JP2017176394A - Absorbent article - Google Patents
Absorbent article Download PDFInfo
- Publication number
- JP2017176394A JP2017176394A JP2016067074A JP2016067074A JP2017176394A JP 2017176394 A JP2017176394 A JP 2017176394A JP 2016067074 A JP2016067074 A JP 2016067074A JP 2016067074 A JP2016067074 A JP 2016067074A JP 2017176394 A JP2017176394 A JP 2017176394A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- liquid
- fiber
- absorbent article
- lipophilic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、吸収性物品に関する。 The present invention relates to an absorbent article.
使い捨ておむつ、生理用ナプキン、失禁パッドなどの吸収性物品は、通常、使用者の肌に直接触れ得る状態で使用される。また、使用者の肌に触れ得る部分には、肌触りを良くするために透液性不織布が配置されている。一般的に、このような透液性不織布は、尿などの水分の透過性を高めるために親水性である。そのため、親水性の透液性不織布は、水分の透過性には優れるものの、軟便、母乳などのように水分、油分を含む***物に対しては、目詰まりを発生することが多かった。 Absorbent articles such as disposable diapers, sanitary napkins, and incontinence pads are usually used in a state where they can directly touch the user's skin. Moreover, the liquid-permeable nonwoven fabric is arrange | positioned in the part which can touch a user's skin in order to improve the touch. Generally, such a liquid-permeable nonwoven fabric is hydrophilic in order to increase the permeability of moisture such as urine. Therefore, although the hydrophilic liquid-permeable nonwoven fabric is excellent in moisture permeability, it often clogs excrement containing moisture and oil such as soft stool and breast milk.
そこで、このような軟便を吸収、保持する性能を高めた吸収性物品が提案されている。例えば、特許文献１には、少なくとも、表面側に配置されるトップシートと、裏面側に配置されるバックシートと、前記シート間に介在された吸収体とを具備することにより物品本体が構成され、該物品本体の臀部当接部に***物を収納保持する便ポケットを設けて成る使い捨ての吸収性物品において、前記便ポケットの開口部をメッシュシートにより被覆して成る吸収性物品が記載されている（特許文献１（請求項１）参照）。
Then, the absorbent article which improved the performance which absorbs and hold | maintains such a soft stool is proposed. For example,
また、特許文献２には、おむつとその使用者の股との間に配置されるシートであり、少なくとも前記シートの周縁を除く領域に、厚み方向を切断した複数の切断部を有し、互いに隣接する前記切断部どうしの間に、前記股からの***物が付着することで前記おむつ側に落ち込むように変位する変位部が形成され、前記変位部は間隔をあけて複数配置されているおむつ用補助シートが記載されている（特許文献２（請求項１）参照）。
Further,
従来、水分、油分を含む***物を吸収する性能を高める方法として、トップシートに孔を開ける方法、***物を一時的に閉じ込めておく空間を設ける方法などがとられている。しかしながら、根本的な解決には至っておらず、使用時に横漏れを発生する問題があった。本発明は、上記事情に鑑みてなされたものであり、トップシートに物理的な加工を施すことなく、軟便、母乳などの水分および油分を含有する***物を効率よく吸収できる吸収性物品を提供することを目的とする。 Conventionally, as a method of improving the performance of absorbing excrement including moisture and oil, a method of opening a hole in the top sheet, a method of providing a space for temporarily confining excrement, and the like have been taken. However, the fundamental solution has not been reached, and there has been a problem of causing side leakage during use. The present invention has been made in view of the above circumstances, and provides an absorbent article that can efficiently absorb excreta containing moisture and oil such as soft stool and breast milk without subjecting the top sheet to physical processing. The purpose is to do.
本発明の吸収性物品は、透液性不織布と、不透液性シートと、これらの間に配置された吸収体とを有し、前記透液性不織布を構成する繊維が、親油化セルロース系繊維を含有することを特徴とする。親油化セルロース系繊維は、セルロース骨格を有するため親水性が高く、かつ、親油化されているため油分に対する親和性も高い。よって、この親油化セルロース系繊維を含有する透液性不織布をトップシートに使用することで、軟便、母乳などの水分および油分を含有する***物を効率よく吸収できる吸収性物品が得られる。 The absorbent article of the present invention has a liquid-permeable nonwoven fabric, a liquid-impervious sheet, and an absorbent body disposed therebetween, and the fibers constituting the liquid-permeable nonwoven fabric are lipophilic cellulose. It contains a system fiber. Since the lipophilic cellulosic fiber has a cellulose skeleton, it has high hydrophilicity, and since it is oleophilic, it has a high affinity for oil. Therefore, by using the liquid-permeable nonwoven fabric containing the lipophilic cellulosic fiber for the top sheet, an absorbent article that can efficiently absorb excreta containing moisture and oil such as soft stool and breast milk can be obtained.
前記透液性不織布を構成する繊維は、前記親油化セルロース系繊維と合成樹脂繊維とを含有し、前記透液性不織布を構成する繊維中の前記親油化セルロール系繊維の含有率が、５質量％〜４０質量％であることが好ましい。前記親油化セルロール系繊維は、油剤により表面処理されたセルロース系繊維が好適である。前記透液性不織布は、エアスルー不織布であり、その目付けが１５ｇ／ｍ２〜４０ｇ／ｍ２であることが好ましい。 The fiber constituting the liquid-permeable nonwoven fabric contains the lipophilic cellulose fiber and the synthetic resin fiber, and the content of the lipophilic cellulose fiber in the fiber constituting the liquid-permeable nonwoven fabric is as follows: It is preferable that it is 5 mass%-40 mass%. The oleophilic cellulose fiber is preferably a cellulosic fiber surface-treated with an oil agent. The liquid-pervious nonwoven fabric is an air-through nonwoven fabric preferably has a basis weight is 15g / m 2 ~40g / m 2 .
本発明によれば、軟便、母乳などの水分および油分を含有する***物を効率よく吸収できる吸収性物品が得られる。 ADVANTAGE OF THE INVENTION According to this invention, the absorbent article which can absorb efficiently the excretion containing water | moisture contents and oil components, such as loose stool and breast milk, is obtained.
本発明の吸収性物品は、透液性不織布と、不透液性シートと、これらの間に配置された吸収体とを有する。 The absorbent article of this invention has a liquid-permeable nonwoven fabric, a liquid-impervious sheet, and the absorber arrange | positioned among these.
