JP2016022173A - Absorber, and absorbent article and incontinence supply including the same - Google Patents
Absorber, and absorbent article and incontinence supply including the same Download PDFInfo
- Publication number
- JP2016022173A JP2016022173A JP2014148321A JP2014148321A JP2016022173A JP 2016022173 A JP2016022173 A JP 2016022173A JP 2014148321 A JP2014148321 A JP 2014148321A JP 2014148321 A JP2014148321 A JP 2014148321A JP 2016022173 A JP2016022173 A JP 2016022173A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- absorber
- fibers
- fiber
- water absorption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、吸収性物品、特には失禁用品に用いる吸収体、これを含む吸収性物品及び失禁用品に関し、詳細には、不織布で構成されている吸収体、これを含む吸収性物品及び失禁用品に関する。 TECHNICAL FIELD The present invention relates to an absorbent article, in particular, an absorbent body used for incontinence articles, an absorbent article including the absorbent article, and an incontinence article, and more particularly, an absorbent body composed of a nonwoven fabric, an absorbent article including the absorbent article, and an incontinence article. About.
失禁用品等の吸収性物品は、主に装着者の肌に当接する表面シート、尿などの水分を吸収する吸収体、水分を外に漏れさせない防漏シートで構成されている。特に、尿などの水分を吸収する吸収体には、通常、不織布が用いられている。例えば、特許文献１には、尿受け部において、最も内側に位置している部材からの尿などの水分を吸収し、保持する第２の部材を、繊維内に複数の孔が形成された合成繊維で形成されているニードルパンチ不織布２枚で構成することが記載されている。また、特許文献２には、ポリエステルとレーヨンと低融点ファイバーとを含むニードルパンチ不織布で構成した保水層と、太番手の単繊維が集積された繊維素材と細番手の単繊維が集積された繊維素材とを交編したニットで構成された吸水拡散層を設けた尿漏れ対策生地が記載されている。また、特許文献３には、吸水性布帛として高吸水性繊維５〜６０重量％、１デニール以下の極細繊維５〜５０重量％、その他の天然繊維及び／又は合成繊維０〜９０重量％からなる不織布を用いた失禁ショーツが記載されている。 Absorbent articles such as incontinence articles are mainly composed of a surface sheet that comes into contact with the skin of the wearer, an absorbent that absorbs moisture such as urine, and a leak-proof sheet that does not allow moisture to leak out. In particular, a nonwoven fabric is usually used for an absorber that absorbs moisture such as urine. For example, in Patent Document 1, a second member that absorbs and retains moisture such as urine from a member located on the innermost side in the urine receiving portion is a composite in which a plurality of holes are formed in the fiber. It is described that it is composed of two needle punched nonwoven fabrics formed of fibers. Patent Document 2 discloses a water retention layer composed of a needle punched nonwoven fabric including polyester, rayon and low melting point fibers, a fiber material in which thick single fibers are integrated, and a fiber in which fine single fibers are integrated. A urine leakage countermeasure fabric provided with a water-absorbing diffusion layer composed of a knit knitted with a material is described. Further, Patent Document 3 includes 5 to 60% by weight of superabsorbent fibers as a water absorbent fabric, 5 to 50% by weight of ultrafine fibers of 1 denier or less, and 0 to 90% by weight of other natural fibers and / or synthetic fibers. Incontinence shorts using non-woven fabric are described.
特許文献１では、繊維内に複数の孔が形成された合成繊維を用いているため、親水性素材とは異なり、スポンジ効果によって加圧時に水分が逆戻りする恐れがある。特許文献２では、保水層が疎水生繊維であるポリエステル繊維を含む場合、保水層内の滞留液が移動してしまう恐れがある。また、吸収拡散層が複雑という問題がある。特許文献３では、高吸水性繊維が吸水するとゲル化する性質を有しているので、吸水性に優れるものの、失禁用品のように、洗濯して繰り返し使用する場合は、繊維の形態を崩しやすく、洗濯耐久性が十分ではなかった。 In Patent Document 1, since synthetic fibers in which a plurality of holes are formed in the fibers are used, unlike the hydrophilic material, there is a risk that the moisture may be reversed during pressurization due to the sponge effect. In patent document 2, when a water retention layer contains the polyester fiber which is a hydrophobic raw fiber, there exists a possibility that the staying liquid in a water retention layer may move. There is also a problem that the absorption diffusion layer is complicated. In Patent Document 3, since the superabsorbent fiber has a property of gelling when it absorbs water, it is excellent in water absorbency, but when used repeatedly after washing like an incontinence product, the form of the fiber is easily broken. Washing durability was not enough.
本発明は、かかる実情に鑑みてなされたものであり、不織布で構成され、吸液速度が速く、保水性が高く、水分の逆戻りが低減された吸収体、これを含む吸収性物品及び失禁用品を提供する。 The present invention has been made in view of such circumstances, and is composed of a non-woven fabric, has a high liquid absorption speed, high water retention, and reduced moisture reversion, absorbent articles including the same, and incontinence articles I will provide a.
本発明は、吸収性物品に用いる吸収体であって、上記吸収体は、第２不織布と、上記第２不織布の表面上に積層されている第１不織布を含み、上記第１不織布は、繊度が上記第２不織布の構成繊維の平均繊度より大きく、且つ３．０ｄｔｅｘ以下の第１のセルロース繊維を７０質量％以上含み、上記第２不織布は、繊度が上記第１不織布の構成繊維の平均繊度より小さく、且つ０．２〜１．０ｄｔｅｘの第２の再生セルロース繊維を７０質量％以上含むことを特徴とする吸収体に関する。 This invention is an absorber used for an absorbent article, Comprising: The said absorber contains the 1st nonwoven fabric laminated | stacked on the surface of the 2nd nonwoven fabric and the said 2nd nonwoven fabric, and the said 1st nonwoven fabric has a fineness. Is greater than the average fineness of the constituent fibers of the second nonwoven fabric and contains 70% by mass or more of the first cellulose fibers of 3.0 dtex or less, and the second nonwoven fabric has an average fineness of the constituent fibers of the first nonwoven fabric. It is related with the absorber characterized by including 70 mass% or more of 2nd regenerated cellulose fibers smaller and 0.2-1.0 dtex.
上記第１不織布の構成繊維と上記第２不織布の構成繊維の平均繊度比は、１／０．２５〜１／０．７０であることが好ましい。上記第１のセルロース繊維は、繊度が１．４〜２．４ｄｔｅｘであることが好ましい。上記第１不織布は、水流交絡不織布又はニードルパンチ不織布であり、上記第２不織布は、ニードルパンチ不織布であることが好ましい。 The average fineness ratio of the constituent fibers of the first nonwoven fabric and the constituent fibers of the second nonwoven fabric is preferably 1 / 0.25 to 1 / 0.70. The first cellulose fiber preferably has a fineness of 1.4 to 2.4 dtex. The first nonwoven fabric is preferably a hydroentangled nonwoven fabric or a needle punched nonwoven fabric, and the second nonwoven fabric is preferably a needle punched nonwoven fabric.
上記第１不織布は水流交絡不織布であり、上記第２不織布はニードルパンチ不織布であり、上記第１不織布の水流交絡不織布は上記第２不織布のニードルパンチ不織布より比容積が大きいことが好ましい。上記第１不織布の水流交絡不織布は上記第２不織布のニードルパンチ不織布より目付及び/又は厚みが小さいことが好ましい。 It is preferable that the first nonwoven fabric is a hydroentangled nonwoven fabric, the second nonwoven fabric is a needle punched nonwoven fabric, and the hydroentangled nonwoven fabric of the first nonwoven fabric has a larger specific volume than the needle punched nonwoven fabric of the second nonwoven fabric. It is preferable that the hydroentangled nonwoven fabric of the first nonwoven fabric has a smaller basis weight and / or thickness than the needle punched nonwoven fabric of the second nonwoven fabric.
上記第１不織布と上記第２不織布は共にニードルパンチ不織布であり、上記第１不織布のニードルパンチ不織布は上記第２不織布のニードルパンチ不織布より比容積が小さいことが好ましい。 The first nonwoven fabric and the second nonwoven fabric are both needle punched nonwoven fabrics, and the needle punched nonwoven fabric of the first nonwoven fabric preferably has a smaller specific volume than the needle punched nonwoven fabric of the second nonwoven fabric.
本発明は、また、上記の吸収体を含むことを特徴とする吸収性物品に関する。 The present invention also relates to an absorbent article comprising the above-described absorber.
本発明は、また、上記の吸収体を含むことを特徴とする失禁用品に関する。 The present invention also relates to an incontinence product characterized by including the above-mentioned absorber.
本発明は、不織布を積層して吸収体を構成するとともに、上層に配置する第１不織布と、下層に配置する第２不織布に含まれる主成分繊維及びその繊度を特定のものにすることで、吸液速度が速く、保水性が高く、水分の逆戻りが低減された吸収体、これを含む吸収性物品及び失禁用品を提供することができる。 The present invention constitutes an absorbent body by laminating non-woven fabrics, and by making the main fiber and the fineness contained in the first non-woven fabric disposed in the upper layer and the second non-woven fabric disposed in the lower layer specific, It is possible to provide an absorbent body having a high liquid absorption rate, high water retention, and reduced water reversion, an absorbent article including the same, and an incontinence article.
