JP2016056466A - Indelible paper - Google Patents
Indelible paper Download PDFInfo
- Publication number
- JP2016056466A JP2016056466A JP2014182266A JP2014182266A JP2016056466A JP 2016056466 A JP2016056466 A JP 2016056466A JP 2014182266 A JP2014182266 A JP 2014182266A JP 2014182266 A JP2014182266 A JP 2014182266A JP 2016056466 A JP2016056466 A JP 2016056466A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- tamper
- layer
- tampering
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、銀行券、有価証券、旅券等、偽造防止が必要とされる貴重印刷物に用いられる用紙に関するものである。 The present invention relates to paper used for valuable printed matter that needs to be prevented from forgery, such as banknotes, securities, and passports.
近年のカラーコピーやカラースキャナ等による複製技術の進歩に伴い、銀行券、有価証券、旅券等の貴重印刷物が偽造される危険性が高まってきているとともに、複製技術を用いて偽造品を一から作製するのではなく、一つの真正品から複数の偽造品を作製するという改竄行為が問題となっている。 With the recent progress in copying technology using color copying and color scanners, there is an increased risk of counterfeiting of valuable printed materials such as banknotes, securities, and passports. There is a problem of tampering, in which a plurality of counterfeit products are produced from one genuine product, rather than production.
例えば、図１５（ａ）に示す、真正品である一枚の用紙（１１）を、図１５（ｂ）に示すように矢印方向に複数枚に剥がして分解したのち、図１５（ｃ）に示すように、その分解した個々の紙層（Ｑ）を、複製した偽造用紙（１２）に貼り合わせることで一部を真正品とした複数の偽造品（１３）が作製されてしまうという問題がある。よって、このような貴重印刷物に用いられる用紙の剥離を防止する手段として、層間剥離強度が従来の用紙よりも向上した用紙が提案されている。 For example, an authentic sheet (11) shown in FIG. 15 (a) is separated into a plurality of sheets in the direction of the arrow as shown in FIG. 15 (b) and disassembled. As shown, there is a problem in that a plurality of counterfeit products (13), some of which are genuine products, are produced by pasting the individual paper layers (Q) that have been disassembled onto the copied counterfeit paper (12). is there. Therefore, as a means for preventing the peeling of the paper used for such precious printed matter, a paper having a delamination strength higher than that of a conventional paper has been proposed.
例えば、特許文献１において、図１６（ａ）に示すように、芯鞘型熱融着性繊維と親水性繊維を含むバインダーを塗布した不織布（１４ｂ）を中間層とした多層紙（１４）が開示されている。特許文献１の多層紙（１４）に用いる不織布（１４ｂ）は、バインダー塗布後に熱乾燥をすることで作製している。よって、芯鞘型熱融着性繊維が熱溶融することで繊維間結合が増し、不織布（１４ｂ）内の剥離強度が向上する。さらに不織布（１４ｂ）と上層（１４ａ）及び下層（１４ｃ）を抄紙機で抄き合わせる際の乾燥部において、芯鞘型熱融着繊維が再び熱溶融することで、各層の層間剥離強度を向上させることが可能となる。
For example, in
特許文献１により、層間剥離強度が従来の用紙よりも向上した貴重印刷物用の多層紙（１４）を得ることが可能となった。しかしながら、中間層に熱溶融する不織布（１４ｂ）を用いるため、多層で抄き合わせることが必須となる。よって、層間剥離強度は向上しているが、特許文献１の多層紙（１４）を貴重印刷物に用いた場合、ＡＴＭや券売機などの現金処理機内を複数回搬送されることで、層間剥離強度が低下し、図１６（ｂ）に示すように、層間で剥離してしまうという問題が残る。貴重印刷物の用紙が剥離した場合、図１５（ｃ）を用いて前述したとおり、一つの真正品から複数の偽造品を作製するという改竄行為が行われる危険性があり、改善の余地がある。
また、特許文献１により、中間層である不織布（１４ｂ）と上層（１４ａ）又は下層（１４ｃ）の隣接する面同士を、強固に接着することが可能となった。しかしながら、隣接する面同士のみ接着性を強固としたことで、隣接する面同士と、上層又は下層の一つの紙層内との剥離強度の差が大きくなる。よって、層間剥離強度は向上したが、一つの紙層内、例えば、図１６（ｃ）の拡大図（Ａ）に示すように、上層（１４ａ）内の剥離強度の弱い箇所（Ｔ）で剥離されるという新たな問題が発生する。
Further, according to
本発明は、上記課題の解決を目的とするものであり、具体的には、単層の用紙の紙層内部に、剥離による改ざん防止効果を有する改ざん防止模様が付与された用紙を提供することを目的とする。 The present invention aims to solve the above-described problems. Specifically, the present invention provides a paper in which a tamper-proof pattern having an anti-tampering effect due to peeling is provided inside the paper layer of a single-layer paper. With the goal.
本発明の改ざん防止用紙は、単層の用紙における紙層内の一部に、改ざん防止模様が形成され、改ざん防止模様は、用紙表面に対し、少なくとも一部が深さ方向に異なった領域を有し、紙層と化学結合可能な官能基を有する及び／又は繊維で形成された紙層による三次元の網目より大きい幅を有する少なくとも一種類の改ざん防止材料から成ることを特徴とする。 In the tamper-proof paper of the present invention, a tamper-proof pattern is formed in a part of the paper layer of a single-layer paper, and at least a part of the tamper-proof pattern has a different area in the depth direction with respect to the paper surface. And having at least one tamper-proof material having a functional group capable of chemically bonding to the paper layer and / or having a width larger than a three-dimensional network by the paper layer formed of fibers.
また、改ざん防止模様の一部が、用紙の少なくとも一方の面に表出して成ることを特徴とする。 Further, a part of the tamper-proof pattern is formed on at least one surface of the sheet.
単層の紙層内に、紙層と化学結合可能な官能基を有する及び／又は繊維で形成された紙層による三次元の網目より大きい幅を有する複数の改ざん防止材料から成る改ざん防止模様を形成することで、多層紙に付与された場合と比べて層間剥離を防ぎ、定着性に優れた改ざん防止用紙となる。 A tamper-proof pattern comprising a plurality of tamper-proof materials having a functional group capable of chemically bonding to the paper layer and / or having a width larger than a three-dimensional network by a paper layer formed of fibers in a single paper layer. By forming the sheet, delamination is prevented as compared with the case where it is applied to the multilayer paper, and the falsification preventing paper is excellent in fixability.
また、改ざん防止模様は、用紙表面に対し、少なくとも一部が深さ方向に異なった領域を有することで、前述した、一枚の真正品を、複数枚に剥がして分解したのち、複数の偽造品を作製するという偽造を行おうとした場合、剥離時に改ざん防止模様が壊れ、かつ、壊れた改ざん防止模様を復元することは非常に困難であることから、偽造抑止力に優れた改ざん防止用紙となる。 In addition, the tamper-proof pattern has at least a part of the paper surface that differs in the depth direction, so that a single genuine product, as described above, is separated into a plurality of sheets and then disassembled, and then a plurality of counterfeits. If you try to forge to make a product, the tamper-proof pattern is broken at the time of peeling, and it is very difficult to restore the broken tamper-proof pattern. Become.
本発明は、以下に述べる発明を実施するための形態に限定されるものではなく、特許請求の範囲記載における技術的思想の範囲内であれば、その他の色々な実施の形態が含まれる。 The present invention is not limited to the embodiments for carrying out the invention described below, and includes various other embodiments within the scope of the technical idea described in the scope of claims.
図１は、本発明の改ざん防止用紙（Ｓ１）の平面図である。改ざん防止用紙（Ｓ１）の領域（Ｚ）には、図１（ａ）に示すように、反射光下では表面からは視認することができないが、図１（ｂ）に示すように、透過光下で視認可能な改ざん防止模様（１）が付与されている。 FIG. 1 is a plan view of a tamper-proof sheet (S1) according to the present invention. As shown in FIG. 1A, the region (Z) of the falsification preventing paper (S1) cannot be viewed from the surface under reflected light, but the transmitted light as shown in FIG. 1B. A tamper-proof pattern (1) that is visible below is provided.
図２は、改ざん防止用紙（Ｓ１）の図１におけるＹ−Ｙ’断面図である。改ざん防止用紙（Ｓ１）は、繊維から成る単層の用紙における紙層（Ｑ）内の一部に、改ざん防止模様（１）が形成されている。改ざん防止模様（１）は、拡大図に示すように、少なくとも一種類の改ざん防止材料（２）から成る。なお、本発明において単層とは、抄紙機上の長網部における一つの網で形成された用紙の層のことをいう。 FIG. 2 is a cross-sectional view of the falsification preventing sheet (S1) taken along the line Y-Y 'in FIG. In the falsification preventing paper (S1), a falsification preventing pattern (1) is formed in a part of the paper layer (Q) of the single-layer paper made of fibers. As shown in the enlarged view, the alteration prevention pattern (1) is made of at least one type of alteration prevention material (2). In the present invention, the term “single layer” refers to a paper layer formed by a single net in a long net on a paper machine.
用紙を形成する繊維は、特に限定されるものではなく、木材や非木材などの植物繊維を原料とするＫＰ、ＳＰ等の化学パルプ、ＧＰ、ＴＭＰ、ＣＴＭＰ等の機械パルプ、古紙再生パルプ等のパルプを適宜選択して使用できるが、木材や非木材繊維から成る紙、水素結合を形成できる官能基を持つ合成繊維から成る合成繊維紙が好ましい。 The fibers forming the paper are not particularly limited, such as chemical pulps such as KP and SP made from plant fibers such as wood and non-wood, mechanical pulps such as GP, TMP, and CTMP, recycled paper recycled pulp, etc. Pulp can be appropriately selected and used, but paper made of wood or non-wood fibers, and synthetic fiber paper made of synthetic fibers having a functional group capable of forming hydrogen bonds are preferred.
