JP2017010935A - Electrode mixture layer for nonaqueous electrolyte secondary battery, electrode for nonaqueous electrolyte secondary battery including the same, and nonaqueous electrolyte secondary battery - Google Patents

Electrode mixture layer for nonaqueous electrolyte secondary battery, electrode for nonaqueous electrolyte secondary battery including the same, and nonaqueous electrolyte secondary battery Download PDF

Info

Publication number
JP2017010935A
JP2017010935A JP2016119930A JP2016119930A JP2017010935A JP 2017010935 A JP2017010935 A JP 2017010935A JP 2016119930 A JP2016119930 A JP 2016119930A JP 2016119930 A JP2016119930 A JP 2016119930A JP 2017010935 A JP2017010935 A JP 2017010935A
Authority
JP
Japan
Prior art keywords
mixture layer
carbon
electrode mixture
electrode
secondary battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2016119930A
Other languages
Japanese (ja)
Other versions
JP7240801B2 (en
Inventor
亮太 平川
Ryota Hirakawa
亮太 平川
伸弥 小村
Nobuya Komura
伸弥 小村
一輝 谷内
Kazuki Yachi
一輝 谷内
大道　高弘
Takahiro Omichi
高弘 大道
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Teijin Ltd
Original Assignee
Teijin Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Teijin Ltd filed Critical Teijin Ltd
Publication of JP2017010935A publication Critical patent/JP2017010935A/en
Application granted granted Critical
Publication of JP7240801B2 publication Critical patent/JP7240801B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an electrode mixture layer with favorable characteristics, capable of being formed more easily as compared with conventional ones, an electrode for a nonaqueous electrolyte secondary battery including the electrode mixture layer, and a nonaqueous electrolyte secondary battery including the electrode.SOLUTION: There is provided an electrode mixture layer for a nonaqueous electrolyte secondary battery which is an electrode mixture layer containing at least an electrode active material and a carbon-based conductive assistant having an average diameter of 10 nm or more. The volume content of the carbon-based conductive assistant is within a range of 0.9-5.0%, and the density of the electrode mixture layer is 0.50 g/cmor more and less than 2.10 g/cm.SELECTED DRAWING: None

Description

本発明は、非水電解質二次電池用電極合剤層及び該合剤層が形成されている非水電解質二次電池用電極、並びに該電極を有する非水電解質二次電池に関する。詳しくは、所定の炭素系導電助剤を含む低密度の非水電解質二次電池用電極合剤層及び該合剤層が形成されている非水電解質二次電池用電極、並びに該電極を有する非水電解質二次電池に関する。   The present invention relates to an electrode mixture layer for a non-aqueous electrolyte secondary battery, a non-aqueous electrolyte secondary battery electrode on which the mixture layer is formed, and a non-aqueous electrolyte secondary battery having the electrode. Specifically, it has a low-density nonaqueous electrolyte secondary battery electrode mixture layer containing a predetermined carbon-based conductive additive, a nonaqueous electrolyte secondary battery electrode on which the mixture layer is formed, and the electrode The present invention relates to a non-aqueous electrolyte secondary battery.

非水電解質二次電池の一種であるリチウムイオン二次電池は、電解質中のリチウムイオンが電気伝導を担う二次電池であり、正極にリチウム金属酸化物を電極活物質として用い、負極にグラファイトなどの炭素材を電極活物質として用いるものが主流である。リチウムイオン二次電池は、二次電池の中でもエネルギー密度が高い特徴を持つことから、携帯電話などの小型機器から電気自動車などの大型機器まで、応用範囲が広がっている。   A lithium ion secondary battery, which is a type of non-aqueous electrolyte secondary battery, is a secondary battery in which lithium ions in the electrolyte are responsible for electrical conduction, using lithium metal oxide as the electrode active material for the positive electrode and graphite for the negative electrode Most of these materials use carbon materials as electrode active materials. Lithium ion secondary batteries are characterized by high energy density among secondary batteries, and thus have a wide range of applications from small devices such as mobile phones to large devices such as electric vehicles.

リチウムイオン電池は、さらなる高エネルギー密度化が求められている。その一つの手法として、電極合剤層を厚く形成して電極活物質の担持量を増やすことが考えられる。しかし、電極合剤層の厚膜化に伴う課題の一つとして、集電体までの導電パスが十分に形成されず、電極の電気抵抗が増大してしまい、高出力化時の電池の容量維持率が低下してしまうという問題がある。電極の抵抗を低減する手法として電極密度を上げることが提案されている。しかし、電極密度を上げすぎると、空隙率が低くなり、物質の拡散が阻害されるため、抵抗の上昇につながってしまうことも記載されている（特許文献１参照）。すなわち、電極密度の最適化による抵抗低減には限界があると考えられる。   Lithium ion batteries are required to have higher energy density. One approach is to increase the amount of electrode active material supported by forming a thick electrode mixture layer. However, one of the problems associated with increasing the thickness of the electrode mixture layer is that the conductive path to the current collector is not sufficiently formed, increasing the electrical resistance of the electrode and increasing the battery capacity at the time of high output. There is a problem that the maintenance rate decreases. Increasing the electrode density has been proposed as a technique for reducing the resistance of the electrode. However, it is also described that if the electrode density is increased too much, the porosity decreases and the diffusion of the substance is inhibited, leading to an increase in resistance (see Patent Document 1). That is, it is considered that there is a limit in reducing the resistance by optimizing the electrode density.

この問題を解決する一つの手段として、特許文献２では低密度の電極合剤層と高密度の電極合剤層とを組み合わせることによって電極を作製することにより、良好な特性の電池が得られることが報告されている。しかし、二つの異なる密度の電極合剤層を用いて電極を作るため、電極作製工程が煩雑化するという問題があった。   As one means for solving this problem, in Patent Document 2, a battery having good characteristics can be obtained by fabricating an electrode by combining a low-density electrode mixture layer and a high-density electrode mixture layer. Has been reported. However, since an electrode is formed using two electrode mixture layers having different densities, there is a problem that the electrode manufacturing process becomes complicated.

特許文献３には、正極合剤層の合剤密度は、１．５ｇ／ｃｃ〜４ｇ／ｃｃであってもよい旨が記載されている（段落００１４）。   Patent Document 3 describes that the mixture density of the positive electrode mixture layer may be 1.5 g / cc to 4 g / cc (paragraph 0014).

特開２０１０−１５９０４号公報JP 2010-15904 A 特開２０１３−２５１２１３号公報JP 2013-251213 A 特開２０１４−９３２９５号公報JP 2014-93295 A

本発明の目的は、従来と比較してより簡便に作製できる良好な特性の電極合剤層及び該合剤層が形成されている非水電解質二次電池用電極並びに該電極を有する非水電解質二次電池を提供することにある。   An object of the present invention is to provide an electrode mixture layer with good characteristics that can be more easily produced compared to the prior art, a nonaqueous electrolyte secondary battery electrode on which the mixture layer is formed, and a nonaqueous electrolyte having the electrode It is to provide a secondary battery.

本発明者らは、上記の従来技術に鑑みて鋭意検討を重ねた結果、電極合剤層の組成に着目し、特定の炭素系導電助剤を使用することで、低密度であっても電極電導度が良好で十分な性能を得ることができることを見出し、本発明を完成するに至った。   As a result of intensive studies in view of the above-described conventional techniques, the present inventors focused on the composition of the electrode mixture layer, and by using a specific carbon-based conductive additive, the electrode even at low density It has been found that electrical conductivity is good and sufficient performance can be obtained, and the present invention has been completed.

即ち、上記課題を解決する本発明は以下に記載するものである。   That is, the present invention for solving the above problems is described below.

〔１〕 電極活物質と、平均径が１０ｎｍ以上の炭素系導電助剤と、を少なくとも含む電極合剤層であって、前記炭素系導電助剤の体積含有率が０．９〜５．０（％）であり、かつ前記電極合剤層の密度が０．５０（ｇ／ｃｍ３）以上２．１０（ｇ／ｃｍ３）未満であることを特徴とする非水電解質二次電池用電極合剤層。 [1] An electrode mixture layer containing at least an electrode active material and a carbon-based conductive aid having an average diameter of 10 nm or more, wherein the volume content of the carbon-based conductive aid is 0.9 to 5.0. The electrode mixture layer has a density of 0.50 (g / cm 3 ) or more and less than 2.10 (g / cm 3 ), and the electrode for a non-aqueous electrolyte secondary battery Mixture layer.

〔２〕 活性炭を含まない〔１〕に記載の非水電解質二次電池用電極合剤層。   [2] The electrode mixture layer for a nonaqueous electrolyte secondary battery according to [1], which does not contain activated carbon.

〔３〕 前記炭素系導電助剤が、平均実効繊維長が１０μｍ以上の繊維状炭素である〔１〕又は〔２〕に記載の非水電解質二次電池用電極合剤層。   [3] The electrode mixture layer for a non-aqueous electrolyte secondary battery according to [1] or [2], wherein the carbon-based conductive additive is fibrous carbon having an average effective fiber length of 10 μm or more.

〔４〕 前記繊維状炭素における、Ｘ線回折法で測定した結晶子長さ（Ｌａ）が、１１０〜５００ｎｍである〔３〕に記載の非水電解質二次電池用電極合剤層。   [4] The electrode mixture layer for a nonaqueous electrolyte secondary battery according to [3], wherein the fibrous carbon has a crystallite length (La) measured by an X-ray diffraction method of 110 to 500 nm.

〔５〕 厚みが５０〜１０００μｍである〔１〕乃至〔４〕の何れかに記載の非水電解質二次電池用電極合剤層。   [5] The electrode mixture layer for a nonaqueous electrolyte secondary battery according to any one of [1] to [4], which has a thickness of 50 to 1000 μm.

〔６〕 集電体と、
前記集電体に積層された〔１〕乃至〔５〕の何れかに記載の非水電解質二次電池用電極合剤層と、
から成る非水電解質二次電池用電極。 [6] current collector;
The electrode mixture layer for a nonaqueous electrolyte secondary battery according to any one of [1] to [5] laminated on the current collector,
An electrode for a nonaqueous electrolyte secondary battery.

〔７〕 〔６〕に記載の非水電解質二次電池用電極を有する非水電解質二次電池。   [7] A nonaqueous electrolyte secondary battery comprising the electrode for a nonaqueous electrolyte secondary battery according to [6].

本発明によれば、従来技術で得られていた非水電解質二次電池用電極合剤層よりも簡便な工程で、電極電導度が良好な非水電解質二次電池用電極合剤層を得ることができる。   According to the present invention, an electrode mixture layer for a nonaqueous electrolyte secondary battery having good electrode conductivity is obtained in a simpler process than the electrode mixture layer for a nonaqueous electrolyte secondary battery obtained by the conventional technology. be able to.

以下、本発明について詳細に説明する。   Hereinafter, the present invention will be described in detail.

１．非水電解質二次電池用電極合剤層
本発明の非水電解質二次電池用電極合剤層（以下、単に「正極合剤層」、「負極合剤層」又は「電極合剤層」ともいう）は、電極活物質と、炭素系導電助剤とを少なくとも含み、該炭素系導電助剤の体積含有率が０．９〜５．０（％）の範囲にある。本発明の電極合剤層は、正極合剤層及び負極合剤層の双方に適用可能である。 1. Electrode mixture layer for non-aqueous electrolyte secondary battery Electrode mixture layer for non-aqueous electrolyte secondary battery of the present invention (hereinafter simply referred to as “positive electrode mixture layer”, “negative electrode mixture layer” or “electrode mixture layer”) ) Includes at least an electrode active material and a carbon-based conductive assistant, and the volume content of the carbon-based conductive assistant is in the range of 0.9 to 5.0 (%). The electrode mixture layer of the present invention can be applied to both the positive electrode mixture layer and the negative electrode mixture layer.

本発明の電極合剤層の密度（２５℃）は０．５０（ｇ／ｃｍ３）以上２．１０（ｇ／ｃｍ３）未満の範囲にある。電極合剤層の密度が０．５０（ｇ／ｃｍ３）未満であると、空隙率が高すぎて十分な電池特性を出すことができない。２．１０（ｇ／ｃｍ３）以上であると、空隙率が低すぎて電気抵抗の上昇が起こり電池の特性が悪くなる。密度の下限値は、０．９５（ｇ／ｃｍ３）以上であることが好ましく、１．００（ｇ／ｃｍ３）以上であることがより好ましい。密度の上限値は、２．０７（ｇ／ｃｍ３）未満であることが好ましく、２．００（ｇ／ｃｍ３）未満であることがより好ましく、１．８０（ｇ／ｃｍ３）未満であることがさらに好ましく、１．７０（ｇ／ｃｍ３）未満であることがよりさらに好ましく、１．６０（ｇ／ｃｍ３）未満であることが特に好ましい。 Density of the electrode mixture layer of the present invention (25 ° C.) is in the range of less than 0.50 (g / cm 3) or more 2.10 (g / cm 3). If the density of the electrode mixture layer is less than 0.50 (g / cm 3 ), the porosity is too high to provide sufficient battery characteristics. If it is 2.10 (g / cm 3 ) or more, the porosity is too low and the electrical resistance increases, resulting in poor battery characteristics. The lower limit of the density is preferably 0.95 (g / cm 3 ) or more, and more preferably 1.00 (g / cm 3 ) or more. The upper limit of the density is preferably less than 2.07 (g / cm 3 ), more preferably less than 2.00 (g / cm 3 ), and less than 1.80 (g / cm 3 ). More preferably, it is more preferably less than 1.70 (g / cm 3 ), and particularly preferably less than 1.60 (g / cm 3 ).

本発明の電極合剤層の厚さ（膜厚）は５０μｍ以上であることが好ましく、６０μｍ以上であることがより好ましく、７０μｍ以上であることがさらに好ましく、８０μｍ以上であることがよりさらに好ましく、９０μｍ以上であることが特に好ましく、１００μｍ以上、特には１００μｍ超であることがさらに好ましく、１２０μｍ以上であることが最も好ましい。本発明の電極合剤層の厚さ（膜厚）は特に制限はないが、１０００μｍ以下であることが好ましく、１０００μｍ未満であることがより好ましく、９００μｍ未満であることがさらに好ましく、８００μｍ未満であることが特に好ましい。また、本発明の電極合剤層の厚さ（膜厚）は５０〜１０００μｍであり、８０〜１０００μｍであることが好ましく、１００〜１０００μｍであることがさらに好ましく、１２０〜１０００μｍであることが特に好ましい。   The thickness (film thickness) of the electrode mixture layer of the present invention is preferably 50 μm or more, more preferably 60 μm or more, further preferably 70 μm or more, and further preferably 80 μm or more. 90 μm or more, particularly preferably 100 μm or more, particularly preferably more than 100 μm, and most preferably 120 μm or more. The thickness (film thickness) of the electrode mixture layer of the present invention is not particularly limited, but is preferably 1000 μm or less, more preferably less than 1000 μm, still more preferably less than 900 μm, and less than 800 μm. It is particularly preferred. Moreover, the thickness (film thickness) of the electrode mixture layer of the present invention is 50 to 1000 μm, preferably 80 to 1000 μm, more preferably 100 to 1000 μm, and particularly preferably 120 to 1000 μm. preferable.