本発明者らは、失禁用品等の吸収性物品に用いる吸収体を不織布で構成することについて鋭意検討した結果、不織布を積層して吸収体を構成するとともに、上層に配置されている第１不織布に、繊度が下層に配置されている第２不織布の構成繊維の平均繊度より大きく、且つ３．０ｄｔｅｘ以下の第１のセルロース繊維を７０質量％以上含ませ、上記下層不織布に、繊度が上層不織布の構成繊維の平均繊度より小さく、且つ０．２〜１．０ｄｔｅｘの第２の再生セルロース繊維を７０質量％以上含ませることで、吸液速度が速く、保水性が高く、水分の逆戻りが低減されることを見出し、本発明に至った。第１不織布が、繊度が大きい第１のセルロース繊維を７０質量％以上含むことにより、吸液速度が速くなり、第２不織布が、繊度が小さい第２の再生セルロース繊維を７０質量％以上含むことにより、水分の吸収量が増える。それゆえ、第１不織布を上層に配置し、第２不織布を下層に配置した吸収体は、吸液速度が速く、保水性が高く、水分の逆戻りが低減される。本発明の吸収体は、尿、体液などの水分（液体）を吸収して保持するものである。吸収性物品において、第１不織布（上層）が表面シート側に近接することになる。 As a result of intensive studies on the construction of an absorbent body used for absorbent articles such as incontinence articles, the present inventors have laminated the nonwoven fabric to form the absorbent body, and the first nonwoven fabric disposed in the upper layer. 70% by mass or more of the first cellulose fibers having a fineness larger than the average fineness of the constituent fibers of the second nonwoven fabric disposed in the lower layer and 3.0 dtex or less, and the fineness of the upper nonwoven fabric is contained in the lower nonwoven fabric. By containing 70% by mass or more of the second regenerated cellulose fiber having an average fineness of 0.2 to 1.0 dtex, the liquid absorption speed is high, the water retention is high, and the moisture reversion is reduced. As a result, the present invention has been achieved. When the first nonwoven fabric contains 70% by mass or more of the first cellulose fibers having a large fineness, the liquid absorption speed is increased, and the second nonwoven fabric contains 70% by mass or more of the second regenerated cellulose fibers having a small fineness. This increases the amount of moisture absorbed. Therefore, the absorbent body in which the first nonwoven fabric is disposed in the upper layer and the second nonwoven fabric is disposed in the lower layer has a high liquid absorption rate, high water retention, and reduced water reversion. The absorber of the present invention absorbs and retains moisture (liquid) such as urine and body fluid. In the absorbent article, the first nonwoven fabric (upper layer) comes close to the top sheet side.
本発明において、不織布の構成繊維の平均繊度（ｄｔｅｘ）とは、各構成繊維の繊度（ｄｔｅｘ）と不織布の全体質量に対する各構成繊維の質量割合（質量％）の積の合計を１００質量％で割り算したものである。 In the present invention, the average fineness (dtex) of the constituent fibers of the nonwoven fabric is 100% by mass of the product of the fineness (dtex) of each constituent fiber and the mass ratio (mass%) of each constituent fiber to the total mass of the nonwoven fabric. Divided.
(吸収体)
上記第１不織布は、繊度が第２不織布の構成繊維の平均繊度より大きく、且つ３．０ｄｔｅｘ以下の第１のセルロース繊維を７０質量％以上含む。上記第１不織布は、特に限定されないが、親水性によって吸液速度を向上させる観点から、第１のセルロース繊維を８０質量％以上含み、より好ましくは９０質量％以上含み、さらに好ましくは９５質量％以上含み、特に好ましくは１００質量％含む。第１のセルロース繊維の繊度は、特に限定されないが、下層への液移動性及び下層からの液戻り抑制の観点から、１．４〜２．４ｄｔｅｘであることが好ましく、１．５〜２．３ｄｔｅｘであることがより好ましい。上記第１のセルロース繊維は、特に限定されないが、カード通過性を考慮すると、繊維長は２５ｍｍ以上６５ｍｍ未満であることが好ましく、２８〜６０ｍｍであることがより好ましく、３５〜５５ｍｍであることがさらに好ましい。上記第１のセルロース繊維は、天然セルロース繊維であってもよく、再生セルロース繊維であってもよい。構成繊維の繊度を調整できる観点から、再生セルロース繊維であることが好ましい。天然セルロース繊維としては、コットン、麻などが挙げられる。再生セルロース繊維としては、ビスコースレーヨン繊維、銅アンモニアレーヨン繊維、溶剤紡糸セルロース繊維などが挙げられるが、ビスコースレーヨン繊維であることが好ましい。ビスコースレーヨン繊維は、通常、繊維断面が菊花状であり、繊維表面の軸方向に筋が存在するため、繊維表面での水分移動性及び繊維間の水分保持性に優れる。通常のビスコースレーヨン以外にも、尿等の水分を保持する保水性に優れるという観点から、繊維内に空隙を有する再生セルロース繊維、繊維表面に３つ以上の突起を有する再生セルロース繊維、及び繊維内に吸水性物質を有する再生セルロース繊維からなる群から選ばれる一種以上の繊維（以下、総じて特殊再生セルロース繊維ともいう。）を用いることができる。また、セルロース繊維自体が、消臭性、抗菌性、抗アレルゲン性などの機能性セルロース繊維であってもよい。以下において、単に「レーヨン繊維」と記載した場合は、ビスコースレーヨン繊維を意味する。
(Absorber)
The first nonwoven fabric contains 70% by mass or more of first cellulose fibers having a fineness larger than the average fineness of the constituent fibers of the second nonwoven fabric and 3.0 dtex or less. Although the said 1st nonwoven fabric is not specifically limited, From a viewpoint of improving a liquid absorption speed by hydrophilicity, 80 mass% or more of 1st cellulose fiber is contained, More preferably, 90 mass% or more is contained, More preferably, 95 mass% is contained. Including the above, particularly preferably 100% by mass. Although the fineness of a 1st cellulose fiber is not specifically limited, From a viewpoint of the liquid mobility to a lower layer, and a liquid return suppression from a lower layer, it is preferable that it is 1.4-2.4 dtex, and 1.5-2. More preferably, it is 3 dtex. The first cellulose fiber is not particularly limited, but considering the card passing property, the fiber length is preferably 25 mm or more and less than 65 mm, more preferably 28 to 60 mm, and more preferably 35 to 55 mm. Further preferred. The first cellulose fiber may be a natural cellulose fiber or a regenerated cellulose fiber. From the viewpoint of adjusting the fineness of the constituent fibers, regenerated cellulose fibers are preferable. Examples of natural cellulose fibers include cotton and hemp. Examples of the regenerated cellulose fiber include viscose rayon fiber, copper ammonia rayon fiber, solvent-spun cellulose fiber, and the like. Viscose rayon fiber is preferable. Viscose rayon fibers usually have a chrysanthemum fiber cross section and have streaks in the axial direction of the fiber surface, so that they have excellent moisture mobility on the fiber surface and moisture retention between fibers. In addition to ordinary viscose rayon, regenerated cellulose fiber having voids in the fiber, regenerated cellulose fiber having three or more protrusions on the fiber surface, and fiber from the viewpoint of excellent water retention for retaining water such as urine One or more kinds of fibers selected from the group consisting of regenerated cellulose fibers having a water-absorbing substance therein (hereinafter also referred to as special regenerated cellulose fibers) can be used. Further, the cellulose fiber itself may be a functional cellulose fiber such as deodorant property, antibacterial property, and antiallergenic property. In the following, the simple description of “rayon fiber” means viscose rayon fiber.
上記第１不織布は、第１のセルロース繊維に加えて、他の繊維を含んでもよい。他の繊維としては、本発明の効果を阻害しない範囲内で適宜選択して用いることができる。例えば、アクリル系繊維、ポリエステル系繊維、ポリアミド系繊維、ポリオレフィン系繊維、ポリウレタン系繊維などの合成繊維を用いることができる。他の繊維としては、上述した繊維から、１種又は複数種の繊維を用途等に応じて適宜に選択することができる。上記他の繊維は、特に限定されないが、繊度が１．０〜２．４ｄｔｅｘであることが好ましく、より好ましくは１．２〜１．９ｄｔｅｘであり、さらに好ましくは１．２〜１．７ｄｔｅｘである。上記他の繊維は、特に限定されないが、カード通過性を考慮すると、繊維長は２５ｍｍ以上６５ｍｍ未満であることが好ましく、２８〜６０ｍｍであることがより好ましく、３５〜５５ｍｍであることがさらに好ましい。 The first nonwoven fabric may include other fibers in addition to the first cellulose fibers. Other fibers can be appropriately selected and used within a range that does not impair the effects of the present invention. For example, synthetic fibers such as acrylic fibers, polyester fibers, polyamide fibers, polyolefin fibers, and polyurethane fibers can be used. As the other fibers, one or more kinds of fibers can be appropriately selected from the above-described fibers depending on the application. The other fibers are not particularly limited, but the fineness is preferably 1.0 to 2.4 dtex, more preferably 1.2 to 1.9 dtex, and still more preferably 1.2 to 1.7 dtex. is there. The other fibers are not particularly limited, but considering the card passing property, the fiber length is preferably 25 mm or more and less than 65 mm, more preferably 28 to 60 mm, and further preferably 35 to 55 mm. .
