JP2012171042A - Method of polishing glass substrate - Google Patents
Method of polishing glass substrate Download PDFInfo
- Publication number
- JP2012171042A JP2012171042A JP2011034779A JP2011034779A JP2012171042A JP 2012171042 A JP2012171042 A JP 2012171042A JP 2011034779 A JP2011034779 A JP 2011034779A JP 2011034779 A JP2011034779 A JP 2011034779A JP 2012171042 A JP2012171042 A JP 2012171042A
- Authority
- JP
- Japan
- Prior art keywords
- polishing
- glass substrate
- surface plate
- substrate
- euvl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、ガラス基板の研磨方法に関する。より具体的には、EUV(Extreme Ultra Violet:極端紫外)光を用いたリソグラフィ(以下、「EUVL」と略する)の際に使用される反射型マスクや反射型ミラーの基材として使用されるガラス基板(以下、「EUVL光学基材用ガラス基板」と略する。)の研磨方法に関する。 The present invention relates to a method for polishing a glass substrate. More specifically, it is used as a base material for a reflective mask or a reflective mirror used in lithography (hereinafter abbreviated as “EUVL”) using EUV (Extreme Ultra Violet) light. The present invention relates to a method for polishing a glass substrate (hereinafter, abbreviated as “glass substrate for EUVL optical substrate”).
従来から、半導体製造工程においては、ウェハ上に微細な回路パターンを転写して集積回路を製造するための露光装置が広く使用されている。近年、半導体集積回路の高集積化、高機能化に伴い、集積回路の微細化が進み、回路パターンをウェハ面上に正確に結像させるために、露光装置のフォトマスクに使用される光学基材用ガラス基板は高度の平坦性と平滑性が求められている。 Conventionally, in a semiconductor manufacturing process, an exposure apparatus for manufacturing an integrated circuit by transferring a fine circuit pattern onto a wafer has been widely used. In recent years, along with the higher integration and higher functionality of semiconductor integrated circuits, the miniaturization of integrated circuits has progressed, and an optical substrate used in a photomask of an exposure apparatus to accurately form a circuit pattern on a wafer surface. The glass substrate for materials is required to have high flatness and smoothness.
さらに、このような技術動向にあって、次の世代の露光光源としてEUV光を使用したリソグラフィ技術(すなわち、EUVL技術)が、45nm以降の複数の世代にわたって適用可能と見られ注目されている。EUV光とは軟X線領域または真空紫外域の波長帯の光を指し、具体的には波長が0.2〜100nm程度の光のことである。現時点では、リソグラフィ光源として13.5nmの波長光の使用が検討されている。このEUVLの露光原理は、投影光学系を用いてマスクパターンを転写する点では、従来のリソグラフィと同じであるが、EUV光のエネルギー領域では光を透過する材料がないために屈折光学系は用いることができず、反射光学系を用いることとなり、反射型マスクや反射型ミラーが用いられる(特許文献1参照)。 Further, in such a technical trend, a lithography technique using EUV light as a next generation exposure light source (ie, EUVL technique) is considered to be applicable over a plurality of generations of 45 nm and after, and has attracted attention. EUV light refers to light in the wavelength band of the soft X-ray region or the vacuum ultraviolet region, specifically, light having a wavelength of about 0.2 to 100 nm. At present, the use of 13.5 nm wavelength light as a lithography light source is being studied. The EUVL exposure principle is the same as that of conventional lithography in that a mask pattern is transferred using a projection optical system, but a refractive optical system is used because there is no material that transmits light in the EUV light energy region. Therefore, a reflective optical system is used, and a reflective mask or a reflective mirror is used (see Patent Document 1).
EUVLに用いられる反射型マスクは、(1)基材、(2)基材上に形成された反射多層膜、(3)反射多層膜上に形成された吸収体層から基本的に構成される。反射型ミラーの場合は、(1)基材、(2)基材上に形成された反射多層膜から基本的に構成される。
反射型マスクや反射型ミラーの製造に用いられる基材(EUVL光学基材)としては、EUV光照射の下においても歪みが生じないよう低熱膨張係数を有する材料が必要とされ、低熱膨張係数を有するガラスや結晶化ガラスで作製されたガラス基板(EUVL光学基材用ガラス基板)が検討されている。EUVL光学基材用ガラス基板は、これらガラスや結晶化ガラスの素材を、高精度に研磨、洗浄することによって製造される。
A reflective mask used for EUVL basically includes (1) a base material, (2) a reflective multilayer film formed on the base material, and (3) an absorber layer formed on the reflective multilayer film. . In the case of a reflective mirror, it is basically composed of (1) a base material and (2) a reflective multilayer film formed on the base material.
As a base material (EUVL optical base material) used for manufacturing a reflective mask or a reflective mirror, a material having a low thermal expansion coefficient is required so that distortion does not occur even under EUV light irradiation. A glass substrate (a glass substrate for EUVL optical base material) made of glass or crystallized glass has been studied. The glass substrate for EUVL optical base material is manufactured by polishing and washing these glass and crystallized glass materials with high accuracy.
一般に、磁気記録媒体用基板や半導体用基板などを平滑度の高い表面に研磨する方法は知られている。例えば、特許文献2には、メモリーハードディスクの仕上げ研磨や半導体素子用基板などの研磨について、研磨後の被研磨物の表面粗さが小さく、かつ微小突起(凸状欠点)を低減させる研磨方法として、水、研磨材、酸化合物を含有してなり、pHが酸性かつ研磨材の濃度が10重量%未満である研磨液組成物と、研磨パッドと、を用いて機械研磨することが記載されている。そして、研磨材として酸化アルミニウム、シリカ、酸化セリウム、酸化ジルコニウムなどが、またpHを酸性にするための酸として硝酸、硫酸、塩酸や有機酸などがそれぞれ例示されている。 In general, a method for polishing a magnetic recording medium substrate, a semiconductor substrate, or the like to a highly smooth surface is known. For example, Patent Document 2 discloses a polishing method for finishing polishing of a memory hard disk and polishing of a substrate for a semiconductor element, etc., in which the surface roughness of the polished object is small and fine protrusions (convex defects) are reduced. And polishing with a polishing composition comprising water, an abrasive and an acid compound, having an acidic pH and an abrasive concentration of less than 10% by weight, and a polishing pad. Yes. Examples of the abrasive include aluminum oxide, silica, cerium oxide, and zirconium oxide, and examples of acids for making the pH acidic include nitric acid, sulfuric acid, hydrochloric acid, and organic acids.
EUVL光学基材用ガラス基板についても、特定の研磨スラリーと、研磨パッドと、を用いて機械研磨することによって、基板表面の凸欠点や凹欠点を減少させて、ガラス基板の表面平滑性を向上させる方法が特許文献3〜7に記載されている。
ガラス基板表面の凸欠点や凹欠点を減少させることが求められるのは、凸欠点や凹欠点が存在するガラス基板表面上に反射多層膜を形成すると、反射多層膜の周期構造が乱され、位相欠陥を生じるからである。
したがって、EUVL光学基材用ガラス基板において、表面平滑性の向上が特に重要となるのは、反射型マスクや反射型ミラーの製造時に反射多層膜や吸収体層が形成されるガラス基板の成膜面である。以下、本明細書において、EUVL光学基材用ガラス基板の成膜面といった場合、ガラス基板の両主表面(すなわち、ガラス基板の表裏面)のうち、反射型マスクや反射型ミラーの製造時に反射多層膜や吸収体層が形成される側の主表面を指す。
The glass substrate for EUVL optical substrate is also mechanically polished with a specific polishing slurry and a polishing pad to reduce convex defects and concave defects on the substrate surface and improve the surface smoothness of the glass substrate. Patent Documents 3 to 7 describe the methods of making them.
It is required to reduce convex defects and concave defects on the surface of a glass substrate. When a reflective multilayer film is formed on a glass substrate surface where convex defects and concave defects exist, the periodic structure of the reflective multilayer film is disturbed, and the phase This is because defects are produced.
Therefore, in the glass substrate for EUVL optical base material, the improvement of the surface smoothness is particularly important when the reflective multilayer film or the absorber layer is formed during the production of the reflective mask or the reflective mirror. Surface. Hereinafter, in the present specification, in the case of the film formation surface of the glass substrate for EUVL optical base material, it is reflected at the time of manufacturing the reflective mask or the reflective mirror among the two main surfaces of the glass substrate (that is, the front and back surfaces of the glass substrate). The main surface on the side where the multilayer film and the absorber layer are formed.
EUVL光学基材用ガラス基板(以下、単に「ガラス基板」と記載する場合がある。)を機械研磨する場合、研磨に要する時間を短縮できる、表裏面の基板平坦度を同時に確保できる、板厚偏差(TTV)を小さくできる等の理由から、また、片面研磨では非研磨面をチャッキングする必要があり、非研磨面となる基板表面でパーティクル付着が発生する等の理由から、通常は両面研磨機が使用される(特許文献3、4、8、9)。
両面研磨機を用いてガラス基板を研磨する場合、特許文献3、4、8、9に示すように、それぞれ研磨パッドが取り付けられた上定盤と、下定盤と、で、キャリアに保持されたガラス基板を挟持し、上下定盤の研磨パッドと、ガラス基板と、の間に研磨液(研磨スラリー)を供給しつつ、ガラス基板を保持するキャリアを公転および自転させながら、ガラス基板の両主表面を同時に研磨する。
両面研磨機を用いてガラス基板を研磨する場合、ガラス基板の下面は、自重により定盤(下定盤)に取り付けられた研磨パッドに吸着しやすく、下定盤に取り付けられた研磨パッドから取り外す際に傷が生じるおそれがあるので、EUVL光学基材用ガラス基板の成膜面側を上向きにした状態(すなわち、ガラス基板の成膜面が上定盤に取り付けられた研磨パッドと対面した状態)で両面研磨を行うことが好ましいと考えられていた。
When mechanically polishing a glass substrate for EUVL optical base material (hereinafter sometimes simply referred to as “glass substrate”), the time required for polishing can be shortened, and the flatness of the substrate on the front and back surfaces can be secured at the same time. Double-side polishing is usually used because the deviation (TTV) can be reduced, and because non-polished surfaces need to be chucked in single-side polishing, and particle adhesion occurs on the non-polished substrate surface. Machine is used (Patent Documents 3, 4, 8, 9).
When a glass substrate is polished using a double-side polishing machine, as shown in Patent Documents 3, 4, 8, and 9, the upper surface plate and the lower surface plate to which the polishing pad is attached are held by the carrier. While holding the glass substrate, supplying the polishing liquid (polishing slurry) between the polishing pad of the upper and lower surface plate and the glass substrate, revolving and rotating the carrier holding the glass substrate, Polish the surface simultaneously.
When polishing a glass substrate using a double-side polishing machine, the lower surface of the glass substrate is easily adsorbed to the polishing pad attached to the surface plate (lower surface plate) by its own weight, and when removing from the polishing pad attached to the lower surface plate Since there is a risk of scratches, the film formation surface side of the glass substrate for EUVL optical base material faces up (that is, the film formation surface of the glass substrate faces the polishing pad attached to the upper surface plate). It was considered preferable to perform double-side polishing.
