JP2014098098A - Solid fuel, method for producing the same and method for producing mixed fuel - Google Patents
Solid fuel, method for producing the same and method for producing mixed fuel Download PDFInfo
- Publication number
- JP2014098098A JP2014098098A JP2012250675A JP2012250675A JP2014098098A JP 2014098098 A JP2014098098 A JP 2014098098A JP 2012250675 A JP2012250675 A JP 2012250675A JP 2012250675 A JP2012250675 A JP 2012250675A JP 2014098098 A JP2014098098 A JP 2014098098A
- Authority
- JP
- Japan
- Prior art keywords
- solid fuel
- biomass
- coal
- binder
- fuel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、バイオマスを用いた固形燃料、その製造方法及びこれを用いた混合燃料の製造方法に関する。 The present invention relates to a solid fuel using biomass, a method for producing the same, and a method for producing a mixed fuel using the same.
製紙産業においては、資源の有効活用や環境への負荷低減等の観点から種々のリサイクルが行われている。このリサイクルとしては、古紙パルプの再利用を始め、古紙に含まれる填料等の再利用、製紙スラッジの再利用等が行われている(特開2007−120159号公報及び特開2003−13069号公報参照)。 In the paper industry, various types of recycling are performed from the viewpoint of effective use of resources and reduction of environmental load. As this recycling, reuse of waste paper pulp, reuse of fillers contained in waste paper, reuse of papermaking sludge, and the like are carried out (JP 2007-120159 A and JP 2003-13069 A). reference).
このように製紙産業全体を俯瞰すると、製紙工場での製紙段階以降においては、システムが確立し、高いレベルでのリサイクルが行われている。しかし、より有効な資源の活用を進める観点からは、製紙工場に主原料たる木材パルプが搬入される以前の段階におけるリサイクルを進める必要がある。すなわち具体的には、間伐材や樹皮チップの有効活用を検討する必要がある。 As described above, when the paper industry as a whole is viewed, after the paper manufacturing stage in the paper factory, a system is established and recycling is performed at a high level. However, from the viewpoint of promoting more effective use of resources, it is necessary to proceed with recycling at the stage before wood pulp, which is the main raw material, is carried into a paper mill. Specifically, it is necessary to consider the effective use of thinned wood and bark chips.
この間伐材や樹皮チップ等の木材は、いわゆるバイオマス燃料としてそのまま利用することもできるが、焙焼(焙煎、半炭化、トレファクション等とも称される。)することにより発熱量を高めた燃料として利用する技術が開発されている(特許第4136772号公報参照)。このように焙焼された木材は、作業性や運搬性等を向上させるために、一般的なバイオマス燃料と同様に通常ペレット化される。しかし、焙焼された木材は水分量が少ないこと等が原因となって成型性が悪いため、運搬又は作業中に砕けやすく、取扱性が悪い。 Wood such as thinned wood and bark chips can be used as it is as so-called biomass fuel, but it is a fuel whose calorific value has been increased by roasting (also called roasting, semi-carbonization, refracting, etc.). Has been developed (see Japanese Patent No. 4136772). The wood thus roasted is usually pelletized in the same manner as general biomass fuels in order to improve workability and transportability. However, roasted wood has poor moldability due to a small amount of water, etc., and therefore it is easy to break during transportation or work, and handling properties are poor.
また、焙焼された木材を用いより高熱量かつ安定的な燃焼を行うため、石炭と混合して粉砕したものを燃焼させることが行われている。しかし、焙焼された木材と石炭とは、サイズ、密度、硬さ等が大きく異なるため、均一に混合及び粉砕することが困難となり、石炭と焙焼された木材との混合ムラに起因する発熱量の変動や操業の安定化を損なう問題を生じる。 Moreover, in order to perform more high calorie | heat amount and stable combustion using the roasted timber, what was pulverized by mixing with coal is burned. However, roasted wood and coal differ greatly in size, density, hardness, etc., making uniform mixing and pulverization difficult, and heat generated due to uneven mixing of coal and roasted wood. It causes problems that impair fluctuations in quantity and stabilization of operations.
本発明は、上述のような事情に基づいてなされたものであり、焙焼されたバイオマスを用いた、取扱性に優れかつ石炭と混合した場合の粉砕性も良好で、均一な石炭との混合が図れる固形燃料、このような固形燃料の製造方法、及び上記固形燃料を用いた混合燃料の製造方法を提供することを目的とする。 The present invention has been made on the basis of the circumstances as described above, and it is excellent in handling property when roasted biomass is used and has good grindability when mixed with coal, and is mixed with uniform coal. It is an object of the present invention to provide a solid fuel capable of achieving the above, a method for producing such a solid fuel, and a method for producing a mixed fuel using the solid fuel.
上記課題を解決するためになされた発明は、
焙焼されたバイオマスとバインダーとを含む固形燃料である。
The invention made to solve the above problems is
It is a solid fuel containing roasted biomass and a binder.
当該固形燃料は、焙焼されたバイオマスと共にバインダーを含むため、成型性に優れ、強度等を高めることができる。従って、当該固形燃料は、運搬作業中などにおいて粉砕し難く取扱性に優れる。また、当該固形燃料は、バインダーを用いることで石炭と同程度の強度に成型することができ、石炭と混合し、共に粉砕する際の粉砕性、混合性も良好である。 Since the solid fuel contains a binder together with the roasted biomass, it is excellent in moldability and can increase strength and the like. Therefore, the solid fuel is not easily pulverized during transportation work or the like and has excellent handleability. Moreover, the said solid fuel can be shape | molded by the intensity | strength comparable to coal by using a binder, and the pulverization property and mixing property at the time of mixing with coal and grind | pulverizing together are also favorable.
焙焼されたバイオマスの成形には、バインダーレスで高温高圧下で成形する方法、フェノール類をバインダーと用いる方法が検討されるが、新たな設備投資や薬品購入が必要とされる問題が生じるため、パルプ工場内で生じる副産物や既存購入薬品の援用を考慮し焙焼されたバイオマスの成形に好適なバインダーとして、木材チップを蒸解する工程で生じる所謂リグニンを含む黒液と紙力剤やサイズ剤として用いられている澱粉が好適に選択される。そのため、上記バインダーがリグニンを含む黒液及び/又は澱粉を含有することが好ましい。このようにバインダーとしてリグニンを含む黒液や澱粉を用いることで、パルプ工場における副産物の利用や既存購入薬品の援用とともに成型性をより高めることができる。また、バインダーとしてもリグニンを含む黒液や澱粉といったバイオマスを用いることで、資源の有効利用を図ることができる。さらに、リグニンを含む黒液や澱粉を用い押出成型により成型する場合、押出成型の際にリグニンの溶融や澱粉の糊化を利用するため、バインダー機能をより効果的に発現させることができ、より強固な固形燃料を得ることができる。なお、「及び/又は」とは、両方或いはいずれか一方を意味する。 For the molding of roasted biomass, methods of molding without binders at high temperature and high pressure, and methods of using phenols with binders are considered, but problems arise that require new equipment investment and chemical purchases. , Black liquor and paper strength agent and sizing agent containing so-called lignin produced in the process of digesting wood chips as a binder suitable for the formation of roasted biomass in consideration of the by-products produced in pulp mills and the use of existing purchased chemicals The starch used as is preferably selected. Therefore, it is preferable that the binder contains black liquor and / or starch containing lignin. Thus, by using the black liquor and starch containing lignin as a binder, the moldability can be further enhanced with the use of by-products in the pulp mill and the assistance of existing purchased chemicals. Further, by using biomass such as black liquor or starch containing lignin as a binder, it is possible to effectively use resources. Furthermore, when molding by extrusion molding using black liquor or starch containing lignin, the binder function can be expressed more effectively because of the melting of lignin and starch gelatinization during extrusion molding, A strong solid fuel can be obtained. Note that “and / or” means both or one of them.
