JP2013252107A - Shading net and method for weaving the same - Google Patents
Shading net and method for weaving the same Download PDFInfo
- Publication number
- JP2013252107A JP2013252107A JP2012130295A JP2012130295A JP2013252107A JP 2013252107 A JP2013252107 A JP 2013252107A JP 2012130295 A JP2012130295 A JP 2012130295A JP 2012130295 A JP2012130295 A JP 2012130295A JP 2013252107 A JP2013252107 A JP 2013252107A
- Authority
- JP
- Japan
- Prior art keywords
- weft
- light
- pattern
- warp
- warp group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、遮光ネット及び遮光ネットの製織方法に関し、詳しくは、高い遮光率と良好な通気性とを両立しつつ、軽量化可能な遮光ネット及び遮光ネットの製織方法に関する。 The present invention relates to a light-shielding net and a method for weaving the light-shielding net, and more particularly to a light-shielding net and a method for weaving the light-shielding net that can reduce the weight while achieving both a high light-shielding rate and good air permeability.
従来より、茶樹、椎茸、イチゴ等の農作物の生育（栽培）や漁業により採取された海産物の熟成には、例えば、経糸（縦糸、たていと）をフィラメントとし、緯糸（横糸、よこいと）をフラットヤーン（テープヤーン）として編織した遮光ネットが使用されている。当該遮光ネットを上述した農作物や海産物の上面側に所定の展帳方法で被覆することで、太陽からの直射日光を遮光するとともに、適度に通気し、生育環境や熟成環境を適切に維持することが可能となる。 Conventionally, for the growth (cultivation) of crops such as tea trees, shiitake mushrooms, strawberries, and the ripening of marine products collected by fishing, for example, warps (warp, warp) are used as filaments and wefts (wefts, warp) are used. A shading net knitted as a flat yarn (tape yarn) is used. By covering the above-mentioned shading net on the top side of the above-mentioned crops and marine products with a predetermined exhibition method, it shields the direct sunlight from the sun and ventilates appropriately to maintain the growth environment and aging environment appropriately Is possible.
ここで、前記遮光ネットに要求される特性（性能）としては、主として遮光率と通気性であるが、この両者は相反するという問題がある。例えば、遮光率を大きくするために、緯糸の密度（インチ当たりの本数）を増加したり、緯糸の繊度（一定の繊維長に対する重量の割合、繊維の太さ）を大きくしたりすると、緯糸の間隔が小さくなり、遮光ネットの目が詰まり、通気性が悪化することになる。 Here, the characteristics (performance) required for the light-shielding net are mainly a light-shielding rate and air permeability, but there is a problem in that both are contradictory. For example, increasing the density of the weft (number per inch) or increasing the fineness of the weft (weight ratio to the constant fiber length, fiber thickness) The interval is reduced, the light shielding net is clogged, and the air permeability is deteriorated.
上述した問題を解決するために、例えば、実開平６−１９４３９号公報（特許文献１）には、多数本の各フラットヤーンと多数本の各糸条とで所定の遮光率に編成されたネット状の密編み部により農作物を被覆する遮光ネットが開示されている。当該遮光ネットは、上記ネット状に編成された密編み部に、該密編み部の編み目よりも幅広間隔のスリット部を形成している。これにより、遮光率を低減すること無く、通水性及び通気性のみを向上させて、農作物の生育に適した生育環境を保持することが出来るとしている。 In order to solve the above-described problem, for example, Japanese Utility Model Laid-Open No. 6-19439 (Patent Document 1) describes a net knitted with a large number of flat yarns and a large number of yarns to a predetermined shading rate. A light-shielding net that covers crops with a dense knitted portion is disclosed. In the light-shielding net, slit portions having a wider interval than the stitches of the densely knitted portion are formed in the densely knitted portion knitted in the net shape. Thereby, without reducing the light shielding rate, it is said that only water permeability and air permeability can be improved and a growth environment suitable for the growth of agricultural products can be maintained.
又、特開平６−１５３７１０号公報（特許文献２）には、遮光性を有する素材でテープ状に形成した多数本の各フラットヤーンと、伸縮性を有する素材で形成した多数本の各糸条とを交差してネット状に編成した遮光ネットが開示されている。これにより、所定の遮光率を有するとともに、不必要な暖気及び湿気を放出し、雨水や寒気等の侵入を防止するため、被覆空間内の光量、温度、湿度を容易に調節することが可能となり、農作物の生育に適した生育環境を保つことが出来るとしている。 Japanese Patent Laid-Open No. 6-153710 (Patent Document 2) discloses a large number of flat yarns formed in a tape shape from a light-shielding material and a large number of yarns formed from a stretchable material. And a light-shielding net that is knitted into a net shape. This makes it possible to easily adjust the amount of light, temperature, and humidity in the coating space in order to have a predetermined light shielding rate, release unnecessary warm air and moisture, and prevent intrusion of rainwater and cold air. It is said that it is possible to maintain a growth environment suitable for growing crops.
又、特開２００７−９７４８０号公報（特許文献３）には、捲縮処理された嵩高線条体が密に並列し、該嵩高線条体の長さ方向に８ｍｍ以上の間隔をおいて交差する熱可塑性樹脂製の細幅線条体によって、嵩高線条体が締止されてなることを特徴とする農業用遮光シートが開示されている。これにより、嵩高のシートとなり、遮光性が優れると同時に高い通気性を保持することが可能となり、風圧による損傷が少ないとしている。 Japanese Patent Application Laid-Open No. 2007-97480 (Patent Document 3) discloses that crimped bulky striates are closely arranged in parallel and intersect with the lengthwise direction of the bulky striates at an interval of 8 mm or more. An agricultural light-shielding sheet is disclosed in which a bulky striate is fastened by a narrow striate made of thermoplastic resin. Thereby, it becomes a bulky sheet, and it is possible to maintain a high air permeability while at the same time having excellent light shielding properties, and is said to be less damaged by wind pressure.
又、特開２００８−７９５４３号公報（特許文献４）には、緯糸及び経糸の少なくともいずれかに意匠撚糸を用いて編織されており、前記意匠撚糸が、テープ状のフラットヤーンに縦方向の切れ目を多数形成したスプリットヤーンを芯糸に対して押さえ糸を巻回して固定してなることを特徴とする農業用遮光シートが開示されている。これにより、通気性を阻害することなく遮光性に優れ、風圧に対して強度が高く、又、形状保持性に優れるとしている。 Japanese Patent Laid-Open No. 2008-79543 (Patent Document 4) is knitted using a design twist yarn for at least one of a weft and a warp yarn, and the design twist yarn is cut into a tape-like flat yarn in a longitudinal direction. An agricultural light-shielding sheet is disclosed in which a split yarn formed with a large number of yarns is fixed by winding a pressing yarn around a core yarn. Thereby, it is said that it is excellent in light-shielding properties without impairing air permeability, high in strength against wind pressure, and excellent in shape retention.
しかしながら、上述した特許文献１−４に記載の発明でも、未だに十分な遮光率と通気性を満足する遮光ネットを製織することが出来ないという問題がある。 However, even the inventions described in Patent Documents 1-4 described above still have a problem that it is not possible to weave a light shielding net that satisfies a sufficient light shielding rate and air permeability.
一方、遮光ネットの製織方法として、従来より、専用の絡み織機を用いて、二本のフィラメントの経糸を捩りながら、フラットヤーンの緯糸に絡めて織り込む絡み織（搦み織、捩り織、からめ織）が存在する。この絡み織は、具体的には、図８に示すように、二本の経糸８０１を一組の経糸群として一本の緯糸８０２に上下に交互に交差（交錯）させて絡ませることで、遮光ネット８００を製織する方法である。 On the other hand, as a method of weaving a light-shielding net, a traditionally woven weaving machine is used to twist and weave two filaments while twisting them into a flat yarn weft. ) Exists. Specifically, as shown in FIG. 8, the entangled weave is obtained by alternately intersecting (intersecting) two weft yarns 801 as a set of warp yarns with a single weft yarn 802 vertically. This is a method of weaving the light shielding net 800.
ここで、従来の絡み織の遮光ネット８００では、一の経糸群における二本の経糸８０１を一本の緯糸８０２毎に絡ませるため、二本の経糸８０１を一本の緯糸８０２に絡ませるパターン８０３（組織）が、経方向及び緯方向で繰り返し行われることになる。 Here, in the conventional shading net 800 of woven fabric, a pattern in which two warps 801 are entangled with one weft 802 in order to entangle two warps 801 in one warp group for each weft 802. 803 (organization) is repeatedly performed in the warp direction and the weft direction.
このパターン８０３では、一本の緯糸８０２が、二本の経糸８０１の２つの交差箇所８０４に経方向に囲まれる構成となり、遮光ネット８００を製織していくと、図９に示すように、前記２つの交差箇所８０４が一本の緯糸８０２を折り曲げるように締め付けることになる。又、前記パターン８０３は、緯方向に隣接して存在するため、前記一本の緯糸８０２は、緯方向の両方のパターン８０３（交差箇所８０４）から折り曲げる力を受けることになり、当該一本の緯糸８０２の交差箇所８０４近傍が、容易に折り畳まれてしまう。すると、当該折り畳まれた緯糸８０２間に大きな隙間８０５が生じて、遮光ネット８００の遮光率を低下させるという問題がある。 In this pattern 803, one weft 802 is surrounded by two intersecting portions 804 of two warps 801 in the warp direction, and when the light shielding net 800 is woven, as shown in FIG. The two intersections 804 are tightened so that one weft 802 is bent. Further, since the pattern 803 is adjacent to the weft direction, the one weft 802 receives a bending force from both patterns 803 (intersections 804) in the weft direction. The vicinity of the intersection 804 of the weft 802 is easily folded. Then, there is a problem that a large gap 805 is generated between the folded weft yarns 802 and the light shielding rate of the light shielding net 800 is lowered.
一方、上述した緯糸８０２の折り畳みを防止するために、例えば、緯糸８０２の密度を上げたり、緯糸８０２の短手方向の幅（テープ幅）を大きくしたり、緯糸８０２の厚みを厚くしたり、緯糸８０２の材質を剛性にしたりする設計変更は適宜行なわれている。しかしながら、そのような設計変更にも限界があるという問題がある。 On the other hand, in order to prevent the above-described folding of the weft 802, for example, the density of the weft 802 is increased, the width of the weft 802 in the short direction (tape width) is increased, the thickness of the weft 802 is increased, Design changes such as making the material of the weft yarn 802 rigid are made as appropriate. However, there is a problem that such a design change has a limit.