電極合剤層の膜厚が５０μｍ未満であると、任意の容量セルを製造しようとした場合、セパレータや集電体を多量に使用することになり、セル内における電極合剤層の体積占有率が低下する。これは、エネルギー密度の観点から好ましくなく、用途がかなり制限されてしまう。特に、エネルギー密度の要求の高い電源用途への適用は困難となってしまう。一方、電極合剤層の膜厚が１０００μｍを超える電極は、電極合剤層にクラックが発生し易くなり製造が比較的困難である。電極の安定的製造の観点からは、電極合剤層の膜厚は１０００μｍ以下であることが好ましい。また、電極合剤層の膜厚が１０００μｍを超える電極は、Ｌｉイオンの輸送が阻害されやすく、抵抗の上昇につながる。そのため、電極合剤層の膜厚は１０００μｍ以下とすることが、抵抗低減の観点からも好ましい。なお、本発明における電極合剤層の厚さは、後述する集電体の厚さを含まない電極合剤層のみの厚さを意味する。
電極合剤層の膜厚の測定方法としては特に限定されないが、例えばマイクロメーターを使用して計測することができる。 If the electrode mixture layer has a film thickness of less than 50 μm, when an arbitrary capacity cell is to be manufactured, a large amount of separator and current collector will be used, and the volume ratio of the electrode mixture layer in the cell Decreases. This is not preferable from the viewpoint of energy density, and its application is considerably limited. In particular, it becomes difficult to apply to power supply applications that require high energy density. On the other hand, an electrode having an electrode mixture layer with a film thickness exceeding 1000 μm is relatively difficult to produce because cracks are likely to occur in the electrode mixture layer. From the viewpoint of stable production of the electrode, the thickness of the electrode mixture layer is preferably 1000 μm or less. Moreover, the electrode in which the film thickness of the electrode mixture layer exceeds 1000 μm tends to hinder the transport of Li ions, leading to an increase in resistance. Therefore, the thickness of the electrode mixture layer is preferably 1000 μm or less from the viewpoint of resistance reduction. In addition, the thickness of the electrode mixture layer in this invention means the thickness of only the electrode mixture layer which does not include the thickness of the electrical power collector mentioned later.
Although it does not specifically limit as a measuring method of the film thickness of an electrode mixture layer, For example, it can measure using a micrometer.

（１−１） 炭素系導電助剤
本発明の電極合剤層は炭素系導電助剤を所定の体積含有率で含有している。炭素系導電助剤としては、例えば、アセチレンブラック、カーボンブラックなどの粒子状炭素、単層カーボンナノチューブ、多層カーボンナノチューブ、カーボンナノファイバー、カーボンナノホーン、炭素繊維などの繊維状炭素、鱗片状炭素、グラフェン、グラファイトなどを挙げることができる。本発明の電極合剤層に含まれる炭素系導電助剤は、本発明の効果を奏すれば、特に限定されることはなく、これらの炭素系導電助剤の一種又は二種以上を含んでいれば良い。
上記の中で、繊維状炭素は取扱い性と導電性とのバランスが良好である。繊維状炭素の形状は特に限定されるものではないが、実質的に分岐を有さない直線構造であることが好ましい。分岐とは、繊維状炭素の主軸が中途で枝分かれしていることや、繊維状炭素の主軸が枝状の副軸を有することをいう。実質的に分岐を有さない直線構造とは、繊維状炭素の分岐度が０．０１個／μｍ以下であることを意味する。なお、この繊維状炭素は、全体として繊維状の形態を有していればよく、例えば、後述のアスペクト比の好ましい範囲未満のものが接触したり結合したりして一体的に繊維形状を持っているもの（例えば、球状炭素が数珠状に連なっているもの、極めて短い少なくとも１本または複数本の繊維が融着等によりつながっているものなど）も含む。 (1-1) Carbon-based conductive auxiliary agent The electrode mixture layer of the present invention contains a carbon-based conductive auxiliary agent at a predetermined volume content. Examples of carbon-based conductive aids include particulate carbon such as acetylene black and carbon black, single-walled carbon nanotubes, multi-walled carbon nanotubes, carbon nanofibers, carbon nanohorns, carbon fibers, and other fibrous carbon, scaly carbon, graphene And graphite. The carbon-based conductive additive contained in the electrode mixture layer of the present invention is not particularly limited as long as the effects of the present invention are achieved, and includes one or more of these carbon-based conductive assistants. It only has to be.
Among the above, fibrous carbon has a good balance between handleability and conductivity. The shape of the fibrous carbon is not particularly limited, but is preferably a linear structure having substantially no branching. The term “branch” means that the main axis of fibrous carbon is branched in the middle, or the main axis of fibrous carbon has a branch-like minor axis. The linear structure having substantially no branch means that the degree of branching of the fibrous carbon is 0.01 piece / μm or less. The fibrous carbon only needs to have a fibrous form as a whole. For example, a fibrous carbon having an aspect ratio less than a preferable range described below is brought into contact with or bonded to each other to have an integral fiber shape. (For example, those in which spherical carbons are connected in a beaded manner, or those in which at least one or a plurality of very short fibers are connected by fusion or the like).

本発明の電極合剤層は、活性炭を含まないことが好ましい。その理由は、活性炭を含むと電極合剤層を作成する際に粘度が上昇するため工程上好ましくないからである。   The electrode mixture layer of the present invention preferably does not contain activated carbon. The reason is that if activated carbon is included, the viscosity increases when forming the electrode mixture layer, which is not preferable in the process.

本発明の電極合剤層における炭素系導電助剤の２５℃における体積含有率は、電極合剤層の体積を基準として０．９〜５．０（％）である。体積含有率をこの範囲とすることにより、電極合剤層の導電性を高くすることが出来る。５．０％を超えると、活物質の割合が減少するため、電池の容量も低下する。体積含有率の下限は、１．０％以上であることが好ましく、１．１％以上であることがより好ましく、１．２％以上であることがさらに好ましく、１．３％以上であることが特に好ましい。また、体積含有率の上限は、４．０％以下であることが好ましく、３．０％以下であることがより好ましく、２．５％以下であることがさらに好ましく、２．０％以下であることが特に好ましい。   The volume content at 25 ° C. of the carbon-based conductive additive in the electrode mixture layer of the present invention is 0.9 to 5.0 (%) based on the volume of the electrode mixture layer. By making volume content into this range, the electroconductivity of an electrode mixture layer can be made high. If it exceeds 5.0%, the ratio of the active material decreases, so the capacity of the battery also decreases. The lower limit of the volume content is preferably 1.0% or more, more preferably 1.1% or more, further preferably 1.2% or more, and 1.3% or more. Is particularly preferred. Further, the upper limit of the volume content is preferably 4.0% or less, more preferably 3.0% or less, further preferably 2.5% or less, and 2.0% or less. It is particularly preferred.

炭素系導電助剤は、結晶性が高いと電極電導度が良好であり、また、耐電圧に優れるため望ましい。本発明に用いる炭素系導電助剤は、結晶性の指標であるＸ線回折法で測定した結晶子長さ（Ｌａ）が１００〜５００ｎｍであることが好ましく、１１０〜５００ｎｍであることがより好ましく、１５０〜５００ｎｍであることがさらに好ましく、２００〜５００ｎｍであることが特に好ましい。１００ｎｍ未満である場合、炭素材料の導電性が十分ではない。一方、結晶子サイズは、Ｘ線回折法によって測定を行うが、結晶が大きく発達すると測定誤差が大きくなることから、実質的には５００ｎｍが測定の限界である。
本発明において、Ｘ線回折法で測定した結晶子長さ（Ｌａ）とは、日本工業規格ＪＩＳ Ｒ ７６５１「炭素材料の格子定数及び結晶子の大きさ測定方法」（２００７）により測定される値をいう。 A carbon-based conductive aid is desirable because of high crystallinity, good electrode conductivity, and excellent withstand voltage. The carbon-based conductive additive used in the present invention preferably has a crystallite length (La) measured by an X-ray diffraction method that is an index of crystallinity of 100 to 500 nm, and more preferably 110 to 500 nm. 150 to 500 nm is more preferable, and 200 to 500 nm is particularly preferable. When the thickness is less than 100 nm, the conductivity of the carbon material is not sufficient. On the other hand, the crystallite size is measured by the X-ray diffraction method. However, since the measurement error increases as the crystal grows greatly, the measurement limit is substantially 500 nm.
In the present invention, the crystallite length (La) measured by the X-ray diffraction method is a value measured by Japanese Industrial Standard JIS R 7651 “Lattice constant of carbon material and crystallite size measuring method” (2007). Say.

本発明における炭素系導電助剤は、Ｘ線回折法で測定した隣接するグラファイトシート間の距離である結晶面間隔（ｄ００２）が０．３３５〜０．３４０ｎｍであることが好ましく、０．３３５〜０．３３９ｎｍであることがより好ましい。０．３３５〜０．３４０ｎｍの範囲を逸脱すると、炭素系導電助剤の導電性が著しく低下するため好ましくない。   The carbon-based conductive additive in the present invention preferably has a crystal plane distance (d002) which is a distance between adjacent graphite sheets measured by X-ray diffraction method is 0.335 to 0.340 nm, and 0.335 to More preferably, it is 0.339 nm. It is not preferable to deviate from the range of 0.335 to 0.340 nm because the conductivity of the carbon-based conductive aid is remarkably lowered.

本発明における炭素系導電助剤は、グラフェン（網平面群）の厚さ（Ｌｃ）が１．０〜１３０ｎｍであることが好ましい。１．０ｎｍ未満である場合、炭素材料の導電率が著しく低下してしまうため好ましくない。   The carbon-based conductive additive in the present invention preferably has a graphene (network plane group) thickness (Lc) of 1.0 to 130 nm. When the thickness is less than 1.0 nm, the conductivity of the carbon material is remarkably lowered, which is not preferable.

本発明における炭素系導電助剤は、平均径が１０ｎｍ以上である。ここで、平均径とは、炭素性導電助剤が繊維状炭素の場合にはその繊維径をいい、球状であれば直径をいい、扁平であれば短径をいう。即ち、炭素系導電助剤の最も小さい次元の長さをいう。   The carbon-based conductive additive in the present invention has an average diameter of 10 nm or more. Here, the average diameter means the fiber diameter when the carbonaceous conductive additive is fibrous carbon, the diameter when it is spherical, and the short diameter when flat. That is, it refers to the length of the smallest dimension of the carbon-based conductive additive.

本発明に用いる炭素系導電助剤は、電極合剤層内に導電性のネットワークを形成する効果が高く、電池出力改善、電池耐久性向上の観点から繊維状炭素であることが好ましい。繊維状炭素としては、例えば、カーボンナノチューブ、カーボンナノリボンなどの気相成長炭素材料も含まれるが、結晶性の高い炭素材料である必要から、ＰＡＮ系よりもピッチを原料とする炭素繊維が好ましい。   The carbon-based conductive auxiliary agent used in the present invention is highly effective in forming a conductive network in the electrode mixture layer, and is preferably fibrous carbon from the viewpoint of improving battery output and battery durability. Examples of the fibrous carbon include vapor grown carbon materials such as carbon nanotubes and carbon nanoribbons. However, carbon fibers using pitch as a raw material are preferable to PAN-based materials because they need to be highly crystalline carbon materials.

本発明に用いる炭素系導電助剤としての繊維状炭素の平均繊維径は、１０〜９００ｎｍであることが好ましい。該上限値は、６００ｎｍ以下であることが好ましく、５００ｎｍ以下であることがより好ましく、４００ｎｍ以下であることがさらに好ましく、３００ｎｍ以下であることがよりさらに好ましく、２５０ｎｍ以下であることが特に好ましく、２００ｎｍ以下であることが最も好ましい。該下限値は、５０ｎｍ以上であることが好ましく、１００ｎｍ以上であることがより好ましく、１５０ｎｍ以上であることがさらに好ましい。
１０ｎｍ未満であると、嵩密度が非常に小さくハンドリング性に劣る。また、電極合剤層を構成した際、電極強度が低下する傾向がある。９００ｎｍ超である場合、電極合剤層内において隙間が生じ易くなる。
ここで、本発明における繊維径は、電界放射型走査電子顕微鏡によって倍率２，０００倍で撮影した写真図より測定された値を意味する。 The average fiber diameter of fibrous carbon as the carbon-based conductive aid used in the present invention is preferably 10 to 900 nm. The upper limit is preferably 600 nm or less, more preferably 500 nm or less, further preferably 400 nm or less, still more preferably 300 nm or less, and particularly preferably 250 nm or less, Most preferably, it is 200 nm or less. The lower limit is preferably 50 nm or more, more preferably 100 nm or more, and further preferably 150 nm or more.
If it is less than 10 nm, the bulk density is very small and the handling property is poor. Moreover, when an electrode mixture layer is constructed, the electrode strength tends to decrease. When it exceeds 900 nm, a gap is easily generated in the electrode mixture layer.
Here, the fiber diameter in the present invention means a value measured from a photograph taken at a magnification of 2,000 with a field emission scanning electron microscope.

繊維状炭素の平均実効繊維長は、１〜１００μｍの範囲が好ましく、１〜５０μｍであることがより好ましく、５〜２０μｍであることがさらに好ましい。１μｍ未満である場合、電極合剤層内の導電性、電極の強度、電解液保液性が低くなるため好ましくない。１００μｍ超の場合、繊維状炭素の分散性が損なわれることから好ましくない。即ち、繊維状炭素が長すぎる場合、繊維状炭素が電極合剤層の面内方向に配向し易くなる。その結果、膜厚方向への導電パスを形成し難くなってしまう。特に、本発明の繊維状炭素の平均実効繊維長は、１０μｍ以上であることが好ましい。平均実効繊維長が１０μｍ以上であると本発明のように低密度の電極合剤層であってもその長い実効繊維長から活物質間の導電パスをより十分に形成することができるからである。平均実効繊維長は、１２μｍ以上が好ましく、１５μｍ以上がより好ましい。   The average effective fiber length of the fibrous carbon is preferably in the range of 1 to 100 μm, more preferably 1 to 50 μm, and further preferably 5 to 20 μm. When the thickness is less than 1 μm, the conductivity in the electrode mixture layer, the strength of the electrode, and the electrolyte solution retention are lowered, which is not preferable. If it exceeds 100 μm, the dispersibility of the fibrous carbon is impaired, which is not preferable. That is, when the fibrous carbon is too long, the fibrous carbon is easily oriented in the in-plane direction of the electrode mixture layer. As a result, it becomes difficult to form a conductive path in the film thickness direction. In particular, the average effective fiber length of the fibrous carbon of the present invention is preferably 10 μm or more. This is because when the average effective fiber length is 10 μm or more, a conductive path between the active materials can be more sufficiently formed from the long effective fiber length even in the case of a low-density electrode mixture layer as in the present invention. . The average effective fiber length is preferably 12 μm or more, and more preferably 15 μm or more.

本発明において繊維状炭素の繊維長は、実際の繊維長ではなく、実効繊維長によって定義される。なぜなら、繊維状炭素は、電極合剤層内において実際の繊維長で導電に寄与しているとは限らないからである。例えば、電極合剤層内で繊維が折れ曲がったり丸まったりして、実際の繊維長で導電に寄与していない場合がある。本発明において、繊維状炭素の実効繊維長は、単体の繊維状炭素に両端が接する最長の線分の長さとして定義される。換言すれば、単体の繊維状炭素が導電することができる最大の直線距離である。即ち、繊維状炭素が完全な直線構造を有する場合は、実効繊維長は実際の繊維長と略等しい。繊維状炭素が分岐構造を有する場合や丸まっている場合は、その単体の繊維状炭素上にある２点間を結ぶ最大の線分の長さをいう。   In the present invention, the fiber length of fibrous carbon is defined not by the actual fiber length but by the effective fiber length. This is because fibrous carbon does not always contribute to conduction with the actual fiber length in the electrode mixture layer. For example, the fiber may be bent or rounded in the electrode mixture layer, and the actual fiber length may not contribute to conduction. In the present invention, the effective fiber length of fibrous carbon is defined as the length of the longest line segment in which both ends are in contact with a single fibrous carbon. In other words, it is the maximum linear distance that a single fibrous carbon can conduct. That is, when the fibrous carbon has a complete linear structure, the effective fiber length is substantially equal to the actual fiber length. When the fibrous carbon has a branched structure or is rounded, it means the maximum length of a line segment connecting two points on the single fibrous carbon.

