JP2012139609A - Sorting method of mixed metal - Google Patents

Sorting method of mixed metal Download PDF

Info

Publication number
JP2012139609A
JP2012139609A JP2010291866A JP2010291866A JP2012139609A JP 2012139609 A JP2012139609 A JP 2012139609A JP 2010291866 A JP2010291866 A JP 2010291866A JP 2010291866 A JP2010291866 A JP 2010291866A JP 2012139609 A JP2012139609 A JP 2012139609A
Authority
JP
Japan
Prior art keywords
metal
sorting
mixed
copper wire
eddy current
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2010291866A
Other languages
Japanese (ja)
Inventor
Naoya Yamakawa
直也 山川
Junichiro Hara
順一郎 原
Hiroshi Honjo
寛 本城
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HIRABAYASHI KINZOKU KK
Original Assignee
HIRABAYASHI KINZOKU KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HIRABAYASHI KINZOKU KK filed Critical HIRABAYASHI KINZOKU KK
Priority to JP2010291866A priority Critical patent/JP2012139609A/en
Publication of JP2012139609A publication Critical patent/JP2012139609A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a sorting method of a mixed metal in which sorting of a mixed metal by hand work is made minimum.SOLUTION: The method in which a mixed metal 1 is sorted in each of metal species includes: a metal nonmetal sorting process 2 in which a metal 21 in the mixed metal is perceived by a metal sensor and the mixed metal 1 is sorted to the metal 21 and a nonmetal 22; an eddy current sorting process 3 in which the metal 21 sorted by the metal nonmetal sorting process 2 is made to generate an eddy current and the metal 21 is sorted to a fly side metal 32 and a fall side metal 31 by the repulsion with a magnet; a specific gravity separation process 4 in which the fly side metal 32 sorted by the eddy current sorting process 3 is sorted by the specific gravity; and a color sorting process 5 in which the fall side metal 31 sorted by the eddy current sorting process 3 is sorted by a color sensor.

Description

本発明は、ミックスメタルを金属種ごとに選別するミックスメタルの選別方法に関する。 The present invention relates to a method for selecting a mixed metal in which the mixed metal is selected for each metal species.

エアコン、冷蔵庫、テレビ、洗濯機などの廃家電、産業機械廃棄物、廃車等は大型の破砕機に投入し破砕処理される。破砕物は磁力選別により鉄が回収され、その他の破砕物は、例えば風力選別等を利用して非金属が除去される。非金属除去後に残される雑多な金属（非鉄金属）と除去しきれなかったプラスチックを含む非金属との混合物はミックスメタルと呼ばれる。 Waste home appliances such as air conditioners, refrigerators, televisions, and washing machines, industrial machine waste, and scrap cars are put into a large crusher and crushed. Iron is recovered from the crushed material by magnetic sorting, and non-metals are removed from the other crushed materials using, for example, wind sorting. A mixture of a miscellaneous metal (non-ferrous metal) left after the non-metal removal and a non-metal including a plastic that cannot be removed is called a mixed metal.

ミックスメタルは機械的な工程のみで金属種ごとに完全に選別することが難しく、国内での選別コストも高いことから、従来は、外国に売却されそこで手作業による選別が行われていた。 Mixed metal is difficult to be completely sorted by metal type using only a mechanical process, and the sorting cost in Japan is high. Conventionally, mixed metal has been sold to foreign countries and manually sorted there.

ミックスメタルに含まれる非鉄金属を選別する方法としては例えば特許文献１がある。特許文献１は、非鉄金属屑を重液選別機、渦電流選別機、カラー識別選別機の順にかけてアルミニウム、銅、亜鉛、ステンレススチール（以下、単にステンレスと称する）を選別する方法である。 For example, Patent Document 1 discloses a method for selecting non-ferrous metals contained in a mixed metal. Patent Document 1 is a method of sorting aluminum, copper, zinc, and stainless steel (hereinafter simply referred to as stainless steel) by applying non-ferrous metal scraps in the order of heavy liquid sorter, eddy current sorter, and color discrimination sorter.

