JP2012226236A - Organic photoreceptor, image forming apparatus, and image forming cartridge - Google Patents
Organic photoreceptor, image forming apparatus, and image forming cartridge Download PDFInfo
- Publication number
- JP2012226236A JP2012226236A JP2011095811A JP2011095811A JP2012226236A JP 2012226236 A JP2012226236 A JP 2012226236A JP 2011095811 A JP2011095811 A JP 2011095811A JP 2011095811 A JP2011095811 A JP 2011095811A JP 2012226236 A JP2012226236 A JP 2012226236A
- Authority
- JP
- Japan
- Prior art keywords
- organic photoreceptor
- image forming
- layer
- organic
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、有機感光体、この有機感光体を具えた画像形成装置および画像形成用カートリッジに関する。 The present invention relates to an organic photoconductor, an image forming apparatus including the organic photoconductor, and an image forming cartridge.
新興国市場においては、画像支持体として酸性紙を用いることが今なお主流とされている。この酸性紙を用いた画像形成においては、当該酸性紙の紙粉により、一種の像流れ現象である紙粉ボケなどの画像不良が発生するという問題がある。この紙粉ボケは、酸性紙の紙粉が感光体表面に付着し、空気中の水分が酸性紙成分であるタルク（３ＭｇＯ・４ＳｉＯ2 ・Ｈ2 Ｏ）やカオリン（Ａｌ2 Ｏ3 ・Ｈ2 Ｏ）により取り込まれ、感光体の表面抵抗が低下し、現像特性が低下することによって発生する現象である。従って、高温高湿環境の地域においては、この紙粉ボケなどの画像不良が顕著に発生する。 In emerging markets, the use of acidic paper as the image support is still the mainstream. In the image formation using the acid paper, there is a problem that image defects such as paper dust blur, which is a kind of image flow phenomenon, occur due to the paper dust of the acid paper. In this paper powder blur, talc (3MgO · 4SiO 2 · H 2 O) or kaolin (Al 2 O 3 · H 2 O) in which acid paper dust adheres to the surface of the photoconductor and moisture in the air is an acidic paper component. O) is a phenomenon that occurs when the surface resistance of the photoreceptor decreases and the development characteristics deteriorate. Therefore, image defects such as paper dust blur occur remarkably in high temperature and high humidity environments.
このような問題を解決するため、感光体表面に付着した紙粉を除去する紙粉除去装置を具えた画像形成装置が提案されているが、装置の小型化やコストの観点から望ましいものではない（例えば特許文献１参照）。 In order to solve such a problem, an image forming apparatus including a paper dust removing device that removes paper dust attached to the surface of the photosensitive member has been proposed, but it is not desirable from the viewpoint of downsizing and cost of the device. (For example, refer to Patent Document 1).
また、感光体表面に付着した紙粉を除去するために当該感光体表面を構成する樹脂を削り取る際に、感光体表面に傷がつき、形成される画像に白スジ状の画像ノイズが発生するという問題がある。 Further, when the resin constituting the surface of the photoconductor is scraped to remove paper dust attached to the surface of the photoconductor, the surface of the photoconductor is scratched and white streak-like image noise is generated in the formed image. There is a problem.
本発明は、以上のような事情に基づいてなされたものであって、その目的は、画像支持体として酸性紙を用いる場合において、紙粉ボケや画像ノイズなどの画像不良の発生を抑制することのできる有機感光体、画像形成装置および画像形成用カートリッジを提供することにある。 The present invention has been made based on the above circumstances, and its purpose is to suppress the occurrence of image defects such as paper dust blur and image noise in the case of using acidic paper as an image support. It is an object of the present invention to provide an organic photoreceptor, an image forming apparatus, and an image forming cartridge.
本発明の有機感光体は、導電性支持体上に、少なくとも有機感光層が積層されてなる有機感光体において、
当該有機感光体の最表面層の弾性変形率が３５〜５５％であり、
前記最表面層を構成する樹脂が、スチレンブロックと、ソフトセグメントブロックとのブロック共重合体よりなり、
前記ソフトセグメントブロックは、ブタジエン、イソプレン、ペンタジエン、エチレン／ブチレンおよびエチレン／プロピレンから選ばれる１種以上により形成されるものであり、
前記ソフトセグメントブロックの組成比が、前記ブロック共重合体に対して２５〜６５質量％であることを特徴とする。
The organic photoreceptor of the present invention is an organic photoreceptor in which at least an organic photosensitive layer is laminated on a conductive support.
The elastic deformation rate of the outermost surface layer of the organophotoreceptor is 35 to 55%,
The resin constituting the outermost surface layer is a block copolymer of a styrene block and a soft segment block,
The soft segment block is formed of one or more selected from butadiene, isoprene, pentadiene, ethylene / butylene and ethylene / propylene,
The composition ratio of the soft segment block is 25 to 65% by mass with respect to the block copolymer.
本発明の画像形成装置は、上記の有機感光体と、
当該有機感光体の表面に脂肪族金属塩よりなる潤滑剤を塗布する潤滑剤塗布手段とを有することを特徴とする。
この画像形成装置においては、前記潤滑剤を構成する脂肪族金属塩がステアリン酸亜鉛であることが好ましい。
The image forming apparatus of the present invention includes the above organic photoreceptor,
And a lubricant applying means for applying a lubricant composed of an aliphatic metal salt to the surface of the organic photoreceptor.
In this image forming apparatus, the aliphatic metal salt constituting the lubricant is preferably zinc stearate.
本発明の画像形成装置は、上記の有機感光体と、
当該有機感光体の表面に一様な電位を付与する帯電手段とを有し、
前記帯電手段が接触帯電方式のものであることを特徴とする。
The image forming apparatus of the present invention includes the above organic photoreceptor,
Charging means for applying a uniform potential to the surface of the organic photoreceptor,
The charging means is of a contact charging type.
本発明の画像形成装置は、上記の有機感光体と、
当該有機感光体の表面に残留した未転写トナーを除去するクリーニング手段とを有し、
前記クリーニング手段が弾性ブレードよりなることを特徴とする。
The image forming apparatus of the present invention includes the above organic photoreceptor,
Cleaning means for removing untransferred toner remaining on the surface of the organic photoreceptor,
The cleaning means comprises an elastic blade.
本発明の画像形成用カートリッジは、画像形成装置本体と脱着可能な画像形成用カートリッジであって、
上記の有機感光体を具えてなることを特徴とする。
The image forming cartridge of the present invention is an image forming cartridge that is detachable from the image forming apparatus main body,
It comprises the above-mentioned organic photoreceptor.
本発明の有機感光体によれば、当該有機感光体の最表面層の弾性変形率が特定の範囲内であり、この最表面層を構成する樹脂がスチレンブロックとソフトセグメントブロックとのブロック共重合体（以下、「特定のブロック共重合体」ともいう。）よりなり、この特定のブロック共重合体を構成するソフトセグメントブロックの組成比が特定の範囲内にあることにより、最表面層を構成する樹脂が適度な硬さおよび弾性を有するものとなることから、最表面層を構成する樹脂を適宜の手段を用いて紙粉と共に容易に削り取ることができ、その上、優れた耐傷性が得られるので最表面層を構成する樹脂を削り取る際にも表面傷がつきにくく、紙粉ボケや画像ノイズなど画像不良の発生を抑制することができる。 According to the organophotoreceptor of the present invention, the elastic deformation rate of the outermost surface layer of the organophotoreceptor is within a specific range, and the resin constituting the outermost surface layer is a block co-polymer of styrene block and soft segment block. The outermost surface layer is formed by the composition ratio of the soft segment blocks constituting the specific block copolymer being within a specific range (hereinafter, also referred to as “specific block copolymer”). Since the resin to be used has moderate hardness and elasticity, the resin constituting the outermost surface layer can be easily scraped off with paper powder using appropriate means, and excellent scratch resistance is obtained. Therefore, even when the resin constituting the outermost surface layer is scraped off, the surface is hardly damaged, and the occurrence of image defects such as paper dust blur and image noise can be suppressed.
本発明の画像形成装置によれば、上記の有機感光体と、この有機感光体の最表面層を構成する樹脂を削り取る適宜の手段とを有することにより、画像支持体として酸性紙を用いる場合において、当該有機感光体の最表面層を構成する樹脂が適度な硬さおよび弾性を有するものであることから、最表面層を構成する樹脂を紙粉と共に容易に削り取ることができ、その上、優れた耐傷性が得られるので最表面層を構成する樹脂を削り取る際にも表面傷がつきにくく、紙粉ボケや画像ノイズなど画像不良の発生を抑制することができる。 According to the image forming apparatus of the present invention, in the case where acid paper is used as an image support, the organic photoreceptor and the appropriate means for scraping off the resin constituting the outermost surface layer of the organic photoreceptor are used. Since the resin constituting the outermost surface layer of the organophotoreceptor has appropriate hardness and elasticity, the resin constituting the outermost surface layer can be easily scraped off with paper powder, and in addition, excellent Therefore, even when the resin constituting the outermost surface layer is scraped off, the surface is hardly damaged, and the occurrence of image defects such as paper dust blur and image noise can be suppressed.
以下、本発明について詳細に説明する。 Hereinafter, the present invention will be described in detail.
〔有機感光体〕
本発明の有機感光体は、導電性支持体上に、少なくとも有機感光層が積層されてなるものであり、当該有機感光体の最表面層の弾性変形率が特定の範囲内であり、この最表面層を構成する樹脂が特定のブロック共重合体よりなり、この特定のブロック共重合体を構成するソフトセグメントブロックの組成比が特定の範囲内であるものとされる。
[Organic photoconductor]
The organic photoreceptor of the present invention is obtained by laminating at least an organic photosensitive layer on a conductive support, and the elastic deformation rate of the outermost surface layer of the organic photoreceptor is within a specific range. The resin constituting the surface layer is made of a specific block copolymer, and the composition ratio of the soft segment blocks constituting the specific block copolymer is within a specific range.
本発明の有機感光体の層構成は、特に限定されるものではないが、具体的には下記（１）および（２）の層構成が挙げられる。
（１）導電性支持体上に、中間層、有機感光層として電荷発生層および電荷輸送層がこの順に積層されてなり、前記電荷輸送層が最表面層となる層構成。
（２）導電性支持体上に、中間層、有機感光層として電荷発生物質および電荷輸送物質を含む単層がこの順に積層されてなり、前記単層が最表面層となる層構成。
The layer structure of the organophotoreceptor of the present invention is not particularly limited, but specific examples include the following (1) and (2) layer structures.
(1) A layer structure in which a charge generation layer and a charge transport layer are laminated in this order as an intermediate layer and an organic photosensitive layer on a conductive support, and the charge transport layer is the outermost surface layer.
(2) A layer structure in which a single layer containing a charge generation material and a charge transport material is laminated in this order as an intermediate layer and an organic photosensitive layer on a conductive support, and the single layer is the outermost surface layer.
