JP2015230923A - 薄膜太陽電池及び薄膜太陽電池の製造方法 - Google Patents
薄膜太陽電池及び薄膜太陽電池の製造方法 Download PDFInfo
- Publication number
- JP2015230923A JP2015230923A JP2014115211A JP2014115211A JP2015230923A JP 2015230923 A JP2015230923 A JP 2015230923A JP 2014115211 A JP2014115211 A JP 2014115211A JP 2014115211 A JP2014115211 A JP 2014115211A JP 2015230923 A JP2015230923 A JP 2015230923A
- Authority
- JP
- Japan
- Prior art keywords
- thin film
- solar cell
- photoelectric conversion
- film solar
- sulfide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】光電変換効率を高めることができ、特に開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少ない薄膜太陽電池を提供する。また、該薄膜太陽電池の製造方法を提供する。
【解決手段】陰極と、陽極と、前記陰極と前記陽極との間に配置された光電変換層と、前記陰極と前記光電変換層との間に配置された電子輸送層とを有し、前記光電変換層が、有機半導体を含有する部位と、硫化物及び/又はセレン化物を含有する部位とを有し、前記光電変換層と前記電子輸送層との間に、チタン酸アルカリ土類化合物を含有する層が配置されている薄膜太陽電池。
【選択図】図2
【解決手段】陰極と、陽極と、前記陰極と前記陽極との間に配置された光電変換層と、前記陰極と前記光電変換層との間に配置された電子輸送層とを有し、前記光電変換層が、有機半導体を含有する部位と、硫化物及び/又はセレン化物を含有する部位とを有し、前記光電変換層と前記電子輸送層との間に、チタン酸アルカリ土類化合物を含有する層が配置されている薄膜太陽電池。
【選択図】図2
Description
本発明は、光電変換効率を高めることができ、特に開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少ない薄膜太陽電池に関する。また、本発明は、該薄膜太陽電池の製造方法に関する。
従来から、有機半導体層と無機半導体層とを積層し、この積層体の両側に電極を設けた光電変換素子が開発されている。このような構造の光電変換素子では、光励起により有機半導体層又は無機半導体層で光キャリア(電子−ホール対)が生成し、電子が無機半導体層を、ホールが有機半導体層を移動することで、電界が生じる。更に、電子及びホールが再接合することなく効率的に移動するよう、無機半導体層と電極との間に電子輸送層を設けたり、有機半導体層と電極との間にホール輸送層を設けたりすることも検討されている。
しかしながら、光キャリア生成に活性な領域は有機半導体層と無機半導体層との接合界面付近の数十nm程度と非常に狭く、この活性な領域以外は光キャリア生成に寄与できないため、光電変換効率が低くなってしまうという欠点があった。
しかしながら、光キャリア生成に活性な領域は有機半導体層と無機半導体層との接合界面付近の数十nm程度と非常に狭く、この活性な領域以外は光キャリア生成に寄与できないため、光電変換効率が低くなってしまうという欠点があった。
この問題を解決する目的で、有機半導体と、無機半導体とを混合して複合化した複合膜を用いることが検討されている。
例えば、特許文献1には、有機半導体と無機半導体を共蒸着によって複合化した共蒸着薄膜と、この薄膜を挟んでその両面に設けられ、この複合薄膜に内蔵電界を与えるための半導体もしくは金属、又はそれら双方からなる電極部とを備えた有機・無機複合薄膜太陽電池が記載されている。特許文献1には、同文献に記載の有機・無機複合薄膜においては、pn接合(有機/無機半導体接合)が膜全体に張り巡らされた構造のため、膜全体が光キャリア生成に対して活性に働き、膜で吸収された光すべてがキャリア生成に寄与するため、大きな光電流が得られる効果がある旨が記載されている。
例えば、特許文献1には、有機半導体と無機半導体を共蒸着によって複合化した共蒸着薄膜と、この薄膜を挟んでその両面に設けられ、この複合薄膜に内蔵電界を与えるための半導体もしくは金属、又はそれら双方からなる電極部とを備えた有機・無機複合薄膜太陽電池が記載されている。特許文献1には、同文献に記載の有機・無機複合薄膜においては、pn接合(有機/無機半導体接合)が膜全体に張り巡らされた構造のため、膜全体が光キャリア生成に対して活性に働き、膜で吸収された光すべてがキャリア生成に寄与するため、大きな光電流が得られる効果がある旨が記載されている。
また、有機半導体に対して無機半導体を密充填させて、光電変換効率を向上させる試みもなされている。
例えば、特許文献2には、有機電子供与体と化合物半導体結晶とを含有する活性層を二つの電極の間に設けた有機太陽電池において、前記活性層は有機電子供与体と化合物半導体結晶とを混合して分散してなり、且つ、化合物半導体結晶が平均粒径が異なる二種類のロッド状の結晶を含み、この二種類のロッド状結晶の平均粒径及び含有比率を所定範囲内とする有機太陽電池が記載されている。特許文献2には、活性層中における化合物半導体結晶の充填率を増大することができ、これにより変換効率の高い太陽電池を得ることができる旨が記載されている。
例えば、特許文献2には、有機電子供与体と化合物半導体結晶とを含有する活性層を二つの電極の間に設けた有機太陽電池において、前記活性層は有機電子供与体と化合物半導体結晶とを混合して分散してなり、且つ、化合物半導体結晶が平均粒径が異なる二種類のロッド状の結晶を含み、この二種類のロッド状結晶の平均粒径及び含有比率を所定範囲内とする有機太陽電池が記載されている。特許文献2には、活性層中における化合物半導体結晶の充填率を増大することができ、これにより変換効率の高い太陽電池を得ることができる旨が記載されている。
しかしながら、特許文献1又は2に記載の光電変換素子であっても未だ光電変換効率はかなり低く、実用化に耐えうる有機太陽電池の開発のためには更なる光電変換効率の改善が不可欠である。
本発明は、光電変換効率を高めることができ、特に各層のエネルギー準位の制御によって電子−ホール対の再結合を抑制することで開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少ない薄膜太陽電池を提供することを目的とする。また、本発明は、該薄膜太陽電池の製造方法を提供することを目的とする。
本発明は、陰極と、陽極と、前記陰極と前記陽極との間に配置された光電変換層と、前記陰極と前記光電変換層との間に配置された電子輸送層とを有し、前記光電変換層が、有機半導体を含有する部位と、硫化物及び/又はセレン化物を含有する部位とを有し、前記光電変換層と前記電子輸送層との間に、チタン酸アルカリ土類化合物を含有する層が配置されている薄膜太陽電池である。
以下、本発明を詳述する。
以下、本発明を詳述する。
本発明者らは、陰極と、陽極と、上記陰極と上記陽極との間に配置された光電変換層と、上記陰極と上記光電変換層との間に配置された電子輸送層とを有し、上記光電変換層が、有機半導体を含有する部位と、硫化物及び/又はセレン化物を含有する部位とを有する薄膜太陽電池に対して、更に、上記光電変換層と上記電子輸送層との間にチタン酸アルカリ土類化合物を含有する層を設けることにより、各層のエネルギー準位を制御し、薄膜太陽電池の光電変換効率、特に開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少なくなることを見出し、本発明を完成させるに至った。
なお、光電変換効率は、短絡電流の大きさ、開放電圧の高さ等に依存するものである。従って、開放電圧が高くなると、光電変換効率も高くなる。また、開放電圧が高くなると、実際に得られる電圧も大きくなるため、薄膜太陽電池セル同士を並列に接続することが可能となり、太陽電池モジュール(透明保護材と裏面保護材との間に薄膜太陽電池セルを封止したもの)の施工面での簡便性及び自由度が向上するという利点もある。