［透液性不織布］
前記透液性不織布とは、液体を透過し得る不織布である。前記透液性不織布は、不織布を構成する繊維として、親油化セルロース系繊維を含有することを特徴とする。親油化セルロース系繊維を含有する透液性不織布は、水分および油分のいずれに対しても親和性が高く、これらの水分および油分を容易に透過できる。よって、親油化セルロース系繊維を含有する透液性不織布を使用することで、軟便、母乳などの水分および油分を含有する***物を効率よく吸収できる吸収性物品が得られる。
[Liquid permeable nonwoven fabric]
The said liquid-permeable nonwoven fabric is a nonwoven fabric which can permeate | transmit a liquid. The liquid-permeable nonwoven fabric includes lipophilic cellulosic fibers as fibers constituting the nonwoven fabric. The liquid-permeable nonwoven fabric containing lipophilic cellulosic fibers has high affinity for both moisture and oil, and can easily permeate these moisture and oil. Therefore, by using a liquid-permeable nonwoven fabric containing lipophilic cellulosic fibers, an absorbent article that can efficiently absorb excreta containing moisture and oil such as soft stool and breast milk can be obtained.
（親油化セルロース系繊維）
前記親油化セルロース系繊維とは、セルロース骨格を有し、繊維表面が親油化（疎水化）処理された繊維である。前記親油化セルロース系繊維は、セルロース骨格を有するため親水性に優れている。また、親油化セルロース系繊維は、親油化されているため油分に対する親和性も高められている。
(Lipophilic cellulose fiber)
The lipophilic cellulosic fiber is a fiber having a cellulose skeleton and having a fiber surface subjected to lipophilicity (hydrophobization). Since the lipophilic cellulosic fiber has a cellulose skeleton, it is excellent in hydrophilicity. Moreover, since the lipophilic cellulosic fiber is oleophilic, the affinity for oil is also increased.
前記親油化セルロース系繊維は、水に対する接触角が８１°以上が好ましく、より好ましくは９０°以上であり、１２５°以下が好ましく、より好ましくは１２１°以下である。親油化セルロース系繊維の水に対する接触角が、８１°以上であれば体液中の水分を吸収することによってセルロース繊維が膨潤することが抑制され、繊維間の空隙が維持され、体液の透過速度が向上し、１２５°以下であれば液の透過速度が良好となる。なお、親油化処理がされていないセルロース系繊維の水に対する接触角は、１０°以下である。 The lipophilic cellulosic fiber preferably has a contact angle with water of 81 ° or more, more preferably 90 ° or more, preferably 125 ° or less, and more preferably 121 ° or less. If the contact angle of the lipophilic cellulosic fiber with respect to water is 81 ° or more, the cellulose fibers are prevented from swelling by absorbing moisture in the body fluid, the gap between the fibers is maintained, and the permeation rate of the body fluid If it is 125 ° or less, the liquid permeation rate is good. In addition, the contact angle with respect to the water of the cellulosic fiber which has not been made lipophilic is 10 ° or less.
前記親油化セルロール系繊維としては、親油性が高められたセルロース系繊維であれば特に限定されないが、例えば、親油化剤で表面処理されたセルロース系繊維が挙げられる。親油化剤により表面処理することで、セルロース系繊維の親油性（疎水度）を容易に調整することができる。 The lipophilic cellulose fiber is not particularly limited as long as it is a cellulosic fiber having improved lipophilicity, and examples thereof include a cellulosic fiber surface-treated with a lipophilic agent. By performing the surface treatment with the oleophilic agent, the lipophilicity (hydrophobicity) of the cellulosic fiber can be easily adjusted.
前記セルロース系繊維としては、天然セルロース繊維、再生セルロース繊維、半合成セルロース繊維が挙げられる。天然セルロース繊維としては、綿、麻、木材パルプなどが挙げられる。再生セルロース繊維としては、レーヨン、ポリノジック、キュプラ、リヨセルが挙げられる。半合成セルロース繊維としては、ジアセテート繊維、トリアセテート繊維が挙げられる。これらの中でも、再生セルロース繊維が好ましく、レーヨンがより好ましい。 Examples of the cellulose fibers include natural cellulose fibers, regenerated cellulose fibers, and semi-synthetic cellulose fibers. Examples of natural cellulose fibers include cotton, hemp and wood pulp. Examples of the regenerated cellulose fiber include rayon, polynosic, cupra, and lyocell. Examples of the semisynthetic cellulose fiber include diacetate fiber and triacetate fiber. Among these, regenerated cellulose fibers are preferable, and rayon is more preferable.
前記親油化剤としては、セルロース系繊維の親油性を高めることができる化合物であれば特に限定されない。前記親油化剤としては、セルロース系繊維の水酸基に結合し、疎水性基（親油性基）を導入し得る化合物；親油性を有し、セルロース系繊維の表面を被覆し得る化合物；が挙げられる。つまり、親油化セルロース系繊維としては、水酸基と親油化剤とが結合し、疎水性基が導入されたセルロース系繊維；表面が親油化剤で被覆されたセルロース系繊維が挙げられる。 The oleophilic agent is not particularly limited as long as it is a compound that can enhance the lipophilicity of the cellulosic fiber. Examples of the oleophilic agent include compounds capable of binding to hydroxyl groups of cellulosic fibers and introducing hydrophobic groups (lipophilic groups); compounds having lipophilicity and capable of covering the surface of cellulosic fibers. It is done. That is, examples of the lipophilic cellulosic fiber include a cellulosic fiber in which a hydroxyl group and a lipophilic agent are bonded and a hydrophobic group is introduced; and a cellulosic fiber having a surface coated with a lipophilic agent.
前記疎水性基としては、炭素数４〜２６個のアルキル基、炭素数６〜２０個のアリール基、炭素数７〜２６個のアラルキル基；などが挙げられる。前記疎水性基を導入し得る化合物としては、分子中に、水酸基と反応し得る官能基と、前記疎水性基とを有する化合物が挙げられる。このような化合物として、例えば、疎水性基を有するカルボン酸、疎水性基を有するアミンなどが挙げられる。 Examples of the hydrophobic group include an alkyl group having 4 to 26 carbon atoms, an aryl group having 6 to 20 carbon atoms, and an aralkyl group having 7 to 26 carbon atoms. Examples of the compound capable of introducing the hydrophobic group include compounds having a functional group capable of reacting with a hydroxyl group and the hydrophobic group in the molecule. Examples of such a compound include a carboxylic acid having a hydrophobic group and an amine having a hydrophobic group.
