JP2014055210A - 模様形成皮革 - Google Patents
模様形成皮革 Download PDFInfo
- Publication number
- JP2014055210A JP2014055210A JP2012199549A JP2012199549A JP2014055210A JP 2014055210 A JP2014055210 A JP 2014055210A JP 2012199549 A JP2012199549 A JP 2012199549A JP 2012199549 A JP2012199549 A JP 2012199549A JP 2014055210 A JP2014055210 A JP 2014055210A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- leather
- parts
- polyurethane resin
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 本発明は、皮革基材上にベースコート層、模様層が順に積層されてなる模様形成皮革であって、前記ベースコート層に含有されるウレタン樹脂が、ポリカーボネート系ポリウレタン樹脂およびポリエーテル系ポリウレタン樹脂で構成されており、前記模様層が、少なくともジオキソラン基を有する単官能アクリレートモノマー、ヘキサヒドロフタルイミド基を有する単官能アクリレートモノマーおよび重合開始剤を含有する紫外線硬化型インクの硬化物によって構成されており、さらに、前記重合開始剤が光ラジカル重合開始剤であることを特徴とする、模様形成皮革である。
【選択図】 なし
Description
例えば、特許文献1には、天然または合成皮革上に紫外線硬化インクジェット方式で顔料樹脂塗装またはコーティングすることにより、意匠性を付与した模様形成皮革が開示されている。また、これによれば、皮革特有の柔軟性を保ちつつ引っ張りに対し、硬化膜が割れることなく追従する模様形成皮革を提供することができる。
[耐揉み性評価]
JIS K 6404−6に準拠し、スコット形もみ試験機を用いて、荷重1kg、ストローク40mm、掴み間隔15mm、サンプル幅25mmの条件のもと、15000回往復させ、往復後の塗膜破断・剥離状態を確認し、以下の基準で判定を行った。
<判定基準>
○:ベースコート層、模様層ともに破断・剥離が見られない
△:ベースコート層、模様層のどちらかに破断・剥離が見られる
×:ベースコート層、模様層ともに破断・剥離が見られる
150mm四方の大きさの試験片を1枚採取し、触感計測器(商品名「ST300 Leather Softness Tester」、BLC Leather Technology Center Ltd.製)を用いて、500gの荷重で押し込んだときの、歪み測定値(BLC値)を測定し、結果を以下の基準に従って判定した。BLC値が大きいものほど柔らかな風合いであることを意味する。
<判定基準>
○:BLC値が3.0以上
△:BLC値が2.5以上3.0未満
×:BLC値が2.5未満
(1)天然皮革基材
成牛皮の原皮を用い、クロム鞣などの通常の工程を経ることによりクラストを得た。次いで、銀むき、染色を行い、天然皮革基材を得た。
下記処方に従い、各原料をミキサーにて混合し、ベースコート塗料A1を調製した。
<ベースコート塗料処方:A1>
BAYDERM Bottom DLV 250重量部
(ポリカーボネート系ポリウレタン樹脂、固形分40%)
BAYDERM Bottom 51UD 100重量部
(ポリエーテル系ポリウレタン樹脂、固形分35%)
PRIMAL SB−300 150重量部
(アクリル樹脂、固形分34%)
EUDERM BLACK BN 120重量部
(顔料、固形分23%)
EUDERM Nappa Softs 110重量部
(艶消し剤、固形分25%)
EUDERM Matting Agent SN−C 120重量部
(充填剤、固形分23%)
EUDERM Paste DO 40重量部
(充填剤、固形分52%)
