JP2017155392A

JP2017155392A - Clothing

Info

Publication number: JP2017155392A
Application number: JP2016042876A
Authority: JP
Inventors: 拓美山下; Takumi Yamashita; 高橋　朋子; Tomoko Takahashi; 朋子高橋; 哲行渡部; Tetsuyuki Watabe
Original assignee: Asahi Kasei Corp; Fast Retailing Co Ltd
Current assignee: Asahi Kasei Corp; Fast Retailing Co Ltd
Priority date: 2016-03-04
Filing date: 2016-03-04
Publication date: 2017-09-07
Anticipated expiration: 2036-03-04
Also published as: JP6824612B2

Abstract

PROBLEM TO BE SOLVED: To provide a clothing that exhibits excellent stretchability in addition to characteristics such as moisture absorption/desorption and quick-drying properties.SOLUTION: Clothing, which includes a knitted fabric 10 knitted in such a manner that one or more courses 3 made of a first fiber 1 including a cellulose fiber and one or more courses 4 made of a second fiber 2 including an elastic fiber are repeated in a warp direction, is provided. A knitting loop 5 of the course 3 made of the first fiber 1 is longer than a knitting loop 6 of the course 4 made of the second fiber 2.SELECTED DRAWING: Figure 1

Description

本発明は、衣服に関する。 The present invention relates to clothes.

従来、タンクトップ、キャミソール、Ｔシャツ、ショーツ等のインナーウェアなどの衣服には、吸放湿性、速乾性などの特性に加えて、ストレッチ性が求められている。 2. Description of the Related Art Conventionally, clothes such as tank tops, camisoles, T-shirts, and shorts are required to have stretch properties in addition to characteristics such as moisture absorption and desorption and quick drying.

国際公開第２０１５／００５４３２号International Publication No. 2015/005432

しかしながら、従来の衣服では、吸放湿性、速乾性などの特性を損なわずに、十分なストレッチ性を与えるのは難しかった。
本発明の一態様は、吸放湿性、速乾性などの特性に加え、優れたストレッチ性を有する衣服を提供することを目的とする。 However, with conventional garments, it has been difficult to provide sufficient stretchability without impairing properties such as moisture absorption and desorption and quick drying.
An object of one embodiment of the present invention is to provide a garment having excellent stretch properties in addition to properties such as moisture absorption and desorption and quick drying.

本発明の一態様は、セルロース繊維を含む第１繊維からなる１または複数のコースと、弾性繊維を含む第２繊維からなる１または複数のコースとが、経方向に繰り返されて編成された編地を含み、前記第１繊維からなるコースの編みループ長は、前記第２繊維からなるコースの編みループ長より長い、衣服を提供する。
前記セルロース繊維は、長繊維であることが好ましい。
前記セルロース繊維は、再生セルロース繊維であることが好ましい。
前記セルロース繊維は、キュプラであることが好ましい。
前記弾性繊維は、ポリウレタン弾性糸であることが好ましい。
前記編地は、前記第１繊維からなる１〜３つのコースと、前記第２繊維からなる１つのコースとが、経方向に繰り返されて編成されていることが好ましい。
前記第１繊維からなるコースの編みループは、前記第２繊維からなるコースの編みループに比べて経方向の寸法が大きいことが好ましい。
本発明の一態様は、筒状部を有し、前記筒状部がシームレス形状である衣服を提供する。
前記編地は、天竺組織であることが好ましい。
本発明の一態様は、インナーウェアである衣服を提供する。 One embodiment of the present invention is a knitted fabric in which one or more courses including first fibers including cellulose fibers and one or more courses including second fibers including elastic fibers are repeatedly knitted in the warp direction. The knitting loop length of the course including the ground and made of the first fiber is longer than the knitting loop length of the course made of the second fiber.
The cellulose fiber is preferably a long fiber.
The cellulose fiber is preferably a regenerated cellulose fiber.
The cellulose fiber is preferably a cupra.
The elastic fiber is preferably a polyurethane elastic yarn.
It is preferable that the knitted fabric is knitted by repeating one to three courses made of the first fibers and one course made of the second fibers in the warp direction.
It is preferable that the knitted loop of the course made of the first fiber has a larger dimension in the warp direction than the knitted loop of the course made of the second fiber.
One embodiment of the present invention provides a garment having a tubular portion, wherein the tubular portion has a seamless shape.
The knitted fabric is preferably a tengu structure.
One embodiment of the present invention provides a garment that is innerwear.

本発明の一態様によれば、吸放湿性、速乾性などの特性に加え、優れたストレッチ性を示す衣服が得られる。 According to one embodiment of the present invention, clothes that exhibit excellent stretch properties in addition to properties such as moisture absorption and desorption and quick drying properties can be obtained.

実施形態の衣服に用いられる編地を模式的に示す図である。It is a figure which shows typically the knitted fabric used for the clothes of embodiment. 図１に示す編地が伸長した状態を模式的に示す図である。It is a figure which shows typically the state which the knitted fabric shown in FIG. 1 expanded. 図１に示す編地の編成図である。FIG. 2 is a knitting diagram of the knitted fabric shown in FIG. 1. 編地の第１変形例を模式的に示す図である。It is a figure which shows typically the 1st modification of a knitted fabric. 編地の第２変形例を模式的に示す図である。It is a figure which shows typically the 2nd modification of a knitted fabric. 実施形態の衣服の例を示す図である。It is a figure which shows the example of the clothes of embodiment. 実施形態の衣服の例を示す図である。It is a figure which shows the example of the clothes of embodiment. 実施形態の衣服の例を示す図である。It is a figure which shows the example of the clothes of embodiment. 実施形態の衣服の例を示す図である。It is a figure which shows the example of the clothes of embodiment. 試験結果を示すグラフである。It is a graph which shows a test result. 試験結果を示すグラフである。It is a graph which shows a test result. 試験結果を示すグラフである。It is a graph which shows a test result. 試験結果を示すグラフである。It is a graph which shows a test result. 試験結果を示すグラフである。It is a graph which shows a test result. 試験結果を示すグラフである。It is a graph which shows a test result.

以下、本発明の実施形態について、詳細に説明する。
実施形態の衣服は、セルロース繊維を含む１または複数の第１繊維からなるコースと、弾性繊維を含む第２繊維からなる１または複数のコースとが、経方向に繰り返されて編成された編地を含む。 Hereinafter, embodiments of the present invention will be described in detail.
The garment of the embodiment is a knitted fabric in which a course made of one or more first fibers containing cellulose fibers and one or more courses made of second fibers containing elastic fibers are knitted repeatedly in the warp direction. including.

セルロース繊維は、短繊維でも長繊維でもよいが、特に、長繊維が好ましい。長繊維のセルロース繊維を使用することによって、吸放湿性、速乾性などの特性を良好にすることができる。
セルロース繊維としては、天然繊維（綿等）、再生セルロース繊維が使用できる。特に、再生セルロース繊維が好ましい。再生セルロース繊維としては、キュプラ（銅アンモニアレーヨン）、レーヨン（ビスコースレーヨン）、テンセル、ポリノジック等がある。これらの繊維は単独で使用してもよいし、２以上を併用してもよい。なかでも特に、キュプラが好ましい。
再生セルロース繊維としては、フィラメント糸、紡績糸、複合糸（２種以上の繊維を撚糸、カバーリング、エアー混繊等により混合した糸）などを使用できる。フィラメント糸の場合は、例えば、原糸（未加工糸）、仮撚加工糸、先染糸などであってよい。 The cellulose fibers may be short fibers or long fibers, but long fibers are particularly preferable. By using a long cellulose fiber, it is possible to improve the properties such as moisture absorption and desorption and quick drying.
As cellulose fiber, natural fiber (cotton etc.) and regenerated cellulose fiber can be used. In particular, regenerated cellulose fiber is preferable. Examples of regenerated cellulose fibers include cupra (copper ammonia rayon), rayon (viscose rayon), tencel, polynosic and the like. These fibers may be used alone or in combination of two or more. Of these, cupra is particularly preferable.
As the regenerated cellulose fiber, filament yarn, spun yarn, composite yarn (a yarn obtained by mixing two or more kinds of fibers by twisting, covering, air blending, or the like) can be used. In the case of a filament yarn, it may be, for example, a raw yarn (unprocessed yarn), a false twisted yarn, a pre-dyed yarn, or the like.

