JP2013023988A - Fireproof double glazing and fireproof double glazing unit - Google Patents

Fireproof double glazing and fireproof double glazing unit Download PDF

Info

Publication number
JP2013023988A
JP2013023988A JP2011162440A JP2011162440A JP2013023988A JP 2013023988 A JP2013023988 A JP 2013023988A JP 2011162440 A JP2011162440 A JP 2011162440A JP 2011162440 A JP2011162440 A JP 2011162440A JP 2013023988 A JP2013023988 A JP 2013023988A
Authority
JP
Japan
Prior art keywords
glass
fireproof
extinguishing agent
fire
double glazing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2011162440A
Other languages
Japanese (ja)
Other versions
JP5849493B2 (en
Inventor
Hirotsune Okubo
洋常 大久保
Tsutomu Funaoka
努 舟岡
Akinori Sato
明憲 佐藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Priority to JP2011162440A priority Critical patent/JP5849493B2/en
Publication of JP2013023988A publication Critical patent/JP2013023988A/en
Application granted granted Critical
Publication of JP5849493B2 publication Critical patent/JP5849493B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide fireproof double glazing excellent in fire resistance, and a fireproof double glazing unit.SOLUTION: Fireproof double glazing 12 of the present invention includes a fire-extinguishing agent 40. The fire-extinguishing agent 40 is a powder fire-extinguishing chemical and the main component thereof is sodium bicarbonate. The fire-extinguishing agent 40 is provided in a hollow part 24 of a spacer 16 of the fireproof double glazing 12, mixed in primary sealants 18A and 18B and a secondary sealant 22 of the fireproof double glazing 12, and also provided in a hollow part 42 of a frame body 30 of a fireproof double glazing unit 10. Arrangement parts of the fire-extinguishing agent 40 are not limited to the above-mentioned parts, and the fire-extinguishing agent 40 needs to be provided near the primary sealants 18A and 18B. Also, the fire-extinguishing agent 40 needs to be provided on at least one of the above-mentioned parts.

Description

本発明は、防火複層ガラス及び防火複層ガラスユニットに関する。   The present invention relates to fireproof double glazing and fireproof double glazing units.

複層ガラスのうち、防火複層ガラスと称されるものは、防火複層ガラスを構成するガラス板の少なくとも一枚に網入りガラス、耐熱強化ガラス、低膨張強化ガラス、透明結晶化ガラス等の耐熱防火性ガラス板が使用されたものをいう。   Among the double-glazed glass, what is called fire-proof double-glazed glass is such as at least one of the glass plates constituting the fire-proof double-glazed glass such as netted glass, heat-resistant tempered glass, low expansion tempered glass, transparent crystallized glass, etc. This refers to the use of heat and fireproof glass plates.

また、一般的な複層ガラスは、対向する少なくとも二枚のガラス板を、スペーサを介して隔置し、これらの二枚のガラス板と対向するスペーサの各側面を一次シール材によって二枚のガラス板にそれぞれ接着し、一次シール材の外側を二次シール材によって封止することにより構成される。   In addition, a general multilayer glass is formed by separating at least two glass plates facing each other through a spacer, and separating each side surface of the spacer facing these two glass plates with a primary sealing material. It is configured by adhering to a glass plate and sealing the outside of the primary sealing material with a secondary sealing material.

前記一次シール材は、複層ガラスの中空層の乾燥状態を保つ上で不可欠な構成部材であり、ガラス板との接着性が良好で、かつ透湿抵抗が高い有機系のブチル系シーリング材（ブチルゴム）が一般的に使用される。また、上述した防火複層ガラスにおいても、同様のブチル系シーリング材が一次シール材として使用される。   The primary sealing material is an indispensable component for maintaining the dry state of the hollow layer of the multi-layer glass, and is an organic butyl sealing material having good adhesion to the glass plate and high moisture resistance ( Butyl rubber) is generally used. Moreover, the same butyl-type sealing material is used as a primary sealing material also in the fireproof multilayer glass mentioned above.

ところで火災時に、防火複層ガラスを構成するガラス板のうち、火災発生側（以下、加熱面側とする）ではない側（以下、非加熱面側とする）のガラス板が高熱によって割れると、高温になった一次シール材から可燃性ガスが発生して一次シール材自身が発炎する場合があり、非加熱面側に火炎が生じるというおそれがある。   By the way, when the glass plate on the side (hereinafter referred to as the non-heating surface side) that is not the fire occurrence side (hereinafter referred to as the heating surface side) among the glass plates constituting the fireproof multilayer glass is broken by high heat, There is a case where flammable gas is generated from the primary sealing material that has become high temperature, and the primary sealing material itself may ignite, which may cause a flame on the non-heated surface side.

そこで、特許文献１の防火複層ガラスは、一次シール材の内側に内面シール材層を形成し、内面シール材層によって耐火難燃性能を高めている。   Therefore, the fireproof double-glazed glass of Patent Document 1 forms an inner surface sealing material layer on the inner side of the primary sealing material, and the fire resistance and flame retardancy is enhanced by the inner surface sealing material layer.

また、特許文献２の防火複層ガラスは、難燃性テープの層からなる一次シール材と難燃性の二次シール材との間に、防湿性シール材を介在させることによって耐火難燃性能を高めている。   Moreover, the fireproof double-glazed glass of Patent Document 2 has a fireproof and flameproof performance by interposing a moistureproof seal material between a primary seal material composed of a layer of flame retardant tape and a flame retardant secondary seal material. Is increasing.

特開平７−２３７９４１号公報JP 7-237941 A 特開２００１−１２１５７号公報JP 2001-12157 A

しかしながら、特許文献１の防火複層ガラスの内面シール材層、及び特許文献２の防火複層ガラスの防湿性シール材は、一次シール材の発炎を積極的に抑制するものではなく、一次シール材の発炎温度（発炎に至る時点の温度）を大幅に上げることができないという問題があった。   However, the inner surface sealing material layer of the fireproof double-glazed glass of Patent Document 1 and the moistureproof seal material of the fireproof double-glazed glass of Patent Document 2 do not actively suppress the flame of the primary seal material. There was a problem that the flame temperature of the material (the temperature at the time of reaching the flame) could not be increased significantly.

