JP2016037722A - Header stop block and header wall equipped with the same, laying block and retaining wall body part equipped with the same, and retaining wall - Google Patents

Header stop block and header wall equipped with the same, laying block and retaining wall body part equipped with the same, and retaining wall Download PDF

Info

Publication number
JP2016037722A
JP2016037722A JP2014160280A JP2014160280A JP2016037722A JP 2016037722 A JP2016037722 A JP 2016037722A JP 2014160280 A JP2014160280 A JP 2014160280A JP 2014160280 A JP2014160280 A JP 2014160280A JP 2016037722 A JP2016037722 A JP 2016037722A
Authority
JP
Japan
Prior art keywords
block
lightness
less
retaining wall
pair
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2014160280A
Other languages
Japanese (ja)
Other versions
JP5985552B2 (en
Inventor
隆之 早川
Takayuki Hayakawa
隆之 早川
真一 黒澤
Shinichi Kurosawa
真一 黒澤
了司 寺田
Norikazu Terada
了司 寺田
福田　康昭
Yasuaki Fukuda
康昭 福田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiheiyo Cement Corp
Original Assignee
Taiheiyo Cement Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiheiyo Cement Corp filed Critical Taiheiyo Cement Corp
Priority to JP2014160280A priority Critical patent/JP5985552B2/en
Publication of JP2016037722A publication Critical patent/JP2016037722A/en
Application granted granted Critical
Publication of JP5985552B2 publication Critical patent/JP5985552B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a header stop block and a header wall equipped with the same, a laying block and a retaining wall body part equipped with the same, and a retaining wall, which have brightness and texture close to that of natural material, do not stand out among the surrounding environment and are lightweight.SOLUTION: A header stop block 2 includes: a pair of side surface parts 11, 11 which oppose to each other with an interval; a front surface part 12 which connects one end parts 11a, 11a of the pair of the side surface parts 11, 11 with each other; and an intermediate part 13 which connects the pair of the side surface parts 11, 11 with each other on the side nearer to the front surface part 12 side than other end parts 11b, 11b of the pair of the side wall parts 11, 11, and opposes to the front surface part 12 with an interval. A surface 12a of the front surface part 12 has a split shape, a brightness (L value) of 57.20 or less, and a brightness scale (N) of 7.2 or less.SELECTED DRAWING: Figure 2

Description

この発明は、道路法面や宅地法面等の急勾配の傾斜地の地盤の安定のために構築される擁壁の端部に形成される小口壁用小口止めブロック及びこれを備える小口壁と、積みブロック及びこれを備える擁壁本体部と、小口壁と擁壁本体部とで構築された擁壁とに関する。   The present invention includes a small-mouth stop block for a small-wall wall formed at the end of a retaining wall constructed for the stability of the ground of a steep slope such as a road slope and a residential land slope, and a small-mouth wall including the same. The present invention relates to a stacking block and a retaining wall main body provided with the same, and a retaining wall constructed of a small wall and a retaining wall main body.

従来、擁壁の構築に用いられていた積みブロック（間知ブロックとも呼ばれている）の概観は極めて無味乾燥であり、そのブロック表面は平滑面であって、装飾を施したといっても、せいぜい、型枠により得た単純な凹凸が設けられているだけであったり、あるいは、顔料を用いて着色されていたりするに過ぎなかった。そして、この擁壁の端部に形成される小口壁も現場打ちコンクリートで打設され、灰白色の平滑なコンクリート面が露出したままであった。   Previously, the appearance of the building blocks (also known as the cognitive blocks) used in the construction of retaining walls is extremely dry, and the surface of the blocks is smooth and decorated. At best, it was only provided with simple irregularities obtained by the formwork, or only colored with pigments. The small edge wall formed at the end of the retaining wall was also cast with cast-in-place concrete, and the grayish white smooth concrete surface remained exposed.

ところが近年、景観が非常に重要視されるようになってきたため、擁壁にも環境と程好く調和する外観が求められてきた。その結果、ブロック表面を割裂状に加工したコンクリートブロックや、ポーラスコンクリート層を設けた表層部を割裂状に加工したコンクリートブロックなど、自然の風合い（色彩）に近いコンクリートブロックが開発されてきている（特許文献１）。しかしながら、擁壁の端部に形成される小口壁は依然として、現場打ちコンクリートで打設され、コンクリート面が露出したままであった。   In recent years, however, the landscape has become very important, and the retaining wall has been required to have an appearance that is in harmony with the environment. As a result, concrete blocks that are close to the natural texture (color) have been developed, such as concrete blocks that have been processed into a split surface on the surface of the block, and concrete blocks that have been processed in a split shape on the surface layer where the porous concrete layer is provided ( Patent Document 1). However, the edge wall formed at the end of the retaining wall was still cast with cast-in-place concrete and the concrete surface remained exposed.

一方、小口壁を構築する際の現場作業の軽減・効率化の観点から、大型の小口止めブロックが開発されている。さらに、景観上及び効率化の観点から、自然石模様の擁壁と全く同様の自然石模様を施すことができる小口壁用ブロックが開発されている（特許文献２）。   On the other hand, from the viewpoint of reducing and improving the efficiency of on-site work when constructing a small wall, a large small-sized block is being developed. Furthermore, from the viewpoints of landscape and efficiency, a small-abutment block has been developed that can be provided with a natural stone pattern exactly the same as a natural stone retaining wall (Patent Document 2).

特開２０００−３１９９０８号公報JP 2000-319908 A 特開２００３−３２８３７５号公報JP 2003-328375 A

しかしながら、前記大型の小口止めブロックは、施工に重機が必要であり、重機が持ち込めない山間部等では使用できないといった問題点があった。また、このブロック表面は、平滑なコンクリート面が露出したままであるといった問題点もあった。   However, there is a problem that the large-sized small stop block requires heavy machinery for construction and cannot be used in a mountainous area where heavy machinery cannot be carried. Further, this block surface has a problem that a smooth concrete surface remains exposed.

一方、前記自然石模様を施すことができる小口壁用ブロックは、コンクリートの色合いがそのまま残っていて、自然石模様の積みブロック（擁壁）とは景観的な一体感はとれていても、擁壁周囲の自然環境とは調和がとれているとは言い難いといった問題点があった。すなわち、コンクリートであるために、素材のそのものの明度が９〜１０と高く、自然石模様であっても光を反射しやすく、全体として周囲よりも明度が高く、結果として周囲の環境から浮き上がって見えてしまい、景観の調和が損なわれていた。   On the other hand, the block for small edge wall that can be given the natural stone pattern has a concrete color as it is, and even if it has a natural sense of unity with the natural stone pattern building block (retaining wall), There was a problem that it was difficult to say that it was in harmony with the natural environment around the walls. In other words, because it is concrete, the lightness of the material itself is as high as 9-10, it is easy to reflect light even if it is a natural stone pattern, the lightness is higher than the surroundings as a whole, and as a result, it floats from the surrounding environment It was visible and the harmony of the landscape was impaired.