繊維状炭素の平均実効繊維長（Ｌ）と平均繊維径（Ｄ）との比（Ｌ／Ｄ）は３０以上であることが好ましく、５０以上であることがより好ましい。比（Ｌ／Ｄ）を３０以上とすることにより、電極合剤層中において導電パスが効率的に形成され、得られる電池特性を高くすることができる。３０未満の場合、電極合剤層中において導電パスの形成が不十分になり易く、電極合剤層の膜厚方向の抵抗値が十分に低下しない場合がある。比（Ｌ／Ｄ）の上限値は特に限定されないが、一般に４０００以下であり、１０００以下であることが好ましく、５００以下であることがより好ましい。４０００を超える場合、炭素繊維の分散性が損なわれることから好ましくない。   The ratio (L / D) between the average effective fiber length (L) and the average fiber diameter (D) of the fibrous carbon is preferably 30 or more, and more preferably 50 or more. By setting the ratio (L / D) to 30 or more, a conductive path is efficiently formed in the electrode mixture layer, and the obtained battery characteristics can be enhanced. If it is less than 30, the formation of the conductive path is likely to be insufficient in the electrode mixture layer, and the resistance value in the film thickness direction of the electrode mixture layer may not be sufficiently reduced. The upper limit of the ratio (L / D) is not particularly limited, but is generally 4000 or less, preferably 1000 or less, and more preferably 500 or less. When it exceeds 4000, the dispersibility of the carbon fiber is impaired, which is not preferable.

上記のような繊維状炭素を低密度の電極合剤層に適用することにより、得られる電極合剤層の電気伝導性や耐電圧に貢献することができる。通常、電極合剤層の厚膜化に伴う課題の一つとして、高出力化時の電池の容量維持率が低下してしまうという問題がある。一般に、電極の抵抗を低減する手法としては、電極密度を上げることが提案されている。本発明は、電極密度を上げずに寧ろ小さくして、かつ所定の炭素材料、即ち高結晶性で好ましくは繊維長の長い繊維状炭素を用いることにより、高出力化時の電池の容量維持率を高くすることができる。   By applying the fibrous carbon as described above to the low-density electrode mixture layer, it is possible to contribute to the electrical conductivity and withstand voltage of the obtained electrode mixture layer. In general, as one of the problems associated with increasing the thickness of the electrode mixture layer, there is a problem in that the capacity retention rate of the battery at the time of high output decreases. In general, increasing the electrode density has been proposed as a technique for reducing the resistance of the electrode. The present invention reduces the capacity of the battery without increasing the electrode density, and uses a predetermined carbon material, that is, fibrous carbon having a high crystallinity and preferably a long fiber length, so that the capacity retention rate of the battery at the time of high output is increased. Can be high.

（１−２） 炭素系導電助剤の製造方法
本発明の電極合剤層に用いる炭素系導電助剤として好ましく用いることができる炭素繊維の製造方法について以下に説明する。炭素繊維の製造方法は特に限定されないが、例えば次に記載する（１）〜（４）の工程を経ることにより製造することができる。
（１）熱可塑性樹脂及び炭素前駆体から成る樹脂組成物を溶融状態で成形することにより、炭素前駆体を繊維化して樹脂複合繊維を得る工程、
（２）前記樹脂複合繊維を安定化し、樹脂複合安定化繊維を得る安定化工程、
（３）樹脂複合安定化繊維から前記熱可塑性樹脂を除去して安定化繊維のみを分離する熱可塑性樹脂除去工程、
（４）安定化繊維を不活性雰囲気下で加熱して炭素化乃至黒鉛化して炭素繊維を得る炭化焼成工程。 (1-2) Method for Producing Carbon-Based Conductive Auxiliary A method for producing carbon fiber that can be preferably used as the carbon-based conductive aid used in the electrode mixture layer of the present invention will be described below. Although the manufacturing method of carbon fiber is not specifically limited, For example, it can manufacture by passing through the process of (1)-(4) described below.
(1) A step of forming a resin composition comprising a thermoplastic resin and a carbon precursor in a molten state, thereby obtaining a resin composite fiber by fiberizing the carbon precursor;
(2) a stabilization step of stabilizing the resin composite fiber to obtain a resin composite stabilized fiber;
(3) a thermoplastic resin removing step of removing only the stabilized fiber by removing the thermoplastic resin from the resin composite stabilized fiber;
(4) A carbonization firing step in which the stabilized fiber is heated in an inert atmosphere to be carbonized or graphitized to obtain carbon fiber.

＜熱可塑性樹脂＞
この炭素繊維の製造方法で使用する熱可塑性樹脂は、樹脂複合繊維を製造することができるとともに、熱可塑性樹脂除去工程において容易に除去される必要がある。このような熱可塑性樹脂としては、ポリオレフィン、ポリメタクリレート、ポリメチルメタクリレート等のポリアクリレート系ポリマー、ポリスチレン、ポリカーボネート、ポリアリレート、ポリエステル、ポリアミド、ポリエステルカーボネート、ポリサルホン、ポリイミド、ポリエーテルイミド、ポリケトン、ポリ乳酸が例示される。これらの中でも、ポリオレフィンが好ましく用いられる。 <Thermoplastic resin>
The thermoplastic resin used in this carbon fiber production method can produce resin composite fibers and needs to be easily removed in the thermoplastic resin removal step. Examples of such thermoplastic resins include polyolefins, polymethacrylates, polymethylmethacrylates and other polyacrylate polymers, polystyrene, polycarbonate, polyarylate, polyester, polyamide, polyester carbonate, polysulfone, polyimide, polyetherimide, polyketone, and polylactic acid. Is exemplified. Among these, polyolefin is preferably used.

ポリオレフィンの具体例としては、ポリエチレン、ポリプロピレン、ポリ−４−メチルペンテン−１、及びこれらを含む共重合体が挙げられる。熱可塑性樹脂除去工程において除去し易いという観点からは、ポリエチレンを用いることが好ましい。ポリエチレンとしては、高圧法低密度ポリエチレン、気相法・溶液法・高圧法直鎖状低密度ポリエチレンなどの低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレンなどの単独重合体又はエチレンとα−オレフィンとの共重合体；エチレン・酢酸ビニル共重合体などのエチレンと他のビニル系単量体との共重合体が挙げられる。   Specific examples of the polyolefin include polyethylene, polypropylene, poly-4-methylpentene-1, and a copolymer containing these. From the viewpoint of easy removal in the thermoplastic resin removal step, it is preferable to use polyethylene. Polyethylene includes high pressure method low density polyethylene, gas phase method, solution method, high pressure method low density polyethylene such as linear low density polyethylene, homopolymer such as medium density polyethylene, high density polyethylene or ethylene and α-olefin. A copolymer of ethylene and another vinyl monomer such as an ethylene / vinyl acetate copolymer.

この熱可塑性樹脂は、ＪＩＳ Ｋ ７２１０に準拠して測定されたメルトマスフローレート（ＭＦＲ）が０．１〜１０ｇ／１０ｍｉｎであることが好ましく、０．１〜５ｇ／１０ｍｉｎであることがより好ましく、０．１〜３ｇ／１０ｍｉｎであることが特に好ましい。ＭＦＲが上記範囲であると、熱可塑性樹脂中にメソフェーズピッチを良好にミクロ分散することができる。また、樹脂複合繊維を成形する際に、繊維が引き延ばされることにより、炭素前駆体の分子配向性を制御して得られる炭素繊維の結晶性を向上させるとともに、得られる炭素繊維の繊維径をより小さくすることができる。熱可塑性樹脂は炭素前駆体と容易に溶融混練できるという点から、非晶性の場合はガラス転移温度が２５０℃以下、結晶性の場合は融点が３００℃以下であることが好ましい。   This thermoplastic resin preferably has a melt mass flow rate (MFR) measured according to JIS K 7210 of 0.1 to 10 g / 10 min, more preferably 0.1 to 5 g / 10 min. It is especially preferable that it is 0.1-3 g / 10min. When the MFR is in the above range, the mesophase pitch can be finely dispersed in the thermoplastic resin. Further, when the resin composite fiber is formed, the fiber is stretched to improve the crystallinity of the carbon fiber obtained by controlling the molecular orientation of the carbon precursor, and the fiber diameter of the obtained carbon fiber is increased. It can be made smaller. The thermoplastic resin preferably has a glass transition temperature of 250 ° C. or lower in the case of amorphous and a melting point of 300 ° C. or lower in the case of crystallinity because it can be easily melt-kneaded with the carbon precursor.

＜炭素前駆体＞
炭素前駆体としてはメソフェーズピッチを用いることが好ましい。以下、炭素前駆体としてメソフェーズピッチを用いる場合について説明する。メソフェーズピッチとは、溶融状態において光学的異方性相（液晶相）を形成しうるピッチである。使用するメソフェーズピッチとしては、石炭や石油の蒸留残渣を原料とするものや、ナフタレン等の芳香族炭化水素を原料とするものが挙げられる。例えば、石炭由来のメソフェーズピッチは、コールタールピッチの水素添加・熱処理を主体とする処理、水素添加・熱処理・溶剤抽出を主体とする処理等により得られる。 <Carbon precursor>
It is preferable to use mesophase pitch as the carbon precursor. Hereinafter, the case where mesophase pitch is used as the carbon precursor will be described. The mesophase pitch is a pitch that can form an optically anisotropic phase (liquid crystal phase) in a molten state. Examples of the mesophase pitch to be used include those using a distillation residue of coal or petroleum as a raw material and those using an aromatic hydrocarbon such as naphthalene as a raw material. For example, a coal-derived mesophase pitch can be obtained by a process mainly including hydrogenation / heat treatment of coal tar pitch, a process mainly including hydrogenation / heat treatment / solvent extraction, and the like.

より具体的には、以下の方法により得ることができる。
先ず、キノリン不溶分を除去した軟化点８０℃のコールタールピッチを、Ｎｉ−Ｍｏ系触媒存在下、圧力１３ＭＰａ、温度３４０℃で水添し、水素化コールタールピッチを得る。この水素化コールタールピッチを常圧下、４８０℃で熱処理した後、減圧して低沸点分を除去し、粗メソフェーズピッチを得る。この粗メソフェーズピッチを温度３４０℃でフィルターを用いてろ過を行って異物を取り除くことにより、精製メソフェーズピッチを得ることができる。 More specifically, it can be obtained by the following method.
First, a coal tar pitch having a softening point of 80 ° C. from which quinoline-insoluble components have been removed is hydrogenated at a pressure of 13 MPa and a temperature of 340 ° C. in the presence of a Ni—Mo catalyst to obtain a hydrogenated coal tar pitch. The hydrogenated coal tar pitch is heat-treated at 480 ° C. under normal pressure, and then reduced in pressure to remove low boiling point components to obtain a crude mesophase pitch. By purifying the crude mesophase pitch with a filter at a temperature of 340 ° C. to remove foreign matters, a purified mesophase pitch can be obtained.

メソフェーズピッチの光学的異方性含有量（メソフェーズ率）は、８０％以上であることが好ましく、９０％以上であることがより好ましい。   The optically anisotropic content (mesophase ratio) of the mesophase pitch is preferably 80% or more, and more preferably 90% or more.

また、上記メソフェーズピッチは、軟化点が１００〜４００℃であることが好ましく、１５０〜３５０℃であることがより好ましい。   Further, the mesophase pitch preferably has a softening point of 100 to 400 ° C, more preferably 150 to 350 ° C.

＜樹脂組成物＞
この炭素繊維の製造方法において用いられる、熱可塑性樹脂とメソフェーズピッチとから成る樹脂組成物（以下、メソフェーズピッチ組成物ともいう）は、熱可塑性樹脂と、該熱可塑性樹脂１００質量部に対して１〜１５０質量部のメソフェーズピッチと、を含んで成ることが好ましい。メソフェーズピッチの含有量は５〜１００質量部であることがより好ましい。メソフェーズピッチの含有量が１５０質量部を超えると所望の繊維径を有する樹脂複合繊維が得られず、１質量部未満であると目的とする炭素繊維を安価に製造することができない等の問題が生じるため好ましくない。 <Resin composition>
A resin composition composed of a thermoplastic resin and mesophase pitch (hereinafter also referred to as a mesophase pitch composition) used in this carbon fiber production method is 1 per 100 parts by mass of the thermoplastic resin and the thermoplastic resin. It is preferable to comprise -150 mass parts mesophase pitch. The mesophase pitch content is more preferably 5 to 100 parts by mass. If the mesophase pitch content exceeds 150 parts by mass, a resin composite fiber having a desired fiber diameter cannot be obtained, and if it is less than 1 part by mass, the target carbon fiber cannot be produced at a low cost. Since it occurs, it is not preferable.

繊維径が９００ｎｍ以下である炭素繊維を製造するためには、熱可塑性樹脂中におけるメソフェーズピッチの分散径を０．０１〜５０μｍとすることが好ましく、０．０１〜３０μｍとすることがより好ましい。メソフェーズピッチの熱可塑性樹脂中への分散径が０．０１〜５０μｍの範囲を逸脱すると、所望の炭素繊維を製造することが困難となることがある。なお、メソフェーズピッチ組成物中において、メソフェーズピッチは球状又は楕円状の島相を形成するが、上記分散径とは、島成分が球状の場合はその直径を意味し、楕円状の場合はその長軸径を意味する。   In order to produce carbon fibers having a fiber diameter of 900 nm or less, the dispersion diameter of the mesophase pitch in the thermoplastic resin is preferably 0.01 to 50 μm, and more preferably 0.01 to 30 μm. If the dispersion diameter of the mesophase pitch in the thermoplastic resin is out of the range of 0.01 to 50 μm, it may be difficult to produce a desired carbon fiber. In the mesophase pitch composition, the mesophase pitch forms a spherical or elliptical island phase, but the above dispersion diameter means the diameter when the island component is spherical, and the length when it is elliptical. It means the shaft diameter.

上記０．０１〜５０μｍの分散径は、メソフェーズピッチ組成物を３００℃で３分間保持した後においても上記範囲を維持していることが好ましく、３００℃で５分間保持した後においても維持していることがより好ましく、３００℃で１０分間保持した後においても維持していることが特に好ましい。一般に、メソフェーズピッチ組成物を溶融状態で保持しておくと、メソフェーズピッチ組成物中においてメソフェーズピッチが時間と共に凝集する。メソフェーズピッチが凝集してその分散径が５０μｍを超えると、所望の炭素繊維を製造することが困難となることがある。メソフェーズピッチ組成物中におけるメソフェーズピッチの凝集速度は、使用する熱可塑性樹脂及びメソフェーズピッチの種類により変動する。   The dispersion diameter of 0.01 to 50 μm is preferably maintained within the above range even after the mesophase pitch composition is held at 300 ° C. for 3 minutes, and is maintained even after being held at 300 ° C. for 5 minutes. It is more preferable that it is maintained even after being held at 300 ° C. for 10 minutes. Generally, when the mesophase pitch composition is kept in a molten state, the mesophase pitch aggregates with time in the mesophase pitch composition. When the mesophase pitch is aggregated and the dispersion diameter exceeds 50 μm, it may be difficult to produce a desired carbon fiber. The aggregation rate of the mesophase pitch in the mesophase pitch composition varies depending on the type of the thermoplastic resin and mesophase pitch used.