上記焙焼されたバイオマス100質量部に対するバインダーの含有量が、固形分換算で0.01質量部以上10質量部以下であることが好ましい。過剰なバインダーの含有は、成型物の形状維持や成型物の硬さを低下させる原因になり、取扱性に優れかつ石炭と混合した場合の粉砕性も良好で、均一な石炭との混合が図れる固形燃料が得られ難くなるため、このような範囲の量のバインダーを用いることで、より良好な成型性等を発揮することができる。 It is preferable that the content of the binder with respect to 100 parts by mass of the roasted biomass is 0.01 parts by mass or more and 10 parts by mass or less in terms of solid content. Excessive binder content causes the shape of the molded product to be maintained and the hardness of the molded product to be reduced. It is easy to handle and has good grindability when mixed with coal, allowing uniform mixing with coal. Since it becomes difficult to obtain solid fuel, better moldability and the like can be exhibited by using an amount of the binder in such a range.
上記課題を解決するためになされた別の発明は、
バイオマスを焙焼する工程、
焙焼されたバイオマスにバインダーを混合する工程、及び
上記焙焼されたバイオマスをバインダーと共に成型する工程
を有する固形燃料の製造方法である。
Another invention made to solve the above problems is as follows:
A process of roasting biomass;
A method for producing a solid fuel, comprising: mixing a binder with roasted biomass; and molding the roasted biomass together with a binder.
当該製造方法によれば、焙焼されたバイオマスをバインダーと共に成型するため、良好な成型性を有し、取扱性に優れかつ石炭と混合した場合の粉砕性も良好で、均一な石炭との混合が図れる優れた取扱性や高い強度を有する固形燃料を得ることができる。 According to the production method, since the roasted biomass is molded together with the binder, it has good moldability, excellent handleability and good pulverization when mixed with coal, and is mixed with uniform coal. Therefore, it is possible to obtain a solid fuel having excellent handleability and high strength.
上記課題を解決するためになされた別の発明は、
当該固形燃料と石炭とを混合する工程、及び
混合された上記固形燃料と石炭とを粉砕する工程
を有する混合燃料の製造方法である。
Another invention made to solve the above problems is as follows:
A method for producing a mixed fuel, comprising: a step of mixing the solid fuel and coal; and a step of pulverizing the mixed solid fuel and coal.
当該製造方法によれば、強度が高い固形燃料と石炭とを混合して粉砕するため、これら2種の混合物が偏り無く粉砕された混合燃料を得ることができる。 According to the manufacturing method, since the solid fuel with high strength and coal are mixed and pulverized, it is possible to obtain a mixed fuel in which these two kinds of mixtures are pulverized without unevenness.
以上説明したように、本発明の固形燃料は、取扱性に優れ、かつ石炭と混合した場合の粉砕性も高めることができる。また、本発明の固形燃料の製造方法は、このような固形燃料を得ることができる。本発明の混合燃料の製造方法は、石炭と上記固形燃料をむら無く粉砕することができ、均一な石炭との混合が図れるため燃焼性等が安定した良好な混合燃料を得ることができる。従って、本発明によれば、チップや廃材、間伐材等の従来活用が十分に進んでいなかった木材、さらには木材などの繊維分を含有する製紙スラッジ等の有効活用を図ることができる。 As described above, the solid fuel of the present invention is excellent in handleability and can improve pulverizability when mixed with coal. Moreover, the manufacturing method of the solid fuel of this invention can obtain such a solid fuel. The method for producing a mixed fuel according to the present invention can pulverize coal and the above solid fuel evenly, and can achieve uniform mixing with coal, so that a good mixed fuel with stable combustibility and the like can be obtained. Therefore, according to the present invention, it is possible to effectively use wood, which has not been sufficiently utilized in the past, such as chips, waste wood, and thinned wood, and papermaking sludge containing fibers such as wood.
以下、本発明の固形燃料、この固形燃料の製造方法、及びこの固形燃料を用いた混合燃料の製造方法の実施の形態を詳説する。 Embodiments of a solid fuel, a method for producing the solid fuel, and a method for producing a mixed fuel using the solid fuel will be described in detail below.
<固形燃料>
本発明の固形燃料は、焙焼されたバイオマスとバインダーとを含む成型物である。当該固形燃料は、このように焙焼されたバイオマスと共にバインダーを含むため、成型性に優れ、強度等を高めることができる。従って、当該固形燃料は、運搬作業中などにおいて粉砕し難く取扱性に優れる。また、当該固形燃料は、バインダーを用いることで石炭と同程度の強度に成型することができ、石炭と混合し、共に粉砕する際の粉砕性も良好である。
<Solid fuel>
The solid fuel of the present invention is a molded product containing roasted biomass and a binder. Since the solid fuel contains a binder together with the roasted biomass in this way, the solid fuel is excellent in moldability and can increase strength and the like. Therefore, the solid fuel is not easily pulverized during transportation work or the like and has excellent handleability. Moreover, the said solid fuel can be shape | molded by the same intensity | strength as coal by using a binder, and the pulverization property at the time of mixing with coal and grind | pulverizing together is also favorable.
(焙焼されたバイオマス)
上記バイオマスとは、化石燃料以外の生物由来の資源をいい、間伐材、剪定枝、廃材、樹皮チップ、その他の木材、竹、草、やし殻、パームオイル残渣、野菜、果実、食品残渣、製紙スラッジ、汚泥等を挙げることができる。これらのバイオマスの中でも、間伐材、剪定枝、廃材、樹皮チップ、その他の木材等の木質系バイオマスが好ましく、樹皮チップがさらに好ましい。このような材料を用いることで、製紙工程において十分に活用されていなかった資源の有効活用を図ることができる。樹脂チップとしては、特に限定されず、例えば杉、松、檜、ラワン、チーク等から得られるものが挙げられる。
(Roasted biomass)
Biomass refers to biological resources other than fossil fuels, such as thinned wood, pruned branches, waste wood, bark chips, other wood, bamboo, grass, coconut shells, palm oil residues, vegetables, fruits, food residues, Examples include papermaking sludge and sludge. Among these biomass, woody biomass such as thinned wood, pruned branches, waste wood, bark chips, and other wood is preferable, and bark chips are more preferable. By using such a material, it is possible to effectively use resources that have not been sufficiently utilized in the papermaking process. The resin chip is not particularly limited, and examples thereof include those obtained from cedar, pine, firewood, lawan, teak and the like.
