JP2014210936A - Resin composition, resin cured product, wiring board, and method for manufacturing wiring board - Google Patents
Resin composition, resin cured product, wiring board, and method for manufacturing wiring board Download PDFInfo
- Publication number
- JP2014210936A JP2014210936A JP2014158915A JP2014158915A JP2014210936A JP 2014210936 A JP2014210936 A JP 2014210936A JP 2014158915 A JP2014158915 A JP 2014158915A JP 2014158915 A JP2014158915 A JP 2014158915A JP 2014210936 A JP2014210936 A JP 2014210936A
- Authority
- JP
- Japan
- Prior art keywords
- wiring board
- resin layer
- ultraviolet
- resin composition
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、樹脂組成物、樹脂硬化物、配線板及び配線板の製造方法に関する。さらに詳しくは、本発明は、絶縁樹脂層表面の凹凸形状が小さい状態でも、配線導体に対して高い接着力を発現し得る絶縁樹脂、配線板及び配線板の製造方法に関するものである。 The present invention relates to a resin composition, a cured resin, a wiring board, and a method for manufacturing a wiring board. More specifically, the present invention relates to an insulating resin, a wiring board, and a method for manufacturing a wiring board that can exhibit a high adhesive force to a wiring conductor even when the uneven shape on the surface of the insulating resin layer is small.
電子機器の小型化、軽量化、多機能化が一段と進み、これに伴い、ＬＳＩやチップ部品等の高集積化が進みその形態も多ピン化、小型化へと急速に変化している。このため、電子部品の実装密度を向上するために、微細配線化に対応できる配線板の開発が進められている。このような配線板としては、ガラスクロスを含まない絶縁樹脂をプリプレグの代わりに用い、必要な部分のみビアホールで接続しながら配線層を形成するビルドアップ方式の配線板があり、軽量化や小型化、微細化に適した手法として主流になりつつある。 As electronic devices are further reduced in size, weight, and functionality, LSIs and chip components have been highly integrated, and their forms are rapidly changing to multiple pins and downsizing. For this reason, in order to improve the mounting density of electronic components, development of a wiring board that can cope with miniaturization is underway. As such a wiring board, there is a build-up type wiring board that uses insulating resin that does not contain glass cloth instead of prepreg, and forms a wiring layer while connecting only necessary parts with via holes, making it lighter and smaller It is becoming mainstream as a method suitable for miniaturization.
このビルドアップ方式の配線板は、まず、回路を有した基板上に絶縁樹脂層を形成する。そして、絶縁樹脂層を硬化した後、配線導体との接着力を確保するために、絶縁樹脂層表面を酸化性の処理液に浸して粗化処理を行う。次いで、めっき前処理を行って無電解めっきする。さらに、レジストパターンを無電解めっき層上に形成し、電解めっきで厚付けしたのち、レジストパターンを剥離し、無電解めっき層を除去して配線板とする。
しかしながら、配線の微細化に伴い、絶縁樹脂層表面を粗化して形成した絶縁樹脂層表面の凹凸が配線形成の歩留まり低下の原因となっている。この理由は、無電解金属めっき層が絶縁樹脂層表面の凹凸に食い込み、除去しづらくなって配線ショートの原因となることや、絶縁樹脂層表面の凹凸に起因してレジストパターンの形成精度が低下するためである。
In this build-up type wiring board, first, an insulating resin layer is formed on a substrate having a circuit. And after hardening an insulating resin layer, in order to ensure the adhesive force with a wiring conductor, the insulating resin layer surface is immersed in an oxidizing process liquid, and a roughening process is performed. Next, electroless plating is performed by pre-plating treatment. Furthermore, after forming a resist pattern on the electroless plating layer and thickening by electroplating, the resist pattern is peeled off and the electroless plating layer is removed to obtain a wiring board.
However, with the miniaturization of the wiring, the unevenness on the surface of the insulating resin layer formed by roughening the surface of the insulating resin layer causes a decrease in the yield of wiring formation. This is because the electroless metal plating layer bites into the irregularities on the surface of the insulating resin layer, making it difficult to remove and causing wiring shorts, and the resist pattern formation accuracy decreases due to the irregularities on the surface of the insulating resin layer. It is to do.
したがって、絶縁樹脂層表面の凹凸を小さくすることが微細配線化の実現に重要となるが、凹凸が小さくなると、絶縁樹脂層と無電解金属めっき層との接着力が低下するため、該接着力を向上させる必要がある。また、絶縁樹脂層表面に凹凸を形成するために使用する酸化性の粗化液は、一般に過マンガン酸ナトリウムと水酸化ナトリウムの強アルカリ液が使用される。過マンガン酸ナトリウムは強アルカリ下で樹脂を溶解するが、７価のマンガンが酸化処理で消費されるため、電解再生装置によりマンガンを再生する必要がある。通常の絶縁樹脂は、絶縁信頼性や耐熱性を確保するために、粗化液への耐性を上げて設計するためマンガンの管理は重要である。しかし、溶解した樹脂は処理液内に浮遊するため、マンガンの電解再生が間に合わず、液の建浴を頻繁に行う必要が生じる。これらは、水洗処理や廃液処理といったコストが付加されるため、結果的にコストアップの要因となる。 Therefore, reducing the unevenness on the surface of the insulating resin layer is important for realizing fine wiring. However, if the unevenness is reduced, the adhesive force between the insulating resin layer and the electroless metal plating layer is reduced. It is necessary to improve. Further, as the oxidizing roughening liquid used for forming irregularities on the surface of the insulating resin layer, a strong alkaline liquid of sodium permanganate and sodium hydroxide is generally used. Sodium permanganate dissolves the resin under strong alkali. However, since 7-valent manganese is consumed in the oxidation treatment, it is necessary to regenerate manganese with an electrolytic regeneration device. In order to ensure insulation reliability and heat resistance of ordinary insulating resins, management of manganese is important because it is designed with increased resistance to the roughening solution. However, since the dissolved resin floats in the treatment liquid, the electrolytic regeneration of manganese is not in time, and the liquid needs to be frequently bathed. These add costs such as water washing treatment and waste liquid treatment, resulting in a cost increase.
以上に記載したように、ビルドアップ方式の配線板に使用される絶縁樹脂層には、凹凸が小さくても接着力が確保されることが要求される。
また、長時間高温にさらした際にも、絶縁樹脂層と無電解金属めっき層の接着力はそのまま保たれることが望ましいが、銅の酸化などにより該接着力が低下することがある。これに対して銅の酸化を防ぐなど、接着力の維持をしなければならない。
As described above, the insulating resin layer used in the build-up type wiring board is required to have an adhesive force even if the unevenness is small.
Further, it is desirable that the adhesive strength between the insulating resin layer and the electroless metal plating layer is maintained as it is even when exposed to a high temperature for a long time, but the adhesive strength may be reduced due to copper oxidation or the like. On the other hand, the adhesive strength must be maintained, for example, by preventing oxidation of copper.
これらの要求に対して、種々の提案がなされている。例えば、特許文献１では、ポリフェニレンエーテル樹脂を用いた絶縁樹脂層に酸素存在下、紫外線を照射し、導体層を設けた後、熱処理し、該導体層に回路を形成する、又は回路を形成した後に熱処理する方法が提案されている（特許文献１、請求項１参照）。該技術により、絶縁層の表面粗度を小さく抑えることができ、絶縁層と導体層の密着性を良好とすることができる旨開示されている（特許文献１、段落０００６参照）。
また、特許文献２には、オゾン溶液下で絶縁樹脂層を紫外線処理する技術が開示されている。該技術によれば、配線と絶縁層間の密着力を確保しつつ、めっき触媒が絶縁層表面に過剰に付与されることを抑制することができ、配線間の絶縁抵抗の劣化を抑制することができる旨開示されている（特許文献２、請求項１、段落０００６参照）。
Various proposals have been made for these requirements. For example, in Patent Document 1, an insulating resin layer using a polyphenylene ether resin is irradiated with ultraviolet rays in the presence of oxygen to provide a conductor layer, and then heat-treated to form a circuit in the conductor layer or to form a circuit. A method of performing heat treatment later has been proposed (see Patent Document 1 and Claim 1). The technique discloses that the surface roughness of the insulating layer can be kept small, and the adhesion between the insulating layer and the conductor layer can be improved (see Patent Document 1, paragraph 0006).
Patent Document 2 discloses a technique for treating an insulating resin layer with an ultraviolet ray under an ozone solution. According to this technique, it is possible to suppress the plating catalyst from being excessively applied to the surface of the insulating layer while ensuring the adhesion between the wiring and the insulating layer, and to suppress the deterioration of the insulation resistance between the wirings. It is disclosed that it can be done (see Patent Document 2, Claim 1, Paragraph 0006).
上述の特許文献１に開示される技術によれば、絶縁層の表面粗度を抑え、絶縁層と導体層の密着性を良好にすることができるとしているが、粗化処理をした際の接着力の強度については具体的な開示がなく、その効果の程度は不明である。また、特許文献１で絶縁樹脂として用いられるポリフェニレンエーテル樹脂は、通常ソルダレジストの後露光などで汎用的に用いられている紫外線ランプとは異なる３００ｎｍ以下の波長を有するキセノンエキシマランプや、低圧水銀ランプを使用せざるを得ないという製造上の問題点がある。
また、特許文献２に開示される技術では、絶縁樹脂組成物については、なんら言及されていないため、その効果の程度は不明である。また、実質的には、オゾン濃度が１００ｐｐｍ以上のオゾン溶液に浸漬させる工程が必須であり、操作が煩雑であるという問題点がある。
According to the technique disclosed in Patent Document 1 described above, the surface roughness of the insulating layer can be suppressed and the adhesion between the insulating layer and the conductor layer can be improved. There is no specific disclosure about the strength of the force, and the extent of the effect is unknown. In addition, the polyphenylene ether resin used as an insulating resin in Patent Document 1 is a xenon excimer lamp having a wavelength of 300 nm or less, which is different from an ultraviolet lamp generally used for post-exposure of a solder resist, or a low-pressure mercury lamp. There is a problem in manufacturing that must be used.
Further, in the technique disclosed in Patent Document 2, since no mention is made of the insulating resin composition, the degree of the effect is unknown. Moreover, the process of immersing in the ozone solution whose ozone concentration is 100 ppm or more is essential, and there exists a problem that operation is complicated.
本発明は、このような状況下になされたものであり、絶縁樹脂層表面の凹凸形状が小さい状態でも、配線導体に対して高い接着力を有し、高温で長時間放置しても、絶縁樹脂層が配線導体に対して高い接着力を維持する樹脂組成物、該樹脂組成物を硬化してなる樹脂硬化物、及び該樹脂硬化物を用いた配線板、並びに該配線板の製造方法を提供することを目的とする。 The present invention has been made under such circumstances. Even when the surface of the insulating resin layer has a small uneven shape, the present invention has a high adhesion to the wiring conductor and can be insulated even if left at a high temperature for a long time. A resin composition in which a resin layer maintains high adhesion to a wiring conductor, a cured resin obtained by curing the resin composition, a wiring board using the cured resin, and a method for manufacturing the wiring board The purpose is to provide.
本発明者らは、前記目的を達成するために鋭意研究を重ねた結果、エポキシ樹脂と、紫外線活性型エステル基含有化合物と、イソシアネートシランと、エポキシ樹脂硬化促進剤とを含む樹脂組成物を用いることで、前記目的を達成し得ることを見出した。
また、回路を有する基板に、該樹脂組成物を用いて未硬化樹脂層を設け、該未硬化樹脂層を、熱硬化後、これに紫外線を照射する処理を施して得た硬化樹脂層上に、めっき法にて配線を形成することにより、効率よく目的の配線板が得られることを見出した。
本発明は、かかる知見に基づいて完成したものである。
As a result of intensive studies to achieve the above object, the present inventors use a resin composition containing an epoxy resin, a UV-active ester group-containing compound, an isocyanate silane, and an epoxy resin curing accelerator. It has been found that the above object can be achieved.