上記第２不織布は、繊度が第１不織布の構成繊維の平均繊度より小さく、且つ０．２〜１．０ｄｔｅｘの第２の再生セルロース繊維を７０質量％以上含む。上記第２不織布は、特に限定されないが、親水性による吸水性及び保水性向上の観点から、第２の再生セルロース繊維を８０質量％以上含み、より好ましくは９０質量％以上含み、さらに好ましくは９５質量％以上含み、特に好ましくは１００質量％含む。第２の再生セルロース繊維の繊度は、特に限定されないが、吸収水分の拡散性及び保水性向上の観点から、０．５〜１．０ｄｔｅｘであることが好ましく、０．７〜０．９５ｄｔｅｘであることがより好ましい。上記第２の再生セルロース繊維は、特に限定されないが、カード通過性を考慮すると、繊維長は２５ｍｍ以上６５ｍｍ未満であることが好ましく、２８〜６０ｍｍであることがより好ましく、３５〜５５ｍｍであることがさらに好ましい。上記第２の再生セルロース繊維は、ビスコースレーヨン繊維、銅アンモニアレーヨン繊維、溶剤紡糸セルロース繊維などのいずれの繊維であってもよいが、ビスコースレーヨン繊維であることが好ましい。ビスコースレーヨン繊維は、通常、繊維断面が菊花状であり、繊維表面の軸方向に筋が存在するため、繊維表面での水分移動性及び繊維間の水分保持性に優れる。また、第１のセルロース繊維の場合と同様に、保水性に優れるという観点から、特殊再生セルロース繊維を用いることができる。さらにまた、再生セルロース繊維自体が、消臭性、抗菌性、抗アレルゲン性などの機能性再生セルロース繊維であってもよい。 The second nonwoven fabric contains 70% by mass or more of second regenerated cellulose fiber having a fineness smaller than the average fineness of the constituent fibers of the first nonwoven fabric and 0.2 to 1.0 dtex. Although the said 2nd nonwoven fabric is not specifically limited, From a viewpoint of the water absorption by hydrophilicity and a water retention improvement, it contains 80 mass% or more of 2nd regenerated cellulose fibers, More preferably, it contains 90 mass% or more, More preferably, it is 95. It is contained in an amount of not less than mass%, particularly preferably 100 mass%. The fineness of the second regenerated cellulose fiber is not particularly limited, but is preferably 0.5 to 1.0 dtex, and preferably 0.7 to 0.95 dtex from the viewpoint of improving the diffusibility of absorbed moisture and improving water retention. It is more preferable. The second regenerated cellulose fiber is not particularly limited, but considering the card passing property, the fiber length is preferably 25 mm or more and less than 65 mm, more preferably 28 to 60 mm, and 35 to 55 mm. Is more preferable. The second regenerated cellulose fiber may be any fiber such as a viscose rayon fiber, a copper ammonia rayon fiber, or a solvent-spun cellulose fiber, but is preferably a viscose rayon fiber. Viscose rayon fibers usually have a chrysanthemum fiber cross section and have streaks in the axial direction of the fiber surface, so that they have excellent moisture mobility on the fiber surface and moisture retention between fibers. Moreover, the special reproduction | regeneration cellulose fiber can be used from a viewpoint of being excellent in water retention similarly to the case of the 1st cellulose fiber. Furthermore, the regenerated cellulose fibers themselves may be functional regenerated cellulose fibers such as deodorant, antibacterial and antiallergenic properties.
上記第２不織布は、第２の再生セルロース繊維に加えて、他の繊維を含んでもよい。他の繊維としては、本発明の効果を阻害しない範囲内で適宜選択して用いることができる。他の繊維としては、例えば、コットン、麻などの天然繊維、アクリル系繊維、ポリエステル系繊維、ポリアミド系繊維、ポリオレフィン系繊維、ポリウレタン系繊維などの合成繊維を用いることができる。また、他の繊維として、消臭性繊維、抗菌性繊維、抗アレルゲン性繊維などの機能性繊維を用いてもよい。他の繊維としては、上述した繊維から、１種又は複数種の繊維を用途等に応じて適宜に選択することができる。上記他の繊維は、特に限定されないが、繊度が１．０〜１．６ｄｔｅｘであることが好ましく、より好ましくは１．０〜１．４ｄｔｅｘであり、さらに好ましくは１．０〜１．２ｄｔｅｘである。上記他の繊維は、特に限定されないが、カード通過性を考慮すると、繊維長は２５ｍｍ以上６５ｍｍ未満であることが好ましく、２８〜６０ｍｍであることがより好ましく、３５〜５５ｍｍであることがさらに好ましい。 The second nonwoven fabric may contain other fibers in addition to the second regenerated cellulose fiber. Other fibers can be appropriately selected and used within a range that does not impair the effects of the present invention. Examples of other fibers include natural fibers such as cotton and hemp, and synthetic fibers such as acrylic fibers, polyester fibers, polyamide fibers, polyolefin fibers, and polyurethane fibers. Moreover, you may use functional fibers, such as a deodorizing fiber, an antibacterial fiber, and an antiallergenic fiber, as another fiber. As the other fibers, one or more kinds of fibers can be appropriately selected from the above-described fibers depending on the application. The other fibers are not particularly limited, but the fineness is preferably 1.0 to 1.6 dtex, more preferably 1.0 to 1.4 dtex, and still more preferably 1.0 to 1.2 dtex. is there. The other fibers are not particularly limited, but considering the card passing property, the fiber length is preferably 25 mm or more and less than 65 mm, more preferably 28 to 60 mm, and further preferably 35 to 55 mm. .
上記第１不織布の構成繊維と上記第２不織布の構成繊維の平均繊度比は、特に限定されないが、吸液速度の向上及び水分の逆戻りの抑制という観点から、１／０．２５〜１／０．７０であることが好ましく、より好ましくは１／０．３０〜１／０．６５であり、さらに好ましくは１／０．３５〜１／０．６０である。 The average fineness ratio of the constituent fibers of the first nonwoven fabric and the constituent fibers of the second nonwoven fabric is not particularly limited, but is 1 / 0.25 to 1/0 from the viewpoint of improving the liquid absorption rate and suppressing the reversion of moisture. Is preferably .70, more preferably 1 / 0.30 to 1 / 0.65, and even more preferably 1 / 0.35 to 1 / 0.60.
上記吸収体の第１実施形態において、上記第１不織布は水流交絡不織布であり、上記第２不織布はニードルパンチ不織布であることが好ましい。水流交絡不織布では、構成繊維の繊維軸が比較的不織布の平面方向に配向するため、水分の拡散吸収性及び水分の逆戻りの抑制効果に優れる。ニードルパンチ不織布では、構成繊維の繊維軸が比較的不織布の厚み方向に配向するため、水分の吸水性及び保水性に優れる。該実施形態において、吸収体の上層が水流交絡不織布で構成され、下層がニードルパンチ不織布で構成されているので、上層の水流交絡不織布全面に拡散して吸収された尿などの水分が下層のニードルパンチ不織布に吸収保持されるとともに、水分の逆戻りも抑制されている。 In 1st Embodiment of the said absorber, it is preferable that a said 1st nonwoven fabric is a hydroentangled nonwoven fabric, and a said 2nd nonwoven fabric is a needle punch nonwoven fabric. In the hydroentangled nonwoven fabric, the fiber axes of the constituent fibers are relatively oriented in the plane direction of the nonwoven fabric, so that it is excellent in moisture diffusion and absorbability and moisture suppression effect. In the needle punched nonwoven fabric, the fiber axes of the constituent fibers are relatively oriented in the thickness direction of the nonwoven fabric, and thus are excellent in water absorption and water retention. In this embodiment, since the upper layer of the absorbent body is composed of hydroentangled nonwoven fabric and the lower layer is composed of needle punched nonwoven fabric, moisture such as urine diffused and absorbed throughout the entire upper layer hydroentangled nonwoven fabric While being absorbed and held by the punched nonwoven fabric, the return of moisture is also suppressed.
第１実施形態の吸収体において、上層の水流交絡不織布は、下層のニードルパンチ不織布より、比容積が大きいことが好ましい。下層のニードルパンチ不織布が上層の水流交絡不織布より比容積が小さく、高密度であることにより、尿などの水分を保持しやすく、水分の逆戻りが抑制されやすい。上記水流交絡不織布は、特に限定されないが、水分の拡散吸収と水分の逆戻りの抑制という観点から、比容積が９．０〜２０ｃｍ3／ｇであることが好ましく、９．５〜１８ｃｍ3／ｇであることがより好ましい。上記ニードルパンチ不織布は、特に限定されないが、水分の逆戻りの抑制という観点から、比容積が６．５〜２０ｃｍ3／ｇであることが好ましく、７．０〜１８ｃｍ3／ｇであることがより好ましい。 In the absorbent body of the first embodiment, the upper layer hydroentangled nonwoven fabric preferably has a larger specific volume than the lower layer needle punched nonwoven fabric. Since the lower layer needle punched nonwoven fabric has a smaller specific volume and higher density than the upper layer hydroentangled nonwoven fabric, it is easy to retain moisture such as urine, and moisture reversion is easily suppressed. The hydroentangled non-woven fabric is not particularly limited, but the specific volume is preferably 9.0 to 20 cm 3 / g, preferably 9.5 to 18 cm 3 / g, from the viewpoint of diffusion absorption of moisture and suppression of moisture reversion. It is more preferable that The needle punched nonwoven fabric is not particularly limited, but it is preferable from the viewpoint of moisture reversion inhibition, specific volume is 6.5~20cm 3 / g, and more to be 7.0~18cm 3 / g preferable.
