JP2012149507A - Prevention or repair method of asphalt pavement - Google Patents
Prevention or repair method of asphalt pavement Download PDFInfo
- Publication number
- JP2012149507A JP2012149507A JP2011284934A JP2011284934A JP2012149507A JP 2012149507 A JP2012149507 A JP 2012149507A JP 2011284934 A JP2011284934 A JP 2011284934A JP 2011284934 A JP2011284934 A JP 2011284934A JP 2012149507 A JP2012149507 A JP 2012149507A
- Authority
- JP
- Japan
- Prior art keywords
- pavement
- layer
- base layer
- asphalt
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、アスファルト舗装路の予防又は補修方法に関するものである。 The present invention relates to a method for preventing or repairing an asphalt pavement.
アスファルト舗装路は、舗装路では現在最も汎用されているものであるが、老朽化すると、道路に凹部(陥没)が生じ事故の原因になる。また、アスファルト骨材が離脱、飛散することにより、道路の断面が露出するようになり、骨材の飛散がより加速されることになる。 Asphalt pavement is the most widely used pavement at present, but when it ages, it causes a recess (sink) on the road, causing an accident. Moreover, when the asphalt aggregate is separated and scattered, the cross section of the road is exposed, and the scattering of the aggregate is further accelerated.
また、最近では車道でのスリップ事故を軽減するため、道路は排水性や透水性を有し、表面に水がたまらないようにしている。このため、骨材間のアスファルトが少なくより強度が落ちることにもなっている。 Recently, in order to reduce slip accidents on the roadway, the road has drainage and water permeability so that water does not accumulate on the surface. For this reason, there is little asphalt between aggregates, and intensity | strength falls also.
このような老朽化した舗装路は補修しなければならない。補修の方法は、既設のアスファルト舗装の基層、表層部をすべて切削除去し、そこに新しいアスファルト合材を敷き均して行なってきた。また、表層部のみを切削除去する方法もある。 Such an old pavement must be repaired. The repair method has been carried out by cutting and removing all the base layer and surface layer of the existing asphalt pavement, and then spreading a new asphalt composite material there. There is also a method of cutting and removing only the surface layer portion.
しかし、このようにアスファルト層を切削することは非常に手間と経費、時間がかかり、道路の解放も遅れ交通渋滞の原因ともなる。 However, cutting the asphalt layer in this way is very time consuming, expensive and time consuming, and the release of the road is delayed, causing traffic congestion.
そこで、排水性アスファルト舗装路を簡単に予防又は補修でき、排水性も確保する方法を提供する。 Therefore, a method for easily preventing or repairing a drainage asphalt pavement and ensuring drainage is provided.
以上のような状況に鑑み、本発明者は鋭意研究の結果本発明舗装路の予防又は補修方法を完成したものであり、その特徴とするところは、非透水性の基層の上方に排水性舗装材層を設けた舗装路の補修方法であって、該基層の上方部に固化材を注入し、該基層と該排水性舗装材層との剥離を防止するものにおいて、該固化材は該排水性舗装材層の下部5〜30mm(基層上面からの高さないし厚み)程度充填され、該固化材の粘度は200mPa・s以下であり、該固化材が硬化した固化物の針入度が150以下であり、注入は舗装路の表面から散布するものである点にある。 In view of the above situation, the present inventor has completed the method for preventing or repairing the paved road according to the present invention as a result of earnest research, and its feature is that the drainage pavement is located above the non-permeable base layer. A method for repairing a paved road provided with a material layer, in which a solidifying material is injected into an upper part of the base layer to prevent separation of the base layer and the drainage pavement material layer. The lower pavement material layer is filled to the lower portion of about 5 to 30 mm (the height or thickness from the upper surface of the base layer), the viscosity of the solidified material is 200 mPa · s or less, and the penetration of the solidified product obtained by curing the solidified material is 150. It is as follows, and the injection is to be sprayed from the surface of the paved road.
ここで予防とは、舗装路が舗装した状態を保つようにすること、すなわち剥離やクラック、陥没、凹部発生等が生じないようにすることをいい、補修はすでにある程度そのような状態になっているものを埋めたり、それ以上にならないようにすること等をいう。 Here, prevention means keeping the paved road in a paved state, that is, preventing peeling, cracks, depressions, depressions, etc. from occurring, and repair has already been in such a state to some extent. It means to fill in what is present or not to exceed it.
非透水性基層とは、密粒アスファルト舗装層、コンクリート層等の舗装材層等であり、後述する排水性舗装材層の下方にある非透水の部分を指し、その材質や構造を限定するものではない。 The non-permeable base layer is a pavement material layer such as a dense-grained asphalt pavement layer or a concrete layer, and refers to a non-water-permeable portion below the drainage pavement layer described later, and its material and structure are limited. is not.
