JP2017080905A - Moistureproof decorative laminate and fitting - Google Patents

Moistureproof decorative laminate and fitting Download PDF

Info

Publication number
JP2017080905A
JP2017080905A JP2015208334A JP2015208334A JP2017080905A JP 2017080905 A JP2017080905 A JP 2017080905A JP 2015208334 A JP2015208334 A JP 2015208334A JP 2015208334 A JP2015208334 A JP 2015208334A JP 2017080905 A JP2017080905 A JP 2017080905A
Authority
JP
Japan
Prior art keywords
moisture
proof
base material
layer
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2015208334A
Other languages
Japanese (ja)
Other versions
JP6648484B2 (en
Inventor
聡史 竹中
Satoshi Takenaka
聡史 竹中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP2015208334A priority Critical patent/JP6648484B2/en
Publication of JP2017080905A publication Critical patent/JP2017080905A/en
Priority to JP2020005119A priority patent/JP6984669B2/en
Application granted granted Critical
Publication of JP6648484B2 publication Critical patent/JP6648484B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a moistureproof decorative laminate and a fitting, with improved adhesiveness between a woody base material and a moistureproof sheet.SOLUTION: A moistureproof decorative laminate includes: a woody base material 2; a decorative sheet 4 arranged at one side 2a of the woody base material 2; and a moistureproof sheet 6 arranged at the other side 2b of the woody base material 2. One side (a side on the woody base material) 6a of the moistureproof sheet 6 has a surface wettability modification part with surface wettability modified. The surface wettability modification part is, for instance, formed by applying a reactive etching treatment using plasma. A second adhesion layer 5 adhering the woody base material 2 and the moistureproof sheet 6 includes ethylene vinyl acetate copolymer resin (EVA) having an urethane bond.SELECTED DRAWING: Figure 1

Description

本発明は、防湿化粧板および建具に関し、例えば、室内ドア、キッチンドア、収納ドア又は襖などの建具に用いられる防湿化粧板及び、この防湿化粧板を備える建具に関するものである。   The present invention relates to a moisture-proof decorative board and a fitting, for example, a moisture-proof decorative board used for a fitting such as an indoor door, a kitchen door, a storage door, or a bag, and a fitting including the moisture-proof decorative board.

室内のドアパネルなどの化粧板では、室内雰囲気での温度や湿度の変化による吸湿・放湿などが原因で発生する基材の反りを防止するために、化粧板を構成する木質基材の表面に防湿シートが貼り合わされる場合がある。すなわち、化粧板は、合板、中密度繊維板（ＭＤＦ）、ベニア板、ボード材、その他の多層構造の木質基材の表面に、隠蔽性を与えるためのベタ印刷層や意匠性を向上させるための絵柄摸様層を印刷した化粧シートを貼り合わせて構成される。そして、これらの化粧板には、温度や湿度による変形（反り、寸法変化）を防止するために、木質基材の裏面に塗料を塗ったり、防湿シートを貼り合せたりする方法が知られている。なお、防湿シートとして、特許文献１に開示されたものがある。   For decorative panels such as indoor door panels, to prevent warping of the base material due to moisture absorption and release due to changes in temperature and humidity in the indoor atmosphere, the surface of the wooden base material that constitutes the decorative board is used. A moisture-proof sheet may be attached. In other words, the decorative board is intended to improve the solid printing layer and design for providing concealability to the surface of plywood, medium density fiber board (MDF), veneer board, board material, and other multi-layer woody base materials. It is composed by pasting together a decorative sheet printed with a pattern-like layer. And in these decorative boards, in order to prevent the deformation | transformation (warpage and dimensional change) by temperature and humidity, the method of applying a coating material on the back surface of a wooden base material, or bonding a moisture-proof sheet is known. . In addition, there exists what was disclosed by patent document 1 as a moisture-proof sheet.

特許第４９４６３５０号公報Japanese Patent No. 4946350

木質基材と防湿シートとの間に単に接着剤を塗布するだけでは、十分な接着性が見込めない場合がある。特に、温度や湿度の変化が大きい環境下に化粧板が長期間置かれる場合、木質基材と防湿シートとの接着性を十分に維持することは困難である。
そこで、本発明は、このような事情に鑑みてなされたものであり、木質基材と防湿シートとの接着性を高めた防湿化粧板及び建具を提供することを目的とする。 In some cases, sufficient adhesiveness cannot be expected by simply applying an adhesive between the wooden substrate and the moisture-proof sheet. In particular, when the decorative board is placed for a long time in an environment where the temperature and humidity change are large, it is difficult to sufficiently maintain the adhesiveness between the wooden substrate and the moisture-proof sheet.
Then, this invention is made | formed in view of such a situation, and it aims at providing the moisture-proof decorative board and fitting which improved the adhesiveness of a wooden base material and a moisture-proof sheet | seat.

上記課題を解決するために、本発明の一態様に係る防湿化粧板は、木質基材と、前記木質基材の一方の面側に設けられた化粧シートと、前記木質基材の他方の面側に設けられた防湿シートと、を備え、前記防湿シートの前記木質基材側の面には、表面濡れ性が改質された表面濡れ性改質部が設けられており、前記木質基材と前記防湿シートとを接着する接着層は、ウレタン結合を有するエチレン・酢酸ビニル共重合樹脂を含むことを特徴とする。
ここで、表面濡れ性改質部は、例えば、リアクティブエッチング処理（すなわち、リアクティブイオンエッチング（ＲＩＥ）処理）などの物理的な表面改質処理で形成される。リアクティブエッチング処理は、プラズマを利用したエッチング処理である。
また、本発明の別の態様に係る建具は、上記の防湿化粧板と、芯材とを備え、前記芯材の少なくとも一方の面側に前記防湿化粧板が貼り付けられていることを特徴とする。 In order to solve the above-described problems, a moisture-proof decorative board according to one aspect of the present invention includes a wooden base material, a decorative sheet provided on one surface side of the wooden base material, and the other surface of the wooden base material. A moisture-proof sheet provided on the side, and the surface of the moisture-proof sheet on the side of the wooden substrate is provided with a surface wettability modified portion having a modified surface wettability. The adhesive layer for adhering the moisture-proof sheet includes an ethylene / vinyl acetate copolymer resin having a urethane bond.
Here, the surface wettability modified portion is formed by physical surface modification processing such as reactive etching processing (that is, reactive ion etching (RIE) processing). The reactive etching process is an etching process using plasma.
A fitting according to another aspect of the present invention includes the moisture-proof decorative board and a core material, and the moisture-proof decorative board is attached to at least one surface side of the core material. To do.

本発明の一態様によれば、木質基材と防湿シートとの接着性を高めた防湿化粧板及び建具を提供することができる。   According to one embodiment of the present invention, it is possible to provide a moisture-proof decorative board and joinery that have improved adhesion between the wooden substrate and the moisture-proof sheet.

本発明の実施形態に係る防湿化粧板１の構成例を示す断面図である。It is sectional drawing which shows the structural example of the moisture-proof decorative board 1 which concerns on embodiment of this invention. 本発明の実施形態に係る防湿シート６の構成例を示す断面図である。It is sectional drawing which shows the structural example of the moistureproof sheet 6 which concerns on embodiment of this invention. 本発明の実施形態に係る建具１０の構成例を示す断面図である。It is sectional drawing which shows the structural example of the fitting 10 which concerns on embodiment of this invention.

以下、本発明の実施形態を図面を用いて説明する。なお、以下に説明する各図において相互に対応する部分には同一符号を付し、同一符号を付した部分について繰り返しの説明を適宜省略する。また、本発明の実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、各部の材質、形状、構造、配置、寸法等を下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることができる。   Hereinafter, embodiments of the present invention will be described with reference to the drawings. In the drawings described below, parts corresponding to each other are denoted by the same reference numerals, and repeated description of the same reference numerals will be omitted as appropriate. Further, the embodiment of the present invention exemplifies a configuration for embodying the technical idea of the present invention, and specifies the material, shape, structure, arrangement, dimensions, etc. of each part as follows. Not. The technical idea of the present invention can be variously modified within the technical scope defined by the claims described in the claims.

＜防湿化粧板＞
図１は、本発明の実施形態に係る防湿化粧板１の構成例を示す断面図である。図１に示すように、防湿化粧板１は、木質基材２と、木質基材２の一方の面２ａ側に設けられた化粧シート４と、木質基材２の他方の面２ｂ側に設けられた防湿シート６と、を備える。木質基材２の一方の面２ａを表面としたとき、木質基材２の他方の面２ｂは裏面となる。
木質基材２と化粧シート４の間には第１の接着層３が設けられており、この第１の接着層３により木質基材２と化粧シート４とが接着されている。また、木質基材２と防湿シート６との間には第２の接着層５が設けられており、この第２の接着層５により木質基材２と防湿シート６とが接着されている。防湿シート６の木質基材側の面（一方の面）６ａには、表面濡れ性が改質されている表面濡れ性改質部が設けられている。また、第２の接着層５は、ウレタン結合を有するエチレン・酢酸ビニル共重合樹脂を含む。 <Dampproof decorative board>
FIG. 1 is a cross-sectional view showing a configuration example of a moisture-proof decorative board 1 according to an embodiment of the present invention. As shown in FIG. 1, the moisture-proof decorative board 1 is provided on a wooden base material 2, a decorative sheet 4 provided on one surface 2 a side of the wooden base material 2, and the other surface 2 b side of the wooden base material 2. A moisture-proof sheet 6. When one surface 2a of the wooden substrate 2 is the front surface, the other surface 2b of the wooden substrate 2 is the back surface.
A first adhesive layer 3 is provided between the wooden substrate 2 and the decorative sheet 4, and the wooden substrate 2 and the decorative sheet 4 are bonded to each other by the first adhesive layer 3. In addition, a second adhesive layer 5 is provided between the wooden substrate 2 and the moisture-proof sheet 6, and the wooden substrate 2 and the moisture-proof sheet 6 are bonded by the second adhesive layer 5. The surface (one surface) 6a on the wooden substrate side of the moisture-proof sheet 6 is provided with a surface wettability modified portion in which the surface wettability is modified. The second adhesive layer 5 includes an ethylene / vinyl acetate copolymer resin having a urethane bond.

