JP2017114819A - Oily solid cosmetics - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide oily solid cosmetics having excellent spreadability while having a mat texture.SOLUTION: The oily solid cosmetics comprise following components (A)-(C): (A) kaolinite of 15-30 mass%, (B) spherical silica, and (C) dimethyl polysiloxane with an average molecular weight of 500-1500.SELECTED DRAWING: None

Description

本発明は、油性固形化粧料に関する。   The present invention relates to an oily solid cosmetic.

従来から油性固形化粧料は、口紅やリップグロス等の***化粧料に広く用いられており、一般的に塗布時の使用感については、均一で伸び広がりの良好な感触が求められている。一方、仕上がりについては、近年ニーズが多様化し、不自然なツヤ感が出ないマットな質感に仕上がることが求められてきている。   Conventionally, oily solid cosmetics have been widely used in lip cosmetics such as lipsticks and lip glosses, and in general, the feeling of use at the time of application is required to be uniform and have a good spread. On the other hand, with respect to the finish, the needs have been diversified in recent years, and it has been demanded that the finish should have a matte texture that does not give an unnatural luster.

例えば、伸び広がりを向上させる技術としては、平均分子量５００〜３０００のポリエチレンワックス、凝固点−１０℃以下の脂肪酸２−オクチルドデカノールエステル、顔料を用いる技術（特許文献１）、マットな質感を向上させる技術としては、多孔性無機粉体、架橋型オルガノポリシロキサン、着色無機顔料を内包するポリマーを用いる技術（特許文献２）等が検討されてきた。   For example, as a technique for improving the spread of spread, a technique using a polyethylene wax having an average molecular weight of 500 to 3000, a fatty acid 2-octyldodecanol ester having a freezing point of −10 ° C. or lower, and a pigment (Patent Document 1), a matte texture is improved. As a technique, a technique using a porous inorganic powder, a crosslinked organopolysiloxane, a polymer containing a colored inorganic pigment (Patent Document 2), and the like has been studied.

しかしながら、特許文献１の技術では、凝固点−１０℃以下の脂肪酸２−オクチルドデカノールエステル由来の油特有のツヤ感が出てしまい、満足のいくマットな質感が得られていなかった。また、特許文献２の技術では、マットな質感は得られるものの、多孔性無機粉体由来のざらつき感が出てしまい、満足のいく伸び広がりが得られていなかった。   However, in the technique of Patent Document 1, a gloss feeling peculiar to oil derived from fatty acid 2-octyldodecanol ester having a freezing point of −10 ° C. or lower was obtained, and a satisfactory matte texture was not obtained. Further, in the technique of Patent Document 2, although a matte texture is obtained, a rough feeling derived from the porous inorganic powder is produced, and a satisfactory expansion and spread cannot be obtained.

特開平６−１９９６３１号公報JP-A-6-199631 特開２０１４−２１４１２８号公報JP 2014-214128 A

すなわち本発明は、マットな質感がありながらも、伸び広がりに優れた油性固形化粧料を提供することを課題とするものである。   That is, an object of the present invention is to provide an oily solid cosmetic material that has a matte texture and is excellent in stretch spread.

本発明者らは、上記実情に鑑み、鋭意研究を行った結果、粒子の表面に凹凸を有するカオリナイトが光の拡散反射を起こすことに着目し、油性固形化粧料にカオリナイトを含有したところ、含有量が１５〜３０質量％の範囲において、マットな質感を具現化できることを見出した。さらに、透明性が高く伸展性に優れた球状シリカと表面張力が低くさらさらとした感触を有する平均分子量が５００〜１５００であるジメチルポリシロキサンを組み合わせたところ、マットな質感を有しながら、塗布時の伸び広がりが良好で、さらには発色が良く、排液等の安定性にも優れる油性固形化粧料が得られることを見出し、本発明を完成させるに至った。   As a result of earnest research in view of the above circumstances, the present inventors have focused on the fact that kaolinite having irregularities on the surface of the particles causes diffuse reflection of light, and the oily solid cosmetic contains kaolinite. The present inventors have found that a matte texture can be realized when the content is in the range of 15 to 30% by mass. Furthermore, when spherical silica with high transparency and excellent extensibility and dimethylpolysiloxane with an average molecular weight of 500-1500 having a low surface tension and a dry feel are combined, it has a matte texture while being applied. The present invention was completed by finding that an oily solid cosmetic material having a good elongation spread, good color development and excellent stability of drainage can be obtained.

次の成分（Ａ）〜（Ｃ）；
（Ａ）カオリナイト １５〜３０質量％
（Ｂ）球状シリカ
（Ｃ）平均分子量が５００〜１５００であるジメチルポリシロキサン
を含有する油性固形化粧料に関する。 The following components (A) to (C);
(A) Kaolinite 15-30% by mass
(B) Spherical silica (C) It is related with the oil-based solid cosmetics containing dimethylpolysiloxane whose average molecular weight is 500-1500.

本発明の油性固形化粧料は、マットな質感がありながらも、伸び広がりに優れ、さらには発色が良く、排液等の安定性にも優れるものである。   The oily solid cosmetic of the present invention has a matte texture, but is excellent in spreading and spreading, and also has good color development and excellent stability such as drainage.

本発明の詳細について以下に説明する。なお、本明細書において、「〜」はその前後の数値を含む範囲を意味するものとする。   Details of the present invention will be described below. In the present specification, “to” means a range including numerical values before and after.

本発明における成分（Ａ）カオリナイトは、酸化アルミニウム・二酸化ケイ素を主成分とする粘土鉱物のひとつである。化粧品表示名称で表すと、「カオリン」であり、製造方法の違いにより、湿式カオリン、焼成カオリン、乾式カオリン等がある。成分（Ａ）カオリナイトは、化粧料に用いられるものであれば、特に限定されないが、平均粒子径は０．１〜１０．０μｍが好ましい。この範囲であれば、油性固形化粧料の使用時の伸び広がり、マットな質感、排液等の安定性等に優れる点でより好ましい。市販品としては、ホワイトクレイ（Ａｌｂａｎ Ｍｕｌｌｅｒ Ｉｎｔｅｒｎａｔｉｏｎａｌ社製）、日本薬局法カオリン ＪＰ−１００（竹原化学工業社製）等が挙げられる。   The component (A) kaolinite in the present invention is one of clay minerals mainly composed of aluminum oxide and silicon dioxide. It is “kaolin” in terms of a cosmetic label, and there are wet kaolin, calcined kaolin, dry kaolin and the like depending on the production method. Although a component (A) kaolinite will not be specifically limited if it is used for cosmetics, As for an average particle diameter, 0.1-10.0 micrometers is preferable. If it is this range, it is more preferable at the point which is excellent in stability at the time of use at the time of use of oil-based solid cosmetics, matte texture, drainage, etc. Examples of commercially available products include white clay (manufactured by Alba Muller International), Japanese pharmacy method Kaolin JP-100 (manufactured by Takehara Chemical Industry Co., Ltd.), and the like.