しかしながら、EUVL光学基材用ガラス基板の成膜面側を上向きにした状態で両面研磨機を用いてガラス基板を研磨した場合に、研磨後のガラス基板の成膜面にピットやスクラッチと呼ばれる凹欠点が生じる場合があることを本願発明者は見出した。
両面研磨機を用いてガラス基板を研磨する場合、ガラス基板と、上下定盤に取り付けられた研磨パッドと、の間に研磨スラリーを供給するが、この際、重力を利用して、ガラス基板と、上下定盤に取り付けられた研磨パッドと、の間に研磨液(研磨スラリー)を供給するために、特許文献8、9に示すように、上定盤および該上定盤に取り付けられた研磨パッドに研磨液(研磨スラリー)供給用の孔を設け、該孔から研磨液(研磨スラリー)を供給することが好ましいとされている。
本願発明者は、この研磨液(研磨スラリー)供給用の孔の存在が、上定盤に取り付けられた研磨パッドで研磨されるガラス基板の成膜面に、ピットやスクラッチと呼ばれる凹欠点が生じる原因であることを見出した。
However, when a glass substrate is polished using a double-side polishing machine with the film formation surface side of the glass substrate for EUVL optical base material facing upward, a recess called pit or scratch is formed on the film formation surface of the polished glass substrate. The inventor of the present application has found that defects may occur.
When polishing a glass substrate using a double-side polishing machine, a polishing slurry is supplied between the glass substrate and the polishing pad attached to the upper and lower surface plates. At this time, using the gravity, the glass substrate and In order to supply a polishing liquid (polishing slurry) between the polishing pad attached to the upper and lower surface plates, as shown in Patent Documents 8 and 9, the upper surface plate and the polishing attached to the upper surface plate It is preferable that a hole for supplying a polishing liquid (polishing slurry) is provided in the pad and the polishing liquid (polishing slurry) is supplied from the hole.
The inventor of the present application indicates that the presence of the holes for supplying the polishing liquid (polishing slurry) causes concave defects called pits and scratches on the film formation surface of the glass substrate polished by the polishing pad attached to the upper surface plate. I found out that it was the cause.
なお、特許文献3〜7に記載の発明では、両面研磨機を用いてガラス基板を研磨する際に、ガラス基板の一方の面にピットやスクラッチと呼ばれる凹欠点が生じること、および、凹欠点の原因が上定盤(および該上定盤に取り付けられた研磨パッド)設けられた研磨液(研磨スラリー)供給用の孔であることは全く認識されていなかった。 In the inventions described in Patent Documents 3 to 7, when a glass substrate is polished using a double-side polishing machine, a concave defect called pit or scratch occurs on one surface of the glass substrate, and the concave defect It was not recognized at all that the cause was a hole for supplying a polishing liquid (polishing slurry) provided on the upper surface plate (and the polishing pad attached to the upper surface plate).
本発明は、上記した従来技術の問題点を解決するため、EUVL光学基材用での成膜面における凹欠点の発生が抑制されたEUVL光学基材用ガラス基板の研磨方法を提供することを目的とする。 In order to solve the above-described problems of the prior art, the present invention provides a method for polishing a glass substrate for an EUVL optical substrate in which the occurrence of concave defects on the film formation surface for the EUVL optical substrate is suppressed. Objective.
本発明は、両面研磨装置の上下定盤の研磨面でキャリアに保持されたガラス基板を挟持し、上定盤に設けられた供給孔から研磨粒子を含む流体を供給しつつ、前記上下定盤と、前記キャリアに保持された前記ガラス基板と、を相対的に移動させて前記ガラス基板の両主表面を研磨するEUVリソグラフィ(EUVL)光学基材用ガラス基板の研磨方法であって、
EUVL光学基材での成膜面が、前記下定盤の研磨面と対面するように前記ガラス基板を挟持することを特徴とするEUVL光学基材用ガラス基板の研磨方法。
The present invention provides the above-described upper and lower surface plates while sandwiching a glass substrate held by a carrier between the polishing surfaces of the upper and lower surface plates of a double-side polishing apparatus and supplying a fluid containing abrasive particles from a supply hole provided in the upper surface plate. And polishing the glass substrate for an EUV lithography (EUVL) optical base material, wherein the glass substrate held by the carrier is relatively moved to polish both main surfaces of the glass substrate,
A method for polishing a glass substrate for an EUVL optical substrate, wherein the glass substrate is sandwiched so that a film formation surface on the EUVL optical substrate faces a polishing surface of the lower surface plate.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記上下両定盤を同心の回転軸で回転させつつ、
前記キャリアを、その中心が前記研磨面上の前記定盤の回転軸と一致しない位置に配置し、前記研磨面上で前記ガラス基板を保持する前記キャリアを前記定盤の回転軸を中心に相対的に公転させ、かつ、前記キャリアの中心を回転軸として前記研磨面上で該キャリアを自転させることによって、前記ガラス基板の両主表面を研磨することが好ましい。
In the method for polishing a glass substrate for an EUVL optical substrate of the present invention, while rotating the upper and lower both surface plates around a concentric rotating shaft,
The carrier is disposed at a position where the center thereof does not coincide with the rotation axis of the surface plate on the polishing surface, and the carrier holding the glass substrate on the polishing surface is relative to the rotation axis of the surface plate. It is preferable that both main surfaces of the glass substrate are polished by revolving and rotating the carrier on the polishing surface around the center of the carrier as a rotation axis.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記上下両定盤の研磨面による研磨荷重が1〜120g/cm2であることが好ましい。 In the method for polishing a glass substrate for an EUVL optical substrate of the present invention, it is preferable that a polishing load by the polishing surfaces of the upper and lower surface plates is 1 to 120 g / cm 2 .
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記上下両定盤には、表面の最大山と最小山の高低差が50μm以下のパッド表面を有するスウェード系研磨パッドが取り付けられていることが好ましい。 In the method for polishing a glass substrate for an EUVL optical substrate according to the present invention, a suede type polishing pad having a pad surface whose height difference between the maximum peak and the minimum peak of the surface is 50 μm or less is attached to the upper and lower surface plates. It is preferable.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨パッドの平均開口径が5〜100μmであることが好ましい。 In the method for polishing a glass substrate for an EUVL optical substrate according to the present invention, the polishing pad preferably has an average opening diameter of 5 to 100 μm.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記下定盤に取り付けられた研磨パッドの平均開口径と、前記上定盤に取り付けられた研磨パッドの平均開口径と、の差(下定盤の研磨パッド平均開口径 − 上定盤の研磨パッドの平均開口径)が、0.01μm以上であることが好ましい。 In the method for polishing a glass substrate for an EUVL optical substrate according to the present invention, the difference between the average opening diameter of the polishing pad attached to the lower surface plate and the average opening diameter of the polishing pad attached to the upper surface plate (lower limit) The average opening diameter of the polishing pad of the board—the average opening diameter of the polishing pad of the upper surface plate) is preferably 0.01 μm or more.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨パッドのパッド表面がドレス板でドレッシング加工されていることが好ましい。
ここで、前記ドレス板が電着ダイヤであることが好ましい。
In the method for polishing a glass substrate for an EUVL optical substrate according to the present invention, the pad surface of the polishing pad is preferably dressed with a dress plate.
Here, the dress plate is preferably an electrodeposition diamond.
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨粒子がコロイダルシリカまたは酸化セリウムであることが好ましい。
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨粒子が平均一次粒子径が5〜100nmのコロイダルシリカであることがより好ましい。
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨粒子を含む流体におけるコロイダルシリカの含有率が5〜40質量%であることがより好ましい。
本発明のEUVL光学基材用ガラス基板の研磨方法において、前記研磨粒子を含む流体のpHが8以下のコロイダルシリカ水溶液であることがより好ましい。
In the polishing method for a glass substrate for an EUVL optical substrate of the present invention, the abrasive particles are preferably colloidal silica or cerium oxide.
In the method for polishing a glass substrate for an EUVL optical substrate of the present invention, the abrasive particles are more preferably colloidal silica having an average primary particle diameter of 5 to 100 nm.
In the method for polishing a glass substrate for an EUVL optical substrate of the present invention, the colloidal silica content in the fluid containing the abrasive particles is more preferably 5 to 40% by mass.
In the method for polishing a glass substrate for an EUVL optical substrate according to the present invention, the fluid containing the abrasive particles is more preferably a colloidal silica aqueous solution having a pH of 8 or less.
本発明のEUVL光学基材用ガラス基板の研磨方法において、表面粗さ(Rms)が1nm以下、平坦度(P−V値)が1μm以下となるように、ガラス基板の被研磨面が予備研磨されていることがより好ましい。 In the method for polishing a glass substrate for an EUVL optical substrate of the present invention, the surface to be polished of the glass substrate is preliminarily polished so that the surface roughness (Rms) is 1 nm or less and the flatness (PV value) is 1 μm or less. More preferably.
本発明によれば、基板両主表面が平滑性に優れ、かつ、EUVL光学基材での成膜面における凹欠点の発生が抑制されたEUVL光学基材用ガラス基板を得ることができる。
本発明において、上定盤に取り付けられる研磨パッドの平均開口径を、下定盤に取り付けられる研磨パッドの平均開口径よりも小さくした場合、研磨終了後、上定盤の研磨面(研磨パッドのパッド面)にガラス基板が吸着することになり、ガラス基板の成膜面が下定盤の研磨面(研磨パッドのパッド面)に吸着することがない。この結果、両面研磨装置からガラス基板を取り外す際に、ガラス基板の成膜面に傷が生じるおそれがない。
According to the present invention, it is possible to obtain a glass substrate for an EUVL optical substrate in which both main surfaces of the substrate are excellent in smoothness and generation of concave defects on the film forming surface of the EUVL optical substrate is suppressed.
In the present invention, when the average opening diameter of the polishing pad attached to the upper surface plate is made smaller than the average opening diameter of the polishing pad attached to the lower surface plate, the polishing surface of the upper surface plate (the pad of the polishing pad) is finished after polishing. The glass substrate is adsorbed on the surface), and the film forming surface of the glass substrate is not adsorbed on the polishing surface of the lower surface plate (pad surface of the polishing pad). As a result, when removing the glass substrate from the double-side polishing apparatus, there is no possibility that the film forming surface of the glass substrate is damaged.