（１）木質基材
木質基材２は、例えば合板、パーティクルボード、中密度繊維板（ＭＤＦ）、又はハードボード等である。木質基材２の厚さは、例えば１ｍｍ以上５０ｍｍ以下である。 (1) Wood base material The wood base material 2 is a plywood, a particle board, a medium density fiber board (MDF), or a hard board, for example. The thickness of the wooden substrate 2 is, for example, 1 mm or more and 50 mm or less.

（２）化粧シート
化粧シート４は、樹脂層を含む樹脂系の化粧シートである。化粧シート４に含まれる樹脂層として、例えばポリプロピレン、ポリエチレン、ポリエステル、ポリ塩化ビニル等が挙げられる。なお、化粧シート４に含まれる樹脂層として、後述の具体例で示すように、樹脂基材又は樹脂系の表面保護層等が挙げられる。
意匠性の観点から、化粧シート４の厚さは０．０５ｍｍ以上０．３０ｍｍ以下であることが好ましい。また、発熱性低減の観点から、化粧シート４は、ポリエステル、ポリ塩化ビニル等、又は、これらと他の樹脂との複合化粧シートであることが好ましい。 (2) Decorative sheet The decorative sheet 4 is a resin-based decorative sheet including a resin layer. Examples of the resin layer included in the decorative sheet 4 include polypropylene, polyethylene, polyester, and polyvinyl chloride. Examples of the resin layer included in the decorative sheet 4 include a resin base material or a resin-based surface protective layer, as shown in a specific example described later.
From the viewpoint of design properties, the thickness of the decorative sheet 4 is preferably 0.05 mm or more and 0.30 mm or less. Further, from the viewpoint of reducing heat generation, the decorative sheet 4 is preferably polyester, polyvinyl chloride, or the like, or a composite decorative sheet of these and other resins.

（２．１）具体例
具体例を挙げると、化粧シート４は、樹脂基材と、樹脂基材上に形成された絵柄層（すなわち、印刷層）と、樹脂基材上に形成されて絵柄層を覆う表面保護層（すなわち、オーバーレイフィルム層）と、を含んでいる。樹脂基材の厚さは、化粧シート４の用途や樹脂の種類にもよるが、２０μｍ〜３００μｍ程度が好ましく、５０μｍ〜２００μｍ程度がより好ましい。基材の成形方法としては、例えば押出成形法、インフレーション成形法、カレンダー成形法、キャスト成形法等が挙げられる。 (2.1) Specific Example To give a specific example, the decorative sheet 4 includes a resin base material, a pattern layer (that is, a printing layer) formed on the resin base material, and a pattern formed on the resin base material. And a surface protective layer (ie, an overlay film layer) covering the layer. The thickness of the resin base material is preferably about 20 μm to 300 μm, more preferably about 50 μm to 200 μm, although it depends on the use of the decorative sheet 4 and the type of resin. Examples of the base material molding method include an extrusion molding method, an inflation molding method, a calendar molding method, and a cast molding method.

なお、本実施形態では、樹脂基材の代わりに紙基材を用いてもよい。紙基材としては、２０〜５０ｇ／ｍ２ の薄葉紙、紙間強化紙、片艶クラフト、純白ロールを用いることができる。
絵柄層を形成するインキの樹脂バインダーとしては、ニトロセルロース等のセルロース誘導体（セルロースの０Ｈ基の一部をのこしたものも含む）、ポリビニルアルコール、ポリビニルブチラール及びそれらにイソシアネート化合物を混合したものや、アクリル酸アミド−アクリル酸エステル共重合体、塩化ビニル−酢酸ビニル共重合体を用いることができる。 In this embodiment, a paper base material may be used instead of the resin base material. As the paper substrate, 20-50 g / m 2 thin paper, inter-paper reinforced paper, single gloss craft, and pure white roll can be used.
As the resin binder of the ink for forming the pattern layer, cellulose derivatives such as nitrocellulose (including those with a part of the 0H group of cellulose), polyvinyl alcohol, polyvinyl butyral, and those obtained by mixing isocyanate compounds with them Acrylic acid amide-acrylic acid ester copolymer and vinyl chloride-vinyl acetate copolymer can be used.

絵柄層の形成方法に特に制限はなく、例えばグラビア印刷法やオフセット印刷法、スクリーン印刷法、フレキソ印刷法、静電印刷法、インキジェット印刷法等、各種の印刷方法を使用することができる。また、例えば全面ベタ状の場合には前記した各種の印刷方法の他、例えばロールコート法やナイフコート法、エアーナイフコート法、ダイコート法、リップコート法、コンマコート法、キスコート法、フローコート法、ディップコート法等の各種のコーティング方法によることもできる。その他、例えば手描き法、墨流し法、写真法、レーザービーム又は電子ビーム描画法、金属等の部分蒸着法やエッチング法等、又はこれらの方法を複数組み合わせて行ってもよい。
絵柄層が示す絵柄の種類には特に制限はなく、例えば木目柄や、石目柄、布目柄、抽象柄、幾何学模様等でもよく、或いは単なる着色や色彩調整を目的とする場合には単色無地であってもよい。化粧シート４の用途に応じて、任意の所望の絵柄を採用することができる。 There is no restriction | limiting in particular in the formation method of a pattern layer, For example, various printing methods, such as a gravure printing method, an offset printing method, a screen printing method, a flexographic printing method, an electrostatic printing method, an ink jet printing method, can be used. In addition, for example, in the case of a solid surface, in addition to the above-described various printing methods, for example, roll coating method, knife coating method, air knife coating method, die coating method, lip coating method, comma coating method, kiss coating method, flow coating method Various coating methods such as a dip coating method can also be used. In addition, for example, the hand-drawn method, the ink-washing method, the photographic method, the laser beam or electron beam drawing method, the partial vapor deposition method of metal or the like, the etching method, or a combination of these methods may be used.
There is no particular limitation on the type of pattern shown by the pattern layer, and it may be, for example, a wood grain pattern, a stone pattern, a cloth pattern, an abstract pattern, a geometric pattern, or a single color for the purpose of simple coloring or color adjustment. It may be plain. Any desired picture can be adopted according to the use of the decorative sheet 4.

表面保護層としては、水酸基（−ＯＨ）を有するポリエステル系、アクリル系、ポリエーテル系、エチレン−酢酸ビニル共重合体の部分ケン化物等のポリオールプレポリマーとイソシアネート化合物を混合して、架橋硬化してなる樹脂を用いることができる。表面保護層の厚さは、１０μｍ〜２００μｍ程度が好ましく、１０μｍ〜１００μｍ程度の範囲内がより好ましい。表面保護層の成形方法としては、例えば押出成形法、インフレーション成形法、カレンダー成形法、キャスト成形法等が挙げられる。
なお、表面保護層は、その下方にある絵柄層を透視可能とする程度に透明性を有している必要がある。このため、表面保護層は、無色透明であることが特に望ましいが、着色透明や半透明であってもよい。透明とは、表から裏が視認できる程度の透明度を指す。透明性を有する限りにおいて、表面保護層は着色剤や充填剤を含有していてもよい。 As a surface protective layer, a polyester prepolymer having a hydroxyl group (—OH), an acrylic type, a polyether type, a partially saponified product of an ethylene-vinyl acetate copolymer, and an isocyanate compound are mixed and crosslinked and cured. Can be used. The thickness of the surface protective layer is preferably about 10 μm to 200 μm, and more preferably in the range of about 10 μm to 100 μm. Examples of the method for forming the surface protective layer include an extrusion molding method, an inflation molding method, a calendar molding method, and a cast molding method.
In addition, the surface protective layer needs to have transparency to such an extent that the picture layer below it can be seen through. For this reason, the surface protective layer is particularly preferably colorless and transparent, but may be colored and transparent or translucent. Transparent refers to the degree of transparency that allows the back to be seen from the front. As long as it has transparency, the surface protective layer may contain a colorant and a filler.