成分（Ａ）の含有量は、１５〜３０質量％（以下単に「％」と記す）であるが、更に好ましくは１８〜２５％である。この範囲であれば、油性固形化粧料の使用時の伸び広がり、マットな質感、排液等の安定性等に優れる点でより好ましい。   The content of the component (A) is 15 to 30% by mass (hereinafter simply referred to as “%”), and more preferably 18 to 25%. If it is this range, it is more preferable at the point which is excellent in stability at the time of use at the time of use of oil-based solid cosmetics, matte texture, drainage, etc.

本発明の成分（Ｂ）球状シリカは、形状が球状の二酸化ケイ素であり、化粧料に一般的に用いられるものであれば、無孔質、多孔質、中空等の形状のいずれでも良い。成分（Ｂ）球状シリカは特に限定されないが、平均粒子径１．０〜３０．０μｍが好ましく、更に好ましくは５．０〜１７．０μｍで ある。この範囲であれば、油性固形化粧料の使用時の伸び広がり、マットな質感等が優れる点でより好ましい。また、これらは疎水化処理したものであってもよく、疎水化処理してはジメチルジクロロシラン処理、トリメチルシリルクロライドやヘキサメチルジシラザンによるトリメチルシロキシ処理、オクチルシラン化処理、ジメチルシリコーンオイル処理、メチルハイドロジェンポリシロキサンを用いたコーティング焼付け処理、金属石鹸によるコーティング等が挙げられる。   The component (B) spherical silica of the present invention is a silicon dioxide having a spherical shape, and may be any shape such as nonporous, porous and hollow as long as it is generally used in cosmetics. The component (B) spherical silica is not particularly limited, but preferably has an average particle size of 1.0 to 30.0 μm, more preferably 5.0 to 17.0 μm. If it is this range, it is more preferable at the point which the expansion | extension spread at the time of use of oil-based solid cosmetics, a mat | matte texture, etc. are excellent. These may be hydrophobized and treated with dimethyldichlorosilane, trimethylsiloxy chloride or hexamethyldisilazane, trimethylsiloxy, octylsilanization, dimethylsilicone oil, methyl hydrolyzate. Examples thereof include a coating baking process using genpolysiloxane and a coating with metal soap.

本発明における成分（Ｂ）球状シリカは、無孔質、多孔質、中空等の形状のいずれでも良いが、好ましくは中空シリカであり、更に好ましくは比重が０．２〜１．０ｇ／ｍＬの中空シリカである。この形状であれば、発色の良さ、および滑らかな伸び広がり等が得られる点でより好ましい。   The component (B) spherical silica in the present invention may have any shape such as nonporous, porous, hollow, etc., preferably hollow silica, and more preferably a specific gravity of 0.2 to 1.0 g / mL. Hollow silica. If it is this shape, it is more preferable at the point from which the favorable color development, smooth expansion spread, etc. are obtained.

本発明の成分（Ｂ）の市販品としては、サンスフェア ＮＰ−３０（ＡＧＣエスアイテック株式会社製）、サンスフェア ＮＰ−１００（ＡＧＣエスアイテック株式会社製）、シリカマイクロビード Ｎ−１５０５（日揮触媒化成株式会社製）、ＳＩＬＩＣＡ ＭＩＣＲＯ ＢＥＡＤ ＢＡ−１（日揮触媒化成株式会社製）等が挙げられ、これら１種又は２種以上用いることができる。   As a commercial item of the component (B) of the present invention, Sunsphere NP-30 (manufactured by AGC S-Tech Co., Ltd.), Sunsphere NP-100 (manufactured by AGC S-Tech Co., Ltd.), silica microbead N-1505 (JGC Catalyst) Kasei Co., Ltd.), SILICA MICRO BEAD BA-1 (manufactured by JGC Catalysts & Chemicals Co., Ltd.) and the like, and one or more of these can be used.

尚、成分（Ａ）と成分（Ｂ）の平均粒子径は、レーザー型乾式粒度分布測定装置（セイシン企業社製ＰＲＯ７０００Ｓ）を用い、体積平均粒子径（Ｄ５０）として測定される。   In addition, the average particle diameter of a component (A) and a component (B) is measured as a volume average particle diameter (D50) using the laser type dry-type particle size distribution measuring apparatus (PRO7000S by Seishin Enterprise Co., Ltd.).

本発明において、成分（Ａ）と成分（Ｂ）は、質量比において（Ａ）：（Ｂ）が１５：１〜１：１で含有されると、油性固形化粧料のマットな質感、使用時の伸び広がり、発色、排液等の安定性等がより優れる点で好ましく、更に好ましくは５：１〜２：１ある。   In the present invention, when the component (A) and the component (B) are contained in a mass ratio of (A) :( B) at 15: 1 to 1: 1, the matte texture of the oily solid cosmetic, when used It is preferable from the viewpoint of more excellent in the stability of spreading, color development, drainage, etc., more preferably 5: 1 to 2: 1.

本発明における成分（Ｃ）の平均分子量が５００〜１５００であるジメチルポリシロキサンとは、化粧料に一般的に使用されるものであれば特に限定されず、１気圧、２５℃で液状のシリコーン油である。化粧品表示名称では「ジメチコン」と表され、ＩＮＣＩ（Ｉｎｔｅｒｎａｔｉｏｎａｌ Ｎｏｍｅｎｃｌａｔｕｒｅ ｏｆ Ｃｏｓｍｅｔｉｃ Ｉｎｇｒｅｄｉｅｎｔｓ）名では「ＤＩＭＥＴＨＩＣＯＮＥ」と表される。市販品としては、ＫＦ−９６Ａ−６ＣＳ（信越化学工業株式会社製）、ＫＦ−５６−１０ＣＳ（信越化学工業株式会社製）、ＳＨ２００Ｃ ＦＬＵＩＤ ６ＣＳ（東レ株式会社製）等が挙げられ、これらの１種又は２種以上を用いることができる。中でも、ＫＦ−９６Ａ−６ＣＳ及びＳＨ２００Ｃ ＦＬＵＩＤ ６ＣＳが好ましく用いられ、ＫＦ−９６Ａ−６ＣＳ及びＳＨ２００Ｃ ＦＬＵＩＤ ６ＣＳを含有すると、油性固形化粧料の使用時の伸び広がり、排液等の安定性が優れる点でより好ましい。   The dimethylpolysiloxane having an average molecular weight of component (C) in the present invention of 500 to 1500 is not particularly limited as long as it is generally used in cosmetics, and is a silicone oil that is liquid at 1 atm and 25 ° C. It is. The cosmetic display name is represented as “dimethicone”, and the INCI (International Nomenclature of Cosmetic Ingredients) name is represented as “DIMETHICONE”. Examples of commercially available products include KF-96A-6CS (manufactured by Shin-Etsu Chemical Co., Ltd.), KF-56-10CS (manufactured by Shin-Etsu Chemical Co., Ltd.), SH200C FLUID 6CS (manufactured by Toray Industries, Inc.), and the like. Species or two or more can be used. Among them, KF-96A-6CS and SH200C FLUID 6CS are preferably used, and when KF-96A-6CS and SH200C FLUID 6CS are contained, the oily solid cosmetic composition is excellent in terms of elongation and stability such as drainage. More preferred.