本発明は、このような事情に鑑みてなされたもので、一次シール材の発炎を積極的に抑制することで、一次シール材の発炎温度を大幅に上げることができる耐火難燃性能の高い防火複層ガラス及び防火複層ガラスユニットを提供することを目的とする。   The present invention has been made in view of such circumstances. By actively suppressing the flame of the primary seal material, the flame resistance of the primary seal material can be greatly increased. It aims at providing a high fireproof double glazing and a fireproof double glazing unit.

本発明は、前記目的を達成するために、対向する少なくとも二枚のガラス板がスペーサを介して隔置されるとともに、二枚のガラス板と対向するスペーサの各側面が一次シール材によって二枚のガラス板にそれぞれ接着されて二枚のガラス板間に中空層が形成され、一次シール材の外側が二次シール材によって封止され、少なくとも一枚のガラス板が耐熱防火性ガラス板によって構成された防火複層ガラスにおいて、前記防火複層ガラスに消火剤が備えられていることを特徴とする防火複層ガラスを提供する。   In order to achieve the above object, the present invention provides that at least two glass plates facing each other are separated by a spacer, and each side surface of the spacer facing the two glass plates is formed by two primary sealing materials. A hollow layer is formed between two glass plates by being bonded to each glass plate, the outer side of the primary sealing material is sealed with a secondary sealing material, and at least one glass plate is constituted by a heat-resistant and fire-resistant glass plate In the fire-resistant multilayer glass, the fire-resistant multilayer glass is provided with a fire extinguishing agent.

前記消火剤は、前記スペーサの中空部に備えられていることが好ましい。   The fire extinguishing agent is preferably provided in a hollow portion of the spacer.

前記消火剤は、前記一次シール材に備えられていることが好ましい。   The fire extinguishing agent is preferably provided in the primary sealing material.

また、本発明は、前記目的を達成するために、対向する少なくとも二枚のガラス板がスペーサを介して隔置されるとともに、二枚のガラス板と対向するスペーサの各側面が一次シール材によって二枚のガラス板にそれぞれ接着されて二枚のガラス板間に中空層が形成され、一次シール材の外側が二次シール材によって封止された複層ガラスであって、少なくとも一枚のガラス板が耐熱防火性ガラス板によって構成された防火複層ガラスと、該防火複層ガラスが装着される枠体と、からなる防火複層ガラスユニットにおいて、前記枠体の中空部に消火剤が備えられていることを特徴とする防火複層ガラスユニットを提供する。   In order to achieve the above object, the present invention provides that at least two glass plates facing each other are spaced apart via a spacer, and each side surface of the spacer facing the two glass plates is formed by a primary sealing material. A double-layer glass in which a hollow layer is formed between two glass plates by being bonded to two glass plates and the outer side of the primary sealing material is sealed with a secondary sealing material, and at least one glass In a fireproof double glazing unit comprising a fireproof double glazing glass comprising a heat and fireproof glass plate and a frame to which the fire proof double glazing is mounted, a fire extinguishing agent is provided in the hollow portion of the frame. A fireproof double glazing unit is provided.

本発明によれば、消火剤が防火複層ガラス、及び防火複層ガラスユニットに備えられているので、火炎時に、前記消火剤による燃焼の反応を抑える抑制作用、あるいは前記消火剤が熱分解して発生した不活性ガスの窒息作用で一次シール材の発炎を抑制できる。すなわち、一次シール材から発生した可燃性ガスが、前記不活性ガスによって希釈され、また前記不活性ガスの発生によって一次シール材近傍の酸素濃度が抑制されるので、一次シール材の発炎を積極的に抑制できる。よって、本発明によれば、消火剤を備えない防火複層ガラス、及び防火複層ガラスユニットと比較して、発炎温度が大幅に上がる。   According to the present invention, since the fire extinguishing agent is provided in the fireproof double glazing and the fireproof double glazing unit, the suppressing action of suppressing the combustion reaction by the fire extinguishing agent or the fire extinguishing agent is thermally decomposed during the flame. The suffocation of the inert gas generated in this way can suppress the flame of the primary sealing material. That is, the combustible gas generated from the primary seal material is diluted with the inert gas, and the oxygen concentration in the vicinity of the primary seal material is suppressed by the generation of the inert gas, so that the primary seal material is actively flamed. Can be suppressed. Therefore, according to this invention, compared with the fire prevention double glazing and fire prevention double glazing unit which are not equipped with a fire extinguisher, the flame emission temperature rises significantly.

前記消火剤は、防火複層ガラスの構成部材であって一次シール材の近傍にあるスペーサの中空部に備えることが好ましく、また、一次シール材に配合させてもよい。更に、防火複層ガラスユニットの場合には、防火複層ガラスの枠体の中空部に消火剤を備えることが好ましい。すなわち、消火剤は一次シール材の近傍に配置すること、及び一次シール材に配合することが好ましい。   The fire extinguishing agent is preferably a constituent member of fireproof double glazing, and is preferably provided in the hollow portion of the spacer in the vicinity of the primary sealing material, or may be blended in the primary sealing material. Furthermore, in the case of a fireproof multilayer glass unit, it is preferable to provide a fire extinguishing agent in the hollow part of the frame of the fireproof multilayer glass. That is, it is preferable to arrange | position a fire extinguisher in the vicinity of a primary sealing material, and to mix | blend with a primary sealing material.

前記消火剤は粉末消火薬剤であることが好ましい。これに対して液体消火薬剤の場合には、液体消火薬剤を封入する袋体が必要になり、この袋体が火炎時以外の平常時に破損すると液体消火薬剤が防火複層ガラスから漏出するので好ましくない。本発明の如く、消火剤が粉末消火薬剤であれば、スペーサの中空部に粉末消火薬剤を容易に充填できるとともに、スペーサ自体が粉末消火薬剤の袋体となるので、粉末消火薬剤が防火複層ガラスから漏れ出ることはない。   The fire extinguishing agent is preferably a powder fire extinguishing agent. On the other hand, in the case of a liquid fire extinguishing agent, a bag body that encloses the liquid fire extinguishing agent is required. Absent. When the extinguishing agent is a powder extinguishing agent as in the present invention, the hollow part of the spacer can be easily filled with the powder extinguishing agent, and the spacer itself becomes a powder extinguishing agent bag. There is no leakage from the glass.

