JP2013104009A - Nonaqueous ink composition for inkjet recording and inkjet recording method - Google Patents
Nonaqueous ink composition for inkjet recording and inkjet recording method Download PDFInfo
- Publication number
- JP2013104009A JP2013104009A JP2011249597A JP2011249597A JP2013104009A JP 2013104009 A JP2013104009 A JP 2013104009A JP 2011249597 A JP2011249597 A JP 2011249597A JP 2011249597 A JP2011249597 A JP 2011249597A JP 2013104009 A JP2013104009 A JP 2013104009A
- Authority
- JP
- Japan
- Prior art keywords
- ink composition
- mass
- aqueous ink
- pigment
- inkjet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、インクジェット記録用非水系インク組成物およびそれを用いたインクジェット記録方法に関する。 The present invention relates to a non-aqueous ink composition for ink jet recording and an ink jet recording method using the same.
従来、インクジェット記録用ヘッドのノズルから吐出させた微小なインク滴によって、紙等の吸水性記録媒体上に画像や文字を記録するインクジェット記録方法が知られている。このようなインクジェット記録方法に用いるインクとしては、水を主溶媒とする水系インクが広く普及している。しかしながら、インクジェット記録方法は、近年多様な分野において、種々の記録媒体に対する記録に使用されるようになってきている。特に低吸収性記録媒体を対象とした印刷方式に対応する観点から、従来の水系インクに代えて、溶媒として実質的に水を含まない非水系インクが開発された。 2. Description of the Related Art Conventionally, there is known an ink jet recording method for recording an image or a character on a water-absorbing recording medium such as paper with fine ink droplets ejected from a nozzle of an ink jet recording head. As an ink used for such an ink jet recording method, a water-based ink containing water as a main solvent is widely used. However, ink jet recording methods have recently been used for recording on various recording media in various fields. In particular, a non-aqueous ink that does not substantially contain water as a solvent has been developed in place of the conventional aqueous ink from the viewpoint of corresponding to a printing method for a low-absorbency recording medium.
低吸収性記録媒体を対象とした印刷方式としては、軟包材用グラビア印刷、サニタリー用フレキソ印刷、金属板用シルクスクリーン印刷、屋内外広告用インクジェット印刷等が一般的に知られている。しかしながら、これらの印刷方式に用いられる非水系インクは第2種有機溶剤に該当するトルエン、酢酸エチル、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサン等の溶剤を用いることが一般的であり、環境濃度設定、臭気等から局所排気設備の設置、または定期健康診断等の義務が発生する等取扱いが難しく、より安全衛生性の高い非水系インクが求められてきた。 As printing methods for low-absorbency recording media, gravure printing for soft packaging materials, flexographic printing for sanitary, silk screen printing for metal plates, inkjet printing for indoor and outdoor advertising, etc. are generally known. However, non-aqueous inks used in these printing methods generally use solvents such as toluene, ethyl acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexane, etc., which are the second type organic solvents. Non-water-based inks that are difficult to handle and have higher safety and hygiene have been demanded, such as the installation of local exhaust equipment or the occurrence of regular health checkups.
このような観点から、第2種有機溶剤に非該当である、エチレングリコールモノブチルエーテルアセテート等のグリコールエーテルアセテート類、γ−ブチロラクトン等の環状エステル類等の溶媒を含む非水系インクが提案されている(例えば、特許文献1参照)。 From such a viewpoint, non-aqueous inks containing solvents such as glycol ether acetates such as ethylene glycol monobutyl ether acetate and cyclic esters such as γ-butyrolactone, which are not applicable to the second type organic solvent, have been proposed. (For example, refer to Patent Document 1).
しかしながら、上記のような非水系インクに含まれる溶剤は低吸収性記録媒体の表面を溶解させる能力に乏しいため、低吸収性記録媒体上に記録された画像の定着性が劣る場合があった。また、低吸収性記録媒体は溶媒を吸収する能力が乏しいため、上記のような非水系インクを用いて低吸収性記録媒体上に画像を記録すると、表面乾燥性が著しく低くなる場合があった。また、上記のような非水系インクは、使用する低吸収性記録媒体の種類によっては、記録された画像の滲みが顕著になる場合があった。 However, since the solvent contained in the non-aqueous ink as described above has a poor ability to dissolve the surface of the low-absorbency recording medium, the fixability of an image recorded on the low-absorbency recording medium may be inferior. Further, since the low-absorbency recording medium has a poor ability to absorb the solvent, when the image is recorded on the low-absorbency recording medium using the non-aqueous ink as described above, the surface drying property may be remarkably lowered. . In addition, the non-aqueous ink as described above may have noticeable blurring of the recorded image depending on the type of the low-absorbency recording medium used.
本発明に係る幾つかの態様は、上述の課題の少なくとも一部を解決することで、低吸収性記録媒体に記録される画像の滲みが少なく、画像の定着性および表面乾燥性に優れており、かつ安全衛生性にも優れたインクジェット記録用非水系インク組成物、ならびにそれを用いたインクジェット記録方法を提供することにある。 Some embodiments according to the present invention solve at least a part of the above-described problems, thereby reducing bleeding of an image recorded on a low-absorbency recording medium, and being excellent in image fixability and surface drying. Another object of the present invention is to provide a non-aqueous ink composition for ink jet recording excellent in safety and hygiene, and an ink jet recording method using the same.
本発明は、以下の態様または適用例として実現することができる。 The present invention can be realized as the following aspects or application examples.
[適用例1]
本発明に係るインクジェット記録用非水系インク組成物の一態様は、
下記一般式(1)で表される化合物と、
ラクトン類と、
を含有する。
[Application Example 1]
One aspect of the non-aqueous ink composition for inkjet recording according to the present invention is:
A compound represented by the following general formula (1):
Lactones,
Containing.
(式(1)中、R1は、炭素数1以上4以下のアルキル基を示し、R2およびR3は、メチル基またはエチル基を示す。)
適用例1のインクジェット記録用非水系インク組成物によれば、低吸収性記録媒体(特に、被記録面に塩化ビニル樹脂を含有する記録媒体)に記録された画像の定着性および表面乾燥性を向上させ、かつ滲みの発生を抑制できる。また、従来の非水系インク組成物に使用されていた第2種有機溶剤を低減、あるいは含有しないことが可能となるため、安全衛生性の面でも優れている。
(In Formula (1), R 1 represents an alkyl group having 1 to 4 carbon atoms, and R 2 and R 3 represent a methyl group or an ethyl group.)
According to the non-aqueous ink composition for ink-jet recording of Application Example 1, the fixability and surface drying property of an image recorded on a low-absorbency recording medium (particularly, a recording medium containing a vinyl chloride resin on the recording surface). And the occurrence of bleeding can be suppressed. Moreover, since it is possible to reduce or not contain the second type organic solvent used in the conventional non-aqueous ink composition, it is excellent in terms of safety and hygiene.
[適用例2]
適用例1において、
前記一般式(1)中、R1がメチル基であることができる。
[Application Example 2]
In application example 1,
In the general formula (1), R 1 may be a methyl group.
[適用例3]
適用例1または適用例2において、
前記一般式(1)で表される化合物の含有量[MA(質量%)]と、前記ラクトン類の含有量[MB(質量%)]と、の含有比(MA/MB)が、0.1以上9以下であることができる。
[Application Example 3]
In application example 1 or application example 2,
The content ratio (MA / MB) of the content [MA (% by mass)] of the compound represented by the general formula (1) and the content [MB (% by mass)] of the lactone is 0. It can be 1 or more and 9 or less.
[適用例4]
適用例1ないし適用例3のいずれか1例において、
前記一般式(1)で表される化合物の含有量[MA(質量%)]と、前記ラクトン類の含有量[MB(質量%)]と、の合計(MA+MB)が、6質量%以上40質量%以下であることができる。
[Application Example 4]
In any one of Application Examples 1 to 3,
The sum (MA + MB) of the content [MA (mass%)] of the compound represented by the general formula (1) and the content [MB (mass%)] of the lactone is 6 mass% or more and 40 It can be up to mass%.
[適用例5]
適用例1ないし適用例4のいずれか1例において、
前記ラクトン類が、炭素原子数6以下のラクトンであることができる。
[Application Example 5]
In any one of Application Examples 1 to 4,
The lactone may be a lactone having 6 or less carbon atoms.
[適用例6]
適用例1ないし適用例5のいずれか1例において、
さらに、アルキレングリコール化合物を含有することができる。
[Application Example 6]
In any one of Application Examples 1 to 5,
Furthermore, an alkylene glycol compound can be contained.
[適用例7]
本発明に係るインクジェット記録方法の一態様は、
適用例1ないし適用例6のいずれか1例に記載のインクジェット記録用非水系インク組成物の液滴を吐出して、塩化ビニル系樹脂を含む被記録面に該液滴を付着させて画像を記録する。
[Application Example 7]
One aspect of the inkjet recording method according to the present invention is:
The droplets of the non-aqueous ink composition for ink jet recording described in any one of the application examples 1 to 6 are ejected, and the droplets are attached to the recording surface containing the vinyl chloride resin to form an image. Record.
[適用例8]
適用例7において、
前記被記録面は、凹凸の形状を有しており、
前記凹凸の高低差が、0.01mm以上1mm以下であることができる。
[Application Example 8]
In Application Example 7,
The recording surface has an uneven shape,
The height difference of the unevenness may be 0.01 mm or more and 1 mm or less.
以下に本発明の好適な実施の形態について説明する。以下に説明する実施の形態は、本発明の一例を説明するものである。また、本発明は、以下の実施の形態に限定されるものではなく、本発明の要旨を変更しない範囲において実施される各種の変形例も含む。 Hereinafter, preferred embodiments of the present invention will be described. The embodiment described below describes an example of the present invention. In addition, the present invention is not limited to the following embodiments, and includes various modifications that are implemented within a range that does not change the gist of the present invention.
1.インクジェット記録用非水系インク組成物
本発明の一実施形態に係るインクジェット記録用非水系インク組成物(以下、単に「非水系インク組成物」ともいう。)は、後述する一般式(1)で表される化合物と、ラクトン類と、を含有する。一般式(1)で表される化合物およびラクトン類は、非水系インクの溶媒として機能する有機溶剤である。
1. Non-aqueous ink composition for ink-jet recording The non-aqueous ink composition for ink-jet recording according to one embodiment of the present invention (hereinafter also simply referred to as “non-aqueous ink composition”) is represented by the general formula (1) described below. And lactones. The compound and lactone represented by the general formula (1) are organic solvents that function as a solvent for non-aqueous inks.