特許文献１の方法は、最初の工程として重液（比重２．８〜３．０）による選別工程を経るものであるから、非鉄金属屑が濡れてしまい、乾燥工程が必要となり、あわせて水処理工程も必要となることから、コスト、エネルギーが余分に必要となる問題があった。さらに、プラスチック等の分離が考慮されておらず、重液による選別を経たアルミニウムにプラスチック等の軽量物が混ざり、再度の選別が必要になるという問題があった。 Since the method of patent document 1 passes through the selection process by a heavy liquid (specific gravity 2.8-3.0) as an initial process, a nonferrous metal waste gets wet, a drying process is needed, and water is also added. Since a processing step is also required, there is a problem that extra cost and energy are required. In addition, separation of plastics and the like is not taken into consideration, and there is a problem that light materials such as plastics are mixed with aluminum that has been subjected to selection with heavy liquid, so that re-selection is necessary.

また、特許文献１の渦電流選別では、ステンレスを含む落下側の金属については、何らの処理をすることなくリサイクルされるが、落下側の金属には渦電流の生じにくい細長い銅線が混入するという問題があった。さらに、飛側の金属（銅、鉛、亜鉛）について、カラー選別機による選別を行っているが、実際には銅、鉛、亜鉛はメッキされていることがあり、機械的に完全に選別することが難しいという問題があった。 In addition, in the eddy current selection of Patent Document 1, the drop-side metal including stainless steel is recycled without any treatment, but the drop-side metal is mixed with an elongated copper wire that is unlikely to generate eddy current. There was a problem. In addition, the flying side metal (copper, lead, zinc) is sorted by a color sorter, but in reality, copper, lead, and zinc may be plated and are completely sorted mechanically. There was a problem that it was difficult.

一方、本発明者は特許文献２の乾式分離方法を提案している。特許文献２の発明は、粉体を流動化させた固気流動層に処理対象物を入れて、比重に応じて処理対象物を選別する方法である。この方法によれば廃液処理や選別後の乾燥工程が不要になるという利点がある。 On the other hand, the present inventor has proposed the dry separation method of Patent Document 2. The invention of Patent Document 2 is a method of putting a processing object in a solid-gas fluidized bed in which powder is fluidized and selecting the processing object according to specific gravity. According to this method, there is an advantage that a waste liquid treatment and a drying step after sorting become unnecessary.

特開平６−１０６０９１JP-A-6-106091 特開平２００８−２４６３９３JP 2008-246393 A

我が国は産出資源が乏しいことから、ミックスメタルを国内でリサイクルし金属資源を循環させ、金属資源の流出を防ぐことが望まれている。本発明は、手作業によるミックスメタルの選別を最小限としたミックスメタルの選別方法を提供することを目的とする。これによりミックスメタルの選別に要するコストを削減し、国内でのミックスメタルの循環を可能にする。 Since Japan has limited output resources, it is desirable to recycle mixed metal in Japan and circulate metal resources to prevent the outflow of metal resources. An object of the present invention is to provide a method for selecting a mixed metal that minimizes manual selection of the mixed metal. This will reduce the cost of sorting mixed metal and enable circulation of mixed metal in the country.

ミックスメタルを金属種ごとに選別する方法であって、該方法は金属センサによりミックスメタル中の金属を感知してミックスメタルを金属と非金属とに選別する金属非金属選別工程と、該金属非金属選別工程で選別された金属に渦電流を発生させて磁石との反発力によって金属を飛側金属と落下側金属とに選別する渦電流選別工程とからなり、該渦電流選別工程で選別された飛側金属については比重により選別する比重分離工程で処理し、前記渦電流選別工程で選別された落下側金属については色彩センサによって選別する色彩選別工程で処理することを特徴とするミックスメタルの選別方法により、上記の課題を解決する。 A method of selecting a mixed metal for each metal species, wherein the method detects a metal in the mixed metal by a metal sensor and selects the mixed metal into a metal and a nonmetal, and a metal nonmetal selecting step. It consists of an eddy current sorting process in which eddy current is generated in the metal sorted in the metal sorting process and the metal is sorted into a flying side metal and a falling side metal by the repulsive force with the magnet. The mixed metal is characterized in that the flying metal is processed in a specific gravity separation process that selects by specific gravity, and the falling metal selected in the eddy current screening process is processed in a color selection process that is selected by a color sensor. The above problem is solved by the sorting method.

