JP2017060901A - Electrode catalyst and method for producing same - Google Patents

Electrode catalyst and method for producing same Download PDF

Info

Publication number
JP2017060901A
JP2017060901A JP2014022809A JP2014022809A JP2017060901A JP 2017060901 A JP2017060901 A JP 2017060901A JP 2014022809 A JP2014022809 A JP 2014022809A JP 2014022809 A JP2014022809 A JP 2014022809A JP 2017060901 A JP2017060901 A JP 2017060901A
Authority
JP
Japan
Prior art keywords
noble metal
catalyst
carbon material
electrode catalyst
platinum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2014022809A
Other languages
Japanese (ja)
Inventor
允宣 内村
Masanobu Uchimura
允宣 内村
伊藤　仁
Hitoshi Ito
仁 伊藤
京谷　隆
Takashi Kyotani
隆 京谷
洋知 西原
Hirotomo Nishihara
洋知 西原
弘行 糸井
Hiroyuki Itoi
弘行 糸井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tohoku University NUC
Nissan Motor Co Ltd
Original Assignee
Tohoku University NUC
Nissan Motor Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tohoku University NUC, Nissan Motor Co Ltd filed Critical Tohoku University NUC
Priority to JP2014022809A priority Critical patent/JP2017060901A/en
Priority to PCT/JP2015/050968 priority patent/WO2015118922A1/en
Publication of JP2017060901A publication Critical patent/JP2017060901A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an electrode catalyst with desired catalytic activity to be used in a fuel cell, in a solid polymer type fuel cell using a proton conductivity solid polymer membrane.SOLUTION: An electrode catalyst according to the present invention is obtained by having a carbon material loaded with a noble metal, the electrode catalyst being produced by bringing a carbon material and an organic noble metal complex in a gaseous form into contact, having the carbon material loaded with the organic noble metal complex, and by reducing the loaded organic noble metal complex. An average particle diameter of the loaded noble metal is 1 nm or less and the loading density of the noble metal is 5-60% by mass relative to the mass of the electrode catalyst.SELECTED DRAWING: None

Description

本発明は、電極触媒およびその製造方法に関する。より詳細には、本発明は、燃料電池に用いられる電極触媒の触媒活性を向上させるための技術に関する。   The present invention relates to an electrode catalyst and a method for producing the same. More specifically, the present invention relates to a technique for improving the catalytic activity of an electrode catalyst used in a fuel cell.

プロトン伝導性固体高分子膜を用いた固体高分子形燃料電池は、例えば、固体酸化物形燃料電池や溶融炭酸塩形燃料電池など、他のタイプの燃料電池と比較して低温で作動する。このため、固体高分子形燃料電池は、定置用電源や、自動車などの移動体用動力源として期待されており、その実用も開始されている。   A solid polymer fuel cell using a proton conductive solid polymer membrane operates at a lower temperature than other types of fuel cells such as a solid oxide fuel cell and a molten carbonate fuel cell. For this reason, the polymer electrolyte fuel cell is expected as a stationary power source or a power source for a moving body such as an automobile, and its practical use has been started.

このような固体高分子形燃料電池には、一般的に、Ｐｔ（白金）やＰｔ合金に代表される高価な貴金属触媒が用いられており、このような燃料電池の高価格要因となっている。このため、貴金属触媒の使用量を低減して、燃料電池の低コスト化が可能な技術の開発が求められている。   In such a polymer electrolyte fuel cell, generally, an expensive noble metal catalyst represented by Pt (platinum) or a Pt alloy is used, which is a high cost factor of such a fuel cell. . For this reason, development of a technique capable of reducing the cost of fuel cells by reducing the amount of noble metal catalyst used is required.

例えば、特許文献１では、カーボン担体をアンモニアガス雰囲気下で熱処理した後、当該カーボン担体を白金塩溶液と接触させ、得られたカーボン担体を不活性ガス雰囲気下で熱処理してなる、燃料電池用電極触媒の製造方法が開示されている。当該文献によれば、アンモニアガス雰囲気下での熱処理により、カーボン担体表面に白金塩を吸着することができる官能基が導入され、白金が担体表面に均一に分散・分布される。これにより、凝集やシンタリングによる白金粒子の比表面積の減少が抑制され、微小な白金粒子が担持された電極触媒が得られる。その結果、燃料電池において、白金使用量を削減しながらも高い発電効率が得られる、としている。   For example, in Patent Document 1, a carbon carrier is heat-treated in an ammonia gas atmosphere, then the carbon carrier is brought into contact with a platinum salt solution, and the obtained carbon carrier is heat-treated in an inert gas atmosphere. A method for producing an electrocatalyst is disclosed. According to this document, a functional group capable of adsorbing a platinum salt on the surface of a carbon carrier is introduced by heat treatment in an ammonia gas atmosphere, and platinum is uniformly dispersed and distributed on the surface of the carrier. Thereby, the reduction | decrease of the specific surface area of the platinum particle by aggregation and sintering is suppressed, and the electrode catalyst with which the fine platinum particle was carry | supported is obtained. As a result, in the fuel cell, high power generation efficiency can be obtained while reducing the amount of platinum used.

特開２０１２−５２９７２２号公報JP 2012-529722 A

しかしながら、上記特許文献１に記載の方法によると、電極触媒における貴金属の粒子サイズは小さくすることができるが、炭素材料に十分な量の貴金属を担持させることができず、所望の触媒活性を有する電極触媒が得られない、という問題点を有していた。   However, according to the method described in Patent Document 1, the particle size of the noble metal in the electrode catalyst can be reduced, but a sufficient amount of the noble metal cannot be supported on the carbon material and has a desired catalytic activity. There was a problem that an electrode catalyst could not be obtained.

そこで、本発明は、所望の触媒活性を有する燃料電池用電極触媒を提供することを目的とする。   Then, an object of this invention is to provide the electrode catalyst for fuel cells which has desired catalyst activity.

上記課題を解決するための、本発明の電極触媒は、炭素材料に貴金属が担持されてなる電極触媒であって、貴金属の平均粒子径は、１ｎｍ以下であり、貴金属の担持密度は、電極触媒の質量に対し、５〜６０質量％であることを特徴とする。   In order to solve the above problems, the electrode catalyst of the present invention is an electrode catalyst in which a noble metal is supported on a carbon material, the average particle diameter of the noble metal is 1 nm or less, and the noble metal loading density is an electrode catalyst. It is characterized by being 5-60 mass% with respect to the mass of.

本発明の電極触媒は、微細な貴金属粒子が高い担持密度で炭素材料に担持されているため、反応に関与する貴金属の比表面積が、従来よりも大きい。よって、本発明の電極触媒は、優れた触媒活性を発揮することができる。   In the electrode catalyst of the present invention, fine noble metal particles are supported on a carbon material at a high supporting density, and therefore, the specific surface area of the noble metal involved in the reaction is larger than before. Therefore, the electrode catalyst of the present invention can exhibit excellent catalytic activity.

本発明の一実施形態に係る固体高分子形燃料電池の基本構成を示す概略断面図である。It is a schematic sectional drawing which shows the basic composition of the polymer electrolyte fuel cell which concerns on one Embodiment of this invention. 触媒１、ブランク（ケッチェンブラックのみ）、市販の白金担持カーボン触媒（田中貴金属工業製、ＴＥＣ１０Ｅ５０Ｅ）についてのＸ線回折（ＸＲＤ）パターンを表すグラフである。It is a graph showing the X-ray-diffraction (XRD) pattern about the catalyst 1, blank (only ketjen black), and a commercially available platinum carrying | support carbon catalyst (the Tanaka Kikinzoku Kogyo make, TEC10E50E). 触媒１および２ならびに比較触媒１についての電気化学的評価を行った際のサイクリックボルタモグラムを表すグラフである。It is a graph showing the cyclic voltammogram at the time of performing electrochemical evaluation about the catalysts 1 and 2 and the comparative catalyst 1. FIG. 触媒１および２ならびに比較触媒１についてのＣＯストリッピングの結果を表すグラフである。3 is a graph showing the results of CO stripping for Catalysts 1 and 2 and Comparative Catalyst 1. 触媒１および２ならびに比較触媒１についての白金粒子の比表面積と粒子径との関係を表すグラフである。3 is a graph showing the relationship between the specific surface area of platinum particles and the particle diameter for Catalysts 1 and 2 and Comparative Catalyst 1. 比較触媒１の高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）写真である。It is a high angle scattering dark field scanning transmission electron microscope (HAADF-STEM) photograph of the comparative catalyst 1. 比較触媒１の高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）写真である。It is a high angle scattering dark field scanning transmission electron microscope (HAADF-STEM) photograph of the comparative catalyst 1. 比較触媒１の高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）写真である。It is a high angle scattering dark field scanning transmission electron microscope (HAADF-STEM) photograph of the comparative catalyst 1. 比較触媒１の高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）写真である。It is a high angle scattering dark field scanning transmission electron microscope (HAADF-STEM) photograph of the comparative catalyst 1.

＜電極触媒＞
本発明の一形態に係る電極触媒は、炭素材料に貴金属が担持されてなる。そして、貴金属の平均粒子径は、１ｎｍ以下であり、貴金属の担持密度は、電極触媒の質量に対し、５〜６０質量％であることを特徴とする。本形態の電極触媒は、従来の電極触媒と比較して、微細な貴金属粒子が高い担持密度で炭素材料に担持されているため、反応に関与する貴金属の表面積が、従来よりも大きい。よって、本形態の電極触媒は、優れた触媒活性を発揮することができる。以下、本形態の電極触媒について説明する。なお、本明細書では、「電極触媒」を、単に「触媒」とも称する。 <Electrocatalyst>
The electrode catalyst according to an embodiment of the present invention is formed by supporting a noble metal on a carbon material. And the average particle diameter of a noble metal is 1 nm or less, The supporting density of a noble metal is 5-60 mass% with respect to the mass of an electrode catalyst, It is characterized by the above-mentioned. In the electrode catalyst of this embodiment, compared with the conventional electrode catalyst, fine noble metal particles are supported on the carbon material at a high support density, so that the surface area of the noble metal involved in the reaction is larger than that of the conventional electrode catalyst. Therefore, the electrode catalyst of this embodiment can exhibit excellent catalytic activity. Hereinafter, the electrode catalyst of this embodiment will be described. In the present specification, the “electrode catalyst” is also simply referred to as “catalyst”.

［炭素材料］
本形態の電極触媒において、炭素材料は、貴金属を担持するための担体としての役割、発生した電気エネルギーを外部回路へと伝導する役割を有する。このような炭素材料は、特に限定されないが、貴金属を分散状態で担持させるのに十分な比表面積と、十分な導電性とを有するものであれば特に制限されない。具体的には、天然黒鉛、人造黒鉛、コークス、炭素繊維、グラッシーカーボン、活性炭、活性炭素繊維、カーボンブラック（ケッチェンブラック（登録商標）、ガスファーネスブラック（例えば、バルカン）、オイルファーネスブラック、チャネルブラック、ランプブラック、サーマルブラック、アセチレンブラックなど）、還元酸化黒鉛、還元酸化グラフェン、カーボンゲル、特開２０１０−２０８８８７号公報や国際公開第２００９／７５２６４号公報等に記載される方法によって製造されるナノサイズの帯状グラフェンが３次元状に規則的に連結した構造を有するゼオライト鋳型炭素（ＺＴＣ）が挙げられる。なかでも、高い担持密度で貴金属を担持させる観点から、比表面積の大きな、ケッチェンブラック（登録商標）、ゼオライト鋳型炭素（ＺＴＣ）であることが好ましい。なお、これらの炭素材料は、１種のみを単独で使用してもよいし、２種以上を組み合わせて使用しても構わない。 [Carbon material]
In the electrode catalyst of this embodiment, the carbon material has a role as a carrier for supporting a noble metal and a role of conducting generated electric energy to an external circuit. Such a carbon material is not particularly limited, and is not particularly limited as long as it has a specific surface area sufficient to support a noble metal in a dispersed state and sufficient conductivity. Specifically, natural graphite, artificial graphite, coke, carbon fiber, glassy carbon, activated carbon, activated carbon fiber, carbon black (Ketjen Black (registered trademark), gas furnace black (for example, Vulcan), oil furnace black, channel Black, lamp black, thermal black, acetylene black, etc.), reduced graphite oxide, reduced graphene oxide, carbon gel, manufactured by the method described in JP 2010-208887 A, International Publication No. 2009/75264, etc. Zeolite-templated carbon (ZTC) having a structure in which nano-sized band-shaped graphene is regularly connected in a three-dimensional manner is exemplified. Of these, Ketjen Black (registered trademark) and zeolite template carbon (ZTC) having a large specific surface area are preferable from the viewpoint of supporting a noble metal at a high support density. In addition, these carbon materials may be used individually by 1 type, and may be used in combination of 2 or more type.

