JP2016151081A - Carbon fiber sheet and carbon fiber reinforced resin compact using the same - Google Patents
Carbon fiber sheet and carbon fiber reinforced resin compact using the same Download PDFInfo
- Publication number
- JP2016151081A JP2016151081A JP2015030971A JP2015030971A JP2016151081A JP 2016151081 A JP2016151081 A JP 2016151081A JP 2015030971 A JP2015030971 A JP 2015030971A JP 2015030971 A JP2015030971 A JP 2015030971A JP 2016151081 A JP2016151081 A JP 2016151081A
- Authority
- JP
- Japan
- Prior art keywords
- carbon fiber
- fiber sheet
- sheet
- carbon
- reinforced resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、炭素繊維シート及びこれを用いた炭素繊維強化樹脂成形体に関する。さらに詳しくは、短繊維からなる炭素繊維シート及びこれを用いた炭素繊維強化樹脂成形体に関する。 The present invention relates to a carbon fiber sheet and a carbon fiber reinforced resin molded article using the same. More specifically, the present invention relates to a carbon fiber sheet made of short fibers and a carbon fiber reinforced resin molded body using the same.
炭素繊維とマトリックス樹脂からなる炭素繊維強化プラスチック(CFRP)は、軽量で比強度、比弾性率が高く、力学的特性に優れ、耐候性、耐薬品性も高いことから、航空機、自動車、タンク、コンクリート補強材、スポーツ用途等様々な用途に使用され、あるいは適用することが検討されている。CFRPの製造の際には炭素繊維シートの切断などにより端材が発生し、有効活用が問題となる。また、CFRP成形体を処分する際も炭素繊維の有効活用(リサイクル)が問題となる。 Carbon fiber reinforced plastic (CFRP) made of carbon fiber and matrix resin is lightweight, has high specific strength, high specific modulus, excellent mechanical properties, weather resistance, and chemical resistance. It is considered to be used or applied to various applications such as concrete reinforcement and sports applications. In the production of CFRP, scraps are generated by cutting the carbon fiber sheet, and effective utilization becomes a problem. In addition, effective disposal (recycling) of carbon fibers becomes a problem when disposing of CFRP compacts.
廃CFRPから炭素繊維を取り出す方法として、常圧溶解法が提案されている(特許文献1)。これは加圧せずに樹脂を溶かす方法であり、高品質なリサイクル炭素繊維を得ることができる。しかし、溶解処理後の炭素繊維は綿状に絡まり合った状態であり、そのままではCFRPに再生することは難しい。リサイクル炭素繊維をCFRPに再生する方法として、特許文献2〜4には炭素繊維に他の合成繊維を加えて乾式法(カード)で開繊することが提案されている。湿式法については非特許文献1〜2の報告例がある。非特許文献3にもリサイクル炭素繊維をCFRPに成形することが報告されている。 As a method for extracting carbon fiber from waste CFRP, a normal pressure melting method has been proposed (Patent Document 1). This is a method of dissolving a resin without applying pressure, and a high-quality recycled carbon fiber can be obtained. However, the carbon fiber after the dissolution treatment is in a state of being entangled in a cotton shape, and it is difficult to regenerate the CFRP as it is. As a method for regenerating recycled carbon fibers into CFRP, Patent Documents 2 to 4 propose that other synthetic fibers are added to carbon fibers and opened by a dry method (card). There are reported examples of Non-Patent Documents 1 and 2 for the wet method. Non-Patent Document 3 also reports that recycled carbon fiber is molded into CFRP.
しかし、従来の技術は炭素繊維以外の合成繊維や他の添加物等の第三成分が入ったり、短繊維からなる炭素繊維の開繊性及び配向性に問題があり、CFRPに成形すると、高強度が発現しないという問題があった。
本発明は、前記従来の問題を解決するため、短繊維からなる炭素繊維群の開繊性及び配向性を改善し、高強度のCFRPが成形できる炭素繊維シート及びこれを用いた炭素繊維強化樹脂成形体を提供する。
However, the conventional technology contains a third component such as synthetic fibers other than carbon fibers and other additives, or there is a problem in the opening and orientation of carbon fibers made of short fibers. There was a problem that strength did not develop.