前記セルロース系繊維の表面を被覆し得る化合物としては、脂肪酸塩、脂肪酸エステル、脂肪酸アミド、シリコン系油剤、フッ素系油剤などが挙げられる。前記脂肪酸塩としては、炭素数８〜３５の脂肪酸の塩が挙げられ、ラウリン酸バリウム、ラウリン酸亜鉛、ステアリン酸カルシウム、ステアリン酸亜鉛、ステアリン酸マグネシウムなどが挙げられる。前記脂肪酸エステルとしては、炭素数８〜３５個の脂肪酸とアルコールとのエステルが挙げられ、グリセリン脂肪酸エステル、ペンタエリスリトール脂肪酸エステル、ジグリセリン脂肪酸エステル、ポリグリセリン脂肪酸エステルなどが挙げられる。前記脂肪酸アミドとしては、炭素数８〜３５の脂肪酸とアミンとのアミドが挙げられ、ステアリン酸アミド、エルカ酸アミド、メチレンビスステアリン酸アミド、エチレンビスステアリン酸アミド、エチレンビスヒドロキシステアリン酸アミドなどが挙げられる。前記シリコン系油剤としては、シリコーンオイルが挙げられ、ポリジメチルシロキサン、ポリメチルフェニルシロキサンなどが挙げられる。 Examples of the compound capable of coating the surface of the cellulosic fiber include fatty acid salts, fatty acid esters, fatty acid amides, silicone oils, and fluorine oils. Examples of the fatty acid salts include salts of fatty acids having 8 to 35 carbon atoms, such as barium laurate, zinc laurate, calcium stearate, zinc stearate, and magnesium stearate. Examples of the fatty acid esters include esters of fatty acids having 8 to 35 carbon atoms and alcohols, such as glycerin fatty acid esters, pentaerythritol fatty acid esters, diglycerin fatty acid esters, and polyglycerin fatty acid esters. Examples of the fatty acid amide include amides of fatty acids having 8 to 35 carbon atoms and amines, such as stearic acid amide, erucic acid amide, methylene bis stearic acid amide, ethylene bis stearic acid amide, and ethylene bishydroxy stearic acid amide. Can be mentioned. Examples of the silicone oil include silicone oil, such as polydimethylsiloxane and polymethylphenylsiloxane.
セルロース系繊維を親油化剤で処理する方法としては、セルロース系繊維を、親油化剤を含有する溶液に浸漬した後、乾燥させる方法；シート化したセルロース系繊維に親油化剤または親油化剤を含有する溶液をスプレーする方法；シート化したセルロース系繊維に親油化剤をロールで転写する方法；などが挙げられる。 Cellulosic fibers can be treated with a lipophilic agent by immersing the cellulosic fiber in a solution containing the lipophilic agent and then drying; Examples include a method of spraying a solution containing an oiling agent; a method of transferring a lipophilic agent to a sheet-like cellulosic fiber by a roll; and the like.
前記セルロース系繊維の表面を被覆し得る化合物を用いる場合、この化合物の使用量は、所望とするセルロース系繊維の親油性に応じて適宜調節すればよい。なお、前記化合物の付与量は、セルロース系繊維１００質量部に対して、０．０５質量部以上、１５質量部以下が好ましい。 When using a compound capable of coating the surface of the cellulosic fiber, the amount of the compound used may be appropriately adjusted according to the desired lipophilicity of the cellulosic fiber. In addition, as for the provision amount of the said compound, 0.05 mass part or more and 15 mass parts or less are preferable with respect to 100 mass parts of cellulose fibers.
前記親油化セルロース系繊維の繊度は、１．０ｄｔｅｘ以上が好ましく、より好ましくは１．２ｄｔｅｘ以上、さらに好ましくは２．０ｄｔｅｘ以上であり、２０ｄｔｅｘ以下が好ましく、より好ましくは１８ｄｔｅｘ以下、さらに好ましくは１５ｄｔｅｘ以下である。繊度が１．０ｄｔｅｘ以上であれば、不織布の機械的強度が高くなり、使用時の破れの発生が抑制され、２０ｄｔｅｘ以下であれば、不織布の風合いが良好となる。 The fineness of the lipophilic cellulosic fiber is preferably 1.0 dtex or more, more preferably 1.2 dtex or more, still more preferably 2.0 dtex or more, preferably 20 dtex or less, more preferably 18 dtex or less, still more preferably. 15 dtex or less. If the fineness is 1.0 dtex or more, the mechanical strength of the nonwoven fabric is increased and the occurrence of tearing during use is suppressed, and if it is 20 dtex or less, the texture of the nonwoven fabric is improved.
前記親油化セルロース系繊維の平均繊維長は、２ｍｍ以上が好ましく、より好ましくは４ｍｍ以上、さらに好ましくは１０ｍｍ以上であり、２００ｍｍ以下が好ましく、より好ましくは１８０ｍｍ以下、さらに好ましくは１５０ｍｍ以下である。平均繊維長が、２ｍｍ以上であれば目詰まりによる液の透過速度の低下が抑制され、２００ｍｍ以下であれば液の透過速度と固形分の濾過性能の両立が可能となる。平均繊維長は、ＪＩＳ Ｌ １０１５（２０１０）のステープルダイヤグラム法（Ａ法）によって測定する。 The average fiber length of the lipophilic cellulosic fiber is preferably 2 mm or more, more preferably 4 mm or more, further preferably 10 mm or more, preferably 200 mm or less, more preferably 180 mm or less, and further preferably 150 mm or less. . If the average fiber length is 2 mm or more, a decrease in the permeation rate of the liquid due to clogging is suppressed, and if it is 200 mm or less, both the permeation rate of the liquid and the filtration performance of the solid content can be achieved. The average fiber length is measured by the staple diagram method (Method A) of JIS L 1015 (2010).
（合成樹脂繊維）
前記透液性不織布を構成する繊維は、前記親油化セルロース系繊維に加えて、合成樹脂繊維を含有することが好ましい。合成樹脂繊維を含有させることで、不織布の物性を容易に制御できる。
(Synthetic resin fiber)
The fibers constituting the liquid-permeable nonwoven fabric preferably contain synthetic resin fibers in addition to the lipophilic cellulosic fibers. By including the synthetic resin fiber, the physical properties of the nonwoven fabric can be easily controlled.
合成樹脂繊維としては、特に限定されないが、ポリエチレン繊維、ポリプロピレン繊維などのポリオレフィン繊維；ポリエチレンテレフタレート繊維、ポリトリメチレンテレフタレート繊維、ポリブチレンテレフタレート繊維などのポリエステル繊維；ポリアミド６繊維、ポリアミド６６繊維などのポリアミド繊維；ポリアクリロニトリル繊維などのアクリル繊維；ポリビニルアルコール繊維；ポリウレタン繊維；ポリ塩化ビニル繊維；などが挙げられる。前記合成樹脂繊維としては、熱融着性を有するものが好ましい。熱融着性を有する合成樹脂繊維を含有することで、熱的な接着法により繊維同士を融着させることができる。
Although it does not specifically limit as synthetic resin fiber, Polyolefin fiber, such as polyethylene fiber and polypropylene fiber; Polyester fiber, such as polyethylene terephthalate fiber, polytrimethylene terephthalate fiber, polybutylene terephthalate fiber; Polyamide, such as
前記合成樹脂繊維は、単層構造でもよいし、２層以上の多層構造を有していてもよい。多層構造を有する繊維としては、第１成分からなる芯部および第２成分からなる鞘部から構成される芯鞘型繊維であることが好ましい。第１成分と第２成分との組合せとしては、ポリエチレン／ポリエチレンテレフタレート、ポリアミド／ポリウレタン、ポリエチレン／ポリプロピレンなどが挙げられる。 The synthetic resin fiber may have a single-layer structure or a multilayer structure of two or more layers. The fiber having a multilayer structure is preferably a core-sheath fiber composed of a core portion made of the first component and a sheath portion made of the second component. Examples of the combination of the first component and the second component include polyethylene / polyethylene terephthalate, polyamide / polyurethane, and polyethylene / polypropylene.
