JP2015096060A - Plant cultivation medium, and plant cultivation device and plant cultivation method using the same - Google Patents
Plant cultivation medium, and plant cultivation device and plant cultivation method using the same Download PDFInfo
- Publication number
- JP2015096060A JP2015096060A JP2014198476A JP2014198476A JP2015096060A JP 2015096060 A JP2015096060 A JP 2015096060A JP 2014198476 A JP2014198476 A JP 2014198476A JP 2014198476 A JP2014198476 A JP 2014198476A JP 2015096060 A JP2015096060 A JP 2015096060A
- Authority
- JP
- Japan
- Prior art keywords
- plant cultivation
- chip
- ethylene
- vinyl alcohol
- alcohol copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、花卉、根菜類を含む野菜、果実類、穀類などの各種作物の栽培の際に、従来の土壌やロックウールの代わりに用いることのできる植物栽培用培地、並びにそれを用いた植物栽培装置および植物栽培方法に関する。 The present invention relates to a plant culture medium that can be used in place of conventional soil and rock wool when cultivating various crops such as flowers, vegetables including root vegetables, fruits, and cereals, and plants using the same. The present invention relates to a cultivation apparatus and a plant cultivation method.
養液栽培は、作物を栽培するのに土壌を使用しないため、連作障害がなく、栽培環境や養分管理をコントロールしやすい。また、自動化、省力化ができ、収穫物の清浄性や肥料効率が高い栽培方法として注目されている。 Hydroponics does not use soil to cultivate crops, so there are no continuous cropping obstacles and it is easy to control the cultivation environment and nutrient management. It is also attracting attention as a cultivation method that can be automated and labor-saving and has high cleanliness of crops and high fertilizer efficiency.
養液栽培用の固形培地は水に浸漬されるため、ある程度の耐水性が必要であると共に、透水性、保水性、通気性、強度などが要求される。従来、養液栽培用の固形培地としては天然石（おもに玄武岩）を繊維状にしたものを収束させたロックウールなどが知られている。 Since the solid medium for hydroponics is immersed in water, it needs a certain level of water resistance, and also requires water permeability, water retention, air permeability, strength, and the like. Conventionally, as a solid medium for hydroponics, rock wool or the like obtained by converging a natural stone (mainly basalt) in a fibrous form is known.
養液栽培においては根が固形培地の内部に張り詰めるために新たな固形培地に交換する必要が生じることがあるが、ロックウールを固形培地に使用した場合には、リサイクルが困難であるという問題がある。その上、ロックウールは無機物であるため使用後のロックウールの有効な処分方法がない。現在、使用後のロックウールの処分方法としては、産業廃棄物として廃棄する、田に少量ずつ鋤き込むなどの方法が採られているが、これらのような方法で処分するにも限界がある。また、ロックウールでは、植物の根の成長が物理的に阻害されるので、根菜類の栽培が困難であるという問題もある。そのため、植物栽培用培地として必要な耐水性、透水性、保水性、通気性、強度などの物性を保持し、理化学的にも安定していて作物を充分に生長させることができ、しかも、環境への負荷の小さい培地が求められている。 In hydroponic culture, it may be necessary to replace the root with a new solid medium to fill the inside of the solid medium. However, when rock wool is used for the solid medium, it is difficult to recycle. There is. Moreover, since rock wool is an inorganic substance, there is no effective disposal method for rock wool after use. Currently, methods for disposing of rock wool after use include methods such as discarding it as industrial waste and pouring it into rice fields in small quantities. However, there are limits to how these can be disposed of. . In addition, in the case of rock wool, there is a problem that it is difficult to cultivate root vegetables because plant root growth is physically inhibited. Therefore, it retains the physical properties such as water resistance, water permeability, water retention, breathability, strength, etc. necessary for plant cultivation medium, is stable in physicochemical and can sufficiently grow crops, There is a need for a medium with a low load on the medium.
特開平８−２８０２８１号公報（特許文献１）には、ポリビニルアルコールを用いた植物栽培用培地が開示されている。特許文献１では、たとえば木炭粉の結合剤としてけん化度９８モル％以上の完全けん化型ポリビニルアルコール樹脂を用い、このようなけん化度９８モル％以上の完全けん化型ポリビニルアルコール樹脂が親水性でありながら水に溶解しにくく、木炭粉の結合剤として使用した場合、木炭粉粒子表面の水に対する濡れ性を向上させると共に水中に浸漬されても容易には倒壊しない培地となることが記載されている。しかしながら、たとえけん化度９８モル％以上の完全けん化型ポリビニルアルコール樹脂を使用したとしても水溶性ポリマーであることには変わりなく、特許文献１に記載された培地を長期使用した場合にはポリビニルアルコール樹脂が徐々に溶出するため、長期にわたり作物を生長させることは困難であった。 JP-A-8-280281 (Patent Document 1) discloses a plant cultivation medium using polyvinyl alcohol. In Patent Document 1, for example, a fully saponified polyvinyl alcohol resin having a saponification degree of 98 mol% or more is used as a binder for charcoal powder, and such a fully saponified polyvinyl alcohol resin having a saponification degree of 98 mol% or more is hydrophilic. It is described that it is difficult to dissolve in water and when used as a binder for charcoal powder, it improves the wettability of the charcoal powder particle surface to water and is a medium that does not easily collapse even when immersed in water. However, even if a completely saponified polyvinyl alcohol resin having a saponification degree of 98 mol% or more is used, it remains a water-soluble polymer, and when the medium described in Patent Document 1 is used for a long time, the polyvinyl alcohol resin is used. It was difficult to grow crops over a long period of time because of the leaching of
また、特開平２−１０９９２０号公報（特許文献２）には、培地として粒状またはチップ状の多孔体を用いる養液栽培方法が記載されており、当該多孔体としては、ポリビニルアルコールを素材とするものが吸水性および吸湿性の保持力の点で好ましいことが記載されている。しかしながら、上述のようにポリビニルアルコールは水溶性ポリマーであるために湿潤下で長期安定性に乏しく、長期にわたり作物を生長させる場合には、培地の形状を維持することが困難であり、実用性に乏しかった。 JP-A-2-109920 (Patent Document 2) describes a nourishing culture method using a granular or chip-like porous body as a medium, and the porous body is made of polyvinyl alcohol. It is described that those are preferable in terms of water-absorbing and hygroscopic holding power. However, as described above, since polyvinyl alcohol is a water-soluble polymer, it has poor long-term stability under humidity, and when growing crops over a long period of time, it is difficult to maintain the shape of the medium. It was scarce.
特開平６−９８６２７号公報（特許文献３）には、吸収性材料に水および香料を含ませてなる吸水ゲルを用いた芳香性人工培地が開示され、吸収性材料としてエチレン−ビニルアルコール共重合体を用い得ることが記載されている。エチレン−ビニルアルコール共重合体を用いた場合には、上述のポリビニルアルコールのように徐々に溶出してしまうことは防止できる。 JP-A-6-98627 (Patent Document 3) discloses an aromatic artificial medium using a water-absorbing gel in which water and a fragrance are contained in an absorbent material, and ethylene-vinyl alcohol copolymer as an absorbent material. It is described that coalescence can be used. When an ethylene-vinyl alcohol copolymer is used, it can be prevented that it gradually elutes like the above-mentioned polyvinyl alcohol.
出願人は、国際公開第２０１２／１０８３７４号（特許文献４）において、エチレン−ビニルアルコール共重合体チップを含む植物栽培用培地について提案している。この特許文献４に記載された植物栽培用培地によれば、作物を充分に生長させることができるとともに、リサイクル性にも優れていて繰り返し使用することができ、使用後に焼却などによって容易に廃棄することができ、環境への負荷の小さい植物栽培用培地を提供することができる。 The applicant has proposed a culture medium for plant cultivation containing an ethylene-vinyl alcohol copolymer chip in International Publication No. 2012/108374 (Patent Document 4). According to the plant cultivation medium described in Patent Document 4, the crop can be sufficiently grown and is excellent in recyclability and can be used repeatedly, and is easily discarded by incineration after use. It is possible to provide a medium for plant cultivation with a low environmental burden.
本発明の目的は、作物の生長効率がさらに改善された、エチレン−ビニルアルコール共重合体を含むチップを用いた植物栽培用培地、並びにこれを用いた植物栽培装置および植物栽培方法を提供することである。 An object of the present invention is to provide a plant cultivation medium using a chip containing an ethylene-vinyl alcohol copolymer, and a plant cultivation apparatus and a plant cultivation method using the same, wherein the growth efficiency of the crop is further improved. It is.
本発明者らは、植物栽培用培地に用いられるエチレン−ビニルアルコール共重合体を含むチップの形状に着目し、チップの特定の面の算術平均粗さが、チップ間に含まれる水の割合である保水量に影響することを見出した。また、前記算術平均粗さが一定以上の値であるチップを用いた植物栽培用培地での栽培が、植物の生長の効率に影響を及ぼすことを見出し、本発明を完成させた。すなわち、本発明は以下のとおりである。 The inventors pay attention to the shape of a chip containing an ethylene-vinyl alcohol copolymer used in a plant cultivation medium, and the arithmetic average roughness of a specific surface of the chip is the ratio of water contained between the chips. It has been found to affect a certain amount of water retention. Further, the inventors have found that cultivation on a plant cultivation medium using a chip having an arithmetic average roughness of a certain value or more affects the efficiency of plant growth, thereby completing the present invention. That is, the present invention is as follows.