なお、光電変換効率は、短絡電流の大きさ、開放電圧の高さ等に依存するものである。従って、開放電圧が高くなると、光電変換効率も高くなる。また、開放電圧が高くなると、実際に得られる電圧も大きくなるため、薄膜太陽電池セル同士を並列に接続することが可能となり、太陽電池モジュール(透明保護材と裏面保護材との間に薄膜太陽電池セルを封止したもの)の施工面での簡便性及び自由度が向上するという利点もある。
なお、開放電圧は、バンドギャップ電圧の向上、電子−ホール対の再結合の抑制等に依存して高くなるものである。
バンドギャップ電圧とは、絶対零度(T=0(K))における電圧で示すことができ、その系で理論的に得られる最大の電圧を示している。
また、再結合の度合いを示す指標のひとつとして、逆方向飽和電流密度が知られている。逆方向飽和電流密度は、電子−ホール対の再結合によって生じる電流値を示しており、逆方向飽和電流密度が小さければ、電子−ホール対の再結合が少なくなり、開放電圧が高くなる。
バンドギャップ電圧とは、絶対零度(T=0(K))における電圧で示すことができ、その系で理論的に得られる最大の電圧を示している。
また、再結合の度合いを示す指標のひとつとして、逆方向飽和電流密度が知られている。逆方向飽和電流密度は、電子−ホール対の再結合によって生じる電流値を示しており、逆方向飽和電流密度が小さければ、電子−ホール対の再結合が少なくなり、開放電圧が高くなる。
本発明の薄膜太陽電池は、陰極と、陽極と、上記陰極と上記陽極との間に配置された光電変換層と、前記陰極と前記光電変換層との間に配置された電子輸送層とを有する。
なお、本明細書中、層とは、明確な境界を有する層だけではなく、含有元素が徐々に変化する濃度勾配のある層をも意味する。なお、層の元素分析は、例えば、薄膜太陽電池の断面のFE−TEM/EDS線分析測定を行い、特定元素の元素分布を確認する等によって行うことができる。また、本明細書中、層とは、平坦な薄膜状の層だけではなく、他の層と一緒になって複雑に入り組んだ構造を形成しうる層をも意味する。
なお、本明細書中、層とは、明確な境界を有する層だけではなく、含有元素が徐々に変化する濃度勾配のある層をも意味する。なお、層の元素分析は、例えば、薄膜太陽電池の断面のFE−TEM/EDS線分析測定を行い、特定元素の元素分布を確認する等によって行うことができる。また、本明細書中、層とは、平坦な薄膜状の層だけではなく、他の層と一緒になって複雑に入り組んだ構造を形成しうる層をも意味する。
上記陰極及び上記陽極の材料は特に限定されず、従来公知の材料を用いることができる。陰極材料として、例えば、FTO(フッ素ドープ酸化スズ)、ナトリウム、ナトリウム−カリウム合金、リチウム、マグネシウム、アルミニウム、マグネシウム−銀混合物、マグネシウム−インジウム混合物、アルミニウム−リチウム合金、Al/Al2O3混合物、Al/LiF混合物等が挙げられる。陽極材料として、例えば、金等の金属、CuI、ITO(インジウムスズ酸化物)、SnO2、AZO(アルミニウム亜鉛酸化物)、IZO(インジウム亜鉛酸化物)、GZO(ガリウム亜鉛酸化物)等の導電性透明材料、導電性透明ポリマー等が挙げられる。これらの材料は単独で用いられてもよく、2種以上が併用されてもよい。
上記光電変換層は、有機半導体を含有する部位(本明細書中、有機半導体部位ともいう)と、硫化物及び/又はセレン化物を含有する部位(本明細書中、硫化物及び/又はセレン化物半導体部位ともいう)とを有する。
上記有機半導体部位は、主にP型半導体として、上記硫化物及び/又はセレン化物半導体部位は、主にN型半導体として働くと推測され、光励起によりP型半導体又はN型半導体で光キャリア(電子−ホール対)が生成し、電子がN型半導体を、ホールがP型半導体を移動することで、電界が生じる。ただし、上記有機半導体部位は、部分的にはN型半導体として働いていてもよいし、上記硫化物及び/又はセレン化物半導体部位は、部分的にはP型半導体として働いていてもよい。
上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位とを有することにより、本発明の薄膜太陽電池は、光電変換効率が高くなる。また、P型半導体とN型半導体とがいずれも無機半導体である場合はこれらの固溶体が界面で析出する可能性があるのに対し、本発明の薄膜太陽電池においては固溶体の析出がなく、高温時においても高い安定性を得ることができるため、高温での加温後にも光電変換効率の低下が少ない。
上記有機半導体部位は、主にP型半導体として、上記硫化物及び/又はセレン化物半導体部位は、主にN型半導体として働くと推測され、光励起によりP型半導体又はN型半導体で光キャリア(電子−ホール対)が生成し、電子がN型半導体を、ホールがP型半導体を移動することで、電界が生じる。ただし、上記有機半導体部位は、部分的にはN型半導体として働いていてもよいし、上記硫化物及び/又はセレン化物半導体部位は、部分的にはP型半導体として働いていてもよい。
上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位とを有することにより、本発明の薄膜太陽電池は、光電変換効率が高くなる。また、P型半導体とN型半導体とがいずれも無機半導体である場合はこれらの固溶体が界面で析出する可能性があるのに対し、本発明の薄膜太陽電池においては固溶体の析出がなく、高温時においても高い安定性を得ることができるため、高温での加温後にも光電変換効率の低下が少ない。
上記光電変換層は、薄膜状の上記有機半導体部位と薄膜状の上記硫化物及び/又はセレン化物半導体部位とを積層した積層体であってもよいし、上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位とを複合化した複合膜であってもよい。製法が簡便である点では積層体が好ましく、上記有機半導体部位の電荷分離効率を向上させることができる点では複合膜が好ましい。
上記有機半導体部位を有することにより、本発明の薄膜太陽電池は、耐衝撃性、フレキシビリティ等が優れたものとなる。上記有機半導体は特に限定されず、例えば、ポリ(3−アルキルチオフェン)等のチオフェン骨格を有する化合物等が挙げられる。また、例えば、ポリパラフェニレンビニレン骨格、ポリビニルカルバゾール骨格、ポリアニリン骨格、ポリアセチレン骨格等を有する導電性高分子等も挙げられる。更に、例えば、フタロシアニン骨格、ナフタロシアニン骨格、ペンタセン骨格、ベンゾポルフィリン骨格等のポルフィリン骨格等を有する化合物も挙げられる。なかでも、比較的耐久性が高いことから、チオフェン骨格、フタロシアニン骨格、ナフタロシアニン骨格、ベンゾポルフィリン骨格を有する化合物が好ましい。
上記有機半導体は、長波長領域の光を吸収できることから、ドナー−アクセプター型であることも好ましい。なかでも、チオフェン骨格を有するドナー−アクセプター型の化合物がより好ましく、チオフェン骨格を有するドナー−アクセプター型の化合物のなかでも、光吸収波長の観点から、チオフェン−ジケトピロロピロール重合体が特に好ましい。
上記硫化物及び/又はセレン化物は耐久性が高いことから、上記硫化物及び/又はセレン化物半導体部位を有することにより、本発明の薄膜太陽電池は、耐久性に優れたものとなる。上記硫化物及び/又はセレン化物は特に限定されず、好ましくは周期表14族又は15族元素の硫化物及び/又はセレン化物であり、より好ましくは周期表15族元素の硫化物及び/又はセレン化物である。硫化物及び/又はセレン化物は、単独で用いられてもよく、2種以上が併用されてもよく、周期表14族又は15族元素の2種以上の元素を同一の分子に含有する複合硫化物及び/又は複合セレン化物であってもよい。なかでも、硫化アンチモン、硫化ビスマス、硫化スズ、硫化鉛、セレン化アンチモン、セレン化ビスマスが好ましく、硫化アンチモン、硫化スズ、硫化鉛、セレン化アンチモンがより好ましく、硫化アンチモン、セレン化アンチモンが更に好ましい。
硫化アンチモン及びセレン化アンチモンは、有機半導体とのエネルギー準位の相性がよく、かつ、従来の酸化亜鉛、酸化チタン等より可視光に対する吸収が大きい。このため、上記硫化物及び/又はセレン化物半導体部位に硫化アンチモン及び/又はセレン化アンチモンが含まれることにより、薄膜太陽電池のバンドギャップ電圧が向上し、開放電圧が高くなるため、光電変換効率が高くなる。