以下、図面を参照して本発明のEUVL光学基材用ガラス基板の研磨方法(以下、「本発明の基板研磨方法」という。)を説明する。
本発明の基板研磨方法では、両面研磨装置を用いてEUVL光学基材用ガラス基板の両主表面を研磨する。ここで、ガラス基板の主表面とは使用時に基板として機能する面を指し、具体的には端面を除く表裏面である。以下、本明細書において、ガラス基板の両面研磨といった場合、ガラス基板の両主表面、すなわち、ガラス基板の表裏面を研磨することを指す。
両面研磨装置には様々な構成のものがあるが、上下定盤の研磨面でキャリアに保持されたガラス基板を挟持し、上定盤に設けられた供給孔から研磨粒子を含む流体(以下、本明細書において、「研磨スラリー」という。)を供給しつつ、上下定盤と、キャリアに保持されたガラス基板と、を相対的に移動させることにより、ガラス基板の両面を研磨する点では共通である。
以下、図面を参照して両面研磨装置について説明するが、本発明の基板研磨方法に用いる両面研磨装置は上記を満たすものであればよく、両面研磨装置の構成、動作機構、両面研磨装置でのガラス基板の配置等はこれに限定されない。
Hereinafter, a method for polishing a glass substrate for an EUVL optical substrate of the present invention (hereinafter referred to as “substrate polishing method of the present invention”) of the present invention will be described with reference to the drawings.
In the substrate polishing method of the present invention, both main surfaces of the glass substrate for EUVL optical substrate are polished using a double-side polishing apparatus. Here, the main surface of a glass substrate refers to the surface which functions as a substrate at the time of use, specifically the front and back surfaces excluding the end surfaces. Hereinafter, in this specification, in the case of double-side polishing of a glass substrate, it refers to polishing both main surfaces of the glass substrate, that is, the front and back surfaces of the glass substrate.
There are various configurations of the double-side polishing apparatus, but the glass substrate held by the carrier is sandwiched between the polishing surfaces of the upper and lower surface plates, and a fluid containing abrasive particles (hereinafter, referred to as a supply hole provided in the upper surface plate). In this specification, it is common in that both surfaces of the glass substrate are polished by relatively moving the upper and lower surface plates and the glass substrate held by the carrier while supplying “polishing slurry”). It is.
Hereinafter, a double-side polishing apparatus will be described with reference to the drawings, but the double-side polishing apparatus used in the substrate polishing method of the present invention only needs to satisfy the above requirements. The arrangement of the glass substrate is not limited to this.
図1は、本発明のEUVL光学基材用ガラス基板の研磨方法に用いる両面研磨装置の一構成例を示した側断面図である。
図1に示す両面研磨装置10は、ガラス基板22の両面を研磨する遊星歯車方式の研磨装置である。図1に示す両面研磨装置10は、上定盤12、下定盤14、太陽歯車16、及び内歯歯車18を備える。詳しくは後述するが、太陽歯車16及び内歯歯車18は、上下両定盤(上定盤12、下定盤14)と、キャリア20に保持されたガラス基板22と、を相対的に移動させる手段である。
上下両定盤(上定盤12、下定盤14)は、中心部に空洞12a,14aを有するドーナツ状である。
FIG. 1 is a side sectional view showing an example of the configuration of a double-side polishing apparatus used in the method for polishing a glass substrate for an EUVL optical substrate of the present invention.
A double-side polishing apparatus 10 shown in FIG. 1 is a planetary gear type polishing apparatus that polishes both surfaces of a glass substrate 22. A double-side polishing apparatus 10 shown in FIG. 1 includes an upper surface plate 12, a lower surface plate 14, a sun gear 16, and an internal gear 18. As will be described in detail later, the sun gear 16 and the internal gear 18 are means for relatively moving the upper and lower surface plates (upper surface plate 12, lower surface plate 14) and the glass substrate 22 held by the carrier 20. It is.
Both the upper and lower surface plates (upper surface plate 12, lower surface plate 14) have a donut shape having cavities 12a and 14a at the center.
図2は、図1に示す両面研磨装置10内におけるガラス基板22の配置の一構成例を示した図であり、下定盤14上にガラス基板22を保持したキャリア20を配置した状態を示している。図2において、下定盤14上(実際には、上下両定盤(上定盤12、下定盤14)の間)には、複数のキャリア20が配置されている。複数のキャリア20は、例えば、図1における太陽歯車16と内歯歯車18との間のドーナツ状の領域において、下定盤14(実際には上定盤12及び下定盤14)の円周方向へ並べて配置される。
また、キャリア20は、ガラス基板22を収容する4角穴状の貫通部を中央に有する円板状体であり、外周に歯車が設けられており、外周部において太陽歯車16及び内歯歯車18と噛み合う。各キャリア20は、ガラス基板22をそれぞれ1枚保持する。なお、図2では、各キャリア20は、ガラス基板22をそれぞれ1枚保持しているが、各キャリアが複数のガラス基板を保持していてもよい。
FIG. 2 is a diagram showing a configuration example of the arrangement of the glass substrate 22 in the double-side polishing apparatus 10 shown in FIG. 1, and shows a state in which the carrier 20 holding the glass substrate 22 is arranged on the lower surface plate 14. Yes. In FIG. 2, a plurality of carriers 20 are arranged on the lower surface plate 14 (in practice, between the upper and lower surface plates (the upper surface plate 12 and the lower surface plate 14)). For example, in a donut-shaped region between the sun gear 16 and the internal gear 18 in FIG. 1, the plurality of carriers 20 are arranged in the circumferential direction of the lower surface plate 14 (actually, the upper surface plate 12 and the lower surface plate 14). Arranged side by side.
The carrier 20 is a disk-like body having a square hole-shaped through-hole that accommodates the glass substrate 22 in the center, and a gear is provided on the outer periphery. The sun gear 16 and the internal gear 18 are provided on the outer periphery. Mesh with. Each carrier 20 holds one glass substrate 22. In FIG. 2, each carrier 20 holds one glass substrate 22, but each carrier may hold a plurality of glass substrates.
上定盤12及び下定盤14は、ガラス基板22の上側及び下側の定盤である。上定盤12及び下定盤14は、ドーナツ状体であり、これらのドーナツ状体の中心軸である定盤中心軸102を中心にして、キャリア20に保持されたガラス基板22をその研磨面(上下両定盤(上定盤12、下定盤14)の研磨面))の間に挟みつつ、同じ方向へ回転する。
上定盤12及び下定盤14は、基板22と対向する面に研磨パッド24が取り付けられている。本明細書において、上下両定盤(上定盤12、下定盤14)の研磨面と言った場合、上下両定盤(上定盤12、下定盤14)に取り付けられた研磨パッド24のパッド表面を指す。
The upper surface plate 12 and the lower surface plate 14 are upper and lower surface plates of the glass substrate 22. The upper surface plate 12 and the lower surface plate 14 are donut-shaped bodies, and the glass substrate 22 held by the carrier 20 is polished on its polishing surface (centered on the surface plate center axis 102 which is the central axis of these donut-shaped bodies). Rotating in the same direction while sandwiched between upper and lower surface plates (polishing surfaces of upper surface plate 12 and lower surface plate 14)).
The upper surface plate 12 and the lower surface plate 14 have a polishing pad 24 attached to the surface facing the substrate 22. In this specification, when the polishing surfaces of the upper and lower surface plates (upper surface plate 12, lower surface plate 14) are referred to, the pads of the polishing pad 24 attached to the upper and lower surface plates (upper surface plate 12, lower surface plate 14). Refers to the surface.
図3は、図1に示す両面研磨装置10における上定盤12の一構成例を示す図である。図3に示すように、上定盤12には、研磨スラリーの供給孔30が設けられている。これにより、両面研磨装置10は、上定盤12及び下定盤14の研磨面に設けられた研磨パッド24と、基板22と、の間に、研磨スラリーを供給する。図3において、上定盤12には、複数の供給孔30が設けられている。なお、図3では、上定盤12における供給孔30を示しているが、上定盤12の研磨面に設けられた研磨パッドにも、図3と同様の供給孔が存在する。
複数の供給孔30は、上定盤12の回転軸側から外側に、かつ上定盤12の回転方向の進行側に向かって、螺旋状に等間隔で配置されている。但し、図3は、上定盤12における研磨スラリー供給孔30の配置の一構成例を示したものであり、上定盤12における研磨スラリー供給孔30の配置はこれに限定されない。
FIG. 3 is a diagram showing a configuration example of the upper surface plate 12 in the double-side polishing apparatus 10 shown in FIG. As shown in FIG. 3, a polishing slurry supply hole 30 is provided in the upper surface plate 12. Thus, the double-side polishing apparatus 10 supplies the polishing slurry between the polishing pad 24 provided on the polishing surfaces of the upper surface plate 12 and the lower surface plate 14 and the substrate 22. In FIG. 3, the upper surface plate 12 is provided with a plurality of supply holes 30. 3 shows the supply holes 30 in the upper surface plate 12, the same supply holes as in FIG. 3 also exist in the polishing pad provided on the polishing surface of the upper surface plate 12.
The plurality of supply holes 30 are arranged at regular intervals in a spiral manner from the rotation axis side of the upper surface plate 12 to the outside and toward the traveling side in the rotation direction of the upper surface plate 12. However, FIG. 3 shows a configuration example of the arrangement of the polishing slurry supply holes 30 in the upper surface plate 12, and the arrangement of the polishing slurry supply holes 30 in the upper surface plate 12 is not limited to this.
太陽歯車16及び内歯歯車18は、キャリア20の外周面と噛み合うギアである。太陽歯車16は、上定盤12及び下定盤14の中心側からキャリア20と接する外歯の歯車であり、上下両定盤(上定盤12及び下定盤14)中心部の空洞12a,14aに備えられ、上下両定盤(上定盤12及び下定盤14)の回転軸である定盤中心軸102と同心の回転軸で回転する。また、内歯歯車18は、上定盤12及び下定盤14の外周側からキャリア20と接する内歯の歯車である。内歯歯車18は、リング状で内側に歯車を有する歯車であり、上下両定盤(上定盤12及び下定盤14)の外周に備えられ、定盤の回転軸である定盤中心軸102と同心の回転軸で回転する。 The sun gear 16 and the internal gear 18 are gears that mesh with the outer peripheral surface of the carrier 20. The sun gear 16 is an externally toothed gear that comes into contact with the carrier 20 from the center side of the upper surface plate 12 and the lower surface plate 14, and is formed in the cavities 12 a and 14 a at the center of the upper and lower surface plates (upper surface plate 12 and lower surface plate 14). It is provided and rotates about a rotation axis concentric with the center axis 102 of the surface plate which is the rotation axis of the upper and lower surface plates (upper surface plate 12 and lower surface plate 14). The internal gear 18 is an internal gear that contacts the carrier 20 from the outer peripheral side of the upper surface plate 12 and the lower surface plate 14. The internal gear 18 is a ring-shaped gear having a gear inside, and is provided on the outer periphery of both upper and lower surface plates (upper surface plate 12 and lower surface plate 14), and a surface plate central axis 102 that is a rotation axis of the surface plate. Rotate on a concentric rotation axis.