第１実施形態の吸収体において、上層の水流交絡不織布は、下層のニードルパンチ不織布より、目付及び/又は厚みが小さいことが好ましい。尿などの水分に対する吸液速度が速くなりやすい。上記水流交絡不織布は、特に限定されないが、吸水量向上の観点から、目付が３０〜７０ｇ／ｍ2であることが好ましく、３５〜６０ｇ／ｍ2であることがより好ましい。上記ニードルパンチ不織布は、特に限定されないが、吸水量及び保水性向上ならびに水分の逆戻りの抑制という観点から、目付が７０〜１３０ｇ／ｍ2であることが好ましく、７５〜１２５ｇ／ｍ2であることがより好ましい。上記水流交絡不織布は、特に限定されないが、吸水時の液移動性の観点から、厚みが０．４〜０．８ｍｍであることが好ましく、０．４５〜０．７５ｍｍであることがより好ましい。上記ニードルパンチ不織布は、特に限定されないが、水分の逆戻りの抑制という観点から、厚みが０．６〜１．６ｍｍであることが好ましく、０．６５〜１．５ｍｍであることがより好ましい。 In the absorbent body according to the first embodiment, the upper layer hydroentangled nonwoven fabric preferably has a smaller basis weight and / or thickness than the lower layer needle punched nonwoven fabric. The liquid absorption rate for water such as urine tends to increase. The hydroentangled nonwoven fabric is not particularly limited, from the viewpoint of water absorption improved, it is preferable that the basis weight is 30~70g / m 2, and more preferably 35~60g / m 2. The needle punched nonwoven fabric is not particularly limited, from the viewpoint of water absorption and water retention improver and water reversion inhibition is preferably basis weight is 70~130g / m 2, a 75~125g / m 2 Is more preferable. Although the said hydroentangled nonwoven fabric is not specifically limited, From a viewpoint of the liquid mobility at the time of water absorption, it is preferable that thickness is 0.4-0.8 mm, and it is more preferable that it is 0.45-0.75 mm. The needle punched nonwoven fabric is not particularly limited, but the thickness is preferably 0.6 to 1.6 mm, and more preferably 0.65 to 1.5 mm, from the viewpoint of suppressing the reversion of moisture.
第１実施形態の吸収体において、好ましくは、上層の水流交絡不織布が、下層のニードルパンチ不織布より、構成繊維の平均繊度が大きく、比容積が大きく、目付及び/又は厚みが小さいことにより、より効果的に、吸液速度が向上し、水分の逆戻りが抑制される。また、下層のニードルパンチ不織布が、上層の水流交絡不織布より、構成繊維の平均繊度が小さく、比容積が小さいことにより、より効果的に、保水性が向上し、水分の逆戻りが抑制される。 In the absorbent body according to the first embodiment, preferably, the upper layer hydroentangled nonwoven fabric has a larger average fineness of the constituent fibers, a larger specific volume, and a smaller basis weight and / or thickness than the lower layer needle punched nonwoven fabric. Effectively, the liquid absorption speed is improved and the return of moisture is suppressed. Further, the lower needle punched nonwoven fabric has a smaller average fineness of the constituent fibers and a smaller specific volume than the upper layer hydroentangled nonwoven fabric, so that the water retention is more effectively improved and the reversion of moisture is suppressed.
第２実施形態の吸収体において、上記第１不織布と上記第２不織布は共にニードルパンチ不織布で構成されていることが好ましく、上記第１不織布のニードルパンチ不織布（上層のニードルパンチ不織布）は、上記第２不織布のニードルパンチ不織布（下層のニードルパンチ不織布）より比容積が小さいことがより好ましい。上層のニードルパンチ不織布が下層のニードルパンチ不織布より、構成繊維の繊度が大きく、比容積が小さい（高密度）ことにより、より効果的に、吸液速度が向上し、水分の逆戻りが抑制される。また、下層のニードルパンチ不織布が上層のニードルパンチ不織布より、構成繊維の繊度が小さく、比容積が大きい（低密度）ことにより、より効果的に、保水性が向上し、水分の逆戻りが抑制される。該実施形態の吸収体においては、上層のニードルパンチ不織布の表面にスポット吸収された尿などの水分が下層のニードルパンチ不織布で拡散吸収される。 In the absorbent body of the second embodiment, the first nonwoven fabric and the second nonwoven fabric are preferably both needle punched nonwoven fabrics, and the needle punched nonwoven fabric (upper needle punched nonwoven fabric) of the first nonwoven fabric is It is more preferable that the specific volume is smaller than that of the needle punch nonwoven fabric (lower needle punch nonwoven fabric) of the second nonwoven fabric. The upper layer needle punched nonwoven fabric has a finer fiber and lower specific volume (high density) than the lower layer needle punched nonwoven fabric, so that the liquid absorption rate is improved more effectively and the reversion of moisture is suppressed. . In addition, the lower needle punched nonwoven fabric is smaller than the upper needle punched nonwoven fabric in that the fineness of the constituent fibers is smaller and the specific volume is larger (low density), so that the water retention is more effectively improved and the reversion of moisture is suppressed. The In the absorbent body of this embodiment, moisture such as urine spot-absorbed on the surface of the upper needle punched nonwoven fabric is diffused and absorbed by the lower needle punched nonwoven fabric.
第２実施形態の吸収体において、上記第１不織布のニードルパンチ不織布は、特に限定されないが、吸液速度の向上と水分の逆戻りの抑制という観点から、比容積が７．０〜２０ｃｍ3／ｇであることが好ましく、８．０〜１８ｃｍ3／ｇであることがより好ましい。上記下層のニードルパンチ不織布は、特に限定されないが、水分の逆戻りの抑制という観点から、比容積が９．０〜２０ｃｍ3／ｇであることが好ましく、９．５〜１８ｃｍ3／ｇであることがより好ましい。 In the absorbent body of the second embodiment, the needle punched nonwoven fabric of the first nonwoven fabric is not particularly limited, but the specific volume is 7.0 to 20 cm 3 / g from the viewpoint of improving the liquid absorption speed and suppressing the return of moisture. It is preferable that it is 8.0-18 cm < 3 > / g. That said lower layer of needle punched nonwoven fabric is not particularly limited, from the viewpoint of moisture back inhibition, it specific volume is 9.0~20cm 3 / g and preferably, 9.5~18cm 3 / g Is more preferable.
第２実施形態の吸収体において、第１不織布及び第２不織布（上層及び下層のニードルパンチ不織布）は、特に限定されないが、吸水量及び保水性向上の観点から、目付が５０〜１００ｇ／ｍ2であることが好ましく、５５〜９５ｇ／ｍ2であることがより好ましい。また、第１不織布及び第２不織布（上層及び下層のニードルパンチ不織布）は、特に限定されないが、吸水時の液移動性向上の観点から、厚みが０．５〜１．０ｍｍであることが好ましく、０．６〜０．９ｍｍであることがより好ましい。 In the absorbent body of the second embodiment, the first nonwoven fabric and the second nonwoven fabric (upper layer and lower layer needle punched nonwoven fabric) are not particularly limited, but the basis weight is 50 to 100 g / m 2 from the viewpoint of water absorption and water retention improvement. It is preferable that it is 55-95 g / m < 2 >. Further, the first nonwoven fabric and the second nonwoven fabric (upper layer and lower layer needle punched nonwoven fabric) are not particularly limited, but the thickness is preferably 0.5 to 1.0 mm from the viewpoint of improving liquid mobility at the time of water absorption. More preferably, the thickness is 0.6 to 0.9 mm.
上記吸収体は、特に限定されないが、水分の逆戻りの抑制という観点から、比容積が８．０〜２０ｃｍ3／ｇであることが好ましく、より好ましくは８．０〜１８ｃｍ3／ｇである。第２実施形態の吸収体においては、比容積が大きいほど、吸液速度が速くなる傾向がある。 Although the said absorber is not specifically limited, From a viewpoint of suppression of a reversion | return of a water | moisture content, it is preferable that a specific volume is 8.0-20 cm < 3 > / g, More preferably, it is 8.0-18 cm < 3 > / g. In the absorber of the second embodiment, the liquid absorption rate tends to increase as the specific volume increases.
上記吸収体は、特に限定されないが、吸水性、着用感及び耐洗濯性の観点から、厚みが１．０〜２．０ｍｍであることが好ましく、より好ましくは１．２〜２．０ｍｍである。 Although the said absorber is not specifically limited, From a viewpoint of water absorption, a feeling of wear, and washing resistance, it is preferable that thickness is 1.0-2.0 mm, More preferably, it is 1.2-2.0 mm. .
上記吸収体は、特に限定されないが、吸水性、着用感及び耐洗濯性の観点から、目付が１００〜３００ｇ／ｍ2であることが好ましく、より好ましくは１００〜２１０ｇ／ｍ2であり、さらに好ましくは１１０〜１８０ｇ／ｍ2であり、さらにより好ましくは１２０〜１７０ｇ／ｍ2である。 Although the said absorber is not specifically limited, It is preferable that a fabric weight is 100-300 g / m < 2 > from a viewpoint of water absorption, a feeling of wear, and washing resistance, More preferably, it is 100-210 g / m < 2 >, Furthermore, Preferably it is 110-180 g / m < 2 >, More preferably, it is 120-170 g / m < 2 >.