セルロース繊維の繊度は、例えば３０〜２００ｄｔｅｘとすることができる。セルロース繊維の繊度を３０ｄｔｅｘ以上とすることによって、十分な強度を有する衣服が得られる。セルロース繊維の繊度を２００ｄｔｅｘ以下とすることによって、衣服に柔らかな風合いを与えることができる。
セルロース繊維の単糸繊度は、速乾性をよくするため１．９ｄｔｅｘ以下とすることが好ましい。単糸が細過ぎると速乾性は低下するため、前記単糸繊度は、好ましくは０．９ｄｔｅｘ以上１．９ｄｔｅｘ以下であり、特に１．３〜１．６ｄｔｅｘが好ましい。 The fineness of the cellulose fiber can be set to, for example, 30 to 200 dtex. By setting the fineness of the cellulose fiber to 30 dtex or more, clothes having sufficient strength can be obtained. By setting the fineness of the cellulose fiber to 200 dtex or less, a soft texture can be given to the clothes.
The single yarn fineness of the cellulose fiber is preferably 1.9 dtex or less in order to improve quick drying. If the single yarn is too thin, the quick-drying property is lowered. Therefore, the single yarn fineness is preferably 0.9 dtex or more and 1.9 dtex or less, and particularly preferably 1.3 to 1.6 dtex.

第１繊維は、セルロース繊維のみからなる構成（すなわちセルロース繊維の使用比率１００質量％）であってもよいが、セルロース繊維と他の補助繊維との複合繊維を用いるのが好ましい。
セルロース繊維の補助繊維もしくは複合相手糸としては、ポリアミド系繊維、ポリエステル系繊維、アクリル系繊維、ポリフ口ピレン系繊維、塩化ビニル系繊維などが使用できる。これらの繊維は単独で使用してもよいし、２以上を併用してもよい。特に、ポリアミド系繊維（例えばナイロン）が好ましい。
補助繊維もしくは複合相手糸の繊度は、例えば１０〜２００ｄｔｅｘとすることができる。 The first fiber may be composed of only cellulose fibers (that is, the use ratio of cellulose fibers is 100% by mass), but it is preferable to use a composite fiber of cellulose fibers and other auxiliary fibers.
As the auxiliary fiber or composite partner yarn of the cellulose fiber, polyamide fiber, polyester fiber, acrylic fiber, polypropylene fiber, vinyl chloride fiber and the like can be used. These fibers may be used alone or in combination of two or more. In particular, polyamide fibers (for example, nylon) are preferable.
The fineness of the auxiliary fiber or the composite partner yarn can be, for example, 10 to 200 dtex.

第１繊維は、セルロース繊維を含む主繊維と、補助繊維からなる副繊維とを含む複合繊維であってもよい。主繊維は、セルロース繊維と補助繊維との複合繊維であってよい。
第１繊維の断面形状は、丸形、三角形、十字形、Ｗ形、Ｍ形、Ｃ形、Ｉ形、ドッグボーン形、中空糸などであってよい。 The first fiber may be a composite fiber including a main fiber including a cellulose fiber and a sub fiber made of an auxiliary fiber. The main fiber may be a composite fiber of cellulose fiber and auxiliary fiber.
The cross-sectional shape of the first fiber may be a round shape, a triangular shape, a cross shape, a W shape, an M shape, a C shape, an I shape, a dogbone shape, a hollow fiber, or the like.

第１繊維が複合繊維である場合、第１繊維中のセルロース繊維の使用比率は、例えば５０質量％以上である。セルロース繊維の使用比率を５０質量％以上とすることによって、衣服の吸放湿性などの特性を高めることができる。セルロース繊維の使用比率は、例えば９０質量％以下とすることができる。セルロース繊維の使用比率は好ましくは５０〜７５質量％である。
前記混率範囲（セルロース繊維の使用比率５０〜９０質量％）で、かつセルロース繊維の単糸繊度を前記範囲（０．９〜１．９ｄｔｅｘ）にすることによって、吸放湿性と速乾性を両立することができる。 When the first fiber is a composite fiber, the use ratio of the cellulose fiber in the first fiber is, for example, 50% by mass or more. By setting the use ratio of the cellulose fiber to 50% by mass or more, characteristics such as moisture absorption and desorption of clothes can be enhanced. The use ratio of the cellulose fiber can be, for example, 90% by mass or less. The use ratio of the cellulose fiber is preferably 50 to 75% by mass.
The moisture absorption / release property and the quick-drying property are achieved by adjusting the mixing ratio range (the use ratio of the cellulose fiber is 50 to 90% by mass) and the single fiber fineness of the cellulose fiber within the range (0.9 to 1.9 dtex). be able to.

第１繊維の繊度は、例えば３０〜２００ｄｔｅｘとすることができる。第１繊維の繊度を３０ｄｔｅｘ以上することによって、十分な強度を有する衣服が得られる。第１繊維の繊度を２００ｄｔｅｘ以下とすることによって、衣服に柔らかな風合いを与えることができる。 The fineness of the first fiber can be set to, for example, 30 to 200 dtex. By setting the fineness of the first fiber to 30 dtex or more, clothes having sufficient strength can be obtained. By setting the fineness of the first fiber to 200 dtex or less, a soft texture can be given to the clothes.

弾性繊維としては、ポリウレタン弾性糸、ポリエーテル・エステル弾性糸、ポリアミド弾性糸、ポリオレフィン弾性糸などが使用できる。これらの繊維は単独で使用してもよいし、２以上を併用してもよい。
弾性繊維としては、特に、ポリウレタン弾性糸が好ましい。ポリウレタン弾性糸としては、乾式紡糸または溶融紡糸により得られるものが使用できる。弾性繊維としては、フィラメント糸、紡績糸、複合糸を使用できる。弾性繊維は、ベア、被覆糸のいずれであってもよい。 As the elastic fiber, polyurethane elastic yarn, polyether / ester elastic yarn, polyamide elastic yarn, polyolefin elastic yarn and the like can be used. These fibers may be used alone or in combination of two or more.
As the elastic fiber, polyurethane elastic yarn is particularly preferable. As the polyurethane elastic yarn, one obtained by dry spinning or melt spinning can be used. As the elastic fiber, a filament yarn, a spun yarn, and a composite yarn can be used. The elastic fiber may be either bare or coated yarn.

弾性繊維は、弾性を有する繊維であり、セルロース繊維に比べて破断伸度（例えばＪＩＳＣ２１５１に準拠）が大きい。
弾性繊維の破断伸度は、４００％以上が好ましい。これによって、伸長性が良好であり、着用しやすい衣服が得られる。弾性繊維の破断伸度は、１０００％以下とすると、伸長回復性が高く、フィット性に優れた衣服が得られる。
弾性繊維の繊度は、例えば１０〜２００ｄｔｅｘとすることができる。これによって、フィット性および着用しやすさに優れた衣服が得られる。
弾性繊維を用いることによって、衣服のストレッチ性が高められる。 The elastic fiber is a fiber having elasticity, and has a higher elongation at break (for example, conforming to JIS C2151) than the cellulose fiber.
The breaking elongation of the elastic fiber is preferably 400% or more. As a result, clothes that have good extensibility and are easy to wear can be obtained. When the breaking elongation of the elastic fiber is 1000% or less, a clothes having high stretch recovery and excellent fit can be obtained.
The fineness of the elastic fiber can be set to 10 to 200 dtex, for example. Thereby, a garment excellent in fit and ease of wearing can be obtained.
By using elastic fibers, the stretchability of the clothes is enhanced.

第２繊維は弾性繊維を含めばよく、弾性繊維のみからなる構成（すなわち弾性繊維の使用比率１００質量％）であってもよいが、弾性繊維と他の補助繊維との複合繊維であってもよい。また他の補助繊維を引きそろえてもよい。
第２繊維の補助繊維としては、ポリアミド系繊維、ポリエステル系繊維、アクリル系繊維、ポリフ口ピレン系繊維、塩化ビニル系繊維などが使用できる。これらの繊維は単独で使用してもよいし、２以上を併用してもよい。補助繊維としては、特に、ポリアミド系繊維（例えばナイロン）が好ましい。補助繊維としては、フィラメント糸、紡績糸、複合糸を使用できる。
補助繊維の繊度は、例えば１０〜２００ｄｔｅｘとすることができる。 The second fiber only needs to include an elastic fiber, and may be composed of only the elastic fiber (that is, the elastic fiber use ratio is 100% by mass), but may be a composite fiber of the elastic fiber and another auxiliary fiber. Good. Other auxiliary fibers may be arranged.
As the auxiliary fiber for the second fiber, polyamide fiber, polyester fiber, acrylic fiber, polypyrene fiber, vinyl chloride fiber, or the like can be used. These fibers may be used alone or in combination of two or more. As the auxiliary fiber, a polyamide fiber (for example, nylon) is particularly preferable. As the auxiliary fiber, a filament yarn, a spun yarn, and a composite yarn can be used.
The fineness of the auxiliary fiber can be set to 10 to 200 dtex, for example.

