JP2016069034A - Multilayer container made of synthetic resin - Google Patents
Multilayer container made of synthetic resin Download PDFInfo
- Publication number
- JP2016069034A JP2016069034A JP2014201386A JP2014201386A JP2016069034A JP 2016069034 A JP2016069034 A JP 2016069034A JP 2014201386 A JP2014201386 A JP 2014201386A JP 2014201386 A JP2014201386 A JP 2014201386A JP 2016069034 A JP2016069034 A JP 2016069034A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin layer
- layer
- container
- synthetic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、複数の樹脂層を積層させた合成樹脂製多層容器に関するものである。 The present invention relates to a synthetic resin multilayer container in which a plurality of resin layers are laminated.
従来、内容物として化粧料や食品調味料などを収容可能であって、胴部を押圧することで内容物を注出させることができるスクイズ変形可能な合成樹脂製の容器が知られている。このような容器においては、酸素透過性が低い酸素バリア層を含む、複数の樹脂層を積層させた合成樹脂製多層容器が既知である(例えば特許文献1参照)。酸素バリア層を設けることによって容器を透過する酸素の量を抑制することができるので、内容物の酸化が抑えられて品質を長期に亘って維持することができる。 2. Description of the Related Art Conventionally, a squeeze-deformable synthetic resin container that can accommodate cosmetics, food seasonings, and the like as contents, and that allows the contents to be poured out by pressing a body part is known. As such a container, a synthetic resin multilayer container in which a plurality of resin layers including an oxygen barrier layer having low oxygen permeability is laminated is known (see, for example, Patent Document 1). By providing the oxygen barrier layer, the amount of oxygen that permeates the container can be suppressed, so that the oxidation of the contents can be suppressed and the quality can be maintained over a long period of time.
ところで特許文献1の容器は、容器の外側から内側に向かって、主要樹脂層、接着樹脂層、酸素バリア性樹脂層、接着樹脂層、主要樹脂層の順で積層されている。すなわち、少なくとも5層の樹脂層で構成しなければならず、コスト削減にも限界を来していた。 By the way, the container of patent document 1 is laminated | stacked in order of the main resin layer, the adhesive resin layer, the oxygen-barrier resin layer, the adhesive resin layer, and the main resin layer toward the inner side from the outer side of the container. That is, it must be composed of at least five resin layers, and there has been a limit to cost reduction.
本発明は、このような問題点を解決することを課題とするものであり、その目的は、実使用において求められる強度や酸素の透過を抑制する機能は維持したまま、より少ない数の樹脂層で構成することができる、新たな合成樹脂製多層容器を提案するところにある。 An object of the present invention is to solve such problems, and the object thereof is to reduce the number of resin layers while maintaining the strength required in actual use and the function of suppressing the permeation of oxygen. A new synthetic resin multilayer container can be proposed.
本発明は、内容物を収容する内部空間を有し、スクイズ変形可能な合成樹脂製多層容器であって、
容器の外側から前記内部空間に向かって、外側樹脂層、酸素バリア樹脂層、接着樹脂層、内側樹脂層の順で積層される層構成を有する合成樹脂製多層容器である。
The present invention has an internal space for storing contents, and is a squeeze-deformable synthetic resin multilayer container,
It is a synthetic resin multilayer container having a layer structure in which an outer resin layer, an oxygen barrier resin layer, an adhesive resin layer, and an inner resin layer are laminated in this order from the outside of the container toward the internal space.
前記外側樹脂層は、ベース樹脂と接着樹脂とをブレンドした樹脂で構成されることが好ましい。 The outer resin layer is preferably made of a resin obtained by blending a base resin and an adhesive resin.
前記ベース樹脂と前記接着樹脂との合計100質量部当たり、該接着樹脂を0質量部超50質量部未満含むことが好ましい。 It is preferable that the adhesive resin is included more than 0 parts by mass and less than 50 parts by mass per 100 parts by mass in total of the base resin and the adhesive resin.
前記内側樹脂層は、再生材層と、該再生材層に積層されるとともに前記内部空間に面するバージン材層とを有することが好ましい。 The inner resin layer preferably includes a recycled material layer and a virgin material layer that is laminated on the recycled material layer and faces the internal space.