本発明の植物栽培用培地は、エチレン−ビニルアルコール共重合体を含むチップを用いた植物栽培用培地であって、前記チップの形状が柱状、扁平状またはフレーク状であり、柱状のチップにおいては側面、扁平状のチップにおいては短手方向を中心軸とした周方向の曲面、フレーク状のチップにおいては主面のＪＩＳ Ｂ０６０１に準拠して測定される算術平均粗さが０．０５μｍ以上である。 The plant cultivation medium of the present invention is a plant cultivation medium using a chip containing an ethylene-vinyl alcohol copolymer, and the shape of the chip is a columnar shape, a flat shape, or a flake shape. In the side and flat chips, the curved surface in the circumferential direction with the short side as the central axis, and in the flake chips, the arithmetic average roughness measured according to JIS B0601 of the main surface is 0.05 μm or more. .
本発明の植物栽培用培地において、前記算術平均粗さが０．０５μｍ〜１０μｍであることが好ましい。 In the plant cultivation medium of the present invention, the arithmetic average roughness is preferably 0.05 μm to 10 μm.
本発明の植物栽培用培地において、前記エチレン−ビニルアルコール共重合体を含むチップの体積１００ｍＬに対する保水量が５ｇ以上であることが好ましい。 In the plant cultivation medium of the present invention, it is preferable that the amount of water retained for a volume of 100 mL of the chip containing the ethylene-vinyl alcohol copolymer is 5 g or more.
本発明の植物栽培用培地において、前記エチレン−ビニルアルコール共重合体のエチレン含有量が２０〜６０モル％であることが好ましい。 In the plant cultivation medium of the present invention, the ethylene content of the ethylene-vinyl alcohol copolymer is preferably 20 to 60 mol%.
本発明はまた、上述した本発明の植物栽培用培地を用いた植物栽培装置についても提供する。 The present invention also provides a plant cultivation apparatus using the above-described plant cultivation medium of the present invention.
本発明はさらに、上述した本発明の植物栽培用培地を用いた植物栽培方法についても提供する。 The present invention further provides a plant cultivation method using the above-described plant cultivation medium of the present invention.
本発明によれば、花卉、根菜類を含む野菜、果実類、穀類などの各種作物を栽培するにあたり、後述する実施例および比較例に実証されるように、高い効率で充分にこれら作物を生長させることができる。また本発明によれば、リサイクル性にも優れていて繰り返し使用することができ、使用後に焼却などによって容易に廃棄することができ、環境への負荷の小さい植物栽培用培地を提供することができる。 According to the present invention, when cultivating various crops such as flowers, vegetables including root vegetables, fruits, and cereals, these crops are sufficiently grown with high efficiency as demonstrated in Examples and Comparative Examples described later. Can be made. Further, according to the present invention, it is excellent in recyclability, can be used repeatedly, can be easily discarded by incineration after use, and can provide a plant cultivation medium with a low environmental load. .
本発明の植物栽培用培地には、エチレン−ビニルアルコール共重合体を含むチップを用いる。ここで、本発明におけるチップは、他の樹脂成分、たとえば各種ポリオレフィン（ポリエチレン、ポリプロピレン、ポリ１−ブテン、ポリ４−メチル−１−ペンテン、エチレン−プロピレン共重合体、エチレンと炭素数４以上のα−オレフィンとの共重合体、エチレン−ビニルエステル共重合体、エチレン−アクリル酸エステル共重合体、またはこれらを不飽和カルボン酸で変性、若しくはその誘導体でグラフト変性、若しくは無水マレイン酸で変性した変性ポリオレフィンなど）、各種ナイロン（ナイロン−６、ナイロン−６６、ナイロン−６／６６共重合体など）、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリエステル、ポリスチレン、ポリアクリロニトリル、ポリウレタン、ポリアセタールおよび変性ポリビニルアルコールなどとの組成物であってもよい。エチレン−ビニルアルコール共重合体と他の樹脂成分との全質量に対するエチレン−ビニルアルコール共重合体の含有量は３質量％以上であることが好ましく、５質量％以上であることがより好ましく、１０質量％以上であることがさらに好ましい。エチレン−ビニルアルコール共重合体の比率が上記範囲を下回る場合には、得られる植物栽培用培地の保水量が低下する虞がある。 The chip | tip containing an ethylene-vinyl alcohol copolymer is used for the culture medium for plant cultivation of this invention. Here, the chip in the present invention is composed of other resin components such as various polyolefins (polyethylene, polypropylene, poly 1-butene, poly 4-methyl-1-pentene, ethylene-propylene copolymer, ethylene and 4 or more carbon atoms. Copolymer with α-olefin, ethylene-vinyl ester copolymer, ethylene-acrylic ester copolymer, or these modified with unsaturated carboxylic acid, or graft modified with derivatives thereof, or modified with maleic anhydride Modified polyolefin, etc.), various nylons (nylon-6, nylon-66, nylon-6 / 66 copolymer, etc.), polyvinyl chloride, polyvinylidene chloride, polyester, polystyrene, polyacrylonitrile, polyurethane, polyacetal, modified polyvinyl alcohol, etc. Pair with It may be ones. The content of the ethylene-vinyl alcohol copolymer with respect to the total mass of the ethylene-vinyl alcohol copolymer and the other resin components is preferably 3% by mass or more, more preferably 5% by mass or more. More preferably, it is at least mass%. When the ratio of the ethylene-vinyl alcohol copolymer is below the above range, the water retention amount of the obtained plant cultivation medium may decrease.
また、本発明におけるチップは、上述の他の樹脂成分の表面をエチレン−ビニルアルコール共重合体でコーティングしたものであってもよい。エチレン−ビニルアルコール共重合体のコート厚みとしては０．１μｍ以上が好ましく、０．３μｍ以上がより好ましく、０．５μｍ以上であることがさらに好ましい。エチレン−ビニルアルコール共重合体のコート厚みが上記厚みよりも薄い場合、得られる植物栽培用培地の保水量が低下する虞がある。 Moreover, the chip | tip in this invention may coat the surface of the above-mentioned other resin component with the ethylene-vinyl alcohol copolymer. The coat thickness of the ethylene-vinyl alcohol copolymer is preferably 0.1 μm or more, more preferably 0.3 μm or more, and further preferably 0.5 μm or more. When the coat thickness of an ethylene-vinyl alcohol copolymer is thinner than the said thickness, there exists a possibility that the water retention amount of the culture medium for plant cultivation obtained may fall.
本発明におけるエチレン−ビニルアルコール共重合体は、主としてエチレン単位（−ＣＨ２ＣＨ２−）とビニルアルコール単位（−ＣＨ２−ＣＨ（ＯＨ）−）とからなる共重合体である。当該エチレン−ビニルアルコール共重合体を構成する全構造単位のモル数に対してエチレン単位およびビニルアルコール単位の合計のモル数が占める割合は８０モル％以上であることが好ましく、９０モル％以上であることがより好ましく、９５モル％以上であることがさらに好ましく、９９モル％以上であることが特に好ましい。 The ethylene-vinyl alcohol copolymer in the present invention is a copolymer mainly composed of ethylene units (—CH 2 CH 2 —) and vinyl alcohol units (—CH 2 —CH (OH) —). The ratio of the total number of moles of ethylene units and vinyl alcohol units to the number of moles of all structural units constituting the ethylene-vinyl alcohol copolymer is preferably 80 mol% or more, and 90 mol% or more. More preferably, it is more preferably 95 mol% or more, and particularly preferably 99 mol% or more.
また、エチレン−ビニルアルコール共重合体のエチレン含有量（エチレン−ビニルアルコール共重合体を構成する全構造単位のモル数に対してエチレン単位のモル数が占める割合）は、２０〜６０モル％の範囲内であることが好ましく、２２〜５８モル％の範囲内であることがより好ましい。エチレン含有量が上記範囲を下回る場合には、得られる植物栽培用培地の耐久性が不足し、長時間連続して使用した際にエチレン−ビニルアルコール共重合体が溶出する虞がある。また、エチレン含有量が上記範囲を上回る場合には、得られる植物栽培用培地の親水性や強度が低下する虞がある。 The ethylene content of the ethylene-vinyl alcohol copolymer (ratio of the number of moles of ethylene units to the number of moles of all structural units constituting the ethylene-vinyl alcohol copolymer) is 20 to 60 mol%. It is preferably within the range, and more preferably within the range of 22 to 58 mol%. When the ethylene content is below the above range, the durability of the obtained plant cultivation medium is insufficient, and the ethylene-vinyl alcohol copolymer may be eluted when used continuously for a long time. Moreover, when ethylene content exceeds the said range, there exists a possibility that the hydrophilic property and intensity | strength of the culture medium for plant cultivation obtained may fall.
本発明におけるエチレン−ビニルアルコール共重合体の製造方法は特に制限されるものではなく、公知の適宜の製造方法を採用することができる。たとえば、エチレンとビニルエステル系単量体とを共重合して得られたエチレン−ビニルエステル共重合体をけん化触媒の存在下にアルコールを含む有機溶媒中でけん化する方法が一般的である。 The production method of the ethylene-vinyl alcohol copolymer in the present invention is not particularly limited, and any known appropriate production method can be employed. For example, a general method is to saponify an ethylene-vinyl ester copolymer obtained by copolymerizing ethylene and a vinyl ester monomer in an organic solvent containing alcohol in the presence of a saponification catalyst.
上述のビニルエステル系単量体としては、たとえばギ酸ビニル、酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、イソ酪酸ビニル、ピバリン酸ビニル、バーサティック酸ビニル、カプロン酸ビニル、カプリル酸ビニル、ラウリル酸ビニル、パルミチン酸ビニル、ステアリン酸ビニル、オレイン酸ビニル、安息香酸ビニルなどが挙げられるが、とりわけ酢酸ビニルが好ましい。 Examples of the vinyl ester monomers described above include vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl pivalate, vinyl versatate, vinyl caproate, vinyl caprylate, vinyl laurate, Examples thereof include vinyl palmitate, vinyl stearate, vinyl oleate, vinyl benzoate and the like, and vinyl acetate is particularly preferable.