また、前記粉末消火薬剤の主成分が炭酸水素ナトリウム（ＮａＨＣＯ３）であることが好ましい。炭酸水素ナトリウム（重曹）は、約２７０℃で熱分解し、熱分解によって生成されたナトリウム金属イオンが燃焼反応で生じる遊離基（ＯＨ・、Ｈ・）と結合することで燃焼の継続を抑制する。また、不活性ガスである炭酸ガスや水蒸気（２ＮａＨＣＯ３→Ｎａ２ＣＯ３＋ＣＯ２＋Ｈ２Ｏ）を発生する。一方、炭酸水素ナトリウム水溶液は、約６５℃以上で急速に分解するので、盛夏時等に太陽熱によって防火複層ガラスが加熱されて６５℃以上になると炭酸水素ナトリウム水溶液が分解する。すなわち、炭酸水素ナトリウム水溶液は、火炎時のみその機能（燃焼抑制機能）を発揮するものではないので好ましくない。 The main component of the powder fire extinguishing agent is preferably sodium hydrogen carbonate (NaHCO 3 ). Sodium hydrogencarbonate (bicarbonate) is thermally decomposed at about 270 ° C, and sodium metal ions generated by thermal decomposition are combined with free radicals (OH ·, H ·) generated in the combustion reaction to suppress the continuation of combustion. . Further, carbon dioxide gas or water vapor ( 2 NaHCO 3 → Na 2 CO 3 + CO 2 + H 2 O), which is an inert gas, is generated. On the other hand, the aqueous sodium hydrogen carbonate solution decomposes rapidly at about 65 ° C. or higher. Therefore, the sodium hydrogen carbonate aqueous solution decomposes when the fireproof multilayer glass is heated to 65 ° C. or higher due to solar heat in midsummer or the like. That is, an aqueous sodium hydrogen carbonate solution is not preferable because it does not exhibit its function (combustion suppression function) only during a flame.

よって、消火剤としては粉末消火薬剤を使用することが好ましく、粉末消火薬剤としては炭酸水素ナトリウムを使用することが好ましい。これにより、防火複層ガラス、及び防火複層ガラスユニットの耐火難燃性能をより一層高めることができる。なお、粉末消火薬剤としては、前記炭酸水素ナトリウムの他、リン酸アンモニウム、炭酸水素カリウム等も挙げることができる。   Therefore, it is preferable to use a powder fire extinguishing agent as the fire extinguishing agent, and it is preferable to use sodium bicarbonate as the powder extinguishing agent. Thereby, the fireproof flame retardant performance of a fireproof multilayer glass and a fireproof multilayer glass unit can be improved further. In addition, as a powder fire extinguishing agent, ammonium phosphate, potassium hydrogen carbonate, etc. other than the said sodium hydrogen carbonate can be mentioned.

本発明によれば、火炎時に燃焼の抑制作用あるいは窒息作用を有する消火剤が防火複層ガラス、及び防火複層ガラスユニットに備えられているので、防火複層ガラス、及び防火複層ガラスユニットの耐火難燃性能が向上する。   According to the present invention, the fireproof double-glazed glass and the fireproof double-glazed glass unit are provided with the fire-extinguishing double-glazed glass and the fire-proof double-glazed glass unit provided with a fire suppression agent or a suffocating action at the time of the flame. Fire resistance and flame retardant performance is improved.

実施の形態の防火複層ガラスの要部拡大断面図The principal part expanded sectional view of the fire prevention multilayer glass of embodiment 簡易試験装置の全体斜視図Overall perspective view of simple test equipment 簡易試験装置においてバーナーを使用して試料を加熱している説明図Explanatory drawing of heating a sample using a burner in a simple test device

以下、添付図面に従って本発明に係る防火複層ガラス及び防火複層ガラスユニットの好ましい実施の形態を詳説する。   Hereinafter, preferred embodiments of the fireproof double glazing and fireproof double glazing unit according to the present invention will be described in detail with reference to the accompanying drawings.

図１の断面図に示す実施の形態の防火複層ガラスユニット１０は、防火複層ガラス１２と枠体３０とから構成される。防火複層ガラス１２は、枠体３０の溝３２にセッティングブロック３４を介して載置されるとともに、枠体３０の両壁面３６Ａ、３６Ｂに、気密、水密機能のあるグレージングガスケット３８Ａ、３８Ｂを介して嵌合されている。枠体３０は、アルミニウム材等からなる金属製のユニット枠であり、このユニット枠を介して防火複層ガラス１２が、建物の壁部の開口部に取り付けられる。枠体３０は、アルミニウム材等の押し出し成形によって製造される。   The fireproof multilayer glass unit 10 according to the embodiment shown in the cross-sectional view of FIG. 1 includes a fireproof multilayer glass 12 and a frame 30. The fireproof multi-layer glass 12 is placed in the groove 32 of the frame body 30 via a setting block 34, and on both wall surfaces 36A and 36B of the frame body 30 through glazing gaskets 38A and 38B having airtight and watertight functions. Are mated. The frame body 30 is a metal unit frame made of an aluminum material or the like, and the fireproof multilayer glass 12 is attached to the opening of the wall portion of the building through the unit frame. The frame 30 is manufactured by extrusion molding of an aluminum material or the like.

防火複層ガラス１２は、対向する二枚のガラス板１４Ａ、１４Ｂがスペーサ１６を介して隔置されるとともに、二枚のガラス板１４Ａ、１４Ｂと対向するスペーサ１６の各側面１６Ａ、１６Ｂが一次シール材１８Ａ、１８Ｂによって二枚のガラス板１４Ａ、１４Ｂにそれぞれ接着されている。これにより、二枚のガラス板１４Ａ、１４Ｂ間に中空層２０が形成される。また、一次シール材１８Ａ、１８Ｂの外側が二次シール材２２によって封止されている。   In the fireproof multilayer glass 12, two glass plates 14A and 14B facing each other are separated by a spacer 16, and the side surfaces 16A and 16B of the spacer 16 facing the two glass plates 14A and 14B are primary. It is bonded to the two glass plates 14A and 14B by the sealing materials 18A and 18B, respectively. Thereby, the hollow layer 20 is formed between the two glass plates 14A and 14B. Further, the outer sides of the primary sealing materials 18A and 18B are sealed by the secondary sealing material 22.

スペーサ１６としては、アルミニウムを主材質とする金属製のスペーサが用いられる場合が多いが、ステンレス材や硬質樹脂からなるものも使用される場合がある。スペーサ１６はその内部に中空部２４を有し、中空部２４には粒状ゼオライト等の乾燥剤２６が充填されている。スペーサ１６には、中空部２４を中空層２０に連通させる貫通孔２８が開口されており、この貫通孔２８を介して中空層２０の空気が乾燥される。   As the spacer 16, a metal spacer mainly made of aluminum is often used, but a spacer made of stainless steel or hard resin may also be used. The spacer 16 has a hollow portion 24 therein, and the hollow portion 24 is filled with a desiccant 26 such as granular zeolite. The spacer 16 has a through hole 28 that allows the hollow portion 24 to communicate with the hollow layer 20, and the air in the hollow layer 20 is dried through the through hole 28.