上記焙焼とは、バイオマスを140℃以上350℃以下で熱処理することをいい、この熱処理温度としては240℃以上280℃以下が好ましい。焙焼時間としては、特に限定されず、通常5分以上10時間以下、好ましくは10分以上8時間以下である。この焙焼により、有機物が部分的に分解し、質量(乾燥基準)が初期質量の70%程度となる。また、焙焼されたバイオマスは疎水性が高まるため、高い保存安定性を有し、長期保存等に優れる。 The roasting means that the biomass is heat-treated at 140 ° C. or higher and 350 ° C. or lower, and the heat treatment temperature is preferably 240 ° C. or higher and 280 ° C. or lower. The roasting time is not particularly limited, and is usually 5 minutes to 10 hours, preferably 10 minutes to 8 hours. By this roasting, organic substances are partially decomposed, and the mass (dry basis) becomes about 70% of the initial mass. Moreover, since the roasted biomass has increased hydrophobicity, it has high storage stability and is excellent in long-term storage and the like.
焙焼に付す前のバイオマスの総発熱量は、特に限定されず、通常11MJ/kg以上30MJ/kg以下、好ましくは13MJ/kg以上28MJ/kg以下である。総発熱量が上記範囲内である場合、上記成型性及び粉砕性に加えて、固形燃料の燃焼性も高められる傾向がある。総発熱量が上記上限を超えると、焙焼に製造コストが多く必要となる場合がある。逆に、総発熱量が上記下限未満であると、固形燃料の燃焼性が低下する場合がある。 The total calorific value of biomass before being subjected to roasting is not particularly limited, and is usually 11 MJ / kg or more and 30 MJ / kg or less, preferably 13 MJ / kg or more and 28 MJ / kg or less. When the total calorific value is within the above range, in addition to the moldability and grindability, the combustibility of the solid fuel tends to be improved. When the total calorific value exceeds the above upper limit, the production cost may be required for roasting. Conversely, if the total calorific value is less than the lower limit, the combustibility of the solid fuel may be reduced.
(バインダー)
上記バインダーは焙焼された上記バイオマスの成型性を高めるために含有される成分である。上記バインダーとしては、上記効果を奏するものであれば特に限定されず、リグニンを含む黒液、澱粉、ポリビニルアルコール、その他の熱可塑性樹脂等を挙げることができ、これらを2種以上を組み合わせることもできるが、これらの中でも、リグニンを含む黒液及び/又は澱粉が好ましい。バインダーとしてリグニンを含む黒液及び/又は澱粉を用いることで、取扱性に優れかつ石炭と混合した場合の粉砕性も良好で、均一な石炭との混合が図れる固形燃料を得ることができる。また、バインダーとしてもパルプ工場の副産物であるリグニンを含む黒液や紙力剤やサイズ剤で用いられている澱粉の援用といったバイオマスを用いることで、資源の有効利用を図ることができる。さらに、リグニンを含む黒液を用い押出成型により成型する場合、押出成型の際に黒液中のリグニンが溶融するため、澱粉を用いた場合は澱粉の糊化によりバインダー機能をより効果的に発現させることができ、より強固な固形燃料を得ることができる。上記バインダーは一種又は二種以上を混合して用いることができる。
(binder)
The binder is a component contained in order to improve the moldability of the roasted biomass. The binder is not particularly limited as long as it exhibits the above-mentioned effects, and examples thereof include black liquor containing lignin, starch, polyvinyl alcohol, other thermoplastic resins, and the like. Among these, black liquor and / or starch containing lignin is preferable among these. By using black liquor and / or starch containing lignin as a binder, it is possible to obtain a solid fuel that has excellent handleability and good pulverizability when mixed with coal, and can be uniformly mixed with coal. Further, by using biomass such as black liquor containing lignin, which is a by-product of a pulp mill, and a starch used in a paper strength agent and a sizing agent as a binder, resources can be effectively used. In addition, when molding by extrusion using black liquor containing lignin, the lignin in the black liquor melts at the time of extrusion molding, so when starch is used, the binder function is more effectively expressed by starch gelatinization. And a stronger solid fuel can be obtained. The said binder can be used 1 type or in mixture of 2 or more types.
上記澱粉としては、グラフト化澱粉、リン酸エステル化澱粉、カチオン化澱粉、ヒドロキシプロピル澱粉、カルボキシル澱粉、酢酸澱粉等の各種加工澱粉、コーンスターチ、馬鈴薯澱粉(ジャガイモ)等が挙げられ、これらを一種又は二種以上を混合して用いることができる。特に好ましくは、安価で糊化温度が高い穀類澱粉、特にコーンスターチが押出成形時の高温での糊化と澱粉粒子が他の澱粉と比べ比較的小粒径で粘性が低いため、焙焼されたバイオマスとの混合に好ましい。 Examples of the starch include grafted starch, phosphate esterified starch, cationized starch, hydroxypropyl starch, carboxyl starch, acetate starch and other processed starches, corn starch, potato starch (potato), and the like. Two or more kinds can be mixed and used. Particularly preferably, cereal starches that are inexpensive and have a high gelatinization temperature, especially corn starch, are gelatinized at a high temperature during extrusion, and the starch particles are roasted because they have a relatively small particle size and low viscosity compared to other starches. Preferred for mixing with biomass.
上記リグニンを含む黒液としては、クラフトパルプ製造工場の副産物である黒液が用いられ、針葉樹クラフトパルプ製造工程にて得られる針葉樹クラフトパルプ系の黒液、広葉樹クラフトパルプ系の黒液が挙げられ、これらを一種又は二種以上を混合して用いることができる。特にクラフトパルプ蒸解工程における歩留り向上剤として添加されているアンスラキノン系パルプ歩留向上剤(環状ケト化合物)を含む黒液は、焙焼されたバイオマスの成形に有効であり、理由は明確ではないがアンスラキノン系パルプ歩留向上剤にて脱リグニンが促進され黒液中のリグニン含有量が多いためと推測される。 As the black liquor containing lignin, black liquor, which is a by-product of a kraft pulp manufacturing plant, is used. These can be used alone or in combination of two or more. In particular, black liquor containing anthraquinone pulp yield improver (cyclic keto compound) added as a yield improver in the kraft pulp cooking process is effective in forming roasted biomass, and the reason is not clear. However, it is assumed that delignification is promoted by the anthraquinone-based pulp yield improver and the lignin content in the black liquor is large.