エチレンとビニルエステル系単量体とを共重合する方法としては、溶液重合法、塊状重合法、懸濁重合法、乳化重合法など、公知の方法を採用することができる。重合開始剤としては、重合方法に応じて、アゾ系開始剤、過酸化物系開始剤、レドックス系開始剤などが適宜選ばれる。このとき、チオール酢酸、メルカプトプロピオン酸などのチオール化合物や、その他の連鎖移動剤の存在下で重合を行ってもよい。 As a method for copolymerizing ethylene and a vinyl ester monomer, known methods such as a solution polymerization method, a bulk polymerization method, a suspension polymerization method, and an emulsion polymerization method can be employed. As the polymerization initiator, an azo initiator, a peroxide initiator, a redox initiator, or the like is appropriately selected depending on the polymerization method. At this time, the polymerization may be performed in the presence of a thiol compound such as thiol acetic acid or mercaptopropionic acid, or other chain transfer agent.
けん化反応としては、有機溶媒中で公知のアルカリ触媒または酸触媒をけん化触媒として用いる加アルコール分解、加水分解などを採用することができ、中でもメタノールを溶媒として苛性ソーダ触媒を用いるけん化反応が簡便であり最も好ましい。 As the saponification reaction, it is possible to employ alcoholysis or hydrolysis using a known alkali catalyst or acid catalyst as a saponification catalyst in an organic solvent. Among them, a saponification reaction using a caustic soda catalyst with methanol as a solvent is simple. Most preferred.
上述のエチレン−ビニルアルコール共重合体のメルトフローレート（温度２１０℃、荷重２．１６ｋｇの条件下にＪＩＳ Ｋ ７２１０に記載の方法により測定）は、チップへの成形加工が良好になることから、０．１〜１００ｇ／１０分の範囲内であることが好ましく、０．５〜５０ｇ／１０分の範囲内であることがより好ましく、１〜２０ｇ／１０分の範囲内であることがさらに好ましい。メルトフローレートが上記範囲を下回る場合には、チップへの成形加工を溶融混練によって行なう際に成形加工機のトルクが上がりすぎることがある。また、メルトフローレートが上記範囲を上回る場合には、チップの連続生産性が難しく、かつ、チップにした場合の強度が不足して培地としての性能が低下する虞がある。 Since the melt flow rate of the above-mentioned ethylene-vinyl alcohol copolymer (measured by the method described in JIS K 7210 under the conditions of a temperature of 210 ° C. and a load of 2.16 kg) is excellent in molding into a chip, It is preferably within the range of 0.1 to 100 g / 10 minutes, more preferably within the range of 0.5 to 50 g / 10 minutes, and even more preferably within the range of 1 to 20 g / 10 minutes. . When the melt flow rate is lower than the above range, the torque of the molding machine may be excessively increased when the chip is molded by melt kneading. If the melt flow rate exceeds the above range, continuous productivity of the chips is difficult, and the strength of the chips may be insufficient and the performance as a medium may be deteriorated.
本発明に用いられるエチレン−ビニルアルコール共重合体を含むチップは、その形状が、柱状、扁平状またはフレーク状であることを特徴の１つとする。ここで、図１は、本発明におけるチップの各形状を模式的に示す図であり、図１（ａ）が円柱状、図１（ｂ）が扁平状、図１（ｃ）がフレーク状をそれぞれ示している。本発明の植物栽培用培地は、柱状、扁平状またはフレーク状のチップにおいて、特定の面が、一定以上の算術平均粗さを有していることを特徴とする。以下、各図を参照しながら、各形状のそれぞれについて説明する。 One feature of the chip containing the ethylene-vinyl alcohol copolymer used in the present invention is that it has a columnar shape, a flat shape, or a flake shape. Here, FIG. 1 is a diagram schematically showing each shape of the chip according to the present invention. FIG. 1 (a) is a columnar shape, FIG. 1 (b) is a flat shape, and FIG. 1 (c) is a flake shape. Each is shown. The culture medium for plant cultivation of the present invention is characterized in that a specific surface has an arithmetic average roughness of a certain level or more in a columnar, flat or flaky chip. Hereinafter, each shape will be described with reference to the drawings.
図１（ａ）には、柱状の一例として円柱状である場合のチップ１を示す。ここで、「円柱状」とは、軸線方向Ｘに垂直な方向における断面が円状（真円状、楕円状のいずれでもよい）である柱状の形状を指す。通常、軸線方向Ｘに沿った直線距離Ａの方が円状である断面の径Ｂよりも大きいが、断面の径Ｂと軸線方向Ｘに沿った直線距離Ａとが同程度か、または、断面の径Ｂの方が大きくても勿論よい。本発明の植物栽培用培地においては、円柱状のチップ１の場合、側面（周方向の面）２におけるＪＩＳ Ｂ０６０１に準拠して測定される算術平均粗さ（Ｒａ）が０．０５μｍ以上である必要がある。算術平均粗さの下限値としては、０．１０μｍであることが好ましく、０．２０μｍであることがより好ましく、０．３０μｍであることがさらに好ましい。算術平均粗さの上限値としては、１０．００μｍであることが好ましく、７．００μｍであることがより好ましく、５．００μｍであることがさらに好ましい。この算術平均粗さは、その値が大きければ大きいほどその表面が粗い（平滑さが低い）ことを意味する。なお、本発明における「柱状」はこの円柱状に限定されるものでは勿論なく、三角柱状、四角柱状、六角形状、八角形状など適宜の角柱状であってもよい。 FIG. 1A shows a chip 1 in a columnar shape as an example of a columnar shape. Here, the “cylindrical shape” refers to a columnar shape whose cross section in a direction perpendicular to the axial direction X is circular (which may be a perfect circle or an ellipse). Usually, the straight line distance A along the axial direction X is larger than the diameter B of the cross section that is circular, but the cross section diameter B and the straight line distance A along the axial direction X are approximately the same, or the cross section Of course, the diameter B may be larger. In the plant cultivation medium of the present invention, in the case of the cylindrical chip 1, the arithmetic average roughness (Ra) measured in accordance with JIS B0601 on the side surface (circumferential surface) 2 is 0.05 μm or more. There is a need. The lower limit value of the arithmetic average roughness is preferably 0.10 μm, more preferably 0.20 μm, and further preferably 0.30 μm. The upper limit of the arithmetic average roughness is preferably 10.00 μm, more preferably 7.00 μm, and even more preferably 5.00 μm. The arithmetic average roughness means that the larger the value, the rougher the surface (lower smoothness). The “columnar shape” in the present invention is not limited to this cylindrical shape, and may be an appropriate prismatic shape such as a triangular prism shape, a quadrangular prism shape, a hexagonal shape, or an octagonal shape.
さらに、円柱状のチップ１の場合、側面（周方向の面）２は、ＪＩＳ Ｂ０６０１に準拠して測定される輪郭曲線要素の平均長さ（ＲＳｍ）が２０μｍ以下であることが好ましく、１．００〜２０．００μｍの範囲内であることがより好ましく、１．５０〜１５．００μｍの範囲内であることがさらに好ましい。この輪郭曲線要素の平均長さは、その値が小さければ小さいほどその表面が粗い（平滑さが低い）ことを意味する。 Further, in the case of the cylindrical chip 1, the side surface (circumferential surface) 2 preferably has an average length (RSm) of contour curve elements measured in accordance with JIS B0601 of 20 μm or less. It is more preferably in the range of 00 to 20.00 μm, and further preferably in the range of 1.50 to 15.00 μm. The average length of the contour curve element means that the smaller the value, the rougher the surface (the lower the smoothness).
円柱状のチップ１は、通常、エチレン−ビニルアルコール共重合体を含むストランドを適宜の長さ（上記直線距離Ａ）でカットして得られる。このため、カットにより生じた端面（カット面）３ａ，３ｂはもともと粗い表面を有するが、本発明においては、端面３ａ，３ｂと比較して平滑な側面（周方向の面）２において、０．０５μｍ以上の算術平均粗さを有することで、特に後述するチップの保水量が向上することを見出した。なお、円柱状のチップ１の側面（周方向の面）２の算術平均粗さを０．０５μｍ以上とするためには、カット後のチップ１の側面（周方向の面）２に、適宜の治具を用いて適度な傷をつける、または上記ストランドを作製する際の金型等の表面粗さがチップの側面を上記範囲に傷つける程度の粗いものを用いるなどなどすればよい。 The cylindrical chip 1 is usually obtained by cutting a strand containing an ethylene-vinyl alcohol copolymer with an appropriate length (the above-mentioned linear distance A). For this reason, the end surfaces (cut surfaces) 3a and 3b generated by the cutting originally have a rough surface, but in the present invention, in the smooth side surface (circumferential surface) 2 compared to the end surfaces 3a and 3b, 0. It has been found that by having an arithmetic average roughness of not less than 05 μm, the water retention amount of the chip described later is improved. In order to make the arithmetic average roughness of the side surface (circumferential surface) 2 of the cylindrical chip 1 0.05 μm or more, the side surface (circumferential surface) 2 of the chip 1 after cutting is appropriately What is necessary is just to use a jig | tool etc. to make a moderate damage | wound, or to use the rough thing of the surface roughness, such as a metal mold | die at the time of producing the said strand, to the extent which damages the side surface of a chip | tip in the said range.
