JP2013092432A - Life estimation of metallic material due to occurrence of stress corrosion crack, and inspection planning system for structure used under corrosive water environment - Google Patents
Life estimation of metallic material due to occurrence of stress corrosion crack, and inspection planning system for structure used under corrosive water environment Download PDFInfo
- Publication number
- JP2013092432A JP2013092432A JP2011234144A JP2011234144A JP2013092432A JP 2013092432 A JP2013092432 A JP 2013092432A JP 2011234144 A JP2011234144 A JP 2011234144A JP 2011234144 A JP2011234144 A JP 2011234144A JP 2013092432 A JP2013092432 A JP 2013092432A
- Authority
- JP
- Japan
- Prior art keywords
- scc
- occurrence
- lower limit
- oxide film
- metal material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、腐食環境下で使用される構造物を構成する金属材料の応力腐食割れ(SCC)の発生寿命評価方法及び検査計画策定システムに係り、特に、高温水環境を有する発電プラントに適用するのに好適なSCC発生寿命評価方法および及び検査計画策定システムに関する。 The present invention relates to a stress corrosion cracking (SCC) occurrence life evaluation method and an inspection plan formulation system of a metal material constituting a structure used in a corrosive environment, and particularly to a power plant having a high-temperature water environment. The present invention relates to an SCC generation life evaluation method and an inspection plan formulation system suitable for the above.
発電プラントは高い稼働率で長期間運転されることが望ましい。発電プラントを安全かつ高い稼働率で長期間運転するためには、発電プラント構造物に対して適切な時期に検査を行い、予防保全、的確なメンテナンスおよび機器交換を行うことが必要であり、検査等は発電プラントの構造物に対する高精度な寿命評価方法に基づいて行われることが望ましい。特に高温水環境を有する発電プラント損傷の主要な要因の一つである、構造物の金属材料に発生する応力腐食割れ(以下SCC)に対しては、定期検査以外で日常的に状態をモニタリングすることが難しいことと、発生した場合の影響が大きいことから、検査および対策の必要性を明確にし、未然に的確な予防保全を実施する必要がある。そのため、SCC発生寿命を高精度かつ定量的に予測する寿命評価技術開発が不可欠であると指摘されてきた。 It is desirable that the power plant be operated for a long time at a high operating rate. In order to operate a power plant for a long time at a safe and high operating rate, it is necessary to inspect the power plant structure at an appropriate time, and to perform preventive maintenance, accurate maintenance, and equipment replacement. Etc. are preferably performed based on a highly accurate life evaluation method for a power plant structure. Especially for stress corrosion cracking (hereinafter referred to as SCC) occurring in metal materials of structures, which is one of the main causes of damage to power plants with high-temperature water environments, the status is monitored on a daily basis other than periodic inspections. Because it is difficult and the impact when it occurs, it is necessary to clarify the necessity of inspections and countermeasures and to carry out accurate preventive maintenance beforehand. Therefore, it has been pointed out that it is essential to develop a life evaluation technology for predicting the SCC occurrence life with high accuracy and quantitatively.
発電プラント構造物を構成する金属材料に対するSCCの診断は定期検査における目視判断や非破壊検査等に依存している。しかし、SCCの目視判断や非破壊検査等による検査は時間がかかり、定期検査の際に、すべての部位を検査するのは非効率的である。したがって、SCCを発生する可能性の有無を事前に判断することで、検査の必要な部位を効率的に特定することが望ましい。 The diagnosis of SCC for the metal material constituting the power plant structure depends on visual judgment, non-destructive inspection, etc. in periodic inspection. However, inspection by visual judgment of SCC, non-destructive inspection, etc. takes time, and it is inefficient to inspect all parts at the time of regular inspection. Therefore, it is desirable to efficiently specify a site that needs to be examined by determining in advance whether or not there is a possibility of generating SCC.
SCC発生寿命評価方法に関する従来技術として、実験室でのSCC発生加速試験と実環境におけるSCC発生寿命分布は同じ指数分布モデルに近似できることを前提に、SCC発生に影響を及ぼす材料・環境・応力の要因に対して加速試験の結果から各々のSCC発生加速因子に対する裕度評価が進められてきた。例えば、特許文献1では、寿命を評価したい構造物と同様の環境に、構造物に使用されている金属材料を所定の負荷応力をかけて複数個浸漬してSCC発生加速試験を行う。その結果から、SCC発生加速試験における金属材料の最小SCC発生寿命を求め、実験室的に求めた応力裕度及び鋭敏化裕度と、実機の推定応力と推定鋭敏化度の関係から、実機のSCC発生寿命を推定している。 As a conventional technology related to the SCC generation life evaluation method, assuming that the SCC generation acceleration test in the laboratory and the SCC generation life distribution in the actual environment can be approximated by the same exponential distribution model, the material, environment, and stress that affect the SCC generation The tolerance evaluation for each SCC generation acceleration factor has been advanced from the result of the acceleration test for the factor. For example, in Patent Document 1, an SCC generation acceleration test is performed by immersing a plurality of metal materials used in a structure under a predetermined load stress in the same environment as the structure whose life is to be evaluated. From the result, the minimum SCC generation life of the metal material in the SCC generation acceleration test is obtained, and from the relationship between the stress tolerance and sensitization tolerance obtained in the laboratory, the estimated stress of the actual machine and the estimated sensitization degree, SCC life is estimated.
また、特許文献2には、金属材料表面の皮膜中のボイドが移動して集合することで皮膜が破壊した箇所でSCCが発生するメカニズムを前提に、皮膜中のボイド移動速度を監視して、予め取得した皮膜中のボイド移動速度と応力腐食割れ発生確率の関係から、当該部材のSCC発生確率を求める方法が開示されている。
In addition,
しかし、従来技術では以下のような課題がある。 However, the conventional techniques have the following problems.
特許文献1では、寿命を評価したい構造物と同様の環境での金属材料に対するSCC発生加速試験でのSCC発生寿命から、実機でのSCC発生寿命を求めている。そのためには実験室での試験データの拡充が不可欠であり、SCC発生試験に長時間が必要である。特に、近年、より優れた耐SCC特性を有する改良材料が研究・開発されており、このような高耐食材のSCC発生試験には更に時間が必要である。 In Patent Document 1, the SCC generation life in the actual machine is obtained from the SCC generation life in the SCC generation acceleration test for the metal material in the same environment as the structure whose life is to be evaluated. For this purpose, it is indispensable to expand test data in the laboratory, and a long time is required for the SCC generation test. In particular, recently, improved materials having better SCC resistance have been researched and developed, and more time is required for the SCC generation test of such a high corrosion resistance material.
また、加速条件下でのSCC発生寿命に加速要因係数を乗ずることにより、実機でのSCC発生寿命を求めており、SCC発生寿命を律速する要因とメカニズムが考慮されていないため、構造物の当該部位に対する真に定量的なSCC発生寿命を評価することができない。 In addition, the SCC generation life in the actual machine is obtained by multiplying the SCC generation life under the acceleration condition by the acceleration factor coefficient, and the factors and mechanisms that determine the SCC generation life are not considered. A truly quantitative SCC generation lifetime for a site cannot be evaluated.
特許文献2では、SCCの起点となる皮膜割れの発生を予測・検知して、当該部位のSCC発生確率を求めるものであり、定量的なSCC発生寿命を予測するものではない。また、SCC発生寿命を律速する要因とメカニズムが、本願発明者が新たに見出した知見(実施形態にて詳述)と異なる。
In
本発明の目的は、腐食環境下で使用される構造物を構成する金属材料に対して、応力腐食割れ(SCC)が発生するまでの寿命を定量的に評価できる方法を提供することにある。 An object of the present invention is to provide a method capable of quantitatively evaluating the life until stress corrosion cracking (SCC) occurs for a metal material constituting a structure used in a corrosive environment.