また、「多自然川づくりポイントブックＩＩＩ〜中小河川に関する河道計画の技術基準・解説〜」（平成２３年１０月発行、日本河川協会）では、護岸ブロックの明度は６以下が好ましいと記載されているが、明度計測の具体的な方法が示されていないため、計測条件の違いによって結果にばらつきが生じる事が懸念されていた。このため、「護岸ブロックの平均明度計測方法（案）について」（土木研究所自然共生研究センター、全国土木コンクリートブロック協会）の中で、撮影条件（天候、撮影時間帯、照度、ブロック積上方法等）、撮影方法（撮影位置、光源の方向）、解析方法（解析アプリケーションソフト）等について規定されたが、計測方法が煩雑であり、しかも解析及び計測結果は全国土木コンクリートブロック協会が取り扱うことになっているため、撮影者自ら明度を求めることは難しかった。   In addition, the “Natural River Creation Point Book III ~ Technical Standards and Explanations for River Channel Plans on Small and Medium Rivers ~" (issued in October 2011, Japan River Association) states that the lightness of the revetment block is preferably 6 or less. However, since a specific method for measuring brightness has not been shown, there has been a concern that the results may vary due to differences in measurement conditions. For this reason, in "About the average brightness measurement method (draft) of the revetment block" (Public Works Research Institute Nature Conservation Research Center, National Civil Engineering Concrete Block Association), the shooting conditions (weather, shooting time zone, illuminance, block accumulation method) Etc.), shooting method (shooting position, direction of light source), analysis method (analysis application software), etc., but the measurement method is complicated, and the analysis and measurement results are to be handled by the Japan Civil Engineering Concrete Block Association. Therefore, it was difficult for the photographer to ask for brightness.

この発明はこのような問題点を解決するためになされたもので、自然素材に近い明度とテクスチャーとを有し、周囲の環境から浮き上がって見えることのない軽量の小口止めブロック及びこれを備える小口壁、積みブロック及びこれを備える擁壁本体部、並びに擁壁を提供することを目的とする。   The present invention has been made to solve such problems, and has a lightness and texture close to natural materials and has a lightness and texture that does not appear to float up from the surrounding environment, and a forehead having the same An object is to provide a wall, a stacking block, a retaining wall main body including the same, and a retaining wall.

この発明に係る小口止めブロックは、間隔を空けて対向する一対の側面部と、一対の側面部が対向する方向に対して垂直な方向の一対の側面部の一方の端部同士を接続する前面部と、一対の側面部の他方の端部よりも前面部側で前記一対の側面部同士を接続し、前面部と間隔を空けて対向する中間部とを備え、前面部の表面は割裂状であり、その明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下である。
前面部は、ポーラスコンクリートを割裂して形成されてもよい。
前面部の表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、前面部の表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 The fore mouth block according to the present invention is a front surface that connects a pair of side surfaces facing each other with a gap therebetween and one end of a pair of side surfaces perpendicular to the direction in which the pair of side surfaces oppose each other. A pair of side portions connected to each other on the front side of the other end portion of the pair of side portions, and an intermediate portion facing the front portion with a space therebetween, and the surface of the front portion is split. And its lightness (L value) is 57.20 or less or its lightness scale (N) is 7.2 or less.
The front portion may be formed by splitting porous concrete.
The lightness (L value) of the front surface is 46.50 or lower, or its lightness scale (N) is 5.0 or lower, and the lightness scale (N) of the front surface is 5.0 or lower, and The saturation (C) may be 5.0 or less.

この発明に係る積みブロックは、割裂状の表面を有し、この表面の明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下である。
表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 The stacked block according to the present invention has a split-like surface, and the lightness (L value) of this surface is 57.20 or less or its lightness scale (N) is 7.2 or less.
The lightness (L value) of the surface is 46.50 or less, or its lightness scale (N) is 5.0 or less. Furthermore, the lightness scale (N) of the surface is 5.0 or less, and its chroma (C) May be 5.0 or less.

この発明に係る小口壁は、上記いずれかの小口止めブロックを備える。
この発明に係る擁壁本体部は、上記いずれかの積みブロックを備える。
この発明に係る擁壁は、上記小口壁と上記擁壁本体部とを備える。 The small edge wall according to the present invention includes any of the small edge stopper blocks described above.
The retaining wall main body according to the present invention includes any one of the above-described stacking blocks.
The retaining wall according to the present invention includes the small wall and the retaining wall main body.

この発明によれば、小口止めブロック及び積みブロックの前面部の表面が割裂状であり、その明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下であることにより、自然素材に近い明度とテクスチャーとを実現し、周囲の環境から浮き上がって見えることを防止することができる。   According to this invention, the surface of the front portion of the small mouth block and the stacking block is split, and its lightness (L value) is 57.20 or less or its lightness scale (N) is 7.2 or less. Realizes brightness and texture similar to natural materials, and prevents it from appearing floating from the surrounding environment.

この発明の実施の形態に係る擁壁の正面図である。It is a front view of the retaining wall which concerns on embodiment of this invention. この実施の形態に係る擁壁の小口壁を構成する小口止めブロックの平面図である。It is a top view of the small edge stop block which comprises the small edge wall of the retaining wall which concerns on this embodiment. この実施の形態に係る擁壁の小口壁を構成する小口止めブロックの側面図である。It is a side view of the fore edge stop block which comprises the fore edge wall of the retaining wall which concerns on this embodiment. この実施の形態に係る擁壁の小口壁を構成する小口止めブロックの正面図である。It is a front view of the fore edge stop block which comprises the fore edge wall of the retaining wall which concerns on this embodiment. 図１のＶ−Ｖ線に沿った断面図である。It is sectional drawing along the VV line of FIG. 明度（Ｌ）、彩度（Ｃ）、及び明度スケール（Ｎ）との関係を表したグラフである。It is a graph showing the relationship between lightness (L), saturation (C), and lightness scale (N).

以下、この発明の実施の形態を添付図面に基づいて説明する。
図１に示されるように、擁壁１は、複数の小口止めブロック２を鉛直方向に堆積した２つの小口壁３，３と、小口壁３，３間に設けられ、複数の積みブロック４を堆積した擁壁本体部５とから構成されている。小口止めブロック２及び積みブロック４は、基礎コンクリート６の上に堆積され、最上位置にある小口止めブロック２及び積みブロック４の上に、板状の天端コンクリート７が配置されている。尚、以下の説明において、小口止めブロック２を堆積する方向に関して上下方向を定義する。 Embodiments of the present invention will be described below with reference to the accompanying drawings.
As shown in FIG. 1, the retaining wall 1 is provided between two small edge walls 3 and 3 in which a plurality of small edge stopper blocks 2 are stacked in a vertical direction, and between the small edge walls 3 and 3. It is comprised from the retaining wall main-body part 5 which accumulated. The pawl block 2 and the stack block 4 are deposited on the foundation concrete 6, and the plate-like top end concrete 7 is disposed on the pawl block 2 and the stack block 4 at the uppermost position. In the following description, the vertical direction is defined with respect to the direction in which the small mouth block 2 is deposited.