図１（ｂ）には、扁平状である場合のチップ１１を示す。ここで、「扁平状」とは、断面が楕円状の形状を指す。本発明の植物栽培用培地においては、扁平状のチップ１１の場合、当該扁平状のチップ１１を水平面上に静置した際に、水平方向に沿って一番長い直線距離を有する部分に沿った方向を長手方向（図１（ｂ）中、方向Ｄ：水平方向と平行）とし、その長手方向Ｄに対し垂直かつ水平面に垂直な方向で、最も直線距離の長い部分に沿った方向を短手方向Ｃとする。本発明における扁平状のチップ１１は、短手方向Ｃに垂直かつ長手方向Ｄに沿った周方向の曲面（すなわち、図１（ｂ）中、破線で囲った領域。図１（ｂ）の紙面に関し裏側に該当する領域も同様。）１２におけるＪＩＳ Ｂ０６０１に準拠して測定される算術平均粗さ（Ｒａ）が０．０５μｍ以上である必要がある。算術平均粗さの下限値としては、０．１０μｍであることが好ましく、０．２０μｍであることがより好ましく、０．３０μｍであることがさらに好ましい。算術平均粗さの上限値としては、１０．００μｍであることが好ましく、７．００μｍであることがより好ましく、５．００μｍであることがさらに好ましい。
FIG. 1B shows the
さらに、扁平状のチップ１１の場合、周方向の曲面１２は、ＪＩＳ Ｂ０６０１に準拠して測定される輪郭曲線要素の平均長さ（ＲＳｍ）が２０μｍ以下であることが好ましく、１．００〜２０．００μｍの範囲内であることがより好ましく、１．５０〜１５．００μｍの範囲内であることがさらに好ましい。
Furthermore, in the case of the
扁平状のチップ１１は、通常、エチレン−ビニルアルコール共重合体を含む溶融物をホットカットするなどして得られる。このため、ホットカットにより生じた端面（カット面）１３ａ，１３ｂはもともと粗い表面を有するが、本発明においては、端面１３ａ，１３ｂと比較して平滑な周方向の曲面１２において、０．０５μｍ以上の算術平均粗さを有するようにすることで、特に後述するチップの保水量を向上できることを見出したものである。なお、扁平状のチップ１１の周方向の曲面１２の算術平均粗さを０．０５μｍ以上とするためには、切断後のチップ１１の周方向の曲面１２に、適宜の治具を用いて適度な傷をつける、または上記チップを作製する際の金型等の表面粗さがチップの側面を上記範囲に傷つける程度の粗いものを用いるなどすればよい。
The
図１（ｃ）には、フレーク状である場合のチップ２１を示す。ここで、「フレーク状」とは、裏表２つの主面を有する薄片状の形状を指す。本発明の植物栽培用培地においては、フレーク状のチップ２１の場合、その主面２２ａ，２２ｂ（表面および裏面）におけるＪＩＳ Ｂ０６０１に準拠して測定される算術平均粗さ（Ｒａ）が０．０５μｍ以上である必要がある。算術平均粗さの下限値としては、０．１０μｍであることが好ましく、０．２０μｍであることがより好ましく、０．３０μｍであることがさらに好ましい。算術平均粗さの上限値としては、１０．００μｍであることが好ましく、７．００μｍであることがより好ましく、５．００μｍであることがさらに好ましい。
FIG. 1C shows the
さらに、フレーク状のチップ２１の場合、主面２２ａ，２２ｂは、ＪＩＳ Ｂ０６０１に準拠して測定される輪郭曲線要素の平均長さ（ＲＳｍ）が２０μｍ以下であることが好ましく、１．００〜２０．００μｍの範囲内であることがより好ましく、１．５０〜１５．００μｍの範囲内であることがさらに好ましい。
Further, in the case of the
フレーク状のチップ２１は、通常、エチレン−ビニルアルコール共重合体を薄膜状の成形体とした後、これを破砕することで得られる。薄膜状の成形体は積層体であってもよい。積層体を製造する方法としては、特に制限されないが、たとえばエチレン−ビニルアルコール共重合体を薄膜状に成形後、複数枚を重ねてニップロール等で圧着する方法、熱可塑性樹脂から得られる成形体（フィルム、シート等）にエチレン−ビニルアルコール共重合体を溶融押出する方法、エチレン−ビニルアルコール共重合体と他の熱可塑性樹脂とを共押出する方法、エチレン−ビニルアルコール共重合体と他の熱可塑性樹脂とを共射出する方法、エチレン−ビニルアルコール共重合体から得られる上記成形体と他の基材のフィルム、シート等とを有機チタン化合物、イソシアネート化合物、ポリエステル系化合物等の公知の接着剤を用いてラミネートする方法、等が挙げられる。本発明においては、得られる主面２２ａ，２２ｂが、上述のように０．０５μｍ以上の算術平均粗さを有するようにすることで、特に後述するチップの保水量を向上できることを見出した。なお、フレーク状のチップ２１の主面２２ａ，２２ｂの算術平均粗さを０．０５μｍ以上とするためには、破砕後のチップ２１の主面２２ａ，２２ｂに、適宜の治具を用いて適度な傷をつける、または薄膜状を成形する際のダイス等の表面粗さが薄膜状の主面を上記範囲に傷つける程度の粗いものを用いるなどすればよい。
The
なお、チップの形状が上述のように柱状、扁平状、フレーク状のいずれであっても、算術平均粗さ（Ｒａ）および輪郭曲線要素の平均長さ（ＲＳｍ）は、たとえば形状測定レーザマイクロスコープ「ＶＫ−Ｘ２００」（株式会社キーエンス社製）を用い、ＪＩＳ規格 Ｂ０６０１：２００１に準拠することで測定できる。後述する実施例では、１００個のチップで測定を行い、その平均値を算術平均粗さ（Ｒａ）として算出している。 Note that the arithmetic average roughness (Ra) and the average length (RSm) of the contour curve element are, for example, the shape measuring laser microscope, regardless of whether the shape of the chip is columnar, flat, or flaky as described above. It can be measured by using “VK-X200” (manufactured by Keyence Corporation) and complying with JIS standard B0601: 2001. In an example described later, measurement is performed with 100 chips, and the average value is calculated as the arithmetic average roughness (Ra).
本発明の植物栽培用培地は、上述のようにチップの特定の面が一定以上の算術平均粗さを有することで、当該算術平均粗さを有さない場合と比較して、チップの保水量が向上する。 As described above, the plant cultivation medium of the present invention has a certain surface of the chip having an arithmetic average roughness of a certain level or more, so that the water retention amount of the chip compared to the case where the arithmetic average roughness is not present. Will improve.
ここで、本発明の植物栽培用培地は、エチレン−ビニルアルコール共重合体を含むチップの体積１００ｍＬに対する保水量が５ｇ以上であることが好ましく、５〜１００ｇの範囲内であることがより好ましく、１０〜７０ｇの範囲内であることがより好ましく、１３ｇ〜５０ｇの範囲内であることがさらに好ましく、２０ｇ〜５０ｇの範囲内であることが最も好ましい。ここで、保水量は、植物栽培用培地とした際のチップ間に保持する水分の量を指す。このようにチップの体積１００ｍＬに対する保水量が５ｇ以上であることで、従来よりも植物の生長の効率が改善される。この保水量の具体的な測定方法は、後述する実施例において詳しく説明する。 Here, the plant cultivation medium of the present invention preferably has a water retention amount of 5 g or more with respect to a volume of 100 mL of a chip containing an ethylene-vinyl alcohol copolymer, more preferably within a range of 5 to 100 g. More preferably, it is in the range of 10 to 70 g, more preferably in the range of 13 g to 50 g, and most preferably in the range of 20 g to 50 g. Here, the amount of water retained refers to the amount of moisture retained between the chips when used as a plant cultivation medium. Thus, the efficiency of the growth of a plant is improved more than before because the amount of water retained for a volume of 100 mL of the chip is 5 g or more. A specific method for measuring the water retention amount will be described in detail in Examples described later.
また本発明の植物栽培用培地は、エチレン−ビニルアルコール共重合体を含むチップの含水率の下限値が３質量％であることが好ましく、１０質量％であることがより好ましく、２０質量％であることがさらに好ましい。また、含水率の上限値が３００質量％であることが好ましく、２５０質量％であることがより好ましく、２００質量％であることがさらに好ましい。ここで、チップの含水率とは、チップ内部に形成されている空孔内に入り込んだ水の含有率を指す。このように、チップの含水率が３質量％以上であることでも、従来よりも植物の生長の効率が改善される。 In the plant cultivation medium of the present invention, the lower limit of the moisture content of the chip containing the ethylene-vinyl alcohol copolymer is preferably 3% by mass, more preferably 10% by mass, and 20% by mass. More preferably it is. Moreover, it is preferable that the upper limit of a moisture content is 300 mass%, It is more preferable that it is 250 mass%, It is further more preferable that it is 200 mass%. Here, the moisture content of the chip refers to the content of water that has entered the pores formed inside the chip. Thus, even if the moisture content of the chip is 3% by mass or more, the efficiency of plant growth is improved as compared with the prior art.