本発明において、有機感光体とは、電子写真感光体の構成に必要不可欠な電荷発生機能および電荷輸送機能の少なくとも一方の機能が有機化合物により発揮されて構成されるものをいい、公知の有機電荷発生物質または有機電荷輸送物質から構成される感光層を有する感光体、電荷発生機能と電荷輸送機能とが高分子錯体により構成される感光層を有する感光体など公知の有機感光体全てを含むものをいう。 In the present invention, the organic photoreceptor means a structure in which at least one of a charge generation function and a charge transport function essential to the configuration of the electrophotographic photoreceptor is exhibited by an organic compound. Includes all known organic photoreceptors such as a photoreceptor having a photosensitive layer composed of a generating material or an organic charge transport material, and a photoreceptor having a photosensitive layer in which a charge generating function and a charge transport function are composed of a polymer complex Say.
〔最表面層〕
本発明の有機感光体は、当該有機感光体の最表面層の弾性変形率が３５〜５５％とされ、より好ましくは４０〜５０％とされる。
最表面層の弾性変形率が上記範囲内であることにより、最表面層に優れた耐傷性が得られ、画像ノイズなどの画像不良の発生を抑制することができる。
最表面層の弾性変形率が過小である場合においては、最表面層に優れた耐傷性が得られず、画像ノイズなどの画像不良の発生を十分に抑制することができないおそれがある。一方、最表面層の弾性変形率が過大である場合においては、最表面層を構成する樹脂を容易に削り取ることができなくなり、紙粉ボケなどの画像不良の発生を十分に抑制することができないおそれがあると共に、有機感光体の表面に残留した未転写トナーを除去するクリーニング手段を有する場合においては、クリーニング手段との滑り性が悪化し、クリーニング不良を誘発し、また、クリーニング手段としてブレードを用いる場合には、ブレードめくれを誘発するおそれがある。
[Outermost surface layer]
In the organic photoreceptor of the present invention, the elastic deformation rate of the outermost surface layer of the organic photoreceptor is 35 to 55%, more preferably 40 to 50%.
When the elastic deformation rate of the outermost surface layer is within the above range, excellent scratch resistance is obtained in the outermost surface layer, and the occurrence of image defects such as image noise can be suppressed.
When the elastic deformation rate of the outermost surface layer is excessively small, the scratch resistance excellent in the outermost surface layer cannot be obtained, and the occurrence of image defects such as image noise may not be sufficiently suppressed. On the other hand, when the elastic deformation rate of the outermost surface layer is excessive, the resin constituting the outermost surface layer cannot be easily scraped off, and image defects such as paper dust blur cannot be sufficiently suppressed. When there is a cleaning means for removing untransferred toner remaining on the surface of the organic photoreceptor, there is a possibility that the slipperiness with the cleaning means is deteriorated, causing poor cleaning, and a blade is used as the cleaning means. When used, there is a risk of inducing blade turning.
最表面層の弾性変形率は、下記式（１）により算出される値である。
式（１）：弾性変形率（％）＝Ｗｅ／Ｗｔｏｔ
上記式（１）中、「Ｗｅ」は弾性エネルギーを示し、「Ｗｔｏｔ」は弾性エネルギーと塑性エネルギーの和を示す。
なお、「Ｗｅ」および「Ｗｔｏｔ」は、下記測定条件に従って微小硬度計「Ｈ１００Ｖ」（Ｆｓｃｈｅｒ社製）により測定されるものである。
−測定条件−
・使用圧子：対面角１３６°のビッカース四角錘ダイアモンド圧子
・負荷条件：速度６ｍＮ／ｓｅｃで有機感光体の表面からビッカース圧子を押しこむ
・負荷時間：５ｓｅｃ（最大負荷 ３０ｍＮ）
・保持時間：５ｓｅｃ
・除荷条件：負荷と同じ速度で負荷を除く
The elastic deformation rate of the outermost surface layer is a value calculated by the following formula (1).
Formula (1): Elastic deformation rate (%) = We / Wtot
In the above formula (1), “We” represents elastic energy, and “Wtot” represents the sum of elastic energy and plastic energy.
“We” and “Wtot” are measured by a microhardness meter “H100V” (manufactured by Fscher) according to the following measurement conditions.
-Measurement conditions-
・ Used indenter: Vickers square pyramid diamond indenter with a face angle of 136 ° ・ Loading condition: Push the Vickers indenter from the surface of the organophotoreceptor at a speed of 6 mN / sec ・ Loading time: 5 sec (maximum load 30 mN)
・ Retention time: 5 sec
-Unloading conditions: Remove the load at the same speed as the load
なお、上記弾性変形率は、特定のブロック共重合体におけるソフトセグメントブロックの組成比を調整することにより制御することができる。具体的には、弾性変形率を上昇させるためには、ソフトセグメントブロックの組成比を高くすればよく、特に、ソフトセグメントブロックが、二重結合が残存するブタジエンやペンタジエンを含むことにより、効果的に弾性変形率を上昇させることができる。一方、弾性変形率を低下させるためには、スチレンブロックの組成比を高くすればよい。 In addition, the said elastic deformation rate can be controlled by adjusting the composition ratio of the soft segment block in a specific block copolymer. Specifically, in order to increase the elastic deformation rate, the composition ratio of the soft segment block may be increased. In particular, the soft segment block is effective by including butadiene or pentadiene in which a double bond remains. The elastic deformation rate can be increased. On the other hand, in order to reduce the elastic deformation rate, the composition ratio of the styrene block may be increased.
最表面層を構成する樹脂は、スチレンブロックと、ソフトセグメントブロックとのブロック共重合体とされる。このブロック共重合体は、上記範囲内の最表面層の弾性変形率を得る観点から、スチレンブロック−ソフトセグメントブロック−スチレンブロック型のトリブロック共重合体であることが好ましい。 The resin constituting the outermost surface layer is a block copolymer of a styrene block and a soft segment block. This block copolymer is preferably a styrene block-soft segment block-styrene block type triblock copolymer from the viewpoint of obtaining the elastic deformation rate of the outermost surface layer within the above range.
特定のブロック共重合体を構成するソフトセグメントブロックは、ブタジエン、イソプレン、ペンタジエン、エチレン／ブチレン共重合ブロックおよびエチレン／プロピレン共重合ブロックから選ばれる１種以上により形成される。ソフトセグメントブロックは、１種単独でまたは２種以上を混合して用いてもよい。これらの中でも、特に、ブタジエン、イソプレン、エチレン／プロピレン共重合ブロックが好ましい。 The soft segment block constituting the specific block copolymer is formed of one or more selected from butadiene, isoprene, pentadiene, ethylene / butylene copolymer block and ethylene / propylene copolymer block. The soft segment block may be used alone or in combination of two or more. Among these, butadiene, isoprene, and ethylene / propylene copolymer block are particularly preferable.
本発明に係るブロック共重合体は、有機溶媒中で有機リチウム化合物を重合開始剤とし、ビニル芳香族炭化水素および共役ジエンの中から、それぞれ１種または２種以上を選びリビングアニオン重合させることにより製造できる。
リビングアニオン重合では、重合活性末端が存在する限り原料モノマーの重合が継続するため、当該モノマーの残留を低く抑えることができる。また、連鎖移動反応による重合途中での反応活性末端の失活や新規生成しにくいという重合反応上の特徴を持つ。そのため、本発明におけるブロック共重合体の分子量や分子構造は、モノマー、重合開始剤、ランダム化剤、活性末端の失活のために用いるプロトン供与性の物質の仕込量、およびその添加時期、添加回数を適宜調整することにより目的に応じて制御することが可能である。
また、本発明に係るソフトセグメントブロックにおいては、ブタジエン系のモノマーの共重合体、及びこれらに水素添加したものが用いられ、本発明に係るエチレンブロックにおいては、共役ジエンに水素添加した構造も含まれる。スチレン−共役ジエンブロック共重合体の水素添加物としては、例えば、スチレン・ブタジエンブロック共重合体の水素添加物（スチレン・エチレン／ブチレン・スチレン共重合体）、スチレン・イソプレンブロック共重合体の水素添加物（スチレン・エチレン／プロピレン・スチレン共重合体）、または、これらの混合物を好適に使用することができる。これらのブロック共重合体の水素添加処理は、例えば特公昭４２−８７０４号公報、特公昭４３−６６３６号公報、あるいは特開昭５９−１３３２０３号公報および特開昭６０−７９００５号公報に記載された方法により、不活性溶媒中で水素添加触媒の存在下で行うことができる。このようなブロック共重合体の市販品としては、「ＫＲＡＴＯＮ−Ｇ」（クレイトンポリマー株式会社製）、「セプトン」（株式会社クラレ製）、「タフテック」（旭化成株式会社製）などの商品が例示できる。
The block copolymer according to the present invention is a living anion polymerization in which an organic lithium compound is used as a polymerization initiator in an organic solvent, and one or more of vinyl aromatic hydrocarbons and conjugated dienes are selected. Can be manufactured.
In the living anion polymerization, the polymerization of the raw material monomer continues as long as the polymerization active terminal exists, so that the residual monomer can be kept low. Moreover, it has the characteristic on the polymerization reaction that it is hard to deactivate the reaction active terminal in the middle of the polymerization by chain transfer reaction, and it is hard to produce it newly. Therefore, the molecular weight and molecular structure of the block copolymer in the present invention are the monomer, the polymerization initiator, the randomizing agent, the charged amount of the proton donating substance used for deactivation of the active terminal, and the addition timing and addition thereof. It is possible to control according to the purpose by appropriately adjusting the number of times.
In the soft segment block according to the present invention, a copolymer of butadiene monomers and hydrogenated ones thereof are used, and the ethylene block according to the present invention includes a structure in which conjugated dienes are hydrogenated. It is. Examples of hydrogenated styrene-conjugated diene block copolymers include hydrogenated styrene / butadiene block copolymers (styrene / ethylene / butylene / styrene copolymers) and hydrogenated styrene / isoprene block copolymers. An additive (styrene / ethylene / propylene / styrene copolymer) or a mixture thereof can be suitably used. The hydrogenation treatment of these block copolymers is described in, for example, JP-B-42-8704, JP-B-43-6636, JP-A-59-133203, and JP-A-60-79005. Can be carried out in an inert solvent in the presence of a hydrogenation catalyst. Examples of such commercially available block copolymers include “KRATON-G” (manufactured by Kraton Polymer Co., Ltd.), “Septon” (manufactured by Kuraray Co., Ltd.), “Tough Tech” (manufactured by Asahi Kasei Co., Ltd.), and the like. it can.
ソフトセグメントブロックの組成比は、特定のブロック共重合体における２５〜６５質量％とされ、より好ましくは３０〜５５質量％とされる。
ソフトセグメントブロックの組成比が上記範囲内であることにより、最表面層を構成する樹脂を容易に削り取ることができ、紙粉ボケなどの画像不良の発生を抑制することができる。
ソフトセグメントブロックの組成比が過小である場合においては、最表面層に優れた耐傷性が得られず、画像ノイズなどの画像不良の発生を十分に抑制することができないおそれがある。一方、ソフトセグメントブロックの組成比が過大である場合においては、最表面層を構成する樹脂を容易に削り取ることができなくなり、紙粉ボケなどの画像不良の発生を十分に抑制することができないおそれがある。
なお、ソフトセグメントブロックの組成比は、1 Ｈ−ＮＭＲと熱分解ガスクロマトグラフィーにより算出することができる。
The composition ratio of the soft segment block is 25 to 65% by mass in the specific block copolymer, and more preferably 30 to 55% by mass.
