JP2014152145A - Hair dye material in film form, and method of hair dyeing - Google Patents
Hair dye material in film form, and method of hair dyeing Download PDFInfo
- Publication number
- JP2014152145A JP2014152145A JP2013023847A JP2013023847A JP2014152145A JP 2014152145 A JP2014152145 A JP 2014152145A JP 2013023847 A JP2013023847 A JP 2013023847A JP 2013023847 A JP2013023847 A JP 2013023847A JP 2014152145 A JP2014152145 A JP 2014152145A
- Authority
- JP
- Japan
- Prior art keywords
- hair
- dye
- film
- water
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明はフィルム状染毛材料および染毛方法に関する。 The present invention relates to a film-like hair dyeing material and a hair dyeing method.
従来、例えば下記の特許文献1や特許文献2で開示される泡状の染毛剤、特許文献3や特許文献4に開示されている液状やゲル、泡の染毛剤が用いられていた。しかし、これらの従来の染毛剤は刷毛や櫛などで塗り広げる必要がある。
また毛髪全体を染めるには有用だが、生え際やメッシュなど一部分のみを好みの形状に染めることは出来なかった。また、泡やゲル自体が毛髪へ塗布後に液垂れして、地肌だけでなく、周囲を汚染することが問題であった。さらに部分染めするのに必要な量が分かり難く、本来必要な量以上に染毛剤を無駄に使用することがあった。
これに加えて、上記の各種染毛剤を使用すると、手や指まで染料で染まる恐れがあるため、手袋やマスキングテープの使用が必要であり、一人で簡便に自身の毛髪を染毛することは困難であった。特別の櫛やテープなどを用いるのは作業するのに不便であり、特に泡状の染毛剤では特別な容器が必要となりコストが高くなる傾向にある。
以上のように、肌などを汚さず、簡便に染毛できるフィルム形状の染毛材料及び染毛方法は今まで無かった。
ここで言う染毛材料は医薬部外品の染毛剤と化粧品の染毛料の両者を言う。
Conventionally, for example, foam-like hair dyes disclosed in Patent Document 1 and Patent Document 2 below, and liquid, gel, and foam hair dyes disclosed in Patent Document 3 and Patent Document 4 have been used. However, these conventional hair dyes need to be spread with a brush or a comb.
Although it is useful for dyeing the entire hair, it was not possible to dye only a part of the hairline or mesh into the desired shape. In addition, it has been a problem that bubbles and gel itself dripped after application to the hair and contaminate not only the background but also the surroundings. Furthermore, it is difficult to understand the amount necessary for partial dyeing, and the hair dye was sometimes used wastefully in excess of the originally necessary amount.
In addition, the use of the above-mentioned various hair dyes may result in dyeing to the hands and fingers, so it is necessary to use gloves and masking tape. Was difficult. The use of special combs or tapes is inconvenient to work, and especially for foamy hair dyes, special containers are required and the cost tends to increase.
As described above, there has been no film-shaped hair dyeing material and hair coloring method that can easily dye hair without polluting the skin and the like.
The hair dyeing material mentioned here refers to both quasi-drug hair dyes and cosmetic hair dyes.
さらに、例えば、下記の特許文献5や特許文献6で開示される染毛剤では、保存するために成型容器が用いられており、店舗で陳列する際に広い場所の確保が必要であった。また、染毛作業後のゴミの容積が大きいことも問題であった。そして、液体物やガスの使用により、飛行機での手荷物・機内持ち込みに適さない場合があった。
このため、特許文献7には支持体に染毛剤などを含浸させてなる化粧用品が記載されているが、このような化粧用品は液状の染毛剤を単に支持体に含浸させたものであって、特許文献1〜6に示す染毛剤を単に支持体に担持させたものに過ぎず、使用時、あるいは染毛終了時に支持体を剥がす際には、依然として手や指、肌などを汚さないようにすることが困難であった。
そして、下記の特許文献8には、多孔質で可撓性の支持体上及び/又は支持体内に直接染料又は直接染料プリカーサが結合してなり、乾式含浸法によって毛髪を染色するための物品が記載されているが、これは別に用意した熱源によって、毛髪に該直接染料又は直接染料プリカーサを転写するためのものであり、この物品により毛髪を染色するためには予め熱源を準備しておく必要がある。
以上のように、保存容器がかさばらず、飛行機の手荷物・機内持ち込みの可能な、フィルム形状の染毛材料及び染毛方法は今まで無かった。
Furthermore, for example, in the hair dye disclosed in Patent Document 5 and Patent Document 6 below, a molded container is used for storage, and it is necessary to secure a wide space when displaying in a store. Another problem is that the volume of dust after the hair dyeing work is large. Also, due to the use of liquids and gas, there are cases where it is not suitable for baggage and carry-on on airplanes.