上記硫化物及び/又はセレン化物半導体部位は、結晶性半導体であることが好ましい。上記硫化物及び/又はセレン化物半導体部位が結晶性半導体であることにより、電子の移動度が高くなり、光電変換効率が向上する。
なお、結晶性半導体とは、X線回折測定等で測定し、散乱ピークが検出できる半導体を意味する。
なお、結晶性半導体とは、X線回折測定等で測定し、散乱ピークが検出できる半導体を意味する。
また、上記硫化物及び/又はセレン化物半導体部位の結晶性の指標として、結晶化度を用いることもできる。上記硫化物及び/又はセレン化物半導体部位の結晶化度は、好ましい下限が30%である。上記結晶化度が30%以上であれば、電子の移動度が高くなり、光電変換効率が向上する。上記結晶化度のより好ましい下限は50%、更に好ましい下限は70%である。
なお、結晶化度は、X線回折測定等により検出された結晶質由来の散乱ピークと、非晶質部由来のハローとをフィッティングにより分離し、それぞれの強度積分を求めて、全体のうちの結晶質部分の比を算出することにより求めることができる。
なお、結晶化度は、X線回折測定等により検出された結晶質由来の散乱ピークと、非晶質部由来のハローとをフィッティングにより分離し、それぞれの強度積分を求めて、全体のうちの結晶質部分の比を算出することにより求めることができる。
上記硫化物及び/又はセレン化物半導体部位の硫化物及び/又はセレン化物の結晶化度を高める方法として、例えば、上記硫化物及び/又はセレン化物半導体部位に対して、焼成、レーザー又はフラッシュランプ等の強度の強い光の照射、エキシマ光照射、プラズマ照射等を行う方法が挙げられる。なかでも、上記硫化物及び/又はセレン化物半導体部位の酸化を低減できることから、強度の強い光の照射、プラズマ照射等を行う方法が好ましい。
上記硫化物及び/又はセレン化物半導体部位は、本発明の効果を阻害しない範囲内であれば、上述したような主成分となる金属元素に加えて他の元素を含有していてもよい。上記他の元素は特に限定されないが、具体的には例えば、カドミウム、亜鉛、アルミニウム、チタン、ランタン等が挙げられる。これらの他の元素は単独で用いられてもよく、2種以上が併用されてもよい。なかでも、特に結晶化が促進しやすく開放電圧が高くなることから、他の元素は亜鉛が好ましい。
上記他の元素の含有量は、上記硫化物及び/又はセレン化物半導体中の好ましい上限が50重量%である。上記含有量が50重量%以下であれば、上記硫化物及び/又はセレン化物の光学特性を維持しつつ、付加機能を付与することが可能である。
上記光電変換層が薄膜状の上記有機半導体部位と薄膜状の上記硫化物及び/又はセレン化物半導体部位とを積層した積層体である場合、上記薄膜状の有機半導体部位の厚みは、好ましい下限が5nm、好ましい上限が5000nmである。上記厚みが5nm以上であれば、充分に光を吸収することができるようになり、光電変換効率が高くなる。上記厚みが5000nm以下であれば、電荷分離できない領域が発生することを抑制できるため、光電変換効率の向上につながる。上記厚みのより好ましい下限は10nm、より好ましい上限は2000nmであり、更に好ましい下限は20nm、更に好ましい上限は1000nmである。
また、上記薄膜状の硫化物及び/又はセレン化物半導体部位の厚みは、好ましい下限が5nm、好ましい上限が5000nmである。上記厚みが5nm以上であれば、充分に光を吸収することができるようになり、光電変換効率が高くなる。上記厚みが5000nm以下であれば、電荷分離できない領域が発生することを抑制できるため、光電変換効率の向上につながる。上記厚みのより好ましい下限は10nm、より好ましい上限は1000nmであり、更に好ましい下限は20nm、更に好ましい上限は500nmである。
上記光電変換層が上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位とを複合化した複合膜である場合、上記複合膜の厚みの好ましい下限は30nm、好ましい上限は3000nmである。上記厚みが30nm以上であれば、充分に光を吸収することができるようになり、光電変換効率が高くなる。上記厚みが3000nm以下であれば、電荷が電極に到達しやすくなるため、光電変換効率が高くなる。上記厚みのより好ましい下限は40nm、より好ましい上限は2000nmであり、更に好ましい下限は50nm、更に好ましい上限は1000nmである。
また、上記複合膜においては、上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位との比率が非常に重要である。上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位との比率は、1:9〜9:1(体積比)であることが好ましい。上記比率が上記範囲内であれば、ホール又は電子が電極まで到達しやすくなり、そのため光電変換効率の向上につながる。上記比率は、2:8〜8:2(体積比)であることがより好ましい。
上記電子輸送層の材料は特に限定されず、例えば、N型導電性高分子、N型低分子有機半導体、N型金属酸化物、N型金属硫化物、ハロゲン化アルカリ金属、アルカリ金属、界面活性剤等が挙げられ、具体的には例えば、シアノ基含有ポリフェニレンビニレン、ホウ素含有ポリマー、バソキュプロイン、バソフェナントレン、ヒドロキシキノリナトアルミニウム、オキサジアゾール化合物、ベンゾイミダゾール化合物、ナフタレンテトラカルボン酸化合物、ペリレン誘導体、ホスフィンオキサイド化合物、ホスフィンスルフィド化合物、フルオロ基含有フタロシアニン、酸化チタン、酸化亜鉛、酸化インジウム、酸化スズ、酸化ガリウム、硫化スズ、硫化インジウム、硫化亜鉛等が挙げられる。
上記電子輸送層は、薄膜状の電子輸送層のみからなっていてもよいが、多孔質状の電子輸送層を含むことが好ましい。特に、上記光電変換層が上記有機半導体部位と上記硫化物及び/又はセレン化物半導体部位とを複合化した複合膜である場合、より複雑な複合膜(より複雑に入り組んだ構造)が得られ、光電変換効率が高くなることから、多孔質状の電子輸送層上に後述するチタン酸アルカリ土類化合物を含有する層が成膜されていることが好ましい。
上記電子輸送層の厚みは、好ましい下限が1nm、好ましい上限が2000nmである。上記厚みが1nm以上であれば、充分にホールをブロックできるようになる。上記厚みが2000nm以下であれば、電子輸送の際の抵抗になり難く、光電変換効率が高くなる。上記電子輸送層の厚みのより好ましい下限は3nm、より好ましい上限は1000nmであり、更に好ましい下限は5nm、更に好ましい上限は500nmである。
本発明の薄膜太陽電池においては、上記光電変換層と上記電子輸送層との間に、チタン酸アルカリ土類化合物を含有する層が配置されている。チタン酸アルカリ土類化合物は、一般式MTiO3で表され、Mはアルカリ土類金属を表す。Mはカルシウム(Ca)、ストロンチウム(Sr)及びバリウム(Ba)からなる群より選択される少なくとも1種を含むことが好ましい。
上記光電変換層と上記電子輸送層との間にチタン酸アルカリ土類化合物を含有する層を設けることにより、各層のエネルギー準位を制御することができる。これにより、本発明の薄膜太陽電池は、バンドギャップ電圧が向上するとともに電子−ホール対の再結合が少なくなり、開放電圧が高くなるため、光電変換効率が高くなる。
上記光電変換層と上記電子輸送層との間にチタン酸アルカリ土類化合物を含有する層を設けることにより、各層のエネルギー準位を制御することができる。これにより、本発明の薄膜太陽電池は、バンドギャップ電圧が向上するとともに電子−ホール対の再結合が少なくなり、開放電圧が高くなるため、光電変換効率が高くなる。
上記チタン酸アルカリ土類化合物を含有する層におけるチタン酸アルカリ土類化合物は特に限定されず、アルカリ土類金属Mが単独である化合物であってもよく、2種以上のアルカリ土類金属Mを同一のサイトに含有する複合チタン酸化合物であってもよい。なかでも、ワイドバンドギャップをもつCaTiO3、(Ca,Sr)TiO3、SrTiO3、(Sr,Ba)TiO3が好ましく、SrTiO3がより好ましい。また、より低温で結晶化することができ、比較的低い焼成温度であっても高い開放電圧が得られることから、上記チタン酸アルカリ土類化合物は、ストロンチウム(Sr)を含むことが好ましい。更に、上記チタン酸アルカリ土類化合物における金属元素は、一部がアルカリ土類金属以外の添加元素で置換されていてもよい。上記アルカリ土類金属以外の添加元素としては、キャリアドープが可能である点ではランタン(La)、アンチモン(Sb)、ニオブ(Nb)が好ましく、エネルギー準位の調整ができる点ではジルコニウム(Zr)が好ましい。