When the composition ratio of the soft segment block is within the above range, the resin constituting the outermost surface layer can be easily scraped off, and the occurrence of image defects such as paper dust blur can be suppressed.
When the composition ratio of the soft segment block is too small, the outermost surface layer may not have excellent scratch resistance, and the occurrence of image defects such as image noise may not be sufficiently suppressed. On the other hand, when the composition ratio of the soft segment block is excessive, the resin constituting the outermost surface layer cannot be easily scraped off, and the occurrence of image defects such as paper dust blur may not be sufficiently suppressed. There is.
The composition ratio of the soft segment block can be calculated by 1 H-NMR and pyrolysis gas chromatography.
以上のような最表面層は、特定のブロック共重合体を公知の溶媒で溶解した溶液中に例えば電荷輸送物質を溶解させ、必要に応じて酸化防止剤やフィラー等を添加して塗布液を調製し、この塗布液を塗布することにより得られる。 The outermost surface layer as described above is prepared by, for example, dissolving a charge transport material in a solution obtained by dissolving a specific block copolymer in a known solvent, and adding an antioxidant or a filler as necessary to form a coating solution. It is obtained by preparing and applying this coating solution.
本発明の有機感光体の最表面層が以上のような構成であることにより、最表面層を構成する樹脂が適度な硬さおよび弾性を有するものとなることから、最表面層を構成する樹脂を適宜の手段を用いて紙粉と共に容易に削り取ることができ、その上、優れた耐傷性が得られるので最表面層を構成する樹脂を削り取る際にも表面傷がつきにくく、紙粉ボケや画像ノイズなどの画像不良の発生を抑制することができる。 Since the outermost surface layer of the organophotoreceptor of the present invention has the above-described configuration, the resin constituting the outermost surface layer has appropriate hardness and elasticity. Can be easily scraped off with paper dust using appropriate means, and in addition, excellent scratch resistance can be obtained, so even when scraping off the resin constituting the outermost layer, the surface scratches are less likely to occur. Occurrence of image defects such as image noise can be suppressed.
以下、本発明の有機感光体が上記（１）の層構成である場合について具体的に説明する。 Hereinafter, the case where the organophotoreceptor of the present invention has the layer configuration (1) will be specifically described.
〔導電性支持体〕
本発明の有機感光体を構成する導電性支持体としては、導電性を有するものであれば特に限定されるものではないが、例えば、アルミニウム、銅、クロム、ニッケル、亜鉛、ステンレスなどの金属をドラム状またはシート状に成形したもの、アルミニウムや銅などの金属箔をプラスチックフィルムにラミネートしたもの、アルミニウム、酸化インジウムおよび酸化スズなどをプラスチックフィルムに蒸着したもの、導電性物質を単独またはバインダー樹脂と共に塗布して導電層を設けた金属、プラスチックフィルムおよび紙などが挙げられる。
[Conductive support]
The conductive support constituting the organic photoreceptor of the present invention is not particularly limited as long as it has conductivity. For example, a metal such as aluminum, copper, chromium, nickel, zinc, and stainless steel is used. Molded in drum or sheet form, laminated metal foil such as aluminum or copper on plastic film, deposited aluminum, indium oxide and tin oxide on plastic film, conductive material alone or with binder resin Examples include metals, plastic films, and papers that are coated to provide a conductive layer.
〔中間層〕
本発明の有機感光体においては、導電性支持体と有機感光層との間にバリアー機能と接着機能とを有する中間層を設ける構成とすることができる。種々の故障防止などの観点から、このような中間層を設けることが好ましい。
この中間層は、バインダー樹脂（以下、「中間層用バインダー樹脂」ともいう。）、および、当該中間層の抵抗を調整する目的で含有される各種の導電性微粒子や金属酸化物微粒子（以下、「中間層用金属酸化物微粒子」ともいう。）などの無機微粒子よりなるものである。
[Middle layer]
In the organic photoreceptor of the present invention, an intermediate layer having a barrier function and an adhesive function can be provided between the conductive support and the organic photosensitive layer. From the viewpoint of preventing various failures, it is preferable to provide such an intermediate layer.
This intermediate layer includes a binder resin (hereinafter also referred to as “binder resin for intermediate layer”), and various conductive fine particles and metal oxide fine particles (hereinafter referred to as “intermediate layer binder resin”) for the purpose of adjusting the resistance of the intermediate layer. It is also composed of inorganic fine particles such as “intermediate layer metal oxide fine particles”.
中間層用バインダー樹脂としては、例えば、カゼイン、ポリビニルアルコール、ニトロセルロース、エチレン−アクリル酸コポリマー、ポリアミド樹脂、ポリウレタン樹脂、ゼラチンなどが挙げられるが、アルコール可溶性のポリアミド樹脂であることが好ましい。 Examples of the intermediate layer binder resin include casein, polyvinyl alcohol, nitrocellulose, ethylene-acrylic acid copolymer, polyamide resin, polyurethane resin, gelatin and the like, and alcohol-soluble polyamide resins are preferable.
中間層用金属酸化物微粒子としては、例えば、アルミナ、酸化亜鉛、酸化チタン、酸化スズ、酸化アンチモン、酸化インジウム、酸化ビスマスなどの金属酸化物微粒子が挙げられ、スズをドープした酸化インジウム、アンチモンをドープした酸化スズおよび酸化ジルコニウムなどの超微粒子を用いることもできる。これらの中間層用金属酸化物微粒子は、単独または２種以上を組み合わせて用いることができる。中間層用金属酸化物微粒子を２種類以上組み合わせて用いる場合においては、当該中間層用金属酸化物微粒子が固溶体状態であってもよいし、また、融着状態であってもよい。
このような中間層用金属酸化物微粒子の数平均一次粒径は、０．３μｍ以下であることが好ましく、より好ましくは０．１μｍ以下である。
本発明において、中間層用金属酸化物微粒子の数平均一次粒径は、以下のように測定されるものである。
すなわち、走査型電子顕微鏡「ＪＳＭ−７５００Ｆ」（日本電子社製）により１００００倍の拡大写真を撮影し、ランダムに３００個の中間層用金属酸化物微粒子をスキャナーにより取り込んだ写真画像（凝集粒子を除く）を自動画像処理解析装置「ＬＵＺＥＸ ＡＰ」（ソフトウエアバージョン Ｖｅｒ．１．３２、ニレコ社製）を使用して算出する。
Examples of the metal oxide fine particles for the intermediate layer include metal oxide fine particles such as alumina, zinc oxide, titanium oxide, tin oxide, antimony oxide, indium oxide, bismuth oxide, and tin-doped indium oxide and antimony. Ultrafine particles such as doped tin oxide and zirconium oxide can also be used. These metal oxide fine particles for intermediate layer can be used alone or in combination of two or more. When two or more kinds of intermediate layer metal oxide fine particles are used in combination, the intermediate layer metal oxide fine particles may be in a solid solution state or in a fused state.
The number average primary particle size of such metal oxide fine particles for intermediate layer is preferably 0.3 μm or less, more preferably 0.1 μm or less.
In the present invention, the number average primary particle size of the intermediate layer metal oxide fine particles is measured as follows.
That is, a 10000 times magnified photograph was taken with a scanning electron microscope “JSM-7500F” (manufactured by JEOL Ltd.), and 300 photographic images of metal oxide particles for intermediate layer were randomly taken by a scanner (aggregated particles were Is excluded) using an automatic image processing analyzer “LUZEX AP” (software version Ver. 1.32, manufactured by Nireco).
中間層の形成方法は、中間層用バインダー樹脂を公知の溶媒に溶解して中間層塗布液を調製し、この中間層塗布液を導電性支持体上に浸漬、塗布する方法が好ましい。 The method for forming the intermediate layer is preferably a method in which an intermediate layer coating solution is prepared by dissolving the binder resin for the intermediate layer in a known solvent, and this intermediate layer coating solution is immersed and coated on a conductive support.
中間層を形成するために用いられる溶媒としては、無機微粒子を良好に分散し、ポリアミド樹脂を溶解するものが好ましく、具体的には、エタノール、ｎ−プロピルアルコール、イソプロピルアルコール、ｎ−ブタノール、ｔ−ブタノール、ｓｅｃ−ブタノールなどの炭素数２〜４のアルコール類が、ポリアミド樹脂の溶解性と塗布性の観点から、特に好ましい。また、保存性、無機微粒子の分散性を向上するために、前記溶媒と併用することのできる助溶媒としては、例えば、メタノール、ベンジルアルコール、トルエン、メチレンクロライド、シクロヘキサノン、テトラヒドロフランなどが挙げられる。 As the solvent used for forming the intermediate layer, those in which inorganic fine particles are well dispersed and the polyamide resin is dissolved are preferable. Specifically, ethanol, n-propyl alcohol, isopropyl alcohol, n-butanol, t -Alcohols having 2 to 4 carbon atoms such as butanol and sec-butanol are particularly preferred from the viewpoints of solubility and applicability of the polyamide resin. Examples of the co-solvent that can be used in combination with the above-described solvent in order to improve the storage stability and the dispersibility of the inorganic fine particles include methanol, benzyl alcohol, toluene, methylene chloride, cyclohexanone, and tetrahydrofuran.
中間層用バインダー樹脂の濃度は、中間層の層厚や生産速度に合わせて適宜選択される。 The density | concentration of binder resin for intermediate | middle layers is suitably selected according to the layer thickness and production rate of an intermediate | middle layer.
無機微粒子の分散手段としては、特に限定されないが、例えば、超音波分散機、ボールミル、サンドグラインダーおよびホモミキサーなどの分散機が挙げられる。 The means for dispersing the inorganic fine particles is not particularly limited, and examples thereof include a disperser such as an ultrasonic disperser, a ball mill, a sand grinder, and a homomixer.
中間層用バインダー樹脂に対する無機微粒子の添加量は、中間層用バインダー樹脂１００質量部に対して２０〜４００質量部であることが好ましく、より好ましくは５０〜２００質量部である。 The amount of the inorganic fine particles added to the intermediate layer binder resin is preferably 20 to 400 parts by mass, more preferably 50 to 200 parts by mass with respect to 100 parts by mass of the intermediate layer binder resin.
中間層の乾燥方法は、溶媒の種類、層厚に応じて適宜選択することができるが、熱乾燥による方法が好ましい。 The method for drying the intermediate layer can be appropriately selected according to the type of solvent and the layer thickness, but a method by thermal drying is preferred.
中間層の層厚は、０．１〜１５μｍであることが好ましく、より好ましくは０．３〜１０μｍである。 The thickness of the intermediate layer is preferably 0.1 to 15 μm, more preferably 0.3 to 10 μm.