For this reason, Patent Document 7 describes a cosmetic product in which a support is impregnated with a hair dye or the like. However, such a cosmetic product is obtained by simply impregnating a support with a liquid hair dye. In addition, the hair dye shown in Patent Documents 1 to 6 is merely carried on the support, and when the support is peeled off at the time of use or at the end of the hair dyeing, still hands, fingers, skin, etc. It was difficult to keep it clean.
Patent Document 8 below discloses an article for dyeing hair by a dry impregnation method in which a direct dye or a direct dye precursor is bonded on and / or in a porous and flexible support. Although described, this is for transferring the direct dye or the direct dye precursor to the hair with a separately prepared heat source, and it is necessary to prepare a heat source in advance to dye the hair with this article. There is.
As described above, there has been no film-shaped hair dyeing material and hair dyeing method that is not bulky and can be carried in an airplane's baggage or cabin.
本発明は、地肌や周囲を汚さずに、適量の染毛剤を使用して、簡便に好みのデザインに毛髪を染毛することができるフィルム形状の染毛材料及びその染毛方法を提供する。また、水が含浸して収縮する担体を使用することによる、染色したい箇所に対して正確に担体を配置することの困難性と、使用時に初めて担体表面に化粧製品を設けるという使用時の煩雑さを解消させる。 The present invention provides a film-shaped hair dyeing material and a hair dyeing method capable of easily dyeing hair into a desired design by using an appropriate amount of hair dye without contaminating the background and surroundings. . In addition, the use of a carrier that is impregnated with water and shrinks makes it difficult to accurately place the carrier on the portion to be dyed, and the complexity of using a cosmetic product on the carrier surface for the first time at the time of use. To eliminate.
本発明者らは、上記目的を達成すべく鋭意検討した結果、水溶性樹脂と染料とを複合化させると、毛髪に貼付するだけで簡便に染毛できることを見出し、またフィルム状であるため好みの形状にカットして染毛に用いればデザイン性に優れ、染毛したい部分のみに無駄なく染毛できることを見出し、本発明を完成するに至った。
具体的には下記の通り。
1.染料を主成分とする染毛剤と水溶性樹脂を複合化することを特徴とするフィルム状染毛材料。
2.染毛剤が直接染料または酸性染料であることを特徴とする1記載のフィルム状染毛材料。
3.非水溶性の支持体層と水溶性の染毛材料層からなる2層構造であることを特徴とする、1又は2に記載のフィルム状染毛材料。
4.水溶性樹脂がケン化度:65〜90モル%、重合度:400〜3000のポリビニルアルコールからなることを特徴とする1〜3のいずれかに記載のフィルム状染毛材料。
5.1〜4のいずれかに記載のフィルム状染毛材料を毛髪へ貼付して染毛する方法。
As a result of intensive studies to achieve the above object, the present inventors have found that when a water-soluble resin and a dye are combined, they can be easily dyed by simply applying them to the hair. It has been found that if it is cut into the shape of the hair and used for hair dyeing, it is excellent in design and hair can be dyed without waste on only the part to be hair dyed, and the present invention has been completed.
Specifically:
1. A film-like hair dyeing material comprising a hair dye comprising a dye as a main component and a water-soluble resin.
2. 2. The film-like hair dyeing material according to 1, wherein the hair dye is a direct dye or an acid dye.
3. 3. The film-like hair dyeing material according to 1 or 2, which has a two-layer structure comprising a water-insoluble support layer and a water-soluble hair dyeing material layer.
4). The film-like hair dyeing material according to any one of 1 to 3, wherein the water-soluble resin comprises polyvinyl alcohol having a saponification degree of 65 to 90 mol% and a polymerization degree of 400 to 3000.
5. A method for dyeing hair by applying the film-like hair dyeing material according to any one of 1 to 4 to hair.
本発明によると、染毛するのに、溶液状、ゲルや泡状の染毛方法と異なり、地肌を汚すことなく、希望する部分のみフィルム状染毛材料を貼り付けることで、肌や周囲を汚すことなく無駄なく簡便に狙った所のみに均一に染毛できる。また容器の簡素化も図ることができる。さらに、使用時に担体が収縮することがなく、加えて使用時に担体表面に染毛剤を塗布する手間を省くことができる。
さらに担体がフィルム状であるので、その表面に染料を水溶性樹脂と共に正確な量に調製して設けることができるので、染毛の程度が過不足無い状態となるように染毛を行うことができる。
According to the present invention, unlike a solution-like, gel- or foam-like hair dyeing method, the film or hair dyeing material is applied only to a desired portion without staining the background, so that the skin and surroundings can be dyed. Hair can be uniformly dyed only in the targeted area without waste and without waste. In addition, the container can be simplified. Furthermore, the carrier does not shrink during use, and in addition, it is possible to save the trouble of applying a hair dye on the surface of the carrier during use.