In order to solve the above-mentioned conventional problems, the present invention improves the openability and orientation of a group of carbon fibers composed of short fibers and can form a high-strength CFRP and a carbon fiber reinforced resin using the same A molded body is provided.
本発明の炭素シートは、短繊維シートで構成される炭素繊維単独系からなる炭素繊維シートであって、前記炭素繊維シートはカード機の開繊装置上に開繊されて巻き付いたものを剥がして形成され、かつ実質的に同一方向に配向されており、単位面積当たりの質量が5g/m2以上であることを特徴とする。 The carbon sheet of the present invention is a carbon fiber sheet composed of a single carbon fiber system composed of short fiber sheets, and the carbon fiber sheet is peeled off after being opened and wound on the opening device of the card machine. It is formed and oriented in substantially the same direction, and has a mass per unit area of 5 g / m 2 or more.
本発明の炭素繊維強化樹脂成形体は、炭素繊維シートとマトリックス樹脂を含む炭素繊維強化樹脂成形体であって、前記炭素繊維シートはカード機の開繊装置上に開繊されて巻き付いたものを剥がして形成され、かつ実質的に同一方向に配向されており、単位面積当たりの質量が5g/m2以上であることを特徴とする。 The carbon fiber reinforced resin molded body of the present invention is a carbon fiber reinforced resin molded body including a carbon fiber sheet and a matrix resin, the carbon fiber sheet being opened and wound on a card machine opening device. It is formed by peeling and is oriented in substantially the same direction, and has a mass per unit area of 5 g / m 2 or more.
本発明は、短繊維シートで構成される炭素繊維単独系からなる炭素繊維シートをカード機の開繊装置上に開繊されて巻き付いたものを剥がして形成され、かつ実質的に同一方向に炭素繊維が配向されており、単位面積当たりの質量が5g/m2以上であることにより、炭素繊維の開繊性及び配向性を改善でき、均一性が高く、高強度CFRPが成形できる炭素繊維シート及びこれを用いた炭素繊維強化樹脂成形体を提供できる。コスト的にも有利なCFRPが成形できる The present invention is formed by peeling a carbon fiber sheet made of a single carbon fiber system composed of short fiber sheets, which is opened and wound on a card machine opening device, and carbon in substantially the same direction. A carbon fiber sheet in which the fibers are oriented and the mass per unit area is 5 g / m 2 or more, so that the openability and orientation of the carbon fibers can be improved, the uniformity is high, and a high strength CFRP can be formed. And the carbon fiber reinforced resin molding using the same can be provided. CFRP advantageous in terms of cost can be molded
本発明の炭素繊維シートは、短繊維シートで構成される炭素繊維単独系からなる炭素繊維シートである。炭素繊維単独系とは、他の合成繊維、バインダー樹脂、油剤、滑剤などを含まないことを意味する。 これにより、CFRPとしたときに炭素繊維以外の合成繊維や他の添加物等の第三成分が入ることはなく、強度が高く、品質の高い成形体が得られる。 The carbon fiber sheet of the present invention is a carbon fiber sheet composed of a single carbon fiber system composed of short fiber sheets. A carbon fiber single system means that other synthetic fiber, binder resin, oil agent, lubricant, etc. are not included. Thereby, when it is set as CFRP, third components, such as synthetic fibers other than carbon fiber, and other additives, do not enter, and a molded article with high strength and high quality can be obtained.
本発明の炭素繊維シートは、カード機の開繊装置上に開繊されて巻き付いたものを剥がして形成される。開繊装置はシリンダー又はベルトコンベアが好ましい。シリンダー又はベルトコンベア上には多数の金属製針が備えられているが、炭素繊維はこの多数の金属製針の間に、開繊されかつ実質的に同一方向に配向されて巻き付いており、これを剥がすことにより短繊維シートとして取り扱うことができる。シリンダー又はベルトコンベア幅及び直径又は長さは様々なものを選択できるので、生産量に見合ったものを選択して使用する。 The carbon fiber sheet of the present invention is formed by peeling off the wound and wound material on the opening device of the card machine. The opening device is preferably a cylinder or a belt conveyor. Many metal needles are provided on the cylinder or belt conveyor, and the carbon fiber is wound between the metal needles so that the fibers are opened and oriented in substantially the same direction. Can be handled as a short fiber sheet. Various cylinder or belt conveyor widths and diameters or lengths can be selected, so select and use one that matches the production volume.