本発明において、「非水系インク組成物」とは、インク組成物を製造する際に水を意図的に添加しないという意味であり、インク組成物を製造中または保管中に不可避的に混入する微量の水分を含んでいても構わない。 In the present invention, the term “non-aqueous ink composition” means that water is not intentionally added when the ink composition is produced, and a trace amount that inevitably mixes the ink composition during production or storage. It may also contain water.
以下、本実施形態に係る非水系インク組成物に含まれる成分について、詳細に説明する。 Hereinafter, components contained in the non-aqueous ink composition according to this embodiment will be described in detail.
1.1.有機溶剤
1.1.1一般式(1)で表される化合物
本実施形態に係る非水系インク組成物は、下記一般式(1)で表される化合物を含有する。
1.1. Organic Solvent 1.1.1 Compound Represented by General Formula (1) The non-aqueous ink composition according to this embodiment contains a compound represented by the following general formula (1).
上記式(1)中、R1は、炭素数1以上4以下のアルキル基を示し、R2およびR3は、メチル基またはエチル基を示す。「炭素数1以上4以下のアルキル基」は、直鎖状または分岐状のアルキル基であることができ、例えば、メチル基、エチル基、n−プロピル基、iso−プロピル基、n−ブチル基、sec−ブチル基、iso−ブチル基、tert−ブチル基であることができる。上記式(1)で表される化合物は、1種単独で用いてもよいし、2種以上混合して用いてもよい。 In the above formula (1), R 1 represents an alkyl group having 1 to 4 carbon atoms, and R 2 and R 3 represent a methyl group or an ethyl group. The “alkyl group having 1 to 4 carbon atoms” may be a linear or branched alkyl group such as a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, or an n-butyl group. , Sec-butyl group, iso-butyl group, and tert-butyl group. The compounds represented by the above formula (1) may be used singly or in combination of two or more.
式(1)で表される化合物の機能としては、低吸収性記録媒体上に付着させたインクの表面乾燥性および定着性を高めることが挙げられる。特に、上記式(1)で表される化合物は、塩化ビニル系樹脂を溶解する作用に優れている。そのため、上記式(1)で表される化合物は、塩化ビニル系樹脂を含有する被記録面を溶解して、低吸収性記録媒体の内部にインクを浸透させることができる。このようにインクが低吸収性記録媒体に浸透することで、インクが強固に定着し、かつ、インクの表面が乾燥しやすくなる。したがって、得られる画像は、耐擦性および表面乾燥性に優れたものとなる。 Examples of the function of the compound represented by the formula (1) include improving the surface drying property and fixing property of the ink deposited on the low-absorbency recording medium. In particular, the compound represented by the above formula (1) is excellent in the action of dissolving the vinyl chloride resin. Therefore, the compound represented by the above formula (1) can dissolve the recording surface containing the vinyl chloride resin and allow the ink to penetrate into the low-absorbency recording medium. As the ink penetrates into the low-absorbency recording medium in this way, the ink is firmly fixed and the surface of the ink is easily dried. Therefore, the obtained image is excellent in abrasion resistance and surface dryness.
また、上記式(1)中、R1は、炭素数1のメチル基であることが好ましい。上記式(1)において、R1がメチル基である化合物の標準沸点は、R1の炭素数が2以上4以下のアルキル基である化合物の標準沸点と比較して低い。そのため、上記式(1)において、R1がメチル基である化合物を用いると、記録される画像の表面乾燥性を一層向上できる場合がある。 In the above formula (1), R 1 is preferably a methyl group having 1 carbon atom. In the above formula (1), the standard boiling point of the compound in which R 1 is a methyl group is lower than the standard boiling point of the compound in which R 1 is an alkyl group having 2 to 4 carbon atoms. Therefore, in the above formula (1), when a compound in which R 1 is a methyl group is used, the surface drying property of the recorded image may be further improved.
上記式(1)で表される化合物のHLB値は、8.0以上20.0以下であることが好ましく、8.5以上18.5以下であることがより好ましく、12.0以上18.5以下であることが特に好ましい。上記式(1)で表される化合物のHLB値が上記範囲内にあると、塩化ビニル系樹脂との相互作用の点でより好適となる。なお、本明細書におけるHLB値とは、有機概念図における無極性値(I)と有機性値(O)との比(以下、単に「I/O値」ともいう)から下記式(2)により算出された値である。 The HLB value of the compound represented by the formula (1) is preferably 8.0 or more and 20.0 or less, more preferably 8.5 or more and 18.5 or less, and more preferably 12.0 or more and 18. Particularly preferred is 5 or less. When the HLB value of the compound represented by the formula (1) is within the above range, it is more preferable in terms of interaction with the vinyl chloride resin. In addition, the HLB value in this specification is the following formula (2) from the ratio of the nonpolar value (I) and the organic value (O) in the organic conceptual diagram (hereinafter also simply referred to as “I / O value”). Is a value calculated by
HLB値=(無極性値(I)/有機性値(O))×10 …(2)
具体的には、I/O値は、藤田穆著、「系統的有機定性分析混合物編」、風間書房、1974年;黒木宣彦著、「染色理論化学」、槙書店、1966年;井上博夫著、「有機化合物分離法」、裳華房、1990年、の各文献に基づいて算出することができる。
HLB value = (Nonpolar value (I) / Organic value (O)) × 10 (2)
Specifically, I / O values are written by Atsushi Fujita, “Systematic Organic Qualitative Analysis Mixture”, Kazama Shobo, 1974; Norihiko Kuroki, “Dyeing Theoretical Chemistry”, Sakai Shoten, 1966; Hiroo Inoue , “Organic Compound Separation Method”, Suikabo, 1990.
上記式(1)で表される化合物の含有量は、非水系インク組成物の全質量に対して、1質量%以上30質量%以下であることが好ましく、3質量%以上20質量%以下であることがより好ましく、10質量%以上20質量%以下であることが特に好ましい。上記式(1)で表される化合物の含有量が上記範囲にあることで、画像の耐擦性および表面乾燥性を一層向上できる場合がある。 The content of the compound represented by the above formula (1) is preferably 1% by mass or more and 30% by mass or less, and preferably 3% by mass or more and 20% by mass or less with respect to the total mass of the non-aqueous ink composition. More preferably, it is more preferably 10% by mass or more and 20% by mass or less. When the content of the compound represented by the above formula (1) is in the above range, the abrasion resistance and surface drying property of the image may be further improved.
1.1.2.ラクトン類
本実施形態に係る非水系インク組成物は、ラクトン類を含有する。ラクトン類の機能としては、低吸収性記録媒体上に付着したインクの定着性を向上させることが挙げられる。特に、ラクトン類は、上記式(1)で表される化合物ほどではないが、塩化ビニル系樹脂を溶解する作用が良好であるので、塩化ビニル系樹脂を含有する低吸収性記録媒体に対するインクの定着性を向上させることができる。
1.1.2. Lactones The non-aqueous ink composition according to this embodiment contains lactones. Examples of the function of lactones include improving the fixability of ink deposited on a low-absorbency recording medium. In particular, lactones are not as good as the compounds represented by the above formula (1), but have a good effect of dissolving vinyl chloride resins, so that the ink of a low-absorbency recording medium containing vinyl chloride resins can be used. Fixability can be improved.
ラクトン類としては、炭素原子数6以下のラクトンが好ましく、β−プロピオラクトン、β−ブチロラクトン、γ−ブチロラクトン、γ−バレロラクトン、γ−カプロラクトン、σ−バレロラクトン、ε−カプロラクトンであることがより好ましい。ラクトン類は、1種単独で用いてもよいし、2種以上混合して用いてもよい。 The lactone is preferably a lactone having 6 or less carbon atoms, and is preferably β-propiolactone, β-butyrolactone, γ-butyrolactone, γ-valerolactone, γ-caprolactone, σ-valerolactone, or ε-caprolactone. More preferred. Lactones may be used alone or in combination of two or more.
ラクトン類の含有量は、非水系インク組成物の全質量に対して、1質量%以上30質量%以下であることが好ましく、3質量%以上20質量%以下であることがより好ましく、10質量%以上20質量%以下であることが特に好ましい。ラクトン類の含有量が上記範囲にあることで、画像の耐擦性を向上できる場合がある。 The content of the lactone is preferably 1% by mass or more and 30% by mass or less, more preferably 3% by mass or more and 20% by mass or less, more preferably 10% by mass with respect to the total mass of the non-aqueous ink composition. % To 20% by mass is particularly preferable. When the content of the lactone is in the above range, the abrasion resistance of the image may be improved.
ラクトン類と上記式(1)で表される化合物とを併用すると、これらの化合物の相乗的な作用によって、多様な種類の低吸収性記録媒体に対して画像の滲みの発生を抑制できる。例えば、低吸収性記録媒体を構成する材料が同一であっても、その表面状態によっては、記録された画像に滲みが生じやすくなる場合がある。このような場合に、両化合物(ラクトン類および上記式(1)で表される化合物)を併用することで、低吸収性記録媒体の表面状態に関わらず、滲みの少ない良好な画像を記録できる。 When a lactone and a compound represented by the above formula (1) are used in combination, the occurrence of blurring of an image on various types of low-absorbency recording media can be suppressed by the synergistic action of these compounds. For example, even if the materials constituting the low-absorbency recording medium are the same, depending on the surface state, bleeding may easily occur in the recorded image. In such a case, by using both compounds (the lactones and the compound represented by the above formula (1)) in combination, a good image with little bleeding can be recorded regardless of the surface state of the low-absorbency recording medium. .
上記一般式(1)で表される化合物の含有量[MA(質量%)]と、ラクトン類の含有量[MB(質量%)]と、の含有比(MA/MB)は、0.1以上9以下であることが好ましく、0.5以上2以下であることがより好ましい。両化合物の含有比が上記範囲内にあると、滲みが少なく、表面乾燥性および耐擦性に優れた画像が得られる。 The content ratio (MA / MB) of the content [MA (mass%)] of the compound represented by the general formula (1) and the content of lactones [MB (mass%)] is 0.1. It is preferably 9 or less and more preferably 0.5 or more and 2 or less. When the content ratio of both compounds is within the above range, an image having less bleeding and excellent surface drying and abrasion resistance can be obtained.