〔有機感光層〕
（電荷発生層）
本発明の有機感光体を構成する有機感光層における電荷発生層は、電荷発生物質およびバインダー樹脂（以下、「電荷発生層用バインダー樹脂」ともいう。）よりなるものであり、この電荷発生層は、電荷発生物質を電荷発生層用バインダー樹脂溶液中に分散、塗布することにより形成することができる。
[Organic photosensitive layer]
(Charge generation layer)
The charge generation layer in the organic photosensitive layer constituting the organic photoreceptor of the present invention is composed of a charge generation material and a binder resin (hereinafter also referred to as “binder resin for charge generation layer”). The charge generation material can be formed by dispersing and coating in a binder resin solution for a charge generation layer.
電荷発生物質としては、特に限定されるものではないが、例えば、スーダンレッド、ダイアンブルーなどのアゾ原料；ピレンキノン、アントアントロンなどのキノン顔料；キノシアニン顔料；ペリレン顔料；インジゴ、チオインジゴなどのインジゴ顔料；フタロシアニン顔料などが挙げられる。これらの電荷発生物質は、単独または２種以上を組み合わせて用いることができる。 Although it does not specifically limit as a charge generation substance, For example, azo raw materials, such as Sudan red and diane blue; Quinone pigments, such as pyrenequinone and anthanthrone; Quinocyanine pigment; Perylene pigment; Indigo pigments, such as indigo and thioindigo; And phthalocyanine pigments. These charge generation materials can be used alone or in combination of two or more.
電荷発生層用バインダー樹脂としては、公知の樹脂を用いることができ、例えば、ポリスチレン樹脂、ポリエチレン樹脂、ポリプロピレン樹脂、アクリル樹脂、メタクリル樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、ポリビニルブチラール樹脂、エポキシ樹脂、ポリウレタン樹脂、フェノール樹脂、ポリエステル樹脂、アルキッド樹脂、ポリカーボネート樹脂、シリコーン樹脂、メラミン樹脂、並びにこれらの樹脂の内２つ以上を含む共重合体樹脂（例えば、塩化ビニル−酢酸ビニル共重合体樹脂、塩化ビニル−酢酸ビニル−無水マレイン酸共重合体樹脂）、ポリ−ビニルカルバゾール樹脂などが挙げられるが、これらに限定されるものではない。 As the binder resin for the charge generation layer, known resins can be used. For example, polystyrene resin, polyethylene resin, polypropylene resin, acrylic resin, methacrylic resin, vinyl chloride resin, vinyl acetate resin, polyvinyl butyral resin, epoxy resin, Polyurethane resins, phenol resins, polyester resins, alkyd resins, polycarbonate resins, silicone resins, melamine resins, and copolymer resins containing two or more of these resins (eg, vinyl chloride-vinyl acetate copolymer resins, chlorides) Vinyl-vinyl acetate-maleic anhydride copolymer resin), poly-vinylcarbazole resin, and the like, but are not limited thereto.
電荷発生層の形成方法は、電荷発生層用バインダー樹脂を溶媒で溶解した溶液中に分散機を用いて電荷発生物質を分散して電荷発生層塗布液を調製し、この電荷発生層塗布液を塗布機で一定の層厚に導電性支持体上または中間層上塗布して塗膜を形成し、この塗膜を乾燥する方法が好ましい。 The charge generation layer is formed by preparing a charge generation layer coating solution by dispersing a charge generation material using a disperser in a solution obtained by dissolving a binder resin for a charge generation layer with a solvent. A method is preferred in which a coating film is formed by coating on a conductive support or an intermediate layer to a constant layer thickness with a coating machine, and then the coating film is dried.
電荷発生層を形成するために用いられる溶媒としては、例えば、トルエン、キシレン、メチレンクロライド、１，２−ジクロロエタン、メチルエチルケトン、シクロヘキサン、酢酸エチル、酢酸ブチル、メタノール、エタノール、プロパノール、ブタノール、メチルセロソルブ、エチルセロソルブ、テトラヒドロフラン、１−ジオキサン、１，３−ジオキソラン、ピリジン、ジエチルアミンなどが挙げられるが、これらに限定されるものではない。 Examples of the solvent used for forming the charge generation layer include toluene, xylene, methylene chloride, 1,2-dichloroethane, methyl ethyl ketone, cyclohexane, ethyl acetate, butyl acetate, methanol, ethanol, propanol, butanol, methyl cellosolve, Examples include, but are not limited to, ethyl cellosolve, tetrahydrofuran, 1-dioxane, 1,3-dioxolane, pyridine, diethylamine and the like.
電荷発生物質の分散手段としては、特に限定されないが、例えば、超音波分散機、ボールミル、サンドグラインダーおよびホモミキサーなどの分散機が挙げられる。 The means for dispersing the charge generating material is not particularly limited, and examples thereof include a dispersing machine such as an ultrasonic dispersing machine, a ball mill, a sand grinder, and a homomixer.
電荷発生層用バインダー樹脂に対する電荷発生物質の添加量は、電荷発生層用バインダー樹脂１００質量部に対して１〜６００質量部であることが好ましく、より好ましくは５０〜５００質量部である。 The amount of the charge generation material added to the charge generation layer binder resin is preferably 1 to 600 parts by mass, and more preferably 50 to 500 parts by mass with respect to 100 parts by mass of the charge generation layer binder resin.
電荷発生層の層厚は、電荷発生物質の特性、電荷発生層用バインダー樹脂の特性および混合割合などにより異なるが、０．０１〜５μｍであることが好ましく、より好ましくは０．０５〜３μｍである。なお、電荷発生層塗布液は塗布前に異物や凝集物を濾過することで画像欠陥の発生を防ぐことができる。前記顔料を真空蒸着することによって形成すこともできる。 The layer thickness of the charge generation layer varies depending on the characteristics of the charge generation material, the characteristics of the binder resin for the charge generation layer and the mixing ratio, but is preferably 0.01 to 5 μm, more preferably 0.05 to 3 μm. is there. It should be noted that the charge generation layer coating liquid can prevent the occurrence of image defects by filtering foreign matter and aggregates before coating. The pigment can also be formed by vacuum deposition.
（電荷輸送層）
本発明の有機感光体を構成する有機感光層における電荷輸送層は、電荷輸送物質（ＣＴＭ）およびバインダー樹脂（以下、「電荷輸送層用バインダー樹脂」ともいう。）よりなるものであり、この電荷輸送層は、電荷輸送物質を電荷輸送層用バインダー樹脂溶液中に溶解、塗布することにより形成することができる。
(Charge transport layer)
The charge transport layer in the organic photosensitive layer constituting the organic photoreceptor of the present invention comprises a charge transport material (CTM) and a binder resin (hereinafter also referred to as “binder resin for charge transport layer”). The transport layer can be formed by dissolving and coating a charge transport material in a binder resin solution for a charge transport layer.
電荷輸送物質としては、例えば、カルバゾール誘導体、オキサゾール誘導体、オキサジアゾール誘導体、チアゾール誘導体、チアジアゾール誘導体、トリアゾール誘導体、イミダゾール誘導体、イミダゾロン誘導体、イミダゾリジン誘導体、ビスイミダゾリジン誘導体、スチリル化合物、ヒドラゾン化合物、ピラゾリン化合物、オキサゾロン誘導体、ベンズイミダゾール誘導体、キナゾリン誘導体、ベンゾフラン誘導体、アクリジン誘導体、フェナジン誘導体、アミノスチルベン誘導体、トリアリールアミン誘導体、フェニレンジアミン誘導体、スチルベン誘導体、ベンジジン誘導体、ポリ−Ｎ−ビニルカルバゾール、ポリ−１−ビニルピレンおよびポリ−９−ビニルアントラセン、トリフェニルアミン誘導体などが挙げられる。これらの電荷輸送物質は、単独または２種以上を組み合わせて用いることができる。 Examples of the charge transport material include carbazole derivatives, oxazole derivatives, oxadiazole derivatives, thiazole derivatives, thiadiazole derivatives, triazole derivatives, imidazole derivatives, imidazolone derivatives, imidazolidine derivatives, bisimidazolidine derivatives, styryl compounds, hydrazone compounds, pyrazolines. Compound, oxazolone derivative, benzimidazole derivative, quinazoline derivative, benzofuran derivative, acridine derivative, phenazine derivative, aminostilbene derivative, triarylamine derivative, phenylenediamine derivative, stilbene derivative, benzidine derivative, poly-N-vinylcarbazole, poly-1 -Vinylpyrene, poly-9-vinylanthracene, triphenylamine derivatives and the like. These charge transport materials can be used alone or in combination of two or more.
このような層構成の場合、当該電荷輸送層が有機感光体の最表面層となるので、電荷輸送層用バインダー樹脂は、特定のブロック共重合体により構成され、この特定のブロック共重合体においてソフトセグメントブロックの組成比は当該特定のブロック共重合体に対して２５〜６５質量％とされる。 In the case of such a layer structure, the charge transport layer is the outermost surface layer of the organophotoreceptor, so that the binder resin for charge transport layer is composed of a specific block copolymer, and in this specific block copolymer, The composition ratio of the soft segment block is 25 to 65% by mass with respect to the specific block copolymer.
電荷輸送層の形成方法は、電荷輸送層用バインダー樹脂と電荷輸送物質を溶解して電荷輸送層塗布液を調製し、この電荷輸送層塗布液を塗布機で一定の層厚に電荷発生層上に塗布して塗膜を形成し、この塗膜を乾燥する方法が好ましい。 The charge transport layer is formed by dissolving a charge transport layer binder resin and a charge transport material to prepare a charge transport layer coating solution, and this charge transport layer coating solution is applied on the charge generation layer to a constant layer thickness by a coating machine. A method is preferred in which a coating film is formed by coating on the substrate and the coating film is dried.
電荷輸送層を形成するために用いられる溶媒としては、例えば、トルエン、キシレン、メチレンクロライド、１，２−ジクロロエタン、メチルエチルケトン、シクロヘキサノン、酢酸エチル、酢酸ブチル、メタノール、エタノール、プロパノール、ブタノール、テトラヒドロフラン、１，４−ジオキサン、１，３−ジオキソラン、ピリジン、ジエチルアミンなどが挙げられるが、これらに限定されるものではない。 Examples of the solvent used for forming the charge transport layer include toluene, xylene, methylene chloride, 1,2-dichloroethane, methyl ethyl ketone, cyclohexanone, ethyl acetate, butyl acetate, methanol, ethanol, propanol, butanol, tetrahydrofuran, 1 , 4-dioxane, 1,3-dioxolane, pyridine, diethylamine and the like, but are not limited thereto.
電荷輸送層用バインダー樹脂に対する電荷輸送物質の添加量は、電荷輸送層用バインダー樹脂１００質量部に対して１０〜５００質量部であることが好ましく、より好ましくは２０〜１００質量部である。 The amount of the charge transport material added to the charge transport layer binder resin is preferably 10 to 500 parts by weight, more preferably 20 to 100 parts by weight, based on 100 parts by weight of the charge transport layer binder resin.
電荷輸送層の層厚は、電荷輸送物質の特性、電荷輸送層用バインダー樹脂の特性および混合割合などにより異なるが、５〜４０μｍであることが好ましく、より好ましくは１０〜３０μｍである。 The layer thickness of the charge transport layer varies depending on the characteristics of the charge transport material, the characteristics of the binder resin for charge transport layer and the mixing ratio, but is preferably 5 to 40 μm, more preferably 10 to 30 μm.