詳細については後述するが、改ざん防止模様（１）は、改ざん防止材料（２）を水に分散させた後に、その分散液（以下「改ざん防止分散液」という。）を、抄紙機上の湿紙に、噴射流量を変動させながら噴射することで、用紙の紙層（Ｑ）に付与される。よって、用紙を、木材繊維や非木材繊維等の天然繊維や水素結合を形成できる官能基を持つ合成繊維で形成することで、水に分散させた改ざん防止材料（２）を、水素結合により紙層（Ｑ）内に強固に定着することが、可能となる。 Although details will be described later, the anti-tamper pattern (1) is obtained by dispersing the anti-tamper material (2) in water, and then dispersing the dispersion (hereinafter referred to as “tamper-preventing dispersion”) on a paper machine. The ink is applied to the paper layer (Q) of the paper by jetting the paper while changing the jet flow rate. Therefore, the paper is formed of natural fibers such as wood fibers and non-wood fibers or synthetic fibers having a functional group capable of forming hydrogen bonds, so that the anti-tampering material (2) dispersed in water is formed by hydrogen bonding. It is possible to firmly fix in the layer (Q).
なお、水素結合を形成できる官能基を持たない合成繊維から成る合成繊維紙や、水素結合をしないプラスチック繊維やガラス繊維が入った用紙であっても、改ざん防止分散液に少量のバインダー成分を配合して、改ざん防止材料（２）を紙層（Ｑ）内に定着することができれば、使用することができる。 Even if it is a synthetic fiber paper made of synthetic fibers that do not have a functional group that can form hydrogen bonds, or paper that contains plastic fibers or glass fibers that do not have hydrogen bonds, a small amount of binder component is added to the anti-tampering dispersion. If the falsification preventing material (2) can be fixed in the paper layer (Q), it can be used.
改ざん防止模様（１）は、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）に対し、少なくとも一部が深さ方向（Ｌ）に異なった領域を有する。例えば、図２において、改ざん防止模様（１）は、用紙の表面（Ｆ）に対し、ｈ１とｈ２で深さ方向に異なった領域を有している。 The tamper-prevention pattern (1) has at least part of a region in the depth direction (L) different from the surface (F) of the paper in a part of the paper layer (Q) of the single-layer paper. For example, in FIG. 2, the falsification preventing pattern (1) has different areas in the depth direction at h1 and h2 with respect to the surface (F) of the paper.
改ざん防止模様（１）を、用紙の表面（Ｆ）から全て同じ深さで形成した場合、図１６（ｃ）を用いて前述したように、一つの紙層内の剥離強度の弱い箇所で剥離され、改ざん防止模様（１）が、剥離された一方の紙層にのみ付与されることで、剥離された用紙と、異なる用紙とを貼り合わせる偽造に用いられる可能性があり、好ましくない。改ざん防止模様（１）を、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）から深さが異なる箇所を、少なくとも二箇所有して形成された場合、紙層（Ｑ）内に剥離強度の弱い箇所がなくなることで、紙層（Ｑ）のどの位置で剥離しようとしても、剥離が困難となる。 When the tamper-proof pattern (1) is formed at the same depth from the surface (F) of the paper, as described above with reference to FIG. 16 (c), it is peeled off at a place where the peel strength is weak in one paper layer. In addition, since the anti-tampering pattern (1) is applied only to one of the peeled paper layers, it may be used for counterfeiting to bond the peeled paper and a different paper, which is not preferable. When the tamper-proof pattern (1) is formed on a part of the paper layer (Q) of a single-layer paper and has at least two places having different depths from the surface (F) of the paper, the paper Since there is no portion having a low peel strength in the layer (Q), it becomes difficult to peel off at any position on the paper layer (Q).
また、用紙が剥離された場合においても、紙層（Ｑ）内において、改ざん防止模様（１）が、用紙の表面（Ｆ）から深さが異なることで、異なる用紙と貼りあわせても、改ざん防止模様（１）の平面形状及び断面形状を再現することが困難であることから、偽造防止効果が高くなる。よって、本発明においては、改ざん防止模様（１）を、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）から深さが異なる箇所を、少なくとも二箇所有して形成される必要がある。 Even when the paper is peeled off, the tamper-proof pattern (1) has a different depth from the surface (F) of the paper in the paper layer (Q). Since it is difficult to reproduce the planar shape and the cross-sectional shape of the prevention pattern (1), the forgery prevention effect is enhanced. Therefore, in the present invention, the tamper-proof pattern (1) has at least two locations having different depths from the surface (F) of the paper in a part of the paper layer (Q) in the single-layer paper. Need to be formed.
なお、図２において改ざん防止模様（１）は、Ｙ−Ｙ’断面形状が波線状となるように、用紙の表面（Ｆ）から異なる深さに付与されているが、一つの改ざん防止模様（１）内において、表面（Ｆ）から少なくとも二箇所深さがが異なる箇所を有してもよく、断面形状に特に限定はない。 In FIG. 2, the tamper-proof pattern (1) is given to different depths from the surface (F) of the paper so that the YY ′ cross-sectional shape is a wavy line. Within 1), there may be a location where the depth differs from the surface (F) by at least two locations, and the cross-sectional shape is not particularly limited.
図３及び図４は、改ざん防止模様（１）の他の断面形状を示す図である。前述した、波線状に限らず、図３（ａ）に示すように、断面形状が鋸歯状となるように形成することも、可能である。また、前述した図２及び図３（ａ）は、規則的な断面形状であったが、図３（ｂ）に示すように、一つの改ざん防止模様（１）内に、幅が異なる箇所を有していてもよい。例えば、図３（ｂ）においては、Ｅ１とＥ２で幅が異なる箇所を有している。 3 and 4 are diagrams showing other cross-sectional shapes of the anti-tampering pattern (1). Not only the wavy line shape described above but also a cross-sectional shape can be formed in a sawtooth shape as shown in FIG. Moreover, although FIG.2 and FIG.3 (a) mentioned above was regular cross-sectional shape, as shown in FIG.3 (b), the location from which a width | variety differs in one alteration prevention pattern (1). You may have. For example, in FIG.3 (b), it has a location where width differs in E1 and E2.
また、断面形状を、図３（ｃ）に示す矩形状や、一つの改ざん防止模様（１）内で、厚みの異なる箇所を有していてもよい。例えば、図３（ｃ）においては、Ｇ１とＧ２で厚みが異なる箇所を有している。 Moreover, the cross-sectional shape may have the location where thickness differs in the rectangular shape shown in FIG.3 (c), or one alteration prevention pattern (1). For example, in FIG.3 (c), it has a location where thickness differs by G1 and G2.
さらに、図４（ａ）に示すように、改ざん防止模様（１）は、Ｅ１に示す用紙の表面（Ｆ）に対し、深さ方向に異なった領域と、Ｅ２に示す深さ方向に同じ領域とを有する構成としてもよい。図４（ａ）の構成とした場合でも、一つの改ざん防止模様（１）において、表面（Ｆ）からの深さが、ｈ３とｈ４で異なっていることから、少なくとも二箇所深さがが異なる箇所を有する本発明の構成となる。 Further, as shown in FIG. 4 (a), the tamper-proof pattern (1) has different areas in the depth direction with respect to the surface (F) of the paper indicated by E1, and the same area in the depth direction indicated by E2. It is good also as a structure which has. Even in the case of the configuration shown in FIG. 4A, the depth from the surface (F) is different between h3 and h4 in one tamper-proof pattern (1), so that at least two depths are different. It becomes the structure of this invention which has a location.
また、図４（ｂ）に示すように、斜めの直線形状や、改ざん防止用紙（Ｓ１）の幅方向（Ｅ３）に対して、全体ではなく、一部（Ｅ４）に改ざん防止模様（１）を形成してもよい。 Further, as shown in FIG. 4B, the tamper-preventing pattern (1) is not part of the whole (E4) with respect to the oblique linear shape or the width direction (E3) of the tamper-preventing paper (S1). May be formed.
次に、改ざん防止模様（１）を形成する、改ざん防止材料（２）について説明する。改ざん防止材料（２）は、単層の用紙における紙層（Ｑ）内の一部に付与される、材料のことである。 Next, the falsification preventing material (2) for forming the falsification preventing pattern (1) will be described. The falsification preventing material (2) is a material applied to a part of the paper layer (Q) in the single-layer paper.
改ざん防止材料（２）には、アクリル系樹脂、エポキシ系樹脂等の樹脂、インクジェット印刷用のインク、プロセスインキ等の印刷インキ、着色繊維、蛍光繊維、ポリマー繊維、金属繊維、ナノファイバー、サーモ繊維等の繊維や、カーボン、酸化チタン、有色顔料、雲母（パール顔料）、有色蛍光顔料、無色蛍光顔料等の顔料、有色染料である機能性染料、金属粉末、金属片、金属箔、蒸着薄膜等の細片等がある。 Anti-falsification material (2) includes acrylic resin, epoxy resin, etc., ink for inkjet printing, printing ink such as process ink, colored fiber, fluorescent fiber, polymer fiber, metal fiber, nano fiber, thermo fiber Fiber, carbon, titanium oxide, colored pigment, mica (pearl pigment), pigment such as colored fluorescent pigment, colorless fluorescent pigment, functional dye that is colored dye, metal powder, metal piece, metal foil, evaporated thin film, etc. There are strips, etc.