排水性舗装材層とは、中間粒度骨材の混合比率を下げ(トップサイズ骨材を多く)、又は粗骨材のサイズを単粒化する等によって、空隙をつくり、舗装層に水の通過する連続孔を形成したものである。空隙の量としては、限定はしないが、全体の10〜25容量%程度である。要するに現在施工されている通常の排水性舗装等である。 Drainable pavement layer means that the mixing ratio of medium-sized aggregate is lowered (more top-size aggregate) or the size of coarse aggregate is made single, etc., creating voids and passing water through the pavement layer A continuous hole is formed. The amount of voids is not limited, but is about 10 to 25% by volume of the whole. In short, it is the normal drainage pavement currently being constructed.
ここでいう固化材とは、注入(散布)するときには200mPa・s以下の粘度の流体であり、注入後一定時間経過後固化するものであって、アスファルト乳剤、又はアスファルト乳剤と樹脂の混合物をいう。一定時間とは、数十分〜数十時間であり、分解剤を使用することもある。 The term “solidifying material” as used herein refers to a fluid having a viscosity of 200 mPa · s or less when injected (dispersed), which solidifies after a certain time has elapsed after injection, and refers to an asphalt emulsion or a mixture of an asphalt emulsion and a resin. . The fixed time is several tens of minutes to several tens of hours, and a decomposing agent may be used.
アスファルト乳剤とは、アスファルトを水中で乳化剤とともに乳化したものであり、水の量や乳化剤の種類により粘度が異なる。本発明で使用するものは粘度が200mPa・s以下、好ましくは100mPa・s以下、より好ましくは60mPa・s以下のものである。また、流出の問題から30mPa・s以上が好ましい。
これは後述する樹脂を混合した場合も当てはまるものである。
これが、基層のクラック等にも浸透でき、排水性舗装の排水性層の下層部の空隙にとどまり、その上層部の空隙を埋めることのない程度の粘度であり、固化物も一定以上の硬さであるということである。
Asphalt emulsions are those obtained by emulsifying asphalt together with an emulsifier in water, and the viscosity varies depending on the amount of water and the type of emulsifier. What is used in the present invention has a viscosity of 200 mPa · s or less, preferably 100 mPa · s or less, more preferably 60 mPa · s or less. Moreover, 30 mPa * s or more is preferable from the problem of outflow.
This is also true when a resin described later is mixed.
This is a viscosity that can penetrate into the cracks of the base layer, stays in the lower part of the drainage layer of the drainage pavement, and does not fill the gap in the upper part of the drainage pavement. It is that.
さらに、固化材としては、アスファルト乳剤だけでなく、樹脂を混合したものでもよい。この混合は、アスファルト乳剤と樹脂の利点を合わせるためである。すなわち、樹脂の浸透性のよさや強度、アスファルト乳剤の接着性や施工のよさ等の両方の利点を持たせるためである。樹脂としては、基本的にアスファルト乳剤と混合できるものであればどのようなものでもよい。例えば、ゴム、熱可塑性エラストマー、熱可塑性樹脂、及び熱硬化性樹脂等であり、石油樹脂、アクリル系、ウレタン系、エポキシ系の樹脂等がある。 Furthermore, as the solidifying material, not only asphalt emulsion but also resin mixed may be used. This mixing is to combine the advantages of the asphalt emulsion and the resin. That is, it is for giving the advantages of both good permeability and strength of the resin, adhesiveness of the asphalt emulsion and good construction. As the resin, any resin can be used as long as it can basically be mixed with an asphalt emulsion. For example, there are rubber, thermoplastic elastomer, thermoplastic resin, thermosetting resin, etc., and there are petroleum resin, acrylic resin, urethane resin, epoxy resin, and the like.
樹脂の混合量は自由である。例えば、容積比でアスファルト乳剤:樹脂=1:9〜10:0まで可能であるが、3:7〜9:1が好適であり、6:4〜9:1がより好適である。 The mixing amount of the resin is free. For example, asphalt emulsion: resin = 1: 9 to 10: 0 is possible in a volume ratio, but 3: 7 to 9: 1 is preferable, and 6: 4 to 9: 1 is more preferable.
基層の上方部とは、基層の上方で排水性層の下層部という意味であり、基層にクラックや凹部があればそこにも浸透してもよい。排水性層の下層部5〜30mm程度充填する。好ましくは、5〜15mmである。 The upper part of the base layer means the lower part of the drainage layer above the base layer. If there are cracks or recesses in the base layer, they may penetrate there. The lower layer part of the drainage layer is filled about 5 to 30 mm. Preferably, it is 5-15 mm.