第２実施形態の吸収体において、積層は特に限定されないが、あらかじめニードルパンチ処理をした第２不織布の上に、あらかじめニードルパンチ処理をした第１不織布を重ね合わせる方法の他、第２不織布を構成する繊維ウェブの上に第１不織布を構成する繊維ウェブを重ね合わせた後、ニードルパンチ処理により一体化する方法であってもよい。 In the absorbent body of the second embodiment, the lamination is not particularly limited, but the second nonwoven fabric is constituted in addition to the method of superimposing the first nonwoven fabric previously needle-punched on the second nonwoven fabric previously needle-punched. Alternatively, a method may be used in which the fiber web constituting the first nonwoven fabric is superimposed on the fiber web to be integrated and then integrated by needle punching.
上記吸収体は、ウェットバック率が５２％以下であることが好ましく、より好ましくは５１．５％以下であり、さらに好ましくは５０％以下である。本発明において、ウェットバック率は水分の逆戻りの指標であり、ウェットバック率が低いほど水分の逆戻りが少ないことを意味する。本発明において、吸収体のウェットバック率は、後述するとおりに、吸水／ウェットバック試験により測定評価する。 The absorbent body preferably has a wetback rate of 52% or less, more preferably 51.5% or less, and even more preferably 50% or less. In the present invention, the wetback rate is an index of moisture reversion, and the lower the wetback rate, the less moisture reversion. In the present invention, the wet back rate of the absorber is measured and evaluated by a water absorption / wet back test as described later.
上記吸収体は、吸水率が４５％以上であることが好ましく、より好ましくは５０％以上であり、さらに好ましくは５５％以上である。本発明において、吸水率は保水性の指標であり、吸水率が高いほど保水性に優れることを意味する。本発明において、吸収体の吸水率は、後述するとおりに、吸水／ウェットバック試験により測定評価する。 The absorbent body preferably has a water absorption rate of 45% or more, more preferably 50% or more, and still more preferably 55% or more. In the present invention, the water absorption is an index of water retention, and the higher the water absorption, the better the water retention. In the present invention, the water absorption rate of the absorber is measured and evaluated by a water absorption / wetback test as described later.
上記吸収体は、吸液時間が４．０秒以下であることが好ましく、より好ましくは３．９５秒以下であり、さらに好ましくは３．９０秒以下であり、さらにより好ましくは３．５０秒以下であり、特に好ましくは３．０秒以下である。本発明において、吸収体の吸液時間は、後述するとおりに、吸水／ウェットバック試験により測定評価する。 The absorber preferably has a liquid absorption time of 4.0 seconds or less, more preferably 3.95 seconds or less, still more preferably 3.90 seconds or less, and even more preferably 3.50 seconds. Or less, and particularly preferably 3.0 seconds or less. In the present invention, the liquid absorption time of the absorber is measured and evaluated by a water absorption / wetback test as described later.
＜吸水／ウェットバック試験＞
（１）試料（吸収体）、表面シート(エアスルー不織布、目付５０ｇ／ｍ2、厚み０．８６ｍｍ（１９６０Ｐａ荷重時）、ＰＥＴ／ＰＥ製）)をそれぞれ１０ｃｍ角にカットして質量を測定し、それぞれ、試料の吸水前質量、表面シートの吸水前質量とする。
（２）１０ｃｍ角にカットした濾紙（東洋濾紙社製、ＡＤＶＡＮＴＥＣ（登録商標） Ｎｏ．２）を２０枚重ね、質量を測定し、濾紙の吸水前質量とする。
（３）１０ｃｍ角の樹脂板（塩化ビニル樹脂製）上に、試料、表面シート、注水板（アクリル樹脂製、１０ｃｍ角、中央に１０ｍｍ直径の孔（注水口）を有する）をこの順番に重ね置きする。
（４）水６ｍｌを注水口から注加し、注加直後から水が全量吸収されるまでの時間を計測し、吸液時間とする。
（５）注水板を除いた表面シート上に、上記（２）で準備した濾紙２０枚、１０ｃｍ角の樹脂板（塩化ビニル樹脂製）、４ｋｇ分銅をこの順に重ね置きし、３９２０Ｐａ（４０ｇｆ／ｃｍ2）の荷重を３分間加える。
（６）荷重除去後、試料、濾紙（２０枚）及び表面シートの質量をそれぞれ測定し、それぞれ、試料、濾紙及び表面シートの吸水後質量とする。
（７）下記式により、試料（吸収体）の吸水量、表面シートの吸水量、ウェットバック量を算出する。そして、下記式により、吸収体の吸水量、表面シートの吸水量及びウェットバック量の合計に対する吸収体の吸水量及びウェットバック量の比率を求め、それぞれ、吸収体の吸水率及びウェットバック率とする。
吸水体の吸水量（ｇ）＝試料の吸水後質量（ｇ）−試料の吸水前質量（ｇ）
表面シートの吸水量（ｇ）＝表面シートの吸水後質量（ｇ）−表面シートの吸水前質量（ｇ）
ウェットバック量（ｇ）＝濾紙の吸水後質量（ｇ）−濾紙の吸水前質量（ｇ）
吸収体の吸水率（％）＝[吸水体の吸水量（ｇ）／（吸収体の吸水量＋表面シートの吸水量＋ウェットバック量）（ｇ）]×１００
吸収体のウェットバック率（％）＝[ウェットバック量（ｇ）／（吸収体の吸水量＋表面シートの吸水量＋ウェットバック量）（ｇ）]×１００
<Water absorption / wet back test>
(1) Sample (absorber), surface sheet (air-through non-woven fabric, basis weight 50 g / m 2 , thickness 0.86 mm (at 1960 Pa load), made of PET / PE)) are cut into 10 cm squares, and the mass is measured. The mass before water absorption of the sample and the mass before water absorption of the surface sheet are used respectively.
(2) 20 sheets of filter paper (ADVANTEC (registered trademark) No. 2 manufactured by Toyo Roshi Kaisha Co., Ltd.) cut into 10 cm squares are stacked, and the mass is measured to obtain the mass of the filter paper before water absorption.
(3) On a 10 cm square resin plate (made of vinyl chloride resin), a sample, a surface sheet, and a water injection plate (made of acrylic resin, 10 cm square, with a 10 mm diameter hole (water injection port) in the center) are stacked in this order. Put.
(4) 6 ml of water is added from the water injection port, and the time from immediately after the addition until the entire amount of water is absorbed is measured and is defined as the liquid absorption time.
(5) On the top sheet excluding the water injection plate, 20 sheets of filter paper prepared in (2) above, 10 cm square resin plate (made of vinyl chloride resin), 4 kg weight were stacked in this order, 3920 Pa (40 gf / cm Apply the load of 2 ) for 3 minutes.
(6) After removing the load, the masses of the sample, the filter paper (20 sheets), and the surface sheet are measured, and the mass after water absorption of the sample, the filter paper, and the surface sheet, respectively.
(7) The water absorption amount of the sample (absorber), the water absorption amount of the top sheet, and the wet back amount are calculated by the following formula. Then, the ratio of the water absorption amount and the wet back amount of the absorber with respect to the sum of the water absorption amount of the absorber, the water absorption amount of the top sheet and the wet back amount is obtained by the following formula, and the water absorption rate and the wet back rate of the absorber respectively. To do.
Water absorption amount of water absorbent (g) = mass after water absorption of sample (g) −mass before water absorption of sample (g)
Water absorption amount of top sheet (g) = mass after water absorption of top sheet (g) −mass before water absorption of top sheet (g)
Wet back amount (g) = mass after water absorption of filter paper (g) −mass before water absorption of filter paper (g)
Absorbent water absorption rate (%) = [water absorption amount of the water absorber (g) / (water absorption amount of the absorber + water absorption amount of the top sheet + wet back amount) (g)] × 100
Absorbent wetback rate (%) = [wetback amount (g) / (absorber water absorption + surface sheet water absorption + wetback amount) (g)] × 100
第１実施形態の吸収体は、吸水面において、拡散面積比が４０％以上であることが好ましく、４５％以上であることがより好ましく、５０％以上であることがさらに好ましい。第２実施形態の吸収体は、裏面（吸水面の反対面）において、拡散面積比が３５％以上であることが好ましく、４０％以上であることがより好ましく、４５％以上であることがさらに好ましい。本発明において、拡散面積比は水分の拡散吸収性を評価する指標であり、拡散面積比が高いほど水分の拡散吸収性に優れることを意味する。本発明において、吸収体の拡散面積比は、後述するとおりに、拡散性試験により測定評価する。 The absorbent body according to the first embodiment preferably has a diffusion area ratio of 40% or more, more preferably 45% or more, and further preferably 50% or more on the water absorption surface. In the absorber of the second embodiment, the diffusion area ratio is preferably 35% or more, more preferably 40% or more, and further preferably 45% or more on the back surface (opposite surface of the water absorption surface). preferable. In the present invention, the diffusion area ratio is an index for evaluating the diffusion and absorption of moisture, and the higher the diffusion area ratio, the better the diffusion and absorption of moisture. In the present invention, the diffusion area ratio of the absorber is measured and evaluated by a diffusivity test as described later.