（２．２）耐候性の処方
本実施形態では、耐候性の処方として、樹脂基材に耐候性処方添加剤（ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、トリアジン系紫外線吸収剤、ヒンダードアミン系光安定剤、ヒンダードフェノール系酸化防止剤等）を適宜添加してよい。これら各種の添加剤は、それぞれ単独で又は複数種混合して使用してもよい。
トリアジン系としては、２−（４，６−ジフェニル−１，３，５−トリアジン−２−イル）−５−［（ヘキシル）オキシ］−フェノール、２−［４−［（２−ヒドロキシ−３−ドデシルオキシプロピル）オキシ］−２−ヒドロキシフェニル］−４，６−ビス（２，４−ジメチルフェニル）−１，３，５−トリアジン、２−［４−［（２−ヒドロキシ−３−トリデシルオキシプロピル）オキシ］−２−ヒドロキシフェニル］−４，６−ビス（２，４ジメチルフェニル）−１，３，５−トリアジン、２，４−ビス（２，４−ジメチルフェニル）−６−（２−ヒドロキシ−４−イソ−オクチルオキシフェニル）−ｓ−トリアジン等やこれらの混合物、変性物、重合物、誘導体が使用できる。さらに、ベンゾフェノン系としては、オクタベンゾンやこの変性物、重合物、誘導体が使用できる。 (2.2) Weather-resistant prescription In this embodiment, as a weather-resistant prescription, a weather-resistant prescription additive (benzotriazole-based UV absorber, benzophenone-based UV absorber, triazine-based UV absorber, hindered amine) System light stabilizers, hindered phenol antioxidants, etc.) may be added as appropriate. These various additives may be used singly or in combination.
Examples of triazines include 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-[(hexyl) oxy] -phenol, 2- [4-[(2-hydroxy-3 -Dodecyloxypropyl) oxy] -2-hydroxyphenyl] -4,6-bis (2,4-dimethylphenyl) -1,3,5-triazine, 2- [4-[(2-hydroxy-3-tri Decyloxypropyl) oxy] -2-hydroxyphenyl] -4,6-bis (2,4dimethylphenyl) -1,3,5-triazine, 2,4-bis (2,4-dimethylphenyl) -6 (2-Hydroxy-4-iso-octyloxyphenyl) -s-triazine and the like, mixtures, modified products, polymers and derivatives thereof can be used. Furthermore, as the benzophenone series, octabenzone, modified products thereof, polymers and derivatives can be used.

ヒンダードアミン系光安定剤を添加することで、樹脂自体の光・熱・水等による劣化を防止することができる。ヒンダードアミン系光安定剤の添加部数は所望の耐候性に応じて添加すればよいが、樹脂固形分に対して０．１％〜１０％、好ましくは１％〜５％である。ヒンダードアミン系光安定剤としては、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）［［３，５−ビス（１，１−ジメチルエチル）−４−ヒドリキシフェニル］メチル］ブチルマロネート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジニル）セバケート、メチル（１，２，２，６，６−ペンタメチル−４−ポペリジニル）セバケート、デカン二酸ビス（２，２，６，６−テトラメチル−１（オクチルオキシ）−４−ピペリジニル）エステル等やこれらの混合物、変性物、重合物、誘導体等が使用できる。   By adding a hindered amine light stabilizer, deterioration of the resin itself by light, heat, water, etc. can be prevented. The added part of the hindered amine light stabilizer may be added according to the desired weather resistance, but is 0.1% to 10%, preferably 1% to 5% with respect to the resin solid content. As a hindered amine light stabilizer, bis (1,2,2,6,6-pentamethyl-4-piperidyl) [[3,5-bis (1,1-dimethylethyl) -4-hydroxyphenyl] methyl] Butyl malonate, bis (1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate, methyl (1,2,2,6,6-pentamethyl-4-popperidinyl) sebacate, bis (2) decanedioate , 2,6,6-tetramethyl-1 (octyloxy) -4-piperidinyl) ester, mixtures thereof, modified products, polymers, derivatives, and the like.

（２．３）遮熱性の処方
本実施形態では、遮熱性の処方として、樹脂基材における赤外光の反射率を高めるための顔料を、樹脂基材に含有させてもよい。樹脂基材に含有させる顔料としては、イソインドリノン、ジスアゾ、ポリアゾ、ジケトピロロピロール、キイナクリドン、フタロシアニン、酸化チタンの少なくとも一つ以上が用いられる。
例えば、樹脂基材に酸化チタンを２３質量部以上含有させることにより、遮熱性を向上させることができる。或いは、樹脂基材のうち絵柄層が形成される面に酸化チタンを塗布して、酸化チタン層を設けてもよい。酸化チタン層を設ける場合は、酸化チタン層及び樹脂基材の全体に対して、酸化チタン層における酸化チタンの含有量と、樹脂基材における酸化チタンの含有量との合計が、２３質量部以上であればよい。
なお、樹脂基材に添加される酸化チタンが多くなると、樹脂基材の膜質に酸化チタンが影響を及ぼす。このため、樹脂基材における酸化チタンの好適な含有量は、２３質量部以上５０質量部以下である。 (2.3) Heat-shielding prescription In this embodiment, as a heat-shielding prescription, the resin base material may contain a pigment for increasing the reflectance of infrared light in the resin base material. As the pigment to be contained in the resin substrate, at least one of isoindolinone, disazo, polyazo, diketopyrrolopyrrole, quinacridone, phthalocyanine, and titanium oxide is used.
For example, heat shielding properties can be improved by containing 23 parts by mass or more of titanium oxide in the resin base material. Or you may apply | coat titanium oxide to the surface in which a pattern layer is formed among resin base materials, and may provide a titanium oxide layer. When providing the titanium oxide layer, the total of the titanium oxide content in the titanium oxide layer and the titanium oxide content in the resin base material is 23 parts by mass or more with respect to the entire titanium oxide layer and the resin base material. If it is.
In addition, when the titanium oxide added to the resin base material increases, the titanium oxide affects the film quality of the resin base material. For this reason, suitable content of the titanium oxide in a resin base material is 23 to 50 mass parts.

（２．４）意匠性の処方
本実施形態では、意匠性の処方として、化粧シート４の表面（例えば、表面保護層の表面）に凹凸からなる模様が設けられていてもよい。凹凸からなる模様として、エンボス加工により形成される模様（すなわち、エンボス模様）が挙げられる。エンボス模様の種類にも特に制限はなく、例えば木目調（特に導管模様状）、石目調、布目調、和紙調、幾何学模様状等の各種模様状であってもよいし、或いは例えば単なる艶消状や砂目状、ヘアライン状、スウェード調等であってもよい。 (2.4) Designable Prescription In the present embodiment, as a designable prescription, a pattern made of unevenness may be provided on the surface of the decorative sheet 4 (for example, the surface of the surface protective layer). A pattern formed by embossing (that is, an embossed pattern) is an example of the pattern made of unevenness. There is no particular limitation on the type of embossed pattern, and it may be various patterns such as wood grain (particularly conduit pattern), stone pattern, cloth pattern, Japanese paper pattern, geometric pattern, etc. It may be matte, grainy, hairlined, suede or the like.

また、これらのエンボス模様を絵柄層と同調させることによって更なる意匠性の向上を図ることもできるが、その必要がなければ非同調であってもよく、また絵柄層と同調した模様と同調しない模様との両者を含むエンボス用を設けることもできる。
エンボス模様の形成方法にも特に制限はないが、金属製のエンボス版を使用した機械エンボス法が一般的である。またエンボス模様の形成時期にも特に制限はなく、表面保護層を基材に積層する前、積層と同時又は積層後の中から任意の時期を選択してよい。また各時期から選ばれる複数の時期に、同一又は異なる形のエンボス模様を複数回に亘って形成してもよい。 In addition, it is possible to further improve the design by synchronizing these embossed patterns with the pattern layer, but if it is not necessary, it may be non-synchronized and not synchronized with the pattern synchronized with the pattern layer. Embossing including both the pattern and the pattern can be provided.
Although there is no restriction | limiting in particular also in the formation method of an embossing pattern, The mechanical embossing method using a metal embossing plate is common. There is no particular limitation on the formation time of the embossed pattern, and any time may be selected from before the surface protective layer is laminated on the substrate, simultaneously with the lamination or after the lamination. Moreover, you may form the same or different embossed pattern in multiple times chosen from each time in multiple times.

（３）防湿シート
図２は、防湿シート６の構成例を示す断面図である。図２に示すように、防湿シート６は、ポリエチレンテレフタレート製の基材層１１と、基材層１１の一方の面側に設けられた無機酸化物からなる蒸着層１２と、蒸着層１２上に設けられ主成分がポリビニルアルコールである樹脂層１３と、樹脂層１３上に設けられた接着用プライマー層１４と、有する。基材層１１の他方の面は、防湿シート６の木質基材側の面（一方の面）６ａである。この基材層１１の他方の面に、表面濡れ性改質部１５が設けられている。上述したように、表面濡れ性改質部１５は、例えば、リアクティブエッチング処理などの物理的な表面改質処理で形成される。 (3) Moisture-Proof Sheet FIG. 2 is a cross-sectional view showing a configuration example of the moisture-proof sheet 6. As shown in FIG. 2, the moisture-proof sheet 6 includes a base material layer 11 made of polyethylene terephthalate, a vapor deposition layer 12 made of an inorganic oxide provided on one surface side of the base material layer 11, and a vapor deposition layer 12. It has the resin layer 13 provided and the main component is polyvinyl alcohol, and the primer layer 14 for adhesion provided on the resin layer 13. The other surface of the base material layer 11 is a surface (one surface) 6 a on the wooden base material side of the moisture-proof sheet 6. A surface wettability modifying portion 15 is provided on the other surface of the base material layer 11. As described above, the surface wettability modification unit 15 is formed by a physical surface modification process such as a reactive etching process, for example.

防湿シート６は、その一方の面６ａ側から他方の面６ｂ側を透視可能な透明度を有する。防湿シート６は、無色透明でもよいし、有色透明でもよい。透明とは、表から裏が視認できる程度の透明度を指す。
また、防湿シート６全体の水蒸気透過度が１．０ｇ／ｍ２・ｄａｙ以下である。また、防湿シート６は、防湿シート６全体の酸素透過度が１．０ｇ／ｍ２・ｄａｙ以下であることが好ましい。
防湿シート６は熱可塑性であってもよい。すなわち、防湿シート６は、熱可塑性樹脂系の防湿シートであってもよい。次に、図２に示す各層について、より具体的に説明する。 The moisture-proof sheet 6 has transparency that allows the other surface 6b side to be seen through from the one surface 6a side. The moisture-proof sheet 6 may be colorless and transparent, or may be colored and transparent. Transparent refers to the degree of transparency that allows the back to be seen from the front.
Moreover, the water vapor permeability of the entire moisture-proof sheet 6 is 1.0 g / m 2 · day or less. The moisture-proof sheet 6 preferably has an oxygen permeability of the entire moisture-proof sheet 6 of 1.0 g / m 2 · day or less.
The moisture-proof sheet 6 may be thermoplastic. That is, the moisture-proof sheet 6 may be a thermoplastic resin-based moisture-proof sheet. Next, each layer shown in FIG. 2 will be described more specifically.