針入度とは、JISK2207で規定される固化物の硬さを表す指標であり、通常のアスファルト乳剤では蒸発残留後の針入度が60〜300である。本発明では、舗装路の表面に固化物が残った場合のベタツキを考慮してこれを150以下にしている。しかし、100以下、さらには60以下がより好適である。 The penetration is an index representing the hardness of the solidified product specified by JISK2207. In a normal asphalt emulsion, the penetration after evaporation is 60 to 300. In the present invention, in consideration of the stickiness when the solidified material remains on the surface of the paved road, this is set to 150 or less. However, 100 or less, more preferably 60 or less is more suitable.
上記の固化材の注入は、上方から散布する方法である。上記基層の上方に注入する方法としては、排水性舗装の表面から散布する方法が簡単である。この上方から散布しても十分浸透すること、また十分浸透する固化材を用いたことが本発明のポイントである。 The injection of the solidified material is a method of spraying from above. As a method of injecting above the base layer, a method of spraying from the surface of the drainage pavement is simple. The point of the present invention is that the solidified material that permeates sufficiently even when sprayed from above is used, and that a solidified material that permeates sufficiently is used.
固化材の散布量としては、排水性舗装の空隙率が12〜20%として1m2あたり0.75〜7.5リットル程度であり、1.8〜2.2リットルが好適である。約2リットルで13mm程度充填できた。 The amount of the solidified material sprayed is about 0.75 to 7.5 liters per m 2 when the porosity of the drainage pavement is 12 to 20%, and preferably 1.8 to 2.2 liters. About 2 mm and about 13 mm could be filled.
本発明の実施時期は、いつでもよく予防の意味では舗装路敷設後2〜3年後でも、または4〜6年後でもよい。また補修の意味では、排水性層の空隙詰まりや空隙潰れが生じていなければいつでもよい。 The implementation time of the present invention may be anytime, and may be 2 to 3 years after pavement laying or 4 to 6 years after pavement laying. In terms of repair, it may be any time as long as the drainage layer is not clogged or crushing.
工法としては、単に固化材を散布するだけでよく、表層には手をつけないため、施工すればすぐに交通開放できる。よって、施工も簡単であるため、交通規制時間は非常に短時間である。 As a construction method, it is only necessary to spray the solidified material, and since the surface layer is not touched, traffic can be opened immediately after construction. Therefore, since the construction is easy, the traffic regulation time is very short.
本発明自体は、固化材を上方から散布し、排水性層の空隙を通過して所定位置に充填するため、排水性層の空隙が詰まっていると施工できない。よって、空隙詰まりを解消するため、バキューム装置(減圧吸引する装置)等によって、排水性層の空隙に詰まったゴミ等を吸引除去してもよい。 Since the present invention itself is sprayed with a solidified material from above and passes through the voids of the drainage layer and fills in a predetermined position, the construction cannot be performed if the voids of the drainage layer are clogged. Therefore, in order to eliminate the clogging of the voids, the dust or the like clogged in the voids of the drainage layer may be sucked and removed by a vacuum device (a device that sucks under reduced pressure) or the like.
排水性舗装の下層の補修は、一般的には開削したり孔を開けたりしなければ補修できないのに対して、本発明では非破壊、即ち現状のままで下層以下舗装全体を補修強化できるものである。このため、特別な固化材を選定したものである。即ち、上記した種類、粘度及び強度を特別に選定したということである。 In general, repair of the lower layer of drainage pavement cannot be repaired unless it is opened or drilled, but in the present invention, it is non-destructive, that is, the entire lower pavement can be repaired and strengthened as it is. It is. For this reason, a special solidifying material is selected. That is, the kind, viscosity and strength described above were specially selected.
本発明には次のような効果がある。
(1) 排水性舗装を切削または開削したり孔を開けたりすることなく基層を補強、補修することができる。
(2) 排水性舗装を切削または開削したり孔を開けたりすることなく基層上に防水層(遮水層)を形成できる。その結果基層の保護になる。
(3) 基層が補強、補修されるため、その結果道路の陥没や、基層の剥離が軽減される。
(4) 排水性舗装を切削または開削したり孔を開けたりすることなく基層を補強、補修することができるため、道路の開放が迅速にできる。
(5) 排水層に固化材が被膜、充填されるため、排水層の剥離や骨材飛散が軽減される。
(6) 排水層と基層の層間剥離が軽減される。
(7) 排水性舗装の寿命が延びる。
The present invention has the following effects.
(1) The base layer can be reinforced and repaired without cutting or opening the drainage pavement or making a hole.
(2) A waterproof layer (water shielding layer) can be formed on the base layer without cutting or opening the drainage pavement or making a hole. As a result, the base layer is protected.
(3) Since the base layer is reinforced and repaired, road depression and base layer peeling are reduced as a result.
(4) Since the base layer can be reinforced and repaired without cutting or opening the drainage pavement or making a hole, the road can be opened quickly.