そして、太陽歯車16と内歯歯車18は、キャリア20の歯車と噛み合うことによって、キャリア20を回転させる。また、これにより、太陽歯車16及び内歯歯車18は、上定盤12と下定盤14との間において、ガラス基板22を保持するキャリア20を公転及び自転させる。詳しくは後述するが、本明細書でキャリア20の公転といった場合、定盤中心軸102に対してキャリア20が相対的に公転することを指す。なお、両面研磨装置10では、ガラス基板22を保持するキャリア20が公転及び自転することによって、上下両定盤(上定盤12、下定盤14)と、ガラス基板22と、が相対的に移動する。 The sun gear 16 and the internal gear 18 are engaged with the gear of the carrier 20 to rotate the carrier 20. Accordingly, the sun gear 16 and the internal gear 18 revolve and rotate the carrier 20 holding the glass substrate 22 between the upper surface plate 12 and the lower surface plate 14. Although details will be described later, in this specification, when the carrier 20 revolves, it means that the carrier 20 revolves relative to the center axis 102 of the surface plate. In the double-side polishing apparatus 10, both the upper and lower surface plates (upper surface plate 12 and lower surface plate 14) and the glass substrate 22 move relatively as the carrier 20 holding the glass substrate 22 revolves and rotates. To do.
両面研磨装置10を用いてガラス基板22を研磨する場合、上下両定盤(上定盤12、下定盤14)を同心の回転軸(定盤中心軸102)で同一方向に回転させる。また、ガラス基板22を保持するキャリア20を、その中心が上下両定盤(上定盤12、下定盤14)の研磨面上の定盤の回転軸(定盤中心軸102)と一致しない位置に配置して、上下両定盤(上定盤12、下定盤14)の研磨面上で(定盤中心軸102)を定盤の回転軸(定盤中心軸102)を中心に相対的に公転させる。また、キャリア20の中心を回転軸104として、上下両定盤(上定盤12、下定盤14)と例えば同じ方向に回転させて、該キャリア20を上下両定盤(上定盤12、下定盤14)の研磨面上で自転させる。これにより、両面研磨装置10は、ガラス基板20の両面を研磨する。図示した例では、キャリア20が1枚のガラス基板22を保持しているため、ガラス基板22の被研磨面の中心と、それを保持するキャリア20の中心と、が一致している。このため、キャリア20の自転により、ガラス基板22も被研磨面の中心を回転軸104として自転する。これに対し、キャリアが複数のガラス基板を保持する場合は、ガラス基板の被研磨面の中心と、それを保持するキャリアの中心と、が一致しないため、キャリアが自転する際に、ガラス基板は自転しない。
なお、キャリア20の中心(回転軸104)を定盤の回転軸(定盤中心軸102)と一致しない位置に配置するのは、定盤中心軸102に対してキャリア20が相対的に公転させるためである。
When the glass substrate 22 is polished using the double-side polishing apparatus 10, the upper and lower surface plates (upper surface plate 12 and lower surface plate 14) are rotated in the same direction by concentric rotation shafts (surface plate central axis 102). Further, the carrier 20 holding the glass substrate 22 is positioned so that the center thereof does not coincide with the rotation axis of the surface plate (the surface plate center axis 102) on the polishing surface of the upper and lower surface plates (upper surface plate 12, lower surface plate 14). On the polishing surface of both the upper and lower surface plates (upper surface plate 12, lower surface plate 14), the (surface plate center axis 102) is relatively centered on the rotation axis of the surface plate (surface plate center axis 102). Revolve. The carrier 20 is rotated in the same direction as the upper and lower surface plates (upper surface plate 12, lower surface plate 14), for example, in the same direction with the center of the carrier 20 as the rotation axis 104, and the carrier 20 is rotated in both the upper and lower surface plates (upper surface plate 12, lower surface plate). Rotate on the polishing surface of the disc 14). Thereby, the double-side polishing apparatus 10 polishes both surfaces of the glass substrate 20. In the illustrated example, since the carrier 20 holds one glass substrate 22, the center of the surface to be polished of the glass substrate 22 coincides with the center of the carrier 20 that holds the glass substrate 22. For this reason, the glass substrate 22 also rotates with the center of the surface to be polished as the rotation axis 104 by the rotation of the carrier 20. On the other hand, when the carrier holds a plurality of glass substrates, the center of the surface to be polished of the glass substrate does not match the center of the carrier that holds the glass substrate. Does not rotate.
The center of the carrier 20 (rotating shaft 104) is disposed at a position that does not coincide with the rotating shaft of the surface plate (the surface plate central axis 102) so that the carrier 20 revolves relative to the surface plate center axis 102. Because.
図4は、図1に示す両面研磨装置10におけるガラス基板22の公転及び自転の動作について説明する図である。上述したように、両面研磨装置10における太陽歯車16及び内歯歯車18がキャリア20の歯車と噛み合うことによって、キャリア20を回転させる。図4において、キャリア20は、例えば矢印Aで示す方向へ自転する。また、キャリア20は、太陽歯車16と内歯歯車18と間に回転数差を設ける、例えば、内歯歯車18の回転数の方を早くすると、矢印Bで示す方向へ移動することにより、定盤中心軸102の周りを周回する。そして、キャリア20のこの移動と、上下両定盤(上定盤12、下定盤14)自体の回転により、キャリア20は、上下両定盤(上定盤12、下定盤14)の研磨面に対して矢印Bの方向への公転運動を行う。キャリア20の自転の方向や、研磨面に対する相対的な公転の方向は、図4に図示した方向と逆方向に回転させてもよい。また、キャリア20の自転の方向や、研磨面に対する相対的な公転の方向は、互いに方向が同じでも違っていてもよい。 FIG. 4 is a diagram for explaining the revolution and rotation of the glass substrate 22 in the double-side polishing apparatus 10 shown in FIG. As described above, the sun gear 16 and the internal gear 18 in the double-side polishing apparatus 10 are engaged with the gear of the carrier 20 to rotate the carrier 20. In FIG. 4, the carrier 20 rotates in the direction indicated by the arrow A, for example. Further, the carrier 20 is provided with a rotational speed difference between the sun gear 16 and the internal gear 18. For example, when the rotational speed of the internal gear 18 is increased, the carrier 20 moves in the direction indicated by the arrow B. Circulate around the center axis 102 of the panel. Then, by this movement of the carrier 20 and the rotation of the upper and lower surface plates (upper surface plate 12, lower surface plate 14) itself, the carrier 20 is brought into the polished surface of the upper and lower surface plates (upper surface plate 12, lower surface plate 14). On the other hand, a revolving motion in the direction of arrow B is performed. The direction of rotation of the carrier 20 and the direction of revolution relative to the polishing surface may be rotated in the direction opposite to the direction illustrated in FIG. Further, the direction of rotation of the carrier 20 and the direction of revolution relative to the polishing surface may be the same or different.
本発明の基板研磨方法は、両面研磨装置10で用いてEUVL光学基材用ガラス基板を研磨する際に、EUVL光学基材での成膜面(すなわち、該ガラス基板をEULV光学基材として使用する際の成膜面)が、下定盤14の研磨面と対面するようにガラス基板22を挟持することを特徴とする。
上述したように、上定盤12(および上定盤12に取り付けられた研磨パッド)には研磨スラリーの供給孔30が設けられている。研磨スラリーの供給孔30は、多孔体である研磨パッド表面の孔径を示す目的で用いる平均開口径(後述)と比較した場合、(1)供給孔30のほうがはるかに径が大きいこと(供給孔30の径は通常5〜10mm程度である)、(2)研磨パッド表面には凹凸形状が均一に分布しているのに対して、図3に示すように、上定盤12(および上定盤12の研磨面に設けられた研磨パッド)における供給孔30の分布は不均一であること、(3)研磨パッド表面の凹凸形状とは違い、上定盤12(および上定盤12の研磨面に設けられた研磨パッド)に貫通孔として設けられた供給孔30は端部が粗く、両面研磨機を用いてガラス基板を研磨する際に、ガラス基板の被研磨面のうち、上定盤12の研磨面による被研磨面にはピットやスクラッチと呼ばれる凹欠点が生じるおそれがある。
The substrate polishing method of the present invention uses the double-side polishing apparatus 10 to polish a glass substrate for an EUVL optical substrate, and uses the film formation surface on the EUVL optical substrate (that is, the glass substrate as an EULV optical substrate). The glass substrate 22 is sandwiched so that the film forming surface) faces the polished surface of the lower surface plate 14.
As described above, the polishing slurry supply hole 30 is provided in the upper surface plate 12 (and the polishing pad attached to the upper surface plate 12). The supply hole 30 of the polishing slurry is (1) the supply hole 30 is much larger in diameter than the average opening diameter (described later) used for the purpose of indicating the hole diameter of the polishing pad surface which is a porous body (supply hole) The diameter of 30 is usually about 5 to 10 mm.) (2) The uneven surface is uniformly distributed on the surface of the polishing pad. On the other hand, as shown in FIG. The distribution of the supply holes 30 in the polishing pad provided on the polishing surface of the board 12 is non-uniform. (3) Unlike the uneven shape on the surface of the polishing pad, the upper surface plate 12 (and the upper surface plate 12 is polished). The supply hole 30 provided as a through hole in the polishing pad provided on the surface has a rough end, and when polishing the glass substrate using a double-side polishing machine, the upper surface plate among the surfaces to be polished of the glass substrate There are pits and scratches on the surface to be polished by 12 polishing surfaces There is a risk that concave defect called occurs.
研磨後のガラス基板をEULV光学基材として使用する際に、該EUVL光学基材の成膜面にこのような凹欠点が存在すると、反射型マスクや反射型ミラーの製造時に、該EUVL光学基材の成膜面上に形成される反射多層膜の周期構造が乱され、位相欠陥を生じるおそれがある。
位相欠点に関する要求は、EUVLを実施して作製する半導体デバイスによって異なるが、たとえば32nmハーフピッチの半導体デバイスの作製時に使用する反射型マスクや反射型ミラーの場合、球相当直径(SEVD)換算で30nm以上の欠点が、反射多層膜において、10個未満であることが求められる可能性がある。
なお、反射多層膜での位相欠陥の防止という観点からは、該EUVL光学基材の成膜面には深さ3nm超の凹欠点が存在しないことが好ましく、深さ2nm超の凹欠点が存在しないことがより好ましい。
When the polished glass substrate is used as the EULV optical base material, if such a concave defect exists on the film formation surface of the EUVL optical base material, the EUVL optical base is produced during the production of the reflective mask or the reflective mirror. The periodic structure of the reflective multilayer film formed on the film-forming surface of the material may be disturbed to cause phase defects.
The requirements regarding the phase defects differ depending on the semiconductor device manufactured by performing EUVL. For example, in the case of a reflective mask or a reflective mirror used when manufacturing a semiconductor device with a 32 nm half pitch, it is 30 nm in terms of sphere equivalent diameter (SEVD). The above disadvantages may be required to be less than 10 in the reflective multilayer film.
From the viewpoint of preventing phase defects in the reflective multilayer film, it is preferable that there is no concave defect with a depth of more than 3 nm, and there is a concave defect with a depth of more than 2 nm on the film formation surface of the EUVL optical substrate. More preferably not.