Furthermore, since the carrier is in the form of a film, the dye can be prepared on the surface in an accurate amount together with the water-soluble resin, so that the hair can be dyed so that the degree of hair coloring is not excessive or insufficient. it can.
以下にフィルム状染毛材料および染毛方法について具体的に説明する。
本発明のフィルム状染毛材料は、水溶性樹脂フィルムの内部または表面に染毛剤が複合化されているフィルム状染毛材料であれば良い。そのため、髪に対して泡状や溶液状、ゲル状の染毛剤を直接使用するものではなく、担体にこれらの染毛剤を付着させるものでもないので、作業者が染料に直接手を触れずに、毛髪に貼付して染毛でき、しかも、添付時に収縮することがないので正確に対象とする髪を染毛することができる。毛髪へ貼付し染毛後には、水で洗い流すことによって水溶性樹脂フィルムごと濯ぎ除去することができる。
本発明のフィルム状染毛材料は、毛髪に貼付した後に、フィルムに複合化されていた染毛剤がフィルムから水分によって毛髪表面に移行して、毛髪が染色されるものである。
The film-like hair dyeing material and the hair dyeing method will be specifically described below.
The film-like hair dye material of the present invention may be a film-like hair dye material in which a hair dye is combined inside or on the surface of the water-soluble resin film. For this reason, foam, solution, and gel hair dyes are not used directly on the hair, and these hair dyes are not attached to the carrier, so the operator touches the dye directly. In addition, the hair can be dyed by being attached to the hair, and since it does not shrink when attached, the target hair can be dyed accurately. After being applied to hair and dyed, the entire water-soluble resin film can be rinsed and removed by rinsing with water.
The film-like hair dye material of the present invention is one in which the hair dye compounded on the film moves from the film to the hair surface by moisture after being applied to the hair, and the hair is dyed.
(水溶性樹脂フィルム)
本発明において水溶性樹脂フィルムは、染毛剤を担持させる担体として機能し、かつ染毛時において髪に対してより均一に、染毛剤を馴染ませる機能をも備えるものである。
このような水溶性樹脂フィルムとしては、水分により少なくともその表面が溶解し、毛髪表面に貼付することができる材料からなるフィルムであれば特に材質の制限はない。そのような材質の具体的な材料として、ゼラチン、デンプン、寒天、ポリビニルアルコール及びその変性体などが挙げられる。中でも、ポリビニルアルコール系樹脂およびその変性体が好ましい。さらに好ましくは、部分ケン化ポリビニルアルコールである。
(Water-soluble resin film)
In the present invention, the water-soluble resin film functions as a carrier for carrying a hair dye, and also has a function of making the hair dye more evenly mixed with the hair during hair dyeing.
Such a water-soluble resin film is not particularly limited as long as it is a film made of a material that can be attached to the hair surface, at least the surface of which is dissolved by moisture. Specific examples of such materials include gelatin, starch, agar, polyvinyl alcohol and modified products thereof. Among these, polyvinyl alcohol resins and modified products thereof are preferable. More preferred is partially saponified polyvinyl alcohol.
このなかでも部分ケン化ポリビニルアルコールのケン化度は65.0〜90.0モル%、重合度は400〜3000の範囲にあることが好ましい。部分ケン化ポリビニルアルコールのケン化度が65.0モル%〜90.0モル%の範囲であると、さらに高い溶解性を示すことができ、染毛後に水で洗い流すことがより容易となる。重合度が400以上であると、フィルム形状を保つためにより十分な強度を保つことができ、かつ重合度が3000以下であると、溶解した際の粘度が高くなりすぎず、さらに洗い流し易くなる。
なお、上記水溶性樹脂には、必要に応じて任意の添加剤を加えても良い。添加剤として、可塑剤、スリップ剤、アンチブロッキング剤、賦形剤、着色剤などが挙げられる。可塑剤としてはグリセリン、ジグリセリン、トリエチレングリコール、ポリエチレエングリコールなどが挙げられるが、特にグリセリンが経済性の面からも好ましい。その添加量は水溶性樹脂フィルムの重量に対し、2〜20wt%の範囲が好ましい。
Of these, the saponification degree of the partially saponified polyvinyl alcohol is preferably 65.0 to 90.0 mol%, and the polymerization degree is preferably in the range of 400 to 3000. When the degree of saponification of the partially saponified polyvinyl alcohol is in the range of 65.0 mol% to 90.0 mol%, it is possible to show higher solubility, and it is easier to wash away with water after dyeing. When the degree of polymerization is 400 or more, sufficient strength can be maintained to maintain the film shape, and when the degree of polymerization is 3000 or less, the viscosity at the time of dissolution does not become too high, and it becomes easier to wash away.
In addition, you may add arbitrary additives to the said water-soluble resin as needed. Examples of the additive include a plasticizer, a slip agent, an antiblocking agent, an excipient, and a colorant. Examples of the plasticizer include glycerin, diglycerin, triethylene glycol, and polyethylene glycol, and glycerin is particularly preferable from the viewpoint of economy. The addition amount is preferably in the range of 2 to 20 wt% with respect to the weight of the water-soluble resin film.