第２繊維が複合繊維である場合、第２繊維中の弾性繊維の使用比率は、例えば３０質量％以上である。弾性繊維の使用比率を３０質量％以上とすることによって、ストレッチ性を高めることができる。弾性繊維の使用比率は、例えば９０質量％以下とすることができる。
第２繊維の繊度は、例えば１０〜２００ｄｔｅｘとすることができる。 When the second fiber is a composite fiber, the usage ratio of the elastic fiber in the second fiber is, for example, 30% by mass or more. Stretchability can be enhanced by setting the use ratio of the elastic fiber to 30% by mass or more. The use ratio of the elastic fiber can be set to 90% by mass or less, for example.
The fineness of the second fiber can be set to 10 to 200 dtex, for example.

第２繊維は、第１繊維に比べて破断伸度（例えばＪＩＳＣ２１５１に準拠）が大きいことが好ましい。
第２繊維の破断伸度は、１００％以上が好ましい。これによって、伸長性が良好であり、着用しやすい衣服が得られる。第２繊維の破断伸度は、１０００％以下とすると、伸長回復性が高く、フィット性に優れた衣服が得られる。 The second fiber preferably has a higher elongation at break (for example, in accordance with JIS C2151) than the first fiber.
The breaking elongation of the second fiber is preferably 100% or more. As a result, clothes that have good extensibility and are easy to wear can be obtained. When the breaking elongation of the second fiber is 1000% or less, a clothes having high stretch recovery and excellent fit can be obtained.

編地の編み組織は、天竺、インレー、スムース、フライスなどが好ましいが、これらに限定されず、カノコ、ハニカム、メッシュ、コンフォート等の組織も可能である。 The knitting structure of the knitted fabric is preferably a tenji, inlay, smooth, milling, etc., but is not limited to these, and a structure such as canopy, honeycomb, mesh, and comfort is also possible.

編地１０の目付は特に限定されないが、例えば１００ｇ／ｍ^２〜２００ｇ／ｍ^２とすることができる。目付を１００ｇ／ｍ^２以上とすることで、汗処理機能を高めることができる。また、目付を２００ｇ／ｍ^２以下とすることで、衣服の着用しやすさを良好にすることができる。 Basis weight of the knitted fabric 10 is not particularly limited, it can be, for example, ^{^{100g / m 2 ~200g / m 2}} . By setting the basis weight to 100 g / m ² or more, the sweat treatment function can be enhanced. Moreover, the ease of wearing of clothes can be made favorable by a fabric weight being 200 g / m < ² > or less.

実施形態の衣服としては、特に限定されないが、例えば、タンクトップ、キャミソール、シャツ（Ｔシャツ等）、スリップ、ブラジャー、ショーツ、ガードル、スパッツ、腹巻き、パンティストッキング、タイツ等のインナーウェアを挙げることができる。
実施形態の衣服はストレッチ性に優れており、フィット性および着用しやすさを良好にすることができるため、これらの特性が特に要求される女性用のインナーウェアとして好適である。 Although it does not specifically limit as clothes of embodiment, For example, innerwear, such as a tank top, a camisole, a shirt (T-shirt etc.), a slip, a bra, shorts, a girdle, spats, a stomach wrap, pantyhose, tights, etc. are mentioned. it can.
The garment according to the embodiment is excellent in stretchability, and can have good fit and ease of wearing. Therefore, the garment is suitable as an innerwear for women particularly requiring these characteristics.

衣服における第１繊維の使用比率は、例えば５０質量％以上である。第１繊維の使用比率を５０質量％以上とすることによって、吸放湿性、速乾性などを高めることができる。第１繊維の使用比率は、例えば９０質量％以下とすることができる。
衣服における第２繊維の使用比率は、例えば１０質量％以上である。第２繊維の使用比率を１０質量％以上とすることによって、ストレッチ性を高めることができる。第２繊維の使用比率は、例えば５０質量％以下とすることができる。 The use ratio of the first fibers in the clothes is, for example, 50% by mass or more. By setting the use ratio of the first fiber to 50% by mass or more, moisture absorption and desorption, quick drying, and the like can be improved. The use ratio of the first fibers can be set to 90% by mass or less, for example.
The use ratio of the second fibers in the garment is, for example, 10% by mass or more. By making the use ratio of the second fiber 10% by mass or more, the stretchability can be enhanced. The use ratio of the second fibers can be set to, for example, 50% by mass or less.

実施形態の衣服は、筒状部を有し、前記筒状部はシームレス形状（周方向に継ぎ目がない形状）であることが好ましい。
シームレス形状の衣服を製造するための編機は、特に限定されない。
シームレス形状の筒状部は、使用者の肌を局所的に強く圧迫する部位がないため、肌にフィットしていても使用者に違和感を与えず、着用感が良好となる。そのため、ストレッチ性という実施形態の衣服の長所が生かされやすい。
また、実施形態の衣服はストレッチ性に優れているため、使用者の体形に幅広く対応できる。そのため、サイズが異なる製品を多数用意する必要がなく、製造コストの点で有利となる。 The garment of the embodiment preferably has a tubular portion, and the tubular portion is preferably a seamless shape (a shape having no seam in the circumferential direction).
The knitting machine for manufacturing seamless-shaped clothes is not particularly limited.
Since the seamless-shaped tubular portion does not have a site that strongly presses the user's skin locally, the user does not feel uncomfortable even when the skin is fitted, and the wearing feeling is improved. Therefore, the advantage of the clothes of the embodiment called stretchability is easily utilized.
Moreover, since the clothes of the embodiments are excellent in stretchability, they can be used in a wide range of user shapes. Therefore, it is not necessary to prepare many products with different sizes, which is advantageous in terms of manufacturing cost.

以下、図面を参照して、実施形態の衣服を詳しく説明する。
図１は、実施形態の衣服に用いられる編地の一例である編地１０を模式的に示す図である。図２は、編地１０が伸長した状態を模式的に示す図である。図３は、編地１０の編成図である。
図１に示すように、編地１０は、第１繊維１からなるコース３と、第２繊維２からなるコース４とが、経方向に繰り返されて編成されている。図１では、上下方向（Ｙ方向）が経方向であり、左右方向（Ｘ方向）が緯方向である。
図１に示す編地１０は、天竺組織である。
編地１０では、第１繊維１は、セルロース繊維を含む主繊維１ａと、副繊維１ｂとを含む複合繊維である。 Hereinafter, the clothes of the embodiment will be described in detail with reference to the drawings.
Drawing 1 is a figure showing typically knitted fabric 10 which is an example of knitted fabric used for clothes of an embodiment. FIG. 2 is a diagram schematically showing a state in which the knitted fabric 10 is extended. FIG. 3 is a knitting diagram of the knitted fabric 10.
As shown in FIG. 1, the knitted fabric 10 is knitted by repeating a course 3 made of the first fibers 1 and a course 4 made of the second fibers 2 in the warp direction. In FIG. 1, the vertical direction (Y direction) is the longitudinal direction, and the horizontal direction (X direction) is the weft direction.
The knitted fabric 10 shown in FIG.
In the knitted fabric 10, the 1st fiber 1 is a composite fiber containing the main fiber 1a containing a cellulose fiber, and the subfiber 1b.

編地１０は、第１繊維１からなる１〜３つのコース３と、第２繊維２からなる１つのコース４とが、経方向に繰り返されて編成されていることが好ましい。
図１に示す編地１０は、第１繊維１からなる１つのコース３と、第２繊維２からなる１つのコース４とが、経方向に繰り返されて編成されている。
図４に示す編地１０Ａは、図１に示す編地１０の第１変形例であって、第１繊維１からなる２つのコース３と、第２繊維２からなる１つのコース４とが、経方向に繰り返されて編成されている。２つのコース３は経方向に隣り合っている。
図５に示す編地１０Ｂは、図１に示す編地１０の第２変形例であって、第１繊維１からなる３つのコース３と、第２繊維２からなる１つのコース４とが、経方向に繰り返されて編成されている。３つのコース３は経方向に隣り合っている。 The knitted fabric 10 is preferably knitted by repeating one to three courses 3 made of the first fibers 1 and one course 4 made of the second fibers 2 in the warp direction.
The knitted fabric 10 shown in FIG. 1 is knitted by repeating one course 3 made of the first fibers 1 and one course 4 made of the second fibers 2 in the warp direction.
A knitted fabric 10A shown in FIG. 4 is a first modification of the knitted fabric 10 shown in FIG. 1, and includes two courses 3 made of the first fibers 1 and one course 4 made of the second fibers 2. Repeatedly organized in the warp direction. The two courses 3 are adjacent in the warp direction.
A knitted fabric 10B shown in FIG. 5 is a second modification of the knitted fabric 10 shown in FIG. 1, and includes three courses 3 made of the first fibers 1 and one course 4 made of the second fibers 2. Repeatedly organized in the warp direction. The three courses 3 are adjacent in the warp direction.