上記バインダーとして純粋なリグニンを用いることもできるが、リグニンを含む黒液をリグニンの代用として用いることができる。黒液とは、木材チップ等からパルプを作る工程において、木材チップ等が化学的に分解・分離する際に発生する黒又は褐色の液体であり、成分は主にリグニン、樹脂成分及び薬品(蒸解剤等)である。 Pure lignin can be used as the binder, but black liquor containing lignin can be used as a substitute for lignin. Black liquor is a black or brown liquid generated when wood chips, etc. are chemically decomposed and separated in the process of making pulp from wood chips, etc., and the components are mainly lignin, resin components and chemicals (digestion). Agent).
上記黒液の種類としては、例えば蒸解に使用した直後の黒液や濃縮処理を施した黒液等が挙げられるが、これらのなかでも蒸解直後の比較的粘度が低い黒液が好ましく、L材(広葉樹)と比べ比較的リグニン含有量が多いN材(針葉樹)をKP蒸解して得られる針葉樹クラフトパルプ系の黒液がより好ましい。 Examples of the type of black liquor include black liquor immediately after being used for cooking and black liquor having been subjected to concentration treatment. Among these, black liquor having a relatively low viscosity immediately after cooking is preferable. A coniferous kraft pulp black liquor obtained by KP digestion of N material (coniferous tree) having a relatively high lignin content compared to (hardwood) is more preferred.
黒液濃度は、特に限定されず、通常1質量%以上60質量%以下、好ましくは2質量%以上55質量%以下である。黒液固形分中のリグニン含有量も、特に限定されず、通常1質量%以上50質量%以下、好ましくは2質量%以上40質量%以下である。黒液に含まれる液体としては、特に限定されず、例えば水、少量の水溶性有機溶媒を含む水溶液等が挙げられる。 The black liquor concentration is not particularly limited, and is usually 1% by mass to 60% by mass, and preferably 2% by mass to 55% by mass. The lignin content in the black liquor solid content is also not particularly limited, and is usually 1% by mass to 50% by mass, preferably 2% by mass to 40% by mass. The liquid contained in the black liquor is not particularly limited, and examples thereof include water and an aqueous solution containing a small amount of a water-soluble organic solvent.
上記焙焼されたバイオマス100質量部に対するバインダーの含有量(固形分換算)としては、0.01質量部以上10質量部以下が好ましく、0.1質量部以上5質量部以下がより好ましい。このような範囲の量のバインダーを用いることで、より良好な成型性等を発揮することができる。 The binder content (in terms of solid content) with respect to 100 parts by mass of the roasted biomass is preferably 0.01 parts by mass or more and 10 parts by mass or less, and more preferably 0.1 parts by mass or more and 5 parts by mass or less. By using the binder in such an amount, better moldability and the like can be exhibited.
バインダーの含有量が上記範囲未満の場合は、十分な成型性が発揮されない場合がある。逆に、バインダーの含有量が上記範囲を超える場合は、強固に接着しすぎて粉砕性が低下する場合がある。 When the content of the binder is less than the above range, sufficient moldability may not be exhibited. On the contrary, when the content of the binder exceeds the above range, it may adhere too strongly and the grindability may be lowered.
(他の成分)
当該固形燃料には、本発明の目的を損なわない範囲において、上記焙焼されたバイオマス及びバインダー以外に、その他の原料を加えることができる。その他の原料としては、古紙パルプ等のパルプ繊維や合成繊維等の繊維状物質や、その他、製紙スラッジ等が挙げられるが、これらのなかでも繊維状物質が好ましい。繊維状物質を含有させることで、当該固形燃料の成型性をさらに高めることができる。
(Other ingredients)
In addition to the roasted biomass and binder, other raw materials can be added to the solid fuel as long as the object of the present invention is not impaired. Examples of other raw materials include fibrous materials such as pulp fibers such as waste paper pulp and synthetic fibers, and other papermaking sludges. Among these, fibrous materials are preferable. By including the fibrous substance, the moldability of the solid fuel can be further enhanced.
(形状等)
当該固形燃料の密度としては、0.6g/cm3以上2.0g/cm3以下が好ましく、0.8g/cm3以上1.8g/cm3以下がより好ましい。当該固形燃料の密度を上記範囲とすることで、石炭との密度差が小さくなる。当該固形燃料は、石炭の代替として好適に用いることができるため、石炭と混合してボイラ等の燃料に用いることが想定される。その場合、当該固形燃料と石炭とは、後に詳述するように、ミル等で押しつぶされながら微粉化される。そのため、当該固形燃料と石炭との密度差が小さい方が、二者をより均一に混合することができ、かつ、同等の速度で粉砕することができる。従って、当該固形燃料の密度を上記範囲とすることで、熱量がより均一化され、安定的な燃焼性を発揮することができる。なお、当該固形燃料の密度が上記下限未満の場合は、混合及び粉砕の際に石炭との分離等が生じ、均一かつ効率的な混合及び粉砕が困難となる場合がある。逆に、当該固形燃料の密度が上記上限を超えると、成型物が粉砕されにくくなり、石炭との混合が不均一となる場合がある。
(Shape, etc.)
The density of the solid fuel is preferably 0.6 g / cm 3 or more and 2.0 g / cm 3 or less, and more preferably 0.8 g / cm 3 or more and 1.8 g / cm 3 or less. By setting the density of the solid fuel in the above range, the density difference from coal is reduced. Since the solid fuel can be suitably used as an alternative to coal, it is assumed that it is mixed with coal and used as fuel for boilers and the like. In this case, the solid fuel and coal are pulverized while being crushed by a mill or the like, as will be described in detail later. Therefore, the one where the density difference of the said solid fuel and coal is smaller can mix two more uniformly, and can grind | pulverize at an equivalent speed | rate. Therefore, by setting the density of the solid fuel within the above range, the amount of heat can be made more uniform and stable combustibility can be exhibited. When the density of the solid fuel is less than the lower limit, separation from coal may occur during mixing and pulverization, and uniform and efficient mixing and pulverization may be difficult. On the contrary, when the density of the solid fuel exceeds the above upper limit, the molded product becomes difficult to be pulverized, and the mixing with coal may be uneven.
当該固形燃料の形状としては、特に限定されず、例えば球状、柱状等が挙げられるが、柱状が好ましい。上記柱状としては、例えば円柱状、四角柱状、三角柱状等が挙げられるが、円柱状が好ましい。このように当該固形燃料の形状を柱状とすることで、石炭と混合する場合の粉砕を容易に行うことができる。 The shape of the solid fuel is not particularly limited, and examples thereof include a spherical shape and a columnar shape, and a columnar shape is preferable. Examples of the columnar shape include a columnar shape, a quadrangular columnar shape, and a triangular columnar shape, and a columnar shape is preferable. Thus, by making the shape of the solid fuel into a columnar shape, pulverization when mixing with coal can be easily performed.
