JP2017070515A - Sheet for absorbent article, absorbent article, and manufacturing method thereof - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a highly antibacterial sheet for an absorbent article and an absorbent article.SOLUTION: A sheet for an absorbent article includes a hydrophobic organic antibacterial agent, a hydrophilic and non-volatile organic solvent, and water of 10 mass% or less. The sheet for an absorbent article is appropriately manufactured by containing an antibacterial agent solution including the hydrophobic organic antibacterial agent, the hydrophilic and non-volatile organic solvent, and water of 8 mass% or less in the sheet. An absorbent article includes an absorbent core containing the hydrophobic organic antibacterial agent and the hydrophilic and non-volatile organic solvent. The absorbent article is appropriately manufactured by containing the antibacterial agent solution, obtained by dissolving the hydrophobic organic antibacterial agent in the hydrophilic and non-volatile organic solvent, in the absorbent core.SELECTED DRAWING: None

Description

本発明は、吸収性物品用シート及び吸収性物品に関する。また本発明は、それらの製造方法に関する。   The present invention relates to an absorbent article sheet and an absorbent article. Moreover, this invention relates to those manufacturing methods.

抗菌剤を付与したティッシュペーパー等の紙を用いることによって、使用者の皮膚に抗菌作用を施す技術が知られている。例えば特許文献１には、抗菌剤と活性炭とが、吸収性コアと表面シートとの間に施されている吸収性物品が記載されている。特許文献２には、鼻かみ時における肌への刺激を低減することを目的として、抗菌剤を付与したティッシュペーパーが提案されている。特許文献３には、皮膚の表面を清浄にし、細菌の増殖と生存性を制御するための抗菌拭き取り用品が提案されている。この拭き取り用品には抗菌剤が含まれている。   A technique is known in which antibacterial action is applied to the skin of a user by using paper such as tissue paper to which an antibacterial agent is applied. For example, Patent Document 1 describes an absorbent article in which an antibacterial agent and activated carbon are applied between an absorbent core and a surface sheet. Patent Document 2 proposes a tissue paper to which an antibacterial agent is added for the purpose of reducing irritation to the skin during nose biting. Patent Document 3 proposes an antibacterial wipe for cleaning the skin surface and controlling bacterial growth and viability. This wipe contains an antibacterial agent.

特開２００６−１９１９６６号公報JP 2006-191966 A 特開２００７−１９５９３６号公報JP 2007-195936 A 特表２００２−５４０８９８号公報Special Table 2002-540898

上述した各特許文献に記載の技術によれば、ある程度の抗菌効果は発現する。しかし、抗菌効果が発現する部位が、抗菌剤を付与した部位にとどまり、更に高い抗菌効果を発現することが望まれていた。また、高い抗菌効果が発現するように抗菌剤を施す方法は、これらの特許文献には記載されていない。   According to the technology described in each patent document described above, a certain degree of antibacterial effect is exhibited. However, it has been desired that the site where the antibacterial effect is expressed stays at the site where the antibacterial agent is applied, and a higher antibacterial effect is expressed. Moreover, the method of applying an antibacterial agent so that a high antibacterial effect is expressed is not described in these patent documents.

したがって本発明の課題は、抗菌剤を含有する物品の改良にあり、更に詳しくは、吸収性物品用シート及び吸収性物品の抗菌性を従来よりも高めることにある。また本発明の課題は、抗菌性の高い吸収性物品用シート及び吸収性物品を容易に製造し得る方法を提供することにある。   Therefore, the subject of this invention exists in improvement of the articles | goods containing an antibacterial agent, and exists in improving the antibacterial property of the sheet | seat for absorbent articles, and an absorbent article more conventionally. Another object of the present invention is to provide a sheet for absorbent articles having a high antibacterial property and a method for easily producing the absorbent article.

本発明は、有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、１０質量％以下の水とを含む吸収性物品用シートを提供するものである。   This invention provides the sheet | seat for absorbent articles containing an organic hydrophobic antibacterial agent, a hydrophilic and non-volatile organic solvent, and 10 mass% or less of water.

また本発明は、前記のシートの好適な製造方法として、有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、８質量％以下の水とを含む抗菌剤溶液をシートに含有させる工程を有する吸収性物品用シートの製造方法を提供するものである。   Further, the present invention provides a method for producing the above sheet by including an antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 8% by mass or less of water in the sheet. The manufacturing method of the sheet | seat for absorbent articles which has this is provided.

また本発明は、有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、３０質量％以下の水とを含む抗菌剤溶液をシートに含有させた後、乾燥させる工程を有する吸収性物品用シートの製造方法を提供するものである。   The present invention also provides an absorbent article having a step of allowing an antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 30% by mass or less of water to be contained in a sheet and then drying the sheet. The manufacturing method of the sheet | seat is provided.

また本発明は、有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒とを含有する吸収性コアを含む吸収性物品を提供するものである。   Moreover, this invention provides the absorbent article containing the absorptive core containing an organic hydrophobic antibacterial agent and a hydrophilic and non-volatile organic solvent.

本発明は、前記の吸収性物品の好適な製造方法として、有機疎水性抗菌剤を親水性かつ不揮発性の有機溶媒に溶解してなる抗菌剤溶液を、吸収性コアに含有させる工程を有する吸収性物品の製造方法を提供するものである。   In the present invention, as a preferred method for producing the absorbent article, the absorbent core includes an antibacterial agent solution obtained by dissolving an organic hydrophobic antibacterial agent in a hydrophilic and non-volatile organic solvent. The manufacturing method of a property article is provided.

本発明によれば、抗菌性の高い吸収性物品用シート及び吸収性物品が提供される。また本発明によれば、抗菌性の高い吸収性物品用シート及び吸収性物品を容易に製造することができる。   According to the present invention, a highly antibacterial absorbent article sheet and absorbent article are provided. Moreover, according to this invention, a sheet | seat for absorbent articles and an absorbent article with high antimicrobial property can be manufactured easily.

以下本発明を、その好ましい実施形態に基づき説明する。本発明の吸収性物品用シートは、吸収性物品の構成部材の一つとして好適に用いられるものである。吸収性物品は、人体から排出される体液、例えば尿、経血、軟便、汗等の吸収に用いられる物品を広く包含し、使い捨ておむつ、生理用ナプキン、生理用ショーツ等が包含される。吸収性物品用シートの具体的な適用例としては、吸収性コアの少なくとも肌対向面側を被覆する被覆シートが挙げられる。この被覆シートは、コアラップシートとも呼ばれる。被覆シートに被覆される吸収性コアとしては、例えばフラップパルプと吸水性ポリマーとの混合積繊体、吸収性ポリマーのみの堆積体、及びフラッフパルプのみの積繊体などが挙げられる。吸収性コアの少なくとも肌対向面側を被覆シートで被覆することで吸収体が構成される。被覆シートの肌対向面側には表面シートが配置される。吸収性物品用シートの他の適用例としては、医療用、産業資材用、生活関連資材用等に用いられる、特に、抗菌性能を必要とする手術衣、包帯、絆創膏、ベッドシーツ、枕カバー、脇の下用パッドの吸収紙、靴用抗菌紙等が挙げられる。   Hereinafter, the present invention will be described based on preferred embodiments thereof. The sheet | seat for absorbent articles of this invention is used suitably as one of the structural members of an absorbent article. Absorbent articles widely include articles used to absorb body fluids discharged from the human body, such as urine, menstrual blood, loose stool, sweat, and the like, including disposable diapers, sanitary napkins, sanitary shorts, and the like. As a specific application example of the absorbent article sheet, there is a covering sheet that covers at least the skin facing surface side of the absorbent core. This covering sheet is also called a core wrap sheet. As an absorptive core coat | covered with a coating sheet, the mixed fiber body of a flap pulp and a water absorbing polymer, the deposit body only of an absorptive polymer, the stack fiber body only of a fluff pulp, etc. are mentioned, for example. An absorber is comprised by coat | covering at least the skin opposing surface side of an absorptive core with a coating sheet. A surface sheet is disposed on the skin facing surface side of the covering sheet. Other application examples of the absorbent article sheet are used for medical use, industrial materials, life-related materials, etc., especially surgical clothes, bandages, bandages, bed sheets, pillow covers, which require antibacterial performance, Examples include absorbent paper for underarm pads and antibacterial paper for shoes.

吸収性物品用シートは、基材シートに、抗菌剤及び有機溶媒を含有させたものであることが好ましい。抗菌剤は１種を単独で、又は２種以上を組み合わせて用いることができる。同様に、有機溶媒も、１種を単独で、又は２種以上を組み合わせて用いることができる。吸収性物品用シートは水を含んでいてもよいが、水の含有量は、吸収性物品用シートの質量に対して１０質量％以下とすることが、抗菌性能の点から好ましい。１０質量％以下の水の含有量は、周囲環境下に吸収性物品用シートを置いたときに周囲環境から不可避的に自然に吸収される水の量に概ね等しい。吸収性物品用シートに含まれる水の量は、日本工業規格ＪＩＳＰ８１２７紙及び板紙-ロットの水分試験方法-乾燥機（１０５℃±２℃、乾燥時間３０分以上）による方法に準じて測定される。   The absorbent article sheet is preferably a base sheet containing an antibacterial agent and an organic solvent. An antimicrobial agent can be used individually by 1 type or in combination of 2 or more types. Similarly, an organic solvent can also be used individually by 1 type or in combination of 2 or more types. The absorbent article sheet may contain water, but the water content is preferably 10% by mass or less with respect to the mass of the absorbent article sheet from the viewpoint of antibacterial performance. The content of water of 10% by mass or less is approximately equal to the amount of water that is unavoidably naturally absorbed from the surrounding environment when the absorbent article sheet is placed in the surrounding environment. The amount of water contained in the absorbent article sheet is measured according to the Japanese Industrial Standard JISP8127 paper and paperboard-lot water test method-dryer (105 ° C. ± 2 ° C., drying time 30 minutes or more). .

吸収性物品用シートは液透過性を有することが好ましい。この観点から、吸収性物品用シートを構成する基材シートは繊維シートや、フィルムに複数の貫通孔を形成した穿孔シートであることが好ましい。繊維シートとしては、紙、不織布、織布、織物地、又はそれらの複合材などが挙げられる。吸収性物品用シートを構成する基材シートは、その坪量が、５０ｇ／ｍ^２以上であることが好ましく、７０ｇ／ｍ^２以上であることが更に好ましく、１００ｇ／ｍ^２以上であることが一層好ましい。また、１０００ｇ／ｍ^２以下であることが好ましく、５００ｇ／ｍ^２以下であることが更に好ましく、３００ｇ／ｍ^２以下であることが一層好ましい。吸収性物品用シートの坪量は、１０ｇ／ｍ^２以上５０ｇ／ｍ^２以下であることが好ましく、１２ｇ／ｍ^２以上４０ｇ／ｍ^２以下であることが更に好ましく、１３ｇ／ｍ^２以上３５ｇ／ｍ^２以下であることが一層好ましい。 It is preferable that the sheet | seat for absorbent articles has liquid permeability. From this viewpoint, the base material sheet constituting the absorbent article sheet is preferably a fiber sheet or a perforated sheet in which a plurality of through holes are formed in the film. Examples of the fiber sheet include paper, non-woven fabric, woven fabric, woven fabric, or a composite material thereof. The base sheet constituting the absorbent article sheet preferably has a basis weight of 50 g / m ² or more, more preferably 70 g / m ² or more, and 100 g / m ² or more. Even more preferred. Further, it is preferably 1000 g / m ² or less, more preferably 500 g / m ² or less, and even more preferably 300 g / m ² or less. The basis weight of the absorbent article sheet is preferably 10 g / m ² or more and 50 g / m ² or less, more preferably 12 g / m ² or more and 40 g / m ² or less, and 13 g / m ² or more and 35 g / m ² or less. More preferably, it is m ² or less.

基材シートには、抗菌剤及び有機溶媒を含む抗菌剤溶液が施されて、本発明の吸収性物品用シートが構成されることが好ましい。抗菌剤溶液は水を含んでいてもよいが、水の含有量は、抗菌剤溶液の質量に対して８質量％以下とすることが、抗菌剤溶液の安定性、並びに、抗菌剤溶液中の抗菌剤の発泡及び析出を抑制する点から好ましい。８質量％以下の水の含有量は、周囲環境下に抗菌剤溶液を置いたときに周囲環境から不可避的に自然に吸収される水の量に概ね等しい。吸収性物品用シートに抗菌剤が含まれているか否の定性分析、及び含まれている場合の定量分析を含めた分析方法は以下のとおりである。
分析方法：市販の製品から、コールドスプレー等を用いて接着剤の接着力を弱め、各材料を丁寧に剥がす。各材料に対し、まず蛍光Ｘ線回折を行い、金属が含まれているか否かを確認する。金属以外の剤（抗菌剤、有機溶媒）については、各材料をメタノール溶液に浸漬後、該メタノール溶液に含まれる該剤を、ＨＰＬＣ等を用いて分画する。該分画に含まれる化合物を、ＮＭＲ測定器などを用いて同定する。前記メタノール溶液をＬＣ−ＵＶなどを用いることで濃度を算出して定量する。
また、本発明の吸収性物品用シートは、３０質量％以下の水を含んだ抗菌剤溶液を、基材シートに施すことによって構成されていてもよい。その場合、基材シートに抗菌剤溶液を施した後、乾燥により水を除去する工程を設ける。乾燥手段は熱風を噴き当てる方法や、加熱したロールに沿わせるなど、周知の方法を制限なく用いることができる。 It is preferable that an antibacterial agent solution containing an antibacterial agent and an organic solvent is applied to the base material sheet to constitute the absorbent article sheet of the present invention. The antibacterial agent solution may contain water. However, the content of water should be 8% by mass or less based on the mass of the antibacterial agent solution. It is preferable from the point which suppresses foaming and precipitation of an antibacterial agent. The content of water of 8% by mass or less is approximately equal to the amount of water that is unavoidably naturally absorbed from the surrounding environment when the antimicrobial solution is placed in the surrounding environment. The analysis method including the qualitative analysis of whether or not the antibacterial agent is contained in the absorbent article sheet and the quantitative analysis in the case where it is contained are as follows.
Analysis method: From a commercial product, use a cold spray or the like to weaken the adhesive strength of the adhesive and carefully peel off each material. Each material is first subjected to fluorescent X-ray diffraction to check whether or not a metal is contained. For agents other than metals (antibacterial agent, organic solvent), each material is immersed in a methanol solution, and then the agent contained in the methanol solution is fractionated using HPLC or the like. The compound contained in the fraction is identified using an NMR measuring instrument or the like. The methanol solution is quantified by calculating the concentration using LC-UV or the like.
Moreover, the sheet | seat for absorbent articles of this invention may be comprised by applying the antimicrobial agent solution containing 30 mass% or less of water to a base material sheet. In that case, after giving an antibacterial agent solution to a base material sheet, the process of removing water by drying is provided. As the drying means, a well-known method such as a method of spraying hot air or a heating roll can be used without limitation.