油性固形化粧料の全液状油中の成分（Ｃ）の含有量は、特に限定されないが、２５％以上が好ましく、更に好ましくは４０〜６５％である。この範囲であれば、油性固形化粧料の使用時の伸び広がり、排液等の安定性等がより優れる点でより好ましい。   Although content of the component (C) in the whole liquid oil of oily solid cosmetics is not specifically limited, 25% or more is preferable, More preferably, it is 40 to 65%. If it is this range, it is more preferable at the point which stability, such as extension spread at the time of use of oil-based solid cosmetics, and drainage, is more excellent.

本発明において、成分（Ａ）と成分（Ｃ）は、質量比において（Ａ）：（Ｃ）が１：３〜２：１で含有されると、油性固形化粧料の使用時の伸び広がり、マットな質感等がより優れる点で好ましく、更に好ましくは１：２〜３：２ある。   In the present invention, when the component (A) and the component (C) are contained at a mass ratio of (A) :( C) of 1: 3 to 2: 1, the elongation at the time of use of the oily solid cosmetic is expanded, It is preferable in terms of more excellent matte texture and the like, and more preferably 1: 2 to 3: 2.

本発明の油性固形化粧料は、上記の成分（Ａ）〜（Ｃ）の他に、通常化粧料に使用される成分、油性成分、無機顔料、有機顔料及び色素等の粉体及びそれらのシリコーン処理物やフッ素化合物処理物、界面活性剤、繊維、多価アルコール、水溶性高分子、水溶性皮膜形成性樹脂、保湿剤等の水性成分、糖類、紫外線吸収剤、褪色防止剤、酸化防止剤、消泡剤、美容成分、防腐剤、香料等を本発明の効果を妨げない範囲で含有することができる。   In addition to the components (A) to (C) described above, the oily solid cosmetic of the present invention includes powders such as components usually used in cosmetics, oily components, inorganic pigments, organic pigments and dyes, and silicones thereof. Treated products, treated with fluorine compounds, surfactants, fibers, polyhydric alcohols, water-soluble polymers, water-soluble film-forming resins, aqueous components such as humectants, sugars, UV absorbers, anti-fading agents, antioxidants Further, an antifoaming agent, a cosmetic ingredient, an antiseptic, a fragrance and the like can be contained as long as the effects of the present invention are not hindered.