炭素繊維シートの単位面積当たりの質量は5g/m2以上であり、好ましくは5〜50g/m2であり、より好ましくは5〜25g/m2である。前記の範囲であれば、取扱い性も良く、CFRP成形に都合が良い。炭素繊維シートの質量が5g/m2未満では取扱い性が困難でCFRP成形に適用するのは困難となる。 Mass per unit area of the carbon fiber sheet is at 5 g / m 2 or more, preferably from 5 to 50 g / m 2, more preferably from 5 to 25 g / m 2. If it is the said range, it will be easy to handle and convenient for CFRP molding. If the mass of the carbon fiber sheet is less than 5 g / m 2 , the handleability is difficult and it is difficult to apply to CFRP molding.
炭素繊維シートを構成する炭素繊維は、50質量%以上が±10度以内の角度で配向されていることが好ましく、さらに好ましくは60質量%以上が±10度以内の角度で配向されており、より好ましくは70質量%以上が±10度以内の角度で配向されている。前記の範囲であれば、配向性が高く、強度が高く、品質の高い成形体が得られる。 The carbon fiber constituting the carbon fiber sheet is preferably oriented at an angle of ± 10 degrees or more, and more preferably 60 mass% or more is oriented at an angle of ± 10 degrees or more, More preferably, 70 mass% or more is oriented at an angle within ± 10 degrees. Within the above range, a molded article having high orientation, high strength and high quality can be obtained.
炭素繊維シートは、荷重500Paをかけたときの密度0.01〜0.15g/cm3であることが好ましく、さらに好ましい密度は0.02〜0.10g/cm3であり、より好ましくは0.03〜0.09g/cm3である。前記の範囲であれば、取扱い性も良く、CFRP成形に都合が良い。 The carbon fiber sheet preferably has a density of 0.01 to 0.15 g / cm 3 when a load of 500 Pa is applied, and a more preferable density is 0.02 to 0.10 g / cm 3 , more preferably 0. 0.03 to 0.09 g / cm 3 . If it is the said range, it will be easy to handle and convenient for CFRP molding.
炭素繊維の繊維長は任意とすることができるが、好ましくは30〜200mmであり、さらに好ましい繊維長は50〜100mmであり、より好ましくは50〜80mmである。前記の範囲であれば、取扱い性も良く、CFRP成形に都合が良い。 Although the fiber length of carbon fiber can be made arbitrary, Preferably it is 30-200 mm, The still more preferable fiber length is 50-100 mm, More preferably, it is 50-80 mm. If it is the said range, it will be easy to handle and convenient for CFRP molding.
炭素繊維は、資源の有効活用からリサイクルされた炭素繊維であるのが好ましいが、バージンの炭素繊維を切断したもの、CFRPの製造の際の炭素繊維シートの切断などにより端材として発生したものなど、どのようなものでも使用できる。炭素繊維の原料は、ポリアクリロニトリル(PAN)系、ピッチ系等どのようなものでもよい。また、本発明の炭素繊維シートと別の方法で作成された炭素繊維シート(例えば長繊維シート)とを積層して使用することもできる。 The carbon fibers are preferably recycled carbon fibers from the effective use of resources. However, those obtained by cutting virgin carbon fibers, those produced as cutting materials by cutting carbon fiber sheets during the production of CFRP, etc. Anything can be used. The raw material of the carbon fiber may be any material such as polyacrylonitrile (PAN) or pitch. Moreover, the carbon fiber sheet of the present invention and a carbon fiber sheet (for example, a long fiber sheet) prepared by another method can be laminated and used.