メソフェーズピッチ組成物は、熱可塑性樹脂とメソフェーズピッチとを溶融状態において混練することにより製造することができる。熱可塑性樹脂とメソフェーズピッチとの溶融混練は公知の装置を用いて行うことができる。例えば、一軸式混練機、二軸式混練機、ミキシングロール、バンバリーミキサーからなる群より選ばれる１種類以上を用いることができる。これらの中でも、熱可塑性樹脂中にメソフェーズピッチを良好にミクロ分散させるという目的から、二軸式混練機を用いることが好ましく、特に各軸が同方向に回転する二軸式混練機を用いることが好ましい。   The mesophase pitch composition can be produced by kneading a thermoplastic resin and mesophase pitch in a molten state. Melting and kneading of the thermoplastic resin and the mesophase pitch can be performed using a known apparatus. For example, at least one selected from the group consisting of a single-screw kneader, a twin-screw kneader, a mixing roll, and a Banbury mixer can be used. Among these, a biaxial kneader is preferably used for the purpose of satisfactorily microdispersing the mesophase pitch in the thermoplastic resin, and in particular, a biaxial kneader in which each axis rotates in the same direction is used. preferable.

混練温度としては、熱可塑性樹脂とメソフェーズピッチとが溶融状態であれば特に制限されないが、１００〜４００℃であることが好ましく、１５０〜３５０℃であることが好ましい。混練温度が１００℃未満であると、メソフェーズピッチが溶融状態にならず、熱可塑性樹脂中にミクロ分散させることが困難であるため好ましくない。一方、４００℃を超える場合、熱可塑性樹脂及びメソフェーズピッチの分解が進行するため好ましくない。また、溶融混練の時間としては、０．５〜２０分間であることが好ましく、１〜１５分間であることがより好ましい。溶融混練の時間が０．５分間未満の場合、メソフェーズピッチのミクロ分散が困難であるため好ましくない。一方、２０分間を超える場合、炭素繊維の生産性が著しく低下するため好ましくない。   The kneading temperature is not particularly limited as long as the thermoplastic resin and the mesophase pitch are in a molten state, but is preferably 100 to 400 ° C, and more preferably 150 to 350 ° C. When the kneading temperature is less than 100 ° C., the mesophase pitch is not in a molten state, and it is difficult to micro-disperse in the thermoplastic resin, which is not preferable. On the other hand, when the temperature exceeds 400 ° C., decomposition of the thermoplastic resin and mesophase pitch proceeds, which is not preferable. Further, the melt kneading time is preferably 0.5 to 20 minutes, and more preferably 1 to 15 minutes. When the melt kneading time is less than 0.5 minutes, it is not preferable because micro dispersion of mesophase pitch is difficult. On the other hand, if it exceeds 20 minutes, the productivity of the carbon fiber is remarkably lowered, which is not preferable.

溶融混練は、酸素ガス含有量が１０体積％未満の不活性雰囲気下で行うことが好ましく、酸素ガス含有量が５体積％未満の不活性雰囲気下で行うことがより好ましく、酸素ガス含有量が１％体積未満の不活性雰囲気下で行うことが特に好ましい。本発明で使用するメソフェーズピッチは、溶融混練時に酸素と反応することにより変性してしまい、熱可塑性樹脂中へのミクロ分散を阻害することがある。このため、酸素とメソフェーズピッチとの反応を抑制するために不活性雰囲気下で溶融混練を行うことが好ましい。   The melt-kneading is preferably performed in an inert atmosphere having an oxygen gas content of less than 10% by volume, more preferably performed in an inert atmosphere having an oxygen gas content of less than 5% by volume, and the oxygen gas content is It is particularly preferred to carry out in an inert atmosphere of less than 1% volume. The mesophase pitch used in the present invention may be modified by reacting with oxygen during melt-kneading and may inhibit micro-dispersion in the thermoplastic resin. For this reason, it is preferable to perform melt kneading in an inert atmosphere in order to suppress the reaction between oxygen and mesophase pitch.

＜樹脂複合繊維＞
上記のメソフェーズピッチ組成物から樹脂複合繊維を製造する方法としては、所望の炭素繊維が作製できれば限定されないが、メソフェーズピッチ組成物を紡糸口金より溶融紡糸する方法、メソフェーズピッチ組成物を矩形口金より溶融製膜する方法を例示することができる。 <Resin composite fiber>
The method for producing a resin composite fiber from the above mesophase pitch composition is not limited as long as a desired carbon fiber can be produced, but the mesophase pitch composition is melt-spun from a spinneret, and the mesophase pitch composition is melted from a rectangular die. A method for forming a film can be exemplified.

結晶性の高い炭素繊維を得るためには、樹脂複合繊維を得る段階において、樹脂複合繊維に含まれるメソフェーズピッチの分子配向性を高める操作を行うことが必要である。樹脂複合繊維に含まれるメソフェーズピッチの分子配向性を高める操作としては、溶融状態のメソフェーズピッチの分子配向性を高めるために変形を加えることが好ましい。係る方法としては、溶融状態のメソフェーズピッチにせん断によるひずみを加える方法、伸長によるひずみを加える方法を例示することができる。   In order to obtain carbon fibers with high crystallinity, it is necessary to increase the molecular orientation of the mesophase pitch contained in the resin composite fiber at the stage of obtaining the resin composite fiber. As an operation for increasing the molecular orientation of the mesophase pitch contained in the resin composite fiber, it is preferable to add a deformation to increase the molecular orientation of the mesophase pitch in the molten state. Examples of such a method include a method of applying strain due to shear to a mesophase pitch in a molten state and a method of applying strain due to elongation.

せん断によるひずみを加える方法としては、メソフェーズピッチが溶融した状態において、溶融状態のメソフェーズピッチ組成物の線速度を大きくする方法が例示される。具体的には、溶融状態のメソフェーズピッチ組成物が流路内を通過する際の通過速度を高くすることにより、せん断によるひずみを加える方法が挙げられる。
また、伸長によるひずみを加える方法としては、メソフェーズピッチが溶融した状態において、溶融状態のメソフェーズピッチ組成物の線速度を、口金の吐出側に向けて大きくしていく方法が挙げられる。具体的には、口金の流路内の断面積を吐出側に向けて漸減させる方法や、口金から吐出されたメソフェーズピッチ組成物を、吐出線速度よりも大きな線速度で引き取る方法などが挙げられる。 Examples of the method of applying strain due to shear include a method of increasing the linear velocity of a mesophase pitch composition in a molten state in a state where the mesophase pitch is melted. Specifically, a method of applying strain due to shearing by increasing the passing speed when the mesophase pitch composition in a molten state passes through the flow path can be mentioned.
Further, as a method of applying strain due to elongation, there is a method of increasing the linear velocity of the melted mesophase pitch composition toward the discharge side of the die in a state where the mesophase pitch is melted. Specifically, a method of gradually decreasing the cross-sectional area in the flow path of the die toward the discharge side, a method of taking the mesophase pitch composition discharged from the die at a linear velocity larger than the discharge linear velocity, and the like are mentioned. .

メソフェーズピッチの分子配向性を高める操作の際の温度は、メソフェーズピッチの溶融温度よりも高いことが必要であり、１５０〜４００℃であることが好ましく、１８０〜３５０℃であることがより好ましい。４００℃を超える場合、メソフェーズピッチの変形緩和速度が大きくなり、繊維の形態を保つことが難しくなる。   The temperature during the operation for increasing the molecular orientation of the mesophase pitch needs to be higher than the melting temperature of the mesophase pitch, preferably 150 to 400 ° C, and more preferably 180 to 350 ° C. When it exceeds 400 ° C., the deformation relaxation rate of the mesophase pitch is increased, and it is difficult to maintain the fiber form.

また、樹脂複合繊維の製造工程は冷却工程を有していてもよい。冷却工程としては、例えば、溶融紡糸の場合、紡糸口金の下流の雰囲気を冷却する方法が挙げられる。溶融製膜の場合、矩形口金の下流に冷却ドラムを設ける方法が挙げられる。冷却工程を設けることにより、メソフェーズピッチが伸長により変形する領域を調整でき、ひずみの速度を調整することができる。また、冷却工程を設けることにより、紡糸又は製膜後の樹脂複合繊維を直ちに冷却固化させて安定した成形を可能とする。   Moreover, the manufacturing process of resin composite fiber may have a cooling process. Examples of the cooling step include a method of cooling the atmosphere downstream of the spinneret in the case of melt spinning. In the case of melt film formation, a method of providing a cooling drum downstream of the rectangular die can be used. By providing the cooling step, it is possible to adjust the region in which the mesophase pitch is deformed by extension, and to adjust the strain rate. Further, by providing a cooling step, the resin composite fiber after spinning or film formation is immediately cooled and solidified to enable stable molding.

＜樹脂複合安定化繊維＞
上記のようにして得られた樹脂複合繊維は、該樹脂複合繊維に含まれるメソフェーズピッチ繊維を安定化（不融化ともいう）して樹脂複合安定化繊維が作製される。安定化は、空気、酸素、オゾン、二酸化窒素、ハロゲンなどを用いるガス気流処理、酸性水溶液などを用いる溶液処理など公知の方法で行うことができるが、生産性の面からガス気流処理による不融化が好ましい。 <Resin composite stabilized fiber>
The resin composite fibers obtained as described above are stabilized (also referred to as infusible) mesophase pitch fibers contained in the resin composite fibers to produce resin composite stabilized fibers. Stabilization can be performed by a known method such as gas flow treatment using air, oxygen, ozone, nitrogen dioxide, halogen, etc., solution treatment using an acidic aqueous solution, etc., but infusibility by gas flow treatment from the viewpoint of productivity. Is preferred.

使用するガス成分としては、取り扱いの容易性から空気、酸素、又はこれを含む混合ガスであることが好ましく、コストの関係から空気を用いるのが特に好ましい。使用する酸素ガス濃度としては、全ガス組成の０．５〜１００体積％の範囲にあることが好ましい。酸素ガス濃度が全ガス組成の１０体積％未満であると、樹脂複合繊維に含まれるメソフェーズピッチを安定化するのに多大の時間を要してしまうので好ましくない。   The gas component to be used is preferably air, oxygen, or a mixed gas containing this from the viewpoint of ease of handling, and it is particularly preferable to use air from the viewpoint of cost. The oxygen gas concentration used is preferably in the range of 0.5 to 100% by volume of the total gas composition. If the oxygen gas concentration is less than 10% by volume of the total gas composition, it takes a long time to stabilize the mesophase pitch contained in the resin composite fiber, which is not preferable.

安定化の反応温度は、３０〜３５０℃が好ましく、４０〜３００℃がより好ましい。安定化の処理時間は、１０〜１２００分間が好ましく、１０〜６００分間がより好ましく、３０〜３００分間が特に好ましい。   The reaction temperature for stabilization is preferably 30 to 350 ° C, more preferably 40 to 300 ° C. The treatment time for stabilization is preferably 10 to 1200 minutes, more preferably 10 to 600 minutes, and particularly preferably 30 to 300 minutes.

上記安定化処理によりメソフェーズピッチの軟化点は著しく上昇するが、所望の炭素繊維を得るという目的から、メソフェーズピッチの軟化点は４００℃以上となることが好ましく、５００℃以上となることがさらに好ましい。   Although the softening point of the mesophase pitch is remarkably increased by the stabilization treatment, the softening point of the mesophase pitch is preferably 400 ° C. or higher and more preferably 500 ° C. or higher for the purpose of obtaining a desired carbon fiber. .

＜熱可塑性樹脂除去工程＞
次に、上述のようにして得られる樹脂複合安定化繊維は、その中に含まれる熱可塑性樹脂が除去されて安定化繊維が分離される。この工程では、安定化繊維の熱分解を抑制しながら、熱可塑性樹脂を分解・除去する。熱可塑性樹脂を分解・除去する方法としては、例えば、溶剤を用いて熱可塑性樹脂を除去する方法や、熱可塑性樹脂を熱分解して除去する方法が挙げられる。 <Thermoplastic resin removal step>
Next, in the resin composite stabilized fiber obtained as described above, the thermoplastic resin contained therein is removed and the stabilized fiber is separated. In this step, the thermoplastic resin is decomposed and removed while suppressing thermal decomposition of the stabilizing fiber. Examples of the method for decomposing and removing the thermoplastic resin include a method for removing the thermoplastic resin using a solvent and a method for thermally decomposing and removing the thermoplastic resin.

熱可塑性樹脂の熱分解は、不活性雰囲気下で行うことが好ましい。ここでいう不活性雰囲気とは、二酸化炭素、窒素、アルゴン等のガス雰囲気をいい、その酸素濃度は３０体積ｐｐｍ以下であることが好ましく、２０体積ｐｐｍ以下であることがより好ましい。本工程で使用する不活性ガスとしては、コストの関係から二酸化炭素及び窒素を用いることが好ましく、窒素を用いることが特に好ましい。   The thermal decomposition of the thermoplastic resin is preferably performed in an inert atmosphere. The inert atmosphere here refers to a gas atmosphere such as carbon dioxide, nitrogen, and argon, and the oxygen concentration thereof is preferably 30 ppm by volume or less, and more preferably 20 ppm by volume or less. As the inert gas used in this step, it is preferable to use carbon dioxide and nitrogen from the viewpoint of cost, and it is particularly preferable to use nitrogen.

熱可塑性樹脂の熱分解は減圧下で行うこともできる。減圧下で熱分解することにより、熱可塑性樹脂を十分に除去することができる。その結果、安定化繊維を炭素化又は黒鉛化して得られる炭素繊維又は黒鉛化繊維の繊維間における融着を少なくすることができる。雰囲気圧力は低いほど好ましいが、５０ｋＰａ以下であることが好ましく、３０ｋＰａ以下であることがより好ましく、１０ｋＰａ以下であることがさらに好ましく、５ｋＰａ以下であることが特に好ましい。一方、完全な真空は達成が困難であるため、圧力の下限は一般に０．０１ｋＰａ以上である。   Thermal decomposition of the thermoplastic resin can also be performed under reduced pressure. By thermally decomposing under reduced pressure, the thermoplastic resin can be sufficiently removed. As a result, fusion between carbon fibers or graphitized fibers obtained by carbonizing or graphitizing the stabilizing fibers can be reduced. The atmospheric pressure is preferably as low as possible, but is preferably 50 kPa or less, more preferably 30 kPa or less, still more preferably 10 kPa or less, and particularly preferably 5 kPa or less. On the other hand, since a complete vacuum is difficult to achieve, the lower limit of the pressure is generally 0.01 kPa or more.

熱可塑性樹脂の熱分解を減圧下で行う場合、上記の雰囲気圧力が保たれれば、微量の酸素や不活性ガスが存在してもよい。特に微量の不活性ガスが存在すると、熱可塑性樹脂の熱劣化による繊維間の融着が抑制される利点があり好ましい。なお、ここでいう微量の酸素とは、酸素濃度が３０体積ｐｐｍ以下であることをいい、微量の不活性ガスとは、不活性ガス濃度が２０体積ｐｐｍ以下であることをいう。用いる不活性ガスの種類は、上述したとおりである。   When the thermal decomposition of the thermoplastic resin is performed under reduced pressure, a trace amount of oxygen or inert gas may be present as long as the above atmospheric pressure is maintained. In particular, the presence of a trace amount of inert gas is preferable because there is an advantage that fusion between fibers due to thermal deterioration of the thermoplastic resin is suppressed. Here, the trace amount of oxygen means that the oxygen concentration is 30 ppm by volume or less, and the trace amount of inert gas means that the inert gas concentration is 20 ppm by volume or less. The kind of the inert gas used is as described above.