抗菌剤及び有機溶媒は、吸収性物品用シートの全域にわたって均一に存在していてもよい。あるいは抗菌剤及び有機溶媒は、吸収性物品用シートにおける特定の部位に局所的に存在していてもよい。いずれの場合であっても、吸収性物品用シートにおける抗菌剤の存在量は０．０２ｇ／ｍ^２以上であることが好ましく、０．０４ｇ／ｍ^２以上であることが更に好ましく、０．０５ｇ／ｍ^２以上であることが一層好ましい。また、０．５ｇ／ｍ^２以下であることが好ましく、０．４ｇ／ｍ^２以下であることが更に好ましく、０．３ｇ／ｍ^２以下であることが一層好ましい。吸収性物品用シートにおける抗菌剤の存在量は０．０２ｇ／ｍ^２以上０．５ｇ／ｍ^２以下であることが好ましく、０．０４ｇ／ｍ^２以上０．４ｇ／ｍ^２以下であることが更に好ましく、０．０５ｇ／ｍ^２以上０．３ｇ／ｍ^２以下であることが一層好ましい。この存在量は、抗菌剤が局所的に存在している場合であっても、吸収性物品用シートの全面積を基準として算出されるものである。 The antibacterial agent and the organic solvent may be present uniformly over the entire area of the absorbent article sheet. Or an antibacterial agent and an organic solvent may exist locally in the specific site | part in the sheet | seat for absorbent articles. In any case, the amount of antibacterial agent present in the absorbent article sheet is preferably 0.02 g / m ² or more, more preferably 0.04 g / m ² or more, and 0.05 g. / M ² or more is more preferable. Further, it is preferably 0.5 g / ^{m 2} or less, further preferably 0.4 g / ^{m 2} or less, and still more preferably 0.3 g / ^{m 2} or less. The abundance of the antibacterial agent in the absorbent article sheet is preferably 0.02 g / m ² or more and 0.5 g / m ² or less, and preferably 0.04 g / m ² or more and 0.4 g / m ² or less. more preferably, it is more preferably 0.05 g / ^{m 2} or more 0.3 g / ^{m 2} or less. This abundance is calculated on the basis of the total area of the absorbent article sheet even when the antibacterial agent is present locally.

吸収性物品用シートにおける有機溶媒の存在量は０．１ｇ／ｍ^２以上であることが好ましく、０．２ｇ／ｍ^２以上であることが更に好ましく、０．４ｇ／ｍ^２以上であることが一層好ましい。また、２０ｇ／ｍ^２以下であることが好ましく、１５ｇ／ｍ^２以下であることが更に好ましく、１２ｇ／ｍ^２以下であることが一層好ましい。吸収性物品用シートにおける有機溶媒の存在量は０．１ｇ／ｍ^２以上２０ｇ／ｍ^２以下であることが好ましく、０．２ｇ／ｍ^２以上１５ｇ／ｍ^２以下であることが更に好ましく、０．４ｇ／ｍ^２以上１２ｇ／ｍ^２以下であることが一層好ましい。この存在量は、有機溶媒が局所的に存在している場合であっても、吸収性物品用シートの全面積を基準として算出されるものである。 The abundance of the organic solvent in the absorbent article sheet is preferably 0.1 g / m ² or more, more preferably 0.2 g / m ² or more, and 0.4 g / m ² or more. Even more preferred. Further, it is preferably 20 g / m ² or less, more preferably 15 g / m ² or less, and further preferably 12 g / m ² or less. The amount of the organic solvent in the absorbent article sheet is preferably 0.1 g / m ² or more and 20 g / m ² or less, more preferably 0.2 g / m ² or more and 15 g / m ² or less. it is more preferably .4g / ^{m 2} or more 12 g / ^{m 2} or less. This abundance is calculated on the basis of the total area of the absorbent article sheet even when the organic solvent is present locally.

抗菌剤の使用量と有機溶媒の使用量との比率は、抗菌剤の質量に対して有機溶媒の質量が４倍以上であることが好ましく、５倍以上であることが更に好ましく、８倍以上であることが一層好ましい。また、１０００倍以下であることが好ましく、１００倍以下であることが更に好ましく、５０倍以下であることが一層好ましい。抗菌剤の質量に対して有機溶媒の質量は、４倍以上１０００倍以下であることが好ましく、５倍以上１００倍以下であることが更に好ましく、８倍以上５０倍以下であることが一層好ましい。両者の比率をこの範囲内に設定することで、抗菌剤の溶解性及び抗菌剤溶液の塗布しやすさが良好になり、また、噴霧時や散布時の均一塗布性が向上する点から好ましい。   The ratio of the amount of the antibacterial agent used and the amount of the organic solvent used is preferably 4 times or more, more preferably 5 times or more, and more preferably 8 times or more, with respect to the mass of the antibacterial agent. It is more preferable that Further, it is preferably 1000 times or less, more preferably 100 times or less, and even more preferably 50 times or less. The mass of the organic solvent with respect to the mass of the antibacterial agent is preferably 4 to 1000 times, more preferably 5 to 100 times, and even more preferably 8 to 50 times. . By setting the ratio between the two in this range, the solubility of the antibacterial agent and the ease of application of the antibacterial agent solution are improved, and the uniform applicability during spraying and spraying is improved.

本発明においては、吸収性物品用シートが抗菌剤及び有機溶媒を含有することに代えて、又はこれに加えて吸収性コアが抗菌剤及び有機溶媒を含有する実施形態を採用することもできる。この実施形態の場合、吸収性コアにおける抗菌剤の存在量は０．０１ｇ／ｍ^２以上であることが好ましく、０．０５ｇ／ｍ^２以上であることが更に好ましく、０．１ｇ／ｍ^２以上であることが一層好ましい。また、１０．０ｇ／ｍ^２以下であることが好ましく、５．０ｇ／ｍ^２以下であることが更に好ましく、２．０ｇ／ｍ^２以下であることが一層好ましい。吸収性コアにおける抗菌剤の存在量は０．０１ｇ／ｍ^２以上１０．０ｇ／ｍ^２以下であることが好ましく、０．０５ｇ／ｍ^２以上５．０ｇ／ｍ^２以下であることが更に好ましく、０．１ｇ／ｍ^２以上２．０ｇ／ｍ^２以下であることが一層好ましい。この存在量は、抗菌剤が局所的に存在している場合であっても、吸収性コアの全面積を基準として算出されるものである。 In this invention, it can replace with or in addition to this that the sheet | seat for absorbent articles contains an antibacterial agent and an organic solvent, and can also employ | adopt the embodiment in which an absorptive core contains an antibacterial agent and an organic solvent. In this embodiment, it is preferable that the abundance of antimicrobials in the absorbent core is 0.01 g / ^{m 2} or more, further preferably 0.05 g / ^{m 2} or more, 0.1 g / ^{m 2} or more It is more preferable that Further, it is preferably 10.0 g / m ² or less, more preferably 5.0 g / m ² or less, and further preferably 2.0 g / m ² or less. Abundance of antimicrobials in the absorbent core is more preferably not less 0.01 g / ^{m 2} or more 10.0 g / ^{m 2} or less and preferably, 0.05 g / ^{m 2} or more 5.0 g / ^{m 2} or less More preferably, it is 0.1 g / m ² or more and 2.0 g / m ² or less. This abundance is calculated on the basis of the total area of the absorbent core even when the antibacterial agent is present locally.

一方、吸収性コアにおける有機溶媒の存在量は０．０１ｇ／ｍ^２以上であることが好ましく、０．０２ｇ／ｍ^２以上であることが更に好ましく、０．０５ｇ／ｍ^２以上であることが一層好ましい。また、１０ｇ／ｍ^２以下であることが好ましく、５ｇ／ｍ^２以下であることが更に好ましく、３ｇ／ｍ^２以下であることが一層好ましい。吸収性コアにおける有機溶媒の存在量は０．０１ｇ／ｍ^２以上１０ｇ／ｍ^２以下であることが好ましく、０．０２ｇ／ｍ^２以上５ｇ／ｍ^２以下であることが更に好ましく、０．０５ｇ／ｍ^２以上３ｇ／ｍ^２以下であることが一層好ましい。この存在量は、有機溶媒が局所的に存在している場合であっても、吸収性コアの全面積を基準として算出されるものである。 On the other hand, that existing amount of the organic solvent in the absorbent core is preferably 0.01 g / ^{m 2} or more, and further preferably 0.02 g / ^{m 2} or more, 0.05 g / ^{m 2} or more Even more preferred. Further, it is preferably 10 g / m ² or less, more preferably 5 g / m ² or less, and further preferably 3 g / m ² or less. The abundance of the organic solvent in the absorbent core is preferably 0.01 g / m ² or more and 10 g / m ² or less, more preferably 0.02 g / m ² or more and 5 g / m ² or less, 0.05 g / M ² or more and 3 g / m ² or less is more preferable. This abundance is calculated based on the total area of the absorbent core even when the organic solvent is present locally.

吸収性コアに抗菌剤及び有機溶媒が含有される場合、抗菌剤の使用量と有機溶媒の使用量との比率は、吸収性物品用シートに抗菌剤及び有機溶媒が含有される場合の両者の比率と同様とすることができる。   When the absorbent core contains an antibacterial agent and an organic solvent, the ratio between the use amount of the antibacterial agent and the use amount of the organic solvent is the same as that when the absorbent article sheet contains the antibacterial agent and the organic solvent. The ratio can be similar.

吸収性コアは水を含んでいてもよいが、水の含有量は、吸収性コアの質量に対して１０質量％以下とすることが好ましい。この理由は、先に述べたとおりである。１０質量％以下の水の含有量は、周囲環境下に吸収性コアを置いたときに周囲環境から不可避的に自然に吸収される水の量に概ね等しい。吸収性コアに含まれる水の量は、上述した吸収性物品用シートに含まれる水の量と同様の方法によって測定される。   Although the absorptive core may contain water, it is preferable that content of water shall be 10 mass% or less with respect to the mass of an absorptive core. The reason for this is as described above. The content of water of 10% by mass or less is approximately equal to the amount of water that is unavoidably naturally absorbed from the surrounding environment when the absorbent core is placed in the surrounding environment. The amount of water contained in the absorbent core is measured by the same method as the amount of water contained in the absorbent article sheet described above.

抗菌剤が吸収性物品用シート及び吸収性コアのどちらに含有される場合であっても、抗菌剤としては、有機化合物が用いられることが好ましい。有機抗菌剤は、酸化亜鉛や銀含有抗菌剤等の無機抗菌剤に比べて抗菌効果が高いからである。また抗菌剤としては、疎水性のものが用いられることが好ましい。疎水性抗菌剤は、親水性抗菌剤に比べて皮膚刺激性が低いからである。親水性抗菌剤は、親水性であるがゆえに皮膚に浸透しやすく、そのことに起因して皮膚に刺激を与えやすい。これとは対照的に、疎水性抗菌剤は、疎水性であるがゆえに皮膚に浸透しづらく、皮膚の表面にとどまりやすいので、皮膚に刺激を与えづらい。抗菌剤が疎水性であるとは、２５℃の水に対する溶解度が４０ｇ以下であることを言い、好ましくは１０ｇ以下、更に好ましくは１ｇ以下であることを言う。抗菌剤の溶解度は次の方法によって測定することができる。２５℃の純水１００ｇに対して、十分乾燥させた抗菌剤を投入し、スターラー又は振とう機で撹拌して溶解させ、１時間撹拌しても溶解できない直前の投入量を、当該抗菌剤の２５℃の水に対する溶解度とする。   Regardless of whether the antibacterial agent is contained in either the absorbent article sheet or the absorbent core, an organic compound is preferably used as the antibacterial agent. This is because organic antibacterial agents have a higher antibacterial effect than inorganic antibacterial agents such as zinc oxide and silver-containing antibacterial agents. Moreover, it is preferable that a hydrophobic thing is used as an antibacterial agent. This is because the hydrophobic antibacterial agent has lower skin irritation than the hydrophilic antibacterial agent. Hydrophilic antibacterial agents are hydrophilic and thus easily penetrate into the skin, which is likely to irritate the skin. In contrast, hydrophobic antibacterial agents are hydrophobic and therefore difficult to penetrate the skin and tend to stay on the surface of the skin, making it difficult to irritate the skin. The antibacterial agent being hydrophobic means that the solubility in water at 25 ° C. is 40 g or less, preferably 10 g or less, more preferably 1 g or less. The solubility of the antibacterial agent can be measured by the following method. To 100 g of pure water at 25 ° C., a sufficiently dried antibacterial agent is charged, dissolved by stirring with a stirrer or a shaker, and the amount immediately before stirring cannot be dissolved even after stirring for 1 hour, The solubility in water at 25 ° C.

以上のとおり、本発明では有機疎水性抗菌剤を用いることが好ましい。有機疎水性抗菌剤としては、例えば以下の式（１）又は（２）で表される有機化合物を用いることが好ましい。これらの有機化合物は、抗菌効果が高く、かつ皮膚刺激性が低いからである。これらの有機化合物は１種を単独で、又は２種以上を組み合わせて用いることができる。   As described above, in the present invention, it is preferable to use an organic hydrophobic antibacterial agent. As the organic hydrophobic antibacterial agent, for example, an organic compound represented by the following formula (1) or (2) is preferably used. This is because these organic compounds have high antibacterial effects and low skin irritation. These organic compounds can be used individually by 1 type or in combination of 2 or more types.

式（１）で表される有機疎水性抗菌剤において、Ｒ^１及びＲ^２における炭素数は、メチル基、エチル基を除き、それぞれ独立に６以上であることが好ましく、８以上であることが更に好ましく、１０以上であることが一層更に好ましく、また２４以下であることが好ましく、２２以下であることが更に好ましく、２０以下であることが一層更に好ましい。具体的には、６以上２４以下であることが好ましく、８以上２２以下であることが更に好ましく、１０以上２０以下であることが一層更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (1), the number of carbon atoms in R ¹ and R ² is preferably 6 or more independently of each other except for a methyl group and an ethyl group, and preferably 8 or more. More preferably, it is 10 or more, still more preferably 24 or less, further preferably 22 or less, and still more preferably 20 or less. Specifically, it is preferably 6 or more and 24 or less, more preferably 8 or more and 22 or less, and still more preferably 10 or more and 20 or less.