＜拡散性試験＞
（１）５ｃｍ角にカットした吸収体（試料）を樹脂板（塩化ビニル樹脂製、５ｃｍ角）上に配置する。
（２）試料上３ｃｍに先端位置を調整したビュレットから、着色水（食用色素 黄（共立食品社）０．３％水溶液）を０．５ｍｌ注加した後、試料上に５ｃｍ角の濾紙２０枚、５ｃｍ角の樹脂板（塩化ビニル樹脂製）、４ｋｇ分銅をこの順に重ね置きし、３９２０Ｐａ（４０ｇｆ／ｃｍ2）の荷重を３分間加える。
（３）荷重を除去した後、試料表面及び裏面における注加液（着色水）の拡散状態をデジ タルカメラ（ＯＬＹＭＰＵＳ社製、型番「ＳＰ−３５０」）で写真撮影する。
（４）注加液の拡散領域の面積を印刷紙面上で計測し、下式により、試料面積（２５ｃｍ 2）に対する試料表面（吸水面）及び裏面（吸水面の反対面）における拡散領域の面積 の比率を求め、拡散面積比とする。
拡散面積比（％）＝[拡散領域の面積（ｃｍ2）／２５（ｃｍ2）]×１００
<Diffusion test>
(1) An absorber (sample) cut into a 5 cm square is placed on a resin plate (made of vinyl chloride resin, 5 cm square).
(2) After adding 0.5 ml of colored water (food dye yellow (0.3% aqueous solution of Kyoritsu Foods)) from a burette whose tip position is adjusted to 3 cm above the sample, 20 pieces of 5 cm square filter paper are placed on the sample. A 5 cm square resin plate (made of vinyl chloride resin) and a 4 kg weight are stacked in this order, and a load of 3920 Pa (40 gf / cm 2 ) is applied for 3 minutes.
(3) After removing the load, the diffusion state of the pouring liquid (colored water) on the front and back surfaces of the sample is photographed with a digital camera (model number “SP-350” manufactured by OLYMPUS).
(4) The area of the diffusion region of the pouring liquid is measured on the surface of the printing paper, and the area of the diffusion region on the sample surface (water absorption surface) and back surface (opposite to the water absorption surface) with respect to the sample area (25 cm 2 ) by the following formula Is determined as the diffusion area ratio.
Diffusion area ratio (%) = [area of diffusion region (cm 2 ) / 25 (cm 2 )] × 100
上記水流交絡不織布は、繊維ウェブに水流交絡処理を施すことにより作製することができる。繊維ウェブの形態は、特に限定されず、パラレルウェブ、クロスウェブ、クリスクロスウェブ、セミランダムウェブ及びランダムウェブ等のカードウェブ、エアレイウェブ、湿式抄紙ウェブ、ならびにスパンボンドウェブ等から選択されるいずれの形態であってもよい。繊維ウェブは、水流交絡処理による交絡性を考慮すると、カードウェブであることが好ましい。 The hydroentangled nonwoven fabric can be produced by subjecting the fiber web to hydroentanglement treatment. The form of the fiber web is not particularly limited, and any one selected from a card web such as a parallel web, a cross web, a Chris cross web, a semi-random web and a random web, an airlaid web, a wet papermaking web, and a spunbond web. It may be a form. The fiber web is preferably a card web in consideration of entanglement due to hydroentanglement treatment.
水流交絡処理条件は、特に限定されず、一般的な条件であればよく、繊維ウェブの目付及び繊維ウェブの搬送支持体の速度等に応じて適宜設定することができる。例えば、孔径０．０５〜０．５ｍｍのオリフィスが、０．５〜１．５ｍｍの間隔で設けられたノズルから、水圧１〜１０ＭＰａの水流を、繊維ウェブの表裏面側からそれぞれ１〜４回ずつ噴射するとよい。好ましい水圧は、１．５〜４ＭＰａである。水流噴射処理後、乾燥処理に付する。乾燥処理は、例えば、熱風乾燥器を用いて実施される。乾燥温度は、例えば、４０〜１００℃であればよい。或いは、乾燥処理は、自然乾燥でもよい。 The hydroentanglement processing conditions are not particularly limited, and may be general conditions, and can be appropriately set according to the basis weight of the fiber web, the speed of the transport support of the fiber web, and the like. For example, from a nozzle in which orifices having a hole diameter of 0.05 to 0.5 mm are provided at intervals of 0.5 to 1.5 mm, a water flow with a water pressure of 1 to 10 MPa is applied 1 to 4 times from the front and back sides of the fiber web. It is good to inject one by one. A preferable water pressure is 1.5 to 4 MPa. After the water jet process, it is subjected to a drying process. A drying process is implemented using a hot air dryer, for example. A drying temperature should just be 40-100 degreeC, for example. Alternatively, the drying process may be natural drying.
上記ニードルパンチ不織布は、繊維ウェブにニードルパンチ処理を施すことにより作製することができる。繊維ウェブの形態は、特に限定されず、パラレルウェブ、クロスウェブ、クリスクロスウェブ、セミランダムウェブ及びランダムウェブ等のカードウェブ、エアレイウェブ、湿式抄紙ウェブ、ならびにスパンボンドウェブ等から選択されるいずれの形態であってもよい。 The needle punched nonwoven fabric can be produced by subjecting the fiber web to needle punching. The form of the fiber web is not particularly limited, and any one selected from a card web such as a parallel web, a cross web, a Chris cross web, a semi-random web and a random web, an airlaid web, a wet papermaking web, and a spunbond web. It may be a form.
ニードルパンチ処理の条件は、特に限定されず、従来から知られているニードルパンチ不織布を製造する際の条件で行うことができる。例えば、ニードルパンチの針本数を２００〜６００本/ｃｍ2にすることが好ましい。 The conditions for the needle punch treatment are not particularly limited, and can be performed under the conditions for producing conventionally known needle punch nonwoven fabrics. For example, the number of needle punch needles is preferably 200 to 600 / cm 2 .
本発明の吸収体は、必要に応じて、消臭剤、抗菌剤、アレルゲン分解剤などの機能剤を含有しても良い。また、吸水性を調整するために、高吸水性樹脂（Superabsorbent polymer、略称：ＳＡＰ）を担持させても良い。 The absorber of the present invention may contain a functional agent such as a deodorant, an antibacterial agent, and an allergen decomposing agent, if necessary. In order to adjust water absorption, a superabsorbent polymer (abbreviation: SAP) may be supported.
（吸収性物品及び失禁用品）
本発明の吸収性物品は、上記吸収体を含むものであればよく、特に限定されない。例えば、上記吸収性物品は、吸収体の表面（第１不織布側）には主に装着者の肌に当接する表面シート（表生地）が配置され、吸収体の裏面（第２不織布側）には液体を外に漏れさせない防漏シート（防水生地）が配置されていてもよい。上記吸収性物品としては、例えば、生理用ナプキン；おりものシート；失禁パッド、失禁ライナー、失禁用ショーツ、失禁用パンツ等の失禁用品等が挙げられる。上記表面シート及び防漏シートとしては、特に限定されず、通常、吸収性物品に使用するものを用いることができる。
(Absorbent articles and incontinence products)
The absorbent article of this invention should just contain the said absorber, and is not specifically limited. For example, in the absorbent article, a surface sheet (front fabric) that mainly contacts the skin of the wearer is disposed on the surface of the absorbent body (first nonwoven fabric side), and on the back surface (second nonwoven fabric side) of the absorbent body. May be provided with a leak-proof sheet (waterproof fabric) that does not allow liquid to leak out. Examples of the absorbent article include sanitary napkins; vaginal sheets; incontinence articles such as incontinence pads, incontinence liners, incontinence shorts, and incontinence pants. It does not specifically limit as said surface sheet and leak-proof sheet, Usually, what is used for an absorbent article can be used.
上記吸収性物品は、失禁パッド、失禁ライナー、失禁用ショーツ、失禁用パンツ等の失禁用品として用いることが好ましい。上記失禁用品において、吸収体は尿受け部として機能する。上記吸収体、上記吸収性物品及び上記失禁用品は、尿が１０〜１００ｃｃ程度の軽度失禁から重度失禁対応型として好適であり、特に、尿が１０〜３０ｃｃ程度の軽度失禁対応型として好適である。 The absorbent article is preferably used as an incontinence article such as an incontinence pad, incontinence liner, incontinence shorts, incontinence pants. In the incontinence product, the absorber functions as a urine receiving part. The absorbent body, the absorbent article, and the incontinence article are suitable as a mild incontinence type with a urine of about 10 to 100 cc, and particularly suitable as a mild incontinence type with a urine of about 10 to 30 cc. .
以下、実施例により、本発明をさらに具体的に説明するが、本発明はこれらの実施例に限定されない。 EXAMPLES Hereinafter, although an Example demonstrates this invention further more concretely, this invention is not limited to these Examples.
実施例及び比較例では、下記の繊維を用いた。 In the examples and comparative examples, the following fibers were used.
繊維１：レーヨン繊維、繊度０．９ｄｔｅｘ、繊維長３８ｍｍ、ダイワボウレーヨン社製、品名「コロナ（ＢＨ）」、以下において、単に「ＢＨ０．９ｄｔｅｘ」とも記す。
繊維２：レーヨン繊維、繊度１．７ｄｔｅｘ、繊維長４０ｍｍ、ダイワボウレーヨン社製、品名「コロナ（ＣＤ）」、以下において、単に「ＣＤ１．７ｄｔｅｘ」とも記す。
繊維３：レーヨン繊維、繊度２．２ｄｔｅｘ、繊維長５１ｍｍ、ダイワボウレーヨン社製、品名「コロナ（ＲＢ）」、以下において、単に「ＲＢ２．２ｄｔｅｘ」とも記す。
繊維４：レーヨン繊維、繊度３．３ｄｔｅｘ、繊維長５１ｍｍ、ダイワボウレーヨン社製、品名「コロナ（ＣＤ）」、以下において、単に「ＣＤ３．３ｄｔｅｘ」とも記す。
繊維５：ポリエチレンテレフタレート繊維、繊度１．４２ｄｔｅｘ、繊維長３８ｍｍ、東レ社製、品名「４０２」、以下において、単に「ＰＥＴ１．４２ｄｔｅｘ」とも記す。
Fiber 1: Rayon fiber, fineness 0.9 dtex, fiber length 38 mm, manufactured by Daiwabo Rayon Co., Ltd., product name “Corona (BH)”, hereinafter also simply referred to as “BH 0.9 dtex”.