本発明者が検討を重ねたところ、従来の容器における、容器の外側に配される主要樹脂層と酸素バリア性樹脂層との間に設けられていた接着樹脂層を廃止して、容器の外側から前記内部空間に向かって、外側樹脂層、酸素バリア樹脂層、接着樹脂層、内側樹脂層の順で積層しても、実使用において樹脂層の層間剥離が生じないことを見出した。すなわち本発明によれば、実使用において必要な強度や酸素の透過を抑制する機能を維持しつつ、従来の容器に対して樹脂層が1層少なくなる分、コストを抑えることができる。 As a result of repeated studies by the present inventor, in the conventional container, the adhesive resin layer provided between the main resin layer and the oxygen barrier resin layer disposed outside the container is abolished, and the outside of the container is removed. It was found that even when the outer resin layer, the oxygen barrier resin layer, the adhesive resin layer, and the inner resin layer are laminated in this order from the inner space to the inner space, the delamination of the resin layer does not occur in actual use. That is, according to the present invention, it is possible to reduce the cost as much as one resin layer is reduced from the conventional container while maintaining the strength required for actual use and the function of suppressing permeation of oxygen.
以下、図面を参照して、本発明に従う合成樹脂製多層容器の一実施形態をより具体的に説明する。 Hereinafter, an embodiment of a synthetic resin multilayer container according to the present invention will be described in more detail with reference to the drawings.
図中、符号1は、本発明に従う合成樹脂製多層容器(以下、「容器」と称呼する。)の一実施形態を示す。容器1は、楕円板状の底部2と、底部2の縁部に連結する筒状の胴部3(下部が底部2の縁部に対応する楕円筒状であり、上部が円筒状であって、中間部は上方へ向けて縮径しながら下部と上部を滑らかにつないでいる)と、胴部3の上部に連結する円筒状の口部(不図示)とから形成されている。容器1の内側には、内容物を収容する内部空間Nが形成されている。また、容器1の口部には、内部空間Nを閉鎖するキャップCが着脱自在に装着されている。 In the drawing, reference numeral 1 denotes an embodiment of a synthetic resin multilayer container (hereinafter referred to as “container”) according to the present invention. The container 1 has an elliptical plate-like bottom 2 and a cylindrical body 3 connected to the edge of the bottom 2 (the lower part is an elliptical cylinder corresponding to the edge of the bottom 2 and the upper part is cylindrical. The intermediate portion is formed of a cylindrical mouth portion (not shown) connected to the upper portion of the body portion 3 and the lower portion and the upper portion are smoothly connected while reducing the diameter upward. Inside the container 1, an internal space N that stores the contents is formed. A cap C that closes the internal space N is detachably attached to the mouth of the container 1.
容器1は、複数の樹脂層を積層して形成されている。具体的には、図1の部分断面拡大図に示すように、容器1の外側から内部空間Nに向かって、外側樹脂層4、酸素バリア樹脂層5、接着樹脂層6、内側樹脂層7の順で積層されている。 The container 1 is formed by laminating a plurality of resin layers. Specifically, as shown in the enlarged partial sectional view of FIG. 1, the outer resin layer 4, the oxygen barrier resin layer 5, the adhesive resin layer 6, and the inner resin layer 7 are formed from the outside of the container 1 toward the internal space N. They are stacked in order.
外側樹脂層4は、ベース樹脂のみ、或いはベース樹脂と接着樹脂とをブレンドした樹脂で構成されている。ベース樹脂としては、ポリオレフィン系樹脂(例えば低密度ポリエチレン樹脂(LDPE)、高密度ポリエチレン樹脂(HDPE)等のポリエチレン樹脂(PE)や、ポリプロピレン樹脂(PP))、ポリエステル系樹脂(例えばポリエチレンテレフタレート樹脂(PET)やポリエチレンナフタレート樹脂(PEN))等を用いることができる。また、接着樹脂は、接着性を有する種々のものが適用可能であって、例えば、変性ポリオレフィン樹脂(例えば三井化学株式会社製「アドマー」(登録商標)等)等を用いることができる。 The outer resin layer 4 is made of only a base resin or a resin obtained by blending a base resin and an adhesive resin. Examples of the base resin include polyolefin resins (for example, polyethylene resins (PE) such as low density polyethylene resin (LDPE) and high density polyethylene resin (HDPE), polypropylene resins (PP)), and polyester resins (for example, polyethylene terephthalate resin ( PET) or polyethylene naphthalate resin (PEN)) or the like can be used. Various adhesive resins can be used as the adhesive resin. For example, a modified polyolefin resin (for example, “Admer” (registered trademark) manufactured by Mitsui Chemicals, Inc.) can be used.