油性成分としては、通常化粧料に用いられるものであれば特に限定されず、動物油、植物油、合成油等の起源や固形油、半固形油、液体油、揮発性油等の性状を問わず、炭化水素類、油脂類、ロウ類、硬化油類、エステル油類、脂肪酸類、高級アルコール類、成分（Ｃ）以外のシリコーン油類、フッ素系油類、ラノリン誘導体類、油性ゲル化剤類等が挙げられる。具体的には、流動パラフィン、スクワラン、モンタンワックス、ポリイソブチレン、ポリブテン、（エチレン／プロピレン）コポリマー、フィッシャートロプシュワックス、マイクロクリスタリンワックス、ポリエチレンワックス、オゾケライトワックス、パラフィンワックス、セレシンワックス等の炭化水素類、モクロウ、オリーブ油、ヒマシ油、ミンク油、マカデミアンナッツ油等の油脂類、ミツロウ、ゲイロウ、カルナウバワックス等のロウ類、ホホバ油、２−エチルヘキサン酸セチル、乳酸イソステアリル、乳酸オクチルドデシル、乳酸オレイル、乳酸ステアリル、リンゴ酸ジイソステアリル、トリメリト酸トリトリデシル、ミリスチン酸イソプロピル、パルミチン酸イソプロピル、ミリスチン酸オクチルドデシル、ロジン酸ペンタエリトリットエステル、ジオクタン酸ネオペンチルグリコール、ジオクタン酸ネオペンチルグリコール、コレステロール脂肪酸エステル、フィトステロール脂肪酸エステル等のエステル類、ステアリン酸、ラウリン酸、ミリスチン酸、ベヘニン酸、イソステアリン酸、オレイン酸等の脂肪酸類、ステアリルアルコール、セチルアルコール、ラウリルアルコール、オレイルアルコール、イソステアリルアルコール、ベヘニルアルコール等の高級アルコール類、メチルフェニルポリシロキサン、デカメチルシクロペンタシロキサン、オクタメチルシクロテトラシロキサン、トリメチルシロキシケイ酸、高重合度メチルフェニルポリシロキサン、架橋型メチルポリシロキサン、ポリオキシ変性オルガノポリシロキサン、架橋型ポリエーテル変性メチルポリシロキサン、メタクリル変性ポリシロキサン、ステアリル変性メチルポリシロキサン、オレイル変性メチルポリシロキサン、ベヘニル変性メチルポリシロキサン、ポリビニルピロリドン変性メチルポリシロキサン、高重合度ジメチルポリシロキサン、ポリオキシアルキレン・アルキルメチルポリシロキサン・メチルポリシロキサン共重合体、アルコキシ変性ポリシロキサン、架橋型オルガノポリシロキサン、フッ素変性ポリシロキサン等のシリコーン類、パーフルオロデカン、パーフルオロオクタン、パーフルオロポリエーテル等のフッ素系油剤類、ラノリン、酢酸ラノリン、ラノリン脂肪酸イソプロピル、ラノリンアルコール等のラノリン誘導体、オクタン酸デキストリン、ラウリン酸デキストリン、パルミチン酸デキストリン、ミリスチン酸デキストリン、ステアリン酸デキストリン、ベヘニン酸デキストリン、ヤシ油脂肪酸デキストリン、（パルミチン酸／オクタン酸）デキストリン、蔗糖脂肪酸エステル、デンプン脂肪酸エステル、イソステアリン酸アルミニウム、ステアリン酸カリウム、１２−ヒドロキシステアリン酸等の油性ゲル化剤類等が挙げられ、これらを一種または二種以上用いることができる。   The oil component is not particularly limited as long as it is usually used in cosmetics, regardless of the origin such as animal oil, vegetable oil, synthetic oil, and the properties of solid oil, semi-solid oil, liquid oil, volatile oil, etc. Hydrocarbons, fats and oils, waxes, hardened oils, ester oils, fatty acids, higher alcohols, silicone oils other than component (C), fluorinated oils, lanolin derivatives, oily gelling agents, etc. Is mentioned. Specifically, hydrocarbons such as liquid paraffin, squalane, montan wax, polyisobutylene, polybutene, (ethylene / propylene) copolymer, Fischer-Tropsch wax, microcrystalline wax, polyethylene wax, ozokerite wax, paraffin wax, ceresin wax Oils, such as beeswax, olive oil, castor oil, mink oil, macadamian nut oil, waxes such as beeswax, gay wax, carnauba wax, jojoba oil, cetyl 2-ethylhexanoate, isostearyl lactate, octyldodecyl lactate Oleyl lactate, stearyl lactate, diisostearyl malate, tritridecyl trimerate, isopropyl myristate, isopropyl palmitate, octyldodecyl myristate, penta rosinate Esters such as lithitol ester, neopentyl glycol dioctanoate, neopentyl glycol dioctanoate, cholesterol fatty acid ester, phytosterol fatty acid ester, fatty acids such as stearic acid, lauric acid, myristic acid, behenic acid, isostearic acid, oleic acid, Higher alcohols such as stearyl alcohol, cetyl alcohol, lauryl alcohol, oleyl alcohol, isostearyl alcohol, behenyl alcohol, methylphenyl polysiloxane, decamethylcyclopentasiloxane, octamethylcyclotetrasiloxane, trimethylsiloxysilicic acid, high degree of polymerization methylphenyl Polysiloxane, cross-linked methylpolysiloxane, polyoxy-modified organopolysiloxane, cross-linked polyether-modified methyl Polysiloxane, methacrylic-modified polysiloxane, stearyl-modified methylpolysiloxane, oleyl-modified methylpolysiloxane, behenyl-modified methylpolysiloxane, polyvinylpyrrolidone-modified methylpolysiloxane, high polymerization dimethylpolysiloxane, polyoxyalkylene, alkylmethylpolysiloxane, methyl Silicones such as polysiloxane copolymers, alkoxy-modified polysiloxanes, cross-linked organopolysiloxanes, fluorine-modified polysiloxanes, fluorine-based oils such as perfluorodecane, perfluorooctane, perfluoropolyether, lanolin, lanolin acetate, Lanolin derivatives such as lanolin fatty acid isopropyl, lanolin alcohol, dextrin octoate, dextrin laurate, dextrin palmitate, milli Oily properties such as dextrin statin, dextrin stearate, dextrin behenate, coconut oil fatty acid dextrin, (palmitic acid / octanoic acid) dextrin, sucrose fatty acid ester, starch fatty acid ester, aluminum isostearate, potassium stearate, 12-hydroxystearic acid Examples thereof include gelling agents, and one or more of these can be used.

粉体としては、化粧料に一般に使用される粉体として用いられる粉体であれば、球状、板状、針状等の形状、煙霧状、微粒子、顔料級等の粒子径、多孔質、無孔質等の粒子構造等により特に限定されず、無機粉体類、光輝性粉体類、有機粉体類、色素粉体類、金属粉体類、複合粉体類等が挙げられる。具体的に例示すれば、酸化チタン、酸化亜鉛、酸化セリウム、硫酸バリウム等の白色無機顔料、酸化鉄、カーボンブラック、チタン・酸化チタン焼結物、酸化クロム、水酸化クロム、紺青、群青等の有色無機顔料、白雲母、金雲母、紅雲母、黒雲母、合成雲母、絹雲母（セリサイト）、合成セリサイト、炭化珪素、ベントナイト、スメクタイト、酸化アルミニウム、酸化マグネシウム、酸化ジルコニウム、酸化アンチモン、珪ソウ土、ケイ酸アルミニウム、メタケイ酸アルミニウムマグネシウム、ケイ酸カルシウム、ケイ酸バリウム、ケイ酸マグネシウム、炭酸カルシウム、炭酸マグネシウム、ヒドロキシアパタイト、窒化ホウ素等の白色体質粉体、酸化チタン被覆雲母、酸化チタン被覆オキシ塩化ビスマス、酸化鉄雲母チタン、紺青処理雲母チタン、カルミン処理雲母チタン、オキシ塩化ビスマス、魚鱗箔、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末、ポリエチレンテレフタレート・ポリオレフィン積層フィルム末、ポリエチレンテレフタレート・ポリメチルメタクリレート積層フィルム末等の光輝性粉体、ポリアミド系樹脂、ポリエチレン系樹脂、ポリアクリル系樹脂、ポリエステル系樹脂、フッ素系樹脂、セルロース系樹脂、ポリスチレン系樹脂、スチレン−アクリル共重合樹脂等のコポリマー樹脂、ポリプロピレン系樹脂、ウレタン樹脂等の有機高分子樹脂粉体、ステアリン酸亜鉛、Ｎ−アシルリジン等の有機低分子性粉体、シルク粉末、セルロース粉末、デキストリン粉末等の天然有機粉体、赤色２０１号、赤色２０２号、赤色２０５号、赤色２２６号、赤色２２８号、橙色２０３号、橙色２０４号、青色４０４号、黄色４０１号等や、赤色３号、赤色１０４号、赤色１０６号、橙色２０５号、黄色４号、黄色５号、緑色３号、青色１号等のジルコニウム、バリウム又はアルミニウムレーキ等の有機顔料粉体あるいは更にアルミニウム粉、金粉、銀粉等の金属粉体、微粒子酸化チタン被覆雲母チタン、微粒子酸化亜鉛被覆雲母チタン、硫酸バリウム被覆雲母チタン、酸化チタン含有二酸化珪素、酸化亜鉛含有二酸化珪素等の複合粉体、ナイロン、ポリエステル、レーヨン、セルロース等の維等が挙げられる。これらはフッ素化合物、シリコ−ン油、粉体、油剤、ゲル化剤、エマルションポリマー、界面活性剤等で表面処理されていてもよい。これらを１種又は２種以上を用いることができ、更に複合化したものを用いても良い。   As the powder, as long as it is a powder generally used in cosmetics, it has a spherical shape, a plate shape, a needle shape, a fume shape, a fine particle, a pigment class particle size, a porous shape, no It is not particularly limited by the particle structure such as the porosity, and examples thereof include inorganic powders, glitter powders, organic powders, pigment powders, metal powders, composite powders and the like. Specifically, white inorganic pigments such as titanium oxide, zinc oxide, cerium oxide, barium sulfate, iron oxide, carbon black, titanium / titanium oxide sintered product, chromium oxide, chromium hydroxide, bitumen, ultramarine blue, etc. Colored inorganic pigments, muscovite, phlogopite, saucite, biotite, synthetic mica, sericite, synthetic sericite, silicon carbide, bentonite, smectite, aluminum oxide, magnesium oxide, zirconium oxide, antimony oxide, silica Soil, aluminum silicate, magnesium aluminum silicate, calcium silicate, barium silicate, magnesium silicate, calcium carbonate, magnesium carbonate, hydroxyapatite, boron nitride, etc., white powder, titanium oxide coated mica, titanium oxide coated Bismuth oxychloride, titanium oxide mica titanium, bitumen treated cloud Bright powder such as titanium, carmine-treated mica titanium, bismuth oxychloride, fish scale foil, polyethylene terephthalate / aluminum / epoxy laminated powder, polyethylene terephthalate / polyolefin laminated film powder, polyethylene terephthalate / polymethyl methacrylate laminated film powder, polyamide resin , Polyethylene resin, polyacrylic resin, polyester resin, fluorine resin, cellulose resin, polystyrene resin, copolymer resin such as styrene-acrylic copolymer resin, organic polymer resin powder such as polypropylene resin and urethane resin Body, organic low molecular weight powder such as zinc stearate, N-acyl lysine, natural organic powder such as silk powder, cellulose powder, dextrin powder, red 201, red 202, red 205, red 226 Red 228, Orange 203, Orange 204, Blue 404, Yellow 401, Red 3, Red 104, Red 106, Orange 205, Yellow 4, Yellow 5, Green 3 Organic pigment powder such as zirconium, barium or aluminum lake such as Blue No. 1 or metal powder such as aluminum powder, gold powder, silver powder, fine titanium oxide coated mica titanium, fine zinc oxide coated mica titanium, barium sulfate coated mica Examples thereof include composite powders such as titanium, titanium oxide-containing silicon dioxide, and zinc oxide-containing silicon dioxide, and fibers such as nylon, polyester, rayon, and cellulose. These may be surface-treated with a fluorine compound, silicone oil, powder, oil agent, gelling agent, emulsion polymer, surfactant or the like. These may be used alone or in combination of two or more, and may be combined.