本発明の炭素繊維強化樹脂成形体は前記本発明の炭素繊維シートを使用する。本発明の炭素繊維シートとともに、別の例えばバージンの炭素繊維シートを積層して使用することもできる。炭素繊維強化樹脂成形体は、一例として真空樹脂含浸法(VaRTM)により成形するのが好ましい。VaRTMはマトリックス樹脂が炭素繊維シートの内部まで均一に含浸し、品質の高い成形体が得られる。マトリックス樹脂としてはエポキシ樹脂等公知の樹脂を使用できる。 The carbon fiber reinforced resin molded product of the present invention uses the carbon fiber sheet of the present invention. Along with the carbon fiber sheet of the present invention, another carbon fiber sheet of virgin, for example, can be laminated and used. As an example, the carbon fiber reinforced resin molded body is preferably molded by a vacuum resin impregnation method (VaRTM). VaRTM is uniformly impregnated with the matrix resin to the inside of the carbon fiber sheet, and a high-quality molded article is obtained. A known resin such as an epoxy resin can be used as the matrix resin.
炭素繊維シートには炭素繊維の絡まり部分が存在していることもある。この絡まり部分は炭素繊維が横向きになっていたり、曲がっていたり、重なっていることにより発現している。炭素繊維の配向性は低下しているが、炭素繊維100質量%当たり10質量%以下、好ましくは5質量%以下、さらに好ましくは1質量%以下であれば実用上の問題は少ない。 The carbon fiber sheet may have entangled portions of carbon fibers. This entangled portion is manifested when the carbon fibers are sideways, bent, or overlapped. Although the orientation of the carbon fibers is lowered, there are few practical problems as long as it is 10% by mass or less, preferably 5% by mass or less, more preferably 1% by mass or less per 100% by mass of the carbon fibers.
以下、図面を用いて説明する。以下の図面において、同一符号は同一物を示す。図1は本発明の一実施例のカード機1の模式的斜視図、図2は同断面図である。カード機1本体は、針布又はメタリックワイヤ6が表面に固定されているシリンダー5と、供給ローラ7とツール又はホイール等と呼ばれる開繊ローラ8a,8b,8cで主要部が構成されている。カード機1には通常排出ベルト10が設けられているが、本発明においは、炭素繊維シート9はシリンダー5の表面に巻き付いて形成されるので排出ベルト10は省略しても良い。 Hereinafter, it demonstrates using drawing. In the following drawings, the same symbols indicate the same items. FIG. 1 is a schematic perspective view of a card machine 1 according to an embodiment of the present invention, and FIG. 2 is a sectional view thereof. The main body of the card machine 1 is mainly composed of a cylinder 5 having a needle cloth or metallic wire 6 fixed to the surface thereof, a supply roller 7 and fiber opening rollers 8a, 8b and 8c called tools or wheels. Although the card machine 1 is usually provided with a discharge belt 10, in the present invention, the carbon fiber sheet 9 is formed by wrapping around the surface of the cylinder 5, so the discharge belt 10 may be omitted.
短繊維からなる炭素繊維原綿は、まず供給ボックス2に供給される。少量の場合は供給ボックス2を使わなくても良い。供給ベルト3及び供給ローラ7により炭素繊維原綿4はカード機1本体に送られる。炭素繊維原綿4はシリンダー5と供給ローラ7、開繊ローラ8a,8b,8cの針布又はメタリックワイヤで開繊されるとともに一方向に配向され、シリンダー上の金属製針の間に巻き付く。巻き付いた状態を図2に示す。これを剥がすことにより図3に示す炭素繊維シート11が得られる。12は炭素繊維の絡まり部分である。 The carbon fiber raw cotton made of short fibers is first supplied to the supply box 2. In the case of a small amount, the supply box 2 need not be used. The carbon fiber raw cotton 4 is sent to the card machine 1 main body by the supply belt 3 and the supply roller 7. The carbon fiber raw cotton 4 is opened by the cloth of the cylinder 5 and the supply roller 7 and the opening rollers 8a, 8b and 8c or the metallic wire and oriented in one direction, and is wound around the metal needle on the cylinder. The wound state is shown in FIG. By removing this, the carbon fiber sheet 11 shown in FIG. 3 is obtained. 12 is a entangled portion of carbon fibers.