Further, an uncured resin layer is provided on a substrate having a circuit by using the resin composition, and the uncured resin layer is thermally cured and then subjected to a treatment of irradiating with ultraviolet rays on the cured resin layer. It has been found that a desired wiring board can be efficiently obtained by forming a wiring by a plating method.
The present invention has been completed based on such findings.
すなわち、本発明は、
（１）（Ａ）１分子中に２個以上のエポキシ基を有するエポキシ樹脂、（Ｂ）紫外線活性型エステル基含有化合物、（Ｃ）イソシアネートシラン、及び（Ｄ）エポキシ樹脂硬化促進剤を含む樹脂組成物、
（２）上記（１）に記載の樹脂組成物を熱硬化し、紫外線を照射してなる樹脂硬化物、
（３）配線導体の回路を有する基板上に、上記（２）に記載の樹脂硬化物からなる硬化樹脂層を配し、該硬化樹脂層上に、配線をめっきで形成してなる配線板、及び
（４）（ａ）配線導体の回路を有する基板上に、上記（１）に記載の樹脂組成物を用いて未硬化樹脂層を形成する工程、（ｂ）該未硬化樹脂層を熱硬化処理し、次いで紫外線照射処理して硬化樹脂層を形成する工程、及び（ｃ）該硬化樹脂層に無電解めっき処理を施す工程、を含む配線板の製造方法、を提供するものである。
なお、本発明における硬化樹脂層は絶縁性を有するため、以下「絶縁樹脂層」と称する場合がある。
That is, the present invention
(1) (A) an epoxy resin having two or more epoxy groups in one molecule, (B) a UV-active ester group-containing compound, (C) an isocyanate silane, and (D) an epoxy resin curing accelerator Composition,
(2) A cured resin product obtained by thermally curing the resin composition according to (1) above and irradiating with ultraviolet rays;
(3) A wiring board in which a cured resin layer made of the resin cured product described in (2) above is disposed on a substrate having a circuit of a wiring conductor, and wiring is formed on the cured resin layer by plating, And (4) (a) a step of forming an uncured resin layer using the resin composition according to (1) above on a substrate having a circuit of a wiring conductor, and (b) thermosetting the uncured resin layer. The present invention provides a method for manufacturing a wiring board, comprising: a step of forming a cured resin layer by treatment with ultraviolet rays, and a step of (c) subjecting the cured resin layer to electroless plating.
In addition, since the cured resin layer in this invention has insulation, it may be called the "insulating resin layer" below.
本発明によれば、絶縁樹脂層表面の凹凸形状が小さい状態でも、配線導体に対して高い接着力を発現し、ビアホール底のスミアを除去するために過マンガン酸ナトリウム系などの粗化液で処理しても、絶縁樹脂層表面の粗化凹凸形状が小さく、かつ配線導体に対して高い接着力を維持し得る樹脂組成物、配線板及び配線板の製造方法を提供することができる。 According to the present invention, even in a state where the uneven shape on the surface of the insulating resin layer is small, a high adhesive force is exerted on the wiring conductor, and a roughening liquid such as sodium permanganate is used to remove smear on the bottom of the via hole. Even if it processes, the roughening uneven | corrugated shape of the insulating resin layer surface is small, and the manufacturing method of the resin composition which can maintain the high adhesive force with respect to a wiring conductor, a wiring board, and a wiring board can be provided.
本発明の樹脂組成物は、（Ａ）１分子中に２個以上のエポキシ基を有するエポキシ樹脂、（Ｂ）紫外線活性型エステル基含有化合物、（Ｃ）イソシアネートシラン、及び（Ｄ）エポキシ樹脂硬化促進剤を含む。 The resin composition of the present invention comprises (A) an epoxy resin having two or more epoxy groups in one molecule, (B) an ultraviolet active ester group-containing compound, (C) an isocyanate silane, and (D) an epoxy resin cured. Contains an accelerator.
［樹脂組成物］
（（Ａ）エポキシ樹脂）
本発明の樹脂組成物において、（Ａ）成分として用いられるエポキシ樹脂は、１分子中に２個以上のエポキシ基を有するものであればよく、特に制限されず、例えば、クレゾールノボラック型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、ナフトールノボラック型エポキシ樹脂、ビフェニルノボラック型エポキシ樹脂、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、ビスフェノールＳ型エポキシ樹脂、ビスフェノールＴ型エポキシ樹脂、ビスフェノールＺ型エポキシ樹脂、テトラブロモビスフェノールＡ型エポキシ樹脂、ビフェニル型エポキシ樹脂、テトラメチルビフェニル型エポキシ樹脂、トリフェニル型エポキシ樹脂、テトラフェニル型エポキシ樹脂、ナフトールアラルキル型エポキシ樹脂、ナフタレンジオールアラルキル型エポキシ樹脂、ナフトールアラルキル型エポキシ樹脂、フルオレン型エポキシ樹脂、ジシクロペンタジエン骨格を有するエポキシ樹脂、エチレン性不飽和基を骨格に有するエポキシ樹脂、脂環式エポキシ樹脂などが挙げられる。また、絶縁信頼性や耐熱性の観点から、二種以上を組み合わせて用いてもよい。
[Resin composition]
((A) Epoxy resin)
In the resin composition of the present invention, the epoxy resin used as the component (A) is not particularly limited as long as it has two or more epoxy groups in one molecule. For example, a cresol novolac type epoxy resin, Phenol novolac type epoxy resin, naphthol novolak type epoxy resin, biphenyl novolac type epoxy resin, bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, bisphenol T type epoxy resin, bisphenol Z type epoxy resin, tetrabromo Bisphenol A type epoxy resin, biphenyl type epoxy resin, tetramethyl biphenyl type epoxy resin, triphenyl type epoxy resin, tetraphenyl type epoxy resin, naphthol aralkyl type epoxy resin, naphthalene All aralkyl type epoxy resin, naphthol aralkyl type epoxy resin, fluorene epoxy resin, an epoxy resin having a dicyclopentadiene skeleton, epoxy resins having an ethylenically unsaturated group in the backbone, and alicyclic epoxy resins. Moreover, you may use 2 or more types in combination from a viewpoint of insulation reliability or heat resistance.
（（Ｂ）紫外線活性型エステル基含有化合物）
本発明の樹脂組成物において、（Ｂ）成分の紫外線活性型エステル基含有化合物は、紫外線の照射により、活性化されるエステル基を含有する化合物であり、前記（Ａ）成分のエポキシ樹脂の硬化剤としても用いることのできる成分である。より具体的には、１分子中に１個以上のエステル基を含み、水酸基を含まずエポキシ樹脂を硬化させることができるものであり、例えば、脂肪族又は、芳香族カルボン酸と脂肪族又は芳香族ヒドロキシ化合物から得られるエステル化合物などが挙げられる。これらのうち、脂肪族カルボン酸や脂肪族ヒドロキシ化合物などで構成されるエステル化合物は、脂肪族鎖を含むことにより有機溶媒への可溶性やエポキシ樹脂との相溶性を高くすることができる。一方、芳香族カルボン酸や芳香族ヒドロキシ化合物などで構成されるエステル化合物は、芳香族環を有することにより、樹脂組成物の耐熱性を向上させることができる。
((B) UV-active ester group-containing compound)
In the resin composition of the present invention, the UV-active ester group-containing compound as the component (B) is a compound containing an ester group that is activated by irradiation with UV light, and the epoxy resin as the component (A) is cured. It is a component that can also be used as an agent. More specifically, one or more ester groups are contained in one molecule, and the epoxy resin can be cured without containing a hydroxyl group. For example, aliphatic or aromatic carboxylic acid and aliphatic or aromatic And ester compounds obtained from group hydroxy compounds. Among these, an ester compound composed of an aliphatic carboxylic acid, an aliphatic hydroxy compound, or the like can increase the solubility in an organic solvent and the compatibility with an epoxy resin by including an aliphatic chain. On the other hand, an ester compound composed of an aromatic carboxylic acid or an aromatic hydroxy compound can improve the heat resistance of the resin composition by having an aromatic ring.
紫外線活性型エステル基含有化合物の好適なものとしては、ベンゼン、ナフタレン、ビフェニル、ジフェニルプロパン、ジフェニルメタン、ジフェニルエーテル、ジフェニルスルホン、ベンゾフェノン等の芳香環の水素原子の２〜４個をカルボキシ基で置換したものから選ばれる芳香族カルボン酸成分と、前記した芳香環の水素原子の１個を水酸基で置換した１価フェノール系化合物と芳香環の水素原子の２〜４個を水酸基で置換した多価フェノール系化合物との混合物を原材料として、芳香族カルボン酸とフェノール性水酸基との縮合反応にて得られる芳香族エステルが挙げられる。
１価フェノール系化合物としては、例えばフェノール、各種クレゾール、α−ナフトール、β−ナフトールなどが挙げられ、多価フェノール系化合物としては、例えばハイドロキノン、レゾルシン、カテコール、４，４’−ビフェノール、４，４’−ジヒドロキシジフェニルエーテル、ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ、ビスフェノールＺ、臭素化ビスフェノールＡ、臭素化ビスフェノールＦ、臭素化ビスフェノールＳ、メチル化ビスフェノールＳ、各種ジヒドロキシナフタレン、各種ジヒドロキシベンゾフェノン、各種トリヒドロキシベンゾフェノン、各種テトラヒドロキシベンゾフェノン、フロログリシンなどが挙げられる。
一方、芳香族カルボンとしては、例えばフタル酸、イソフタル酸、テレフタル酸、ベンゼントリカルボン酸などが挙げられる。
当該紫外線活性型エステル基含有化合物としては、１分子中にエステル基１個以上を有する樹脂であってもよく、市販品としても入手可能である。例えば、ＤＩＣ株式会社製の「ＥＸＢ−９４６０」、「ＥＸＢ−９４６０Ｓ」、「ＥＸＢ−９４７０」、「ＥＸＢ−９４８０」、「ＥＸＢ−９４２０」、三井化学株式会社製の「ＢＰＮ８０」などが挙げられる。
これらの紫外線活性型エステル基含有化合物は、一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。
Preferred examples of the ultraviolet active ester group-containing compound include benzene, naphthalene, biphenyl, diphenylpropane, diphenylmethane, diphenyl ether, diphenylsulfone, benzophenone, etc., substituted by 2 to 4 hydrogen atoms of an aromatic ring with a carboxy group An aromatic carboxylic acid component selected from: a monohydric phenol compound in which one of the hydrogen atoms of the aromatic ring is substituted with a hydroxyl group, and a polyhydric phenol type in which 2 to 4 hydrogen atoms of the aromatic ring are substituted with a hydroxyl group An aromatic ester obtained by a condensation reaction of an aromatic carboxylic acid and a phenolic hydroxyl group can be mentioned using a mixture with a compound as a raw material.
Examples of monohydric phenol compounds include phenol, various cresols, α-naphthol, β-naphthol, and the like. Examples of polyhydric phenol compounds include hydroquinone, resorcin, catechol, 4,4′-biphenol, 4, 4'-dihydroxydiphenyl ether, bisphenol A, bisphenol F, bisphenol S, bisphenol Z, brominated bisphenol A, brominated bisphenol F, brominated bisphenol S, methylated bisphenol S, various dihydroxynaphthalenes, various dihydroxybenzophenones, various trihydroxybenzophenones And various tetrahydroxybenzophenones and phloroglycines.
On the other hand, examples of the aromatic carboxylic acid include phthalic acid, isophthalic acid, terephthalic acid, and benzenetricarboxylic acid.
The ultraviolet-active ester group-containing compound may be a resin having one or more ester groups in one molecule, and is also commercially available. Examples include “EXB-9460”, “EXB-9460S”, “EXB-9470”, “EXB-9480”, “EXB-9420” manufactured by DIC Corporation, “BPN80” manufactured by Mitsui Chemicals, Inc. .