Fiber 2: Rayon fiber, fineness 1.7 dtex, fiber length 40 mm, manufactured by Daiwabo Rayon Co., Ltd., product name “Corona (CD)”, hereinafter, also simply referred to as “CD 1.7 dtex”.
Fiber 3: Rayon fiber, fineness 2.2 dtex, fiber length 51 mm, manufactured by Daiwabo Rayon Co., Ltd., product name “Corona (RB)”, hereinafter, also simply referred to as “RB2.2 dtex”.
Fiber 4: Rayon fiber, fineness 3.3 dtex, fiber length 51 mm, manufactured by Daiwabo Rayon Co., Ltd., product name “Corona (CD)”, hereinafter, also simply referred to as “CD 3.3 dtex”.
Fiber 5: Polyethylene terephthalate fiber, fineness 1.42 dtex, fiber length 38 mm, manufactured by Toray Industries, Inc., product name “402”, hereinafter also simply referred to as “PET 1.42 dtex”.
実施例及び比較例において、水流交絡不織布及びニードルパンチ不織布は下記のように作製した。 In Examples and Comparative Examples, hydroentangled nonwoven fabrics and needle punched nonwoven fabrics were prepared as follows.
＜水流交絡不織布の作製＞
繊維をセミランダムカードで解繊して所定の目付のカードウェブを作製した。次いで、ノズル孔径０．１３ｍｍのオリフィスが１ｍｍ間隔で配置されたノズルから、ウェブ表面から２ＭＰａ、ウェブ裏面から３ＭＰａの水圧で水流を噴射した後、自然乾燥させて、水流交絡不織布を作製した。
<Production of hydroentangled nonwoven fabric>
The fiber was defibrated with a semi-random card to produce a card web with a predetermined basis weight. Next, from a nozzle in which orifices having a nozzle hole diameter of 0.13 mm were arranged at intervals of 1 mm, a water flow was jetted with a water pressure of 2 MPa from the web surface and 3 MPa from the web back surface, and then naturally dried to produce a hydroentangled nonwoven fabric.
＜ニードルパンチ不織布の作製＞
繊維をセミランダムカードで解繊して所定の目付のカードウェブを作製した。次いで、以下の条件により両面のニードルパンチ処理を行い、ニードルパンチ不織布を作製した。
使用ニードル：４０番手、バーブ数６；ペネ数：６４本／ｃｍ２（単位面積当たりの針の打ち込み本数）；針深度：１０ｍｍ
<Production of needle punched nonwoven fabric>
The fiber was defibrated with a semi-random card to produce a card web with a predetermined basis weight. Next, needle punching on both sides was performed under the following conditions to produce a needle punched nonwoven fabric.
Needle used: 40th, barb number 6; Number of penets: 64 / cm 2 (number of needles driven per unit area); Needle depth: 10 mm
（実施例1〜３、比較例１〜５）
下記表１に示すように、ニードルパンチ不織布又は水流交絡不織布を第１不織布として用い、ニードルパンチ不織布を第２不織布として用い、第２不織布の表面上に第１不織布を積層して、積層不織布を得た。第１不織布（上層）及び第２不織布（下層）に用いた不織布の厚み及び目付を下記表１に示した。不織布の厚み及び目付は、下記のように測定したものである。
(Examples 1 to 3, Comparative Examples 1 to 5)
As shown in Table 1 below, a needle punched nonwoven fabric or hydroentangled nonwoven fabric is used as the first nonwoven fabric, a needle punched nonwoven fabric is used as the second nonwoven fabric, the first nonwoven fabric is laminated on the surface of the second nonwoven fabric, and a laminated nonwoven fabric is obtained. Obtained. The thickness and basis weight of the nonwoven fabric used for the first nonwoven fabric (upper layer) and the second nonwoven fabric (lower layer) are shown in Table 1 below. The thickness and basis weight of the nonwoven fabric are measured as follows.
実施例1〜３、比較例１〜５で得られた吸収体（積層不織布）の物性を下記のように評価した。また、実施例1〜３、比較例１〜５で得られた吸収体（積層不織布）の吸水特性を下記のように吸水／ウェットバック試験により測定・評価した。これらの結果を下記表１に示した。さらに、実施例1〜３、比較例１〜５で得られた吸収体（積層不織布）の拡散性を下記のように拡散性試験により測定・評価した。これらの結果を下記表１に示した。参考例１として、市販のピジョン社製の失禁用品（品名「リクープかろやか１５ｍｌ」）における吸収体（ニードルパンチ不織布、レーヨン繊維５０質量％、アクリル系繊維５０質量％）の吸収特性及び吸水拡散性を、それぞれ、下記の吸水／ウェットバック試験及び拡散性試験により測定・評価し、その結果も下記表１に示した。下記表１において、「−」は、測定していないことを意味する。 The physical properties of the absorbent bodies (laminated nonwoven fabrics) obtained in Examples 1 to 3 and Comparative Examples 1 to 5 were evaluated as follows. Moreover, the water absorption property of the absorber (laminated nonwoven fabric) obtained in Examples 1 to 3 and Comparative Examples 1 to 5 was measured and evaluated by a water absorption / wet back test as described below. These results are shown in Table 1 below. Furthermore, the diffusibility of the absorber (laminated nonwoven fabric) obtained in Examples 1 to 3 and Comparative Examples 1 to 5 was measured and evaluated by a diffusivity test as described below. These results are shown in Table 1 below. As Reference Example 1, the absorption characteristics and water absorption diffusion of an absorbent body (needle punched nonwoven fabric, rayon fiber 50 mass%, acrylic fiber 50 mass%) in a commercially available incontinence product (product name “Recoup Kamoka 15 ml”) manufactured by Pigeon The properties were measured and evaluated by the following water absorption / wetback test and diffusivity test, respectively. The results are also shown in Table 1 below. In Table 1 below, “−” means not measured.
＜目付＞
ＪＩＳ Ｌ １９１３に準じて測定した。
<Unit weight>
It measured according to JIS L 1913.
＜厚み＞
厚み測定機（商品名「ＴＨＩＣＫＮＥＳＳ ＧＡＵＧＥ」、モデル「ＣＲ−６０Ａ」、株式会社大栄科学精器製作所製）を使用して、１９６０Ｐａ（２０ｇｆ／ｃｍ2）荷重下で厚みを測定した。
<Thickness>
The thickness was measured under a load of 1960 Pa (20 gf / cm 2 ) using a thickness measuring machine (trade name “THICKNESS GAUGE”, model “CR-60A”, manufactured by Daiei Kagaku Seisakusho Co., Ltd.).
＜比容積＞
比容積は、上述した測定方法によって測定した厚み及び目付に基づき、下記式により算出した。
比容積(ｃｍ3／ｇ)＝｛１９６０Ｐａ荷重時厚み（ｍｍ）／目付（ｇ／ｍ2）｝×１０００
<Specific volume>
The specific volume was calculated by the following formula based on the thickness and basis weight measured by the measurement method described above.
Specific volume (cm 3 / g) = {1960 Pa load thickness (mm) / weight per unit area (g / m 2 )} × 1000
＜吸水／ウェットバック試験＞
（１）試料（吸収体）、表面シート(エアスルー不織布、目付５０ｇ／ｍ2、厚み０．８６ｍｍ（１９６０Ｐａ荷重時）、ＰＥＴ／ＰＥ製）)をそれぞれ１０ｃｍ角にカットして質量を測定し、それぞれ、試料の吸水前質量、表面シートの吸水前質量とした。
（２）１０ｃｍ角にカットした濾紙（東洋濾紙社製、ＡＤＶＡＮＴＥＣ（登録商標） Ｎｏ．２）を２０枚重ね、質量を測定し、濾紙の吸水前質量とした。
（３）１０ｃｍ角の樹脂板（塩化ビニル樹脂製）上に、試料、表面シート、注水板（アクリル樹脂製、１０ｃｍ角、中央に１０ｍｍ直径の孔（注水口）を有する）をこの順番に重ね置きした。
（４）水６ｍｌを注水口から注加し、注加直後から全量吸収されるまでの時間を計測し、吸液時間とした。
（５）注水板を除いた表面シート上に、上記（２）で準備した濾紙２０枚、１０ｃｍ角の樹脂板（塩化ビニル樹脂製）、４ｋｇ分銅をこの順に重ね置きし、３９２０Ｐａ（４０ｇｆ／ｃｍ2）の荷重を３分間加えた。
（６）荷重除去後、試料、濾紙（２０枚）及び表面シートの質量をそれぞれ測定し、それぞれ、試料、濾紙及び表面シートの吸水後質量とした。
（７）下記式により、試料（吸収体）の吸水量、表面シートの吸水量、ウェットバック量を算出した。そして、下記式により、吸収体の吸水量、表面シートの吸水量及びウェットバック量の合計に対する吸収体の吸水量及びウェットバック量の比率を求め、それぞれ、吸収体の吸水率及びウェットバック率とした。
吸水体の吸水量（ｇ）＝試料の吸水後質量（ｇ）−試料の吸水前質量（ｇ）
表面シートの吸水量（ｇ）＝表面シートの吸水後質量（ｇ）−表面シートの吸水前質量（ｇ）
ウェットバック量（ｇ）＝濾紙の吸水後質量（ｇ）−濾紙の吸水前質量（ｇ）
吸収体の吸水率（％）＝[吸水体の吸水量（ｇ）／（吸収体の吸水量＋表面シートの吸水量＋ウェットバック量）（ｇ）]×１００
吸収体のウェットバック率（％）＝[ウェットバック量（ｇ）／（吸収体の吸水量＋表面シートの吸水量＋ウェットバック量）（ｇ）]×１００
<Water absorption / wet back test>
(1) Sample (absorber), surface sheet (air-through non-woven fabric, basis weight 50 g / m 2 , thickness 0.86 mm (at 1960 Pa load), made of PET / PE)) are cut into 10 cm squares, and the mass is measured. The mass before water absorption of the sample and the mass before water absorption of the surface sheet were used, respectively.