本発明の基板研磨方法では、両面研磨装置10で用いてEUVL光学基材用ガラス基板を研磨する際に、EUVL光学基材での成膜面(すなわち、該ガラス基板をEULV光学基材として使用する際の成膜面)が、下定盤14の研磨面と対面するようにガラス基板22を挟持するため、EUVL光学基材での成膜面が下定盤14の研磨面によって研磨される。下定盤14の研磨面には研磨スラリーの供給孔が存在しないため、研磨後のガラス基板において、EUVL光学基材での成膜面に凹欠点が生じることが抑制される。この結果、研磨後のガラス基板をEUVL光学基材として使用した際に、該EUVL光学基材の成膜面上に形成される反射多層膜に位相欠陥を生じることが抑制される。 In the substrate polishing method of the present invention, when the glass substrate for EUVL optical substrate is polished by using the double-side polishing apparatus 10, the film formation surface on the EUVL optical substrate (that is, the glass substrate is used as the EULV optical substrate). Since the glass substrate 22 is sandwiched so that the film forming surface) faces the polishing surface of the lower surface plate 14, the film forming surface on the EUVL optical base material is polished by the polishing surface of the lower surface plate 14. Since there are no polishing slurry supply holes on the polishing surface of the lower surface plate 14, it is possible to suppress the formation of concave defects on the film formation surface of the EUVL optical base material in the polished glass substrate. As a result, when the polished glass substrate is used as the EUVL optical substrate, it is possible to suppress the occurrence of phase defects in the reflective multilayer film formed on the film formation surface of the EUVL optical substrate.
なお、特許文献3〜7に記載の発明において、両面研磨機を用いてガラス基板を研磨する際に、上定盤によるガラス基板の被研磨面に研磨スラリー供給孔に起因する凹欠点が生じることが認識されていなかったのは、反射多層膜での位相欠陥の発生原因として、反射多層膜の成膜時に膜中に混入する異物が重視されていたためと考えられる。その後、反射多層膜の成膜技術の向上により、膜中に混入する異物は減少したことにより、研磨後の成膜面に生じた凹欠点が、反射多層膜での位相欠陥の発生原因として重要であることを本願発明者は見出した。また、EUVLの検証が進むにつれ、反射型マスクや反射型ミラーに要求される位相欠陥サイズはより小さくなり、研磨後の成膜面に生じた微小サイズの凹欠点が反射多層膜での位相欠陥の発生原因として重要となってきた。 In the inventions described in Patent Documents 3 to 7, when a glass substrate is polished using a double-side polishing machine, a concave defect caused by the polishing slurry supply hole occurs on the surface to be polished of the glass substrate by the upper surface plate. This is probably because the foreign matter mixed in the reflective multilayer film was emphasized as a cause of the occurrence of the phase defect in the reflective multilayer film. Later, due to improvements in the technology for forming reflective multilayer films, the number of foreign substances mixed in the film has decreased, so the concave defects that occur on the film-formed surface after polishing are important causes of phase defects in the reflective multilayer film. The present inventors have found that Further, as EUVL verification progresses, the phase defect size required for the reflective mask and the reflective mirror becomes smaller, and the microscopic concave defect generated on the film-formed surface after polishing is a phase defect in the reflective multilayer film. It has become important as a cause of occurrence.
本発明のガラス基板研磨方法を実施する場合、以下の点に留意する必要がある。
研磨終了時において、ガラス基板の下面(すなわち、EUVL光学基材での成膜面)は、自重によって下定盤の研磨面に吸着するおそれがある。このような吸着が起こると、下定盤の研磨面からガラス基板を取り外す際に、ガラス基板の下面(すなわち、EUVL光学基材での成膜面)に傷が生じるおそれがある。
このため、本発明のガラス基板研磨方法を実施する際には、下定盤の研磨面へのガラス基板の吸着が起こらないようにする必要がある。または、ガラス基板の下面の吸着が起こった場合であっても、下定盤の研磨面からガラス基板を取り外す際に、ガラス基板の下面(すなわち、EUVL光学基材での成膜面)に傷が生じないようにする必要がある。
When carrying out the glass substrate polishing method of the present invention, it is necessary to pay attention to the following points.
At the end of polishing, the lower surface of the glass substrate (that is, the film formation surface of the EUVL optical base material) may be adsorbed to the polishing surface of the lower surface plate by its own weight. When such adsorption occurs, when the glass substrate is removed from the polished surface of the lower surface plate, the lower surface of the glass substrate (that is, the film formation surface on the EUVL optical base material) may be damaged.
For this reason, when carrying out the glass substrate polishing method of the present invention, it is necessary to prevent the glass substrate from adsorbing to the polishing surface of the lower surface plate. Or, even when the lower surface of the glass substrate is attracted, when the glass substrate is removed from the polished surface of the lower surface plate, the lower surface of the glass substrate (that is, the film formation surface on the EUVL optical base material) is scratched. It is necessary to prevent it from occurring.
下定盤の研磨面へのガラス基板の吸着が起こらないようにするためには、研磨終了時において、上定盤の研磨面にガラス基板の上面が吸着するようにすればよい。定盤(上定盤、下定盤)の研磨面と、ガラス基板の両主表面と、の吸着のしやすさは、両者の接触面積に影響され、両者の接触面積が大きいほど吸着が起こりやすい。したがって、上定盤の研磨面とガラス基板との接触面積を、下定盤の研磨面とガラス基板との接触面積よりも大きくすれば、上定盤の研磨面にガラス基板が吸着することになる。
上定盤の研磨面とガラス基板との接触面積を大きくする方法としては、たとえば研磨パッドとして、後述するスウェード系研磨パッドを使用する場合には、上定盤に取り付ける研磨パッドの平均開口径を、下定盤に取り付ける研磨パッドの平均開口径よりも小さくすればよい。なお、研磨パッドの平均開口径については後述する。
また、上定盤の研磨面とガラス基板との接触面積を大きくする方法としては、上定盤の研磨面に取り付ける研磨パッドを、下定盤の研磨面に取り付けられる研磨パッドよりも軟質の研磨パッドとする方法がある。
In order to prevent the glass substrate from adsorbing to the polishing surface of the lower surface plate, the upper surface of the glass substrate may be adsorbed to the polishing surface of the upper surface plate at the end of polishing. The ease of adsorption between the polishing surface of the surface plate (upper surface plate, lower surface plate) and both main surfaces of the glass substrate is affected by the contact area between the two, and the greater the contact area between the both, the easier the adsorption occurs. . Therefore, if the contact area between the polishing surface of the upper surface plate and the glass substrate is larger than the contact area between the polishing surface of the lower surface plate and the glass substrate, the glass substrate is adsorbed on the polishing surface of the upper surface plate. .
As a method for increasing the contact area between the polishing surface of the upper surface plate and the glass substrate, for example, when using a suede type polishing pad described later as the polishing pad, the average opening diameter of the polishing pad attached to the upper surface plate is set. What is necessary is just to make smaller than the average opening diameter of the polishing pad attached to a lower surface plate. The average opening diameter of the polishing pad will be described later.
As a method of increasing the contact area between the polishing surface of the upper surface plate and the glass substrate, the polishing pad attached to the polishing surface of the upper surface plate is a softer polishing pad than the polishing pad attached to the polishing surface of the lower surface plate. There is a method.
また、下定盤の研磨面からガラス基板を取り外す際に、ガラス基板の下面(すなわち、EUVL光学基材での成膜面)に傷が生じないようにするためには、研磨終了後、すみやかにガラス基板を取り外す方法がある。研磨終了から時間が経過すると、下定盤の研磨面と、ガラス基板の下面と、の間に存在する研磨スラリーが乾燥して、より強固に吸着するからである。目安としては、研磨終了後、5分以内、より好ましくは3分以内、さらに好ましくは、30秒以内にガラス基板を取り外すことが好ましい。
また、下定盤の研磨面と、ガラス基板ガラス基板の下面と、の間に窒素ガス等を吹き付けて、両者の間に存在する研磨スラリーを強制的に除去して、吸着力を下げることで、ガラス基板の下面(すなわち、EUVL光学基材での成膜面)に傷が生じないようにすることもできる。
In addition, when removing the glass substrate from the polishing surface of the lower surface plate, in order to prevent scratching on the lower surface of the glass substrate (that is, the film formation surface on the EUVL optical base material), immediately after the polishing is completed, There is a method of removing the glass substrate. This is because the polishing slurry existing between the polishing surface of the lower platen and the lower surface of the glass substrate dries and adsorbs more firmly when time elapses from the end of polishing. As a guide, it is preferable to remove the glass substrate within 5 minutes after polishing, more preferably within 3 minutes, and even more preferably within 30 seconds.
In addition, by blowing nitrogen gas or the like between the polishing surface of the lower surface plate and the lower surface of the glass substrate glass substrate, forcibly removing the polishing slurry existing between the two, lowering the adsorption power, It is also possible to prevent scratches on the lower surface of the glass substrate (that is, the film formation surface of the EUVL optical base material).
本発明の基板研磨方法における好ましい態様を以下に示す。 Preferred embodiments of the substrate polishing method of the present invention are shown below.
[基板]
本発明の基板研磨方法を用いて研磨するガラス基板は、EUVL光学基材用ガラス基板であることから、該ガラス基板を構成するガラスは、熱膨張係数が小さくかつそのばらつきの小さいガラスであることが好ましい。具体的には20℃における熱膨張係数が0±30ppb/℃の低膨張ガラスが好ましく、20℃における熱膨張係数が0±10ppb/℃の超低膨張ガラスがより好ましく、20℃における熱膨張係数が0±5ppb/℃の超低膨張ガラスがさらに好ましい。
上記低膨張ガラスおよび超低膨張ガラスとしては、SiO2を主成分とするガラス、典型的には石英ガラスが使用できる。具体的には例えばSiO2を主成分とし1〜12質量%のTiO2を含有する合成石英ガラス、ULE(登録商標:コーニングコード7972)を挙げることができる。ガラス基板は通常四角形状の板状体で研磨されるが、形状はこれに限定されない。
[substrate]
Since the glass substrate polished using the substrate polishing method of the present invention is a glass substrate for EUVL optical substrate, the glass constituting the glass substrate is a glass having a small coefficient of thermal expansion and a small variation. Is preferred. Specifically, a low expansion glass having a thermal expansion coefficient at 20 ° C. of 0 ± 30 ppb / ° C. is preferable, an ultra low expansion glass having a thermal expansion coefficient at 20 ° C. of 0 ± 10 ppb / ° C. is more preferable, and a thermal expansion coefficient at 20 ° C. Is more preferably an ultra low expansion glass having a 0 ± 5 ppb / ° C.
As the low expansion glass and ultra low expansion glass, glass mainly composed of SiO 2 , typically quartz glass can be used. Synthetic quartz glass in particular containing 1 to 12 wt% of TiO 2 as a main component, for example, SiO 2, ULE (registered trademark Corning Code 7972) can be mentioned. The glass substrate is usually polished with a rectangular plate-like body, but the shape is not limited thereto.