（３．１）基材層
基材層１１の材料としては、ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、エチレン−ビニルアルコール共重合体、あるいは、これらの混合物等のオレフィン系熱可塑性樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンナフタレート−イソフタレート共重合体、ポリカーボネート、ポリアリレート等のエステル系熱可塑性樹脂、ポリメタアクリル酸メチル、ポリメタアクリル酸エチル、ポリアクリル酸ブチル等のアクリル系熱可塑性樹脂、あるいは、ポリイミド、ポリウレタン、ポリスチレン、アクリロニトリル−ブタジエン−スチレン樹脂等の非ハロゲン系熱可塑性樹脂などを挙げることができる。 (3.1) Base material layer As a material of the base material layer 11, polyethylene, polypropylene, an ethylene-propylene copolymer, an ethylene-vinyl alcohol copolymer, or an olefin-based thermoplastic resin such as a mixture thereof, polyethylene Ester thermoplastic resins such as terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyethylene naphthalate-isophthalate copolymer, polycarbonate, polyarylate, methyl polymethacrylate, ethyl polymethacrylate, polybutyl acrylate, etc. Acrylic thermoplastic resins or non-halogen thermoplastic resins such as polyimide, polyurethane, polystyrene, and acrylonitrile-butadiene-styrene resin can be used.

基材層１１には上記の各材料を使用することできるが、その中でもより好適な材料として、ポリエチレンテレフタレート（ＰＥＴ）を挙げることができる。これは、基材層１１と木質基材２とを接着する第２の接着層５が、ウレタン結合を有するエチレン・酢酸ビニル共重合樹脂（ＥＶＡ）を含むからである。ＰＥＴは、ウレタン結合を有するＥＶＡ系の接着剤と接着の相性がよい。
基材層１１は、後述する蒸着層１２が一方の面に設けられる基材となるものであり、機械的強度が強く、寸法安定性に優れるなどの理由から、二軸延伸の樹脂シートであることが好ましい（ただし、本実施形態において、基材層１１は二軸延伸に限定されるものではなく、未延伸であってもよい。）。また、基材層１１は、例えばポリエチレンテレフタレート（ＰＥＴ）を含む。例えば、基材層１１は、二軸延伸のポリエチレンテレフタレート、又は、未延伸のポリエチレンテレフタレートからなる。基材層１１の厚さは、例えば９〜１００μｍの範囲である。また、基材層１１は、無色透明又は有色透明である。 Although each said material can be used for the base material layer 11, a polyethylene terephthalate (PET) can be mentioned as a more suitable material among them. This is because the second adhesive layer 5 that bonds the base material layer 11 and the woody base material 2 contains an ethylene / vinyl acetate copolymer resin (EVA) having a urethane bond. PET has good adhesion compatibility with EVA adhesives having urethane bonds.
The base material layer 11 is a base material on which a vapor deposition layer 12 described later is provided on one surface, and is a biaxially stretched resin sheet for reasons such as high mechanical strength and excellent dimensional stability. It is preferable (however, in this embodiment, the base material layer 11 is not limited to biaxial stretching, and may be unstretched). The base material layer 11 includes, for example, polyethylene terephthalate (PET). For example, the base material layer 11 is made of biaxially stretched polyethylene terephthalate or unstretched polyethylene terephthalate. The thickness of the base material layer 11 is, for example, in the range of 9 to 100 μm. The base material layer 11 is colorless and transparent or colored and transparent.

基材層１１の他方の面（例えば、裏面）には、表面濡れ性が改質された表面濡れ性改質部１５が設けられている。表面濡れ性改質部１５の形成は、リアクティブエッチング処理やコロナ処理などの物理的処理によって表面をナノレベルで粗面として、表面濡れ性を改質して形成される。改質処理としては、コロナ処理よりもリアクティブエッチング処理の方が好ましい。その理由は、リアクティブエッチング処理の方が、コロナ処理に比べて、経時的な接着強度の維持性が高いことを確認したためである。   On the other surface (for example, the back surface) of the base material layer 11, a surface wettability modified portion 15 whose surface wettability is modified is provided. The surface wettability modified portion 15 is formed by modifying the surface wettability by making the surface rough at a nano level by a physical process such as a reactive etching process or a corona process. As the modification process, the reactive etching process is preferable to the corona process. The reason is that it has been confirmed that the reactive etching process has higher maintainability of the adhesive strength over time than the corona process.

（３．２）蒸着層
蒸着層１２は、酸化珪素、酸化マグネシウム又は酸化アルミニウムなどの無機酸化物の薄膜からなる。ここで、アルミニウムに代表される金属薄膜は金属光沢があるが、無機酸化物の薄膜は透明な蒸着膜となる。
蒸着層１２の厚さは、用いられる無機酸化物の種類・構成により最適条件が異なるが、一般的には５〜３００ｎｍの範囲内が望ましく、その値は適宜選択される。ただし、無機酸化物の膜厚が５ｎｍ未満であると均一な膜が得られないことや膜厚が十分ではないことがあり、防湿シートとしての機能を十分に果たすことができない場合がある。また、無機酸化物の膜厚が３００ｎｍを越える場合は薄膜の残留応力によりフレキシビリティを保持させることができず、成膜後の外的要因により、薄膜に亀裂を生じるおそれがある。このため、蒸着層１２の厚さは、より好ましくは、１０〜１５０ｎｍの範囲内である。 (3.2) Vapor deposition layer The vapor deposition layer 12 consists of thin films of inorganic oxides, such as silicon oxide, magnesium oxide, or aluminum oxide. Here, a metal thin film typified by aluminum has a metallic luster, but an inorganic oxide thin film becomes a transparent deposited film.
The optimum condition for the thickness of the vapor-deposited layer 12 varies depending on the type and configuration of the inorganic oxide used, but generally it is preferably in the range of 5 to 300 nm, and the value is appropriately selected. However, if the film thickness of the inorganic oxide is less than 5 nm, a uniform film may not be obtained or the film thickness may not be sufficient, and the function as a moisture-proof sheet may not be sufficiently achieved. Further, when the film thickness of the inorganic oxide exceeds 300 nm, the flexibility cannot be maintained due to the residual stress of the thin film, and the thin film may be cracked due to external factors after the film formation. For this reason, the thickness of the vapor deposition layer 12 is more preferably in the range of 10 to 150 nm.

蒸着層１２を基材層１１に積層する方法としては、真空蒸着法、スパッタリング法、イオンプレーティング法、プラズマ気相成長法（ＣＶＤ）などを用いることができる。ただし、生産性を考慮すれば、真空蒸着法が最も優れている。真空蒸着法の加熱手段としては電子線加熱方式や抵抗加熱方式、誘導加熱方式のいずれかの方式を用いることが好ましいが、蒸発材料の選択性の幅広さを考慮すると電子線加熱方式または抵抗加熱方式を用いることがより好ましい。また、蒸着層１２と基材層１１との密着性及び蒸着層１２の緻密性を向上させるために、プラズマアシスト法やイオンビームアシスト法を用いて、蒸着層１２を蒸着することも可能である。また、蒸着層１２の透明性を高めるために、蒸着の際、酸素等の各種ガスを吹き込む反応蒸着を用いてもよい。   As a method of laminating the vapor deposition layer 12 on the base material layer 11, a vacuum vapor deposition method, a sputtering method, an ion plating method, a plasma vapor deposition method (CVD), or the like can be used. However, in consideration of productivity, the vacuum deposition method is the best. As the heating means of the vacuum evaporation method, it is preferable to use any one of an electron beam heating method, a resistance heating method, and an induction heating method. It is more preferable to use the method. Further, in order to improve the adhesion between the vapor deposition layer 12 and the base material layer 11 and the denseness of the vapor deposition layer 12, the vapor deposition layer 12 can be vapor-deposited by using a plasma assist method or an ion beam assist method. . Moreover, in order to improve the transparency of the vapor deposition layer 12, you may use the reactive vapor deposition which blows in various gases, such as oxygen, in the case of vapor deposition.

（３．３）樹脂層
樹脂層１３は、主成分としてポリビニルアルコールを含む。主成分とは、物質全体の中で占める割合が高い成分のことであり、例えば、全体を１００質量部とした場合に７０質量部以上の場合を指す。樹脂層１３は、ポリビニルアルコールに無機酸化物を含有した組成物であってもよい。樹脂層１３は、蒸着層１２を保護すると共に、蒸着層１２のガスバリア性を向上させるために設けられる。
樹脂層１３は、例えば、ポリビニルアルコール、或いはポリビニルアルコールに酸化珪素、酸化マグネシウム、酸化アルミニウム等の無機酸化物を添加した組成物をロールコート法又はグラビアコート法等により、蒸着層１２上に塗布することで形成される。樹脂層１３は、無色透明又は有色透明である。 (3.3) Resin layer The resin layer 13 contains polyvinyl alcohol as a main component. The main component is a component that occupies a high ratio in the whole substance. For example, when the whole is 100 parts by mass, the main component is 70 parts by mass or more. The resin layer 13 may be a composition containing an inorganic oxide in polyvinyl alcohol. The resin layer 13 is provided to protect the vapor deposition layer 12 and improve the gas barrier property of the vapor deposition layer 12.
The resin layer 13 is applied on the vapor deposition layer 12 by, for example, polyvinyl alcohol or a composition obtained by adding an inorganic oxide such as silicon oxide, magnesium oxide, or aluminum oxide to polyvinyl alcohol by a roll coating method or a gravure coating method. Is formed. The resin layer 13 is colorless and transparent or colored and transparent.