このように構成された防火複層ガラス１２は、一方のガラス板１４Ａが耐熱防火性ガラス板である網入りガラス板であり、他方のガラス板１４Ｂが一般的なソーダライムガラスに代表される非耐熱防火性ガラス板である。なお、ガラス板１４Ａとして耐熱強化ガラス、低膨張強化ガラス、透明結晶化ガラス等の別の耐熱防火性ガラス板を使用してもよい。   The fireproof multi-layer glass 12 configured as described above is a netted glass plate in which one glass plate 14A is a heat and fireproof glass plate, and the other glass plate 14B is non-typified by general soda lime glass. It is a heat and fire resistant glass plate. In addition, you may use another heat-resistant fireproof glass plates, such as heat-resistant tempered glass, low expansion | strengthening tempered glass, and transparent crystallized glass, as the glass plate 14A.

また、本発明の防火複層ガラス１２の一次シール材１８Ａ、１８Ｂは、ガラス板との接着性が良好で透湿抵抗の高いブチル系シーリング材である。二次シール材２２は、ポリサルファイド、シリコーン、ウレタンなどの硬化性エラストマをベースとし、ガラスとの接着性を発現するために適当な変性を加えられたものなどが好適である。   Moreover, the primary sealing materials 18A and 18B of the fireproof multilayer glass 12 of the present invention are butyl-based sealing materials that have good adhesion to a glass plate and high moisture permeability resistance. The secondary sealing material 22 is preferably based on a curable elastomer such as polysulfide, silicone, urethane, or the like, which has been appropriately modified to exhibit adhesion to glass.

実施の形態の防火複層ガラスユニット１０には、消火剤４０が備えられている。この消火剤４０は、粉末消火薬剤であり、その主成分が炭酸水素ナトリウムである。   The fireproof multilayer glass unit 10 of the embodiment is provided with a fire extinguishing agent 40. This fire extinguisher 40 is a powder fire extinguisher, and the main component is sodium hydrogen carbonate.

消火剤４０は、防火複層ガラス１２のスペーサ１６の中空部２４に備えられるとともに、防火複層ガラス１２の一次シール材１８Ａ、１８Ｂ、及び二次シール材２２に配合され、また、防火複層ガラスユニット１０の枠体３０の中空部４２に備えられている。スペーサ１６の中空部２４に備えられた消火剤４０は、貫通孔２８を介して一次シール材１８Ａ、１８Ｂに連通される。また、枠体３０の中空部４２に備えられ消火剤４０は、枠体３０の両壁面３６Ａ、３６Ｂの貫通孔４４を介して防火複層ガラス１２に連通される。   The fire extinguishing agent 40 is provided in the hollow portion 24 of the spacer 16 of the fireproof multilayer glass 12, and is blended in the primary seal materials 18A and 18B and the secondary seal material 22 of the fireproof multilayer glass 12, and the fireproof multilayer It is provided in the hollow part 42 of the frame 30 of the glass unit 10. The fire extinguishing agent 40 provided in the hollow portion 24 of the spacer 16 is communicated with the primary sealing materials 18A and 18B through the through hole 28. Further, the fire extinguishing agent 40 provided in the hollow portion 42 of the frame 30 is communicated with the fireproof multilayer glass 12 through the through holes 44 of both wall surfaces 36A and 36B of the frame 30.

なお、消火剤４０の配置箇所は、上記箇所に限定されるものではなく、消火剤４０は一次シール材１８Ａ、１８Ｂの近傍に備えられていればよい。また、消火剤４０は、上記箇所のうち、少なくとも１箇所に備えられていればよい。   In addition, the arrangement | positioning location of the fire extinguishing agent 40 is not limited to the said location, The fire extinguishing agent 40 should just be provided in the vicinity of the primary sealing materials 18A and 18B. Moreover, the fire extinguishing agent 40 should just be provided in at least 1 place among the said places.

炭酸水素ナトリウム等の消火剤４０は、火炎により熱分解してナトリウム金属イオンや不活性ガス（炭酸ガス）を発生する。このような消火剤４０が防火複層ガラス１２、及び防火複層ガラスユニット１０に備えられているので、火炎時に消火剤４０から発生した前記ナトリウム金属イオンの抑制作用、あるいは前記不活性ガスの窒息作用で一次シール材１８Ａ、１８Ｂの発炎を抑制できる。すなわち、一次シール材１８Ａ、１８Ｂの燃焼反応で生じる遊離基（ＯＨ・、Ｈ・）と前記ナトリウム金属イオンが結合することで燃焼の継続が抑制される。また一次シール材１８Ａ、１８Ｂから発生した可燃性ガスが、前記不活性ガスによって希釈され、また前記不活性ガスの発生によって一次シール材近傍の酸素濃度が抑制されるので、一次シール材１８Ａ、１８Ｂの発炎を積極的に抑制できる。   The fire extinguishing agent 40 such as sodium hydrogen carbonate is thermally decomposed by a flame to generate sodium metal ions and inert gas (carbon dioxide gas). Since such a fire extinguishing agent 40 is provided in the fireproof double glazing 12 and the fireproof double glazing unit 10, it suppresses the sodium metal ions generated from the fire extinguishing agent 40 during a flame, or suffocates the inert gas. The action can suppress the flames of the primary sealing materials 18A and 18B. That is, the free radicals (OH., H.) generated by the combustion reaction of the primary sealing materials 18A, 18B are combined with the sodium metal ions to suppress the continuation of combustion. Further, since the combustible gas generated from the primary sealing materials 18A and 18B is diluted with the inert gas, and the generation of the inert gas suppresses the oxygen concentration in the vicinity of the primary sealing material, the primary sealing materials 18A and 18B. Can positively suppress the inflammation.