また、上記一般式(1)で表される化合物の含有量[MA(質量%)]と、前記ラクトン類の含有量[MB(質量%)]との合計(MA+MB)が、6質量%以上40質量%以下であることが好ましく、10質量%以上40質量%以下であることがより好ましく、20質量%以上30質量%以下であることが特に好ましい。両化合物の含有量の合計が上記範囲内にあることで、滲みが少なく、表面乾燥性および耐擦性に優れた画像が得られる。特に、両化合物の合計が30質量%を超えずにあることで、低吸収性記録媒体上に付着したインク滴を適度な大きさに保つことができるので、インクの埋まりが良好で筋むらの少ない画像が得られる場合がある。また、両化合物がそれぞれ10質量%以上含有されていると、画像の滲みがより一層生じにくくなる場合がある。 The total (MA + MB) of the content [MA (mass%)] of the compound represented by the general formula (1) and the content [MB (mass%)] of the lactone is 6 mass% or more. It is preferably 40% by mass or less, more preferably 10% by mass or more and 40% by mass or less, and particularly preferably 20% by mass or more and 30% by mass or less. When the total content of both compounds is within the above range, an image with less bleeding and excellent surface dryness and abrasion resistance can be obtained. In particular, since the total of both compounds does not exceed 30% by mass, the ink droplets adhering to the low-absorbency recording medium can be maintained in an appropriate size, so that the ink filling is good and the stripes are uneven. In some cases, fewer images may be obtained. Moreover, when both compounds are contained in an amount of 10% by mass or more, bleeding of an image may be more difficult to occur.
1.2.その他の成分
本実施形態に係る非水系インク組成物は、必要に応じて、上述した有機溶剤以外の有機溶剤、界面活性剤、顔料、分散剤等を含有してもよい。
1.2. Other Components The non-aqueous ink composition according to the present embodiment may contain an organic solvent other than the organic solvent described above, a surfactant, a pigment, a dispersant, and the like as necessary.
1.2.1.その他の有機溶剤
本実施形態に係る非水系インク組成物は、塩化ビニル系樹脂に対してインクを強固に定着させる観点から、常温常圧下で液体のアルキレングリコール化合物を含有することが好ましい。
1.2.1. Other Organic Solvent The non-aqueous ink composition according to this embodiment preferably contains an alkylene glycol compound that is liquid at normal temperature and pressure from the viewpoint of firmly fixing the ink to the vinyl chloride resin.
アルキレングリコール化合物としては、国際公開第2002/055619パンフレットに記載されているような、エチレングリコール化合物またはプロピレングリコール化合物であることが好ましい。 The alkylene glycol compound is preferably an ethylene glycol compound or a propylene glycol compound as described in International Publication No. 2002/055619 pamphlet.
本実施形態に係る非水系インク組成物にアルキレングリコール化合物を含有する場合において、印刷特性によって適宜選択することができるが、その含有量は、非水系インク組成物の全質量に対して、20質量%以上85質量%以下であることが好ましい。 In the case where the non-aqueous ink composition according to this embodiment contains an alkylene glycol compound, it can be appropriately selected depending on the printing characteristics, but the content thereof is 20 mass relative to the total mass of the non-aqueous ink composition. % Or more and 85% by mass or less is preferable.
好ましいエチレングリコール化合物としては、エチレングリコール、ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、またはポリエチレングリコールのモノエーテルないしはジエーテルが挙げられ、好ましくはジエチレングリコール化合物である。また、好ましいプロピレングリコール化合物としては、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、またはポリプロピレングリコールのモノエーテルないしはジエーテルが挙げられ、好ましくはジプロピレングリコールである。なお、エチレングリコール化合物のうち、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノエチルエーテルアセテートおよびエチレングリコールモノブチルエーテルは、第2種有機溶剤に分類されるので、取扱いの困難性および環境等への負荷を低減するという観点から、使用しないことが好ましい。 Preferred ethylene glycol compounds include ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, or polyethylene glycol monoethers or diethers, with diethylene glycol compounds being preferred. Preferred propylene glycol compounds include propylene glycol, dipropylene glycol, tripropylene glycol, or polypropylene glycol monoether or diether, preferably dipropylene glycol. Among the ethylene glycol compounds, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate and ethylene glycol monobutyl ether are classified as the second type organic solvent, so that the handling difficulty, environment, etc. From the viewpoint of reducing the load on the battery, it is preferable not to use it.
前記ジエチレングリコール化合物としては、例えば、下記一般式(3)で示されるジエチレングリコール化合物を用いることができる。 As the diethylene glycol compound, for example, a diethylene glycol compound represented by the following general formula (3) can be used.
式(3)中、R4およびR5は、それぞれ独立して、水素原子、炭素数1〜4のアルキル基、またはR6CO基である。R6は、炭素数1〜4のアルキル基である。「炭素数1〜4のアルキル基」は、直鎖状または分岐状のアルキル基であることができ、例えば、メチル基、エチル基、n−プロピル基、iso−プロピル基、n−ブチル基、sec−ブチル基、またはtert−ブチル基であることができる。式(3)で示されるジエチレングリコール化合物の具体例としては、ジエチレングリコール、ジエチレングリコールモノメチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールモノn−ブチルエーテル、ジエチレングリコールジn−ブチルエーテル、ジエチレングリコールブチルメチルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノn−ブチルエーテルアセテート等が挙げられる。 In formula (3), R 4 and R 5 are each independently a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, or an R 6 CO group. R 6 is an alkyl group having 1 to 4 carbon atoms. The “C1-C4 alkyl group” may be a linear or branched alkyl group such as a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, an n-butyl group, It can be a sec-butyl group or a tert-butyl group. Specific examples of the diethylene glycol compound represented by the formula (3) include diethylene glycol, diethylene glycol monomethyl ether, diethylene glycol dimethyl ether, diethylene glycol methyl ethyl ether, diethylene glycol monoethyl ether, diethylene glycol diethyl ether, diethylene glycol mono n-butyl ether, diethylene glycol di n-butyl ether, Examples include diethylene glycol butyl methyl ether, diethylene glycol monoethyl ether acetate, and diethylene glycol mono n-butyl ether acetate.
前記ジプロピレングリコール化合物としては、例えば、下記一般式(4)で示されるジプロピレングリコール化合物を用いることができる。 As the dipropylene glycol compound, for example, a dipropylene glycol compound represented by the following general formula (4) can be used.
式(4)中、R7およびR8は、それぞれ独立して、水素原子、炭素数1〜4のアルキル基、またはR9CO基である。R9は、炭素数1〜4のアルキル基である。「炭素数1〜4のアルキル基」は、直鎖状または分岐状のアルキル基であることができ、例えば、メチル基、エチル基、n−プロピル基、iso−プロピル基、n−ブチル基、sec−ブチル基、またはtert−ブチル基であることができる。式(4)で示されるジプロピレングリコール化合物としては、例えば、ジプロピレングリコール、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル等が挙げられる。 In formula (4), R 7 and R 8 are each independently a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, or an R 9 CO group. R 9 is an alkyl group having 1 to 4 carbon atoms. The “C1-C4 alkyl group” may be a linear or branched alkyl group such as a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, an n-butyl group, It can be a sec-butyl group or a tert-butyl group. Examples of the dipropylene glycol compound represented by the formula (4) include dipropylene glycol, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, and the like.
本実施形態に係る非水系インク組成物において用いることができるジエチレングリコール化合物およびジプロピレングリコール化合物は、それらの沸点が常圧下で、それぞれ好ましくは150℃以上、より好ましくは180℃以上である。 The diethylene glycol compound and dipropylene glycol compound that can be used in the non-aqueous ink composition according to this embodiment preferably have a boiling point of 150 ° C. or higher, more preferably 180 ° C. or higher, respectively, under normal pressure.
また、本実施形態に係る非水系インク組成物において用いることができる前記ジエチレングリコール化合物およびジプロピレングリコール化合物は、それらの20℃での蒸気圧が、好ましくは1hPa以下、より好ましくは0.7hPa以下である。 Further, the diethylene glycol compound and the dipropylene glycol compound that can be used in the non-aqueous ink composition according to the present embodiment have a vapor pressure at 20 ° C. of preferably 1 hPa or less, more preferably 0.7 hPa or less. is there.
前述したような高沸点および低蒸気圧の条件を満たすジエチレングリコール化合物およびジプロピレングリコール化合物を用いることにより、局所的排気設備または排ガス処理設備を設ける負担が軽減され、作業環境の向上が可能となり、また周辺環境への環境負荷も軽減することが可能となる。 By using a diethylene glycol compound and a dipropylene glycol compound that satisfy the high boiling point and low vapor pressure conditions as described above, the burden of installing a local exhaust facility or exhaust gas treatment facility is reduced, and the work environment can be improved. It is also possible to reduce the environmental load on the surrounding environment.
本実施形態に係る非水系インク組成物は、前述したジエチレングリコール化合物、ジプロピレングリコール化合物、ないしそれらの混合物に加えて、さらに、常温常圧下で液体であり、下記一般式(5)で示されるポリアルキレングリコール化合物を含有してもよい。 In addition to the diethylene glycol compound, dipropylene glycol compound, or mixture thereof described above, the non-aqueous ink composition according to the present embodiment is a liquid at normal temperature and pressure, and is represented by the following general formula (5). An alkylene glycol compound may be contained.
式(5)中、R10は、炭素数2以上3以下のアルキレン基である。R11およびR12は、それぞれ独立して、水素原子または炭素数1〜6のアルキル基(好ましくは炭素数1〜4のアルキル基)である。nは、3〜6の整数である。炭素数2以上3以下のアルキレン基としては、例えば、エチレン基およびプロピレン基が挙げられる。「炭素数1〜6のアルキル基」は、直鎖状または分岐状のアルキル基であることができ、例えば前記「炭素数1〜4のアルキル基」に加えて、直鎖状もしくは分岐状のペンチル基またはヘキシル基であることができる。 In Formula (5), R 10 is an alkylene group having 2 to 3 carbon atoms. R 11 and R 12 are each independently a hydrogen atom or an alkyl group having 1 to 6 carbon atoms (preferably an alkyl group having 1 to 4 carbon atoms). n is an integer of 3-6. Examples of the alkylene group having 2 to 3 carbon atoms include an ethylene group and a propylene group. The “C 1-6 alkyl group” may be a linear or branched alkyl group. For example, in addition to the “C 1-4 alkyl group”, a linear or branched alkyl group may be used. It can be a pentyl group or a hexyl group.