（３．４）接着プライマー層
接着用プライマー層１４は、後述する芯材との接着を良くするために設けられるものである。接着用プライマー層１４として、具体的にはエステル樹脂、ウレタン樹脂、アクリル樹脂、ポリカーボネート樹脂、塩化ビニル−酢酸ビニル共重合体、ポリビニルブチラール樹脂、ニトロセルロース樹脂等を挙げることができる。接着用プライマー層１４は、これらの樹脂を単独ないし混合して接着組成物とし、ロールコート法やグラビア印刷法等の適宜の塗布手段を用いて形成することができる。 (3.4) Adhesion primer layer The adhesion primer layer 14 is provided in order to improve adhesion with a core material to be described later. Specific examples of the adhesion primer layer 14 include ester resins, urethane resins, acrylic resins, polycarbonate resins, vinyl chloride-vinyl acetate copolymers, polyvinyl butyral resins, and nitrocellulose resins. The adhesion primer layer 14 can be formed by using an appropriate coating means such as a roll coating method or a gravure printing method by using these resins alone or mixed to form an adhesive composition.

接着用プライマー層１４を構成するプライマーは、アクリル樹脂とウレタン樹脂との共重合体とイソシアネートとからなる樹脂で形成するのが特に好ましい。すなわち、アクリル樹脂とウレタン樹脂との共重合体は、末端に水酸基を有するアクリル重合体成分（成分Ａ）、両末端に水酸基を有するポリエステルポリオール成分（成分Ｂ）、ジイソシアネート成分（成分Ｃ）を配合して反応させてプレポリマーとなし、該プレポリマーにさらにジアミンなどの鎖延長剤（成分Ｄ）を添加して鎖延長することで得られる。この反応によりポリエステルウレタンが形成されると共にアクリル重合体成分が分子中に導入され、末端に水酸基を有するアクリル−ポリエステルウレタン共重合体が形成される。接着用プライマー層１４を構成するプライマーは、このアクリル−ポリエステルウレタン共重合体の末端の水酸基をイソシアネートと反応させて硬化させて形成される。   The primer constituting the adhesion primer layer 14 is particularly preferably formed of a resin comprising a copolymer of an acrylic resin and a urethane resin and an isocyanate. That is, a copolymer of an acrylic resin and a urethane resin includes an acrylic polymer component having a hydroxyl group at the terminal (component A), a polyester polyol component having a hydroxyl group at both ends (component B), and a diisocyanate component (component C). To obtain a prepolymer, and a chain extender (component D) such as diamine is further added to the prepolymer to extend the chain. By this reaction, polyester urethane is formed and an acrylic polymer component is introduced into the molecule to form an acrylic-polyester urethane copolymer having a hydroxyl group at the terminal. The primer constituting the adhesion primer layer 14 is formed by reacting and curing the terminal hydroxyl group of this acrylic-polyester urethane copolymer with isocyanate.

成分Ａは、末端に水酸基を有する直鎖状のアクリル酸エステル重合体が用いられる。具体的には、末端に水酸基を有する直鎖状のポリメチルメタクリレート（ＰＭＭＡ）が耐候性（特に光劣化に対する特性）に優れ、ウレタンと共重合させて相溶化するのが容易である点から好ましい。成分Ａは、共重合体においてアクリル樹脂成分となるものであり、分子量５０００〜７０００（重量平均分子量）のものが耐候性、接着性が特に良好であるために好ましく用いられる。また、成分Ａは、両末端に水酸基を有するもののみを用いてもよいが、片末端に共役二重結合が残っているものを上記の両末端に水酸基を有するものと混合して用いてもよい。   As the component A, a linear acrylate polymer having a hydroxyl group at the terminal is used. Specifically, linear polymethyl methacrylate (PMMA) having a hydroxyl group at the terminal is preferable because it is excellent in weather resistance (particularly the property against photodegradation) and can be easily copolymerized with urethane. . Component A is an acrylic resin component in the copolymer, and those having a molecular weight of 5000 to 7000 (weight average molecular weight) are preferably used because of particularly good weather resistance and adhesiveness. In addition, component A may be used only having hydroxyl groups at both ends, or a component having a conjugated double bond remaining at one end may be mixed with one having hydroxyl groups at both ends. Good.

成分Ｂは、ジイソシアネートと反応してポリエステルウレタンを形成し、共重合体においてウレタン樹脂成分を構成するものである。成分Ｂは、両末端に水酸基を有するポリエステルジオールが用いられる。このポリエステルジオールとしては、芳香族ないしスピロ環骨格を有するジオール化合物とラクトン化合物ないしその誘導体、またはエポキシ化合物との付加反応生成物、二塩基酸とジオールとの縮合生成物、および、環状エステル化合物から誘導されるポリエステル化合物等を挙げることができる。ジオールとしては、エチレングリコール、プロピレングリコール、ジエチレングリコール、ブタンジオール、ヘキサンジオール、メチルペンテンジオール等の短鎖ジオール、１，４−シクロへキサンジメタノール等の脂環族短鎖ジオール等を挙げることができる。また、塩基酸としては、アジピン酸、フタル酸、イソフタル酸、テレフタル酸等を挙げることができる。ポリエステルポリオールとして好ましいのは、酸成分としてアジピン酸ないしアジピン酸とテレフタル酸の混合物、特にアジピン酸が好ましく、ジオール成分として３−メチルペンテンジオールおよび１，４−シクロへキサンジメタノールを用いたアジペート系ポリエステルである。   Component B reacts with diisocyanate to form polyester urethane and constitutes a urethane resin component in the copolymer. Component B is a polyester diol having hydroxyl groups at both ends. Examples of the polyester diol include an addition reaction product of a diol compound having an aromatic or spiro ring skeleton and a lactone compound or a derivative thereof, or an epoxy compound, a condensation product of a dibasic acid and a diol, and a cyclic ester compound. Examples thereof include a derived polyester compound. Examples of the diol include short-chain diols such as ethylene glycol, propylene glycol, diethylene glycol, butanediol, hexanediol, and methylpentenediol, and alicyclic short-chain diols such as 1,4-cyclohexanedimethanol. . Examples of the basic acid include adipic acid, phthalic acid, isophthalic acid, terephthalic acid and the like. The polyester polyol is preferably adipic acid or a mixture of adipic acid and terephthalic acid as an acid component, particularly preferably adipic acid, and an adipate system using 3-methylpentenediol and 1,4-cyclohexanedimethanol as diol components. Polyester.

成分Ｂと成分Ｃとが反応して形成されるウレタン樹脂成分は、接着用プライマー層１４に柔軟性を与え、接着性の向上に寄与する。また、アクリル重合体からなるアクリル樹脂成分は、接着用プライマー層１４の耐候性および耐ブロッキング性に寄与する。ウレタン樹脂において、成分Ｂの分子量は接着用プライマー層１４に柔軟性を十分に発揮可能なウレタン樹脂が得られる範囲であればよいのであって、アジピン酸ないしアジピン酸とテレフタル酸の混合物と、３−メチルペンタンジオールおよび１，４−シクロへキサンジメタノールからなるポリエステルジオールの場合、５００〜５０００（重量平均分子量）が好ましい。   The urethane resin component formed by the reaction between the component B and the component C gives flexibility to the adhesion primer layer 14 and contributes to improvement in adhesion. The acrylic resin component made of an acrylic polymer contributes to the weather resistance and blocking resistance of the adhesion primer layer 14. In the urethane resin, the molecular weight of the component B may be within a range in which a urethane resin capable of sufficiently exhibiting flexibility in the primer layer for adhesion 14 is obtained, and adipic acid or a mixture of adipic acid and terephthalic acid; -In the case of the polyester diol which consists of methylpentanediol and 1, 4- cyclohexane dimethanol, 500-5000 (weight average molecular weight) are preferable.

成分Ｃは、１分子中に２個のイソシアネート基を有する脂肪族ないし脂環族のジイソシアネート化合物が用いられる。このジイソシアネートとしては、例えば、テトラメチレンジイソシアネート、２，２，４（２，４，４）−１，６−ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、４，４’−ジシクロヘキシルメタンジイソシアネート、１，４’−シクロヘキシルジイソシアネート等を挙げることができる。ジイソシアネート成分としては、イソホロンジイソシアネートが物性およびコストが優れる点で好ましい。成分Ａ〜Ｃを反応させる場合のアクリル重合体、ポリエステルポリオールおよび後述する鎖延長剤の合計の水酸基（アミノ基の場合もある）と、イソシアネート基の当量比はイソシアネート基が過剰となるようにする。   Component C is an aliphatic or alicyclic diisocyanate compound having two isocyanate groups in one molecule. Examples of the diisocyanate include tetramethylene diisocyanate, 2,2,4 (2,4,4) -1,6-hexamethylene diisocyanate, isophorone diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, and 1,4′-cyclohexyl. A diisocyanate etc. can be mentioned. As the diisocyanate component, isophorone diisocyanate is preferable in terms of excellent physical properties and cost. When the components A to C are reacted, the equivalent ratio of the total hydroxyl group (which may be an amino group) of the acrylic polymer, polyester polyol and chain extender described below and the isocyanate group is such that the isocyanate group becomes excessive. .