(1)上記目的を達成するために、本発明は、 腐食水環境下で使用される構造物を構成する金属材料の応力腐食割れ(以下SCC)発生寿命評価方法であって、前記金属材料の表面で成長する酸化皮膜が破壊され、前記金属材料が腐食水環境中に露出するとき、前記金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値を求める下限値取得ステップと、前記構造物実機を再現した腐食水環境下で、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求める下限値到達時間取得ステップと、前記構造物の運転履歴および運転計画に基づき、表面酸化皮膜の破壊要因となるイベントであって、前記下限値到達後に発生するイベントを想定し、SCC発生可能性の有無を前記構造物の各部位ごとに検討するSCC発生可能性検討ステップとを有し、前記SCC発生可能性検討ステップにおいて、SCC発生可能性有と判断する部位に対し、前記イベント発生時を当該部位のSCC発生寿命と評価するものとする。 (1) In order to achieve the above object, the present invention is a stress corrosion cracking (hereinafter referred to as SCC) occurrence life evaluation method of a metal material constituting a structure used in a corrosive water environment, When the oxide film growing on the surface is destroyed and the metal material is exposed to a corrosive water environment, a lower limit value obtaining step for obtaining a lower limit value of the surface oxide film thickness indicating SCC generation sensitivity of the metal material, and the structure In a corrosive water environment that reproduces a real machine, based on a lower limit value arrival time obtaining step for obtaining a time until the surface oxide film thickness reaches the lower limit value, an operation history and an operation plan of the structure, An event that causes an oxide film destruction, and an event that occurs after reaching the lower limit value, and examines the possibility of occurrence of SCC for each part of the structure. And a step in the SCC likelihood study step, to the site to determine the occurrence of SCC possibility Yes, the time of the event occurrence shall be evaluated as SCC generation lifetime of the site.
このような構成により、腐食環境下で使用される構造物を構成する金属材料に対して、応力腐食割れ(SCC)が発生するまでの寿命を定量的に評価できる。 With such a configuration, the life until stress corrosion cracking (SCC) occurs can be quantitatively evaluated for a metal material constituting a structure used in a corrosive environment.
本発明は、金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値に着目するものであり、時間軸の概念から切り離される。このため、時間軸の概念に基づく従来技術に比べて、短時間でSCC発生寿命を評価できる。 The present invention focuses on the lower limit of the thickness of the surface oxide film showing the SCC generation sensitivity of the metal material, and is separated from the concept of the time axis. For this reason, compared with the prior art based on the concept of a time axis, SCC generation lifetime can be evaluated in a short time.
さらに、下限値到達時間を求めることにより、下限値到達時間後に発生するイベントを想定できる。たとえば、部位ごとに検査後再稼動時に各部位に負荷される動的ひずみを想定できる。これにより、SCC発生可能性の有無を各部位ごとに検討でき、SCC発生寿命を各部位ごとに評価できる。その結果、実機検査において優先的、重点的に検査する部位を特定でき、検査項数削減に寄与できる。 Furthermore, an event occurring after the lower limit value arrival time can be assumed by obtaining the lower limit value arrival time. For example, it is possible to assume a dynamic strain applied to each part at the time of restart after inspection for each part. Thereby, the presence or absence of possibility of SCC generation can be examined for each part, and the SCC generation life can be evaluated for each part. As a result, it is possible to identify the parts to be preferentially and preferentially examined in the actual machine inspection, which can contribute to the reduction of the number of inspection items.
(2)上記(1)において、好ましくは、前記下限値取得ステップは、前記金属材料と同一材料の試験片を加速条件環境中に浸漬し、被膜厚さの異なる複数の試験片を形成する浸漬試験と、前記浸漬した試験片に引張応力を負荷するSCC試験とを含み、SCC試験時のSCC発生の有無から表面酸化皮膜厚さの下限値を求めるものである。 (2) In the above (1), preferably, the lower limit acquisition step includes immersing a test piece of the same material as the metal material in an accelerated condition environment to form a plurality of test pieces having different film thicknesses. The test includes a test and an SCC test in which tensile stress is applied to the immersed test piece, and the lower limit of the thickness of the surface oxide film is determined from the presence or absence of SCC during the SCC test.
これにより、表面酸化皮膜厚さの下限値を求めることができる。 Thereby, the lower limit of the surface oxide film thickness can be obtained.
(3)上記(2)において、好ましくは、前記SCC試験は、前記試験片に負荷する最大負荷応力値と、前記最大負荷応力値よりも所定の値低い初期負荷応力値と、ひずみ速度とをあらかじめ設定し、腐食環境下で前記試験片に対して前記初期負荷応力値で荷重した後に前記最大負荷応力値まで前記ひずみ速度を保ちながら徐々に荷重を増大させる動的荷重負荷過程と、前記最大負荷応力値に到達した後に該最大負荷応力値を荷重し続ける定荷重負荷過程とを含むものとする。 (3) In the above (2), preferably, the SCC test includes a maximum load stress value applied to the test piece, an initial load stress value lower than the maximum load stress value by a predetermined value, and a strain rate. Dynamic load application process in which the load is gradually increased while the strain rate is maintained up to the maximum load stress value after being set in advance and loaded at the initial load stress value on the test piece in a corrosive environment, and the maximum And a constant load loading process of continuing to load the maximum load stress value after reaching the load stress value.
これにより、より確実にSCC試験ができる。 Thereby, the SCC test can be performed more reliably.
(4)上記(1)において、好ましくは、前記下限値到達時間取得ステップは、前記金属材料と同一材料の試験片を実機条件環境中に浸漬して、表面酸化皮膜厚さの経時変化を求め、前記経時変化より、表面酸化皮膜厚さの成長予測式を求め、前記成長予測式より、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求めるものである。 (4) In the above (1), preferably, the lower limit arrival time obtaining step includes immersing a test piece of the same material as the metal material in an actual machine condition environment to obtain a change with time in the surface oxide film thickness. The growth prediction formula for the surface oxide film thickness is obtained from the change over time, and the time until the surface oxide film thickness reaches the lower limit value is obtained from the growth prediction formula.
これにより、下限値到達時間を求めることができる。 Thereby, the lower limit arrival time can be obtained.
(5)上記(1)において、好ましくは、前記SCC発生可能性検討ステップにおいて想定するイベントは、前記構造物の稼働及び再稼動である。 (5) In the above (1), preferably, the event assumed in the SCC occurrence possibility examination step is the operation and restart of the structure.
構造物の検査後の再稼動に伴う温度と圧力の上昇は、表面酸化皮膜の破壊要因となる。 The rise in temperature and pressure accompanying the restart after inspection of the structure becomes a cause of destruction of the surface oxide film.
(6)上記目的を達成するために、本発明は、腐食水環境下で使用される構造物を構成する金属材料の表面で成長する酸化皮膜が破壊され、前記金属材料が腐食水環境中に露出するとき、前記金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値を設定する下限値設定手段と、前記構造物実機を再現した腐食水環境下で、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求める下限値到達時間取得手段と、前記構造物の運転履歴、検査計画を含む運転計画および表面酸化皮膜の破壊要因となるイベント発生時の前記構造物の各部位ごとの特性を記憶する記憶手段と、前記イベントが前記下限値到達後に発生すると想定する場合に、SCC発生可能性を検討する部位を選択する検討部位選択手段と、前記検討部位選択手段により選択された部位がSCC発生可能性有と判断された場合、当該部位を実機検査する部位と特定する検査部位特定手段とを備えるものである。 (6) To achieve the above object, according to the present invention, an oxide film growing on the surface of a metal material constituting a structure used in a corrosive water environment is destroyed, and the metal material is in a corrosive water environment. When exposed, a lower limit value setting means for setting a lower limit value of the surface oxide film thickness indicating the SCC generation sensitivity of the metal material, and the surface oxide film thickness in a corrosive water environment reproducing the actual structure. Lower limit arrival time acquisition means for obtaining a time until the lower limit value is reached, each of the structure at the time of occurrence of an event that causes destruction of the surface oxide film, an operation plan including an operation history of the structure, an inspection plan, and an inspection plan Storage means for storing characteristics for each part; examination part selection means for selecting a part for examining the possibility of occurrence of SCC when the event is assumed to occur after reaching the lower limit; and If Ri selected site is judged to SCC likelihood Yes, those comprising an inspection site specifying means for specifying a site where the site to actual testing.