上記チタン酸アルカリ土類化合物を含有する層は、上記硫化物及び/又はセレン化物半導体部位と同様に、電子の移動度が高くなるため、結晶性半導体であることが好ましい。また、上記チタン酸アルカリ土類化合物を含有する層の結晶化度は、上記硫化物及び/又はセレン化物半導体部位と同様に、好ましい下限が30%、より好ましい下限が50%、更に好ましい下限が70%である。
上記チタン酸アルカリ土類化合物を含有する層の結晶化度を高める方法としても、上記硫化物及び/又はセレン化物半導体部位の場合と同様に、例えば、上記チタン酸アルカリ土類化合物を含有する層に対して、焼成、レーザー又はフラッシュランプ等の強度の強い光の照射、エキシマ光照射、プラズマ照射等を行う方法が挙げられる。
上記チタン酸アルカリ土類化合物を含有する層の結晶化度を高める方法としても、上記硫化物及び/又はセレン化物半導体部位の場合と同様に、例えば、上記チタン酸アルカリ土類化合物を含有する層に対して、焼成、レーザー又はフラッシュランプ等の強度の強い光の照射、エキシマ光照射、プラズマ照射等を行う方法が挙げられる。
上記チタン酸アルカリ土類化合物を含有する層の厚みは、好ましい下限が1nm、好ましい上限が100nmである。上記厚みが1nm以上であれば、上記チタン酸アルカリ土類化合物を含有する層が上記電子輸送層上を充分に覆うことができ、光電変換効率、特に開放電圧が高くなる。上記厚みが100nm以下であれば、不純物準位の形成による開放電圧の低下、及び、フィルファクターの低下を抑制することができる。上記厚みのより好ましい下限は3nm、より好ましい上限は50nmである。
本発明の薄膜太陽電池においては、上記陽極と上記光電変換層との間に、ホール輸送層が配置されていてもよい。
上記ホール輸送層の材料は特に限定されず、例えば、P型導電性高分子、P型低分子有機半導体、P型金属酸化物、P型金属硫化物、界面活性剤等が挙げられ、具体的には例えば、ポリエチレンジオキシチオフェンのポリスチレンスルホン酸付加物、カルボキシル基含有ポリチオフェン、フタロシアニン、ポルフィリン、酸化モリブデン、酸化バナジウム、酸化タングステン、酸化ニッケル、酸化銅、酸化スズ、硫化モリブデン、硫化タングステン、硫化銅、硫化スズ等、フルオロ基含有ホスホン酸、カルボニル基含有ホスホン酸等が挙げられる。
上記ホール輸送層の材料は特に限定されず、例えば、P型導電性高分子、P型低分子有機半導体、P型金属酸化物、P型金属硫化物、界面活性剤等が挙げられ、具体的には例えば、ポリエチレンジオキシチオフェンのポリスチレンスルホン酸付加物、カルボキシル基含有ポリチオフェン、フタロシアニン、ポルフィリン、酸化モリブデン、酸化バナジウム、酸化タングステン、酸化ニッケル、酸化銅、酸化スズ、硫化モリブデン、硫化タングステン、硫化銅、硫化スズ等、フルオロ基含有ホスホン酸、カルボニル基含有ホスホン酸等が挙げられる。
上記ホール輸送層の厚みは、好ましい下限は1nm、好ましい上限は2000nmである。上記厚みが1nm以上であれば、充分に電子をブロックできるようになる。上記厚みが2000nm以下であれば、ホール輸送の際の抵抗になり難く、光電変換効率が高くなる。上記厚みのより好ましい下限は3nm、より好ましい上限は1000nmであり、更に好ましい下限は5nm、更に好ましい上限は500nmである。
本発明の薄膜太陽電池は、更に、基板等を有していてもよい。上記基板は特に限定されず、例えば、ソーダライムガラス、無アルカリガラス等の透明ガラス基板、セラミック基板、透明プラスチック基板等が挙げられる。
図1に、薄膜状の有機半導体部位と薄膜状の硫化物及び/又はセレン化物半導体部位とを積層した積層体である光電変換層を有する本発明の薄膜太陽電池の一例を模式的に示す。
図1に示す薄膜太陽電池1においては、基板2、透明電極(陰極)3、電子輸送層4、チタン酸アルカリ土類化合物を含有する層5、光電変換層8(薄膜状の有機半導体部位7と薄膜状の硫化物及び/又はセレン化物半導体部位6とを積層した積層体)、ホール輸送層9、電極(陽極)10がこの順で積層されている。
図1に示す薄膜太陽電池1においては、基板2、透明電極(陰極)3、電子輸送層4、チタン酸アルカリ土類化合物を含有する層5、光電変換層8(薄膜状の有機半導体部位7と薄膜状の硫化物及び/又はセレン化物半導体部位6とを積層した積層体)、ホール輸送層9、電極(陽極)10がこの順で積層されている。
図2に、有機半導体部位と硫化物及び/又はセレン化物半導体部位とを複合化した複合膜である光電変換層を有する本発明の薄膜太陽電池の一例を模式的に示す。
図2に示す薄膜太陽電池1’においては、基板2’、透明電極(陰極)3’、電子輸送層4’(薄膜状の電子輸送層4aと多孔質状の電子輸送層4bとを含む)、チタン酸アルカリ土類化合物を含有する層5’、光電変換層8’(有機半導体部位7’と硫化物及び/又はセレン化物半導体部位6’とを複合化した複合膜)、ホール輸送層9’、電極(陽極)10’がこの順で積層されている。
図2に示す薄膜太陽電池1’においては、基板2’、透明電極(陰極)3’、電子輸送層4’(薄膜状の電子輸送層4aと多孔質状の電子輸送層4bとを含む)、チタン酸アルカリ土類化合物を含有する層5’、光電変換層8’(有機半導体部位7’と硫化物及び/又はセレン化物半導体部位6’とを複合化した複合膜)、ホール輸送層9’、電極(陽極)10’がこの順で積層されている。
本発明の薄膜太陽電池を製造する方法は特に限定されず、例えば、基板上に電極(陽極)、光電変換層、チタン酸アルカリ土類化合物を含有する層、電子輸送層、電極(陰極)をこの順で形成する方法が挙げられる。また、基板上に電極(陰極)、電子輸送層、チタン酸アルカリ土類化合物を含有する層、光電変換層、電極(陽極)をこの順で形成してもよい。
本発明の薄膜太陽電池を製造する方法であって、光電変換層又は電子輸送層上にチタン酸アルカリ土類化合物を含有する層を成膜する工程を有する薄膜太陽電池の製造方法もまた、本発明の1つである。
上記光電変換層又は上記電子輸送層上にチタン酸アルカリ土類化合物を含有する層を成膜する方法は特に限定されず、例えば、真空蒸着法、スピンコート法等の印刷法、ディップコーティング法、化学析出法、電解法、その他の真空プロセス(例えば、スパッタリング、CVD等)等が挙げられる。なかでも、高い光電変換効率を発揮できる薄膜太陽電池を大面積で簡易に形成できることから、チタン酸アルカリ土類化合物を形成可能な塗布液を用いたスピンコート法等の印刷法が好ましい。
上記光電変換層又は上記電子輸送層上にチタン酸アルカリ土類化合物を含有する層を成膜する方法は特に限定されず、例えば、真空蒸着法、スピンコート法等の印刷法、ディップコーティング法、化学析出法、電解法、その他の真空プロセス(例えば、スパッタリング、CVD等)等が挙げられる。なかでも、高い光電変換効率を発揮できる薄膜太陽電池を大面積で簡易に形成できることから、チタン酸アルカリ土類化合物を形成可能な塗布液を用いたスピンコート法等の印刷法が好ましい。
上記チタン酸アルカリ土類化合物を形成可能な塗布液は、上述したチタン酸アルカリ土類化合物を形成可能であれば特に限定されないが、チタン錯体とアルカリ土類金属イオンとを含有することが好ましい。
上記チタン錯体として、乳酸チタン錯体、クエン酸チタン錯体、グリコール酸チタン錯体、リンゴ酸チタン錯体、酒石酸チタン錯体等が挙げられ、特に残渣が残りづらい乳酸チタン錯体がより好ましい。上記アルカリ土類金属イオン源として、塩化物、硝酸塩、炭酸塩、酢酸塩等が挙げられ、不純物元素が混入しない点では炭酸塩、酢酸塩がより好ましい。
上記チタン酸アルカリ土類化合物を形成可能な塗布液中の上記チタン錯体及び上記アルカリ土類金属イオン源のモル濃度がそれぞれ0.05〜5mol/Lであることが好ましい。