本発明の選別方法が適用できるミックスメタルとしては、例えば、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物が挙げられる。ここでいう銅は、渦電流の生じやすいものを指し、その点で銅線と区別される。 Examples of the mixed metal to which the screening method of the present invention can be applied include a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic. Copper here refers to a material in which eddy current is easily generated, and is distinguished from copper wire in that respect.

金属非金属選別工程は、金属センサでミックスメタル中の金属を感知して、金属と非金属を選別する工程である。ここで言う非金属としては、除去しきれなかったプラスチックが含まれる。ミックスメタルが、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物である場合は、金属非金属選別工程により、銅、銅線、アルミニウム、亜鉛、真鍮及びステンレスを含む金属と、プラスチックを含む非金属とに選別する。金属センサは非鉄金属とプラスチックを識別することができる公知の金属センサを使用すればよい。 The metal non-metal sorting step is a step of sorting the metal and non-metal by sensing the metal in the mixed metal with a metal sensor. The nonmetal mentioned here includes plastic that could not be removed. When the mixed metal is a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel, and plastic, by a metal non-metal sorting process, a metal containing copper, copper wire, aluminum, zinc, brass, and stainless steel, Sort into non-metals including plastic. As the metal sensor, a known metal sensor that can distinguish nonferrous metal and plastic may be used.

渦電流選別工程は、電磁誘導により生ずる渦電流の磁界と磁石の磁界の反発力を利用して金属非金属選別工程で選別された金属を飛側金属と、落下側金属とに選別する工程である。ミックスメタルが、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物である場合は、金属非金属選別工程に続く渦電流選別工程により、ステンレス及び銅線を含む落下側金属と、銅、アルミニウム、亜鉛及び真鍮を含む飛側金属とに選別する。 The eddy current sorting process is a process of sorting the metal selected in the metal non-metal sorting process into the flying side metal and the falling side metal using the repulsive force of the magnetic field of the eddy current generated by electromagnetic induction and the magnetic field of the magnet. is there. When the mixed metal is a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic, an eddy current sorting step following the metal non-metal sorting step, a drop side metal containing stainless steel and copper wire, Sort by flying metal including copper, aluminum, zinc and brass.

比重分離工程は、渦電流選別工程において磁石との反発力で飛ばされた金属（飛側金属）について、その比重によって選別を行う工程である。ミックスメタルが、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物である場合は、金属非金属選別工程及び渦電流選別工程に続く比重分離工程により、飛側金属を、アルミニウムを含む浮上側金属と、銅、亜鉛及び真鍮を含む沈下側金属に選別する。比重分離は重液を使用した湿式装置を使用してもよいが、固気流動層を備えた乾式装置を使用すれば、乾燥が不要となり処理を効率化することができるので、好ましい。 The specific gravity separation step is a step in which the metal (flying side metal) blown by the repulsive force with the magnet in the eddy current selection step is selected based on its specific gravity. When the mixed metal is a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic, the flying side metal is replaced with aluminum by the specific gravity separation step following the metal non-metal sorting step and the eddy current sorting step. Sorting into floating metal containing and subsidence metal containing copper, zinc and brass. For the specific gravity separation, a wet apparatus using a heavy liquid may be used. However, using a dry apparatus equipped with a solid-gas fluidized bed is preferable because drying is unnecessary and the processing can be made more efficient.

色彩選別工程は、渦電流選別工程において落下した金属（落下側金属）について、色彩の違いによって金属種ごとに選別を行う工程である。ミックスメタルが、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物である場合は、金属非金属選別工程及び渦電流選別工程に続く色彩選別工程により、落下側金属を、銅線を含む赤色金属と、ステンレスを含む非赤色金属に選別する。 The color sorting step is a step of sorting the metal (falling side metal) dropped in the eddy current sorting step for each metal type depending on the color difference. When the mixed metal is a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic, the drop side metal is converted to copper wire by the color sorting step following the metal non-metal sorting step and the eddy current sorting step. Sorting into red metal containing and non-red metal containing stainless steel.