電荷輸送層には、必要に応じて酸化防止剤、電子導電剤、安定剤などが含有されていてもよい。酸化防止剤については特願平１１−２００１３５号に記載のものが挙げられ、電子導電剤については特開昭５０−１３７５４３号、同５８−７６４８３号などに記載のものが挙げられる。 The charge transport layer may contain an antioxidant, an electronic conductive agent, a stabilizer and the like as necessary. Examples of the antioxidant include those described in Japanese Patent Application No. 11-200135, and examples of the electronic conductive agent include those described in JP-A Nos. 50-137543 and 58-76483.
本発明の有機感光体によれば、当該有機感光体の最表面層の弾性変形率が特定の範囲内であり、この最表面層を構成する樹脂が特定のブロック共重合体よりなり、この特定のブロック共重合体を構成するソフトセグメントブロックの組成比が特定の範囲内にあることにより、最表面層を構成する樹脂が適度な硬さおよび弾性を有するものとなることから、最表面層を構成する樹脂を適宜の手段を用いて紙粉と共に容易に削り取ることができ、その上、優れた耐傷性が得られるので最表面層を構成する樹脂を削り取る際にも表面傷がつきにくく、紙粉ボケや画像ノイズなど画像不良の発生を抑制することができる。 According to the organophotoreceptor of the present invention, the elastic deformation rate of the outermost surface layer of the organophotoreceptor is within a specific range, and the resin constituting the outermost surface layer is made of a specific block copolymer. When the composition ratio of the soft segment block constituting the block copolymer is within a specific range, the resin constituting the outermost surface layer has appropriate hardness and elasticity. The constituent resin can be easily scraped off with paper powder using an appropriate means, and in addition, excellent scratch resistance is obtained, so that even when scraping off the resin constituting the outermost surface layer, the surface scratches are less likely to occur. Occurrence of image defects such as powder blur and image noise can be suppressed.
〔画像形成装置〕
本発明の画像形成装置は、本発明の有機感光体と、当該有機感光体の表面に接触する部材であって有機感光体の最表面層を構成する樹脂を削り取る手段とを有するものであれば、特に限定されず、この最表面層を構成する樹脂を削り取る手段としては、例えば、有機感光体の表面に潤滑剤を塗布する潤滑剤塗布手段に樹脂を削り取る機能を担わせる方法、接触帯電方式による帯電手段を用いる方法、有機感光体上の未転写トナーを除去するクリーニング手段に樹脂を削り取る機能を担わせる方法などが挙げられ、これらは単独でまたは２種以上組み合わせ採用することができる。
[Image forming apparatus]
As long as the image forming apparatus of the present invention has the organophotoreceptor of the present invention and a member that contacts the surface of the organophotoreceptor and scrapes off the resin that forms the outermost surface layer of the organophotoreceptor, The means for scraping off the resin constituting the outermost surface layer is not particularly limited, for example, a method of applying a function of scraping the resin to a lubricant applying means for applying a lubricant to the surface of the organic photoreceptor, contact charging method And a method of using a charging unit for removing untransferred toner on the organic photoreceptor, and a method of causing the resin to scrape off the resin. These can be used alone or in combination of two or more.
以下、本発明の画像形成装置について具体的に説明する。図１は、本発明の画像形成装置の構成の一例を示す説明用断面図である。
この画像形成装置は、図１において矢印方向に回転されるドラム状の有機感光体１０と、各々、この有機感光体１０の外周面に沿って、有機感光体１０の回転方向に従って並ぶよう配設された、有機感光体１０の表面を一様に帯電させる帯電手段１１、有機感光体１０の表面を露光することにより静電潜像を形成する露光手段１２、トナーを含む現像剤を用いて静電潜像を顕在化させることによりトナー像を形成する現像手段１３、有機感光体１０上に形成されたトナー像を転写領域において画像支持体Ｐに転写する転写手段１４、有機感光体１０に密着した状態にある画像支持体Ｐを分離させる分離手段１５、潤滑剤を有機感光体１０の表面に塗布する潤滑剤塗布手段３０および有機感光体１０上に残存している未転写のトナーを除去するクリーニング手段２０とを備えている。１６は、転写領域より搬送される画像支持体Ｐ上の未定着トナー像を定着させて画像を形成する定着手段である。
The image forming apparatus of the present invention will be specifically described below. FIG. 1 is an explanatory sectional view showing an example of the configuration of the image forming apparatus of the present invention.
The image forming apparatus is arranged so that the drum-shaped organic photoreceptors 10 rotated in the direction of the arrow in FIG. 1 are arranged along the outer peripheral surface of the organic photoreceptor 10 according to the rotation direction of the organic photoreceptors 10. The charging means 11 for uniformly charging the surface of the organic photoreceptor 10, the exposure means 12 for forming an electrostatic latent image by exposing the surface of the organic photoreceptor 10, and a developer containing toner The developing means 13 for forming the toner image by making the latent image visible, the transfer means 14 for transferring the toner image formed on the organic photoreceptor 10 to the image support P in the transfer region, and the organic photoreceptor 10 Separating means 15 for separating the image support P in the state, lubricant applying means 30 for applying a lubricant to the surface of the organic photoconductor 10, and untransferred toner remaining on the organic photoconductor 10 are removed. And a cleaning means 20. A fixing unit 16 fixes the unfixed toner image on the image support P conveyed from the transfer region to form an image.
有機感光体１０は、図１における紙面に対して垂直な方向に伸びる状態で配設されている。 The organic photoreceptor 10 is arranged in a state extending in a direction perpendicular to the paper surface in FIG.
帯電手段１１は、帯電部材である導電性ローラや磁気ブラシに電圧を印加して、被帯電体である有機感光体１０に接触させ、有機感光体１０の表面を所定の電位に帯電させる接触帯電方式のものである。なお、例えば制御グリッドと帯電極とを有するスコロトロン帯電器よりなる非接触帯電方式のものを用いることもできる。 The charging means 11 applies a voltage to a conductive roller or a magnetic brush as a charging member to bring it into contact with the organic photoconductor 10 as a member to be charged, and charges the surface of the organic photoconductor 10 to a predetermined potential. It is of the method. For example, a non-contact charging type composed of a scorotron charger having a control grid and a band electrode can be used.
露光手段１２は、例えばレーザ照射装置よりなるものである。 The exposure means 12 is composed of, for example, a laser irradiation device.
現像手段１３は、例えばマグネットを内蔵し現像剤を保持して回転する現像スリーブ１３１および有機感光体１０とこの現像スリーブ１３１との間に直流および／または交流バイアス電圧を印加する電圧印加装置（図示せず）が設けられてなるものである。 The developing means 13 includes, for example, a developing sleeve 131 that contains a magnet and rotates while holding the developer, and a voltage applying device that applies a DC and / or AC bias voltage between the organic photosensitive member 10 and the developing sleeve 131 (see FIG. (Not shown) is provided.
転写手段１４は、例えばコロナ転写方式のものよりなり、接触転写方式のものを用いることもできる。 The transfer means 14 is made of, for example, a corona transfer type, and a contact transfer type can also be used.
分離手段１５は、有機感光体１０に密着した状態にある画像支持体Ｐの電荷を除去することによりこの画像支持体Ｐを有機感光体１０から分離させるものであり、例えばコロトロン帯電器よりなるものが用いられる。 The separating means 15 separates the image support P from the organic photoreceptor 10 by removing the charge of the image support P in close contact with the organic photoreceptor 10, and is composed of, for example, a corotron charger. Is used.
定着手段１６は、例えば、内部に加熱源を備えた加熱ローラ１６１と、この加熱ローラ１６１に定着ニップ部が形成されるよう圧接された状態で設けられた加圧ローラ１６２とにより構成されてなる熱ローラ定着方式のものである。 The fixing unit 16 includes, for example, a heating roller 161 provided with a heating source therein, and a pressure roller 162 provided in pressure contact with the heating roller 161 so as to form a fixing nip portion. The heat roller fixing method.
クリーニング手段２０は、例えば、先端部分が有機感光体１０の表面に当接した状態で、有機感光体１０の軸方向に伸びるよう設けられたウレタンゴムなどの弾性体よりなる板状の弾性ブレード２０１を備えてなる方式のものが用いられており、弾性ブレード２０１の先端部分が、有機感光体１０との当接部分における当該有機感光体１０の回転による移動方向と反対方向に向く状態（カウンター状態）とされることが好ましい。この弾性ブレード２０１は、例えば硬度が６５〜８０°（アスカーＣ硬度）、反発弾性が５０％以上、有機感光体１０に対する当接荷重が０．９８〜２９４ｍＮ／ｃｍ、当接角度が０〜４０°であるものが用いられることが好ましい。 The cleaning means 20 is, for example, a plate-like elastic blade 201 made of an elastic body such as urethane rubber provided so as to extend in the axial direction of the organic photoconductor 10 with the tip portion being in contact with the surface of the organic photoconductor 10. In which the tip portion of the elastic blade 201 faces in the direction opposite to the moving direction due to the rotation of the organic photoconductor 10 at the contact portion with the organic photoconductor 10 (counter state). ). The elastic blade 201 has, for example, a hardness of 65 to 80 ° (Asker C hardness), a rebound resilience of 50% or more, a contact load with respect to the organic photoreceptor 10 of 0.98 to 294 mN / cm, and a contact angle of 0 to 40. It is preferable to use one that is at °.
潤滑剤塗布手段３０は、図２に示すように、図２における紙面に対して垂直な方向に細長く伸びた直方体形状を有する固形状の潤滑剤により構成された潤滑剤ストック３０２と、削取領域３０ａにおいて潤滑剤ストック３０２の表面と当接し、塗布領域３０ｂにおいて有機感光体１０の表面と当接し、潤滑剤ストック３０２の表面を摺擦することにより掻き取った潤滑剤を有機感光体１０に塗布するよう回転駆動されるブラシローラ３０１と、潤滑剤ストック３０２をブラシローラ３０１に対して押圧するよう支持するスプリングからなる押圧装置３０３とから構成される。 As shown in FIG. 2, the lubricant application means 30 includes a lubricant stock 302 composed of a solid lubricant having a rectangular parallelepiped shape elongated in a direction perpendicular to the paper surface in FIG. The lubricant contacted with the surface of the lubricant stock 302 at 30a and the surface of the organic photoreceptor 10 in the application region 30b, and the lubricant scraped off by rubbing the surface of the lubricant stock 302 is applied to the organic photoreceptor 10. The brush roller 301 is driven to rotate, and a pressing device 303 including a spring that supports the lubricant stock 302 so as to press the lubricant stock 302 against the brush roller 301.