水溶性樹脂フィルムの厚みは10μmから200μm程度が適当であり、好ましくは20μmから70μm、より好ましくは40μmから60μmの範囲である。10μmを下回ると染毛のための染毛剤を十分複合化させることができず、200μmより厚いと経済的に不適となるためである。また1枚の水溶性樹脂フィルムの大きさは必要に応じて断裁して使用するため、A4サイズ(210mm×297mm)程度や、ロール状としても良い。
水溶性樹脂フィルムの製膜方法に特に限定はなく、樹脂フィルムを製造するための一般的な手法を用いることができる。具体的には水溶性樹脂材料又はその溶液の溶融押出法、溶液流延法、スプレーコートなどであるが、ここに挙げた手法に限定されるものではない。
いずれにしても本発明のフィルム状染毛材料は、水に濡れることにより収縮を起こさないという性質を備えるものである。
The thickness of the water-soluble resin film is suitably about 10 μm to 200 μm, preferably 20 μm to 70 μm, more preferably 40 μm to 60 μm. If the thickness is less than 10 μm, the hair dye for hair coloring cannot be sufficiently combined, and if it is more than 200 μm, it is economically unsuitable. Moreover, since the size of one water-soluble resin film is cut and used as necessary, it may be about A4 size (210 mm × 297 mm) or a roll shape.
There is no limitation in particular in the film forming method of a water-soluble resin film, The general method for manufacturing a resin film can be used. Specific examples include a water-soluble resin material or a solution extrusion method, a solution casting method, and spray coating of the solution, but are not limited to the methods listed here.
In any case, the film-like hair dye material of the present invention has the property of not causing shrinkage when wet with water.
(染毛剤の複合化)
水溶性樹脂フィルムを上記の方法により成膜する際に、予め水溶性樹脂材料又はその溶液に染毛剤等を添加しておき、それをフィルム化しても良く、成膜した水溶性樹脂フィルム上に染毛剤等を塗布したり、あるいは成膜した水溶性樹脂フィルム上に、別に成膜した染毛剤等を含有する水溶性樹脂フィルムを積層させること等により複合化させても良い。
特に本発明においては、上記の方法により染毛剤を複合化できるので、得られた本発明のフィルム状染毛材料には、均一に染毛剤が含有され、またその含有量の調整も容易である。
また、水溶性樹脂材料中に染毛剤を含有させて得たフィルム状染毛材料には、その表面に存在する染毛剤の量は少ないので、直接手に触れる染毛剤の量はわずかであるか、あるいは手に触れないので、使用時に不用意に手が汚れることがない。
これに対して、不織布のような他の基材を採用してその上に染毛剤を塗布するよりも、均一に染毛剤を含有させることが可能であるし、染毛剤が剥がれて手が汚れる可能性が少なくなる。
またフィルム状の染色剤であるから、髪に付着させた際により均一に付着することができ、フィルム状染毛材料が含有する染色剤を無駄無く染色に使用することができる。なお、仮に不織布のように空隙が多く存在する場合には、髪への付着を均一にすることが困難であり染色にムラが発生する可能性がある。
(Combination of hair dyes)
When the water-soluble resin film is formed by the above method, a hair dye or the like may be added in advance to the water-soluble resin material or a solution thereof, and the film may be formed on the water-soluble resin film. It may be combined by applying a hair dye or the like, or by laminating a water-soluble resin film containing a hair dye or the like separately formed on the water-soluble resin film formed.
Particularly in the present invention, since the hair dye can be combined by the above-described method, the obtained film-like hair dye material of the present invention contains the hair dye uniformly, and the content can be easily adjusted. It is.
In addition, since the amount of the hair dye present on the surface of the film-like hair dye material obtained by incorporating the hair dye in the water-soluble resin material is small, the amount of the hair dye that directly touches the hand is small. Because it is or does not touch the hand, the hand will not be inadvertently soiled during use.
On the other hand, it is possible to contain the hair dye uniformly, and the hair dye is peeled off rather than adopting another base material such as a nonwoven fabric and applying the hair dye thereon. There is less chance of getting your hands dirty.
Moreover, since it is a film-like dyeing agent, it can adhere more uniformly when it is attached to the hair, and the dyeing agent contained in the film-like hair dyeing material can be used for dyeing without waste. In addition, if there are many voids like a nonwoven fabric, it is difficult to make the adhesion to the hair uniform, and there is a possibility that unevenness occurs in the dyeing.