前記合成樹脂繊維が疎水性繊維である場合、親水化処理が施されていてもよい。合成樹脂繊維を親水化することで、透液性不織布全体の親水度（疎水度）をより高度に制御できる。 When the synthetic resin fiber is a hydrophobic fiber, a hydrophilic treatment may be performed. By making the synthetic resin fibers hydrophilic, the hydrophilicity (hydrophobicity) of the entire liquid-permeable nonwoven fabric can be controlled to a higher degree.
前記合成樹脂繊維の繊度は、１．０ｄｔｅｘ以上が好ましく、より好ましくは１．２ｄｔｅｘ以上、さらに好ましくは１．５ｄｔｅｘ以上であり、２０ｄｔｅｘ以下が好ましく、より好ましくは１８ｄｔｅｘ以下、さらに好ましくは１５ｄｔｅｘ以下である。繊度が１．０ｄｔｅｘ以上であれば体液の濾過速度が高くなり、漏れの発生を抑制でき、２０ｄｔｅｘ以下であれば不織布の風合いが良好となる。 The fineness of the synthetic resin fiber is preferably 1.0 dtex or more, more preferably 1.2 dtex or more, further preferably 1.5 dtex or more, preferably 20 dtex or less, more preferably 18 dtex or less, and further preferably 15 dtex or less. is there. If the fineness is 1.0 dtex or more, the filtration rate of the body fluid is increased, and the occurrence of leakage can be suppressed.
前記合成樹脂繊維の平均繊維長は、２ｍｍ以上が好ましく、より好ましくは３ｍｍ以上、さらに好ましくは４ｍｍ以上であり、２００ｍｍ以下が好ましく、より好ましくは１８０ｍｍ以下、さらに好ましくは１５０ｍｍ以下である。合成樹脂繊維の平均繊維長が２ｍｍ以上であれば体液の濾過速度に優れた不織布の作製が可能となり、２００ｍｍ以下であれば不織布作製の作業効率が良好となる。 The average fiber length of the synthetic resin fiber is preferably 2 mm or more, more preferably 3 mm or more, further preferably 4 mm or more, preferably 200 mm or less, more preferably 180 mm or less, and further preferably 150 mm or less. If the average fiber length of the synthetic resin fiber is 2 mm or more, it is possible to produce a nonwoven fabric having an excellent body fluid filtration rate.
合成樹脂繊維を用いる場合、前記透液性不織布を構成する繊維中の前記親油化セルロール系繊維の含有率は、５質量％以上が好ましく、より好ましくは７質量％以上、さらに好ましくは１０質量％以上であり、４０質量％以下が好ましく、より好ましくは３５質量％以下、さらに好ましくは３０質量％以下である。前記親油化セルロール系繊維の含有率が５質量％以上であれば透液性不織布の親油性（疎水性）が高く、油分の透過性が向上し、４０質量％以下であれば透液性不織布の親水性が高く、水分の透過性が向上する。 When using synthetic resin fibers, the content of the lipophilic cellulose fiber in the fibers constituting the liquid-permeable nonwoven fabric is preferably 5% by mass or more, more preferably 7% by mass or more, and still more preferably 10% by mass. % Or more, preferably 40% by mass or less, more preferably 35% by mass or less, and still more preferably 30% by mass or less. When the content of the lipophilic cellulose fiber is 5% by mass or more, the liquid-permeable nonwoven fabric has high lipophilicity (hydrophobicity), and the oil permeability is improved. When the content is 40% by mass or less, the liquid permeability is obtained. The nonwoven fabric has high hydrophilicity and improves moisture permeability.
（不織布）
前記透液性不織布の種類としては、ポイントボンド不織布、エアスルー不織布、スパンレース不織布、スパンボンド不織布、エアレイド不織布などが挙げられ、これらの中でもエアスルー不織布が好ましい。エアスルー不織布は、繊維間の隙間が多く、固形分の透過性に優れる。
(Nonwoven fabric)
Examples of the liquid-permeable nonwoven fabric include point bond nonwoven fabric, air-through nonwoven fabric, spunlace nonwoven fabric, spunbond nonwoven fabric, and airlaid nonwoven fabric. Among these, air-through nonwoven fabric is preferable. The air-through nonwoven fabric has many interstices between fibers and is excellent in solid content permeability.
前記透液性不織布の目付けは、１５ｇ／ｍ２以上が好ましく、より好ましくは１８ｇ／ｍ２以上、さらに好ましくは２０ｇ／ｍ２以上であり、４０ｇ／ｍ２以下が好ましく、より好ましくは３５ｇ／ｍ２以下、さらに好ましくは３０ｇ／ｍ２以下である。目付けが１５ｇ／ｍ２以上であれば不織布の引張強さが高くなり、使用時に破れることが抑制され、４０ｇ／ｍ２以下であれば固形分の透過性が良好となる。 The basis weight of the liquid-permeable nonwoven fabric is preferably 15 g / m 2 or more, more preferably 18 g / m 2 or more, still more preferably 20 g / m 2 or more, and preferably 40 g / m 2 or less, more preferably 35 g / m 2. m 2 or less, more preferably 30 g / m 2 or less. If the basis weight is 15 g / m 2 or more, the tensile strength of the nonwoven fabric becomes high and is prevented from being broken at the time of use, and if it is 40 g / m 2 or less, the solids permeability is good.
前記透液性不織布は、不織布全体にわたって親油化セルロース系繊維を含有してもよいし、特定の部分にのみ親油化セルロース系繊維を含有させてもよい。不織布の特定の部分に親油化セルロース系繊維を含有させる場合、少なくとも透液性不織布の吸収性物品の幅方向略中央部に相当する部分に親油化セルロース系繊維を配置することが好ましい。具体的には、吸収性物品の幅方向において、透液性不織布の一方端から他方端までの距離を１００％としたとき、一方端からの距離が２０％〜８０％（より好ましくは３０％〜７０％、さらに好ましくは４０％〜６０％）の範囲に親油化セルロース系繊維を配置する。なお、一方端からの距離が５０％の地点が幅方向中央部である。 The liquid-permeable nonwoven fabric may contain lipophilic cellulosic fibers throughout the nonwoven fabric, or may contain lipophilic cellulosic fibers only in specific portions. When the lipophilic cellulosic fiber is contained in a specific portion of the nonwoven fabric, it is preferable to dispose the lipophilic cellulosic fiber at least in a portion corresponding to the substantially central portion in the width direction of the absorbent article of the liquid-permeable nonwoven fabric. Specifically, in the width direction of the absorbent article, when the distance from one end to the other end of the liquid-permeable nonwoven fabric is 100%, the distance from one end is 20% to 80% (more preferably 30%). ˜70%, more preferably 40% to 60%). In addition, the point where the distance from one end is 50% is the central portion in the width direction.