よって、実施の形態の防火複層ガラス１２、及び防火複層ガラスユニット１０によれば、消火剤を備えない防火複層ガラス、及び防火複層ガラスユニットと比較して、一次シール材１８Ａ、１８Ｂの発炎温度が大幅に上がり、耐火難燃性能が向上する。   Therefore, according to the fireproof multilayer glass 12 and the fireproof multilayer glass unit 10 of the embodiment, the primary sealing materials 18A and 18B are compared with the fireproof multilayer glass and the fireproof multilayer glass unit that do not include a fire extinguishing agent. This significantly increases the flame temperature and improves fire and flame resistance.

消火剤４０は、液体消火薬剤であってもよいが、実施の形態の如く粉末消火薬剤であることが好ましい。前記液体消火薬剤の場合には、液体消火薬剤を封入する袋体が必要になり、この袋体が火炎時以外の通常時に破損すると液体消火薬剤が防火複層ガラス１２から漏出するので好ましくない。   The extinguishing agent 40 may be a liquid extinguishing agent, but is preferably a powder extinguishing agent as in the embodiment. In the case of the liquid fire-extinguishing agent, a bag body that encloses the liquid fire-extinguishing agent is required, and if the bag body is damaged at a normal time other than the time of the flame, the liquid fire-extinguishing agent leaks from the fire-proof multilayer glass 12, which is not preferable.

実施の形態の如く、消火剤４０が粉末消火薬剤であれば、スペーサ１６の中空部に消火剤４０を容易に充填できるとともに、スペーサ１６自体が消火剤４０の袋体となるので、消火剤４０が防火複層ガラス１２から漏れ出ることはない。   If the extinguishing agent 40 is a powder extinguishing agent as in the embodiment, the extinguishing agent 40 can be easily filled into the hollow portion of the spacer 16 and the spacer 16 itself becomes a bag of the extinguishing agent 40. Does not leak out from the fireproof multilayer glass 12.

また、前記粉末消火薬剤の主成分が炭酸水素ナトリウム（ＮａＨＣＯ３）であることが好ましい。炭酸水素ナトリウムは、約２７０℃で熱分解し、熱分解によって生成されたナトリウム金属イオンが燃焼反応で生じる遊離基（OH・、H・）と結合することで燃焼の継続を抑制する。また、不活性ガスである炭酸ガス（２ＮａＨＣＯ３→Ｎａ２ＣＯ３＋ＣＯ２＋Ｈ２Ｏ）を発生する。一方、炭酸水素ナトリウム水溶液は、約６５℃以上で急速に分解するので、盛夏時等に太陽熱によって防火複層ガラスが加熱されて６５℃以上になると炭酸水素ナトリウム水溶液が分解する。すなわち、炭酸水素ナトリウム水溶液は、火炎時のみその機能（燃焼抑制機能）を発揮するものではないので好ましくない。 The main component of the powder fire extinguishing agent is preferably sodium hydrogen carbonate (NaHCO 3 ). Sodium bicarbonate is thermally decomposed at about 270 ° C., and sodium metal ions generated by the thermal decomposition are combined with free radicals (OH ·, H ·) generated in the combustion reaction, thereby suppressing the continuation of combustion. Further, carbon dioxide gas ( 2 NaHCO 3 → Na 2 CO 3 + CO 2 + H 2 O) which is an inert gas is generated. On the other hand, the aqueous sodium hydrogen carbonate solution decomposes rapidly at about 65 ° C. or higher. Therefore, the sodium hydrogen carbonate aqueous solution decomposes when the fireproof multilayer glass is heated to 65 ° C. or higher due to solar heat in midsummer or the like. That is, an aqueous sodium hydrogen carbonate solution is not preferable because it does not exhibit its function (combustion suppression function) only during a flame.

よって、消火剤４０としては粉末消火薬剤を使用することが好ましく、粉末消火薬剤としては炭酸水素ナトリウムを使用することが好ましい。これにより、防火複層ガラス１２、及び防火複層ガラスユニット１０の耐火難燃性能をより一層高めることができる。なお、粉末消火薬剤としては、前記炭酸水素ナトリウムの他、リン酸アンモニウム、炭酸水素カリウム等も挙げることができる。   Therefore, it is preferable to use a powder fire extinguisher as the fire extinguishing agent 40, and it is preferable to use sodium hydrogen carbonate as the powder fire extinguishing agent. Thereby, the fire-resistant flame-retardant performance of the fireproof multilayer glass 12 and the fireproof multilayer glass unit 10 can be further improved. In addition, as a powder fire extinguishing agent, ammonium phosphate, potassium hydrogen carbonate, etc. other than the said sodium hydrogen carbonate can be mentioned.

なお、図１では二枚のガラス板１４Ａ、１４Ｂを備えた防火複層ガラス１２を例示したが、３枚以上のガラス板を備えた防火複層ガラスであってもよい。   In addition, in FIG. 1, although the fire prevention multilayer glass 12 provided with the two glass plates 14A and 14B was illustrated, the fire prevention multilayer glass provided with the 3 or more glass plate may be sufficient.

また、防火複層ガラスユニット１０、及び防火複層ガラス１２の耐火難燃性をより一層高めるために、一次シール材１８Ａ、１８Ｂに難燃剤を配合してもよい。すなわち、一次シール材１８Ａ、１８Ｂを、ブチル系シーリング材の主成分であるポリイソブチレン、又はブチルゴムと難燃剤とが配合されたブチル系（ポリイソブチレン系、又はブチルゴム系）組成物としてもよい。この一次シール材１８Ａ、１８Ｂには、前記のゴム成分の他に、一般にゴム成形に用いられる加硫剤、加硫促進剤、加硫助剤等の架橋剤、加硫遅延剤が配合され得る。更に、その効果を阻害しない範囲で、その他の添加剤等も配合され得る。前記添加剤としては、例えば、カーボンブラック、シリカ、クレー、タルク、炭酸カルシウムなどの充填剤（フィラー）、ワックス、シランカップリング剤、活性剤、可塑剤、軟化剤、老化防止剤、酸化防止剤、滑剤、顔料、紫外線吸収剤、分散剤、脱水剤、粘着付与剤、帯電防止剤、加工助剤等が挙げられる。これらの添加剤は、ゴム組成物用の一般的なものを挙げることができる。それらの配合量も特に制限されず、任意に選択される。   Moreover, in order to further improve the fire resistance and flame resistance of the fireproof multilayer glass unit 10 and the fireproof multilayer glass 12, a flame retardant may be blended in the primary sealing materials 18A and 18B. That is, the primary sealing materials 18A and 18B may be polyisobutylene which is a main component of a butyl sealant, or a butyl (polyisobutylene or butyl rubber) composition in which butyl rubber and a flame retardant are blended. In addition to the rubber component described above, the primary sealants 18A and 18B can be blended with a vulcanizing agent, a vulcanization accelerator, a vulcanization aid, and the like, which are generally used for rubber molding, and a vulcanization retarder. . Furthermore, other additives and the like can be blended as long as the effect is not impaired. Examples of the additive include fillers such as carbon black, silica, clay, talc, calcium carbonate, wax, silane coupling agent, activator, plasticizer, softener, anti-aging agent, antioxidant. , Lubricants, pigments, ultraviolet absorbers, dispersants, dehydrating agents, tackifiers, antistatic agents, processing aids, and the like. These additives may include those commonly used for rubber compositions. Their blending amounts are not particularly limited, and are arbitrarily selected.