図２に示されるように、小口止めブロック２は、間隔を空けて対向する一対の側面部１１，１１と、一対の側面部１１，１１の一方の端部１１ａ，１１ａ同士を接続する前面部１２と、一対の側面部１１，１１の他方の端部１１ｂ，１１ｂよりも前面部１２側で一対の側面部１１，１１同士を接続し前面部１２と間隔を空けて対向する中間部１３とを備えている。一対の側面部１１，１１と、前面部１２と、中間部１３とにより、上下方向に開口した第１空間部１４が形成されている。また、一対の側面部１１，１１と、中間部１３とにより、上下方向及び側面部１１，１１の端部１１ｂ，１１ｂ間に開口した第２空間部１５が形成されている。   As shown in FIG. 2, the mouthpiece block 2 includes a pair of side surfaces 11, 11 that are opposed to each other with a space therebetween, and a front surface portion that connects one end portions 11 a, 11 a of the pair of side surfaces 11, 11. 12 and an intermediate portion 13 which connects the pair of side surface portions 11, 11 on the front surface portion 12 side with respect to the other end portions 11b, 11b of the pair of side surface portions 11, 11, and faces the front surface portion 12 with a gap therebetween. It has. The pair of side surface portions 11, 11, the front surface portion 12, and the intermediate portion 13 form a first space portion 14 that opens in the vertical direction. In addition, the pair of side surface portions 11 and 11 and the intermediate portion 13 form a second space portion 15 opened in the vertical direction and between the end portions 11 b and 11 b of the side surface portions 11 and 11.

図３に示されるように、各側面部１１の上縁部１１ｃには、上縁部１１ｃから上方に突出した凸部１６が形成されている。各側面部１１の下縁部１１ｄには、下縁部１１ｄに対して窪んだ凹部１７が形成されている。小口止めブロック２を堆積する際に凸部１６が、真上に位置する小口止めブロック２の凹部１７に嵌まりこむように、凸部１６及び凹部１７が形成されている。   As shown in FIG. 3, a convex portion 16 that protrudes upward from the upper edge portion 11 c is formed on the upper edge portion 11 c of each side surface portion 11. A concave portion 17 that is recessed with respect to the lower edge portion 11d is formed in the lower edge portion 11d of each side surface portion 11. The convex portion 16 and the concave portion 17 are formed so that the convex portion 16 fits into the concave portion 17 of the small-mouth stopper block 2 located right above when depositing the small-mouth stopper block 2.

図４に示されるように、前面部１２の表面１２ａは割裂状になっている。前面部１２の表面１２ａを割裂状にするには、例えば、表面同士が一体的に形成されたコンクリートブロック連結体を、その略中央にて二つに割裂すればよい。このようにすれば、その割裂面には、コンクリートの粗骨材が一般のコンクリートを用いた場合よりも多く、なおかつ割れて露出する。このため粗骨材の自然な風合い（色彩）が現れて、コンクリートブロックに自然な風合い（色彩）を効率よく付与できる。   As shown in FIG. 4, the surface 12a of the front surface portion 12 is split. In order to split the surface 12a of the front surface portion 12, for example, a concrete block connected body whose surfaces are integrally formed may be split into two at the approximate center. If it does in this way, the coarse aggregate of concrete will be more cracked and exposed to the splitting surface than the case where general concrete is used. For this reason, the natural texture (color) of the coarse aggregate appears, and the natural texture (color) can be efficiently imparted to the concrete block.

尚、上記表面同士が一体的に形成されたコンクリートブロック連結体において、その略中央付近をポーラスコンクリート層とすることがより好ましい。こうすることによって、割裂面に割れた粗骨材からなる断面を最大限に露出させることができ、粗骨材のもつ自然な風合い（色彩）を更に高めることができる。これは、ポーラスコンクリート層の割裂面が粗いので光を反射しにくくなるだけでなく、陰影がつくことで目立ちにくくなり、より自然の景観に馴染みやすくなるためである。   In addition, in the concrete block coupling body in which the surfaces are integrally formed, it is more preferable that the vicinity of the substantial center is a porous concrete layer. By doing so, the cross section made of the coarse aggregate cracked on the split surface can be exposed to the maximum, and the natural texture (color) of the coarse aggregate can be further enhanced. This is because the split surface of the porous concrete layer is not only difficult to reflect light, but it is also less noticeable due to the shading, making it easier to become familiar with the natural landscape.

図１に示されるように、積みブロック４の前面部の表面も割裂状になっている。積みブロック４の前面部の割裂状の表面も、小口止めブロック２の前面部１２の表面１２ａ（図４参照）の作成方法と同じ方法で作成することができる。   As shown in FIG. 1, the front surface of the stacking block 4 is also split. The split-like surface of the front portion of the stacking block 4 can also be created by the same method as the method of creating the surface 12a (see FIG. 4) of the front portion 12 of the small mouth block 2.

図５に示されるように、小口壁３において、各小口止めブロック２の各第１空間部１４は、基礎コンクリート６から天端コンクリート７まで連通して上下方向に延びる１つの大きな空間を形成している。この空間全体に胴込めコンクリート２１が充填されている。また、各小口止めブロック２の各第２空間部１５も同様に、基礎コンクリート６から天端コンクリート７まで連通して上下方向に延びる１つの大きな空間を形成している。この空間全体に裏込めコンクリート２２が充填されている。各第２空間部１５に充填されている裏込めコンクリート２２は、各小口止めブロック２の側面部１１，１１の端部１１ｂ，１１ｂ（図２参照）間の開口から突出して上下の裏込めコンクリート２２と連結して、当該開口を塞ぐような板状の裏込めコンクリート８を構成している。裏込めコンクリート８と地山９との間には、砂利等の裏込材２３が存在している。   As shown in FIG. 5, in the fore edge wall 3, each first space portion 14 of each fore edge stop block 2 forms one large space that communicates from the foundation concrete 6 to the top concrete 7 and extends in the vertical direction. ing. The entire space is filled with trunked concrete 21. Similarly, each second space portion 15 of each small-mouth stopper block 2 forms one large space that communicates from the foundation concrete 6 to the top concrete 7 and extends in the vertical direction. The entire space is filled with backfill concrete 22. The backfill concrete 22 filled in each second space portion 15 protrudes from the opening between the end portions 11b and 11b (see FIG. 2) of the side surface portions 11 and 11 of each of the small-mouth stopper blocks 2 so as to be upper and lower backfill concrete. The plate-shaped back-filled concrete 8 is configured so as to close the opening. Between the backfill concrete 8 and the natural ground 9, there is a backfill material 23 such as gravel.