ブラシローラ３０１は、例えば、ポリプロピレン樹脂やアクリル樹脂などの樹脂製のブラシ繊維が高密度に植設されてなる長尺の織布がローラ基体の周面に巻きつけられてロール状に形成されてなるものにより構成されたものであり、各々のブラシ繊維の太さが３〜７デニール、ブラシ繊維の毛長が２〜５ｍｍ、ブラシ繊維の電気抵抗率が１０10Ω・ｃｍ以下、ブラシ繊維のヤング率が４９００〜９８００Ｎ／ｍｍ2 、ブラシ繊維の植設密度が５０〜２００ｋ本／ｉｎｃｈ2 のものであることが好ましく、有機感光体１０に対する食い込み量が例えば０．５〜１．０ｍｍとなる状態とされている。ここにおける「有機感光体に対する食い込み量」とは、有機感光体１０が存在しなかったときの、ブラシ繊維の先端が有機感光体１０内へ入り込む最大値と定義される。 The brush roller 301 is formed, for example, in a roll shape by winding a long woven fabric in which resin brush fibers such as polypropylene resin and acrylic resin are planted at a high density around the peripheral surface of the roller base. Each brush fiber having a thickness of 3 to 7 denier, a brush fiber having a bristle length of 2 to 5 mm, an electrical resistivity of the brush fiber of 10 10 Ω · cm or less, It is preferable that the Young's modulus is 4900 to 9800 N / mm 2 , the brush fiber density is 50 to 200 k / inch 2 , and the amount of biting into the organic photoreceptor 10 is, for example, 0.5 to 1.0 mm. It is in a state. Here, “the amount of biting into the organic photoreceptor” is defined as the maximum value at which the tip of the brush fiber enters the organic photoreceptor 10 when the organic photoreceptor 10 does not exist.
潤滑剤ストック３０２を構成する潤滑剤は、脂肪酸金属塩からなる潤滑剤成分と、無機化合物の粉末からなる研磨剤成分とよりなり、潤滑剤成分中に研磨剤成分を構成する微粒子が分散した状態のものである。
潤滑剤成分を構成する脂肪酸金属塩としては、例えばステアリン酸亜鉛が用いられ、また、研磨剤成分を構成する無機化合物の粉末としては、例えばマグネシウム、亜鉛、アルミニウム、コバルト、鉄、ジルコニウム、マンガン、クロムおよびストロンチウムから選ばれた金属の酸化物の粉末、またはチタン酸カルシウム、チタン酸マグネシウム、チタン酸ストロンチウムおよびチタン酸バリウムから選ばれた金属化合物の粉末が用いられる。
特に、塗布剤は、潤滑剤成分がステアリン酸亜鉛よりなり、研磨剤成分がチタン酸ストロンチウムの粉末よりなるものであることが好ましい。
The lubricant constituting the lubricant stock 302 is composed of a lubricant component composed of a fatty acid metal salt and an abrasive component composed of a powder of an inorganic compound, in which fine particles constituting the abrasive component are dispersed in the lubricant component. belongs to.
As the fatty acid metal salt constituting the lubricant component, for example, zinc stearate is used, and as the inorganic compound powder constituting the abrasive component, for example, magnesium, zinc, aluminum, cobalt, iron, zirconium, manganese, A powder of an oxide of a metal selected from chromium and strontium, or a powder of a metal compound selected from calcium titanate, magnesium titanate, strontium titanate and barium titanate is used.
In particular, the coating agent is preferably such that the lubricant component is made of zinc stearate and the abrasive component is made of strontium titanate powder.
研磨剤成分の含有割合は、潤滑剤１００質量％に対して５〜３５質量％であり、好ましくは１０〜３５質量％、より好ましくは２０〜３０質量％である。 The content rate of an abrasive | polishing agent component is 5-35 mass% with respect to 100 mass% of lubricants, Preferably it is 10-35 mass%, More preferably, it is 20-30 mass%.
以上の画像形成装置においては、次のようにして画像形成動作が行われる。
すなわち、駆動源による動力が適宜の動力伝達手段により伝達されて有機感光体１０が回転駆動されると、有機感光体１０が帯電手段１１によって所定の極性（例えば負極性）に帯電され、次いで、露光手段１２によって露光されて照射箇所（露光領域）の電位が低下されることにより静電潜像が有機感光体１０上に形成され、現像手段１３によって現像剤を構成する有機感光体１０の表面電位と同じ極性（例えば負極性）に帯電されたトナーが有機感光体１０の静電潜像に付着して反転現像が行われ、これにより、トナー像が形成される。
次いで、転写手段１４により有機感光体１０上のトナー像が画像支持体Ｐに転写された後、分離手段１５により有機感光体１０と密着した状態にある画像支持体Ｐが分離され、その後、定着手段１６によって定着処理が行われる。
In the above image forming apparatus, an image forming operation is performed as follows.
That is, when the power from the drive source is transmitted by an appropriate power transmission means and the organic photoreceptor 10 is rotationally driven, the organic photoreceptor 10 is charged to a predetermined polarity (for example, negative polarity) by the charging means 11, and then The electrostatic latent image is formed on the organic photoreceptor 10 by being exposed by the exposure means 12 and the potential of the irradiated portion (exposure area) is lowered, and the surface of the organic photoreceptor 10 constituting the developer by the developing means 13. Toner charged with the same polarity (for example, negative polarity) as the potential adheres to the electrostatic latent image of the organic photoreceptor 10 and is subjected to reversal development, whereby a toner image is formed.
Next, after the toner image on the organic photoreceptor 10 is transferred to the image support P by the transfer means 14, the image support P that is in close contact with the organic photoreceptor 10 is separated by the separating means 15, and then fixed. A fixing process is performed by means 16.
一方、転写領域を通過して有機感光体１０上に残留する未転写のトナーがクリーニング手段２０によって除去されるが、弾性ブレード２０１によるクリーニングが行われるに際して、潤滑剤塗布手段３０によって、潤滑剤が有機感光体１０の表面に塗布されると共に有機感光体１０上の未転写トナーの一部および有機感光体１０の表面層を構成する樹脂の一部がブラシローラ３０１により削り取られ、さらに、未転写トナーの残りおよび有機感光体１０の表面層を構成する樹脂の残りが弾性ブレード２０１によって削り取られる。 On the other hand, untransferred toner that passes through the transfer region and remains on the organic photoreceptor 10 is removed by the cleaning unit 20, but when the elastic blade 201 performs cleaning, the lubricant is applied by the lubricant application unit 30. A part of the untransferred toner on the organic photoreceptor 10 and a part of the resin constituting the surface layer of the organic photoreceptor 10 are scraped off by the brush roller 301 and applied to the surface of the organic photoreceptor 10. The remaining toner and the remaining resin constituting the surface layer of the organic photoreceptor 10 are scraped off by the elastic blade 201.
本発明の画像形成装置によれば、本発明の有機感光体と、この有機感光体の最表面層を構成する樹脂を削り取る適宜の手段とを有することにより、画像支持体として酸性紙を用いる場合において、当該有機感光体の最表面層を構成する樹脂が適度な硬さおよび弾性を有するものであることから、最表面層を構成する樹脂を紙粉と共に容易に削り取ることができ、その上、優れた耐傷性が得られるので最表面層を構成する樹脂を削り取る際にも表面傷がつきにくく、紙粉ボケや画像ノイズなど画像不良の発生を抑制することができる。 According to the image forming apparatus of the present invention, by using the organic photoreceptor of the present invention and an appropriate means for scraping off the resin constituting the outermost surface layer of the organic photoreceptor, acid paper is used as an image support. The resin constituting the outermost surface layer of the organophotoreceptor has appropriate hardness and elasticity, so that the resin constituting the outermost surface layer can be easily scraped off with paper dust, Since excellent scratch resistance is obtained, even when the resin constituting the outermost surface layer is scraped off, surface scratches are difficult to occur, and occurrence of image defects such as paper dust blur and image noise can be suppressed.
〔画像形成用カートリッジ〕
本発明の画像形成用カートリッジは、画像形成装置本体と脱着可能に構成されており、例えば上記の画像形成装置においては、少なくとも有機感光体１０を含み、必要に応じて、帯電手段１１、現像手段１３およびクリーニング手段２０から選ばれる少なくとも１種以上が共通の支持体に装着されることにより一体化されて画像形成用カートリッジが構成されている。
[Image forming cartridge]
The image forming cartridge of the present invention is configured to be detachable from the main body of the image forming apparatus. For example, the above image forming apparatus includes at least the organic photoreceptor 10 and, if necessary, the charging unit 11 and the developing unit. At least one selected from 13 and the cleaning means 20 are mounted on a common support to be integrated into an image forming cartridge.
以下、本発明の実施例を説明するが、本発明はこれらの実施例に限定されるものではない。 Examples of the present invention will be described below, but the present invention is not limited to these examples.
〔有機感光体の製造例１〕
（１）ブロック共重合体の合成
撹拌装置付き耐圧容器中にシクロヘキサン５０ｋｇ、充分に脱水したスチレン２７５０ｇおよびｓｅｃ−ブチルリチウムのシクロヘキサン溶液（１０質量％）２１０ｇを加え、１２０℃で６０分間重合し、次いでテトラヒドロフラン２５０ｇを添加し、１，３−ブタジエン４５００ｇを加えて６０分間、さらにスチレン２７５０ｇを加えて６０分間重合した後、メタノールを加えて反応を停止してスチレンブロック−ブタジエンブロック−スチレンブロック型のトリブロック共重合体であるブロック共重合体〔１〕を合成した。このブロック共重合体〔１〕は、ソフトセグメントブロック（ブタジエンブロック）の組成比が、ブロック共重合体〔１〕に対して４５質量％であった。
[Organic photoconductor production example 1]
(1) Synthesis of block copolymer In a pressure vessel equipped with a stirrer, 50 kg of cyclohexane, 2750 g of sufficiently dehydrated styrene and 210 g of a cyclohexane solution of sec-butyllithium (10% by mass) were added, and polymerized at 120 ° C. for 60 minutes. Next, 250 g of tetrahydrofuran was added, 4500 g of 1,3-butadiene was added for 60 minutes, and 2750 g of styrene was further added for polymerization for 60 minutes, then methanol was added to stop the reaction, and the styrene block-butadiene block-styrene block type was added. A block copolymer [1], which is a triblock copolymer, was synthesized. In this block copolymer [1], the composition ratio of the soft segment block (butadiene block) was 45% by mass with respect to the block copolymer [1].
（２）導電性支持体の作製
ＪＩＳ６０６３合金の円筒状アルミニウム基体（Φ３０×３５０ｍｍ、インロー径：φ２８．４ｍｍの肉厚０．８ｍｍ、引張強度：２１０（Ｎ／ｍｍ2 ））を切削加工（ＪＩＳ Ｂ−０６０１規定の十点表面粗さＲｚ：０．８μｍ）した後、洗浄して導電性支持体〔１〕を作製した。
(2) Production of conductive support JIS6063 alloy cylindrical aluminum substrate (Φ30 × 350 mm, inlay diameter: φ28.4 mm, wall thickness 0.8 mm, tensile strength: 210 (N / mm 2 )) was cut (JIS B-0601 specified ten-point surface roughness Rz: 0.8 μm), and then washed to produce a conductive support [1].