当該固形燃料のアスペクト比としては、2以上10以下が好ましく、3以上8以下がさらに好ましい。当該固形燃料のアスペクト比が上記下限未満の場合、体積に対する面積比が小さくなるため、中心部が燃え残りやすく十分な発熱量を得られないおそれがある。逆に、当該固形燃料のアスペクト比が上記上限を超えると、成型が困難となったり、運搬等の際に折れが生じたりするなど、取扱性が低下するおそれがある。ここで、アスペクト比とは、底面の直径に対する高さの比(高さ/直径)をいう。なお、底面が円ではない場合、直径は2(S/π)1/2(Sは底面積)で求められる値とする。 The aspect ratio of the solid fuel is preferably 2 or more and 10 or less, more preferably 3 or more and 8 or less. When the aspect ratio of the solid fuel is less than the above lower limit, the area ratio with respect to the volume is small, so that the central portion is likely to remain unburned and there is a fear that a sufficient calorific value cannot be obtained. On the other hand, when the aspect ratio of the solid fuel exceeds the above upper limit, the handleability may be deteriorated, such as difficulty in molding or breakage during transportation. Here, the aspect ratio refers to the ratio of the height to the diameter of the bottom surface (height / diameter). When the bottom surface is not a circle, the diameter is 2 (S / π) 1/2 (S is the bottom area).
当該固形燃料の断面積としては、12mm2以上180mm2以下が好ましく、24mm2以上120mm2以下がさらに好ましい。また、当該固形燃料の高さとしては、4mm以上60mm以下が好ましく、8mm以上40mm以下がさらに好ましい。このように当該固形燃料のサイズを上記範囲とすることで、取扱性を高めつつ、混合及び粉砕をより均一に行うことができる。当該固形燃料の断面積及び高さが上記下限未満の場合は、サイズが小さくなりすぎて取扱性が低下する場合がある。逆に、当該固形燃料の断面積及び高さが上記上限を超えると石炭との均一な混合が困難となる場合がある。 The cross-sectional area of the solid fuel is preferably 12 mm 2 or more and 180 mm 2 or less, and more preferably 24 mm 2 or more and 120 mm 2 or less. The height of the solid fuel is preferably 4 mm or more and 60 mm or less, and more preferably 8 mm or more and 40 mm or less. Thus, by making the size of the solid fuel in the above range, mixing and pulverization can be performed more uniformly while improving the handleability. When the cross-sectional area and height of the solid fuel are less than the above lower limit, the size may become too small, and the handleability may deteriorate. Conversely, if the cross-sectional area and height of the solid fuel exceed the above upper limit, uniform mixing with coal may be difficult.
当該固形燃料の水分量としては、0.01質量%以上5質量%以下が好ましい。このように低い水分量とすることで、高い燃焼性を発揮させることができる。この水分量が5質量%を超えると燃焼性が低下する場合がある。逆に、この水分量が0.01質量%未満であると成型性や粉砕性が低下する場合がある。 The water content of the solid fuel is preferably 0.01% by mass or more and 5% by mass or less. By setting the moisture content to be low in this way, high combustibility can be exhibited. When this moisture content exceeds 5 mass%, combustibility may fall. On the other hand, if the water content is less than 0.01% by mass, moldability and pulverization may be deteriorated.
当該固形燃料の総発熱量は、特に限定されず、通常13MJ/kg以上32MJ/kg以下、好ましくは15MJ/kg以上30MJ/kg以下である。固形燃料の総発熱量が上記範囲内である場合、上記成型性及び粉砕性に加えて、固形燃料の燃焼性を高められる傾向がある。総発熱量が上記上限を超えると、固形燃料の製造コストが多く必要となる場合がある。逆に、総発熱量が上記下限未満であると、固形燃料の燃焼性が低下する場合がある。 The total calorific value of the solid fuel is not particularly limited, and is usually 13 MJ / kg or more and 32 MJ / kg or less, preferably 15 MJ / kg or more and 30 MJ / kg or less. When the total calorific value of the solid fuel is within the above range, in addition to the moldability and grindability, the combustibility of the solid fuel tends to be improved. If the total calorific value exceeds the above upper limit, the production cost of the solid fuel may be increased. Conversely, if the total calorific value is less than the lower limit, the combustibility of the solid fuel may be reduced.
このように当該固形燃料は、成型性に優れ、強度等を高めることができるため、運搬作業中などにおいて粉砕し難く取扱性に優れる。また、当該固形燃料は石炭と同程度の強度とすることができるため、石炭と混合し、石炭との混合状態で粉砕したりする場合の混合性や粉砕性を向上することができる。 Thus, since the said solid fuel is excellent in a moldability and can raise intensity | strength etc., it is hard to grind | pulverize during conveyance work etc., and is excellent in handleability. Moreover, since the said solid fuel can be made into the same intensity | strength as coal, the mixability and grindability at the time of mixing with coal and grind | pulverizing in a mixed state with coal can be improved.
<固形燃料の製造方法>
当該固形燃料は、例えば
バイオマスを焙焼する工程、
焙焼されたバイオマスにバインダーを混合する工程、及び
上記焙焼されたバイオマスをバインダーと共に成型する工程
を有する製造方法により製造することができる。
<Method for producing solid fuel>
The solid fuel is, for example, a process of roasting biomass,
It can be produced by a production method comprising a step of mixing a binder with the baked biomass and a step of molding the baked biomass together with the binder.
当該製造方法によれば、焙焼されたバイオマスをバインダーと共に成型するため、良好な成型性を有し、優れた取扱性や高い強度を有する固形燃料を得ることができる。以下、各工程について説明する。 According to the manufacturing method, since the roasted biomass is molded together with the binder, it is possible to obtain a solid fuel having good moldability and excellent handling properties and high strength. Hereinafter, each step will be described.
(1)焙焼工程
本工程ではバイオマスを焙焼する。上記焙焼は、公知の加熱(焙焼)装置を用いて行うことができ、例えば、固定式の箱型乾燥炉や、回転式の乾燥炉等を挙げることができる。これらの中でも、回転式の乾燥炉を用いることが好ましく、ロータリーキルンを用いることがさらに好ましい。ロータリーキルンは、通常、バイオマスが供給される筒と、この筒の内部に備えられ、バイオマスを送り出すスパイラルリフターとを有する。このようなロータリーキルンを用いることで、バイオマスを連続的に、焙焼及び冷却することができる。また、焙焼に先駆けて、バイオマスの水分量を減少させる乾燥も一体的に行うことができるため、設備費や製造コストの削減にも繋がる。さらに、ロータリーキルンは、通常、内部にバイオマスを撹拌・掻揚する並行リフターを有する。このようなロータリーキルンを用いることで、バイオマスの均一な焙焼や冷却等を行うことができる。
(1) Roasting process In this process, biomass is roasted. The roasting can be performed using a known heating (roasting) apparatus, and examples thereof include a fixed box-type drying furnace and a rotary drying furnace. Among these, it is preferable to use a rotary drying furnace, and it is more preferable to use a rotary kiln. The rotary kiln usually includes a cylinder to which biomass is supplied and a spiral lifter that is provided inside the cylinder and sends out the biomass. By using such a rotary kiln, biomass can be continuously roasted and cooled. Further, prior to roasting, drying that reduces the moisture content of biomass can also be performed integrally, leading to a reduction in equipment costs and manufacturing costs. Furthermore, the rotary kiln usually has a parallel lifter that stirs and rakes the biomass inside. By using such a rotary kiln, biomass can be uniformly roasted or cooled.