[研磨スラリー]
上述したように、本発明における研磨スラリーとは、研磨粒子を含む流体である。
研磨粒子としては、コロイダルシリカ又は酸化セリウムなどが好ましい。コロイダルシリカを使用した場合には、より精密にガラス基板を研磨することが可能になり、その結果、より良好な精度で、凹状の欠陥が低減された又は除去されたガラス基板を得ることができるので、特に好ましい。
[Polishing slurry]
As described above, the polishing slurry in the present invention is a fluid containing abrasive particles.
As the abrasive particles, colloidal silica or cerium oxide is preferable. When colloidal silica is used, it becomes possible to polish a glass substrate more precisely, and as a result, a glass substrate in which concave defects are reduced or removed can be obtained with better accuracy. Therefore, it is particularly preferable.
コロイダルシリカを用いる場合、平均一次粒子径は、好ましくは、5nm以上100nm以下である。より好ましくは10nm以上50nm以下である。ここで、コロイダルシリカの平均一次粒子径が、5nm以上である場合には、ガラス基板の研磨効率を向上させることが可能になる。一方、コロイダルシリカの平均一次粒子径が、100nm以下である場合には、研磨スラリーを用いて研磨された基板の表面粗さを低減することが可能になる。 When colloidal silica is used, the average primary particle size is preferably 5 nm or more and 100 nm or less. More preferably, it is 10 nm or more and 50 nm or less. Here, when the average primary particle diameter of colloidal silica is 5 nm or more, it becomes possible to improve the polishing efficiency of a glass substrate. On the other hand, when the average primary particle diameter of colloidal silica is 100 nm or less, it becomes possible to reduce the surface roughness of the substrate polished with the polishing slurry.
研磨スラリーにおけるコロイダルシリカの含有率は、好ましくは、5質量%以上40質量%以下である。より好ましくは、10質量%以上30質量%以下である。研磨スラリーにおけるコロイダルシリカの含有率が、5質量%以上である場合には、ガラス基板の研磨効率を向上させることが可能になる。一方、研磨スラリーにおけるコロイダルシリカの含有率が、40質量%以下である場合には、研磨されたガラス基板の洗浄の効率を向上させることが可能になる。 The content of colloidal silica in the polishing slurry is preferably 5% by mass or more and 40% by mass or less. More preferably, it is 10 mass% or more and 30 mass% or less. When the content of colloidal silica in the polishing slurry is 5% by mass or more, the polishing efficiency of the glass substrate can be improved. On the other hand, when the content of the colloidal silica in the polishing slurry is 40% by mass or less, it is possible to improve the cleaning efficiency of the polished glass substrate.
研磨スラリーにおける流体とは、研磨粒子の分散媒体である。分散媒としては、水、有機溶剤が挙げられ、水が好ましい。 The fluid in the polishing slurry is a dispersion medium of abrasive particles. Examples of the dispersion medium include water and organic solvents, and water is preferable.
上記の研磨粒子および該研磨粒子の分散媒体を含む研磨スラリーとしては、pHが8以下のコロイダルシリカ水溶液を用いることが好ましい。
研磨粒子が凝集すると、ガラス基板上に付着しやすくなると考えられるが、研磨スラリーのpHが8を超えると、研磨粒子が付着していない部分のガラス基板の表面が、研磨スラリーによって溶解し、凸状の欠陥を生じさせるおそれがある。研磨スラリーのpHが8以下であることにより、このような凸状の欠陥は生じにくいものと考えられる。研磨スラリーのpHは7以下であることがより好ましい。pHは1〜4であることがさらに好ましい。
研磨スラリーのpHは、無機酸及び/又は有機酸を用い調整できる。例えば、無機酸としては、硝酸、硫酸、塩酸、過塩素酸、リン酸などが挙げられ、硝酸が好ましい。有機酸としては、シュウ酸、クエン酸などが挙げられる。
As the polishing slurry containing the abrasive particles and the dispersion medium of the abrasive particles, it is preferable to use an aqueous colloidal silica solution having a pH of 8 or less.
When the abrasive particles are aggregated, it is considered that the abrasive particles are likely to adhere to the glass substrate. However, when the pH of the polishing slurry exceeds 8, the surface of the glass substrate where the abrasive particles are not attached is dissolved by the polishing slurry and becomes convex. There is a risk of causing defects. It is considered that such convex defects are less likely to occur when the pH of the polishing slurry is 8 or less. The pH of the polishing slurry is more preferably 7 or less. More preferably, the pH is 1-4.
The pH of the polishing slurry can be adjusted using an inorganic acid and / or an organic acid. For example, examples of the inorganic acid include nitric acid, sulfuric acid, hydrochloric acid, perchloric acid, phosphoric acid, and the like, and nitric acid is preferable. Examples of the organic acid include oxalic acid and citric acid.
[研磨パッド]
上下両定盤の研磨面には研磨パッドが設けられていることが好ましい。研磨パッドとしては、不織布などの基布に、ポリウレタン樹脂を含浸させ、湿式凝固処理を行って得られたポリウレタン樹脂発泡層を有する研磨パッドなどが挙げられる。研磨パッドとしては、スウェード系研磨パッドが好ましい。
スウェード系研磨パッドにおけるナップ層の厚さは0.3〜1.0mm程度が実用上で好ましい。また、スウェード系研磨パッドとしては、適度の圧縮弾性率を有する軟質の樹脂発泡体が好ましく使用でき、具体的には例えばエーテル系、エステル系、カーボネート系などの樹脂発泡体が挙げられる。
[Polishing pad]
It is preferable that polishing pads are provided on the polishing surfaces of the upper and lower surface plates. Examples of the polishing pad include a polishing pad having a polyurethane resin foam layer obtained by impregnating a base fabric such as a nonwoven fabric with a polyurethane resin and performing wet coagulation treatment. As the polishing pad, a suede polishing pad is preferable.
The thickness of the nap layer in the suede polishing pad is preferably about 0.3 to 1.0 mm in practical use. As the suede type polishing pad, a soft resin foam having an appropriate compression modulus can be preferably used, and specific examples include resin foams such as ether, ester and carbonate.
スウェード系研磨パッドは、平均開口径が5〜100μmであることが好ましく、5〜40μmであることがより好ましく、5〜30μmであることがさらに好ましく、10〜25μmであると特に好ましい。
ここで、研磨パッドの平均開口径とは、多孔体である研磨パッド表面の孔径を示す目的で用いる平均開口径を指し、後述する方法で算出することができる。
研磨パッドの平均開口径が100μm超であると、研磨荷重の分布が生じ、所定の研磨品質を維持することが困難になるおそれがある。また、研磨パッドの平均開口径が5μm未満であると、研磨スラリーを保持してムラなく研磨することができなくなるおそれがある。
The suede polishing pad preferably has an average opening diameter of 5 to 100 μm, more preferably 5 to 40 μm, still more preferably 5 to 30 μm, and particularly preferably 10 to 25 μm.
Here, the average opening diameter of the polishing pad refers to an average opening diameter used for the purpose of indicating the hole diameter of the surface of the polishing pad, which is a porous body, and can be calculated by the method described later.
When the average opening diameter of the polishing pad is more than 100 μm, a distribution of polishing load is generated, and it may be difficult to maintain a predetermined polishing quality. Further, if the average opening diameter of the polishing pad is less than 5 μm, there is a possibility that the polishing slurry cannot be retained and polished uniformly.
研磨パッドの平均開口径は、CCDカメラを用いて200倍の倍率でパッド表面の画像を取り込み、得られた画像を2値化処理して算出することができる。具体的には、ドーナツ状の研磨パッドの場合、研磨パッドの任意の半径方向におけるパッド内縁から20mmの部分をx、外縁から20mmの部分をy、およびこれらx、yの中間部分をzとし、これら3箇所の各開口径を求め、平均値を算出したものが平均開孔径である。なお、ドーナツ状でない研磨パッドの場合(中心部分に空洞の無い円形の研磨パッドの場合)は、xをパッド中心から20mmの部分とする。 The average opening diameter of the polishing pad can be calculated by taking an image of the pad surface at a magnification of 200 times using a CCD camera and binarizing the obtained image. Specifically, in the case of a donut-shaped polishing pad, a portion 20 mm from the inner edge of the pad in an arbitrary radial direction of the polishing pad is x, a portion 20 mm from the outer edge is y, and an intermediate portion of these x and y is z. What calculated | required each opening diameter of these three places, and computed the average value is an average hole diameter. In the case of a polishing pad that is not doughnut-shaped (in the case of a circular polishing pad having no cavity at the center), x is a portion 20 mm from the center of the pad.
上述したように、研磨終了後、上定盤の研磨面にガラス基板が吸着させるためには、下定盤に取り付ける研磨パッドの平均開口径と、上定盤に取り付ける研磨パッドの平均開口径と、の差(すなわち、下定盤の研磨パッドの平均開口径 − 上定盤の研磨パッドの平均開口径)が0.01μm以上、より好ましくは1μ以上、さらに好ましくは10μm以上、特に好ましくは20μm以上となるように両者の差を設定すればよい。 As described above, after the polishing is completed, in order for the glass substrate to be adsorbed to the polishing surface of the upper surface plate, the average opening diameter of the polishing pad attached to the lower surface plate, the average opening diameter of the polishing pad attached to the upper surface plate, Difference (that is, the average opening diameter of the polishing pad of the lower surface plate−the average opening diameter of the polishing pad of the upper surface plate) is 0.01 μm or more, more preferably 1 μm or more, further preferably 10 μm or more, and particularly preferably 20 μm or more. What is necessary is just to set the difference of both so that it may become.
スウェード系研磨パッドは、パッド表面の最大山と最小山の高低差(以下、最大高さ差Rhとする)が50μm以下であることが好ましい。この最大高さ差Rhは30μm以下がより好ましく、さらに好ましくは20μm以下である。定盤に取り付けられた直後の研磨パッドのパッド表面は、一見したところでは平坦を呈しているが、実際には微細な凹凸が存在する。このような凹凸における最大山(高さが最も高い山)と最小山(高さが最も低い山)との高低差として規定される。
なお、上記最大高さ差Rhは、例えば表面粗さ測定装置を用いて求めることができる。具体的には、上記した平均開口径の測定箇所と同じ研磨パッドの半径方向の3箇所x、y、zの研磨面粗さを、表面粗さ測定装置を使用して測定して各測定箇所のそれぞれの最大高さ差Rhを求め、それらの中の最大のものを該研磨パッドの最大高さ差Rhとすることができる。
The suede polishing pad preferably has a height difference between the maximum peak and the minimum peak on the pad surface (hereinafter referred to as the maximum height difference Rh) of 50 μm or less. The maximum height difference Rh is more preferably 30 μm or less, and further preferably 20 μm or less. The pad surface of the polishing pad immediately after being attached to the surface plate is flat at first glance, but actually there are fine irregularities. It is defined as the height difference between the maximum mountain (the highest mountain) and the minimum mountain (the lowest mountain) in such irregularities.
In addition, the said maximum height difference Rh can be calculated | required, for example using a surface roughness measuring apparatus. Specifically, the polishing surface roughness at three locations x, y, and z in the radial direction of the polishing pad that is the same as the measurement location of the average opening diameter described above is measured using a surface roughness measuring device, and each measurement location is measured. The maximum height difference Rh can be obtained, and the maximum of them can be used as the maximum height difference Rh of the polishing pad.