界面活性剤としては、化粧料一般に用いられている界面活性剤であればいずれのものも使用でき、非イオン性界面活性剤、アニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤等が挙げられる。
水性成分としては、水に可溶な成分であれば何れでもよく、水の他に、例えば、プロピレングリコール、１，３−ブチレングリコール、ジプロピレングリコール、グリセリン、ジグリセリン、ポリグリセリン、アロエベラ、ウイッチヘーゼル、ハマメリス、キュウリ、レモン、ラベンダー、ローズ水等の植物抽出液が挙げられる。
紫外線吸収剤としては、例えばベンゾフェノン系、ＰＡＢＡ系、ケイ皮酸系、サリチル酸系等、例えば、４−ｔｅｒｔ−ブチル−４’−メトキシジベンゾイルメタン、オキシベンゾン、２，４，６−トリス［４−（２−エチルへキシルオキシカルボニル）アニリノ］−１，３，５−トリアジン、ジエチルアミノヒドロキシベンゾイル安息香酸ヘキシル、ビスエチルヘキシルオキシフェノールメトキシフェニルトリアジン等をあげることができる。
酸化防止剤としては、例えばトコフェロール、アスコルビン酸等、美容成分としては例えばビタミン類、消炎剤、生薬等、防腐剤としては、例えばパラオキシ安息香酸エステル、フェノキシエタノール、１，２−ペンタジオール等が挙げられる。 As the surfactant, any surfactant that is generally used in cosmetics can be used. Nonionic surfactants, anionic surfactants, cationic surfactants, amphoteric surfactants, etc. Is mentioned.
The aqueous component may be any component that is soluble in water. In addition to water, for example, propylene glycol, 1,3-butylene glycol, dipropylene glycol, glycerin, diglycerin, polyglycerin, aloe vera, witch. Plant extracts such as hazel, hamamelis, cucumber, lemon, lavender, rose water and the like can be mentioned.
Examples of the ultraviolet absorber include benzophenone-based, PABA-based, cinnamic acid-based, salicylic acid-based, such as 4-tert-butyl-4'-methoxydibenzoylmethane, oxybenzone, 2,4,6-tris [4- (2-ethylhexyloxycarbonyl) anilino] -1,3,5-triazine, diethylaminohydroxybenzoyl hexyl benzoate, bisethylhexyloxyphenol methoxyphenyl triazine and the like.
Examples of the antioxidant include tocopherol and ascorbic acid, examples of the beauty component include vitamins, anti-inflammatory agents, herbal medicines, and examples of the antiseptic include paraoxybenzoate, phenoxyethanol, 1,2-pentadiol, and the like. .

本発明の油性固形化粧料は、１気圧、２５℃で流動性を有しない油性化粧料である。また、特に限定されないが、本発明は油性、又は油相性成分を連続相とする油中水型に適用されうるが、水の含有量が１％以下である実質的に水を含まない油性化粧料において、本発明の効果をより発揮することができる。具体的には、口紅、ほほ紅、アイカラー、コンシーラー等のメークアップ化粧料に用いることができるが、口紅、リップグロス、リップクリーム等の***化粧料に好適に用いられる。   The oily solid cosmetic of the present invention is an oily cosmetic that does not have fluidity at 1 atm and 25 ° C. Further, although not particularly limited, the present invention can be applied to an oily or water-in-oil type in which an oil phase component is a continuous phase, but the water content is 1% or less and the oily makeup substantially free of water. In the material, the effect of the present invention can be exhibited more. Specifically, it can be used for makeup cosmetics such as lipsticks, cheeks, eye colors, and concealers, but is preferably used for lip cosmetics such as lipsticks, lip glosses, and lip balms.