更に、近年の遮光ネットには、上述した遮光率、通気性の他に、当該遮光ネットにより被覆された農作物等への損傷を防止し、当該遮光ネットを展帳する作業者の負担を軽減するために、単位当たりのネットの重量を示す目付重量の低減（軽量化）が求められている。例えば、目付重量が大きい遮光ネットを農作物に被覆した状態で、当該遮光ネットが風等によりガサツクと、当該遮光ネットにより農作物が擦れて傷が生じるという問題がある。又、目付重量が大きい遮光ネットは、当然に、作業者が展帳し難いという問題がある。ここで、遮光ネットにおける緯糸８０２の繊度を下げたり、緯糸８０２の密度を下げたりすれば、遮光ネットの軽量化を図ることが出来るものの、遮光率が低下してしまうため、通気性と同様に、遮光率との両立は困難であるという問題がある。 Furthermore, in addition to the above-described light shielding rate and air permeability, recent light shielding nets prevent damage to crops and the like covered with the light shielding nets, and reduce the burden on the operator who exhibits the light shielding nets. Therefore, there is a demand for reduction in weight per unit weight (weight reduction) indicating the weight of the net per unit. For example, there is a problem that in a state where a light-shielding net having a large weight per unit area is covered with a crop, the light-shielding net is rubbed with wind or the like, and the crop is rubbed and scratched by the light-shielding net. In addition, the shading net having a large weight per unit weight naturally has a problem that it is difficult for an operator to register. Here, if the fineness of the weft 802 in the light-shielding net is reduced or the density of the weft 802 is reduced, the light-shielding net can be reduced, but the light-shielding rate is lowered. There is a problem that it is difficult to achieve both the light shielding rate and the light shielding rate.
又、従来の遮光ネットの製織方法として、上述した絡み織の他に、経編に類するラッセル編、経糸と緯糸を交互に上下させて織る平織等が存在するが、これらの編織方法であっても、未だに高い遮光率と良好な通気性を確保するとともに目付重量を低減させる遮光ネットを製織することが出来ないという問題がある。 In addition to the entangled weave described above, there are conventional weaving methods for light-shielding nets such as raschel knitting similar to warp knitting, plain weaving by alternately moving up and down warps and wefts, these knitting methods. However, there is still a problem that it is not possible to weave a light-shielding net that secures a high light-shielding rate and good air permeability and reduces the weight per unit area.
そこで、本発明は、前記問題を解決するためになされたものであり、高い遮光率と良好な通気性とを両立しつつ、軽量化可能な遮光ネット及び遮光ネットの製織方法を提供することを目的とする。 Accordingly, the present invention has been made to solve the above problems, and provides a light-shielding net and a method for weaving the light-shielding net that can be reduced in weight while achieving both a high light-shielding rate and good air permeability. Objective.
本発明者は、鋭意研究を重ねた結果、本発明に係る新規な遮光ネット及び遮光ネットの製織方法を完成させた。 As a result of intensive studies, the present inventor has completed a novel light shielding net and a method for weaving the light shielding net according to the present invention.
先ず、本発明に係る遮光ネットは、二本のフィラメントの経糸を一組とした経糸群を、フラットヤーンの緯糸に対して直角に所定の間隔で配列させて、各経糸群の二本の経糸を緯糸に上下に交差させて絡ませることで得られる絡み織の遮光ネットであって、以下の構成を採用する。 First, the light-shielding net according to the present invention has a warp group in which warp yarns of two filaments are set as one set and arranged at a predetermined interval at right angles to the weft yarns of a flat yarn, and two warp yarns of each warp yarn group. Is a shading woven shading net obtained by crossing up and down the weft yarn and adopts the following configuration.
即ち、本発明に係る遮光ネットは、経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するとともに、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織することで、前記パターンにおける緯糸の緯方向の形状を平面視で各経糸群間で傾斜させたことを特徴とする。 That is, the light-shielding net according to the present invention repeatedly weaves a repeating pattern including a pattern in which two warps of a warp group are entangled with two or more wefts as a repeating unit of the warp group. Weaving the position of the pattern in the warp direction is shifted by at least one weft relative to the position of the pattern in the other warp group adjacent to the one warp group in the weft direction. The shape in the weft direction is inclined between each warp group in plan view.
又、前記パターンは、経糸群の二本の経糸を二本の緯糸に絡ませるパターンとし、前記繰り返しパターンは、前記パターンの後に、経糸群の二本の経糸を一本の緯糸に絡ませる繰り返しパターンとするよう構成することが出来る。 The pattern is a pattern in which two warps of a warp group are entangled with two wefts, and the repetitive pattern is a repetition in which two warps of the warp group are entangled with one weft after the pattern. It can be configured to be a pattern.
又、前記遮光ネットの遮光率は、７５％以上であり、通気性は、２００ｃｍ３／ｃｍ２／ｓｅｃ以上であり、目付重量は、８０ｇ／ｍ２未満であるよう構成することが出来る。 The light shielding net has a light shielding rate of 75% or more, a gas permeability of 200 cm 3 / cm 2 / sec or more, and a weight per unit area of less than 80 g / m 2 .
又、前記緯糸の短手方向の幅は、１．０ｍｍ〜４．０ｍｍの範囲内であるよう構成することが出来る。 Further, the width in the short direction of the weft can be configured to be in the range of 1.0 mm to 4.0 mm.
又、前記緯糸の密度は、８本／インチ〜１４本／インチの範囲内であるよう構成することが出来る。 Further, the density of the weft can be configured to be in the range of 8 / inch to 14 / inch.
又、本発明は、二本のフィラメントの経糸を一組とした経糸群を、フラットヤーンの緯糸に対して直角に所定の間隔で配列させて、各経糸群の二本の経糸を緯糸に上下に交差させて絡ませることで得られる絡み織の遮光ネットの製織方法としても提供することが可能である。 In the present invention, a set of warps of two filaments is arranged at a predetermined interval perpendicular to the weft of the flat yarn, and the two warps of each warp group are vertically moved to the weft. It is also possible to provide a method for weaving a light-shielding net of entangled weave obtained by crossing and entangled.
即ち、本発明に係る遮光ネットの製織方法は、経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するステップと、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織するステップとを備えることを特徴とする。 That is, the weaving method of the light-shielding net according to the present invention includes a step of repeatedly weaving a repeating pattern including a pattern in which two warps of a warp group are entangled with two or more wefts as a repeating unit of the warp group, Weaving is performed by shifting the position of the pattern in the warp group in the warp direction by at least one weft with respect to the position of the pattern in the other warp group adjacent to the one warp group in the weft direction. It is characterized by that.
本発明に係る遮光ネット及び遮光ネットの製織方法によれば、高い遮光率と良好な通気性とを両立しつつ、軽量化可能となるため、品質が高く経済的な遮光ネットを提供することが可能となる。 According to the light-shielding net and the method for weaving the light-shielding net according to the present invention, it is possible to reduce the weight while achieving both a high light-shielding rate and good air permeability. Therefore, it is possible to provide a high-quality and economical light-shielding net. It becomes possible.
以下に、添付図面を参照して、本発明に係る遮光ネット及び遮光ネットの製織方法の実施形態について説明し、本発明の理解に供する。尚、以下の実施形態は、本発明を具体化した一例であって、本発明の技術的範囲を限定する性格のものではない。又、後述では、遮光ネットの太陽の直射日光を受ける面を平面、経糸の経方向の一面を正面（立面）、緯糸の緯方向の一面を側面とする。 Below, with reference to an accompanying drawing, an embodiment of a shading net concerning the present invention and a weaving method of a shading net is described, and it serves for an understanding of the present invention. In addition, the following embodiment is an example which actualized this invention, Comprising: The thing of the character which limits the technical scope of this invention is not. In the following description, the surface of the light-shielding net that receives the direct sunlight is a plane, one surface in the warp direction is the front surface (elevation surface), and one surface in the weft direction is the side surface.
＜遮光ネット＞
本発明に係る遮光ネット１００は、絡み織の遮光ネットであり、図１に示すように、二本のフィラメントの経糸１０１を一組とした経糸群を、フラットヤーンの緯糸１０２に対して直角に所定の間隔Ｘで配列させて、各経糸群の二本の経糸１０１を緯糸１０２に上下に交差させて絡ませることで得られる。
<Shading net>
A shading net 100 according to the present invention is a woven weave shading net. As shown in FIG. 1, a warp group consisting of a set of two filament warps 101 is perpendicular to a weft 102 of a flat yarn. It is obtained by arranging the two warps 101 of each warp group so as to cross the wefts 102 vertically and arrange them at a predetermined interval X.
そして、本発明に係る遮光ネット１００は、経糸群の二本の経糸１０１を二本以上の緯糸１０２に絡ませたパターン１０３を含む繰り返しパターン１０４を当該経糸群１０１の繰り返し単位として繰り返し（周期的に）製織することで得られる。 The light-shielding net 100 according to the present invention repeats a repeating pattern 104 including a pattern 103 in which two warps 101 of a warp group are entangled with two or more wefts 102 as a repeating unit of the warp group 101 (periodically). ) Obtained by weaving.
ここで、前記パターン１０３とは、絡み織の遮光ネット１００の一組織（態様）に対応し、当該パターン１０３では、二本の経糸１０１を二本以上の緯糸１０２に絡ませることで、当該二本の経糸１０１における交差箇所１０５の間の絡み目に緯糸１０２が二本以上挿通されることになる。又、前記繰り返しパターン１０４とは、前記パターン１０３を含んだ繰り返し単位組織に対応し、各経糸群１０１では、当該繰り返しパターン１０４が経方向に繰り返し表れることになる。 Here, the pattern 103 corresponds to one structure (mode) of the woven weave shading net 100, and in the pattern 103, two warps 101 are entangled with two or more wefts 102. Two or more wefts 102 are inserted through the entanglement between the intersections 105 in the warp yarn 101. The repetitive pattern 104 corresponds to a repetitive unit structure including the pattern 103. In each warp group 101, the repetitive pattern 104 appears repeatedly in the warp direction.
更に、本発明に係る遮光ネット１００は、一の経糸群１０１ａにおける前記パターン１０３ａの位置を、当該一の経糸群１０１ａと緯方向に隣接する他の経糸群１０１ｂにおける前記パターン１０３ｂの位置に対して少なくとも一本の緯糸１０２分だけ経方向にずらして製織することで得られる。 Furthermore, the light-shielding net 100 according to the present invention positions the pattern 103a in one warp group 101a with respect to the position of the pattern 103b in another warp group 101b adjacent to the one warp group 101a in the weft direction. It is obtained by weaving by shifting in the warp direction by at least one weft yarn 102 minutes.