酸素バリア樹脂層5は、酸素透過性が低い(酸素を透過させにくい)バリア性樹脂で構成されていて、例えばエチレンビニルアルコール共重合樹脂(EVOH)やナイロン樹脂(PA)を用いることができる。 The oxygen barrier resin layer 5 is composed of a barrier resin having low oxygen permeability (difficult to transmit oxygen), and for example, ethylene vinyl alcohol copolymer resin (EVOH) or nylon resin (PA) can be used.
接着樹脂層6は、隣接する酸素バリア樹脂層5と内側樹脂層7とに接着する機能を有する樹脂で構成されている。接着樹脂層6に用いる樹脂は、上述した外側樹脂層4の接着樹脂とは異なるものを用いてもよいが、使用する樹脂の種類を抑えるために、外側樹脂層4の接着樹脂と同一の樹脂を用いることが好ましい。 The adhesive resin layer 6 is made of a resin having a function of adhering to the adjacent oxygen barrier resin layer 5 and the inner resin layer 7. The resin used for the adhesive resin layer 6 may be different from the adhesive resin for the outer resin layer 4 described above, but the same resin as the adhesive resin for the outer resin layer 4 in order to suppress the type of resin used. Is preferably used.
内側樹脂層7は、水分を透過させにくい樹脂で構成されている。上述した酸素バリア樹脂層5に用いるバリア性樹脂は、一般に水分を吸着するとバリア性が低下する傾向があるが、内部空間Nに収容された内容物の水分は、内側樹脂層7によって透過が妨げられることになるので、酸素バリア樹脂層5のバリア性を維持することができる。内側樹脂層7に用いる樹脂は、使用する樹脂の種類を抑えるために、外側樹脂層4のベース樹脂を用いることが好ましい。なお、内側樹脂層7は一層のみで構成することも可能であるが、本実施形態のように、容器1を成形する際に不要になった部材(トリミングした際の端材等)で構成される再生樹脂を含む再生材層8と、再生樹脂を含まないバージン材層9とを積層して構成してもよい。再生樹脂を用いることによって必要になる樹脂の量を削減することができるので、コストを抑えることができる。また、再生樹脂を用いる故に再生材層8の特性は多少の変動を伴うことがあるため、その影響を抑えるべく、バージン材層9は、再生材層8を覆って内部空間Nに面するように設けることが好ましい。 The inner resin layer 7 is made of a resin that hardly allows moisture to pass therethrough. The barrier resin used for the oxygen barrier resin layer 5 described above generally has a tendency that the barrier property is lowered when moisture is adsorbed, but the inner resin layer 7 prevents the moisture contained in the contents contained in the internal space N from being permeated. Therefore, the barrier property of the oxygen barrier resin layer 5 can be maintained. The resin used for the inner resin layer 7 is preferably the base resin of the outer resin layer 4 in order to suppress the type of resin used. Although the inner resin layer 7 can be composed of only one layer, it is composed of a member (such as a trimmed end material) that is no longer necessary when the container 1 is molded as in this embodiment. The recycled material layer 8 containing the recycled resin and the virgin material layer 9 not containing the recycled resin may be laminated. Since the amount of resin required by using the recycled resin can be reduced, the cost can be suppressed. Further, since the characteristics of the recycled material layer 8 may be slightly changed due to the use of the recycled resin, the virgin material layer 9 covers the recycled material layer 8 and faces the internal space N in order to suppress the influence. It is preferable to provide in.
このような容器1は、例えば上述したそれぞれの樹脂を溶融状態とし、ダイスを介してこれらを共押出しすることで円筒状の積層パリソンを成形し、この積層パリソンをブロー成形することにより得ることができる。なお、本実施形態の容器1は、成形時においてはブロー成形の割り金型を閉めて積層パリソンの下部を食い切ることで、底部の端部が溶着された状態でブロー成形し、その後口部(口部は、図示のものより長めに形成している)を溶着することで、内部空間Nが密閉された状態で形成されるものであって、内容物を充填する前に口部を所定の長さにカットしたものである。 Such a container 1 can be obtained, for example, by forming each of the above-described resins in a molten state, co-extruding them through a die to form a cylindrical laminated parison, and blow molding the laminated parison. it can. In addition, the container 1 of the present embodiment is blow-molded with the bottom end welded by closing the blow mold split mold and biting the lower part of the laminated parison at the time of molding. (The mouth part is formed longer than that shown in the figure) by welding, the inner space N is formed in a sealed state, and the mouth part is predetermined before filling the contents. It is cut to the length.