また前記のように一次シール材１８Ａ、１８Ｂに難燃剤を配合する場合、一次シール材１８Ａ、１８Ｂに配合される難燃剤の種類は特に限定されず、公知のものが使用でき、例えば、無機系難燃剤、有機系難燃剤等が挙げられる。前記無機系難燃剤としては、例えば、金属水酸化物（水酸化アルミニウム、水酸化マグネシウム等）、アンチモン系化合物（三酸化アンチモン、アンチモン酸ソーダ等）、その他無機系化合物（ホウ素化合物、モリブデン系化合物、赤リン系化合物等）が挙げられる。中でも毒性が比較的低いという点で、金属水酸化物が好ましい。前記有機系難燃剤としては、例えば、ハロゲン系化合物（塩素化パラフィン、臭素化芳香族トリアジン化合物、デカブロモジフェニルエーテル、テトラブロモビスフェノールＡ誘導体等）、リン系化合物（ポリリン酸アンモニウム類、リン酸メラミン等）、窒素系化合物（メラミンシアヌレート等）等が挙げられる。   Moreover, when mix | blending a flame retardant with primary sealing material 18A, 18B as mentioned above, the kind of flame retardant mix | blended with primary sealing material 18A, 18B is not specifically limited, A well-known thing can be used, for example, inorganic type Examples include flame retardants and organic flame retardants. Examples of the inorganic flame retardant include metal hydroxide (aluminum hydroxide, magnesium hydroxide, etc.), antimony compounds (antimony trioxide, sodium antimonate, etc.), and other inorganic compounds (boron compounds, molybdenum compounds). , Red phosphorus compounds, etc.). Of these, metal hydroxides are preferred because of their relatively low toxicity. Examples of the organic flame retardant include halogen compounds (chlorinated paraffin, brominated aromatic triazine compounds, decabromodiphenyl ether, tetrabromobisphenol A derivatives, etc.), phosphorus compounds (ammonium polyphosphates, melamine phosphate, etc.) ), Nitrogen compounds (such as melamine cyanurate) and the like.

一次シール材１８Ａ、１８Ｂに対する難燃剤の配合量は、ベースになるブチル系成分１００質量部に対して添加した難燃剤の量で表す（単位を質量部（ｐｈｒ）と表す）。すなわち、前記の難燃剤を配合した一次シール材１８Ａ、１８Ｂにおける難燃剤の含有量は、ベースのブチル系成分１００質量部に対して５〜２００質量部であり、好ましくは１０〜１５０質量部、更に好ましくは２０〜６０質量部である。難燃剤が５質量部以上配合されていることにより、防火試験の基準を安定して満たすことができる。また、２００質量部以下に配合量を抑えることにより、加工性や粘着性等が適度なものになるという利点がある。   The blending amount of the flame retardant with respect to the primary sealing materials 18A and 18B is represented by the amount of the flame retardant added with respect to 100 parts by mass of the base butyl-based component (the unit is represented by parts by mass (phr)). That is, the content of the flame retardant in the primary sealing materials 18A and 18B blended with the above flame retardant is 5 to 200 parts by mass, preferably 10 to 150 parts by mass, with respect to 100 parts by mass of the base butyl component. More preferably, it is 20-60 mass parts. By blending 5 parts by mass or more of the flame retardant, it is possible to stably meet the fire test standard. Moreover, there exists an advantage that processability, adhesiveness, etc. become moderate by restraining a compounding quantity to 200 mass parts or less.

以上、本発明の実施の形態を図面により詳述してきたが、本発明は前記実施の形態に限定されるものではなく、本発明の要旨を逸脱しない範囲での種々の設計変更等が可能である。例えば、防火複層ガラス１２を構成するガラス板１４Ｂとして、通常のフロートガラス板を用いるほか、強化ガラス、合わせガラス、熱線吸収ガラス、更には、熱線反射ガラス、低反射率ガラスなどのように、表面に金属や他の無機物を薄くコーティングしたガラス板などであり、特に限定されない。また、防火複層ガラス１２は中空層２０をアルゴンやクリプトン等の断熱ガスで置換したものでもよい。その他の構成についても、同様である。   Although the embodiments of the present invention have been described in detail with reference to the drawings, the present invention is not limited to the above-described embodiments, and various design changes and the like can be made without departing from the scope of the present invention. is there. For example, as a glass plate 14B constituting the fireproof multilayer glass 12, in addition to using an ordinary float glass plate, tempered glass, laminated glass, heat ray absorbing glass, further, heat ray reflecting glass, low reflectance glass, etc. It is a glass plate with a thin coating of metal or other inorganic material on the surface, and is not particularly limited. Further, the fireproof double-glazed glass 12 may be one in which the hollow layer 20 is replaced with a heat insulating gas such as argon or krypton. The same applies to other configurations.

〔簡易試験装置、簡易試験方法、及び試験結果〕
図２に示す簡易試験装置５０は、５５０℃まで昇温可能な市販のセラミックホットプレート（アズワン社製：ＣＨＰ−２５０ＤＮ）５２を備えている。このセラミックホットプレート５２の加熱面５４の略中央部に、試料５６であるブチル系シーリング材を載せた鉄板（１００×１５０ｍｍ：厚さ３ｍｍ）５８が載置される。 [Simple test equipment, simple test method, and test results]
A simple test apparatus 50 shown in FIG. 2 includes a commercially available ceramic hot plate (manufactured by ASONE: CHP-250DN) 52 capable of raising the temperature to 550 ° C. An iron plate (100 × 150 mm: thickness 3 mm) 58 on which a butyl-based sealing material, which is a sample 56, is placed at a substantially central portion of the heating surface 54 of the ceramic hot plate 52.