一般に、新規の研磨パッドはパッド表面の凹凸が尖鋭な先部を有しさらに高さの不揃いの程度が大きいため、パッド表面の最大高さ差Rhは60〜100μm程度となっている。このような最大高さ差Rhを有する研磨パッドを使用した場合、研磨荷重の分布や研磨材の偏りが生じやすく、また凹凸の不揃いが支障してガラス基板を満足に研磨することが得られないことが懸念される。
すなわち、最大高さ差Rhの大きいパッド表面を有する研磨パッドでガラス基板を研磨した場合、研磨荷重の分布や研磨粒子に偏りが生じるために凹状欠点が生じやすく、かつ均一な研磨が得られ難くい。また、突出度の高い凹凸が主体にガラス基板に接触して研磨が行われるため、研磨パッドとガラス基板との接触部が少なくなり、研磨効率が低下してしまうという問題も生じる。
パッド表面の最大高さ差Rhが50μm以下であると、研磨荷重を小さくしても所定の研磨効率を維持し、また凹状欠点を抑制しながらガラス基板を均一かつ高精緻に研磨できる。
In general, since a new polishing pad has a sharp tip on the surface of the pad and a large degree of unevenness of the height, the maximum height difference Rh of the pad surface is about 60 to 100 μm. When a polishing pad having such a maximum height difference Rh is used, the distribution of the polishing load and the unevenness of the polishing material are likely to occur, and the unevenness of the irregularities is hindered, so that the glass substrate cannot be satisfactorily polished. There is concern.
That is, when a glass substrate is polished with a polishing pad having a pad surface having a large maximum height difference Rh, the distribution of polishing load and the unevenness of polishing particles are likely to cause concave defects, and uniform polishing is difficult to obtain. Yes. Further, since polishing is performed mainly with unevenness having a high degree of protrusion in contact with the glass substrate, there is a problem that the contact portion between the polishing pad and the glass substrate is reduced and the polishing efficiency is lowered.
When the maximum height difference Rh on the pad surface is 50 μm or less, a predetermined polishing efficiency can be maintained even when the polishing load is reduced, and the glass substrate can be polished uniformly and highly precisely while suppressing concave defects.
新規の研磨パッドを使用する場合、研磨パッドのパッド表面をドレッシング加工することによって、パッド表面の最大高さ差Rhを50μm以下にすることができる。ここでドレッシング加工とは、研磨パッドのパッド表面をドレス板で研磨することによって、パッド表面の尖鋭な先部を除去し、凹凸の高さをより均一な状態とする処理を指す。
ドレッシング加工は、図示した両面研磨装置10のキャリア20にガラス基板22の代わりにドレス板を設置し、研磨を実施することで容易に実施できる。
ドレッシング加工に用いるドレス板としては平坦度の良い基板にダイヤ微粒子を接着したものが好ましく使用できる。具体的には電着ダイヤ、メタルボンドダイヤ、レジンボンドダイヤ、ビトリファイドボンドダイヤ等が挙げられる。なかでも、電着ダイヤは表面の凹凸を小さく抑えやすく、またダイヤの脱落が稀少であり、脱落ダイヤが研磨パッドに残存してガラス基板の被研磨面に引掻き傷を発生させることが少ないので好ましい。上記基板の材質としては耐薬品性の高いSUSが優れている。その平坦度は10μm以下であることが好ましい。
基板に接着するダイヤ微粒子のサイズは限定されないが、ドレッシング加工の作業性と所望の最大高さ差Rhが得られるように#100〜#1200メッシュのものが好ましく、#300〜#1000メッシュのものがより好ましく、#300〜#600メッシュのものが特に好ましい。
また、ドレス板のサイズや形状は、両面研磨装置10のキャリア20に対応して適宜決めることができ限定されない。例えば、形状としては円形または正方形が好ましく、サイズは30〜700mmの範囲を目安に径または辺の長さを決めることができる。
When a new polishing pad is used, the maximum height difference Rh of the pad surface can be reduced to 50 μm or less by dressing the pad surface of the polishing pad. Here, the dressing process refers to a process of removing the sharp tip of the pad surface by polishing the pad surface of the polishing pad with a dress plate and making the height of the unevenness more uniform.
The dressing can be easily performed by installing a dressing plate instead of the glass substrate 22 on the carrier 20 of the double-side polishing apparatus 10 shown in the figure and performing polishing.
As a dressing plate used for dressing processing, a substrate obtained by bonding diamond fine particles to a substrate having good flatness can be preferably used. Specific examples include electrodeposition diamond, metal bond diamond, resin bond diamond, and vitrified bond diamond. Among them, the electrodeposited diamond is preferable because it is easy to suppress the unevenness of the surface to be small, the diamond is rarely dropped, and the diamond is not likely to remain on the polishing pad and cause scratches on the polished surface of the glass substrate. . As the material of the substrate, SUS having high chemical resistance is excellent. The flatness is preferably 10 μm or less.
The size of the diamond fine particles to be bonded to the substrate is not limited, but is preferably # 100 to # 1200 mesh, and # 300 to # 1000 mesh so that the dressing workability and the desired maximum height difference Rh can be obtained. Are more preferable, and those of # 300 to # 600 mesh are particularly preferable.
Further, the size and shape of the dress plate can be appropriately determined according to the carrier 20 of the double-side polishing apparatus 10 and are not limited. For example, the shape is preferably a circular shape or a square shape, and the size or the length of the side can be determined with the size in the range of 30 to 700 mm.
本発明の基板研磨方法を実施する際、上下両定盤の研磨面による研磨荷重を1〜120g/cm2とすることが、ガラス基板を凹状欠点が少なく表面平滑性の優れる表面に研磨できることから好ましい。研磨荷重が1g/cm2未満では、研磨パッドの荷重制御が困難になるとともに、研磨効果が実質的に得られなくなるおそれがある。また、120g/cm2より大きい研磨荷重では、凹状欠点の発生を抑え表面粗さの改善を図ることが困難になる。
また、本発明の基板研磨方法の実施時における研磨荷重は一定であってもよく、徐々にまたは段階的に変化させてもよい。例えば、研磨開始時は大きい荷重とし、徐々にまたは段階的に研磨荷重を下げ、研磨終了時は小さい荷重としてもよい。逆に、研磨開始時は小さい荷重とし、徐々にまたは段階的に研磨荷重を上げ、研磨終了時は大きい荷重としてもよい。
例えば、研磨荷重50〜120g/cm2で、好ましくは、50〜100g/cm2で研磨を開始し、徐々にまたは段階的に研磨荷重を下げ、研磨終了時の荷重を5〜50g/cm2で、より好ましくは、5〜20g/cm2とすることができる。また、逆に、研磨開始時は荷重を5〜50g/cm2、より好ましくは、5〜20g/cm2として、徐々にまたは段階的に研磨荷重を上げ、荷重50〜120g/cm2で、好ましくは、50〜100g/cm2で研磨を終了してもよい。
また、例えば、50〜120g/cm2、好ましくは、50〜100g/cm2の一定荷重で研磨することもできる。
When carrying out the substrate polishing method of the present invention, it is possible to polish the glass substrate to a surface with few concave defects and excellent surface smoothness by setting the polishing load by the polishing surfaces of the upper and lower surface plates to 1 to 120 g / cm 2. preferable. When the polishing load is less than 1 g / cm 2, it is difficult to control the load of the polishing pad and the polishing effect may not be substantially obtained. Further, when the polishing load is larger than 120 g / cm 2 , it becomes difficult to suppress the generation of concave defects and improve the surface roughness.
Further, the polishing load at the time of carrying out the substrate polishing method of the present invention may be constant or may be changed gradually or stepwise. For example, the load may be a large load at the start of polishing, the polishing load may be reduced gradually or stepwise, and the load may be reduced at the end of polishing. Conversely, the load may be small at the start of polishing, the polishing load may be increased gradually or stepwise, and the load may be increased at the end of polishing.
For example, polishing is started at a polishing load of 50 to 120 g / cm 2 , preferably 50 to 100 g / cm 2 , the polishing load is gradually or stepwise reduced, and the load at the end of polishing is 5 to 50 g / cm 2. More preferably, it can be set to 5 to 20 g / cm 2 . Conversely, the polishing start time is 5 to 50 g / cm 2 load, more preferably, a 5 to 20 g / cm 2, and gradually or stepwise increasing the polishing load, a load 50 to 120 / cm 2, Preferably, the polishing may be terminated at 50 to 100 g / cm 2 .
Further, for example, polishing can be performed with a constant load of 50 to 120 g / cm 2 , preferably 50 to 100 g / cm 2 .
本発明の基板研磨方法は、ガラス基板を研磨度の異なる複数の研磨工程で研磨するときの最後に行う仕上げ研磨として特に適している。このためガラス基板は、本発明の方法で研磨する前にあらかじめ所定の厚さに粗研磨し、端面研磨と面取り加工を行い、更にその両主表面を表面粗さ、および、平坦度が一定以下になるように予備研磨しておくことが好ましい。予備研磨方法は限定されないで公知の方法によってできる。例えば、複数の両面ラップ研磨機を連続して設置し、研磨材や研磨条件を変えながら該研磨機で順次研磨することにより、ガラス基板の両主表面を所定の表面粗さおよび平坦度に予備研磨できる。予備研磨後の表面粗さ(Rms)としては、1nm以下が好ましく、0.5nm以下がより好ましい。予備研磨後の平坦度(P−V値)としては、1μm以下が好ましく、0.5μm以下がより好ましい。さらに好ましくは0.2μmである。 The substrate polishing method of the present invention is particularly suitable as final polishing performed at the end when a glass substrate is polished in a plurality of polishing steps having different polishing degrees. For this reason, the glass substrate is roughly polished to a predetermined thickness before being polished by the method of the present invention, end face polishing and chamfering are performed, and the surface roughness and flatness of both main surfaces are not more than a certain level. It is preferable to perform preliminary polishing so that The preliminary polishing method is not limited and can be performed by a known method. For example, a plurality of double-sided lapping machines are installed in succession, and the two main surfaces of the glass substrate are preliminarily maintained at a predetermined surface roughness and flatness by sequentially polishing with the polishing machine while changing the polishing material and polishing conditions. Can be polished. The surface roughness (Rms) after preliminary polishing is preferably 1 nm or less, and more preferably 0.5 nm or less. The flatness (PV value) after preliminary polishing is preferably 1 μm or less, and more preferably 0.5 μm or less. More preferably, it is 0.2 μm.