尚、小口止めブロック２は、第１空間部１４及び第２空間部１５を有するので、通常のコンクリートブロックよりは一段と軽量化が図られており、小口壁３を形成する際に、重機によらず人手による施工も可能となる。   In addition, since the small-mouth stopper block 2 has the 1st space part 14 and the 2nd space part 15, weight reduction is achieved more than a normal concrete block, and when forming the small-wall 3, a heavy machine is used. It is also possible to perform construction manually.

次に、本発明における小口止めブロック２の前面部１２の割裂状の表面１２ａによる自然な風合い（色彩）について説明する。
小口止めブロック２の前面部１２の表面１２ａの明度（Ｌａｂ表色系のＬ値、以下明度（Ｌ値）と称す）は５６以下であり、明度スケール（ＪＩＳ Ｚ ８７２１に準拠）では５．０以下である。 Next, the natural texture (color) due to the split surface 12a of the front surface portion 12 of the mouthpiece block 2 in the present invention will be described.
The lightness (L value of the Lab color system, hereinafter referred to as lightness (L value)) of the surface 12a of the front end portion 12 of the small-mouth stopper block 2 is 56 or less, and the lightness scale (conforming to JIS Z8721) is 5.0. It is as follows.

「中小河川に関する河道計画の技術基準」（平成２２年８月改定、国土交通省）には、「石礫、土、植物など、河川景観を構成する要素の多くは自然物であり、一般的に明度（明るさ）や彩度（鮮やかさ）は比較的低いものが多い。土木研究所の研究によると、明度、彩度ともに５以下のものが多いとされている。」と記載されている。すなわち、この小口止めブロック２は、自然物に近い要素（以下、「自然物要素」と称す）であると言える。   According to “Technical standards for river channel plans for small and medium rivers” (revised in August 2010, Ministry of Land, Infrastructure, Transport and Tourism), “Many of the elements that make up the river landscape, such as stones, soil, and plants, are natural objects. Many of them have relatively low brightness (brightness) and saturation (brightness). According to a study by the Civil Engineering Research Institute, both brightness and saturation are 5 or less. " . That is, it can be said that the mouthpiece block 2 is an element close to a natural object (hereinafter referred to as “natural object element”).

次に、本発明の小口止めブロック２の構成材料とその配合等について説明する。
本発明で用いるセメントとしては、各種ポルトランドセメント、各種混合セメント、エコセメント、アルミナセメントからなる群より選ばれる１種以上を使用することができる。また、このセメントに石灰石粉末、石英粉末、石膏、シリカフュームからなる群より選ばれる１種以上を添加して使用することができる。石灰石粉末、石英粉末、石膏については、ブレーン比表面積が３０００〜２００００ｃｍ２／ｇのものを内割りで５０質量％以下で混合することが好ましい。また、シリカフュームについては、ＢＥＴ比表面積が５〜２２ｍ２／ｇであるのものを内割りで２５質量％以下で混合することが好ましい。 Next, the constituent material of the mouthpiece block 2 of the present invention, its formulation and the like will be described.
As the cement used in the present invention, one or more selected from the group consisting of various Portland cements, various mixed cements, eco-cements, and alumina cements can be used. One or more selected from the group consisting of limestone powder, quartz powder, gypsum, and silica fume can be added to this cement. As for the limestone powder, quartz powder, and gypsum, it is preferable to mix those having a Blaine specific surface area of 3000 to 20000 cm 2 / g at 50% by mass or less. Moreover, about a silica fume, it is preferable to mix the thing whose BET specific surface area is 5-22 m < 2 > / g by an internal division at 25 mass% or less.

本発明で用いる細骨材としては、川砂、山砂、陸砂、海砂、砕砂、硅砂、天然軽量細骨材（パーライト、ヒル石等）、人工軽量細骨材、高炉スラグ細骨材、電気炉酸化スラグ細骨材等からなる群より選ばれる１種以上を使用することができる。   As fine aggregates used in the present invention, river sand, mountain sand, land sand, sea sand, crushed sand, dredged sand, natural lightweight fine aggregates (perlite, leech stone, etc.), artificial lightweight fine aggregates, blast furnace slag fine aggregates, One or more selected from the group consisting of an electric furnace oxidation slag fine aggregate and the like can be used.

本発明で用いる粗骨材としては、川砂利、海砂利、山砂利、砕石、天然軽量骨材、人工軽量骨材、石灰石粗骨材、高炉スラグ粗骨材、電気炉酸化スラグ粗骨材、再生骨材等からなる群より選ばれる１種以上を使用することができる。   As the coarse aggregate used in the present invention, river gravel, sea gravel, mountain gravel, crushed stone, natural lightweight aggregate, artificial lightweight aggregate, limestone coarse aggregate, blast furnace slag coarse aggregate, electric furnace oxidation slag coarse aggregate, One or more selected from the group consisting of recycled aggregates and the like can be used.

本発明で用いる水は、特に限定されるものではなく、本発明の小口止めブロック２の強度等の物性に悪影響を与えないものであれば使用することができる。   The water used in the present invention is not particularly limited, and any water that does not adversely affect the physical properties such as the strength of the small mouth block 2 of the present invention can be used.

本発明で用いる減水剤は、高性能ＡＥ減水剤、高性能減水剤、ＡＥ減水剤等からなる群より選ばれる１種以上の減水剤が挙げられる。この減水剤の種類（化合物）は、ポリカルボン酸、ナフタレンスルホン酸ホルムアルデヒド縮合物、メラミンスルホン酸ホルムアルデヒド縮合物、リグニンスルホン酸、これらの塩からなる群より選ばれる１種以上が挙げられる。   Examples of the water reducing agent used in the present invention include one or more water reducing agents selected from the group consisting of a high performance AE water reducing agent, a high performance water reducing agent, an AE water reducing agent, and the like. Examples of the water reducing agent (compound) include at least one selected from the group consisting of polycarboxylic acid, naphthalenesulfonic acid formaldehyde condensate, melamine sulfonic acid formaldehyde condensate, lignin sulfonic acid, and salts thereof.

本発明においては、上記材料以外に、本発明の目的を阻害しない範囲で、空気量調整剤、収縮低減剤、膨張材、顔料等を使用してもよい。   In the present invention, in addition to the above materials, an air amount adjusting agent, a shrinkage reducing agent, an expansion material, a pigment, and the like may be used as long as the object of the present invention is not impaired.

ポーラスコンクリート層の配合としては、セメント：３２０〜４２０ｋｇ／ｍ３、細骨材：９０〜２６０ｋｇ／ｍ３、粗骨材：１４００〜１８００ｋｇ／ｍ３、水：６５〜８５ｋｇ／ｍ３、混和剤（製品の質量）：３．０〜９．０ｋｇ／ｍ３が好ましい。 As the composition of the porous concrete layer, cement: 320 to 420 kg / m 3 , fine aggregate: 90 to 260 kg / m 3 , coarse aggregate: 1400 to 1800 kg / m 3 , water: 65 to 85 kg / m 3 , admixture (Mass of product): 3.0 to 9.0 kg / m 3 is preferable.