These ultraviolet active ester group-containing compounds may be used alone or in combination of two or more.
本発明の樹脂組成物における前記（Ｂ）成分の紫外線活性型エステル基含有化合物は、前記（Ａ）エポキシ樹脂のエポキシ１当量に対して０．９５〜１．２５当量になるように含有されることが好ましい。この範囲内であると、十分な硬化性や耐熱性が得られる。 In the resin composition of the present invention, the UV-active ester group-containing compound of the component (B) is contained in an amount of 0.95 to 1.25 equivalents relative to 1 equivalent of the epoxy of the (A) epoxy resin. It is preferable. If it is within this range, sufficient curability and heat resistance can be obtained.
本発明の樹脂組成物における（Ｃ）成分はイソシアネートシランである。イソシアネートシランを、後述する配線板における絶縁樹脂層に用いることで、該樹脂層上に配線導体を形成した際に、銅との高い接着性を確保することができる。その機構については、必ずしも明確ではないが、銅配線が空気中の酸素によって、その表面が酸化される過程において、（Ｃ）イソシアネートシランによって、銅が酸化銅（ＣｕＯ）まで酸化されることを抑制し、亜酸化銅（Ｃｕ２Ｏ）の状態を多く作り出しているためと推察している。
また、後に詳述する紫外線照射処理によって、（Ｂ）成分の紫外線活性型エステル基含有化合物の活性エステル基が分解してＯＨ基が生成すると考えられるが、該ＯＨ基とイソシアネートシランのイソシアネートが結合し、末端にあるシランがめっき触媒であるＰｄと結合することで、さらに絶縁樹脂層と銅との高い接着性が得られていると思われる。
The component (C) in the resin composition of the present invention is isocyanate silane. By using isocyanate silane in an insulating resin layer in a wiring board to be described later, high adhesiveness with copper can be secured when a wiring conductor is formed on the resin layer. Although the mechanism is not necessarily clear, in the process where the surface of copper wiring is oxidized by oxygen in the air, it is suppressed that copper is oxidized to copper oxide (CuO) by (C) isocyanate silane. It is presumed that many states of cuprous oxide (Cu 2 O) are produced.
In addition, it is considered that the active ester group of the ultraviolet ray active ester group-containing compound (B) is decomposed to generate an OH group by the ultraviolet irradiation treatment described in detail later, but the OH group and isocyanate of isocyanate silane are combined. And it seems that the high adhesiveness of an insulating resin layer and copper is acquired because the terminal silane couple | bonds with Pd which is a plating catalyst.
本発明で用いるイソシアネートシランとしては、種々のものを用いることができ、例えば、イソシアネートメチルトリメトキシシラン、２−イソシアネートエチルトリメトキシシラン、３−イソシアネートプロピルトリメトキシシラン、４−イソシアネートブチルトリメトキシシラン、５−イソシアネートペンチルトリメトキシシラン、イソシアネートメチルトリエトキシシラン、２−イソシアネートエチルトリエトキシシラン、３−イソシアネートプロピルトリエトキシシラン、４−イソシアネートブチルトリエトキシシラン、５−イソシアネートペンチルトリエトキシシラン、イソシアネートメチルメチルジメトキシシシラン、２−イソシアネートエチルエチルジメトキシシラン、３−イソシアネートプロピルトリメトキシシラン、２−フェニルイミダゾール又は３−イソシアネートプロピルトリエトキシシラン等が挙げられる。これらのうち、銅配線の酸化を抑制する点、接着強度向上の点などから、３−イソシアネートプロピルトリエトキシシラン又は２−フェニルイミダゾールが特に好ましい。 As the isocyanate silane used in the present invention, various types can be used. For example, isocyanate methyltrimethoxysilane, 2-isocyanatoethyltrimethoxysilane, 3-isocyanatepropyltrimethoxysilane, 4-isocyanatobutyltrimethoxysilane, 5-isocyanatepentyltrimethoxysilane, isocyanatemethyltriethoxysilane, 2-isocyanateethyltriethoxysilane, 3-isocyanatepropyltriethoxysilane, 4-isocyanatobutyltriethoxysilane, 5-isocyanatepentyltriethoxysilane, isocyanatemethylmethyldimethoxy Sisilane, 2-isocyanatoethylethyldimethoxysilane, 3-isocyanatopropyltrimethoxysilane, 2- E sulfonyl imidazole or 3- isocyanatepropyltriethoxysilane, and the like. Of these, 3-isocyanatopropyltriethoxysilane or 2-phenylimidazole is particularly preferable from the viewpoint of suppressing oxidation of copper wiring and improving adhesive strength.
上記イソシアネートシランは、一種を単独で、又は二種以上を組み合わせて用いることができ、また、イソシアネートシランは、（Ｂ）成分である紫外線活性型エステル基含有化合物１００質量部に対して、３〜２０質量部の範囲で含有することが好ましい。３質量部以上であると、上述の効果、特に銅配線の酸化を抑制する効果を十分発揮することができる。一方、２０質量部以下であると、樹脂とイソシアネートシランが十分に相溶する点で好ましい。以上の観点から、イソシアネートシランは、３〜１５質量部の範囲がさらに好ましく、３〜１０質量部の範囲が特に好ましい。 The said isocyanate silane can be used individually by 1 type or in combination of 2 or more types, Moreover, isocyanate silane is 3 to 100 mass parts of ultraviolet active ester group containing compounds which are (B) components. It is preferable to contain in 20 mass parts. When the amount is 3 parts by mass or more, the above-described effects, in particular, the effect of suppressing the oxidation of the copper wiring can be sufficiently exhibited. On the other hand, the content of 20 parts by mass or less is preferable in that the resin and the isocyanate silane are sufficiently compatible. From the above viewpoint, the isocyanate silane is more preferably in the range of 3 to 15 parts by mass, and particularly preferably in the range of 3 to 10 parts by mass.
（（Ｄ）エポキシ樹脂硬化促進剤）
本発明の樹脂組成物において、（Ｄ）成分のエポキシ樹脂硬化促進剤としては特に制限はなく、エポキシ樹脂の硬化に用いられる一般的な硬化促進剤を使用することができる。
当該硬化促進剤の具体例としては、２−メチルイミダゾール、２−エチル−４−メチルイミダゾール、１−ベンジル−２−メチルイミダゾール、２−ヘプタデシルイミダゾール、２−ウンデシルイミダゾール、１−シアノエチル−２−フェニルイミダゾリウムトリメリテートなどのイミダゾール系化合物；トリフェニルホスフィン、トリブチルホスフィンなどの有機ホスフィン系化合物；トリメチルホスファイト、トリエチルホスファイトなどの有機ホスファイト系化合物；エチルトリフェニルホスホニウムブロミド、テトラフェニルホスホニウムテトラフェニルボレートなどのホスホニウム塩化合物；トリエチルアミン、トリブチルアミンなどのトリアルキルアミン；４−ジメチルアミノピリジン、ベンジルジメチルアミン、２，４，６−トリス（ジメチルアミノメチル）フェノール、１，８−ジアザビシクロ（５．４．０）−ウンデセン−７（以下ＤＢＵと略称する）などのアミン系化合物及びＤＢＵとテレフタル酸や２，６−ナフタレンジカルボン酸等との塩；テトラエチルアンモニウムクロリド、テトラプロピルアンモニウムクロリド、テトラブチルアンモニウムクロリド、テトラブチルアンモニウムブロミド、テトラヘキシルアンモニウムブロミド、ベンジルトリメチルアンモニウムクロリドなどの第４級アンモニウム塩化合物等を挙げることができる。これらは一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。
また、本発明の樹脂組成物における当該硬化促進剤の含有量は、（Ａ）成分のエポキシ樹脂１００質量部に対して、０．０２〜３．０質量部であることが好ましい。０．０２質量部以上であるとエポキシ樹脂の硬化が充分となって、耐熱性を維持することができ、一方、３．０質量部以下であると樹脂組成物の保存安定性やＢステージの樹脂組成物の取り扱い性が良好となる。以上の観点から、（Ｄ）硬化促進剤の含有量は０．１〜２．０質量部の範囲がより好ましく、０．３〜１．５質量部の範囲が特に好ましい。
((D) Epoxy resin curing accelerator)
In the resin composition of this invention, there is no restriction | limiting in particular as an epoxy resin hardening accelerator of (D) component, The general hardening accelerator used for hardening of an epoxy resin can be used.
Specific examples of the curing accelerator include 2-methylimidazole, 2-ethyl-4-methylimidazole, 1-benzyl-2-methylimidazole, 2-heptadecylimidazole, 2-undecylimidazole, 1-cyanoethyl-2. -Imidazole compounds such as phenylimidazolium trimellitate; Organic phosphite compounds such as triphenylphosphine and tributylphosphine; Organic phosphite compounds such as trimethylphosphite and triethylphosphite; Ethyltriphenylphosphonium bromide and tetraphenylphosphonium Phosphonium salt compounds such as tetraphenylborate; Trialkylamines such as triethylamine and tributylamine; 4-dimethylaminopyridine, benzyldimethylamine, 2,4,6- Amine compounds such as lis (dimethylaminomethyl) phenol, 1,8-diazabicyclo (5.4.0) -undecene-7 (hereinafter abbreviated as DBU), DBU and terephthalic acid, 2,6-naphthalenedicarboxylic acid, etc. And quaternary ammonium salt compounds such as tetraethylammonium chloride, tetrapropylammonium chloride, tetrabutylammonium chloride, tetrabutylammonium bromide, tetrahexylammonium bromide, and benzyltrimethylammonium chloride. These may be used individually by 1 type, and may be used in combination of 2 or more types.
Moreover, it is preferable that content of the said hardening accelerator in the resin composition of this invention is 0.02-3.0 mass parts with respect to 100 mass parts of (A) component epoxy resins. If it is 0.02 parts by mass or more, the epoxy resin is sufficiently cured and heat resistance can be maintained. On the other hand, if it is 3.0 parts by mass or less, the storage stability of the resin composition and the B stage can be maintained. The handleability of the resin composition is improved. From the above viewpoint, the content of the (D) curing accelerator is more preferably in the range of 0.1 to 2.0 parts by mass, and particularly preferably in the range of 0.3 to 1.5 parts by mass.
上述の（Ａ）成分〜（Ｄ）成分を含有する本発明の樹脂組成物は、これを熱硬化し、紫外線を照射して樹脂硬化物とすることができ、種々の用途に展開することができる。具体的には、例えば、後に詳述するように、配線導体の回路を有する基板上に、該樹脂硬化物からなる硬化樹脂層を配して、絶縁樹脂層とし、該樹脂層の上に配線をめっきで形成することで、配線板を得ることができる。
上述のようにして得た絶縁樹脂層は、該絶縁樹脂層表面の凹凸形状が小さいにもかかわらず、上述のように配線導体に対して高い接着力を発現する。
The resin composition of the present invention containing the components (A) to (D) described above can be thermally cured and irradiated with ultraviolet rays to form a cured resin, which can be developed for various uses. it can. Specifically, for example, as will be described in detail later, a cured resin layer made of the cured resin is disposed on a substrate having a circuit of a wiring conductor to form an insulating resin layer, and wiring is formed on the resin layer. A wiring board can be obtained by forming by plating.
The insulating resin layer obtained as described above exhibits a high adhesive force to the wiring conductor as described above, even though the uneven shape on the surface of the insulating resin layer is small.
上記熱硬化の条件については後述する。また、紫外線照射条件としては、最大波長３００〜４５０ｎｍの範囲で放射する紫外線ランプを用い、大気圧雰囲気下に、光量が１０００〜５０００ｍＪ／ｃｍ２程度、好ましくは３０００〜４０００ｍＪ／ｃｍ２になるように、紫外線を照射することが望ましい。
なお、前記光量（ｍＪ／ｃｍ２）は、「照度（ｍＷ／ｃｍ２）×照射時間（秒）」で表される。
The thermosetting conditions will be described later. Further, as the ultraviolet irradiation conditions, using a UV lamp emitting in the range of the maximum wavelength 300 to 450 nm, under atmospheric pressure, the amount of light is 1000~5000mJ / cm 2 or so, so that preferably becomes 3000~4000mJ / cm 2 In addition, it is desirable to irradiate ultraviolet rays.