炭素材料のＢＥＴ比表面積は、特に制限されないが、好ましくは９００ｍ２／ｇ以上、より好ましくは１０００〜３０００ｍ２／ｇ、さらに好ましくは１１００〜１８００ｍ２／ｇである。上記したような比表面積であれば、十分な量の貴金属を担持させることができるとともに、触媒層における良好なガス輸送性を達成することができる。なお、触媒のＢＥＴ比表面積（ｍ２／ｇ）は、後述の実施例に記載の窒素吸着法により求めることができる。 The BET specific surface area of the carbon material is not particularly limited, but is preferably 900 m 2 / g or more, more preferably 1000 to 3000 m 2 / g, and further preferably 1100 to 1800 m 2 / g. With the specific surface area as described above, a sufficient amount of noble metal can be supported and good gas transportability in the catalyst layer can be achieved. In addition, the BET specific surface area (m 2 / g) of the catalyst can be obtained by a nitrogen adsorption method described in Examples described later.

炭素材料の粒子径（平均二次粒子径）は、特に制限されないが、２０〜１００ｎｍであることが好ましい。または、担持の容易さ、触媒利用率などの観点から、炭素材料の粒子径（平均一次粒子径）は、好ましくは１〜１０ｎｍ、より好ましくは２〜５ｎｍである。かような範囲であれば、炭素材料の機械的強度が維持され、かつ、後述の触媒層を適切な範囲で制御することができる。「炭素材料の粒子径」の値としては、走査型電子顕微鏡（ＳＥＭ）や透過型電子顕微鏡（ＴＥＭ）などの観察手段を用い、数〜数十視野中に観察される粒子の粒子径の平均値として算出される値を採用するものとする。また、「粒子径」とは、粒子の中心を通りかつ粒子の輪郭線上の任意の２点間の距離のうち、最大の距離を意味するものとする。   The particle diameter (average secondary particle diameter) of the carbon material is not particularly limited, but is preferably 20 to 100 nm. Alternatively, from the viewpoint of ease of loading, catalyst utilization, and the like, the particle diameter (average primary particle diameter) of the carbon material is preferably 1 to 10 nm, more preferably 2 to 5 nm. Within such a range, the mechanical strength of the carbon material can be maintained, and the later-described catalyst layer can be controlled within an appropriate range. The value of the “particle diameter of the carbon material” is the average of the particle diameters of particles observed in several to several tens of fields using an observation means such as a scanning electron microscope (SEM) or a transmission electron microscope (TEM). A value calculated as a value is adopted. The “particle diameter” means the maximum distance among the distances between any two points passing through the center of the particle and on the particle outline.

なお、本形態における炭素材料は、必ずしも上述のような多孔質の粒子状の形態を有して必要はなく、非多孔質の炭素材料や、炭素繊維、炭素繊維から成る不織布、カーボンペーパー、カーボンクロスなどを使用しても構わない。   In addition, the carbon material in this form does not necessarily need to have a porous particulate form as described above, and is not a non-porous carbon material, carbon fiber, a nonwoven fabric made of carbon fiber, carbon paper, carbon A cloth or the like may be used.

［貴金属］
本形態において、貴金属は、電気的化学反応等の触媒として機能する。燃料電池においては、アノード触媒層に用いられる貴金属は、水素の酸化反応の触媒として機能し、カソード触媒層に用いられる貴金属は、酸素の還元反応の触媒として機能する。貴金属としては、具体的には、白金（Ｐｔ）、パラジウム（Ｐｄ）、ロジウム（Ｒｈ）、イリジウム（Ｉｒ）、ルテニウム（Ｒｕ）、オスミウム（Ｏｓ）、金（Ａｕ）、銀（Ａｇ）およびこれらの元素を少なくとも１種含有する合金が挙げられる。 [Precious metal]
In this embodiment, the noble metal functions as a catalyst such as an electrochemical reaction. In the fuel cell, the noble metal used for the anode catalyst layer functions as a catalyst for hydrogen oxidation reaction, and the noble metal used for the cathode catalyst layer functions as a catalyst for oxygen reduction reaction. Specific examples of noble metals include platinum (Pt), palladium (Pd), rhodium (Rh), iridium (Ir), ruthenium (Ru), osmium (Os), gold (Au), silver (Ag), and these. An alloy containing at least one of these elements can be used.

なかでも、触媒活性、一酸化炭素等に対する耐被毒性、耐熱性に優れ、高い触媒活性を発揮することができるといった観点から、貴金属として、白金または白金含有合金を用いることが好ましい。上記白金含有合金の場合の当該合金の組成は、合金化する金属の種類にもよるが、白金の含有量を３０〜９０原子％とし、白金と合金化する金属の含有量を１０〜７０原子％とするのがよい。なお、合金とは、一般に金属元素に１種以上の金属元素または非金属元素を加えたものであって、金属的性質をもっているものの総称である。合金の組織には、成分元素が別個の結晶となるいわば混合物である共晶合金、成分元素が完全に溶け合い固溶体となっているもの、成分元素が金属間化合物または金属と非金属との化合物を形成しているものなどがある。本形態においては、それらのいずれであってもよい。   Among these, platinum or a platinum-containing alloy is preferably used as the noble metal from the viewpoint of excellent catalytic activity, poisoning resistance to carbon monoxide, heat resistance, and high catalytic activity. The composition of the alloy in the case of the platinum-containing alloy depends on the type of metal to be alloyed, but the platinum content is 30 to 90 atomic%, and the metal content to be alloyed with platinum is 10 to 70 atoms. % Is good. In general, an alloy is a generic term for a metal element having one or more metal elements or non-metal elements added and having metallic properties. The alloy structure consists of a eutectic alloy, which is a mixture of the component elements as separate crystals, a component element completely melted into a solid solution, and a component element composed of an intermetallic compound or a compound of a metal and a nonmetal. There are things that are forming. In the present embodiment, any of them may be used.

本形態の電極触媒において、貴金属は、平均粒子径が１ｎｍ以下であることを特徴とする。なお、当該平均粒子径の下限値は、特に制限されず、２．６Å以上であればよいが、通常は０．５ｎｍ以上、好ましくは０．７ｎｍ以上、より好ましくは０．８ｎｍ以上、さらに好ましくは０．８５ｎｍ以上、最も好ましくは０．９ｎｍ以上である。貴金属の粒子サイズをこのように小さくすることによって、貴金属の比表面積が大きくなるため、より高い触媒活性を発揮させることが可能となる。なお、貴金属の平均粒子径が１ｎｍ以下と小さいと、その平均粒子径を直接測定することは困難である。よって、本明細書では、後述の実施例に記載のＣＯストリッピングによる電気化学的な評価方法により貴金属の比表面積を測定し、当該比表面積から平均粒子径を算出するものとする。特に、当該比表面積が２８０ｍ２／ｇ以上である場合に、貴金属の平均粒子径が１ｎｍ以下であるとみなす。 In the electrode catalyst of the present embodiment, the noble metal has an average particle diameter of 1 nm or less. The lower limit of the average particle diameter is not particularly limited and may be 2.6 mm or more, but is usually 0.5 nm or more, preferably 0.7 nm or more, more preferably 0.8 nm or more, and further preferably Is 0.85 nm or more, most preferably 0.9 nm or more. By reducing the particle size of the noble metal in this way, the specific surface area of the noble metal is increased, so that higher catalytic activity can be exhibited. If the average particle diameter of the noble metal is as small as 1 nm or less, it is difficult to directly measure the average particle diameter. Therefore, in this specification, the specific surface area of the noble metal is measured by an electrochemical evaluation method by CO stripping described in Examples described later, and the average particle diameter is calculated from the specific surface area. In particular, when the specific surface area is 280 m 2 / g or more, it is considered that the average particle diameter of the noble metal is 1 nm or less.

本形態の電極触媒において、貴金属の担持密度は、電極触媒の質量に対し、５〜６０質量％であり、好ましくは８〜５０質量％、より好ましくは１０〜３０質量％である。担持密度を上記範囲とすることにより、触媒のコストを抑えつつも十分な触媒活性を有する電極触媒とすることができる。なお、本明細書において、貴金属の担持密度を算出する際の、電極触媒中の貴金属の質量は、後述の実施例に記載の方法により求める。より詳細には、十分に乾燥させた電極触媒をアルカリ融解し、溶液化した後に、当該溶液中に含まれる貴金属を誘導結合プラズマ（ＩＣＰ）発光分光分析装置（エスアイアイナノテクノロジー社製、ＳＰＳ−３５００型）を用いて定量し、これを電極触媒中の貴金属の質量とする。   In the electrode catalyst of the present embodiment, the noble metal loading density is 5 to 60% by mass, preferably 8 to 50% by mass, and more preferably 10 to 30% by mass with respect to the mass of the electrode catalyst. By setting the loading density in the above range, an electrode catalyst having sufficient catalytic activity can be obtained while suppressing the cost of the catalyst. In the present specification, the mass of the noble metal in the electrode catalyst when calculating the loading density of the noble metal is determined by the method described in Examples described later. More specifically, after the fully dried electrode catalyst is alkali-melted and made into a solution, an inductively coupled plasma (ICP) emission spectroscopic analyzer (SPS-manufactured by SII Nano Technology Co., Ltd.) is added to the noble metal contained in the solution. 3500 type), and this is defined as the mass of the noble metal in the electrode catalyst.

＜電極触媒の製造方法＞
上述の本発明に係る電極触媒の製造方法は、特に制限されないが、一例として、以下の貴金属源として有機貴金属錯体を用いた新規な製造方法が挙げられる。すなわち、本発明の他の一形態に係る電極触媒の製造方法は、炭素材料と気体状の有機貴金属錯体とを接触させて、有機貴金属錯体を炭素材料に担持させる工程（以下、単に「担持工程」とも称する）と、炭素材料に担持された有機貴金属錯体を還元する工程（以下、単に「還元工程」とも称する）とを含む。この新規な製造方法によれば、微細な貴金属粒子を高い担持密度で炭素材料に担持させることができるため、上述の本形態の電極触媒の製造方法として好適である。以下、本形態の電極触媒の製造方法について説明する。 <Method for producing electrode catalyst>
Although the manufacturing method of the electrode catalyst which concerns on the above-mentioned this invention is not restrict | limited in particular, The novel manufacturing method using an organic noble metal complex as the following noble metal source is mentioned as an example. That is, the method for producing an electrode catalyst according to another aspect of the present invention includes a step of bringing a carbon material and a gaseous organic noble metal complex into contact with each other and supporting the organic noble metal complex on the carbon material (hereinafter simply referred to as “supporting step”). And a step of reducing the organic noble metal complex supported on the carbon material (hereinafter also simply referred to as “reduction step”). According to this novel manufacturing method, fine noble metal particles can be supported on the carbon material at a high supporting density, which is suitable as a method for manufacturing the above-described electrode catalyst of the present embodiment. Hereinafter, the manufacturing method of the electrode catalyst of this form is demonstrated.

［担持工程］
担持工程では、炭素材料と気体状の有機貴金属錯体とを接触させて、有機貴金属錯体を炭素材料に担持させる。 [Supporting process]
In the supporting step, the carbon material and the gaseous organic noble metal complex are brought into contact with each other to support the organic noble metal complex on the carbon material.

本形態で用いられる炭素材料は、上述の電極触媒における炭素材料と同じなので、ここでは詳細な説明を省略する。   Since the carbon material used in this embodiment is the same as the carbon material in the electrode catalyst described above, detailed description thereof is omitted here.