普通コンクリート層の配合としては、セメント：２６０〜３２０ｋｇ／ｍ３、細骨材：１０００〜１３００ｋｇ／ｍ３、粗骨材：８００〜１０００ｋｇ／ｍ３、水：９０〜１２０ｋｇ／ｍ３、混和剤（製品の質量）：０．８〜２．０ｋｇ／ｍ３が好ましい。 As the composition of the ordinary concrete layer, cement: 260-320 kg / m 3 , fine aggregate: 1000-1300 kg / m 3 , coarse aggregate: 800-1000 kg / m 3 , water: 90-120 kg / m 3 , admixture (Mass of product): 0.8 to 2.0 kg / m 3 is preferable.

本発明においては、即時脱型したコンクリートブロック連結体を、積算温度が２１６０℃・ｈｒ以上となるように保温養生を行うことが好ましい。   In the present invention, it is preferable that the concrete block connected body immediately demolded is subjected to heat curing so that the integrated temperature becomes 2160 ° C. · hr or more.

本発明に係る小口止めブロック２の効果を検証するための検証実験を行った。以下に、その検証実験の準備及び方法並びに結果を示す。   A verification experiment was performed to verify the effect of the small mouth stopper block 2 according to the present invention. The preparation and method of the verification experiment and the results are shown below.

［ポーラスコンクリート層の配合］
ポーラスコンクリート層の配合は、普通ポルトランドセメント：３６０ｋｇ／ｍ３、水：７２ｋｇ／ｍ３、粗骨材（最大寸法１３ｍｍ）：１６４５ｋｇ／ｍ３、細骨材（砕砂）：２２５ｋｇ／ｍ３、混和剤：７．５ｋｇ／ｍ３であった。その結果、成形時空隙率は１５．０％、成形時空気量は１．０％であった。 [Composition of porous concrete layer]
The composition of the porous concrete layer is: ordinary Portland cement: 360 kg / m 3 , water: 72 kg / m 3 , coarse aggregate (maximum dimension 13 mm): 1645 kg / m 3 , fine aggregate (crushed sand): 225 kg / m 3 , mixed Agent: 7.5 kg / m 3 . As a result, the porosity during molding was 15.0%, and the air amount during molding was 1.0%.

［普通コンクリート層の配合］
普通コンクリート層の配合は、普通ポルトランドセメント：２８０ｋｇ／ｍ３、水：１０５ｋｇ／ｍ３、粗骨材（最大寸法１０ｍｍ）：８５８ｋｇ／ｍ３、細骨材（山砂）：１，１６８ｋｇ／ｍ３、混和剤：１．３ｋｇ／ｍ３であった。その結果、成形時空隙率は４．０％、成形時空気量は１．０％であった。 [Combination of ordinary concrete layer]
The composition of the ordinary concrete layer is as follows: ordinary Portland cement: 280 kg / m 3 , water: 105 kg / m 3 , coarse aggregate (maximum dimension 10 mm): 858 kg / m 3 , fine aggregate (mountain sand): 1,168 kg / m 3 and admixture: 1.3 kg / m 3 . As a result, the porosity during molding was 4.0%, and the amount of air during molding was 1.0%.

［ポーラスコンクリート層の割裂状の表面を有するブロックの製造］
２個のコンクリートブロックの表面同士が一体的に形成されるコンクリートブロック連結体製造用型枠に、該型枠中央部に上記ポーラスコンクリート層の配合で示したポーラスコンクリートを、その他の部分に上記普通コンクリート層の配合で示した普通コンクリートをそれぞれ充填して、即時脱型してコンクリートブロック連結体を製造した。次に、このコンクリートブロック連結体を３０℃で３日間養生した。その後、このコンクリートブロック連結体をその中心部で破断装置により破断し、ポーラスコンクリート層の割裂状の表面を有する二つのコンクリートブロックを得た（以下、群１のブロックと称す）。尚、群１のブロックは、実施例１〜８の合計８個のブロックである。 [Manufacture of block having split surface of porous concrete layer]
The concrete block connected formwork in which the surfaces of the two concrete blocks are integrally formed, the porous concrete indicated by the composition of the porous concrete layer in the center part of the formwork, and the ordinary part in the other part Each of the ordinary concrete indicated by the composition of the concrete layer was filled and immediately demolded to produce a concrete block connector. Next, this concrete block coupling body was cured at 30 ° C. for 3 days. Thereafter, the concrete block connected body was broken at the center by a breaking device to obtain two concrete blocks having a split concrete surface of a porous concrete layer (hereinafter referred to as group 1 blocks). In addition, the group 1 block is a total of 8 blocks of Examples 1-8.

［普通コンクリート層の割裂状の表面を有するブロックの製造］
表面同士が一体的に形成されるコンクリートブロック連結体製造用型枠に、上記普通コンクリート層の配合で示した普通コンクリートを充填して、即時脱枠してコンクリートブロック連結体を製造した。次に、このコンクリートブロック連結体を３０℃で３日間養生した。その後、このコンクリートブロック連結体をその中心部で破断装置により破断し、ブロック表面が普通コンクリート層の割裂面を有する二つのコンクリートブロックを得た（以下、群２のブロックと称す）。尚、群２のブロックは、実施例９〜２３の合計１５個のブロックである。 [Manufacture of blocks having split-like surfaces of ordinary concrete layers]
The concrete block connecting body form, in which the surfaces are integrally formed, was filled with the ordinary concrete shown by the blending of the above-mentioned ordinary concrete layer, and immediately de-framed to produce a concrete block connecting body. Next, this concrete block coupling body was cured at 30 ° C. for 3 days. Then, this concrete block coupling body was fractured at its center by a breaking device, and two concrete blocks having a split surface of a normal concrete layer on the block surface were obtained (hereinafter referred to as group 2 blocks). In addition, the group 2 block is a total of 15 blocks of Examples 9-23.

［割裂状の表面を有しないブロックの製造］
１個取り用型枠に、上記普通コンクリート層の配合で示した普通コンクリートを充填して、即時脱枠してコンクリートブロックを製造した。次に、このコンクリートブロックを３０℃で３日間養生して、表層に割裂面を有しないコンクリートブロックを製造した（以下、群３のブロックと称す）。尚、群３のブロックは、比較例１の１個のブロックである。 [Manufacture of a block having no split surface]
A single block mold was filled with the ordinary concrete shown in the above-mentioned composition of the ordinary concrete layer, and immediately deframed to produce a concrete block. Next, the concrete block was cured at 30 ° C. for 3 days to produce a concrete block having no split surface on the surface layer (hereinafter referred to as a group 3 block). The block of group 3 is one block of comparative example 1.

