016102400A 2016-05-23 2016-05-23 Construction method for concrete structure, and concrete structure Pending JP2017210724A (en)