式（１）で表される有機疎水性抗菌剤において、Ｒ^３及びＲ^４における炭素数は、メチル基、エチル基を除き、それぞれ独立に６以上であることが好ましく、８以上であることが更に好ましく、１０以上であることが一層更に好ましく、
また３０以下であることが好ましく、２４以下であることが更に好ましいく、２２以下であることが一層更に好ましい。具体的には、６以上３０以下であることが好ましく、８以上２４以下であることが更に好ましく、１０以上２２以下であることが一層更に好ましい。 In the organic hydrophobic antibacterial agent represented by formula (1), the number of carbon atoms in R ³ and R ⁴ is preferably independently 6 or more, and preferably 8 or more, except for a methyl group and an ethyl group. More preferably, it is still more preferably 10 or more,
Further, it is preferably 30 or less, more preferably 24 or less, and even more preferably 22 or less. Specifically, it is preferably 6 or more and 30 or less, more preferably 8 or more and 24 or less, and still more preferably 10 or more and 22 or less.

式（１）で表される有機疎水性抗菌剤において、Ｒ^３及び／又はＲ^４がアルキルアルキレンオキサイド基である場合、該基におけるアルキル基の炭素数は、６以上であることが好ましく、８以上であることが更に好ましく、また２４以下であることが好ましく、２２以下であることが更に好ましい。具体的には、６以上２４以下であることが好ましく、８以上２２以下であることが更に好ましい。アルキルアルキレンオキサイド基におけるアルキレン基の炭素数は、２以上であることが更に好ましく、また６以下であることが好ましく、４以下であることが更に好ましい。具体的には、２以上６以下であることが好ましく、２以上４以下であることが更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (1), when R ³ and / or R ⁴ is an alkylalkylene oxide group, the alkyl group in the group preferably has 6 or more carbon atoms, More preferably, it is preferably 24 or less, more preferably 22 or less. Specifically, it is preferably 6 or more and 24 or less, and more preferably 8 or more and 22 or less. The number of carbon atoms of the alkylene group in the alkylalkylene oxide group is more preferably 2 or more, preferably 6 or less, and more preferably 4 or less. Specifically, it is preferably 2 or more and 6 or less, and more preferably 2 or more and 4 or less.

式（２）で表される有機疎水性抗菌剤において、Ｒ^５における炭素数は、１以上であることが好ましく、３以上であることが更に好ましく、６以上であることが一層更に好ましく、また３０以下であることが好ましく、２４以下であることが更に好ましく、２２以下であることが一層更に好ましい。具体的には、１以上３０以下であることが好ましく、３以上２４以下であることが更に好ましく、６以上２２以下であることが一層更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), the number of carbon atoms in R ⁵ is preferably 1 or more, more preferably 3 or more, still more preferably 6 or more, It is preferably 30 or less, more preferably 24 or less, and even more preferably 22 or less. Specifically, it is preferably 1 or more and 30 or less, more preferably 3 or more and 24 or less, and even more preferably 6 or more and 22 or less.

式（２）で表される有機疎水性抗菌剤において、Ｒ^５がシクロアルキル基である場合、該基における炭素数は、６以上であることが好ましく、７以上であることが更に好ましく、また３０以下であることが好ましく、２４以下であることが更に好ましい。具体的には、６以上３０以下であることが好ましく、７以上２４以下であることが更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), when R ⁵ is a cycloalkyl group, the number of carbon atoms in the group is preferably 6 or more, more preferably 7 or more, It is preferably 30 or less, and more preferably 24 or less. Specifically, it is preferably 6 or more and 30 or less, and more preferably 7 or more and 24 or less.

式（２）で表される有機疎水性抗菌剤において、Ｒ^５がアリール基である場合、該基は、フェニル基、炭素数１〜１８のアルキル基で置換されたフェニル基、ベンジル基、炭素数１以上１８以下のアルキル基で置換されたベンジル基、炭素数７以上２４以下のフェノキシアルキル基であることが好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), when R ⁵ is an aryl group, the group is a phenyl group, a phenyl group substituted with an alkyl group having 1 to 18 carbon atoms, a benzyl group, a carbon A benzyl group substituted with an alkyl group having 1 to 18 carbon atoms and a phenoxyalkyl group having 7 to 24 carbon atoms are preferable.

式（２）で表される有機疎水性抗菌剤において、Ｒ^５がアルキルアルキレンオキサイド基である場合、該基におけるアルキル基の炭素数は、６以上であることが更に好ましく、また２４以下であることが好ましく、２２以下であることが更に好ましい。具体的には、６以上２４以下であることが好ましく、６以上２２以下であることが更に好ましい。アルキルアルキレンオキサイド基におけるアルキレン基の炭素数は、２以上であることが更に好ましく、また６以下であることが好ましく、４以下であることが更に好ましい。具体的には、２以上６以下であることが好ましく、２以上４以下であることが更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), when R ⁵ is an alkyl alkylene oxide group, the number of carbon atoms of the alkyl group in the group is more preferably 6 or more, and is 24 or less. It is preferable that it is 22 or less. Specifically, it is preferably 6 or more and 24 or less, and more preferably 6 or more and 22 or less. The number of carbon atoms of the alkylene group in the alkylalkylene oxide group is more preferably 2 or more, preferably 6 or less, and more preferably 4 or less. Specifically, it is preferably 2 or more and 6 or less, and more preferably 2 or more and 4 or less.

式（２）で表される有機疎水性抗菌剤において、Ｒ^６における炭素数は、１以上であることが好ましく、また６以下であることが好ましく、４以下であることが更に好ましい。具体的には、１以上６以下であることが好ましく、１以上４以下であることが更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), the number of carbon atoms in R ⁶ is preferably 1 or more, preferably 6 or less, and more preferably 4 or less. Specifically, it is preferably 1 or more and 6 or less, and more preferably 1 or more and 4 or less.

式（２）で表される有機疎水性抗菌剤において、Ｒ^６がシクロアルキル基である場合、該基はシクロペンチル基、シクロヘキシル基であることが更に好ましい。 In the organic hydrophobic antibacterial agent represented by the formula (2), when R ⁶ is a cycloalkyl group, the group is more preferably a cyclopentyl group or a cyclohexyl group.

式（２）で表される有機疎水性抗菌剤において、Ｘ^＋がアルカリ金属イオンである場合、その例としては、リチウムイオン、ナトリウムイオン及びカリウムイオンが挙げられる。Ｘ^＋がアルカリ土類金属イオンである場合、その例としては、マグネシウムイオン、カルシウムイオン及びストロンチウムイオンが挙げられる。Ｘ^＋が２価以上４価以下のカチオンである場合、その例としては、エタノールアミン、ジエタノールアミン、トリエタノールアミン、Ｎ置換エタノールアミン、Ｎ置換ジエタノールアミン、トリスヒドロキシアミノメタン、グアニジン、エチレンジアミン、ヘキサメチレンジアミン、ヘキサメチレンテトラミン等のアミンのプロトン塩（アミンにＨ^＋が付加したもの）が挙げられる。 In the organic hydrophobic antibacterial agent represented by the formula (2), when X ⁺ is an alkali metal ion, examples thereof include lithium ion, sodium ion and potassium ion. When X ⁺ is an alkaline earth metal ion, examples thereof include magnesium ion, calcium ion, and strontium ion. When X ⁺ is a divalent to tetravalent cation, examples thereof include ethanolamine, diethanolamine, triethanolamine, N-substituted ethanolamine, N-substituted diethanolamine, trishydroxyaminomethane, guanidine, ethylenediamine, hexamethylenediamine. And a proton salt of an amine such as hexamethylenetetramine (a compound obtained by adding H ⁺ to an amine).

式（１）で表される有機疎水性抗菌剤の具体例としては、セチルリン酸ベンザルコニウムが挙げられる。セチルリン酸ベンザルコニウムとしては、花王株式会社より商品名サニゾールＰとして販売されている抗菌剤を用いることができる。一方、式（２）で表される有機疎水性抗菌剤の具体例としては、１−ヒドロキシ−４−メチル−６−（２，４，４−トリメチルペンチル）−２（１Ｈ）−ピリドン モノエタノールアミン塩〔1-Hydroxy-4-methyl-6-(2,4,4-trimethyl-pentyl)-2(1H)-pyridone; combination with 2-aminoethanol(1:1)〕（ＣＡＳ登録番号６８８９０−６６−４、別名ピロクトンオラミン）が挙げられる。この抗菌剤は式（２Ａ）で表され、クラリアント社により商品名オクトピロックスとして販売されている   Specific examples of the organic hydrophobic antibacterial agent represented by the formula (1) include benzalkonium cetyl phosphate. As the benzalkonium cetyl phosphate, an antibacterial agent sold as trade name Sanizole P by Kao Corporation can be used. On the other hand, specific examples of the organic hydrophobic antibacterial agent represented by the formula (2) include 1-hydroxy-4-methyl-6- (2,4,4-trimethylpentyl) -2 (1H) -pyridone monoethanol. Amine salt [1-Hydroxy-4-methyl-6- (2,4,4-trimethyl-pentyl) -2 (1H) -pyridone; combination with 2-aminoethanol (1: 1)] (CAS registration number 68890-66 -4, also known as piroctone olamine). This antibacterial agent is represented by the formula (2A) and is sold under the trade name Octopirox by Clariant.

前記以外の有機疎水性抗菌剤としては、例えば５−クロロ−２−［２，４−ジクロロフェノキシ］フェノールが挙げられる。この化合物はトリクロサンとも呼ばれている。   Examples of organic hydrophobic antibacterial agents other than the above include 5-chloro-2- [2,4-dichlorophenoxy] phenol. This compound is also called triclosan.

有機疎水性抗菌剤を基材シート及び／又は吸収性コアに付着させることを目的として、本発明においては、有機疎水性抗菌剤を有機溶媒に溶解して抗菌剤溶液となし、この抗菌剤溶液を基材シート及び／又は吸収性コアに含有させる工程を採用することが好ましい。抗菌剤溶液は、有機疎水性抗菌剤を完全溶解している溶液であることが好ましい。未溶解の有機疎水性抗菌剤が抗菌剤溶液に存在している場合には、そのような抗菌剤溶液を基材シート及び／又は吸収性コアに含有させると、有機疎水性抗菌剤が不均一に付着してしまう可能性がある。   In order to adhere the organic hydrophobic antibacterial agent to the base sheet and / or the absorbent core, in the present invention, the organic hydrophobic antibacterial agent is dissolved in an organic solvent to form an antibacterial agent solution. It is preferable to employ a step of incorporating selenium into the base sheet and / or absorbent core. The antibacterial agent solution is preferably a solution in which the organic hydrophobic antibacterial agent is completely dissolved. When undissolved organic hydrophobic antibacterial agent is present in the antibacterial agent solution, the organic hydrophobic antibacterial agent is non-uniform when such antibacterial agent solution is included in the base sheet and / or the absorbent core. There is a possibility of sticking to.

抗菌剤溶液に含まれる有機溶媒は２５℃において液体のものであることが好ましい。有機溶媒としては、有機疎水性抗菌剤を溶解し得るものが用いられる。特に、有機疎水性抗菌剤の溶解度が好ましくは５質量％以上、更に好ましくは１０質量％以上、一層好ましくは１５質量％以上である有機溶媒を用いることが有利である。ここで、溶解度がＸ質量％であるとは、１００ｇの有機溶媒に対してＸｇ以上の有機疎水性抗菌剤が溶解することをいう。有機疎水性抗菌剤の溶解度が温度に依存して変化する場合には、抗菌剤溶液を基材シート及び／又は吸収性コアに含有させるときの温度における溶解度が上述のとおりであることが好ましい。   The organic solvent contained in the antibacterial agent solution is preferably a liquid at 25 ° C. As the organic solvent, those capable of dissolving the organic hydrophobic antibacterial agent are used. In particular, it is advantageous to use an organic solvent in which the solubility of the organic hydrophobic antibacterial agent is preferably 5% by mass or more, more preferably 10% by mass or more, and even more preferably 15% by mass or more. Here, the solubility of X mass% means that an organic hydrophobic antibacterial agent of X g or more dissolves in 100 g of an organic solvent. When the solubility of the organic hydrophobic antibacterial agent changes depending on the temperature, the solubility at the temperature when the antibacterial agent solution is contained in the base sheet and / or the absorbent core is preferably as described above.

有機疎水性抗菌剤の溶解性を十分に確保する観点から、有機溶媒はその溶解度パラメータが１２以上であることが好ましく、１３以上であることが更に好ましく、１３．５以上であることが一層好ましく、１４以上であることが更に一層好ましい。また溶解度パラメータは２８以下であることが好ましく、２７以下であることが更に好ましく、２６以下であることが一層好ましく、２５以下であることが更に一層好ましい。具体的には、溶解度パラメータは１２以上２８以下であることが好ましく、１３以上２７以下であることが更に好ましく、１３．５以上２６以下であることが一層好ましく、１４以上２５以下であることが更に一層好ましいい。溶解度パラメータとは、Fedorsの方法［R.F.Fedors, Polym. Eng. Sci., 14, 147(1974)］により計算され、単位は（ｃａｌ／ｃｍ³）^1/2で表されるものである。溶解度パラメータは、有機疎水性抗菌剤と有機溶媒との親和性を表す指標の一つであり、この値が近いほど両者の相溶性が高いことを示す。 From the viewpoint of sufficiently ensuring the solubility of the organic hydrophobic antibacterial agent, the solubility parameter of the organic solvent is preferably 12 or more, more preferably 13 or more, and even more preferably 13.5 or more. 14 or more is even more preferable. The solubility parameter is preferably 28 or less, more preferably 27 or less, still more preferably 26 or less, and even more preferably 25 or less. Specifically, the solubility parameter is preferably 12 or more and 28 or less, more preferably 13 or more and 27 or less, still more preferably 13.5 or more and 26 or less, and more preferably 14 or more and 25 or less. Even more preferable. The solubility parameter is calculated by the method of Fedors [RFFedors, Polym. Eng. Sci., 14, 147 (1974)], and the unit is represented by (cal / cm ³ ) ^1/2 . The solubility parameter is one of the indexes representing the affinity between the organic hydrophobic antibacterial agent and the organic solvent, and the closer the value, the higher the compatibility between the two.