本発明によれば、腐食環境下で使用される金属材料に対して、SCCが発生するまでの寿命を定量的に評価できる。 ADVANTAGE OF THE INVENTION According to this invention, the lifetime until SCC generate | occur | produces can be evaluated quantitatively with respect to the metal material used in a corrosive environment.
更に、本発明は、金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値に着目するものであり、時間軸の概念から切り離される。このため、時間軸の概念に基づく従来技術と比較し、短時間でSCC発生寿命を評価できる。 Furthermore, the present invention pays attention to the lower limit value of the surface oxide film thickness indicating the SCC generation sensitivity of the metal material, and is separated from the concept of the time axis. For this reason, compared with the prior art based on the concept of a time axis, the SCC occurrence lifetime can be evaluated in a short time.
また、下限値到達時間を求めることにより、下限値到達時間後に発生するイベントを想定できる。たとえば、部位ごとに検査後再稼動時に各部位に負荷される動的ひずみを想定できる。これにより、SCC発生可能性の有無を各部位ごとに検討でき、SCC発生寿命を各部位ごとに評価できる。その結果、実機検査において優先的、重点的に検査する部位を特定でき、検査項数削減に寄与できる。 Further, an event occurring after the lower limit value arrival time can be assumed by obtaining the lower limit value arrival time. For example, it is possible to assume a dynamic strain applied to each part at the time of restart after inspection for each part. Thereby, the presence or absence of possibility of SCC generation can be examined for each part, and the SCC generation life can be evaluated for each part. As a result, it is possible to identify the parts to be preferentially and preferentially examined in the actual machine inspection, which can contribute to the reduction of the number of inspection items.
本発明は、発明者が新たに見出したSCC発生寿命を律速する要因とメカニズムに基づくものであり、この点で従来技術と根本的に相違する。 The present invention is based on a factor and a mechanism for rate-determining the SCC generation life newly found by the inventor, and is fundamentally different from the prior art in this respect.
以下、本発明の実施形態を図面を用いて説明する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings.
〜SCC発生寿命を律速する要因とメカニズム〜
金属材料のSCC発生のメカニズムは完全に解明されているわけではないが、本願出願人は、SCC発生寿命を律速する要因およびメカニズムを検討し、新たな知見を見出した。
-Factors and mechanisms that determine SCC life-
Although the mechanism of SCC generation in metal materials has not been completely elucidated, the applicant of the present application has studied factors and mechanisms for determining the SCC generation lifetime, and has found new knowledge.
図1に、金属材料のSCC発生過程の模式図を示す。腐食環境下にさらされた金属材料表面で酸化皮膜が成長する。種々の要因で皮膜の破壊によって、母材(金属材料)が環境中に露出する。ここで、皮膜が薄い場合には不動態化を阻害するほどの腐食環境は形成されず、母材は再び不動態化してSCC発生には至らない。一方、皮膜が厚い場合、皮膜割れ先端では、すきま効果により溶出イオンの拡散阻害や皮膜表面との酸素濃淡差により厳しい腐食環境が形成され、母材の局部腐食が進行する。このとき金属材料表面に引張応力が生じていれば、SCCを発生する。 In FIG. 1, the schematic diagram of the SCC generation | occurrence | production process of a metal material is shown. An oxide film grows on the surface of a metal material exposed to a corrosive environment. Due to the destruction of the film due to various factors, the base material (metal material) is exposed to the environment. Here, when the film is thin, a corrosive environment that inhibits passivation is not formed, and the base material is passivated again, and SCC does not occur. On the other hand, when the film is thick, a severe corrosive environment is formed at the tip of the film crack due to the inhibition of diffusion of eluted ions and the difference in oxygen concentration from the surface of the film due to the gap effect, and the local corrosion of the base material proceeds. At this time, if tensile stress is generated on the surface of the metal material, SCC is generated.
このSCC発生過程に基づけば、金属材料で構成される構造物の当該部位でSCCが発生するか否かを決定する要因は、酸化皮膜が破壊された後に皮膜割れ先端で形成される腐食環境であり、SCC発生には形成された皮膜割れがある程度以上の深さを持つ必要がある。そのため、SCC発生感受性を示す酸化皮膜の厚さには下限のしきい値(SCC発生下限値)が存在すると考えられる。 Based on this SCC generation process, the factor that determines whether or not SCC is generated at the relevant part of the structure composed of a metal material is the corrosive environment formed at the tip of the film crack after the oxide film is destroyed. In order to generate SCC, the formed film crack needs to have a certain depth or more. Therefore, it is considered that there is a lower threshold value (SCC generation lower limit value) in the thickness of the oxide film exhibiting SCC generation sensitivity.
そこで、本願出願人は、SCC発生感受性を示す表面酸化皮膜厚さの下限値に着目し、新たなSCC発生寿命評価方法を発明した。 Therefore, the applicant of the present application has invented a new SCC generation lifetime evaluation method by paying attention to the lower limit value of the surface oxide film thickness indicating SCC generation sensitivity.
〜SCC発生寿命評価方法概略〜
本実施形態のSCC発生寿命評価方法は、以下の3つのステップから構成される。
(ステップ1)SCC発生感受性を示す表面酸化皮膜厚さの下限値を求める下限値取得ステップ
(ステップ2)表面酸化皮膜厚さが下限値に到達するまでの時間を求める下限値到達時間取得ステップ
(ステップ3)下限値到達後に表面酸化皮膜の破壊要因となるイベントを想定し、SCC発生可能性の有無を各部位ごとに検討するSCC発生可能性検討ステップ
図2に、SCC発生寿命評価の概念図を示す。まず、金属材料がSCC発生感受性を示す表面酸化皮膜厚さの下限値pxを設定する。図示実線で示す表面酸化皮膜の時間依存性から、酸化皮膜厚さpが、下限値pxに到達するまでの時間txを求める。
-Outline of SCC generation life evaluation method-
The SCC generation lifetime evaluation method of the present embodiment includes the following three steps.
(Step 1) Lower limit value acquisition step for determining the lower limit value of the surface oxide film thickness indicating SCC generation sensitivity (Step 2) Lower limit value arrival time acquisition step for determining the time until the surface oxide film thickness reaches the lower limit value ( Step 3) SCC occurrence possibility examination step that considers the presence or absence of SCC occurrence for each part assuming an event that causes destruction of the surface oxide film after reaching the lower limit value. FIG. 2 is a conceptual diagram of SCC occurrence lifetime evaluation. Indicates. First, the lower limit px of the surface oxide film thickness at which the metal material exhibits SCC generation sensitivity is set. The time tx until the oxide film thickness p reaches the lower limit px is determined from the time dependency of the surface oxide film indicated by the solid line in the figure.