一つの繰り返し単位におけるコース３の数を１以上とすることによって、十分なストレッチ性を有し、かつ、吸放湿性、速乾性などの特性に優れた衣服が得られる。
一つの繰り返し単位におけるコース３の数を３以下とすることによって、吸放湿性、速乾性などの特性を低下させることなく、十分なストレッチ性を衣服に与えることができる。 By setting the number of courses 3 in one repeating unit to 1 or more, a garment having sufficient stretch properties and excellent properties such as moisture absorption / release properties and quick drying properties can be obtained.
By setting the number of courses 3 in one repeating unit to 3 or less, sufficient stretch properties can be imparted to the garment without deteriorating properties such as moisture absorption / release properties and quick drying properties.

編地１０全体のコース３，４の比率、すなわちコース３の数Ｎ１とコース４の数Ｎ２との比率（Ｎ１／Ｎ２）は、１〜３が好ましい。
コース３とコース４の比率（Ｎ１／Ｎ２）を１以上とすることによって、十分なストレッチ性を有し、かつ、吸放湿性、速乾性などの特性に優れた衣服が得られる。コース３とコース４の比率（Ｎ１／Ｎ２）を３以下とすることによって、吸放湿性、速乾性などの特性を低下させることなく、十分なストレッチ性を衣服に与えることができる。 The ratio of the courses 3 and 4 of the entire knitted fabric 10, that is, the ratio (N1 / N2) of the number N1 of courses 3 to the number N2 of courses 4 is preferably 1 to 3.
By setting the ratio (N1 / N2) between the course 3 and the course 4 to 1 or more, clothes having sufficient stretch properties and excellent properties such as moisture absorption / release properties and quick drying properties can be obtained. By setting the ratio (N1 / N2) of the course 3 and the course 4 to 3 or less, sufficient stretchability can be imparted to the garment without deteriorating characteristics such as moisture absorption / release properties and quick drying properties.

第１繊維１からなるコース３の編みループ５は、第２繊維２からなるコース４の編みループ６に比べて長い。編みループ５の長さは、例えば編みループ６の長さに対して１０５％以上（好ましくは１１０％以上）とすることができる。
第１繊維１の編みループ５に十分な長さが確保されるため、編地１０の伸長を妨げることがなく、しかも収縮力を高めることができる。また、第２繊維２の編みループ６が比較的短いため、伸長時に引張力が第２繊維２に作用しやすいことから、第２繊維２は収縮時には高い弾性回復力を発揮する。よって、編地１０の伸長性および伸長回復性を向上させることができる。
また、編地１０における第１繊維１の表面積が大きくなるため、セルロース繊維によって得られる特性、すなわち、吸放湿性、速乾性などを高めることができる。 The knitting loop 5 of the course 3 made of the first fibers 1 is longer than the knitting loop 6 of the course 4 made of the second fibers 2. The length of the knitting loop 5 can be, for example, 105% or more (preferably 110% or more) with respect to the length of the knitting loop 6.
Since a sufficient length is secured for the knitting loop 5 of the first fiber 1, the expansion of the knitted fabric 10 is not hindered and the contraction force can be increased. In addition, since the knitted loop 6 of the second fiber 2 is relatively short, a tensile force is likely to act on the second fiber 2 at the time of extension, so that the second fiber 2 exhibits a high elastic recovery force at the time of contraction. Therefore, the stretchability and stretch recovery property of the knitted fabric 10 can be improved.
Moreover, since the surface area of the 1st fiber 1 in the knitted fabric 10 becomes large, the characteristic obtained by a cellulose fiber, ie, moisture absorption / release property, quick-drying property, etc. can be improved.

編みループ５，６の長さは、例えば次のようにして測定することができる。
編地１０を経方向および緯方向にそれぞれ３０％伸長させ、その状態で、編地１０に垂直な方向（図１の紙面に垂直な方向）から編地１０を観察する。観察可能な編みループ５の一端５ａ，６ａと他端５ｂ，６ｂをそれぞれ始点および終点とし、始点から終点に至る編みループ５，６の長さを測定し、これを編みループ５，６の長さとすることができる。 The length of the knitting loops 5 and 6 can be measured, for example, as follows.
The knitted fabric 10 is stretched by 30% in the warp direction and the weft direction, and in this state, the knitted fabric 10 is observed from a direction perpendicular to the knitted fabric 10 (direction perpendicular to the paper surface of FIG. 1). One end 5a, 6a and the other end 5b, 6b of the observable knitting loop 5 are set as the start point and the end point, respectively, and the lengths of the knitting loops 5, 6 from the start point to the end point are measured. It can be.

第１繊維１の編みループ５に十分な長さが確保されるため、編地１０の伸長を妨げることがなく、しかも収縮力を高めることができる。また、第２繊維２の編みループ６が比較的短いため、伸長時に引張力が第２繊維２に作用しやすいことから、第２繊維２は収縮時には高い弾性回復力を発揮する。よって、編地１０の伸長性および伸長回復性を向上させることができる。
また、編地１０における第１繊維１の表面積が大きくなるため、セルロース繊維によって得られる特性、すなわち、吸放湿性、速乾性などを高めることができる。 Since a sufficient length is secured for the knitting loop 5 of the first fiber 1, the expansion of the knitted fabric 10 is not hindered and the contraction force can be increased. In addition, since the knitted loop 6 of the second fiber 2 is relatively short, a tensile force is likely to act on the second fiber 2 at the time of extension, so that the second fiber 2 exhibits a high elastic recovery force at the time of contraction. Therefore, the stretchability and stretch recovery property of the knitted fabric 10 can be improved.
Moreover, since the surface area of the 1st fiber 1 in the knitted fabric 10 becomes large, the characteristic obtained by a cellulose fiber, ie, moisture absorption / release property, quick-drying property, etc. can be improved.

第１繊維１からなるコース３の編みループ５は、第２繊維２からなるコース４の編みループ６に比べて径方向の寸法が大きいことが好ましい。すなわち、第１繊維１の編みループ５の径方向寸法Ｌ１は、第２繊維２の編みループ６の径方向寸法Ｌ２よりも大きいことが好ましい。
寸法Ｌ１は、例えば一端５ａと他端５ｂとを結ぶ直線から編みループ５の先端までの距離である。寸法Ｌ２は、例えば一端６ａと他端６ｂとを結ぶ直線から編みループ６の先端までの距離である。寸法Ｌ１，Ｌ２は、編みループ５，６の長さと同様に、編地１０を経方向および緯方向にそれぞれ３０％伸長させた状態で測定することができる。 The knitted loop 5 of the course 3 made of the first fibers 1 preferably has a larger dimension in the radial direction than the knitted loop 6 of the course 4 made of the second fibers 2. That is, the radial dimension L1 of the knitted loop 5 of the first fiber 1 is preferably larger than the radial dimension L2 of the knitted loop 6 of the second fiber 2.
The dimension L1 is, for example, the distance from the straight line connecting the one end 5a and the other end 5b to the tip of the knitted loop 5. The dimension L2 is, for example, the distance from the straight line connecting the one end 6a and the other end 6b to the tip of the knitted loop 6. Similar to the lengths of the knitting loops 5 and 6, the dimensions L1 and L2 can be measured in a state where the knitted fabric 10 is stretched by 30% in the warp direction and the weft direction, respectively.