これにより、前記パターン１０３における緯糸１０２の緯方向の形状を平面視で各経糸群１０１間で傾斜させることが可能となる。その結果、前記パターン１０３における緯糸１０２の形状を正面視でも側面視でも曲面的に変形させることが可能となり、当該緯糸１０２の折り畳みを防止することが可能となる。 Thereby, the shape of the weft 102 in the pattern 103 in the weft direction can be inclined between the warp groups 101 in a plan view. As a result, the shape of the weft yarn 102 in the pattern 103 can be deformed in a curved shape in front view or side view, and the weft yarn 102 can be prevented from being folded.
つまり、経糸群１０１に前記パターン１０３を構成することで、当該パターン１０３における二本以上の緯糸１０２が、二本の経糸１０１における２つの交差箇所１０５に経方向に囲まれることになる。そのため、前記２つの交差箇所１０５が二本以上の緯糸１０２を締め付けたとしても、各緯糸１０２は当該２つの交差箇所１０５近傍で折り畳まれ難くなり、フラットな状態を保つことになる。尚、従来では、上述したように、一本の緯糸が二本の経糸における２つの交差箇所で締め付けられて絞られて、折り畳まれる。 That is, by forming the pattern 103 in the warp group 101, two or more wefts 102 in the pattern 103 are surrounded in the warp direction by two intersecting portions 105 in the two warps 101. Therefore, even if the two intersections 105 tighten two or more wefts 102, each weft 102 is difficult to be folded in the vicinity of the two intersections 105, and the flat state is maintained. Conventionally, as described above, one weft is tightened and squeezed and folded at two intersections of two warps.
更に、一の経糸群１０１ａにおける前記パターン１０３ａの位置を、他の経糸群１０１ｂにおける前記パターン１０３ｂの位置に対して少なくとも一本の緯糸１０２分だけ経方向（図１では、下方向）にずらすことで、各パターン１０３ａ、１０３ｂ間の一本の緯糸１０２ａは、緯方向の両方のパターン１０３ａ、１０３ｂ（交差箇所１０５）から折り曲げる力を受け難くなる。 Further, the position of the pattern 103a in one warp group 101a is shifted in the warp direction (downward in FIG. 1) by at least one weft 102 relative to the position of the pattern 103b in the other warp group 101b. Thus, one weft yarn 102a between the patterns 103a and 103b is unlikely to receive a bending force from both the patterns 103a and 103b (intersection 105) in the weft direction.
一方、各パターン１０３ａ、１０３ｂ間の一本の緯糸１０２ａは、緯方向に対して傾斜した方向に力を受けることになる。図１では、前記一本の緯糸１０２ａは、一の経糸群１０１ａにおける交差箇所１０５から上方に力を受けるとともに、他の経糸群１０１ｂにおける交差箇所１０５から下方に力を受けていることを示している。 On the other hand, one weft yarn 102a between the patterns 103a and 103b receives a force in a direction inclined with respect to the weft direction. FIG. 1 shows that the one weft yarn 102a receives a force upward from the intersection 105 in one warp group 101a and receives a force downward from the intersection 105 in the other warp group 101b. Yes.
このような状態で、二本の経糸１０１ａ、１０１ｂが緯糸１０２ａを締め付けると、図２に示すように、当該緯糸１０２ａの緯方向の形状は、嵩高く捻られて（捩じられて）平面視で傾斜することになる。 In this state, when the two warp yarns 101a and 101b tighten the weft yarn 102a, as shown in FIG. 2, the shape of the weft yarn 102a in the weft direction is bulky and twisted (twisted) in plan view. Will tilt.
このように、前記緯糸１０２ａの緯方向の形状を平面視で各経糸群１０２ａ、１０２ｂ間で傾斜させることで、以下の作用効果が得られる。先ず、遮光ネット１００を水平に展張した際に、当該遮光ネット１００は、太陽の直射日光を平面視の方向から受けるため、図３に示すように、平面視における緯糸１０２ａの緯方向の形状が各経糸群１０１間で傾斜すると、各緯糸１０２間に生じる隙間１０６の拡大を最小限に抑え、従来の平面視における直線形状と比較すると、遮光面積を広くして、遮光ネット１００の遮光率を向上させる。 In this way, by inclining the shape of the weft 102a in the weft direction between the warp groups 102a and 102b in a plan view, the following effects can be obtained. First, when the light-shielding net 100 is horizontally extended, the light-shielding net 100 receives the direct sunlight of the sun from the direction of the plan view. Therefore, as shown in FIG. When the warp groups 101 are inclined, the expansion of the gap 106 between the wefts 102 is minimized, and the light shielding area of the light shielding net 100 is increased by increasing the light shielding area as compared with the linear shape in the conventional plan view. Improve.
一方、一の緯糸１０２ａは、経方向の２つの交差箇所１０５でも緯方向の２つの交差箇所１０５でも折り畳まれ難くなる（フラットな状態を保つ）ことから、図４Ａに示すように、正面視（立面視）における緯糸１０２ａの緯方向の形状は、２つの交差箇所１０５の間で曲面的に変形し（アーチ状となり）、風が内部に入り込み易くなり、風の案内板として機能する。尚、従来では、一の緯糸が、経方向の２つの交差箇所でも緯方向の２つの交差箇所でも折り畳みの力を受けることから、図４Ｂに示すように、正面視における緯糸の緯方向の形状は、２つの交差箇所の間で直線的に変形したままとなる。これでは、風が緯糸１０２ａに当たった場合に、内部に入り込み難く、当然、風の案内板としては機能しない。 On the other hand, the one weft yarn 102a is difficult to be folded (maintains a flat state) at two intersecting points 105 in the warp direction or at two intersecting points 105 in the weft direction, so as shown in FIG. The shape in the weft direction of the weft yarn 102a (in an elevation view) deforms in a curved shape between the two intersections 105 (becomes an arch shape), and the wind easily enters the inside, and functions as a wind guide plate. Conventionally, since one weft is subjected to folding force at two intersecting points in the warp direction and at two intersecting points in the weft direction, as shown in FIG. 4B, the shape of the weft in the weft direction in the front view is shown. Remains linearly deformed between the two intersections. In this case, when the wind hits the weft yarn 102a, it is difficult to enter the inside, and naturally it does not function as a wind guide plate.
又、二本（以上）の緯糸１０２が、２つの交差箇所１０５で経方向に締め付けられることで、図４Ｃに示すように、二本の緯糸１０２の一部が上下に相互に重なり合い、左側面視における緯糸１０２の経方向の形状は、２つの交差箇所１０５の間で曲面的に変形する（アーチ状となる）。ここで、上下に重なった二本の緯糸１０２に風が当たると、当該重なり合いが解けて、二本の緯糸１０２の間に風が通過可能な大きな隙間１０７が作られ、風の案内板として機能する。尚、従来では、一の緯糸が、経方向の２つの交差箇所で折り畳みの力を受けることから、図４Ｄに示すように、左側面視における緯糸の経方向の形状は、２つの交差箇所の間で直線的に変形したままとなる。これでは、一本の緯糸が経糸の２つの交差箇所で拘束されて、上述のような隙間１０７を生じることが無く、上記と同様に、風の案内板としては機能しない。 Further, as shown in FIG. 4C, two (or more) wefts 102 are tightened in the warp direction at two intersecting points 105, so that a part of the two wefts 102 overlap each other vertically, The shape in the warp direction of the weft 102 when viewed is deformed in a curved shape between the two intersections 105 (becomes an arch shape). Here, when the wind hits the two wefts 102 that overlap vertically, the overlap is released, and a large gap 107 through which the wind can pass is created between the two wefts 102, and functions as a wind guide plate. To do. Conventionally, since one weft is subjected to folding force at two intersecting points in the warp direction, as shown in FIG. 4D, the shape of the weft in the left side view is Remains linearly deformed between. In this case, one weft is not restrained at two intersecting points of the warp, so that the gap 107 as described above is not generated, and it does not function as a wind guide plate as described above.
ここで、水平に展張した遮光ネット１００は、通常、正面視又は側面視から風を受けるため、上述した緯糸１０２の形状が、正面視でも側面視でも曲面的に変形したことにより、風の案内板としての機能を十分に発揮し、当該風を内部へ案内したり、内部の風を外部へ放出したりして、遮光ネット１００の通気性を向上させる。 Here, since the horizontally extended light shielding net 100 normally receives wind from the front view or the side view, the shape of the weft 102 described above is curved in both the front view and the side view. The air function of the light-shielding net 100 is improved by sufficiently exhibiting the function as a plate, guiding the wind to the inside, and discharging the internal wind to the outside.
更に、上述した作用・効果は、主として緯糸１０２の傾斜的な変形により得ているため、従来の設計変更のように、緯糸１０２の密度を上げたりする必要が無い。言い換えると、従来の設計変更に伴う目付重量の増加を考慮する必要が無い。その結果、本発明に係る遮光ネット１００は、従来の遮光ネットと比較して目付重量の低減（軽量化）を図ることが可能となり、遮光ネット１００の被覆物への損傷を防止し、当該遮光ネット１００を展帳する作業者の負担を軽減することが可能となるのである。 Further, since the above-described actions and effects are obtained mainly by the oblique deformation of the weft yarn 102, it is not necessary to increase the density of the weft yarn 102 as in the conventional design change. In other words, it is not necessary to consider the increase in the weight per unit area due to the conventional design change. As a result, the light-shielding net 100 according to the present invention can reduce the weight per unit area (weight reduction) compared to the conventional light-shielding net, prevent damage to the covering of the light-shielding net 100, and prevent the light-shielding net 100 from being damaged. Therefore, it is possible to reduce the burden on the operator who holds the net 100.
又、本発明に係る遮光ネット１００は、上述のように、緯糸１０２が比較的フラットな状態となることから、緯糸の折り畳みが激しく剛性の高い従来の遮光ネットと比較して、手触りにごわつき感が無く、柔らかい感触となる。そのため、本発明に係る遮光ネット１００のソフト感と、上述した目付重量の低減とが相俟って、被覆物への損傷を確実に防止することが可能となる。尚、図１、図２、図４は、本発明に係る遮光ネット１００の模式図である。 In addition, as described above, the light shielding net 100 according to the present invention has a relatively flat state of the weft 102, so that the feel of the hand is stiff compared to a conventional light shielding net that is heavily folded and highly rigid. There is no soft touch. For this reason, the soft feeling of the light-shielding net 100 according to the present invention and the reduction in the weight per unit area described above can be combined to reliably prevent damage to the covering. 1, 2, and 4 are schematic views of a light shielding net 100 according to the present invention.