三成分Ａ、Ｂ、Ｃを６０〜１２０℃で２〜１０時間程度反応させると、ジイソシアネートのイソシアネート基がポリエステルポリオール末端の水酸基と反応してポリエステルウレタン樹脂成分が形成されると共にアクリル重合体末端の水酸基にジイソシアネートが付加した化合物も混在し、過剰のイソシアネート基および水酸基が残存した状態のプレポリマーが形成される。このプレポリマーに鎖延長剤として、例えば、イソホロンジアミン、ヘキサメチレンジアミン等のジアミンを加えてイソシアネート基を鎖延長剤と反応させ、鎖延長することでアクリル重合体成分がポリエステルウレタンの分子中に導入され、末端に水酸基を有する（Ｉ）のアクリル−ポリエステルウレタン共重合体を得ることができる。   When the three components A, B, and C are reacted at 60 to 120 ° C. for about 2 to 10 hours, the isocyanate group of the diisocyanate reacts with the hydroxyl group at the end of the polyester polyol to form a polyester urethane resin component and at the end of the acrylic polymer. A compound in which a diisocyanate is added to a hydroxyl group is also mixed to form a prepolymer in which an excess of isocyanate groups and hydroxyl groups remain. As a chain extender to this prepolymer, for example, diamines such as isophorone diamine and hexamethylene diamine are added, the isocyanate group is reacted with the chain extender, and the chain is extended to introduce the acrylic polymer component into the polyester urethane molecule. Thus, an acrylic-polyester urethane copolymer (I) having a hydroxyl group at the terminal can be obtained.

アクリル−ポリエステルウレタン共重合体に、イソシアネートを加えると共に、塗布法、乾燥後の塗布量を考慮して必要な粘度に調節した塗布液となし、グラビアコート法、ロールコート法等の周知の塗布法で塗布することにより接着用プライマー層１４を形成すればよい。また、イソシアネートとしては、アクリル−ポリエステルウレタン共重合体の水酸基と反応して架橋硬化させることが可能なものであればよく、例えば、２価以上の脂肪族ないし芳香族イソシアネートが使用でき、特に熱変色防止、耐候性の点から脂肪族イソシアネートが望ましい。具体的には、トリレンジイソシアネート、キシリレンジイソシアネート、４，４’−ジシクロヘキシルメタンジイソシアネート、ヘキサメチレンジイソシアネート、リジンジイソシアネートの単量体、または、これらの２量体、３量体などの多量体、あるいは、これらのイソシアネートをポリオールに付加した誘導体（アダクト体）のようなポリイソシアネートなどを挙げることができる。
接着用プライマー層１４の乾燥後の塗布量としては、１〜２０ｇ／ｍ２であり、好ましくは１〜５ｇ／ｍ２である。また、接着用プライマー層１４は、必要に応じてシリカ粉末などの充填剤、光安定剤、着色剤等の添加剤を添加した層としてもよいものである。 Addition of isocyanate to acrylic-polyester urethane copolymer, coating method, coating solution adjusted to necessary viscosity in consideration of coating amount after drying, known coating methods such as gravure coating method, roll coating method, etc. The primer layer 14 for adhesion may be formed by applying the coating. The isocyanate is not particularly limited as long as it can react with the hydroxyl group of the acrylic-polyester urethane copolymer and can be crosslinked and cured. For example, divalent or higher aliphatic or aromatic isocyanates can be used. Aliphatic isocyanates are desirable from the viewpoint of discoloration prevention and weather resistance. Specifically, a monomer such as tolylene diisocyanate, xylylene diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, hexamethylene diisocyanate, lysine diisocyanate, or a multimer such as a dimer or trimer thereof, or And polyisocyanates such as derivatives (adducts) obtained by adding these isocyanates to polyols.
The coating amount after drying of adhesive primer layer 14, a from 1 to 20 g / m 2, preferably from 1 to 5 g / m 2. Moreover, the primer layer 14 for adhesion | attachment is good also as a layer which added additives, such as fillers, such as a silica powder, a light stabilizer, and a coloring agent, as needed.

（４）第１の接着層
第１の接着層３は、例えば熱可塑性樹脂系、熱硬化型樹脂系、ゴム（エラストマー）系等のいずれのタイプの接着剤を含む。これらは、公知のもの、ないし、市販品を適宜選択して使用することができる。熱可塑性樹脂系接着剤としては、例えば、ポリ酢酸ビニル樹脂、ポリビニルアルコール、ポリビニルアセタール（ポリビニルホルマール、ポリビニルブチラール等）、シアノアクリレート、ポリビニルアルキルエーテル、ポリ塩化ビニル、ポリアミド、ポリメタクリル酸メチル、ニトロセルロース、酢酸セルロース、熱可塑性エポキシ、ポリスチレン、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸エチル共重合体等を挙げることができる。また、熱硬化型樹脂系接着剤としては、ユリア樹脂、メラミン樹脂、フェノール樹脂、レゾルシノール樹脂、フラン樹脂、エポキシ樹脂、不飽和ポリエステル樹脂、ポリウレタン樹脂、ポリイミド樹脂、ポリアミドイミド、ポリベンツイミダゾール、ポリベンゾチアゾール等を挙げることができる。ゴム系接着剤としては、天然ゴム、再生ゴム、スチレン−ブタジエンゴム、アクリロニトリル−ブタジエンゴム、クロロプレンゴム、ブチルゴム、ポリスルフィドゴム、シリコーンゴム、ポリウレタンゴム、ステレオゴム（合成天然ゴム）、エチレンプロピレンゴム、ブロックコポリマーゴム（ＳＢＳ、ＳＩＳ、ＳＥＢＳ等）等を挙げることができる。 (4) First Adhesive Layer The first adhesive layer 3 includes any type of adhesive such as a thermoplastic resin system, a thermosetting resin system, and a rubber (elastomer) system. These can be used by appropriately selecting known products or commercially available products. Examples of the thermoplastic resin adhesive include polyvinyl acetate resin, polyvinyl alcohol, polyvinyl acetal (polyvinyl formal, polyvinyl butyral, etc.), cyanoacrylate, polyvinyl alkyl ether, polyvinyl chloride, polyamide, polymethyl methacrylate, nitrocellulose. , Cellulose acetate, thermoplastic epoxy, polystyrene, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, and the like. Thermosetting resin adhesives include urea resin, melamine resin, phenol resin, resorcinol resin, furan resin, epoxy resin, unsaturated polyester resin, polyurethane resin, polyimide resin, polyamideimide, polybenzimidazole, polybenzo Examples include thiazole. Rubber-based adhesives include natural rubber, recycled rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, chloroprene rubber, butyl rubber, polysulfide rubber, silicone rubber, polyurethane rubber, stereo rubber (synthetic natural rubber), ethylene propylene rubber, block Examples include copolymer rubber (SBS, SIS, SEBS, etc.).

（５）第２の接着層
第２の接着層５は、ウレタン結合を有するエチレン・酢酸ビニル共重合樹脂（ＥＶＡ）を含む。すなわち、第２の接着層５は、ウレタン結合を有するＥＶＡ系接着層である。第２の接着層５は、主成分として、ウレタン結合を有するＥＶＡを有する。ここで、主成分とは、物質全体の中で占める割合が高い成分のことであり、例えば、全体を１００質量部とした場合に７０質量部以上の場合を指す。 (5) Second Adhesive Layer The second adhesive layer 5 includes an ethylene / vinyl acetate copolymer resin (EVA) having a urethane bond. That is, the second adhesive layer 5 is an EVA adhesive layer having a urethane bond. The second adhesive layer 5 has EVA having a urethane bond as a main component. Here, the main component is a component that occupies a high ratio in the whole substance. For example, when the whole is 100 parts by mass, the main component is 70 parts by mass or more.

＜建具＞
図３は、本発明の実施形態に係る建具１０の構成例を示す断面図である。図３に示すように、建具１０は、上述した防湿化粧板１と、芯材９とを備える。そして、芯材９の少なくとも一方の面側に、防湿化粧板１の防湿シート６側が貼り付けられている。例えば、芯材９の一方の面２０ａ及び他方の面２０ｂに、防湿化粧板１がそれぞれ貼り付けられている。この建具１０は、例えば、室内ドア、キッチンドア、収納ドア又は襖などに用いることができる。 <Furniture>
FIG. 3 is a cross-sectional view illustrating a configuration example of the joinery 10 according to the embodiment of the present invention. As shown in FIG. 3, the joinery 10 includes the moisture-proof decorative board 1 and the core material 9 described above. And the moisture-proof sheet 6 side of the moisture-proof decorative board 1 is stuck on at least one surface side of the core material 9. For example, the moisture-proof decorative board 1 is affixed to one surface 20a and the other surface 20b of the core material 9, respectively. This joinery 10 can be used for, for example, an indoor door, a kitchen door, a storage door, or a basket.

＜実施形態の効果＞
本発明の実施形態によれば、防湿化粧板１の一方の面は化粧シート４で覆われている。これにより、外界と木質基材２との間での水分の移動を抑制することができる。また、防湿化粧板１の他方の面は防湿シート６で覆われている。これにより、芯材９と木質基材２との間での水分の移動を抑制することができる。このため、木質基材２は、その表裏の側からの吸放湿を抑制することができ、吸放湿に伴う膨張又は収縮を抑制することができる。 <Effect of embodiment>
According to the embodiment of the present invention, one surface of the moisture-proof decorative board 1 is covered with the decorative sheet 4. Thereby, the movement of the water | moisture content between the external world and the wooden base material 2 can be suppressed. Further, the other surface of the moisture-proof decorative board 1 is covered with a moisture-proof sheet 6. Thereby, the movement of the water | moisture content between the core material 9 and the wooden base material 2 can be suppressed. For this reason, the wooden base material 2 can suppress moisture absorption / release from the front and back sides, and can suppress expansion or contraction associated with moisture absorption / release.