有機貴金属錯体は、上述の電極触媒の貴金属の原料（貴金属源）となるものである。有機貴金属錯体は、貴金属そのものよりも一般的に融点が低いため、減圧条件下において比較的低温で気体となり得る。有機貴金属錯体としては、特に制限されないが、具体的には、１，５−シクロオクタジエンジメチル白金錯体、エチレンビス（トリフェニルホスフィン）白金（０）、テトラキス（トリフェニルホスフィン）白金（０）、ビス（トリ−ｔｅｒｔ−ブチルホスフィン）白金（０）、（トリメチル）シクロペンタジエニル白金（ＩＶ）、シアン化白金（ＩＩ）、（トリメチル）メチルシクロペンタジエニル白金（ＩＶ）、（トリメチル）ペンタメチルシクロペンタジエニル白金（ＩＶ）が挙げられる。なお、これらの有機貴金属錯体は、１種のみを単独で使用してもよいし、２種以上を組み合わせて使用しても構わない。   The organic noble metal complex serves as a noble metal raw material (noble metal source) of the above-mentioned electrode catalyst. An organic noble metal complex generally has a lower melting point than the noble metal itself, and can therefore become a gas at a relatively low temperature under reduced pressure conditions. Although it does not restrict | limit especially as an organic noble metal complex, Specifically, 1, 5- cyclooctadiene dimethyl platinum complex, ethylenebis (triphenylphosphine) platinum (0), tetrakis (triphenylphosphine) platinum (0), Bis (tri-tert-butylphosphine) platinum (0), (trimethyl) cyclopentadienylplatinum (IV), platinum (II) cyanide, (trimethyl) methylcyclopentadienylplatinum (IV), (trimethyl) penta And methylcyclopentadienylplatinum (IV). These organic noble metal complexes may be used alone or in combination of two or more.

有機貴金属錯体の使用量（仕込み量）は、特に制限されないが、炭素材料の質量に対し、好ましくは３０〜１５０質量％であり、より好ましくは４０〜８０質量％である。このような量であれば、炭素材料に十分な有機貴金属錯体を担持させることができる。   The amount of use (charge amount) of the organic noble metal complex is not particularly limited, but is preferably 30 to 150% by mass and more preferably 40 to 80% by mass with respect to the mass of the carbon material. With such an amount, a sufficient organic noble metal complex can be supported on the carbon material.

本形態の製造方法では、炭素材料と気体状の有機貴金属錯体とを接触させる前に、炭素材料を減圧条件下で乾燥させることが好ましい。当該減圧条件は、特に制限されず、当業者が適宜設定することができるが、好ましくは１．０×１０−７〜１．０×１０−２Ｐａであり、より好ましくは１．０×１０−７〜１．０×１０−４Ｐａである。なお、乾燥の際の温度も特に制限されず、当業者が適宜設定することき、炭素材料に悪影響を及ぼさない範囲においては、加熱条件下で乾燥させても構わない。 In the production method of the present embodiment, it is preferable to dry the carbon material under reduced pressure conditions before bringing the carbon material into contact with the gaseous organic noble metal complex. The decompression condition is not particularly limited, and can be appropriately set by those skilled in the art, but is preferably 1.0 × 10 −7 to 1.0 × 10 −2 Pa, more preferably 1.0 × 10 10. It is −7 to 1.0 × 10 −4 Pa. In addition, the temperature at the time of drying is not particularly limited, and when appropriately set by a person skilled in the art, drying may be performed under heating conditions as long as the carbon material is not adversely affected.

炭素材料と気体状の有機貴金属錯体とを接触させる際の温度は、特に制限されないが、好ましくは４０〜２００℃であり、より好ましくは６０〜１５０℃である。上記範囲とすることにより、有機貴金属錯体の熱分解等を抑制しつつ、有機貴金属錯体を十分に気化させることができる。   Although the temperature at the time of making a carbon material and a gaseous organic noble metal complex contact is not restrict | limited, Preferably it is 40-200 degreeC, More preferably, it is 60-150 degreeC. By setting it as the said range, an organic noble metal complex can fully be vaporized, suppressing the thermal decomposition etc. of an organic noble metal complex.

炭素材料と気体状の有機貴金属錯体とを接触させる時間も、特に制限されないが、好ましくは１〜７２時間であり、より好ましくは６〜４８時間である。上記範囲とすることにより、炭素材料に担持された後の有機貴金属錯体の粒径が大きくなり過ぎず、十分な量の有機貴金属錯体を担持させることができる。   The time for contacting the carbon material with the gaseous organic noble metal complex is also not particularly limited, but is preferably 1 to 72 hours, more preferably 6 to 48 hours. By setting it as the above range, the particle diameter of the organic noble metal complex after being supported on the carbon material does not become too large, and a sufficient amount of the organic noble metal complex can be supported.

本形態における担持工程は、炭素材料と気体状の有機貴金属錯体とを接触させることができれば、その他の条件、使用する装置、操作方法等は、特に制限されない。一例を挙げると、後述の実施例のように、有機貴金属錯体を入れたガラス管Ａと炭素材料とをガラス管Ｂに入れて減圧下で封じ、当該ガラス管Ｂを加熱する方法が挙げられる。これにより、ガラス管Ａ内の有機貴金属錯体が気体状となってガラス管Ｂに充満し、炭素材料と接触することによって有機貴金属錯体が炭素材料に担持される。   If the carbon material and the gaseous organic noble metal complex can be brought into contact with each other in the present embodiment, the other conditions, the apparatus used, the operation method, and the like are not particularly limited. As an example, a glass tube A containing an organic noble metal complex and a carbon material are placed in a glass tube B, sealed under reduced pressure, and the glass tube B is heated as in the examples described later. Thereby, the organic noble metal complex in the glass tube A becomes a gas and fills the glass tube B, and the organic noble metal complex is supported on the carbon material by contacting with the carbon material.

［還元工程］
本形態の製造方法では、上記担持工程の後、炭素材料に担持された有機貴金属錯体を還元し、炭素材料に貴金属が担持された電極触媒を得る。 [Reduction process]
In the production method of this embodiment, after the supporting step, the organic noble metal complex supported on the carbon material is reduced to obtain an electrode catalyst in which the noble metal is supported on the carbon material.

本工程において、炭素材料に担持された有機貴金属錯体を還元する方法は特に制限されず、公知の方法を適宜採用することができる。一例を挙げると、後述の実施例のように、有機貴金属錯体が担持された炭素材料を減圧条件下で熱処理することによって有機貴金属錯体を還元する方法（以下、単に「熱還元法」とも称する）が挙げられる。ただし、この方法は減圧条件下のみに限定されるわけではなく、不活性雰囲気や水素雰囲気で熱処理してもよい。熱還元法における熱処理条件は、特に制限されないが、好ましい条件は以下の通りである。熱処理の際の温度は、好ましくは１５０〜４００℃であり、より好ましくは２００〜３００℃である。熱処理の際の気圧は、好ましくは１．０×１０−２Ｐａ以下であり、より好ましくは１．０×１０−７〜１．０×１０−４Ｐａである。熱処理の時間は、好ましくは０．５〜４８時間であり、より好ましくは１〜１２時間である。上記範囲内であれば、炭素材料に担持された有機貴金属錯体を十分に還元することができる。 In this step, the method for reducing the organic noble metal complex supported on the carbon material is not particularly limited, and a known method can be appropriately employed. As an example, a method of reducing an organic noble metal complex by heat-treating a carbon material carrying the organic noble metal complex under reduced pressure conditions (hereinafter also simply referred to as “thermal reduction method”) as in the examples described later. Is mentioned. However, this method is not limited only to the reduced pressure condition, and heat treatment may be performed in an inert atmosphere or a hydrogen atmosphere. The heat treatment conditions in the thermal reduction method are not particularly limited, but preferable conditions are as follows. The temperature during the heat treatment is preferably 150 to 400 ° C, more preferably 200 to 300 ° C. The atmospheric pressure during the heat treatment is preferably 1.0 × 10 −2 Pa or less, and more preferably 1.0 × 10 −7 to 1.0 × 10 −4 Pa. The heat treatment time is preferably 0.5 to 48 hours, more preferably 1 to 12 hours. Within the above range, the organic noble metal complex supported on the carbon material can be sufficiently reduced.

また、上記熱還元法以外に、有機貴金属錯体が担持された炭素材料を水素処理することによって有機貴金属錯体を還元する方法（以下、単に「水素還元法」とも称する）を用いてもよい。水素還元法における条件も、特に制限されないが、好ましくは２５〜１００℃の温度条件下で、好ましくは３０分間以上、有機貴金属錯体が担持された炭素材料と接触させる。これにより、熱還元法の場合と同様に、炭素材料に担持された有機貴金属錯体を十分に還元することができる。   In addition to the thermal reduction method, a method of reducing the organic noble metal complex by treating the carbon material carrying the organic noble metal complex with hydrogen (hereinafter also simply referred to as “hydrogen reduction method”) may be used. The conditions in the hydrogen reduction method are not particularly limited, but are preferably brought into contact with a carbon material on which an organic noble metal complex is supported under a temperature condition of 25 to 100 ° C., preferably for 30 minutes or more. Thereby, similarly to the case of the thermal reduction method, the organic noble metal complex supported on the carbon material can be sufficiently reduced.

＜燃料電池＞
上述の本発明に係る電極触媒は、従来の電極触媒と比較して、微細な貴金属粒子が高い担持密度で炭素材料に担持されているため、反応に関与する貴金属の比表面積が、従来よりも大きく、その結果、優れた触媒活性を発揮することができる。そのため、上記電極触媒を燃料電池の触媒層に使用することにより、燃料電池の発電性能を向上させることが可能である。よって、本発明の他の一形態によると、上記電極触媒を有する電極触媒層を備えた燃料電池が提供される。以下、本形態の燃料電池について説明する。 <Fuel cell>
In the electrode catalyst according to the present invention described above, since the fine noble metal particles are supported on the carbon material at a higher support density than the conventional electrode catalyst, the specific surface area of the noble metal involved in the reaction is higher than that of the conventional one. As a result, excellent catalytic activity can be exhibited. Therefore, the power generation performance of the fuel cell can be improved by using the electrode catalyst in the catalyst layer of the fuel cell. Therefore, according to another aspect of the present invention, there is provided a fuel cell including an electrode catalyst layer having the electrode catalyst. Hereinafter, the fuel cell of this embodiment will be described.

燃料電池は、一般に、膜電極接合体（ＭＥＡ）と、燃料ガスが流れる燃料ガス流路を有するアノード側セパレータと酸化剤ガスが流れる酸化剤ガス流路を有するカソード側セパレータとからなる一対のセパレータとから構成される。   A fuel cell generally includes a pair of separators comprising a membrane electrode assembly (MEA), an anode separator having a fuel gas passage through which fuel gas flows, and a cathode separator having an oxidant gas passage through which oxidant gas flows. It consists of.

図１は、本発明の一実施形態に係る固体高分子形燃料電池（ＰＥＦＣ）１の基本構成を示す概略図である。ＰＥＦＣ１は、まず、固体高分子電解質膜２と、これを挟持する一対の触媒層（アノード触媒層３ａおよびカソード触媒層３ｃ）とを有する。そして、固体高分子電解質膜２と触媒層（３ａ、３ｃ）との積層体はさらに、一対のガス拡散層（ＧＤＬ）（アノードガス拡散層４ａおよびカソードガス拡散層４ｃ）により挟持されている。このように、固体高分子電解質膜２、一対の触媒層（３ａ、３ｃ）および一対のガス拡散層（４ａ、４ｃ）は、積層された状態で膜電極接合体（ＭＥＡ）１０を構成する。   FIG. 1 is a schematic diagram showing a basic configuration of a polymer electrolyte fuel cell (PEFC) 1 according to an embodiment of the present invention. The PEFC 1 first includes a solid polymer electrolyte membrane 2 and a pair of catalyst layers (an anode catalyst layer 3a and a cathode catalyst layer 3c) that sandwich the membrane. The laminate of the solid polymer electrolyte membrane 2 and the catalyst layers (3a, 3c) is further sandwiched between a pair of gas diffusion layers (GDL) (anode gas diffusion layer 4a and cathode gas diffusion layer 4c). Thus, the polymer electrolyte membrane 2, the pair of catalyst layers (3a, 3c), and the pair of gas diffusion layers (4a, 4c) constitute a membrane electrode assembly (MEA) 10 in a stacked state.