図２に示すように、編地１０は、緯方向に引張力を加えると、同方向に伸長する。この際、第１繊維１からなるコース３は、長い編みループ５を有するため、伸長過程の早期においては、第１繊維１自体はそれほど伸びず、編みループ５の曲がりが緩くなることによって緯方向に長くなる。さらに引張力が加えられると、第１繊維１自体が伸び始める。
すなわち、第１繊維１は、２つの段階、すなわち、編みループ５が緩くなる第１段階と、第１繊維１自体が伸びる第２段階とを経て伸長する。そのため、第１繊維１は、第１繊維１自体の伸びが小さいにもかかわらず、編地１０の伸長を妨げることはない。
編地１０は、引張力を弱めると収縮し、図１に示す状態に戻る。この際、コース３は、第１繊維１自体が収縮することに加え、緩くなった編みループ５が回復する動作によって緯方向に収縮する。
このように、コース３は、第１繊維１自体の収縮力だけに頼ることなく収縮することから、編地１０に高い伸長回復性を与えることができる。 As shown in FIG. 2, when a tensile force is applied in the weft direction, the knitted fabric 10 extends in the same direction. At this time, since the course 3 made of the first fibers 1 has the long knitting loops 5, the first fibers 1 themselves do not stretch so much in the early stage of the elongation process, and the bending of the knitting loops 5 becomes loose so that the weft direction. It becomes long. When a tensile force is further applied, the first fiber 1 itself starts to grow.
That is, the first fiber 1 extends through two stages, that is, a first stage in which the knitting loop 5 becomes loose and a second stage in which the first fiber 1 itself extends. Therefore, the first fiber 1 does not hinder the extension of the knitted fabric 10 even though the extension of the first fiber 1 itself is small.
When the tensile force is weakened, the knitted fabric 10 contracts and returns to the state shown in FIG. At this time, the course 3 contracts in the weft direction by the operation of recovering the loosened knitting loop 5 in addition to the contraction of the first fiber 1 itself.
Thus, since the course 3 contracts without relying only on the contraction force of the first fiber 1 itself, it is possible to impart high stretch recovery to the knitted fabric 10.

一方、第２繊維２からなるコース４は、第１繊維１からなるコース３と比較すると、伸長過程の早期から第２繊維２自体が伸び始める。第２繊維２は、弾性繊維を含むため伸びが大きいことから、編地１０の伸長を妨げない。
また、第２繊維２は、第２繊維２自身の弾性により編地１０に伸長回復性を与えている。さらに、第２繊維２は、編みループ６が比較的短いため、伸長時に引張力が第２繊維２に作用しやすいことから、収縮時には高い弾性回復力を発揮する。
このように、編地１０は、引張力が加えられると十分な伸びを示し、かつ、第１繊維１と第２繊維２のそれぞれの作用により伸長回復性が高められている。
したがって、編地１０を用いた衣服は、セルロース繊維によって得られる特性である、吸放湿性、速乾性などに加え、優れたストレッチ性を示す。 On the other hand, compared to the course 3 made of the first fiber 1, the course 4 made of the second fiber 2 starts to elongate from the early stage of the elongation process. Since the second fiber 2 includes elastic fibers and has a large elongation, the second fiber 2 does not prevent the knitted fabric 10 from extending.
Moreover, the 2nd fiber 2 has given the stretch recovery property to the knitted fabric 10 with the elasticity of 2nd fiber 2 itself. Further, since the second fiber 2 has a relatively short knitted loop 6, a tensile force is likely to act on the second fiber 2 when stretched, and thus exhibits a high elastic recovery force when contracted.
Thus, the knitted fabric 10 exhibits sufficient elongation when a tensile force is applied, and the stretch recovery property is enhanced by the action of the first fiber 1 and the second fiber 2.
Accordingly, the garment using the knitted fabric 10 exhibits excellent stretch properties in addition to moisture absorption / release properties, quick drying properties, and the like, which are characteristics obtained by cellulose fibers.

ストレッチ性は、例えば、伸長性と、伸長回復性とを含む。伸長性は、衣服を着用しようとするときに使用者が感じる抵抗に影響を与える。伸長回復性は、使用者が衣服を着用しているときのフィット性に影響を与える。
編地１０を用いた衣服は、ストレッチ性に優れているため、伸長性が高く、かつ伸長回復性も高い。よって、運動時や日常動作時におけるフィット性および動作性に優れ、しかも着用しやすい。
なお、編みループは、繊維がループ状（例えばヘアピン形状、馬蹄形状）に形成された部分である。 The stretchability includes, for example, stretchability and stretch recovery property. Extensibility affects the resistance felt by the user when trying to wear clothes. The stretch recovery property affects the fit when the user is wearing clothes.
Since the garment using the knitted fabric 10 is excellent in stretchability, the stretchability is high and the stretch recovery property is also high. Therefore, it is excellent in fit and operability during exercise and daily operation, and is easy to wear.
The knitted loop is a portion in which fibers are formed in a loop shape (for example, a hairpin shape or a horseshoe shape).

図６〜図９は、衣服の例を示す図である。
図６に示す衣服はタンクトップ２０である。図７に示す衣服はキャミソール３０である。図８に示す衣服はＴシャツ４０である。図９に示す衣服はショーツ５０である。 6 to 9 are diagrams illustrating examples of clothes.
The garment shown in FIG. The garment shown in FIG. The clothes shown in FIG. The clothes shown in FIG. 9 are shorts 50.

図７に示すキャミソール３０は、筒状の本体部３１（筒状部）と、本体部３１の上縁に設けられた肩紐３２とを有する。キャミソール３０は、本体部３１に肩紐３２が縫い付けられた構造である。
本体部３１は、図１等に示す編地１０からなることが好ましい。本体部３１はシームレス形状であることが好ましい。
肩紐３２は、両面平２本針のミシンで縫製すると、平坦に仕上げることができる。 The camisole 30 shown in FIG. 7 includes a cylindrical main body 31 (cylindrical portion) and a shoulder strap 32 provided on the upper edge of the main body 31. The camisole 30 has a structure in which a shoulder strap 32 is sewn to the main body 31.
The main body 31 is preferably made of the knitted fabric 10 shown in FIG. The main body 31 is preferably seamless.
The shoulder strap 32 can be finished flat when it is sewn with a double-sided flat needle sewing machine.

図８に示すＴシャツ４０は、筒状の本体部４１（筒状部）と、本体部４１の両側部に設けられた袖部４２とを有する。Ｔシャツ４０は、本体部４１に袖部４２が縫い付けられた構造である。
本体部４１および袖部４２は、図１等に示す編地１０からなることが好ましい。本体部４１はシームレス形状であることが好ましい。 A T-shirt 40 shown in FIG. 8 has a cylindrical main body portion 41 (tubular portion) and sleeve portions 42 provided on both side portions of the main body portion 41. The T-shirt 40 has a structure in which a sleeve portion 42 is sewn to a main body portion 41.
The main body 41 and the sleeve 42 are preferably made of the knitted fabric 10 shown in FIG. The main body 41 is preferably seamless.

図９に示すショーツ５０は、筒状の本体部５１（筒状部）と、マチ部５２と、本体部５１の上縁に設けられた胴縁部５３と、脚開口部５６の周縁前部に設けられた前脚縁部５４と、脚開口部５６の周縁後部に設けられた後脚縁部５５とを有する。
ショーツ５０は、本体部５１とマチ部５２と胴縁部５３と前脚縁部５４と後脚縁部５５とが組み合わされて縫製された構造である。
本体部５１およびマチ部５２は、図１等に示す編地１０からなることが好ましい。本体部５１はシームレス形状であることが好ましい。 A shorts 50 shown in FIG. 9 includes a cylindrical main body 51 (cylindrical portion), a gusset 52, a trunk edge 53 provided on the upper edge of the main body 51, and a front edge of the leg opening 56. And a rear leg edge 55 provided at the rear edge of the peripheral edge of the leg opening 56.
The shorts 50 has a structure in which a main body portion 51, a gusset portion 52, a trunk edge portion 53, a front leg edge portion 54, and a rear leg edge portion 55 are combined and sewn.
The main body 51 and the gusset 52 are preferably made of the knitted fabric 10 shown in FIG. The main body 51 is preferably seamless.

胴縁部５３は、かがり縫いによって本体部５１の上縁に縫付けされていることが好ましい。前脚縁部５４および後脚縁部５５は、かがり縫いによって本体部５１の脚開口部５６の周縁後部に縫付けされていることが好ましい。かがり縫いを採用すると縫い目が露出しないため、美観の点で好ましい。
胴縁部５３、前脚縁部５４および後脚縁部５５にはリブ編みを採用することができる。これによって、胴縁部５３、前脚縁部５４および後脚縁部５５の伸縮性を高めることができる。
前脚縁部５４および後脚縁部５５には、脚開口部５６の周縁部を折り返し、帯状の折り返し部分を本体部５１に縫い付けた構造を採用することもできる。これによって、胴縁部５３、前脚縁部５４および後脚縁部５５の耐久性を高めることができる。
マチ部５２と本体部５１との継目部分にはフラットシーマによる縫付けを採用できる。これによって、マチ部５２と本体部５１との継目部分に段差が生じず、使用者の肌への圧迫を小さくできる。 The trunk edge portion 53 is preferably sewn to the upper edge of the main body portion 51 by overlock stitching. The front leg edge portion 54 and the rear leg edge portion 55 are preferably sewn to the rear edge of the peripheral edge of the leg opening 56 of the main body 51 by overlock stitching. Adopting overlock stitching is preferable in terms of aesthetics because the seam is not exposed.
Rib knitting can be used for the trunk edge 53, the front leg edge 54 and the rear leg edge 55. Thereby, the stretchability of the trunk edge 53, the front leg edge 54, and the rear leg edge 55 can be enhanced.
The front leg edge portion 54 and the rear leg edge portion 55 may employ a structure in which the peripheral edge portion of the leg opening 56 is folded back and a belt-like folded portion is sewn to the main body portion 51. Thereby, durability of the trunk edge part 53, the front leg edge part 54, and the rear leg edge part 55 can be improved.
The seam between the gusset portion 52 and the main body 51 can be sewn with a flat seam. Thereby, no step is produced at the joint between the gusset part 52 and the main body part 51, and the pressure on the user's skin can be reduced.