The light quantity (mJ / cm 2 ) is represented by “illuminance (mW / cm 2 ) × irradiation time (seconds)”.
このように、絶縁樹脂層を熱硬化処理後、紫外線照射処理することにより、該絶縁樹脂層は、従来用いられる過マンガン酸ナトリウム系などの粗化液を用いて凹凸形状を形成しなくても、配線導体に対して高い接着力を発現し得ることから、配線形成の歩留まりの低下を抑えることができると共に、粗化液使用による水洗処理や廃液処理をなくすことができ、コスト的にも有利である。
また、ビアホール底のスミアを除去するために、過マンガン酸ナトリウム系などの粗化液で処理しても、粗化凹凸形状が小さく、かつ配線導体に対して高い接着力を確保することができる。
なお、紫外線照射時の絶縁樹脂層の温度は５０〜８０℃程度が好ましく、６０〜７０℃がより好ましい。
As described above, the insulating resin layer is not subjected to an uneven shape using a conventional roughening liquid such as sodium permanganate by performing ultraviolet irradiation treatment after the thermosetting treatment of the insulating resin layer. In addition, since high adhesive strength can be expressed with respect to the wiring conductor, it is possible to suppress a decrease in the yield of wiring formation, and it is possible to eliminate water washing processing and waste liquid processing by using a roughening liquid, which is advantageous in terms of cost. It is.
In addition, even if it is treated with a roughening solution such as sodium permanganate to remove smear at the bottom of the via hole, the roughened uneven shape is small and high adhesion to the wiring conductor can be secured. .
In addition, the temperature of the insulating resin layer at the time of ultraviolet irradiation is preferably about 50 to 80 ° C, and more preferably 60 to 70 ° C.
本発明の樹脂組成物には、本発明の目的が損なわれない範囲で、必要に応じ、無機フィラーや、各種添加成分、例えばレベリング剤、酸化防止剤、難燃剤、揺変性付与剤、増粘剤、溶媒などを含有させることができる。 In the resin composition of the present invention, an inorganic filler and various additive components, for example, a leveling agent, an antioxidant, a flame retardant, a thixotropic agent, a thickening agent, as necessary, as long as the object of the present invention is not impaired. An agent, a solvent, etc. can be contained.
［無機フィラー］
無機フィラーは、熱膨張率の抑制や塗膜強度を上げる目的で含有させるものであり、例えばシリカ、溶融シリカ、タルク、アルミナ、水酸化アルミニウム、硫酸バリウム、水酸化カルシウム、エーロジル、炭酸カルシウムの中から選ばれるものが使用可能であり、これらは一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。なお、誘電特性や低熱膨張の点からシリカを用いるのが好ましく、その含有量は溶媒を除く樹脂組成物の固形分中で５〜３５ｖｏｌ％であることが好ましく、１０〜３０ｖｏｌ％であることがより好ましい。５ｖｏｌ％以上であると熱膨張係数と誘電損失の増大を抑制することができ、一方３５ｖｏｌ％以下であると絶縁樹脂を内層回路に形成する際の必要フローが充分となり未充填箇所が発生しにくくなる。
これらの無機フィラーは、分散性を高める目的で、カップリング剤で処理してもよく、ニーダー、ボールミル、ビーズミル、３本ロール等既知の混練により樹脂組成物中に均質に分散してもよい。
[Inorganic filler]
Inorganic fillers are included for the purpose of suppressing the coefficient of thermal expansion and increasing the coating strength. For example, silica, fused silica, talc, alumina, aluminum hydroxide, barium sulfate, calcium hydroxide, aerosil, calcium carbonate. What is chosen from these can be used, and these may be used individually by 1 type and may be used in combination of 2 or more type. In addition, it is preferable to use silica from the viewpoint of dielectric properties and low thermal expansion, and the content thereof is preferably 5-35 vol% in the solid content of the resin composition excluding the solvent, and is preferably 10-30 vol%. More preferred. If it is 5 vol% or more, an increase in the thermal expansion coefficient and dielectric loss can be suppressed. On the other hand, if it is 35 vol% or less, the necessary flow for forming the insulating resin in the inner layer circuit is sufficient, and unfilled portions are hardly generated. Become.
These inorganic fillers may be treated with a coupling agent for the purpose of enhancing dispersibility, or may be uniformly dispersed in the resin composition by known kneading such as a kneader, a ball mill, a bead mill, or a three roll.
（カップリング剤）
無機フィラーの分散性を高める目的で、該無機フィラーの表面処理に用いられるカップリング剤としては、シラン系カップリング剤が好ましい。例えば、Ｎ−フェニル−γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−（２−アミノエチル）アミノプロピルトリメトキシシラン、γ−（２−アミノエチル）アミノプロピルトリエトキシシラン、γ−アニリノプロピルトリメトキシシラン、γ−アニリノプロピルトリエトキシシラン、Ｎ−β−（Ｎ−ビニルベンジルアミノエチル）−γ−アミノプロピルトリメトキシシランおよびＮ−β− （Ｎ−ビニルベンジルアミノエチル）−γ−アミノプロピルトリエトキシシランなどのアミノシラン化合物、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシランおよびβ−（３，４−エポキシシクロヘキシル）エチルトリメトキシシランなどのエポキシシラン化合物、その他として、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルビニルエトキシシラン、γ−メルカトプロピルトリメトキシシラン、γ−メルカトプロピルトリエトキシシラン、γ−ウレイドプロピルトリメトキシシラン、γ−ウレイドプロピルトリエトキシシラン、γ−メタクロキシプロピルトリメトキシシランなどが挙げられる。
(Coupling agent)
For the purpose of enhancing the dispersibility of the inorganic filler, a silane coupling agent is preferred as the coupling agent used for the surface treatment of the inorganic filler. For example, N-phenyl-γ-aminopropyltrimethoxysilane, γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, γ- (2-aminoethyl) aminopropyltrimethoxysilane, γ- (2-amino Ethyl) aminopropyltriethoxysilane, γ-anilinopropyltrimethoxysilane, γ-anilinopropyltriethoxysilane, N-β- (N-vinylbenzylaminoethyl) -γ-aminopropyltrimethoxysilane and N-β -Aminosilane compounds such as (N-vinylbenzylaminoethyl) -γ-aminopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane and β- (3,4-epoxy) (Cyclohexyl) ethyltrimethoxy As other epoxy silane compounds such as γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylvinylethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropyltriethoxysilane, γ- Examples include ureidopropyltrimethoxysilane, γ-ureidopropyltriethoxysilane, and γ-methacryloxypropyltrimethoxysilane.
［溶媒］
本発明の樹脂組成物は、溶媒に希釈して用いることができる。溶媒としては、例えばメチルエチルケトン、キシレン、トルエン、アセトン、エチレングリコールモノエチルエーテル、シクロヘキサノン、エチルエトキシプロピオネート、Ｎ，Ｎ−ジメチルホルムアミド、Ｎ，Ｎ−ジメチルアセトアミド、プロピレングリコールモノメチルエーテル等を挙げることができる。これらは一種を単独で用いてもよく、二種以上を混合して用いてもよい。この溶媒の前記樹脂組成物に対する使用割合は、従来使用されている割合でよく、目的とする絶縁樹脂の塗膜形成の設備に合わせて使用量を調整することができる。
[solvent]
The resin composition of the present invention can be used after diluted in a solvent. Examples of the solvent include methyl ethyl ketone, xylene, toluene, acetone, ethylene glycol monoethyl ether, cyclohexanone, ethyl ethoxypropionate, N, N-dimethylformamide, N, N-dimethylacetamide, propylene glycol monomethyl ether and the like. it can. These may be used individually by 1 type, and 2 or more types may be mixed and used for them. The ratio of the solvent used with respect to the resin composition may be a conventionally used ratio, and the amount used can be adjusted in accordance with the facility for forming the coating film of the target insulating resin.
［樹脂組成物の調製］
本発明の樹脂組成物の調製方法には、特に制限はなく、従来公知の調製方法を用いることができる。
例えば、前記溶媒中に、前述した（Ａ）成分のエポキシ樹脂、（Ｂ）成分の紫外線活性型エステル基含有化合物、（Ｃ）成分のイソシアネートシラン及び（Ｄ）成分のエポキシ樹脂硬化促進剤を加えると共に、必要に応じて用いられる無機フィラーや各種添加成分を加えたのち、超音波分散方式、高圧衝突式分散方式、高速回転分散方式、ビーズミル方式、高速せん断分散方式、及び自転公転式分散方式などの各種混合機を用いて混合・攪拌することにより、ワニスとして調製することができる。
このワニス中の溶媒を除く固形分濃度は４０〜７０質量％であることが、塗工性などの観点から好ましい。
[Preparation of resin composition]
There is no restriction | limiting in particular in the preparation method of the resin composition of this invention, A conventionally well-known preparation method can be used.
For example, the above-mentioned epoxy resin of component (A), UV-active ester group-containing compound of component (B), isocyanate silane of component (C) and epoxy resin curing accelerator of component (D) are added to the solvent. In addition, after adding inorganic filler and various additive components used as necessary, ultrasonic dispersion method, high-pressure collision dispersion method, high-speed rotation dispersion method, bead mill method, high-speed shear dispersion method, rotation and revolution dispersion method, etc. It can be prepared as a varnish by mixing and stirring using various mixers.
The solid content concentration excluding the solvent in the varnish is preferably 40 to 70% by mass from the viewpoint of coating property and the like.
［配線板］
本発明の配線板は、配線導体の回路を有する基板上に、前述した樹脂組成物によって未硬化樹脂層を形成し、これを熱硬化し、次いで紫外線を照射して得た硬化樹脂層（絶縁樹脂層）上に、配線をめっきで形成してなる。
（絶縁樹脂層付キャリアフィルムの作製）
本発明の配線板において、配線導体の回路を有する基板上に絶縁樹脂層を形成するには、まず、本発明の樹脂組成物（ワニス）をキャリアフィルムに塗工したのち、８０〜１８０℃程度の温度で、５〜１０分間程度乾燥処理して、絶縁樹脂層付キャリアフィルムを作製する。乾燥処理の温度が８０℃以上であり、かつ時間が５分以上である場合、乾燥が充分に進行し、絶縁樹脂層内にボイドが発生するのを抑制することができ好ましい。一方、乾燥処理の温度が１８０℃以下で、かつ時間が１０分以下であると、乾燥が進みすぎて、樹脂フロー量が低下するのを抑制することができ好ましい。なお、ここでは乾燥により、ワニス中の溶媒が揮散した状態であり、硬化処理を行っていない未硬化の状態、いわゆる未硬化の絶縁樹脂層である。
絶縁樹脂層の厚み（乾燥後の厚み）に関しては、絶縁性の観点から、最小絶縁距離が確保できる最小膜厚以上であることが好ましく、この最小絶縁距離は絶縁樹脂の組成により変わるものであるが、一般的には、５μｍ以上であることが好ましい。絶縁樹脂層の膜厚を厚くすることは絶縁性の点では有利になるが、経済性の観点から、通常は４０μｍ以下程度とすることが好ましい。
前記キャリアフィルムの厚さとしては特に制限はないが、１０〜２００μｍ程度が好ましく、２０〜１００μｍがより好ましい。また、キャリアフィルムとしては、ポリエチレンテレフタレート（ＰＥＴ）フィルムがよく用いられ、表面に離型剤処理を施しているＰＥＴフィルムでもよい。
[Wiring board]
The wiring board of the present invention is a cured resin layer (insulating) obtained by forming an uncured resin layer on a substrate having a circuit of a wiring conductor with the above-described resin composition, thermally curing it, and then irradiating with ultraviolet rays. A wiring is formed on the (resin layer) by plating.