ここで、前記パターン１０３と、前記繰り返しパターン１０４とは、本発明の目的を阻害しない限り、特に限定することはない。例えば、図１に示すように、前記パターン１０３を、経糸群の二本の経糸１０１を二本の緯糸１０２に絡ませるパターンとし、前記繰り返しパターン１０４を、前記パターン１０３の後に、経糸群の二本の経糸１０１を一本の緯糸１０２に絡ませる繰り返しパターンとしてもよい。言い換えると、前記繰り返しパターン１０４を、経糸群の二本の経糸１０１を二本の緯糸１０２に絡ませ、次いで一本の緯糸１０２に絡ませる繰り返しパターンとするのである。 Here, the pattern 103 and the repetitive pattern 104 are not particularly limited as long as the object of the present invention is not impaired. For example, as shown in FIG. 1, the pattern 103 is a pattern in which two warps 101 of a warp group are entangled with two wefts 102, and the repetitive pattern 104 is two patterns of a warp group after the pattern 103. A repetitive pattern in which one warp 101 is entangled with one weft 102 may be used. In other words, the repetitive pattern 104 is a repetitive pattern in which two warps 101 of a warp group are entangled with two wefts 102 and then entangled with one weft 102.
又、図５に示すように、前記パターン１０３を、経糸群の二本の経糸１０１を二本の緯糸１０２に絡ませたパターンとし、前記繰り返しパターン１０４を、当該パターン１０３に対応させても構わない。更に、前記繰り返しパターン１０４を、二本の経糸１０１を三本の緯糸１０２に絡ませ、次いで一本の緯糸１０２に絡ませた繰り返しパターンとしたり、二本の経糸１０１を三本の緯糸１０２に絡ませ、次いで二本の緯糸１０２に絡ませた繰り返しパターンとしたりしても良い。尚、上述した緯糸１０２の曲面的な変形を効率よく生じさせるには、図１に示すパターン１０３と繰り返しパターン１０４が好ましい。 Further, as shown in FIG. 5, the pattern 103 may be a pattern in which two warps 101 of a warp group are entangled with two wefts 102, and the repetitive pattern 104 may correspond to the pattern 103. . Further, the repetitive pattern 104 is a repetitive pattern in which two warps 101 are entangled with three wefts 102 and then entangled with one weft 102, or two warps 101 are entangled with three wefts 102, Next, a repeated pattern entangled with two wefts 102 may be used. Note that the pattern 103 and the repetitive pattern 104 shown in FIG. 1 are preferable in order to efficiently cause the curved deformation of the weft 102 described above.
上述した遮光ネット１００では、絡み織の遮光ネットであるにも関わらず、その遮光率を、７５％以上とし、その通気性を、２００ｃｍ３／ｃｍ２／ｓｅｃ以上とし、目付重量を、８０ｇ／ｍ２未満とすることが可能となる（後述する）。 Although the shading net 100 described above is a woven shading net, the shading rate is 75% or more, the air permeability is 200 cm 3 / cm 2 / sec or more, and the weight per unit area is 80 g / It is possible to make it less than m 2 (described later).
又、一の経糸群１０１ａにおける前記パターン１０３ａの位置を、他の経糸群１０１ｂにおける前記パターン１０３ｂの位置に対して経方向にずらす緯糸１０２の本数は、前記パターン１０３で絡ませる緯糸１０２の本数にも寄るものの、一本以上であれば、上述した緯糸１０２の曲面的な変形を生じさせることが可能である。 Further, the number of wefts 102 that shifts the position of the pattern 103a in one warp group 101a in the warp direction with respect to the position of the pattern 103b in another warp group 101b is equal to the number of wefts 102 entangled in the pattern 103. However, if it is one or more, it is possible to cause the curved deformation of the weft 102 described above.
又、緯糸１０２の短手方向の幅Ｙは、本発明の目的を阻害しない限り、特に限定することはないが、例えば、前記幅Ｙを、１．０ｍｍ〜４．０ｍｍの範囲内とすると好ましく、１．５ｍｍ〜３．０ｍｍの範囲内とすると更に好ましい。このように構成すると、緯糸１０２の折り畳みを防止するとともに、曲面的な変形を生じやすくすることが可能となる。一方、前記幅Ｙを１．０ｍｍ未満とすると、緯糸１０２の曲面的な変形が生じない場合があり、前記幅Ｙを４．０ｍｍより大きくすると、緯糸１０２の折り畳みが生じやすくなるため、好ましくない。 Further, the width Y in the short direction of the weft 102 is not particularly limited as long as it does not impair the object of the present invention. For example, the width Y is preferably in the range of 1.0 mm to 4.0 mm. More preferably, it is in the range of 1.5 mm to 3.0 mm. With this configuration, it is possible to prevent the weft 102 from being folded and to easily cause curved deformation. On the other hand, if the width Y is less than 1.0 mm, the warp yarn 102 may not be curvedly deformed. If the width Y is greater than 4.0 mm, the weft yarn 102 is likely to be folded, which is not preferable. .
又、緯糸１０２の密度は、本発明の目的を阻害しない限り、特に限定することはないが、例えば、前記密度を、８本／インチ〜１４本／インチの範囲内とすると好ましい。このように構成すると、緯糸１０２の曲面的変形を生じさせやすく、遮光率、通気性、目付重量をバランスよく向上させることが可能となる。一方、前記密度を８本／インチ未満とすると、遮光率が悪化する場合があり、前記密度を１４本／インチより大きくすると、通気性、目付重量が悪化する場合があるため、好ましくない。 The density of the weft yarn 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the density is preferably in the range of 8 yarns / inch to 14 yarns / inch. If comprised in this way, it will be easy to produce the curved-form deformation | transformation of the weft 102, and it will become possible to improve a light-shielding rate, air permeability, and a fabric weight with good balance. On the other hand, if the density is less than 8 lines / inch, the light shielding rate may be deteriorated. If the density is higher than 14 lines / inch, air permeability and weight per unit area may be deteriorated.
又、経糸群１０１の間隔Ｘは、本発明の目的を阻害しない限り、特に限定することはないが、例えば、前記間隔Ｘを、５ｍｍ〜２０ｍｍの範囲内とすると好ましく、８ｍｍ〜１５ｍｍの範囲内とすると更に好ましい。このように構成すると、緯糸１０２を曲面状に保ちやすくなり、高い遮光率を維持することが可能となる。一方、前記間隔Ｘを５ｍｍ未満とすると、緯糸１０２が強制的に折り畳まれて、遮光率が低下する場合があり、前記間隔Ｘを２０ｍｍより大きくすると、緯糸１０２の形状が乱れて（規則性が無くなり）、当該緯糸１０２の曲面的変形が生じ難くなり、遮光率が悪化し、適当な風の通り道（隙間）を形成出来ない場合があり、好ましくない。 The interval X of the warp group 101 is not particularly limited as long as the object of the present invention is not impaired. For example, the interval X is preferably in the range of 5 mm to 20 mm, and in the range of 8 mm to 15 mm. More preferably. If comprised in this way, it will become easy to keep the weft 102 in a curved surface shape, and it will become possible to maintain a high light-shielding rate. On the other hand, if the distance X is less than 5 mm, the weft yarn 102 may be forcibly folded and the light shielding rate may be reduced. If the distance X is greater than 20 mm, the shape of the weft yarn 102 is disturbed (regularity is reduced). This is not preferable because the weft yarn 102 is less likely to be curvedly deformed, the light shielding rate is deteriorated, and an appropriate wind path (gap) may not be formed.
又、緯糸１０２の厚みは、本発明の目的を阻害しない限り、特に限定することはないが、例えば、前記厚みを、４５μｍ〜６５μｍの範囲内とすると好ましい。このように構成すると、緯糸１０２に適度な剛性を付与出来て、当該緯糸１０２の折り畳みを防止し、曲面的な変形を生じやすくすることが可能となる。一方、前記厚みを、４５μｍ未満とすると、緯糸１０２の折り畳みが生じやすくなる場合があり、前記厚みを、６５μｍより大きくすると、緯糸１０２の曲面的な変形が生じない場合があり、好ましくない。 The thickness of the weft yarn 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the thickness is preferably in the range of 45 μm to 65 μm. If comprised in this way, moderate rigidity can be provided to the weft 102, the folding of the said weft 102 can be prevented, and it becomes easy to produce curved deformation. On the other hand, if the thickness is less than 45 μm, the weft 102 may be easily folded, and if the thickness is greater than 65 μm, the curved deformation of the weft 102 may not occur.
又、経糸１０１の繊度は、本発明の目的を阻害しない限り、特に限定はないが、例えば、経糸１０１の繊度を、３００ｄｔｅｘ〜７００ｄｔｅｘの範囲内とすると好ましく、４００ｄｔｅｘ〜６００ｄｔｅｘの範囲内とすると更に好ましい。又、緯糸１０２の繊度は、本発明の目的を阻害しない限り、特に限定はないが、例えば、緯糸１０２の繊度を、５００ｄｔｅｘ〜１５００ｄｔｅｘの範囲内とすると好ましく、８００ｄｔｅｘ〜１２００ｄｔｅｘの範囲内とすると更に好ましい。ここで、経糸１０１又は緯糸１０２の繊度は、ＪＩＳ Ｌ １０１５「化学繊維ステープル試験方法」に規定されているＡ法により得られる値をいう。 The fineness of the warp 101 is not particularly limited as long as the object of the present invention is not impaired. For example, the fineness of the warp 101 is preferably in the range of 300 dtex to 700 dtex, and more preferably in the range of 400 dtex to 600 dtex. preferable. The fineness of the weft yarn 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the fineness of the weft yarn 102 is preferably in the range of 500 dtex to 1500 dtex, and more preferably in the range of 800 dtex to 1200 dtex. preferable. Here, the fineness of the warp yarn 101 or the weft yarn 102 is a value obtained by the method A defined in JIS L 1015 “Testing method for chemical fiber staples”.
又、経糸１０１又は緯糸１０２の引張強さは、本発明の目的を阻害しない限り、特に限定はないが、例えば、経糸１０１又は緯糸１０２の引張強さを、４ｃＮ／ｄｔｅｘ以上とすると好ましい。又、経糸１０１又は緯糸１０２の伸度は、本発明の目的を阻害しない限り、特に限定はないが、例えば、経糸１０１又は緯糸１０２の伸度を、４０％以下とすると好ましい。ここで、経糸１０１又は緯糸１０２の引張強さ及び伸度は、ＪＩＳ Ｌ １０１３「化学繊維 フィラメント糸試験方法」に規定されている方法により得られる値をいう。又、上記引張強さ（ｃＮ／ｄｔｅｘ）は、引張強度（Ｎ／本）を繊度（ｄｔｅｘ）で除算した値に対応する。 The tensile strength of the warp 101 or the weft 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the tensile strength of the warp 101 or the weft 102 is preferably 4 cN / dtex or more. Further, the elongation of the warp 101 or the weft 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the elongation of the warp 101 or the weft 102 is preferably 40% or less. Here, the tensile strength and elongation of the warp 101 or the weft 102 are values obtained by the method defined in JIS L 1013 “Testing method for chemical fiber and filament yarn”. The tensile strength (cN / dtex) corresponds to a value obtained by dividing the tensile strength (N / piece) by the fineness (dtex).