熱分解の温度は、３５０〜６００℃であることが好ましく、３８０〜５５０℃であることがより好ましい。熱分解の温度が３５０℃未満である場合、安定化繊維の熱分解は抑えられるものの、熱可塑性樹脂の熱分解を十分行うことができない場合がある。一方、６００℃を超える場合、熱可塑性樹脂の熱分解は十分行うことができるものの、安定化繊維までが熱分解される場合があり、その結果、炭素化時の収率が低下し易い。熱分解の時間としては、０．１〜１０時間であることが好ましく、０．５〜１０時間であることがより好ましい。   The thermal decomposition temperature is preferably 350 to 600 ° C, and more preferably 380 to 550 ° C. When the thermal decomposition temperature is less than 350 ° C., the thermal decomposition of the stabilized fiber may be suppressed, but the thermoplastic resin may not be sufficiently decomposed. On the other hand, when the temperature exceeds 600 ° C., the thermoplastic resin can be sufficiently thermally decomposed, but even the stabilized fiber may be thermally decomposed, and as a result, the yield at the time of carbonization tends to decrease. The time for thermal decomposition is preferably 0.1 to 10 hours, and more preferably 0.5 to 10 hours.

安定化工程及び熱可塑性樹脂除去工程は、樹脂複合繊維又は樹脂複合安定化繊維を、支持基材上に目付け２０００ｇ／ｍ２以下で保持して行うことが好ましい。支持基材に保持することによって、安定化処理時又は熱可塑性樹脂除去時の加熱処理による樹脂複合繊維又は樹脂複合安定化繊維の凝集を抑制することができ、通気性を保つことが可能となる。 The stabilization step and the thermoplastic resin removal step are preferably performed by holding the resin composite fiber or the resin composite stabilized fiber on the support base with a weight per unit area of 2000 g / m 2 or less. By holding on the support substrate, aggregation of the resin composite fiber or the resin composite stabilized fiber due to the heat treatment at the time of the stabilization treatment or removal of the thermoplastic resin can be suppressed, and air permeability can be maintained. .

支持基材の材質としては、溶剤や加熱によって変形や腐食を生じないことが必要である。また、支持基材の耐熱温度としては、上記の熱可塑性樹脂除去工程の熱分解温度で変形しないことが必要であることから、６００℃以上の耐熱性を有していることが好ましい。このような材質としては、ステンレスなどの金属材料やアルミナ、シリカなどのセラミックス材料を挙げることができる。   As a material of the supporting base material, it is necessary that deformation or corrosion does not occur due to a solvent or heating. Moreover, as the heat resistant temperature of the support base material, it is preferable that the supporting base material has a heat resistance of 600 ° C. or higher because it does not need to be deformed at the thermal decomposition temperature in the thermoplastic resin removing step. Examples of such materials include metal materials such as stainless steel and ceramic materials such as alumina and silica.

また、支持基材の形状としては、面垂直方向への通気性を有する形状であることが好ましい。このような形状としては網目構造が好ましい。網目の目開きは０．１〜５ｍｍであることが好ましい。目開きが５ｍｍよりも大きい場合、加熱処理によって網目の線上に繊維が凝集し易くなり、メソフェーズピッチの安定化や熱可塑性樹脂の除去が不十分となる場合があり好ましくない。一方、網目の目開きが０．１ｍｍ未満である場合、支持基材の開孔率の減少により、支持基材の面垂直方向への通気性が低下する場合があり好ましくない。   Moreover, as a shape of a support base material, it is preferable that it is a shape which has air permeability to a surface perpendicular direction. As such a shape, a mesh structure is preferable. The mesh opening is preferably 0.1 to 5 mm. When the mesh opening is larger than 5 mm, the fibers are likely to aggregate on the mesh line by the heat treatment, and the stabilization of the mesophase pitch and the removal of the thermoplastic resin may be insufficient. On the other hand, when the mesh opening is less than 0.1 mm, the air permeability in the direction perpendicular to the surface of the support base material may decrease due to the decrease in the hole area ratio of the support base material, which is not preferable.

＜炭化焼成工程＞
上記安定化繊維を不活性雰囲気下で炭素化及び／又は黒鉛化することにより炭素繊維が得られる。その際に使用する容器としては、黒鉛製のルツボ状のものが好ましい。ここで、炭素化とは比較的低温（好ましくは１０００℃程度）で加熱することをいい、黒鉛化とはさらに高温で加熱（好ましくは３０００℃程度）することにより黒鉛の結晶を成長させることをいう。 <Carbonization firing process>
Carbon fiber can be obtained by carbonizing and / or graphitizing the stabilized fiber under an inert atmosphere. As a container used in that case, a crucible made of graphite is preferable. Here, carbonization refers to heating at a relatively low temperature (preferably about 1000 ° C.), and graphitization refers to growing graphite crystals by heating at a higher temperature (preferably about 3000 ° C.). Say.

上記安定化繊維の炭素化及び／又は黒鉛化時に使用される不活性ガスとしては、窒素、アルゴン等が挙げられる。不活性雰囲気中の酸素濃度は、２０体積ｐｐｍ以下であることが好ましく、１０体積ｐｐｍ以下であることがより好ましい。炭素化及び／又は黒鉛化時の焼成温度は、５００〜３５００℃が好ましく、８００〜３２００℃がより好ましい。特に黒鉛化の際の焼成温度としては、２０００〜３５００℃が好ましく、２１００〜３２００℃がより好ましい。黒鉛化時の温度が２０００℃未満である場合、結晶成長が妨げられ、結晶子長さが不十分となり導電性が著しく低下するおそれがある。また、黒鉛化温度が３５００℃を超える場合、結晶成長の点では好ましいが、炭素繊維の酸素含有量が減少する傾向がある。焼成時間は、０．１〜２４時間が好ましく、０．２〜１０時間がより好ましい。   Nitrogen, argon etc. are mentioned as an inert gas used at the time of carbonization and / or graphitization of the said stabilization fiber. The oxygen concentration in the inert atmosphere is preferably 20 ppm by volume or less, and more preferably 10 ppm by volume or less. The firing temperature during carbonization and / or graphitization is preferably from 500 to 3500 ° C, more preferably from 800 to 3200 ° C. In particular, the firing temperature during graphitization is preferably 2000 to 3500 ° C, more preferably 2100 to 3200 ° C. When the temperature during graphitization is less than 2000 ° C., crystal growth is hindered, the crystallite length becomes insufficient, and the conductivity may be significantly lowered. Further, when the graphitization temperature exceeds 3500 ° C., it is preferable in terms of crystal growth, but the oxygen content of the carbon fiber tends to decrease. The firing time is preferably 0.1 to 24 hours, and more preferably 0.2 to 10 hours.

＜粉砕処理＞
上記炭素繊維の製造方法は、粉砕処理工程を有していても良い。粉砕処理は、熱可塑性樹脂除去工程、及び／又は、炭化焼成工程において実施するのが好ましい。粉砕方法としては、ジェットミル、ボールミル、ビーズミル、インペラーミル、カッターミル等の微粉砕機を適用することが好ましく、粉砕後に必要に応じて分級を行ってもよい。湿式粉砕の場合、粉砕後に分散媒体を除去するが、この際に２次凝集が顕著に生じるとその後の取り扱いが非常に困難となる。このような場合は、乾燥後、ボールミルやジェットミル等を用いて解砕操作を行うことが好ましい。 <Crushing process>
The carbon fiber manufacturing method may include a pulverization process. The pulverization treatment is preferably performed in the thermoplastic resin removal step and / or the carbonization firing step. As a pulverization method, it is preferable to apply a fine pulverizer such as a jet mill, a ball mill, a bead mill, an impeller mill, or a cutter mill, and classification may be performed as necessary after pulverization. In the case of wet pulverization, the dispersion medium is removed after pulverization, but if secondary aggregation occurs significantly at this time, subsequent handling becomes very difficult. In such a case, it is preferable to perform a crushing operation using a ball mill or a jet mill after drying.

（１−３） バインダー
本発明の電極合剤層にはバインダーを使用してもよい。用いられるバインダーとしては、電極成形が可能であり、十分な電気化学的安定性を有しているバインダーであれば用いることが可能である。係るバインダーとしては、ポリビニルアルコール、ポリアクリル酸、カルボキシメチルセルロース、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリフッ化ビニリデン（ＰＶＤＦ）、スチレンブタジエンゴム（ＳＢＲ）、フルオロオレフィン共重合体架橋ポリマー、ポリイミド、ポリアミドイミド、アラミド、フェノール樹脂等よりなる群から選ばれる１種以上を用いることが好ましく、特にポリフッ化ビニリデン（ＰＶＤＦ）やカルボキシメチルセルロースやスチレンブタジエンゴム（ＳＢＲ）が好ましい。バインダーとして用いる際の形態としては特に制限はなく、固体状であっても液体状（例えばエマルション）であってもよく、電極の製造方法（特に乾式混練か湿式混練か）、電解液への溶解性等を考慮して適宜選択することができる。 (1-3) Binder A binder may be used in the electrode mixture layer of the present invention. As a binder to be used, any electrode can be used as long as it can be molded and has sufficient electrochemical stability. As such a binder, polyvinyl alcohol, polyacrylic acid, carboxymethyl cellulose, polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), styrene butadiene rubber (SBR), fluoroolefin copolymer crosslinked polymer, polyimide, polyamideimide, It is preferable to use one or more selected from the group consisting of aramid, phenol resin, and the like, and in particular, polyvinylidene fluoride (PVDF), carboxymethyl cellulose, and styrene butadiene rubber (SBR) are preferable. There are no particular restrictions on the form used as a binder, which may be solid or liquid (eg, emulsion), electrode manufacturing method (especially dry or wet kneading), dissolution in electrolyte It can be appropriately selected in consideration of the properties and the like.

本発明の電極合剤層におけるバインダーの含有量は、電極合剤層の質量を基準として１〜２５質量％であることが好ましく、３〜２０質量％であることがより好ましく、５〜２０質量％であることがさらに好ましい。   The binder content in the electrode mixture layer of the present invention is preferably 1 to 25 mass%, more preferably 3 to 20 mass%, more preferably 5 to 20 mass% based on the mass of the electrode mixture layer. % Is more preferable.

（１−４） 正極活物質
本発明の電極合剤層は、主に非水電解質二次電池、特にリチウムイオン二次電池に好ましく使用される。以下、リチウムイオン二次電池に用いられる正極活物質について説明する。 (1-4) Positive Electrode Active Material The electrode mixture layer of the present invention is preferably used mainly for non-aqueous electrolyte secondary batteries, particularly lithium ion secondary batteries. Hereinafter, the positive electrode active material used for the lithium ion secondary battery will be described.

本発明の正極合剤層に含まれる正極活物質としては、非水電解質二次電池において、正極活物質として知られている従来公知の材料の中から、任意のものを１種又は２種以上適宜選択して用いることができる。例えば、リチウムイオン二次電池であれば、リチウムイオンを吸蔵・放出可能なリチウム含有金属酸化物が好適である。このリチウム含有金属酸化物としては、リチウムと、Ｃｏ、Ｍｇ、Ｍｎ、Ｎｉ、Ｆｅ、Ａｌ、Ｍｏ、Ｖ、Ｗ及びＴｉなどからなる群より選ばれる少なくとも１種の元素と、を含む複合酸化物を挙げることができる。   As a positive electrode active material contained in the positive electrode mixture layer of the present invention, any one or more kinds of conventionally known materials known as positive electrode active materials in nonaqueous electrolyte secondary batteries are used. It can be appropriately selected and used. For example, in the case of a lithium ion secondary battery, a lithium-containing metal oxide capable of inserting and extracting lithium ions is suitable. The lithium-containing metal oxide includes a composite oxide containing lithium and at least one element selected from the group consisting of Co, Mg, Mn, Ni, Fe, Al, Mo, V, W, Ti, and the like. Can be mentioned.

具体的には、ＬｉｘＣｏＯ２、ＬｉｘＮｉＯ２、ＬｉｘＭｎＯ２、ＬｉｘＣｏａＮｉ１−ａＯ２、ＬｉｘＣｏｂＶ１−ｂＯｚ、ＬｉｘＣｏｂＦｅ１−ｂＯ２、ＬｉｘＭｎ２Ｏ４、ＬｉｘＭｎｃＣｏ２−ｃＯ４、ＬｉｘＭｎｃＮｉ２−ｃＯ４、ＬｉｘＭｎｃＶ２−ｃＯ４、ＬｉｘＭｎｃＦｅ２−ｃＯ４、（ここで、ｘ＝０．０２〜１．２、ａ＝０．１〜０．９、ｂ＝０．８〜０．９８、ｃ＝１．２〜１．９６、ｚ＝２．０１〜２．３である。）などからなる群より選ばれる少なくとも１種が挙げられる。好ましいリチウム含有金属酸化物としては、ＬｉｘＣｏＯ２、ＬｉｘＮｉＯ２、ＬｉｘＭｎＯ２、ＬｉｘＣｏａＮｉ１−ａＯ２、ＬｉｘＭｎ２Ｏ４、ＬｉｘＣｏｂＶ１−ｂＯｚ（ここで、ｘ、ａ、ｂ及びｚは上記と同じである。）からなる群より選ばれる少なくとも１種を挙げることができる。なお、ｘの値は充放電開始前の値であり、充放電により増減する。 Specifically, Li x CoO 2, Li x NiO 2, Li x MnO 2, Li x Co a Ni 1-a O 2, Li x Co b V 1-b O z, Li x Co b Fe 1-b O 2, Li x Mn 2 O 4, Li x Mn c Co 2-c O 4, Li x Mn c Ni 2-c O 4, Li x Mn c V 2-c O 4, Li x Mn c Fe 2- c O 4, (where, x = 0.02~1.2, a = 0.1~0.9 , b = 0.8~0.98, c = 1.2~1.96, z = At least one selected from the group consisting of 2.01 to 2.3. Preferred lithium-containing metal oxides, Li x CoO 2, Li x NiO 2, Li x MnO 2, Li x Co a Ni 1-a O 2, Li x Mn 2 O 4, Li x Co b V 1-b Mention may be made of at least one selected from the group consisting of O z (where x, a, b and z are the same as above). In addition, the value of x is a value before the start of charging / discharging, and increases / decreases by charging / discharging.

上記正極活物質は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。また、当該正極活物質の平均粒子径は、１０μｍ以下であることが好ましく、０．０５〜７μｍであることがより好ましく、１〜７μｍであることがさらに好ましい。平均粒子径が１０μｍを超えると、大電流下での充放電反応の効率が低下してしまう場合がある。   The said positive electrode active material may be used individually by 1 type, and may be used in combination of 2 or more type. The average particle diameter of the positive electrode active material is preferably 10 μm or less, more preferably 0.05 to 7 μm, and further preferably 1 to 7 μm. If the average particle size exceeds 10 μm, the efficiency of the charge / discharge reaction under a large current may be reduced.

（１−５） 負極活物質
次に本発明の負極合剤層に用いられる負極活物質について説明する。
本発明の負極合剤層において用いる負極活物質としては、非水電解質二次電池において、負極活物質として知られている従来公知の材料の中から、任意のものを１種又は２種以上適宜選択して用いることができる。リチウムイオン二次電池の場合、リチウムイオンを吸蔵・放出可能な材料として、例えば、炭素材料や、Ｓｉ及び／又はＳｎを含む合金や酸化物などを用いることができる。これらの中でもコストなどの観点からは炭素材料が好ましい。上記炭素材料としては、天然黒鉛、石油系又は石炭系コークスを熱処理することで製造される人造黒鉛、樹脂を炭素化したハードカーボン、メソフェーズピッチ系炭素材料などが挙げられる。 (1-5) Negative electrode active material Next, the negative electrode active material used for the negative electrode mixture layer of the present invention will be described.
As the negative electrode active material used in the negative electrode mixture layer of the present invention, any one or two or more kinds of conventionally known materials known as negative electrode active materials in nonaqueous electrolyte secondary batteries are appropriately used. It can be selected and used. In the case of a lithium ion secondary battery, as a material capable of inserting and extracting lithium ions, for example, a carbon material, an alloy or oxide containing Si and / or Sn, and the like can be used. Among these, a carbon material is preferable from the viewpoint of cost and the like. Examples of the carbon material include artificial graphite produced by heat-treating natural graphite, petroleum-based or coal-based coke, hard carbon obtained by carbonizing a resin, mesophase pitch-based carbon material, and the like.