次に、表面酸化被膜の破壊要因となるイベントを想定する。イベントが到達時間tx後に発生する場合、酸化被膜破壊から母材の腐食が進行しSCC発生の可能性がある。母材腐食によるSCC進行を図示破線で示す。そこで、SCC発生可能性の有無を検討し、その結果、SCC発生可能性有と判断すると、イベント発生時をSCC発生寿命Lと評価する。なお、イベントが到達時間tx前に発生する場合、イベントによるSCC発生可能性の有無を検討しなくてもよい。 Next, an event that causes the destruction of the surface oxide film is assumed. When the event occurs after the arrival time tx, the corrosion of the base material progresses from the oxide film destruction, and there is a possibility that SCC occurs. The progress of SCC due to the corrosion of the base metal is indicated by a broken line in the figure. Therefore, the presence or absence of the possibility of occurrence of SCC is examined. As a result, when it is determined that the possibility of occurrence of SCC is found, the event occurrence time is evaluated as SCC occurrence life L. If the event occurs before the arrival time tx, it is not necessary to consider the possibility of occurrence of SCC due to the event.
以下、ステップ1〜3について詳細に説明する。 Hereinafter, Steps 1 to 3 will be described in detail.
一例として、288℃、溶存酸素濃度0.2 ppmの環境中で運転されている発電プラントの構造物の溶接部におけるSCC発生寿命を評価する。 As an example, the SCC generation life in a welded part of a power plant structure operated in an environment of 288 ° C. and a dissolved oxygen concentration of 0.2 ppm is evaluated.
〜試験片〜
発電プラントの金属材料としてSUS316L鋼を選定した。SUS316L鋼の組成を表1に示す。
~Test pieces~
SUS316L steel was selected as the metal material for the power plant. Table 1 shows the composition of SUS316L steel.
発電プラントを構成する金属材料と同一材料の試験片に対し、発電プラントの構造物の溶接部における状態を模擬するため、溶接による熱影響を想定して、620℃で24時間保持した後に室温(27℃)まで緩やかに炉冷する熱処理を施した。試験片は、図3に示した形状の単軸引張タイプの試験片(平行部寸法:長さ×幅×厚さ=20mm×3mm×2mm)に機械加工した後、溶接後の仕上げ加工による表面状態と残留応力を模擬するため、表面にグラインダ研削によって加工層を付与し、溶接によって付与される残留応力に相当する約300 MPaの引張残留応力を付与したものを試験に供した。 In order to simulate the state of the welded part of the power plant structure for a test piece of the same material as the metal material that constitutes the power plant, assuming a thermal effect due to welding, after holding at 620 ° C for 24 hours, Heat treatment was performed to gently cool the furnace to 27 ° C. The test piece was machined into a uniaxial tension type test piece (parallel portion dimensions: length × width × thickness = 20 mm × 3 mm × 2 mm) having the shape shown in FIG. In order to simulate the state and the residual stress, a test layer was applied to the surface by applying a processed layer by grinder grinding and applying a tensile residual stress of about 300 MPa corresponding to the residual stress applied by welding.
〜ステップ1〜
発電プラントの冷却水環境を模擬した環境で、SUS316L鋼にSCCを発生する皮膜厚さの下限値を決定するため、表面の皮膜厚さの異なる金属材料を作製し、SCC試験を行った。
~ Step 1
In order to determine the lower limit value of the film thickness for generating SCC on SUS316L steel in an environment simulating the cooling water environment of a power plant, metallic materials having different surface film thicknesses were produced and subjected to an SCC test.
表面酸化皮膜厚さの異なる試験片を用意するため、まず予浸漬として、試験片をオートクレーブ内で試験水に浸漬し、80気圧まで加圧することで沸騰を抑えながら、約3時間かけて288℃の試験温度まで昇温した後、発電プラントの冷却水の温度を模擬し、且つ酸化皮膜の成長を加速するため、288℃の純水中(水圧=80気圧、溶存酸素濃度=約8ppm(空気飽和条件))を選定した(加速条件)。各試験片は所定の予浸漬時間が経過した時点で試験片を取り出して、表面に形成した皮膜厚さを評価した。表2に、予浸漬時間及び予浸漬後に試験片表面に形成した表面酸化皮膜の厚さを示す。試験片に形成した酸化皮膜厚さは断面SEM(走査電子顕微鏡scanning electron microscopy)観察から、酸化皮膜と考えられる領域の面積を見積もり、被膜の長さで除した値を平均皮膜厚さとして求めた。断面SEM観察の際には、表面をエポキシ樹脂でコーティングして皮膜を保護した後、イオンミリングによって断面観察試験片を作製した。 In order to prepare test pieces having different thicknesses of the surface oxide film, first, as a pre-immersion, the test piece is immersed in test water in an autoclave and pressurized to 80 atm. In order to simulate the temperature of the cooling water of the power plant and accelerate the growth of the oxide film, the temperature is increased to 288 ° C. pure water (water pressure = 80 atm, dissolved oxygen concentration = about 8 ppm (air Saturation condition)) was selected (acceleration condition). Each test piece was taken out when a predetermined pre-immersion time had elapsed, and the thickness of the film formed on the surface was evaluated. Table 2 shows the pre-soaking time and the thickness of the surface oxide film formed on the surface of the test piece after pre-soaking. The thickness of the oxide film formed on the specimen was estimated from the cross-sectional SEM (scanning electron microscopy) observation to estimate the area of the region considered to be an oxide film, and the value obtained by dividing the area by the length of the film was obtained as the average film thickness. . In cross-sectional SEM observation, the surface was coated with an epoxy resin to protect the film, and a cross-section observation test piece was prepared by ion milling.
予浸漬が完了した試験片に対して、前記のSCC試験を実施した。試験環境としては、発電プラントの環境を模擬するため、288℃の純水中(水圧=80気圧、溶存酸素濃度=約0.2ppm)を選定した(実機条件)。 The SCC test was performed on the test piece that had been pre-soaked. As a test environment, 288 ° C. pure water (water pressure = 80 atm, dissolved oxygen concentration = about 0.2 ppm) was selected to simulate the power plant environment (actual machine conditions).
ところで、発明者は、より短時間でSCCを進展させるSCC試験を提案しており(特願2010−227073)、このSCC試験をおこなった。SUS316L鋼のSCC発生を最大限加速するように、初期荷重336MPa、一定ひずみ速度8.3×10−8s−1、最大荷重384MPaを設定し、試験片に対して初期荷重を負荷した後に、一定ひずみ速度を保ちながら徐々に荷重を増大させる動的荷重負荷過程と、最大負荷荷重に到達した後に該最大負荷荷重を維持し続ける定荷重負荷過程とからなることを特徴とするSCC試験を2000時間実施した。 By the way, the inventor has proposed an SCC test that advances SCC in a shorter time (Japanese Patent Application No. 2010-227073), and performed this SCC test. The initial load 336 MPa, constant strain rate 8.3 × 10 −8 s −1, maximum load 384 MPa were set so that the SCC generation of SUS316L steel was accelerated to the maximum. The SCC test is characterized by a 2000-hour SCC test comprising a dynamic load process in which the load is gradually increased while maintaining the strain rate, and a constant load process in which the maximum load is maintained after reaching the maximum load. Carried out.