（３）中間層の形成
下記原料を分散機としてサンドミルを用いて、バッチ式により１０時間の分散を行い、中間層形成用塗布液〔１〕を調製した。
・バインダー樹脂：ポリアミド樹脂「ＣＭ８０００」（東レ社製） １質量部
・溶媒：イソプロピルアルコール １０質量部
・金属酸化物微粒子：数平均一次粒径３５ｎｍブルッカイト形酸化チタン ３質量部
上記導電性支持体〔１〕上に、この中間層形成用塗布液〔１〕を浸漬塗布法により塗布して塗布膜を形成し、この塗布膜を１２０℃で３０分間乾燥し、層厚３μｍの中間層〔１〕を形成した。
(3) Formation of intermediate layer Using a sand mill with the following raw materials as a disperser, dispersion was carried out for 10 hours by a batch method to prepare an intermediate layer forming coating solution [1].
-Binder resin: Polyamide resin "CM8000" (manufactured by Toray Industries Inc.) 1 part by mass-Solvent: 10 parts by mass of isopropyl alcohol-Metal oxide fine particles: Number average primary particle size 35 nm Brookite-type titanium oxide 3 parts by mass The above conductive support [ 1] On top, this intermediate layer forming coating solution [1] is applied by a dip coating method to form a coating film, and this coating film is dried at 120 ° C. for 30 minutes, and an intermediate layer [1] having a layer thickness of 3 μm is formed. Formed.
（４）有機感光層の形成
（電荷発生層の形成）
下記原料を分散機としてサンドミルを用いて、２０時間の分散を行い、電荷発生層形成用塗布液〔１〕を調製した。
・電荷発生物質：チタニルフタロシアニン顔料（Ｃｕ−Ｋα特性Ｘ線回折スペクトル測定で５少なくとも２７．３°の位置に最大回折ピークを有するもの） ２０質量部
・バインダー樹脂：ポリビニルブチラール樹脂「＃６０００−Ｃ」（電気化学工業社製）
１０質量部
・溶媒：酢酸ｔ−ブチル ７００質量部
・溶媒：４−メトキシ−４−メチル−２−ペンタノン ３００質量部
上記中間層〔１〕の上に、この電荷発生層形成用塗布液〔１〕を浸漬塗布法によりで塗布して塗布膜を形成し、層厚０．８μｍの電荷発生層〔１〕を形成した。
(4) Formation of organic photosensitive layer (formation of charge generation layer)
Dispersion was carried out for 20 hours using a sand mill using the following raw materials as a disperser to prepare a charge generation layer forming coating solution [1].
Charge generating material: titanyl phthalocyanine pigment (having a maximum diffraction peak at a position of 5 at least 27.3 ° by Cu-Kα characteristic X-ray diffraction spectrum measurement) 20 parts by mass Binder resin: polyvinyl butyral resin “# 6000-C (Electric Chemical Industry Co., Ltd.)
10 parts by mass / solvent: 700 parts by mass of t-butyl acetate / solvent: 300 parts by mass of 4-methoxy-4-methyl-2-pentanone On the intermediate layer [1], this coating solution for forming a charge generation layer [1] ] Was applied by a dip coating method to form a coating film, and a charge generation layer [1] having a layer thickness of 0.8 μm was formed.
（電荷輸送層の形成）
下記原料を混合して溶解し、電荷輸送層形成用塗布液〔１〕を調製した。
・電荷輸送物質：４−メトキシ−４′−（４−メチル−α−フェニルスチリル）トリフェニルアミン １５０質量部
・バインダー樹脂：ブロック共重合体〔１〕 １００質量部
・溶媒：テトラヒドロフラン／トルエン＝７／３体積％ ７５０質量部
・酸化防止剤：「Ｉｒｇａｎｏｘ１０１０」（日本チバガイギー社製） ２質量部
上記電荷発生層〔１〕上に、この電荷輸送層形成用塗布液〔１〕を浸漬塗布法により塗布して塗布膜を形成し、この塗布膜を１２０℃で７０分間乾燥し、層厚２５μｍの電荷輸送層〔１〕を形成し、有機感光体〔１〕を製造した。この有機感光体〔１〕の最表面層の弾性変形率を表１に示す。
(Formation of charge transport layer)
The following raw materials were mixed and dissolved to prepare a charge transport layer forming coating solution [1].
Charge transport material: 4-methoxy-4 ′-(4-methyl-α-phenylstyryl) triphenylamine 150 parts by mass Binder resin: block copolymer [1] 100 parts by mass Solvent: tetrahydrofuran / toluene = 7 / 3 parts by volume 750 parts by mass · Antioxidant: "Irganox 1010" (manufactured by Ciba Geigy Japan) 2 parts by mass On the charge generation layer [1], this coating solution for forming a charge transport layer [1] is applied by a dip coating method. Coating was performed to form a coating film, and this coating film was dried at 120 ° C. for 70 minutes to form a charge transport layer [1] having a layer thickness of 25 μm, thereby producing an organic photoreceptor [1]. The elastic deformation rate of the outermost surface layer of this organophotoreceptor [1] is shown in Table 1.
〔有機感光体の製造例２〕
有機感光体の製造例１において、（１）ブロック共重合体の合成におけるスチレンブロック／ブタジエンブロックの配合比を、ブタジエンブロックの組成比が、ブロック共重合体に対して６５質量％となるように１，３−ブタジエンを増量したことの他は同様にして有機感光体〔２〕を製造した。この有機感光体〔２〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 2]
In Production Example 1 of the organic photoreceptor, (1) the composition ratio of styrene block / butadiene block in the synthesis of the block copolymer is set so that the composition ratio of the butadiene block is 65% by mass with respect to the block copolymer. An organic photoreceptor [2] was produced in the same manner except that the amount of 1,3-butadiene was increased. Table 1 shows the elastic deformation rate of the outermost surface layer of the organophotoreceptor [2].
〔有機感光体の製造例３〕
有機感光体の製造例１において、（１）ブロック共重合体の合成におけるスチレンブロック／ブタジエンブロックの配合比を、ブタジエンブロックの組成比が、ブロック共重合体に対して３５質量％となるように１，３−ブタジエンを減量したことの他は同様にして有機感光体〔３〕を製造した。この有機感光体〔３〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 3]
In Production Example 1 of the organic photoreceptor, (1) the composition ratio of styrene block / butadiene block in the synthesis of the block copolymer is set so that the composition ratio of the butadiene block is 35% by mass with respect to the block copolymer. An organic photoreceptor [3] was produced in the same manner except that 1,3-butadiene was reduced. Table 1 shows the elastic deformation rate of the outermost surface layer of this organophotoreceptor [3].
〔有機感光体の製造例４〕
有機感光体の製造例１において、（１）ブロック共重合体の合成における１，３−ブタジエンをエチレン／プロピレン（＝５０／５０）の配合比が、ブロック共重合体に対して６０質量％となるように変更したことの他は同様にして有機感光体〔４〕を製造した。この有機感光体〔４〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 4]
In Production Example 1 of the organic photoreceptor, (1) the blending ratio of 1,3-butadiene to ethylene / propylene (= 50/50) in the synthesis of the block copolymer was 60% by mass with respect to the block copolymer. An organophotoreceptor [4] was produced in the same manner except that the change was made. Table 1 shows the elastic deformation rate of the outermost surface layer of this organophotoreceptor [4].
〔有機感光体の製造例５〕
有機感光体の製造例１において、（１）ブロック共重合体の合成における１，３−ブタジエンをエチレン／ブチレン（＝５０／５０）の配合比が、ブロック共重合体に対して６０質量％となるように変更したことの他は同様にして有機感光体〔５〕を製造した。この有機感光体〔５〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 5]
In Production Example 1 of the organophotoreceptor, (1) 1,3-butadiene in the synthesis of the block copolymer had a blending ratio of ethylene / butylene (= 50/50) of 60% by mass with respect to the block copolymer. An organophotoreceptor [5] was produced in the same manner except that the change was made. Table 1 shows the elastic deformation rate of the outermost surface layer of the organic photoreceptor [5].
〔有機感光体の製造例６〕
有機感光体の製造例１において、（１）ブロック共重合体の合成における１，３−ブタジエンをイソプレンに変更したことの他は同様にして有機感光体〔６〕を製造した。この有機感光体〔６〕の最表面層の弾性変形率を表１に示す。
[Production Example 6 of Organic Photoreceptor]
An organic photoreceptor [6] was produced in the same manner as in Production Example 1 of the organophotoreceptor except that (1,1) -butadiene in the synthesis of the block copolymer was changed to isoprene. Table 1 shows the elastic deformation rate of the outermost surface layer of the organophotoreceptor [6].
〔有機感光体の製造例７〕
有機感光体の製造例１において、（１）ブロック共重合体の合成における１，３−ブタジエンをペンタジエンに変更したことの他は同様にして有機感光体〔７〕を製造した。この有機感光体〔７〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 7]
An organic photoreceptor [7] was prepared in the same manner as in Production Example 1 of the organic photoreceptor except that 1,3-butadiene in the synthesis of (1) the block copolymer was changed to pentadiene. The elastic deformation rate of the outermost surface layer of this organophotoreceptor [7] is shown in Table 1.
〔有機感光体の製造例８〕
有機感光体の製造例１において、（４）有機感光層の形成におけるバインダー樹脂としてブロック共重合体〔１〕の代わりにスチレン樹脂「スタイロン６７９」（旭化成社製）に変更したことの他は同様にして有機感光体〔８〕を製造した。この有機感光体〔８〕の最表面層の弾性変形率を表１に示す。
[Production Example 8 of Organic Photoreceptor]
The same as in Production Example 1 of the organic photoreceptor, except that (4) the styrene resin “Styron 679” (manufactured by Asahi Kasei Co., Ltd.) was used instead of the block copolymer [1] as the binder resin in the formation of the organic photosensitive layer. Thus, an organic photoreceptor [8] was produced. Table 1 shows the elastic deformation rate of the outermost surface layer of the organic photoreceptor [8].
〔有機感光体の製造例９〕
有機感光体の製造例１において、（４）有機感光層の形成におけるバインダー樹脂としてブロック共重合体〔１〕の代わりにスチレン−メチルメタクリレート共重合体（配合比Ｓｔ／ＭＭＡ＝８０／２０）に変更したことの他は同様にして有機感光体〔９〕を製造した。この有機感光体〔９〕の最表面層の弾性変形率を表１に示す。
[Production Example 9 of Organic Photoreceptor]
In Production Example 1 of the organic photoreceptor, (4) a styrene-methyl methacrylate copolymer (blending ratio St / MMA = 80/20) is used instead of the block copolymer [1] as a binder resin in the formation of the organic photosensitive layer. An organophotoreceptor [9] was produced in the same manner except that it was changed. Table 1 shows the elastic deformation rate of the outermost surface layer of the organophotoreceptor [9].
〔有機感光体の製造例１０〕
有機感光体の製造例１において、（４）有機感光層の形成におけるバインダー樹脂としてブロック共重合体〔１〕の代わりにＺ型ポリカーボネート樹脂「ユーピロンＺ−３００」（三菱エンジニアリングプラスチックス社製）に変更したことの他は同様にして有機感光体〔１０〕を製造した。この有機感光体〔１０〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 10]
In Production Example 1 of the organic photoreceptor, (4) Z-type polycarbonate resin “Iupilon Z-300” (manufactured by Mitsubishi Engineering Plastics) instead of the block copolymer [1] as a binder resin in the formation of the organic photosensitive layer An organophotoreceptor [10] was produced in the same manner except that it was changed. The elastic deformation rate of the outermost surface layer of this organophotoreceptor [10] is shown in Table 1.