天然黒鉛や人造黒鉛を用いる場合、電池容量の増大の観点から、粉末Ｘ線回折による黒鉛構造の（００２）面の面間隔ｄ（００２）が０．３３５〜０．３３７ｎｍの範囲にあるものが好ましい。天然黒鉛とは、鉱石として天然に産出する黒鉛質材料のことをいう。天然黒鉛は、その外観と性状によって、結晶化度の高い鱗状黒鉛と結晶化度が低い土状黒鉛の２種類に分けられる。鱗状黒鉛はさらに外観が葉状の鱗片状黒鉛と、塊状である鱗状黒鉛とに分けられる。黒鉛質材料となる天然黒鉛は、産地や性状、種類は特に制限されない。また、天然黒鉛又は天然黒鉛を原料として製造した粒子に熱処理を施して用いてもよい。   When natural graphite or artificial graphite is used, one having a (002) plane spacing d (002) of the graphite structure by powder X-ray diffraction in the range of 0.335 to 0.337 nm from the viewpoint of increasing battery capacity. preferable. Natural graphite refers to a graphite material that is naturally produced as ore. Natural graphite is classified into two types according to its appearance and properties: scaly graphite with high crystallinity and earthy graphite with low crystallinity. The scaly graphite is further divided into scaly graphite having a leaf-like appearance and scaly graphite having a lump shape. There are no particular restrictions on the origin, properties, and types of natural graphite used as the graphite material. Further, natural graphite or particles produced using natural graphite as a raw material may be subjected to a heat treatment.

人造黒鉛とは、広く人工的な手法で作られた黒鉛及び黒鉛の完全結晶に近い黒鉛質材料をいう。代表的な例としては、石炭の乾留、原油の蒸留による残渣などから得られるタールやコークスを原料にして、５００〜１０００℃程度の焼成工程、２０００℃以上の黒鉛化工程を経て得たものが挙げられる。また、溶解鉄から炭素を再析出させることで得られるキッシュグラファイトも人造黒鉛の一種である。   Artificial graphite refers to graphite made by a wide variety of artificial techniques and graphite materials that are close to perfect crystals of graphite. As a typical example, a material obtained from a tar and coke obtained from dry distillation of coal, a residue obtained by distillation of crude oil, and the like, through a firing process of about 500 to 1000 ° C. and a graphitization process of 2000 ° C. or more is used. Can be mentioned. Kish graphite obtained by reprecipitation of carbon from dissolved iron is also a kind of artificial graphite.

負極活物質として炭素材料の他に、Ｓｉ及び／又はＳｎを含む合金を使用すると、Ｓｉ及び／又はＳｎを単体で用いる場合やそれぞれの酸化物を用いる場合に比べ、充放電時の電極の膨張率が小さくなり、サイクル特性が良好になる。これらの中でも、Ｓｉ系合金が好ましい。Ｓｉ系合金としては、Ｂ、Ｍｇ、Ｃａ、Ｔｉ、Ｆｅ、Ｃｏ、Ｍｏ、Ｃｒ、Ｖ、Ｗ、Ｎｉ、Ｍｎ、Ｚｎ及びＣｕなどからなる群より選ばれる少なくとも１種の元素と、Ｓｉと、の合金などが挙げられる。具体的には、ＳｉＢ４、ＳｉＢ６、Ｍｇ２Ｓｉ、Ｎｉ２Ｓｉ、ＴｉＳｉ２、ＭｏＳｉ２、ＣｏＳｉ２、ＮｉＳｉ２、ＣａＳｉ２、ＣｒＳｉ２、Ｃｕ５Ｓｉ、ＦｅＳｉ２、ＭｎＳｉ２、ＶＳｉ２、ＷＳｉ２、ＺｎＳｉ２などからなる群より選ばれる少なくとも１種が挙げられる。
負極を構成する電極合剤層においては、負極活物質として、既述の材料を１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。 When an alloy containing Si and / or Sn in addition to the carbon material is used as the negative electrode active material, the expansion of the electrode during charge / discharge is greater than when using Si and / or Sn alone or using each oxide. The rate is reduced and the cycle characteristics are improved. Among these, Si-based alloys are preferable. As the Si-based alloy, at least one element selected from the group consisting of B, Mg, Ca, Ti, Fe, Co, Mo, Cr, V, W, Ni, Mn, Zn and Cu, Si, And alloys thereof. Specifically, SiB 4 , SiB 6 , Mg 2 Si, Ni 2 Si, TiSi 2 , MoSi 2 , CoSi 2 , NiSi 2 , CaSi 2 , CrSi 2 , Cu 5 Si, FeSi 2 , MnSi 2 , VSi 2 , There may be mentioned at least one selected from the group consisting of WSi 2 , ZnSi 2 and the like.
In the electrode mixture layer constituting the negative electrode, the above-described materials may be used alone or in combination of two or more as the negative electrode active material.

また、当該負極活物質の平均粒子径は１０μｍ以下とする。平均粒子径が１０μｍを超えると、大電流下での充放電反応の効率が低下してしまう。平均粒子径は０．１〜１０μｍとすることが好ましく、１〜７μｍとすることがより好ましい。   The average particle diameter of the negative electrode active material is 10 μm or less. When the average particle diameter exceeds 10 μm, the efficiency of the charge / discharge reaction under a large current is reduced. The average particle diameter is preferably 0.1 to 10 μm, and more preferably 1 to 7 μm.

２． 非水電解質二次電池用電極
第２の本発明は、上記電極合剤層が形成された非水電解質二次電池用電極（以下、単に「電極」ともいう）である。この電極は、集電体の表面に本発明の電極合剤層が形成されて成る。 2. Nonaqueous Electrolyte Secondary Battery Electrode The second aspect of the present invention is an electrode for a nonaqueous electrolyte secondary battery (hereinafter, also simply referred to as “electrode”) in which the electrode mixture layer is formed. This electrode is formed by forming the electrode mixture layer of the present invention on the surface of a current collector.

本発明の電極合剤層を備える電極の作製方法としては、以下の二つの方法が一般的である。一つの方法は、上記電極活物質、上記炭素系導電助剤、好ましくはバインダー、及び必要に応じて他の成分を混合・混練し、押し出し成形によりフィルム化して、これを圧延、延伸した後、集電体と貼り合わせる方法である。
もう一つの方法は、上記電極活物質、上記炭素系導電助剤、好ましくはバインダー、バインダーを溶解する溶媒、及び必要に応じて他の成分を混合してスラリーを調製し、このスラリーを集電体表面に塗布して溶媒を除去した後、プレスを行う方法である。
本発明の場合、どちらの方法も採用できるが、後者の方法が好適であるので、以下後者の方法について詳述する。 The following two methods are common as a method for producing an electrode including the electrode mixture layer of the present invention. One method is to mix and knead the electrode active material, the carbon-based conductive aid, preferably a binder, and other components as necessary, to form a film by extrusion, after rolling and stretching, This is a method of pasting together with a current collector.
Another method is to prepare a slurry by mixing the electrode active material, the carbon-based conductive additive, preferably a binder, a solvent for dissolving the binder, and other components as necessary, and collect the slurry. In this method, the solvent is removed after coating on the body surface and then pressing.
In the present invention, either method can be adopted, but the latter method is preferable, and the latter method will be described in detail below.

上記スラリーにおける固形分濃度（上記スラリーの溶媒以外の成分の合計質量がスラリーの全質量に占める割合をいう。）は、１０〜３０質量％であることが好ましく、１５〜２５質量％であることがより好ましい。固形分濃度が３０質量％を超えると、均一なスラリー作製が困難である場合がある。また、固形分濃度が１０質量％未満であると、スラリーの粘度が不十分であり、集電体に積層される電極合剤層の厚みが不均一になってしまう場合がある。   The solid content concentration in the slurry (referring to the ratio of the total mass of components other than the solvent in the slurry to the total mass of the slurry) is preferably 10 to 30% by mass, and preferably 15 to 25% by mass. Is more preferable. When solid content concentration exceeds 30 mass%, uniform slurry preparation may be difficult. Moreover, when the solid content concentration is less than 10% by mass, the viscosity of the slurry is insufficient, and the thickness of the electrode mixture layer laminated on the current collector may become uneven.

スラリーに用いる溶媒としては、バインダーを溶解する溶媒である限り特に制限されない。具体的には、Ｎ−メチルピロリドン（ＮＭＰ）、ジメチルアセトアミド（ＤＭＡｃ）、ジメチルホルムアミド（ＤＭＦ）、ジメチルスルホオキシド（ＤＭＳＯ）、水等よりなる群から選ばれる１種類以上を挙げることができ、特にＮＭＰ、ＤＭＡｃ又は水が好ましい。   The solvent used in the slurry is not particularly limited as long as it is a solvent that dissolves the binder. Specific examples include one or more selected from the group consisting of N-methylpyrrolidone (NMP), dimethylacetamide (DMAc), dimethylformamide (DMF), dimethylsulfoxide (DMSO), water, and the like. NMP, DMAc or water is preferred.

電極を作製する際に、スラリー中のチクソ性が強過ぎると、塗布に適した流動性を確保することが困難となる場合がある。このような場合には、スラリー化助剤を使用してもよい。スラリー化助剤としては、ポリビニルピロリドン、カルボキシメチルセルロース、ポリビニルアセテート、ポリビニルアルコール等よりなる群から選ばれる１つ以上を挙げることができる。特に、ポリビニルピロリドンを使用することが好適である。上記のようなスラリー化助剤を添加することにより、少ない溶媒量であっても十分な流動性を確保することができ、炭素系導電助剤の分散性も格段に向上する。また、溶媒除去後のクラックの発生も抑制できる。スラリー化助剤の添加量としては、スラリー中の溶媒以外の成分の合計量に対して、１０質量％以下であることが好ましく、０．５〜１０質量％であることがより好ましく、０．５〜８質量％であることがさらに好ましい。スラリー化助剤の添加量が１０質量％を超えると、逆にスラリー粘度が急激に低下し、分散不良を生じて好適なスラリー作製が困難となる場合がある。スラリー化助剤の添加量が０．５質量％未満である場合、スラリー化助剤の効果が現れ難い。   When producing an electrode, if the thixotropy in the slurry is too strong, it may be difficult to ensure fluidity suitable for coating. In such a case, a slurrying aid may be used. Examples of the slurrying aid include one or more selected from the group consisting of polyvinylpyrrolidone, carboxymethylcellulose, polyvinyl acetate, polyvinyl alcohol and the like. In particular, it is preferable to use polyvinylpyrrolidone. By adding the above-mentioned slurrying aid, sufficient fluidity can be ensured even with a small amount of solvent, and the dispersibility of the carbon-based conductive aid can be remarkably improved. Moreover, generation | occurrence | production of the crack after solvent removal can also be suppressed. The addition amount of the slurrying aid is preferably 10% by mass or less, more preferably 0.5 to 10% by mass, based on the total amount of components other than the solvent in the slurry. More preferably, it is 5-8 mass%. If the addition amount of the slurrying aid exceeds 10% by mass, on the contrary, the slurry viscosity is drastically lowered, resulting in poor dispersion, and it may be difficult to prepare a suitable slurry. When the addition amount of the slurrying aid is less than 0.5% by mass, the effect of the slurrying aid is difficult to appear.

上記スラリーは、後述する集電体の表面に塗布する。塗布方法としては、ドクターブレード等の適宜の塗布方法を採用することができる。塗布後、例えば、６０〜１００℃、好ましくは７５〜８５℃において、好ましくは６０〜１８０分間加熱処理することにより溶媒を除去する。その後、溶媒除去後の塗布物をプレスしても良い。本発明において好ましいプレス条件は、１０〜３０Ｐａの圧力下、１〜５分間である。   The slurry is applied to the surface of a current collector described later. As a coating method, an appropriate coating method such as a doctor blade can be employed. After the application, for example, the solvent is removed by heat treatment at 60 to 100 ° C., preferably 75 to 85 ° C., preferably for 60 to 180 minutes. Then, you may press the coating material after solvent removal. In the present invention, preferable pressing conditions are 1 to 5 minutes under a pressure of 10 to 30 Pa.

電極を構成する集電体としては、任意の導電性材料を用いることができる。例えば、アルミニウム、ニッケル、鉄、ステンレス鋼、チタン又は銅の金属材料を用いることができる。特に、アルミニウム、ステンレス鋼又は銅が好ましく、アルミニウム又はカーボンコートを施したアルミニウムを用いることがより好ましい。
集電体の厚みとしては、１０〜５０μｍが好ましい。 As the current collector constituting the electrode, any conductive material can be used. For example, a metal material such as aluminum, nickel, iron, stainless steel, titanium, or copper can be used. In particular, aluminum, stainless steel or copper is preferable, and aluminum or aluminum coated with carbon is more preferably used.
The thickness of the current collector is preferably 10 to 50 μm.

３． 非水電解質二次電池
第３の本発明は、本発明の電極（正極又は負極の何れか若しくはその両方）を含んで構成される非水電解質二次電池である。
本発明の非水電解質二次電池は、本発明の電極を用いるとともに、セパレータ及び電解液等を用いて構成される。非水電解質二次電池としては、リチウムイオン二次電池が例示される。以下、主として本発明の非水電解質二次電池がリチウムイオン二次電池である場合について説明する。 3. Non-aqueous electrolyte secondary battery The third aspect of the present invention is a non-aqueous electrolyte secondary battery including the electrode of the present invention (either the positive electrode or the negative electrode or both).
The non-aqueous electrolyte secondary battery of the present invention uses the electrode of the present invention and is configured using a separator, an electrolytic solution, and the like. As the nonaqueous electrolyte secondary battery, a lithium ion secondary battery is exemplified. Hereinafter, the case where the nonaqueous electrolyte secondary battery of the present invention is a lithium ion secondary battery will be mainly described.

本発明の非水電解質二次電池は、本発明の電極と、電解質を含む電解質層と、から構成され、正極の正極材料層と負極の負極材料層とが向き合い、かつ、正極材料層と負極材料層との間に電解質層が挿入されるようにして積層される。   The nonaqueous electrolyte secondary battery of the present invention is composed of the electrode of the present invention and an electrolyte layer containing an electrolyte, the positive electrode material layer of the positive electrode and the negative electrode material layer of the negative electrode face each other, and the positive electrode material layer and the negative electrode Lamination is performed such that an electrolyte layer is inserted between the material layers.