図4は本発明の別の実施例のカード機21の模式的断面図である。図2のシリンダーに換えてベルトコンベア状(例えば針布)のカード機である。炭素繊維原綿14は、供給ベルト13及び供給ローラ17によりカード機21本体に送られ、ベルトコンベア15上の金属製針16と供給ローラ17、開繊ローラ18a,18b,18cの金属製針16で開繊されるとともに一方向に配向され、ベルトコンベア上の金属製針16の間に巻き付く。巻き付いた炭素繊維シート19を剥がすことにより本発明の炭素繊維シートが得られる。 FIG. 4 is a schematic sectional view of a card machine 21 according to another embodiment of the present invention. It is a card machine of a belt conveyor type (for example, cloth) instead of the cylinder of FIG. The carbon fiber raw cotton 14 is sent to the card machine 21 main body by the supply belt 13 and the supply roller 17, and the metal needle 16 on the belt conveyor 15, the supply roller 17, and the metal needles 16 of the opening rollers 18 a, 18 b and 18 c. The fiber is opened and oriented in one direction, and is wound between the metal needles 16 on the belt conveyor. The carbon fiber sheet of the present invention is obtained by peeling off the wound carbon fiber sheet 19.
以下、実施例を用いてさらに具体的に説明する。なお、本発明は下記の実施例に限定されるものではない。 Hereinafter, more specific description will be made using examples. In addition, this invention is not limited to the following Example.
<試験片の引張試験>
ASTM D3039に従い、インストロン万能試験機 モデル8501を使用し、ロードセル100kN、引張速度1.0mm/sec、つかみ圧1600psiでCFRPの引張強度を測定した。
<厚み(mm)、見掛け密度(g/cm3)>
JIS L1913「一般短繊維不織布試験方法」に準じて
厚みを測定し、この値と目付けの値とから見かけ密度を算出した。
<Tensile test of test piece>
According to ASTM D3039, the tensile strength of CFRP was measured using an Instron universal tester model 8501 with a load cell of 100 kN, a tensile speed of 1.0 mm / sec, and a gripping pressure of 1600 psi.
<Thickness (mm), apparent density (g / cm 3 )>
The thickness was measured according to JIS L1913 “Test method for general short fiber nonwoven fabric”, and the apparent density was calculated from this value and the basis weight value.
(実施例1)
一方向に揃えられた炭素繊維がポリアミド製バインダーによってまとめられているテープ(SAERTEX社製、商品名"Unidirectional Non Crimp Fabric V96069")から、常圧溶解法によりリサイクルされた炭素繊維(東レ社製、商品名“T800”、繊維径5μm、繊維長80mm)を、メタリックワイヤ(ワイヤ高さ5mm、ワイヤトップの間隔5mm)を組み込んだカード機(シリンダー直径500mm、回転数100m/分)に幅270mm、長さ60mmで10g投入し、5分間運転した。次いでシリンダーから炭素繊維層を剥がし取り、幅270mm、長さ900mm、単位面積当たりの質量20g/m2、荷重500Paをかけたときの密度が0.06g/cm3の炭素繊維シートを形成した。この炭素繊維シートを構成する炭素繊維はデジタルカメラの画像を観察したところ、60質量%以上が±10度以内の角度で配向されていた。さらに、開繊性は良く均一に開繊されていた。得られた炭素繊維シートの表面写真を図5に示す。図5において黒い筋状に見えるのは炭素繊維の絡まり部分である。
Example 1
Carbon fiber that has been unidirectionally aligned with a polyamide binder (SAERTEX, trade name "Unidirectional Non Crimp Fabric V96069"), carbon fiber recycled by atmospheric pressure melting (Toray, The product name “T800”, fiber diameter 5 μm, fiber length 80 mm) is 270 mm wide in a card machine (cylinder diameter 500 mm, rotation speed 100 m / min) incorporating a metallic wire (wire height 5 mm, wire top spacing 5 mm), 10 g was introduced at a length of 60 mm and operated for 5 minutes. Next, the carbon fiber layer was peeled off from the cylinder to form a carbon fiber sheet having a width of 270 mm, a length of 900 mm, a mass per unit area of 20 g / m 2 , and a density of 0.06 g / cm 3 when a load of 500 Pa was applied. When the carbon fiber which comprises this carbon fiber sheet observed the image of the digital camera, 60 mass% or more was orientated at the angle within +/- 10 degree | times. Furthermore, the spreadability was good and evenly spread. The surface photograph of the obtained carbon fiber sheet is shown in FIG. In FIG. 5, the tangled portions of carbon fibers appear as black streaks.