又、経糸１０１又は緯糸１０２を構成する材質は、本発明の目的を阻害しない限り、特に限定はないが、例えば、前記材質を、ポリエチレン樹脂やポリプロピレン樹脂等のポリオレフィン樹脂、塩化ビニル樹脂、ポリスチレン樹脂、エチレン−酢酸ビニル共重合体等の熱可塑性樹脂とすると好ましく、安価で、熱的特性、機械的特性、リサイクル特性が優れ、燃焼時に有害なガスを発生しないポリオレフィン樹脂とすると更に好ましい。 The material constituting the warp yarn 101 or the weft yarn 102 is not particularly limited as long as the object of the present invention is not impaired. For example, the material is a polyolefin resin such as polyethylene resin or polypropylene resin, vinyl chloride resin, polystyrene resin. It is preferable to use a thermoplastic resin such as an ethylene-vinyl acetate copolymer, and it is more preferable to use a polyolefin resin that is inexpensive, has excellent thermal characteristics, mechanical characteristics, and recycling characteristics and does not generate harmful gases during combustion.
又、前記熱可塑性樹脂は、必要に応じて、一般に用いられる各種添加剤を添加（配合）しても構わない。前記添加剤として、例えば、酸化防止剤、光安定剤、紫外線吸収剤、フィラー、帯電防止剤、中和剤、滑剤、ブロッキング防止剤、難燃剤、抗菌剤、顔料（無機顔料、有機顔料、パール顔料等）等が好ましい。又、遮光ネット１００は、通常、屋外使用であるため、前記添加剤として、光安定剤、紫外線吸収剤、劣化防止機能を有する顔料、遮光防止機能を有するブラック顔料が特に好適に用いられる。 The thermoplastic resin may be added (mixed) with various commonly used additives as required. Examples of the additive include an antioxidant, a light stabilizer, an ultraviolet absorber, a filler, an antistatic agent, a neutralizing agent, a lubricant, an antiblocking agent, a flame retardant, an antibacterial agent, and a pigment (inorganic pigment, organic pigment, pearl Pigments, etc.) are preferred. Further, since the light shielding net 100 is usually used outdoors, a light stabilizer, an ultraviolet absorber, a pigment having a deterioration preventing function, and a black pigment having a light shielding function are particularly preferably used as the additive.
又、経糸１０１の種類は、本発明の目的を阻害しない限り、特に限定はないが、例えば、モノフィラメント、マルチフィラメント、スパン糸、テープヤーンでも構わない。 The type of the warp 101 is not particularly limited as long as the object of the present invention is not hindered. For example, it may be a monofilament, a multifilament, a spun yarn or a tape yarn.
又、本発明に係る遮光ネット１００は、更に、遮熱性を付与するために、アルミニウムなどの金属層を予め蒸着した緯糸１０２を用いて製織してもよい。金属層が緯糸１０２に設けられることで、当該金属層で太陽からの直射日光を反射させて、遮光ネット１００の光の反射率を高めるとともに、光の吸収率を抑えることが可能となる。この反射率の向上と吸収率の逓減は、遮光ネット１００そのものに熱が蓄積されることを防止して、遮光ネット１００に遮熱性を付与するに繋がる。尚、金属層を設ける方法は、公知の金属真空蒸着装置等を用いてなされる。 Further, the light-shielding net 100 according to the present invention may be further woven using a weft yarn 102 pre-deposited with a metal layer such as aluminum in order to impart heat-shielding properties. By providing the metal layer on the weft yarn 102, it is possible to reflect the direct sunlight from the sun by the metal layer to increase the light reflectance of the light shielding net 100 and to suppress the light absorption rate. The improvement in reflectance and the decrease in absorption rate prevent heat from being accumulated in the light-shielding net 100 itself and lead to imparting heat-shielding properties to the light-shielding net 100. In addition, the method of providing a metal layer is made | formed using a well-known metal vacuum evaporation system etc.
＜遮光ネットの製織方法＞
本発明に係る遮光ネットの製織方法を簡単に説明する。尚、絡み織機の具体的な構成はよく知られているため、図示は省略する。
<Weaving method of shading net>
A method for weaving a light-shielding net according to the present invention will be briefly described. In addition, since the specific structure of a tangle loom is well known, illustration is abbreviate | omitted.
本発明に係る遮光ネット１００の製織方法は、二本のフィラメントの経糸１０１を一組とした経糸群を、フラットヤーンの緯糸１０２に対して直角に所定の間隔Ｘで配列させて、各経糸群の二本の経糸１０１を緯糸１０２に上下に交差させて絡ませることで得られる絡み織の遮光ネット１００の製織方法である。 In the weaving method of the light-shielding net 100 according to the present invention, a set of warps 101 of two filaments is arranged at a predetermined interval X perpendicular to the flat yarn weft 102, and each warp group This is a weaving method of the shading net 100 of the woven fabric obtained by crossing the two warp yarns 101 with the weft yarn 102 in the vertical direction.
そして、経糸群の二本の経糸１０１を二本以上の緯糸１０２に絡ませたパターン１０３を含む繰り返しパターン１０４を当該経糸群１０１の繰り返し単位として繰り返し製織するステップと、一の経糸群１０１ａにおける前記パターン１０３ａの位置を、当該一の経糸群１０１ａと緯方向に隣接する他の経糸群１０１ｂにおける前記パターン１０３ｂの位置に対して一本の緯糸１０２分だけ経方向にずらして製織するステップとを備える。これにより、本発明に係る遮光ネット１００を得ることが可能となる。 Then, a step of repeatedly weaving a repeating pattern 104 including a pattern 103 in which two warps 101 of a warp group are entangled with two or more wefts 102 as a repeating unit of the warp group 101, and the pattern in one warp group 101a. And a step of weaving by shifting the position of 103a in the warp direction by one weft 102 relative to the position of the pattern 103b in the other warp group 101b adjacent to the one warp group 101a in the weft direction. Thereby, the light-shielding net 100 according to the present invention can be obtained.
ここで、前記パターン１０３を含む繰り返しパターン１０４を前記経糸群１０１の繰り返し単位として繰り返し製織するステップは、例えば、所定の絡み織機を用いて、前記パターン１０３の製織の際に、二本の経糸１０１を一本の緯糸１０２に絡ませるタイミング（交差時点）を、二本の経糸１０１を二本以上の緯糸１０２に絡ませるタイミングに延長して、当該二本の経糸１０１を二本以上の緯糸１０２に交差させることにより実行される。 Here, the step of repeatedly weaving the repeating pattern 104 including the pattern 103 as a repeating unit of the warp group 101 includes, for example, two warps 101 when weaving the pattern 103 by using a predetermined entanglement loom. Is extended to the timing at which two warp yarns 101 are entangled with two or more wefts 102, and the two warp yarns 101 are entangled with two or more weft yarns 102. It is executed by crossing.
尚、前記絡み織機では、二枚一組となる綜絖枠を二組用意して、それぞれの綜絖枠に二本の経糸１０１をそれぞれセットして、二組の綜絖枠を上下にそれぞれ交互に昇降することで、二本の経糸１０１を交差させて絡ませる。そして、各上下昇降毎に一本の緯糸１０２を二本の経糸１０１の間（杼口）に挿通させることで、二本の経糸１０１と一本の緯糸１０２とを絡ませる。 In the entanglement loom, two sets of cocoon frames are prepared, and two warps 101 are set in each cocoon frame, and the two sets of cocoon frames are alternately raised and lowered alternately. By doing so, the two warps 101 are crossed and entangled. Then, by inserting one weft 102 between the two warps 101 (the shed) for each up and down movement, the two warps 101 and one weft 102 are entangled.
前記絡み織機では、通常の絡み織を実行する場合、二組の綜絖枠を上下にそれぞれ交互に昇降した後に、一本の緯糸１０２を挿通させて、更に、当該二組の綜絖枠を上下にそれぞれ交互に昇降するが、本発明に係る遮光ネット１００の製織方法では、例えば、二組の綜絖枠を上下にそれぞれ交互に昇降した後に、一本の緯糸１０２を挿通させても、当該二組の綜絖枠の位置をそのまま維持し、次に、二本目の緯糸１０２が挿通された時点で、当該二組の綜絖枠を上下にそれぞれ交互に昇降する。これにより、二本の経糸１０１を二本の緯糸１０２に絡ませたパターン１０３を形成させる。緯糸１０２が二本以上であっても同様である。 In the entwining loom, when performing normal entangled weaving, the two sets of reed frames are alternately raised and lowered alternately, and then one weft 102 is inserted, and further, the two sets of reed frames are moved up and down. The weaving method of the light-shielding net 100 according to the present invention, for example, in the weaving method of the shading net 100 according to the present invention, for example, even if the two sets of reed frames are alternately raised and lowered alternately, The position of the heel frame is maintained as it is, and then when the second weft 102 is inserted, the two sets of heel frames are alternately raised and lowered. Thereby, a pattern 103 in which two warps 101 are entangled with two wefts 102 is formed. The same applies to the case where there are two or more wefts 102.
又、一の経糸群１０１ａにおける前記パターン１０３ａの位置を、他の経糸群１０１ｂにおける前記パターン１０３ｂの位置に対して一本の緯糸１０２分だけ経方向にずらして製織するステップは、例えば、前記絡み織機を用いて、一の経糸群１０１ａにおける二本の経糸１０１ａを緯糸１０２に絡ませるタイミングと、他の経糸群１０１ｂにおける二本の経糸１０１ｂを緯糸１０２に絡ませるタイミングとを一本の緯糸１０２分だけずらすことにより実行される。 The step of weaving by shifting the position of the pattern 103a in one warp group 101a in the warp direction by one weft 102 with respect to the position of the pattern 103b in another warp group 101b is, for example, the entanglement Using a loom, the timing at which two warps 101a in one warp group 101a are entangled with the weft 102 and the timing at which two warps 101b in the other warp group 101b are entangled with the weft 102 are one weft 102. It is executed by shifting by minutes.