(Preparation of carrier film with insulating resin layer)
In the wiring board of the present invention, in order to form an insulating resin layer on a substrate having a circuit of a wiring conductor, first, the resin composition (varnish) of the present invention is applied to a carrier film, and then about 80 to 180 ° C. The carrier film with an insulating resin layer is produced by drying for about 5 to 10 minutes at a temperature of 5 ° C. When the temperature of the drying treatment is 80 ° C. or more and the time is 5 minutes or more, it is preferable because drying proceeds sufficiently and generation of voids in the insulating resin layer can be suppressed. On the other hand, when the temperature of the drying treatment is 180 ° C. or lower and the time is 10 minutes or shorter, it is preferable because drying progresses excessively and the resin flow amount can be suppressed from decreasing. Here, the solvent in the varnish is volatilized by drying, and is a so-called uncured insulating resin layer in an uncured state where no curing treatment is performed.
The thickness of the insulating resin layer (thickness after drying) is preferably at least the minimum film thickness that can ensure the minimum insulation distance from the viewpoint of insulation, and this minimum insulation distance varies depending on the composition of the insulating resin. However, in general, the thickness is preferably 5 μm or more. Although increasing the thickness of the insulating resin layer is advantageous in terms of insulation, it is usually preferably about 40 μm or less from the viewpoint of economy.
Although there is no restriction | limiting in particular as thickness of the said carrier film, About 10-200 micrometers is preferable and 20-100 micrometers is more preferable. Further, as the carrier film, a polyethylene terephthalate (PET) film is often used, and a PET film whose surface is treated with a release agent may be used.
（配線回路を有する基板）
本発明の配線板に用いられる配線導体の回路を有する基板（以下、回路付絶縁基板と称することがある。）としては、少なくとも一方の面に回路を備えた絶縁基板であれば特に限定するものではなく、片面にのみ回路を形成したものや両面銅張積層板を用いて得られるような、絶縁基板の両面に回路が形成されたものであってもよい。この回路付絶縁基板は、通常の配線板において用いられている公知の積層板、たとえば、ガラス布−エポキシ樹脂、紙−フェノール樹脂、紙−エポキシ樹脂、ガラス布・ガラス紙−エポキシ樹脂等を使用することができる。回路は公知のいずれの方法により形成されていてもよく、銅箔と上記絶縁基板を張り合わせた銅張り積層板を用い、銅箔の不要な部分をエッチング除去するサブトラクティブ法や、上記絶縁基板の必要な箇所に無電解めっきによって回路を形成するアディティブ法等、公知の配線板の製造法を用いることができる。
また、この回路表面には、接着性を向上させるための回路表面処理を行ってもよい。この処理方法も、特に制限されることはなく、例えば、次亜塩素酸ナトリウムのアルカリ水溶液により回路表面に酸化銅の針状結晶を形成し、形成した酸化銅の針状結晶をジメチルアミンボラン水溶液に浸漬して還元するなどの公知の方法を採用することができる。
(Board with wiring circuit)
The substrate having the circuit of the wiring conductor used for the wiring board of the present invention (hereinafter sometimes referred to as an insulating substrate with circuit) is not particularly limited as long as it is an insulating substrate having a circuit on at least one surface. Instead, the circuit may be formed on both sides of the insulating substrate, such as a circuit formed only on one side or a double-sided copper-clad laminate. As this insulating substrate with circuit, a known laminated board used in a normal wiring board, for example, glass cloth-epoxy resin, paper-phenol resin, paper-epoxy resin, glass cloth / glass paper-epoxy resin, etc. is used. can do. The circuit may be formed by any known method, using a copper-clad laminate in which a copper foil and the insulating substrate are bonded together, using a subtractive method for etching away unnecessary portions of the copper foil, A known method for manufacturing a wiring board such as an additive method for forming a circuit by electroless plating at a necessary location can be used.
Moreover, you may perform the circuit surface treatment for improving adhesiveness to this circuit surface. This treatment method is also not particularly limited. For example, a copper oxide needle crystal is formed on the circuit surface with an alkaline aqueous solution of sodium hypochlorite, and the formed copper oxide needle crystal is converted into a dimethylamine borane aqueous solution. It is possible to employ a known method such as dipping in a reducing solution.
（回路付絶縁基板の回路上への絶縁樹脂層の形成）
次に、前述した回路付絶縁基板の回路上に絶縁樹脂層を形成する方法としては、前述の絶縁樹脂層付キャリアフィルムを用い、ラミネート方式やプレス方式で絶縁樹脂層を形成することができる。
ラミネート方式は、回路付絶縁基板の回路に、絶縁樹脂層付キャストフィルムを、その絶縁樹脂層が対面するように接触させ、例えば真空加圧ラミネータ積層装置を用いて、該絶縁樹脂層を積層したのち、キャリアフィルムを剥離する方法である。
真空加圧ラミネータ積層装置を用いる場合、温度は５０〜１７０℃程度、圧力０．２ＭＰａ以上であることが好ましい。好ましい圧力値も、加熱温度と同様に、基板の厚みや残存銅率などにより変化するが、圧力が高すぎると基板が変形する恐れがあるため、１．０ＭＰａ以下であることが好ましい。また、真空度は、１５ｈＰａ以下であると内層回路板への埋め込み性が良好となる。真空度は低ければ低い方が好ましいが、装置の能力や所定値への到達までの待ち時間等が生産性に及ぼす影響などを考慮すると、５〜１０ｈＰａの範囲で行うことが好ましい。熱圧着時間は１０〜９０秒程度が好ましい。１０秒以上であると内層回路への樹脂の流動に要する時間が充分となり、９０秒以下であれば生産性が良好となる。より好ましい熱圧着時間は２０〜６０秒である。
(Formation of an insulating resin layer on the circuit of an insulating substrate with circuit)
Next, as a method of forming the insulating resin layer on the circuit of the above-described insulating substrate with circuit, the insulating resin layer can be formed by a laminate method or a press method using the carrier film with an insulating resin layer described above.
In the laminating method, a cast film with an insulating resin layer is brought into contact with a circuit of an insulating substrate with a circuit so that the insulating resin layer faces, and the insulating resin layer is laminated using, for example, a vacuum pressure laminator laminator. Thereafter, the carrier film is peeled off.
When using a vacuum pressurizing laminator laminator, the temperature is preferably about 50 to 170 ° C. and the pressure is 0.2 MPa or more. The preferred pressure value also varies depending on the thickness of the substrate, the remaining copper ratio, etc., as with the heating temperature. However, if the pressure is too high, the substrate may be deformed, so it is preferably 1.0 MPa or less. Further, when the degree of vacuum is 15 hPa or less, the embedding property to the inner layer circuit board is good. If the degree of vacuum is low, it is preferable to be low. However, in consideration of the influence of the capability of the apparatus, the waiting time until reaching a predetermined value, and the like on the productivity, it is preferable to carry out in the range of 5 to 10 hPa. The thermocompression bonding time is preferably about 10 to 90 seconds. If it is 10 seconds or more, the time required for the resin to flow to the inner layer circuit is sufficient, and if it is 90 seconds or less, the productivity is good. A more preferable thermocompression bonding time is 20 to 60 seconds.
一方、プレス方式の場合、前記と同様に、回路付絶縁基板の回路に絶縁樹脂層付キャストフィルムを、その絶縁樹脂層が対面するように接触させ、使用する絶縁樹脂層に合わせた適正な条件で行うことが望ましく、例えば昇温速度３℃／分程度で、３５℃から１９０℃程度まで約５０分間を要して昇温させ、その温度にて２．０〜３．０ＭＰａ程度の圧力で、６０〜９０分間程度保持したのち、室温まで３０分間程度を要して冷却する方法を用いることで、回路付絶縁基板の回路上に、絶縁樹脂層を形成することができる。 On the other hand, in the case of the press method, as described above, the cast film with the insulating resin layer is brought into contact with the circuit of the insulating substrate with circuit so that the insulating resin layer faces, and appropriate conditions are matched to the insulating resin layer to be used. For example, at a rate of temperature increase of about 3 ° C./min, the temperature is increased from 35 ° C. to about 190 ° C. for about 50 minutes, and the pressure is about 2.0 to 3.0 MPa at that temperature. The insulating resin layer can be formed on the circuit of the insulating substrate with circuit by using a method of cooling for about 30 minutes to room temperature after holding for about 60 to 90 minutes.
（絶縁樹脂層の熱硬化処理）
本発明の配線板においては、前記のようにして回路付絶縁基板の回路上に形成された絶縁樹脂層を、まず熱硬化処理する。
この熱硬化処理は、後のめっき処理や配線導体のアニール処理などを考慮した温度や時間で行うことが望ましい。あまり硬化を進めると、後のめっき処理時に配線導体との接着性が低下する恐れがあり、反対に硬化が足りないと、めっき処理時のアルカリ処理液に浸食され、めっき液に溶解する恐れがあるからである。これらのことを考慮すると、例えば１５０〜１９０℃で３０〜９０分間程度の熱処理を施して硬化させることが好ましい。
(Thermosetting treatment of insulating resin layer)
In the wiring board of the present invention, the insulating resin layer formed on the circuit of the insulating substrate with circuit as described above is first heat-cured.
This thermosetting treatment is desirably performed at a temperature and time taking into account subsequent plating treatment or annealing treatment of the wiring conductor. If the curing is advanced too much, the adhesion to the wiring conductor may be reduced during the subsequent plating process. On the contrary, if the curing is insufficient, it may be eroded by the alkaline treatment liquid during the plating process and dissolved in the plating solution. Because there is. In consideration of these matters, it is preferable to cure by applying a heat treatment at 150 to 190 ° C. for about 30 to 90 minutes, for example.
（紫外線照射処理）
本発明の配線板においては、前記のようにして熱硬化処理された絶縁樹脂層を、紫外線照射処理する。この紫外線照射処理の目的は、前述した本発明の樹脂組成物において説明したとおりである。
紫外線照射処理の条件については、紫外線は、最大波長が３００〜４５０ｎｍの範囲を有する紫外線ランプを用い、大気圧雰囲気下に、紫外線を光量が１０００〜５０００ｍＪ／ｃｍ２の範囲になるように照射することが好ましい。絶縁樹脂層に大気圧雰囲気下で紫外線を照射する方法は、紫外線装置により異なるため特に限定はしないが、生産性を考慮すればコンベア式の紫外線照射方式が好ましい。紫外線ランプとして、最大波長が３００〜４５０ｎｍの範囲を有するものは、水銀ショートアークランプ、高圧水銀ランプ、毛細管型超高圧ランプ、高圧ランプ、メタルハライドランプなどを用いることができる。これらのランプにおいて、紫外線の波長が全域で広いメタルハライドランプが好ましい。
(UV irradiation treatment)
In the wiring board of the present invention, the insulating resin layer that has been heat-cured as described above is subjected to ultraviolet irradiation treatment. The purpose of the ultraviolet irradiation treatment is as described in the above-described resin composition of the present invention.
With respect to the conditions of the ultraviolet irradiation treatment, ultraviolet rays are irradiated so that the amount of light is in the range of 1000 to 5000 mJ / cm 2 under an atmospheric pressure atmosphere using an ultraviolet lamp having a maximum wavelength in the range of 300 to 450 nm. It is preferable. A method of irradiating the insulating resin layer with ultraviolet rays under an atmospheric pressure atmosphere is not particularly limited because it differs depending on the ultraviolet device, but a conveyor type ultraviolet irradiation method is preferable in consideration of productivity. As the ultraviolet lamp, a lamp having a maximum wavelength in the range of 300 to 450 nm may be a mercury short arc lamp, a high pressure mercury lamp, a capillary type ultra high pressure lamp, a high pressure lamp, a metal halide lamp, or the like. Among these lamps, metal halide lamps having a wide ultraviolet wavelength over the entire region are preferable.