前記親油化セルロース系繊維と親水性処理を施した合成繊維樹脂を含有する不織布は、水に対する接触角が３９°以上が好ましく、より好ましくは４２°以上であり、９７°以下が好ましく、より好ましくは９０°以下である。不織布の水に対する接触角が３９°以上であれば、油分を含んだ液の透過性がより良好となり、９７°以下であれば、尿など油分を含まない液の透過性がより良好となる。 The non-woven fabric containing the lipophilic cellulosic fiber and the synthetic fiber resin subjected to the hydrophilic treatment preferably has a contact angle with water of 39 ° or more, more preferably 42 ° or more, and preferably 97 ° or less, more Preferably it is 90 degrees or less. If the contact angle of the nonwoven fabric with respect to water is 39 ° or more, the permeability of the liquid containing oil becomes better, and if it is 97 ° or less, the permeability of the liquid containing no oil such as urine becomes better.
前記透液性不織布は必要に応じて、切れ目や貫通孔を形成してもよいが、切れ目や貫通孔を有さないことが好ましい。なお、本発明で使用する透液性不織布は、親油化セルロース系繊維を含有することで、微細な固形分に対する透過性も向上している。そのため、透液性不織布に貫通孔を設けなくとも、吸収性物品の軟便などに対する吸収性に優れる。 Although the said liquid-permeable nonwoven fabric may form a cut and a through-hole as needed, it is preferable not to have a cut and a through-hole. In addition, the liquid-permeable nonwoven fabric used by this invention is improving the permeability | transmittance with respect to fine solid content by containing lipophilic cellulose type fiber. Therefore, it is excellent in the absorptivity with respect to the soft stool etc. of an absorbent article, without providing a through-hole in a liquid-permeable nonwoven fabric.
［吸収体］
前記吸収体は、体液を吸収し得る。前記吸収体は、少なくとも一層の吸収層から構成される。吸収層は、吸水性材料として、吸水性樹脂粉末を含有するものが好ましい。前記吸収層は、吸水性材料として、さらに、吸水性繊維を含有してもよい。前記吸水性樹脂粉末としては、従来吸収性物品に使用されているものが使用できる。前記吸水性樹脂粉末には、防腐剤、防かび剤、抗菌剤、酸化防止剤、紫外線吸収剤、着色剤、芳香剤、消臭剤、無機質粉末及び有機質繊維状物などの添加剤を含むことができる。前記吸水性繊維としては、例えば、パルプ繊維、セルロース繊維、レーヨン、アセテート繊維が挙げられる。前記吸収層は、吸水性樹脂粉末に加えて、繊維基材を含有してもよい。前記繊維基材としては、熱融着繊維などを挙げることができる。熱融着性繊維は、保形性を高めるために使用される。熱融着繊維の具体例としては、例えば、ポリエチレン、ポリプロピレン等のポリオレフィン系繊維、ポリエステル系繊維や複合繊維などが用いられる。吸水性材料として、吸水性樹脂粉末のみを含有する吸収層は、薄型化が可能である。繊維基材を含有する吸収層は、体液の分散性に優れる。
[Absorber]
The absorber can absorb body fluid. The absorber is composed of at least one absorption layer. The absorbent layer preferably contains a water absorbent resin powder as a water absorbent material. The absorbent layer may further contain water-absorbing fibers as a water-absorbing material. As the water absorbent resin powder, those conventionally used for absorbent articles can be used. The water-absorbent resin powder contains additives such as preservatives, fungicides, antibacterial agents, antioxidants, ultraviolet absorbers, colorants, fragrances, deodorants, inorganic powders and organic fibrous materials. Can do. Examples of the water absorbent fiber include pulp fiber, cellulose fiber, rayon, and acetate fiber. The absorbent layer may contain a fiber base material in addition to the water absorbent resin powder. Examples of the fiber base material include heat fusion fibers. The heat-fusible fiber is used for improving shape retention. Specific examples of the heat-sealing fiber include polyolefin fibers such as polyethylene and polypropylene, polyester fibers, and composite fibers. The absorbent layer containing only the water absorbent resin powder as the water absorbent material can be thinned. The absorption layer containing a fiber base material is excellent in dispersibility of body fluid.
前記吸収層は、例えば、粉砕したパルプ繊維やセルロース繊維等の親水性繊維集合層に粒状の吸水性樹脂粉末を混合したものを、ティッシュペーパーなどの紙シートまたは液透過性不織布シートに固定する、あるいはこれらの液透過性不織布シートで包み、長方形、砂時計型、ひょうたん型、羽子板型等の所定形状に成形することにより得られる。 The absorbent layer is, for example, fixed to a paper sheet such as tissue paper or a liquid-permeable non-woven sheet mixed with a hydrophilic fiber aggregate layer such as pulverized pulp fiber or cellulose fiber mixed with granular water-absorbing resin powder. Or it wraps with these liquid-permeable nonwoven fabric sheets, and it obtains by shape | molding in predetermined shapes, such as a rectangle, an hourglass type, a gourd type, a battledore type.
前記吸水層および吸収体の平面視形状は特に限定されず、例えば、長方形型、砂時計型、ひょうたん型、羽子板型などが挙げられる。また、吸収体は、前記吸水層の他に、吸水性樹脂粉末を固定するための接着剤層を有していてもよい。 The planar view shape of the water absorption layer and the absorber is not particularly limited, and examples thereof include a rectangular shape, an hourglass shape, a gourd shape, and a battledore shape. Moreover, the absorber may have an adhesive layer for fixing the water absorbent resin powder in addition to the water absorbing layer.