本発明の植物栽培用培地が含むエチレン−ビニルアルコール共重合体を含むチップは、上述したエチレン−ビニルアルコール共重合体のみ、またはエチレン−ビニルアルコール共重合体と水のみから構成されていてもよいが、必要に応じて、アルカリ金属塩、ホウ素化合物、カルボン酸またはその塩、リン系化合物、アルカリ土類金属塩、炭酸ガス、可塑剤、安定剤、界面活性剤、色剤、紫外線吸収剤、スリップ剤、帯電防止剤、乾燥剤、架橋剤、充填剤などの、エチレン−ビニルアルコール共重合体および水以外の他の成分をさらに含んでいてもよい。 The chip containing the ethylene-vinyl alcohol copolymer contained in the plant cultivation medium of the present invention may be composed of only the above-described ethylene-vinyl alcohol copolymer or only the ethylene-vinyl alcohol copolymer and water. As required, alkali metal salts, boron compounds, carboxylic acids or salts thereof, phosphorus compounds, alkaline earth metal salts, carbon dioxide, plasticizers, stabilizers, surfactants, colorants, UV absorbers, Other components other than the ethylene-vinyl alcohol copolymer and water, such as a slip agent, an antistatic agent, a drying agent, a crosslinking agent, and a filler, may be further included.
なお、本発明におけるチップは、いずれの形状であっても、そのサイズは特に制限されるものではないが、その最大長さが１〜５０ｍｍの範囲内であることが好ましく、１〜２０ｍｍの範囲内であることがより好ましい。なお、当該最大長さはノギスを用いて測定することができる。 In addition, the chip in the present invention is not particularly limited in size, but the maximum length is preferably in the range of 1 to 50 mm, and in the range of 1 to 20 mm. More preferably, it is within. The maximum length can be measured using a caliper.
なお、本発明の植物栽培用培地においては、上述した柱状、扁平状、フレーク状のチップは、いずれか１種類のみを用いてもよいし、いずれか２種以上を混在させて用いても勿論よい。 In the plant cultivation medium of the present invention, only one of the above-mentioned columnar, flat, and flake chips may be used, or two or more of them may be used in combination. Good.
本発明の植物栽培用培地は、上述したエチレン−ビニルアルコール共重合体を含むチップのみから構成されていてもよいが、当該チップと共に、ロックウール、砂、土、セラミックボール、ヤシガラ、バーク、ピートモス、水苔などの成分をさらに含んでいてもよい。本発明の植物栽培用培地におけるエチレン−ビニルアルコール共重合体を含むチップの含有率は、５０質量％以上であることが好ましく、８０質量％以上であることがより好ましく、９５質量％以上であることがさらに好ましい。 The plant cultivation medium of the present invention may be composed only of chips containing the above-described ethylene-vinyl alcohol copolymer, but together with the chips, rock wool, sand, earth, ceramic balls, coconut shells, bark, peat moss. In addition, it may further contain components such as moss. The content of the chip containing the ethylene-vinyl alcohol copolymer in the culture medium for plant cultivation of the present invention is preferably 50% by mass or more, more preferably 80% by mass or more, and 95% by mass or more. More preferably.
本発明の植物栽培用培地の使用形態に特に制限はないが、培養液を用いた養液培養用の培地として用いることが好ましい。 Although there is no restriction | limiting in particular in the usage form of the culture medium for plant cultivation of this invention, It is preferable to use as a culture medium for nutrient solution culture using a culture solution.
本発明の植物栽培用培地を用いて栽培する植物の種類には特に制限はなく、たとえば花卉、根菜類を含む野菜、果物類、穀類などが挙げられ、特に大根、さつまいも、ごぼう、にんじん、キュウリ、トマト、ナス、ピーマンなどの野菜栽培に使用することが好ましい。特に、ロックウールでは栽培が困難であった根菜類にも好適に用いることができるという利点もある。 There are no particular restrictions on the types of plants cultivated using the plant cultivation medium of the present invention, and examples include flowers, vegetables including root vegetables, fruits, cereals, etc., especially radish, sweet potato, burdock, carrot, cucumber, etc. It is preferable to use for the cultivation of vegetables such as tomatoes, eggplants and peppers. In particular, there is also an advantage that it can be suitably used for root vegetables that have been difficult to grow with rock wool.
本発明はまた、上述した本発明の植物栽培用培地を用いた植物栽培装置についても提供する。本発明の植物栽培装置は、上述の本発明の植物栽培用培地を用いたものであるならば特に制限されるものではなく、植物栽培用培地以外の構成は、従来公知の適宜の植物栽培装置の構成を備えていてもよい。 The present invention also provides a plant cultivation apparatus using the above-described plant cultivation medium of the present invention. The plant cultivation apparatus of the present invention is not particularly limited as long as it uses the above-described plant cultivation medium of the present invention, and the configuration other than the plant cultivation medium is a conventionally known appropriate plant cultivation apparatus. You may have the structure of.
ここで、図２は、本発明の好ましい一例の植物栽培装置５１を模式的に示す図である。図２に示す例の植物栽培装置５１は、上方に開口５３を有する箱状物であり、側壁５４の適当な高さに排水口５５を有するプランター５２を備え、プランター５２内に、排水口５５から零れ出さない程度の高さ（深さ）にまで、養分を含んだ水（養液）５６が収容される。プランター５２の底壁５７には、水５６の面よりも上にその載置面５８ａが配置されるように棚５８が設けられ、棚５８の上に、吸水シート５９が、上方から見てプランター５２の底壁５７を殆ど覆うように設けられる。この吸水シート５９は、たとえばセルロース繊維、ナイロン繊維、ビニロン繊維、ポリエステル繊維、ポリオレフィン繊維、レーヨン繊維、アラミド繊維、ガラス繊維などの材料で形成されたシート状物であり、その中央部５９ａは棚５８の載置面５８ａ上にあり、かつ、その端部５９ｂがプランター５２内の水５６に浸かるように設けられ、端部５９ｂから吸収した水５６を、中央部５９ａに送るように構成されている。
Here, FIG. 2 is a diagram schematically showing a
図２に示す例では、吸水シート５９上に、その端部６０ａがプランター５２の側壁５４の上端５４ａに引っかかるようにして防根透水シート６０が配置される。防根透水シート６０は、当該植物栽培装置５１で根菜類を生育させる際に設けられることが好ましく、生育させる植物６１が根菜類ではない場合には必ずしも設けなくともよい。このような防根シート６０が設けられる場合、プランター５２内の水５６は、吸水シート５９を介して防根透水シート６０へと送られる。
In the example shown in FIG. 2, the root water-
防根透水シート６０は、繊維状物で構成される織布、不織布、マット状物、あるいは、たとえば各種ポリオレフィン（ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、エチレン−ビニルアルコール共重合体、エチレン−ビニルエステル共重合体、エチレン−アクリル酸エステル共重合体、又はこれらを不飽和カルボン酸で変性、若しくはその誘導体でグラフト変性、若しくは無水マレイン酸で変性した変性ポリオレフィンなど）、各種ナイロン（ナイロン−６、ナイロン−６６、ナイロン−６／６６共重合体など）、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリエステル、ポリスチレン、ポリアクリロニトリル、ポリウレタン、ポリアセタールおよび変性ポリビニルアルコールなどの樹脂からなるシート等であり、親水性、透水性、柔軟性を有し、根を通さないシートである。上記樹脂からなるシートを防根透水シート６０として用いる場合、微細孔を無数にかつ均一な分布で有していることが好ましく、この場合、微細孔の最大径は２０μｍ以下であることが好ましい。微細孔の最大径が２０μｍを超えると、植物の根が防根透水シート６０を貫通し、吸水シート５９に侵入してからみつき、根が過剰に吸水することにより植物の成長に問題が生じる虞がある。また微細孔の最大径が非常に小さい場合、たとえば５μｍ以下の場合には、吸水シートからの水の浸出が阻害され植物の生育に問題が生じる虞がある。
The root-proof
図２に示す例では、防根透水シート６０上に、上述した本発明の植物栽培用培地６２が載せられ、その中で植物６１が生育される。図２には、本発明の植物栽培用培地６２として、複数個の円柱状のチップ６３が用いられた例が示されている。
In the example illustrated in FIG. 2, the above-described
本発明は、上述した本発明の植物栽培用培地を用いた植物栽培方法についても提供する。本発明の植物栽培方法において、上述した本発明の植物栽培用培地を養液栽培用の培地として使用する場合、たとえば本発明の植物栽培用培地をポットなどの容器に入れ、これに培養液を加えた後に、播種したり苗を移植したりする方法などを例示することができる。また本発明の植物栽培用培地が敷き詰められた栽培用ベッドを用意し、これに生育した苗を移植して各種作物を栽培する方法なども例示できる。 The present invention also provides a plant cultivation method using the above-described plant cultivation medium of the present invention. In the plant cultivation method of the present invention, when the above-described plant cultivation medium of the present invention is used as a nutrient culture medium, for example, the plant cultivation medium of the present invention is placed in a container such as a pot, and the culture solution is added thereto. After the addition, a method of sowing or transplanting seedlings can be exemplified. Moreover, the method of cultivating various crops by preparing the bed for cultivation in which the culture medium for plant cultivation of this invention was spread, transplanting the seedling which grew to this can be illustrated.
以下、実施例および比較例を挙げて本発明をより詳細に説明するが、本発明はこれらに限定されるものではない。 EXAMPLES Hereinafter, although an Example and a comparative example are given and this invention is demonstrated in detail, this invention is not limited to these.
［算術平均粗さ（Ｒａ）の測定方法］
柱状のチップにおいては側面、フレーク状のチップにおいては主面を、形状測定レーザマイクロスコープ「ＶＫ−Ｘ２００」（キーエンス社製）を用い、ＪＩＳ規格 Ｂ０６０１：２００１に準拠して算術平均粗さ（Ｒａ）の測定を、１００個のチップに対して行った。その平均値を算術平均粗さ（Ｒａ）とした。
[Measurement method of arithmetic average roughness (Ra)]
Arithmetic average roughness (Ra) according to JIS standard B0601: 2001 using a shape measuring laser microscope “VK-X200” (manufactured by Keyence Corporation) on the side surface in the columnar chip and on the main surface in the flake-shaped chip. ) Measurement was performed on 100 chips. The average value was defined as the arithmetic average roughness (Ra).