紫外線の最大波長が３００〜４５０ｎｍの範囲を有する紫外線ランプを使用する目的は、汎用性と紫外線の波長域が関係する。すなわち、最大波長が３００〜４５０ｎｍを示す紫外線ランプは、コンベア式型の紫外線照射装置、例えばソルダレジストの後露光装置として一般的に用いられているからである。さらに、メタルハライド型のコンベア照射装置は、紫外線波長領域が広く、特別な装置を必要としないでこれらの装置を代替することで本発明の効果を発揮できる。紫外線の光量が、１０００ｍＪ／ｃｍ２以上であると酸化性粗化液で絶縁樹脂層を処理しなくてもめっき導体との接着力が十分となり、一方、５０００ｍＪ／ｃｍ２以下であると該接着力は、良好に発現され、経済的にも有利である。より好ましい光量は、３０００〜４０００ｍＪ／ｃｍ２の範囲である。
このように、熱硬化処理後の絶縁樹脂層を紫外線照射処理することにより、該絶縁樹脂層表面の凹凸形状が小さい状態でも、配線導体に対して、高い接着力を発現することができる。
The purpose of using an ultraviolet lamp having a maximum ultraviolet wavelength in the range of 300 to 450 nm relates to versatility and the wavelength range of ultraviolet rays. That is, an ultraviolet lamp having a maximum wavelength of 300 to 450 nm is generally used as a conveyor type ultraviolet irradiation device, for example, a solder resist post-exposure device. Furthermore, the metal halide conveyor irradiation device has a wide ultraviolet wavelength region, and the effects of the present invention can be exhibited by substituting these devices without requiring a special device. Quantity of ultraviolet light is, adhesive force between the even plating conductor without processing the insulating resin layer between at 1000 mJ / cm 2 or more oxidizing roughening solution becomes sufficient, whereas, the adhesive When it is 5000 mJ / cm 2 or less The force is well expressed and economically advantageous. A more preferable light amount is in the range of 3000 to 4000 mJ / cm 2 .
In this way, by performing the ultraviolet irradiation treatment on the insulating resin layer after the thermosetting treatment, a high adhesive force can be exerted on the wiring conductor even when the uneven shape on the surface of the insulating resin layer is small.
（酸化性粗化液による処理）
ビアホール底のスミアの除去が必要な場合、酸化性粗化液を用いて除去処理することができる。この酸化性粗化液としては、クロム／硫酸粗化液、アルカリ過マンガン酸粗化液、フッ化ナトリウム／クロム／硫酸粗化液、ホウフッ酸粗化液などを用いることができる。また、この酸化性粗化液で処理する際、溶媒またはアルカリ液、あるいはこれらの混合物液（一般には、膨潤液またはプリディップ液）に浸したのち、酸化性粗化液で処理してもよい。上記溶媒としては、アルコール系の溶媒例えばジエチレングリコールモノメチルエーテル、ジエチレングリコールモノブチルエーテル、イソプロピルアルコール等が使用できる。また、アルカリ液は、水に溶解した際にアルカリ性を示す液であれば特に制限はなく、水酸化ナトリウム溶液、水酸化カリウム溶液等が使用できる。さらに、溶媒またはアルカリ液を混合してもよく、例えば水酸化ナトリウム３ｇ／Ｌとジエチレングリコールモノブチルエーテル３００ｍＬ／Ｌの組成のものが使用できる。
(Treatment with oxidizing roughening solution)
When it is necessary to remove the smear on the bottom of the via hole, it can be removed using an oxidizing roughening solution. As this oxidizing roughening liquid, a chromium / sulfuric acid roughening liquid, an alkaline permanganic acid roughening liquid, a sodium fluoride / chromium / sulfuric acid roughening liquid, a borofluoric acid roughening liquid, or the like can be used. Moreover, when processing with this oxidizing roughening liquid, after immersing in a solvent or alkali liquid, or a mixture liquid (generally swelling liquid or pre-dip liquid), you may process with an oxidizing roughening liquid. . As the solvent, alcohol solvents such as diethylene glycol monomethyl ether, diethylene glycol monobutyl ether, isopropyl alcohol and the like can be used. Further, the alkaline solution is not particularly limited as long as it is a solution that exhibits alkalinity when dissolved in water, and a sodium hydroxide solution, a potassium hydroxide solution, or the like can be used. Furthermore, you may mix a solvent or an alkali liquid, for example, the thing of the composition of sodium hydroxide 3g / L and diethylene glycol monobutyl ether 300mL / L can be used.
（めっき処理）
本発明の配線板においては、前述のようにして処理された絶縁樹脂層の表面に、例えば以下に示すようにめっき処理が施される。
まず、上記絶縁樹脂層を塩化第１錫の塩酸水溶液に浸漬して、中和処理を行い、さらに、パラジウムを付着させるめっき触媒付与処理を行う。めっき触媒付与処理は、塩化パラジウム系のめっき触媒液に浸漬することにより行われる。次に、無電解めっき液に浸漬することにより、めっき触媒上に厚さが０．３〜１．５μｍ程度の無電解めっき層を析出させる。必要により、更に電気めっきを行うことができる。無電解めっき処理に使用する無電解めっき液は、公知の無電解めっき液を使用することができ、特に制限はない。また、電気めっき処理についても公知の方法によることができ特に制限はない。
これらの手法を繰り返して多層配線板を作製することもできる。
(Plating treatment)
In the wiring board of the present invention, the surface of the insulating resin layer treated as described above is subjected to a plating treatment as shown below, for example.
First, the insulating resin layer is immersed in an aqueous hydrochloric acid solution of stannous chloride, neutralized, and further subjected to a plating catalyst application treatment for depositing palladium. The plating catalyst application treatment is performed by immersing in a palladium chloride plating catalyst solution. Next, an electroless plating layer having a thickness of about 0.3 to 1.5 μm is deposited on the plating catalyst by being immersed in an electroless plating solution. If necessary, further electroplating can be performed. As the electroless plating solution used for the electroless plating treatment, a known electroless plating solution can be used, and there is no particular limitation. Further, the electroplating treatment can be performed by a known method and is not particularly limited.
These methods can be repeated to produce a multilayer wiring board.
［配線板の製造方法］
本発明はまた、配線板の製造方法をも提供する。
本発明の配線板の製造方法は、（ａ）配線導体の回路を有する基板上に、本発明の樹脂組成物を用いて未硬化樹脂層を形成する工程、（ｂ）該未硬化樹脂層を熱硬化処理し、次いで、紫外線照射処理して硬化樹脂層を形成する工程、（ｃ）該硬化樹脂層に無電解めっき処理を施す工程、を含むことを特徴とする。
本発明の配線板の製造方法においては、さらに、（ｄ）無電解めっき上に、電気めっき処理を施す工程を含むことができ、また、前記（ｂ）工程と（ｃ）工程との間に、（ｃ’）硬化樹脂層表面を、酸化性粗化液で粗化処理する工程を含むことができる。
前記の各工程については、前述した本発明の配線板の説明において示したとおりである。
[Method of manufacturing a wiring board]
The present invention also provides a method for manufacturing a wiring board.
The method for producing a wiring board of the present invention comprises (a) a step of forming an uncured resin layer on a substrate having a circuit of a wiring conductor using the resin composition of the present invention, and (b) the uncured resin layer. It includes a step of heat-curing treatment and then forming a cured resin layer by ultraviolet irradiation treatment, and a step (c) performing an electroless plating treatment on the cured resin layer.
In the method for manufacturing a wiring board according to the present invention, the method may further include (d) a step of performing electroplating on the electroless plating, and between the steps (b) and (c). (C ′) A step of roughening the surface of the cured resin layer with an oxidizing roughening solution may be included.
Each of the above steps is as shown in the description of the wiring board of the present invention described above.
次に、本発明を実施例により、さらに詳細に説明するが、本発明は、これらの例によってなんら限定されるものではない。
（評価方法）
各実施例及び比較例の評価は、以下に示す方法により行った。
（１）外層回路との接着強度（９０度剥離、単位；ｋＮ／ｍ）
外層回路層（第３回路層）の一部に幅１０ｍｍ、長さ１００ｍｍの部分を形成し、この一端を剥がしてつかみ具でつかみ、室温中で、垂直方向に約５０ｍｍ引き剥がした際の荷重を測定した。
（２）めっき銅エッチング除去面の絶縁樹脂層粗さ（表面平均粗さ、単位；μｍ）
外層回路をエッチング処理して銅を除去した試験片を作製する。この試験片を２ｍｍ角程度に切断し、（株）キーエンス社製超深度形状測定顕微鏡「ＶＫ−８５００型」を用いて、試験片中の異なる箇所３点について、測定長さ１４９μｍ、倍率２０００倍、分解能０．０５μｍの条件で測定し、測定長さ１４９μｍ中の粗さの最大部から最小部を引いた値を絶縁樹脂層の表面粗さとし、３箇所の平均値を算出した。
（３）はんだ耐熱性
多層配線板を２５ｍｍ角に切断し、その直後に２８８℃±２℃に調整したはんだ浴に浮かべ、ふくれが発生するまでの時間を調べた。
（４）高温保持後の外層回路との接着強度（９０度剥離、単位；ｋＮ／ｍ）
防爆乾燥機内で、１８０℃、１００時間保持した後、外層回路層（第３回路層）の一部に幅１０ｍｍ、長さ１００ｍｍの部分を形成し、この一端を剥がしてつかみ具でつかみ、室温中で、垂直方向に約５０ｍｍ引き剥がした際の荷重を測定した。
EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited at all by these examples.
(Evaluation method)
Each Example and Comparative Example were evaluated by the following methods.
(1) Adhesive strength with outer layer circuit (90 degree peeling, unit: kN / m)
A part of the outer circuit layer (third circuit layer) is formed with a portion of width 10mm and length 100mm, one end is peeled off and gripped with a gripper, and the load when stripped about 50mm vertically at room temperature Was measured.
(2) Roughness of insulating resin layer on the plated copper etching removal surface (surface average roughness, unit: μm)
A test piece from which copper is removed by etching the outer layer circuit is produced. This test piece was cut into about 2 mm square, and using a ultra deep shape measurement microscope “VK-8500 type” manufactured by Keyence Corporation, the measurement length was 149 μm and the magnification was 2000 times at three different points in the test piece. The measurement was performed under the condition of a resolution of 0.05 μm, and a value obtained by subtracting the minimum portion from the maximum portion of the roughness in the measurement length of 149 μm was defined as the surface roughness of the insulating resin layer, and the average value of the three locations was calculated.
(3) Solder heat resistance The multilayer wiring board was cut into 25 mm squares, and immediately after that, it floated in a solder bath adjusted to 288 ° C. ± 2 ° C., and the time until blistering was examined.
(4) Adhesive strength with outer layer circuit after holding at high temperature (90 degree peeling, unit: kN / m)
After holding at 180 ° C. for 100 hours in an explosion-proof dryer, a portion having a width of 10 mm and a length of 100 mm is formed on a part of the outer layer circuit layer (third circuit layer), this one end is peeled off and grasped with a grasping tool. In particular, the load when peeling about 50 mm in the vertical direction was measured.