本発明の改ざん防止材料（２）は、紙層（Ｑ）と化学結合可能な官能基を有するか及び／又は繊維で形成された紙層（Ｑ）による三次元の網目より大きい幅を有する必要がある。 The tamper-proof material (2) of the present invention needs to have a functional group capable of chemically bonding with the paper layer (Q) and / or a width larger than the three-dimensional network formed by the paper layer (Q) formed of fibers. There is.
まず、改ざん防止材料（２）が、紙層（Ｑ）と化学結合可能な官能基を有する必要について説明する。前述のとおり、紙層（Ｑ）は、繊維間の水素結合によって繊維が結合してシート状になっている。よって、改ざん防止材料（２）が、紙層（Ｑ）と化学結合の一つである水素結合可能な官能基を有することで、紙層（Ｑ）の繊維と水素結合して、紙層（Ｑ）の内部に歩留まるという理由からである。 First, the necessity for the falsification preventing material (2) to have a functional group capable of chemically bonding with the paper layer (Q) will be described. As described above, the paper layer (Q) has a sheet shape in which fibers are bonded by hydrogen bonding between the fibers. Therefore, the falsification preventing material (2) has a hydrogen bondable functional group that is one of the chemical bonds with the paper layer (Q), so that it is hydrogen bonded to the fibers of the paper layer (Q), and the paper layer ( This is because the yield is within Q).
紙層（Ｑ）と水素結合可能な官能基を有する改ざん防止材料（２）は、水酸基を持つ材料であれば、レーヨン、ポリビニルアルコール製の合成繊維等を適宜用いることが可能である。 As long as the falsification preventing material (2) having a functional group capable of hydrogen bonding with the paper layer (Q) is a material having a hydroxyl group, rayon, synthetic fiber made of polyvinyl alcohol, or the like can be appropriately used.
また、水素結合以外の化学結合としては、バインダーを用いた分子間力による結合がある。例えば、パール顔料、ポリエステル製の合成繊維、マイクロカプセル等、水素結合可能な官能基を有さない機能性材料（３）と、少量のバインダー成分を配合した機能性分散液を抄紙機上で湿紙に付与することで、紙層（Ｑ）の内部に機能性材料（３）を付与することが、可能である。 In addition, as a chemical bond other than a hydrogen bond, there is a bond by intermolecular force using a binder. For example, a functional dispersion liquid containing a functional material (3) having no functional group capable of hydrogen bonding, such as pearl pigment, polyester synthetic fiber, and microcapsule, and a small amount of a binder component is wetted on a paper machine. By applying to the paper, it is possible to apply the functional material (3) to the inside of the paper layer (Q).
次に、機能性材料（３）が、繊維で形成された紙層（Ｑ）による三次元の網目（Ｋ）より大きい幅を有する必要について説明する。図２の拡大図に示すように、本発明の用紙は、紙層（Ｑ）内で繊維が立体的に入り組んだ形状となることで、網目（Ｋ）を有する構造となる。 Next, the necessity that the functional material (3) has a width larger than the three-dimensional network (K) by the paper layer (Q) formed of fibers will be described. As shown in the enlarged view of FIG. 2, the paper of the present invention has a structure having a mesh (K) by forming a three-dimensionally complicated fiber in the paper layer (Q).
本発明の機能性材料（３）は、三次元の網目（Ｋ）の大きさ（ＫＷ）より、大きい幅を有する材料とする。機能性材料（３）が、紙層（Ｑ）による三次元の網目（Ｋ）より大きい幅を有することで、紙層（Ｑ）と化学結合可能な官能基を有していない機能性材料（３）であっても、紙層（Ｑ）の三次元の網目（Ｋ）から抜け落ちず、紙層（Ｑ）内に歩留まるという理由からである。 The functional material (3) of the present invention is a material having a width larger than the size (KW) of the three-dimensional mesh (K). The functional material (3) has a larger width than the three-dimensional network (K) of the paper layer (Q), and thus has no functional group capable of chemically bonding to the paper layer (Q) ( 3), the reason is that it does not fall out from the three-dimensional mesh (K) of the paper layer (Q) and the yield is within the paper layer (Q).
紙層（Ｑ）の三次元の網目（Ｋ）より大きい幅とは、改ざん防止材料（２）が顔料であるならば、紙層（Ｑ）の三次元の網目（Ｋ）より大きい粒子径のことをいう。紙層（Ｑ）の三次元の網目（Ｋ）より大きい粒子径を有する改ざん防止材料（２）には、例えば、網目（Ｋ）の大きさが１０μｍであるならば、金属顔料、液晶顔料等がある。 The width larger than the three-dimensional network (K) of the paper layer (Q) means that the particle size larger than the three-dimensional network (K) of the paper layer (Q) if the anti-falsification material (2) is a pigment. That means. For the anti-tampering material (2) having a particle size larger than the three-dimensional network (K) of the paper layer (Q), for example, if the size of the network (K) is 10 μm, a metal pigment, a liquid crystal pigment, etc. There is.
また、改ざん防止材料（２）が繊維であるならば、紙層（Ｑ）の三次元の網目（Ｋ）より大きい幅とは、紙層（Ｑ）の三次元の網目（Ｋ）より長い繊維長のことをいう。紙層（Ｑ）の三次元の網目（Ｋ）より長い繊維長を有する機能性材料（３）には、例えば、網目（Ｋ）の大きさが１０μｍであるならば、ＮＢＫＰ繊維、木綿繊維等がある。 If the tamper-proof material (2) is a fiber, the width larger than the three-dimensional network (K) of the paper layer (Q) means a fiber longer than the three-dimensional network (K) of the paper layer (Q). It means long. For the functional material (3) having a fiber length longer than the three-dimensional mesh (K) of the paper layer (Q), for example, if the size of the mesh (K) is 10 μm, NBKP fiber, cotton fiber, etc. There is.
さらに、改ざん防止材料（２）が細片であるならば、紙層（Ｑ）の三次元の網目（Ｋ）より大きい幅とは、紙層（Ｑ）の三次元の網目（Ｋ）より長い細片長のことをいう。紙層（Ｑ）の三次元の網目（Ｋ）より長い細片長を有する改ざん防止材料（２）には、例えば、網目（Ｋ）の大きさが１０μｍであるならば、金属細片、アルミ細片等がある。 Further, if the tamper-proof material (2) is a strip, the width larger than the three-dimensional mesh (K) of the paper layer (Q) is longer than the three-dimensional mesh (K) of the paper layer (Q). The length of a strip. For the tamper-proof material (2) having a strip length longer than the three-dimensional mesh (K) of the paper layer (Q), for example, if the mesh (K) has a size of 10 μm, a metal strip, an aluminum strip There is a piece.
以上の理由から、紙層（Ｑ）内に改ざん防止材料（２）を付与するために、改ざん防止材料（２）は、紙層（Ｑ）と化学結合可能な官能基を有するか及び／又は繊維で形成された紙層（Ｑ）における三次元的な網目より大きい幅を有する必要がある。 For the above reasons, in order to provide the anti-tampering material (2) in the paper layer (Q), the anti-tampering material (2) has a functional group capable of chemically bonding with the paper layer (Q) and / or It is necessary to have a width larger than the three-dimensional network in the paper layer (Q) formed of fibers.
詳細については後述するが、改ざん防止材料（２）は、改ざん防止材料（２）を水に分散させたのち、分散剤や水溶性高分子、改ざん防止材料（２）の分散状態を阻害しない水溶性液体、有機溶媒、あるいは粉末や微粒子等を加えることで作製した改ざん防止分散液を抄紙機上で湿紙に付与することで付与することが可能である。 Although details will be described later, the anti-tampering material (2) is a water-soluble material that does not inhibit the dispersion state of the dispersant, the water-soluble polymer, and the anti-tampering material (2) after the anti-tampering material (2) is dispersed in water. It can be applied by applying an anti-tampering dispersion prepared by adding a functional liquid, an organic solvent, powder or fine particles to a wet paper on a paper machine.
改ざん防止分散液は、改ざん防止材料（２）同士が、すぐに水素結合で再結合しない程度の濃度が必要であり、固形分濃度０．１〜３％程度での使用が望ましい。本発明における固形分濃度とは、改ざん防止分散液中に含まれる改ざん防止材料（２）の割合のことである。ただし、改ざん防止材料（２）を強撹拌又は分散剤を添加することで、改ざん防止材料（２）同士を再分離させることができれば、３〜３５％程度でも問題はない。 The anti-tampering dispersion liquid needs to have a concentration such that the anti-tampering materials (2) do not immediately recombine with each other by hydrogen bonding, and is preferably used at a solid content concentration of about 0.1 to 3%. The solid content concentration in the present invention is a ratio of the anti-tampering material (2) contained in the anti-tampering dispersion. However, if anti-falsification material (2) can be re-separated by adding strong stirring or dispersing agent to anti-falsification material (2), there is no problem even if it is about 3 to 35%.
これは、固形分濃度が３５％以上の高濃度になると、撹拌又は分散剤を加えるのみでは、改ざん防止材料（２）同士の再結合を抑止できず、再解繊処理が必要となる可能性があるためであり、逆に、固形分濃度が０．１％以下の低濃度では、用紙への付与及び乾燥段階において、水分過多による用紙の膨潤等を促進する可能性があるためである。ただし、それらの問題が他の手段で回避できれば特に制限はない。 This means that when the solid content concentration is 35% or higher, the rebonding between the anti-tampering materials (2) cannot be suppressed only by adding a stirring or dispersing agent, and re-defibration treatment may be necessary. On the contrary, if the solid content is a low concentration of 0.1% or less, there is a possibility of promoting swelling of the paper due to excessive moisture in the application and drying stages of the paper. However, there is no particular limitation as long as these problems can be avoided by other means.