本実施形態に係る非水系インク組成物において用いることができる前記ポリアルキレングリコール化合物は、その沸点が常圧下で、好ましくは200℃以上、より好ましくは250℃以上である。また、その引火点は、好ましくは100℃以上、より好ましくは130℃以上である。このようなポリアルキレングリコール化合物を用いることにより、非水系インク組成物に揮発抑制性を付与することができる。例えば、インクカートリッジからインクジェット記録用ヘッドへ非水系インク組成物を輸送するチューブ内での非水系インク組成物の揮発を抑制することにより、チューブ内での固形分の堆積を防止ないし軽減することができる。 The polyalkylene glycol compound that can be used in the non-aqueous ink composition according to this embodiment has a boiling point of 200 ° C. or higher, more preferably 250 ° C. or higher, under normal pressure. The flash point is preferably 100 ° C. or higher, more preferably 130 ° C. or higher. By using such a polyalkylene glycol compound, volatilization suppression can be imparted to the non-aqueous ink composition. For example, by suppressing the volatilization of the non-aqueous ink composition in the tube that transports the non-aqueous ink composition from the ink cartridge to the inkjet recording head, it is possible to prevent or reduce the accumulation of solids in the tube. it can.
好ましいポリアルキレングリコール化合物としては、例えば、ポリアルキレングリコールモノアルキルエーテル、ポリアルキレングリコールジアルキルエーテル等が挙げられる。これらの化合物は、1種単独で用いてもよいし、2種以上混合して用いてもよい。 Preferred polyalkylene glycol compounds include, for example, polyalkylene glycol monoalkyl ether, polyalkylene glycol dialkyl ether and the like. These compounds may be used individually by 1 type, and may be used in mixture of 2 or more types.
ポリアルキレングリコールモノアルキルエーテルとしては、例えば、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノブチルエーテル、トリプロピレングリコールモノブチルエーテル、前記一般式(5)においてnが4以上6以下であるポリエチレングリコールモノブチルエーテル、テトラエチレングリコールモノメチルエーテル、ペンタエチレングリコールモノメチルエーテル、ヘキサエチレングリコールモノメチルエーテル等が挙げられる。 Examples of the polyalkylene glycol monoalkyl ether include triethylene glycol monomethyl ether, triethylene glycol monobutyl ether, tripropylene glycol monobutyl ether, polyethylene glycol monobutyl ether in which n is 4 or more and 6 or less in the general formula (5), tetra Examples include ethylene glycol monomethyl ether, pentaethylene glycol monomethyl ether, and hexaethylene glycol monomethyl ether.
ポリアルキレングリコールジアルキルエーテルとしては、テトラエチレングリコールジメチルエーテルが挙げられる。 Examples of the polyalkylene glycol dialkyl ether include tetraethylene glycol dimethyl ether.
また、本実施形態に係る非水系インク組成物は、前記例示した有機溶剤の他に、以下に例示する有機溶剤をさらに含有してもよい。 Further, the non-aqueous ink composition according to this embodiment may further contain an organic solvent exemplified below in addition to the organic solvent exemplified above.
その他の有機溶剤としては、好ましくは極性有機溶媒、例えば、アルコール類(例えば、エチルアルコール、1−プロパノール、フッ化アルコール等)、エーテル類(例えば、ジエチルエーテル、ジプロピルエーテル等)等が挙げられる。 Other organic solvents are preferably polar organic solvents such as alcohols (eg, ethyl alcohol, 1-propanol, fluorinated alcohol, etc.), ethers (eg, diethyl ether, dipropyl ether, etc.) and the like. .
なお、本実施形態に係る非水系インク組成物は、取扱いの容易性および環境負荷の低減等の観点から、第2種有機溶剤(労働安全衛生法施行令の別表第六の二参照)を含有しないことが好ましい。 In addition, the non-aqueous ink composition according to the present embodiment contains a second type organic solvent (see Attached Table 6-2 of the Industrial Safety and Health Act Enforcement Ordinance) from the viewpoint of ease of handling and reduction of environmental load. Preferably not.
1.2.2.界面活性剤
本実施形態に係る非水系インク組成物には、前記有機溶剤の他に、表面張力を低下させ記録媒体との濡れ性を向上させる観点から、シリコン系界面活性剤、フッ素系界面活性剤、または非イオン性界面活性剤であるポリオキシエチレン誘導体を添加してもよい。
1.2.2. Surfactant In addition to the organic solvent, the non-aqueous ink composition according to the embodiment includes a silicon surfactant, a fluorine-based surfactant, from the viewpoint of reducing surface tension and improving wettability with a recording medium. An agent or a polyoxyethylene derivative that is a nonionic surfactant may be added.
シリコン系界面活性剤としては、ポリエステル変性シリコンやポリエーテル変性シリコンを用いることが好ましい。具体例としては、BYK−347、348、BYK−UV3500、3510、3530、3570(いずれもビックケミー・ジャパン社製)が挙げられる。 As the silicon surfactant, it is preferable to use polyester-modified silicon or polyether-modified silicon. Specific examples include BYK-347, 348, BYK-UV3500, 3510, 3530, 3570 (all manufactured by Big Chemie Japan).
フッ素系界面活性剤としては、フッ素変性ポリマーを用いることが好ましく、具体例としては、BYK−340(ビックケミー・ジャパン社製)が挙げられる。 As the fluorine-based surfactant, a fluorine-modified polymer is preferably used, and specific examples thereof include BYK-340 (manufactured by BYK Japan).
また、ポリオキシエチレン誘導体としては、アセチレングリコール系界面活性剤を用いることが好ましい。具体例としては、サーフィノール82、104、465、485、TG(いずれもエアープロダクツジャパン社製)、オルフィンSTG、E1010(いずれも日信化学株式会社製)、ニッサンノニオンA−10R、A−13R(いずれも日油株式会社製)、フローレンTG−740W、D−90(共栄社化学株式会社製)、ノイゲンCX−100(第一工業製薬株式会社製)等が挙げられる。 As the polyoxyethylene derivative, it is preferable to use an acetylene glycol surfactant. Specific examples include Surfinol 82, 104, 465, 485, TG (all manufactured by Air Products Japan), Olphine STG, E1010 (all manufactured by Nissin Chemical Co., Ltd.), Nissan Nonion A-10R, A-13R. (All manufactured by NOF Corporation), Floren TG-740W, D-90 (manufactured by Kyoeisha Chemical Co., Ltd.), Neugen CX-100 (manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) and the like.
本実施形態に係る非水系インク組成物中における界面活性剤の含有量は、好ましくは0.05質量%以上3質量%以下、より好ましくは0.5質量%以上2質量%以下である。 The content of the surfactant in the non-aqueous ink composition according to this embodiment is preferably 0.05% by mass to 3% by mass, more preferably 0.5% by mass to 2% by mass.
1.2.3.顔料
本実施形態に係る非水系インク組成物には、色材として、従来の非水系インク組成物に通常用いられている有色無機顔料または有色有機顔料等の顔料を用いることができる。これらの顔料は、1種単独で用いてもよいし、2種以上混合して用いてもよい。
1.2.3. Pigment In the non-aqueous ink composition according to this embodiment, a pigment such as a colored inorganic pigment or a colored organic pigment that is usually used in a conventional non-aqueous ink composition can be used as a color material. These pigments may be used alone or in combination of two or more.
顔料としては、例えば、アゾレーキ、不溶性アゾ顔料、縮合アゾ顔料、キレートアゾ顔料等のアゾ顔料;フタロシアニン顔料、ペリレンおよびペリレン顔料、アントラキノン顔料、キナクリドン顔料、ジオキサンジン顔料、チオインジゴ顔料、イソインドリノン顔料、キノフタロニ顔料等の多環式顔料;塩基性染料型レーキ、酸性染料型レーキ等の染料レーキ;ニトロ顔料、ニトロソ顔料、アニリンブラック、昼光蛍光顔料等の有機顔料;カーボンブラック等の無機顔料等が挙げられる。顔料粒子の平均一次粒径は、特に限定されるものではないが、好ましくは50nm以上500nm以下である。 Examples of the pigment include azo pigments such as azo lake, insoluble azo pigment, condensed azo pigment, chelate azo pigment; phthalocyanine pigment, perylene and perylene pigment, anthraquinone pigment, quinacridone pigment, dioxazine pigment, thioindigo pigment, isoindolinone pigment, quinophthalone Polycyclic pigments such as pigments; dye lakes such as basic dye type lakes and acid dye type lakes; organic pigments such as nitro pigments, nitroso pigments, aniline black, daylight fluorescent pigments; inorganic pigments such as carbon black It is done. The average primary particle size of the pigment particles is not particularly limited, but is preferably 50 nm or more and 500 nm or less.
本実施形態に係る非水系インク組成物をマゼンタまたはレッドインクとする場合の顔料としては、例えば、C.I.ピグメントレッド2、C.I.ピグメントレッド3、C.I.ピグメントレッド5、C.I.ピグメントレッド6、C.I.ピグメントレッド7、C.I.ピグメントレッド15、C.I.ピグメントレッド16、C.I.ピグメントレッド48:1、C.I.ピグメントレッド53:1、C.I.ピグメントレッド57:1、C.I.ピグメントレッド122、C.I.ピグメントレッド123、C.I.ピグメントレッド139、C.I.ピグメントレッド144、C.I.ピグメントレッド149、C.I.ピグメントレッド166、C.I.ピグメントレッド170、C.I.ピグメントレッド177、C.I.ピグメントレッド178、C.I.ピグメントレッド194、C.I.ピグメントレッド209、C.I.ピグメントレッド222、C.I.ピグメントレッド224等が挙げられる。 Examples of the pigment when the non-aqueous ink composition according to this embodiment is magenta or red ink include C.I. I. Pigment red 2, C.I. I. Pigment red 3, C.I. I. Pigment red 5, C.I. I. Pigment red 6, C.I. I. Pigment red 7, C.I. I. Pigment red 15, C.I. I. Pigment red 16, C.I. I. Pigment red 48: 1, C.I. I. Pigment red 53: 1, C.I. I. Pigment red 57: 1, C.I. I. Pigment red 122, C.I. I. Pigment red 123, C.I. I. Pigment red 139, C.I. I. Pigment red 144, C.I. I. Pigment red 149, C.I. I. Pigment red 166, C.I. I. Pigment red 170, C.I. I. Pigment red 177, C.I. I. Pigment red 178, C.I. I. Pigment red 194, C.I. I. Pigment red 209, C.I. I. Pigment red 222, C.I. I. And CI Pigment Red 224.