［不透液性シート］
不透液性シートは、吸収性物品の最も外面側に配置されるものであり、体液等が外部に漏れ出すことを防止する。不透液性シートとしては、例えば、疎水性繊維（例えば、ポリプロピレン、ポリエチレン、ポリエステル、ポリアミド、ナイロン）にて形成された撥水性または不透液性の不織布（例えば、スパンボンド不織布やメルトブロー不織布、ＳＭＳ（スパンボンド・メルトブロー・スパンボンド）不織布）や、撥水性または不透液性のプラスチックフィルムが利用され、不透液性シートに到達した体液が、吸収性物品の外側にしみ出すのを防止する。不透液性シートにプラスチックフィルムが利用される場合、ムレを防止して着用者の快適性を向上するという観点からは、透湿性（通気性）を有するプラスチックフィルムが利用されることが好ましい。また、さらなる拡散性付与、形状安定性のために、プラスチックフィルムと、吸収体との間に紙シートを配置してもよい。
[Impermeable sheet]
The liquid-impervious sheet is disposed on the outermost surface side of the absorbent article, and prevents body fluid and the like from leaking outside. As the liquid-impervious sheet, for example, a water-repellent or liquid-impervious nonwoven fabric (for example, a spunbond nonwoven fabric or a melt blown nonwoven fabric, formed of hydrophobic fibers (for example, polypropylene, polyethylene, polyester, polyamide, nylon), SMS (spunbond / meltblown / spunbond) non-woven fabric) and water-repellent or liquid-impervious plastic film are used to prevent body fluid reaching the liquid-impervious sheet from seeping out of the absorbent article. To do. When a plastic film is used for the liquid-impermeable sheet, it is preferable to use a plastic film having moisture permeability (breathability) from the viewpoint of preventing stuffiness and improving wearer's comfort. Moreover, you may arrange | position a paper sheet between a plastic film and an absorber for the further diffusibility provision and shape stability.
［吸収性物品］
次に、本発明の吸収体の具体的な適用例について説明する。本発明の吸収体を使用し得る吸収性物品としては、例えば、吸収パッド、使い捨ておむつ、生理用ナプキンなどの人体から排出される体液を吸収するために用いられる吸収性物品が挙げられる。
[Absorbent articles]
Next, a specific application example of the absorber of the present invention will be described. As an absorbent article which can use the absorber of this invention, the absorbent article used in order to absorb the bodily fluid discharged | emitted from a human body, such as an absorption pad, a disposable diaper, a sanitary napkin, is mentioned, for example.
前記吸収性物品が、吸収パッド、生理用ナプキンである場合、例えば、トップシート（透液性不織布）とバックシート（不透液性シート）との間に、吸収体が配置される。吸収パッド、生理用ナプキンの形状としては、略長方形、砂時計型、ひょうたん型などが挙げられる。また、必要に応じて、前記透液性のトップシートの幅方向両側に不透液性のサイドシートが設けられていてもよい。サイドシートは、トップシートの幅方向両側の上面に接合され、接合点より幅方向内方のサイドシートは、吸収体の両側縁に沿って一対の立ち上がりフラップを形成する。 When the said absorbent article is an absorption pad and a sanitary napkin, an absorber is arrange | positioned between a top sheet (liquid-permeable nonwoven fabric) and a back sheet (liquid-impermeable sheet), for example. Examples of the shape of the absorbent pad and sanitary napkin include a substantially rectangular shape, an hourglass shape, and a gourd shape. Further, if necessary, liquid-impervious side sheets may be provided on both sides in the width direction of the liquid-permeable top sheet. The side sheets are bonded to the upper surfaces on both sides in the width direction of the top sheet, and the side sheets inward in the width direction from the bonding points form a pair of rising flaps along both side edges of the absorber.
前記吸収性物品が使い捨ておむつである場合、使い捨ておむつとしては、例えば、後背部または前腹部の左右に一対の止着部材が設けられ、当該止着部材により着用時にパンツ型に形成する展開型使い捨ておむつ；前腹部と後背部とが接合されることによりウエスト開口部と一対の脚開口部とが形成されたパンツ型使い捨ておむつ；などが挙げられる。 When the absorbent article is a disposable diaper, as the disposable diaper, for example, a pair of fastening members are provided on the left and right of the back part or the front part of the abdomen, and the deployable disposable that is formed into a pants shape when worn by the fastening member Diapers; pants-type disposable diapers in which a waist opening and a pair of leg openings are formed by joining the front part and the back part;
吸収性物品が、使い捨ておむつである場合、使い捨ておむつは、例えば、内側シート（透液性不織布）と外側シート（不透液性シート）とからなる積層体が前腹部と後背部とこれらの間に位置する股部とからなるおむつ本体を形成し、前記股部に吸水体が配置されていてもよい。また、使い捨ておむつは、例えば、トップシート（透液性不織布）とバックシート（不透液性シート）との間に、吸収体が配置された積層体からなり、この積層体が前腹部と後背部とこれらの間に位置する股部とを有していてもよい。なお、前腹部、後背部、股部とは、使い捨ておむつを着用の際に、着用者の腹側に当てる部分を前腹部と称し、着用者の尻側に当てる部分を後背部と称し、前腹部と後背部との間に位置し着用者の股間に当てる部分を股部と称する。前記内側シートは、親水性または撥水性であることが好ましく、前記外側シートは、撥水性であることが好ましい。 When the absorbent article is a disposable diaper, the disposable diaper is, for example, a laminate composed of an inner sheet (liquid-permeable non-woven fabric) and an outer sheet (liquid-impermeable sheet) between the front and back parts. The diaper main body which consists of a crotch part located in this may be formed, and the water absorption body may be arrange | positioned at the said crotch part. Moreover, a disposable diaper consists of a laminated body by which the absorber was arrange | positioned between a top sheet (liquid-permeable nonwoven fabric) and a back sheet (liquid-impermeable sheet), for example, and this laminated body is a front part and a back part. You may have a back part and a crotch part located among these. The front part, the back part, and the crotch part are referred to as the front part of the abdomen when wearing the disposable diaper and the back part as the part of the front part of the abdomen. A portion that is located between the abdomen and the back portion and is placed between the wearer's crotch is referred to as a crotch portion. The inner sheet is preferably hydrophilic or water repellent, and the outer sheet is preferably water repellent.
吸収性物品には、吸収体の両側縁部に沿って、立ち上がりフラップが設けられていることが好ましい。立ち上がりフラップは、例えば、吸収体の上面の幅方向両側縁部に設けられてもよく、吸収体の幅方向両外側に設けられてもよい。立ち上がりフラップを設けることにより、体液の横漏れを防ぐことができる。立ち上がりフラップは、トップシートの幅方向両側に設けられたサイドシートの内方端が立ち上げられて、形成されてもよい。前記立ち上がりフラップおよびサイドシートは、撥水性であることが好ましい。 The absorbent article is preferably provided with rising flaps along both side edges of the absorbent body. For example, the rising flaps may be provided on both side edges in the width direction of the upper surface of the absorber, or may be provided on both outer sides in the width direction of the absorber. By providing the rising flap, it is possible to prevent side leakage of body fluid. The rising flaps may be formed by raising the inner ends of the side sheets provided on both sides of the top sheet in the width direction. The rising flap and the side sheet are preferably water-repellent.