ＰＥＦＣ１において、ＭＥＡ１０はさらに、一対のセパレータ（アノードセパレータ５ａおよびカソードセパレータ５ｃ）により挟持されている。図１において、セパレータ（５ａ、５ｃ）は、図示したＭＥＡ１０の両端に位置するように図示されている。ただし、複数のＭＥＡが積層されてなる燃料電池スタックでは、セパレータは、隣接するＰＥＦＣ（図示せず）のためのセパレータとしても用いられるのが一般的である。換言すれば、燃料電池スタックにおいてＭＥＡは、セパレータを介して順次積層されることにより、スタックを構成することとなる。なお、実際の燃料電池スタックにおいては、セパレータ（５ａ、５ｃ）と固体高分子電解質膜２との間や、ＰＥＦＣ１とこれと隣接する他のＰＥＦＣとの間にガスシール部が配置されるが、図１ではこれらの記載を省略する。   In PEFC1, the MEA 10 is further sandwiched between a pair of separators (anode separator 5a and cathode separator 5c). In FIG. 1, the separators (5 a, 5 c) are illustrated so as to be positioned at both ends of the illustrated MEA 10. However, in a fuel cell stack in which a plurality of MEAs are stacked, the separator is generally used as a separator for an adjacent PEFC (not shown). In other words, in the fuel cell stack, the MEAs are sequentially stacked via the separator to form a stack. In an actual fuel cell stack, a gas seal portion is disposed between the separator (5a, 5c) and the solid polymer electrolyte membrane 2, or between the PEFC 1 and another adjacent PEFC. These descriptions are omitted in FIG.

セパレータ（５ａ、５ｃ）は、例えば、厚さ０．５ｍｍ以下の薄板にプレス処理を施すことで図１に示すような凹凸状の形状に成形することにより得られる。セパレータ（５ａ、５ｃ）のＭＥＡ側から見た凸部はＭＥＡ１０と接触している。これにより、ＭＥＡ１０との電気的な接続が確保される。また、セパレータ（５ａ、５ｃ）のＭＥＡ側から見た凹部（セパレータの有する凹凸状の形状に起因して生じるセパレータとＭＥＡとの間の空間）は、ＰＥＦＣ１の運転時にガスを流通させるためのガス流路として機能する。具体的には、アノードセパレータ５ａのガス流路６ａには燃料ガス（例えば、水素など）を流通させ、カソードセパレータ５ｃのガス流路６ｃには酸化剤ガス（例えば、空気など）を流通させる。   The separators (5a, 5c) are obtained, for example, by forming a concavo-convex shape as shown in FIG. The convex part seen from the MEA side of the separator (5a, 5c) is in contact with the MEA 10. Thereby, the electrical connection with MEA10 is ensured. Further, a recess (space between the separator and the MEA generated due to the concavo-convex shape of the separator) viewed from the MEA side of the separator (5a, 5c) is a gas for circulating gas during operation of the PEFC 1 Functions as a flow path. Specifically, a fuel gas (for example, hydrogen) is circulated through the gas flow path 6a of the anode separator 5a, and an oxidant gas (for example, air) is circulated through the gas flow path 6c of the cathode separator 5c.

一方、セパレータ（５ａ、５ｃ）のＭＥＡ側とは反対の側から見た凹部は、ＰＥＦＣ１の運転時にＰＥＦＣを冷却するための冷媒（例えば、水）を流通させるための冷媒流路７とされる。さらに、セパレータには通常、マニホールド（図示せず）が設けられる。このマニホールドは、スタックを構成した際に各セルを連結するための連結手段として機能する。かような構成とすることで、燃料電池スタックの機械的強度が確保されうる。   On the other hand, the recess viewed from the side opposite to the MEA side of the separator (5a, 5c) serves as a refrigerant flow path 7 for circulating a refrigerant (for example, water) for cooling the PEFC during operation of the PEFC 1. . Further, the separator is usually provided with a manifold (not shown). This manifold functions as a connection means for connecting cells when a stack is formed. With such a configuration, the mechanical strength of the fuel cell stack can be ensured.

なお、図１に示す実施形態においては、セパレータ（５ａ、５ｃ）は凹凸状の形状に成形されている。ただし、セパレータは、かような凹凸状の形態のみに限定されるわけではなく、ガス流路および冷媒流路の機能を発揮できる限り、平板状、一部凹凸状などの任意の形態であってもよい。   In addition, in embodiment shown in FIG. 1, the separator (5a, 5c) is shape | molded by the uneven | corrugated shape. However, the separator is not limited to such a concavo-convex shape, and may be any form such as a flat plate shape and a partially concavo-convex shape as long as the functions of the gas flow path and the refrigerant flow path can be exhibited. Also good.

上記のような、本発明のＭＥＡを有する燃料電池は、優れた発電性能を発揮する。ここで、燃料電池の種類としては、特に限定されず、上記した説明中では固体高分子形燃料電池を例に挙げて説明したが、この他にも、アルカリ型燃料電池、ダイレクトメタノール型燃料電池、マイクロ燃料電池などが挙げられる。なかでも小型かつ高密度・高出力化が可能であるから、固体高分子形燃料電池（ＰＥＦＣ）が好ましく挙げられる。また、前記燃料電池は、搭載スペースが限定される車両などの移動体用電源の他、定置用電源などとして有用である。なかでも、比較的長時間の運転停止後に高い出力電圧が要求される自動車などの移動体用電源として用いられることが特に好ましい。   The fuel cell having the MEA of the present invention as described above exhibits excellent power generation performance. Here, the type of the fuel cell is not particularly limited. In the above description, the solid polymer fuel cell has been described as an example. However, in addition to the above, an alkaline fuel cell and a direct methanol fuel cell are used. And a micro fuel cell. Among them, a polymer electrolyte fuel cell (PEFC) is preferable because it is small and can achieve high density and high output. The fuel cell is useful as a stationary power source in addition to a power source for a moving body such as a vehicle in which a mounting space is limited. Among them, it is particularly preferable to use as a power source for a mobile body such as an automobile that requires a high output voltage after a relatively long time of operation stop.

燃料電池を運転する際に用いられる燃料は特に限定されない。例えば、水素、メタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノール、第２級ブタノール、第３級ブタノール、ジメチルエーテル、ジエチルエーテル、エチレングリコール、ジエチレングリコールなどが用いられうる。なかでも、高出力化が可能である点で、水素やメタノールが好ましく用いられる。   The fuel used when operating the fuel cell is not particularly limited. For example, hydrogen, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, secondary butanol, tertiary butanol, dimethyl ether, diethyl ether, ethylene glycol, diethylene glycol and the like can be used. Of these, hydrogen and methanol are preferably used in that high output is possible.

また、燃料電池の適用用途は特に限定されるものではないが、車両に適用することが好ましい。本発明の電解質膜−電極接合体は、発電性能および耐久性に優れ、小型化が実現可能である。このため、本発明の燃料電池は、車載性の点から、車両に該燃料電池を適用した場合、特に有利である。   Further, the application application of the fuel cell is not particularly limited, but it is preferably applied to a vehicle. The electrolyte membrane-electrode assembly of the present invention is excellent in power generation performance and durability, and can be downsized. For this reason, the fuel cell of this invention is especially advantageous when this fuel cell is applied to a vehicle from the point of in-vehicle property.

以下、本形態の燃料電池を構成する部材について簡単に説明するが、本発明の技術的範囲は下記の形態のみに制限されない。   Hereinafter, although the member which comprises the fuel cell of this form is demonstrated easily, the technical scope of this invention is not restrict | limited only to the following form.

［触媒層］
触媒層は、上述の本発明に係る電極触媒および電解質を含む。本形態の燃料電池では、上述の本発明に係る電極触媒は、カソード触媒層またはアノード触媒層のいずれか一方に存在していればよく、両方に存在していても構わない。酸素還元活性の観点から、上述の本発明に係る電極触媒は、アノード触媒層に存在していることが好ましい。 [Catalyst layer]
The catalyst layer includes the above-described electrode catalyst and electrolyte according to the present invention. In the fuel cell of the present embodiment, the above-described electrode catalyst according to the present invention may be present in either the cathode catalyst layer or the anode catalyst layer, or may be present in both. From the viewpoint of oxygen reduction activity, the above-described electrode catalyst according to the present invention is preferably present in the anode catalyst layer.

電解質は、特に制限されないが、イオン伝導性の高分子電解質であることが好ましい。上記高分子電解質は、燃料極側の触媒活物質周辺で発生したプロトンを伝達する役割を果たすことから、プロトン伝導性高分子とも呼ばれる。   The electrolyte is not particularly limited, but is preferably an ion conductive polymer electrolyte. Since the polymer electrolyte plays a role of transmitting protons generated around the catalyst active material on the fuel electrode side, it is also called a proton conductive polymer.

当該高分子電解質は、特に限定されず従来公知の知見が適宜参照されうる。高分子電解質は、構成材料であるイオン交換樹脂の種類によって、フッ素系高分子電解質と炭化水素系高分子電解質とに大別される。   The polymer electrolyte is not particularly limited, and conventionally known knowledge can be appropriately referred to. Polymer electrolytes are roughly classified into fluorine-based polymer electrolytes and hydrocarbon-based polymer electrolytes depending on the type of ion exchange resin that is a constituent material.

フッ素系高分子電解質を構成するイオン交換樹脂としては、例えば、ナフィオン（登録商標、デュポン社製）、アシプレックス（登録商標、旭化成株式会社製）、フレミオン（登録商標、旭硝子株式会社製）等のパーフルオロカーボンスルホン酸系ポリマー、パーフルオロカーボンホスホン酸系ポリマー、トリフルオロスチレンスルホン酸系ポリマー、エチレンテトラフルオロエチレン−ｇ−スチレンスルホン酸系ポリマー、エチレン−テトラフルオロエチレン共重合体、ポリビニリデンフルオリド−パーフルオロカーボンスルホン酸系ポリマーなどが挙げられる。耐熱性、化学的安定性、耐久性、機械強度に優れるという観点からは、これらのフッ素系高分子電解質が好ましく用いられ、特に好ましくはパーフルオロカーボンスルホン酸系ポリマーから構成されるフッ素系高分子電解質が用いられる。   Examples of ion exchange resins constituting the fluorine-based polymer electrolyte include Nafion (registered trademark, manufactured by DuPont), Aciplex (registered trademark, manufactured by Asahi Kasei Co., Ltd.), Flemion (registered trademark, manufactured by Asahi Glass Co., Ltd.), and the like. Perfluorocarbon sulfonic acid polymer, perfluorocarbon phosphonic acid polymer, trifluorostyrene sulfonic acid polymer, ethylene tetrafluoroethylene-g-styrene sulfonic acid polymer, ethylene-tetrafluoroethylene copolymer, polyvinylidene fluoride-per Examples thereof include fluorocarbon sulfonic acid polymers. From the viewpoint of excellent heat resistance, chemical stability, durability, and mechanical strength, these fluorine-based polymer electrolytes are preferably used, and particularly preferably fluorine-based polymer electrolytes composed of perfluorocarbon sulfonic acid polymers. Is used.