改ざん防止分散液を付与する量は、付与する方式によって異なるが、乾燥後の改ざん防止材料（２）の固形分量が、０．０１ｇ／ｍ２以上と成るように調製する必要がある。固形分量が０．０１ｇ／ｍ２未満であると、可視光による透過光下において、改ざん防止分散液の付与部が肉眼で視認しづらくなり、好ましくない。また、付与方式によっては、一回での付与限界量が当該量以下の場合もあるが、この場合は数回付与を繰り返し、目標の固形分量を得ればよい。改ざん防止材料（２）は、改ざん防止分散液を湿紙の状態の紙層（Ｑ）内に付与した後、乾燥させることで、本発明の改ざん防止用紙（Ｓ１）が作製される。 The amount of the anti-tampering dispersion applied varies depending on the method of application, but it is necessary to prepare so that the solid content of the anti-tampering material (2) after drying is 0.01 g / m 2 or more. When the solid content is less than 0.01 g / m 2, it is difficult to visually recognize the application portion of the anti-tampering dispersion under visible light transmission, which is not preferable. Depending on the application method, the application limit amount at one time may be equal to or less than the amount, but in this case, application may be repeated several times to obtain a target solid content. The anti-tampering material (2) is applied to the anti-tampering dispersion in the wet paper layer (Q) and then dried to produce the anti-tamper paper (S1) of the present invention.
いずれの断面形状においも、単層用紙の表面（Ｆ）から異なる深さに改ざん防止模様（１）を形成することで、層間同士が剥がれるということがなくなり、仮に真正品の表裏を剥がして複数枚に分解したのち、その分解した個々の紙層を、他の用紙に貼り合わせることで一部を真正品とした複数の偽造品を作製しようとした場合、厚み方向の異なる位置に改ざん防止材料（２）を付与することで形成された改ざん防止模様（１）が破断することから、偽造が困難となる。 In any cross-sectional shape, the anti-falsification pattern (1) is formed at different depths from the surface (F) of the single-layer paper, so that the layers are not peeled off. After disassembling into sheets, if the individual paper layers that have been disassembled are bonded to other papers to create multiple counterfeit products, some of which are genuine, anti-tampering materials at different positions in the thickness direction Since the anti-tampering pattern (1) formed by applying (2) breaks, forgery becomes difficult.
次に、改ざん防止用紙の他の形態について、図５に示す、本発明の第二の形態の改ざん防止用紙（Ｓ２）の平面図を用いて説明をする。前述した改ざん防止模様（１）は、図１（ｂ）に示したように、透過光下では、用紙の表面（Ｆ）から実線状に視認される構成であったが、図５（ａ）に示す、改ざん防止用紙（Ｓ２）は、反射光下では視認することができないが、図５（ｂ）に示すように、透過光下では、用紙の表面（Ｆ）から破線状に視認可能となるように、改ざん防止模様（１）が付与されている。 Next, another form of the falsification preventing paper will be described with reference to the plan view of the falsification preventing paper (S2) of the second aspect of the present invention shown in FIG. As shown in FIG. 1B, the tamper-preventing pattern (1) described above is configured to be viewed as a solid line from the surface (F) of the paper under transmitted light. The tamper-proof sheet (S2) shown in FIG. 5 cannot be viewed under reflected light, but as shown in FIG. 5B, it can be viewed as a broken line from the surface (F) of the sheet under transmitted light. As shown, an alteration prevention pattern (1) is given.
図６は、改ざん防止用紙（Ｓ２）の図５（ａ）のＹ−Ｙ’断面図を示す。なお、紙層（Ｑ）及び用いる改ざん防止材料（２）は、前述した改ざん防止用紙（Ｓ１）と同様であることから、説明を省略する。図６においては、改ざん防止材料（２）を、間隔（Ｐ２）を有して付与することで、紙層（Ｑ）内に改ざん防止模様（１）が付与されている。改ざん防止模様（１）は、間隔（Ｐ２）を有している場合においても、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）から、深さが異なる箇所を、少なくとも二箇所有して形成されている。例えば、図６においては、表面（Ｆ）から改ざん防止模様（１）までの深さが、ｈ１とｈ２で異なっている。 FIG. 6 is a cross-sectional view taken along line Y-Y ′ of FIG. Note that the paper layer (Q) and the anti-tampering material (2) to be used are the same as the above-described anti-tampering paper (S1), and thus description thereof is omitted. In FIG. 6, the anti-tampering pattern (1) is provided in the paper layer (Q) by applying the anti-tampering material (2) with the interval (P2). Even when the tamper-proof pattern (1) has a gap (P2), a part of the single-layer paper within the paper layer (Q) has a different depth from the surface (F) of the paper. Are formed at least in two places. For example, in FIG. 6, the depth from the surface (F) to the tamper-resistant pattern (1) is different between h1 and h2.
図７は、間隔（Ｐ２）を有する改ざん防止模様（１）の他の断面形状を示す図である。前述した、図６において、間隔（Ｐ２）は一定間隔であったが、図７（ａ）に示すように、一つの改ざん防止模様（１）内で間隔を、Ｐ３とＰ４のように、異ならせて形成したり、断面形状を、斜めの波線状となるように形成したりすることも、可能である。 FIG. 7 is a diagram showing another cross-sectional shape of the tamper-resistant pattern (1) having the interval (P2). In FIG. 6 described above, the interval (P2) is a constant interval, but as shown in FIG. 7 (a), the intervals in the tamper-resistant pattern (1) are different as in P3 and P4. It is also possible to form the cross section or form the cross-sectional shape so as to be an oblique wavy line.
また、波線状の断面形状に限らず、紙層（Ｑ）内に、用紙の表面（Ｆ）から、深さが異なる箇所を、少なくとも二箇所有して形成されるなら、図７（ｂ）に示すように、
断面形状が鋸歯状となるように形成することも、可能である。
In addition, the cross-sectional shape is not limited to a wavy line shape, and if the paper layer (Q) is formed to have at least two places having different depths from the surface (F) of the paper, FIG. As shown in
It is also possible to form the cross-sectional shape to be a sawtooth shape.
さらに、図７（ｃ）に示すように、一つの改ざん防止模様（１）内において、間隔（Ｐ２）を有する箇所（１ｂ）と、有さない箇所（１ａ）を形成してもよい。さらには、図７（ｄ）に示すように、一つの改ざん防止模様（１）内において、平面状の間隔（Ｐ５）に加え、紙層（Ｑ）内の厚みに対し、改ざん防止材料（２）が付与されていない空白部（Ｋ）を有する構成としてもよい。 Furthermore, as shown in FIG.7 (c), you may form the location (1b) which has the space | interval (P2), and the location (1a) which does not have in one alteration prevention pattern (1). Furthermore, as shown in FIG. 7 (d), in one alteration prevention pattern (1), in addition to the planar interval (P5), the alteration prevention material (2 It is good also as a structure which has the blank part (K) to which () is not provided.
第二の形態の改ざん防止用紙（Ｓ２）とすることで、改ざん防止材料（２）を付与した箇所と付与していない箇所では、剥離強度に差が生じることから、仮に剥離をして用紙を改竄しようとした場合、図２の構成と比べ、一つの改ざん防止模様（１）内で複数箇所が破断することから、より復元が困難となり、さらに剥離対策が向上した用紙を形成することが、可能となる。 By using the anti-tamper paper (S2) of the second form, there is a difference in the peel strength between the location where the anti-tamper material (2) is applied and the location where the anti-tamper material (2) is not applied. When trying to tamper, compared to the configuration of FIG. 2, a plurality of locations in one tamper-proof pattern (1) breaks, making it more difficult to restore and forming a sheet with improved anti-peeling properties. It becomes possible.
また、他のメリットとして、間隔（Ｐ２）を有して付与することで、間隔（Ｐ２）を有さずに実線状に付与した場合と比べて、紙層（Ｑ）内に付与する改ざん防止材料（２）の量が少なくて済む。よって、実線状に付与した場合と比べ、コストを削減することが、可能となる。 In addition, as another merit, by providing with the interval (P2), tampering prevention provided in the paper layer (Q) compared to the case of providing with a solid line without the interval (P2). The amount of material (2) is small. Therefore, the cost can be reduced as compared with the case where the solid line is used.
次に、改ざん防止用紙の他の形態について、図８に示す、本発明の第三の形態の改ざん防止用紙（Ｓ３）の平面図を用いて説明をする。図８に示す、改ざん防止用紙（Ｓ３）の領域（Ｚ）には、前述した図１（ａ）及び図６（ａ）とは異なり、反射光下では改ざん防止模様（１）の一部が視認可能となるように、改ざん防止材料（２）が付与されている。 Next, another form of the falsification preventing paper will be described with reference to the plan view of the falsification preventing paper (S3) of the third aspect of the present invention shown in FIG. In the region (Z) of the anti-tamper paper (S3) shown in FIG. 8, unlike the above-described FIGS. 1 (a) and 6 (a), a part of the anti-tamper pattern (1) is present under reflected light. An anti-falsification material (2) is provided so as to be visible.
図９は、改ざん防止用紙（Ｓ３）の図９（ａ）のＹ−Ｙ’断面図を示す。前述した改ざん防止用紙（Ｓ１）は、改ざん防止模様（１）は、全て紙層（Ｑ）内に付与されていたが、図９の改ざん防止用紙（Ｓ３）では、改ざん防止模様（１）の一部が、用紙の少なくとも一方の面に表出させて成る。図９においては、一例として、改ざん防止模様（１）の一部が、用紙の表面（Ｆ）に表出している。なお、紙層（Ｑ）及び用いる改ざん防止材料（２）は、前述した改ざん防止用紙（Ｓ１）と同様であることから、説明を省略する。 FIG. 9 is a cross-sectional view of the tamper-proof sheet (S3) taken along the line Y-Y ′ of FIG. In the falsification preventing paper (S1) described above, the falsification preventing pattern (1) is all provided in the paper layer (Q). However, the falsification preventing paper (S3) in FIG. A part is formed on at least one side of the sheet. In FIG. 9, as an example, a part of the tamper-proof pattern (1) is exposed on the surface (F) of the paper. Note that the paper layer (Q) and the anti-tampering material (2) to be used are the same as the above-described anti-tampering paper (S1), and thus description thereof is omitted.