AQUADERM Fluid H 10重量部
(レベリング剤、固形分100%)
ACRYSOL RM−1020 10重量部
(増粘剤、固形分20%)
水 150重量部
上記処方成分は、水を除き全てランクセス(株)製である。また、合計量は1060重量部である。
このうち、ポリカーボネート系ポリウレタン樹脂とポリエーテル系ポリウレタン樹脂との配合比(固形分重量基準)は、100:35である。
下記処方に従い、各材料をミキサーにて混合後、ビースミルにて3分間分散を実施し、ろ過することにより、紫外線硬化型インクB1を得た。
<紫外線硬化型インク処方:B1>
MEDOL−10 37重量部
(大阪有機化学工業(株)(2−メチル−2−エチル−1,3−ジオキソラン−4−イル)メチルアクリレート)
アロニックスM−140 35重量部
(東亞合成(株) 2−(1,2−シクロヘキサンジカルボキシイミド)エチルアクリレート)
IRGALITE BLUE GLNF 2重量部
(チバスペシャルティケミカルズ(株) 顔料 銅フタロシアニン)
フローレンDOPA−33 1重量部
(共栄社化学(株) 分散剤 変性アクリル系共重合物)
Ebecryl270 5重量部
(ダイセルサイテック(株) 脂肪族ウレタンアクリレートオリゴマー)
SR489 10重量部
(サートマー トリデシルアクリレート)
ダロキュア1173 5重量部
(BASFジャパン(株) 光ラジカル重合開始剤 2−ヒドロキシ−2−メチル−1−フェニル−プロパン−1−オン)
<付与条件>
ヘッド加熱温度 50℃
ノズル径 70μm
印加電圧 50V
パルス幅 20μs
駆動周波数 1kHz
解像度 360×360dpi
インク付与量 100g/m2
柄 5mm×5mm格子柄
<硬化条件>
ランプ種類 メタルハライドランプ
出力 80W/cm
照射時間 1秒
照射高さ 10mm
実施例1において、模様層形成後、さらに模様層側にトップコート層を形成した。
(4)トップコート層の形成
下記処方に従い、各原料をミキサーにて混合し、トップコート塗料C1を調製した。
<トップコート塗料処方:C1>
HYDRHOLAC UD−2 400重量部
(ポリカーボネート系ポリウレタン樹脂、固形分25%)
HYDRHOLAC Finish HW−2 60重量部
(ポリカーボネート系ポリウレタン樹脂、固形分35%)
AQUADERM Finish HAT 200重量部
(ポリカーボネート系ポリウレタン樹脂、固形分40%)
EUDERM BLACK BN 10重量部
(顔料、固形分23%)
Rosilk 2229 70重量部
(平滑剤、固形分60%)
AQUADERM Additive SF 30重量部
(平滑剤、固形分50%)
AQUADERM Fluid H 10重量部
(レベリング剤、固形分100%)
AQUADERM SL−50 150重量部
(架橋剤、固形分50%)
RM1020 10重量部
(増粘剤、固形分20%)
水 150重量部
上記処方成分は、水を除き全てランクセス(株)製である。また、合計量は1090重量部である。
実施例1において、ベースコート層形成に用いるベースコート塗料を、下記ベースコート塗料A2に変更した。それ以外は、実施例1と同様にして、比較例1の模様形成皮革を得た。
<ベースコート塗料処方:A2>
BAYDERM Bottom DLV 250重量部
(ポリカーボネート系ポリウレタン樹脂、固形分40%)
PRIMAL SB−300 100重量部
(アクリル樹脂、固形分34%)
EUDERM BLACK BN 120重量部
(顔料、固形分23%)
EUDERM Nappa Softs 110重量部
(艶消し剤、固形分25%)
EUDERM Matting Agent SN−C 120重量部
(充填剤、固形分23%)
EUDERM Paste DO 40重量部
(充填剤、固形分52%)
AQUADERM Fluid H 10重量部
(レベリング剤、固形分100%)
ACRYSOL RM−1020 10重量部
(増粘剤、固形分20%)
水 150重量部