以下に、実施例を用いて本発明を詳細に説明する。ただし、本発明はこれに限定されるものではない。
火炎加水分解法で製造されたTiO2を7質量%含有する合成石英ガラスのインゴットを、縦153mm×横153mm×厚さ6.75mmの板状に内周刃スライサーを用いて切断し、60枚の合成石英ガラスの板材試料(以下、「試料基材」という)を作製した。さらに、これら試料基材を市販のダイアモンド砥石を用い、縦、横の外形寸法が152mm、面取り幅が0.2〜0.4mmになるよう面取り加工した。
次に、この試料基材を両面ラップ機(スピードファム社製)を使用して厚さが6.51mmになるまでその主表面を研磨したあと、両面ポリッシュ機(スピードファム社製)を使用して、表面粗さ(Rms)が約0.8nm、平坦度(P−V値)が約0.6μmになるように予備研磨した。試料基材の外周も研磨して端面を表面粗さRa0.05μmに鏡面加工した。
Hereinafter, the present invention will be described in detail with reference to examples. However, the present invention is not limited to this.
A synthetic quartz glass ingot containing 7% by mass of TiO 2 produced by a flame hydrolysis method was cut into a plate shape of 153 mm in length, 153 mm in width, and 6.75 mm in thickness using an inner peripheral blade slicer, 60 sheets A synthetic quartz glass plate material sample (hereinafter referred to as “sample substrate”) was prepared. Further, these sample substrates were chamfered using a commercially available diamond grindstone so that the vertical and horizontal outer dimensions were 152 mm and the chamfered width was 0.2 to 0.4 mm.
Next, after polishing the main surface of the sample substrate using a double-sided lapping machine (made by Speedfam) until the thickness becomes 6.51 mm, a double-sided polishing machine (made by Speedfam) is used. Then, preliminary polishing was performed so that the surface roughness (Rms) was about 0.8 nm and the flatness (P-V value) was about 0.6 μm. The outer periphery of the sample substrate was also polished, and the end surface was mirror-finished to a surface roughness Ra of 0.05 μm.
次いで、予備研磨した30枚の試料基材を15枚づつ実施例1、比較例1に分け、図示した両面研磨装置10を用いて、試料基材の両主表面を仕上げ研磨した。実施例1では、試料基材の両主表面のうち、評価対象面を研磨スラリーの供給孔が設けられてない下定盤14の研磨面(下定盤14に取り付けられた研磨パッド24のパッド面)と対面するように設置して仕上げ研磨を実施した。比較例1では、評価対象面を研磨スラリーの供給孔30が設けられた上定盤12の研磨面(上定盤12に取り付けられた研磨パッド24のパッド面)と対面するように設置して仕上げ研磨を実施した。使用した研磨スラリーはすべて同一であり、平均一次粒子径10〜20nmのコロイダルシリカを純水に20質量%含有させた研磨スラリーに、硝酸を添加しpHを2に調整して用いた。また、研磨パッドはスウェード系パッドを使用し、試料基材の仕上げ研磨に先がけて電着ダイヤでドレッシング加工したものを用いた。仕上げ研磨の研磨条件は以下の通りである。
(研磨条件)
研磨機 :両面研磨装置
研磨パッド :スウェード系研磨パッド
Rh :3μm
平均開口径 :12μm
研磨定盤回転数 :35rpm
研磨荷重 :80g/cm2
研磨時間 :50分
希釈水 :純水(比抵抗値4.2MΩ・cm、0.2μm以上異物濾過)
スラリー流量 :10L/min
上記条件で試料基材を仕上げ研磨したあと、第一槽目が界面活性剤溶液による洗浄槽、これ以降を超純水によるすすぎ槽とIPAによる乾燥槽で構成した多段式自動洗浄機で洗浄した。この洗浄した試料基材の表面対象面をフォトマスク用表面欠点検査機(レーザーテック社製M1350A)で検査し、142mm×142mm内における凹欠点数を実施例1および比較例1で検出した。検査はそれぞれ15枚全てについて行い、凹欠点の検出数を比較した。その結果、実施例1では15枚全てで凹欠点は検出されなかった。一方、比較例では凹欠点の検出数の平均値が5個/枚であった。
Next, the 30 sample substrates that had been pre-polished were divided into 15 samples each of Example 1 and Comparative Example 1, and both main surfaces of the sample substrate were finish-polished using the illustrated double-side polishing apparatus 10. In Example 1, of the two main surfaces of the sample substrate, the surface to be evaluated is the polishing surface of the lower surface plate 14 in which no polishing slurry supply hole is provided (the pad surface of the polishing pad 24 attached to the lower surface plate 14). Installed to face each other and finished polishing. In Comparative Example 1, the surface to be evaluated is placed so as to face the polishing surface of the upper surface plate 12 provided with the polishing slurry supply hole 30 (the pad surface of the polishing pad 24 attached to the upper surface plate 12). Final polishing was performed. All of the used polishing slurries were the same, and nitric acid was added to a polishing slurry containing 20% by mass of colloidal silica having an average primary particle diameter of 10 to 20 nm in pure water, and the pH was adjusted to 2. The polishing pad used was a suede pad and was dressed with an electrodeposition diamond prior to the final polishing of the sample substrate. The polishing conditions for finish polishing are as follows.
(Polishing conditions)
Polishing machine: Double-side polishing machine Polishing pad: Suede polishing pad Rh: 3 μm
Average opening diameter: 12 μm
Polishing platen rotation speed: 35rpm
Polishing load: 80 g / cm 2
Polishing time: 50 minutes Diluted water: Pure water (specific resistance 4.2 MΩ · cm, foreign matter filtration of 0.2 μm or more)
Slurry flow rate: 10 L / min
After the sample substrate was finish-polished under the above conditions, the first tank was washed with a surfactant solution washing tank, and the subsequent tanks were washed with a multistage automatic washing machine composed of an ultrapure water rinse tank and an IPA drying tank. . The surface target surface of the cleaned sample substrate was inspected with a photomask surface defect inspection machine (M1350A manufactured by Lasertec Corporation), and the number of concave defects within 142 mm × 142 mm was detected in Example 1 and Comparative Example 1. Each of the 15 sheets was inspected, and the number of detected concave defects was compared. As a result, in Example 1, no concave defect was detected in all 15 sheets. On the other hand, in the comparative example, the average number of detected concave defects was 5 / sheet.
次に試料基材の評価対象面に、イオンビームスパッタリング法を用いて多層反射膜(Si/Mo多層反射膜)を形成した。具体的には、Si膜およびMo膜を交互に成膜することを40周期繰り返すことにより、合計膜厚272nm((4.5+2.3)×40)のSi/Mo多層反射膜を形成した。最後にキャップ層として膜厚11.0nmになるようにSi層を形成した。
なお、Si膜およびMo膜の成膜条件は以下の通りである。
Si膜の成膜条件
ターゲット:Siターゲット(ホウ素ドープ)
スパッタガス:Arガス(ガス圧0.02Pa)
電圧:700V
成膜速度:0.077nm/sec
膜厚:4.5nm
Mo膜の成膜条件
ターゲット:Moターゲット
スパッタガス:Arガス(ガス圧0.02Pa)
電圧:700V
成膜速度:0.064nm/sec
膜厚:2.3nm
Si/Mo多層反射膜の表面(キャップ層としてのSi層表面)をフォトマスク用表面欠点検査機(レーザーテック社製M1350A)で検査し、142mm×142mm内における凹欠点数を実施例1および比較例1で検出した。検査はそれぞれ15枚全てについて行い、SEVD34nmの凹欠点の検出数を比較した。その結果、実施例1では検出数の平均値が15個/枚であったのに対して、比較例1では検出数の平均値が120個/枚であった。
Next, a multilayer reflective film (Si / Mo multilayer reflective film) was formed on the evaluation target surface of the sample substrate by using an ion beam sputtering method. Specifically, the Si / Mo multilayer reflective film having a total film thickness of 272 nm ((4.5 + 2.3) × 40) was formed by repeating alternately forming the Si film and the Mo film for 40 cycles. Finally, a Si layer was formed as a cap layer so as to have a film thickness of 11.0 nm.
The film forming conditions for the Si film and the Mo film are as follows.
Conditions for forming the Si film Target: Si target (boron doped)
Sputtering gas: Ar gas (gas pressure 0.02 Pa)
Voltage: 700V
Deposition rate: 0.077 nm / sec
Film thickness: 4.5nm
Conditions for forming the Mo film Target: Mo target Sputtering gas: Ar gas (gas pressure 0.02 Pa)
Voltage: 700V
Deposition rate: 0.064 nm / sec
Film thickness: 2.3 nm
The surface of the Si / Mo multilayer reflective film (the surface of the Si layer as the cap layer) was inspected with a photomask surface defect inspection machine (M1350A manufactured by Lasertec Corporation), and the number of concave defects within 142 mm × 142 mm was determined in Example 1 and Comparative Example. 1 was detected. Each of the 15 sheets was inspected, and the number of detected SEVD 34 nm concave defects was compared. As a result, in Example 1, the average number of detections was 15 / sheet, whereas in Comparative Example 1, the average number of detections was 120 / sheet.
10:両面研磨装置
12:上定盤
12a:空洞
14:下定盤
14a:空洞
16:太陽歯車
18:内歯歯車
20:キャリア
22:ガラス基板
24:研磨パッド
30:研磨スラリー供給孔
102:定盤中心軸
104:キャリアの回転軸
10: Double-side polishing apparatus 12: Upper surface plate 12a: Cavity 14: Lower surface plate 14a: Cavity 16: Sun gear 18: Internal gear 20: Carrier 22: Glass substrate 24: Polishing pad 30: Polishing slurry supply hole 102: Surface plate Center axis 104: rotation axis of the carrier
Claims (13)
EUVL光学基材での成膜面が、前記下定盤の研磨面と対面するように前記ガラス基板を挟持することを特徴とするEUVL光学基材用ガラス基板の研磨方法。 The upper and lower surface plates, the carrier, while holding the glass substrate held by the carrier on the polishing surface of the upper and lower surface plates of the double-side polishing apparatus and supplying a fluid containing abrasive particles from the supply holes provided in the upper surface plate A glass substrate for an EUV lithography (EUVL) optical base material that polishes both main surfaces of the glass substrate by relatively moving the glass substrate held on the glass substrate,
A method for polishing a glass substrate for an EUVL optical substrate, wherein the glass substrate is sandwiched so that a film formation surface on the EUVL optical substrate faces a polishing surface of the lower surface plate.
前記キャリアを、その中心が前記研磨面上の前記定盤の回転軸と一致しない位置に配置し、前記研磨面上で前記ガラス基板を保持する前記キャリアを前記定盤の回転軸を中心に相対的に公転させ、かつ、前記キャリアの中心を回転軸として前記研磨面上で該キャリアを自転させることによって、前記ガラス基板の両主表面を研磨することを特徴とする請求項1に記載のEUVL光学基材用ガラス基板の研磨方法。 While rotating the upper and lower surface plates with a concentric rotating shaft,
The carrier is disposed at a position where the center thereof does not coincide with the rotation axis of the surface plate on the polishing surface, and the carrier holding the glass substrate on the polishing surface is relative to the rotation axis of the surface plate. 2. The EUVL according to claim 1, wherein both main surfaces of the glass substrate are polished by revolving automatically and rotating the carrier on the polishing surface about the center of the carrier as a rotation axis. A method for polishing a glass substrate for an optical substrate.