上記チタン錯体として、乳酸チタン錯体、クエン酸チタン錯体、グリコール酸チタン錯体、リンゴ酸チタン錯体、酒石酸チタン錯体等が挙げられ、特に残渣が残りづらい乳酸チタン錯体がより好ましい。上記アルカリ土類金属イオン源として、塩化物、硝酸塩、炭酸塩、酢酸塩等が挙げられ、不純物元素が混入しない点では炭酸塩、酢酸塩がより好ましい。
上記チタン酸アルカリ土類化合物を形成可能な塗布液中の上記チタン錯体及び上記アルカリ土類金属イオン源のモル濃度がそれぞれ0.05〜5mol/Lであることが好ましい。
上記光電変換層を形成する方法は特に限定されず、真空蒸着法、スパッタ法、気相反応法(CVD)、電気化学沈積法等であってもよいが、周期表14族又は15族元素を含む化合物と、硫黄含有化合物及び/又はセレン含有化合物とを含有する半導体形成用塗布液を用いた印刷法が好ましい。印刷法を採用することで、高い光電変換効率を発揮できる薄膜太陽電池を大面積で簡易に形成することができ、大量生産が可能となる。更に、印刷法を採用することで、薄膜太陽電池の性能安定性を高めることもできる。性能安定性が高いと、薄膜太陽電池の製造の際に、不良品を減らすことができる。印刷法として、例えば、スピンコート法、キャスト法等が挙げられ、印刷法を用いた方法としてロールtoロール法等が挙げられる。
より具体的には、例えば、上記光電変換層が薄膜状の上記硫化物及び/又はセレン化物半導体部位と薄膜状の上記有機半導体部位とを積層した積層体である場合には、上記半導体形成用塗布液を用いてスピンコート法等の印刷法により薄膜状の硫化物及び/又はセレン化物半導体部位を成膜し、この薄膜状の硫化物及び/又はセレン化物半導体部位の上にスピンコート法等の印刷法により薄膜状の有機半導体部位を成膜することが好ましい。また、逆に薄膜状の有機半導体部位の上に薄膜状の硫化物及び/又はセレン化物半導体部位を成膜してもよい。
また、例えば、上記光電変換層が上記硫化物及び/又はセレン化物半導体部位と上記有機半導体部位とを複合化した複合膜である場合には、上記半導体形成用塗布液と有機半導体とを混合した混合液を用いてスピンコート法等の印刷法により複合膜を成膜することが好ましい。
より具体的には、例えば、上記光電変換層が薄膜状の上記硫化物及び/又はセレン化物半導体部位と薄膜状の上記有機半導体部位とを積層した積層体である場合には、上記半導体形成用塗布液を用いてスピンコート法等の印刷法により薄膜状の硫化物及び/又はセレン化物半導体部位を成膜し、この薄膜状の硫化物及び/又はセレン化物半導体部位の上にスピンコート法等の印刷法により薄膜状の有機半導体部位を成膜することが好ましい。また、逆に薄膜状の有機半導体部位の上に薄膜状の硫化物及び/又はセレン化物半導体部位を成膜してもよい。
また、例えば、上記光電変換層が上記硫化物及び/又はセレン化物半導体部位と上記有機半導体部位とを複合化した複合膜である場合には、上記半導体形成用塗布液と有機半導体とを混合した混合液を用いてスピンコート法等の印刷法により複合膜を成膜することが好ましい。
上記半導体形成用塗布液は、周期表14族又は15族元素を含む化合物と、硫黄含有化合物及び/又はセレン含有化合物とを含有することが好ましい。
上記周期表14族又は15族元素を含む化合物と、上記硫黄含有化合物及び/又はセレン含有化合物とは、形成される硫化物及び/又はセレン化物半導体部位において、上述したような周期表14族又は15族元素の硫化物及び/又はセレン化物を形成するものである。上記周期表14族又は15族元素を含む化合物として、周期表14族又は15族の金属元素を含む金属含有化合物が好ましく、周期表15族の金属元素を含む金属含有化合物がより好ましい。上記周期表14族又は15族元素を含む化合物としては、例えば、周期表14族又は15族の金属元素の金属塩、有機金属化合物等が挙げられる。
上記周期表14族又は15族元素を含む化合物と、上記硫黄含有化合物及び/又はセレン含有化合物とは、形成される硫化物及び/又はセレン化物半導体部位において、上述したような周期表14族又は15族元素の硫化物及び/又はセレン化物を形成するものである。上記周期表14族又は15族元素を含む化合物として、周期表14族又は15族の金属元素を含む金属含有化合物が好ましく、周期表15族の金属元素を含む金属含有化合物がより好ましい。上記周期表14族又は15族元素を含む化合物としては、例えば、周期表14族又は15族の金属元素の金属塩、有機金属化合物等が挙げられる。
上記周期表14族又は15族の金属元素の金属塩として、例えば、周期表14族又は15族の金属元素の塩化物、オキシ塩化物、硝酸塩、炭酸塩、硫酸塩、アンモニウム塩、ホウ酸塩、ケイ酸塩、リン酸塩、水酸化物、過酸化物等が挙げられる。また、上記周期表14族又は15族の金属元素の金属塩には、その水和物も含まれる。
上記周期表14族又は15族の金属元素の有機金属化合物として、例えば、周期表14族又は15族の金属元素のカルボン酸、ジカルボン酸、オリゴカルボン酸、ポリカルボン酸の塩化合物が挙げられ、より具体的には、周期表14族又は15族の金属元素の酢酸、ギ酸、プロピオン酸、オクチル酸、ステアリン酸、シュウ酸、クエン酸、乳酸等の塩化合物等が挙げられる。
上記周期表14族又は15族の金属元素の有機金属化合物として、例えば、周期表14族又は15族の金属元素のカルボン酸、ジカルボン酸、オリゴカルボン酸、ポリカルボン酸の塩化合物が挙げられ、より具体的には、周期表14族又は15族の金属元素の酢酸、ギ酸、プロピオン酸、オクチル酸、ステアリン酸、シュウ酸、クエン酸、乳酸等の塩化合物等が挙げられる。
上記半導体形成用塗布液における上記周期表14族又は15族元素を含む化合物の含有量は、好ましい下限が5重量%、好ましい上限が30重量%である。上記含有量が5重量%以上であれば、良質な硫化物及び/又はセレン化物半導体部位を容易に形成することができる。上記含有量が30重量%以下であれば、安定な半導体形成用塗布液を容易に得ることができる。
上記硫黄含有化合物として、例えば、チオ尿素、チオ尿素の誘導体、チオアセトアミド、チオアセトアミドの誘導体、ジチオカルバミン酸塩(Dithiocarbamate)、キサントゲン酸塩(Xanthate)、ジチオリン酸塩(Dithiophosphate)、チオ硫酸塩、チオシアン酸塩等が挙げられる。
上記チオ尿素の誘導体として、例えば、1−アセチル−2−チオ尿素、エチレンチオ尿素、1,3−ジエチルー2−チオ尿素、1,3−ジメチルチオ尿素、テトラメチルチオ尿素、N−メチルチオ尿素、1−フェニルー2−チオ尿素、ジチオビウレット等が挙げられる。上記ジチオカルバミン酸塩として、例えば、ジメチルジチオカルバミン酸ナトリウム、ジエチルジチオカルバミン酸ナトリウム、ジメチルジチオカルバミン酸カリウム、ジエチルジチオカルバミン酸カリウム等が挙げられる。上記キサントゲン酸塩として、例えば、エチルキサントゲン酸ナトリウム(sodium ethyl xanthate)、エチルキサントゲン酸カリウム、イソプロピルキサントゲン酸ナトリウム、イソプロピルキサントゲン酸カリウム等が挙げられる。上記チオ硫酸塩として、例えば、チオ硫酸ナトリウム、チオ硫酸カリウム、チオ硫酸アンモニウム等が挙げられる。上記チオシアン酸塩として、例えば、チオシアン酸カリウム、チオシアン酸カリウム、チオシアン酸アンモニウム等が挙げられる。これらの硫黄含有化合物は単独で用いられてもよく、2種以上が併用されてもよい。
上記セレン含有化合物として、例えば、セレノ尿素、セレノ尿素の誘導体、セレノアセトアミド、セレノセトアミドの誘導体、ジセレノカルバミン酸塩、セレノ硫酸塩、セレノシアン酸塩、セレン化水素、塩化セレン、臭化セレン、ヨウ化セレン、セレノフェノール、亜セレン酸等が挙げられる。これらのセレン含有化合物は単独で用いられてもよく、2種以上が併用されてもよい。
上記セレノ尿素の誘導体として、例えば、1−アセチル−2−セレノ尿素、エチレンセレノ尿素、1,3−ジエチル−2−セレノ尿素、1,3−ジメチルセレノ尿素、テトラメチルセレノ尿素、N−メチルセレノ尿素、1−フェニル−2−セレノ尿素等が挙げられる。上記ジセレノカルバミン酸塩として、例えば、ジメチルジセレノカルバミン酸ナトリウム、ジエチルジセレノカルバミン酸ナトリウム、ジメチルジセレノカルバミン酸カリウム、ジエチルジセレノカルバミン酸カリウム等が挙げられる。上記セレノ硫酸塩として、例えば、セレノ硫酸ナトリウム、セレノ硫酸カリウム、セレノ硫酸アンモニウム等が挙げられる。上記セレノシアン酸塩として、例えば、セレノシアン酸カリウム、セレノシアン酸アンモニウム等が挙げられる。