本発明の油性固形化粧料の製造方法は特に限定されるものではなく、一般的な製法で得ることができる。例えば成分（Ｃ）及びその他の油性成分等を加熱溶融したのち、成分（Ａ）、（Ｂ）及び任意の粉体や水系成分などを均一に混合分散し、加熱溶解後、容器または型に流し込み充填し、冷却して得ることができる。形状としては、皿状容器に充填されたもの、ジャー容器に充填されたもの、スティック状に成形されたもの等いずれのものにも使用されるが、本発明の効果が特に発揮される点において皿状容器に充填されたもの及びジャー容器に充填されたものであることが好ましい。   The method for producing the oily solid cosmetic of the present invention is not particularly limited, and can be obtained by a general production method. For example, after component (C) and other oily components are heated and melted, components (A) and (B) and any powders and water-based components are uniformly mixed and dispersed, and after heating and melting, poured into a container or mold. It can be obtained by filling and cooling. As the shape, it can be used for any one filled in a dish-shaped container, one filled in a jar container, one molded in a stick shape, etc., but in the point where the effect of the present invention is particularly exhibited. It is preferable that it is what was filled in the dish-shaped container and what was filled in the jar container.

以下に実施例をあげて本発明を詳細に説明する。尚、これらは本発明を何ら限定するものではない。
実施例１〜８、比較例１〜６：パレットタイプの口紅
下記表１に示す処方の口紅を調製し、イ．マットな質感、ロ．発色の良さ、ハ．伸び広がり、ニ．排液の抑制について下記の評価方法により判定した。その結果も併せて表１に示す。 Hereinafter, the present invention will be described in detail with reference to examples. Note that these do not limit the present invention.
Examples 1-8, Comparative Examples 1-6: Pallet-type lipsticks Prepare lipsticks with the formulations shown in Table 1 below. Matte texture, b. Good color development, c. Expansion, d. The suppression of drainage was determined by the following evaluation method. The results are also shown in Table 1.

（製造方法）
Ａ．成分（１）〜（８）を１１０℃まで加熱し、均一溶解する。
Ｂ．成分（９）〜（１４）をＡに加え、均一に混合する。
Ｃ．Ｂを１００℃にて充填し、冷却固化して口紅を得た。 (Production method)
A. Ingredients (1) to (8) are heated to 110 ° C. and uniformly dissolved.
B. Ingredients (9) to (14) are added to A and mixed uniformly.
C. B was filled at 100 ° C. and cooled and solidified to obtain a lipstick.

〔評価方法１〕
イ．マットな質感、ロ．発色の良さ、ハ．伸び広がり
各試料について、専門パネル２０名による使用テストを行い、パネル各人が下記絶対評価にて５段階に評価し、パネル全員の評点合計からその平均値を算出し、下記判定基準により４段階で判定した。具体的には、イについては各試料の外観及び塗布直後の膜の状態を観察し、マットな質感を感じるかどうか、ロについては塗布時に発色の良さを感じるかどうか、ハについては塗布時に伸び広がりを感じるかどうかを評価した。 [Evaluation Method 1]
A. Matte texture, b. Good color development, c. Each sample of the panel is tested for use by 20 specialist panels, and each panel member evaluates to 5 levels by the following absolute evaluation. The average value is calculated from the total score of all the panel members, and 4 levels according to the following criteria. Judged by. Specifically, for (i), the appearance of each sample and the state of the film immediately after coating were observed. We evaluated whether we felt expanse.

＜絶対評価基準＞
（評点）：（評価）
４ ：非常に優れている
３ ：優れている
２ ：普通
１ ：やや劣っている
０ ：劣っている
＜判定基準＞
（評点平均値） ：（判定）
３．５点を超える ： ◎
２．５点以上３．５未満： ○
１．５点以上２．５未満： △
１．５点未満 ： × <Absolute evaluation criteria>
(Score): (Evaluation)
4: Excellent 3: Excellent 2: Normal 1: Slightly inferior 0: Inferior <Criteria>
(Average score): (Judgment)
Over 3.5 points: ◎
2.5 or more and less than 3.5: ○
1.5 points or more and less than 2.5: △
Less than 1.5 points: ×

〔評価方法２：経時安定性〕
ニ．排液の抑制
縦２３ｍｍ、横２３ｍｍ、深さ４ｍｍの皿容器に、前記実施例及び比較例の口紅２ｇを充填し、５０℃の高温槽に２週間おいてから室温に戻したサンプルについて、排液の状態を目視観察した。 [Evaluation Method 2: Stability over time]
D. Suppression of drainage Samples that were packed in a 23 mm long, 23 mm wide, 4 mm deep dish container with 2 g of the lipstick of the examples and comparative examples, placed in a high temperature bath at 50 ° C. for 2 weeks, and then returned to room temperature. The state of the liquid was visually observed.

＜判定基準＞
（評価） (判定)
排液なし ：◎
僅かに排液しているが使用可能 ：○
排液が見られる ：× <Criteria>
(Evaluation) (Judgment)
No drainage: ◎
Slightly drained but usable: ○
Drainage is seen: ×

表１の結果より明らかな様に、実施例１〜８は比較例に比べ、全ての評価項目において良好な結果が得られた。
一方、成分（Ａ）の代わりに、マイカ、タルク、シリカをそれぞれ用いた比較例１、２及び３は、マットな質感に満足のいくものではなく、比較例１、２は発色の良さも満足のいくものではなかった。成分（Ｂ）の代わりにポリアクリル酸アルキルを用いた比較例４は、排液の抑制に欠けるものであった。成分（Ａ）の含有量が少ない比較例５は、マットな質感に欠けるものであった。成分（Ｃ）の代わりに、平均分子量の大きいジメチルポリシロキサンを用いた比較例６は、使用時の伸び広がり、排液の抑制に欠けるものであった。 As is clear from the results in Table 1, Examples 1 to 8 obtained better results in all evaluation items than the comparative examples.
On the other hand, Comparative Examples 1, 2 and 3 using mica, talc and silica in place of component (A) are not satisfactory in matte texture, and Comparative Examples 1 and 2 are also satisfactory in color development. It wasn't going to be good. Comparative Example 4 using polyalkyl acrylate instead of component (B) lacked the suppression of drainage. Comparative Example 5 with a low content of component (A) lacked a matte texture. In Comparative Example 6 using dimethylpolysiloxane having a large average molecular weight instead of the component (C), the expansion and spread at the time of use was insufficient and the drainage was not suppressed.