以下、容器1の性能を確認した各種試験について説明する。ここで、確認に用いた容器1は、外側樹脂層4については用いる樹脂の含有割合を変更した一方で、酸素バリア樹脂層5、接着樹脂層6、内側樹脂層7については同一にしたものである。具体的には、外側樹脂層4は、ベース樹脂のみで構成する(実施例1)、或いはベース樹脂と接着樹脂とを表1に示す割合でブレンドした樹脂で構成する(実施例2〜6)ものである。ここで、外側樹脂層4を構成するベース樹脂は低密度ポリエチレン樹脂を用いていて、接着樹脂は変性ポリオレフィン樹脂を用いている。また、酸素バリア樹脂層5は、エチレンビニルアルコール共重合樹脂で構成され、接着樹脂層6は、変性ポリオレフィン樹脂で構成されている。更に内側樹脂層7は、図示のように再生材層8とバージン材層9とを積層したものである。ここで再生材層8は、再生樹脂(低密度ポリエチレン樹脂、エチレンビニルアルコール共重合樹脂、変性ポリオレフィン樹脂)で形成されるものであるが、この再生樹脂に外側樹脂層4のベース樹脂(低密度ポリエチレン樹脂)をブレンドした樹脂で構成してもよい。また、バージン材層9は、外側樹脂層4のベース樹脂(低密度ポリエチレン樹脂)のみで構成されるものである。ここで、実施例1〜6における酸素バリア樹脂層は従来の容器と同等であるため、酸素の透過を抑制する機能は従来と同様に維持されている。 Hereinafter, various tests for confirming the performance of the container 1 will be described. Here, the container 1 used for the confirmation was the same for the oxygen barrier resin layer 5, the adhesive resin layer 6, and the inner resin layer 7 while changing the content ratio of the resin used for the outer resin layer 4. is there. Specifically, the outer resin layer 4 is composed of only the base resin (Example 1), or is composed of a resin obtained by blending the base resin and the adhesive resin at a ratio shown in Table 1 (Examples 2 to 6). Is. Here, the base resin constituting the outer resin layer 4 is a low density polyethylene resin, and the adhesive resin is a modified polyolefin resin. The oxygen barrier resin layer 5 is made of an ethylene vinyl alcohol copolymer resin, and the adhesive resin layer 6 is made of a modified polyolefin resin. Further, the inner resin layer 7 is formed by laminating a recycled material layer 8 and a virgin material layer 9 as shown in the figure. Here, the recycled material layer 8 is formed of a recycled resin (low density polyethylene resin, ethylene vinyl alcohol copolymer resin, modified polyolefin resin), and the recycled resin base resin (low density) is formed on the recycled resin. (Polyethylene resin) may be blended. The virgin material layer 9 is composed only of the base resin (low density polyethylene resin) of the outer resin layer 4. Here, since the oxygen barrier resin layer in Examples 1-6 is equivalent to the conventional container, the function which suppresses permeation | transmission of oxygen is maintained similarly to the past.
[口部端面での層間剥離確認]
ブロー成形後に口部をカットして、口部端面で樹脂層の層間剥離が生じているか目視確認を行った。結果は表1に示す通りである。
[Check delamination at the edge of the mouth]
The mouth part was cut after blow molding, and it was visually confirmed whether or not delamination of the resin layer occurred on the end face of the mouth part. The results are as shown in Table 1.
[落下試験]
表1に示す実施例1〜6の容器に水を充填し、且つ5℃で所定時間(24時間)保管しておいたものを1mの高さから床(コンクリート製)に対して正立姿勢で落下させた。所定の回数(5回)落下させた後、横向きに倒した姿勢で再び所定の回数(5回)落下させた。破損や樹脂層の層間剥離が認められない場合は、同一の容器を1.2mの高さから同じように落下させた。1.2mの高さからの落下でも異常が認められない場合は、同一の容器を1.5mの高さから同じように落下させ、終了後に容器の破損や層間剥離の状態を確認した。結果は表1に示す通りである。
[Drop test]
A container filled with water in Examples 1 to 6 shown in Table 1 and stored at 5 ° C. for a predetermined time (24 hours) for a predetermined time (24 hours) from a height of 1 m to the floor (made of concrete) Was dropped. After being dropped a predetermined number of times (5 times), it was dropped again a predetermined number of times (5 times) in a posture in which it was tilted sideways. When breakage or delamination of the resin layer was not observed, the same container was dropped in the same manner from a height of 1.2 m. When no abnormality was observed even when dropped from a height of 1.2 m, the same container was dropped in the same manner from a height of 1.5 m, and after completion, the damage of the container and the state of delamination were confirmed. The results are as shown in Table 1.