(2) 20 sheets of filter paper (ADVANTEC (registered trademark) No. 2 manufactured by Toyo Roshi Kaisha Co., Ltd.) cut into 10 cm squares were stacked and the mass was measured to obtain the mass before water absorption of the filter paper.
(3) On a 10 cm square resin plate (made of vinyl chloride resin), a sample, a surface sheet, and a water injection plate (made of acrylic resin, 10 cm square, with a 10 mm diameter hole (water injection port) in the center) are stacked in this order. I put it.
(4) 6 ml of water was added from the water injection port, and the time from immediately after the injection until the entire amount was absorbed was measured and used as the liquid absorption time.
(5) On the top sheet excluding the water injection plate, 20 sheets of filter paper prepared in (2) above, 10 cm square resin plate (made of vinyl chloride resin), 4 kg weight were stacked in this order, 3920 Pa (40 gf / cm The load of 2 ) was applied for 3 minutes.
(6) After removing the load, the masses of the sample, filter paper (20 sheets), and the top sheet were measured, and the mass after water absorption of the sample, the filter paper, and the top sheet, respectively.
(7) The water absorption amount of the sample (absorber), the water absorption amount of the top sheet, and the wet back amount were calculated by the following formula. Then, the ratio of the water absorption amount and the wet back amount of the absorber to the sum of the water absorption amount of the absorber, the water absorption amount of the top sheet and the wet back amount is obtained by the following formula, respectively, did.
Water absorption amount of water absorbent (g) = mass after water absorption of sample (g) −mass before water absorption of sample (g)
Water absorption amount of top sheet (g) = mass after water absorption of top sheet (g) −mass before water absorption of top sheet (g)
Wet back amount (g) = mass after water absorption of filter paper (g) −mass before water absorption of filter paper (g)
Absorbent water absorption rate (%) = [water absorption amount of the water absorber (g) / (water absorption amount of the absorber + water absorption amount of the top sheet + wet back amount) (g)] × 100
Absorbent wetback rate (%) = [wetback amount (g) / (absorber water absorption + surface sheet water absorption + wetback amount) (g)] × 100
＜拡散性試験＞
（１）５ｃｍ角にカットした吸収体（試料）を樹脂板（塩化ビニル樹脂製、５ｃｍ角）上に配置した。
（２）試料上３ｃｍに先端位置を調整したビュレットから、着色水（食用色素 黄（共立食品社）０．３％水溶液）を０．５ｍｌ注加した後、試料上に５ｃｍ角の濾紙２０枚、５ｃｍ角の樹脂板（塩化ビニル樹脂製）、４ｋｇ分銅をこの順に重ね置きし、３９２０Ｐａ（４０ｇｆ／ｃｍ2）の荷重を３分間加えた。
（３）荷重を除去した後、試料表面及び裏面における注加液（着色水）の拡散状態をデジ タルカメラ（ＯＬＹＭＰＵＳ社製、型番「ＳＰ−３５０」）で写真撮影した。
（４）注加液の拡散領域の面積を印刷紙面上で計測し、下式により、試料面積（２５ｃｍ２）に対する試料表面（吸水面）及び裏面（吸水面の反対面）における拡散領域の面積の 比率を求め、拡散面積比とした。
拡散面積比（％）＝[拡散領域の面積（ｃｍ2）／２５（ｃｍ2）]×１００
<Diffusion test>
(1) The absorber (sample) cut into 5 cm square was placed on a resin plate (made of vinyl chloride resin, 5 cm square).
(2) After adding 0.5 ml of colored water (food dye yellow (0.3% aqueous solution of Kyoritsu Foods)) from a burette whose tip position is adjusted to 3 cm above the sample, 20 pieces of 5 cm square filter paper are placed on the sample. A 5 cm square resin plate (made of vinyl chloride resin) and a 4 kg weight were stacked in this order, and a load of 3920 Pa (40 gf / cm 2 ) was applied for 3 minutes.
(3) After removing the load, the diffusion state of the pouring liquid (colored water) on the front and back surfaces of the sample was photographed with a digital camera (OLYMPUS, model number “SP-350”).
(4) The area of the diffusion region of the pouring liquid is measured on the printing paper surface, and the area of the diffusion region on the sample surface (water absorption surface) and back surface (opposite surface of the water absorption surface) with respect to the sample area (25 cm 2 ) by the following formula The ratio was determined as the diffusion area ratio.
Diffusion area ratio (%) = [area of diffusion region (cm 2 ) / 25 (cm 2 )] × 100
表１のデータから分かるように、実施例の吸収体は、ウェットバック率が５２％以下であり、水分の逆戻りが少なかった。また、実施例の吸収体は、吸液時間が４．０以下であり、吸液速度が速かった。さらに、実施例の吸収体は、吸水率が高く、保水性が高かった。実施例１〜３の対比から分かるように、第１不織布と第２不織布のいずれもニードルパンチ不織布で構成した実施例１〜２の吸収体が、第１不織布を水流交絡不織布で構成し、第２不織布をニードルパンチ不織布で構成した実施例３の吸収体より、吸液時間が短く、より吸液速度に優れていた。一方、比較例１〜５の吸収体は、ウェットバック率が５５％を超えており、水分の逆戻りが多かった。また、比較例１〜５の吸収体は、吸水率が４５％未満であり、保水性が悪かった。また、実施例の吸収体は、参考例１の市販品の失禁用品における吸収体に比べ、保水性、水分の逆戻り、及び吸液速度の全てが良好であった。 As can be seen from the data in Table 1, the absorbent bodies of the examples had a wetback rate of 52% or less, and there was little reversion of moisture. Moreover, the absorber of the Example had a liquid absorption time of 4.0 or less, and the liquid absorption speed was fast. Furthermore, the absorbers of the examples had high water absorption and high water retention. As can be seen from the comparison of Examples 1 to 3, the absorbent body of Examples 1 and 2 in which both the first nonwoven fabric and the second nonwoven fabric are needle punched nonwoven fabrics, the first nonwoven fabric is composed of a hydroentangled nonwoven fabric, The liquid absorption time was shorter and the liquid absorption speed was more excellent than the absorbent body of Example 3 which comprised 2 nonwoven fabrics with the needle punch nonwoven fabric. On the other hand, the absorbent bodies of Comparative Examples 1 to 5 had a wetback rate of more than 55%, and the moisture content was often reversed. Further, the absorbent bodies of Comparative Examples 1 to 5 had a water absorption rate of less than 45% and poor water retention. In addition, the absorbent bodies of the examples were all good in water retention, moisture reversion, and liquid absorption rate as compared to the absorbent body in the commercial incontinence article of Reference Example 1.
本発明の吸収体は、生理用ナプキン；おりものシート；失禁パッド、失禁ライナー、失禁用パンツ、失禁用ショーツ等の等の失禁用品等の吸収性物品に用いることができ、特に、失禁パッド、失禁ライナー、失禁用パンツ、失禁用ショーツ等の失禁用品、特に軽度失禁用品の尿受け部の吸収体として好適に用いることができる。 The absorbent body of the present invention can be used in absorbent articles such as sanitary napkins; vaginal sheets; incontinence pads, incontinence liners, incontinence pants, incontinence shorts, etc. It can be suitably used as an absorbent body for urine receiving parts of incontinence products such as incontinence liners, incontinence pants, and incontinence shorts, especially mild incontinence products.
Claims (8)
前記吸収体は、第２不織布と、前記第２不織布の表面上に積層されている第１不織布を含み、
前記第１不織布は、繊度が前記第２不織布の構成繊維の平均繊度より大きく、且つ３．０ｄｔｅｘ以下の第１のセルロース繊維を７０質量％以上含み、
前記第２不織布は、繊度が前記第１不織布の構成繊維の平均繊度より小さく、且つ０．２〜１．０ｄｔｅｘの第２の再生セルロース繊維を７０質量％以上含むことを特徴とする吸収体。 An absorbent for use in an absorbent article,
The absorber includes a second nonwoven fabric and a first nonwoven fabric laminated on the surface of the second nonwoven fabric,
The first nonwoven fabric has a fineness greater than the average fineness of the constituent fibers of the second nonwoven fabric and includes 70% by mass or more of first cellulose fibers having a size of 3.0 dtex or less,
The absorbent body, wherein the second nonwoven fabric has a fineness smaller than an average fineness of constituent fibers of the first nonwoven fabric, and contains 70% by mass or more of second regenerated cellulose fibers having a density of 0.2 to 1.0 dtex.