(支持体層)
また、水溶性樹脂フィルムの片面又は両面に、表面保護機能を備え水溶性樹脂フィルムに対して離型性を有する支持体層を重ねることもできる。支持体層を備えた水溶性樹脂フィルムとするために、一旦作成した水溶性樹脂フィルム上に別に用意した支持体層をラミネートする方法、支持体上に上記の溶融押出法、溶液流延法、スプレーコートなどの方法によって水溶性樹脂フィルムを形成しても良い。
そのような支持体層の材質には特に限定はなく、水溶性樹脂フィルムの表面に密着でき、かかる使用時に剥離が容易な材質であればよい。具体的には、例えば、上質紙、ポリプロピレン(PP)、ポリエチレンテレフタレート(PET等)等のポリエステル系樹脂フィルム、ポリエチレン(PE)、ナイロン系樹脂フィルム(PA)などが挙げられる。また樹脂フィルムや紙等の表面に公知のフッ素樹脂やケイ素樹脂等の離型性を有する物質を塗布してなるフィルムを支持体層としてもよい。
フィルム状染毛材料にはある程度の支持体のコシと貼付時の柔軟性及び取り扱い性が良好であることが求められる。そのためこのような支持体層の材質としてはPETやPPが好ましい。さらにコストの面から望ましいのはPPである。離型紙がフィルム形状である場合には、そのフィルム厚みは5μm〜200μmの範囲が好ましい。支持体層は、水溶性樹脂フィルムの片面又は全面に重ねられるため、必要に応じて断裁して使用されるため、水溶性樹脂フィルムと同じくA4サイズ(210mm×297mm)程度が適当である。
なお、水溶性樹脂フィルムの両面に支持体層を設ける場合には、該水溶性樹脂フィルムの、髪に密着する側の面に位置する支持体層は、実質的にその髪に密着する面を保護する保護層ともいえる。
(Support layer)
Moreover, the support body layer which has a surface protection function and has releasability with respect to a water-soluble resin film can also be piled up on the single side | surface or both surfaces of a water-soluble resin film. In order to make a water-soluble resin film provided with a support layer, a method of laminating a support layer separately prepared on a water-soluble resin film once prepared, the above melt extrusion method, solution casting method on the support, The water-soluble resin film may be formed by a method such as spray coating.
The material of such a support layer is not particularly limited as long as it is a material that can adhere to the surface of the water-soluble resin film and can be easily peeled off during use. Specific examples include high-quality paper, polyester resin films such as polypropylene (PP) and polyethylene terephthalate (PET), polyethylene (PE), nylon resin film (PA), and the like. Moreover, it is good also considering the film formed by apply | coating the substance which has mold release properties, such as a well-known fluorine resin and a silicon resin, on the surface of a resin film, paper, etc. as a support body layer.
The film-like hair dye material is required to have a certain degree of stiffness of the support and good flexibility and handling at the time of application. Therefore, PET or PP is preferable as the material for such a support layer. Further, PP is desirable from the viewpoint of cost. When the release paper has a film shape, the film thickness is preferably in the range of 5 μm to 200 μm. Since the support layer is laminated on one side or the entire surface of the water-soluble resin film, it is cut and used as necessary, and therefore, the A4 size (210 mm × 297 mm) is suitable as in the case of the water-soluble resin film.
When providing a support layer on both sides of the water-soluble resin film, the support layer located on the side of the water-soluble resin film that is in close contact with the hair has a surface that is substantially in close contact with the hair. It can be said that it is a protective layer to protect.
(染料)
染毛剤に含有される成分の染毛に用いる染料は、染毛に使用される一般的な染料であれば問題なく、好ましくは水溶性の酸性染料、直接染料であれば良い。酸性染料としては、o−又はp−フェニレンジアミン、トルエン−2,5−ジアミン(p−トルイレンジアミン)、N−フェニル−p−フェニレンジアミン、4,4’−ジアミノフェノール、N,N−ビス(2−ヒドロキシエチル)−p−フェニレンジアミン、4−アミノ−m−クレゾール、2−アミノ−4−ヒドロキシエチルアミノアニソール、2,4−ジアミノフェノール及びそれらの塩類等が例示される。また使用される塩類としては、塩酸塩、硫酸塩、酢酸塩等が例示される。
また、酸性染料と共に使用されるカプラーとしては、主としてm−ジアミン類、アミノフェノール類又はジフェノール類が挙げられ、具体的にはレゾルシン、カテコール、ピロガロール、フロロフルシン、没食子酸、ハイドロキノン、5−アミノ−o−クレゾール、m−アミノフェノール、5−(2−ヒドロキシエチルアミノ)−2−メチルフェノール、m−フェニレンジアミン、2,4−ジアミノフェノキシエタノール、トルエン−3,4ジアミン、α−ナフトール、2,6−ジアミノピリジン、ジフェニルアミン、3,3’−イミノジフェニール、1,5−ジヒドロキシナフタレン及びタンニン酸及びそれらの塩等が例示される。
(dye)
The dye used for the hair dyeing of the components contained in the hair dye is not a problem as long as it is a general dye used for hair dyeing, preferably a water-soluble acid dye or a direct dye. Acid dyes include o- or p-phenylenediamine, toluene-2,5-diamine (p-toluylenediamine), N-phenyl-p-phenylenediamine, 4,4′-diaminophenol, N, N-bis. Examples include (2-hydroxyethyl) -p-phenylenediamine, 4-amino-m-cresol, 2-amino-4-hydroxyethylaminoanisole, 2,4-diaminophenol and salts thereof. Examples of salts used include hydrochlorides, sulfates, acetates and the like.