炭化水素系電解質として、具体的には、スルホン化ポリエーテルスルホン（Ｓ−ＰＥＳ）、スルホン化ポリアリールエーテルケトン、スルホン化ポリベンズイミダゾールアルキル、ホスホン化ポリベンズイミダゾールアルキル、スルホン化ポリスチレン、スルホン化ポリエーテルエーテルケトン（Ｓ−ＰＥＥＫ）、スルホン化ポリフェニレン（Ｓ−ＰＰＰ）などが挙げられる。原料が安価で製造工程が簡便であり、かつ材料の選択性が高いといった製造上の観点からは、これらの炭化水素系高分子電解質が好ましく用いられる。なお、上述したイオン交換樹脂は、１種のみが単独で用いられてもよいし、２種以上が併用されてもよい。また、上述した材料のみに制限されず、その他の材料が用いられてもよい。   Specific examples of the hydrocarbon electrolyte include sulfonated polyethersulfone (S-PES), sulfonated polyaryletherketone, sulfonated polybenzimidazole alkyl, phosphonated polybenzimidazole alkyl, sulfonated polystyrene, and sulfonated poly. Examples include ether ether ketone (S-PEEK) and sulfonated polyphenylene (S-PPP). These hydrocarbon polymer electrolytes are preferably used from the viewpoint of production such that the raw material is inexpensive, the production process is simple, and the selectivity of the material is high. In addition, as for the ion exchange resin mentioned above, only 1 type may be used independently and 2 or more types may be used together. Moreover, it is not restricted only to the material mentioned above, Other materials may be used.

プロトンの伝達を担う高分子電解質においては、プロトンの伝導度が重要となる。ここで、高分子電解質のＥＷが大きすぎる場合には触媒層全体でのイオン伝導性が低下する。したがって、本形態の触媒層は、ＥＷの小さい高分子電解質を含むことが好ましい。具体的には、本形態の触媒層は、好ましくはＥＷが１５００ｇ／ｅｑ．以下の高分子電解質を含み、より好ましくは１２００ｇ／ｅｑ．以下の高分子電解質を含み、特に好ましくは１０００ｇ／ｅｑ．以下の高分子電解質を含む。   Proton conductivity is important in polymer electrolytes responsible for proton transmission. Here, when the EW of the polymer electrolyte is too large, the ionic conductivity in the entire catalyst layer is lowered. Therefore, it is preferable that the catalyst layer of this embodiment contains a polymer electrolyte having a small EW. Specifically, the catalyst layer of this embodiment preferably has an EW of 1500 g / eq. The following polymer electrolyte is contained, More preferably, it is 1200 g / eq. The following polymer electrolyte is included, and particularly preferably 1000 g / eq. The following polymer electrolytes are included.

一方、ＥＷが小さすぎる場合には、親水性が高すぎて、水の円滑な移動が困難となる。かような観点から、高分子電解質のＥＷは６００以上であることが好ましい。なお、ＥＷ（Ｅｑｕｉｖａｌｅｎｔ Ｗｅｉｇｈｔ）は、プロトン伝導性を有する交換基の当量重量を表している。当量重量は、イオン交換基１当量あたりのイオン交換膜の乾燥重量であり、「ｇ／ｅｑ」の単位で表される。   On the other hand, if the EW is too small, the hydrophilicity is too high, making it difficult to smoothly move water. From such a viewpoint, the EW of the polymer electrolyte is preferably 600 or more. Note that EW (Equivalent Weight) represents the equivalent weight of the exchange group having proton conductivity. The equivalent weight is the dry weight of the ion exchange membrane per equivalent of ion exchange group, and is expressed in units of “g / eq”.

また、触媒層は、ＥＷが異なる２種類以上の高分子電解質を発電面内に含み、この際、高分子電解質のうち最もＥＷが低い高分子電解質が流路内ガスの相対湿度が９０％以下の領域に用いることが好ましい。このような材料配置を採用することにより、電流密度領域によらず、抵抗値が小さくなって、電池性能の向上を図ることができる。流路内ガスの相対湿度が９０％以下の領域に用いる高分子電解質、すなわちＥＷが最も低い高分子電解質のＥＷとしては、９００ｇ／ｅｑ．以下であることが望ましい。これにより、上述の効果がより確実、顕著なものとなる。   Further, the catalyst layer includes two or more types of polymer electrolytes having different EWs in the power generation surface. At this time, the polymer electrolyte having the lowest EW among the polymer electrolytes has a relative humidity of 90% or less of the gas in the flow path. It is preferable to use in the region. By adopting such a material arrangement, the resistance value becomes small regardless of the current density region, and the battery performance can be improved. The EW of the polymer electrolyte used in the region where the relative humidity of the gas in the flow channel is 90% or less, that is, the polymer electrolyte having the lowest EW is 900 g / eq. The following is desirable. Thereby, the above-mentioned effect becomes more reliable and remarkable.

さらに、ＥＷが最も低い高分子電解質を冷却水の入口と出口の平均温度よりも高い領域に用いることが望ましい。これによって、電流密度領域によらず、抵抗値が小さくなって、電池性能のさらなる向上を図ることができる。   Further, it is desirable to use a polymer electrolyte having the lowest EW in a region higher than the average temperature of the cooling water inlet and outlet. As a result, the resistance value is reduced regardless of the current density region, and the battery performance can be further improved.

さらには、燃料電池システムの抵抗値を小さくするとする観点から、ＥＷが最も低い高分子電解質は、流路長に対して燃料ガスおよび酸化剤ガスの少なくとも一方のガス供給口から３／５以内の範囲の領域に用いることが望ましい。   Furthermore, from the viewpoint of reducing the resistance value of the fuel cell system, the polymer electrolyte having the lowest EW is within 3/5 from the gas supply port of at least one of the fuel gas and the oxidant gas with respect to the channel length. It is desirable to use it in the range area.

本形態の触媒層は、触媒と高分子電解質との間に、触媒と高分子電解質（固体プロトン伝導材）とをプロトン伝導可能な状態に連結しうる液体プロトン伝導材を含んでもよい。液体プロトン伝導材が導入されることによって、触媒と高分子電解質との間に、液体プロトン伝導材を介したプロトン輸送経路が確保され、発電に必要なプロトンを効率的に触媒表面へ輸送することが可能となる。これにより、触媒の利用効率が向上するため、発電性能を維持しながら触媒の使用量を低減することが可能となる。この液体プロトン伝導材は触媒と高分子電解質との間に介在していればよく、触媒層内の多孔質担体間の空孔（二次空孔）や多孔質担体内の空孔（ミクロ孔またはメソ孔：一次空孔）内に配置されうる。   The catalyst layer of this embodiment may include a liquid proton conductive material that can connect the catalyst and the polymer electrolyte (solid proton conductive material) in a proton conductive state between the catalyst and the polymer electrolyte. By introducing a liquid proton conductive material, a proton transport path through the liquid proton conductive material is secured between the catalyst and the polymer electrolyte, and protons necessary for power generation are efficiently transported to the catalyst surface. Is possible. Thereby, since the utilization efficiency of a catalyst improves, it becomes possible to reduce the usage-amount of a catalyst, maintaining electric power generation performance. The liquid proton conductive material only needs to be interposed between the catalyst and the polymer electrolyte, and the pores (secondary pores) between the porous carriers in the catalyst layer and the pores (micropores) in the porous carrier. Or mesopores: primary vacancies).

液体プロトン伝導材としては、イオン伝導性を有し、触媒と高分子電解質と間のプロトン輸送経路を形成する機能を発揮しうる限り、特に限定されることはない。具体的には水、プロトン性イオン液体、過塩素酸水溶液、硝酸水溶液、ギ酸水溶液、酢酸水溶液などを挙げることができる。   The liquid proton conductive material is not particularly limited as long as it has ionic conductivity and can exhibit a function of forming a proton transport path between the catalyst and the polymer electrolyte. Specific examples include water, protic ionic liquid, aqueous perchloric acid solution, aqueous nitric acid solution, aqueous formic acid solution, and aqueous acetic acid solution.

液体プロトン伝導材として水を使用する場合には、発電を開始する前に少量の液水か加湿ガスにより触媒層を湿らせることによって、触媒層内に液体プロトン伝導材としての水を導入することができる。また、燃料電池の作動時における電気化学反応によって生じた生成水を液体プロトン伝導材として利用することもできる。したがって、燃料電池の運転開始の状態においては、必ずしも液体プロトン伝導材が保持されている必要はない。例えば、触媒と電解質との表面距離を、水分子を構成する酸素イオン径である０．２８ｎｍ以上とすることが望ましい。このような距離を保持することによって、触媒と高分子電解質との非接触状態を保持しながら、触媒と高分子電解質の間（液体伝導材保持部）に水（液体プロトン伝導材）を介入させることができ、両者間の水によるプロトン輸送経路が確保されることになる。   When water is used as the liquid proton conductive material, water as the liquid proton conductive material is introduced into the catalyst layer by moistening the catalyst layer with a small amount of liquid water or humidified gas before starting power generation. Can do. Moreover, the water produced by the electrochemical reaction during the operation of the fuel cell can be used as the liquid proton conductive material. Therefore, it is not always necessary to hold the liquid proton conductive material when the fuel cell is in operation. For example, the surface distance between the catalyst and the electrolyte is preferably 0.28 nm or more, which is the diameter of oxygen ions constituting water molecules. By maintaining such a distance, water (liquid proton conductive material) is interposed between the catalyst and the polymer electrolyte (liquid conductive material holding part) while maintaining a non-contact state between the catalyst and the polymer electrolyte. Therefore, a proton transport route by water between them can be secured.

イオン性液体など、水以外のものを液体プロトン伝導材として使用する場合には、触媒インク作製時に、イオン性液体と高分子電解質と触媒とを溶液中に分散させることが望ましいが、触媒を触媒層基材に塗布する際にイオン性液体を添加してもよい。   When a material other than water, such as an ionic liquid, is used as the liquid proton conducting material, it is desirable to disperse the ionic liquid, the polymer electrolyte, and the catalyst in the solution when preparing the catalyst ink. An ionic liquid may be added when applying to the layer substrate.

触媒層には、必要に応じて、ポリテトラフルオロエチレン、ポリヘキサフルオロプロピレン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体などの撥水剤、界面活性剤などの分散剤、グリセリン、エチレングリコール（ＥＧ）、ポリビニルアルコール（ＰＶＡ）、プロピレングリコール（ＰＧ）などの増粘剤、造孔剤等の添加剤が含まれて
いても構わない。 If necessary, the catalyst layer may be a water repellent such as polytetrafluoroethylene, polyhexafluoropropylene or tetrafluoroethylene-hexafluoropropylene copolymer, a dispersant such as a surfactant, glycerin, ethylene glycol (EG). ), A thickener such as polyvinyl alcohol (PVA) and propylene glycol (PG), and an additive such as a pore-forming agent may be contained.

触媒層の厚み（乾燥膜厚）は、好ましくは０．０５〜３０μｍ、より好ましくは１〜２０μｍ、さらに好ましくは２〜１５μｍである。なお、上記厚みは、カソード触媒層およびアノード触媒層双方に適用される。しかし、カソード触媒層およびアノード触媒層の厚みは、同じであってもあるいは異なってもよい。   The thickness (dry film thickness) of the catalyst layer is preferably 0.05 to 30 μm, more preferably 1 to 20 μm, and still more preferably 2 to 15 μm. In addition, the said thickness is applied to both a cathode catalyst layer and an anode catalyst layer. However, the thickness of the cathode catalyst layer and the anode catalyst layer may be the same or different.

［電解質膜］
電解質膜は、例えば、図１に示す形態のように固体高分子電解質膜２から構成される。この固体高分子電解質膜２は、ＰＥＦＣ１の運転時にアノード触媒層３ａで生成したプロトンを膜厚方向に沿ってカソード触媒層３ｃへと選択的に透過させる機能を有する。また、固体高分子電解質膜２は、アノード側に供給される燃料ガスとカソード側に供給される酸化剤ガスとを混合させないための隔壁としての機能をも有する。 [Electrolyte membrane]
The electrolyte membrane is composed of a solid polymer electrolyte membrane 2 as shown in FIG. The solid polymer electrolyte membrane 2 has a function of selectively permeating protons generated in the anode catalyst layer 3a during operation of the PEFC 1 to the cathode catalyst layer 3c along the film thickness direction. The solid polymer electrolyte membrane 2 also has a function as a partition wall for preventing the fuel gas supplied to the anode side and the oxidant gas supplied to the cathode side from being mixed.