図4に、SCC試験装置を示す。SCC試験装置1は、金属材料の試験片2を内蔵して腐食環境を提供する環境調整部(例えば、オートクレーブ3、ヒータ4、循環水入口5、循環水出口6等)と、試験片2に引張荷重を付与する荷重付与部(例えば、プルロッド7等)と、荷重付与部に接続され引張荷重を検知する荷重検知部(例えば、ロードセル8、ロードセルアンプ9等)と、試料片2のひずみを検出するひずみ検出部(例えば、ひずみ検出器10等)と、試験条件(例えば、最大負荷応力値、初期負荷応力値、ひずみ速度など)が入力され動的荷重負荷過程と定荷重負荷過程とを連続的に制御する引張試験制御部(例えば、制御装置11等)とを具備している。
FIG. 4 shows an SCC test apparatus. The SCC test apparatus 1 includes an environment adjustment unit (for example, an
SCC試験終了後、試験片平行部の表面および断面をSEMで観察し、SCC発生の有無を評価した。観察結果に基づき、SCC試験後の各試験片のSCC発生状況とSCC試験開始時の皮膜厚さの推定値を図5に示す。予浸漬皮膜厚さが0.5μmを超えるとSCCが発生している。そのため、288℃、溶存酸素濃度0.2 ppmの環境中で運転されている発電プラントのSUS316L製構造物の溶接部におけるSCC発生皮膜厚さの下限値は0.5μmと見積もられた。なお、SCC発生下限皮膜厚さの値は、金属材料の組成および金属材料が曝されている環境の条件によって異なる。 After completion of the SCC test, the surface and cross section of the test piece parallel portion were observed with an SEM, and the presence or absence of SCC was evaluated. Based on the observation results, the SCC occurrence state of each test piece after the SCC test and the estimated value of the film thickness at the start of the SCC test are shown in FIG. When the pre-immersion film thickness exceeds 0.5 μm, SCC is generated. Therefore, the lower limit value of the SCC generation film thickness in the welded part of the SUS316L structure of the power plant operated in an environment of 288 ° C. and dissolved oxygen concentration of 0.2 ppm was estimated to be 0.5 μm. Note that the value of the SCC generation lower limit film thickness varies depending on the composition of the metal material and the environmental conditions to which the metal material is exposed.
〜ステップ2〜
金属材料表面の酸化皮膜がSCC発生皮膜厚さの下限値に到達する時間を見積もるため、材料の表面状態毎に酸化皮膜の経時変化を予測する。試験片に対して、循環式オートクレーブ(東伸工業(株)製)を用いて、288℃の純水中(水圧=80気圧、溶存酸素濃度=約0.2ppm)条件(実機条件)で、最長2000hの浸漬試験を実施し、皮膜厚さの時間依存性を求めた。皮膜厚さの評価は、所定の時間浸漬した試験片を取り出して断面SEM観察を実施し、断面SEM観察の結果から酸化皮膜と考えられる領域の面積を見積もり、被膜長さで除して平均値を皮膜厚さとした。高温水中の酸化皮膜は対数則に従って成長するため、プロットした皮膜厚さの経時変化に対して式(1)に示す対数則でフィッティングして酸化皮膜成長の予測式を求め、予測式から下限皮膜厚さに到達するまでの時間を求めた。
p = Alog (Bt +1) 式(1)
p:酸化皮膜厚さ(μm) A、B:定数 t:高温水中浸漬時間(h)
図6に、試験結果をもとに288℃の純水中(水圧=80気圧、溶存酸素濃度=約0.2ppm)における酸化皮膜厚さの経時変化をプロットする。このプロットに対して、式(1)でフィッティングした結果を図中に破線で示す。フィッティングの結果から酸化皮膜成長の予測式は式(2)となった。
p = 0.054×log(0.24×t +1) 式(2)
式(2)に基づき、酸化皮膜が下限値0.5μmに到達するまでの時間を見積もった。その結果、288℃、溶存酸素濃度0.2ppmの環境中(実機条件)で運転されている発電プラントのSUS316L鋼製構造物の溶接部におけるSCC発生皮膜厚さの下限値到達時間は、約5.7×104時間(6.5年)と求められた。なお、SCC発生下限皮膜厚さ到達時間は、金属材料の組成および金属材料が曝されている環境の条件によって異なる。
~
In order to estimate the time for the oxide film on the surface of the metal material to reach the lower limit of the thickness of the SCC-generated film, the change with time of the oxide film is predicted for each surface state of the material. Using a circulating autoclave (manufactured by Toshin Kogyo Co., Ltd.) for the test piece, under pure water (water pressure = 80 atm, dissolved oxygen concentration = about 0.2 ppm) conditions (actual machine conditions) at 288 ° C. The immersion test was conducted for a maximum of 2000 h, and the time dependency of the film thickness was determined. The film thickness is evaluated by taking out a test piece immersed for a predetermined time and carrying out cross-sectional SEM observation, estimating the area of a region considered to be an oxide film from the result of cross-sectional SEM observation, and dividing by the film length to obtain an average value. Was the film thickness. Since the oxide film in high-temperature water grows according to the logarithm rule, the prediction formula of oxide film growth is obtained by fitting the plotted film thickness with the logarithm rule shown in Equation (1), and the lower limit film is calculated from the prediction formula. The time to reach the thickness was determined.
p = Alog (Bt +1) Equation (1)
p: oxide film thickness (μm) A, B: constant t: immersion time in high temperature water (h)
FIG. 6 plots the change over time of the oxide film thickness in pure water at 288 ° C. (water pressure = 80 atm, dissolved oxygen concentration = about 0.2 ppm) based on the test results. The result of fitting with this formula (1) to this plot is shown by a broken line in the figure. From the result of the fitting, the formula for predicting the growth of the oxide film is the formula (2).
p = 0.054 × log (0.24 × t +1) Formula (2)
Based on the formula (2), the time until the oxide film reaches the lower limit of 0.5 μm was estimated. As a result, the time to reach the lower limit of the thickness of the SCC-generated film at the welded portion of the SUS316L steel structure of the power plant operated in an environment (actual machine conditions) at 288 ° C. and a dissolved oxygen concentration of 0.2 ppm is about 5 7 × 10 4 hours (6.5 years). The SCC generation lower limit film thickness arrival time varies depending on the composition of the metal material and the conditions of the environment to which the metal material is exposed.
〜ステップ3〜
運転履歴および運転計画に基づき、下限値到達後に発生する表面酸化皮膜の破壊要因となるイベントを想定する。
~
Based on the operation history and operation plan, an event that causes the destruction of the surface oxide film that occurs after the lower limit is reached is assumed.
酸化皮膜を破壊しSCCが発生する要因となるイベントとして、発電プラントの再稼動に伴う温度と圧力の上昇によって構造物に負荷される動的なひずみを想定した。構造物に動的なひずみが付与された場合は、金属材料と表面酸化皮膜の延性の差から、金属材料のひずみに皮膜が追随できず、皮膜に割れや剥離を生じる可能性がある。 As an event that breaks the oxide film and causes SCC, dynamic strain applied to the structure due to an increase in temperature and pressure accompanying the restart of the power plant was assumed. When dynamic strain is applied to the structure, the film cannot follow the strain of the metal material due to the difference in ductility between the metal material and the surface oxide film, and the film may crack or peel off.
発電プラントの再起動は、運転計画に基づき、下限値到達時間である約5.7×104時間(6.5年)後に行われる検査(連続運転時間 約6.1×104 時間)を想定した。 The restart of the power plant is based on the operation plan, and the inspection (continuous operation time is about 6.1 × 10 4 hours) is performed after the lower limit value arrival time of about 5.7 × 10 4 hours (6.5 years). Assumed.
まず、金属材料表面の皮膜厚さ0.51μmを想定して、288℃、溶存酸素濃度8ppmの純水中(加速条件)で試験片を予浸漬した。図4に示す試験装置を用い、試験片をオートクレーブ内で試験水に浸漬し、80気圧まで加圧することで沸騰を抑えながら、約3時間かけて288℃の試験温度まで昇温した後、288℃の純水中(水圧=80気圧、溶存酸素濃度=約8ppm(空気飽和条件))に1000時間浸漬し、平均皮膜厚さ0.51μmの皮膜を形成した。 First, assuming a film thickness of 0.51 μm on the surface of the metal material, the test piece was pre-soaked in pure water (accelerated conditions) at 288 ° C. and a dissolved oxygen concentration of 8 ppm. Using the test apparatus shown in FIG. 4, the test piece was immersed in test water in an autoclave and heated to a test temperature of 288 ° C. over about 3 hours while suppressing boiling by pressurizing to 80 atm. The film was immersed in pure water (° C. = 80 atm, dissolved oxygen concentration = about 8 ppm (air saturation condition)) at 1000 ° C. for 1000 hours to form a film having an average film thickness of 0.51 μm.