［保水量の測定方法］
イオン交換水５００ｍＬを入れた１Ｌビーカーに、後述する実施例または比較例のエチレン−ビニルアルコール共重合体チップをメスシリンダーで２００ｍＬ容量だけ量りとって加え、２５℃で４時間放置した。その後、回転式水切り器「スピードスター」（株式会社カクセー社製）にて３０回回転脱水した。広口瓶２５０ｍＬ（ポリエチレン製、口内径３０．５ｍｍ胴径６１．５ｍｍ全高１２５ｍｍ）の底部に穴と穴の間隔が１ｃｍ以上となるように電動ドリルを用いて２ｍｍ径の穴を４０個あけ、メスシリンダーで１００ｍＬ容量の上記イオン交換水に浸しておいたチップを量りとり、穴を開けた広口瓶に入れ、チップの入った広口瓶の重量を測定しＷ１とした。その後、３Ｌビーカーにイオン交換水２Ｌを入れ、チップが入った広口瓶の口部の３ｃｍ下まで静かに沈め、上記チップが広口瓶内でイオン交換水に浸っていることを確認した。１分後に広口瓶をビーカーから取り出し、静置することで、電動ドリルで開けた２ｍｍ径の穴から広口瓶内のイオン交換水を除去した。５時間後に上記チップの入った広口瓶の重量を測定してＷ２とし、下記数式（１）に従って算出した値を保水量とした。
保水量（ｇ／１００ｍＬ）＝ Ｗ２ − Ｗ１ （１）
[Measurement method of water retention amount]
To a 1 L beaker containing 500 mL of ion-exchanged water, an ethylene-vinyl alcohol copolymer chip of Example or Comparative Example described later was added in a volume of 200 mL with a graduated cylinder, and allowed to stand at 25 ° C. for 4 hours. Then, spin-drying was performed 30 times with a rotary drainer “Speed Star” (manufactured by Kakusei Co., Ltd.). Drill 40 holes of 2mm diameter with an electric drill so that the distance between the holes is 1cm or more at the bottom of 250mL wide-mouth bottle (made of polyethylene, 30.5mm inside diameter, 61.5mm body diameter, 125mm total height). cylinder in which it weighed a chip that has been soaked in the ion exchange water of 100mL capacity, put in a jar with holes, was W 1 to measure the weight of the jar containing the chip. Thereafter, 2 L of ion-exchanged water was put into a 3 L beaker, and the tip was gently submerged to 3 cm below the mouth of the wide-mouthed bottle, and it was confirmed that the chip was immersed in the ion-exchanged water in the wide-mouthed bottle. After 1 minute, the wide-mouth bottle was taken out from the beaker and allowed to stand to remove ion-exchanged water in the wide-mouth bottle from a 2 mm diameter hole opened with an electric drill. After 5 hours to measure the weight of the contained was jar of the chip and W 2 with the calculated value was defined as water retention capacity according to the following equation (1).
Water retention amount (g / 100 mL) = W 2 −W 1 (1)
［苗の生長度合いの評価方法］
２０１３年１月１１日に３０℃に設定したインキュベーター内でキュウリ（品種「新竜」）の種子を催芽し、２０１３年１月１３日に催芽種子を、育苗用バーク堆肥を充填した育苗バッドに播種した。本葉が展開開始した２０１３年１月２８日に、各実施例または比較例で作製したチップを用いた植物栽培装置に移植して、各々の培地に対し苗を９個準備し養液栽培した。灌水は点滴チューブを用いて培養液を天候に応じて１日あたり１〜４回、大塚アグリテクノ株式会社製の養液栽培用肥料「大塚ハウス１号」、「大塚ハウス２号」および「大塚ハウス５号」を混合溶解した養液（Ｎ：９８．７ｐｐｍ、Ｐ：１９．４ｐｐｍ、Ｋ：１２５．７ｐｐｍ、Ｃａ：６３．０ｐｐｍ、Ｍｇ：１３．４ｐｐｍ、Ｍｎ：０．７０９ｐｐｍ、Ｂ：０．４８７ｐｐｍ、Ｆｅ：２．０２５ｐｐｍ、Ｃｕ：０．０１８ｐｐｍ、Ｚｎ：０．０４８ｐｐｍ、Ｍｏ：０．０１９ｐｐｍ）を与えた。そして、２０１３年３月３日に育成苗の地上部生体重（茎葉部分の重さ）と地上部乾物重とを測定し、地上部乾物率を算出して苗の生長度合いを評価した。なお、キュウリの生育についての判定は、地上部生体重をテューキー検定で優位差があった順に実施例５を基準となるＡとして、Ａ、Ｂ、Ｃ、ＤまたはＥと判定した。
[Evaluation method of seedling growth degree]
On January 11, 2013, seeds of cucumber (variety “Shinryu”) were sprouting in an incubator set at 30 ° C., and on January 13, 2013, the sprouting seeds were put into a seedling bud filled with bark compost for raising seedlings. Sowing. On January 28, 2013, when the true leaves began to be deployed, transplanted to a plant cultivation apparatus using the chips produced in each Example or Comparative Example, and prepared nine seedlings for each medium and cultivated by hydroponics . Irrigation uses an infusion tube, and the culture solution is fertilizer for hydroponics "Otsuka House 1", "
［肥大根数の評価方法］
大根‘たんしん’を用いてハウス内で栽培試験を行った。底部より１ｃｍに排水口を設けたプランター（上部幅２８．５ｃｍ×上部縦４６．５ｃｍ×深さ２６ｃｍ、容量２８Ｌ）を用い、棚の載置面よりも大きく切った吸水シート「ジャームガード」（東洋紡スペシャルティズトレーディング株式会社製）を棚に被せ、余りを底部に折り返してプランターに設置した。さらにその上に防根透水シート（東洋紡スペシャルティズトレーディング株式会社製）をプランター内側に敷いた後、熱可塑性樹脂を深さ２０ｃｍまで充填した。播種は２０１４年４月１７日、幅７ｃｍ×縦８ｃｍ間隔で１５穴、１穴あたり３粒直播した。間引きは２０１４年４月２７日に行い、灌水は１日３〜６回程度、天候および生育状況に応じて「トンボジョーロ４号」（新輝合成株式会社製）で大塚アグリテクノ株式会社製の養液栽培用肥料「大塚ハウス１号」、「大塚ハウス２号」および「大塚ハウス５号」を混合溶解した養液（Ｎ：９８．７ｐｐｍ、Ｐ：１９．４ｐｐｍ、Ｋ：１２５．７ｐｐｍ、Ｃａ：６３．０ｐｐｍ、Ｍｇ：１３．４ｐｐｍ、Ｍｎ：０．７０９ｐｐｍ、Ｂ：０．４８７ｐｐｍ、Ｆｅ：２．０２５ｐｐｍ、Ｃｕ：０．０１８ｐｐｍ、Ｚｎ：０．０４８ｐｐｍ、Ｍｏ：０．０１９ｐｐｍ）を与え、収穫調査は２０１４年６月２５日に行った。収穫調査では、生育した１５穴に対する肥大根が１ｇ以上の大根の数を数え、その結果を肥大根数の評価とした。
[Evaluation method for the number of radish]
A cultivation test was conducted in the house using radish 'tanshin'. Using a planter (top width 28.5 cm x top length 46.5 cm x depth 26 cm, capacity 28 L) provided with a drain outlet 1 cm from the bottom, a water absorbing sheet "Jermguard" cut larger than the shelf mounting surface ( (Toyobo Specialty Trading Co., Ltd.) was placed on the shelf, and the remainder was folded back to the bottom and installed in the planter. Further, a water-proof permeable sheet (manufactured by Toyobo Specialty Trading Co., Ltd.) was laid on the inside of the planter, and then a thermoplastic resin was filled to a depth of 20 cm. On April 17, 2014, seeding was carried out by directly seeding 3 grains per hole at 15 holes at intervals of 7 cm width x 8 cm length. Thinning is performed on April 27, 2014, and irrigation is performed 3 to 6 times a day. Depending on the weather and growth conditions, "Tombo Jolo 4" (manufactured by Shinki Gosei Co., Ltd.) is used by Otsuka Agritechno Co., Ltd. Fertilizer for hydroponics "Otsuka House No. 1,""Otsuka House No. 2," and "Otsuka House No. 5" mixed and dissolved (N: 98.7ppm, P: 19.4ppm, K: 125.7ppm, Ca: 63.0 ppm, Mg: 13.4 ppm, Mn: 0.709 ppm, B: 0.487 ppm, Fe: 2.025 ppm, Cu: 0.018 ppm, Zn: 0.048 ppm, Mo: 0.019 ppm) The harvest survey was conducted on June 25, 2014. In the harvest survey, the number of radishes with 1 g or more of radish with respect to 15 holes grown was counted, and the result was used as the evaluation of the number of radishes.