例えば、前記絡み織機では、図１に示すように、先ず、一の経糸群１０１ａにおける二組の綜絖枠を上下にそれぞれ交互に昇降すると、他の経糸群１０１ｂにおける二組の綜絖枠を上下にそれぞれ交互に昇降する。次に、一の経糸群１０１ａでは、前記パターン１０３を形成するため、二組の綜絖枠をそのままの位置に維持する一方、他の経糸群１０１ｂにおける二組の綜絖枠を上下にそれぞれ交互に昇降する。そして、一の経糸群１０１ａでは、二組の綜絖枠を上下にそれぞれ交互に昇降して、前記パターン１０３を形成する一方、他の経糸群１０１ｂでは、前記パターン１０３を形成するため、二組の綜絖枠をそのままの位置に維持する。更に、一の経糸群１０１ａでも他の経糸群１０１ｂでも、二組の綜絖枠を上下にそれぞれ交互に昇降することで、当該他の経糸群１０１ｂに前記パターン１０３が形成される。 For example, in the entwining loom, as shown in FIG. 1, first, when two sets of reed frames in one warp group 101a are alternately moved up and down, two sets of reed frames in another warp group 101b are moved up and down. Each moves up and down alternately. Next, in one warp group 101a, in order to form the pattern 103, the two sets of heel frames are maintained at the same position, while the two sets of heel frames in the other warp groups 101b are alternately raised and lowered alternately. To do. Then, in one warp group 101a, two sets of reed frames are alternately raised and lowered to form the pattern 103, while in the other warp group 101b, the pattern 103 is formed in two sets. Keep the heel frame in place. Further, in either one warp group 101a or another warp group 101b, the pattern 103 is formed in the other warp group 101b by alternately raising and lowering the two sets of heel frames.
もちろん、上述したタイミングは、目的とするパターン１０３、繰り返しパターン１０４の種類に応じて適宜設計変更されることはいうまでも無い。 Of course, it is needless to say that the design of the timing described above is appropriately changed according to the type of the target pattern 103 and the repetitive pattern 104.
尚、前記絡み織機は、シャトル方式又はレピア方式の絡み織機を採用することが出来る。ここで、シャトル方式の絡み織機は、緯糸を掴んだシャトル（杼）を、二本の経糸の上下に交差させることで形成される各杼口毎に緯方向（左右方向）に打ち込む織機であり、レピア方式の絡み織機は、緯糸をレピア（槍状の金具）の先端で掴んで、各杼口毎に走らせる織機である。 As the entanglement loom, a shuttle type or rapier type entanglement loom can be adopted. Here, a shuttle-type entwining loom is a loom that drives a shuttle (杼) that grabs the weft yarn in the weft direction (left and right direction) for each hook formed by crossing the upper and lower sides of two warps. A rapier-type woven loom is a loom that grabs the weft yarn at the tip of a rapier (saddle-shaped metal fitting) and runs it for each shed.
＜実施例、比較例等＞
以下、実施例及び比較例によって本発明を具体的に説明するが本発明はこれにより限定されるものではない。
<Examples, comparative examples, etc.>
EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention concretely, this invention is not limited by this.
（１）経糸及び緯糸の製造方法
経糸は、下記の手順により作成した。先ず、市販の高密度ポリエチレン樹脂（ＨＤＰＥ、ＭＦＲ：１．０ｇ／１０ｍｉｎ）のペレットに市販のブラック顔料を４０重量％混合してペレット化した第一のマスターバッチを作成した。次に、前記高密度ポリエチレン樹脂のペレットに前記第一のマスターバッチを４重量％添加して混合し、当該混合物を所定のスクリュー押出機で溶融し、円形ダイから水槽へ押出して、棒状の溶融物を冷却固化した後、沸騰水中で延伸することで、繊度が５５０ｄｔｅｘ、引張強度が２９Ｎ／本（２９／５５０＝５．２７ｃＮ／ｄｔｅｘ）、伸度が３５％のモノフィラメントを得た。当該モノフィラメントを経糸とした。
(1) Manufacturing method of warp and weft The warp was prepared according to the following procedure. First, a first master batch was prepared by mixing 40% by weight of a commercially available black pigment with pellets of a commercially available high-density polyethylene resin (HDPE, MFR: 1.0 g / 10 min). Next, 4% by weight of the first master batch is added to the high density polyethylene resin pellets and mixed, the mixture is melted with a predetermined screw extruder, extruded from a circular die to a water tank, and melted into a rod shape. After cooling and solidifying the product, it was stretched in boiling water to obtain a monofilament having a fineness of 550 dtex, a tensile strength of 29 N / fiber (29/550 = 5.27 cN / dtex), and an elongation of 35%. The monofilament was used as a warp.
又、緯糸は、下記の手順により作成した。先ず、市販のポリプロピレン樹脂（ＰＰ、ＭＦＲ：１．９ｇ／１０ｍｉｎ）のペレットに前記ブラック顔料を４０重量％混合してペレット化した第二のマスターバッチを作成した。又、前記ポリプロピレン樹脂のペレットに市販の炭酸カルシウムを８０重量％混合してペレット化した第三のマスターバッチを作成する。そして、前記ポリプロピレン樹脂のペレットに、前記第二のマスターバッチを６重量％、前記第三のマスターバッチを２重量％それぞれ添加して混合し、当該混合物を所定のスクリュー押出機で溶融し、Ｔダイスからチルロールへ押出して、フィルム状の溶融物を冷却固化した後、スリットし、加熱ロールで延伸することで、繊度が１１００ｄｔｅｘ、引張強度が５９Ｎ／本（５９／１１００＝５．３６ｃＮ／ｄｔｅｘ）、伸度が２４％、フラットヤーン（テープヤーン）を得た。尚、スリットの調整により、短手方向の幅が２．１ｍｍと３．４ｍｍの２種類のフラットヤーンを作成した。当該フラットヤーンを緯糸とした。又、得られた緯糸のうち、短手方向の幅が２．１ｍｍの緯糸にアルミニウムを真空蒸着させたものを別途作成した。 The weft was prepared by the following procedure. First, a second master batch was prepared by mixing 40% by weight of the black pigment with pellets of a commercially available polypropylene resin (PP, MFR: 1.9 g / 10 min). A third masterbatch is prepared by mixing 80% by weight of commercially available calcium carbonate with the polypropylene resin pellets. Then, 6% by weight of the second masterbatch and 2% by weight of the third masterbatch are added and mixed with the polypropylene resin pellets, and the mixture is melted with a predetermined screw extruder. After extruding from a die to a chill roll to cool and solidify the film-like melt, it is slit and stretched with a heating roll, so that the fineness is 1100 dtex and the tensile strength is 59 N / piece (59/1100 = 5.36 cN / dtex). A flat yarn (tape yarn) having an elongation of 24% was obtained. Two types of flat yarns having a width in the short side direction of 2.1 mm and 3.4 mm were prepared by adjusting the slit. The flat yarn was used as a weft. In addition, among the obtained wefts, weft was prepared by vacuum-evaporating aluminum on wefts having a width in the short direction of 2.1 mm.
（２）製織方法と評価方法
遮光ネットは、以下の手順により作成した。上述で作成した経糸と緯糸を用いて所定の絡み織機（スルテック社製シャトル織機、１５３インチ幅）で２ｍ幅の遮光ネットを製織した。又、前記絡み織機では、５組（１０枚）の綜絖枠を使用した。又、製織した遮光ネットの緯方向の両端部を平織にしてタック耳を形成し、緯糸の端部を織り込んでほつれないようにした。
(2) Weaving method and evaluation method The shading net was created by the following procedure. Using the warp and weft created above, a 2 m wide light-shielding net was woven using a predetermined entanglement loom (Sultec shuttle loom, 153 inch width). In the entwining loom, 5 sets (10 sheets) of frame were used. Further, both ends in the weft direction of the woven light-shielding net were plain woven to form a tack ear, and the ends of the weft were woven to prevent fraying.
又、評価方法は、後述する遮光率、通気性、目付重量、遮熱性の評価項目に従って総合的に評価した。 Moreover, the evaluation method evaluated comprehensively according to the evaluation item of the light-shielding rate, air permeability, a fabric weight, and heat-shielding property mentioned later.
先ず、製織した遮光ネットの遮光率（％）は、ＪＩＳ Ｌ １０５５ Ａ法「カーテンの遮光性試験方法」に規定されている方法により測定した。当該測定した遮光率（％）を下記に示す４段階で評価した。
◎：８５％以上
○：８０％以上で、８５％未満
△：７５％以上で、８０％未満
×：７５％未満
First, the light-shielding rate (%) of the woven light-shielding net was measured by the method defined in JIS L 1055 A method “Light-shielding test method for curtains”. The measured shading rate (%) was evaluated in the following four stages.
◎: 85% or more ○: 80% or more, less than 85% △: 75% or more, less than 80% ×: less than 75%
次に、製織した遮光ネットの通気性（ｃｍ３／ｃｍ２／ｓｅｃ）は、ＪＩＳ Ｌ １０９６ Ａ法「織物及び編物の生地試験方法」に規定されている方法（フラジール型測定面積３８ｃｍ２、測定範囲０．０５〜７９０）により測定した。当該測定した通気性（ｃｍ３／ｃｍ２／ｓｅｃ）を下記に示す４段階で評価した。
◎：３００ｃｍ３／ｃｍ２／ｓｅｃ以上
○：２５０ｃｍ３／ｃｍ２／ｓｅｃ以上で、３００ｃｍ３／ｃｍ２／ｓｅｃ未満
△：２００ｃｍ３／ｃｍ２／ｓｅｃ以上で、２５０ｃｍ３／ｃｍ２／ｓｅｃ未満
×：２００ｃｍ３／ｃｍ２／ｓｅｃ未満
Next, the air permeability (cm 3 / cm 2 / sec) of the woven light-shielding net is measured according to the method defined in JIS L 1096 A Method “Fabric and Knitted Fabric Test Method” (Fragile measuring area 38 cm 2 , measurement Measured in the range 0.05-790). The measured air permeability (cm 3 / cm 2 / sec) was evaluated in the following four stages.
◎: 300 cm 3 / cm 2 / sec or more ○: 250 cm 3 / cm 2 / sec or more and less than 300 cm 3 / cm 2 / sec Δ: 200 cm 3 / cm 2 / sec or more and less than 250 cm 3 / cm 2 / sec ×: Less than 200 cm 3 / cm 2 / sec
そして、製織した遮光ネットの目付重量（ｇ／ｍ２）は、所定の面積（ｍ２）で裁断した遮光ネットの重量（ｇ）を市販の重量計により測定し、単位面積当たりの重量を目付重量として算出した。当該測定した目付重量（ｇ／ｍ２）を下記に示す４段階で評価した。
◎：７０ｇ／ｍ２未満
○：７０ｇ／ｍ２以上で、８０ｇ／ｍ２未満
△：８０ｇ／ｍ２以上で、９０ｇ／ｍ２未満
×：９０ｇ／ｍ２以上
The weight per unit area (g / m 2 ) of the woven light-shielding net was determined by measuring the weight (g) of the light-shielding net cut at a predetermined area (m 2 ) using a commercially available weighing scale. Calculated as weight. The measured basis weight (g / m 2 ) was evaluated in the following four stages.