改ざん防止模様（１）の一部を、用紙の少なくとも一方の面に表出させて成る構成とすることで、前述した全て紙層（Ｑ）内に形成された構成と比べ、用紙を剥離しようとした場合、用紙表面（Ｆ）に表出した箇所で、紙層（Ｑ）が破壊されるため、改ざん防止模様（１）を剥離することが、より困難となる。 By adopting a structure in which a part of the tamper-proof pattern (1) is exposed on at least one side of the paper, the paper will be peeled off compared to the structure formed in the paper layer (Q) described above. In this case, since the paper layer (Q) is destroyed at the position exposed on the paper surface (F), it becomes more difficult to peel off the tamper-proof pattern (1).
なお、図９においては、改ざん防止模様（１）の一部が、用紙の表面（Ｆ）に表出した構成であるが、裏面（Ｂ）に表出した構成とすることも、可能である。さらには、表面（Ｆ）及び裏面（Ｂ）に表出した構成とすることも、可能である。なお、用紙表面は、深さ方向ゼロとする。 In FIG. 9, a part of the tamper-proof pattern (1) is shown on the front surface (F) of the paper, but it is also possible to use a configuration shown on the back surface (B). . Furthermore, it is also possible to have a structure exposed on the front surface (F) and the back surface (B). The sheet surface is zero in the depth direction.
改ざん防止模様（１）の一部を、用紙の少なくとも一方の面に表出させて成る構成とした場合、表出した面と同一の面から、用紙を剥離しようとした際には、前述のとおり、用紙表面（Ｆ）に表出した箇所で、紙層（Ｑ）が破壊されるため、改ざん防止模様（１）を剥離することが、困難となる。 When a part of the tamper-proof pattern (1) is exposed on at least one side of the paper, when the paper is peeled from the same side as the exposed surface, As described above, since the paper layer (Q) is broken at the place exposed on the paper surface (F), it is difficult to peel off the tamper-proof pattern (1).
しかしながら、表出した面と異なる面から、用紙を剥離しようとした際には、紙層（Ｑ）内において、改ざん防止模様（１）を有さない領域が存在し、その箇所で剥離されてしまう恐れがある。そこで、用紙の表面（Ｆ）及び裏面（Ｂ）に表出した構成とすることで、紙層（Ｑ）内のどこで剥離しても、必ずどちらかの面に表出した部分で、改ざん防止模様（１）が破壊される構成となる。 However, when the paper is to be peeled from a surface different from the exposed surface, there is an area in the paper layer (Q) that does not have the tamper-proof pattern (1) and is peeled off at that location. There is a risk. Therefore, by adopting a structure that is exposed on the front surface (F) and back surface (B) of the paper, no matter where it peels in the paper layer (Q), it always prevents the falsification from appearing on either side. The pattern (1) is destroyed.
なお、改ざん防止模様（１）の形状については、単層の紙層（Ｑ）内に有意味情報として付与してもよく、特に限定はない。図１０は、改ざん防止模様（１）の他の形状を示す平面図である。図１０（ａ）に示すように、改ざん防止模様（１）は、複数の帯状として形成してもよい。また、図１０（ｂ）に示すように、図柄や、図１０（ｃ）に示すように文字としてもよい。 In addition, about the shape of a tamper-proof pattern (1), you may provide as meaningful information in a single layer paper layer (Q), and there is no limitation in particular. FIG. 10 is a plan view showing another shape of the alteration prevention pattern (1). As shown to Fig.10 (a), you may form the tamper-proof pattern (1) as a some strip | belt shape. Moreover, as shown in FIG.10 (b), it is good also as a character as shown in a design or FIG.10 (c).
さらに、図１については、改ざん防止用紙（Ｓ１）の一部に改ざん防止模様（１）を形成していたが、図１０（ｄ）及び図１０（ｅ）に示すように、改ざん防止用紙（Ｓ１）の全面に改ざん防止模様（１）を形成することも可能である。 Further, in FIG. 1, the anti-tamper pattern (1) is formed on a part of the anti-tamper paper (S1), but as shown in FIGS. 10 (d) and 10 (e), the anti-tamper paper ( It is also possible to form a tamper-proof pattern (1) on the entire surface of S1).
なお、改ざん防止用紙（Ｓ１）は、単層構造で説明したが、単層の紙層（Ｑ）内に改ざん防止材料（２）が付与されてもよく、その単層構造を、多層紙の一層とする構成とすることも可能である。 Although the tamper-proof paper (S1) has been described with a single-layer structure, the anti-tamper material (2) may be provided in the single-layer paper layer (Q). A one-layer configuration is also possible.
次に、図１から図９に示した、改ざん防止用紙（Ｓ１、Ｓ２、Ｓ３）の作製方法について、その手順を示した図１１のフローチャートと、図１２の示す、改ざん防止用紙（Ｓ、Ｓ２ 、Ｓ３）を作製する長網抄紙機（Ｍ）の模式図を用いて説明する。 Next, regarding the method for producing the falsification preventing paper (S1, S2, S3) shown in FIG. 1 to FIG. 9, the flowchart of FIG. 11 showing the procedure and the falsification preventing paper (S, S2) shown in FIG. , S3) will be described with reference to a schematic diagram of a long paper machine (M).
長網抄紙機（Ｍ）は、少なくとも、準備部（３）、ワイヤー部（４）、プレス部（５）、乾燥部（６）、カレンダ部（７）、リール部（８）を有し、まず、準備部（３）において、用紙の原料である紙料（Ｗ）内の繊維を分散させたのち、ワイヤー部（４）において、紙料（Ｗ）をワイヤー（４ａ）の上面に供給したのち、シート状の湿紙（９）を形成する。 The long net paper machine (M) has at least a preparation unit (3), a wire unit (4), a press unit (5), a drying unit (6), a calendar unit (7), and a reel unit (8). First, after the fibers in the stock (W), which is the raw material of the paper, were dispersed in the preparation section (3), the stock (W) was supplied to the upper surface of the wire (4a) in the wire section (4). After that, a sheet-like wet paper (9) is formed.
次に、プレス部（５）において、湿紙（９）に対して圧力をかけて脱水し、乾燥部（６）で脱水後の湿紙（９）を乾燥させたのち、最後に、カレンダ部（７）において、カレンダロール（７ａ）の間を通し、圧力をかけて用紙表面を平滑にし、用紙が完成する。完成した用紙は、リール部（８）により巻き取られたのち、次工程に送付する。 Next, in the press section (5), the wet paper web (9) is dehydrated by applying pressure, and after the dewatered wet paper web (9) is dried in the drying section (6), finally, the calender section In (7), the paper roll is smoothed by passing between the calender rolls (7a) and applying pressure to complete the paper. The completed paper is taken up by the reel unit (8) and then sent to the next process.
本発明の改ざん防止用紙（Ｓ１、Ｓ２、Ｓ３）の作製方法は、用紙の表面から異なる深さに改ざん防止模様（１）を形成する為に、二点特徴点がある。一点目は、水分量調整工程（ＳＴ１）として、改ざん防止材料（２）を湿紙（９）内の所望の位置に定着させるために、湿紙（９）の水分量を調整する点であり、二点目は、ノズル噴射流量調整工程（ＳＴ２）として、改ざん防止模様（１）を形成する改ざん防止材料（２）を分散した液体を、ノズルの噴射流量を変動させながら湿紙（９）に付与する点である。 The method for producing the tamper-proof paper (S1, S2, S3) of the present invention has two feature points in order to form the tamper-proof pattern (1) at different depths from the surface of the paper. The first point is to adjust the moisture content of the wet paper (9) in order to fix the tamper-proof material (2) at a desired position in the wet paper (9) as the moisture content adjusting step (ST1). Second, as a nozzle injection flow rate adjustment step (ST2), a wet paper (9) with a liquid in which the anti-tampering material (2) forming the anti-tamper pattern (1) is dispersed while changing the nozzle injection flow rate. It is a point given to.
まず、一点目の特徴点である、水分量調整工程（ＳＴ１）について説明する。図１３（ａ）は、水分量調整工程（ＳＴ１）を示す模式図であり、長網抄紙機（Ｍ）のワイヤー部（４）における、ワイヤー（４ａ）上に湿紙（９）の水分量を調整する。 First, the water content adjustment step (ST1), which is the first feature point, will be described. Fig.13 (a) is a schematic diagram which shows a moisture content adjustment process (ST1), and the moisture content of the wet paper (9) on the wire (4a) in the wire part (4) of the long net paper machine (M). Adjust.
本発明においては、湿紙（９）に対して、複数の改ざん防止材料（２）を分散させた液体を、ノズル噴射により湿紙（９）内部に付与したのち、付与後の改ざん防止材料（２）の上に、湿紙（９）を形成する紙料（Ｗ）が覆いかぶさることで、改ざん防止模様（１）を形成している。 In the present invention, a liquid in which a plurality of anti-tampering materials (2) are dispersed in the wet paper (9) is applied to the inside of the wet paper (9) by nozzle injection, and then the anti-tamper material ( The tamper-proof pattern (1) is formed by covering the material (W) forming the wet paper (9) over 2).