［明度（Ｌ値）の測定］
上記の方法で製造した３種類のコンクリートブロック（群１〜３のブロック）について、以下の方法でそのブロックの表面の明度（Ｌ値）を色差計（コニカミノルタ製ＣＲ−２１０）で測定した。
測定箇所は、ブロック１個につき５ヶ所とし、１ヶ所につき３回の測定を行い、合計１５回の測定結果の平均を試験結果とした。尚、１ヶ所の測定範囲の直径は５ｃｍである。また、測定にあたっては周囲の影響（太陽の位置及び太陽光の強弱、照明の位置及び照明の強弱、反射光）を除去するため、専用のアタッチメント（筒状）を用いて行った。尚、群１のブロックについては、表面の凹凸が大きいため、アタッチメントの先端とブロック表面との間の隙間を粘土で被覆して測定を行った。 [Measurement of lightness (L value)]
With respect to the three types of concrete blocks (groups 1 to 3) produced by the above method, the lightness (L value) of the surface of the block was measured with a color difference meter (CR-210 manufactured by Konica Minolta) by the following method.
The number of measurement locations was 5 for each block, 3 measurements were performed for each location, and the average of 15 measurement results in total was taken as the test result. The diameter of one measurement range is 5 cm. The measurement was performed using a dedicated attachment (cylindrical shape) in order to remove the influence of the surroundings (the position of the sun and the intensity of sunlight, the position of the illumination and the intensity of illumination, and the reflected light). In addition, about the block of group 1, since the unevenness | corrugation of the surface was large, it measured by covering the clearance gap between the front-end | tip of an attachment and a block surface with clay.

ところで、このアタッチメントの材質は特に限定されるものではなく、例えば、紙製、樹脂性、ゴム製等で良く、また、形状は円筒状や四角筒状等で良い。尚、このアタッチメントの先端と測定対象物または色差計受光面（受光部）との間に隙間が生じている場合は、この隙間を粘土等で覆う必要がある。   By the way, the material of this attachment is not particularly limited, and for example, it may be made of paper, resin, rubber or the like, and the shape may be cylindrical or square tube. In addition, when the clearance gap has arisen between the front-end | tip of this attachment and a measurement object or a color difference light-receiving surface (light-receiving part), it is necessary to cover this clearance gap with clay.

群１〜３のブロックについての明度の測定結果を表１に示す。表１には、彩度の値も示されているが、彩度は下記式により計算した。

Figure 2016037722
Table 1 shows the brightness measurement results for the blocks of Groups 1 to 3. Table 1 also shows saturation values, but the saturation was calculated by the following equation.
Figure 2016037722

Figure 2016037722
Figure 2016037722

表１に示した通り、各群の明度（Ｌ値）は、群１では３８．８１〜４４．１２（平均４２．０９）、群２では３９．３０〜５７．２０（平均４７．８１）、群３では５８．０３であり、平滑面を有する普通のコンクリートブロック（群３）に比して、割裂状の表面を有するブロック（群２）の明度（Ｌ値）が低いことがわかり、ポーラスコンクリート層の割裂状の表面を有するブロック（群１）の明度（Ｌ値）がさらに低いことがわかる。     As shown in Table 1, the lightness (L value) of each group was 38.81 to 44.12 (average 42.09) in group 1, and 39.30 to 57.20 (average 47.81) in group 2. It is found that the lightness (L value) of the block (group 2) having a split-like surface is lower than that of an ordinary concrete block (group 3) having a smooth surface. It can be seen that the lightness (L value) of the block (group 1) having the split surface of the porous concrete layer is even lower.

［明度スケールの明度（Ｌ値）測定］
ＪＩＳ Ｚ ８７２１に準じて日本規格協会にて販売されている明度スケールについて、明度（Ｌ）を色差計（コニカミノルタ製ＣＲ−２１０）で測定した（以下、群４と称す）。その結果を表２に示す。尚、明度スケールに示される色は、理論上ａ、ｂの値及び彩度は存在しないことになっているが、色差計の測定範囲と明度スケールの色の大きさの関係で測定値が発生するため、参考値として示した。 [Brightness scale lightness (L value) measurement]
The brightness (L) was measured with a color difference meter (CR-210 manufactured by Konica Minolta) for the brightness scale sold by the Japanese Standards Association in accordance with JIS Z 8721 (hereinafter referred to as group 4). The results are shown in Table 2. The colors shown on the lightness scale theoretically have no values of a and b and no saturation, but the measured values are generated due to the relationship between the colorimeter measurement range and the lightness scale color. Therefore, it is shown as a reference value.

Figure 2016037722
Figure 2016037722

表２に示した通り、明度（Ｌ値）は、明度スケールの記号の数値が０．５増加するのに伴って、約１〜２程度増加することから、色差計で明度（Ｌ値）の傾向を把握することは可能である。明度スケールＮ−５．０を色差計で測定した場合、明度（Ｌ値）は４６．４２である。従って、コンクリートブロックの表面の明度（Ｌ値）が４６．４２以下であれば、周囲の環境と違和感なく調和することになる。   As shown in Table 2, the lightness (L value) increases by about 1-2 as the numerical value of the lightness scale symbol increases by 0.5. It is possible to grasp the trend. When the lightness scale N-5.0 is measured with a color difference meter, the lightness (L value) is 46.42. Therefore, if the lightness (L value) of the surface of the concrete block is 46.42 or less, it will harmonize with the surrounding environment without a sense of incongruity.

そこで、表１と表２の結果から、群１〜群４について、彩度（Ｃ）、明度（Ｌ値）、明度スケール（Ｎ）との関係を図６に示す。図６に示した群４に係わる明度（Ｌ）と明度スケール（Ｎ）の関係は、下記式で表される。

Figure 2016037722
Therefore, from the results of Tables 1 and 2, the relationship between the saturation (C), the lightness (L value), and the lightness scale (N) is shown in FIG. The relationship between the lightness (L) and the lightness scale (N) related to the group 4 shown in FIG. 6 is expressed by the following equation.
Figure 2016037722

図６に示した通り、群３（比較例１）の明度（Ｌ値）は５８．０３であり、このときの明度スケール（Ｎ）は７．４である。これに対して、群２（実施例９〜２３）の中で最大の明度（Ｌ値）となったのは、実施例２３の５７．２０であり、このときの明度スケール（Ｎ）は７．２である。さらに、群１（実施例１〜８）の中で最大の明度（Ｌ値）となったのは、実施例８の４４．１２であり、このときの明度スケール（Ｎ）は４．４である。すなわち、群２の全ての明度（Ｌ）は群３の明度（Ｌ）を下回っており、結果として、群３の明度スケール（Ｎ）も下回っている。そして、群１の全ての明度（Ｌ）は群３の明度（Ｌ）を大幅に下回っており、結果として、群３の明度スケール（Ｎ）も大幅に下回っている。   As shown in FIG. 6, the lightness (L value) of group 3 (Comparative Example 1) is 58.03, and the lightness scale (N) at this time is 7.4. On the other hand, the maximum brightness (L value) in Group 2 (Examples 9 to 23) was 57.20 of Example 23, and the brightness scale (N) at this time was 7 .2. Furthermore, in Group 1 (Examples 1 to 8), the maximum brightness (L value) was 44.12 of Example 8, and the brightness scale (N) at this time was 4.4. is there. That is, all lightness values (L) of group 2 are lower than lightness value (L) of group 3, and as a result, lightness scale (N) of group 3 is also lower. All lightness values (L) of group 1 are significantly lower than lightness value (L) of group 3, and as a result, the lightness scale (N) of group 3 is also significantly lower.