〔有機感光体の製造例１１〕
有機感光体の製造例１において、（４）有機感光層の形成におけるバインダー樹脂としてブロック共重合体〔１〕の代わりにスチレン−ブタジエン共重合体（スチレン含有量５５質量％）に変更したことの他は同様にして有機感光体〔１１〕を製造した。この有機感光体〔１１〕の最表面層の弾性変形率を表１に示す。
[Production Example 11 of Organic Photoreceptor]
In Production Example 1 of the organic photoreceptor, (4) the binder resin in the formation of the organic photosensitive layer was changed to a styrene-butadiene copolymer (styrene content 55% by mass) instead of the block copolymer [1]. Otherwise, an organophotoreceptor [11] was produced in the same manner. The elastic deformation rate of the outermost surface layer of this organophotoreceptor [11] is shown in Table 1.
〔有機感光体の製造例１２〕
有機感光体の製造例１において、（４）有機感光層の形成におけるバインダー樹脂としてブロック共重合体〔１〕の代わりに、Ｚ型ポリカーボネート樹脂「ユーピロンＺ−３００」（三菱エンジニアリングプラスチックス社製）にスチレン−ブタジエン共重合体（スチレン含有量５５質量％）を２０質量％添加して得られたものに変更したことの他は同様にして有機感光体〔１２〕を製造した。この有機感光体〔１２〕の最表面層の弾性変形率を表１に示す。
[Organic photoconductor production example 12]
In Production Example 1 of the organic photoreceptor, (4) Z-type polycarbonate resin “Iupilon Z-300” (manufactured by Mitsubishi Engineering Plastics) instead of the block copolymer [1] as the binder resin in the formation of the organic photosensitive layer An organophotoreceptor [12] was produced in the same manner except that it was changed to that obtained by adding 20% by mass of a styrene-butadiene copolymer (styrene content 55% by mass). Table 1 shows the elastic deformation rate of the outermost surface layer of the organophotoreceptor [12].
〔実施例１〜７および比較例１〜５〕
以上のようにして得られた有機感光体〔１〕〜〔１２〕をモノクロ画像形成装置「ｂｉｚｈｕｂ １６４」（コニカミノルタビジネステクノロジーズ社製）に搭載し、ＨＨ環境（温度３０℃、相対湿度８５％）下において、画像支持体として酸性紙「ＳＰＥＣＴＲＵＭ Ｐａｐｅｒ」（Ｘｅｒｏｘ社製）を用い、印字率５．０％画像で３０００枚プリントする実写を行った後、文字チャート、ハーフトーン画像、黒ベタ画像をそれぞれ出画し、下記評価基準により評価した。また、ハーフトーン画像において、白スジ状の画像ノイズの発生の有無を観察した。結果を表１に示す。なお、表１に示す「膜削れ量」は、１万枚プリント当たりの有機感光体の表面層の減耗量（μｍ／１万枚）を示す。
[Examples 1-7 and Comparative Examples 1-5]
The organophotoreceptors [1] to [12] obtained as described above are mounted on a monochrome image forming apparatus “bizhub 164” (manufactured by Konica Minolta Business Technologies), and in an HH environment (temperature 30 ° C., relative humidity 85%). ) Below, an acid paper “SPECTRUM Paper” (manufactured by Xerox) was used as the image support, and after taking a real image of printing 3000 sheets with a printing rate of 5.0%, a character chart, a halftone image, and a solid black image Were imaged and evaluated according to the following evaluation criteria. Further, the occurrence of white streak-like image noise was observed in the halftone image. The results are shown in Table 1. The “film scraping amount” shown in Table 1 indicates the amount of wear (μm / 10,000 sheets) of the surface layer of the organic photoreceptor per 10,000 prints.
（文字チャートの評価基準）
○：良好
×：文字のかすれや細りが発生
(Character chart evaluation criteria)
○: Good ×: Text blurring or thinning occurs
（ハーフトーン画像の評価基準）
反射濃度計「ＲＤ−９１８」（マクベス社製）を用いて、ハーフトーン画像の５箇所を測定し、各測定箇所の濃度ムラ差（最大濃度−最小濃度）を算出した。
○：濃度ムラ差が１５％以下で良好
△：濃度ムラ差が１５％を超えて３０％以下で実用上問題ないレベル
×：濃度ムラ差が３０％を超えて実用上問題あり
(Evaluation criteria for halftone images)
Using a reflection densitometer “RD-918” (manufactured by Macbeth), five locations of the halftone image were measured, and the density unevenness difference (maximum density−minimum density) at each measurement location was calculated.
○: Good when the density unevenness difference is 15% or less Δ: Level where there is no practical problem when the density unevenness exceeds 15% and 30% or less ×: There is a practical problem when the density unevenness exceeds 30%
（黒ベタ画像の評価基準）
反射濃度計「ＲＤ−９１８」（マクベス社製）を用いて、黒ベタ画像の５箇所を測定し、各測定箇所の濃度ムラ差を算出した。
○：濃度ムラ差が１５％以下で良好
△：濃度ムラ差が１５％を超えて３０％以下で実用上問題ないレベル
×：濃度ムラ差が３０％を超えて実用上問題あり
(Evaluation criteria for solid black images)
Using a reflection densitometer “RD-918” (manufactured by Macbeth Co., Ltd.), five portions of the black solid image were measured, and the density unevenness difference at each measurement portion was calculated.
○: Good when the density unevenness difference is 15% or less Δ: Level where there is no practical problem when the density unevenness exceeds 15% and 30% or less ×: There is a practical problem when the density unevenness exceeds 30%
〔実施例８〜１４および比較例６〜１０〕
モノクロ画像形成装置「ｂｉｚｈｕｂ １６４」（コニカミノルタビジネステクノロジーズ社製）を図１に示すステアリン酸亜鉛よりなる潤滑剤を有機感光体の表面に塗布する潤滑剤塗布手段と接触帯電方式による帯電手段とを具えたものに改造して有機感光体〔１〕〜〔１２〕をそれぞれ搭載し、ＨＨ環境（温度３０℃、相対湿度８５％）下において、画像支持体として酸性紙「ＳＰＥＣＴＲＵＭ Ｐａｐｅｒ」（Ｘｅｒｏｘ社製）を用い、印字率５．０％画像で３０００枚プリントする実写を行った後、文字チャート、ハーフトーン画像、黒ベタ画像をそれぞれ画出し、下記評価基準により評価した。また、ハーフトーン画像において、白スジ状の画像ノイズの発生の有無を観察した。結果を表２に示す。なお、表２に示す「膜削れ量」は、１万枚プリント当たりの有機感光体の表面層の減耗量（μｍ／１万枚）を示す。
[Examples 8 to 14 and Comparative Examples 6 to 10]
A monochrome image forming apparatus “bizhub 164” (manufactured by Konica Minolta Business Technologies, Inc.) includes a lubricant applying means for applying a lubricant made of zinc stearate to the surface of the organic photoreceptor shown in FIG. 1 and a charging means by a contact charging method. The organic photoconductors [1] to [12] are remodeled into the provided ones, and acid paper “SPECTRUM Paper” (Xerox Co., Ltd.) is used as an image support in an HH environment (temperature 30 ° C., relative humidity 85%). After making 3000 photographs with a printing rate of 5.0%, a character chart, a halftone image, and a black solid image were drawn out and evaluated according to the following evaluation criteria. Further, the occurrence of white streak-like image noise was observed in the halftone image. The results are shown in Table 2. The “film scraping amount” shown in Table 2 indicates the amount of wear (μm / 10,000 sheets) of the surface layer of the organic photoreceptor per 10,000 prints.
１０ 有機感光体
１１ 帯電手段
１２ 露光手段
１３ 現像手段
１３１ 現像スリーブ
１４ 転写手段
１５ 分離手段
１６ 定着手段
１６１ 加熱ローラ
１６２ 加圧ローラ
２０ クリーニング手段
２０１ 弾性ブレード
３０ 潤滑剤塗布手段
３０ａ 削取領域
３０ｂ 塗布領域
３０１ ブラシローラ
３０２ 潤滑剤ストック
３０３ 押圧装置
Ｐ 画像支持体
DESCRIPTION OF SYMBOLS 10 Organic photoreceptor 11 Charging means 12 Exposure means 13 Development means 131 Development sleeve 14 Transfer means 15 Separation means 16 Fixing means 161 Heating roller 162 Pressure roller 20 Cleaning means 201 Elastic blade 30 Lubricant application means 30a Cutting area 30b Application area 301 Brush roller 302 Lubricant stock 303 Pressing device P Image support
Claims (6)
当該有機感光体の最表面層の弾性変形率が３５〜５５％であり、
前記最表面層を構成する樹脂が、スチレンブロックと、ソフトセグメントブロックとのブロック共重合体よりなり、
前記ソフトセグメントブロックは、ブタジエン、イソプレン、ペンタジエン、エチレン／ブチレンおよびエチレン／プロピレンから選ばれる１種以上により形成されるものであり、
前記ソフトセグメントブロックの組成比が、前記ブロック共重合体に対して２５〜６５質量％であることを特徴とする有機感光体。 In an organic photoreceptor in which at least an organic photosensitive layer is laminated on a conductive support,
The elastic deformation rate of the outermost surface layer of the organophotoreceptor is 35 to 55%,
The resin constituting the outermost surface layer is a block copolymer of a styrene block and a soft segment block,
The soft segment block is formed of one or more selected from butadiene, isoprene, pentadiene, ethylene / butylene and ethylene / propylene,
An organic photoreceptor, wherein the composition ratio of the soft segment block is 25 to 65% by mass with respect to the block copolymer.
当該有機感光体の表面に脂肪族金属塩よりなる潤滑剤を塗布する潤滑剤塗布手段とを有することを特徴とする画像形成装置。 An organophotoreceptor according to claim 1;
An image forming apparatus comprising: a lubricant application unit configured to apply a lubricant composed of an aliphatic metal salt to the surface of the organic photoreceptor.
当該有機感光体の表面に一様な電位を付与する帯電手段とを有し、
前記帯電手段が接触帯電方式のものであることを特徴とする画像形成装置。 An organophotoreceptor according to claim 1;
Charging means for applying a uniform potential to the surface of the organic photoreceptor,
An image forming apparatus, wherein the charging means is of a contact charging type.
当該有機感光体の表面に残留した未転写トナーを除去するクリーニング手段とを有し、
前記クリーニング手段が弾性ブレードよりなることを特徴とする画像形成装置。 An organophotoreceptor according to claim 1;
Cleaning means for removing untransferred toner remaining on the surface of the organic photoreceptor,
An image forming apparatus according to claim 1, wherein the cleaning means comprises an elastic blade.
請求項１に記載の有機感光体を具えてなることを特徴とする画像形成用カートリッジ。 An image forming cartridge detachable from the image forming apparatus main body,
An image forming cartridge comprising the organic photoreceptor according to claim 1.