上記のミックスメタルが、さらに被覆銅線を含む場合、金属非金属選別工程後の非金属に被覆銅線が混入しやすい。この場合は、長穴フルイを用いて被覆銅線と非金属の混合物から被覆銅線を分離する被覆銅線選別工程を行うとよい。 When said mixed metal contains a covering copper wire further, a covering copper wire tends to mix in the nonmetal after a metal nonmetallic sorting process. In this case, it is preferable to perform a coated copper wire sorting step for separating the coated copper wire from the mixture of the coated copper wire and the nonmetal using a long hole sieve.

本発明のミックスメタルの選別方法によれば、従来、手作業により選別していたミックスメタルの大半を機械的に選別することができる。本発明は、金属非金属選別工程を比重選別工程の前に行うので、アルミニウムを含む浮上側金属にプラスチックを含む非金属が混入することがない。また、渦電流選別工程の落下側金属について色彩選別工程を行うため、ステンレスを含む落下側金属に、銅線を含む赤色金属が混入することがない。これにより、選別に要するコストを低く抑えて、金属資源の国内循環を可能にすることができる。 According to the method for selecting a mixed metal of the present invention, most of the mixed metal that has been conventionally manually selected can be mechanically selected. In the present invention, since the metal non-metal sorting step is performed before the specific gravity sorting step, the non-metal containing plastic is not mixed into the floating metal containing aluminum. Moreover, since the color selection process is performed on the drop-side metal in the eddy current selection process, the red metal including the copper wire is not mixed into the drop-side metal including stainless steel. Thereby, the cost required for sorting can be kept low, and the domestic circulation of metal resources can be made possible.

本発明のミックスメタルの選別方法の流れ図である。It is a flowchart of the selection method of the mixed metal of this invention. 図１の選別方法に加えて、さらに被覆銅線選別工程を行う選別方法の流れ図である。It is a flowchart of the sorting method which performs a covering copper wire sorting process in addition to the sorting method of FIG. 実施例１の選別方法を示す流れ図である。3 is a flowchart illustrating a selection method according to the first embodiment. 実施例２の選別方法を示す流れ図である。6 is a flowchart illustrating a selection method according to the second embodiment.

以下、図面を参照しながら本発明を実施するための形態を説明する。 DESCRIPTION OF EMBODIMENTS Hereinafter, embodiments for carrying out the present invention will be described with reference to the drawings.

本発明は、ミックスメタル１を金属種ごとに選別する方法である。図１に示したように、本発明の選別方法は金属センサによりミックスメタル１中の金属を感知して金属２１と非金属２２とに選別する金属非金属選別工程２と、該金属非金属選別工程２で選別された金属２１に渦電流を発生させて磁石との反発力によって金属２１を落下側金属３１と飛側金属３２とに選別する渦電流選別工程３とからなる。前記渦電流選別工程３で選別された飛側金属３２については比重分離工程４で比重に応じて沈下側金属４１と浮上側金属４２に選別する。一方、前記渦電流選別工程３で選別された落下側金属３１については色彩選別工程５で色彩センサにより処理し、赤色金属５１と非赤色金属５２に選別する。 The present invention is a method of sorting the mix metal 1 for each metal species. As shown in FIG. 1, the sorting method of the present invention detects a metal in the mixed metal 1 by a metal sensor and sorts it into a metal 21 and a nonmetal 22, and the metal nonmetal sorting. It comprises an eddy current sorting step 3 in which an eddy current is generated in the metal 21 sorted in the step 2 and the metal 21 is sorted into a falling side metal 31 and a flying side metal 32 by a repulsive force with the magnet. The flying side metal 32 selected in the eddy current selection step 3 is sorted into a sinking side metal 41 and a floating side metal 42 in a specific gravity separation step 4 according to the specific gravity. On the other hand, the drop side metal 31 selected in the eddy current selection step 3 is processed by the color sensor in the color selection step 5 to be selected into the red metal 51 and the non-red metal 52.