実施例１０：口紅（スティック状）
成分 （％）
１．ジメチルポリシロキサン※１ ２５
２．ジメチルポリシロキサン※１１ ２
３．トリイソステアリン酸ポリグリセリル−２ 残量
４．トリエチルヘキサノイン １３
５．パラフィン ９
６．（エチレン／プロピレン）コポリマー ４．５
７．マイクロクリスタリンワックス １．５
８．カオリナイト ２０
９．無水ケイ酸※８ ７
１０．２，６−ジ−ターシャリ−ブチル−パラ−クレゾール ０．１
１１．パラオキシ安息香酸メチル ０．１
１２．シリル化処理無水ケイ酸 １
１３．２％シリコーン処理タルク １．５
１４．ナイロン粉体※１２ ２
１５．赤色２０２号 ０．１
１６．撥水撥油処理ベンガラ被覆雲母チタン※１３ ５
１７．ローズマリーエキス ０．１
１８．ペンタンジオール ０．１
※１１：ＫＦ−５６−１０ＣＳ（信越化学工業株式会社製）
※１２：オルガソール２００２Ｄ（アトフィナ・ジャパン社製）
※１３：クロイゾネルージュフランベ（ＢＡＳＦ社製）２％パーフルオロアルキルリン酸エステルジエタノールアミン塩処理 Example 10: Lipstick (stick shape)
Ingredient (%)
1. Dimethylpolysiloxane * 1 25
2. Dimethylpolysiloxane * 11 2
3. 3. Polyglyceryl-2 triisostearate remaining amount Triethylhexanoin 13
5. Paraffin 9
6). (Ethylene / Propylene) Copolymer 4.5
7). Microcrystalline wax 1.5
8). Kaolinite 20
9. Silicic anhydride * 8 7
10.2,6-di-tert-butyl-para-cresol 0.1
11. Methyl paraoxybenzoate 0.1
12 Silicic anhydride 1
13.2% silicone-treated talc 1.5
14 Nylon powder * 12 2
15. Red No. 202 0.1
16. Water repellent and oil repellent treated Bengala coated mica titanium * 13 5
17. Rosemary extract 0.1
18. Pentanediol 0.1
* 11: KF-56-10CS (manufactured by Shin-Etsu Chemical Co., Ltd.)
* 12: Olgasol 2002D (manufactured by Atofina Japan)
* 13: Treatment with Cloisonol Rouge Flambe (BASF) 2% perfluoroalkyl phosphate diethanolamine salt

［製造方法］
Ａ．成分（１）〜（７）を１００〜１１０℃にて均一に溶解する。
Ｂ．Ａに成分（８）〜（１８）を加え、均一に混合分散する。
Ｃ．Ｂを脱泡後、１００℃に加熱してスティック状口紅容器に直接流し込み、冷却後、口紅を得た。 [Production method]
A. Ingredients (1) to (7) are uniformly dissolved at 100 to 110 ° C.
B. Add components (8) to (18) to A and mix and disperse uniformly.
C. After defoaming B, it was heated to 100 ° C. and poured directly into a stick-shaped lipstick container, and after cooling, a lipstick was obtained.

以上のようにして得られたスティック状口紅は、マットな質感、発色の良さ、伸び広がり、排液の抑制のすべて点で満足のいくものであった。   The stick-like lipstick obtained as described above was satisfactory in all aspects of matte texture, good color development, spread and suppression of drainage.

実施例１１：コンシーラー（スティック状）
（成分） （％）
１．カルナウバワックス １
２．フィッシャートロプシュワックス ４
３．ワセリン ２
４．リンゴ酸ジイソステアリル 残量
５．ジメチルポリシロキサン※１ ２５
６．ジメチルポリシロキサン※１１ ２
７．スクワラン １
８．パラメトキシケイ皮酸２−エチルヘキシル ５
９．トリメチルシロキシケイ酸 ２
１０．デカメチルシクロペンタシロキサン １０
１１．マカデミアナッツ油脂肪酸フィトステリル ０．５
１２．無水ケイ酸※８ ７
１３．カオリナイト ２０
１４．フェノキシエタノール ０．２
１５．トリイソステアリン酸イソプロピルチタン２％処理酸化チタン ９
１６．メチルハイドロゲンジメチコン２％処理ベンガラ ０．５
１７．ジメチコン３％処理黒酸化鉄 ０．１
１８．黄酸化鉄 ２
１９．香料 ０．１ Example 11: Concealer (stick shape)
(Ingredient) (%)
1. Carnauba wax 1
2. Fischer Tropsch Wax 4
3. Vaseline 2
4). 4. Diisostearyl malate remaining amount Dimethylpolysiloxane * 1 25
6). Dimethylpolysiloxane * 11 2
7). Squalane 1
8). 2-Ethylhexyl paramethoxycinnamate 5
9. Trimethylsiloxysilicic acid 2
10. Decamethylcyclopentasiloxane 10
11. Macadamia nut oil fatty acid phytosteryl 0.5
12 Silicic anhydride * 8 7
13. Kaolinite 20
14 Phenoxyethanol 0.2
15. Isopropyl titanium triisostearate 2% treated titanium oxide 9
16. Methylhydrogen dimethicone 2% treated bengara 0.5
17. Dimethicone 3% treated black iron oxide 0.1
18. Yellow iron oxide 2
19. Fragrance 0.1

（製造方法）
Ａ．成分（１）〜（１１）を均一にて溶解する。
Ｂ．Ａに成分（１２）〜（１９）を加え、均一に混合する。
Ｃ．Ｂを容器に９０℃にて溶解して、スティック状容器に直接流し込み、冷却後、コンシーラーを得た。 (Production method)
A. Ingredients (1) to (11) are uniformly dissolved.
B. Add components (12) to (19) to A and mix uniformly.
C. B was dissolved in a container at 90 ° C. and poured directly into a stick-shaped container, and after cooling, a concealer was obtained.

以上のようにして得られたコンシーラーは、マットな質感、発色の良さ、伸び広がり、排液の抑制のすべて点で満足のいくものであった。 The concealer obtained as described above was satisfactory in all aspects of matte texture, good color development, spread and suppression of drainage.