また、防湿シート６の木質基材側の面（一方の面）６ａには、表面濡れ性改質部１５が設けられている。そして、この一方の面６ａと木質基材２との間には、第２の接着層５として、ウレタン結合を有するＥＶＡ系接着層が設けられている。これにより、木質基材２と防湿シート６との接着性を高めることができ、例えば、温度や湿度の変化が大きい環境下に防湿化粧板１が置かれた場合でも、木質基材２と防湿シート６との接着性を高く維持することができる。
以上から、本実施形態によれば、従来の技術と比べて、防湿化粧板に温度や湿度による変形（反り、寸法変化）が生じることをさらに防ぐことができる。 Further, a surface wettability reforming portion 15 is provided on the surface (one surface) 6 a of the moisture-proof sheet 6 on the wooden substrate side. An EVA adhesive layer having a urethane bond is provided as the second adhesive layer 5 between the one surface 6a and the wooden substrate 2. Thereby, the adhesiveness of the wooden base material 2 and the moisture-proof sheet 6 can be improved. For example, even when the moisture-proof decorative board 1 is placed in an environment where changes in temperature and humidity are large, the wooden base material 2 and the moisture-proof sheet 6 are protected. High adhesion to the sheet 6 can be maintained.
From the above, according to the present embodiment, it is possible to further prevent the moisture-proof decorative board from being deformed (warped or dimensional change) due to temperature or humidity, as compared with the conventional technique.

次に、本発明について、以下に実施例を挙げてさらに詳しく説明する。
＜実施例＞
まず、防湿シート６を作製した。ここでは、基材層１１として、厚さ１２μｍの透明な二軸延伸のポリエチレンテレフタレート（ＰＥＴ）フィルムを用いた。この基材層１１の一方の面（例えば、表面）に蒸着層１２を設けた。蒸着層１２は、酸化アルミニウムを１５０ｎｍの厚さとなるように形成した。蒸着層１２の形成方法として真空蒸着法を用い、また真空蒸着法の加熱手段として電子線加熱方式を用いた。また、その際、蒸着層１２と基材層１１との密着性を向上させるためにプラズマアシスト法を用いるとともに、蒸着層１２の透明性を高めるために酸素ガスを吹き込み、反応蒸着を行った。これにより、防湿シートの水蒸気度透過度が１．０ｇ／ｍ２・ｄａｙ以下であり、且つ、防湿シートの表面側からその裏面側を透視可能な透明度を有する建材用の防湿シート６を作成することが可能となる。 Next, the present invention will be described in more detail with reference to the following examples.
<Example>
First, the moisture-proof sheet 6 was produced. Here, a transparent biaxially stretched polyethylene terephthalate (PET) film having a thickness of 12 μm was used as the base material layer 11. The vapor deposition layer 12 was provided on one surface (for example, the surface) of the base material layer 11. The vapor deposition layer 12 was formed so that aluminum oxide had a thickness of 150 nm. A vacuum vapor deposition method was used as a method for forming the vapor deposition layer 12, and an electron beam heating method was used as a heating means for the vacuum vapor deposition method. At that time, a plasma assist method was used in order to improve the adhesion between the vapor deposition layer 12 and the base material layer 11, and oxygen gas was blown in order to improve the transparency of the vapor deposition layer 12 to perform reactive vapor deposition. Thus, the moisture-proof sheet 6 for building materials having a water-vapor permeability of the moisture-proof sheet of 1.0 g / m 2 · day or less and having transparency that allows the back side of the moisture-proof sheet to be seen through is created. It becomes possible.

次に、蒸着層１２の上に、ポリビニルアルコール溶液を乾燥後に０．５ｇ／ｍ２となるようにグラビア印刷法で塗布して、樹脂層１３を設けた。また、基材層１１の他方の面（例えば、裏面）にリアクティブエッチング処理を施して、表面濡れ性改質部１５を形成した。この際、電極に周波数１３．５６ＭＨｚの高周波電源を用い、自己バイアス値は４５０Ｖ，Ｅｄ値を２１０Ｗ・ｍ２・秒に設定した。次に、主剤としてウレタン樹脂／塩化酢酸ビニル系樹脂、硬化剤としてイソシアネートを添加した２液硬化型樹脂を用意した。この２液硬化型樹脂を樹脂層１３の表面に対し、グラビア印刷法にて固形分で１ｇ／ｍ２の厚みに塗布して、接着用プライマー層１４を設けた。以上により、防湿シート６を得た。
また、化粧シート４を作製した。ここでは、坪量３０ｇ／ｍ２の紙間強化紙（天間特殊製紙（株）製）の表面に、ニトロセルロース系インキ（東洋インキ製造（株）製）により絵柄層を印刷し、その絵柄層上にアクリルウレタン樹脂（２液硬化タイプ、東洋インキ製造（株）製）を固形分で６ｇ／ｍ２の厚みに塗布して、樹脂系の表面保護層を形成した。以上により、化粧シート４を得た。 Next, the polyvinyl alcohol solution was applied onto the vapor deposition layer 12 by a gravure printing method so as to be 0.5 g / m 2 after drying, thereby providing a resin layer 13. Further, the surface wettability modified portion 15 was formed by performing a reactive etching process on the other surface (for example, the back surface) of the base material layer 11. At this time, a high frequency power source having a frequency of 13.56 MHz was used for the electrodes, the self-bias value was set to 450 V, and the Ed value was set to 210 W · m 2 · sec. Next, a two-component curable resin prepared by adding a urethane resin / vinyl acetate resin as a main agent and an isocyanate as a curing agent was prepared. This two-component curable resin was applied to the surface of the resin layer 13 by a gravure printing method in a solid content of 1 g / m 2 to provide an adhesive primer layer 14. Thus, the moisture-proof sheet 6 was obtained.
Moreover, the decorative sheet 4 was produced. Here, a pattern layer is printed on the surface of a paper-reinforced paper having a basis weight of 30 g / m 2 (manufactured by Tenma Special Paper Co., Ltd.) with nitrocellulose-based ink (manufactured by Toyo Ink Co., Ltd.). On the layer, an acrylic urethane resin (two-component curing type, manufactured by Toyo Ink Manufacturing Co., Ltd.) was applied in a solid content to a thickness of 6 g / m 2 to form a resin-based surface protective layer. Thus, the decorative sheet 4 was obtained.

次に、上記の方法で作製した防湿シート６と化粧シート４とを木質基材２の両面に貼り付けて、防湿化粧板１を作製した。ここでは、上記の方法で作製した防湿シート６及び化粧シート４と、木質基材２として厚さ６ｍｍの中密度繊維板（ＭＤＦ）と、第１の接着層３の材料となる酢酸ビニル系エマルジョン接着剤と、第２の接着層５の材料となるウレタン結合を有するＥＶＡ系エマルジョン接着剤とを用意した。ＭＤＦの一方の面に酢酸ビニル系エマルジョン接着剤を塗布し、その上に化粧シート４の紙間強化紙の裏面を貼り合わせた。また、ＭＦＤの他方の面に、ウレタン結合を有するＥＶＡ系エマルジョン接着剤を塗布し、その上に防湿シート６の基材層の裏面を貼り合わせた。以上により、防湿化粧板１を得た。   Next, the moisture-proof decorative board 1 was prepared by pasting the moisture-proof sheet 6 and the decorative sheet 4 produced by the above-described method on both surfaces of the wooden substrate 2. Here, the moisture-proof sheet 6 and the decorative sheet 4 produced by the above method, a medium density fiberboard (MDF) having a thickness of 6 mm as the wooden base material 2, and a vinyl acetate emulsion used as a material for the first adhesive layer 3 An adhesive and an EVA emulsion adhesive having a urethane bond as a material for the second adhesive layer 5 were prepared. A vinyl acetate emulsion adhesive was applied to one side of the MDF, and the back side of the inter-sheet reinforced paper of the decorative sheet 4 was bonded thereto. Moreover, the EVA emulsion adhesive which has a urethane bond was apply | coated to the other surface of MFD, and the back surface of the base material layer of the moisture-proof sheet 6 was bonded together on it. The moisture-proof decorative board 1 was obtained by the above.

その後、上記の方法で作製した防湿化粧板１を芯材９の両面に貼り付けて、建具１０を作製した。ここでは、上記の方法で作製した２枚の防湿化粧板１と、木質の芯材９と、酢酸ビニル系エマルジョン接着剤とを用意した。芯材９の一方の面（例えば、表面）に酢酸ビニル系エマルジョン接着剤を塗布し、その上から１枚目の防湿化粧板１を貼り合わせた。また、芯材９の他方の面（例えば、裏面）に酢酸ビニル系エマルジョン接着剤を塗布し、その上から２枚目の防湿化粧板１を貼り合わせた。以上により、建具１０を得た。この建具１０は、例えば室内ドア、キッチンドア、収納ドア又は襖などに好適に用いることができる。   Then, the moisture-proof decorative board 1 produced by said method was affixed on both surfaces of the core material 9, and the fitting 10 was produced. Here, the two moisture-proof decorative boards 1 produced by said method, the wooden core material 9, and the vinyl acetate emulsion adhesive were prepared. A vinyl acetate emulsion adhesive was applied to one surface (for example, the surface) of the core material 9, and the first moisture-proof decorative board 1 was bonded thereto. Moreover, the vinyl acetate emulsion adhesive agent was apply | coated to the other surface (for example, back surface) of the core material 9, and the 2nd moisture-proof decorative board 1 was bonded together from the top. Thus, joinery 10 was obtained. This fitting 10 can be suitably used for, for example, an indoor door, a kitchen door, a storage door, or a basket.