＜比較例１＞
[含水エチレン−ビニルアルコール共重合体チップの作製]
エチレン含有量３２ｍｏｌ％、ケン化度９９ｍｏｌ％以上のエチレン−ビニルアルコール共重合体２０ｋｇを、水／メタノール＝３２／６８（重量比）の混合液に８０℃で１２時間撹拌しながら溶解させて、３７重量％のエチレン−ビニルアルコール共重合体溶液を得た。次に、撹拌を止めて溶解槽の温度を６５℃に下げて５時間放置し、前記のエチレン−ビニルアルコール共重合体溶液の脱泡を行った。そして、直径２．５ｍｍの円形の開口部を有する金板から、５℃の水／メタノール＝９／１（重量比）の混合溶液中にエチレン−ビニルアルコール共重合体溶液を１時間あたり１５ｋｇで押出してストランド状に析出させ、切断することで、チップの軸線方向Ｘに沿った直線距離Ａが約４．５ｍｍ、径Ｂが約１．７ｍｍの円柱状の含水エチレン−ビニルアルコール共重合体チップを得た。
<Comparative Example 1>
[Production of hydrous ethylene-vinyl alcohol copolymer chip]
20 kg of an ethylene-vinyl alcohol copolymer having an ethylene content of 32 mol% and a saponification degree of 99 mol% or more was dissolved in a mixed solution of water / methanol = 32/68 (weight ratio) at 80 ° C. with stirring for 12 hours, A 37% by weight ethylene-vinyl alcohol copolymer solution was obtained. Next, stirring was stopped and the temperature of the dissolution tank was lowered to 65 ° C. and left for 5 hours to degas the ethylene-vinyl alcohol copolymer solution. Then, from a metal plate having a circular opening having a diameter of 2.5 mm, an ethylene-vinyl alcohol copolymer solution was added at 15 kg per hour in a mixed solution of water / methanol = 9/1 (weight ratio) at 5 ° C. Columnar hydrous ethylene-vinyl alcohol copolymer chip having a straight line distance A of about 4.5 mm and a diameter B of about 1.7 mm along the axial direction X of the chip by extruding, stranding and cutting. Got.
［含水エチレン−ビニルアルコール共重合体チップ（洗浄品）の作製］
上記で得られた含水エチレン−ビニルアルコール共重合体チップ３８．０ｋｇに２００Ｌのイオン交換水を加え、２５℃で２時間撹拌しながら洗浄しては遠心分離機で脱液する操作を２回繰り返した。次に、１ｇ／Ｌの酢酸水溶液で、２５℃で２時間撹拌しながら洗浄しては遠心分離機で脱液する操作を２回繰り返した。さらに、２００Ｌのイオン交換水で、２５℃で２時間撹拌しながら洗浄しては遠心分離機で脱液する操作を６回繰り返し、円柱状の含水エチレン−ビニルアルコール共重合体チップ（洗浄品）を得た。
[Production of hydrous ethylene-vinyl alcohol copolymer chip (cleaned product)]
The operation of adding 200 L of ion-exchanged water to 38.0 kg of the water-containing ethylene-vinyl alcohol copolymer chip obtained above, washing it with stirring at 25 ° C. for 2 hours, and then removing the liquid with a centrifuge is repeated twice. It was. Next, an operation of washing with a 1 g / L aqueous acetic acid solution while stirring at 25 ° C. for 2 hours and then removing the liquid with a centrifuge was repeated twice. Furthermore, washing with 200 L of ion-exchanged water while stirring at 25 ° C. for 2 hours and then removing the liquid with a centrifugal separator were repeated 6 times to obtain a cylindrical hydrous ethylene-vinyl alcohol copolymer chip (cleaned product). Got.
［乾燥エチレン−ビニルアルコール共重合体チップの作製］
０．１ｇ／Ｌの酢酸ナトリウムおよび０．５ｇ／Ｌの酢酸を含有する水溶液２００Ｌに上記含水エチレン−ビニルアルコール共重合体チップ（洗浄品）３８．０ｋｇを投入し、２５℃で５時間、浸漬および撹拌を行った。浸漬および撹拌の処理をしたチップを遠心分離機で脱液して取り出し、８０℃で３時間乾燥した後、引き続き１２０℃で２４時間乾燥することで、円柱状の乾燥エチレン−ビニルアルコール共重合体チップを得た。
[Preparation of dry ethylene-vinyl alcohol copolymer chip]
Into 200 L of an aqueous solution containing 0.1 g / L sodium acetate and 0.5 g / L acetic acid, 38.0 kg of the above water-containing ethylene-vinyl alcohol copolymer chip (cleaned product) was charged and immersed at 25 ° C. for 5 hours. And stirring was performed. The soaked and agitated chip is removed by centrifuging with a centrifuge, dried at 80 ° C. for 3 hours, and then dried at 120 ° C. for 24 hours to obtain a cylindrical dry ethylene-vinyl alcohol copolymer. I got a chip.
上記で得られた円柱状の乾燥エチレン−ビニルアルコール共重合体チップの軸線方向Ｘに沿った直線距離Ａは３．７８ｍｍ、径Ｂは１．３１ｍｍ（アスペクト比（Ａ／Ｂ）：２．８８）であった。また、当該チップの側面（周方向の面）について、算術平均粗さ（Ｒａ）は０．０４μｍ、保水量は４ｇ／１００ｍＬであった。このチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は９．４ｇ、地上部乾物重は０．７９ｇ、地上部乾物率は８．４％であり、テューキー検定で優位差判定を行い序列したところＥ判定であった。また、肥大根数が１ｇ以上の大根の数は１１本であった。結果を表１に示す。 The linear distance A along the axial direction X of the cylindrical dry ethylene-vinyl alcohol copolymer chip obtained above is 3.78 mm, and the diameter B is 1.31 mm (aspect ratio (A / B): 2.88). )Met. Further, the arithmetic mean roughness (Ra) of the side surface (circumferential surface) of the chip was 0.04 μm, and the water retention amount was 4 g / 100 mL. When the growth degree of cucumber seedlings was evaluated using this chip, the above-ground weight was 9.4 g, the above-ground dry weight was 0.79 g, and the above-ground dry matter rate was 8.4%, which is superior in the Tukey test. When the difference was judged and ranked, it was judged as E. The number of radishes with 1 g or more of radish was 11 in number. The results are shown in Table 1.
＜実施例１＞
比較例１で用いた円柱状の乾燥エチレン−ビニルアルコール共重合体チップをタンブラー（日水化工株式会社製）で１分間に６０回転の速度で１時間回転攪拌した。当該円柱状のチップの軸線方向Ｘに沿った直線距離Ａは３．７８ｍｍ、径Ｂは１．３１ｍｍ（アスペクト比（Ａ／Ｂ）：２．８８）であった。このチップの側面（周方向の面）における算術平均粗さ（Ｒａ）は０．０９μｍ、保水量は１２ｇ／１００ｍＬであった。またこのチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は１２．１ｇ、地上部乾物重は０．９８ｇ、地上部乾物率は８．０％であり、テューキー検定で優位差判定を行い序列したところＤ判定であった。また、肥大根数が１ｇ以上の大根の数は１４本であった。
<Example 1>
The cylindrical dry ethylene-vinyl alcohol copolymer chip used in Comparative Example 1 was stirred with a tumbler (manufactured by Nissui Chemical Co., Ltd.) for 1 hour at a speed of 60 revolutions per minute. The linear distance A along the axial direction X of the cylindrical chip was 3.78 mm, and the diameter B was 1.31 mm (aspect ratio (A / B): 2.88). The arithmetic average roughness (Ra) on the side surface (circumferential surface) of this chip was 0.09 μm, and the water retention amount was 12 g / 100 mL. Moreover, when the growth degree of the cucumber seedling was evaluated using this chip, the above-ground living weight was 12.1 g, the above-ground dry weight was 0.98 g, and the above-ground dry matter rate was 8.0%. When the superiority difference was judged and ranked, it was D judgment. The number of radishes with 1 g or more radish was 14 in number.
＜実施例２＞
２５０Ｌ反応容器に実施例１で製造した円柱状のエチレン−ビニルアルコール共重合体チップ２０ｋｇとイオン交換水２００Ｌとを添加し、７５℃で４時間加熱攪拌した。遠心分離機で脱液して取り出し、円柱状のエチレン−ビニルアルコール共重合体チップを得た。当該円柱状のチップの軸線方向Ｘに沿った直線距離Ａは３．９２ｍｍ、径Ｂは１．５９ｍｍ（アスペクト比（Ａ／Ｂ）：２．４７）であった。このチップの側面（周方向の面）における算術平均粗さ（Ｒａ）は０．１２μｍ、保水量は１２ｇ／１００ｍＬであった。このチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は１４．８ｇ、地上部乾物重は１．１８ｇ、地上部乾物率は８．０％であり、テューキー検定で優位差判定を行い序列したところＣ判定であった。また、肥大根数が１ｇ以上の大根の数は１４本であった。
<Example 2>
20 kg of the cylindrical ethylene-vinyl alcohol copolymer chip produced in Example 1 and 200 L of ion-exchanged water were added to a 250 L reaction vessel, and the mixture was heated and stirred at 75 ° C. for 4 hours. The liquid was removed by a centrifuge and taken out to obtain a cylindrical ethylene-vinyl alcohol copolymer chip. The linear distance A along the axial direction X of the cylindrical chip was 3.92 mm, and the diameter B was 1.59 mm (aspect ratio (A / B): 2.47). The arithmetic average roughness (Ra) on the side surface (circumferential surface) of this chip was 0.12 μm, and the water retention amount was 12 g / 100 mL. When the growth degree of the cucumber seedling was evaluated using this chip, the above-ground living weight was 14.8 g, the above-ground dry weight was 1.18 g, and the above-ground dry matter rate was 8.0%, which is superior in the Tukey test. When the difference was judged and ranked, it was C judgment. The number of radishes with 1 g or more radish was 14 in number.