上記半導体形成用塗布液における上記硫黄含有化合物及び/又はセレン含有化合物の含有量は、上記周期表14族又は15族元素を含む化合物のモル数に対して、1〜30倍が好ましく、2〜20倍がより好ましい。上記含有量が1倍以上であれば、量論比の硫化物及び/又はセレン化物半導体が得られやすくなる。上記含有量が30倍以下であれば、半導体形成用塗布液の安定性がより向上する。
上記周期表14族又は15族元素を含む化合物と、上記硫黄含有化合物及び/又はセレン含有化合物とは、錯体を形成していることが好ましく、該錯体は、上記周期表14族又は15族元素と、上記硫黄含有化合物及び/又はセレン含有化合物との間に形成されることがより好ましい。上記硫黄含有化合物中の硫黄元素又はセレン含有化合物中のセレン元素は、化学結合に関与していない孤立電子対を有するため、上記周期表14族又は15族元素の空の電子軌道(d軌道又はf軌道)との間に配位結合を形成しやすい。
このような錯体が形成されることで、半導体形成用塗布液の安定性が向上し、その結果、均一な良質の硫化物及び/又はセレン化物半導体部位が形成されるだけではなく、その電気的な特性及び半導体特性も向上する。
なお、周期表14族又は15族元素と、硫黄含有化合物及び/又はセレン含有化合物との間に形成された錯体は、赤外吸収スペクトルにて、周期表14族又は15族元素−硫黄間の結合に由来する吸収ピーク或いは周期表14族又は15族元素−セレン間の結合に由来する吸収ピークを測定することで確認することができる。
このような錯体が形成されることで、半導体形成用塗布液の安定性が向上し、その結果、均一な良質の硫化物及び/又はセレン化物半導体部位が形成されるだけではなく、その電気的な特性及び半導体特性も向上する。
なお、周期表14族又は15族元素と、硫黄含有化合物及び/又はセレン含有化合物との間に形成された錯体は、赤外吸収スペクトルにて、周期表14族又は15族元素−硫黄間の結合に由来する吸収ピーク或いは周期表14族又は15族元素−セレン間の結合に由来する吸収ピークを測定することで確認することができる。
上記半導体形成用塗布液は、更に、有機溶媒を含有することが好ましい。
上記有機溶媒を適宜選択することで、上述したような錯体を形成させやすくすることができる。上記有機溶媒は特に限定されず、例えば、メタノール、エタノール、N,N−ジメチルホルムアミド、ジメチルスルホキシド、アセトン、ジオキサン、テトラヒドロフラン、イソプロパノール、n−プロパノール、クロロホルム、クロロベンゼン、ピリジン、トルエン等が挙げられる。これらの有機溶媒は単独で用いられてもよく、2種以上が併用されてもよい。なかでも、メタノール、エタノール、アセトン、N,N−ジメチルホルムアミドが好ましく、電気的な特性及び半導体特性のより優れた硫化物及び/又はセレン化物半導体部位が形成されることから、N,N−ジメチルホルムアミドがより好ましい。
上記有機溶媒を適宜選択することで、上述したような錯体を形成させやすくすることができる。上記有機溶媒は特に限定されず、例えば、メタノール、エタノール、N,N−ジメチルホルムアミド、ジメチルスルホキシド、アセトン、ジオキサン、テトラヒドロフラン、イソプロパノール、n−プロパノール、クロロホルム、クロロベンゼン、ピリジン、トルエン等が挙げられる。これらの有機溶媒は単独で用いられてもよく、2種以上が併用されてもよい。なかでも、メタノール、エタノール、アセトン、N,N−ジメチルホルムアミドが好ましく、電気的な特性及び半導体特性のより優れた硫化物及び/又はセレン化物半導体部位が形成されることから、N,N−ジメチルホルムアミドがより好ましい。
また、上記半導体形成用塗布液は、本発明の効果を阻害しない範囲内において、水等の非有機溶媒成分を更に含有してもよい。
本発明によれば、光電変換効率を高めることができ、特に各層のエネルギー準位の制御によって電子−ホール対の再結合を抑制することで開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少ない薄膜太陽電池を提供することができる。また、本発明によれば、該薄膜太陽電池の製造方法を提供することができる。
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されない。
(実施例1)
(チタンを含有する塗布液の作製)
チタン粉末10mmolを精秤し、ビーカーに入れ、過酸化水素水40gを加え、更にアンモニア水10gを加えた。これを2時間水冷した後、L−乳酸30mmolを添加し、80℃に設定したホットプレートで一日加温し、そこへ蒸留水10mLを添加し、チタンを含有する塗布液を作製した。
(チタンを含有する塗布液の作製)
チタン粉末10mmolを精秤し、ビーカーに入れ、過酸化水素水40gを加え、更にアンモニア水10gを加えた。これを2時間水冷した後、L−乳酸30mmolを添加し、80℃に設定したホットプレートで一日加温し、そこへ蒸留水10mLを添加し、チタンを含有する塗布液を作製した。
(チタン酸アルカリ土類化合物を形成可能な塗布液の作製)
チタン粉末10mmolを精秤し、ビーカーに入れ、過酸化水素水40gを加え、更にアンモニア水10gを加えた。これを2時間水冷した後、L−乳酸50mmolと酢酸ストロンチウム0.5水和物10mmolとを添加し、80℃に設定したホットプレートで一日加温し、そこへ蒸留水50mLを添加し、チタン酸アルカリ土類化合物を形成可能な塗布液を作製した。
チタン粉末10mmolを精秤し、ビーカーに入れ、過酸化水素水40gを加え、更にアンモニア水10gを加えた。これを2時間水冷した後、L−乳酸50mmolと酢酸ストロンチウム0.5水和物10mmolとを添加し、80℃に設定したホットプレートで一日加温し、そこへ蒸留水50mLを添加し、チタン酸アルカリ土類化合物を形成可能な塗布液を作製した。
(半導体形成用塗布液の作製)
N,N−ジメチルホルムアミド100重量部に、塩化アンチモン(III)20重量部を添加した後、攪拌することによって溶解した。N,N−ジメチルホルムアミド100重量部に、チオ尿素(CS(NH2)2)20重量部を添加した後、攪拌することによって溶解した。塩化アンチモンのN,N−ジメチルホルムアミド溶液50重量部に、チオ尿素のN,N−ジメチルホルムアミド溶液40重量部を攪拌しながら徐々に添加した。その際、溶液は混合前の無色透明から黄色透明に変わった。添加終了後に更に30分間攪拌することによって、塩化アンチモンとチオ尿素とを含有する半導体形成用塗布液を作製した。
N,N−ジメチルホルムアミド100重量部に、塩化アンチモン(III)20重量部を添加した後、攪拌することによって溶解した。N,N−ジメチルホルムアミド100重量部に、チオ尿素(CS(NH2)2)20重量部を添加した後、攪拌することによって溶解した。塩化アンチモンのN,N−ジメチルホルムアミド溶液50重量部に、チオ尿素のN,N−ジメチルホルムアミド溶液40重量部を攪拌しながら徐々に添加した。その際、溶液は混合前の無色透明から黄色透明に変わった。添加終了後に更に30分間攪拌することによって、塩化アンチモンとチオ尿素とを含有する半導体形成用塗布液を作製した。
(薄膜太陽電池の作製)
FTOガラス基板上に、チタンを含有する塗布液を回転数1500rpmの条件でスピンコート法により100nmの厚みに塗布した。塗布後、大気中550℃で10分間焼成し、電子輸送層を形成した。
得られた電子輸送層上に、チタン酸アルカリ土類化合物を形成可能な塗布液を回転数1500rpmの条件でスピンコート法により30nmの厚みに塗布した。塗布後、大気中600℃で30分間焼成し、チタン酸アルカリ土類化合物を含有する層(チタン酸ストロンチウム層)を形成した。
得られたチタン酸アルカリ土類化合物を含有する層上に、半導体形成用塗布液を回転数1500rpmの条件でスピンコート法により塗布した。塗布後、サンプルを真空炉に入れ、真空に引きながら260℃で10分間焼成し、硫化物半導体薄膜(薄膜状の硫化物半導体部位)を形成した。真空炉から取出した硫化物半導体薄膜は黒色であった。真空炉から取出した後、得られた硫化物半導体薄膜の上に、有機半導体薄膜(薄膜状の有機半導体部位)としてポリ(3−ヘキシルチオフェン)(P3HT)をスピンコート法により50nmの厚みに成膜した。その後、有機半導体薄膜の上にホール輸送層としてポリエチレンジオキサイドチオフェン:ポリスチレンスルフォネート(PEDOT:PSS)をスピンコート法により50nmの厚みに成膜した。次いで、ホール輸送層の上に厚み80nmの金電極を真空蒸着法により成膜することによって薄膜太陽電池を作製した。