その後、288℃の温度を保ったまま約12時間かけて脱気を行い、発電プラントの冷却水環境を模擬した、288℃の純水中(水圧=80気圧、溶存酸素濃度=約0.2ppm)の環境に切り替えた後、酸化皮膜が下限値0.5μmに到達した試験片に対して、発電プラント再稼動時に構造物の選定箇所((1)・(2)・(3))の各部位に負荷される動的ひずみを想定して、発明者が提案しているSCC試験を実施し、各部位ごとにSCC発生可能性の有無を検討した。表3に、再稼動時に、構造物の選定箇所((1)・(2)・(3))を仮定して負荷される平均ひずみ速度およびひずみ付与時間を示す。このとき、最大荷重の条件として、SUS316L鋼の破断応力より低い値であり且つSCC発生を最大限加速するためになるべく高い応力条件である384MPaを採用した。 Then, deaeration was performed over about 12 hours while maintaining the temperature of 288 ° C., and 288 ° C. pure water (water pressure = 80 atm, dissolved oxygen concentration = about 0.2 ppm) simulating the cooling water environment of the power plant. ) After switching to the environment of (), each of the selected parts ((1), (2), (3)) when the power plant is restarted for the test piece whose oxide film reached the lower limit of 0.5 μm The SCC test proposed by the inventor was carried out assuming the dynamic strain applied to the site, and the presence or absence of the possibility of occurrence of SCC was examined for each site. Table 3 shows the average strain rate and strain application time applied assuming the selected locations ((1), (2), and (3)) of the structure during re-operation. At this time, 384 MPa, which is a stress condition as high as possible in order to accelerate the generation of SCC as much as possible, was adopted as the maximum load condition, which is lower than the rupture stress of SUS316L steel.
SCC試験終了後、試験片平行部の表面および断面をSEMで観察し、SCC発生の有無を評価した。ケース1において、SCC発生が確認できたが、ケース2、ケース3では、SCC発生がみられなかった。
After completion of the SCC test, the surface and cross section of the test piece parallel portion were observed with an SEM, and the presence or absence of SCC was evaluated. In case 1, the occurrence of SCC was confirmed, but in
これにより、実機において、6.1×104時間運転後の再稼動時にケース1においてSCC発生可能性が有ると判断する。一方、6.1×104時間運転後の再稼動時に、ケース2およびケース3において、SCC発生可能性は無いと判断する。
As a result, in the actual machine, it is determined that there is a possibility of occurrence of SCC in case 1 at the time of re-operation after operation for 6.1 × 10 4 hours. On the other hand, it is determined that there is no possibility of occurrence of SCC in
〜SCC発生寿命評価〜
ステップ3において、6.1×104時間運転後の再稼動時に選定箇所(1)においてSCC発生可能性が有る(ケース1)と判断すると、6.1×104時間運転後の再稼動時を選定箇所(1)のSCC発生寿命と評価する。したがって、6.1×104時間運転後は、選定箇所(1)の溶接部を優先的、重点的に検査する部位と特定する。
-SCC generation life evaluation-
If it is determined in
実機検査において、被膜厚の成長などSCC発生の徴候が発見された場合は、適切な予防保全対策を取る。予防保全対策としては、酸化被膜の除去や金属材料表面に圧縮応力を付加することなどが考えられる。金属材料表面と内部に温度差を付加したり、ピーニング加工をしたりすることにより圧縮応力を付加する。 Appropriate preventive maintenance measures should be taken when signs of SCC occurrence such as film thickness growth are found during actual machine inspection. As preventive maintenance measures, removal of an oxide film or application of compressive stress to the surface of a metal material can be considered. A compressive stress is applied by adding a temperature difference between the surface and the inside of the metal material or by peening.
〜検査計画策定システム〜
SCC発生寿命評価に基づく検査計画は、検査計画策定システム100により策定される。検査計画策定システム100は、演算装置100の演算機能であり、腐食水環境下で使用される構造物を構成する金属材料の表面で成長する酸化皮膜が破壊され、金属材料が腐食水環境中に露出するとき、金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値を設定する下限値設定部101と、構造物実機を再現した腐食水環境下で、表面酸化皮膜厚さが下限値に到達するまでの時間を求める下限値到達時間取得部102と、構造物の運転履歴、検査計画を含む運転計画および表面酸化皮膜の破壊要因となるイベント発生時の構造物の各部位ごとの特性を記憶する記憶部103と、イベントが下限値到達後に発生すると想定する場合に、SCC発生可能性を検討する部位を選択する検討部位選択部104と、検討部位選択部104により選択された部位がSCC発生可能性有と判断された場合、当該部位を実機検査する部位と特定する検査部位特定部105とを備える。図7は、検査計画策定システム100の機能ブロック図である。
~ Inspection plan development system ~
The inspection plan based on the SCC occurrence life evaluation is formulated by the inspection
〜効果〜
以上のように、腐食環境下で使用される発電プラントを構成する金属材料に対して、SCCが発生するまでの寿命を定量的に評価できる。さらに、本実施形態の特徴は、金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値に着目したことにあり、この特徴より以下の効果が得られる。
~effect~
As described above, the life until SCC occurs can be quantitatively evaluated for the metal material constituting the power plant used in a corrosive environment. Furthermore, the feature of the present embodiment is that attention is paid to the lower limit value of the surface oxide film thickness indicating the SCC generation sensitivity of the metal material, and the following effects are obtained from this feature.
(1)特許文献1記載の従来技術は、加速条件下でのSCC発生寿命に加速要因係数を乗ずることにより、実機でのSCC発生寿命を求めるものである。着目しているのは、あくまでSCC発生寿命という時間軸での概念であり、加速条件を工夫したとしても、SCC発生試験に長時間が必要である。発明者が試算したところ、およそ20000時間以上となった。 (1) The prior art described in Patent Document 1 obtains the SCC generation lifetime in an actual machine by multiplying the SCC generation lifetime under acceleration conditions by the acceleration factor coefficient. The focus is on the concept of the time axis of SCC generation life, and even if the acceleration condition is devised, a long time is required for the SCC generation test. When the inventor estimated, it became about 20000 hours or more.
一方、本実施形態は、金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値に着目するものであり、時間軸の概念から切り離される。このため、特許文献1記載の従来技術と比較し、短時間でSCC発生寿命を評価できる。 On the other hand, this embodiment pays attention to the lower limit value of the surface oxide film thickness indicating the SCC generation sensitivity of the metal material, and is separated from the concept of the time axis. For this reason, compared with the prior art described in Patent Document 1, the SCC occurrence lifetime can be evaluated in a short time.