さらに、群１（実施例１〜８）の全ての明度（Ｌ値）は４６．５０（明度スケール（Ｎ）は５．０）を全て下回っているので、群１は全て明度スケール（Ｎ）５．０以下となる。しかも、群１の彩度（Ｃ）の最大値は実施例２の３．５０であるから、群１の彩度（Ｃ）は全て５．０を大幅に下回っている。   Furthermore, since all the lightness values (L values) of Group 1 (Examples 1 to 8) are all below 46.50 (Lightness Scale (N) is 5.0), all of Group 1 are lightness scales (N). 5.0 or less. Moreover, since the maximum value of the saturation (C) of the group 1 is 3.50 of the second embodiment, the saturations (C) of the group 1 are all significantly lower than 5.0.

以上説明した通り、本発明の割裂状の表面を有するコンクリートブロックは、割裂状の表面を有していないコンクリートブロックよりも明度スケール（Ｎ）が低く、より周囲の環境に調和しやすいものである。さらに、本発明のポーラスコンクリート層の割裂状の表面を有するコンクリートブロックは、割裂状の表面を有していないコンクリートブロックよりも明度スケール（Ｎ）が一段と低く、周囲の環境に極めて調和しやすいものである。しかも、本発明のポーラスコンクリート層の割裂状の表面を有するコンクリートブロックは、明度スケール（Ｎ）及び彩度（Ｃ）とともに５以下であるので、土木研究所の研究によるところの「自然物要素」に該当するものである。   As described above, the concrete block having a split-like surface of the present invention has a lightness scale (N) lower than that of a concrete block having no split-like surface, and is more harmonious with the surrounding environment. . Furthermore, the concrete block having the split-like surface of the porous concrete layer of the present invention has a lightness scale (N) much lower than that of the concrete block having no split-like surface, and is very easy to harmonize with the surrounding environment. It is. Moreover, since the concrete block having the split-like surface of the porous concrete layer of the present invention has a brightness scale (N) and saturation (C) of 5 or less, it is considered as a “natural object” as a result of research by the Public Works Research Institute. Applicable.

したがって、本発明の割裂状の表面を有する小口止めブロックを用いて構築した小口壁は、周囲の環境と調和するものである。そして、本発明のポーラスコンクリート層の割裂状の表面を有する小口止めブロックは、明度（Ｌ値）が４６．５０（明度スケール（Ｎ）は５．０）以下、且つ彩度（Ｃ）が５．０以下であるので、より好ましい。   Accordingly, the fore edge wall constructed using the fore edge block having a split surface according to the present invention is in harmony with the surrounding environment. The mouthpiece block having the split surface of the porous concrete layer of the present invention has a lightness (L value) of 46.50 (lightness scale (N) is 5.0) or less and a chroma (C) of 5 It is more preferable because it is 0.0 or less.

さらに、擁壁の構築に用いられる積みブロックについても、そのブロック表面を割裂状、あるいはポーラスコンクリート層の割裂状の表面とすれば、周囲の環境に極めて調和しやすい積みブロックとなり、この積みブロックで構築した擁壁本体も周囲の環境に極めて調和しやすいものとなる。そして、本発明のポーラスコンクリート層の割裂状の表面を有する積みブロックは、明度（Ｌ値）が４６．５０（明度スケール（Ｎ）は５．０）以下、且つ彩度（Ｃ）が５．０以下であるので、より好ましい。   Furthermore, if the block surface used for the construction of the retaining wall is split or the surface of the porous concrete layer is split, it will be very easy to harmonize with the surrounding environment. The built retaining wall body is also very harmonious with the surrounding environment. The stacked block having the split surface of the porous concrete layer of the present invention has a lightness (L value) of 46.50 (lightness scale (N) is 5.0) or less and a chroma (C) of 5. Since it is 0 or less, it is more preferable.

また、積みブロックと小口止めブロックの両方を本発明の割裂状の表面とすれば、これらのブロックで構築した壁面全体が周囲の環境と調和することになるのでより好ましい。そして、ポーラスコンクリート層の割裂状の表面を有する積みブロックとポーラスコンクリート層の割裂状の表面を有する小口止めブロックとを併用すれば、擁壁全体（擁壁本体部と小口壁の両方）が、明度（Ｌ値）は４６．５０（明度スケール（Ｎ）は５．０）以下、且つ彩度（Ｃ）は５．０以下となるので、特に好ましい。   Moreover, it is more preferable that both the stacking block and the small-mouth stopper block are split-like surfaces of the present invention because the entire wall surface constructed by these blocks is in harmony with the surrounding environment. And, if you use together the pile block that has the split-like surface of the porous concrete layer and the forelock block that has the split-like surface of the porous concrete layer, the entire retaining wall (both the retaining wall body and the fore wall) The lightness (L value) is particularly preferable because it is 46.50 (lightness scale (N) is 5.0) or less and the saturation (C) is 5.0 or less.

１ 擁壁、２ 小口止めブロック、３ 小口壁、４ 積みブロック、５ 擁壁本体部、１１ 側面部、１２ 前面部、１２ａ （前面部の）表面、１３ 中間部。   DESCRIPTION OF SYMBOLS 1 Retaining wall, 2 Small stop block, 3 Small wall, 4 Stack block, 5 Retaining wall main-body part, 11 Side part, 12 Front part, 12a (front part) surface, 13 Middle part.