(5) Since the solidified material is coated and filled in the drainage layer, peeling of the drainage layer and scattering of the aggregate are reduced.
(6) The delamination between the drainage layer and the base layer is reduced.
(7) The life of drainage pavement is extended.
以下図面に示す実施例に基づいて、本発明をより詳細に説明する。 Hereinafter, the present invention will be described in more detail based on embodiments shown in the drawings.
図1は、本発明方法の1例(これに限定するものではない)によって、予防した排水性舗装路の部分断面図である。基層(ここでは密粒アスファルト層)1に約50mmの排水性舗装層2が敷設されている。この排水性舗装層2は、アスファルト合材(10〜25mm程度の大骨材と粗骨材を混合)製であり空隙率約15%のものである。基層1は当然ほとんど透水性はない。
FIG. 1 is a partial cross-sectional view of a drainage pavement prevented by one example (not limited to) of the method of the present invention. A
基層1の最上面3より上方で厚み約7mm程度になるよう固化材4が充填されている。基層1にクラック5があれば、そこにも浸透しているところを示している。
The solidified material 4 is filled so as to have a thickness of about 7 mm above the
図から、基層1の上層部に固化材の層が存在し、十分に固化し基層が崩れるのを防止し、また遮水層ともなるため水による基層の損傷も防止する。さらに、排水性層と基層との固着も確保され、剥がれを防止する。
また、排水性舗装層の下層の骨材をしっかり固定するため、排水性舗装層自体も補強される。
From the figure, there is a solidified material layer in the upper layer portion of the
In addition, the drainage pavement layer itself is reinforced in order to firmly fix the aggregate below the drainage pavement layer.
次に実際の排水性舗装材層を設けた舗装路で性能試験を実施した。
舗装の構造は、下から順に、下層路盤220mm、上層路盤80mm、基層60mm、表層40mmであった。この表層40mmが透水性の部分である。
ここに表層から次の固化材を散布した。この固化材は、アスファルト乳剤に石油樹脂を20重量%(ドライベース)混合したものである。
Next, a performance test was performed on a paved road provided with an actual drainage pavement material layer.
The structure of the pavement was, in order from the bottom, a lower layer roadbed 220 mm, an upper layer roadbed 80 mm, a base layer 60 mm, and a
The following solidification material was sprayed here from the surface layer. This solidifying material is a mixture of 20% by weight (dry base) of petroleum resin in an asphalt emulsion.
固化材の物性は次の通りである。
粘度:50mPa・s
平均粒子径:3μm
蒸発残留分試験:60%
蒸発残留物の針入度:34(1/10mm)
蒸発残留物の軟化点:54.5℃
貯蔵安定試験:1.5%(5日)
The physical properties of the solidified material are as follows.
Viscosity: 50 mPa · s
Average particle size: 3 μm
Evaporation residue test: 60%
Penetration of evaporation residue: 34 (1/10 mm)
Softening point of evaporation residue: 54.5 ° C
Storage stability test: 1.5% (5 days)
この固化材を1m2あたり2リットル散布した。結果は次の通りであった。
図2は、この試験を施した道路からサンプリングした写真をコピーしたものである。基層の上方13mmまで固化材が充填されており、それより上方ではまだ空隙6が残っていることがわかる。
補修開始から完了まではほぼ1時間であった。完了は表面を触診して乳剤がほぼ付かなくなったことを確認した。
2 liters of this solidified material was sprayed per 1 m 2 . The results were as follows.
FIG. 2 is a copy of a photograph taken from the road on which this test was performed. It can be seen that the solidification material is filled up to 13 mm above the base layer, and the
It took almost an hour from the start of repair to completion. Completion was confirmed by palpating the surface and almost no emulsion.
補修の結果、基層1の最上面3から下方に浸透する透水係数が、補修前が10−6cm/sレベルであったものが、10−7〜10−8cm/sになり、防水効果(水遮断)がより確実になったことがわかる。
また、排水性舗装材層のカンタブロ試験の結果は、補修前の損失量が47.5%であったのに対し、補修後は26.5%であった。これにより、骨材間の接着性が補強され飛散が軽減されたことがわかる。
As a result of the repair, the water permeability coefficient penetrating downward from the
Moreover, the result of the cantabulo test of the drainage pavement material layer was 27.5% after the repair, while the loss amount before the repair was 47.5%. Thereby, it turns out that the adhesiveness between aggregates was reinforced and scattering was reduced.
1 基層
2 排水性舗装層
3 基層の上面
4 固化材
5 クラック
6 空隙
DESCRIPTION OF
Claims (2)
The method for preventing or repairing an asphalt pavement according to claim 1, wherein the amount of the solidified material sprayed is 0.75 to 7.5 liters per 1 m 2 of the road surface.