比重分離工程４で処理した沈下側金属４１については、特許文献１と同様に色彩選別機によりさらに選別を行ってもよいし、図１に示したように手作業６により個々の金属種ごと（手選別済金属６１）に選別してもよい。しかしながら、沈下側金属４１に含まれる銅、亜鉛、真鍮等の金属はメッキ処理されていることがあり、色彩センサによる選別が難しいことから、図１のように手作業による選別とすることが好ましい。手作業であれば、メッキされた金属であっても破砕時の傷から部分的な色が確認できるからである。 The subsidence-side metal 41 treated in the specific gravity separation step 4 may be further sorted by a color sorter in the same manner as in Patent Document 1, or as shown in FIG. You may sort into the hand-sorted metal 61). However, since metals such as copper, zinc, and brass contained in the sinking side metal 41 may be plated and it is difficult to select with a color sensor, manual selection as shown in FIG. 1 is preferable. . This is because, if it is manual work, even a plated metal can confirm a partial color from scratches at the time of crushing.

また、ミックスメタル１に被覆銅線７１が多く含まれる場合は、図１の選別方法に加えて、被覆銅線選別工程７を行うことが好ましい。図２に示したように、被覆銅線選別工程７は、金属非金属選別工程２後の非金属２２に混入する被覆銅線７１を選別する工程である。被覆銅線７１は樹脂で被覆されていることから、プラスチック等を含む非金属側に比較的混入しやすい。本発明では、長穴フルイを使用することで、被覆銅線７１を手作業によらず選別することが可能になる。 When the mixed metal 1 contains a large amount of the coated copper wire 71, it is preferable to perform the coated copper wire sorting step 7 in addition to the sorting method of FIG. As shown in FIG. 2, the coated copper wire sorting step 7 is a step of sorting the coated copper wire 71 mixed in the nonmetal 22 after the metal nonmetal sorting step 2. Since the coated copper wire 71 is coated with a resin, it is relatively easy to mix on the non-metal side including plastic. In the present invention, by using the long hole sieve, it becomes possible to sort the coated copper wire 71 without manual operation.

以下、実施例により具体的に説明する。 Hereinafter, specific examples will be described.

［実施例１］
図１及び図３の選別方法により、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含むミックスメタル１を選別した。ここで処理するミックスメタルは、磁力選別により鉄を事前に除去したものである。 [Example 1]
The mixed metal 1 containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic was selected by the selection method shown in FIGS. The mixed metal to be treated here is obtained by removing iron in advance by magnetic separation.

まず、上記のミックスメタル１を金属非金属選別工程２で処理した。本実施例では、ミックスメタル１を載置するエンドレスコンベアと、エンドレスコンベアの搬送経路の途中に配置した金属センサと、金属センサの信号に基づいて非金属にエアを噴射するエアノズルとを備えた金属非金属選別機を使用し、金属２１と非金属２２を選別した。この工程により１００ｔのミックスメタルを約７５ｔの金属２１（銅、銅線、アルミニウム、亜鉛、真鍮及びステンレスを含む混合物）と、約２５ｔの非金属２２（プラスチック）に選別することができた（図３）。 First, the above mixed metal 1 was processed in the metal non-metal sorting step 2. In this embodiment, a metal provided with an endless conveyor on which the mixed metal 1 is placed, a metal sensor disposed in the middle of the transport path of the endless conveyor, and an air nozzle that injects air to a non-metal based on a signal from the metal sensor. The metal 21 and the nonmetal 22 were sorted using a nonmetal sorter. Through this process, 100 tons of mixed metal could be sorted into about 75 tons of metal 21 (a mixture containing copper, copper wire, aluminum, zinc, brass and stainless steel) and about 25 tons of nonmetal 22 (plastic) (Fig. 3).