本実施形態に係る非水系インク組成物をオレンジまたはイエローインクとする場合の顔料としては、例えば、C.I.ピグメントオレンジ31、C.I.ピグメントオレンジ43、C.I.ピグメントオレンジ64、C.I.ピグメントイエロー12、C.I.ピグメントイエロー13、C.I.ピグメントイエロー14、C.I.ピグメントイエロー15、C.I.ピグメントイエロー17、C.I.ピグメントイエロー74、C.I.ピグメントイエロー93、C.I.ピグメントイエロー94、C.I.ピグメントイエロー128、C.I.ピグメントイエロー138、C.I.ピグメントイエロー150、C.I.ピグメントイエロー180等が挙げられる。 Examples of the pigment when the non-aqueous ink composition according to this embodiment is an orange or yellow ink include C.I. I. Pigment orange 31, C.I. I. Pigment orange 43, C.I. I. Pigment orange 64, C.I. I. Pigment yellow 12, C.I. I. Pigment yellow 13, C.I. I. Pigment yellow 14, C.I. I. Pigment yellow 15, C.I. I. Pigment yellow 17, C.I. I. Pigment yellow 74, C.I. I. Pigment yellow 93, C.I. I. Pigment yellow 94, C.I. I. Pigment yellow 128, C.I. I. Pigment yellow 138, C.I. I. Pigment yellow 150, C.I. I. And CI Pigment Yellow 180.
本実施形態に係る非水系インク組成物をグリーンまたはシアンインクとする場合の顔料としては、例えば、C.I.ピグメントブルー15、C.I.ピグメントブルー15:2、C.I.ピグメントブルー15:3、C.I.ピグメントブルー16、C.I.ピグメントブルー60、C.I.ピグメントグリーン7、C.I.ピグメントグリーン36等が挙げられる。 Examples of the pigment when the non-aqueous ink composition according to this embodiment is a green or cyan ink include C.I. I. Pigment blue 15, C.I. I. Pigment blue 15: 2, C.I. I. Pigment blue 15: 3, C.I. I. Pigment blue 16, C.I. I. Pigment blue 60, C.I. I. Pigment green 7, C.I. I. And CI Pigment Green 36.
本実施形態に係る非水系インク組成物をブラックインクとする場合の顔料としては、例えば、カーボンブラック等が挙げられる。 Examples of the pigment when the non-aqueous ink composition according to this embodiment is a black ink include carbon black.
本実施形態に係る非水系インク組成物をホワイトインクとする場合の顔料としては、例えば、Pigment White 6、18、21等が挙げられる。 Examples of the pigment when the non-aqueous ink composition according to this embodiment is a white ink include Pigment White 6, 18, 21 and the like.
本実施形態に係る非水系インク組成物中における顔料の含有量は、用途や印刷特性によって適宜選択することができるが、好ましくは0.5質量%以上25質量%以下、より好ましくは0.5質量%以上15質量%以下、特に好ましくは1質量%以上10質量%以下である。 The content of the pigment in the non-aqueous ink composition according to this embodiment can be appropriately selected depending on the application and printing characteristics, but is preferably 0.5% by mass or more and 25% by mass or less, more preferably 0.5%. The content is from 1% by mass to 15% by mass, particularly preferably from 1% by mass to 10% by mass.
本実施形態に係る非水系インク組成物には、顔料の分散安定性を向上させる観点から、通常の非水系インク組成物において用いられる任意の分散剤を用いることができる。分散剤としては、有機溶媒の溶解パラメーターが8〜11であるときに有効に作用する分散剤を用いることが好ましい。このような分散剤の具体例としては、ヒノアクトKF1−M、T−6000、T−7000、T−8000、T−8350P、T−8000E(いずれも武生ファインケミカル株式会社製)等のポリエステル系高分子化合物、Solsperse20000、24000、32000、32500、33500、34000、35200、37500(いずれもLUBRIZOL社製)、Disperbyk−161、162、163、164、166、180、190、191、192(いずれもビックケミー・ジャパン社製)、フローレンDOPA−17、22、33、G−700(いずれも共栄社化学株式会社製)、アジスパーPB821、PB711(いずれも味の素株式会社製)、LP4010、LP4050、LP4055、POLYMER400、401、402、403、450、451、453(いずれもEFKAケミカルズ社製)等が挙げられる。 In the non-aqueous ink composition according to this embodiment, any dispersant used in a normal non-aqueous ink composition can be used from the viewpoint of improving the dispersion stability of the pigment. As the dispersant, it is preferable to use a dispersant that works effectively when the solubility parameter of the organic solvent is 8 to 11. Specific examples of such a dispersant include polyester polymers such as Hinoact KF1-M, T-6000, T-7000, T-8000, T-8350P, and T-8000E (all manufactured by Takefu Fine Chemical Co., Ltd.). Compound, Solsperse 20000, 24000, 32000, 32500, 33500, 34000, 35200, 37500 (all manufactured by LUBRIZOL), Disperbyk-161, 162, 163, 164, 166, 180, 190, 191, 192 (all are Big Chemie Japan) ), Floren DOPA-17, 22, 33, G-700 (all manufactured by Kyoeisha Chemical Co., Ltd.), Ajisper PB821, PB711 (all manufactured by Ajinomoto Co., Inc.), LP4010, LP4050, LP4055, P LYMER400,401,402,403,450,451,453 (both EFKA Chemicals Co., Ltd.), and the like.
本実施形態に係る非水系インク組成物において、前記分散剤の含有量は、分散すべき顔料によって適宜選択することができるが、非水系インク組成物中の顔料の含有量100質量部に対して、好ましくは5質量部以上200質量部以下、より好ましくは30質量部以上120質量部以下である。 In the non-aqueous ink composition according to this embodiment, the content of the dispersant can be appropriately selected depending on the pigment to be dispersed, but with respect to 100 parts by mass of the pigment in the non-aqueous ink composition. Preferably, it is 5 to 200 mass parts, More preferably, it is 30 to 120 mass parts.
1.2.4.その他の成分
本実施形態に係る非水系インク組成物には、さらに通常の非水系インク組成物に含まれるその他の添加剤を添加してもよい。その他の添加剤としては、例えば、酸化防止剤や紫外線吸収剤等の安定剤、バインダー樹脂等が挙げられる。
1.2.4. Other components The non-aqueous ink composition according to the present embodiment may further contain other additives contained in a normal non-aqueous ink composition. Examples of other additives include stabilizers such as antioxidants and ultraviolet absorbers, and binder resins.
酸化防止剤としては、例えばBHA(2,3−ブチル−4−オキシアニソール)、BHT(2,6−ジ−t−ブチル−p−クレゾール)等が挙げられる。 Examples of the antioxidant include BHA (2,3-butyl-4-oxyanisole), BHT (2,6-di-t-butyl-p-cresol) and the like.
紫外線吸収剤としては、例えばベンゾフェノン系化合物、ベンゾトリアゾール系化合物等が挙げられる。 Examples of the ultraviolet absorber include benzophenone compounds and benzotriazole compounds.
本実施形態に係る非水系インク組成物は、インクの粘度を調整する目的でバインダー樹脂を添加してもよい。バインダー樹脂としては、例えばアクリル樹脂、スチレンアクリル樹脂、ロジン変性樹脂、フェノール樹脂、テルペン系樹脂、ポリエステル樹脂、ポリアミド樹脂、エポキシ樹脂、塩化ビニル酢酸ビニル共重合体樹脂、セルロースアセテートブチレート等の繊維系樹脂、ビニルトルエン−α−メチルスチレン共重合体樹脂等が挙げられる。これらのバインダー樹脂は、1種単独で用いてもよく、2種以上混合して用いてもよい。なお、バインダー樹脂は、その添加量により塩化ビニル系樹脂に対するインクの定着性をさらに良好とすることもできる。 In the non-aqueous ink composition according to this embodiment, a binder resin may be added for the purpose of adjusting the viscosity of the ink. Examples of the binder resin include acrylic resins, styrene acrylic resins, rosin modified resins, phenol resins, terpene resins, polyester resins, polyamide resins, epoxy resins, vinyl chloride vinyl acetate copolymer resins, cellulose acetate butyrate, and the like. Resin, vinyltoluene-α-methylstyrene copolymer resin, and the like. These binder resins may be used alone or in combination of two or more. The binder resin can further improve the fixability of the ink to the vinyl chloride resin depending on the amount of the binder resin added.
1.3.非水系インク組成物の製造方法
本実施形態に係る非水系インク組成物は、公知の慣用方法によって製造することができる。色材として顔料を用いる場合には、最初に、顔料、分散剤、および有機溶剤(一部分)を混合した後、ボールミル、ビーズミル、超音波、またはジェットミル等で顔料分散液を調製し、所望のインク特性を有するように調整する。続いて、有機溶剤(残量)、およびその他の添加剤(例えば、界面活性剤やバインダー樹脂)を撹拌下に加えて非水系インク組成物を得ることができる。
1.3. Method for Producing Non-Aqueous Ink Composition The non-aqueous ink composition according to this embodiment can be produced by a known conventional method. In the case of using a pigment as a colorant, first, a pigment, a dispersant, and an organic solvent (partial) are mixed, and then a pigment dispersion is prepared by a ball mill, a bead mill, an ultrasonic wave, a jet mill or the like, Adjust to have ink characteristics. Subsequently, an organic solvent (remaining amount) and other additives (for example, a surfactant and a binder resin) can be added with stirring to obtain a non-aqueous ink composition.
1.4.物性
本実施形態に係る非水系インク組成物は、記録品質とインクジェット用インク組成物としての信頼性とのバランスの観点から、20℃における表面張力が20mN/m以上50mN/mであることが好ましく、25mN/m以上40mN/m以下であることがより好ましい。なお、表面張力の測定は、自動表面張力計CBVP−Z(協和界面科学社製)を用いて、20℃の環境下で白金プレートをインクで濡らしたときの表面張力を確認することにより測定することができる。
1.4. Physical Properties The non-aqueous ink composition according to this embodiment preferably has a surface tension at 20 ° C. of 20 mN / m or more and 50 mN / m from the viewpoint of the balance between recording quality and reliability as an ink composition for inkjet. 25 mN / m or more and 40 mN / m or less is more preferable. The surface tension is measured by using an automatic surface tension meter CBVP-Z (manufactured by Kyowa Interface Science Co., Ltd.) by confirming the surface tension when the platinum plate is wetted with ink in an environment of 20 ° C. be able to.