本発明の非水電解質二次電池のセル形状は、特に限定されず、いかなる形状においても実施することができる。具体的には、例えばボタン型、円筒型、角型等のセル形状を挙げることができる。また、複数対の正負電極とセパレータが積層された内部構成とすることも好ましく、この場合、公知のスタック積層型、捲回型、折り返し積層型等の方式を採用することが可能である。本発明の非水電解質二次電池の外装材としては、例えば金属缶、アルミラミネート樹脂フィルム等を挙げることができる。本発明の非水電解質二次電池は、電極合剤層に添加されている所定の炭素繊維が直線構造を有しており、かつ高い導電性を有しているため、導電パスを形成しやすく、優れた充放電特性を得ることができる。さらに、電極強度も向上する。   The cell shape of the nonaqueous electrolyte secondary battery of the present invention is not particularly limited, and can be implemented in any shape. Specifically, for example, cell shapes such as a button shape, a cylindrical shape, and a square shape can be given. Further, it is also preferable to have an internal configuration in which a plurality of pairs of positive and negative electrodes and separators are laminated. In this case, a known stack lamination type, wound type, folded lamination type, or the like can be adopted. Examples of the exterior material of the nonaqueous electrolyte secondary battery of the present invention include a metal can, an aluminum laminated resin film, and the like. In the non-aqueous electrolyte secondary battery of the present invention, the predetermined carbon fiber added to the electrode mixture layer has a linear structure and has high conductivity, so that it is easy to form a conductive path. Excellent charge / discharge characteristics can be obtained. Furthermore, the electrode strength is also improved.

（３−１） 電解質層
非水電解質二次電池を構成する電解質層としては、公知の物を用いることができる。本発明の非水電解質二次電池に用いられる電解液の２５℃における電気伝導度は、１×１０−２Ｓ／ｃｍ以上であることが好ましい。非水電解質二次電池がリチウムイオン二次電池である場合、電解質層としては、非水溶媒にリチウム塩等の電解質が溶解した非水電解液が用いられる。 (3-1) Electrolyte layer A well-known thing can be used as an electrolyte layer which comprises a nonaqueous electrolyte secondary battery. The electric conductivity at 25 ° C. of the electrolytic solution used in the nonaqueous electrolyte secondary battery of the present invention is preferably 1 × 10 −2 S / cm or more. When the nonaqueous electrolyte secondary battery is a lithium ion secondary battery, a nonaqueous electrolyte solution in which an electrolyte such as a lithium salt is dissolved in a nonaqueous solvent is used as the electrolyte layer.

一般に非水電解液は、水系の電解液に比べ耐電圧が高く、高いエネルギー密度が得られるという特徴がある。非水溶媒としては、公知のものを制限なく用いることが可能であるが、プロピレンカーボネート、エチレンカーボネート、ジエチルカーボネート、ジメチルカーボネート、メチルエチルカーボネート、ジメトキシエタン、γ−ブチロラクトン、γ−バレロラクトン、アセトニトリル、ニトロメタン、メトキシアセトニトリル、ニトロエタン、Ｎ，Ｎ−ジメチルホルムアミド、３−メトキシプロピオニトリル、Ｎ−メチルピロリドン、Ｎ，Ｎ’−ジメチルイミダゾリジノン、ジメチルスルホキシド、スルホラン、３−メチルスルホラン、エチルメチルカーボネート等が挙げられる。これらの非水溶媒は、１種を単独で用いてもよいし、２種以上を混合して用いてもよい。電解液に用いる溶媒は、適当な沸点、融点、粘性及び比誘電率を有することが重要であり、上記の中でも特にプロピレンカーボネート又はγ−ブチロラクトンを主体とするものが好適に用いられる。   In general, non-aqueous electrolytes are characterized by a higher withstand voltage and higher energy density than aqueous electrolytes. As the non-aqueous solvent, known ones can be used without limitation, but propylene carbonate, ethylene carbonate, diethyl carbonate, dimethyl carbonate, methyl ethyl carbonate, dimethoxyethane, γ-butyrolactone, γ-valerolactone, acetonitrile, Nitromethane, methoxyacetonitrile, nitroethane, N, N-dimethylformamide, 3-methoxypropionitrile, N-methylpyrrolidone, N, N'-dimethylimidazolidinone, dimethyl sulfoxide, sulfolane, 3-methylsulfolane, ethyl methyl carbonate, etc. Is mentioned. These nonaqueous solvents may be used alone or in combination of two or more. It is important that the solvent used in the electrolytic solution has an appropriate boiling point, melting point, viscosity, and relative dielectric constant, and among these, those mainly composed of propylene carbonate or γ-butyrolactone are preferably used.

本発明のリチウムイオン二次電池に用いる電解質としては、例えば、ＬｉＣｌＯ４、ＬｉＢＦ４、ＬｉＰＦ６、ＬｉＡｌＣｌ４、ＬｉＳｂＦ６、ＬｉＳＣＮ、ＬｉＣＦ３ＳＯ３、ＬｉＣＦ３ＣＯ２、ＬｉＡｓＦ６、低級脂肪族カルボン酸リチウム、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、クロロボランリチウム、ホウ酸塩類、イミド塩類が挙げられる。ホウ酸塩類としては、ビス（１，２−ベンゼンジオレート（２−）−Ｏ，Ｏ’）ホウ酸リチウム、ビス（２，３−ナフタレンジオレート（２−）−Ｏ，Ｏ’）ホウ酸リチウム、ビス（２，２’−ビフェニルジオレート（２−）−Ｏ，Ｏ’）ホウ酸リチウム、ビス（５−フルオロ−２−オレート−１−ベンゼンスルホン酸−Ｏ，Ｏ’）ホウ酸リチウムなどが挙げられる。イミド塩類としては、ビストリフルオロメタンスルホン酸イミドリチウム（（ＣＦ３ＳＯ２）２ＮＬｉ）、トリフルオロメタンスルホン酸ノナフルオロブタンスルホン酸イミドリチウム（ＬｉＮ（ＣＦ３ＳＯ２）（Ｃ４Ｆ９ＳＯ２））、ビスペンタフルオロエタンスルホン酸イミドリチウム（（Ｃ２Ｆ５ＳＯ２）２ＮＬｉ）などが挙げられる。電解質の濃度としては、０．５〜２ｍｏｌ／Ｌが好ましい。電解質は、上記のうち１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。サイクル安定性、充放電効率の向上等を目的として、電解質に公知の添加剤を添加してもよい。
本発明のリチウムイオン二次電池に用いる電解液として、エチルメチルイミダゾリウム塩に代表されるイオン性液体も好適に用いることが可能であり、この場合は必ずしも前述の非水溶媒に溶解したうえで用いる必要はない。 Examples of the electrolyte used in the lithium ion secondary battery of the present invention include LiClO 4 , LiBF 4 , LiPF 6 , LiAlCl 4 , LiSbF 6 , LiSCN, LiCF 3 SO 3 , LiCF 3 CO 2 , LiAsF 6 , and lower aliphatic carboxyl. Examples thereof include lithium acid, LiCl, LiBr, LiI, chloroborane lithium, borates, and imide salts. Examples of borates include lithium bis (1,2-benzenediolate (2-)-O, O ') and bis (2,3-naphthalenedioleate (2-)-O, O') boric acid. Lithium, bis (2,2′-biphenyldiolate (2-)-O, O ′) lithium borate, bis (5-fluoro-2-olate-1-benzenesulfonic acid-O, O ′) lithium borate Etc. Examples of imide salts include lithium bistrifluoromethanesulfonate imide ((CF 3 SO 2 ) 2 NLi), lithium trifluoromethanesulfonate nonafluorobutanesulfonate (LiN (CF 3 SO 2 ) (C 4 F 9 SO 2 ) ), Lithium bispentafluoroethanesulfonate imide ((C 2 F 5 SO 2 ) 2 NLi), and the like. The concentration of the electrolyte is preferably 0.5 to 2 mol / L. One of the above electrolytes may be used alone, or two or more electrolytes may be used in combination. For the purpose of improving cycle stability and charge / discharge efficiency, a known additive may be added to the electrolyte.
As an electrolytic solution used in the lithium ion secondary battery of the present invention, an ionic liquid typified by ethylmethylimidazolium salt can also be suitably used. In this case, the electrolyte must be dissolved in the above nonaqueous solvent. There is no need to use it.

（３−２） セパレータ
上記のような非水電解液を用いる場合、負極合剤層と正極合剤層とが直接接触することを防ぐために、セパレータを用いることが一般的である。セパレータの形状としては、紙状（フィルム状）、多孔膜状等の公知の形状を好適に採用することができる。セパレータの材質としては、例えば、セルロース、芳香族ポリアミド、脂肪族ポリイミド、ポリオレフィン、テフロン（登録商標）、ポリフェニレンスルファイド等からなる群より選ばれる１種類以上の材質を好適に用いることができる。これらの中でも、耐熱性と薄膜化の観点から、セルロース紙、芳香族ポリアミド又は脂肪族ポリイミド多孔膜が好ましい。セパレータの膜厚としては、短絡防止の観点から２０〜１００μｍ程度であることが好ましいが、本発明では従来のセパレータに比べて十分薄い５〜２０μｍ程度のセパレータの適用も可能である。薄いセパレータを用いた方がセパレータに由来する内部抵抗が低減されるため出力が向上し、セルのエネルギー密度も向上する。 (3-2) Separator When using the non-aqueous electrolyte as described above, a separator is generally used in order to prevent the negative electrode mixture layer and the positive electrode mixture layer from coming into direct contact. As the shape of the separator, a known shape such as a paper shape (film shape) or a porous film shape can be suitably employed. As the material of the separator, for example, one or more materials selected from the group consisting of cellulose, aromatic polyamide, aliphatic polyimide, polyolefin, Teflon (registered trademark), polyphenylene sulfide, and the like can be suitably used. Among these, cellulose paper, aromatic polyamide or aliphatic polyimide porous membrane is preferable from the viewpoint of heat resistance and thinning. The thickness of the separator is preferably about 20 to 100 μm from the viewpoint of preventing a short circuit, but in the present invention, a separator having a thickness of about 5 to 20 μm that is sufficiently thinner than a conventional separator can be applied. When the thin separator is used, the internal resistance derived from the separator is reduced, so that the output is improved and the energy density of the cell is also improved.

以下、実施例により本発明をさらに具体的に説明するが、本発明はこれにより何ら限定されない。実施例中の各種測定や分析は、それぞれ以下の方法に従って行った。   EXAMPLES Hereinafter, although an Example demonstrates this invention further more concretely, this invention is not limited at all by this. Various measurements and analyzes in the examples were performed according to the following methods.

（１）炭素繊維等の形状確認
卓上電子顕微鏡（日本電子株式会社製、型式ＮｅｏＳｃｏｐｅ ＪＣＭ−６０００）を用いて観察及び写真撮影を行った。炭素繊維等の平均繊維径は、得られた電子顕微鏡写真から無作為に３００箇所を選択して繊維径を測定し、それらすべての測定結果（ｎ＝３００）の平均値を平均繊維径とした。平均実効繊維長についても同様に算出した。 (1) Shape confirmation of carbon fiber, etc. Observation and photography were performed using a tabletop electron microscope (manufactured by JEOL Ltd., model NeoScope JCM-6000). The average fiber diameter of carbon fibers, etc. was measured by randomly selecting 300 locations from the obtained electron micrograph, and the average value of all the measurement results (n = 300) was taken as the average fiber diameter. . The average effective fiber length was similarly calculated.

（２）炭素繊維のＸ線回折測定
Ｘ線回折測定はリガク社製ＲＩＮＴ−２１００を用いてＪＩＳ Ｒ７６５１法に準拠し、格子面間隔（ｄ００２）、結晶子大きさ（Ｌｃ）（六角網面積層方向）及び（Ｌａ）（炭素六角網面方向）を測定した。 (2) X-ray diffraction measurement of carbon fiber X-ray diffraction measurement is based on JIS R7651 method using RINT-2100 manufactured by Rigaku Corporation, lattice spacing (d002), crystallite size (Lc) (hexagonal mesh area layer) Direction) and (La) (carbon hexagonal network surface direction).

（３）繊維状炭素の実効繊維長
繊維状炭素を含む電極を、走査型電子顕微鏡（株式会社日立製作所製ＴＭ−３０００）を用いて観察し、電極を構成する電極合剤層中において繊維状炭素が丸まっていないことを確認した。その後、電極中の電極合剤層を溶媒に溶解し、デジタルマイクロスコープ（株式会社キーエンス製ＶＨＸ−２００）を用いて観察及び写真撮影を行った。繊維状炭素の平均実効繊維長は、写真から無作為に２０箇所を選択して実効繊維長を測定し、それらのすべての測定結果（ｎ＝２０）の平均値を平均実効繊維長とした。 (3) Effective fiber length of fibrous carbon An electrode containing fibrous carbon is observed using a scanning electron microscope (TM-3000 manufactured by Hitachi, Ltd.), and is fibrous in an electrode mixture layer constituting the electrode. It was confirmed that the carbon was not curled. Thereafter, the electrode mixture layer in the electrode was dissolved in a solvent, and observation and photography were performed using a digital microscope (VHX-200 manufactured by Keyence Corporation). The average effective fiber length of the fibrous carbon was measured by selecting 20 locations at random from the photograph, and the average value of all the measurement results (n = 20) was defined as the average effective fiber length.

[製造例１] ＜メソフェーズピッチの製造＞
キノリン不溶分を除去した軟化点８０℃のコールタールピッチを、Ｎｉ−Ｍｏ系触媒存在下、圧力１３ＭＰａ、温度３４０℃で水添し、水素化コールタールピッチを得た。この水素化コールタールピッチを常圧下、４８０℃で熱処理した後、減圧して低沸点分を除き、メソフェーズピッチを得た。このメソフェーズピッチを、フィルターを用いて温度３４０℃でろ過を行い、ピッチ中の異物を取り除き、精製されたメソフェーズピッチを得た。 [Production Example 1] <Production of mesophase pitch>
A coal tar pitch having a softening point of 80 ° C. from which quinoline-insoluble components had been removed was hydrogenated at a pressure of 13 MPa and a temperature of 340 ° C. in the presence of a Ni—Mo catalyst to obtain a hydrogenated coal tar pitch. This hydrogenated coal tar pitch was heat-treated at 480 ° C. under normal pressure, and then reduced in pressure to remove low-boiling components to obtain mesophase pitch. The mesophase pitch was filtered using a filter at a temperature of 340 ° C. to remove foreign matters in the pitch, and a purified mesophase pitch was obtained.