編地１０はストレッチ性に優れているため、幅広い形状の衣服においてフィット性を高めることができる。例えば図９に示すショーツ５０などでは、編地１０を湾曲させた形状で使用することがあるが、そのような形状であっても、高いフィット性を衣服に与えることができる。 Since the knitted fabric 10 is excellent in stretchability, the fitting property can be enhanced in a wide range of clothes. For example, in the shorts 50 shown in FIG. 9 or the like, the knitted fabric 10 may be used in a curved shape, but even with such a shape, high fit can be given to the clothes.

以下、実施例を具体的に説明するが、本発明は以下に示す実施例のみに限定されない。まず、各特性の測定方法について説明する。以下に示す編地試料とは、後述の方法により作製したシームレス形状の編地から切り取ったものである。 Hereinafter, although an Example is described concretely, this invention is not limited only to the Example shown below. First, a method for measuring each characteristic will be described. The knitted fabric sample shown below is cut from a seamless knitted fabric produced by the method described later.

（１）吸放湿性
（１−１）吸湿性
あらかじめ質量を測定した編地試料を、温度２０℃、湿度２０％の低湿環境から、温度２０℃、湿度９０％の高湿環境下に移し、３時間放置した後、編地試料の質量を測定した。質量の測定値に基づいて吸湿率を算出した。
（１−２）放湿性
あらかじめ質量を測定した編地試料を、温度２０℃、湿度９０％の高湿環境から、温度２０℃、湿度２０％の低湿環境下に移し、３時間放置した後、編地試料の質量を測定した。質量の測定値に基づいて放湿率を算出した。
結果を図１０に示す。 (1) Hygroscopicity (1-1) Hygroscopicity A knitted fabric sample whose mass has been measured in advance is transferred from a low humidity environment at a temperature of 20 ° C. and a humidity of 20% to a high humidity environment at a temperature of 20 ° C. and a humidity of 90%. After standing for 3 hours, the mass of the knitted fabric sample was measured. The moisture absorption rate was calculated based on the measured value of mass.
(1-2) Moisture release The knitted fabric sample whose mass was measured in advance was transferred from a high humidity environment at a temperature of 20 ° C. and a humidity of 90% to a low humidity environment at a temperature of 20 ° C. and a humidity of 20%, and left for 3 hours. The mass of the knitted fabric sample was measured. The moisture release rate was calculated based on the measured value of mass.
The results are shown in FIG.

（２）通気性
編地試料の通気度を、通気性Ａ法（フラジール法）（ＪＩＳＬ１０９６）に準じて測定した。
結果を図１１に示す。 (2) Air permeability The air permeability of the knitted fabric sample was measured according to air permeability A method (Fragile method) (JIS L1096).
The results are shown in FIG.

（３）速乾性
温度２０℃、湿度６５％の環境下で編地試料に０．３ｍｌの水を滴下し、残留水分率が３０％に到達するまでの時間を測定した。残留水分率は、編地の質量に基づいて算出した。
結果を図１２に示す。 (3) Quick-drying 0.3 ml of water was dropped onto the knitted fabric sample in an environment of a temperature of 20 ° C. and a humidity of 65%, and the time until the residual moisture content reached 30% was measured. The residual moisture content was calculated based on the mass of the knitted fabric.
The results are shown in FIG.

（４）肌触り
静・動摩擦測定器ＴＬ２０１Ｔｓ（株式会社トリニティーラボ製、テーブル揺動型）を用いた試験を行った。
幅５ｃｍ、長さ（タテ）２５ｃｍにカットした編地試料を、肌にあたる面を上にして、錐を用いて編地試料を２％伸長させた状態で測定機に固定した。接触子として、１．５ｃｍ^２の触覚接触子（指先相当の硬度を有した接触子）を用い、ここに３．７５ｇの荷重をかけ１０ｃｍの移動距離で３往復させた。移動距離は３０ｍｍ／ｓとした。３往復分の両方向の摩擦それぞれについて、１０ｃｍ移動内の最大動摩擦係数、動摩擦係数の標準偏差を求めた。往／復、それぞれの方向で３往復分の値の平均値を算出し、当該評価値とした。
結果を図１３に示す。 (4) Touch A test using a static / dynamic friction measuring instrument TL201Ts (manufactured by Trinity Lab Co., Ltd., table swing type) was performed.
A knitted fabric sample cut to a width of 5 cm and a length (vertical) of 25 cm was fixed to a measuring machine with the surface corresponding to the skin facing up and the knitted fabric sample extended by 2% using a cone. A 1.5 cm ² tactile contact (contact having hardness equivalent to a fingertip) was used as a contact, and a load of 3.75 g was applied to the contact, and the contact was reciprocated three times at a moving distance of 10 cm. The moving distance was 30 mm / s. The maximum dynamic friction coefficient within a 10 cm movement and the standard deviation of the dynamic friction coefficient were determined for each of three reciprocal frictions. The average value of the values for three round trips in each direction was calculated and used as the evaluation value.
The results are shown in FIG.

（５）接触冷温感
温度２０℃、湿度６５％ＲＨの環境下で編地試料を発泡スチロール製の断熱材上に置き、３０℃の熱板兼温度センサーを接触させ、最大瞬間熱流束量（Ｗ／ｃｍ²・１０℃）を測定した。
測定は、試料の表面および裏面についてそれぞれ行った。結果を図１４に示す。 (5) Feeling of coldness of contact Place the knitted fabric sample on a foamed polystyrene insulation in an environment of temperature 20 ° C and humidity 65% RH, and contact a 30 ° C hot plate / temperature sensor to obtain the maximum instantaneous heat flux (W / Cm ² · 10 ° C.).
The measurement was performed on the front and back surfaces of the sample. The results are shown in FIG.

（６）ストレッチ性
（６−１）伸長性
編地試料（２００ｍｍ×２００ｍｍ）を、２カ所で把持し（把持間隔５０ｍｍ）、引張力を加え、最大荷重時の伸長率を測定した。
引張速度は０．１ｍｍ／ｓｅｃとした。引張伸量は５０ｍｍ／１０Ｖとした。引張最大荷重は１ｋｇｆ（５０ｇｆ／ｃｍ）とした。測定は温度２０℃、湿度６５％ＲＨの環境で行った。測定は、縦方向（経方向）および横方向（緯方向）について行った。
結果を図１５に示す。 (6) Stretchability (6-1) Stretchability A knitted fabric sample (200 mm × 200 mm) was gripped at two locations (grip interval 50 mm), a tensile force was applied, and the stretch rate at the maximum load was measured.
The tensile speed was 0.1 mm / sec. The tensile elongation was 50 mm / 10V. The maximum tensile load was 1 kgf (50 gf / cm). The measurement was performed in an environment of a temperature of 20 ° C. and a humidity of 65% RH. The measurement was performed in the vertical direction (longitudinal direction) and the horizontal direction (weft direction).
The results are shown in FIG.

（６−２）伸長回復性
編地試料の経方向及び緯方向の引張試験（ＪＩＳ−Ｌ−１０９６に準ずる）において、伸長率８０％までの繰返し伸長回復における往路応力及び復路応力を測定して得られた伸長回復曲線から３回伸長回復後の残留伸び（％）を読み取り、下記式（Ａ）：
伸長回復率（％）＝｛［（８０−（残留伸び））÷８０］×１００（Ａ）
により算出した。
結果を表１に示す。 (6-2) Elongation recovery property In the tensile test in the warp and weft directions of the knitted fabric sample (according to JIS-L-1096), the outward stress and the return stress in repeated elongation recovery up to an elongation rate of 80% were measured. From the obtained elongation recovery curve, the residual elongation (%) after recovery from stretching three times was read, and the following formula (A):
Elongation recovery rate (%) = {[(80− (residual elongation)) ÷ 80] × 100 (A)
Calculated by
The results are shown in Table 1.