また、同様の観点から、本実施形態に係る非水系インク組成物の20℃における粘度は、2mPa・s以上15mPa・s以下であることが好ましく、2mPa・s以上10mPa・s以下であることがより好ましい。なお、粘度の測定は、粘弾性試験機MCR−300(Pysica社製)を用いて、20℃の環境下で、Shear Rateを10〜1000に上げていき、Shear Rate200時の粘度を読み取ることにより測定することができる。 From the same viewpoint, the viscosity at 20 ° C. of the non-aqueous ink composition according to this embodiment is preferably 2 mPa · s to 15 mPa · s, and preferably 2 mPa · s to 10 mPa · s. More preferred. The viscosity is measured by using a viscoelasticity tester MCR-300 (manufactured by Pysica), increasing the Shear Rate to 10 to 1000 in an environment of 20 ° C., and reading the viscosity at Shear Rate 200. Can be measured.
2.インクジェット記録方法
本実施形態に係るインクジェット記録方法は、前述した非水系インク組成物の液滴を吐出し、低吸収性記録媒体に該液滴を付着させて画像を記録する。
2. Inkjet recording method The inkjet recording method according to this embodiment ejects droplets of the non-aqueous ink composition described above, and attaches the droplets to a low-absorbency recording medium to record an image.
本明細書において「低吸収性記録媒体」とは、ブリストー(Bristow)法において接触開始から30msec1/2までの水吸収量が10mL/m2以下である記録媒体のことをいい、少なくとも被記録面がこの性質を備えていればよい。このブリストー法は、短時間での液体吸収量の測定方法として最も普及している方法であり、日本紙パルプ技術協会(JAPAN TAPPI)でも採用されている。試験方法の詳細は、「JAPAN TAPPI紙パルプ試験方法2000年版」の規格No.51「紙及び板紙−液体吸収性試験方法−ブリストー法」に述べられている。なお、低吸収性記録媒体には、水を全く吸収しない非吸収性記録媒体も含まれる。 In the present specification, the “low-absorbency recording medium” refers to a recording medium having a water absorption amount of 10 mL / m 2 or less from the start of contact to 30 msec 1/2 in the Bristow method, and at least the recording target The surface only needs to have this property. This Bristow method is the most popular method for measuring the amount of liquid absorbed in a short time, and is also adopted by the Japan Paper Pulp Technology Association (JAPAN TAPPI). For details of the test method, refer to Standard No. of “JAPAN TAPPI Paper Pulp Test Method 2000”. 51 "Paper and paperboard-Liquid absorbency test method-Bristow method". The low-absorbency recording medium includes a non-absorbent recording medium that does not absorb water at all.
低吸収性記録媒体としては、具体的には、低吸収性の材料を含むシート、フィルム、繊維製品等が挙げられる。また、低吸収性記録媒体は、基材(例えば、紙、繊維、皮革、プラスチック、ガラス、セラミックス、金属等)の表面に、低吸収性の材料を含む層(以下、「低吸収性層」ともいう。)を備えたものであってもよい。低吸収性の材料としては、特に限定されないが、オレフィン系樹脂、エステル系樹脂、ウレタン系樹脂、アクリル系樹脂、塩化ビニル系樹脂等が挙げられる。 Specific examples of the low-absorbency recording medium include sheets, films, and textile products containing a low-absorbency material. The low-absorbency recording medium is a layer containing a low-absorbency material (hereinafter referred to as “low-absorbency layer”) on the surface of a substrate (for example, paper, fiber, leather, plastic, glass, ceramics, metal, etc.). May also be provided). Although it does not specifically limit as a low absorptive material, Olefin resin, ester resin, urethane resin, acrylic resin, vinyl chloride resin etc. are mentioned.
これらの中でも、低吸収性記録媒体としては、塩化ビニル系樹脂を含む被記録面を有するものを好ましく用いることができる。塩化ビニル系樹脂の具体例としては、ポリ塩化ビニル樹脂、塩化ビニル−エチレン共重合体樹脂、塩化ビニル−酢酸ビニル共重合体樹脂、塩化ビニル−ビニルエーテル共重合体樹脂、塩化ビニル−塩化ビニリデン共重合体樹脂、塩化ビニル−マレイン酸エステル共重合体樹脂、塩化ビニル−(メタ)アクリル酸共重合体樹脂、塩化ビニル−(メタ)アクリル酸エステル共重合体樹脂、塩化ビニル−ウレタン共重合体樹脂等の塩化ビニル系共重合体樹脂が挙げられ、これらを単独、あるいは2種類以上組み合わせて用いることもできる。なお、本明細書において、「(メタ)アクリル」は、アクリルおよびそれに対応するメタクリルのうち少なくともいずれか一方を意味する。 Among these, as the low-absorbency recording medium, one having a recording surface containing a vinyl chloride resin can be preferably used. Specific examples of the vinyl chloride resin include polyvinyl chloride resin, vinyl chloride-ethylene copolymer resin, vinyl chloride-vinyl acetate copolymer resin, vinyl chloride-vinyl ether copolymer resin, vinyl chloride-vinylidene chloride copolymer Polymer resin, vinyl chloride-maleic acid ester copolymer resin, vinyl chloride- (meth) acrylic acid copolymer resin, vinyl chloride- (meth) acrylic acid ester copolymer resin, vinyl chloride-urethane copolymer resin, etc. These may be used alone or in combination of two or more. In the present specification, “(meth) acryl” means at least one of acrylic and methacryl corresponding thereto.
ところで、理由は定かではないが、低吸収性記録媒体の表面が凹凸であると、記録媒体に付着したインク滴が流動し、記録された画像に滲みが生じる場合がある。本実施形態に係る非水系インクによれば、低吸収性記録媒体は、平滑な被記録面(凹凸の高低差が0.01mm未満)を備えるものだけではなく、被記録面に凹凸の形状を有するものも好ましく用いることができる。当該凹凸の高低差は、0.01mm以上1mm以下であることが好ましく、光学顕微鏡等を用いて測定される。凹凸形状は、エンボス加工等の公知の加工方法によって形成されてもよいし、被記録面に低吸収性層を備える記録媒体を用いる場合には、低吸収性層の下地層に由来して形成されてもよい。 By the way, although the reason is not clear, if the surface of the low-absorbency recording medium is uneven, ink droplets attached to the recording medium may flow and bleeding may occur in the recorded image. According to the non-aqueous ink according to the present embodiment, the low-absorbency recording medium is not only provided with a smooth recording surface (difference in height of the unevenness of less than 0.01 mm), but also has an uneven shape on the recording surface. What has is also preferably used. The height difference of the unevenness is preferably 0.01 mm or more and 1 mm or less, and is measured using an optical microscope or the like. The concavo-convex shape may be formed by a known processing method such as embossing, or when a recording medium having a low-absorbent layer on the recording surface is used, it is derived from the underlying layer of the low-absorbent layer May be.
下地層に由来して形成される凹凸形状は、具体的には、繊維基布(例えば、織物、編み物、不織布等)の下地層に低吸収性層を積層させて、繊維基布の表面に低吸収性層を沿わせることで形成できる。繊維基布に用いられる材料(繊維)としては、ポリエチレン繊維、ポリプロピレン繊維、ポリエステル繊維、ナイロン繊維、ビニロン繊維などの合成繊維、木綿、麻、絹、羊毛等の天然繊維が挙げられる。 Specifically, the uneven shape formed from the base layer is formed by laminating a low-absorbency layer on the base layer of a fiber base fabric (for example, woven fabric, knitted fabric, non-woven fabric, etc.) It can be formed by placing a low absorption layer. Examples of materials (fibers) used for the fiber base fabric include synthetic fibers such as polyethylene fiber, polypropylene fiber, polyester fiber, nylon fiber, and vinylon fiber, and natural fibers such as cotton, hemp, silk, and wool.
なお、低吸収性記録媒体の厚み、形状、色、軟化温度、硬さ等の諸特性は、特に限定されるものではない。 Various characteristics such as thickness, shape, color, softening temperature, and hardness of the low-absorbency recording medium are not particularly limited.
前述した非水系インク組成物には、前記一般式(1)で表される化合物と、ラクトン類とが含まれており、両化合物は、塩化ビニル系樹脂を溶解する作用に優れ、かつ、相乗作用によって画像の滲みを抑制する作用に優れる。そのため、本実施形態に係るインクジェット記録方法は、塩化ビニル系樹脂を含有する被記録面に前述した非水系インク組成物の液滴を付着させることで、滲みが少なく、定着性および表面乾燥性により一層優れた画像を記録できる。 The non-aqueous ink composition described above contains the compound represented by the general formula (1) and lactones, and both compounds are excellent in the action of dissolving the vinyl chloride resin and are synergistic. The action is excellent in suppressing the bleeding of the image. Therefore, the ink jet recording method according to the present embodiment has less blur due to adhesion of the droplets of the non-aqueous ink composition described above to the recording surface containing the vinyl chloride resin, and thereby has a fixing property and a surface drying property. A better image can be recorded.
本実施形態に係るインクジェット記録方法に用いるインクジェット記録装置は、特に限定されないが、ドロップオンデマンド型のインクジェット記録装置が好ましい。ドロップオンデマンド型のインクジェット記録装置には、記録ヘッドに配設された圧電素子を用いて記録を行う圧電素子記録方法を採用したもの、記録ヘッドに配設された発熱抵抗素子のヒーター等による熱エネルギーを用いて記録を行う熱ジェット記録方法を採用したもの等があるが、いずれの記録方法も採用することができる。また、本実施の形態に係る非水系インク組成物は、撥インク処理された吐出ノズル表面に対して不活性であるという利点を有するので、例えば撥インク処理された吐出ノズル表面を有するインクジェット記録用ヘッドから吐出させるインクジェット記録方法に有利に用いることができる。 The ink jet recording apparatus used in the ink jet recording method according to the present embodiment is not particularly limited, but a drop-on-demand ink jet recording apparatus is preferable. The drop-on-demand ink jet recording apparatus employs a piezoelectric element recording method in which recording is performed using a piezoelectric element disposed in a recording head, and heat generated by a heater of a heating resistance element disposed in the recording head. There are methods that employ a thermal jet recording method in which recording is performed using energy, and any recording method can be employed. Further, since the non-aqueous ink composition according to the present embodiment has an advantage that it is inactive with respect to the discharge nozzle surface subjected to the ink repellent treatment, for example, for inkjet recording having the discharge nozzle surface subjected to the ink repellent treatment. It can be advantageously used in an ink jet recording method for discharging from a head.