実施例１
（１）回路板の作製
ガラス布基材エポキシ樹脂両面銅張積層板［銅箔の厚さ１８μｍ、基板の厚さ０．８ｍｍ、粗化箔を両面に有する日立化成工業株式会社製「ＭＣＬ−Ｅ−６７」（商品名）］にエッチングを施して片面に回路層（以下、第１回路層とする）を有する回路板を作製した。
（２）樹脂組成物の調製
（Ａ）成分である、テトラフェニル型エポキシ樹脂、「ＪＥＲ−１０３１」（ＪＥＲ株式会社製、商品名、エポキシ当量：２００、第１表ではＡ１と記載）２４質量部、（Ｂ）成分である、紫外線活性型エステル基含有樹脂、「ＥＸＢ−９４７０」（ＤＩＣ株式会社、商品名、エステル当量：２２３）１３．３８質量部、（Ｃ）成分である、３−イソシアネートプロピルトリエトキシシラン（信越化学工業株式会社製「ＫＢＥ−９００７」）２質量部、及び（Ｄ）成分である、１−シアノエチル−２−フェニルイミダゾリウムトリメリテート（四国化成工業株式会社製、商品名「２ＰＺ−ＣＮＳ」）０．０７２質量部を、溶媒であるメチルエチルケトン（以下「ＭＥＫ」と記載する。）４０質量部に溶解して、本発明の樹脂組成物（ワニス）を得た。
Example 1
(1) Fabrication of circuit board Glass cloth base epoxy resin double-sided copper-clad laminate [copper foil thickness 18 μm, substrate thickness 0.8 mm, Hitachi Chemical Co., Ltd. E-67 "(trade name)] was etched to produce a circuit board having a circuit layer (hereinafter referred to as a first circuit layer) on one side.
(2) Preparation of Resin Composition (A) Component, tetraphenyl type epoxy resin, “JER-1031” (manufactured by JER Corporation, trade name, epoxy equivalent: 200, described as A1 in Table 1) 24 mass Part, (B) component, UV-active ester group-containing resin, “EXB-9470” (DIC Corporation, trade name, ester equivalent: 223) 13.38 parts by mass, (C) component, 3- Isocyanatopropyltriethoxysilane ("KBE-9007" manufactured by Shin-Etsu Chemical Co., Ltd.) 2 parts by mass, and (D) component, 1-cyanoethyl-2-phenylimidazolium trimellitate (manufactured by Shikoku Kasei Kogyo Co., Ltd., 0.072 parts by mass of a trade name “2PZ-CNS”) is dissolved in 40 parts by mass of methyl ethyl ketone (hereinafter referred to as “MEK”) as a solvent, and the present invention. A resin composition (varnish) was obtained.
（３）絶縁樹脂層の形成、及び熱硬化・紫外線照射処理
上記（２）で得られた樹脂組成物（ワニス）を、キャリアフィルムとしてのポリエチレンテレフタレート（ＰＥＴ）フィルム（厚さ３８μｍ）上に塗工し、１００℃で１０分間乾燥処理することにより、膜厚５０±３μｍの絶縁樹脂層付キャリアフィルムロールを作製した。
さらに、上記の絶縁樹脂層付キャリアフィルムを、上記（１）で得られた回路板の片面に絶縁樹脂層が回路層と接する面側にしてバッチ式真空加圧ラミネータ「ＭＶＬＰ−５００」（名機株式会社製、商品名）を用いて積層した。
次に、キャリアフィルムを剥がしたのち、絶縁樹脂層を１７０℃、６０分間の硬化条件にて熱硬化処理し、次いで、コンベア式紫外線照射装置を用いて、メタルハライドランプ（最大波長３５０〜３８０ｎｍ）にて、紫外線を光量が３０００ｍＪ／ｃｍ２になるように照射した。
(3) Formation of insulating resin layer and thermosetting / ultraviolet irradiation treatment The resin composition (varnish) obtained in (2) above is applied onto a polyethylene terephthalate (PET) film (thickness 38 μm) as a carrier film. And a carrier film roll with an insulating resin layer having a film thickness of 50 ± 3 μm was produced by drying at 100 ° C. for 10 minutes.
Furthermore, the above-mentioned carrier film with an insulating resin layer is placed on one side of the circuit board obtained in the above (1) on the side where the insulating resin layer is in contact with the circuit layer, and the batch type vacuum pressure laminator “MVLP-500” (name (Trade name, manufactured by Kikai Co., Ltd.).
Next, after peeling off the carrier film, the insulating resin layer is heat-cured under a curing condition of 170 ° C. for 60 minutes, and then applied to a metal halide lamp (maximum wavelength 350 to 380 nm) using a conveyor type ultraviolet irradiation device. Then, ultraviolet rays were irradiated so that the amount of light was 3000 mJ / cm 2 .
（４）無電解めっき処理及び電解めっき処理
無電解めっきの前処理として、コンディショナー液「ＣＬＣ−６０１」（日立化成工業株式会社製、商品名）に上記（３）で得られた絶縁樹脂層付き基板を６０℃で５分間浸漬し、その後水洗し、プリディップ液「ＰＤ−２０１」（日立化成工業株式会社製、商品名）に室温にて２分間浸漬した。次にＰｄＣｌ２を含む無電解めっき用触媒である「ＨＳ−２０２Ｂ」（日立化成工業株式会社製、商品名）に、室温で１０分間浸漬処理したのち、水洗し、無電解銅めっき液である「ＣＵＳＴ−２０１めっき液」（日立化成工業株式会社製、商品名）に室温にて１５分間浸漬し、さらに硫酸銅電解めっきを行った。その後、アニール処理を１７０℃で３０分間行い、絶縁樹脂層表面上に厚さ２０μｍの導体層を形成した。
(4) Electroless plating treatment and electrolytic plating treatment As a pretreatment for electroless plating, the conditioner liquid “CLC-601” (manufactured by Hitachi Chemical Co., Ltd., trade name) is provided with the insulating resin layer obtained in (3) above. The substrate was immersed at 60 ° C. for 5 minutes, then washed with water, and immersed in a pre-dip solution “PD-201” (trade name, manufactured by Hitachi Chemical Co., Ltd.) for 2 minutes at room temperature. Next is an electroless plating catalyst containing PdCl 2 "HS-202B" (manufactured by Hitachi Chemical Co., Ltd., trade name), the glass substrate was immersed for 10 minutes at room temperature, washed with water, is an electroless copper plating solution It was immersed in a “CUST-201 plating solution” (trade name, manufactured by Hitachi Chemical Co., Ltd.) for 15 minutes at room temperature, and further subjected to copper sulfate electrolytic plating. Thereafter, annealing treatment was performed at 170 ° C. for 30 minutes to form a conductor layer having a thickness of 20 μm on the surface of the insulating resin layer.
（５）回路の形成
めっき導体層の不要な箇所をエッチング除去するために銅表面の酸化皮膜を＃６００のバフロール研磨で除去した後、エッチング用レジスト膜を形成してエッチング処理し、その後エッチング用レジスト膜を除去して、第１の回路と接続したビアホールを含む第２の回路形成を行った。さらに、多層化するために、第２の回路導体表面を、亜塩素酸ナトリウム：５０ｇ／Ｌ、ＮａＯＨ：２０ｇ／Ｌ、リン酸三ナトリウム：１０ｇ／Ｌの水溶液に８５℃で２０分間浸漬したのち、水洗し、８０℃で２０分間乾燥して第２の回路導体表面上に酸化銅の凹凸を形成した。
（６）多層配線板の作製
上記（３）〜（５）の工程を繰り返して、３層の多層配線板を作製した。なお、最も外側に形成される回路層を第３の回路層（又は外層回路層）と称する。
該多層配線板について、上記方法にて評価した結果を第１表に示す。
(5) Circuit formation To remove unnecessary portions of the plated conductor layer by etching, the oxide film on the copper surface is removed by buffing # 600, and then an etching resist film is formed and etched, and then for etching. The resist film was removed, and a second circuit including a via hole connected to the first circuit was formed. Furthermore, after the second circuit conductor surface was immersed in an aqueous solution of sodium chlorite: 50 g / L, NaOH: 20 g / L, and trisodium phosphate: 10 g / L at 85 ° C. for 20 minutes for multilayering. This was washed with water and dried at 80 ° C. for 20 minutes to form copper oxide irregularities on the surface of the second circuit conductor.
(6) Production of multilayer wiring board The steps (3) to (5) were repeated to produce a three-layer multilayer wiring board. The outermost circuit layer is referred to as a third circuit layer (or outer circuit layer).
The results of evaluating the multilayer wiring board by the above method are shown in Table 1.
実施例２
実施例１において、（Ａ）成分として、以下の方法により調製したヘキサンジオールを骨格に有するエポキシ樹脂（第１表ではＡ２と記載）を用い、配合量を第１表に示すように変更したこと以外は、実施例１と同様にして、各種多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
（ヘキサンジオールを骨格に有するエポキシ樹脂の調製）
温度計及び撹拌機を取り付けたフラスコに、ビスフェノールＡ２２８ｇ（１．００モル）と１，６−ヘキサンジオールジビニルエーテル９２ｇ（０．８５モル）を仕込み、１２０℃まで１時間要して昇温した後、さらに１２０℃で６時間反応させて透明半固形の変性多価フェノール類４００ｇを得た。
次に、温度計、滴下ロート、冷却管、及び撹拌機を取り付けたフラスコに、上記変性多価フェノール類４００ｇ、エピクロルヒドリン９２５ｇ（１０モル）、ｎ−ブタノール１８５ｇを仕込み溶解させた。その後、窒素ガスパージを施しながら、６５℃に昇温した後、共沸する圧力までに減圧して、４９％水酸化ナトリウム水溶液１２２ｇ（１．５モル）を５時間かけて滴下した。次いでこの条件下で０．５時間撹拌を続けた。この間、共沸で留出してきた留出分をディーンスタークトラップで分離して、水層を除去し、有機層を反応系内に戻しながら反応した。その後、未反応のエピクロルヒドリンを減圧蒸留して留去させた。得られた粗エポキシ樹脂にメチルイソブチルケトン１０００ｇとｎ−ブタノール１００ｇを加え溶解した。さらに、この溶液に１０％水酸化ナトリウム水溶液２０ｇを添加して８０℃で２時間反応させた後に、洗浄液のｐＨが中性となるまで、３００ｇの水で水洗を３回繰り返した。次いで共沸によって系内を脱水し、精密ろ過を経た後に溶媒を減圧下で留去して、透明液体のエポキシ樹脂４５７ｇを得た。エポキシ当量は４０３であった。
Example 2
In Example 1, as component (A), an epoxy resin (described as A2 in Table 1) having skeleton of hexanediol prepared by the following method was used, and the blending amount was changed as shown in Table 1. Except for the above, various multilayer wiring boards were produced in the same manner as in Example 1. The results evaluated in the same manner as in Example 1 are shown in Table 1.
(Preparation of epoxy resin having hexanediol as skeleton)
A flask equipped with a thermometer and a stirrer was charged with 228 g (1.00 mol) of bisphenol A and 92 g (0.85 mol) of 1,6-hexanediol divinyl ether and heated to 120 ° C. for 1 hour. Further, the mixture was reacted at 120 ° C. for 6 hours to obtain 400 g of a transparent semi-solid modified polyphenol.
Next, 400 g of the modified polyphenols, 925 g (10 mol) of epichlorohydrin, and 185 g of n-butanol were charged and dissolved in a flask equipped with a thermometer, a dropping funnel, a condenser, and a stirrer. Thereafter, the temperature was raised to 65 ° C. while purging with nitrogen gas, and then the pressure was reduced to an azeotropic pressure, and 122 g (1.5 mol) of a 49% aqueous sodium hydroxide solution was added dropwise over 5 hours. Stirring was then continued under these conditions for 0.5 hour. During this time, the distillate distilled azeotropically was separated with a Dean-Stark trap, the aqueous layer was removed, and the reaction was conducted while returning the organic layer to the reaction system. Thereafter, unreacted epichlorohydrin was distilled off under reduced pressure. To the resulting crude epoxy resin, 1000 g of methyl isobutyl ketone and 100 g of n-butanol were added and dissolved. Further, 20 g of a 10% sodium hydroxide aqueous solution was added to this solution and reacted at 80 ° C. for 2 hours. Then, washing with 300 g of water was repeated three times until the pH of the washing solution became neutral. Next, the system was dehydrated by azeotropic distillation, and after passing through microfiltration, the solvent was distilled off under reduced pressure to obtain 457 g of a transparent liquid epoxy resin. The epoxy equivalent was 403.