改ざん防止分散液（Ｊ）を付与した直後の湿紙（９）の表面（Ｆ）は、付与した箇所にライン状の跡が残るが、湿紙（９）の水分量を調整することで、そのライン状の跡の上に湿紙（９）を形成する紙料（Ｗ）が流動して、覆いかぶさったのち、表面張力の作用により表面（Ｆ）が平らとなることで、図１３（ｄ）に示すように、改ざん防止分散液（Ｊ）を湿紙（９）の紙層（Ｑ）内に付与することが可能となる。 The surface (F) of the wet paper (9) immediately after application of the anti-tampering dispersion (J) remains a line-like mark at the applied site, but by adjusting the moisture content of the wet paper (9), After the stock (W) forming the wet paper (9) flows on the line-shaped trace and covers it, the surface (F) is flattened by the action of the surface tension. As shown in d), the anti-tampering dispersion (J) can be applied to the paper layer (Q) of the wet paper (9).
湿紙（９）の水分量が多いと、紙層（Ｑ）を形成する繊維及び改ざん防止材料（２）の流動性が高いことに起因し、付与後の改ざん防止材料（２）が、湿紙（９）の内部に留まらず、湿紙（９）全体に拡散するか、又は全て湿紙（９）を通過し、ワイヤー（４ａ）の上に留まってしまう。よって、紙層（Ｑ）内の所望の位置に改ざん防止材料（２）を付与することが不可能となる。 When the moisture content of the wet paper (9) is large, the fibers forming the paper layer (Q) and the anti-tampering material (2) have high fluidity. It does not stay inside the paper (9) but diffuses throughout the wet paper (9) or passes through the wet paper (9) and stays on the wire (4a). Therefore, it becomes impossible to apply the falsification preventing material (2) to a desired position in the paper layer (Q).
一方、湿紙（９）の水分量が少ない場合、改ざん防止材料（２）を付与後、紙層（Ｑ）を形成する繊維の流動性が低いことに起因し、付与後の改ざん防止材料（２）の上に、湿紙（９）を形成する紙料（Ｗ）が流動せず、改ざん防止材料（２）が全て紙層（Ｑ）上に表出したままとなり、紙層（Ｑ）内に改ざん防止材料（２）を付与できない。よって、改ざん防止材料（２）を付与する前に、湿紙（９）の水分量を調節しておく必要がある。 On the other hand, when the moisture content of the wet paper (9) is small, the anti-tampering material (2) after application is given, and the fluidity of the fibers forming the paper layer (Q) is low. On top of 2), the stock (W) forming the wet paper (9) does not flow, and all the anti-tampering materials (2) remain exposed on the paper layer (Q), and the paper layer (Q) The anti-tampering material (2) cannot be provided inside. Therefore, it is necessary to adjust the moisture content of the wet paper (9) before applying the anti-tampering material (2).
湿紙（９）の水分量は、付与する改ざん防止材料（２）の種類や大きさ、また、紙層（Ｑ）を形成する繊維の種類や繊維長等に併せて、湿紙（９）に対し、改ざん防止材料（２）を分散させた液体が、ノズル噴射により湿紙（９）内部に付与したのち、付与後の改ざん防止材料（２）の上に、湿紙（９）を形成する紙料（Ｗ）が流動して、覆いかぶさることが可能となるように、適宜調整するが、本発明においては、湿紙（９）の水分量は、含水率８０〜９７％の範囲とすることが、好ましい。 The moisture content of the wet paper (9) depends on the type and size of the anti-tampering material (2) to be applied, the type of fiber forming the paper layer (Q), the fiber length, etc. On the other hand, after the liquid in which the anti-tampering material (2) is dispersed is applied to the inside of the wet paper (9) by nozzle injection, the wet paper (9) is formed on the anti-tampering material (2) after the application. The paper stock (W) to be flowed is adjusted as appropriate so that it can be covered. In the present invention, the moisture content of the wet paper (9) is in the range of moisture content of 80 to 97%. It is preferable to do.
湿紙（９）の含水率が８０％未満となった場合、前述した湿紙（９）の水分量が少ない場合と、同様の問題が生じる。また、含水率が９７％を超えた場合、前述した湿紙（９）の水分量が多い場合と、同様の問題が生じる。 When the moisture content of the wet paper (9) is less than 80%, the same problem occurs as when the moisture content of the wet paper (9) is small. Further, when the moisture content exceeds 97%, the same problem as that occurs when the moisture content of the wet paper (9) is large.
なお、図８及び図９に示した改ざん防止用紙（Ｓ３）は、改ざん防止模様（１）の一部が、用紙の一方の面に表出させて成る構成である。よって、湿紙（９）に対し、改ざん防止材料（２）を分散させた液体が、ノズル噴射により湿紙（９）内部に付与したのち、付与後の改ざん防止材料（２）の上に、湿紙（９）を形成する紙料（Ｗ）が流動して、全て覆いかぶさる必要はなく、少なくとも一部が覆いかぶさればよい。よって、その際の湿紙（９）の水分量は、前述した含水率より若干（１％程度）多くすることが、可能である。 The tamper-proof paper (S3) shown in FIGS. 8 and 9 has a configuration in which a part of the tamper-proof pattern (1) is exposed on one side of the paper. Therefore, after the liquid in which the anti-falsification material (2) is dispersed in the wet paper (9) is applied to the inside of the wet paper (9) by nozzle injection, on the anti-falsification material (2) after the application, It is not necessary for the stock (W) forming the wet paper (9) to flow and be entirely covered, and at least a part of it may be covered. Therefore, the moisture content of the wet paper (9) at that time can be slightly increased (about 1%) from the moisture content described above.
湿紙（９）の水分量の調整は、脱水により行う。具体的には、ワイヤー（４ａ）上の湿紙（９）は、ワイヤー（４ａ）の下のテーブルロール（４ｂ）により発生するバキューム圧により脱水する。なお、脱水は、テーブルロール（４ｂ）と併せて、サクションボックス等の真空装置を併設したのち、真空装置を用いて強制脱水を行うことも、可能である。 The moisture content of the wet paper (9) is adjusted by dehydration. Specifically, the wet paper (9) on the wire (4a) is dehydrated by the vacuum pressure generated by the table roll (4b) under the wire (4a). In addition, dehydration can be performed by using a vacuum apparatus after a vacuum apparatus such as a suction box is provided together with the table roll (4b).
次に、二点目の特徴点である、ノズル噴射流量調整工程（ＳＴ２）について説明する。図１３（ｂ）は、ノズル噴射流量調整工程（ＳＴ２）を示す模式図である。ノズル（１０）は、少なくとも一つの孔又はスリットを有する、改ざん防止材料（２）を分散させた溶液を噴射するための装置であり、水分量調整工程（ＳＴ１）後のワイヤー（４ａ）上に設ける。 Next, the nozzle injection flow rate adjustment step (ST2), which is the second feature point, will be described. FIG. 13B is a schematic diagram showing the nozzle injection flow rate adjustment step (ST2). The nozzle (10) is an apparatus for injecting a solution in which the anti-tampering material (2) is dispersed, having at least one hole or slit, and is disposed on the wire (4a) after the moisture amount adjusting step (ST1). Provide.
本発明においては、図１から図９に示したように、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）から異なる深さに改ざん防止模様（１）が付与されている。これは、湿紙（９）に対し、ノズル（１０）の噴射流量を変動させながら、改ざん防止分散液（Ｊ）を付与しているからである。 In the present invention, as shown in FIGS. 1 to 9, a tamper-proof pattern (1) is formed in a part of the paper layer (Q) of a single-layer paper at different depths from the surface (F) of the paper. Has been granted. This is because the anti-tampering dispersion liquid (J) is applied to the wet paper (9) while changing the injection flow rate of the nozzle (10).
よって、改ざん防止模様（１）を、用紙の表面（Ｆ）から異なる深さに形成するために、あらかじめ、ノズル（１０）の噴射流量の下限値、中間値及び上限値を設定する必要がある。 Therefore, in order to form the alteration prevention pattern (1) at different depths from the surface (F) of the paper, it is necessary to set the lower limit value, the intermediate value, and the upper limit value of the injection flow rate of the nozzle (10) in advance. .
噴射流量の下限値とは、改ざん防止分散液（Ｊ）が、湿紙（９）の紙層（Ｑ）内に付与されず表面（Ｆ）上に付与される噴射流量のことであり、噴射流量の中間値とは、改ざん防止分散液（Ｊ）が、湿紙（９）の紙層（Ｑ）内の厚み方向における中間に付与される噴射流量のことであり、噴射流量の上限値とは、改ざん防止分散液（Ｊ）が、湿紙（９）紙層（Ｑ）内に付与されず裏面（Ｂ）上に付与される噴射流量のことである。 The lower limit value of the injection flow rate is the injection flow rate at which the anti-tampering dispersion (J) is applied to the surface (F) without being applied to the paper layer (Q) of the wet paper (9). The intermediate value of the flow rate is an injection flow rate at which the anti-tampering dispersion liquid (J) is applied in the middle in the thickness direction in the paper layer (Q) of the wet paper (9). Is the spray flow rate that the anti-tampering dispersion (J) is applied on the back surface (B) without being applied in the wet paper (9) paper layer (Q).
湿紙（９）に対し、ノズル（１０）の噴射流量の下限値、中間値及び上限値の範囲内で、変動させながら、改ざん防止分散液（Ｊ）を付与することで、改ざん防止模様（１）を、用紙の表面（Ｆ）から異なる深さに形成することが、可能となる。 By applying the anti-tampering dispersion (J) to the wet paper (9) within the range of the lower limit value, intermediate value and upper limit value of the injection flow rate of the nozzle (10), the anti-tamper pattern ( 1) can be formed at different depths from the surface (F) of the paper.