固体高分子電解質膜２を構成する電解質材料としては特に限定されず従来公知の知見が適宜参照されうる。例えば、先に高分子電解質として説明したフッ素系高分子電解質や炭化水素系高分子電解質を用いることができる。この際、触媒層に用いた高分子電解質と必ずしも同じものを用いる必要はない。   It does not specifically limit as electrolyte material which comprises the solid polymer electrolyte membrane 2, A conventionally well-known knowledge can be referred suitably. For example, the fluorine-based polymer electrolyte or hydrocarbon-based polymer electrolyte described above as the polymer electrolyte can be used. At this time, it is not always necessary to use the same polymer electrolyte used for the catalyst layer.

電解質層の厚さは、得られる燃料電池の特性を考慮して適宜決定すればよく、特に制限されない。電解質層の厚さは、通常は５〜３００μｍ程度である。電解質層の厚さがかような範囲内の値であると、製膜時の強度や使用時の耐久性および使用時の出力特性のバランスが適切に制御されうる。   The thickness of the electrolyte layer may be appropriately determined in consideration of the characteristics of the obtained fuel cell, and is not particularly limited. The thickness of the electrolyte layer is usually about 5 to 300 μm. When the thickness of the electrolyte layer is within such a range, the balance of strength during film formation, durability during use, and output characteristics during use can be appropriately controlled.

［ガス拡散層］
ガス拡散層（アノードガス拡散層４ａ、カソードガス拡散層４ｃ）は、セパレータのガス流路（６ａ、６ｃ）を介して供給されたガス（燃料ガスまたは酸化剤ガス）の触媒層（３ａ、３ｃ）への拡散を促進する機能、および電子伝導パスとしての機能を有する。 [Gas diffusion layer]
The gas diffusion layers (anode gas diffusion layer 4a, cathode gas diffusion layer 4c) are catalyst layers (3a, 3c) of gas (fuel gas or oxidant gas) supplied via the gas flow paths (6a, 6c) of the separator. ) And a function as an electron conduction path.

ガス拡散層（４ａ、４ｃ）の基材を構成する材料は特に限定されず、従来公知の知見が適宜参照されうる。例えば、炭素製の織物、紙状抄紙体、フェルト、不織布といった導電性および多孔質性を有するシート状材料が挙げられる。基材の厚さは、得られるガス拡散層の特性を考慮して適宜決定すればよいが、３０〜５００μｍ程度とすればよい。基材の厚さがかような範囲内の値であれば、機械的強度とガスおよび水などの拡散性とのバランスが適切に制御されうる。   The material which comprises the base material of a gas diffusion layer (4a, 4c) is not specifically limited, A conventionally well-known knowledge can be referred suitably. For example, a sheet-like material having conductivity and porosity such as a carbon woven fabric, a paper-like paper body, a felt, and a non-woven fabric can be used. The thickness of the substrate may be appropriately determined in consideration of the characteristics of the obtained gas diffusion layer, but may be about 30 to 500 μm. If the thickness of the substrate is within such a range, the balance between mechanical strength and diffusibility such as gas and water can be appropriately controlled.

ガス拡散層は、撥水性をより高めてフラッディング現象などを防止することを目的として、撥水剤を含むことが好ましい。撥水剤としては、特に限定されないが、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリフッ化ビニリデン（ＰＶｄＦ）、ポリヘキサフルオロプロピレン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体（ＦＥＰ）などのフッ素系の高分子材料、ポリプロピレン、ポリエチレンなどが挙げられる。   The gas diffusion layer preferably contains a water repellent for the purpose of further improving water repellency and preventing a flooding phenomenon or the like. Although it does not specifically limit as a water repellent, Fluorine-type high things, such as polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), polyhexafluoropropylene, and tetrafluoroethylene-hexafluoropropylene copolymer (FEP), are included. Examples thereof include molecular materials, polypropylene, and polyethylene.

また、撥水性をより向上させるために、ガス拡散層は、撥水剤を含むカーボン粒子の集合体からなるカーボン粒子層（マイクロポーラス層；ＭＰＬ、図示せず）を基材の触媒層側に有するものであってもよい。   In order to further improve the water repellency, the gas diffusion layer has a carbon particle layer (microporous layer; MPL, not shown) made of an aggregate of carbon particles containing a water repellent agent on the catalyst layer side of the substrate. You may have.

カーボン粒子層に含まれるカーボン粒子は特に限定されず、カーボンブラック、グラファイト、膨張黒鉛などの従来公知の材料が適宜採用されうる。なかでも、電子伝導性に優れ、比表面積が大きいことから、オイルファーネスブラック、チャネルブラック、ランプブラック、サーマルブラック、アセチレンブラックなどのカーボンブラックが好ましく用いられうる。カーボン粒子の平均粒径は、１０〜１００ｎｍ程度とするのがよい。これにより、毛細管力による高い排水性が得られるとともに、触媒層との接触性も向上させることが可能となる。   The carbon particles contained in the carbon particle layer are not particularly limited, and conventionally known materials such as carbon black, graphite, and expanded graphite can be appropriately employed. Among them, carbon black such as oil furnace black, channel black, lamp black, thermal black, acetylene black and the like can be preferably used because of excellent electron conductivity and a large specific surface area. The average particle size of the carbon particles is preferably about 10 to 100 nm. Thereby, while being able to obtain the high drainage property by capillary force, it becomes possible to improve contact property with a catalyst layer.

カーボン粒子層に用いられる撥水剤としては、上述した撥水剤と同様のものが挙げられる。なかでも、撥水性、電極反応時の耐食性などに優れることから、フッ素系の高分子材料が好ましく用いられうる。   Examples of the water repellent used in the carbon particle layer include the same water repellent as described above. Among these, fluorine-based polymer materials can be preferably used because of excellent water repellency, corrosion resistance during electrode reaction, and the like.

カーボン粒子層におけるカーボン粒子と撥水剤との混合比は、撥水性および電子伝導性のバランスを考慮して、重量比で９０：１０〜４０：６０（カーボン粒子：撥水剤）程度とするのがよい。なお、カーボン粒子層の厚さについても特に制限はなく、得られるガス拡散層の撥水性を考慮して適宜決定すればよい。   The mixing ratio of the carbon particles and the water repellent in the carbon particle layer is about 90:10 to 40:60 (carbon particles: water repellent) in weight ratio in consideration of the balance between water repellency and electron conductivity. It is good. In addition, there is no restriction | limiting in particular also about the thickness of a carbon particle layer, What is necessary is just to determine suitably in consideration of the water repellency of the gas diffusion layer obtained.

［セパレータ］
セパレータは、固体高分子形燃料電池などの燃料電池の単セルを複数個直列に接続して燃料電池スタックを構成する際に、各セルを電気的に直列に接続する機能を有する。また、セパレータは、燃料ガス、酸化剤ガス、および冷却剤を互に分離する隔壁としての機能も有する。これらの流路を確保するため、上述したように、セパレータのそれぞれにはガス流路および冷却流路が設けられていることが好ましい。セパレータを構成する材料としては、緻密カーボングラファイト、炭素板などのカーボンや、ステンレスなどの金属など、従来公知の材料が適宜制限なく採用できる。セパレータの厚さやサイズ、設けられる各流路の形状やサイズなどは特に限定されず、得られる燃料電池の所望の出力特性などを考慮して適宜決定できる。 [Separator]
The separator has a function of electrically connecting each cell in series when a plurality of single cells of a fuel cell such as a polymer electrolyte fuel cell are connected in series to form a fuel cell stack. The separator also functions as a partition that separates the fuel gas, the oxidant gas, and the coolant from each other. In order to secure these flow paths, as described above, each of the separators is preferably provided with a gas flow path and a cooling flow path. As a material constituting the separator, conventionally known materials such as dense carbon graphite, carbon such as a carbon plate, and metal such as stainless steel can be appropriately employed without limitation. The thickness and size of the separator and the shape and size of each flow path provided are not particularly limited, and can be appropriately determined in consideration of the desired output characteristics of the obtained fuel cell.

燃料電池の製造方法は、特に制限されることなく、燃料電池の分野において従来公知の知見が適宜参照されうる。   The manufacturing method of the fuel cell is not particularly limited, and conventionally known knowledge can be appropriately referred to in the field of the fuel cell.

さらに、燃料電池が所望する電圧を発揮できるように、セパレータを介して膜電極接合体を複数積層して直列に繋いだ構造の燃料電池スタックを形成してもよい。燃料電池の形状などは、特に限定されず、所望する電圧などの電池特性が得られるように適宜決定すればよい。   Furthermore, a fuel cell stack having a structure in which a plurality of membrane electrode assemblies are stacked and connected in series via a separator may be formed so that the fuel cell can exhibit a desired voltage. The shape of the fuel cell is not particularly limited, and may be determined as appropriate so that desired battery characteristics such as voltage can be obtained.

上述した本形態のＰＥＦＣや膜電極接合体は、触媒層に上述の本発明に係る電極触媒層を用いているため、優れた発電性能を発揮することができる。したがって、本実施形態のＰＥＦＣやこれを用いた燃料電池スタックは、例えば、車両に駆動用電源として搭載されうる。   The PEFC and membrane electrode assembly of the present embodiment described above can exhibit excellent power generation performance because the electrode catalyst layer according to the present invention is used for the catalyst layer. Therefore, the PEFC of this embodiment and the fuel cell stack using the PEFC can be mounted on a vehicle as a driving power source, for example.

本発明を、以下の実施例を用いてさらに詳細に説明する。ただし、本発明の技術的範囲
が以下の実施例のみに制限されるわけではない。なお、以下において、室温とは（２５℃）を意味する。 The invention is explained in more detail using the following examples. However, the technical scope of the present invention is not limited only to the following examples. In the following, room temperature means (25 ° C.).

＜電極触媒の製造＞
［実施例１］
１，５−シクロオクタジエンジメチル白金錯体８０ｍｇをガラス管Ａに入れ、ガラス管の口に石英ウールを詰めた。当該ガラス管Ａを、炭素材料（ケッチェンブラック（登録商標）ＥＣＰ６００ＪＰ、ケッチェン・ブラック・インターナショナル社製）２００ｍｇを入れたガラス管Ｂに入れ、オイルポンプを用いてガラス管Ｂ内を減圧下（１．０×１０−２Ｐａ）としたままガラス管Ｂに入っている炭素担体のみを真空加熱乾燥し、その間はガラス管Ａに入っている錯体が分解しないようにガラス管Ａをガラス管Ｂの加熱されていない柄の部分に寄せておいた。炭素担体を真空加熱乾燥後、炭素担体を放冷させてからガラス管Ａをガラス管Ｂの炭素担体が入っている側に移動させ、ガスバーナーでガラス管Ｂを封じた。次に、ガラス管Ａを封入した当該ガラス管Ｂを、オイルバス中で１００℃、２８時間保持した。これにより、１，５−シクロオクタジエンジメチル白金錯体が昇華し、炭素材料と接触した。その後、ガラス管Ｂを室温まで自然放冷し、ガラス管Ｂから１，５−シクロオクタジエンジメチル白金錯体が吸着した炭素材料を取り出した。 <Manufacture of electrode catalyst>
[Example 1]
80 mg of 1,5-cyclooctadiene dimethylplatinum complex was placed in a glass tube A, and quartz wool was filled in the mouth of the glass tube. The glass tube A is put into a glass tube B containing 200 mg of a carbon material (Ketjen Black (registered trademark) ECP600JP, manufactured by Ketjen Black International), and the inside of the glass tube B is reduced in pressure using an oil pump (1 0.0 × 10 −2 Pa), only the carbon carrier contained in the glass tube B is vacuum-heated and dried, and during this time, the glass tube A is attached to the glass tube B so that the complex contained in the glass tube A is not decomposed. It was put on the part of the handle which was not heated. After drying the carbon support under vacuum heating, the carbon support was allowed to cool, the glass tube A was moved to the side of the glass tube B containing the carbon support, and the glass tube B was sealed with a gas burner. Next, the said glass tube B which enclosed the glass tube A was hold | maintained for 28 hours at 100 degreeC in the oil bath. Thereby, 1,5-cyclooctadiene dimethyl platinum complex sublimated and contacted the carbon material. Thereafter, the glass tube B was naturally allowed to cool to room temperature, and the carbon material on which the 1,5-cyclooctadiene dimethyl platinum complex was adsorbed was taken out of the glass tube B.