FTOガラス基板上に、チタンを含有する塗布液を回転数1500rpmの条件でスピンコート法により100nmの厚みに塗布した。塗布後、大気中550℃で10分間焼成し、電子輸送層を形成した。
得られた電子輸送層上に、チタン酸アルカリ土類化合物を形成可能な塗布液を回転数1500rpmの条件でスピンコート法により30nmの厚みに塗布した。塗布後、大気中600℃で30分間焼成し、チタン酸アルカリ土類化合物を含有する層(チタン酸ストロンチウム層)を形成した。
得られたチタン酸アルカリ土類化合物を含有する層上に、半導体形成用塗布液を回転数1500rpmの条件でスピンコート法により塗布した。塗布後、サンプルを真空炉に入れ、真空に引きながら260℃で10分間焼成し、硫化物半導体薄膜(薄膜状の硫化物半導体部位)を形成した。真空炉から取出した硫化物半導体薄膜は黒色であった。真空炉から取出した後、得られた硫化物半導体薄膜の上に、有機半導体薄膜(薄膜状の有機半導体部位)としてポリ(3−ヘキシルチオフェン)(P3HT)をスピンコート法により50nmの厚みに成膜した。その後、有機半導体薄膜の上にホール輸送層としてポリエチレンジオキサイドチオフェン:ポリスチレンスルフォネート(PEDOT:PSS)をスピンコート法により50nmの厚みに成膜した。次いで、ホール輸送層の上に厚み80nmの金電極を真空蒸着法により成膜することによって薄膜太陽電池を作製した。
(実施例2、3、6、7)
酢酸ストロンチウム0.5水和物10mmolの代わりに炭酸バリウム10mmol又は炭酸カルシウム1mmolを用いてチタン酸アルカリ土類化合物を表1に示すように変更した、或いは、有機半導体を表1に示すように変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
酢酸ストロンチウム0.5水和物10mmolの代わりに炭酸バリウム10mmol又は炭酸カルシウム1mmolを用いてチタン酸アルカリ土類化合物を表1に示すように変更した、或いは、有機半導体を表1に示すように変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例4)
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物7mmol及び炭酸バリウム3mmolの混合物に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物7mmol及び炭酸バリウム3mmolの混合物に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例5)
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物9mmol及び炭酸カルシウム1mmolの混合物に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物9mmol及び炭酸カルシウム1mmolの混合物に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例8)
半導体形成用塗布液に塩化亜鉛を1重量%添加したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
半導体形成用塗布液に塩化亜鉛を1重量%添加したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例9)
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物9mmolと硝酸ランタン1mmolとに変更し、かつ、半導体形成用塗布液に塩化亜鉛を1重量%添加したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
酢酸ストロンチウム0.5水和物10mmolを酢酸ストロンチウム0.5水和物9mmolと硝酸ランタン1mmolとに変更し、かつ、半導体形成用塗布液に塩化亜鉛を1重量%添加したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例10)
チオ尿素(CS(NH2)2)をセレノ尿素に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
チオ尿素(CS(NH2)2)をセレノ尿素に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例11)
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化スズを真空蒸着法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化スズを真空蒸着法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例12)
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化アンチモンを真空蒸着法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化アンチモンを真空蒸着法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(実施例13)
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化アンチモンを化学析出法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
半導体形成用塗布液を用いて硫化アンチモンを作製する工程を、硫化アンチモンを化学析出法により作製する工程に変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(比較例1)
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例1と同様にして薄膜太陽電池を作製した。
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(比較例2)
有機半導体を無機半導体であるCuSCNに変更したこと以外は比較例1と同様にして薄膜太陽電池を作製した。
有機半導体を無機半導体であるCuSCNに変更したこと以外は比較例1と同様にして薄膜太陽電池を作製した。
(比較例3)
有機半導体を無機半導体であるCuSCNに変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
有機半導体を無機半導体であるCuSCNに変更したこと以外は実施例1と同様にして薄膜太陽電池を作製した。
(比較例4)
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例10と同様にして薄膜太陽電池を作製した。
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例10と同様にして薄膜太陽電池を作製した。
(比較例5)
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例11と同様にして薄膜太陽電池を作製した。
チタン酸アルカリ土類化合物を含有する層を作製する工程がないこと以外は実施例11と同様にして薄膜太陽電池を作製した。
<評価>
実施例及び比較例で得られた薄膜太陽電池について、以下の評価を行った。
(太陽電池特性評価)
(1)開放電圧
実施例及び比較例で得られた薄膜太陽電池の電極間に、電源(KEITHLEY社製、236モデル)を接続し、強度100mW/cm2のソーラーシミュレーション(山下電装社製)を用いて薄膜太陽電池の開放電圧V0Cを測定し、チタン酸アルカリ土類化合物を含有する層を形成していない以外は同様の条件で作製した薄膜太陽電池の開放電圧を1.00として規格化した結果を表1に示した。