噴射流量の下限値、中間値及び上限値は、水分量調整工程（ＳＴ１）後の湿紙（９）の坪量及び水分量と、長網抄紙機（Ｍ）の抄速により適宜調整するが、例えば、水分量調整工程（ＳＴ１）後の湿紙（９）の坪量が８５ｇ／ｍ２、水分量が９５％で、長網抄紙機（Ｍ）の抄速が２７ｍ／ｍｉｎとした場合、噴射流量の下限値は、２００ｍｌ／ｍｉｎとなる。また、噴射流量の中間値は、５００ｍｌ／ｍｉｎとなり、噴射流量の上限値は、８００ｍｌ／ｍｉｎとなる。 The lower limit value, the intermediate value, and the upper limit value of the injection flow rate are appropriately adjusted according to the basis weight and moisture content of the wet paper (9) after the moisture content adjusting step (ST1) and the paper making speed of the long net paper machine (M). For example, when the basis weight of the wet paper (9) after the water content adjusting step (ST1) is 85 g / m 2 , the water content is 95%, and the papermaking speed of the long paper machine (M) is 27 m / min. The lower limit value of the injection flow rate is 200 ml / min. Further, the intermediate value of the injection flow rate is 500 ml / min, and the upper limit value of the injection flow rate is 800 ml / min.
なお、ノズル（１０）の噴射流量は、前述した、水分量調整工程（ＳＴ１）後の湿紙（９）の坪量が８５ｇ／ｍ２、含水率が９５％で、長網抄紙機（Ｍ）の抄速が２７ｍ／ｍｉｎとした場合の値である、噴射流量は５００ｍｌ／ｍｉｎを基準値とし、坪量、含水率及び抄速の変動により、適宜調整する。 The jet flow rate of the nozzle (10) was as described above, the basis weight of the wet paper (9) after the water content adjusting step (ST1) was 85 g / m 2 , the water content was 95%, and the long net paper machine (M The injection flow rate, which is a value when the paper making speed of 27) is 27 m / min, is appropriately adjusted according to fluctuations in the basis weight, water content, and paper making speed, with a reference value of 500 ml / min.
例えば、湿紙（９）の坪量が８５ｇ／ｍ２より大きい場合、噴射流量は基準値より大きくする。坪量が大きい場合、湿紙（９）内の繊維量が多くなるため、基準値では、改ざん防止材料（２）が紙層（Ｑ）内に入らない。よって、噴射流量を大きくし、高圧で付与する必要がある。 For example, when the basis weight of the wet paper web (9) is larger than 85 g / m 2 , the jet flow rate is made larger than the reference value. When the basis weight is large, the amount of fibers in the wet paper (9) increases, so that the tamper-proof material (2) does not enter the paper layer (Q) at the reference value. Therefore, it is necessary to increase the injection flow rate and apply it at a high pressure.
また、長網抄紙機（Ｍ）の抄速が２７ｍ／ｍｉｎより早い場合についても、噴射流量は基準値より大きくする。抄速が早い場合、紙層（Ｑ）内に入る前に、ワイヤー（４ａ）上の湿紙（９）が動き、改ざん防止材料（２）は紙層（Ｑ）に入らずに、紙層（Ｑ）の表面（Ｆ）に乗ってしまう。よって、噴射流量を大きくし、高圧で付与する必要がある。 Also, when the papermaking speed of the long paper machine (M) is faster than 27 m / min, the injection flow rate is made larger than the reference value. When the paper making speed is fast, the wet paper (9) on the wire (4a) moves before entering the paper layer (Q), and the falsification preventing material (2) does not enter the paper layer (Q). It rides on the surface (F) of (Q). Therefore, it is necessary to increase the injection flow rate and apply it at a high pressure.
さらに、湿紙（９）の含水率が９５％より高い場合、噴射流量は基準値より小さくする。含水率が高い場合、湿紙（９）内の繊維量が少なくなるため、基準値では、改ざん防止材料（２）が紙層（Ｑ）を突き抜け、湿紙（９）の裏面（Ｂ）に出てしまう。よって、噴射流量を小さくし、低圧で付与する必要がある。 Furthermore, when the moisture content of the wet paper (9) is higher than 95%, the injection flow rate is made smaller than the reference value. When the moisture content is high, the amount of fibers in the wet paper (9) decreases, and therefore, at the reference value, the falsification preventing material (2) penetrates through the paper layer (Q), and the back surface (B) of the wet paper (9). It will come out. Therefore, it is necessary to reduce the injection flow rate and apply it at a low pressure.
最後に、改ざん防止分散液付与工程（ＳＴ３）として、図１３（ｃ）に示すように、水分量調整工程（ＳＴ１）の湿紙（９）に対し、ノズル噴射流量調整工程（ＳＴ２）で調整した、上限値、中間値及び下限値の範囲内で、ノズル（１０）の噴射流量を変動させながら、改ざん防止分散液（Ｊ）を湿紙（９）に付与することで、図１３（ｄ）に示すように、単層の用紙における紙層（Ｑ）内の一部に、用紙の表面（Ｆ）から異なる深さに付与されて成る改ざん防止模様（１）を形成することが、可能となる。 Finally, as shown in FIG. 13C, the anti-tampering dispersion applying step (ST3) is adjusted in the nozzle injection flow rate adjusting step (ST2) with respect to the wet paper (9) in the moisture amount adjusting step (ST1). By applying the anti-tampering dispersion liquid (J) to the wet paper (9) while changing the injection flow rate of the nozzle (10) within the range of the upper limit value, the intermediate value, and the lower limit value, FIG. It is possible to form a tamper-proof pattern (1) formed at a different depth from the surface (F) of the paper in a part of the paper layer (Q) of the single-layer paper as shown in FIG. It becomes.
なお、前述した図５に示す改ざん防止用紙（Ｓ２）を作製する場合、改ざん防止分散液付与工程（ＳＴ３）において、改ざん防止分散液（Ｊ）を、間隔を空けながら付与する。よって、タイマーと、ポンプ、電磁弁等の制御装置をノズル（１０）に取り付けたのち、所望の間隔でノズル（１０）の噴射のスイッチをオンオフすることで、改ざん防止分散液（Ｊ）を、間隔を空けながら湿紙（９）に付与することが、可能となる。 In the case where the falsification preventing paper (S2) shown in FIG. 5 described above is produced, the falsification preventing dispersion liquid (J) is applied at intervals in the falsification preventing dispersion liquid applying step (ST3). Therefore, after attaching a control device such as a timer, a pump, and a solenoid valve to the nozzle (10), turning on / off the injection switch of the nozzle (10) at a desired interval, the anti-tampering dispersion liquid (J), It is possible to apply the wet paper (9) with a gap.
図１４は、図５の改ざん防止用紙（Ｓ２）の領域（Ｚ）を拡大した図である。図１４に示す、改ざん防止材料（２）が付与されない箇所である間隔（Ｐ２）を有する改ざん防止模様（１）を形成する場合、まず、用いる長網抄紙機（Ｍ）の一秒当たりの抄速を測定する。例えば、長網抄紙機（Ｍ）の抄速が２７ｍ／ｍｉｎの場合、一秒当たりの抄速は、４５０ｍｍ／ｓｅｃとなる。 FIG. 14 is an enlarged view of the region (Z) of the falsification preventing paper (S2) in FIG. When forming the tamper-proof pattern (1) having the interval (P2), which is a portion to which the tamper-proof material (2) is not applied, shown in FIG. Measure speed. For example, when the paper making speed of the long paper machine (M) is 27 m / min, the paper making speed per second is 450 mm / sec.
次に、改ざん防止材料（２）を付与する箇所の長さ（Ｐ１）を設定する。例えば、図１４においては、Ｐ１＝２０ｍｍとする。次に、改ざん防止材料（２）を付与する時間、つまり、ノズル（１０）から改ざん防止分散液（Ｊ）の噴射をオンとする時間を算出する。オンとする時間は、改ざん防止材料（２）を付与する箇所の長さ（Ｐ１）を長網抄紙機（Ｍ）の一秒当たりの抄速で割ることで、算出できる。図１４においては、算出すると、０．０４４ｓｅｃとなる。 Next, the length (P1) of the location to which the anti-tampering material (2) is applied is set. For example, in FIG. 14, it is assumed that P1 = 20 mm. Next, the time for applying the anti-tampering material (2), that is, the time for turning on the injection of the anti-tampering dispersion (J) from the nozzle (10) is calculated. The time for turning on can be calculated by dividing the length (P1) of the portion to which the falsification preventing material (2) is applied by the paper making speed per second of the long net paper machine (M). In FIG. 14, the calculation is 0.044 sec.
次に、間隔（Ｐ２）の長さを設定する。例えば、図１４においては、Ｐ２＝２０ｍｍとする。次に、改ざん防止材料（２）を付与しない時間、つまり、ノズル（１０）から改ざん防止分散液（Ｊ）の噴射をオフとする時間を算出する。オフとする時間は、間隔（Ｐ２）の長さを長網抄紙機（Ｍ）の一秒当たりの抄速で割ることで、算出できる。図１４においては、算出すると、０．０４４ｓｅｃとなる。 Next, the length of the interval (P2) is set. For example, in FIG. 14, P2 = 20 mm. Next, the time during which the anti-tampering material (2) is not applied, that is, the time during which the injection of the anti-tampering dispersion (J) from the nozzle (10) is turned off is calculated. The time to turn off can be calculated by dividing the length of the interval (P2) by the paper making speed per second of the long paper machine (M). In FIG. 14, the calculation is 0.044 sec.
以上、間隔（Ｐ２）を有する改ざん防止模様（１）は、改ざん防止分散液（Ｊ）の噴射を０．０４４ｓｅｃごとにオンオフすることで、形成することが、可能となる。 As described above, the alteration prevention pattern (1) having the interval (P2) can be formed by turning on / off the injection of the alteration prevention dispersion liquid (J) every 0.044 sec.