なお、この焙焼の際のバイオマスの雰囲気は、空気でよいが、低酸素濃度下で行うこともできる。低酸素濃度下で行うことで、バイオマスの燃焼が生じることを抑制することができる。この酸素濃度としては、例えば、5体積%以上15体積%以下とすることができる。 In addition, although the atmosphere of biomass in the case of this roasting may be air, it can also be performed under a low oxygen concentration. By performing under a low oxygen concentration, it is possible to suppress the combustion of biomass. As this oxygen concentration, it can be made into 5 volume% or more and 15 volume% or less, for example.
焙焼工程における工程温度は上述の熱処理温度が好ましい。焙焼工程における工程温度が上記範囲内である場合、バイオマスを十分に焙焼できる傾向がある。工程温度が上記上限を超えると、製造コストが多く必要となる場合がある。逆に、工程温度が上記下限未満であると、バイオマスの焙焼が不十分となる場合がある。 The process temperature in the roasting process is preferably the above heat treatment temperature. When the process temperature in the roasting process is within the above range, the biomass tends to be sufficiently roasted. If the process temperature exceeds the above upper limit, a large production cost may be required. Conversely, when the process temperature is lower than the lower limit, biomass roasting may be insufficient.
焙焼工程に供するバイオマスは、ある程度に粉砕されたものが好ましい。このバイオマスのサイズとしては、目開き50mmの篩を95質量%以上透過する粒径が好ましく、目開き25mmの篩を95質量%以上透過する粒径が好ましく、目開き10mmの篩を95質量%以上透過する粒径がさらに好ましい。このようなサイズのバイオマスを用いることで、内部まで十分にかつ均一に焙焼を行うことができる。 The biomass subjected to the roasting step is preferably pulverized to some extent. The size of the biomass is preferably a particle size that allows 95% by mass or more to pass through a sieve having an opening of 50 mm, preferably a particle size that allows 95% or more to pass through a sieve having an opening of 25 mm, and 95% by mass of a sieve having an opening of 10 mm. More preferably, the particle size that permeates is as described above. By using biomass of such a size, the inside can be roasted sufficiently and uniformly.
なお、この粉砕の手段としては、特に限定されず、公知の回転式カッターやハンマーミル等を用いることができる。 The pulverization means is not particularly limited, and a known rotary cutter, hammer mill, or the like can be used.
(2)成型工程
本工程では、上記焙焼工程により焙焼されたバイオマスをバインダーと共に成型する。このバイオマスとバインダーとの混合手段は、特に限定されず、公知の混合機、攪拌機、混練機等を用いて行うことができる。
(2) Molding process In this process, the biomass roasted by the roasting process is molded together with a binder. The mixing means of the biomass and the binder is not particularly limited, and can be performed using a known mixer, stirrer, kneader or the like.
成型工程に供されるバイオマスとバインダー等の混合物の水分量としては、0.1質量%以上20質量%以下が好ましく、1質量%以上15質量%以下がより好ましい。このようにバイオマス等の混合物中に上記範囲の水分を含有させておくことで、成型性を高めることができる。 The water content of the mixture of biomass and binder to be subjected to the molding step is preferably 0.1% by mass or more and 20% by mass or less, and more preferably 1% by mass or more and 15% by mass or less. Thus, moldability can be improved by containing the water | moisture content of the said range in mixtures, such as biomass.
この成型を行う装置としては、特に限定されないが、押出成型機を用いることが好ましい。押出成型機を用いることで、密度を高め、石炭に近い密度への成型物の調製が容易となり、石炭との均一混合性を高めることができる。 An apparatus for performing this molding is not particularly limited, but an extrusion molding machine is preferably used. By using an extrusion molding machine, the density is increased, the preparation of a molded product having a density close to that of coal is facilitated, and uniform mixing with coal can be enhanced.
押出成型機等を用いて成型を行う際の加熱温度としては、80℃以上220℃以下が好ましく、100℃以上150℃以下がより好ましい。バイオマスには、リグニン等の樹脂成分やヘミセルロースが含まれる。リグニンの軟化点は約150℃、ヘミセルロースの軟化点は約180℃とされている。そのため、例えば200℃を超える高温での成型は、リグニン以外にヘミセルロースまでが軟化してしまい、再度硬化することでバインダーとしての役割を果たし、成型物の強度を必要以上に高めてしまうため、粉砕性が低下するおそれがある。そこで、このように200℃以下、より好ましくは150℃以下で成型することで、主にリグニンのみがバインダーとしての役割を果たし、比較的密度が高くかつ脆い状態の成型物を得ることができ、石炭と共に容易に粉砕することができる。また、所定温度以上に加熱して成型することで、バイオマス中の水分が成型の際に蒸発し、得られる成型物の多孔質性を高めることができ、結果として、当該固形燃料の粉砕性を高めることができる。 The heating temperature at the time of molding using an extrusion molding machine or the like is preferably 80 ° C. or higher and 220 ° C. or lower, and more preferably 100 ° C. or higher and 150 ° C. or lower. Biomass contains resin components such as lignin and hemicellulose. The softening point of lignin is about 150 ° C., and the softening point of hemicellulose is about 180 ° C. For this reason, for example, molding at a high temperature exceeding 200 ° C. will soften up to hemicellulose in addition to lignin, and will serve as a binder by curing again, increasing the strength of the molded product unnecessarily, so grinding May decrease. Therefore, by molding at 200 ° C. or lower, more preferably 150 ° C. or lower as described above, mainly lignin serves as a binder, and a molded product having a relatively high density and a brittle state can be obtained. Can be easily pulverized with coal. Moreover, by heating to a predetermined temperature or higher and molding, moisture in the biomass evaporates at the time of molding, and the porosity of the resulting molded product can be improved. As a result, the solid fuel can be pulverized. Can be increased.
<混合燃料の製造方法>
本発明の混合燃料の製造方法は、
(A)固形燃料と石炭とを混合する工程、及び
(B)混合された上記固形燃料と石炭とを粉砕する工程
を有する。
<Production method of mixed fuel>
The method for producing the mixed fuel of the present invention includes
(A) a step of mixing solid fuel and coal, and (B) a step of pulverizing the mixed solid fuel and coal.