有機溶媒の溶解度パラメータδは次式で求められる。
δ＝（ΔＥ／Ｖ）^1/2 （ｃａｌ／ｃｍ³）^1/2
式中、ΔＥは蒸発エネルギーを表し、Ｖはモル体積を表す。 The solubility parameter δ of the organic solvent is obtained by the following equation.
δ = (ΔE / V) ^1/2 (cal / cm ³ ) ^1/2
In the formula, ΔE represents evaporation energy, and V represents molar volume.

２種類以上の有機溶媒を用いる場合には、以下に示す混合物の溶解度パラメータδ_mixが、上述の値以上であることが好ましい。
δ_mix＝Σδ_iφ_i （ｃａｌ／ｃｍ³）^1/2
式中、δ_iは混合物を構成する各有機溶媒の溶解度パラメータを表し、φはその成分の体積分率を表す。 When two or more kinds of organic solvents are used, it is preferable that the solubility parameter δ _{mix of the} mixture shown below is not less than the above value.
δ _mix = Σδ _i φ _i (cal / cm ³ ) ^1/2
In the formula, δ _i represents the solubility parameter of each organic solvent constituting the mixture, and φ represents the volume fraction of the component.

有機溶媒は、揮発性が低いことが好ましい。揮発性の高い有機溶媒を用いると、吸収性物品用シート及び／又は吸収性コアの製造過程において有機溶媒が揮発することがあるので、製造設備に排気装置を付設する必要が生じてしまう。これに対して揮発性の低い有機溶媒を用いれば、そのような装置の付設は不要である。また揮発性の高い有機溶媒は、引火や爆発のおそれがあることから、製造装置に防爆装置を付設する必要があるが、揮発性の低い有機溶媒を用いれば、そのような装置の付設も不要である。このように、揮発性の低い有機溶媒を用いることで、抗菌剤溶液を基材シート及び／又は吸収性コアに含有させた後、有機溶媒を吸収性物品用シート及び／又は吸収性物品中（吸収性コア中）に残留させたままにしておくことができる。   The organic solvent is preferably low in volatility. When an organic solvent having high volatility is used, the organic solvent may volatilize during the manufacturing process of the absorbent article sheet and / or the absorbent core, and thus it is necessary to attach an exhaust device to the manufacturing facility. On the other hand, if an organic solvent having low volatility is used, it is unnecessary to provide such an apparatus. In addition, because highly volatile organic solvents can ignite or explode, it is necessary to attach an explosion-proof device to the manufacturing equipment. However, if a low-volatile organic solvent is used, it is not necessary to install such equipment. It is. Thus, by using an organic solvent having low volatility, the organic solvent is contained in the absorbent article sheet and / or absorbent article after the antibacterial agent solution is contained in the base sheet and / or absorbent core ( Can remain in the absorbent core).

以上の観点から、有機溶媒は、２５℃における蒸気圧が３０Ｐａ以下であることが好ましい。２５℃における蒸気圧が３０Ｐａ以下である有機溶媒を、本発明においては「不揮発性の有機溶媒」と呼ぶこととする。特に、有機溶媒は２５℃における蒸気圧が、２０Ｐａ以下であることが更に好ましく、１５Ｐａ以下であることが一層好ましく、１０Ｐａ以下であることが更に一層好ましい。   From the above viewpoint, the organic solvent preferably has a vapor pressure at 25 ° C. of 30 Pa or less. An organic solvent having a vapor pressure at 25 ° C. of 30 Pa or less is referred to as a “nonvolatile organic solvent” in the present invention. In particular, the organic solvent preferably has a vapor pressure at 25 ° C. of 20 Pa or less, more preferably 15 Pa or less, and even more preferably 10 Pa or less.

吸収性物品用シート及び／又は吸収性コアの製造過程における安全性の確保の観点から、有機溶媒はその引火点が高いことが好ましい。引火点の高い有機溶媒を用いることで、簡易な設備で吸収性物品用シート及び／又は吸収性コアを製造することができる。有機溶媒の引火点は、具体的には１００℃以上であることが好ましく、１０５℃以上であることが更に好ましく、１１０℃以上であることが一層好ましく、１１５℃以上であることが更に一層好ましい。引火点とは、可燃性蒸気が爆発下限値の濃度に達する液温のことであり、ＪＩＳ Ｋ２２６５ クリーブランド開放式引火点測定試験に準じて測定される。   From the viewpoint of ensuring safety in the manufacturing process of the absorbent article sheet and / or the absorbent core, the organic solvent preferably has a high flash point. By using an organic solvent having a high flash point, the absorbent article sheet and / or the absorbent core can be produced with simple equipment. Specifically, the flash point of the organic solvent is preferably 100 ° C. or higher, more preferably 105 ° C. or higher, even more preferably 110 ° C. or higher, and even more preferably 115 ° C. or higher. . The flash point is a liquid temperature at which combustible vapor reaches the concentration of the lower explosion limit, and is measured according to the JIS K2265 Cleveland open-type flash point measurement test.

吸収性物品用シート及び／又は吸収性コアの製造過程における有機溶媒のハンドリング性を良好なものとする観点から、該有機溶媒は、その分子量が低いことが好ましい。有機溶媒が高分子量になると、その粘度が上昇しハンドリング性が低下する傾向にある。有機溶媒の分子量は、具体的には２００未満であることが好ましく、１５０未満であることが更に好ましく、１００未満であることが一層好ましく、９１未満であることが更に一層好ましい。   From the viewpoint of improving the handleability of the organic solvent in the manufacturing process of the absorbent article sheet and / or the absorbent core, the organic solvent preferably has a low molecular weight. When the organic solvent has a high molecular weight, its viscosity increases and the handling property tends to decrease. Specifically, the molecular weight of the organic solvent is preferably less than 200, more preferably less than 150, even more preferably less than 100, and still more preferably less than 91.

分子量と同様の観点から、有機溶媒は適切な粘度を有しハンドリング性が良好であることが好ましい。有機溶媒が過度に高粘度であるとハンドリング性が低下する傾向にある。逆に過度に低粘度であると、有機溶媒が基材シート及び／又は吸収性コアに定着しづらくなり、有機疎水性抗菌剤を基材シート及び／又は吸収性コアに均一に付与しづらくなる。これらの観点から、有機溶媒は、２５℃における粘度が、５ｍＰａ・ｓ以上であることが好ましく、１０ｍＰａ・ｓ以上であることが更に好ましく、３０ｍＰａ・ｓ以上であることが一層好ましく、６０ｍＰａ・ｓ以上であることが更に一層好ましい。また有機溶媒は、２５℃における粘度が、１５００ｍＰａ・ｓ以下であることが好ましく、５００ｍＰａ・ｓ以下であることが更に好ましく、３００ｍＰａ・ｓ以下であることが一層好ましく、９０ｍＰａ・ｓ以下であることが更に一層好ましい。具体的には、有機溶媒は、２５℃における粘度が、５ｍＰａ・ｓ以上１５００ｍＰａ・ｓ以下であることが好ましく、１０ｍＰａ・ｓ以上５００ｍＰａ・ｓ以下であることが更に好ましく、３０ｍＰａ・ｓ以上３００ｍＰａ・ｓ以下であることが一層好ましく、６０ｍＰａ・ｓ以上９０ｍＰａ・ｓ以下であることが更に一層好ましい。有機溶媒の粘度は、２５℃において、東機産業株式会社製Ｂ形やＴＶＢ形粘度計によって測定することができる。ここで、有機溶媒が親水性であるとは、２５℃の水に対する有機溶媒の溶解度が１０質量％以上であることを言う。有機溶媒の溶解度は次の方法によって測定することができる。２５℃の純水１００ｇに対して、有機溶媒を投入し、スターラー又は振とう機で撹拌して溶解させ、１０分撹拌しても溶解できない直前の投入量を、当該抗菌剤の２５℃の水に対する溶解度とする。   From the same viewpoint as the molecular weight, the organic solvent preferably has an appropriate viscosity and good handleability. When the organic solvent has an excessively high viscosity, the handling property tends to decrease. On the other hand, if the viscosity is excessively low, it becomes difficult for the organic solvent to be fixed to the base sheet and / or the absorbent core, and it becomes difficult to uniformly apply the organic hydrophobic antibacterial agent to the base sheet and / or the absorbent core. . From these viewpoints, the organic solvent has a viscosity at 25 ° C. of preferably 5 mPa · s or more, more preferably 10 mPa · s or more, still more preferably 30 mPa · s or more, and 60 mPa · s. The above is even more preferable. The organic solvent preferably has a viscosity at 25 ° C. of 1500 mPa · s or less, more preferably 500 mPa · s or less, still more preferably 300 mPa · s or less, and 90 mPa · s or less. Is even more preferred. Specifically, the viscosity at 25 ° C. of the organic solvent is preferably 5 mPa · s or more and 1500 mPa · s or less, more preferably 10 mPa · s or more and 500 mPa · s or less, and 30 mPa · s or more and 300 mPa · s or less. s or less is more preferable, and 60 mPa · s or more and 90 mPa · s or less is even more preferable. The viscosity of the organic solvent can be measured at 25 ° C. using a B type or TVB type viscometer manufactured by Toki Sangyo Co., Ltd. Here, that the organic solvent is hydrophilic means that the solubility of the organic solvent in water at 25 ° C. is 10% by mass or more. The solubility of the organic solvent can be measured by the following method. An organic solvent is added to 100 g of pure water at 25 ° C., and is stirred and dissolved by a stirrer or a shaker. It is set as the solubility with respect to.

有機溶媒として用いられる好ましい化合物としては、親水性を有するものが好適に挙げられる。例えば二価アルコール（ジオール）、三価アルコール（トリオール）及び四価以上のアルコールなどの多価アルコールのような水溶性有機溶媒が挙げられる。これら多価アルコールにおけるアルキル基の炭素数は、２以上であることが好ましい。また、アルキル基の炭素数は、１８以下であることが好ましく、１０以下であることが更に好ましく、４以下であることが一層好ましい。具体的には、アルキル基の炭素数は、２以上１８以下であることが好ましく、２以上１０以下であることが更に好ましく、２以上４以下であることが一層好ましい。有機溶媒は、特に、上述した親水性を有することに加えて、上述した不揮発性を有することが好ましい。   Preferred examples of the compound used as the organic solvent include those having hydrophilicity. Examples thereof include water-soluble organic solvents such as polyhydric alcohols such as dihydric alcohols (diols), trihydric alcohols (triols), and tetrahydric or higher alcohols. The number of carbon atoms of the alkyl group in these polyhydric alcohols is preferably 2 or more. The carbon number of the alkyl group is preferably 18 or less, more preferably 10 or less, and even more preferably 4 or less. Specifically, the alkyl group preferably has 2 to 18 carbon atoms, more preferably 2 to 10 carbon atoms, and even more preferably 2 to 4 carbon atoms. In particular, the organic solvent preferably has the above-described non-volatility in addition to the above-described hydrophilicity.

特に多価アルコールのうち、炭素数が２以上４以下である低級二価アルコールを用いることが好ましい。具体的には、エチレングリコール、プロピレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の親水性有機溶媒を用いることが好ましい。これらの親水性有機溶媒は、人体に対する安全性が高く、悪臭を生じることがなく、除去工程が不要であり、引火や爆発のおそれが低いからである。プロピレングリコールとしては、１，２−プロピレングリコール及び１，３−プロピレングリコールを用いることができる。ブチレングリコールとしては、１，３−ブチレングリコール、１，４−ブチレングリコール及び２，３−ブチレングリコールを用いることができる。   In particular, among the polyhydric alcohols, it is preferable to use a lower dihydric alcohol having 2 to 4 carbon atoms. Specifically, it is preferable to use at least one hydrophilic organic solvent selected from the group consisting of ethylene glycol, propylene glycol, and butylene glycol. This is because these hydrophilic organic solvents are highly safe for the human body, do not cause malodor, do not require a removal step, and have a low risk of ignition or explosion. As propylene glycol, 1,2-propylene glycol and 1,3-propylene glycol can be used. As butylene glycol, 1,3-butylene glycol, 1,4-butylene glycol and 2,3-butylene glycol can be used.

抗菌剤溶液における有機疎水性抗菌剤の濃度は、０．５質量％以上であることが好ましく、１質量％以上であることが更に好ましく、３質量％以上であることが一層好ましく、５質量％以上であることが更に一層好ましい。また、抗菌剤溶液における有機疎水性抗菌剤の濃度は、５０質量％以下であることが好ましく、３５質量％以下であることが更に好ましく、２５質量％以下であることが一層好ましく、２０質量％以下であることが更に一層好ましい。具体的には、抗菌剤溶液における有機疎水性抗菌剤の濃度は、０．５質量％以上５０質量％以下であることが好ましく、１質量％以上３５質量％以下であることが更に好ましく、３質量％以上２５質量％以下であることが一層好ましく、５質量％以上２０質量％以下であることが更に一層好ましい。この濃度範囲の抗菌剤溶液を用いることで、有機疎水性抗菌剤を基材シート及び／又は吸収性コアに均一に付着させることができる。なお、上述のとおり、抗菌剤溶液に水が含まれていることは許容されるが、水の含有量は８質量％以下とすることが好ましい。   The concentration of the organic hydrophobic antibacterial agent in the antibacterial agent solution is preferably 0.5% by mass or more, more preferably 1% by mass or more, still more preferably 3% by mass or more, and 5% by mass. The above is even more preferable. The concentration of the organic hydrophobic antibacterial agent in the antibacterial agent solution is preferably 50% by mass or less, more preferably 35% by mass or less, still more preferably 25% by mass or less, and 20% by mass. More preferably, it is the following. Specifically, the concentration of the organic hydrophobic antibacterial agent in the antibacterial agent solution is preferably 0.5% by mass or more and 50% by mass or less, more preferably 1% by mass or more and 35% by mass or less. The content is more preferably no less than 25% by mass and no greater than 25% by mass, and still more preferably no less than 5% by mass and no greater than 20% by mass. By using the antibacterial agent solution in this concentration range, the organic hydrophobic antibacterial agent can be uniformly attached to the base sheet and / or the absorbent core. In addition, as above-mentioned, although it is accept | permitted that the antibacterial agent solution contains water, it is preferable that content of water shall be 8 mass% or less.