この炭素繊維シートを繊維方向が同一となるように揃えて20層積層し、400g/m2のCFRP用ラップとした。このCFRP用ラップに、エポキシ樹脂(ナガセケムテックス社製、商品名“XNR/6809”)をVaRTM法で含浸させ、縦900mm、横200mmのCFRPの母板を成形した。この母板からASTMの規格に従って縦240mm、横25mm、厚さ1.5mm、密度1.3g/cm3のCFRPの試験片を切り出した。その物性は表1にまとめて示す。 20 layers of this carbon fiber sheet were aligned so that the fiber directions were the same, and a 400 g / m 2 CFRP wrap was obtained. The CFRP wrap was impregnated with an epoxy resin (manufactured by Nagase ChemteX Corporation, trade name “XNR / 6809”) by the VaRTM method to form a CFRP base plate having a length of 900 mm and a width of 200 mm. A test piece of CFRP having a length of 240 mm, a width of 25 mm, a thickness of 1.5 mm, and a density of 1.3 g / cm 3 was cut out from this base plate in accordance with ASTM standards. The physical properties are summarized in Table 1.
(比較例1)
この比較例は湿式抄紙法により炭素繊維とバインダー繊維をシート化し、実施例1と同様にCFRPの成形体とした例である。炭素繊維トウから常圧溶解法によりリサイクルされた炭素繊維(東邦テナックス社製、商品名“IMS60”、繊維径5μm、繊維長6mm)とバインダー繊維(ポリエチレンテレフタレート(PET)繊維、繊維長6mm)を質量比7:3の割合で混合し、水中で撹拌して繊維スラリーを作成した。得られたスラリーを手抄筒で抄紙して湿紙を得た。この湿紙をヒーターで乾燥させ、単位面積当たりの質量30g/m2の湿式不織布得た。得られた炭素繊維シートの表面写真を図6に示す。図6から明らかなとおり、炭素繊維は一方向には配向していないことが分かる。
(Comparative Example 1)
In this comparative example, carbon fibers and binder fibers are formed into a sheet by a wet papermaking method, and a CFRP molded body is formed in the same manner as in Example 1. Carbon fiber recycled from carbon fiber tow by atmospheric pressure melting method (trade name “IMS60”, fiber diameter 5 μm, fiber length 6 mm, manufactured by Toho Tenax Co., Ltd.) and binder fiber (polyethylene terephthalate (PET) fiber, fiber length 6 mm) The mixture was mixed at a mass ratio of 7: 3 and stirred in water to prepare a fiber slurry. The obtained slurry was made with a hand-making cylinder to obtain a wet paper. The wet paper was dried with a heater to obtain a wet nonwoven fabric having a mass per unit area of 30 g / m 2 . The surface photograph of the obtained carbon fiber sheet is shown in FIG. As is clear from FIG. 6, it can be seen that the carbon fibers are not oriented in one direction.
この炭素繊維シートを8枚積層し、240g/m2のCFRP用ラップを形成した。このCFRP用ラップに、エポキシ樹脂(ナガセケムテックス社製、商品名“XNR/6809”)をVaRTM法で含浸させ、CFRPの母板を成形した。この母板からASTMの規格に従って縦240mm、横25mm、厚さ1.1mm、密度1.2g/cm3の試験片を切り出した。その物性は表1にまとめて示す。 Eight carbon fiber sheets were laminated to form a 240 g / m 2 CFRP wrap. This CFRP wrap was impregnated with an epoxy resin (manufactured by Nagase ChemteX Corporation, trade name “XNR / 6809”) by the VaRTM method to form a CFRP base plate. A test piece having a length of 240 mm, a width of 25 mm, a thickness of 1.1 mm, and a density of 1.2 g / cm 3 was cut out from the base plate in accordance with ASTM standards. The physical properties are summarized in Table 1.