実施例１２：油性アイカラー（パレットタイプ）
成分 （％）
１．ポリエチレンワックス ４
２．キャンデリラワックス １
３．デカイソステアリン酸ポリグリセリル−１０ １０
４．トリイソステアリン酸ポリグリセリル−２ 残量
５．ジメチルポリシロキサン※１ ２７
６．トリエチルヘキサノイン ５
７．ミリスチン酸イソプロピル ３
８．ダイマージリノール酸（フィトステリル／イソステアリル
／セチル／ステアリル／ベヘニル） ５
９．ポリステアリン酸スクロース※１４ １
１０．ジプロピレングリコール ０．３
１１．無水ケイ酸※８ ７
１２．カオリナイト １７
１３．（ジフェニルジメチコン／ビニルジフェニルジメチコン
／シルセスキオキサン）クロスポリマー※１５ １．５
１４．撥水撥油処理タルク※１６ ２
１５．赤色２０１号 １
１６．黄色４号 １
１７．酸化鉄 ０．５
１８．酸化チタン １
１９．ＢＨＴ ０．０１
２０．パラオキシ安息香酸メチル ０．３
※１４：シュガーワックス Ｓ−１０Ｅ（第一工業製薬社製）
※１５：ＫＳＰ−３００（信越化学工業社製）
※１６：３％パーフルオロオクチルトリエトキシシラン処理 Example 12: Oily eye color (pallet type)
Ingredient (%)
1. Polyethylene wax 4
2. Candelilla wax 1
3. Decaisostearate polyglyceryl-10 10
4). 4. Polyglyceryl-2 triisostearate remaining amount Dimethylpolysiloxane * 1 27
6). Triethylhexanoin 5
7). Isopropyl myristate 3
8). Dimer linoleic acid (phytosteryl / isostearyl
/ Cetyl / stearyl / behenyl) 5
9. Polystearic acid sucrose * 14 1
10. Dipropylene glycol 0.3
11. Silicic anhydride * 8 7
12 Kaolinite 17
13. (Diphenyl dimethicone / vinyl diphenyl dimethicone / silsesquioxane) cross polymer * 15 1.5
14 Water / oil repellent talc * 16 2
15. Red 201
16. Yellow No. 1 1
17. Iron oxide 0.5
18. Titanium oxide 1
19. BHT 0.01
20. Methyl paraoxybenzoate 0.3
* 14: Sugar wax S-10E (Daiichi Kogyo Seiyaku Co., Ltd.)
* 15: KSP-300 (manufactured by Shin-Etsu Chemical Co., Ltd.)
* 16: 3% perfluorooctyltriethoxysilane treatment

［製造方法］
Ａ．成分（１）〜（１０）、（１９）及び（２０）を１１０℃〜１２０℃にて加熱溶解後、成分（１１）〜（１８）を加えて均一に混合する。
Ｂ．Ａを脱泡後、金皿に流し込み充填し、冷却して成型する。 [Production method]
A. Components (1) to (10), (19) and (20) are heated and dissolved at 110 ° C. to 120 ° C., and then components (11) to (18) are added and mixed uniformly.
B. After defoaming A, pour into a metal pan, fill, cool and mold.

以上のようにして得られた油性アイカラーは、マットな質感、発色の良さ、伸び広がり、排液の抑制のすべて点で満足のいくものであった。   The oily eye color obtained as described above was satisfactory in all aspects of matte texture, good color development, spread and suppression of drainage.

実施例１３：固形状ほほ紅
（成分） （％）
１．ポリエチレンワックス ３
２．コメヌカロウ ７
３．トリ２−エチルヘキサン酸グリセリル 残量
４．ジメチルポリシロキサン※１ ２７
５．イソステアリン酸デキストリン ０．５
６．（ビニルピロリドン／ヘキサデセン）コポリマー ５
７．ホホバ油 ０．１
８．赤色２２６号 ０．４
９．メチコン・ジメチコン３％処理黄色４号 ０．１
１０．ジメチコン２％処理合成金雲母 ３
１１．酸化亜鉛 ２
１２．硫酸バリウム １
１３．カオリナイト ２０
１４．無水ケイ酸※８ ７
１５．フェノキシエタノール ０．１ Example 13: Solid cheek red (component) (%)
1. Polyethylene wax 3
2. Rice bran 7
3. 3. Glyceryl tri-2-ethylhexanoate Dimethylpolysiloxane * 1 27
5. Dextrin isostearate 0.5
6). (Vinylpyrrolidone / hexadecene) copolymer 5
7). Jojoba oil 0.1
8). Red 226 0.4
9. Methicone / Dimethicone 3% Yellow 4 0.1
10. Dimethicone 2% treated synthetic phlogopite 3
11. Zinc oxide 2
12 Barium sulfate 1
13. Kaolinite 20
14 Silicic anhydride * 8 7
15. Phenoxyethanol 0.1

（製造方法）
Ａ．成分（１）〜（７）を均一に１００℃にて溶解する。
Ｂ．Ａに成分（８）〜（１５）を加え、均一に混合する。
Ｃ．Ｂを樹脂皿に９０℃にて溶解充填して冷却固化し固形状ほほ紅を得た。 (Production method)
A. Ingredients (1) to (7) are uniformly dissolved at 100 ° C.
B. Add components (8) to (15) to A and mix uniformly.
C. B was dissolved and filled in a resin dish at 90 ° C. and cooled and solidified to obtain a solid blusher.

以上のようにして得られた固形状ほほ紅は、マットな質感、発色の良さ、伸び広がり、排液の抑制のすべて点で満足のいくものであった。 The solid blusher obtained as described above was satisfactory in all aspects of matte texture, good color development, spreading and suppression of drainage.

Claims (5)

次の成分（Ａ）〜（Ｃ）；
（Ａ）カオリナイト １５〜３０質量％
（Ｂ）球状シリカ
（Ｃ）平均分子量が５００〜１５００であるジメチルポリシロキサン
を含有する油性固形化粧料。 The following components (A) to (C);
(A) Kaolinite 15-30% by mass
(B) Spherical silica (C) An oily solid cosmetic containing dimethylpolysiloxane having an average molecular weight of 500-1500. 前記成分（Ａ）と前記成分（Ｃ）の含有質量比が（Ａ）：（Ｃ）＝１：３〜２：１である請求項１に記載の油性固形化粧料。 The oily solid cosmetic according to claim 1, wherein the content ratio of the component (A) to the component (C) is (A) :( C) = 1: 3 to 2: 1. 前記油性固形化粧料の全液状油中の成分（Ｃ）の含有量が２５質量％以上である請求項１又は２に記載の油性固形化粧料。 The oily solid cosmetic according to claim 1 or 2, wherein the content of the component (C) in the total liquid oil of the oily solid cosmetic is 25% by mass or more. 前記成分（Ｂ）の平均粒子径が１〜３０μｍである請求項１〜３のいずれかに記載の油性固形化粧料。 The oily solid cosmetic according to any one of claims 1 to 3, wherein the component (B) has an average particle size of 1 to 30 µm. 油性固形化粧料が***化粧料である請求項１〜４のいずれかに記載の油性固形化粧料。 The oily solid cosmetic according to any one of claims 1 to 4, wherein the oily solid cosmetic is a lip cosmetic.