抗菌剤溶液を基材シート及び／又は吸収性コアに施すときの両者の比率は、得られる吸収性物品用シート及び／又は吸収性コアの全面積を基準として、抗菌剤溶液に含まれる有機疎水性抗菌剤及び有機溶媒の坪量がそれぞれ上述した範囲となるようにすることが好ましい。抗菌剤溶液と基材シート及び／又は吸収性コアとをこのような比率で混合することで、有機疎水性抗菌剤を基材シート及び／又は吸収性コアに均一に付着させることができる。また、両者を混合した後に、抗菌剤溶液中の有機溶媒を吸収性物品用シート及び／又は残留させたままにしても、得られる吸収性物品用シート及び／又は吸収性コアの取り扱い性、特に流動性を良好にすることができる。   When applying the antibacterial agent solution to the base sheet and / or the absorbent core, the ratio of both is based on the total area of the resulting absorbent article sheet and / or the absorbent core, and the organic hydrophobicity contained in the antibacterial agent solution It is preferable that the basis weights of the conductive antibacterial agent and the organic solvent are in the ranges described above. By mixing the antibacterial agent solution and the base sheet and / or the absorbent core at such a ratio, the organic hydrophobic antibacterial agent can be uniformly attached to the base sheet and / or the absorbent core. Moreover, after mixing both, even if the organic solvent in the antibacterial agent solution is left as it is, the handleability of the resulting absorbent article sheet and / or absorbent core, particularly, The fluidity can be improved.

抗菌剤溶液を基材シート及び／又は吸収性コアに施す方法としては、例えば部分的に施す場合には滴下法を採用することができる。全面に施す場合には噴霧法を採用することができる。その他、各種の印刷法や、抗菌剤溶液に浸漬させる方法などを採用することもできる。   As a method for applying the antibacterial agent solution to the base sheet and / or the absorbent core, for example, in the case of partial application, a dropping method can be adopted. When it is applied to the entire surface, a spraying method can be employed. In addition, various printing methods and a method of immersing in an antibacterial agent solution can also be employed.

抗菌剤溶液を基材シート及び／又は吸収性コアに施した後は、必要に応じ加熱や減圧等の手段によって有機溶媒を除去してもよい。もちろん有機溶媒を除去せずに残留させておいてもよい。有機溶媒を除去しないことは、簡易設備で目的とする部材が製造できる観点から有利である。   After the antibacterial agent solution is applied to the base sheet and / or the absorbent core, the organic solvent may be removed by means such as heating or decompression as necessary. Of course, the organic solvent may be left without being removed. Not removing the organic solvent is advantageous from the viewpoint of producing a desired member with simple equipment.

以上のとおりの手順で、目的とする吸収性物品用シート及び吸収性コアが得られる。このようにして得られた吸収性物品用シート及び吸収性コアにおいては、抗菌剤溶液が部分的に施されている状態であっても、これらの部材と尿等の体液とが接触すると、抗菌剤溶液が体液と一緒にこれらの部材中を拡散して、これらの部材の全域において高い抗菌効果が発現する。特に吸収性物品用シートを、吸収性コアを被覆するコアラップシートとして用いた場合には、該コアラップシートが体液と接触すると、抗菌剤溶液が体液と一緒にコアラップシート中を拡散し、更には吸収性コア中も拡散するので、吸収体の全域にわたって高い抗菌効果が発現する。これとは対照的に、抗菌剤を粉末状態でこれらの部材に付与しても、該抗菌剤は体液と一緒に部材中を拡散しづらいので、本発明で奏される高い抗菌効果は得られない。   The target absorbent article sheet and absorbent core are obtained by the procedure as described above. In the sheet for absorbent articles and the absorbent core obtained as described above, even when the antibacterial agent solution is partially applied, when these members come into contact with body fluids such as urine, antibacterial The agent solution diffuses in these members together with the body fluid, and a high antibacterial effect is exhibited in the entire area of these members. In particular, when the absorbent article sheet is used as a core wrap sheet that covers the absorbent core, when the core wrap sheet comes into contact with a body fluid, the antibacterial agent solution diffuses in the core wrap sheet together with the body fluid, Furthermore, since it also diffuses in the absorbent core, a high antibacterial effect is exhibited over the entire area of the absorber. In contrast, even when an antibacterial agent is applied to these members in a powder state, the antibacterial agent is difficult to diffuse through the member together with body fluids, so that the high antibacterial effect exhibited by the present invention is obtained. Absent.

本発明の吸収性物品用シート及び／又は吸収性コアを有する吸収性物品は、典型的には、着用時に着用者の肌と接触し得る液透過性の表面シートと、液不透過性ないし撥水性の裏面シートと、これら両シート間に介在配置された液保持性の吸収体とを具備している。表面シートとしては、各種の不織布又は多孔質の合成樹脂シート等を用いることができ、裏面シートとしては、ポリエチレン、ポリプロピレン、ポリ塩化ビニル等からなる合成樹脂フィルム、又は合成樹脂フィルムと不織布との複合材料等を用いることができる。吸収性物品は更に、該吸収性物品の具体的な用途に応じた各種部材を具備していてもよい。そのような部材は当業者に公知である。例えば吸収性物品を使い捨ておむつや生理用ナプキンに適用する場合には、表面シート上の左右両側部に一対又は二対以上の立体ガードを配置することができる。   An absorbent article having an absorbent article sheet and / or an absorbent core of the present invention typically has a liquid-permeable surface sheet that can come into contact with the wearer's skin when worn, and a liquid-impermeable or repellent material. An aqueous back sheet and a liquid-retaining absorbent disposed between the two sheets are provided. As the top sheet, various non-woven fabrics or porous synthetic resin sheets can be used, and as the back sheet, a synthetic resin film made of polyethylene, polypropylene, polyvinyl chloride or the like, or a composite of the synthetic resin film and the non-woven fabric. Materials and the like can be used. The absorbent article may further include various members according to specific uses of the absorbent article. Such members are known to those skilled in the art. For example, when applying an absorbent article to a disposable diaper or a sanitary napkin, a pair or two or more pairs of three-dimensional guards can be disposed on the left and right sides of the topsheet.

上述した実施形態に関し、本発明は更に以下の吸収性物品用シート、吸収性物品用シートの製造方法、吸収性物品及び吸収性物品の製造方法を開示する。
＜１＞
有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、８質量％以下の水とを含む抗菌剤溶液をシートに含有させる工程を有する吸収性物品用シートの製造方法。 In relation to the above-described embodiment, the present invention further discloses the following sheets for absorbent articles, methods for producing sheets for absorbent articles, absorbent articles, and methods for producing absorbent articles.
<1>
The manufacturing method of the sheet | seat for absorbent articles which has the process of making the sheet | seat contain the antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and non-volatile organic solvent, and 8 mass% or less of water.

＜２＞
有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、３０質量％以下の水とを含む抗菌剤溶液をシートに含有させた後、乾燥させる工程を有する吸収性物品用シートの製造方法。
＜３＞
前記有機疎水性抗菌剤が疎水性であるとは、２５℃の水に対する溶解度が４０ｇ以下であり、好ましくは１０ｇ以下、更に好ましくは１ｇ以下である前記＜１＞又は＜２＞に記載の吸収性物品用シートの製造方法。
＜４＞
前記有機溶媒が親水性であるとは、２５℃の水に対する溶解度が１０質量％以上である前記＜１＞ないし＜３＞のいずれか１に記載の吸収性物品用シートの製造方法。
＜５＞
前記有機溶媒が不揮発性であるとは、２５℃における蒸気圧が３０Ｐａ以下であり、好ましくは２０Ｐａ以下、更に好ましくは１５Ｐａ以下、一層好ましくは１０Ｐａ以下である前記＜１＞ないし＜４＞のいずれか１に記載の吸収性物品用シートの製造方法。
＜６＞
前記抗菌剤溶液を前記シートに含有させた後、
前記親水性かつ不揮発性の有機溶媒を前記シートに残留させたままにしておく前記＜１＞ないし＜５＞のいずれか１に記載の吸収性物品用シートの製造方法。 <2>
A method for producing a sheet for absorbent articles, which comprises a step of containing an antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 30% by mass or less of water and then drying the sheet. .
<3>
The organic hydrophobic antibacterial agent being hydrophobic means that the solubility in water at 25 ° C. is 40 g or less, preferably 10 g or less, more preferably 1 g or less, according to <1> or <2>. For producing a sheet for functional articles.
<4>
The said organic solvent is hydrophilic, The manufacturing method of the sheet | seat for absorbent articles in any one of said <1> thru | or <3> whose solubility with respect to 25 degreeC water is 10 mass% or more.
<5>
The organic solvent is non-volatile, wherein the vapor pressure at 25 ° C. is 30 Pa or less, preferably 20 Pa or less, more preferably 15 Pa or less, and even more preferably 10 Pa or less, in any one of <1> to <4> The manufacturing method of the sheet | seat for absorbent articles of Claim 1.
<6>
After containing the antibacterial agent solution in the sheet,
The method for producing a sheet for absorbent articles according to any one of <1> to <5>, wherein the hydrophilic and nonvolatile organic solvent is left on the sheet.

＜７＞
前記有機疎水性抗菌剤は、以下の式（１）若しくは（２）で表される有機化合物、又はトリクロサンである前記＜１＞ないし＜６＞のいずれか１に記載の吸収性物品用シートの製造方法。

＜８＞
前記親水性かつ不揮発性の有機溶媒が、プロピレングリコール、エチレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の有機溶媒である前記＜１＞ないし＜７＞のいずれか１に記載の吸収性物品用シートの製造方法。
＜９＞
抗菌剤溶液を、滴下法によってシートに部分的に施すか、噴霧法によってシートの全面に施すか、各種の印刷法によってシートに施すか、又はシートを抗菌剤溶液に浸漬させる前記＜１＞ないし＜８＞のいずれか１に記載の吸収性物品用シートの製造方法。
＜１０＞
前記＜１＞ないし＜９＞のいずれか１に記載の吸収性物品用シートの製造方法で製造された吸収性物品用シート。
＜１１＞
有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、１０質量％以下の水とを含む吸収性物品用シート。 <7>
The organic hydrophobic antibacterial agent is an organic compound represented by the following formula (1) or (2), or triclosan, wherein the absorbent article sheet according to any one of <1> to <6> is used. Production method.

<8>
The absorption according to any one of <1> to <7>, wherein the hydrophilic and nonvolatile organic solvent is at least one organic solvent selected from the group consisting of propylene glycol, ethylene glycol, and butylene glycol. For producing a sheet for functional articles.
<9>
The antibacterial agent solution is partially applied to the sheet by a dropping method, applied to the entire surface of the sheet by a spraying method, applied to the sheet by various printing methods, or the sheet is immersed in the antibacterial agent solution <1> to The manufacturing method of the sheet | seat for absorbent articles any one of <8>.
<10>
The absorbent article sheet produced by the method for producing an absorbent article sheet according to any one of <1> to <9>.
<11>
An absorbent article sheet comprising an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 10% by mass or less of water.

＜１２＞
抗菌剤が疎水性であるとは、２５℃の水に対する溶解度が好ましくは４０ｇ以下であり、好ましくは１０ｇ以下、更に好ましくは１ｇ以下である前記＜１１＞に記載の吸収性物品用シート。
＜１３＞
前記有機溶媒が親水性であるとは、２５℃の水に対する溶解度が１０質量％以上である前記＜１１＞又は＜１２＞に記載の吸収性物品用シート。
＜１４＞
前記有機溶媒が不揮発性であるとは、２５℃における蒸気圧が３０Ｐａ以下であり、好ましくは２０Ｐａ以下、更に好ましくは１５Ｐａ以下、一層好ましくは１０Ｐａ以下である前記＜１１＞ないし＜１３＞のいずれか１に記載の吸収性物品用シート。
＜１５＞
前記有機疎水性抗菌剤を０．０２ｇ／ｍ^２以上含み、
前記有機疎水性抗菌剤の存在量は０．０２ｇ／ｍ^２以上であることが好ましく、０．０４ｇ／ｍ^２以上であることが更に好ましく、０．０５ｇ／ｍ^２以上であることが一層好ましく、また、０．５ｇ／ｍ^２以下であることが好ましく、０．４ｇ／ｍ^２以下であることが更に好ましく、０．３ｇ／ｍ^２以下であることが一層好ましい前記＜１０＞ないし＜１４＞のいずれか１に記載の吸収性物品用シート。
＜１６＞
前記有機溶媒を、前記有機疎水性抗菌剤の質量の４倍以上１０００倍以下の割合で含み、
前記抗菌剤の使用量と前記有機溶媒の使用量との比率は、該抗菌剤の質量に対して該有機溶媒の質量が４倍以上であることが好ましく、５倍以上であることが更に好ましく、８倍以上であることが一層好ましい。また、１０００倍以下であることが好ましく、１００倍以下であることが更に好ましく、５０倍以下であることが一層好ましい前記＜１０＞ないし＜１５＞のいずれか１に記載の吸収性物品用シート。 <12>
The antibacterial agent is hydrophobic. The sheet for absorbent articles according to <11>, wherein the solubility in water at 25 ° C. is preferably 40 g or less, preferably 10 g or less, more preferably 1 g or less.
<13>
The said organic solvent is a sheet | seat for absorbent articles as described in said <11> or <12> whose solubility with respect to 25 degreeC water is 10 mass% or more.
<14>
The organic solvent is non-volatile that any one of the above <11> to <13>, wherein the vapor pressure at 25 ° C. is 30 Pa or less, preferably 20 Pa or less, more preferably 15 Pa or less, and even more preferably 10 Pa or less. The sheet for absorbent articles according to claim 1.
<15>
Containing 0.02 g / m ² or more of the organic hydrophobic antibacterial agent,
Preferably the abundance of the organic hydrophobic antimicrobial agent is 0.02 g / ^{m 2} or more, further preferably 0.04 g / ^{m 2} or more, more preferably at 0.05 g / ^{m 2} or more Further, it is preferably 0.5 g / m ² or less, more preferably 0.4 g / m ² or less, and still more preferably 0.3 g / m ² or less <10> to <14. > The sheet | seat for absorbent articles of any one of>.
<16>
Including the organic solvent at a ratio of 4 to 1000 times the mass of the organic hydrophobic antibacterial agent;
The ratio of the amount of the antibacterial agent used and the amount of the organic solvent used is preferably 4 times or more, more preferably 5 times or more, relative to the mass of the antibacterial agent. More preferably, it is 8 times or more. The sheet for absorbent articles according to any one of <10> to <15>, preferably 1000 times or less, more preferably 100 times or less, and even more preferably 50 times or less. .