鉄板５８の上面には、試料５６の周囲を囲む４本の耐火ボード（高さ２０ｍｍ）６０、６０…が載置されるとともに、試料５６の上面を覆うように図３の複数本の耐火ボード６２、６２…が耐火ボード６０、６０…に載置される。また、中央の２本の耐火ボード６２、６２の間には、幅１０ｍｍ、長さ５０ｍｍのスリット６４が備えられている。   3 are placed on the upper surface of the iron plate 58 and the plurality of fire-resistant boards shown in FIG. 3 so as to cover the upper surface of the sample 56. 62, 62... Are placed on the fireproof boards 60, 60. A slit 64 having a width of 10 mm and a length of 50 mm is provided between the two fireproof boards 62 and 62 in the center.

上記の如く簡易試験装置５０が構成されるが、この簡易試験装置５０には、試料５６を加熱する市販のバーナー６６も備えられている。   The simple test apparatus 50 is configured as described above, and the simple test apparatus 50 is also provided with a commercially available burner 66 for heating the sample 56.

以下、簡易試験方法について説明する。   Hereinafter, a simple test method will be described.

まず、セラミックホットプレート５２のスイッチ６８を入れて加熱面５４の昇温を開始する。   First, the switch 68 of the ceramic hot plate 52 is turned on to start the heating of the heating surface 54.

次に、セラミックホットプレート５２の表示部７０に表示された温度が３００℃を超えた時点で、図３の如くバーナー６６を点火して、その炎７２を、試料５６に直接当たらないように、スリット６４を介して試料５６の上部にかざし、その状態で試料５６の昇温を継続する。なお、バーナー６６の炎７２の中心から試料５６までの距離は約６５ｍｍである。   Next, when the temperature displayed on the display unit 70 of the ceramic hot plate 52 exceeds 300 ° C., the burner 66 is ignited as shown in FIG. 3 so that the flame 72 does not directly hit the sample 56. The sample 56 is held over the slit 56 through the slit 64, and the temperature of the sample 56 is continued to rise. The distance from the center of the flame 72 of the burner 66 to the sample 56 is about 65 mm.

試料５６が昇温すると、試料５６から発生した分解ガスが着火し、継続的な「発炎」が発生し始めたときに表示部７０に表示された温度を読み取り、その値を試料５６が発炎した温度として記録する。   When the temperature of the sample 56 rises, the decomposition gas generated from the sample 56 ignites, and when the continuous “flame” starts to be generated, the temperature displayed on the display unit 70 is read. Record as flame temperature.

簡易試験結果として、ブチル系シーリング材（横浜ゴム社製ＳＭ４８８）及びその近傍に炭酸水素ナトリウムを配置した試料の発炎温度は、５１９℃以上であり、炭酸水素ナトリウムの配合量が増えるに従って発炎温度が上昇する傾向にあった。また、炭酸水素ナトリウムを配置しないブチル系シーリング材（横浜ゴム社製ＳＭ４８８）の試料では、発炎温度が５０８℃であった。よって、炭酸水素ナトリウムを配置しない試料よりも、炭酸水素ナトリウムを近傍に配置したブチル系シーリング材の発炎温度が高いことを確認できた。   As a result of the simple test, the flame temperature of a sample in which sodium hydrogen carbonate was placed in the vicinity of a butyl sealant (Yokohama Rubber SM488) was 519 ° C. or more, and the flame was emitted as the amount of sodium hydrogen carbonate increased. There was a tendency for the temperature to rise. Moreover, in the sample of the butyl-type sealing material (SM488 manufactured by Yokohama Rubber Co., Ltd.) in which sodium hydrogen carbonate is not disposed, the flame temperature was 508 ° C. Therefore, it was confirmed that the flammable temperature of the butyl-based sealing material in which sodium hydrogen carbonate was arranged in the vicinity was higher than that of the sample in which sodium hydrogen carbonate was not arranged.

この方法により、複層ガラスに使用するブチル系シーリング材に消火剤を混入した場合、ブチル系シーリング材に消火剤を混入した方が、発炎温度が改善されことが分かった。   According to this method, it was found that when a fire extinguishing agent was mixed in a butyl sealant used for a double glazing, the flame temperature was improved by adding a fire extinguishing agent to the butyl sealant.

〔実大防火試験の規格、及び試験方法〕
ユニットフレームに防火複層ガラスを組み付けた試験体を、鉄及び耐火材からなる枠体で保持し、国土交通大臣に認可を受けた性能評価機関が定める「防耐火性能試験・評価業務方法書」に規定される「遮炎・準遮炎性能試験・評価方法」に準拠した防火試験（加熱試験）を実施した。加熱面は、耐熱強化ガラス側とした。 [Standard and test method of full-scale fire prevention test]
A test body in which fireproof double-layer glass is assembled to the unit frame is held by a frame made of iron and refractory material, and the `` Fireproof and Fireproof Performance Test / Evaluation Work Method '' established by a performance evaluation organization approved by the Minister of Land, Infrastructure and Transport A fire prevention test (heating test) in accordance with the “flame shielding / quasi-flame shielding performance test / evaluation method” prescribed in 1) was carried out. The heating surface was the heat-resistant tempered glass side.

下記の表１に試験体である実施例品と比較例品の防火複層ガラスの仕様を示す。   Table 1 below shows the specifications of the fireproof double-glazed glass of the example product and the comparative example product that are test specimens.

試験体の縦辺左右のどちらか中央に位置する炉内側ガラス端部に熱電対を事前に貼り付け、複層ガラス封着部のシール材付近から最初に発炎が生じたときの温度を記録した。   A thermocouple is attached in advance to the furnace inner glass edge located at the center of either the left or right side of the test specimen, and the temperature at which the first flame is generated from the vicinity of the sealing material in the multilayer glass seal is recorded. did.

Figure 2013023988
Figure 2013023988

上記発炎時ガラス端部温度に示すように、比較例品の発炎温度は４１５℃であったのに対し、実施例品の発炎温度は４９２℃であった。よって、双方を比較すると、実施例品の発炎温度が大幅に上がることが確認できた。   As shown in the glass end temperature at the time of the flame, the flame temperature of the comparative product was 415 ° C., whereas the flame temperature of the example product was 492 ° C. Therefore, when both were compared, it was confirmed that the flame temperature of the example product was significantly increased.