(比較例2)
この比較例は湿式抄紙法により炭素繊維と比較例1とは異なるバインダー繊維をシート化し、実施例1と同様にCFRPの成形体とした例である。炭素繊維トウから常圧溶解法によりリサイクルされた炭素繊維(東邦テナックス社製、商品名“IMS60”、繊維径5μm、繊維長6mm)とバインダー繊維(水溶性ポリビニルアルコール(PVA)繊維、繊維長6mm)を9:1の割合で混合し、水中で撹拌して繊維スラリーを作成した。得られたスラリーを手抄筒で抄紙して湿紙を得た。この湿紙をヒーターで乾燥させ、単位面積当たりの質量30g/m2の湿式不織布得た。これを8枚積層した後にPVA繊維を熱水で洗浄して除去し、240g/m2のCFRP用ラップを形成した。このCFRP用ラップに、エポキシ樹脂(ナガセケムテックス社製、商品名“XNR/6809”)をVaRTM法で含浸させ、CFRPの母板を成形した。この母板からASTMの規格に従って縦240mm、横25mm、厚さ1.8mm、密度1.2g/cm3の試験片を切り出した。その物性は表1にまとめて示す。
(Comparative Example 2)
In this comparative example, carbon fiber and a binder fiber different from those in Comparative Example 1 were formed into a sheet by a wet papermaking method, and a CFRP molded body was obtained in the same manner as in Example 1. Carbon fiber recycled from carbon fiber tow by atmospheric pressure melting method (trade name “IMS60” manufactured by Toho Tenax Co., Ltd., fiber diameter 5 μm, fiber length 6 mm) and binder fiber (water-soluble polyvinyl alcohol (PVA) fiber, fiber length 6 mm) ) At a ratio of 9: 1 and stirred in water to create a fiber slurry. The obtained slurry was made with a hand-making cylinder to obtain a wet paper. The wet paper was dried with a heater to obtain a wet nonwoven fabric having a mass per unit area of 30 g / m 2 . After laminating 8 sheets, the PVA fibers were removed by washing with hot water to form a 240 g / m 2 CFRP wrap. This CFRP wrap was impregnated with an epoxy resin (manufactured by Nagase ChemteX Corporation, trade name “XNR / 6809”) by the VaRTM method to form a CFRP base plate. A test piece having a length of 240 mm, a width of 25 mm, a thickness of 1.8 mm, and a density of 1.2 g / cm 3 was cut out from the base plate in accordance with ASTM standards. The physical properties are summarized in Table 1.
(比較例3)
リサイクルされた炭素繊維の繊維長を12.5mmとした以外は比較例2と同様に実験した。以上の実験の物性を表1にまとめて示す。
(Comparative Example 3)
The experiment was performed in the same manner as in Comparative Example 2 except that the recycled carbon fiber had a fiber length of 12.5 mm. The physical properties of the above experiments are summarized in Table 1.
表1から、実施例1は比較例1〜3に比べて引張強度がきわめて高いことがわかる。これは炭素繊維がよく開繊されており、開繊性も均一であり、繊維の配向性も高いことに起因していると思われる。 From Table 1, it can be seen that Example 1 has an extremely high tensile strength as compared with Comparative Examples 1 to 3. This seems to be due to the fact that the carbon fibers are well opened, the spreadability is uniform, and the orientation of the fibers is high.
(実施例2)
この実施例では実施例1と同様に実験し、得られたCFRP成形体の密度と引張強度の関係を調べたものである。合計22の実験例の各成形体の引張強度を示すグラフを図7に示す。図7から明らかなとおり、密度が高くなると引張強度が大きくなる。このことから、炭素繊維の開繊性及び配向性を高め、均一性を高くすることは重要であることが分かる。とくに炭素繊維の開繊性及び配向性を高めると成形体の密度も高くなることから、前記性質は重要である。
(Example 2)
In this example, an experiment was performed in the same manner as in Example 1, and the relationship between the density and tensile strength of the obtained CFRP molded body was examined. The graph which shows the tensile strength of each molded object of a total of 22 experimental examples is shown in FIG. As apparent from FIG. 7, the tensile strength increases as the density increases. From this, it can be seen that it is important to improve the spreadability and orientation of the carbon fiber and to increase the uniformity. In particular, the above properties are important because the density of the molded body increases when the spreadability and orientation of the carbon fibers are increased.