＜１７＞
吸収性物品用シートが基材シートから構成され、該基材シートは繊維シートや、フィルムに複数の貫通孔を形成した穿孔シートであることが好ましく、繊維シートとしては、紙、不織布、織布、織物地、又はそれらの複合材が好ましい前記＜１０＞ないし＜１６＞のいずれか１に記載の吸収性物品用シート。
＜１８＞
前記有機疎水性抗菌剤は、以下の式（１）若しくは（２）で表される有機化合物、又はトリクロサンである前記＜１０＞ないし＜１７＞のいずれか１に記載の吸収性物品用シート。

＜１９＞
前記有機疎水性抗菌剤が、セチルリン酸ベンザルコニウム又はピロクトンオラミンである前記＜１０＞ないし＜１８＞のいずれか１に記載の吸収性物品用シート。
＜２０＞
前記有機溶媒として、前記有機疎水性抗菌剤を溶解し得るものが用いられ、特に、該有機疎水性抗菌剤の溶解度が好ましくは５質量％以上、更に好ましくは１０質量％以上、一層好ましくは１５質量％以上である該有機溶媒を用いる前記＜１０＞ないし＜１９＞のいずれか１に記載の吸収性物品用シート。
＜２１＞
前記有機溶媒はその溶解度パラメータが１２以上であることが好ましく、１３以上であることが更に好ましく、１３．５以上であることが一層好ましく、１４以上であることが更に一層好ましい。また溶解度パラメータは２８以下であることが好ましく、２７以下であることが更に好ましく、２６以下であることが一層好ましく、２５以下であることが更に一層好ましい前記＜１０＞ないし＜２０＞のいずれか１に記載の吸収性物品用シート。 <17>
The absorbent article sheet is composed of a base sheet, and the base sheet is preferably a fiber sheet or a perforated sheet in which a plurality of through holes are formed in the film. Examples of the fiber sheet include paper, nonwoven fabric, and woven fabric. The sheet for absorbent articles according to any one of <10> to <16>, wherein a fabric, or a composite material thereof is preferable.
<18>
The absorbent article sheet according to any one of <10> to <17>, wherein the organic hydrophobic antibacterial agent is an organic compound represented by the following formula (1) or (2) or triclosan.

<19>
The sheet for absorbent articles according to any one of <10> to <18>, wherein the organic hydrophobic antibacterial agent is benzalkonium cetyl phosphate or piroctone olamine.
<20>
As the organic solvent, those capable of dissolving the organic hydrophobic antibacterial agent are used. In particular, the solubility of the organic hydrophobic antibacterial agent is preferably 5% by mass or more, more preferably 10% by mass or more, and further preferably 15%. The sheet for absorbent articles according to any one of <10> to <19>, wherein the organic solvent that is at least% by mass is used.
<21>
The organic solvent preferably has a solubility parameter of 12 or more, more preferably 13 or more, still more preferably 13.5 or more, and still more preferably 14 or more. The solubility parameter is preferably 28 or less, more preferably 27 or less, even more preferably 26 or less, and even more preferably 25 or less, any one of the above <10> to <20> The sheet | seat for absorbent articles of 1.

＜２２＞
有機溶媒として多価アルコールが用いられ、
多価アルコールのうち、炭素数が２以上４以下である低級二価アルコールを用いることが好ましく、
具体的には、エチレングリコール、プロピレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の親水性有機溶媒を用いることが好ましい前記＜１０＞ないし＜２１＞のいずれか１に記載の吸収性物品用シート。
＜２３＞
プロピレングリコールは、１，２−プロピレングリコール及び１，３−プロピレングリコールから選ばれるからなる群から選ばれる少なくとも１種の有機溶媒であることが好ましく、
ブチレングリコールは、１，３−ブチレングリコール、１，４−ブチレングリコール及び２，３−ブチレングリコールから選ばれるからなる群から選ばれる少なくとも１種の有機溶媒であることが好ましい前記＜２２＞に記載の吸収性物品用シート。
＜２４＞
吸収性コアと、該吸収性コアの肌対向面側に配されるコアラップシートと、該コアラップシートの肌対向面側に配される表面シートとを有し、
前記コアラップシートとして前記＜１０＞ないし＜２３＞のいずれか１に記載の吸収性物品用シートを用いた吸収性物品。
＜２５＞
有機疎水性抗菌剤を親水性かつ不揮発性の有機溶媒に溶解してなる抗菌剤溶液を、吸収性コアに含有させる工程を有する吸収性物品の製造方法。
＜２６＞
前記有機疎水性抗菌剤が疎水性であるとは、２５℃の水に対する溶解度が４０ｇ以下であり、好ましくは１０ｇ以下、更に好ましくは１ｇ以下である前記＜２５＞に記載の吸収性物品の製造方法。 <22>
Polyhydric alcohol is used as the organic solvent,
Of the polyhydric alcohols, it is preferable to use a lower dihydric alcohol having 2 to 4 carbon atoms,
Specifically, it is preferable to use at least one hydrophilic organic solvent selected from the group consisting of ethylene glycol, propylene glycol, and butylene glycol, and the absorptivity according to any one of <10> to <21>. Article sheet.
<23>
Propylene glycol is preferably at least one organic solvent selected from the group consisting of 1,2-propylene glycol and 1,3-propylene glycol,
Butylene glycol is preferably at least one organic solvent selected from the group consisting of 1,3-butylene glycol, 1,4-butylene glycol, and 2,3-butylene glycol. Absorbent article sheet.
<24>
An absorbent core, a core wrap sheet disposed on the skin facing surface side of the absorbent core, and a surface sheet disposed on the skin facing surface side of the core wrap sheet,
An absorbent article using the absorbent article sheet according to any one of <10> to <23> as the core wrap sheet.
<25>
The manufacturing method of an absorbent article which has the process of making the absorptive core contain the antibacterial agent solution formed by melt | dissolving an organic hydrophobic antibacterial agent in a hydrophilic and non-volatile organic solvent.
<26>
The organic hydrophobic antibacterial agent being hydrophobic means that the solubility in water at 25 ° C. is not more than 40 g, preferably not more than 10 g, more preferably not more than 1 g, <25>. Method.

＜２７＞
前記有機溶媒が親水性であるとは、２５℃の水に対する溶解度が１０質量％以上である前記＜２５＞又は＜２６＞に記載の吸収性物品の製造方法。
＜２８＞
前記有機溶媒が不揮発性であるとは、２５℃における蒸気圧が３０Ｐａ以下であり、好ましくは２０Ｐａ以下、更に好ましくは１５Ｐａ以下、一層好ましくは１０Ｐａ以下である前記＜２５＞ないし＜２７＞のいずれか１に記載の吸収性物品の製造方法。
＜２９＞
前記抗菌剤溶液が水を含んでおり、水の含有量が該抗菌剤溶液の質量に対して８質量％以下である前記＜２５＞ないし＜２８＞のいずれか１に記載の吸収性物品の製造方法。
＜３０＞
前記抗菌剤溶液を前記吸収性コアに含有させた後、
前記親水性かつ不揮発性の有機溶媒を前記吸収性コアに残留させたままにしておく前記＜２５＞ないし＜２９＞のいずれか１に記載の吸収性物品の製造方法。
＜３１＞
前記有機疎水性抗菌剤は、以下の式（１）若しくは（２）で表される有機化合物、又はトリクロサンである好ましい前記＜２５＞ないし＜３０＞のいずれか１に記載の吸収性物品の製造方法。

<27>
The said organic solvent is hydrophilic is the manufacturing method of the absorbent article as described in said <25> or <26> whose solubility with respect to 25 degreeC water is 10 mass% or more.
<28>
The organic solvent being non-volatile means that the vapor pressure at 25 ° C. is 30 Pa or less, preferably 20 Pa or less, more preferably 15 Pa or less, and even more preferably 10 Pa or less, in any one of <25> to <27> A method for producing an absorbent article according to claim 1.
<29>
The absorbent article according to any one of <25> to <28>, wherein the antibacterial agent solution contains water, and the water content is 8% by mass or less based on the mass of the antibacterial agent solution. Production method.
<30>
After containing the antibacterial agent solution in the absorbent core,
The method for producing an absorbent article according to any one of <25> to <29>, wherein the hydrophilic and non-volatile organic solvent is left in the absorbent core.
<31>
Preferably, the organic hydrophobic antibacterial agent is an organic compound represented by the following formula (1) or (2) or triclosan, wherein the absorbent article according to any one of the above items <25> to <30> is manufactured. Method.

＜３２＞
前記親水性かつ不揮発性の有機溶媒が、プロピレングリコール、エチレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の有機溶媒である前記＜２５＞ないし＜３１＞のいずれか１に記載の吸収性物品の製造方法。
＜３３＞
抗菌剤溶液を、滴下法によって吸収性コアに部分的に施すか、噴霧法によって吸収性コアの全面に施すか、各種の印刷法によって吸収性コアに施すか、又は吸収性コアを抗菌剤溶液に浸漬させる前記＜２５＞ないし＜３２＞のいずれか１に記載の吸収性物品の製造方法。
＜３４＞
前記＜２５＞ないし＜３３＞のいずれか１に記載の吸収性物品の製造方法で製造された吸収性物品。
＜３５＞
有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒とを含有する吸収性コアを含む吸収性物品。
＜３６＞
前記疎水性抗菌剤が疎水性であるとは、２５℃の水に対する溶解度が４０ｇ以下であり、好ましくは１０ｇ以下、更に好ましくは１ｇ以下である前記＜３４＞又は＜３５＞に記載の吸収性物品。 <32>
The absorption according to any one of <25> to <31>, wherein the hydrophilic and nonvolatile organic solvent is at least one organic solvent selected from the group consisting of propylene glycol, ethylene glycol, and butylene glycol. A method for producing an article.
<33>
The antibacterial agent solution is partially applied to the absorbent core by a dropping method, applied to the entire surface of the absorbent core by a spray method, applied to the absorbent core by various printing methods, or the absorbent core is applied to the absorbent core. The method for producing an absorbent article according to any one of <25> to <32>, wherein the absorbent article is immersed in a water.
<34>
An absorbent article manufactured by the method for manufacturing an absorbent article according to any one of <25> to <33>.
<35>
An absorbent article comprising an absorbent core containing an organic hydrophobic antibacterial agent and a hydrophilic and nonvolatile organic solvent.
<36>
The hydrophobic antibacterial agent being hydrophobic means that the solubility in water at 25 ° C. is 40 g or less, preferably 10 g or less, more preferably 1 g or less, as described in <34> or <35> Goods.

＜３７＞
前記有機溶媒が親水性であるとは、２５℃の水に対する溶解度が１０質量％以上である前記＜３４＞ないし＜３６＞のいずれか１に記載の吸収性物品。
＜３８＞
前記有機溶媒が不揮発性であるとは、２５℃における蒸気圧が３０Ｐａ以下であり、好ましくは２０Ｐａ以下、更に好ましくは１５Ｐａ以下、一層好ましくは１０Ｐａ以下である前記＜３４＞ないし＜３７＞のいずれか１に記載の吸収性物品。
＜３９＞
前記吸収性コアが水を含んでおり、水の含有量が、該吸収性コアの質量に対して１０質量％以下とすることが好ましい前記＜３４＞ないし＜３８＞のいずれか１に記載の吸収性物品。
＜４０＞
前記吸収性コアにおける前記有機疎水性抗菌剤の存在量は０．０１ｇ／ｍ^２以上であることが好ましく、０．０５ｇ／ｍ^２以上であることが更に好ましく、０．１ｇ／ｍ^２以上であることが一層好ましく、また、１０．０ｇ／ｍ^２以下であることが好ましく、５．０ｇ／ｍ^２以下であることが更に好ましく、２．０ｇ／ｍ^２以下であることが一層好ましい前記＜３４＞ないし＜３９＞のいずれか１に記載の吸収性物品。
＜４１＞
前記吸収性コアにおける前記有機溶媒の存在量は０．０１ｇ／ｍ^２以上であることが好ましく、０．０２ｇ／ｍ^２以上であることが更に好ましく、０．０５ｇ／ｍ^２以上であることが一層好ましく、また、１０ｇ／ｍ^２以下であることが好ましく、５ｇ／ｍ^２以下であることが更に好ましく、３ｇ／ｍ^２以下であることが一層好ましい前記＜３４＞ないし＜４０＞のいずれか１に記載の吸収性物品。 <37>
The absorbent article according to any one of <34> to <36>, wherein the organic solvent is hydrophilic, the solubility in water at 25 ° C. is 10% by mass or more.
<38>
The organic solvent is non-volatile that any one of the above <34> to <37>, wherein the vapor pressure at 25 ° C. is 30 Pa or less, preferably 20 Pa or less, more preferably 15 Pa or less, and even more preferably 10 Pa or less. Or an absorbent article according to claim 1.
<39>
The absorbent core according to any one of <34> to <38>, wherein the absorbent core contains water, and the water content is preferably 10% by mass or less based on the mass of the absorbent core. Absorbent article.
<40>
Preferably the abundance of the organic hydrophobic antimicrobial agent in the absorbent core is 0.01 g / ^{m 2} or more, further preferably 0.05 g / ^{m 2} or more, at 0.1 g / ^{m 2} or more More preferably, it is preferably 10.0 g / m ² or less, more preferably 5.0 g / m ² or less, and even more preferably 2.0 g / m ² or less. 34> thru | or <39> any one of the absorbent articles.
<41>
Preferably the abundance of the organic solvent in the absorbent core is 0.01 g / ^{m 2} or more, further preferably 0.02 g / ^{m 2} or more, it is 0.05 g / ^{m 2} or more More preferably, it is 10 g / m ² or less, more preferably 5 g / m ² or less, and further preferably 3 g / m ² or less, any one of the above <34> to <40> 2. The absorbent article according to 1.