In addition, examples of couplers used together with acidic dyes include m-diamines, aminophenols or diphenols. Specifically, resorcin, catechol, pyrogallol, fluoroflucine, gallic acid, hydroquinone, 5-amino- o-cresol, m-aminophenol, 5- (2-hydroxyethylamino) -2-methylphenol, m-phenylenediamine, 2,4-diaminophenoxyethanol, toluene-3,4 diamine, α-naphthol, 2,6 -Diaminopyridine, diphenylamine, 3,3'-iminodiphenyl, 1,5-dihydroxynaphthalene, tannic acid and their salts are exemplified.
直接染料としては、酸性染料、ニトロ染料、分散染料、塩基性染料、天然染料等が挙げられる。酸性染料としては、青色1号、紫色401号、黒色401号、だいだい色205号、赤色227号、赤色106号、黄色203号、アシッドオレンジ3号が挙げられ、ニトロ染料としては、2−ニトロ−p−フェニレンジアミン、2−アミノ−6−クロロ−4−ニトロフェノール、3−ニトロ−p−ヒドロキシエチルアミノフェノール、4−ニトロ−o−フェニレンジアミン、4−アミノ−3−ニトロフェノール、4−ヒドロキシプロピルアミノ−3−ニトロフェノール、HCブルーNo.2、HCオレンジNo.1、HCレッドNo.1、HCイエローNo.2、HCイエローNo.4、HCイエローNo.5、HCレッドNo.3、N,N−ビス−(2−ヒドロキシエチル)−2−ニトロ−p−フェニレンジアミン等が挙げられる。 Examples of direct dyes include acid dyes, nitro dyes, disperse dyes, basic dyes, and natural dyes. Examples of acidic dyes include Blue No. 1, Purple No. 401, Black No. 401, Daidai No. 205, Red No. 227, Red No. 106, Yellow No. 203, and Acid Orange No. 3. Nitro dyes include 2-nitro -P-phenylenediamine, 2-amino-6-chloro-4-nitrophenol, 3-nitro-p-hydroxyethylaminophenol, 4-nitro-o-phenylenediamine, 4-amino-3-nitrophenol, 4- Hydroxypropylamino-3-nitrophenol, HC Blue No. 2, HC Orange No. 1, HC Red No. 1, HC Yellow No. 1 2, HC Yellow No. 4. HC Yellow No. 4 5, HC Red No. 3, N, N-bis- (2-hydroxyethyl) -2-nitro-p-phenylenediamine and the like.
分散染料としては、ディスパーズバイオレット1、ディスパーズブルー1、ディスパーズブラック9等が挙げられ、塩基性染料としては、ベーシックブルー99、ベーシックブラウン16、ベーシックブラウン17、ベーシックレッド76、ベーシックレッド51、ベーシックイエロー57、ベーシックイエロー87、ベーシックオレンジ31等が挙げられる。
このような染料を2種以上併用してもよく、また酸化染料を中間体と併用してもよい。その他、染毛助剤や他の添加物を必要に応じて含んでも良い。
上記の各染料と共に、染毛剤の成分として、ベンジルアルコール等の浸透剤、グリコール酸等のpH調整剤、保護剤、顔料、定着剤、漂白剤等の染毛剤に一般的に配合される成分を配合させることもできる。
Disperse dyes include Disperse Violet 1, Disperse Blue 1, Disperse Black 9, etc., and basic dyes include Basic Blue 99, Basic Brown 16, Basic Brown 17, Basic Red 76, Basic Red 51, Basic yellow 57, basic yellow 87, basic orange 31 and the like.
Two or more of these dyes may be used in combination, and an oxidation dye may be used in combination with the intermediate. In addition, hair dyeing assistants and other additives may be included as necessary.
Along with each of the above dyes, as a component of a hair dye, it is generally blended into a hair dye such as a penetrant such as benzyl alcohol, a pH adjuster such as glycolic acid, a protective agent, a pigment, a fixing agent, and a bleach. Ingredients can also be blended.