＜実施例３＞
押出して析出させる工程で、１時間あたり１６ｋｇで押出して切断する間隔を約２．２倍に変更した以外は、比較例１に従ってチップを製造することで、チップの軸線方向Ｘに沿った直線距離Ａが約１０．０ｍｍ、径Ｂが約２．０ｍｍの円柱状のチップを得た。得られた円柱状のチップに対して、比較例１の含水エチレン−ビニルアルコール共重合体チップ（洗浄品）の作製と同様にしてチップの洗浄を行い、軸線方向Ｘに沿った直線距離Ａが１０．０２ｍｍ、径Ｂが１．９５ｍｍ（アスペクト比（Ａ／Ｂ）：５．１４）のチップを得た。このチップの側面（周方向の面）における算術平均粗さ（Ｒａ）は１．９９μｍ、保水量は１２ｇ／１００ｍＬであった。このチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は１７．６ｇ、地上部乾物重は１．３７ｇ、地上部乾物率は７．８％であった。テューキー検定で優位差判定を行い序列したところＢ判定であった。また、肥大根数が１ｇ以上の大根の数は１４本であった。
<Example 3>
In the step of extruding and precipitating, the linear distance along the axial direction X of the chip is produced by manufacturing the chip according to Comparative Example 1 except that the interval of extrusion and cutting at 16 kg per hour is changed to about 2.2 times. A cylindrical chip having A of about 10.0 mm and diameter B of about 2.0 mm was obtained. The obtained cylindrical chip was washed in the same manner as the production of the hydrous ethylene-vinyl alcohol copolymer chip (cleaned product) in Comparative Example 1, and the linear distance A along the axial direction X was A chip having a diameter of 10.02 mm and a diameter B of 1.95 mm (aspect ratio (A / B): 5.14) was obtained. The arithmetic average roughness (Ra) on the side surface (circumferential surface) of this chip was 1.99 μm, and the water retention amount was 12 g / 100 mL. When the growth degree of cucumber seedlings was evaluated using this chip, the above-ground living weight was 17.6 g, the above-ground dry weight was 1.37 g, and the above-ground dry matter rate was 7.8%. When the superior difference was judged by the Tukey test and ranked in order, it was judged as B. The number of radishes with 1 g or more radish was 14 in number.
＜実施例４＞
比較例１で用いた円柱状の乾燥エチレン−ビニルアルコール共重合体チップを、２０ｍｍ押出機「Ｄ２０２０」（東洋精機製作所社製）（Ｄ（ｍｍ）＝２０、Ｌ／Ｄ＝２０、圧縮比＝２．０、スクリュー：フルフライト））を用いて、以下の条件で単層製膜した。
<Example 4>
The cylindrical dry ethylene-vinyl alcohol copolymer chip used in Comparative Example 1 was converted into a 20 mm extruder “D2020” (manufactured by Toyo Seiki Seisakusho) (D (mm) = 20, L / D = 20, compression ratio = 2.0, screw: full flight)) to form a single layer film under the following conditions.
［製膜条件］
・押出温度：供給部／圧縮部／計量部／ダイ＝１８０℃／２２０℃／２２０℃／２２０℃
・スクリュー回転数：８０ｒｐｍ
・吐出量：２．６ｋｇ／ｈｒ
・引取りロール温度：８０℃
・引取りロール速度：１．２ｍ／ｍｉｎ
[Film forming conditions]
Extrusion temperature: supply unit / compression unit / metering unit / die = 180 ° C./220° C./220° C./220° C.
・ Screw rotation speed: 80rpm
・ Discharge rate: 2.6 kg / hr
・ Take-up roll temperature: 80 ℃
・ Take-up roll speed: 1.2 m / min
ダイスから引取りロール上に押出すと同時にエアーナイフにより空気を３０ｍ／秒で吹き付け、厚み０．１０ｍｍのエチレン−ビニルアルコール共重合体単層フィルムを得た。その後、上記エチレン−ビニルアルコール共重合体単層フィルムを６枚重ね、８０℃に加熱したニップロールを通し、フィルム・シート用粉砕機（株式会社ホーライ製）にてスクリーン開目穴径を１５ｍｍに調整して粉砕し、積層したフレーク状のチップを得た。得られたチップの主面における最大の長さは１０．６ｍｍ、厚みは０．６０ｍｍ（アスペクト比：１７．６７）であった。このチップの主面における算術平均粗さ（Ｒａ）は０．３２μｍ、保水量は１４ｇ／１００ｍＬであった。このチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は１８．３ｇ、地上部乾物重は１．５８ｇ、地上部乾物率は８．５％であり、テューキー検定で優位差判定を行い序列したところＢ判定であった。また、肥大根数が１ｇ以上の大根の数は１４本であった。 While extruding from a die onto a take-up roll, air was blown at 30 m / sec with an air knife to obtain an ethylene-vinyl alcohol copolymer monolayer film having a thickness of 0.10 mm. Then, 6 sheets of the above-mentioned ethylene-vinyl alcohol copolymer single layer films were stacked, passed through a nip roll heated to 80 ° C., and the screen opening hole diameter was adjusted to 15 mm with a film / sheet crusher (manufactured by Horai Co., Ltd.) And pulverized to obtain a laminated flaky chip. The maximum length of the main surface of the obtained chip was 10.6 mm, and the thickness was 0.60 mm (aspect ratio: 17.67). The arithmetic average roughness (Ra) on the main surface of this chip was 0.32 μm, and the water retention amount was 14 g / 100 mL. When the growth degree of cucumber seedlings was evaluated using this chip, the above-ground weight was 18.3 g, the above-ground dry weight was 1.58 g, and the above-ground dry matter rate was 8.5%. When the difference was judged and ranked, it was B judgment. The number of radishes with 1 g or more radish was 14 in number.
＜実施例５＞
製膜条件を以下のように変更し、ダイスから引取りロール上に押出すと同時にエアーナイフにより空気を３０ｍ／秒で吹き付けることを行なわなかったこと以外は実施例４と同様にし、厚み０．１１ｍｍのエチレン−ビニルアルコール共重合体単層フィルムを得た。
<Example 5>
The film forming conditions were changed as follows, the same as in Example 4 except that air was not blown at 30 m / sec with an air knife at the same time as extrusion from a die onto a take-up roll. An 11 mm ethylene-vinyl alcohol copolymer monolayer film was obtained.
［製膜条件］
・押出温度：供給部／圧縮部／計量部／ダイ＝１８０℃／２２０℃／２２０℃／２２０℃
・スクリュー回転数：８０ｒｐｍ
・吐出量：２．６ｋｇ／ｈｒ
・引取りロール温度：８０℃
・引取りロール速度：１．１ｍ／ｍｉｎ
[Film forming conditions]
Extrusion temperature: supply unit / compression unit / metering unit / die = 180 ° C./220° C./220° C./220° C.
・ Screw rotation speed: 80rpm
・ Discharge rate: 2.6 kg / hr
・ Take-up roll temperature: 80 ℃
・ Take-up roll speed: 1.1 m / min
得られた単層シートを実施例４で用いたフィルム・シート用粉砕機の内部にあるスクリーン開目穴径を５ｍｍに調整して粉砕することにより、チップの主面における最大の長さが３．５１ｍｍ、厚みが０．１１ｍｍ（アスペクト比：３１．９１）のフレーク状のチップを得た。このチップの主面における算術平均粗さ（Ｒａ）は３．２１μｍ、保水量は２８ｇ／１００ｍＬであった。このチップを用いてキュウリの苗の生長度合いを評価したところ、地上部生体重は２３．２ｇ、地上部乾物重は１．８１ｇ、地上部乾物率は７．８％であり、テューキー検定で優位差判定を行い序列したところＡ判定であった。また、肥大根数が１ｇ以上の大根の数は１４本であった。 The obtained single-layer sheet is pulverized by adjusting the screen opening hole diameter inside the pulverizer for film and sheet used in Example 4 to 5 mm, so that the maximum length on the main surface of the chip is 3 A flake-shaped chip having a thickness of 0.11 mm and a thickness of 0.11 mm (aspect ratio: 31.91) was obtained. The arithmetic average roughness (Ra) on the main surface of this chip was 3.21 μm, and the water retention amount was 28 g / 100 mL. When the growth degree of the cucumber seedling was evaluated using this chip, the above-ground weight was 23.2 g, the above-ground dry weight was 1.81 g, and the above-ground dry matter rate was 7.8%, which is superior in the Tukey test. When the difference was judged and ranked, it was judged as A. The number of radishes with 1 g or more radish was 14 in number.
１ チップ、２ 側面、３ａ，３ｂ 端面（カット面）、１１ チップ、１２ 短手方向を中心軸とした場合の周方向の曲面、１３ａ，１３ｂ 端面（カット面）、２１ チップ、２２ａ，２２ｂ 主面、５１ 植物栽培装置、５２ プランター、５３ 開口、５４ 側壁、５４ａ 側壁の上端、５５ 排水口、５６ 水、５７ 底壁、５８ 棚、５８ａ 棚の載置面、５９ 吸水シート、５９ａ 吸水シートの中央部、５９ｂ 吸水シートの端部、６０ 防根透水シート、６０ａ 防根透水シートの端部、６１ 植物、６２ 植物栽培用培地、６３ チップ。 1 chip, 2 side surfaces, 3a, 3b end surface (cut surface), 11 chip, 12 curved surface in the circumferential direction with the short side as the central axis, 13a, 13b end surface (cut surface), 21 chips, 22a, 22b Main Surface, 51 Plant cultivation device, 52 Planter, 53 Opening, 54 Side wall, 54a Top end of side wall, 55 Drain port, 56 Water, 57 Bottom wall, 58 Shelf, 58a Shelf mounting surface, 59 Water absorbent sheet, 59a Water absorbent sheet Central part, 59b End part of water-absorbing sheet, 60 Root water-permeable sheet, 60a End part of water-permeable sheet, 61 plants, 62 Plant cultivation medium, 63 chips.
Claims (5)