次に、金属非金属選別工程２で分離できなかった銅、銅線、アルミニウム、亜鉛、真鍮、ステンレスを含む金属２１を渦電流選別工程３にかけた。渦電流選別機は、金属２１を載置するエンドレスコンベアと、エンドレスコンベアの末端回転軸の一方に回転可能に取り付けられたマグネットと、マグネットの下方に配されエンドレスコンベアからの飛側金属３２と落下側金属３１を受け入れる独立した二つのホッパを備えた渦電流選別機を使用した。この工程により約７５ｔの金属２１を、約３４ｔの落下側金属３１（ステンレス及び銅線）と、約４１ｔの飛側金属３２（銅、アルミニウム、亜鉛及び真鍮）に選別することができた（図３）。 Next, the metal 21 containing copper, copper wire, aluminum, zinc, brass, and stainless steel that could not be separated in the metal non-metal sorting step 2 was subjected to the eddy current sorting step 3. The eddy current sorter includes an endless conveyor on which the metal 21 is placed, a magnet that is rotatably attached to one of the end rotary shafts of the endless conveyor, and a flying metal 32 that is disposed below the magnet and falls from the endless conveyor. An eddy current sorter with two independent hoppers receiving the side metal 31 was used. Through this process, about 75 t of metal 21 could be sorted into about 34 t of drop side metal 31 (stainless steel and copper wire) and about 41 t of fly side metal 32 (copper, aluminum, zinc and brass) (see FIG. 3).

渦電流選別工程３では分離できなかった銅線及びステンレスを含む落下側金属３１については、色彩選別工程５にかけた。色彩選別機は落下側金属３１を載置するエンドレスコンベアと、エンドレスコンベアの搬送経路に配されるＣＣＤカメラと、ＣＣＤカメラの信号に基づいて赤色金属にエアを噴射するエアノズルを備えた色彩選別機を使用した。この色彩選別工程５により、約３４ｔの落下側金属３１を約５ｔの赤色金属５１（銅線）と、約２９ｔの非赤色金属５２（ステンレス）に選別することができた。 The drop-side metal 31 including copper wire and stainless steel that could not be separated in the eddy current sorting step 3 was subjected to the color sorting step 5. The color sorter includes an endless conveyor on which the drop-side metal 31 is placed, a CCD camera arranged in the transport path of the endless conveyor, and an air nozzle that injects air to the red metal based on the signal from the CCD camera. It was used. By this color sorting step 5, about 34 t of the falling side metal 31 could be sorted into about 5 t of red metal 51 (copper wire) and about 29 t of non-red metal 52 (stainless steel).

一方、渦電流選別工程３では分離できなかった銅、アルミニウム、亜鉛及び真鍮を含む飛側金属３２については、比重分離工程４にかけた。本実施例では、特許文献２の固気流動層を有する乾式比重分離装置を使用した。粉体としては鉄粉を用いて、流動層の見かけ密度を４程度とした。この工程により、約４１ｔの飛側金属３２を約２３ｔの浮上側金属（アルミニウム）と、約１８ｔの沈下側金属４１（銅、亜鉛及び真鍮）に選別することができた（図３）。 On the other hand, the flying side metal 32 including copper, aluminum, zinc and brass that could not be separated in the eddy current sorting step 3 was subjected to the specific gravity separation step 4. In this example, the dry specific gravity separator having a solid-gas fluidized bed of Patent Document 2 was used. Iron powder was used as the powder, and the apparent density of the fluidized bed was about 4. By this step, about 41 t of flying side metal 32 could be sorted into about 23 t of floating side metal (aluminum) and about 18 t of sinking side metal 41 (copper, zinc and brass) (FIG. 3).

本実施例のミックスメタルには、メッキ処理された金属が多く含まれていたため、比重分離工程４で選別できなかった銅、亜鉛、真鍮を含む沈下側金属４１は、破砕時に金属表面にできた傷から色を確認する手作業６により選別した。これにより単体の銅、亜鉛、真鍮（手選別済金属６１）を得ることができた。この際に予めプラスチック、アルミニウム、ステンレス及び銅線が除去されているため、手作業でも効率的に選別することができた。 Since the mixed metal of this example contained a large amount of plated metal, the subsidence-side metal 41 containing copper, zinc, and brass that could not be selected in the specific gravity separation step 4 was formed on the metal surface during crushing. Sorting was done by manual operation 6 to check the color from the scratch. Thereby, simple copper, zinc, and brass (hand-sorted metal 61) could be obtained. At this time, since plastic, aluminum, stainless steel and copper wire were removed in advance, it was possible to sort efficiently even by manual work.