[スクイズ試験]
表1に示す実施例1〜6の容器であって、空の状態で且つ5℃で所定時間(24時間)保管しておいたものに対し、胴部3の最大径付近を、容器1の内面同士が接触するまで押圧した。図1に矢印で示す向き、及び図2で矢印に示す向きにそれぞれ所定回数(10回)押圧し、終了後に容器の層間剥離の状態を確認した。結果は表1に示す通りである。
[Squeeze test]
For the containers of Examples 1 to 6 shown in Table 1 that were kept empty and stored at 5 ° C. for a predetermined time (24 hours), the vicinity of the maximum diameter of the trunk portion 3 was It pressed until inner surfaces contacted. The container was pressed a predetermined number of times (10 times) in the direction indicated by the arrow in FIG. 1 and in the direction indicated by the arrow in FIG. 2, and the state of delamination of the container was confirmed after completion. The results are as shown in Table 1.
[剥離強度確認試験]
表1に示す実施例1〜6の容器から所定の大きさ(15mm幅)になる試料片を切り出して、この試料片における外側樹脂層4と酸素バリア樹脂層5との剥離強度を確認した。表1における「縦方向」とは、容器1の軸線に沿う向きでの剥離強度であり、「横方向」とは、容器1の軸線に直交する向き(容器1の周方向に沿う向き)での剥離強度である。剥離強度を測定するに当たっては、試料片の一端を剥がしておき、水平状態に固定した試料片から剥がした部分をチャックで挟んで、当該チャックを垂直方向に移動させて試料片を剥離させる際の強度をオートグラフ(100mm/min)で測定した。結果は表1に示す通りである。数値が大きいほど剥離強度が大きい(剥離しにくい)ことを示す。
[Peel strength test]
A sample piece having a predetermined size (15 mm width) was cut out from the containers of Examples 1 to 6 shown in Table 1, and the peel strength between the outer resin layer 4 and the oxygen barrier resin layer 5 in the sample piece was confirmed. The “longitudinal direction” in Table 1 is the peel strength in the direction along the axis of the container 1, and the “lateral direction” is the direction orthogonal to the axis of the container 1 (direction along the circumferential direction of the container 1). The peel strength. In measuring the peel strength, one end of the sample piece is peeled off, the part peeled off from the sample piece fixed in a horizontal state is sandwiched between chucks, and the chuck is moved in the vertical direction to peel off the sample piece. The strength was measured with an autograph (100 mm / min). The results are as shown in Table 1. It shows that peeling strength is so large that a numerical value is large (it is hard to peel).
[摩擦係数確認試験]
JIS K7125に準拠して、表1に示す実施例1〜6の容器同士(同一の実施例同士)の静摩擦係数及び動摩擦係数、並びに実施例1〜6の容器とポリアセタール樹脂(POM)との静摩擦係数及び動摩擦係数を確認した。ポリアセタール樹脂は、例えば容器を搬送するために用いるコンベアベルトや、搬送時の容器を案内するガイドレール等に用いられている。静摩擦係数及び動摩擦係数を測定するに当たっては、実施例1〜6の容器と同じ層構成になる所定の大きさの試料を準備し、この試料を相手材(試料と同一の層構成になる樹脂材、又はポリアセタール樹脂材)の上面に載置して、JIS K7125に準拠(1.96N、100mm/min)した手順で測定した。結果は表1に示す通りである。数値が大きいほど摩擦係数が大きいことを示す。
[Friction coefficient confirmation test]
In accordance with JIS K7125, the static friction coefficient and the dynamic friction coefficient between the containers of Examples 1 to 6 shown in Table 1 (the same Examples), and the static friction between the containers of Examples 1 to 6 and the polyacetal resin (POM). The coefficient and dynamic friction coefficient were confirmed. Polyacetal resin is used for, for example, a conveyor belt used for transporting containers, a guide rail for guiding containers during transport, and the like. In measuring the static friction coefficient and the dynamic friction coefficient, a sample of a predetermined size having the same layer configuration as the containers of Examples 1 to 6 is prepared, and this sample is used as a counterpart material (resin material having the same layer configuration as the sample). , Or a polyacetal resin material) and measured according to a procedure based on JIS K7125 (1.96 N, 100 mm / min). The results are as shown in Table 1. It shows that a coefficient of friction is so large that a numerical value is large.