［製造例２］ ＜カーボンナノファイバー（ＣＮＦ）の製造＞
熱可塑性樹脂として直鎖状低密度ポリエチレン（ＥＶＯＬＵＥ（登録商標）ＳＰ−１５１０、（株）プライムポリマ−製、ＭＦＲ＝１ｇ／１０ｍｉｎ）８４質量部及び熱可塑性炭素前駆体として製造例１で得られたメソフェーズピッチ（メソフェーズ率９０．９％、軟化点３０３．５℃）１６質量部を同方向二軸押出機（東芝機械（株）製「ＴＥＭ−２６ＳＳ」、バレル温度３００℃、窒素気流下）で溶融混練して樹脂組成物を調製した。この樹脂組成物をシリンダー式単孔紡糸機を用いて紡糸し、樹脂複合繊維（ピッチを島成分として含有する海島型複合繊維）を作製した。具体的には、この樹脂組成物を溶融紡糸機により、直径が０．２ｍｍ、導入角６０°の円形口金を用いて繊維径１００μｍの長繊維に成形した。口金温度は３４０℃、吐出量は３．８ｇ／口金／時間、せん断速度は１０００ｓ−１、吐出線速度と引取り速度との比率であるドラフト比は４であった。この条件での口金内部での伸長ひずみ速度は９８２ｓ−１であり、口金外部での変形領域は口金下１０ｍｍであり、伸長ひずみ速度は９ｓ−１であった。
次に、この樹脂複合繊維を熱風乾燥機により、酸素濃度を０．７％にした雰囲気中において３４０℃で３時間保持することにより、樹脂複合安定化繊維を得た。
次に、この樹脂複合安定化繊維を真空ガス置換炉中に入れ、窒素置換を行った後に１ｋＰａまで減圧した。減圧状態下で、５℃／分の昇温速度で５００℃まで昇温し、５００℃で１時間保持することにより、熱可塑性樹脂を除去して安定化繊維を得た。得られた安定化繊維をエタノール／イオン交換水混合溶媒（体積比１／１）中に加え、ミキサーで１０分間粉砕することにより、安定化繊維を分散させた。得られた分散液はろ過した。この安定化繊維を流量１Ｌ／ｍｉｎの窒素下で、室温から１０００℃まで５℃／ｍｉｎの条件で昇温し、１０００℃到達後３０分間保持することで炭化を行い、さらにアルゴンガス雰囲気下、室温から３時間で３０００℃まで昇温することでカーボンナノファイバーを作製した。得られたカーボンナノファイバーは乾式ジェットミルを用いて解砕処理を行った。 [Production Example 2] <Production of carbon nanofiber (CNF)>
It is obtained in Production Example 1 as a thermoplastic resin and linear low density polyethylene (EVOLUE (registered trademark) SP-1510, manufactured by Prime Polymer Co., Ltd., MFR = 1 g / 10 min) 84 parts by mass and a thermoplastic carbon precursor. 16 parts by mass of mesophase pitch (mesophase ratio 90.9%, softening point 303.5 ° C.) in the same direction twin screw extruder (“TEM-26SS” manufactured by Toshiba Machine Co., Ltd., barrel temperature 300 ° C., under nitrogen flow) And kneaded to prepare a resin composition. The resin composition was spun using a cylinder type single-hole spinning machine to produce a resin composite fiber (a sea-island composite fiber containing pitch as an island component). Specifically, this resin composition was formed into a long fiber having a fiber diameter of 100 μm by a melt spinning machine using a circular die having a diameter of 0.2 mm and an introduction angle of 60 °. The die temperature was 340 ° C., the discharge amount was 3.8 g / die / hour, the shear rate was 1000 s −1 , and the draft ratio, which is the ratio between the discharge linear velocity and the take-off velocity, was 4. Elongation strain rate in the die interior of this condition is 982s -1, deformation area in the mouth outside is die under 10 mm, elongation strain rate was 9s -1.
Next, this resin composite fiber was retained in an atmosphere with an oxygen concentration of 0.7% by a hot air dryer at 340 ° C. for 3 hours to obtain a resin composite stabilized fiber.
Next, this resin composite stabilized fiber was placed in a vacuum gas replacement furnace, and after nitrogen replacement, the pressure was reduced to 1 kPa. Under reduced pressure, the temperature was increased to 500 ° C. at a temperature increase rate of 5 ° C./min, and held at 500 ° C. for 1 hour to remove the thermoplastic resin and obtain stabilized fibers. The resulting stabilized fiber was added to an ethanol / ion exchange water mixed solvent (volume ratio 1/1) and pulverized with a mixer for 10 minutes to disperse the stabilized fiber. The resulting dispersion was filtered. The stabilized fiber was heated at room temperature to 1000 ° C. under nitrogen at a flow rate of 1 L / min under the condition of 5 ° C./min, carbonized by holding for 30 minutes after reaching 1000 ° C., and further in an argon gas atmosphere. Carbon nanofibers were produced by raising the temperature from room temperature to 3000 ° C. in 3 hours. The obtained carbon nanofibers were crushed using a dry jet mill.

得られたカーボンナノファイバーは、結晶子長さ（Ｌａ）が１１０．８ｎｍ、（ｄ００２）が０．３３７２ｎｍ、（Ｌｃ）が６２．３ｎｍ、平均繊維径が２５７ｎｍ、平均実効繊維長が１６．６μｍであった。   The obtained carbon nanofiber has a crystallite length (La) of 110.8 nm, (d002) of 0.3372 nm, (Lc) of 62.3 nm, an average fiber diameter of 257 nm, and an average effective fiber length of 16.6 μm. Met.

［実施例１］
炭素系導電助剤としてアセチレンブラック（ＡＢ）（電気化学工業株式会社製、デンカブラック、平均粒子径３５ｎｍ）を２質量部、正極活物質（ＬｉＦｅＰＯ４；宝泉株式会社製、ＳＬＦＰ−ＥＳ０１）を９１質量部、バインダーとしてポリフッ化ビニリデン（株式会社クレハ製、Ｗ＃７２００）を７質量部、溶媒としてＮ−メチルピロリドンを用いてスラリーを作製した。作製したスラリーを集電体（厚さ１５μｍのアルミニウム箔）に塗布し電極を作製した。電極を構成する電極合剤層中の炭素系導電助剤の体積含有率（２５℃）は１．５％、電極合剤層の密度（２５℃）は１．５５ｇ／ｃｍ３、平均実効繊維長は０．１μｍであった。 [Example 1]
2 parts by mass of acetylene black (AB) (manufactured by Denki Kagaku Kogyo Co., Ltd., Denka Black, average particle size 35 nm) as a carbon-based conductive additive, positive electrode active material (LiFePO 4 ; manufactured by Hosen Co., Ltd., SLFP-ES01) A slurry was prepared using 91 parts by mass, 7 parts by mass of polyvinylidene fluoride (manufactured by Kureha Co., Ltd., W # 7200) as a binder, and N-methylpyrrolidone as a solvent. The prepared slurry was applied to a current collector (15 μm thick aluminum foil) to prepare an electrode. The volume ratio (25 ° C.) of the carbon-based conductive additive in the electrode mixture layer constituting the electrode is 1.5%, the density (25 ° C.) of the electrode mixture layer is 1.55 g / cm 3 , and the average effective fiber The length was 0.1 μm.

さらに、上記電極を正極とし、ガラス繊維不織布セパレータを介して金属リチウムと対向させ、１ｍｏｌ／Ｌ濃度のＬｉＰＦ６を含むエチレンカーボネートとエチルメチルカーボネート混合溶液（３／７質量比、キシダ化学社製）からなる電解液を２０３２型コインセルに注入して、電池評価用のコインセルを作製して評価したところ、レート特性に優れており、リチウムイオン二次電池として有用であることがわかった。 Further, the above electrode is used as a positive electrode, and is opposed to metallic lithium through a glass fiber nonwoven fabric separator, and a mixed solution of ethylene carbonate and ethyl methyl carbonate containing LiPF 6 at a concentration of 1 mol / L (3/7 mass ratio, manufactured by Kishida Chemical Co., Ltd.) When the coin cell for battery evaluation was produced and evaluated by injecting the electrolyte solution made of 2032 into a coin cell, it was found that the battery was excellent in rate characteristics and useful as a lithium ion secondary battery.

［比較例１］
電極合剤層中の炭素系導電助剤の体積含有率を０．８％、電極合剤層の密度を１．５８ｇ／ｃｍ３としたこと以外は実施例１と同様に操作を行い、電極を作製した。 [Comparative Example 1]
The same operation as in Example 1 was performed except that the volume content of the carbon-based conductive additive in the electrode mixture layer was 0.8% and the density of the electrode mixture layer was 1.58 g / cm 3. Was made.

［実施例２］
炭素系導電助剤として気相成長炭素繊維（ＶＧＣＦ：Ｖａｐｏｒ Ｇｒｏｗｔｈ Ｃａｒｂｏｎ Ｆｉｂｅｒ、平均繊維径１５０ｎｍ）を使用し、電極合剤層中の導電助剤の体積含有率を１．５％、電極合剤層の密度を１．５９ｇ／ｃｍ３としたこと以外は実施例１と同様に操作を行い、電極を作製した。この時、電極を構成する電極合剤層中の炭素系導電助剤の平均実効繊維長は８．５μｍであった。 [Example 2]
Vapor growth carbon fiber (VGCF: Vapor Growth Carbon Fiber, average fiber diameter: 150 nm) is used as a carbon-based conductive additive, and the volume content of the conductive additive in the electrode mixture layer is 1.5%. An electrode was produced in the same manner as in Example 1 except that the density of the layer was 1.59 g / cm 3 . At this time, the average effective fiber length of the carbon-based conductive additive in the electrode mixture layer constituting the electrode was 8.5 μm.

［比較例２］
電極合剤層中の炭素系導電助剤の体積含有率を０．８％、電極合剤層の密度を１．５９ｇ／ｃｍ３としたこと以外は実施例２と同様に操作を行い、電極を作製した。 [Comparative Example 2]
The same operation as in Example 2 was performed except that the volume content of the carbon-based conductive additive in the electrode mixture layer was 0.8% and the density of the electrode mixture layer was 1.59 g / cm 3. Was made.

［実施例３］
炭素系導電助剤として製造例１に記載のカーボンナノファイバー（ＣＮＦ）を使用し、電極合剤層中の導電助剤の体積含有率を１．５％、電極合剤層の密度を１．４６ｇ／ｃｍ３としたこと以外は実施例１と同様に操作を行い、電極を作製した。 [Example 3]
The carbon nanofiber (CNF) described in Production Example 1 is used as the carbon-based conductive additive, the volume content of the conductive additive in the electrode mixture layer is 1.5%, and the density of the electrode mixture layer is 1. An electrode was produced in the same manner as in Example 1 except that the amount was 46 g / cm 3 .

［実施例４］
電極合剤層中の導電助剤の体積含有率を０．９％、電極合剤層の密度を１．３７ｇ／ｃｍ３としたこと以外は実施例３と同様に操作を行い、電極を作製した。 [Example 4]
An electrode was produced in the same manner as in Example 3 except that the volume ratio of the conductive additive in the electrode mixture layer was 0.9% and the density of the electrode mixture layer was 1.37 g / cm 3. did.

［実施例５］
電極合剤層中の導電助剤の体積含有率を２．１％、電極合剤層の密度を１．３１ｇ／ｃｍ３としたこと以外は実施例３と同様に操作を行い、電極を作製した。 [Example 5]
An electrode was produced in the same manner as in Example 3 except that the volume ratio of the conductive additive in the electrode mixture layer was 2.1% and the density of the electrode mixture layer was 1.31 g / cm 3. did.

［実施例６］
電極合剤層中の導電助剤の体積含有率を１．４％、電極合剤層の密度を２．０６ｇ／ｃｍ３としたこと以外は実施例３と同様に操作を行い、電極を作製した。 [Example 6]
An electrode was produced by performing the same operation as in Example 3 except that the volume ratio of the conductive additive in the electrode mixture layer was 1.4% and the density of the electrode mixture layer was 2.06 g / cm 3. did.

［実施例７］
電極合剤層中の導電助剤の体積含有率を３．２％、電極合剤層の密度を２．０３ｇ／ｃｍ３としたこと以外は実施例３と同様に操作を行い、電極を作製した。 [Example 7]
An electrode was produced in the same manner as in Example 3 except that the volume ratio of the conductive additive in the electrode mixture layer was 3.2% and the density of the electrode mixture layer was 2.03 g / cm 3. did.

［実施例８］
炭素系導電助剤として製造例１に記載のカーボンナノファイバー（ＣＮＦ）を粉砕（株式会社スギノマシン社製、スターバースト）し、平均実効繊維長５．５μｍの繊維状炭素（Ｓ−ＣＮＦ）とした。この繊維状炭素（Ｓ−ＣＮＦ）を用い、電極合剤層中の導電助剤の体積含有率を１．４％、電極合剤層の密度を１．５４ｇ／ｃｍ３としたこと以外は実施例１と同様に操作を行い、電極を作製した。 [Example 8]
Carbon nanofibers (CNF) described in Production Example 1 as a carbon-based conductive aid were pulverized (Starburst manufactured by Sugino Machine Co., Ltd.), and fibrous carbon (S-CNF) having an average effective fiber length of 5.5 μm was obtained. did. This fibrous carbon (S-CNF) was used except that the volume content of the conductive additive in the electrode mixture layer was 1.4% and the density of the electrode mixture layer was 1.54 g / cm 3. The same operation as in Example 1 was performed to produce an electrode.

＜電極の抵抗測定＞
ポテンショスタット／ガルバノスタット（北斗電工株式会社製ＨＡ−１５１）を用いて、実施例および比較例にて作製した電極の膜厚方向の電極抵抗を測定し、その抵抗値から算出される電極電導度を表１に示す。導電助剤の体積含有率と電極合剤層密度のどちらもが適正な範囲に入っている電極の電導度が良好であるのがわかる。 <Measurement of electrode resistance>
Using a potentiostat / galvanostat (HA-151 manufactured by Hokuto Denko Co., Ltd.), the electrode resistance in the film thickness direction of the electrodes prepared in Examples and Comparative Examples was measured, and the electrode conductivity calculated from the resistance value Is shown in Table 1. It can be seen that the conductivity of the electrode in which both the volume content of the conductive auxiliary agent and the electrode mixture layer density are in an appropriate range is good.

Figure 2017010935
Figure 2017010935

Claims (7)

電極活物質と、平均径が１０ｎｍ以上の炭素系導電助剤と、を少なくとも含む電極合剤層であって、前記炭素系導電助剤の体積含有率が０．９〜５．０（％）であり、かつ前記電極合剤層の密度が０．５０（ｇ／ｃｍ３）以上２．１０（ｇ／ｃｍ３）未満であることを特徴とする非水電解質二次電池用電極合剤層。 An electrode mixture layer containing at least an electrode active material and a carbon-based conductive aid having an average diameter of 10 nm or more, wherein the volume content of the carbon-based conductive aid is 0.9 to 5.0 (%) And the density of the electrode mixture layer is 0.50 (g / cm 3 ) or more and less than 2.10 (g / cm 3 ), the electrode mixture layer for a non-aqueous electrolyte secondary battery . 活性炭を含まない請求項１に記載の非水電解質二次電池用電極合剤層。   The electrode mixture layer for a non-aqueous electrolyte secondary battery according to claim 1, which does not contain activated carbon. 前記炭素系導電助剤が、平均実効繊維長が１０μｍ以上の繊維状炭素である請求項１又は２に記載の非水電解質二次電池用電極合剤層。   The electrode mixture layer for a non-aqueous electrolyte secondary battery according to claim 1, wherein the carbon-based conductive additive is fibrous carbon having an average effective fiber length of 10 μm or more. 前記繊維状炭素における、Ｘ線回折法で測定した結晶子長さ（Ｌａ）が、１１０〜５００ｎｍである請求項３に記載の非水電解質二次電池用電極合剤層。   The electrode mixture layer for a non-aqueous electrolyte secondary battery according to claim 3, wherein the fibrous carbon has a crystallite length (La) measured by an X-ray diffraction method of 110 to 500 nm. 厚みが５０〜１０００μｍである請求項１乃至４の何れか１項に記載の非水電解質二次電池用電極合剤層。   The electrode mixture layer for a nonaqueous electrolyte secondary battery according to any one of claims 1 to 4, having a thickness of 50 to 1000 µm. 集電体と、
前記集電体に積層された請求項１乃至５の何れか１項に記載の非水電解質二次電池用電極合剤層と、
から成る非水電解質二次電池用電極。 A current collector,
The electrode mixture layer for a nonaqueous electrolyte secondary battery according to any one of claims 1 to 5, laminated on the current collector,
An electrode for a nonaqueous electrolyte secondary battery. 請求項６に記載の非水電解質二次電池用電極を有する非水電解質二次電池。   The nonaqueous electrolyte secondary battery which has an electrode for nonaqueous electrolyte secondary batteries of Claim 6.
JP2016119930A 2015-06-18 2016-06-16 Positive electrode mixture layer for non-aqueous electrolyte secondary battery, positive electrode for non-aqueous electrolyte secondary battery containing the same, and non-aqueous electrolyte secondary battery Active JP7240801B2 (en)