(染毛方法)
本発明のフィルム状染毛材料を使用した染毛方法は、フィルム状染色材料を必要なサイズ・形・デザインに任意にトリミングし、これを毛髪に貼付する方法である。この際毛髪は湿らせておいたほうが好ましい。所定の時間をおいて対象とする毛髪を染毛した後、水でフィルムごと洗い流して染毛は完了する。染毛前に行う、皮膚アレルギー試験(パッチテスト)も必要に応じて同様の方法で行うことが可能となる。
水溶性樹脂フィルムは、2つ以上の異なる染料を使用したフィルムを重ねて染毛してもよい。また、例えば異なる染料を使用したフィルムを複数細かくしたものを並べて使用することにより、新たな色を作り染色することも可能である。
(Hair dyeing method)
The hair dyeing method using the film-like hair dyeing material of the present invention is a method in which the film-like dyeing material is arbitrarily trimmed to a required size, shape and design, and this is applied to the hair. At this time, the hair is preferably moistened. After the target hair is dyed after a predetermined time, the film is washed with water to complete the hair dyeing. A skin allergy test (patch test) performed before hair dyeing can be performed in the same manner as necessary.
The water-soluble resin film may be dyed by overlapping films using two or more different dyes. In addition, for example, a new color can be made and dyed by arranging a plurality of thin films using different dyes.
以下に実施例を示し、本発明をより具体的に説明するが、本発明はこれらに限定されるものではない。
下記表1に示す支持体層の片面に、水溶性樹脂、及び染毛剤である可塑剤、染料及び所要によりベンジルアルコールやグリコール酸からなる組成物を混合してなる組成物を塗布、乾燥して実施例1〜8のフィルム状染毛材料を得た。
(試料の評価)
評価にはウィッグ(ビューラックス社製、型番775S)を用い、染毛処理に慣れていない一般的な人により試料の評価を実施した。霧吹きにて湿潤させた毛髪へ、サイズ5cm×10cmで水溶性樹脂フィルムの厚みが40μmのフィルム状染毛材料を貼付した後、そのまま15分間静置した。その後、頭髪全体を温水で洗い流し、評価に供したフィルム状染毛材料を溶解して洗い流し、さらにシャンプーによる洗浄とすすぎを2回繰り返した後に乾燥させた。また、本発明のフィルム状染毛材料以外の染毛剤は適宜、染毛したのち15分間静置してから、頭髪全体を温水で洗い流し、シャンプーにて2回洗浄してから洗い流して乾燥させた。
The present invention will be described more specifically with reference to the following examples. However, the present invention is not limited to these examples.
On one side of the support layer shown in Table 1 below, a composition comprising a water-soluble resin, a plasticizer as a hair dye, a dye, and a composition comprising benzyl alcohol or glycolic acid as required is applied and dried. Thus, film-like hair dye materials of Examples 1 to 8 were obtained.
(Sample evaluation)
A wig (Beaulux, model number 775S) was used for the evaluation, and the sample was evaluated by a general person who was not used to the hair dyeing treatment. A film-like hair dyeing material having a size of 5 cm × 10 cm and a water-soluble resin film thickness of 40 μm was applied to the hair wetted by spraying, and then allowed to stand for 15 minutes. Thereafter, the entire hair was washed away with warm water, and the film-like hair dye material used for evaluation was dissolved and washed away. Further, washing with a shampoo and rinsing were repeated twice, followed by drying. In addition, hair dyes other than the film-like hair dye material of the present invention are appropriately dyed and allowed to stand for 15 minutes, and then the entire hair is rinsed with warm water, washed twice with shampoo, rinsed and dried. It was.
(染毛性)
染毛後の毛髪をパネラー4名が目視にて評価した。評価基準として以下に示す3段階とした。
「染毛性」 ◎:とても良い
○:良い
×:悪い
(Hair-dyeing)
Four panelists visually evaluated the hair after dyeing. The following three levels were used as evaluation criteria.
“Hair-dyeing” ◎: Very good
○: Good
×: Bad
(染毛時の頭皮への色移り)
染毛後、15分経過した後の頭皮への染毛剤の垂れ具合をパネラー4名が目視にて評価した。評価基準として以下に示す3段階とした。地肌への色移りを、地肌への垂れによる汚れの程度の指標とした。色移りが少ないほど地肌への垂れが少なく、汚れも生じない。
「色移り」 ◎:色移りがみられない
○:僅かに色移りあり
×:色移りあり
(Color transfer to the scalp during hair dyeing)
Four panelists evaluated visually how the hair dye hanged onto the scalp after 15 minutes had passed since hair dyeing. As evaluation criteria, the following three stages were used. The color transfer to the background was used as an index of the degree of contamination due to dripping on the background. The less color transfer, the less dripping on the background, and no stains.