当該製造方法によれば、強度が高い固形燃料と石炭とを混合して粉砕するため、これら2種の混合物が偏り無く粉砕された混合燃料を得ることができる。以下、各工程について説明する。 According to the manufacturing method, since the solid fuel with high strength and coal are mixed and pulverized, it is possible to obtain a mixed fuel in which these two kinds of mixtures are pulverized without unevenness. Hereinafter, each step will be described.
(A)混合工程
本工程では、当該固形燃料と石炭とを混合する。上記石炭としては、特に限定されず、無煙炭、瀝青炭、褐炭、亜炭、泥炭等のいずれも用いることができる。
(A) Mixing step In this step, the solid fuel and coal are mixed. The coal is not particularly limited, and any of anthracite, bituminous coal, lignite, lignite, peat, and the like can be used.
上記混合方法としては特に限定されず、当該固形燃料と石炭とをそれぞれベルトコンベア等の搬送手段により搬送し、石炭バンカー等に供給することにより行えばよい。この石炭バンカー等に供給された状態においては、当該固形燃料と石炭とは均一に混ざっていても混ざっていなくともよい。 It does not specifically limit as said mixing method, What is necessary is just to carry out by conveying the said solid fuel and coal each by conveyance means, such as a belt conveyor, and supplying to a coal bunker etc. In the state of being supplied to the coal bunker or the like, the solid fuel and coal may or may not be mixed uniformly.
この混合工程における当該固形燃料と石炭との混合比としては、特に制限されないが、質量基準で、5:95以上50:50以下が好ましく、10:90以上40:60以下がより好ましい。当該固形燃料の混合比が上記下限未満の場合は、バイオマスの有効利用を十分に図ることができない。一方、この混合比が上記上限を超える場合は、発熱量の安定性に支障をきたす場合がある。 The mixing ratio of the solid fuel and coal in this mixing step is not particularly limited, but is preferably 5:95 or more and 50:50 or less, more preferably 10:90 or more and 40:60 or less on a mass basis. When the mixing ratio of the solid fuel is less than the lower limit, the biomass cannot be effectively used. On the other hand, when the mixing ratio exceeds the above upper limit, the stability of the calorific value may be hindered.
混合する石炭の密度に対する当該固形燃料の密度の比(石炭の密度/当該固形燃料の密度)としては、0.5以上2以下が好ましく、0.67以上1.5がより好ましく、0.75以上1.33以下がさらに好ましい。このように二者の密度を近づけることで、混合及び粉砕の際に均一に混合及び粉砕が生じ、得られる混合燃料の燃焼安定性をさらに高めることができる。 The ratio of the density of the solid fuel to the density of coal to be mixed (density of coal / density of the solid fuel) is preferably 0.5 or more and 2 or less, more preferably 0.67 or more and 1.5 or more. More preferred is 1.33 or less. By bringing the density of the two close to each other in this way, mixing and pulverization occur uniformly during mixing and pulverization, and the combustion stability of the resulting mixed fuel can be further enhanced.
この混合工程に供する石炭は、一定程度の粒径にまで粗粉砕されたものが好ましい。このような石炭を用いることで、均一な混合を図ることができ、また、粉砕工程における効率化を図ることができる。この際の石炭の粒径としては、60mm以下が好ましく、2mm以上50mm以下がさらに好ましい。この粗粉砕は、クラッシャー等の公知の粗粉砕機により行うことができる。 The coal used in this mixing step is preferably coarsely pulverized to a certain particle size. By using such coal, uniform mixing can be achieved, and efficiency in the pulverization process can be improved. The particle size of the coal at this time is preferably 60 mm or less, and more preferably 2 mm or more and 50 mm or less. This coarse pulverization can be performed by a known coarse pulverizer such as a crusher.
(B)粉砕工程
本工程においては、混合された当該固形燃料と石炭とを粉砕し、微粉状の混合燃料を得ることができる。この際の粉砕手段としては、特に限定されず、竪型ローラミル、ボールミル、振動ミル、ローラミル等を挙げることができる。なお、上述のように(A)混合工程として、一旦石炭バンカー等で混合・貯留することを経ずに、粉砕機に直接当該固形燃料と石炭とを供給し、粉砕機において、混合と粉砕とを行ってもよい。
(B) Pulverization step In this step, the mixed solid fuel and coal can be pulverized to obtain a finely mixed fuel mixture. The pulverizing means in this case is not particularly limited, and examples thereof include a vertical roller mill, a ball mill, a vibration mill, and a roller mill. As described above, as the mixing step (A), the solid fuel and the coal are directly supplied to the pulverizer without being mixed and stored in a coal bunker or the like. May be performed.
この粉砕の程度は特に限定されないが、例えば、100メッシュパスが95%以上となるように粉砕することが好ましい。95%を下回ると、燃焼後の燃焼残渣に未燃分が残るなど、燃焼効率が低下するおそれがある。 The degree of pulverization is not particularly limited, but for example, it is preferable to pulverize so that 100 mesh pass is 95% or more. If it is less than 95%, the combustion efficiency may be lowered, for example, unburned residue remains in the combustion residue after combustion.
このように粉砕工程を経て得られた混合燃料は、例えばボイラ用燃料、セメントキルン用燃料等として好適に用いることができる。例えば、ボイラ用燃料として用いる場合、その具体例を以下に説明する。石炭ボイラには、上記粉砕された微粉状の混合燃料が燃料として供給される。この石炭ボイラには燃焼用空気が吹き込まれ、上記混合燃料が燃焼する。この際、石炭ボイラ内に配設されるチューブ内を通る水が上記混合燃料の燃焼により加熱され、蒸気として石炭ボイラから排出される。 Thus, the mixed fuel obtained through the pulverization step can be suitably used, for example, as fuel for boilers, fuel for cement kilns, and the like. For example, when used as fuel for a boiler, a specific example thereof will be described below. The coal boiler is supplied with the pulverized finely mixed fuel as fuel. Combustion air is blown into the coal boiler, and the mixed fuel burns. At this time, the water passing through the tube disposed in the coal boiler is heated by the combustion of the mixed fuel and discharged from the coal boiler as steam.
以下、実施例によって本発明をさらに詳細に説明するが、本発明はこれらの実施例に限定されるものではない。 EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to these Examples.