従来、渦電流による選別では銅線などの細長い形状を有するものは渦電流が生じにくいことから、ステンレスを含む落下側金属３１から分離することが難しかったが、実施例１の方法によれば、ステンレスと銅線を機械的に選別することができた。また、従来は比重分離工程４で単離されたアルミニウムなどの浮上側金属４２には、プラスチック等の軽量物が混入することがあったが、実施例１の方法によれば、プラスチック等の軽量物は金属非金属選別工程２で除去されているため、浮上側金属４２にプラスチックが混入することがなくそのままアルミニウムをリサイクルに回すことができた。 Conventionally, in the selection based on eddy current, an elongated shape such as a copper wire is difficult to generate eddy current, so it was difficult to separate from the drop-side metal 31 including stainless steel, but according to the method of Example 1, Stainless steel and copper wire could be mechanically sorted. Further, conventionally, a light-weight material such as plastic may be mixed in the floating metal 42 such as aluminum isolated in the specific gravity separation step 4, but according to the method of the first embodiment, a light-weight material such as plastic is used. Since the object was removed in the metal nonmetal sorting step 2, the plastic was not mixed into the floating metal 42 and aluminum could be recycled as it was.

［実施例２］
本実施例では、実施例１の銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックに加えて被覆銅線７１を多量に含むミックスメタル１の選別を行った。具体的には、金属非金属選別工程２で選別された非金属２２について、さらに被覆銅線選別工程７を行う方法である（図２及び図４）。被覆銅線選別工程７においては、幅５ｍｍ長さ２５ｍｍの長穴をパンチングしたスクリーンを備えた長穴トロンメルを使用し、長穴から被覆銅線７１をふるいおとした。これにより、プラスチック（非金属２２）に混入した被覆銅線７１を効率的に取り除くことができた。 [Example 2]
In this example, selection of the mixed metal 1 including a large amount of the coated copper wire 71 in addition to the copper, copper wire, aluminum, zinc, brass, stainless steel, and plastic of Example 1 was performed. Specifically, this is a method in which the coated copper wire sorting process 7 is further performed on the nonmetal 22 sorted in the metal / nonmetal sorting process 2 (FIGS. 2 and 4). In the coated copper wire sorting step 7, a long hole trommel having a screen punched with a long hole having a width of 5 mm and a length of 25 mm was used, and the coated copper wire 71 was screened from the long hole. As a result, the coated copper wire 71 mixed in the plastic (nonmetal 22) could be efficiently removed.

１ ミックスメタル
２ 金属非金属選別工程
２１ 金属
２２ 非金属
３ 渦電流選別工程
３１ 落下側金属
３２ 飛側金属
４ 比重分離工程
４１ 沈下側金属
４２ 浮上側金属
５ 色彩選別工程
５１ 赤色金属
５２ 非赤色金属
６ 手作業
６１ 手選別済金属
７ 被覆銅線選別工程
７１ 被覆銅線
７２ 非金属 1 Mixed metal 2 Metal non-metal sorting step 21 Metal 22 Non-metal 3 Eddy current sorting step 31 Falling side metal 32 Flying side metal 4 Specific gravity separation step 41 Sinking side metal 42 Floating side metal 5 Color sorting step 51 Red metal 52 Non-red metal 6 Manual work 61 Hand-sorted metal 7 Coated copper wire sorting process 71 Coated copper wire 72 Non-metal

Claims (7)