なお、本発明は、防火複層ガラスのガラス板構成に限定を加えるものではない。つまり、本発明は、火炎による加熱によって破損する非耐熱防火性ガラスと、耐熱防火性ガラス板とを組み合わせた防火複層ガラスに特に有効であるが、防火複層ガラスを構成する全てのガラス板を耐熱防火性ガラス板とした防火複層ガラスでも有効である。   In addition, this invention does not add limitation to the glass plate structure of a fire prevention multilayer glass. In other words, the present invention is particularly effective for a fireproof double-glazed glass that combines a non-heatproof fireproof glass that is damaged by heating with a flame and a heat-resistant fireproof glass plate, but all the glass plates constituting the fireproof double-glazed glass. It is also effective in fireproof double-glazed glass with heat resistant and fireproof glass plates.

１０…防火複層ガラスユニット、１２…防火複層ガラス、１４Ａ…ガラス板（網入りガラス板等の耐熱防火性ガラス板）、１４Ｂ…ガラス板（ソーダライムガラス等の非耐熱防火性ガラス板）、１６…スペーサ、１６Ａ、１６Ｂ…スペーサの側面、１８Ａ、１８Ｂ…一次シール材、２０…中空層、２２…二次シール材、２４…中空部、２６…乾燥剤、２８…貫通孔、３０…枠体、３２…溝、３４…セッティングブロック、３６Ａ、３６Ｂ…両壁面、３８Ａ、３８Ｂ…グレージングガスケット、４０…消火剤、４２…中空部、４４…貫通孔、５０…簡易試験装置、５２…セラミックホットプレート、５４…加熱面、５６…試料、５８…鉄板、６０…耐火ボード、６２…耐火ボード、６４…スリット、６６…バーナー、６８…スイッチ、７０…表示部、７２…炎   DESCRIPTION OF SYMBOLS 10 ... Fireproof double-glazed glass unit, 12 ... Fireproof double-glazed glass, 14A ... Glass plate (heat-resistant fire-proof glass plate, such as a meshed glass plate), 14B ... Glass plate (non-heat-resistant fire-proof glass plate, such as soda-lime glass) , 16 ... Spacer, 16A, 16B ... Spacer side, 18A, 18B ... Primary sealant, 20 ... Hollow layer, 22 ... Secondary sealant, 24 ... Hollow part, 26 ... Desiccant, 28 ... Through-hole, 30 ... Frame, 32 ... groove, 34 ... setting block, 36A, 36B ... both wall surfaces, 38A, 38B ... glazing gasket, 40 ... extinguishing agent, 42 ... hollow part, 44 ... through hole, 50 ... simple test device, 52 ... ceramic Hot plate, 54 ... heating surface, 56 ... sample, 58 ... iron plate, 60 ... fireproof board, 62 ... fireproof board, 64 ... slit, 66 ... burner, 68 ... switch, 70 ... table Part, 72 ... flame

Claims (8)

対向する少なくとも二枚のガラス板がスペーサを介して隔置されるとともに、二枚のガラス板と対向するスペーサの各側面が一次シール材によって二枚のガラス板にそれぞれ接着されて二枚のガラス板間に中空層が形成され、一次シール材の外側が二次シール材によって封止され、少なくとも一枚のガラス板が耐熱防火性ガラス板によって構成された防火複層ガラスにおいて、
前記防火複層ガラスに消火剤が備えられていることを特徴とする防火複層ガラス。 At least two glass plates facing each other are separated by a spacer, and each side surface of the spacer facing the two glass plates is bonded to the two glass plates by a primary sealing material, respectively. In the fireproof multilayer glass in which a hollow layer is formed between the plates, the outer side of the primary sealant is sealed with a secondary sealant, and at least one glass plate is constituted by a heat and fireproof glass plate,
A fireproof multilayer glass, wherein the fireproof multilayer glass is provided with a fire extinguishing agent. 前記消火剤は、前記スペーサの中空部に備えられている請求項１に記載の防火複層ガラス。   The fire-extinguishing multilayer glass according to claim 1, wherein the extinguishing agent is provided in a hollow portion of the spacer. 前記消火剤は、前記一次シール材に備えられている請求項１、又は２に記載の防火複層ガラス。   The fireproof multilayer glass according to claim 1 or 2, wherein the fire extinguishing agent is provided in the primary sealing material. 前記消火剤は粉末消火薬剤である請求項１、２又は３に記載の防火複層ガラス。   The fireproof multilayer glass according to claim 1, 2, or 3, wherein the fire extinguishing agent is a powder fire extinguishing agent. 前記粉末消火薬剤の主成分が炭酸水素ナトリウムである請求項４に記載の防火複層ガラス。   The fireproof multilayer glass according to claim 4, wherein a main component of the powder fire extinguishing agent is sodium hydrogen carbonate. 対向する少なくとも二枚のガラス板がスペーサを介して隔置されるとともに、二枚のガラス板と対向するスペーサの各側面が一次シール材によって二枚のガラス板にそれぞれ接着されて二枚のガラス板間に中空層が形成され、一次シール材の外側が二次シール材によって封止された複層ガラスであって、少なくとも一枚のガラス板が耐熱防火性ガラス板によって構成された防火複層ガラスと、該防火複層ガラスが装着される枠体と、からなる防火複層ガラスユニットにおいて、
前記枠体の中空部に消火剤が備えられていることを特徴とする防火複層ガラスユニット。 At least two glass plates facing each other are separated by a spacer, and each side surface of the spacer facing the two glass plates is bonded to the two glass plates by a primary sealing material, respectively. A fireproof multilayer in which a hollow layer is formed between plates, and the outer side of the primary sealing material is sealed with a secondary sealing material, and at least one glass plate is constituted by a heat and fireproof glass plate In a fireproof double glazing unit comprising glass and a frame on which the fireproof double glazing is mounted,
A fireproof multilayer glass unit, wherein a fire extinguishing agent is provided in a hollow portion of the frame. 前記消火剤は粉末消火薬剤である請求項６に記載の防火複層ガラスユニット。   The fireproof multilayer glass unit according to claim 6, wherein the fire extinguishing agent is a powder fire extinguishing agent. 前記粉末消火薬剤の主成分が炭酸水素ナトリウムである請求項７に記載の防火複層ガラスユニット。   The fireproof multilayer glass unit according to claim 7, wherein a main component of the powder fire extinguishing agent is sodium hydrogen carbonate.
JP2011162440A 2011-07-25 2011-07-25 Fireproof double glazing and fireproof double glazing unit Active JP5849493B2 (en)