◎: Less than 70 g / m 2 ○: 70 g / m 2 or more and less than 80 g / m 2 Δ: 80 g / m 2 or more and less than 90 g / m 2 ×: 90 g / m 2 or more
更に、製織した遮光ネットの遮熱性（−）は、下記の手順で評価した。先ず、遮光ネットの日射透過率（％）及び日射反射率（％）を、ＪＩＳ Ｒ ３１０６「板ガラス類の透過率・反射率・放射率・日射熱取得率の試験方法」に規定されている方法により測定し、日射透過率と日射吸収率と日射反射率との合計が１００％であることを利用して、日射吸収率（％）は、（１００−日射透過率（％）−日射反射率（％））により算出した。当該算出した日射吸収率（％）を下記に示す２段階で評価し、それを遮熱性とした。
○：５％未満
×：５％以上
Furthermore, the heat shielding property (-) of the woven light shielding net was evaluated by the following procedure. First, the solar radiation transmittance (%) and solar reflectance (%) of the light-shielding net are defined in JIS R 3106 “Testing method of transmittance, reflectance, emissivity, and solar heat acquisition rate of sheet glass”. By using the fact that the total of the solar transmittance, the solar absorption rate and the solar reflectance is 100%, the solar absorption rate (%) is (100−solar transmittance (%) − solar reflectance) (%)). The calculated solar absorptivity (%) was evaluated in the following two stages, and was defined as heat shielding properties.
○: Less than 5% ×: 5% or more
上述した遮光率、通気性、目付重量、遮熱性の総合評価を、◎、○、△、×の４段階で評価した。 The overall evaluation of the above-described light shielding rate, air permeability, weight per unit area, and heat shielding property was evaluated in four stages of ◎, ○, Δ, and ×.
（３）実施例、比較例
実施例１は、図１に示すように、前記パターン１０３を、経糸群の二本の経糸１０１を二本の緯糸１０２に絡ませるパターンとし、前記繰り返しパターン１０４は、前記パターン１０３の後に、経糸群の二本の経糸１０１を一本の緯糸１０２に絡ませる繰り返しパターンとして遮光ネット１００を製織した。この際、緯糸１０２の短手方向の幅Ｙを２．１ｍｍとし、経糸群１０１の間隔Ｘを１０ｍｍとし、緯糸１０２の密度を８本／インチとした。
(3) Examples and Comparative Examples In Example 1, as shown in FIG. 1, the pattern 103 is a pattern in which two warps 101 of a warp group are entangled with two wefts 102, and the repetitive pattern 104 is After the pattern 103, the light-shielding net 100 was woven as a repetitive pattern in which two warps 101 of the warp group were entangled with one weft 102. At this time, the width Y in the short direction of the weft 102 was 2.1 mm, the interval X between the warp groups 101 was 10 mm, and the density of the weft 102 was 8 / inch.
又、実施例２は、実施例１における緯糸１０２の密度を８本／インチから１０本／インチに変更する以外は、実施例１と同様にして遮光ネットを製織した。 In Example 2, the light-shielding net was woven in the same manner as in Example 1 except that the density of the weft yarn 102 in Example 1 was changed from 8 / inch to 10 / inch.
又、実施例３は、実施例１における緯糸１０２の密度を８本／インチから１２本／インチに変更する以外は、実施例１と同様にして遮光ネットを製織した。 In Example 3, the light-shielding net was woven in the same manner as in Example 1 except that the density of the weft yarn 102 in Example 1 was changed from 8 / inch to 12 / inch.
又、実施例４は、実施例１における緯糸１０２の密度を８本／インチから１４本／インチに変更する以外は、実施例１と同様にして遮光ネットを製織した。 In Example 4, the light shielding net was woven in the same manner as in Example 1 except that the density of the weft yarn 102 in Example 1 was changed from 8 / inch to 14 / inch.
又、実施例５は、実施例４における緯糸１０２の短手方向の幅Ｙを２．１ｍｍから３．４ｍｍに変更する以外は、実施例４と同様にして遮光ネットを製織した。 In Example 5, the light-shielding net was woven in the same manner as in Example 4 except that the lateral width Y of the weft yarn 102 in Example 4 was changed from 2.1 mm to 3.4 mm.
又、実施例６は、実施例４における経糸群１０１の間隔Ｘを１０ｍｍから６ｍｍに変更する以外は、実施例４と同様にして遮光ネットを製織した。 In Example 6, a light-shielding net was woven in the same manner as in Example 4 except that the interval X of the warp group 101 in Example 4 was changed from 10 mm to 6 mm.
又、実施例７は、実施例３における緯糸１０２を、アルミニウム層を蒸着した緯糸に変更する以外は、実施例３と同様にして遮光ネットを製織した。 In Example 7, a light-shielding net was woven in the same manner as in Example 3 except that the weft 102 in Example 3 was changed to a weft having an aluminum layer deposited thereon.
又、比較例１は、図７に示すように、一の経糸群における二本の経糸７０１を一本の緯糸７０２毎に絡ませる従来の絡み織の遮光ネット（小泉製麻製、品番＃1000）を採用した、この際、緯糸の材質はＨＤＰＥであり、緯糸の短手方向の幅は６．０ｍｍであり、緯糸の繊度は１０６０ｄｔｅｘであり、経糸群の間隔は９ｍｍであり、緯糸の密度は９．９本／インチであった。 Further, in Comparative Example 1, as shown in FIG. 7, a conventional woven shading shading net (manufactured by Koizumi Hemp, product number # 1000) in which two warps 701 in one warp group are entangled with each weft 702. In this case, the material of the weft is HDPE, the width in the short direction of the weft is 6.0 mm, the fineness of the weft is 1060 dtex, the distance between the warp groups is 9 mm, and the density of the weft Was 9.9 pieces / inch.
比較例２は、比較例１における緯糸の短手方向の幅を１０．０ｍｍに変更し、緯糸の繊度を２２００ｄｔｅｘに変更し、緯糸の密度を７．９本／インチに変更したこと以外は、比較例１と同様の遮光ネット（品番＃1600）を採用した。 In Comparative Example 2, the width in the short direction of the weft in Comparative Example 1 was changed to 10.0 mm, the fineness of the weft was changed to 2200 dtex, and the density of the weft was changed to 7.9 pieces / inch, The same light-shielding net (Part No. # 1600) as in Comparative Example 1 was used.
比較例３は、比較例２における緯糸の密度を１１．２本／インチに変更したこと以外は、比較例２と同様の遮光ネット（品番＃3200）を採用した。 In Comparative Example 3, the same light-shielding net (Product No. # 3200) as in Comparative Example 2 was adopted except that the weft density in Comparative Example 2 was changed to 11.2 yarns / inch.
比較例４は、ラッセル編の遮光ネット（遮光率８５％の市販の遮光ネット）を採用した。この際、前記絡み織の経、緯に相当する素材、及び組織は次の通りであった。前記経糸相当はＨＤＰＥモノフィラメントであり、前記緯糸相当はＰＰテープヤーンであり、当該テープヤーンの繊度が１０１０ｄｔｅｘであり、その短手方向の幅が２．３ｍｍであった。又、前記経糸群の間隔は１２ｍｍであり、前記緯糸相当の密度が１６本/インチであった。 In Comparative Example 4, a Russell knitted light shielding net (a commercially available light shielding net with a light shielding ratio of 85%) was used. At this time, the materials and structures corresponding to the warp and weft of the entangled weave were as follows. The warp equivalent was an HDPE monofilament, the weft equivalent was a PP tape yarn, the fineness of the tape yarn was 1010 dtex, and the width in the short direction was 2.3 mm. The spacing between the warp groups was 12 mm, and the density corresponding to the wefts was 16 / inch.
比較例５は、平織で縦にアルミ蒸着したフィルムをスリットした織物の遮光ネット（市販の遮光ネット）を採用した。この際、前記遮光ネットの緯糸の材質はＨＤＰＥのモノフィラメントであり、その繊度は３１０ｄｔｅｘであり、又、密度は１５本/インチであった。 In Comparative Example 5, a woven light-shielding net (commercially available light-shielding net) obtained by slitting a film of plain weave and vertically evaporated aluminum was employed. At this time, the material of the weft of the light shielding net was HDPE monofilament, the fineness was 310 dtex, and the density was 15 / inch.
（４）評価結果
図６は、実施例と比較例と評価項目と評価結果の表の一例を示す図である。図５に示すように、実施例１−７では、遮光率が高いにも関わらず、通気性が良く、目付重量が低減されており、遮光率、通気性、目付重量のいずれの評価項目もバランスよく良好な結果が得られた。例えば、実施例１では、図３に示すように、緯糸は、当該緯糸と経糸との交差箇所において平面視で傾斜した変形、正面視で曲面的な変形に留まり、殆ど折り畳まれていないことが理解される。又、実施例７では、アルミニウム層を緯糸に備えることで、更に遮熱性が良好になった。
(4) Evaluation Results FIG. 6 is a diagram illustrating an example of a table of examples, comparative examples, evaluation items, and evaluation results. As shown in FIG. 5, in Example 1-7, although the light shielding rate is high, the air permeability is good and the basis weight is reduced, and any of the evaluation items of the light shielding rate, the air permeability, and the basis weight is provided. Good results with good balance were obtained. For example, in Example 1, as shown in FIG. 3, the weft may be deformed by being inclined in a plan view at the intersection of the weft and the warp, or curved in a front view, and hardly folded. Understood. In Example 7, the heat shielding property was further improved by providing the weft with an aluminum layer.