（７）着用試験
図９に示すショーツ５０を作製した。
着用モニター（身長１６０ｃｍ±１０ｃｍの女性、年齢２０代〜６０代）５０人にショーツ５０を着用させ、着用感（肌触り・快適さ・涼しさ等）、およびサイズ感（フィット性）について評価させた。また、着用モニターには、洗濯後のショーツ５０の形状変化を評価させた。 (7) Wear test The shorts 50 shown in FIG. 9 was produced.
Wearing monitors (female 160cm ± 10cm, age 20s-60s) 50 people wore shorts 50 and evaluated their feeling of wear (feel, comfort, coolness, etc.) and size (fitness). . Moreover, the wear monitor evaluated the change in the shape of the shorts 50 after washing.

［実施例１］
第１繊維としては、５６ｄｔｅｘ４５ｆのキュプラ糸（旭化成せんい社製、ベンベルグ（登録商標））と２１ｄｔｅｘ２０ｆの６６ナイロン糸とを含む主繊維と、２２ｄｔｅｘナイロン糸からなる副繊維とを引きそろえた複合繊維を用いた。主繊維の糸長は３００ｍｍ〜３１０ｍｍとし、副繊維の糸長は３３０ｍｍ〜３４５ｍｍとした。
第２繊維としては、３３ｄｔｅｘのポリウレタン弾性糸と、３３ｄｔｅｘのナイロン糸とを含む複合繊維を用いた。第２繊維の糸長は３２０ｍｍ〜３４ｍｍとした。
Ｓａｎｔｏｎｉ社製のＴＯＰ２Ｓ編機（２８ゲージ）を使って、第１繊維と第２繊維とからなる天竺組織の編地を得た。加工のプレセット温度は約９５℃、時間は２０分とした。
編地はシームレス形状であり、第１繊維からなる１つのコースと、第２繊維からなる１つのコースとを経方向に繰り返して編成した。
図９に示すように、この編地を用いてシームレス形状の本体部５１と、マチ部５２とを作製し、これらを縫製してショーツ５０を得た。ショーツ５０において、第１繊維からなるコースの編みループが、第２繊維からなるコースの編みループに比べて長いことを確認した。 [Example 1]
As the first fiber, a composite fiber in which main fibers including 56 dtex 45f cupra yarn (manufactured by Asahi Kasei Fibers Co., Ltd., Bemberg (registered trademark)) and 21 dtex 20f 66 nylon yarn and auxiliary fibers made of 22 dtex nylon yarn are arranged. Using. The yarn length of the main fiber was 300 mm to 310 mm, and the yarn length of the sub fiber was 330 mm to 345 mm.
As the second fiber, a composite fiber containing 33 dtex polyurethane elastic yarn and 33 dtex nylon yarn was used. The yarn length of the second fiber was 320 mm to 34 mm.
Using a TOP2S knitting machine (28 gauge) manufactured by Santoni, a knitted fabric having a tentacle structure composed of first fibers and second fibers was obtained. The processing preset temperature was about 95 ° C. and the time was 20 minutes.
The knitted fabric has a seamless shape, and was knitted by repeating one course made of the first fibers and one course made of the second fibers in the warp direction.
As shown in FIG. 9, a seamless-shaped main body 51 and a gusset portion 52 were produced using the knitted fabric, and these were sewn to obtain a shorts 50. In the shorts 50, it was confirmed that the knitting loop of the course made of the first fiber was longer than the knitting loop of the course made of the second fiber.

［実施例２］
第１繊維としては、６６ｄｔｅｘ４３ｆのキュプラ糸（旭化成せんい社製、ベンベルグ（登録商標））と３６ｄｔｅｘ２６ｆの６ナイロン糸とを含む主繊維と、２２ｄｔｅｘナイロン糸からなる副繊維とを引きそろえた複合繊維を用いた。
第２繊維としては、３３ｄｔｅｘのポリウレタン弾性糸と、３３ｄｔｅｘのナイロン糸とを含む複合繊維を用いた。
第１繊維と第２繊維とを用いて、実施例１と同様にして、天竺組織の編地を得た。編地は、第１繊維からなる１つのコースと、第２繊維からなる１つのコースとを経方向に繰り返して編成した。他の条件は実施例１と同様とした。
この編地を用いて、実施例１と同様にしてショーツ５０を作製した。ショーツ５０において、第１繊維からなるコースの編みループが、第２繊維からなるコースの編みループに比べて長いことを確認した。 [Example 2]
As the first fiber, a composite fiber in which a main fiber including 66 dtex 43f cupra yarn (manufactured by Asahi Kasei Fibers Co., Ltd., Bemberg (registered trademark)) and 36 dtex 26f 6 nylon yarn, and a secondary fiber made of 22 dtex nylon yarn are arranged. Using.
As the second fiber, a composite fiber containing 33 dtex polyurethane elastic yarn and 33 dtex nylon yarn was used.
Using a first fiber and a second fiber, a knitted fabric having a tentacle structure was obtained in the same manner as in Example 1. The knitted fabric was knitted by repeating one course made of the first fibers and one course made of the second fibers in the warp direction. Other conditions were the same as in Example 1.
Using this knitted fabric, a shorts 50 was produced in the same manner as in Example 1. In the shorts 50, it was confirmed that the knitting loop of the course made of the first fiber was longer than the knitting loop of the course made of the second fiber.

［比較例１］
第１繊維は、１１０ｄｔｅｘ７２ｆのポリエステル糸と２２ｄｔｅｘのナイロン糸とを含む主繊維と、副繊維とを引きそろえた複合繊維とした。副繊維は、３３ｄｔｅｘのポリウレタン弾性糸と３３ｄｔｅｘのナイロン糸とを含む複合繊維とした。
第１繊維のみを用いて、天竺組織の編地を作製した。他の条件は実施例１と同様とした。この編地を用いて、実施例１と同様にしてショーツを作製した。 [Comparative Example 1]
The first fiber was a composite fiber in which a main fiber including a 110 dtex 72f polyester yarn and a 22 dtex nylon yarn and a sub fiber were gathered. The secondary fiber was a composite fiber containing a 33 dtex polyurethane elastic yarn and a 33 dtex nylon yarn.
Using only the first fibers, a knitted fabric with a tengu structure was produced. Other conditions were the same as in Example 1. Using this knitted fabric, shorts were produced in the same manner as in Example 1.

［比較例２］
ポリエステル糸とナイロン糸とを含む主繊維に代えて、１１０ｄｔｅｘ９６ｆのナイロン糸と２２ｄｔｅｘナイロン糸とを含む主繊維を用いたこと以外は比較例１と同様にして編地を作製した。この編地を用いて、実施例１と同様にしてショーツを作製した。 [Comparative Example 2]
A knitted fabric was prepared in the same manner as in Comparative Example 1 except that a main fiber containing 110 dtex 96f nylon yarn and 22 dtex nylon yarn was used instead of the main fiber containing polyester yarn and nylon yarn. Using this knitted fabric, shorts were produced in the same manner as in Example 1.

［比較例３］
第１繊維は、６６ｄｔｅｘ４３ｆのキュプラ糸（旭化成せんい社製、ベンベルグ（登録商標））と３６ｄｔｅｘ２６ｆの６ナイロン糸とを含む主繊維とし、第２繊維は８３ｄｔｅｘ６８ｆの６ナイロン糸とした。
ポリウレタン弾性繊維は２２ｄｔｅｘを用いた。
編機はＳａｎｔｏｎｉ社製の開反丸編機ＰＡＮＤＡ（２８ゲージ）を使って、第１繊維と第２繊維を経方向に交互に繰り返し、ポリウレタン弾性繊維は全てのコースに用い、ベア天竺組織の編地を得た。糸長は第１繊維、第２繊維とも２８０ｍｍ／１００Ｗとし、ポリウレタン弾性繊維のドラフト設定は２．５とした。
この開反された生機をプレウェット後に１９８℃×７２秒の条件下で熱セットし、染色及び仕上げ加工し生地を得た。
この生地を裁断、縫製して、実施例１と同じ型のショーツを得た。
このショーツにおいて、第１繊維からなるコースの編みループの大きさが第２繊維からなるコースの編みループの大きさに比べて差がないことを確認した。 [Comparative Example 3]
The first fiber was a main fiber including 66 dtex 43f cupra yarn (Asahi Kasei Fibers, Bemberg (registered trademark)) and 36 dtex 26f 6 nylon yarn, and the second fiber was 83 dtex 68f 6 nylon yarn.
The polyurethane elastic fiber used was 22 dtex.
The knitting machine uses the Santoni open knitting machine PANDA (28 gauge), the first fiber and the second fiber are alternately repeated in the warp direction, and the polyurethane elastic fiber is used for all courses. I got a knitted fabric. The yarn length was 280 mm / 100 W for both the first fiber and the second fiber, and the draft setting of the polyurethane elastic fiber was 2.5.
The opened machine was heat-set under conditions of 198 ° C. × 72 seconds after prewetting, and dyed and finished to obtain a fabric.
The fabric was cut and sewn to obtain the same type of shorts as in Example 1.
In this shorts, it was confirmed that the size of the knitting loop of the course made of the first fiber was not different from the size of the knitting loop of the course made of the second fiber.