次に、本発明の吸収性物品について、吸収パッドを例に挙げ、図１、２を参照して説明する。図１は、吸収パッドの平面図を表す。図２は、図１の吸収パッドのＶ−Ｖ断面図を表す。なお、図では、矢印Ｂを幅方向とし、矢印Ａを長手方向と定義付ける。また、矢印Ａ，Ｂにより形成される面上の方向を、平面方向と定義付ける。 Next, the absorbent article of the present invention will be described with reference to FIGS. FIG. 1 represents a plan view of an absorbent pad. FIG. 2 shows a VV cross-sectional view of the absorbent pad of FIG. In the figure, the arrow B is defined as the width direction, and the arrow A is defined as the longitudinal direction. The direction on the surface formed by the arrows A and B is defined as the plane direction.
吸収パッド１は、透液性不織布からなるトップシート２と、不透液性シートからなるバックシート３と、これらの間に配置された吸収体４とを有している。トップシート２は、着用者の股部の肌に面するように配置され、尿等の液体の***物を透過する。トップシート２を通過した尿等の***物は、吸収体４に取り込まれ吸収される。バックシート３は、***物が外部へ漏れるのを防いでいる。
The
トップシート２の幅方向Ｂの両側縁には、吸収パッド１の長手方向Ａに延在するサイドシート５が接合している。サイドシート５は、液不透過性のプラスチックフィルムや撥水性不織布等により構成される。サイドシート５には、吸収パッド１の幅方向内方端に起立用弾性部材６が設けられている。吸収パッド１の使用時には、起立用弾性部材６の収縮力によりサイドシート５の内方端が着用者の肌に向かって立ち上がり、これにより尿等の***物の横漏れが防止される。
以下、本発明を実施例によって詳細に説明するが、本発明は、下記実施例によって限定されるものではなく、本発明の趣旨を逸脱しない範囲の変更、実施の態様は、いずれも本発明の範囲内に含まれる。 Hereinafter, the present invention will be described in detail by way of examples. However, the present invention is not limited to the following examples, and all modifications and embodiments without departing from the gist of the present invention are not limited thereto. Included in range.
［親油化セルロース系繊維］
親油化セルロース系繊維としては、セルロール系繊維を親油化剤で処理したもの（水酸基と親油化剤とが結合し、疎水性基が導入されたセルロース系繊維）を用いた。この親油化セルロース系繊維は、平均繊維長が４ｃｍ、繊度が２．２ｄｔｅｘ、水に対する接触角が１２１°であった。
[Lipophilic cellulosic fibers]
As the lipophilic cellulosic fiber, a cellulose fiber treated with a lipophilic agent (cellulosic fiber in which a hydroxyl group and a lipophilic agent are bonded and a hydrophobic group is introduced) was used. This lipophilic cellulosic fiber had an average fiber length of 4 cm, a fineness of 2.2 dtex, and a contact angle with water of 121 °.
（接触角）
繊維の水に対する接触角は、自動微小接触角測定装置（協和界面科学社製、型式「ＭＣＡ−２」）を使用し、蒸留水を繊維表面上に滴下したときの繊維と水滴との接触角を測定数５で測定し、平均値を求めた。
(Contact angle)
The contact angle of the fiber with water is determined by using an automatic micro contact angle measuring device (model “MCA-2” manufactured by Kyowa Interface Science Co., Ltd.) and when the distilled water is dropped on the fiber surface. Was measured with a measurement number of 5, and the average value was determined.
［透液性不織布］
エアスルー不織布
親油化セルロース系繊維と合成樹脂繊維（芯鞘型複合繊維、芯部：ポリエチレンテレフタレート、鞘部：ポリエチレン）とを混合し、これらをスクリーンコンベア上に堆積させてウェブを作製した。このウェブにエアスルー方式で熱処理を行い、繊維同士を融着させて、不織布を作製した。なお、親油化セルロース系繊維の含有率、不織布の目付けは、表１に示す値となるように調整した。
[Liquid permeable nonwoven fabric]
Air-through nonwoven fabric Lipophilic cellulosic fibers and synthetic resin fibers (core-sheath type composite fiber, core: polyethylene terephthalate, sheath: polyethylene) were mixed and deposited on a screen conveyor to prepare a web. The web was heat treated by an air-through method, and the fibers were fused together to produce a nonwoven fabric. The content of lipophilic cellulosic fibers and the basis weight of the nonwoven fabric were adjusted to the values shown in Table 1.
ポイントボンド不織布
親油化セルロース系繊維と合成樹脂繊維（芯鞘型複合繊維、芯部：ポリエチレン、鞘部：ポリエチレンテレフタレート）とを混合し、これらをスクリーンコンベア上に堆積させてウェブを作製した。このウェブにエンボスロールで熱処理を行い、繊維同士を融着させて、不織布を作製した。なお、親油化セルロース系繊維の含有率、不織布の目付けは、表１に示す値となるように調整した。
Point bond nonwoven fabric Lipophilic cellulosic fibers and synthetic resin fibers (core-sheath type composite fiber, core: polyethylene, sheath: polyethylene terephthalate) were mixed and deposited on a screen conveyor to prepare a web. The web was heat-treated with an embossing roll to fuse the fibers together to produce a nonwoven fabric. The content of lipophilic cellulosic fibers and the basis weight of the nonwoven fabric were adjusted to the values shown in Table 1.
スパンレース不織布
親油化セルロース系繊維と合成樹脂繊維（芯鞘型複合繊維、芯部：ポリエチレン、鞘部：ポリエチレンテレフタレート）とを混合し、これらをスクリーンコンベア上に堆積させてウェブを作製した。このウェブに高圧水流を吹付けて繊維同士を交絡させて、不織布を作製した。なお、親油化セルロース系繊維の含有率、不織布の目付けは、表１に示す値となるように調整した。
Spunlace nonwoven fabric Lipophilic cellulosic fibers and synthetic resin fibers (core-sheath type composite fiber, core: polyethylene, sheath: polyethylene terephthalate) were mixed and deposited on a screen conveyor to prepare a web. A high-pressure water stream was sprayed on the web to entangle the fibers to produce a nonwoven fabric. The content of lipophilic cellulosic fibers and the basis weight of the nonwoven fabric were adjusted to the values shown in Table 1.
得られた透液性不織布について、引張強さを評価した。 About the obtained liquid-permeable nonwoven fabric, tensile strength was evaluated.
（引張強さ）
透液性不織布の引張強度は、ＪＩＳ Ｌ １９１３（２０１０）に準じて測定した。具体的には、各透液性不織布から、幅５０ｍｍ、長さ２５０ｍｍの試験片を、たて方向（ＭＤ）およびよこ方向（ＣＤ）にそれぞれ５枚切り出した。引張試験機（テンシロン万能材料試験機「ＲＴＧ−１２１０」、エー・アンド・デイ社製）を用いて、各試験片の引張強さ（最大荷重時の強さ）を測定した。測定条件は、チャック間隔１７０ｍｍ、引張速度２００ｍｍ／ｍｉｎとした。５枚の試験片の引張強さの平均値を求め、下記の評価基準で評価した。
○：５Ｎ以上
△：３Ｎ以上、５Ｎ未満
×：３Ｎ未満
(Tensile strength)
The tensile strength of the liquid-permeable nonwoven fabric was measured according to JIS L 1913 (2010). Specifically, 5 test pieces each having a width of 50 mm and a length of 250 mm were cut out from each liquid-permeable nonwoven fabric in the vertical direction (MD) and the transverse direction (CD). The tensile strength (strength at the maximum load) of each test piece was measured using a tensile tester (Tensilon universal material tester “RTG-1210”, manufactured by A & D). The measurement conditions were a chuck interval of 170 mm and a tensile speed of 200 mm / min. The average value of the tensile strength of the five test pieces was determined and evaluated according to the following evaluation criteria.