一方、比較例１では、通気性、目付重量が良好であっても、遮光率が不良であり、比較例２では、遮光率、通気性、目付重量のいずれも顕著に良好な結果を得ることが出来ず、比較例３では、遮光率、通気性が良好であっても、目付重量が不良であった。例えば、比較例１では、図９に示すように、緯糸８０２は、当該緯糸８０２と経糸８０１との交差箇所８０４で殆ど折り畳まれて、大きな隙間８０５が生じていることが理解される。又、比較例４では、遮光率、通気性が良好であっても、目付重量が不良であり、図７に示すように、緯糸７０２は、当該緯糸７０２と経糸７０１との交差箇所７０３で殆ど折り畳まれて、大きな隙間７０４が生じていることが理解される。又、比較例５では、遮光率、目付重量が良好であっても、通気性が不良であった。 On the other hand, in Comparative Example 1, even if the air permeability and the weight per unit area are good, the light shielding rate is poor, and in Comparative Example 2, the light shielding rate, the air permeability, and the basis weight are all significantly good. In Comparative Example 3, the weight per unit area was poor even though the light shielding rate and air permeability were good. For example, in Comparative Example 1, it is understood that the weft yarn 802 is almost folded at the intersection 804 between the weft yarn 802 and the warp yarn 801 as shown in FIG. Further, in Comparative Example 4, even if the light shielding rate and air permeability are good, the weight per unit area is poor. As shown in FIG. 7, the weft 702 is almost at the intersection 703 between the weft 702 and the warp 701. It is understood that a large gap 704 is created when folded. Further, in Comparative Example 5, even though the light shielding rate and the weight per unit area were good, the air permeability was poor.
従って、実施例１−７は、高い遮光率と良好な通気性とを両立しつつ、軽量化が可能であることが理解される。つまり、本発明に係る遮光ネット１００では、従来の絡み織、ラッセル編、平織の問題を解決することが可能となる。 Therefore, it is understood that Example 1-7 can be reduced in weight while achieving both a high light shielding rate and good air permeability. That is, in the light shielding net 100 according to the present invention, it is possible to solve the problems of the conventional woven fabric, raschel knitting, and plain weave.
このように、本発明では、経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するとともに、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織することで、前記パターンにおける緯糸の緯方向の形状を平面視で各経糸群間で傾斜させたことを特徴とする遮光ネットを採用する。 As described above, in the present invention, a repetitive pattern including a pattern in which two warps of a warp group are entangled with two or more wefts is repeatedly woven as a repetitive unit of the warp group. The weft direction of the weft in the pattern is woven by shifting the position in the warp direction by at least one weft relative to the position of the pattern in the other warp group adjacent to the one warp group in the weft direction. The shading net is characterized in that the shape is inclined between each warp group in plan view.
これにより、高い遮光率と良好な通気性とを両立しつつ、軽量化可能となるため、品質が高く経済的な遮光ネットを提供することが可能となる。 This makes it possible to reduce the weight while achieving both a high light-shielding rate and good air permeability, and thus it is possible to provide a high-quality and economical light-shielding net.
ところで、上述した遮光ネット１００の用途は、主として農作物の生育や海産物の熟成であるが、本発明に係る遮光ネット１００は、遮光率は、７５％以上であり、通気性は、２００ｃｍ３／ｃｍ２／ｓｅｃ以上であり、目付重量は、８０ｇ／ｍ２未満であることから、例えば、茶樹の栽培に採用すると好ましい。上述した特性を有する遮光ネット１００を茶樹の栽培に採用すると、遮光率、通気性の適度なバランスにより、テアニンの多い茶葉を栽培することが可能となる。ここで、テアニンとは、飲用するとグルタミン酸（アミノ酸の一種）を誘導する働きがあり、お茶の旨みに対応する成分である。このテアニンが豊富に含まれている茶葉は、高級茶葉に該当するため、栽培する茶葉の品質を向上することが可能となるのである。更に、目付重量が小さく（軽く）、ソフト感があるため、本発明に係る遮光ネット１００を用いると、柔らかい茶葉を傷つけることが殆ど無い。 By the way, the above-described use of the light-shielding net 100 is mainly for the growth of agricultural crops and the ripening of marine products, but the light-shielding net 100 according to the present invention has a light-shielding rate of 75% or more and an air permeability of 200 cm 3 / cm. Since it is 2 / sec or more and the weight per unit area is less than 80 g / m 2 , for example, it is preferably used for cultivation of tea plants. When the light-shielding net 100 having the above-described characteristics is employed for tea plant cultivation, tea leaves rich in theanine can be cultivated with an appropriate balance between light-shielding rate and air permeability. Here, theanine has a function of inducing glutamic acid (a kind of amino acid) when ingested, and is a component corresponding to the taste of tea. The tea leaves rich in theanine correspond to high-quality tea leaves, so that the quality of the tea leaves to be cultivated can be improved. Further, since the weight per unit area is small (light) and there is a soft feeling, the use of the light-shielding net 100 according to the present invention hardly damages the soft tea leaves.
又、本発明では、二本のフィラメントの経糸を一組とした経糸群を、フラットヤーンの緯糸に対して直角に所定の間隔で配列させて、各経糸群の二本の経糸を緯糸に上下に交差させて絡ませることで得られる絡み織の遮光ネットの製織方法としても提供することが可能である。つまり、本発明に係る遮光ネットの製織方法は、経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するステップと、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織するステップとを備えることを特徴とする。このような構成であっても、上述と同様の作用効果を得ることが可能となる。 In the present invention, a set of warps of two filaments is arranged at a predetermined interval perpendicular to the weft of the flat yarn, and the two warps of each warp group are vertically moved to the weft. It is also possible to provide a method for weaving a light-shielding net of entangled weave obtained by crossing and entangled. That is, the method of weaving the light-shielding net according to the present invention includes a step of repeatedly weaving a repeating pattern including a pattern in which two warps of a warp group are entangled with two or more wefts as a repeating unit of the warp group, Weaving is performed by shifting the position of the pattern in the warp group in the warp direction by at least one weft with respect to the position of the pattern in the other warp group adjacent to the one warp group in the weft direction. It is characterized by that. Even with such a configuration, it is possible to obtain the same effects as described above.
又、本発明では、二本のフィラメントの経糸を一組とした経糸群を、フラットヤーンの緯糸に対して直角に所定の間隔で配列させて、各経糸群の二本の経糸を緯糸に上下に交差させて絡ませることで得られる絡み織の遮光ネットの製織装置としても提供することが可能である。つまり、本発明に係る遮光ネットの製織装置は、経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織する第一の製織部と、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織する第二の製織部とを備えることを特徴とする。このような構成であっても、上述と同様の作用効果を得ることが可能となる。 In the present invention, a set of warps of two filaments is arranged at a predetermined interval perpendicular to the weft of the flat yarn, and the two warps of each warp group are vertically moved to the weft. It is also possible to provide as a weaving device for an entangled shading net obtained by crossing and entangled. That is, the light-shielding net weaving apparatus according to the present invention is a first weaving unit that repeatedly weaves a repeating pattern including a pattern in which two warps of a warp group are entangled with two or more wefts as a repeating unit of the warp group. And weaving by shifting the position of the pattern in one warp group in the warp direction by at least one weft relative to the position of the pattern in another warp group adjacent to the one warp group in the weft direction. And a second weaving section. Even with such a configuration, it is possible to obtain the same effects as described above.
以上のように、本発明に係る遮光ネット及び遮光ネットの製織方法は、農業、漁業はもちろん工業等の様々な分野で使用される遮光ネット及び遮光ネットの製織方法として有用であり、高い遮光率と良好な通気性とを両立しつつ、軽量化可能な遮光ネット及び遮光ネットの製織方法として有効である。 As described above, the light-shielding net and the light-shielding net weaving method according to the present invention are useful as a light-shielding net and a light-shielding net weaving method used in various fields such as agriculture, fishery, and industry, and have a high light-shielding rate. It is effective as a light-shielding net that can be reduced in weight and a method for weaving the light-shielding net while achieving both good air permeability and good air permeability.
１００ 遮光ネット
１０１ 経糸
１０２ 緯糸
１０３ パターン
１０４ 繰り返しパターン
１０５ 二本の経糸の交差箇所
１０６ 緯糸間に生じる隙間
100 shading net 101 warp yarn 102 weft yarn 103 pattern 104 repetitive pattern 105 intersection of two warp yarns 106 gap formed between weft yarns
Claims (6)
経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するとともに、一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織することで、前記パターンにおける緯糸の緯方向の形状を平面視で各経糸群間で傾斜させたことを特徴とする遮光ネット。 A set of warps of two filaments are arranged at a predetermined interval perpendicular to the weft of a flat yarn, and the two warps of each warp group are entangled so as to cross the weft vertically. It is a shading net of woven fabric obtained by
A repetitive pattern including a pattern in which two warps of a warp group are entangled with two or more wefts is repeatedly woven as a repeat unit of the warp group, and the position of the pattern in one warp group is set to the one warp group. Each weft in the plan view in the weft direction in the pattern by weaving at least one weft in the warp direction with respect to the position of the pattern in the other warp group adjacent to the weft direction. A shading net characterized by slanting between groups.
前記繰り返しパターンは、前記パターンの後に、経糸群の二本の経糸を一本の緯糸に絡ませる繰り返しパターンとする
請求項１に記載の遮光ネット。 The pattern is a pattern in which two warps of a warp group are entangled with two wefts,
The light-shielding net according to claim 1, wherein the repeating pattern is a repeating pattern in which two warps of a warp group are entangled with one weft after the pattern.
請求項１又は２に記載の遮光ネット。 3. The light-shielding net according to claim 1, wherein a light-shielding rate of the light-shielding net is 75% or more, air permeability is 200 cm 3 / cm 2 / sec or more, and a weight per unit area is less than 80 g / m 2. .
請求項１〜３のいずれか一項に記載の遮光ネット。 The light-shielding net according to any one of claims 1 to 3, wherein the density of the weft is in a range of 8 / inch to 14 / inch.
請求項１〜４のいずれか一項に記載の遮光ネット。 The light-shielding net according to any one of claims 1 to 4, wherein a width in a short direction of the weft is in a range of 1.0 mm to 4.0 mm.
経糸群の二本の経糸を二本以上の緯糸に絡ませたパターンを含む繰り返しパターンを当該経糸群の繰り返し単位として繰り返し製織するステップと、
一の経糸群における前記パターンの位置を、当該一の経糸群と緯方向に隣接する他の経糸群における前記パターンの位置に対して少なくとも一本の緯糸分だけ経方向にずらして製織するステップと
を備えることを特徴とする遮光ネットの製織方法。
A set of warps of two filaments are arranged at a predetermined interval perpendicular to the weft of a flat yarn, and the two warps of each warp group are entangled so as to cross the weft vertically. A method of weaving a shading net of a woven fabric obtained by
A step of repeatedly weaving a repeating pattern including a pattern in which two warps of a warp group are entangled with two or more wefts as a repeating unit of the warp group;
Weaving by shifting the position of the pattern in one warp group in the warp direction by at least one weft with respect to the position of the pattern in another warp group adjacent to the one warp group in the weft direction; A method for weaving a light-shielding net.