実施例３〜５、及び７
実施例１において、樹脂組成物の組成を第１表に示すように変更したこと以外は、実施例１と同様な操作を行い、各種多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Examples 3-5 and 7
In Example 1, except that the composition of the resin composition was changed as shown in Table 1, the same operation as in Example 1 was performed to prepare various multilayer wiring boards. The results evaluated in the same manner as in Example 1 are shown in Table 1.
実施例６
実施例４と同様の樹脂組成物を用いて、実施例１に記載されるのと同様の方法で、絶縁樹脂層の形成、及び熱硬化までを行った。次に、この絶縁樹脂層付き基板に層間接続用のビアホールを、日立ビアメカニクス製ＣＯ２レーザ加工機「ＬＣＯ−１Ｂ２１型」により、ビーム径８０μｍ、周波数５００Ｈｚ、パルス幅５μｓｅｃ、ショット数７の条件で加工して作製した。その後、絶縁樹脂層付き基板をランプがメタルハライドランプのコンベア式紫外線照射装置（最大波長３５０〜３８０ｎｍ）を用い、紫外線を光量が３０００ｍＪ／ｃｍ２になるように照射した。
次に、絶縁樹脂層を化学粗化するために、膨潤液として、ジエチレングリコールモノブチルエーテル：２００ｍＬ／Ｌ、ＮａＯＨ：５ｇ／Ｌの水溶液を８０℃に加温して、これに５分間浸漬処理した。次に、粗化液として、ＫＭｎＯ４：６０ｇ／Ｌ、ＮａＯＨ：４０ｇ／Ｌの水溶液を８０℃に加温して１０分間浸漬処理した。引き続き、中和液（ＳｎＣｌ２：３０ｇ／Ｌ、濃度９８質量％のＨ２ＳＯ４：３００ｍＬ／Ｌ）の水溶液に室温で５分間浸漬処理して中和した。その後は、実施例４と同様な操作を行って多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Example 6
Using the same resin composition as in Example 4, the insulating resin layer was formed and thermally cured in the same manner as described in Example 1. Next, a via hole for the insulating resin layer with the substrate in the interlayer connection by Hitachi Via Mechanics, Ltd. CO 2 laser processing machine "LCO-1B21 Model", beam diameter 80 [mu] m, frequency 500 Hz, pulse width 5 .mu.sec, shot number 7 conditions It was manufactured by processing. Thereafter, the substrate with the insulating resin layer was irradiated with ultraviolet rays so that the amount of light became 3000 mJ / cm 2 using a conveyor type ultraviolet irradiation device (maximum wavelength 350 to 380 nm) in which the lamp was a metal halide lamp.
Next, in order to chemically roughen the insulating resin layer, an aqueous solution of diethylene glycol monobutyl ether: 200 mL / L, NaOH: 5 g / L was heated to 80 ° C. as a swelling liquid, and immersed in this for 5 minutes. Next, as a roughening solution, an aqueous solution of KMnO 4 : 60 g / L, NaOH: 40 g / L was heated to 80 ° C. and immersed for 10 minutes. Subsequently, the mixture was neutralized by immersing in an aqueous solution of a neutralizing solution (SnCl 2 : 30 g / L, H 2 SO 4 having a concentration of 98% by mass: 300 mL / L) at room temperature for 5 minutes. Thereafter, the same operation as in Example 4 was performed to produce a multilayer wiring board. The results evaluated in the same manner as in Example 1 are shown in Table 1.
実施例８
実施例２において、第１表に示すように、無機フィラーとして、平均粒径０．５μｍの球状シリカ、「ＳＯ−２５Ｒ」（株式会社アドマテックス製、商品名）を加えた樹脂組成物を用いた以外は、実施例２と同様な操作を行い、多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Example 8
In Example 2, as shown in Table 1, a resin composition to which spherical silica having an average particle size of 0.5 μm and “SO-25R” (manufactured by Admatechs Co., Ltd., trade name) was added as an inorganic filler. Except for the above, the same operation as in Example 2 was performed to produce a multilayer wiring board. The results evaluated in the same manner as in Example 1 are shown in Table 1.
実施例９
実施例１において、紫外線照射のランプを高圧水銀灯のコンベア式紫外線照射装置（最大波長３１０〜３７０ｎｍ）に変更した以外は、実施例１と同様な操作を行い、多層配線板を作製した。なお、紫外線の照射は、実施例１と同様に、光量が３０００ｍＪ／ｃｍ２になるように行った。
Example 9
A multilayer wiring board was produced in the same manner as in Example 1 except that the ultraviolet irradiation lamp was changed to a high pressure mercury lamp conveyor type ultraviolet irradiation device (maximum wavelength 310 to 370 nm). The ultraviolet irradiation was performed so that the light amount was 3000 mJ / cm 2 as in Example 1.
比較例１
実施例１において、樹脂組成物の組成を第１表に示すように、紫外線活性型エステル基含有化合物を使用しないこと以外は、実施例１と同様な操作を行い、多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Comparative Example 1
In Example 1, as shown in Table 1, the composition of the resin composition was the same as in Example 1 except that the ultraviolet-active ester group-containing compound was not used, and a multilayer wiring board was produced. The results evaluated in the same manner as in Example 1 are shown in Table 1.
比較例２
実施例１の樹脂組成物において、第１表に示すように、紫外線活性型エステル基含有化合物の代わりに、クレゾールノボラック型フェノール樹脂（「ＫＡ−１１６５」、ＤＩＣ株式会社製商品名、水酸基当量：１１９）を使用したこと以外は、実施例１と同様な操作を行い、多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Comparative Example 2
In the resin composition of Example 1, as shown in Table 1, instead of the UV-active ester group-containing compound, a cresol novolac-type phenol resin (“KA-1165”, trade name, manufactured by DIC Corporation, hydroxyl equivalent: Except for using 119), the same operation as in Example 1 was performed to produce a multilayer wiring board. The results evaluated in the same manner as in Example 1 are shown in Table 1.
比較例３
実施例２の樹脂組成物において、第１表に示すように、（Ｃ）成分を用いなかったこと以外は、実施例２と同様な操作を行い、多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Comparative Example 3
As shown in Table 1, in the resin composition of Example 2, the same operation as in Example 2 was performed except that the component (C) was not used, and a multilayer wiring board was produced. The results evaluated in the same manner as in Example 1 are shown in Table 1.
比較例４
実施例２の樹脂組成物において、第１表に示すように、３−イソシアネートプロピルトリエトキシシラン（Ｃ１成分）に代えて、アミノプロピルトリメトキシシラン（Ｃ２成分）を２質量部用いたこと以外は、実施例２と同様な操作を行い、多層配線板を作製した。実施例１と同様にして評価した結果を第１表に示す。
Comparative Example 4
In the resin composition of Example 2, as shown in Table 1, in place of 3-isocyanatopropyltriethoxysilane (C1 component), 2 parts by mass of aminopropyltrimethoxysilane (C2 component) was used. The same operation as in Example 2 was performed to produce a multilayer wiring board. The results evaluated in the same manner as in Example 1 are shown in Table 1.
Ａ１：テトラフェニル型エポキシ樹脂、「ＪＥＲ−１０３１」（ＪＥＲ株式会社社製、商品名、エポキシ当量：２００）
Ａ２：ヘキサンジオールを骨格に有するエポキシ樹脂（エポキシ当量：４０３）
Ａ３：ナフタレン型エポキシ樹脂、「ＨＰ−４７００」（ＤＩＣ株式会社社製、商品名、エポキシ当量：１６８）
Ａ４：フェノールノボラック型エポキシ樹脂、「Ｎ−７７０」（ＤＩＣ株式会社社製、商品名、エポキシ当量：１９０）
Ｂ１：紫外線活性型エステル基含有化合物、「ＥＸＢ−９４７０」（ＤＩＣ株式会社、商品名、エステル当量：２２３）
Ｃ１：３−イソシアネートプロピルトリエトキシシラン、「ＫＢＥ−９００７」（信越シリコーン社製、商品名）
Ｃ２：アミノプロピルトリメトキシシラン（東京化成工業株式会社製）
Ｄ１：硬化促進剤、イミダゾール誘導体化合物、１−シアノエチル−２−フェニルイミダゾリウムトリメリテート（四国化成工業株式会社製、商品名「２ＰＺ−ＣＮＳ」）
Ｅ１：メチルエチルケトン
Ｆ１：無機フィラー、平均粒径０．５μｍの球状シリカ、「ＳＯ−２５Ｒ」（株式会社アドマテックス製、商品名）
Ｇ１：クレゾールノボラック型フェノール樹脂、「ＫＡ−１１６５」（ＤＩＣ株式会社製商品名、水酸基当量：１１９）
A1: Tetraphenyl type epoxy resin, “JER-1031” (manufactured by JER Corporation, trade name, epoxy equivalent: 200)
A2: Epoxy resin having hexanediol in the skeleton (epoxy equivalent: 403)
A3: Naphthalene type epoxy resin, “HP-4700” (manufactured by DIC Corporation, trade name, epoxy equivalent: 168)
A4: phenol novolac type epoxy resin, “N-770” (manufactured by DIC Corporation, trade name, epoxy equivalent: 190)
B1: UV-active ester group-containing compound, “EXB-9470” (DIC Corporation, trade name, ester equivalent: 223)
C1: 3-isocyanatopropyltriethoxysilane, “KBE-9007” (trade name, manufactured by Shin-Etsu Silicone)
C2: Aminopropyltrimethoxysilane (manufactured by Tokyo Chemical Industry Co., Ltd.)
D1: Curing accelerator, imidazole derivative compound, 1-cyanoethyl-2-phenylimidazolium trimellitate (manufactured by Shikoku Kasei Kogyo Co., Ltd., trade name “2PZ-CNS”)
E1: Methyl ethyl ketone F1: Inorganic filler, spherical silica with an average particle size of 0.5 μm, “SO-25R” (trade name, manufactured by Admatechs Co., Ltd.)
G1: Cresol novolac type phenol resin, “KA-1165” (trade name, hydroxyl equivalent: 119 manufactured by DIC Corporation)
第１表から、本発明の樹脂組成物を熱硬化し、これに紫外線を照射した絶縁樹脂層を有する配線板は、実施例に示したように、絶縁樹脂層の表面粗さが小さい状態で外層銅との接着強度が良好で微細配線化に適していることがわかる。また、２８８℃におけるはんだ耐熱性にも優れており、鉛フリーはんだ実装にも優れていることがわかる。 From Table 1, the wiring board having the insulating resin layer obtained by thermally curing the resin composition of the present invention and irradiating the resin composition with ultraviolet rays has a small surface roughness of the insulating resin layer as shown in the examples. It can be seen that the adhesive strength with the outer layer copper is good and is suitable for fine wiring. Moreover, it is understood that the solder heat resistance at 288 ° C. is also excellent, and the lead-free solder mounting is also excellent.
本発明によれば、絶縁樹脂層表面の凹凸形状が小さい状態でも、配線導体に対して、高い接着力を発現し得る上、ビアホール底のスミアを除去するために、過マンガン酸ナトリウム系などの粗化液で処理しても、絶縁樹脂層表面の粗化凹凸形状が小さく、かつ配線導体に対して高い接着力を確保することができる。
本発明の樹脂組成物を用いて作製された配線板は回路との接着強度が良好であり、かつはんだ耐熱性にも優れている。
According to the present invention, in order to remove smear at the bottom of the via hole, in addition to being able to express a high adhesive force to the wiring conductor even in a state where the uneven shape on the surface of the insulating resin layer is small, a sodium permanganate type or the like Even if it processes with a roughening liquid, the roughening uneven | corrugated shape on the surface of an insulating resin layer is small, and high adhesive force can be ensured with respect to a wiring conductor.
The wiring board produced using the resin composition of the present invention has good adhesive strength with a circuit and is excellent in solder heat resistance.
Claims (10)