なお、前述した改ざん防止分散液（Ｊ）の固形分濃度は０．１〜４％が、好ましい。固形分濃度が、３％を超える場合、ノズル（１０）の噴射流量及び噴射口の形状によっては、ノズル（１０）に改ざん防止材料（２）が詰まり、好ましくない。 The solid content concentration of the anti-tampering dispersion (J) is preferably 0.1 to 4%. When the solid content concentration exceeds 3%, depending on the injection flow rate of the nozzle (10) and the shape of the injection port, the nozzle (10) is clogged with the falsification preventing material (2), which is not preferable.
また、固形分濃度が１％未満の場合、改ざん防止材料（２）を紙層（Ｑ）内に付与することは可能であるが、改ざん防止用紙（Ｓ１、Ｓ２）となった際の、改ざん防止模様（１）の視認性や、改ざん防止材料（２）の機械読取性が低下し、好ましくない。 In addition, when the solid content concentration is less than 1%, it is possible to apply the anti-tampering material (2) in the paper layer (Q), but tampering with the anti-tampering paper (S1, S2). The visibility of the prevention pattern (1) and the machine readability of the tamper prevention material (2) are unfavorable.
なお、噴射流量は、ノズル（１０）の噴射口の形状、改ざん防止材料（２）の坪量、固形分濃度等によりも変動することから、適宜調整を行う。 The injection flow rate is appropriately adjusted because it varies depending on the shape of the injection port of the nozzle (10), the basis weight of the falsification preventing material (2), the solid content concentration, and the like.
また、ノズル（１０）は、一つに限らず複数設置することも可能である。 Further, the number of nozzles (10) is not limited to one, and a plurality of nozzles (10) may be installed.
本発明の実施例１について、図１及び図２を用いて説明する。実施例１では、単層の紙層（Ｑ）内に、複数の改ざん防止材料（２）が波線の実線状に付与された改ざん防止用紙（Ｓ１）を作製した例を示す。 A first embodiment of the present invention will be described with reference to FIGS. Example 1 shows an example in which a falsification preventing sheet (S1) in which a plurality of falsification preventing materials (2) are provided in the shape of a solid wavy line in a single paper layer (Q) is shown.
紙層（Ｑ）を形成する繊維は、アバカパルプを使用した。また、改ざん防止材料（２）は、湿紙と化学結合可能な官能基を有する材料として、着色した稲わらパルプを使用した。 Abaca pulp was used as the fiber forming the paper layer (Q). Further, as the falsification preventing material (2), colored rice straw pulp was used as a material having a functional group capable of chemically bonding with wet paper.
改ざん防止分散液（Ｊ）は、改ざん防止材料（２）である着色した稲わらパルプを、水に固形分濃度０．３５％で分散させることで作製した。 The anti-tampering dispersion (J) was prepared by dispersing colored rice straw pulp, which is the anti-tampering material (2), in water at a solid content concentration of 0.35%.
次に、水分量調整工程（ＳＴ１）として、図８及び図９に示す、長網抄紙機（Ｍ）を用いて、長網抄紙機（Ｍ）のワイヤー（４ａ）上に、紙料供給槽（３ａ）から紙層（Ｑ）を形成する紙料（Ｗ）を供給したのち、ワイヤー（４ａ）上に湿紙（９）を形成する。 Next, as a moisture content adjusting step (ST1), a paper supply tank is used on the wire (4a) of the long paper machine (M) using the long paper machine (M) shown in FIGS. After supplying the stock (W) for forming the paper layer (Q) from (3a), the wet paper (9) is formed on the wire (4a).
次に、湿紙（９）の水分量を、テーブルロール（４ｂ）及びサクションボックスを用いて、脱水を行い、含水率９５％に調整した。 Next, the moisture content of the wet paper (9) was dehydrated using a table roll (4b) and a suction box to adjust the water content to 95%.
次に、ノズル噴射流量調整工程（ＳＴ２）として、改ざん防止分散液（Ｊ）を湿紙（９）の紙層（Ｑ）内の異なる位置に付与するために、改ざん防止分散液（Ｊ）が、湿紙（９）の表面（Ｆ）上に付与される噴射流量、改ざん防止分散液（Ｊ）が、湿紙（９）の紙層（Ｑ）内の中間に付与される噴射流量及び、改ざん防止分散液（Ｊ）が、湿紙（９）の裏面（Ｂ）に付与される噴射流量の以上三つの条件における各ノズル（１０）の噴射流量を調整した。 Next, as the nozzle injection flow rate adjustment step (ST2), the anti-tampering dispersion liquid (J) is applied to different positions in the paper layer (Q) of the wet paper (9). A jet flow rate applied to the surface (F) of the wet paper web (9), a jet flow rate applied to the middle of the paper layer (Q) of the wet paper web (9) and the anti-tampering dispersion (J), and The spray flow rate of each nozzle (10) under the above three conditions of the spray flow rate applied to the back surface (B) of the wet paper web (9) by the anti-falsification dispersion liquid (J) was adjusted.
改ざん防止分散液（Ｊ）が、湿紙（９）の表面（Ｆ）上に付与される噴射流量は２００ｍｌ／ｍｉｎに調整し、改ざん防止分散液（Ｊ）が、湿紙（９）の紙層（Ｑ）内の中間に付与される噴射流量は５００ｍｌ／ｍｉｎに調整し、改ざん防止分散液（Ｊ）が、湿紙（９）の裏面（Ｂ）上に付与される噴射流量は８００ｍｌ／ｍｉｎに調整した。なお、噴射流量の調整は、ノズル（１０）に流送ポンプを接続したのち、流送ポンプのインバータを調整することで行った。 The spray flow rate at which the anti-tampering dispersion (J) is applied to the surface (F) of the wet paper (9) is adjusted to 200 ml / min, and the anti-tampering dispersion (J) is a paper of the wet paper (9). The spray flow rate applied to the middle of the layer (Q) is adjusted to 500 ml / min, and the spray flow rate at which the anti-tampering dispersion (J) is applied to the back surface (B) of the wet paper (9) is 800 ml / min. Adjusted to min. The injection flow rate was adjusted by connecting the flow pump to the nozzle (10) and then adjusting the inverter of the flow pump.
次に、改ざん防止分散液付与工程（ＳＴ３）として、水分量調整工程（ＳＴ１）後の湿紙（９）に対し、改ざん防止分散液（Ｊ）を、ポンプを用いて流送し、ノズル（１０）から、ノズル噴射流量調整工程（ＳＴ２）で設定した噴射流量３００ｍｌ／ｍｉｎから７００ｍｌ／ｍｉｎの範囲内で連続的に変動させながら噴射した。なお、この時、ノズル（１０）と湿紙（９）表面の距離は５０ｍｍとした。 Next, as the anti-tampering dispersion applying step (ST3), the anti-tampering dispersion (J) is sent to the wet paper (9) after the water content adjusting step (ST1) using a pump, and the nozzle ( From 10), the injection was performed while continuously fluctuating within the range of the injection flow rate from 300 ml / min to 700 ml / min set in the nozzle injection flow rate adjustment step (ST2). At this time, the distance between the nozzle (10) and the surface of the wet paper (9) was 50 mm.
その後、ワイヤー（４ａ）下部に設置された搾水ボックスにより湿紙（９）の水分が脱水され、改ざん防止材料（２）である着色した稲わらパルプと湿紙（９）が絡み合うとともに、水素結合により結合した。さらに、プレスロールで脱水したのち、乾燥、カレンダ処理を行うことで、繊維間結合はより強固になり、単層の紙層（Ｑ）内における厚み方向の異なる位置に改ざん防止材料（２）が付与された改ざん防止用紙（Ｓ１）となった。 Thereafter, the water in the wet paper (9) is dehydrated by a water extraction box installed at the lower part of the wire (4a), and the colored rice straw pulp and the wet paper (9) as the anti-tampering material (2) are intertwined with each other. Bonded by bonding. Furthermore, after dehydrating with a press roll, drying and calendering are performed, the bond between fibers becomes stronger, and the anti-tampering material (2) is placed at different positions in the thickness direction in the single paper layer (Q). The attached anti-tamper paper (S1) was obtained.
１ 改ざん防止模様
２ 改ざん防止材料
３ 準備部
３ａ 紙料供給槽
４ ワイヤー部
４ａ ワイヤー
４ｂ テーブルロール
５ プレス部
６ 乾燥部
７ カレンダ部
７ａ カレンダロール
８ リール部
９ 湿紙
１０ ノズル
１１ 用紙
１２ 偽造用紙
１３ 偽造品
１４ 多層紙
１４ａ 上層
１４ｂ 不織布
１４ｃ 下層
Ｑ 紙層
Ｗ 紙料
Ｊ 改ざん防止分散液
Ｍ 長網抄紙機
Ｓ１、Ｓ２、Ｓ３ 改ざん防止用紙
Ｆ 表面
Ｂ 裏面
Ｚ 領域
DESCRIPTION OF
Claims (2)
前記改ざん防止模様は、前記用紙表面に対し、少なくとも一部が深さ方向に異なった領域を有し、前記紙層と化学結合可能な官能基を有する及び／又は繊維で形成された紙層による三次元の網目より大きい幅を有する少なくとも一種類の改ざん防止材料から成ることを特徴とする改ざん防止用紙。 A tamper-proof pattern is formed on a part of the paper layer of single-layer paper,
The tamper-proof pattern is based on a paper layer having at least a portion different in the depth direction with respect to the paper surface, having a functional group capable of chemically bonding to the paper layer, and / or formed of fibers. A tamper-proof paper comprising at least one type of tamper-proof material having a width larger than a three-dimensional mesh.