＜４２＞
前記有機疎水性抗菌剤の使用量と前記有機溶媒の使用量との比率は、該有機疎水性抗菌剤の質量に対して該有機溶媒の質量が４倍以上であることが好ましく、５倍以上であることが更に好ましく、８倍以上であることが一層好ましく、また、１０００倍以下であることが好ましく、１００倍以下であることが更に好ましく、５０倍以下であることが一層好ましい前記＜３４＞ないし＜４１＞のいずれか１に記載の吸収性物品。
＜４３＞
前記吸収性コアとして、例えばフラップパルプと吸水性ポリマーとの混合積繊体、吸収性ポリマーのみの堆積体、及びフラッフパルプのみの積繊体などが挙げられる前記＜３４＞ないし＜４２＞のいずれか１に記載の吸収性物品。
＜４４＞
前記有機疎水性抗菌剤は、以下の式（１）若しくは（２）で表される有機化合物、又はトリクロサンである前記＜３４＞ないし＜４３＞のいずれか１に記載の吸収性物品。

＜４５＞
前記有機疎水性抗菌剤が、セチルリン酸ベンザルコニウム又はピロクトンオラミンである前記＜３４＞ないし＜４４＞のいずれか１に記載の吸収性物品。
＜４６＞
前記有機溶媒として、前記有機疎水性抗菌剤を溶解し得るものが用いられ、特に、該有機疎水性抗菌剤の溶解度が好ましくは５質量％以上、更に好ましくは１０質量％以上、一層好ましくは１５質量％以上である該有機溶媒を用いる前記＜３４＞ないし＜４５＞のいずれか１に記載の吸収性物品。 <42>
The ratio of the amount of the organic hydrophobic antibacterial agent used and the amount of the organic solvent used is preferably such that the mass of the organic solvent is 4 times or more with respect to the mass of the organic hydrophobic antibacterial agent, and 5 times or more. More preferably, it is 8 times or more, more preferably 1000 times or less, still more preferably 100 times or less, and even more preferably 50 times or less <34. The absorbent article according to any one of> to <41>.
<43>
Examples of the absorbent core include any of <34> to <42>, in which, for example, a mixed pile of flap pulp and a water-absorbing polymer, a deposit of only an absorbent polymer, and a pile of only fluff pulp are used. Or an absorbent article according to claim 1.
<44>
The absorbent article according to any one of <34> to <43>, wherein the organic hydrophobic antibacterial agent is an organic compound represented by the following formula (1) or (2), or triclosan.

<45>
The absorbent article according to any one of <34> to <44>, wherein the organic hydrophobic antibacterial agent is benzalkonium cetyl phosphate or piroctone olamine.
<46>
As the organic solvent, those capable of dissolving the organic hydrophobic antibacterial agent are used. In particular, the solubility of the organic hydrophobic antibacterial agent is preferably 5% by mass or more, more preferably 10% by mass or more, and further preferably 15%. The absorbent article according to any one of <34> to <45>, wherein the organic solvent is in an amount of mass% or more.

＜４７＞
前記有機溶媒はその溶解度パラメータが１２以上であることが好ましく、１３以上であることが更に好ましく、１３．５以上であることが一層好ましく、１４以上であることが更に一層好ましい。また溶解度パラメータは２８以下であることが好ましく、２７以下であることが更に好ましく、２６以下であることが一層好ましく、２５以下であることが更に一層好ましい前記＜３４＞ないし＜４６＞のいずれか１に記載の吸収性物品。
＜４８＞
有機溶媒として多価アルコールが用いられ、
多価アルコールのうち、炭素数が２以上４以下である低級二価アルコールを用いることが好ましく、
具体的には、エチレングリコール、プロピレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の親水性有機溶媒を用いることが好ましい前記＜３４＞ないし＜４７＞のいずれか１に記載の吸収性物品。
＜４９＞
プロピレングリコールは、１，２−プロピレングリコール及び１，３−プロピレングリコールから選ばれるからなる群から選ばれる少なくとも１種の有機溶媒であることが好ましく、
ブチレングリコールは、１，３−ブチレングリコール、１，４−ブチレングリコール及び２，３−ブチレングリコールから選ばれるからなる群から選ばれる少なくとも１種の有機溶媒であることが好ましい前記＜４８＞に記載の吸収性物品。 <47>
The organic solvent preferably has a solubility parameter of 12 or more, more preferably 13 or more, still more preferably 13.5 or more, and still more preferably 14 or more. The solubility parameter is preferably 28 or less, more preferably 27 or less, even more preferably 26 or less, and even more preferably 25 or less, any one of the above <34> to <46> 2. The absorbent article according to 1.
<48>
Polyhydric alcohol is used as the organic solvent,
Of the polyhydric alcohols, it is preferable to use a lower dihydric alcohol having 2 to 4 carbon atoms,
Specifically, it is preferable to use at least one hydrophilic organic solvent selected from the group consisting of ethylene glycol, propylene glycol, and butylene glycol. The absorbency according to any one of the above <34> to <47> Goods.
<49>
Propylene glycol is preferably at least one organic solvent selected from the group consisting of 1,2-propylene glycol and 1,3-propylene glycol,
Butylene glycol is preferably at least one organic solvent selected from the group consisting of 1,3-butylene glycol, 1,4-butylene glycol, and 2,3-butylene glycol, as described in <48> above. Absorbent articles.

以下、実施例により本発明を更に詳細に説明する。しかしながら本発明の範囲は、かかる実施例に制限されない。特に断らない限り、「％」及び「部」はそれぞれ「質量％」及び「質量部」を意味する。   Hereinafter, the present invention will be described in more detail with reference to examples. However, the scope of the present invention is not limited to such examples. Unless otherwise specified, “%” and “part” mean “% by mass” and “part by mass”, respectively.

〔実施例１〕
１）吸収性物品用シートの作製
坪量が１６ｇ／ｍ^２であり、幅２００ｍｍ×長さ１７０ｍｍの薄葉紙に、有機疎水性抗菌剤と、有機溶媒と、８％以下の水を含む抗菌剤溶液（オクトピロックス：１％、プロピレングリコール：９９％）をスポイトを用いて１箇所につき０．１ｇを２箇所に滴下して薄葉紙に含有させた。抗菌剤溶液を含有させる位置は、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点から３０ｍｍ離れた２箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量は表１に示すとおりとした。表１中、「ＰＧ」は「１，２−プロピレングリコール」を表す。「ＢＧ」は「１，３−ブチレングリコール」を表す。また「ｇｓｍ」は「ｇ／ｍ^２」を表す。
２）吸収体の作製
吸収性物品用シートで吸収性コアを被覆して吸収体を製造した。吸収性コアは、フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなり、サイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。 [Example 1]
1) Preparation of sheet for absorbent article Antibacterial agent solution comprising basis weight of 16 g / m ² , thin paper having a width of 200 mm × length of 170 mm, an organic hydrophobic antibacterial agent, an organic solvent, and 8% or less of water (Octopirox: 1%, propylene glycol: 99%) was added dropwise to a thin paper by adding 0.1 g per spot to two places using a dropper. The positions where the antibacterial agent solution was contained were two positions on the center line drawn parallel to the length direction and 30 mm away from the center point of the center line. The types of the organic hydrophobic antibacterial agent and organic solvent, and the total amount added to the thin paper were as shown in Table 1. In Table 1, “PG” represents “1,2-propylene glycol”. “BG” represents “1,3-butylene glycol”. “Gsm” represents “g / m ² ”.
2) Production of Absorber An absorbent body was produced by covering an absorbent core with a sheet for absorbent articles. The absorbent core is composed of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of the superabsorbent polymer of 160 g / m ² , and the size is 190 mm long × 70 mm wide, The mass was 5.0 g.

〔実施例２〕
抗菌剤溶液を含有させる位置を、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点から２０ｍｍ及び６０ｍｍ離れた４箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量は表１に示すとおりとした。これら以外は実施例１と同様にした。 [Example 2]
The positions where the antibacterial agent solution was contained were four positions on the center line drawn parallel to the length direction and 20 mm and 60 mm away from the center point of the center line. The types of the organic hydrophobic antibacterial agent and organic solvent, and the total amount added to the thin paper were as shown in Table 1. The rest was the same as in Example 1.

〔実施例３〕
１）吸収性物品用シートの準備
実施例１で用いた薄葉紙と同様の薄葉紙（幅２００ｍｍ×長さ１７０ｍｍ）を用いた。
２）吸収体の作製
フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなる吸収性コアを作成した。この吸収性コアのサイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。この吸収性コアに、有機疎水性抗菌剤と、有機溶媒と、１０％以下の水を含む抗菌剤溶液を滴下して含有させた。抗菌剤溶液を含有させる位置は、吸収性コアの肌対向面における長さ方向と平行に引いた中心線上であって、かつ該中心線の中点上の１箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに吸収性コアへのトータルの添加量は表１に示すとおりとした。この吸収性コアを、１）で準備した吸収性物品用シートで被覆して吸収体を製造した。 Example 3
1) Preparation of Absorbent Article Sheet The same thin paper (width 200 mm × length 170 mm) as the thin paper used in Example 1 was used.
2) Production of Absorbent An absorbent core made of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of superabsorbent polymer of 160 g / m ² was prepared. The size of the absorbent core was 190 mm long × 70 mm wide, and the mass was 5.0 g. In this absorbent core, an organic hydrophobic antibacterial agent, an organic solvent, and an antibacterial agent solution containing 10% or less of water were added dropwise. The position where the antibacterial agent solution was contained was on the center line drawn in parallel with the length direction on the skin facing surface of the absorbent core and at one position on the midpoint of the center line. Table 1 shows the types of the organic hydrophobic antibacterial agent and the organic solvent, and the total amount added to the absorbent core. The absorbent core was manufactured by covering the absorbent core with the absorbent article sheet prepared in 1).

〔実施例４〕
抗菌剤溶液を含有させる位置を、吸収性コアの肌対向面における長さ方向と平行に引いた中央線上であって、かつ該中央線の中点上の１箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量は表１に示すとおりとした。これら以外は実施例１と同様にした。 Example 4
The position in which the antibacterial agent solution was contained was a central line drawn in parallel with the length direction of the absorbent core on the skin-facing surface, and one position on the midpoint of the central line. The types of the organic hydrophobic antibacterial agent and organic solvent, and the total amount added to the thin paper were as shown in Table 1. The rest was the same as in Example 1.

〔実施例５〕
有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量を表１に示すとおりとした。これら以外は実施例４と同様にした。 Example 5
Table 1 shows the types of the organic hydrophobic antibacterial agent and the organic solvent, and the total amount added to the thin paper. The others were the same as in Example 4.

〔実施例６〕
坪量が１６ｇ／ｍ^２であり、幅２００ｍｍ×長さ１７０ｍｍの薄葉紙に、有機疎水性抗菌剤と、有機溶媒と、３０％以下の水を含む抗菌剤溶液（オクトピロックス：１０％、プロピレングリコール：７０％、イオン交換水２０％）をスポイトを用いて１箇所につき０．１ｇを２箇所に滴下して薄葉紙に吸収させた後、１０５℃に設定した送風乾燥機に入れ３０分乾燥を行った。抗菌剤溶液を含有させる位置は、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点から３０ｍｍ離れた２箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量は表１に示すとおりとした。
２）吸収体の作製
吸収性物品用シートで吸収性コアを被覆して吸収体を製造した。吸収性コアは、フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなり、サイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。 Example 6
An antibacterial agent solution (octopirox: 10%, propylene) containing an organic hydrophobic antibacterial agent, an organic solvent, and 30% or less of water on a thin paper having a basis weight of 16 g / m ² and a width of 200 mm × a length of 170 mm. Glycol: 70%, ion-exchanged water 20%) 0.1 g per site was dropped into two locations using a dropper and absorbed on a thin paper, then placed in a blow dryer set at 105 ° C. and dried for 30 minutes. went. The positions where the antibacterial agent solution was contained were two positions on the center line drawn parallel to the length direction and 30 mm away from the center point of the center line. The types of the organic hydrophobic antibacterial agent and organic solvent, and the total amount added to the thin paper were as shown in Table 1.
2) Production of Absorber An absorbent body was produced by covering an absorbent core with a sheet for absorbent articles. The absorbent core is composed of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of the superabsorbent polymer of 160 g / m ² , and the size is 190 mm long × 70 mm wide, The mass was 5.0 g.

〔実施例７〕
有機疎水性抗菌剤及び有機溶媒の種類、並びに薄葉紙へのトータルの添加量を表１に示すとおりとした。これら以外は実施例１と同様にした。 Example 7
Table 1 shows the types of the organic hydrophobic antibacterial agent and the organic solvent, and the total amount added to the thin paper. The rest was the same as in Example 1.

〔実施例８〕
１）吸収性物品用シートの準備
実施例１で用いた薄葉紙と同様の薄葉紙（幅２００ｍｍ×長さ１７０ｍｍ）を用いた。
２）吸収体の作製
フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなる吸収性コアを作成した。この吸収性コアのサイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。この吸収性コアに、有機疎水性抗菌剤と、有機溶媒と、１０％以下の水を含む抗菌剤溶液を含有させた。抗菌剤溶液を含有させる位置は、吸収性コアの肌対向面における長さ方向と平行に引いた中心線上であって、かつ該中心線の中点上の１箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに吸収性コアへのトータルの添加量は表１に示すとおりとした。この吸収性コアを、１）で準備した吸収性物品用シートで被覆して吸収体を製造した。 Example 8
1) Preparation of Absorbent Article Sheet The same thin paper (width 200 mm × length 170 mm) as the thin paper used in Example 1 was used.
2) Production of Absorbent An absorbent core made of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of superabsorbent polymer of 160 g / m ² was prepared. The size of the absorbent core was 190 mm long × 70 mm wide, and the mass was 5.0 g. The absorbent core contained an organic hydrophobic antibacterial agent, an organic solvent, and an antibacterial solution containing 10% or less of water. The position where the antibacterial agent solution was contained was on the center line drawn in parallel with the length direction on the skin facing surface of the absorbent core and at one position on the midpoint of the center line. Table 1 shows the types of the organic hydrophobic antibacterial agent and the organic solvent, and the total amount added to the absorbent core. The absorbent core was manufactured by covering the absorbent core with the absorbent article sheet prepared in 1).

〔実施例９〕
１）吸収性物品用シートの準備
実施例１で用いた薄葉紙と同様の薄葉紙（幅２００ｍｍ×長さ１７０ｍｍ）を用いた。
２）吸収体の作製
フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなる吸収性コアを作成した。この吸収性コアのサイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。この吸収性コアに、有機疎水性抗菌剤と、有機溶媒と、１０％以下の水を含む抗菌剤溶液を含有させた。抗菌剤溶液を含有させる位置は、吸収性コアの肌対向面における長さ方向と平行に引いた中心線上であって、かつ該中心線の中点から２０ｍｍ及び６０ｍｍ離れた４箇所の位置とした。有機疎水性抗菌剤及び有機溶媒の種類、並びに吸収性コアへのトータルの添加量は表１に示すとおりとした。この吸収性コアを、１）で準備した吸収性物品用シートで被覆して吸収体を製造した。 Example 9
1) Preparation of Absorbent Article Sheet The same thin paper (width 200 mm × length 170 mm) as the thin paper used in Example 1 was used.
2) Production of Absorbent An absorbent core made of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of superabsorbent polymer of 160 g / m ² was prepared. The size of the absorbent core was 190 mm long × 70 mm wide, and the mass was 5.0 g. The absorbent core contained an organic hydrophobic antibacterial agent, an organic solvent, and an antibacterial solution containing 10% or less of water. The positions containing the antibacterial agent solution were on the center line drawn parallel to the length direction on the skin-facing surface of the absorbent core and at four positions 20 mm and 60 mm away from the center point of the center line. . Table 1 shows the types of the organic hydrophobic antibacterial agent and the organic solvent, and the total amount added to the absorbent core. The absorbent core was manufactured by covering the absorbent core with the absorbent article sheet prepared in 1).