着用試験の結果、８０％以上の着用モニターは、着用感（肌触り・快適さ・涼しさ等）について、実施例１，２は比較例１，２と同等または比較例１，２より優れていると回答した。また、サイズ感（フィット性）については、８０％以上の着用モニターは、実施例１，２は比較例１，２に比べてそれほど劣らないと回答した。
また、８０％以上の着用モニターは、洗濯後のショーツ５０の形状変化について、実施例１，２は比較例１，２と同等または比較例１，２より優れていると回答した。
また、８０％以上の着用モニターは、肌触りについて、実施例１，２は比較例３よりも優れていると回答した。
なお、快適さおよび涼しさは、吸放湿性および速乾性と関係があると考えられる。着用感には伸長性が影響していると考えられる。 As a result of the wearing test, Examples 1 and 2 are equivalent to Comparative Examples 1 and 2 or superior to Comparative Examples 1 and 2 in terms of wearing feeling (feel, comfort, coolness, etc.) of 80% or more of wearing monitors. I replied. Moreover, about a feeling of size (fitness), 80% or more of the wear monitors answered that Examples 1 and 2 were not so inferior to Comparative Examples 1 and 2.
Moreover, 80% or more of the wear monitors answered that Examples 1 and 2 are equivalent to Comparative Examples 1 and 2 or superior to Comparative Examples 1 and 2 in terms of the shape change of the shorts 50 after washing.
Moreover, 80% or more of the wear monitors answered that Examples 1 and 2 were superior to Comparative Example 3 in terms of touch.
Comfort and coolness are considered to be related to moisture absorption and desorption and quick drying. It is considered that stretchability has an influence on the feeling of wearing.

図１０〜図１５に示すように、実施例１，２では、比較例１〜３に比べ、吸放湿性、速乾性、ストレッチ性（伸長性）などにおいて同等以上の結果が得られた。
また、表１に示すように、実施例１，２では、比較例１〜３に比べ、伸長回復性においても遜色ない結果が得られた。
このように、実施例１，２は、吸放湿性、速乾性などの特性に加え、優れたストレッチ性を示した。
また、着用試験の結果より、実施例１，２は、着用感（肌触り・快適さ・涼しさ等）について比較例１，２と同等以上であり、サイズ感（フィット性）の点でも比較例１，２に劣らないことがわかった。さらに実施例１，２は、肌触りの点で比較例３よりも優れることがわかった。また、実施例１，２は、洗濯後の形状変化も少なかった。 As shown in FIGS. 10 to 15, in Examples 1 and 2, compared with Comparative Examples 1 to 3, results equivalent to or higher in moisture absorption / release properties, quick drying properties, stretch properties (extendability), and the like were obtained.
Moreover, as shown in Table 1, in Examples 1 and 2, compared with Comparative Examples 1 to 3, a result comparable to that in stretch recovery was obtained.
As described above, Examples 1 and 2 exhibited excellent stretch properties in addition to properties such as moisture absorption / release properties and quick drying properties.
Moreover, from the result of the wearing test, Examples 1 and 2 are equal to or better than Comparative Examples 1 and 2 in terms of wearing feeling (feel, comfort, coolness, etc.), and are comparative examples in terms of size (fitness). It turned out that it is not inferior to 1 and 2. Further, Examples 1 and 2 were found to be superior to Comparative Example 3 in terms of touch. In Examples 1 and 2, the shape change after washing was small.

以上、本発明の実施形態について図面を参照して詳述したが、具体的な構成はこの実施形態に限られるものではなく、本発明の要旨を逸脱しない範囲の設計変更等も含まれる。
例えば、図１、図４および図５には、第１繊維１からなる１〜３つのコース３と、第２繊維２からなる１つのコース４とが、経方向に繰り返されて編成された編地１０，１０Ａ，１０Ｂを開示したが、一つの繰り返し単位における各コースの数は、これに限定されない。例えば、第１繊維からなるコースの数Ｎ１と、第２繊維からなるコースの数Ｎ２は、１：複数（例えば１：２）であってもよいし、複数：複数（例えば３：２）であってもよい。 As mentioned above, although embodiment of this invention was explained in full detail with reference to drawings, the concrete structure is not restricted to this embodiment, The design change etc. of the range which does not deviate from the summary of this invention are included.
For example, in FIGS. 1, 4, and 5, a knitted fabric in which 1 to 3 courses 3 made of the first fibers 1 and one course 4 made of the second fibers 2 are repeatedly knitted in the warp direction. Although the grounds 10, 10A, and 10B have been disclosed, the number of courses in one repeating unit is not limited to this. For example, the number N1 of courses made of the first fibers and the number N2 of courses made of the second fibers may be 1: plural (for example, 1: 2), or plural: plural (for example, 3: 2). There may be.

１…第１繊維、２…第２繊維、３…第１繊維からなるコース、４…第２繊維からなるコース、５…第１繊維の編みループ、６…第２繊維の編みループ、Ｌ１…第１繊維の編みループの径方向寸法、Ｌ２…第２繊維の編みループの径方向寸法。 DESCRIPTION OF SYMBOLS 1 ... 1st fiber, 2 ... 2nd fiber, 3 ... Course consisting of 1st fiber, 4 ... Course consisting of 2nd fiber, 5 ... Knitting loop of 1st fiber, 6 ... Knitting loop of 2nd fiber, L1 ... The radial dimension of the knitted loop of the first fiber, L2 ... the radial dimension of the knitted loop of the second fiber.

Claims

セルロース繊維を含む第１繊維からなる１または複数のコースと、弾性繊維を含む第２繊維からなる１または複数のコースとが、経方向に繰り返されて編成された編地を含み、
前記第１繊維からなるコースの編みループ長は、前記第２繊維からなるコースの編みループ長より長い、衣服。 Including a knitted fabric in which one or more courses made of first fibers containing cellulose fibers and one or more courses made of second fibers containing elastic fibers are repeatedly knitted in the warp direction,
The knitting loop length of the course made of the first fiber is longer than the knitting loop length of the course made of the second fiber.

前記セルロース繊維は、長繊維である、請求項１に記載の衣服。 The garment according to claim 1, wherein the cellulose fibers are long fibers.

前記セルロース繊維は、再生セルロース繊維である、請求項１または２に記載の衣服。 The garment according to claim 1 or 2, wherein the cellulose fibers are regenerated cellulose fibers.

前記セルロース繊維は、キュプラである、請求項１〜３のうちいずれか１項に記載の衣服。 The garment according to any one of claims 1 to 3, wherein the cellulose fiber is a cupra.

前記弾性繊維は、ポリウレタン弾性糸である、請求項１〜４のうちいずれか１項に記載の衣服。 The garment according to any one of claims 1 to 4, wherein the elastic fiber is a polyurethane elastic yarn.

前記編地は、前記第１繊維からなる１〜３つのコースと、前記第２繊維からなる１つのコースとが、経方向に繰り返されて編成されている、請求項１〜５のうちいずれか１項に記載の衣服。 The knitted fabric is knitted by repeating one to three courses made of the first fibers and one course made of the second fibers in the warp direction. Clothing according to item 1.

前記第１繊維からなるコースの編みループは、前記第２繊維からなるコースの編みループに比べて経方向の寸法が大きい、請求項１〜６のうちいずれか１項に記載の衣服。 The garment according to any one of claims 1 to 6, wherein the knitted loop of the course made of the first fibers has a larger dimension in the warp direction than the knitted loop of the course made of the second fibers.

筒状部を有し、前記筒状部がシームレス形状である、請求項１〜７のうちいずれか１項に記載の衣服。 The garment according to any one of claims 1 to 7, wherein the garment has a tubular portion, and the tubular portion has a seamless shape.

前記編地は、天竺組織である、請求項１〜８のうちいずれか１項に記載の衣服。 The knitted fabric according to any one of claims 1 to 8, wherein the knitted fabric is a tengu tissue.

インナーウェアである、請求項１〜９のうちいずれか１項に記載の衣服。 The garment according to any one of claims 1 to 9, wherein the garment is innerwear.