(比較例4)
実施例1の炭素繊維原綿を用いて、実施例1で使用したカード機を通過させて炭素繊維シートを得た。得られた炭素繊維シートの表面写真を図8に示す。図8から明らかなとおり、カード機を通過させた炭素繊維シート無配向であり、開繊状態も悪く、一見して成形体には利用できないことがわかった。
(Comparative Example 4)
Using the carbon fiber raw cotton of Example 1, the card machine used in Example 1 was passed through to obtain a carbon fiber sheet. The surface photograph of the obtained carbon fiber sheet is shown in FIG. As is clear from FIG. 8, it was found that the carbon fiber sheet passed through the card machine was non-oriented, the state of fiber opening was poor, and at first glance it could not be used for a molded product.
本発明の炭素繊維は、資源の有効活用からリサイクルされた炭素繊維であるのが好ましいが、バージンの炭素繊維を切断したもの、CFRPの製造の際の炭素繊維シートの切断などにより端材として発生したものなど、どのようなものでも使用できる。とくに今後は航空機や自動車などの廃材として廃CFRPが大量に発生することが予想され、廃CFRPから取り出される炭素繊維は絡まり合った状態であるから、このような絡まり合った炭素繊維の開繊性及び配向性を高くすることができる本発明の適用分野は広い。 The carbon fiber of the present invention is preferably a carbon fiber recycled from the effective use of resources, but it is generated as a scrap material by cutting a virgin carbon fiber, cutting a carbon fiber sheet in the production of CFRP, etc. Anything can be used. In particular, in the future, a large amount of waste CFRP is expected to be generated as waste material for aircraft and automobiles, and the carbon fibers extracted from the waste CFRP are in an intertwined state. In addition, the field of application of the present invention that can increase the orientation is wide.
1,21 カード機
2 供給ボックス
3,13 供給ベルト
4,14 炭素繊維原綿
5 シリンダー
6 針布又はメタリックワイヤ
7,17 供給ローラ
8a,8b,8c,18a,18b,18C 開繊ローラ
9,19 巻き付いた炭素繊維シート
10,20 排出ベルト
11 開繊された炭素繊維シート
12 炭素繊維の絡まり部分
15 ベルトコンベア
16 金属製針
1, 21 Card machine 2 Supply box 3, 13 Supply belt 4, 14 Carbon fiber raw cotton 5 Cylinder 6 Needle cloth or metallic wire 7, 17 Supply roller 8a, 8b, 8c, 18a, 18b, 18C Opening roller 9, 19 Carbon fiber sheets 10, 20 Discharge belt 11 Opened carbon fiber sheet 12 Tangled portion 15 of carbon fiber 15 Belt conveyor 16 Metal needle
Claims (8)
前記炭素繊維シートはカード機の開繊装置上に開繊されて巻き付いたものを剥がして形成され、かつ実質的に同一方向に炭素繊維が配向されており、単位面積当たりの質量が5g/m2以上であることを特徴とする炭素繊維シート。 A carbon fiber sheet consisting of a single carbon fiber system composed of short fiber sheets,
The carbon fiber sheet is formed by peeling and winding the carbon fiber sheet that has been opened on a card machine opening device, and the carbon fibers are oriented in substantially the same direction, and the mass per unit area is 5 g / m. A carbon fiber sheet characterized by being 2 or more.
前記炭素繊維シートは請求項1〜6のいずれかに記載の炭素繊維シートであることを特徴とする炭素繊維強化樹脂成形体。 A carbon fiber reinforced resin molded article containing a carbon fiber sheet and a matrix resin,
The said carbon fiber sheet is a carbon fiber sheet in any one of Claims 1-6, The carbon fiber reinforced resin molded object characterized by the above-mentioned.