表1に示した通り、実施例1〜6は、落下試験及びスクイズ試験によって樹脂層の層間剥離が生じておらず、外側樹脂層と酸素バリア樹脂層との間に接着樹脂層を設けなくても、実使用において求められる強度が得られることが確認された。また、外側樹脂層が、ベース樹脂と接着樹脂との合計100質量部当たり、接着樹脂が0質量部(すなわち、外側樹脂層はベース樹脂のみで構成される)である容器(実施例1)に対し、外側樹脂層がベース樹脂と接着樹脂とをブレンドした樹脂で構成される容器(実施例2〜6)では、外側樹脂層と酸素バリア樹脂層との層間剥離強度が高められることが確認された。 As shown in Table 1, in Examples 1 to 6, delamination of the resin layer was not caused by the drop test and the squeeze test, and the adhesive resin layer was not provided between the outer resin layer and the oxygen barrier resin layer. It was also confirmed that the strength required in actual use was obtained. Further, in the container (Example 1) in which the outer resin layer is 0 part by mass (that is, the outer resin layer is composed only of the base resin) per 100 parts by mass of the base resin and the adhesive resin in total. On the other hand, it was confirmed that the delamination strength between the outer resin layer and the oxygen barrier resin layer is increased in the container (Examples 2 to 6) in which the outer resin layer is made of a resin obtained by blending a base resin and an adhesive resin. It was.
なお実施例1は、容器の口部をカットした際に、まれに口部端面で樹脂層の層間剥離が生じることがあるため、歩留まりの低下につながる恐れがある。また、実施例6は、実施例6と同じ層構成の樹脂材が相手材である場合に静止摩擦係数及び動摩擦係数が急激に大きくなっているため、この仕様の容器を用いる場合は、例えば搬送ラインにおいて容器が傾いた状態で他の容器に接触すると、傾いた姿勢のまま搬送されて搬送トラブルを招く可能性がある。これに対し、外側樹脂層の構成を、ベース樹脂と接着樹脂との合計100質量部当たり、接着樹脂を0質量部超50質量部未満含むようにする場合(より好ましくは、ベース樹脂と接着樹脂との合計100質量部当たり、接着樹脂を5質量部以上30質量部以下含むようにする場合)容器の歩留まりが良くなるうえ、搬送性も向上するので、良好な生産性が得られることが確認された。 In Example 1, when the mouth portion of the container is cut, delamination of the resin layer sometimes occurs on the end surface of the mouth portion, which may lead to a decrease in yield. Further, in Example 6, when the resin material having the same layer structure as that of Example 6 is the counterpart material, the static friction coefficient and the dynamic friction coefficient are rapidly increased. If the container comes into contact with another container in a tilted state in the line, the container may be transported in a tilted posture, causing a transport trouble. On the other hand, when the configuration of the outer resin layer includes more than 0 parts by mass and less than 50 parts by mass of the adhesive resin per 100 parts by mass in total of the base resin and the adhesive resin (more preferably, the base resin and the adhesive resin When the adhesive resin is included in an amount of 5 parts by mass or more and 30 parts by mass or less per 100 parts by mass in total) The yield of the container is improved and the transportability is also improved, so that it is confirmed that good productivity can be obtained. It was done.
本発明によれば、より少ない数の樹脂層で構成してコストを抑えることができる、新たな合成樹脂製多層容器を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the new synthetic resin multilayer container which can be comprised by fewer resin layers and can hold down cost can be provided.
1:容器(合成樹脂製多層容器)
2:底部
3:胴部
4:外側樹脂層
5:酸素バリア樹脂層
6:接着樹脂層
7:内側樹脂層
8:再生材層
9:バージン材層
C:キャップ
N:内部空間
1: Container (synthetic resin multilayer container)
2: Bottom part 3: Body part 4: Outer resin layer 5: Oxygen barrier resin layer 6: Adhesive resin layer 7: Inner resin layer 8: Recycled material layer 9: Virgin material layer C: Cap N: Inner space
Claims (4)
容器の外側から前記内部空間に向かって、外側樹脂層、酸素バリア樹脂層、接着樹脂層、内側樹脂層の順で積層される層構成を有する合成樹脂製多層容器。 A multi-layer container made of synthetic resin that has an internal space for containing contents and is squeezable,
A synthetic resin multilayer container having a layer structure in which an outer resin layer, an oxygen barrier resin layer, an adhesive resin layer, and an inner resin layer are laminated in this order from the outside of the container toward the internal space.