実施例1において、ベースコート層形成に用いるベースコート塗料を、下記ベースコート塗料A3に変更した。それ以外は、実施例1と同様にして、比較例2の模様形成皮革を得た。
<ベースコート塗料処方:A3>
BAYDERM Bottom 51UD 100重量部
(ポリエーテル系ポリウレタン樹脂、固形分35%)
PRIMAL SB−300 150重量部
(アクリル樹脂、固形分34%)
EUDERM BLACK BN 120重量部
(顔料、固形分23%)
EUDERM Nappa Softs 110重量部
(艶消し剤、固形分25%)
EUDERM Matting Agent SN−C 120重量部
(充填剤、固形分23%)
EUDERM Paste DO 40重量部
(充填剤、固形分52%)
AQUADERM Fluid H 10重量部
(レベリング剤、固形分100%)
ACRYSOL RM−1020 10重量部
(増粘剤、固形分20%)
水 150重量部
実施例1において、模様層形成に用いる紫外線硬化型インクを、下記紫外線硬化型インクB2に変更した。それ以外は、実施例1と同様にして、比較例3の模様形成皮革を得た。
<紫外線硬化型インク処方:B2>
MEDOL−10 37重量部
(大阪有機化学工業(株)(2−メチル−2−エチル−1,3−ジオキソラン−4−イル)メチルアクリレート)
IRGALITE BLUE GLNF 2重量部
(チバスペシャルティケミカルズ(株) 顔料 銅フタロシアニン)
フローレンDOPA−33 1重量部
(共栄社化学(株) 分散剤 変性アクリル系共重合物)
Ebecryl270 5重量部
(ダイセルサイテック(株) 脂肪族ウレタンアクリレートオリゴマー)
SR489 10重量部
(サートマー トリデシルアクリレート)
IBXA 40重量部
(共栄社化学(株) 反応性希釈剤 イソボニルアクリレート)
ダロキュア1173 5重量部
(BASFジャパン(株) 光ラジカル重合開始剤 2−ヒドロキシ−2−メチル−1−フェニル−プロパン−1−オン)
実施例1において、模様層形成に用いる紫外線硬化型インクを、下記紫外線硬化型インクB3に変更した。それ以外は、実施例1と同様にして、比較例4の模様形成皮革を得た。
<紫外線硬化型インク処方:B3>
IRGALITE BLUE GLNF 2重量部
(チバスペシャルティケミカルズ(株) 顔料 銅フタロシアニン)
フローレンDOPA−33 1重量部
(共栄社化学(株) 分散剤 変性アクリル系共重合物)
Ebecryl270 5重量部
(ダイセルサイテック(株) 脂肪族ウレタンアクリレートオリゴマー)
SR489 10重量部
(サートマー トリデシルアクリレート)
IBXA 37重量部
(共栄社化学(株) 反応性希釈剤 イソボニルアクリレート)
SR9003 40重量部
(サートマー 反応性希釈剤 プロポキシ変性ネオペンチルグリコールジアクリレート)
ダロキュア1173 5重量部
(BASFジャパン(株) 光ラジカル重合開始剤 2−ヒドロキシ−2−メチル−1−フェニル−プロパン−1−オン)
Claims (3)
- 皮革基材上にベースコート層、模様層が順に積層されてなる模様形成皮革であって、前記ベースコート層に含有されるウレタン樹脂が、ポリカーボネート系ポリウレタン樹脂およびポリエーテル系ポリウレタン樹脂で構成されており、前記模様層が、少なくともジオキソラン基を有する単官能アクリレートモノマー、ヘキサヒドロフタルイミド基を有する単官能アクリレートモノマーおよび重合開始剤を含有する紫外線硬化型インクの硬化物によって構成されており、さらに、前記重合開始剤が光ラジカル重合開始剤であることを特徴とする、模様形成皮革。
- 前記紫外線硬化型インク中の、ジオキソラン基を有する単官能アクリレートモノマーの含有量が30〜50重量%であり、ヘキサヒドロフタルイミド基を有する単官能アクリレートモノマーの含有量が30〜50重量%であることを特徴とする、請求項1記載の模様形成皮革。
- 前記ベースコート層に含有されるウレタン樹脂が、ポリカーボネート系ポリウレタン樹脂:ポリエーテル系ポリウレタン樹脂=92〜108:28〜42の割合で構成されることを特徴とする、請求項1記載の模様形成皮革。