ミックスメタルを金属種ごとに選別する方法であって、
該方法は金属センサによりミックスメタル中の金属を感知してミックスメタルを金属と非金属とに選別する金属非金属選別工程と、該金属非金属選別工程で選別された金属に渦電流を発生させて磁石との反発力によって金属を飛側金属と落下側金属とに選別する渦電流選別工程とからなり、
該渦電流選別工程で選別された飛側金属については比重により選別する比重分離工程で処理し、
前記渦電流選別工程で選別された落下側金属については色彩センサによって選別する色彩選別工程で処理することを特徴とするミックスメタルの選別方法。 A method of sorting mixed metal by metal type,
The method detects a metal in a mixed metal by a metal sensor and sorts the mixed metal into a metal and a nonmetal, and generates an eddy current in the metal sorted in the metal nonmetal sorting process. Eddy current sorting process that sorts metal into flying side metal and falling side metal by repulsive force with magnet,
The flying side metal selected in the eddy current selection step is processed in a specific gravity separation step that is selected by specific gravity,
The drop metal selected in the eddy current selection step is processed in a color selection step of selecting by a color sensor. ミックスメタルは、銅、銅線、アルミニウム、亜鉛、真鍮、ステンレス及びプラスチックを含む混合物である請求項１に記載のミックスメタルの選別方法。 The method for selecting a mixed metal according to claim 1, wherein the mixed metal is a mixture containing copper, copper wire, aluminum, zinc, brass, stainless steel and plastic. 金属非金属選別工程は、ミックスメタルを銅、銅線、アルミニウム、亜鉛、真鍮及びステンレスを含む金属と、プラスチックを含む非金属とに選別する工程である請求項1又は２に記載のミックスメタルの選別方法。 The metal-non-metal sorting step is a step of sorting the mixed metal into a metal containing copper, copper wire, aluminum, zinc, brass and stainless steel and a non-metal containing plastic. Sorting method. 渦電流選別工程は、金属非金属選別工程で分離できなかった銅、銅線、アルミニウム、亜鉛、真鍮及びステンレスを含む金属を、ステンレス及び銅線を含む落下側金属と、銅、アルミ及び亜鉛を含む飛側金属とに選別する工程である請求項1又は２に記載のミックスメタルの選別方法。 In the eddy current sorting process, the metal containing copper, copper wire, aluminum, zinc, brass and stainless steel, which could not be separated in the metal non-metal sorting process, the falling side metal containing stainless steel and copper wire, and copper, aluminum and zinc The method for selecting a mixed metal according to claim 1 or 2, wherein the method is a step of selecting the flying metal to be contained. 比重分離工程は、渦電流選別工程で選別できなかった銅、アルミニウム、亜鉛及び真鍮を含む飛側金属を、アルミニウムを含む浮上側金属と、銅、亜鉛及び真鍮を含む沈下側金属とに選別する工程である請求項１又は２に記載のミックスメタルの選別方法。 In the specific gravity separation process, the flying side metal containing copper, aluminum, zinc and brass that could not be sorted in the eddy current sorting process is sorted into a floating metal containing aluminum and a sinking metal containing copper, zinc and brass. The method for selecting a mixed metal according to claim 1, wherein the method is a process. 色彩選別工程は、渦電流選別工程で選別できなかった銅線とステンレスを含む落下側金属を銅線を含む赤色金属と、ステンレスを含む非赤色金属とに選別する工程である請求項１又は２に記載のミックスメタルの選別方法。 The color selection step is a step of selecting a falling metal containing copper wire and stainless steel, which could not be selected in the eddy current selection step, into a red metal containing copper wire and a non-red metal containing stainless steel. The method for sorting mixed metals as described in 1. ミックスメタルは、さらに被覆銅線を含むものであって、
金属非金属選別工程で選別できなかった非金属と被覆銅線の混合物から長穴フルイで被覆銅線を分離する被覆銅線選別工程を行う請求項２に記載のミックスメタルの選別方法。 Mixed metal further includes coated copper wire,
The method for selecting a mixed metal according to claim 2, wherein a coated copper wire sorting step is performed in which the coated copper wire is separated from the mixture of the nonmetal and the coated copper wire that could not be sorted in the metal-nonmetal sorting step using a long hole sieve.
JP2010291866A 2010-12-28 2010-12-28 Sorting method of mixed metal Pending JP2012139609A (en)