具体的には、ステップ1における浸漬試験に2000時間、SCC試験に2000時間、ステップ2における浸漬試験に2000時間、ステップ3における浸漬試験に1000時間、SCC試験に1000時間が必要となる。ステップ1とステップ2は並行して行うことができ、合計すると6000時間程度となる。
Specifically, 2000 hours are required for the immersion test in Step 1, 2000 hours for the SCC test, 2000 hours for the immersion test in
(2)特許文献1記載の従来技術では、SCC発生寿命を律速する要因とメカニズムが考慮されていない。特許文献2記載の従来技術では、SCC発生寿命を律速する要因とメカニズムが発明者が新たに見出した知見と異なる。本実施形態では、発明者が新たに見出した知見に基づき、SCC発生寿命を律速する要因とメカニズムを考慮して、SCC発生寿命を評価できる。
(2) In the prior art described in Patent Document 1, the factor and mechanism for determining the SCC generation lifetime are not considered. In the prior art described in
(3)特許文献1および特許文献2記載の従来技術では、各部位ごとのSCC発生寿命評価をしておらず、実機検査において優先的、重点的に検査する部位を特定できなかった。
(3) In the prior art described in Patent Document 1 and
本実施形態では、スッテプ1およびステップ2により、下限値到達時間を求めることにより、ステップ3において、下限値到達時間後に発生するイベントを想定できる。たとえば、部位ごとに検査後再稼動時に各部位に負荷される動的ひずみを想定できる。これにより、SCC発生可能性の有無を各部位ごとに検討でき、SCC発生寿命を各部位ごとに評価できる。その結果、実機検査において優先的、重点的に検査する部位を特定でき、検査項数削減に寄与できる。
In the present embodiment, an event occurring after the lower limit value arrival time can be assumed in
〜変形例〜
本発明は、上記実施形態に限定されず、発明の範囲内で、さらに多くの変形が可能である。変形例の一例を以下に示す。
~ Modification ~
The present invention is not limited to the above-described embodiments, and many variations are possible within the scope of the invention. An example of a modification is shown below.
(ステップ1の変形例)
本実施形態において、ステップ1では、加速条件により実際に皮膜を形成した試験片に対して、SCC試験によりSCC発生の有無を確認し、SCC発生皮膜厚さの下限値を求めたが、他の方法でも良い。
(Modification of Step 1)
In this embodiment, in Step 1, for the test piece that actually formed the film under the acceleration condition, the presence or absence of SCC generation was confirmed by the SCC test, and the lower limit value of the SCC generation film thickness was obtained. The method is fine.
(1)表面酸化皮膜厚さの異なる試験片を作製するまでの過程は、本実施形態と同じである。その後、腐食電位を測定しながら試験片にひずみを掛ける。ひずみによって皮膜が破壊され、母材が露出したときの腐食電位と、皮膜が破壊される前の腐食電位の差を見積もる。電位差が、再不動態化を阻害する電位差より大きいか否かで母材でSCCが発生するかどうかを判定する。 (1) The process up to producing test pieces having different surface oxide film thicknesses is the same as that of the present embodiment. Thereafter, the test piece is strained while measuring the corrosion potential. Estimate the difference between the corrosion potential when the coating is destroyed by strain and the base material is exposed, and the corrosion potential before the coating is destroyed. Whether or not SCC occurs in the base material is determined based on whether or not the potential difference is larger than the potential difference that inhibits repassivation.
図8は、被膜厚さと電位差の関係を示す図である。横軸は時間経過、縦軸は腐食電位を示す。皮膜厚さ0.2〜0.6μmの試験片を作成する。被膜が破壊されると腐食電位が低下する。皮膜厚さ0.2〜0.4μmのケースに比べ、0.5〜0.6μmのケースの電位差は明らかに大きくなっている。これは、皮膜厚さ0.2〜0.4μmのケースでは、電位差が小さく再不動態化可能であり、0.5〜0.6μmのケースでは、電位差が大きく再不動態化を阻害されることを示している。したがって、皮膜厚さ0.5μm以上になるとSCC発生の可能性がある。すなわち、SCC発生皮膜厚さの下限値は0.5μmと見積もられる。 FIG. 8 is a diagram showing the relationship between the film thickness and the potential difference. The horizontal axis represents time, and the vertical axis represents the corrosion potential. A test piece having a film thickness of 0.2 to 0.6 μm is prepared. When the coating is destroyed, the corrosion potential decreases. The potential difference in the case of 0.5 to 0.6 μm is clearly larger than that in the case of the film thickness of 0.2 to 0.4 μm. This is because the potential difference is small and repassivation is possible in the case of the film thickness of 0.2 to 0.4 μm, and repassivation is inhibited in the case of 0.5 to 0.6 μm. Show. Therefore, SCC may occur when the film thickness is 0.5 μm or more. That is, the lower limit value of the SCC generation film thickness is estimated to be 0.5 μm.
(2)電位差を実験によらず、シミュレーションによって求めてもよい。皮膜破壊前の腐食電位は、皮膜の厚さと、液中の酸素が皮膜中を移動する固体拡散速度と母材の金属が皮膜を通じて液中に溶出する固体拡散速度の内、速度の遅い方から推定する。皮膜破壊後の腐食電位は、皮膜割れによって形成されたすきま内を酸素が母材まで到達する液中の拡散速度と、母材から溶出した金属イオンが移動する拡散速度から推定する。電位差が再不動態化を阻害する電位差より大きいか否かで母材でSCCが発生するかどうかを判定し、下限値を求める。 (2) The potential difference may be obtained by simulation, not by experiment. The corrosion potential before film breakage is determined from the slowest of the film thickness, the solid diffusion rate at which oxygen in the liquid moves through the film, and the solid diffusion rate at which the base metal elutes into the liquid through the film. presume. The corrosion potential after film destruction is estimated from the diffusion rate in the liquid in which oxygen reaches the base material in the gap formed by the film cracking, and the diffusion rate at which the metal ions eluted from the base material move. Determine whether SCC occurs in the base material based on whether the potential difference is greater than the potential difference that inhibits repassivation, and determine the lower limit.
(3)下限値を求める方法として、SCC試験、電位差測定、電位差シミュレーションについて説明したが、これらを複数組み合わせても良い。 (3) Although the SCC test, the potential difference measurement, and the potential difference simulation have been described as the method for obtaining the lower limit value, a plurality of these may be combined.
(ステップ2の変形例)
本実施形態において、ステップ2では、実機条件の浸漬試験により表面酸化皮膜厚さの経時変化を求めたが、他の方法でも良い。
(Modification of step 2)
In the present embodiment, in
(1)実機の運転履歴に基づき、測定した実機表面の酸化皮膜厚さと実機の連続運転時間から表面酸化皮膜厚さの経時変化を取得する。 (1) Based on the operation history of the actual machine, the change with time of the surface oxide film thickness is obtained from the measured oxide film thickness of the actual machine surface and the continuous operation time of the actual machine.
(2)経時変化を実験によらず、酸化皮膜の成長速度にかかるシミュレーションによって求めてもよい。酸化皮膜成長速度は、表面の金属と酸素との反応速度によって決定される。反応速度は、皮膜が薄いときは沖合の酸素が金属表面まで到達する酸素の液中拡散速度に律速される。皮膜が厚いときは,液中の酸素が皮膜中を移動する固体拡散速度と母材の金属が皮膜を通じて液中に溶出する固体拡散速度の内、速度の遅い方に律速される。 (2) The change with time may be obtained by a simulation related to the growth rate of the oxide film, not by an experiment. The oxide film growth rate is determined by the reaction rate between surface metal and oxygen. When the film is thin, the reaction rate is limited by the diffusion rate of oxygen in the liquid that reaches offshore to the metal surface. When the film is thick, the rate is determined by the slower of the solid diffusion rate at which oxygen in the liquid moves through the film and the solid diffusion rate at which the base metal elutes into the liquid through the film.
(3)到達時間を求める予測式として、浸漬試験、実機測定、成長速度シミュレーションについて説明したが、これらを複数組み合わせても良い。 (3) Although the immersion test, the actual machine measurement, and the growth rate simulation have been described as prediction formulas for obtaining the arrival time, a plurality of these may be combined.