上記で得られた１，５−シクロオクタジエンジメチル白金錯体が吸着した炭素材料をガラス管Ｃに入れ、ターボモレキュラーポンプを用いてガラス管Ｃ内を減圧下（１．０×１０−４Ｐａ）としたまま、当該ガラス管Ｃを室温から３００℃まで５℃／分で昇温させ、その後３００℃で１時間保持した。その後、ガラス管Ｃを室温まで自然放冷し、ガラス管Ｃから触媒１を取り出した。 The carbon material adsorbed with the 1,5-cyclooctadiene dimethylplatinum complex obtained above is put into a glass tube C, and the inside of the glass tube C is reduced under reduced pressure (1.0 × 10 −4 Pa) using a turbomolecular pump. The glass tube C was heated from room temperature to 300 ° C. at a rate of 5 ° C./min, and then kept at 300 ° C. for 1 hour. Thereafter, the glass tube C was naturally cooled to room temperature, and the catalyst 1 was taken out from the glass tube C.

［実施例２］
１，５−シクロオクタジエンジメチル白金錯体１６０ｍｇをガラス管Ａに入れ、ガラス管の口に石英ウールを詰めた。当該ガラス管Ａを、炭素材料（ケッチェンブラック（登録商標）ＥＣＰ６００ＪＰ、ケッチェン・ブラック・インターナショナル社製）２００ｍｇを入れたガラス管Ｂに入れ、オイルポンプを用いてガラス管Ｂ内を減圧下（１．０×１０−２Ｐａ）としたままガラス管Ｂに入っている炭素担体のみを真空加熱乾燥し、その間はガラス管Ａに入っている錯体が分解しないようにガラス管Ａをガラス管Ｂの加熱されていない柄の部分に寄せておいた。炭素担体を真空加熱乾燥後、炭素担体を放冷させてからガラス管Ａをガラス管Ｂの炭素担体が入っている側に移動させ、ガスバーナーでガラス管Ｂを封じた。次に、ガラス管Ａを封入した当該ガラス管Ｂを、オイルバス中で１５０℃、２４時間保持した。これにより、１，５−シクロオクタジエンジメチル白金錯体が昇華し、炭素材料と接触した。その後、ガラス管Ｂを室温まで自然放冷し、ガラス管Ｂから１，５−シクロオクタジエンジメチル白金錯体が吸着した炭素材料を取り出した。 [Example 2]
160 mg of 1,5-cyclooctadiene dimethylplatinum complex was placed in a glass tube A, and quartz wool was filled in the mouth of the glass tube. The glass tube A is put into a glass tube B containing 200 mg of a carbon material (Ketjen Black (registered trademark) ECP600JP, manufactured by Ketjen Black International), and the inside of the glass tube B is reduced in pressure using an oil pump (1 0.times.10.sup.-2 Pa), only the carbon support contained in the glass tube B is vacuum-heated and dried, and during that time, the glass tube A is heated to the glass tube B so that the complex contained in the glass tube A is not decomposed. It was put on the part of the handle that was not done. After drying the carbon support under vacuum heating, the carbon support was allowed to cool, the glass tube A was moved to the side of the glass tube B containing the carbon support, and the glass tube B was sealed with a gas burner. Next, the said glass tube B which enclosed the glass tube A was hold | maintained for 24 hours at 150 degreeC in the oil bath. Thereby, 1,5-cyclooctadiene dimethyl platinum complex sublimated and contacted the carbon material. Thereafter, the glass tube B was naturally allowed to cool to room temperature, and the carbon material on which the 1,5-cyclooctadiene dimethyl platinum complex was adsorbed was taken out of the glass tube B.

上記で得られた１，５−シクロオクタジエンジメチル白金錯体が吸着した炭素材料をガラス管Ｃに入れ、ターボモレキュラーポンプを用いてガラス管Ｃ内を減圧下（１．０×１０−４Ｐａ）としたまま、当該ガラス管Ｃを室温から３００℃まで５℃／分で昇温させ、その後３００℃で１時間保持した。その後、ガラス管Ｃを室温まで自然放冷し、ガラス管Ｃから触媒１を取り出した。   The carbon material adsorbed with the 1,5-cyclooctadiene dimethylplatinum complex obtained above is put in a glass tube C, and the inside of the glass tube C is reduced under reduced pressure (1.0 × 10 −4 Pa) using a turbomolecular pump. The glass tube C was heated from room temperature to 300 ° C. at a rate of 5 ° C./min, and then kept at 300 ° C. for 1 hour. Thereafter, the glass tube C was naturally cooled to room temperature, and the catalyst 1 was taken out from the glass tube C.

［比較例１］
炭素材料（ケッチェンブラック（登録商標）ＥＣＰ６００ＪＰ、ケッチェン・ブラック・インターナショナル社製）０．５０１４ｇをマグネチックスターラーバーとともに１００ｍｌの二口ナス型フラスコに入れた。そして、１５０℃で６時間、真空加熱乾燥を行った後、自然放冷した。続いて２５５ｍｇの１，５−シクロオクタジエンジメチル白金錯体を溶解させた２５ｍｌのアセトニトリルを、炭素材料の入ったフラスコにシリンジを用いて真空含浸させ、その後室温で１０分間撹拌した。そして、６時間還流を行った後（還流の際のオイルバスの温度は１１０℃）、放冷させ、２５ｍｌのアセトニトリルを加え、溶液をメンブレンフィルターで濾過した。さらに５０ｍｌのアセトニトリルで試料を洗浄し、１００℃で６時間、真空加熱乾燥し、比較触媒１を得た（収量０．５３５７ｇ）。 [Comparative Example 1]
0.5014 g of carbon material (Ketjen Black (registered trademark) ECP600JP, manufactured by Ketjen Black International Co., Ltd.) was placed in a 100 ml two-necked eggplant type flask together with a magnetic stirrer bar. And after carrying out vacuum heating drying at 150 degreeC for 6 hours, it stood to cool naturally. Subsequently, 25 ml of acetonitrile in which 255 mg of 1,5-cyclooctadienedimethylplatinum complex was dissolved was vacuum impregnated into a flask containing a carbon material using a syringe, and then stirred at room temperature for 10 minutes. After refluxing for 6 hours (the temperature of the oil bath during reflux was 110 ° C.), the mixture was allowed to cool, 25 ml of acetonitrile was added, and the solution was filtered through a membrane filter. Further, the sample was washed with 50 ml of acetonitrile, and dried under vacuum heating at 100 ° C. for 6 hours to obtain a comparative catalyst 1 (yield: 0.5357 g).

＜白金担持密度の測定＞
上記で得られた各触媒における白金の担持密度を下記の方法で測定した。まず、触媒に吸着した水を取り除くために、１００℃で６時間、真空加熱乾燥処理を行った。その後、触媒をグローブボックス内で５ｍｇ程度秤量し、これを溶液化し、得られた溶液中に含まれる白金を誘導結合プラズマ（ＩＣＰ）発光分光分析装置（エスアイアイナノテクノロジー社製、ＳＰＳ−３５００型）を用いて定量した。そして、下記式１に基づき、触媒における白金の担持密度を算出した。結果を表１に示す。 <Measurement of platinum loading density>
The platinum loading density in each catalyst obtained above was measured by the following method. First, in order to remove the water adsorbed on the catalyst, vacuum heat drying treatment was performed at 100 ° C. for 6 hours. Thereafter, about 5 mg of the catalyst is weighed in a glove box, and this is made into a solution, and platinum contained in the obtained solution is converted into an inductively coupled plasma (ICP) emission spectroscopic analyzer (manufactured by SII Nano Technology, SPS-3500 type) ). And based on the following formula 1, the carrying density of platinum in the catalyst was calculated. The results are shown in Table 1.

表１の結果より、本発明に係る触媒１および２は、従来の液相担持方法によって得られた比較触媒１よりも、白金の担持密度が高いことが示された。   From the results in Table 1, it was shown that Catalysts 1 and 2 according to the present invention have a higher platinum loading density than Comparative Catalyst 1 obtained by the conventional liquid phase loading method.

＜Ｘ線回折（ＸＲＤ）測定＞
上記で得られた触媒１、ブランク（ケッチェンブラックのみ）、市販の白金担持カーボン触媒（田中貴金属工業製、ＴＥＣ１０Ｅ５０Ｅ）についてＸ線回折測定を行った。Ｘ線回折測定は、島津製作所製ＸＲＤ−６１００を用いて行い、線源はＣｕ−Ｋα、電圧３０ｋＶ、電流２０ｍＡで行った。結果を図２に示す。 <X-ray diffraction (XRD) measurement>
X-ray diffraction measurement was performed on the catalyst 1, the blank (only Ketjen Black) obtained above, and a commercially available platinum-supported carbon catalyst (manufactured by Tanaka Kikinzoku Kogyo, TEC10E50E). X-ray diffraction measurement was performed using XRD-6100 manufactured by Shimadzu Corporation, and the radiation source was Cu-Kα, voltage 30 kV, and current 20 mA. The results are shown in FIG.

図２より、市販のＴＥＣ１０Ｅ５０ＥのＸＲＤパターンでは、４０°付近に白金由来のピークが観測された。しかしながら、触媒１のＸＲＤパターンでは、４０°付近にピークが観察されず、ブランクと同様のパターンを示した。この結果より、触媒１に担持された白金粒子は、市販のＴＥＣ１０Ｅ５０Ｅの白金粒子と比較して、非常に微細であることが示唆された。   From FIG. 2, a platinum-derived peak was observed at around 40 ° in the XRD pattern of the commercially available TEC10E50E. However, in the XRD pattern of the catalyst 1, no peak was observed in the vicinity of 40 °, and the same pattern as the blank was shown. From this result, it was suggested that the platinum particles supported on the catalyst 1 are very fine compared to the commercially available platinum particles of TEC10E50E.

＜電気化学的評価＞
上記で得られた触媒１および２ならびに比較触媒１について、以下の方法で電気化学的評価を行った。触媒１および２ならびに比較触媒１を、それぞれ１１．４ｍｇ、１２．８ｍｇ、１０．４ｍｇずつ秤量し、水１９ｍＬおよびイソプロパノール６ｍＬの混合液に分散させ、これにナフィオン溶液（ＤＥ５２１ＣＳ、５ｗｔ％、アルドリッチ製）１００μＬ加えて触媒インクを調製した。その後、１時間以上超音波分散を行った。調製した触媒インク１０μＬを研磨済みのグラッシーカーボン電極（φ５．０ｍｍ、北斗電工製）に塗布し、６０℃の乾燥機中で１０分間乾燥した。電極の表面塗布状態は顕微鏡観察により確認し、触媒層の塗り残し、はみ出しのない電極を評価に用いた。 <Electrochemical evaluation>
The catalysts 1 and 2 and the comparative catalyst 1 obtained above were subjected to electrochemical evaluation by the following method. Catalysts 1 and 2 and Comparative Catalyst 1 were weighed 11.4 mg, 12.8 mg, and 10.4 mg, respectively, and dispersed in a mixed solution of 19 mL of water and 6 mL of isopropanol, and Nafion solution (DE521CS, 5 wt%, manufactured by Aldrich) ) 100 μL was added to prepare a catalyst ink. Thereafter, ultrasonic dispersion was performed for 1 hour or longer. 10 μL of the prepared catalyst ink was applied to a polished glassy carbon electrode (φ5.0 mm, manufactured by Hokuto Denko), and dried in a dryer at 60 ° C. for 10 minutes. The surface coating state of the electrode was confirmed by microscopic observation, and the electrode without any uncoated catalyst layer and protruding was used for evaluation.