また、実施例1〜13、比較例3については、薄膜太陽電池の断面のFE−TEM/EDS線分析測定を行い、チタン酸アルカリ土類化合物を含有する層と、硫化物及び/又はセレン化物半導体薄膜(薄膜状の硫化物及び/又はセレン化物半導体部位)とが別々の層として分離して形成されていること、硫化物及び/又はセレン化物半導体部位の厚みが50nm、電子輸送層の厚みが100nm、チタン酸アルカリ土類化合物を含有する層の厚みが20nmであることを確認した。
また、XRD測定より硫化物及び/又はセレン化物半導体及びチタン酸アルカリ土類化合物は結晶化していることを確認した。
実施例及び比較例で得られた薄膜太陽電池について、以下の評価を行った。
(太陽電池特性評価)
(1)開放電圧
実施例及び比較例で得られた薄膜太陽電池の電極間に、電源(KEITHLEY社製、236モデル)を接続し、強度100mW/cm2のソーラーシミュレーション(山下電装社製)を用いて薄膜太陽電池の開放電圧V0Cを測定し、チタン酸アルカリ土類化合物を含有する層を形成していない以外は同様の条件で作製した薄膜太陽電池の開放電圧を1.00として規格化した結果を表1に示した。
また、実施例1〜13、比較例3については、薄膜太陽電池の断面のFE−TEM/EDS線分析測定を行い、チタン酸アルカリ土類化合物を含有する層と、硫化物及び/又はセレン化物半導体薄膜(薄膜状の硫化物及び/又はセレン化物半導体部位)とが別々の層として分離して形成されていること、硫化物及び/又はセレン化物半導体部位の厚みが50nm、電子輸送層の厚みが100nm、チタン酸アルカリ土類化合物を含有する層の厚みが20nmであることを確認した。
また、XRD測定より硫化物及び/又はセレン化物半導体及びチタン酸アルカリ土類化合物は結晶化していることを確認した。
(2)バンドギャップ電圧
実施例及び比較例で得られた薄膜太陽電池を液体ヘリウムで冷却しながら上記と同様に薄膜太陽電池の開放電圧V0Cを測定し、温度と開放電圧とをグラフへプロットし一次の外挿線を引き0(K)での開放電圧V0C(T=0(K))を算出し、表1に示した。
実施例及び比較例で得られた薄膜太陽電池を液体ヘリウムで冷却しながら上記と同様に薄膜太陽電池の開放電圧V0Cを測定し、温度と開放電圧とをグラフへプロットし一次の外挿線を引き0(K)での開放電圧V0C(T=0(K))を算出し、表1に示した。
(3)逆方向飽和電流密度(再結合評価)
上記と同様に実施例及び比較例で得られた薄膜太陽電池の電流−電圧特性を測定し、得られた結果から作成した電圧に対する電流の対数プロットからダイオードの拡散電流領域を求めた。その領域での近似直線をV=0まで外挿し、逆方向飽和電流密度J0を求めた。その結果を表1に示した。
上記と同様に実施例及び比較例で得られた薄膜太陽電池の電流−電圧特性を測定し、得られた結果から作成した電圧に対する電流の対数プロットからダイオードの拡散電流領域を求めた。その領域での近似直線をV=0まで外挿し、逆方向飽和電流密度J0を求めた。その結果を表1に示した。
(4)550℃焼成時の開放電圧
チタン酸アルカリ土類化合物を含有する層を形成する際、焼成温度を550℃にした時の開放電圧V0C(550℃)を、チタン酸アルカリ土類化合物を含有する層を形成していない以外は同様の条件で作製した薄膜太陽電池の開放電圧を1.00として規格化した結果を表1に示した。
チタン酸アルカリ土類化合物を含有する層を形成する際、焼成温度を550℃にした時の開放電圧V0C(550℃)を、チタン酸アルカリ土類化合物を含有する層を形成していない以外は同様の条件で作製した薄膜太陽電池の開放電圧を1.00として規格化した結果を表1に示した。
(性能安定性評価)
上記の実施例及び比較例における薄膜太陽電池の製造方法と同じ方法で、評価用セルを4個作製した。4個の評価用セルの光電変換効率を上記と同様にしてそれぞれ測定した。
△:光電変換効率の最大値と最小値との差が、最大値の20%より大きかった
○:光電変換効率の最大値と最小値との差が、最大値の20%以下であった
上記の実施例及び比較例における薄膜太陽電池の製造方法と同じ方法で、評価用セルを4個作製した。4個の評価用セルの光電変換効率を上記と同様にしてそれぞれ測定した。
△:光電変換効率の最大値と最小値との差が、最大値の20%より大きかった
○:光電変換効率の最大値と最小値との差が、最大値の20%以下であった
(加温後の変換効率)
実施例及び比較例で得られた薄膜太陽電池を370Kで15分加温し、室温まで降温させた薄膜太陽電池の電極間に、電源(KEITHLEY社製、236モデル)を接続し、強度100mW/cm2のソーラーシミュレーション(山下電装社製)を用いて薄膜太陽電池の変換効率を測定した。加温前に室温で同様の条件で測定した薄膜太陽電池の変換効率を1.00として規格化した結果を表1に示した。
×:変換効率が0.9未満であった
○:変換効率が0.9以上であった
実施例及び比較例で得られた薄膜太陽電池を370Kで15分加温し、室温まで降温させた薄膜太陽電池の電極間に、電源(KEITHLEY社製、236モデル)を接続し、強度100mW/cm2のソーラーシミュレーション(山下電装社製)を用いて薄膜太陽電池の変換効率を測定した。加温前に室温で同様の条件で測定した薄膜太陽電池の変換効率を1.00として規格化した結果を表1に示した。
×:変換効率が0.9未満であった
○:変換効率が0.9以上であった
なお、表1中、PcCuは銅フタロシアニンを表し、PCPDTBTはポリ(シクロペンタジチオフェン−ベンゾチアジアゾール)共重合体を表す。
本発明によれば、光電変換効率を高めることができ、特に開放電圧を高めることができ、更に、高温での加温後にも光電変換効率の低下が少ない薄膜太陽電池を提供することができる。また、本発明によれば、該薄膜太陽電池の製造方法を提供することができる。
1 薄膜太陽電池
2 基板
3 透明電極(陰極)
4 電子輸送層
5 チタン酸アルカリ土類化合物を含有する層
6 薄膜状の硫化物及び/又はセレン化物半導体部位
7 薄膜状の有機半導体部位
8 光電変換層(積層体)
9 ホール輸送層
10 電極(陽極)
1’ 薄膜太陽電池
2’ 基板
3’ 透明電極(陰極)
4a 薄膜状の電子輸送層
4b 多孔質状の電子輸送層
4’ 電子輸送層
5’ チタン酸アルカリ土類化合物を含有する層
6’ 硫化物及び/又はセレン化物半導体部位
7’ 有機半導体部位
8’ 光電変換層(複合膜)
9’ ホール輸送層
10’ 電極(陽極)
2 基板
3 透明電極(陰極)
4 電子輸送層
5 チタン酸アルカリ土類化合物を含有する層
6 薄膜状の硫化物及び/又はセレン化物半導体部位
7 薄膜状の有機半導体部位
8 光電変換層(積層体)
9 ホール輸送層
10 電極(陽極)
1’ 薄膜太陽電池
2’ 基板
3’ 透明電極(陰極)
4a 薄膜状の電子輸送層
4b 多孔質状の電子輸送層
4’ 電子輸送層
5’ チタン酸アルカリ土類化合物を含有する層
6’ 硫化物及び/又はセレン化物半導体部位
7’ 有機半導体部位
8’ 光電変換層(複合膜)
9’ ホール輸送層
10’ 電極(陽極)
Claims (6)
- 陰極と、陽極と、前記陰極と前記陽極との間に配置された光電変換層と、前記陰極と前記光電変換層との間に配置された電子輸送層とを有し、
前記光電変換層が、有機半導体を含有する部位と、硫化物及び/又はセレン化物を含有する部位とを有し、
前記光電変換層と前記電子輸送層との間に、チタン酸アルカリ土類化合物を含有する層が配置されていることを特徴とする薄膜太陽電池。 - チタン酸アルカリ土類化合物は、ストロンチウムを含むことを特徴とする請求項1記載の薄膜太陽電池。
- 硫化物及び/又はセレン化物は、周期表14族又は15族元素の硫化物及び/又はセレン化物であることを特徴とする請求項1記載の薄膜太陽電池。
- 硫化物及び/又はセレン化物は、硫化アンチモン又はセレン化アンチモンであることを特徴とする請求項1又は3記載の薄膜太陽電池。
- 陽極と光電変換層との間に、ホール輸送層が配置されていることを特徴とする請求項1、2、3又は4記載の薄膜太陽電池。
- 請求項1、2、3、4又は5記載の薄膜太陽電池を製造する方法であって、光電変換層又は電子輸送層上にチタン酸アルカリ土類化合物を含有する層を成膜する工程を有することを特徴とする薄膜太陽電池の製造方法。