○: 5N or more Δ: 3N or more, less than 5N ×: less than 3N
透液性不織布の評価結果を表１に示した。表１に示したように、不織布の目付けが２０ｇ／ｍ２以上であれば、引張強さが優れていた。 The evaluation results of the liquid-permeable nonwoven fabric are shown in Table 1. As shown in Table 1, the tensile strength was excellent when the basis weight of the nonwoven fabric was 20 g / m 2 or more.
次に、前記透液性不織布を用いた吸水性物品について、疑似軟便の吸収性を評価した。 Next, the absorbability of pseudo soft stool was evaluated for the water-absorbent article using the liquid-permeable nonwoven fabric.
（漏れ評価）
市販の吸収性パッド（リブドゥコーポレーション社製、サラケア（登録商標）パッド ビッグ（全吸収量１１００ｍｌ））のトップシートを、前記透液性不織布に変更し、試験用の吸収性物品を作製した。作製した吸収性物品を、約１０°の傾斜を有する台に載置した。この吸収性物品の略中央部に測定治具を置いた。前記測定治具は、アクリル製板（１０ｃｍ×１０ｃｍ）の中央に開口（内径２．５４ｃｍ）が設けられ、この開口部分に垂直にアクリル製円筒部材（内径２．５４ｃｍ）が取り付けられている。前記測定治具は、アクリル製板の下面を、吸収性物品の透液性不織布に当接させた。この測定治具の円筒に、疑似軟便（トマトジュース）１００ｍｌを投入し、１分後に測定治具を取り上げた。疑似軟便の吸収度合いおよび疑似軟便の吸収性物品外部への漏れの有無を目視にて観察し、下記の評価基準で評価した。
○：外部への漏れなし、かつ、疑似軟便が全て吸収されている。
△：外部への漏れがある、または、透液性不織布上に疑似軟便が残存している。
×：外部への漏れがあり、かつ、透液性不織布上に疑似軟便が残存している。
(Leakage evaluation)
A top sheet of a commercially available absorbent pad (manufactured by Ribdou Corporation, Saracare (registered trademark) pad big (total absorption amount 1100 ml)) was changed to the liquid-permeable nonwoven fabric to prepare an absorbent article for testing. The produced absorbent article was placed on a table having an inclination of about 10 °. A measuring jig was placed in a substantially central part of the absorbent article. The measurement jig is provided with an opening (inner diameter 2.54 cm) at the center of an acrylic plate (10 cm × 10 cm), and an acrylic cylindrical member (inner diameter 2.54 cm) is vertically attached to the opening. In the measurement jig, the lower surface of the acrylic plate was brought into contact with the liquid-permeable nonwoven fabric of the absorbent article. 100 ml of pseudo soft stool (tomato juice) was put into the cylinder of this measuring jig, and the measuring jig was taken up after 1 minute. The degree of absorption of pseudo soft stool and the presence or absence of leakage of the pseudo soft stool to the outside of the absorbent article were visually observed and evaluated according to the following evaluation criteria.
○: No leakage to the outside, and all pseudo soft stools are absorbed.
Δ: There is leakage to the outside, or pseudo soft stool remains on the liquid-permeable nonwoven fabric.
X: There is leakage to the outside, and pseudo soft stool remains on the liquid-permeable nonwoven fabric.
吸収性物品の評価結果を表１に示した。 The evaluation results of the absorbent article are shown in Table 1.
吸収性物品Ｎｏ．１〜８を比較すると、透液性不織布中の親油化セルロース系繊維の含有率が５質量％〜４０質量％であれば、疑似軟便の吸収性に優れていた。吸収性物品Ｎｏ．９〜１４を比較すると、目付けが１５ｇ／ｍ２以上であれば不織布の引張強さが良好となり、目付けが４０ｇ／ｍ２以下であれば疑似軟便の吸収性に優れていた。吸収性物品Ｎｏ．４、１５および１６を比較すると、エアスルー不織布が最も疑似軟便の吸収性に優れていた。 Absorbent article no. When 1 to 8 were compared, if the content of the lipophilic cellulosic fiber in the liquid-permeable nonwoven fabric was 5% by mass to 40% by mass, the pseudo-soft stool absorbability was excellent. Absorbent article no. Comparing 9 to 14, the nonwoven fabric had good tensile strength when the basis weight was 15 g / m 2 or more, and the pseudo soft stool absorbability was excellent when the basis weight was 40 g / m 2 or less. Absorbent article no. When comparing 4, 15, and 16, the air-through nonwoven fabric was most excellent in absorbability of pseudo-soft stool.
本発明の吸収性物品は、例えば、人体から排出される体液を吸収する用途に好適に使用でき、特に失禁パッド、使い捨ておむつ、生理用ナプキンなどとして好適に利用できる。 The absorbent article of the present invention can be suitably used, for example, for applications that absorb bodily fluids discharged from the human body, and can be particularly suitably used as incontinence pads, disposable diapers, sanitary napkins, and the like.
１：吸収パッド（吸収性物品）、２：トップシート（透液性不織布）、３：バックシート（不透液性シート）、４：吸収体、５：サイドシート、６：起立用弾性部材 1: Absorbent pad (absorbent article) 2: Top sheet (liquid-permeable nonwoven fabric) 3: Back sheet (liquid-impermeable sheet) 4: Absorber 5: Side sheet 6: Elastic member for standing
Claims (6)
前記透液性不織布を構成する繊維が、親油化セルロース系繊維を含有することを特徴とする吸収性物品。 An absorbent article having a liquid-permeable nonwoven fabric, a liquid-impervious sheet, and an absorbent body disposed therebetween,
The absorbent article characterized in that the fibers constituting the liquid-permeable nonwoven fabric contain lipophilic cellulosic fibers.
前記透液性不織布を構成する繊維中の前記親油化セルロール系繊維の含有率が、５質量％〜４０質量％である請求項１に記載の吸収性物品。 The fibers constituting the liquid-permeable nonwoven fabric contain the lipophilic cellulosic fibers and synthetic resin fibers,
The absorbent article according to claim 1, wherein the content of the lipophilic cellulose fiber in the fibers constituting the liquid-permeable nonwoven fabric is 5% by mass to 40% by mass.