(ステップ3の変形例)
本実施形態において、ステップ3では、SCC発生可能性検討ステップにおいて想定するイベントは、発電プラントの稼働及び再稼動としたが、地震による動荷重負荷としてもよい。
(Modification of step 3)
In this embodiment, in
(腐食生成物堆積時の補正)
腐食水環境下で使用される発電プラントの当該部位において、腐食生成物の堆積が生じている場合には、堆積した腐食生成物の厚さと、密度と、組成のすべて又はいずれかに基づいて金属材料がSCC発生感受性を示す表面酸化皮膜厚さの下限値と、酸化皮膜厚さが下限値に到達するまでの時間と、下限値到達後に発生するイベントの諸元との少なくとも1つを補正することが望ましい。
(Correction when corrosion products are deposited)
If corrosion products have been deposited at the site of the power plant used in a corrosive water environment, the metal is based on the thickness, density, and / or composition of the deposited corrosion products. Correct at least one of the lower limit value of the surface oxide film thickness at which the material is susceptible to SCC generation, the time until the oxide film thickness reaches the lower limit value, and the specifications of the event that occurs after the lower limit value is reached It is desirable.
1 SCC試験装置
2 試験片
3 オートクレーブ
4 ヒータ
5 循環水入口
6 循環水出口
7 プルロッド
8 ロードセル
9 ロードセルアンプ
10 ひずみ検出器
11 制御装置
100 検査計画策定システム(演算装置)
101 下限値設定部
102 下限値到達時間取得部
103 記憶部
104 検討部位選択部
105 検査部位特定部
DESCRIPTION OF SYMBOLS 1
101 Lower limit
Claims (6)
前記金属材料の表面で成長する酸化皮膜が破壊され、前記金属材料が腐食水環境中に露出するとき、前記金属材料のSCC発生感受性を示す表面酸化皮膜厚さの下限値を求める下限値取得ステップと、
前記構造物実機を再現した腐食水環境下で、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求める下限値到達時間取得ステップと、
前記構造物の運転履歴および運転計画に基づき、表面酸化皮膜の破壊要因となるイベントであって、前記下限値到達後に発生するイベントを想定し、SCC発生可能性の有無を前記構造物の各部位ごとに検討するSCC発生可能性検討ステップとを有し、
前記SCC発生可能性検討ステップにおいて、SCC発生可能性有と判断する部位に対し、前記イベント発生時を当該部位のSCC発生寿命と評価する
ことを特徴とするSCC発生寿命評価方法。 A stress corrosion cracking (hereinafter referred to as SCC) occurrence life evaluation method of a metal material constituting a structure used in a corrosive water environment,
A lower limit value obtaining step for obtaining a lower limit value of a surface oxide film thickness indicating SCC generation sensitivity of the metal material when the oxide film growing on the surface of the metal material is destroyed and the metal material is exposed to a corrosive water environment. When,
Under a corrosive water environment that reproduces the structure actual machine, a lower limit reaching time acquisition step for obtaining a time until the surface oxide film thickness reaches the lower limit; and
Based on the operation history and operation plan of the structure, it is an event that causes the destruction of the surface oxide film, and an event that occurs after the lower limit is reached is assumed. Each SCC occurrence possibility examination step to be examined,
In the SCC occurrence possibility examination step, an SCC occurrence lifetime evaluation method characterized by evaluating the occurrence of the event as the SCC occurrence lifetime of the part for a portion determined to have the possibility of occurrence of SCC.
前記下限値取得ステップは、
前記金属材料と同一材料の試験片を加速条件環境中に浸漬し、被膜厚さの異なる複数の試験片を形成する浸漬試験と、
前記浸漬した試験片に引張応力を負荷するSCC試験とを含み、
SCC試験時のSCC発生の有無から表面酸化皮膜厚さの下限値を求める
ものであることを特徴とするSCC発生寿命評価方法。 In the SCC generation lifetime evaluation method according to claim 1,
The lower limit acquisition step includes
Immersion test in which a test piece of the same material as the metal material is immersed in an accelerated condition environment to form a plurality of test pieces having different film thicknesses;
An SCC test for applying a tensile stress to the immersed specimen,
A method for evaluating the life of an SCC generation, characterized in that the lower limit of the thickness of the surface oxide film is obtained from the presence or absence of SCC generation during an SCC test.
前記SCC試験は、
前記試験片に負荷する最大負荷応力値と、前記最大負荷応力値よりも所定の値低い初期負荷応力値と、ひずみ速度とをあらかじめ設定し、
腐食環境下で前記試験片に対して前記初期負荷応力値で荷重した後に前記最大負荷応力値まで前記ひずみ速度を保ちながら徐々に荷重を増大させる動的荷重負荷過程と、
前記最大負荷応力値に到達した後に該最大負荷応力値を荷重し続ける定荷重負荷過程とを含む
ことを特徴とするSCC発生寿命評価方法。 In the SCC generation lifetime evaluation method according to claim 2,
The SCC test is
Preset a maximum load stress value to be applied to the test piece, an initial load stress value lower than the maximum load stress value by a predetermined value, and a strain rate,
A dynamic loading process in which the load is gradually increased while the strain rate is maintained up to the maximum load stress value after being loaded at the initial load stress value on the test piece in a corrosive environment;
A constant load loading process of continuing to load the maximum load stress value after reaching the maximum load stress value.
前記下限値到達時間取得ステップは、
前記金属材料と同一材料の試験片を実機条件環境中に浸漬して、表面酸化皮膜厚さの経時変化を求め、
前記経時変化より、表面酸化皮膜厚さの成長予測式を求め、
前記成長予測式より、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求める
ものであることを特徴とするSCC発生寿命評価方法。 In the SCC generation lifetime evaluation method according to claim 1,
The lower limit arrival time acquisition step includes:
Immerse the test piece of the same material as the metal material in the environment of the actual machine to determine the change with time of the surface oxide film thickness
From the change over time, find the growth prediction formula of the surface oxide film thickness,
The SCC generation lifetime evaluation method characterized in that the time until the surface oxide film thickness reaches the lower limit value is obtained from the growth prediction formula.
前記SCC発生可能性検討ステップにおいて想定するイベントは、前記構造物の検査後の再稼動である
ことを特徴とするSCC発生寿命評価方法。 In the SCC generation lifetime evaluation method according to claim 1,
The SCC occurrence lifetime evaluation method, wherein the event assumed in the SCC occurrence possibility examination step is a restart after inspection of the structure.
前記構造物実機を再現した腐食水環境下で、前記表面酸化皮膜厚さが前記下限値に到達するまでの時間を求める下限値到達時間取得手段と、
前記構造物の運転履歴、検査計画を含む運転計画および表面酸化皮膜の破壊要因となるイベント発生時の前記構造物の各部位ごとの特性を記憶する記憶手段と、
前記イベントが前記下限値到達後に発生すると想定する場合に、SCC発生可能性を検討する部位を選択する検討部位選択手段と、
前記検討部位選択手段により選択された部位がSCC発生可能性有と判断された場合、当該部位を実機検査する部位と特定する検査部位特定手段と
を備えることを特徴とする腐食水環境下で使用される構造物の検査計画策定システム。 When the oxide film growing on the surface of the metal material constituting the structure used in the corrosive water environment is destroyed and the metal material is exposed to the corrosive water environment, the surface oxidation showing the SCC generation sensitivity of the metal material A lower limit setting means for setting the lower limit of the film thickness;
Under a corrosive water environment that reproduces the actual structure, a lower limit arrival time obtaining means for obtaining a time until the surface oxide film thickness reaches the lower limit; and
Storage means for storing the operation history of the structure, the operation plan including an inspection plan, and the characteristics of each part of the structure at the time of occurrence of an event that causes the destruction of the surface oxide film;
When assuming that the event occurs after reaching the lower limit value, a study site selection means for selecting a site for examining the possibility of occurrence of SCC;
When the site selected by the examination site selection means is determined to have the possibility of occurrence of SCC, the site is provided in a corrosive water environment, characterized by comprising: Structure inspection plan formulation system.