<実施例1>
杉から得られた樹皮チップを破砕装置で破砕した後、目開き50mmの篩を通してバイオマス原料とした(総発熱量21MJ/kg)。このバイオマス原料をロータリーキルンに供給し、260℃で、30分間熱処理することで焙焼されたバイオマスを得た。得られたバイオマスの水分量は0.5質量%であった。また、この際の酸素濃度は10体積%に制御して行った。
この後、バイオマス100質量部に対してバインダーとしてKP黒液(クラフトリグニン)を固形分換算で1質量部混合し、これを押出成型機を用いてペレット化し、固形燃料とした(総発熱量27MJ/kg)。ペレットは、高さ30mm、直径6mm、アスペクト比5の円柱状に成型した。ペレット化の際の加熱温度は140℃で行った。得られたペレットの密度は1.20g/cm3であり、水分は0.4質量%であった。
この固形燃料と、粗粉砕した石炭とを3:7の質量比で混合した後、この混合物をローラミルを用いて粉砕し、粉末状の混合燃料を得た。
<Example 1>
The bark chips obtained from the cedar were crushed with a crushing device, and then passed through a sieve with an opening of 50 mm to obtain a biomass material (total calorific value 21 MJ / kg). This biomass raw material was supplied to a rotary kiln and heat-treated at 260 ° C. for 30 minutes to obtain roasted biomass. The moisture content of the obtained biomass was 0.5% by mass. In this case, the oxygen concentration was controlled to 10% by volume.
Thereafter, 1 part by mass of KP black liquor (kraft lignin) as a binder is mixed with 100 parts by mass of biomass in terms of solid content, and this is pelletized using an extruder to obtain a solid fuel (total calorific value 27 MJ). / Kg). The pellets were molded into a cylindrical shape having a height of 30 mm, a diameter of 6 mm, and an aspect ratio of 5. The heating temperature during pelletization was 140 ° C. The density of the obtained pellet was 1.20 g / cm 3 and the water content was 0.4% by mass.
The solid fuel and the coarsely pulverized coal were mixed at a mass ratio of 3: 7, and the mixture was pulverized using a roller mill to obtain a powdered mixed fuel.
<実施例2〜12>
固形燃料の成型(ペレット化)に係る各条件を表1に示すとおりとしたこと以外は、実施例1と同様にして実施例2〜12の固形燃料及び混合燃料を得た。なお、実施例9でバインダーとして用いた澱粉は、日本食品化工社製、製品名「MS3800」(コーンスターチ)及びJA製、製品名「清里澱粉」(馬鈴薯澱粉)である。
<Examples 2 to 12>
Solid fuels and mixed fuels of Examples 2 to 12 were obtained in the same manner as in Example 1 except that the conditions relating to the molding (pelletization) of the solid fuel were as shown in Table 1. In addition, the starch used as a binder in Example 9 is a product name “MS3800” (corn starch) manufactured by Nippon Shokuhin Kako Co., Ltd. and a product name “Kiyosato starch” (potato starch) manufactured by JA.
<比較例1>
バインダーを使用しなかったこと以外は実施例1と同様にして比較例1の固形燃料及び混合燃料を得た。
<Comparative Example 1>
A solid fuel and a mixed fuel of Comparative Example 1 were obtained in the same manner as in Example 1 except that no binder was used.
<評価>
得られた固形燃料の成型性(取扱性)及び粉砕性を以下の方法で評価した。評価結果を表1に示す。
(成型性(取扱性))
得られた固形燃料の成型性(取扱性)を以下の基準にて評価した。
A:ペレット状に容易に成型することができ、成型後も崩れにくい。
B:ペレット状に成型することができるが、成型後にやや崩れやすい。
C:ペレット状に成型されなかったもの及び成型後に崩れたものも一部にあったが、問題ない範囲であった。
D:ペレット状に成型することが若干困難である。
(粉砕性)
得られた混合燃料が均一に粉砕されているか否かを目視にて以下の基準にて評価した。
A:均一に微粉砕されている。
B:所々にやや大きい固形燃料(バイオマス)の存在が確認できる。
C:粉砕されていない固形燃料(バイオマス)の存在が目立つ。
<Evaluation>
The moldability (handleability) and grindability of the obtained solid fuel were evaluated by the following methods. The evaluation results are shown in Table 1.
(Moldability (handleability))
The moldability (handleability) of the obtained solid fuel was evaluated according to the following criteria.
A: It can be easily molded into a pellet and is not easily broken after molding.
B: Although it can be molded into a pellet shape, it tends to collapse somewhat after molding.
C: Some were not molded into pellets and some were collapsed after molding, but this was in the range of no problem.
D: It is slightly difficult to mold into a pellet.
(Crushability)
Whether the obtained mixed fuel was uniformly pulverized was visually evaluated according to the following criteria.
A: Uniformly pulverized.
B: Presence of slightly larger solid fuel (biomass) can be confirmed in some places.
C: Presence of unpulverized solid fuel (biomass) is conspicuous.
(総発熱量)
総発熱量は、JIS M 8814:2003「石炭類及びコークス類―ボンブ熱量計による総発熱量の測定方法及び真発熱量の計算方法」に準拠して10の試料を測定し、それらの平均値を値とした。
(Total calorific value)
For the total calorific value, 10 samples were measured in accordance with JIS M 8814: 2003 “Coal and cokes—Measurement method of total calorific value by bomb calorimeter and calculation method of true calorific value”, and average value thereof Was the value.
表中、実施例1から実施例7、実施例9及び10の黒液濃度は50質量%である。実施例8の黒液濃度は10質量%である。実施例9及び実施例10においては、2つのバインダーを質量比率は固形分換算で50:50の割合である。リグニン割合は黒液固形分中の含有割合である。 In the table, the black liquor concentrations of Examples 1 to 7, Examples 9 and 10 are 50% by mass. The black liquor concentration of Example 8 is 10% by mass. In Example 9 and Example 10, the mass ratio of the two binders is a ratio of 50:50 in terms of solid content. The lignin ratio is the content ratio in the black liquor solids.
表1に示されるように、本発明の固形燃料は成型性(取扱性)に優れ、石炭と焙焼されたバイオマスとを均一に微粉砕することができることがわかる。従って、このようにして得られた混合燃料は、燃焼安定性に優れることがわかる。 As shown in Table 1, it can be seen that the solid fuel of the present invention is excellent in moldability (handleability) and can uniformly pulverize coal and roasted biomass. Therefore, it turns out that the mixed fuel obtained in this way is excellent in combustion stability.
本発明の固形燃料は、ボイラ用燃料やセメントキルン用燃料等に好適に用いることができる。 The solid fuel of the present invention can be suitably used for boiler fuel, cement kiln fuel, and the like.
Claims (5)
焙焼されたバイオマスにバインダーを混合する工程、及び
上記焙焼されたバイオマスをバインダーと共に成型する工程
を有する固形燃料の製造方法。 A process of roasting biomass;
A method for producing a solid fuel, comprising: mixing a binder with roasted biomass; and molding the roasted biomass together with a binder.
混合された上記固形燃料と石炭とを粉砕する工程
を有する混合燃料の製造方法。 A method for producing a mixed fuel, comprising: mixing the solid fuel according to claim 1, claim 2 or claim 3 and coal; and crushing the mixed solid fuel and coal.