電気化学測定は通常の三室型セル（ミックラボ製）で行った。電解質溶液は０．１Ｍの過塩素酸（Ｕｌｔｒａｐｕｒ、関東化学製）を用いた。対極はＰｔ線、参照極は可逆水素電極（ＲＨＥ）とした。電位制御はＨＺ−５０００（北斗電工製）を用いて行った。回転電極（ＲＤＥ）装置はＨＲ−３０１（北斗電工製）を用いた。セル温度は外部循環方式の恒温槽（ＣＨＬ３００、ＹＡＭＡＴＯ製）を用いて２５℃（±１℃）に制御した。ＣＯストリッピングの測定には１％ＣＯのＡｒバランスガス（太陽日酸製）を使用した。全ての計測はドラフト内で実施した。   Electrochemical measurement was performed with a normal three-chamber cell (Mick Labo). As the electrolyte solution, 0.1 M perchloric acid (Ultrapur, manufactured by Kanto Chemical Co., Inc.) was used. The counter electrode was a Pt line, and the reference electrode was a reversible hydrogen electrode (RHE). The potential control was performed using HZ-5000 (manufactured by Hokuto Denko). The rotating electrode (RDE) apparatus used was HR-301 (manufactured by Hokuto Denko). The cell temperature was controlled to 25 ° C. (± 1 ° C.) using an external circulation thermostat (CHL300, manufactured by YAMATO). For the measurement of CO stripping, 1% CO Ar balance gas (manufactured by Taiyo Nippon Sanso) was used. All measurements were performed in the draft.

電極の前処理として０〜１．２Ｖの範囲を１００ｍＶ／ｓで２０サイクル走査した後、サイクリックボルタンメトリー（結果を図３に示す）や対流ボルタンメトリー等の測定を行った。ＣＯストリッピングの測定では、１％ＣＯガスが飽和した電解質溶液中で、電極を４００ｒｐｍで回転させながら０．０５Ｖに３０分間保持した。この条件においてＣＯ吸着量が飽和に達することを確認した。溶液中のＣＯガスを窒素で完全に置換した後、０．０５Ｖから１．２Ｖまで、２０ｍＶ／ｓで３サイクルのＣＶ計測を行った。２サイクル目と３サイクル目のＣＶはきれいに重なって観察された。１サイクル目と２サイクル目以降の応答電流の差よりＣＯストリッピングピークの電気量を算出し、ＣＯによるＰｔの最大被覆率が０．６８になると仮定し、換算係数２８５．６μＣ・ｃｍＰｔ−２を適用して電気化学的に活性な表面積を算出した。電気化学的面積（ＥＣＡ）はこれを白金量で割り付けることで算出した（結果を図４Ａに示す）。 As the electrode pretreatment, a range of 0 to 1.2 V was scanned for 20 cycles at 100 mV / s, and then measurements such as cyclic voltammetry (results are shown in FIG. 3) and convective voltammetry were performed. In the measurement of CO stripping, the electrode was held at 0.05 V for 30 minutes in an electrolyte solution saturated with 1% CO gas while rotating the electrode at 400 rpm. It was confirmed that the CO adsorption amount reached saturation under these conditions. After the CO gas in the solution was completely replaced with nitrogen, CV measurement was performed for 3 cycles from 0.05 V to 1.2 V at 20 mV / s. The CVs in the second and third cycles were observed with a clear overlap. The amount of electricity at the CO stripping peak is calculated from the difference between the response currents after the first cycle and the second cycle, and the maximum Pt coverage by CO is assumed to be 0.68, and the conversion factor is 285.6 μC · cmPt −2 Was applied to calculate the electrochemically active surface area. The electrochemical area (ECA) was calculated by assigning this by the amount of platinum (the result is shown in FIG. 4A).

図３のサイクリックボルタモグラムに示されるように、いずれの触媒においても白金の存在に由来する水素の発生・酸化による電流が観測された。さらに、白金の担持密度が高くなるにつれて、白金表面への水素の吸脱着と白金の酸化還元による電気量が多くなることが確認された。   As shown in the cyclic voltammogram of FIG. 3, in any catalyst, an electric current due to generation / oxidation of hydrogen derived from the presence of platinum was observed. Furthermore, it was confirmed that the amount of electricity due to adsorption / desorption of hydrogen on the platinum surface and oxidation / reduction of platinum increases as the platinum loading density increases.

図４ＡのＣＯストリッピングの結果を基に算出した値から、白金粒子の比表面積は、触媒１で２９９ｍ２／ｇ、触媒２で３３７ｍ２／ｇ、比較触媒１で２９０ｍ２／ｇであることが分かった。この値は、白金粒子を球と仮定した場合、平均粒子径が１ｎｍ以下であることを意味する（図４Ｂを参照）。 From the value calculated based on the results of the CO stripping Figure 4A, the specific surface area of the platinum particles is 290 m 2 / g in catalyst 1 299m 2 / g, the catalyst 2 337m 2 / g, with comparative catalyst 1 I understood. This value means that when the platinum particles are assumed to be spheres, the average particle diameter is 1 nm or less (see FIG. 4B).

＜高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）観察＞
比較触媒１について、白金が担持されている様子を観察するため、高角度散乱暗視野走査透過電子顕微鏡（ＨＡＡＤＦ−ＳＴＥＭ）観察を行った。具体的には、株式会社日立ハイテクノロジーズ社製、ＨＤ−２７００型の走査透過電子顕微鏡（ＳＴＥＭ）を用い、加速電圧２００ｋＶにて観察した。結果を図５Ａ〜５Ｄに示す。 <High angle scattering dark field scanning transmission electron microscope (HAADF-STEM) observation>
The comparative catalyst 1 was observed with a high angle scattering dark field scanning transmission electron microscope (HAADF-STEM) in order to observe how platinum was supported. Specifically, it was observed at an acceleration voltage of 200 kV using an HD-2700 type scanning transmission electron microscope (STEM) manufactured by Hitachi High-Technologies Corporation. The results are shown in FIGS.

図５Ａ〜５Ｄの結果より、比較触媒１に担持された白金粒子のほとんどが１ｎｍ以下であり、平均粒子径が１ｎｍ以下となることが確認された。上述のＣＯストリッピングの結果を基に算出した白金粒子の比表面積の結果を考慮すると、比較触媒１よりも白金粒子の比表面積が大きい触媒１および２においても白金粒子の平均粒子径が１ｎｍ以下となることが示された。   From the results of FIGS. 5A to 5D, it was confirmed that most of the platinum particles supported on the comparative catalyst 1 were 1 nm or less and the average particle diameter was 1 nm or less. Considering the result of the specific surface area of the platinum particles calculated based on the result of the above-mentioned CO stripping, the average particle diameter of the platinum particles is 1 nm or less even in the catalysts 1 and 2 having a larger specific surface area of the platinum particles than the comparative catalyst 1 It was shown that

＜窒素吸脱着測定＞
上記で得られた触媒１および２ならびにブランク（炭素材料のみ）について窒素吸脱着測定を行った。窒素吸脱着測定は、日本ベル製ＢＥＬＳＯＲＰ ｍｉｎｉを用いて行い、−１９６℃の温度で、多点法で行った。０．０１＜Ｐ／Ｐ０＜０．０５の相対圧の範囲での吸着等温線よりＢＥＴ比表面積（ＳＢＥＴ）を求めた。全空孔容積（Ｖｔｏｔａｌ）は、０．９６の相対圧における吸着Ｎ２の容積より求めた。ミクロ孔容積（Ｖｍｉｃｒｏ）は、それぞれの窒素吸着等温線のデータを使用してＤｕｂｉｎｉｎ−Ｒａｄｕｓｈｋｅｖｉｃｈ（ＤＲ）方程式で算出した。メソ孔容積（Ｖｍｅｓｏ）は、全空孔容積からミクロ孔容積（Ｖｍｉｃｒｏ）を差し引いて求めた。ブランクにおける各値を１．００とした場合の結果を下記表２に示す。 <Measurement of nitrogen adsorption / desorption>
Nitrogen adsorption / desorption measurements were performed on the catalysts 1 and 2 and the blank (carbon material only) obtained above. The nitrogen adsorption / desorption measurement was performed using BELSORP mini manufactured by Nippon Bell Co., Ltd., and was performed at a temperature of −196 ° C. by a multipoint method. The BET specific surface area (S BET ) was determined from the adsorption isotherm in the range of 0.01 <P / P 0 <0.05. The total pore volume (V total ) was determined from the volume of adsorbed N 2 at a relative pressure of 0.96. The micropore volume (V micro ) was calculated by the Dubinin-Radushkevich (DR) equation using the respective nitrogen adsorption isotherm data. The mesopore volume (V meso ) was determined by subtracting the micropore volume (V micro ) from the total pore volume. The results when each value in the blank is set to 1.00 are shown in Table 2 below.

表２に示されるように、本発明の触媒１および２は、ブランクと比較して、相対的にメソ孔よりもミクロ孔が減少していることが分かった。この結果より、触媒１および２では、ミクロ孔に白金が多く担持されていることが示唆された。   As shown in Table 2, it was found that the micropores of the catalysts 1 and 2 of the present invention were relatively smaller than the mesopores compared to the blank. From these results, it was suggested that in Catalysts 1 and 2, a large amount of platinum was supported in the micropores.

１ 固体高分子形燃料電池（ＰＥＦＣ）、
２ 固体高分子電解質膜、
３ 触媒層、
３ａ アノード触媒層、
３ｃ カソード触媒層、
４ａ アノードガス拡散層、
４ｃ カソードガス拡散層、
５ セパレータ、
５ａ アノードセパレータ、
５ｃ カソードセパレータ、
６ａ アノードガス流路、
６ｃ カソードガス流路、
７ 冷媒流路、
１０ 膜電極接合体（ＭＥＡ）。 1 Polymer electrolyte fuel cell (PEFC),
2 solid polymer electrolyte membrane,
3 catalyst layer,
3a anode catalyst layer,
3c cathode catalyst layer,
4a Anode gas diffusion layer,
4c cathode gas diffusion layer,
5 separator,
5a anode separator,
5c cathode separator,
6a Anode gas flow path,
6c cathode gas flow path,
7 Refrigerant flow path,
10 Membrane electrode assembly (MEA).

Claims (3)

炭素材料に貴金属が担持されてなる電極触媒であって、
前記貴金属の平均粒子径は、１ｎｍ以下であり、
前記貴金属の担持密度は、前記電極触媒の質量に対し、５〜６０質量％である電極触媒。 An electrode catalyst in which a noble metal is supported on a carbon material,
The noble metal has an average particle size of 1 nm or less,
The noble metal loading density is 5 to 60% by mass with respect to the mass of the electrode catalyst. 炭素材料と気体状の有機貴金属錯体とを接触させて、有機貴金属錯体を炭素材料に担持させる工程と、
前記炭素材料に担持された有機貴金属錯体を還元する工程と、
を含む、電極触媒の製造方法。 Contacting the carbon material with a gaseous organic noble metal complex to support the organic noble metal complex on the carbon material;
Reducing the organic noble metal complex supported on the carbon material;
A method for producing an electrode catalyst, comprising: 前記有機貴金属錯体は、１，５−シクロオクタジエンジメチル白金錯体、エチレンビス（トリフェニルホスフィン）白金（０）、テトラキス（トリフェニルホスフィン）白金（０）、ビス（トリ−ｔｅｒｔ−ブチルホスフィン）白金（０）、（トリメチル）シクロペンタジエニル白金（ＩＶ）、シアン化白金（ＩＩ）、（トリメチル）メチルシクロペンタジエニル白金（ＩＶ）、（トリメチル）ペンタメチルシクロペンタジエニル白金（ＩＶ）からなる群から選択される少なくとも１種を含む、請求項２に記載の電極触媒の製造方法。   The organic noble metal complex includes 1,5-cyclooctadiene dimethylplatinum complex, ethylenebis (triphenylphosphine) platinum (0), tetrakis (triphenylphosphine) platinum (0), bis (tri-tert-butylphosphine) platinum From (0), (trimethyl) cyclopentadienylplatinum (IV), platinum (II) cyanide, (trimethyl) methylcyclopentadienylplatinum (IV), (trimethyl) pentamethylcyclopentadienylplatinum (IV) The manufacturing method of the electrode catalyst of Claim 2 containing at least 1 sort (s) selected from the group which consists of.
JP2014022809A 2014-02-07 2014-02-07 Electrode catalyst and method for producing same Pending JP2017060901A (en)