3.実施例
以下、本発明の実施形態を実施例および比較例によってさらに具体的に説明するが、本実施形態はこれらの実施例のみに限定されるものではない。
3. Examples Hereinafter, embodiments of the present invention will be described more specifically with reference to examples and comparative examples. However, the present embodiment is not limited to only these examples.
3.1.有機溶剤の合成
3.1.1.下記式(6)で表される化合物
撹拌装置、熱電対および窒素ガス導入管を備えた300mlセパラブルフラスコに、N,N−ジメチルアクリルアミド19.828gおよびメタノール6.408gを入れ、窒素ガスを導入しながら撹拌した。次に、ナトリウム t−ブトキシド0.338gを加え、35℃で4時間反応を行った。加熱終了後、リン酸150mgを加え、溶液を均一にした後、3時間放置した。溶液を濾過して、析出物を除去し、さらにエバポレーターで未反応物を除いた。このようにして、下記式(6)で表される化合物(以下、「有機溶剤A」ともいう。)を得た。
3.1. Synthesis of organic solvent 3.1.1. Compound represented by the following formula (6) Into a 300 ml separable flask equipped with a stirrer, a thermocouple and a nitrogen gas inlet tube, 19.828 g of N, N-dimethylacrylamide and 6.408 g of methanol were introduced, and nitrogen gas was introduced. While stirring. Next, 0.338 g of sodium t-butoxide was added and reacted at 35 ° C. for 4 hours. After completion of heating, 150 mg of phosphoric acid was added to make the solution uniform, and the mixture was allowed to stand for 3 hours. The solution was filtered to remove precipitates, and unreacted substances were removed with an evaporator. In this way, a compound represented by the following formula (6) (hereinafter also referred to as “organic solvent A”) was obtained.
なお、得られた有機溶剤Aの、有機概念図におけるI/O値から上記式(2)により算出されたHLB値は、18.3であった。 In addition, the HLB value calculated by the said Formula (2) from the I / O value in an organic conceptual diagram of the obtained organic solvent A was 18.3.
3.1.2.下記式(7)で表される化合物
撹拌装置、熱電対および窒素ガス導入管を備えた300mlセパラブルフラスコに、N,N−ジメチルアクリルアミド19.828gおよび1−ブタノール14.824gを入れ、窒素ガスを導入しながら撹拌した。次に、ナトリウム t−ブトキシド0.338gを加え、35℃で4時間反応を行った。加熱終了後、リン酸150mgを加え、溶液を均一にした後、3時間放置した。溶液を濾過して、析出物を除去し、さらにエバポレーターで未反応物を除いた。このようにして、下記式(7)で表される化合物(以下、「有機溶剤B」ともいう。)を得た。
3.1.2. Compound represented by the following formula (7) Into a 300 ml separable flask equipped with a stirrer, a thermocouple and a nitrogen gas introduction tube, 19.828 g of N, N-dimethylacrylamide and 14.824 g of 1-butanol were added, and nitrogen gas was added. Was stirred while being introduced. Next, 0.338 g of sodium t-butoxide was added and reacted at 35 ° C. for 4 hours. After completion of heating, 150 mg of phosphoric acid was added to make the solution uniform, and the mixture was allowed to stand for 3 hours. The solution was filtered to remove precipitates, and unreacted substances were removed with an evaporator. In this way, a compound represented by the following formula (7) (hereinafter also referred to as “organic solvent B”) was obtained.
なお、得られた溶剤Bの、有機概念図におけるI/O値から上記式(2)により算出されたHLB値は、12.2であった。 In addition, the HLB value calculated by the said Formula (2) from the I / O value in an organic conceptual diagram of the obtained solvent B was 12.2.
3.2.非水系インク組成物の調製
容器に、表1〜2に記載の濃度に相当する量の有機溶剤をそれぞれのインク毎に投入し、マグネティックスターラーを用いて30分間混合撹拌して混合溶剤を得た。
3.2. Preparation of non-aqueous ink composition Into a container, an organic solvent in an amount corresponding to the concentrations shown in Tables 1 and 2 was added for each ink, and mixed and stirred for 30 minutes using a magnetic stirrer to obtain a mixed solvent. .
得られた混合溶剤の一部を取り分けて、そこにSolsperse37500(LUBRIZOL社製、商品名)およびC.I.ピグメントブラック7(三菱化学株式会社製、商品名「CARBON BLACK #970」)を所定量添加して、ホモジナイザーを用いて粉砕処理した。その後、直径0.3mmのジルコニアビーズを充填したビーズミルで分散処理を行うことにより、顔料分散液(顔料の平均粒子径:150nm)を得た。 Part of the obtained mixed solvent was separated, and Solsperse 37500 (trade name, manufactured by LUBRIZOL) and C.I. I. A predetermined amount of CI Pigment Black 7 (trade name “CARBON BLACK # 970” manufactured by Mitsubishi Chemical Corporation) was added, and the mixture was pulverized using a homogenizer. Then, a pigment dispersion (average particle diameter of pigment: 150 nm) was obtained by performing a dispersion treatment with a bead mill filled with zirconia beads having a diameter of 0.3 mm.
得られた顔料分散液に、有機溶剤の残部およびBYK−340(ビックケミー・ジャパン株式会社製、フッ素系界面活性剤)、パラロイドB60(ローム・アンド・ハース社製、アクリル樹脂)を添加してさらに1時間混合撹拌してから、5μmのPTFE製メンブランフィルターを用いて濾過することで、表1〜2に記載のブラックインク組成物を得た。なお、表中の数値は、質量%を表す。 To the obtained pigment dispersion, the remainder of the organic solvent, BYK-340 (BIC Chemie Japan Co., Ltd., fluorinated surfactant), and Paraloid B60 (Rohm and Haas Co., acrylic resin) are further added. After mixing and stirring for 1 hour, the black ink composition described in Tables 1 and 2 was obtained by filtering using a 5 μm PTFE membrane filter. In addition, the numerical value in a table | surface represents the mass%.
なお、表中で使用した材料は、下記の通りである。
・C.I.ピグメントブラック7(三菱化学株式会社製、商品名「CARBON BLACK #970」、ブラック顔料)
・Solsperse37500(商品名、LUBRIZOL社製、分散剤)
・γ−ブチロラクトン(関東化学株式会社製、有機溶剤)
・γ−バレロラクトン(関東化学株式会社製、有機溶剤)
・σ−バレロラクトン(関東化学株式会社製、有機溶剤)
・ジエチレングリコールジエチルエーテル(日本乳化剤株式会社製、有機溶剤)
・ジエチレングリコールエチルメチルエーテル(商品名「ハイソルブEDM」、東邦化学工業株式会社製、有機溶剤)
・テトラエチレングリコールジメチルエーテル(商品名「ハイソルブMETM」、東邦化学工業株式会社製、有機溶剤)
・BYK−340(商品名、ビックケミー・ジャパン株式会社製、フッ素系界面活性剤)
The materials used in the table are as follows.
・ C. I. Pigment Black 7 (Mitsubishi Chemical Corporation, trade name “Carbon Black # 970”, black pigment)
・ Solsperse 37500 (trade name, manufactured by LUBRIZOL, dispersant)
・ Γ-Butyrolactone (manufactured by Kanto Chemical Co., Inc., organic solvent)
・ Γ-valerolactone (organic solvent, manufactured by Kanto Chemical Co., Inc.)
・ Σ-valerolactone (manufactured by Kanto Chemical Co., Inc., organic solvent)
・ Diethylene glycol diethyl ether (Nippon Emulsifier Co., Ltd., organic solvent)
・ Diethylene glycol ethyl methyl ether (trade name “Hisolv EDM”, manufactured by Toho Chemical Co., Ltd., organic solvent)
・ Tetraethylene glycol dimethyl ether (trade name “Hisolv METM”, manufactured by Toho Chemical Industry Co., Ltd., organic solvent)
-BYK-340 (trade name, manufactured by BYK Japan, fluorinated surfactant)
3.3.評価試験
3.3.1.摩擦堅牢性試験
JローランドDG社製プリンター「SP−300V」を用いて、「3.2.非水系インク組成物の調製」で得られた各インク組成物を光沢ポリ塩化ビニルシート(ローランドDG社製、「SV−G−1270G」)上にDuty100%の条件で印刷した。その後、常温にて1日間乾燥させることで、評価用サンプルを得た。
3.3. Evaluation test 3.3.1. Friction fastness test Using a printer "SP-300V" manufactured by J Roland DG, each ink composition obtained in "3.2. Preparation of non-aqueous ink composition" And “SV-G-1270G”), and printing was performed under the condition of Duty 100%. Then, the sample for evaluation was obtained by making it dry at normal temperature for 1 day.
次に、日本工業規格「JIS L 0849」に準拠して、評価用サンプルについてI型試験機にて乾式試験を行った。その後、試験綿布のOD値をスペクトロリーノ(グレタグマクベス社製)にて測定した。なお、評価基準は、以下の通りである。評価結果を表1および表2に併せて示す。
6:OD値が0.20未満
5:OD値が0.20以上0.25未満
4:OD値が0.25以上0.30未満
3:OD値が0.30以上0.35未満
2:OD値が0.35以上0.40未満
1:OD値が0.40以上
Next, in accordance with Japanese Industrial Standard “JIS L 0849”, a dry test was performed on an evaluation sample using an I-type testing machine. Thereafter, the OD value of the test cotton fabric was measured with Spectrolino (manufactured by Gretag Macbeth). The evaluation criteria are as follows. An evaluation result is combined with Table 1 and Table 2, and is shown.