“Color transfer” ◎: No color transfer
○: Slight color transfer
×: Color transfer
(染毛剤の溶解性)
染毛後、15分経過後、温水で洗い流す際に、水溶性樹脂層の溶解具合をパネラー4名が目視および手で触れたときの感覚にて評価した。評価基準として以下に示す3段階とした。溶解性が高いほど、地肌が汚れにくく、快適に使用できることの指標とした。
「残渣」 ◎:残渣もなく、手に粘りも感じられない
○:残渣はないものの、手に粘りが感じられる
×:残渣がある
(Solubility of hair dye)
After 15 minutes from the hair dyeing, when the water-soluble resin layer was washed away with warm water, the dissolution state of the water-soluble resin layer was evaluated visually and by the feeling when the four panelists touched it. As evaluation criteria, the following three stages were used. The higher the solubility, the less dirty the background becomes and an indicator that it can be used comfortably.
“Residue” ◎: No residue, no stickiness in hand
○: Although there is no residue, the hand feels sticky
×: There is a residue
表1に示すフィルム状染毛材料を調製した。実施例1〜8は、水溶性樹脂中に染毛剤を練りこんで調製して試料を得た。
樹脂層に関して実施例1〜5に記載のPVAは日本酢ビ・ボパール社製JP18(ケン化度88モル%、重合度1800)であり、実施例8にて使用したPVAは日本酢ビ・ボパール社製JR05(ケン化度72モル%、重合度600)である。
表中の支持体層以外の欄の( )外の数字は重量部を示す。
可塑剤に関してPEGに続く数値は重合度を示している。
表中、支持体の欄の数値はその支持体の厚み(μm)を示す。
Film-like hair dye materials shown in Table 1 were prepared. Examples 1 to 8 were prepared by kneading a hair dye in a water-soluble resin.
Regarding the resin layer, PVA described in Examples 1 to 5 is JP18 (Saponification degree: 88 mol%, polymerization degree: 1800) manufactured by Nippon Vinegar Bhopard Co., and PVA used in Example 8 is Nippon Vinegar Bhopard. JR05 (degree of saponification 72 mol%, degree of polymerization 600).
The numbers outside () in the columns other than the support layer in the table indicate parts by weight.
The value following PEG for the plasticizer indicates the degree of polymerization.
In the table, the numerical value in the column of the support indicates the thickness (μm) of the support.
表2に示すフィルム状染毛材料の試料に用いた。
上記の実施例及び比較例の結果をみると、染毛性及び残渣に関しては実施例及び比較例共に同程度であるが、色移りについては、実施例1〜4、6〜8は色移りが無く、実施例5のみがわずかに色移りがみられた程度であったが、比較例1及び2については色移りがみられたので、染毛剤が垂れて地肌を汚していたことがわかる。
この実施例と比較例の結果の違いは、本発明による染毛材料が固体であるフィルムの表面から均一に髪に対して染色を行うものであり、染色しながら髪に浸透するのに対し、比較例1及び2の染毛剤は髪に浸透した後に染色を行うという染色の機構が異なることに由来する。
実施例2、3、5、及び8は支持体の厚さが75μm又は100μmと厚いことが共通し、染毛性がとても良いことはその支持体の厚さに起因する可能性がある。
実施例3は染料である赤色106号が3と他の実施例にて使用した赤色106号よりも多く、実施例5は赤色76号が1.5と実施例4にて使用した赤色76号の量よりも多いことにより、わずかに色移りしたものと考えられるが、それでも比較例1及び2よりも明らかに良好な結果であった。
実施例4及び5はグリセリンやジグリセリンの量が5と少なく、他の実施例にて使用したグリセリンの量よりも少量であったことも影響して、温水で洗い流す際に残渣はないものの、手に粘りが感じられる結果になった。
Looking at the results of the above Examples and Comparative Examples, both the Examples and the Comparative Examples are about the same in terms of hair dyeing properties and residues, but with regard to the color transfer, Examples 1-4 and 6-8 have a color transfer. None, only Example 5 had a slight color transfer, but since Comparative Examples 1 and 2 had a color transfer, it was found that the hair dye dripped and soiled the background. .
The difference between the results of this example and the comparative example is that the hair dye material according to the present invention uniformly dyes the hair from the surface of the film that is solid, whereas it penetrates into the hair while dyeing, The hair dyes of Comparative Examples 1 and 2 are derived from the different dyeing mechanisms of dyeing after penetrating into the hair.
In Examples 2, 3, 5, and 8, it is common that the thickness of the support is as thick as 75 μm or 100 μm, and the very good hair dyeing property may be attributed to the thickness of the support.
In Example 3, red No. 106, which is a dye, is more than 3 and Red No. 106 used in the other examples, and in Example 5, Red No. 76 is 1.5 and Red No. 76 used in Example 4 is used. It is considered that the color was slightly transferred due to being larger than the above amount, but it was still clearly better than Comparative Examples 1 and 2.
In Examples 4 and 5, the amount of glycerin and diglycerin is as small as 5, which is less than the amount of glycerin used in other examples, although there is no residue when rinsed with warm water, The result was sticky hands.
Claims (5)
The method of sticking the film-like hair dye material in any one of Claims 1-4 to hair, and dyeing hair.