この発明に係る小口止めブロックは、間隔を空けて対向する一対の側面部と、一対の側面部が対向する方向に対して垂直な方向の一対の側面部の一方の端部同士を接続する前面部と、一対の側面部の他方の端部よりも前面部側で前記一対の側面部同士を接続し、前面部と間隔を空けて対向する中間部とを備え、前面部の表面は割裂状であり、その明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下であり、明度（Ｌ値）は、周囲の影響を除去するために筒状のアタッチメントを用いて色差計によって測定される。
前面部は、ポーラスコンクリートを割裂して形成されてもよい。
前面部の表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、前面部の表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 The fore mouth block according to the present invention is a front surface that connects a pair of side surfaces facing each other with a gap therebetween and one end of a pair of side surfaces perpendicular to the direction in which the pair of side surfaces oppose each other. A pair of side portions connected to each other on the front side of the other end portion of the pair of side portions, and an intermediate portion facing the front portion with a space therebetween, and the surface of the front portion is split. , and the lightness (L value) of 57.20 or less or a lightness scale (N) is Ri der 7.2 or less, the lightness (L value), the cylindrical attachment in order to remove the effects of ambient Ru is measured by a color difference meter using.
The front portion may be formed by splitting porous concrete.
The lightness (L value) of the front surface is 46.50 or lower, or its lightness scale (N) is 5.0 or lower, and the lightness scale (N) of the front surface is 5.0 or lower, and The saturation (C) may be 5.0 or less.

この発明に係る積みブロックは、割裂状の表面を有し、この表面の明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下であり、明度（Ｌ値）は、周囲の影響を除去するために筒状のアタッチメントを用いて色差計によって測定される。
表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 Block loading according to the present invention has a surface of the split裂状, Ri brightness of this surface (L value) of 57.20 or less or a lightness scale (N) is 7.2 der less lightness (L value) is Ru is measured by a color difference meter using a cylindrical attachment in order to remove the influence of the surroundings.
The lightness (L value) of the surface is 46.50 or less, or its lightness scale (N) is 5.0 or less. Furthermore, the lightness scale (N) of the surface is 5.0 or less, and its chroma (C) May be 5.0 or less.

この発明に係る小口止めブロックは、間隔を空けて対向する一対の側面部と、一対の側面部が対向する方向に対して垂直な方向の一対の側面部の一方の端部同士を接続する前面部と、一対の側面部の他方の端部よりも前面部側で前記一対の側面部同士を接続し、前面部と間隔を空けて対向する中間部とを備え、前面部の表面は割裂状であり、かつ、粗骨材が割れて露出しており、その明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下であり、明度（Ｌ値）は、周囲の影響を除去するために筒状のアタッチメントを用いて色差計によって測定される。
前面部は、ポーラスコンクリートを割裂して形成されてもよい。
前面部の表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、前面部の表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 The fore mouth block according to the present invention is a front surface that connects a pair of side surfaces facing each other with a gap therebetween and one end of a pair of side surfaces perpendicular to the direction in which the pair of side surfaces oppose each other. A pair of side portions connected to each other on the front side of the other end portion of the pair of side portions, and an intermediate portion facing the front portion with a space therebetween, and the surface of the front portion is split. And the coarse aggregate is cracked and exposed, its lightness (L value) is 57.20 or less or its lightness scale (N) is 7.2 or less, and the lightness (L value) is the surroundings In order to remove the influence of, it is measured by a color difference meter using a cylindrical attachment.
The front portion may be formed by splitting porous concrete.
The lightness (L value) of the front surface is 46.50 or lower, or its lightness scale (N) is 5.0 or lower, and the lightness scale (N) of the front surface is 5.0 or lower, and The saturation (C) may be 5.0 or less.

この発明に係る積みブロックは、割裂状の表面を有し、かつ、粗骨材が割れて露出しており、この表面の明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下であり、明度（Ｌ値）は、周囲の影響を除去するために筒状のアタッチメントを用いて色差計によって測定される。
表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下、さらに、表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下であってもよい。 The stacking block according to the present invention has a split-like surface, and the coarse aggregate is cracked and exposed, and the lightness (L value) of this surface is 57.20 or less or its lightness scale (N) is The brightness (L value) is 7.2 or less, and the lightness (L value) is measured by a color difference meter using a cylindrical attachment to remove the influence of the surroundings.
The lightness (L value) of the surface is 46.50 or less, or its lightness scale (N) is 5.0 or less. Furthermore, the lightness scale (N) of the surface is 5.0 or less, and its chroma (C) May be 5.0 or less.

Claims (10)

間隔を空けて対向する一対の側面部と、
該一対の側面部が対向する方向に対して垂直な方向の該一対の側面部の一方の端部同士を接続する前面部と、
前記一対の側面部の他方の端部よりも前記前面部側で前記一対の側面部同士を接続し、前記前面部と間隔を空けて対向する中間部と
を備え、
前記前面部の表面は割裂状であり、その明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下である小口止めブロック。 A pair of side portions facing each other at an interval;
A front part connecting one end of the pair of side parts in a direction perpendicular to the direction in which the pair of side parts opposes;
The pair of side surface portions are connected to each other on the front surface side of the other end portion of the pair of side surface portions, and includes an intermediate portion facing the front surface portion with a space therebetween,
The front end block is split-like, and its lightness (L value) is 57.20 or less or its lightness scale (N) is 7.2 or less. 前記前面部は、ポーラスコンクリートを割裂して形成される、請求項１に記載の小口止めブロック。   The mouthpiece block according to claim 1, wherein the front portion is formed by splitting porous concrete. 前記前面部の表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下である、請求項１または２に記載の小口止めブロック。   The mouthpiece block according to claim 1 or 2, wherein the lightness (L value) of the surface of the front portion is 46.50 or less or its lightness scale (N) is 5.0 or less. 前記前面部の表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下である、請求項３に記載の小口止めブロック。   The mouthpiece block according to claim 3, wherein the lightness scale (N) of the surface of the front portion is 5.0 or less and the saturation (C) is 5.0 or less. 割裂状の表面を有し、該表面の明度（Ｌ値）が５７．２０以下またはその明度スケール（Ｎ）が７．２以下である積みブロック。   A stacked block having a split-like surface and having a lightness (L value) of 57.20 or less or a lightness scale (N) of 7.2 or less. 前記表面の明度（Ｌ値）が４６．５０以下またはその明度スケール（Ｎ）が５．０以下である、請求項５に記載の積みブロック。   The building block according to claim 5, wherein the lightness (L value) of the surface is 46.50 or less or the lightness scale (N) thereof is 5.0 or less. 前記表面の明度スケール（Ｎ）が５．０以下であり、かつ、その彩度（Ｃ）が５．０以下である、請求項６に記載の積みブロック。   The stacked block according to claim 6, wherein the lightness scale (N) of the surface is 5.0 or less and the chroma (C) is 5.0 or less. 請求項１〜４のいずれか一項に記載の小口止めブロックを備える小口壁。   A fore edge wall comprising the fore edge block according to any one of claims 1 to 4. 請求項５〜７のいずれか一項に記載の積みブロックを備える擁壁本体部。   A retaining wall main body comprising the stacking block according to any one of claims 5 to 7. 請求項８に記載の小口壁と、
請求項９に記載の擁壁本体部と
を備える擁壁。 A small wall according to claim 8;
A retaining wall comprising the retaining wall main body according to claim 9.
JP2014160280A 2014-08-06 2014-08-06 Small-mouth stopper block, small-mouth wall including the same, and retaining wall including the small-mouth wall Active JP5985552B2 (en)