6: OD value is less than 0.20 5: OD value is 0.20 or more and less than 0.25 4: OD value is 0.25 or more and less than 0.30 3: OD value is 0.30 or more and less than 0.35 2: OD value is 0.35 or more and less than 0.40 1: OD value is 0.40 or more
3.3.2.表面乾燥性試験
JローランドDG社製プリンター「SP−300V」を用いて、「3.2.非水系インク組成物の調製」で得られた各インク組成物を光沢ポリ塩化ビニルシート(ローランドDG社製、「SV−G−1270G」)上にDuty100%の条件で印刷した後、5分間乾燥させた。次いで、巻き取り装置を用いて光沢ポリ塩化ビニルシートを巻き取った後の光沢面のスリ痕を観察した。スリ痕の観察は、形状測定レーザマイクロスコープ(株式会社キーエンス製、「VK−8700 GenerationII」)にて表面粗さを測定することで、スリ痕のある面積の割合を算出した。なお、評価基準は、以下の通りである。評価結果を表1および表2に併せて示す。
6:スリ痕面積が0%
5:スリ痕面積が0%超10%未満
4:スリ痕面積が10%以上20%未満
3:スリ痕面積が20%以上30%未満
2:スリ痕面積が30%以上40%未満
1:スリ痕面積が40%以上
3.3.2. Surface dryness test Using a printer “SP-300V” manufactured by J Roland DG, each ink composition obtained in “3.2. Preparation of Non-Water-Based Ink Composition” was used as a glossy polyvinyl chloride sheet (Roland DG). (“SV-G-1270G”) manufactured under the condition of 100% duty, and then dried for 5 minutes. Next, the scratch marks on the glossy surface after the glossy polyvinyl chloride sheet was wound up using a winder were observed. The scratch marks were observed by measuring the surface roughness with a shape measurement laser microscope (manufactured by Keyence Corporation, “VK-8700 Generation II”) to calculate the ratio of the area with the scratch marks. The evaluation criteria are as follows. An evaluation result is combined with Table 1 and Table 2, and is shown.
6: Scratch area is 0%
5: Scratch area is more than 0% and less than 10% 4: Scratch area is 10% or more and less than 20% 3: Scratch area is 20% or more and less than 30% 2: Scratch area is 30% or more and less than 40% 1: Scratch area is 40% or more
3.3.3.滲み性試験
JローランドDG社製プリンター「SP−300V」を用いて、「3.2.非水系インク組成物の調製」で得られた各インク組成物を塩ビバナーシート(3M社製、IJ8451、被記録面に凹凸形状を有する低吸収性記録媒体)、および光沢ポリ塩化ビニルシート(ローランドDG社製、「SV−G−1270G」、平滑な被記録面を有する低吸収性記録媒体)上に、Duty100%の条件で、アルファベットA〜Z(大文字および小文字)をフォントサイズ20ポイントで印刷した後、60分間乾燥させた。その後、肉眼でにじみを観察した。
3.3.3. Bleeding test Using a printer “SP-300V” manufactured by J Roland DG, each ink composition obtained in “3.2. Preparation of non-aqueous ink composition” was used as a PVC banner sheet (3J, IJ8451, On a recording surface with a low-absorbency recording medium) and a glossy polyvinyl chloride sheet ("SV-G-1270G", low-absorption recording medium with a smooth recording surface) manufactured by Roland DG. The alphabets A to Z (uppercase and lowercase) were printed at a font size of 20 points under the condition of 100% duty, and then dried for 60 minutes. Thereafter, bleeding was observed with the naked eye.
なお、印刷前の塩ビバナーシートの表面を形状測定レーザマイクロスコープ(株式会社キーエンス製、「VK−8700 GenerationII」)で観察して、表面の凹凸形状を10点ランダムに選択した。そして、その凹凸の高低差を測定したところ、10点の算術平均が0.26mm(最小値0.12mm、最大値0.37mm)であった。 In addition, the surface of the PVC banner sheet before printing was observed with a shape measurement laser microscope (manufactured by Keyence Corporation, “VK-8700 Generation II”), and the surface unevenness shape was randomly selected at 10 points. And when the height difference of the unevenness was measured, the arithmetic average of 10 points was 0.26 mm (minimum value 0.12 mm, maximum value 0.37 mm).
また、評価基準は、以下の通りである。評価結果を表1および表2に併せて示す。
3:滲みが認められない
2:すべての文字を容易に判別でき、滲みがほとんど認められない
1:すべての文字をかろうじて判別できるが、滲みがはっきりと認められる
The evaluation criteria are as follows. An evaluation result is combined with Table 1 and Table 2, and is shown.
3: No bleeding is observed 2: All characters can be easily distinguished, and almost no bleeding is observed 1: All characters can be barely distinguished, but bleeding is clearly recognized
3.3.4.ドットサイズの判定試験
JローランドDG社製プリンター「SP−300V」を用いて、「3.2.非水系インク組成物の調製」で得られた各インク組成物を塩ビバナーシート(3M社製、IJ8451)上に、ドット同士が重ならない条件で印刷を行った。具体的には、Duty30%の条件で3cmの正方形を印刷した後、60分間乾燥させた。その後、光学顕微鏡を用いてドットサイズを観察して、直径を10μm毎に分類した。評価結果を表1および表2に併せて示す。なお、ドットサイズが80μm以下であれば、300dpi以上の解像度を有する画像を印刷することができる。
3.3.4. Dot size determination test Using a printer “SP-300V” manufactured by J Roland DG, each ink composition obtained in “3.2. Preparation of non-aqueous ink composition” was used as a PVC banner sheet (manufactured by 3M, IJ8451) was printed on the condition that the dots did not overlap each other. Specifically, a 3 cm square was printed under a duty of 30%, and then dried for 60 minutes. Then, the dot size was observed using the optical microscope, and the diameter was classified every 10 μm. An evaluation result is combined with Table 1 and Table 2, and is shown. If the dot size is 80 μm or less, an image having a resolution of 300 dpi or more can be printed.
3.3.5.評価結果
実施例1〜実施例9によれば、有機溶剤に上記式(1)で表される化合物およびラクトン類を併用することで、表面乾燥性および耐擦性に優れることが示された。また、これらの有機溶剤の相乗効果により、表面状態の異なる低吸収性記録媒体に対しても、滲みの発生の少ない優れた画像が得られることが示された。
3.3.5. Evaluation Results According to Examples 1 to 9, it was shown that the use of the compound represented by the above formula (1) and the lactone in combination with an organic solvent is excellent in surface drying property and abrasion resistance. In addition, it was shown that an excellent image with less blurring can be obtained on low-absorbency recording media having different surface states due to the synergistic effect of these organic solvents.
比較例1〜比較例3によれば、上記式(1)で表される化合物およびラクトン類を併用していないため、優れた画像が得られなかった。特に、ドット同士が重なる条件では、被記録面に凹凸形状を有する低吸収性記録媒体に対して、画像の滲みが生じた。また、比較例3によれば、上記式(1)で表される化合物を用いなかったため、摩擦堅牢性および表面乾燥性も良好ではなかった。 According to Comparative Examples 1 to 3, an excellent image could not be obtained because the compound represented by the above formula (1) and lactones were not used in combination. In particular, under the condition where dots overlap each other, blurring of an image occurred on a low-absorbency recording medium having an uneven shape on the recording surface. Moreover, according to the comparative example 3, since the compound represented by the said Formula (1) was not used, friction fastness and surface dryness were also not favorable.
本発明は、前述した実施形態に限定されるものではなく、種々の変形が可能である。例えば、本発明は、実施形態で説明した構成と実質的に同一の構成(例えば、機能、方法および結果が同一の構成、あるいは目的および効果が同一の構成)を含む。また、本発明は、実施形態で説明した構成の本質的でない部分を置き換えた構成を含む。また、本発明は、実施形態で説明した構成と同一の作用効果を奏する構成または同一の目的を達成することができる構成を含む。また、本発明は、実施形態で説明した構成に公知技術を付加した構成を含む。 The present invention is not limited to the embodiments described above, and various modifications are possible. For example, the present invention includes substantially the same configuration (for example, a configuration having the same function, method, and result, or a configuration having the same purpose and effect) as the configuration described in the embodiment. In addition, the invention includes a configuration in which a non-essential part of the configuration described in the embodiment is replaced. In addition, the present invention includes a configuration that achieves the same effect as the configuration described in the embodiment or a configuration that can achieve the same object. In addition, the invention includes a configuration in which a known technique is added to the configuration described in the embodiment.
Claims (8)
ラクトン類と、
を含有する、インクジェット記録用非水系インク組成物。
Lactones,
A non-aqueous ink composition for inkjet recording, comprising:
前記一般式(1)中、R1がメチル基である、インクジェット記録用非水系インク組成物。 In claim 1,
The non-aqueous ink composition for inkjet recording whose R < 1 > is a methyl group in the said General formula (1).
前記一般式(1)で表される化合物の含有量[MA(質量%)]と、前記ラクトン類の含有量[MB(質量%)]と、の含有比(MA/MB)が、0.1以上9以下である、インクジェット記録用非水系インク組成物。 In claim 1 or claim 2,
The content ratio (MA / MB) of the content [MA (% by mass)] of the compound represented by the general formula (1) and the content [MB (% by mass)] of the lactone is 0. A non-aqueous ink composition for inkjet recording, which is 1 or more and 9 or less.
前記一般式(1)で表される化合物の含有量[MA(質量%)]と、前記ラクトン類の含有量[MB(質量%)]と、の合計(MA+MB)が、6質量%以上40質量%以下である、インクジェット記録用非水系インク組成物。 In any one of Claims 1 thru | or 3,
The sum (MA + MB) of the content [MA (mass%)] of the compound represented by the general formula (1) and the content [MB (mass%)] of the lactone is 6 mass% or more and 40 A non-aqueous ink composition for ink-jet recording, having a mass% or less.
前記ラクトン類が、炭素原子数6以下のラクトンである、インクジェット記録用非水系インク組成物。 In any one of Claims 1 thru | or 4,
A non-aqueous ink composition for ink jet recording, wherein the lactone is a lactone having 6 or less carbon atoms.
さらに、アルキレングリコール化合物を含有する、インクジェット記録用非水系インク組成物。 In any one of Claims 1 thru | or 5,
Furthermore, the non-aqueous ink composition for inkjet recording containing an alkylene glycol compound.
前記被記録面は、凹凸の形状を有しており、
前記凹凸の高低差が、0.01mm以上1mm以下である、インクジェット記録方法。 In claim 7,
The recording surface has an uneven shape,
The ink jet recording method, wherein the unevenness of the unevenness is 0.01 mm or more and 1 mm or less.