〔比較例１〕
本比較例は、実施例１において、抗菌剤溶液を含有させなかった薄葉紙を吸収性物品用シートとして用いた例である。これ以外は実施例１と同様にした。 [Comparative Example 1]
This comparative example is an example in which the thin paper that did not contain the antibacterial agent solution in Example 1 was used as a sheet for absorbent articles. The rest was the same as in Example 1.

〔比較例２〕
１）吸収性物品用シートの作製
幅２００ｍｍ×長さ１７０ｍｍの薄葉紙に、有機疎水性抗菌剤を散布後、スプレー糊を噴霧して該抗菌剤を固定化した。有機疎水性抗菌剤を散布した位置は、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点上の１箇所の位置とした。有機疎水性抗菌剤の種類、及び薄葉紙への添加量は表１に示すとおりとした。
２）吸収体の作製
吸収性物品用シートで吸収性コアを被覆して吸収体を製造した。吸収性コアは、フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなり、サイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。 [Comparative Example 2]
1) Preparation of sheet for absorbent article An organic hydrophobic antibacterial agent was sprayed on a thin paper sheet having a width of 200 mm and a length of 170 mm, and then the antibacterial agent was immobilized by spraying with a spray paste. The position where the organic hydrophobic antibacterial agent was sprayed was on the center line drawn in parallel with the length direction and at one position on the midpoint of the center line. Table 1 shows the types of organic hydrophobic antibacterial agents and the amount added to the thin paper.
2) Production of Absorber An absorbent body was produced by covering an absorbent core with a sheet for absorbent articles. The absorbent core is composed of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of the superabsorbent polymer of 160 g / m ² , and the size is 190 mm long × 70 mm wide, The mass was 5.0 g.

〔比較例３〕
１）吸収性物品用シートの準備
実施例１で用いた薄葉紙と同様の薄葉紙（幅２００ｍｍ×長さ１７０ｍｍ）を用いた。
２）吸収体の作製
フラッフパルプの坪量が１８０ｇ／ｍ^２であり、高吸収性ポリマーの坪量が１６０ｇ／ｍ^２である混合積繊体からなる吸収性コアを作成した。この吸収性コアのサイズは長さ１９０ｍｍ×幅７０ｍｍであり、質量が５．０ｇであった。この吸収性コアに、有機疎水性抗菌剤を散布後、スプレー糊を噴霧して該抗菌剤を固定化した。有機疎水性抗菌剤を散布した位置は、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点上の１箇所の位置とした。有機疎水性抗菌剤の種類、及び吸収性コアへの添加量は表１に示すとおりとした。この吸収性コアを、１）で準備した吸収性物品用シートで被覆して吸収体を製造した。 [Comparative Example 3]
1) Preparation of Absorbent Article Sheet The same thin paper (width 200 mm × length 170 mm) as the thin paper used in Example 1 was used.
2) Production of Absorbent An absorbent core made of a mixed fiber having a basis weight of fluff pulp of 180 g / m ² and a basis weight of superabsorbent polymer of 160 g / m ² was prepared. The size of the absorbent core was 190 mm long × 70 mm wide, and the mass was 5.0 g. After spraying the organic hydrophobic antibacterial agent on the absorbent core, spray paste was sprayed to fix the antibacterial agent. The position where the organic hydrophobic antibacterial agent was sprayed was on the center line drawn in parallel with the length direction and at one position on the midpoint of the center line. Table 1 shows the types of organic hydrophobic antibacterial agents and the amount added to the absorbent core. The absorbent core was manufactured by covering the absorbent core with the absorbent article sheet prepared in 1).

〔比較例４〕
幅２００ｍｍ×長さ１７０ｍｍの薄葉紙に、有機疎水性抗菌剤を散布後、スプレー糊を噴霧して該抗菌剤を固定化した。有機疎水性抗菌剤を散布した位置は、長さ方向と平行に引いた中心線上であって、かつ該中心線の中点から２０ｍｍ及び６０ｍｍ離れた４箇所の位置とした。有機疎水性抗菌剤の種類、及び薄葉紙への添加量は表１に示すとおりとした。これ以外は比較例２と同様とした。 [Comparative Example 4]
An organic hydrophobic antibacterial agent was sprayed on a thin paper sheet having a width of 200 mm and a length of 170 mm, and then the antibacterial agent was immobilized by spraying spray paste. The positions where the organic hydrophobic antibacterial agent was sprayed were on the center line drawn in parallel with the length direction and at four positions 20 mm and 60 mm apart from the center point of the center line. Table 1 shows the types of organic hydrophobic antibacterial agents and the amount added to the thin paper. The rest was the same as Comparative Example 2.

〔比較例５〕
有機疎水性抗菌剤の種類、及び薄葉紙への添加量を表１に示すとおりとした。これ以外は比較例２と同様とした。 [Comparative Example 5]
Table 1 shows the types of organic hydrophobic antibacterial agents and the amounts added to thin paper. The rest was the same as Comparative Example 2.

〔評価〕
実施例及び比較例で得られた吸収体について、尿臭の抑制についての官能評価を以下の手順で行った。その結果を表１に示す。 [Evaluation]
About the absorber obtained by the Example and the comparative example, sensory evaluation about suppression of urine odor was performed in the following procedures. The results are shown in Table 1.

〔尿臭の抑制についての官能評価〕
＜Ａ＞次の（ａ）ないし（ｄ）の手順で、評価に用いる尿を準備した。
（ａ）坪量２０ｇ／ｍ^２の不織布（抗菌、消臭等の特殊処理をしていないもの、サイズ：１０ｃｍ×１５ｃｍ）を準備した。
（ｂ）水で適度に湿らせた（ａ）の不織布を用いて４名のモニター（成人男性、入浴してから１２時間経過後の状態）それぞれが自身の下半身をよく拭き、肌常在菌と便由来の腸内細菌を採取した。
（ｃ）該モニター４名が採尿を行い、尿２．０ｇを（ｂ）の不織布に付着させ、ビニール袋に入れて密封し、３６℃雰囲気にて２４時間静置した。これにより（ｂ）の不織布における菌を増殖させた。
（ｄ）その後、各前記モニターが採取した尿５００ｇを混ぜ合わせ、そのうちの２０００ｇを共栓付三角フラスコに入れた。その中に（ｃ）菌を増殖させた不織布４枚を入れて、時折撹拌しながら２０分間浸漬した。
＜Ｂ＞次いで、（ｄ）の結果得られた５０ｇの尿を、実施例及び比較例で得られた吸収体の中央部に、溢れないように徐々に注入した。尿が注入された各吸収体をそれぞれ、蓋付のステンレス深型組バット３号（アズワン製）からなる容器に入れて密封した。各容器を恒温乾燥機に保管して３６℃になるように保温し６時間静置した。
６時間経過後の各容器を恒温乾燥機から取り出し、前記モニターとは別の５人のモニター（成人男女）に下記の基準で官能評価を行わせた。官能評価の具体的な方法は、まず恒温乾燥機から容器を取り出し、蓋を開けてから３０秒静置した。その後、鼻を容器に近づけて臭いを嗅ぎ、比較例１を５とした場合に、以下の基準で評価させた。数値の平均値及び中央値を算出し、各吸収体の官能評価の結果とした。
５：強い腐敗臭。
４：弱い腐敗臭。
３：尿と楽に分かる強い臭い。
２：尿と分かる弱い臭い。
１：尿と判別し難い僅かな臭い。
０：臭いがしない。 [Sensory evaluation of urine odor control]
<A> Urine used for evaluation was prepared by the following procedures (a) to (d).
(A) A non-woven fabric having a basis weight of 20 g / m ² (not subjected to special treatment such as antibacterial and deodorant, size: 10 cm × 15 cm) was prepared.
(B) Using the non-woven fabric of (a) moderately moistened with water, each of the four monitors (adult male, 12 hours after bathing) wiped their lower body well, And intestinal bacteria from stool were collected.
(C) The four monitors collected urine, and 2.0 g of urine was adhered to the non-woven fabric of (b), sealed in a plastic bag, and allowed to stand in a 36 ° C. atmosphere for 24 hours. Thereby, the microbe in the nonwoven fabric of (b) was propagated.
(D) Thereafter, 500 g of urine collected by each of the monitors was mixed, and 2000 g of the urine was placed in an Erlenmeyer flask with a stopper. 4 pieces of non-woven fabric on which (c) bacteria were grown was put therein, and immersed for 20 minutes with occasional stirring.
<B> Next, 50 g of urine obtained as a result of (d) was gradually injected into the central part of the absorbent bodies obtained in Examples and Comparative Examples so as not to overflow. Each absorbent body into which urine was injected was sealed in a container made of stainless steel deep-type assembly bat No. 3 (manufactured by ASONE) with a lid. Each container was stored in a constant temperature dryer, kept at 36 ° C. and allowed to stand for 6 hours.
Each container after the elapse of 6 hours was taken out from the constant temperature dryer, and five monitors (adult men and women) other than the monitor were subjected to sensory evaluation based on the following criteria. As a specific method for sensory evaluation, first, the container was taken out of the constant temperature dryer, and the lid was opened, and then allowed to stand for 30 seconds. Then, the nose was brought close to the container to smell it, and when Comparative Example 1 was set to 5, evaluation was made according to the following criteria. The average value and median value of the numerical values were calculated and used as the result of sensory evaluation of each absorber.
5: Strong rot odor.
4: Slight rot odor.
3: Strong odor that can be easily recognized as urine.
2: A weak odor known as urine.
1: Slight odor that is difficult to distinguish from urine.
0: Does not smell.

表中、「＋」は抗菌剤溶液を添加したことを意味し、「−」は何も添加していないことを意味する。

In the table, “+” means that an antibacterial agent solution was added, and “−” means that nothing was added.

表１に示す結果から明らかなとおり、各実施例で得られた吸収体は、抗菌剤の抗菌効果が十分に発現した結果、尿臭の抑制効果が比較例の吸収体よりも高いことが判る。   As is apparent from the results shown in Table 1, it can be seen that the absorbents obtained in each Example exhibited a higher antibacterial effect of the antibacterial agent, and thus the urine odor suppressing effect is higher than that of the absorbent of the comparative example. .

Claims (11)

有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、１０質量％以下の水とを含む吸収性物品用シート。   An absorbent article sheet comprising an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 10% by mass or less of water. 前記有機疎水性抗菌剤を０．０２ｇ／ｍ^２以上含む請求項１に記載の吸収性物品用シート。 The sheet for absorbent articles according to claim 1, comprising 0.02 g / m ² or more of the organic hydrophobic antibacterial agent. 前記有機溶媒を、前記有機疎水性抗菌剤の質量の４倍以上１０００倍以下の割合で含む請求項１又は２に記載の吸収性物品用シート。   The sheet | seat for absorbent articles of Claim 1 or 2 which contains the said organic solvent in the ratio of 4 to 1000 times the mass of the said organic hydrophobic antibacterial agent. 前記有機疎水性抗菌剤は、以下の式（１）若しくは（２）で表される有機化合物、又はトリクロサンである請求項１ないし３のいずれか一項に記載の吸収性物品用シート。

The absorbent article sheet according to any one of claims 1 to 3, wherein the organic hydrophobic antibacterial agent is an organic compound represented by the following formula (1) or (2) or triclosan.

吸収性コアと、該吸収性コアの肌対向面側に配されるコアラップシートと、該コアラップシートの肌対向面側に配される表面シートとを有し、
前記コアラップシートとして請求項１ないし４のいずれか一項に記載の吸収性物品用シートを用いた吸収性物品。 An absorbent core, a core wrap sheet disposed on the skin facing surface side of the absorbent core, and a surface sheet disposed on the skin facing surface side of the core wrap sheet,
An absorbent article using the absorbent article sheet according to any one of claims 1 to 4 as the core wrap sheet. 有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒とを含有する吸収性コアを含む吸収性物品。   An absorbent article comprising an absorbent core containing an organic hydrophobic antibacterial agent and a hydrophilic and nonvolatile organic solvent. 有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、８質量％以下の水とを含む抗菌剤溶液をシートに含有させる工程を有する吸収性物品用シートの製造方法。   The manufacturing method of the sheet | seat for absorbent articles which has the process of making the sheet | seat contain the antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and non-volatile organic solvent, and 8 mass% or less of water. 前記抗菌剤溶液を前記シートに含有させた後、
前記親水性かつ不揮発性の有機溶媒を前記シートに残留させたままにしておく請求項７に記載の吸収性物品用シートの製造方法。 After containing the antibacterial agent solution in the sheet,
The method for producing a sheet for absorbent articles according to claim 7, wherein the hydrophilic and nonvolatile organic solvent is left on the sheet. 前記親水性かつ不揮発性の有機溶媒が、プロピレングリコール、エチレングリコール、及びブチレングリコールからなる群から選ばれる少なくとも１種の有機溶媒である請求項７又は８に記載の吸収性物品用シートの製造方法。   The method for producing a sheet for absorbent articles according to claim 7 or 8, wherein the hydrophilic and nonvolatile organic solvent is at least one organic solvent selected from the group consisting of propylene glycol, ethylene glycol, and butylene glycol. . 有機疎水性抗菌剤を親水性かつ不揮発性の有機溶媒に溶解してなる抗菌剤溶液を、吸収性コアに含有させる工程を有する吸収性物品の製造方法。   The manufacturing method of an absorbent article which has the process of making the absorptive core contain the antibacterial agent solution formed by melt | dissolving an organic hydrophobic antibacterial agent in a hydrophilic and non-volatile organic solvent. 有機疎水性抗菌剤と、親水性かつ不揮発性の有機溶媒と、３０質量％以下の水とを含む抗菌剤溶液をシートに含有させた後、乾燥させる工程を有する吸収性物品用シートの製造方法。   A method for producing a sheet for absorbent articles, which comprises a step of containing an antibacterial agent solution containing an organic hydrophobic antibacterial agent, a hydrophilic and nonvolatile organic solvent, and 30% by mass or less of water and then drying the sheet. .