＜実施例２＞
実施例２では、防湿シートの作製に際し、リアクティブエッチング処理の代わりに、コロナ処理を施した以外は、実施例１と同様の方法で、防湿シートを得た。
また実施例２では、実施例１と同様の方法で化粧シートを得た。
その後、ＭＤＦの一方の面に酢酸ビニル系エマルジョン接着剤を塗布し、その上に化粧シートの紙間強化紙の裏面を貼り合わせた。また、ＭＤＦの他方の面に、ウレタン結合を有するＥＶＡ系エマルジョン接着剤を塗布し、その上に防湿シートの基材層の裏面を貼り合わせた。以上により、防湿化粧板を得た。 <Example 2>
In Example 2, a moisture-proof sheet was obtained in the same manner as in Example 1 except that corona treatment was performed instead of reactive etching treatment when producing the moisture-proof sheet.
In Example 2, a decorative sheet was obtained in the same manner as in Example 1.
Then, the vinyl acetate emulsion adhesive was apply | coated to one side of MDF, and the back surface of the paper reinforcement | strengthening paper of a decorative sheet was bonded together on it. Moreover, the EVA type emulsion adhesive which has a urethane bond was apply | coated to the other surface of MDF, and the back surface of the base material layer of a moisture-proof sheet was bonded together on it. Thus, a moisture-proof decorative board was obtained.

＜比較例１＞
比較例１では、実施例１と同様の方法で、防湿シートと化粧シートとを得た。
その後、ＭＤＦの一方の面に酢酸ビニル系エマルジョン接着剤を塗布し、その上に化粧シートの紙間強化紙の裏面を貼り合わせた。また、ＭＤＦの他方の面に、酢酸ビニル系エマルジョン接着剤を塗布し、その上に防湿シートの基材層の裏面を貼り合わせた。つまり、比較例２では、ウレタン結合を有するＥＶＡ系エマルジョン接着剤を使用しなかった。以上により、防湿化粧板を得た。 <Comparative Example 1>
In Comparative Example 1, a moisture-proof sheet and a decorative sheet were obtained in the same manner as in Example 1.
Then, the vinyl acetate emulsion adhesive was apply | coated to one side of MDF, and the back surface of the paper reinforcement | strengthening paper of a decorative sheet was bonded together on it. Moreover, the vinyl acetate emulsion adhesive agent was apply | coated to the other surface of MDF, and the back surface of the base material layer of a moisture-proof sheet was bonded together on it. That is, in Comparative Example 2, an EVA emulsion adhesive having a urethane bond was not used. Thus, a moisture-proof decorative board was obtained.

＜評価＞
上記で作製した実施例１、２に係る防湿化粧板１と、比較例１に係る防湿化粧板とについて、木質基材と防湿シートとの接着性を評価した。接着性の評価方法とその結果は、以下の通りである。
（１）評価方法
平面引張強度：ＪＡＳ合板 平面引張試験、に準拠して平面引張強度を測定した。平面引張強度の単位はＮ／ｃｍ２である。
なお、評価に供した防湿化粧板は、防湿シートとＭＤＦとを２４時間コールドプレスしたもの用い、防湿化粧板を５ｃｍ角にカットし、底辺が２ｃｍ角の金属治具を防湿シート一面にシアノアクリレート系接着剤にて貼り、２４時間常温（約２３℃）養生した後、カッターナイフにて金属治具に沿ってＭＤＦにまで達する切り込みを入れ、測定試験機器により試験片に対して垂直面方向に引張り、その際の剥離界面を目視観察して評価すると共に平面引張強度を測定した。 <Evaluation>
About the moisture-proof decorative board 1 which concerns on Examples 1 and 2 produced above, and the moisture-proof decorative board which concerns on the comparative example 1, the adhesiveness of a wooden base material and a moisture-proof sheet was evaluated. The adhesive evaluation method and the results are as follows.
(1) Evaluation method Plane tensile strength: JAS plywood Plane tensile strength was measured according to a plane tensile test. The unit of plane tensile strength is N / cm 2 .
The moisture-proof decorative board used for the evaluation was a cold-pressed sheet of moisture-proof sheet and MDF for 24 hours. The moisture-proof decorative board was cut into a 5 cm square, and a metal jig with a base of 2 cm square was attached to the entire surface of the moisture-proof sheet. After sticking with an adhesive and curing at room temperature (about 23 ° C) for 24 hours, cut with a cutter knife up to the MDF along the metal jig, and in the direction perpendicular to the test piece with the measuring test equipment The tensile interface was evaluated by visually observing the peeling interface at that time and measuring the plane tensile strength.

（２）評価結果 (2) Evaluation results

Figure 2017080905
Figure 2017080905

表１に示すように、実施例１、２は、比較例１と比べて、平面引張強度が大きいことを確認した。このことから、実施例１、２は、比較例１と比べて、木質基材と防湿シートとの接着性が高いといえる。   As shown in Table 1, it was confirmed that Examples 1 and 2 had higher planar tensile strength than Comparative Example 1. From this, it can be said that Examples 1 and 2 have higher adhesiveness between the wooden substrate and the moisture-proof sheet than Comparative Example 1.

１ 防湿化粧板
２ 木質基材
３ 第１の接着層
４ 化粧シート
５ 第２の接着層
６ 防湿シート
９ 芯材
１０ 建具
１１ 基材層
１２ 蒸着層
１３ 樹脂層
１４ 接着用プライマー層
１５ 表面濡れ性改質部 DESCRIPTION OF SYMBOLS 1 Moisture-proof decorative board 2 Wood base material 3 First adhesive layer 4 Cosmetic sheet 5 Second adhesive layer 6 Moisture-proof sheet 9 Core material 10 Joinery 11 Base material layer 12 Deposition layer 13 Resin layer 14 Adhesive primer layer 15 Surface wettability Reforming department

Claims (7)

木質基材と、
前記木質基材の一方の面側に設けられた化粧シートと、
前記木質基材の他方の面側に設けられた防湿シートと、を備え、
前記防湿シートの前記木質基材側の面には、表面濡れ性が改質された表面濡れ性改質部が設けられており、
前記木質基材と前記防湿シートとを接着する接着層は、ウレタン結合を有するエチレン・酢酸ビニル共重合樹脂を含むことを特徴とする防湿化粧板。 A wooden substrate;
A decorative sheet provided on one side of the wooden substrate;
A moisture-proof sheet provided on the other surface side of the wooden substrate,
On the surface of the moisture-proof sheet on the side of the wooden base material, a surface wettability modified portion having a modified surface wettability is provided,
The moisture-proof decorative board, wherein the adhesive layer that bonds the wood base material and the moisture-proof sheet contains an ethylene / vinyl acetate copolymer resin having a urethane bond. 前記化粧シートは、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、トリアジン系紫外線吸収剤、ヒンダードアミン系光安定剤、ヒンダードフェノール系酸化防止剤のうち少なくとも一つ以上を含むことを特徴とする請求項１に記載の防湿化粧板。   The decorative sheet includes at least one of a benzotriazole ultraviolet absorber, a benzophenone ultraviolet absorber, a triazine ultraviolet absorber, a hindered amine light stabilizer, and a hindered phenol antioxidant. The moisture-proof decorative board according to claim 1. 前記化粧シートの表面に凹凸からなる模様が設けられていることを特徴とする請求項１又は請求項２に記載の防湿化粧板。   The moisture-proof decorative board according to claim 1 or 2, wherein a pattern made of unevenness is provided on the surface of the decorative sheet. 前記防湿シートは、
ポリエチレンテレフタレートを含む基材層と、
前記基材層の一方の面側に設けられた無機酸化物を含む蒸着層と、
前記蒸着層上に設けられたポリビニルアルコールを含む樹脂層と、
前記樹脂層上に設けられた接着用プライマー層と、有し、
前記基材層の他方の面が前記木質基材側の面であることを特徴とする請求項１から請求項３の何れか一項に記載の防湿化粧板。 The moisture-proof sheet is
A base material layer comprising polyethylene terephthalate;
A vapor deposition layer containing an inorganic oxide provided on one surface side of the base material layer;
A resin layer containing polyvinyl alcohol provided on the vapor deposition layer;
Having an adhesion primer layer provided on the resin layer,
The moisture-proof decorative board according to any one of claims 1 to 3, wherein the other surface of the base material layer is a surface on the wooden base material side. 前記防湿シートは熱可塑性であることを特徴とする請求項１から請求項４の何れか一項に記載の防湿化粧板。   The moisture-proof decorative board according to any one of claims 1 to 4, wherein the moisture-proof sheet is thermoplastic. 前記防湿シートの水蒸気透過度が１．０ｇ／ｍ２・ｄａｙ以下であり、且つ、
前記防湿シートは、該防湿シートの一方の面側から他方の面側を透視可能な透明度を有することを特徴とする請求項１から請求項５の何れか一項に記載の防湿化粧板。 The moisture permeability of the moisture-proof sheet is 1.0 g / m 2 · day or less, and
The moisture-proof decorative board according to any one of claims 1 to 5, wherein the moisture-proof sheet has transparency so that the other surface side can be seen through from one side of the moisture-proof sheet. 請求項１から請求項６の何れか一項に記載の防湿化粧板と、
芯材とを備え、
前記芯材の少なくとも一方の面側に前記防湿化粧板が貼り付けられていることを特徴とする建具。 The moisture-proof decorative board according to any one of claims 1 to 6,
With a core material,
The fitting characterized in that the moisture-proof decorative board is affixed to at least one surface side of the core material.
JP2015208334A 2015-10-22 2015-10-22 Moisture-proof decorative boards and fittings Active JP6648484B2 (en)