JP2012117013A - Adhesive composition and surface protection adhesive film - Google Patents

Adhesive composition and surface protection adhesive film Download PDF

Info

Publication number
JP2012117013A
JP2012117013A JP2010270497A JP2010270497A JP2012117013A JP 2012117013 A JP2012117013 A JP 2012117013A JP 2010270497 A JP2010270497 A JP 2010270497A JP 2010270497 A JP2010270497 A JP 2010270497A JP 2012117013 A JP2012117013 A JP 2012117013A
Authority
JP
Japan
Prior art keywords
polymer
weight
block
polymer block
aromatic alkenyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2010270497A
Other languages
Japanese (ja)
Inventor
Katsue Masaki
克枝 正木
Katsuhiro Nagao
功弘 長尾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP2010270497A priority Critical patent/JP2012117013A/en
Publication of JP2012117013A publication Critical patent/JP2012117013A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an adhesive, capable of peeling the end of the surface protection adhesive film easily from an adherend, even when a blanked piece is obtained by blanking from a laminate of the adherend and the surface protection adhesive film; and to provide a surface protection adhesive film.SOLUTION: This adhesive composition contains a copolymer (which may contain a coupling agent residue) containing a polymer block A mainly composed of an aromatic alkenyl compound unit and an aromatic alkenyl-conjugated diene copolymer block B containing conjugated diene units and aromatic alkenyl compound units at random, or its hydrogenated product, wherein, the aromatic alkenyl compound unit content rate (St(A+B)) in the whole polymer is 30-50 wt.%, and the weight ratio (A:B) of the total amount of the polymer block A to the total amount of the polymer block B is in the range of 5:95 to 25:75, and further at least either of an imine-based compound and fatty acid amide is contained.

Description

本発明は、粘着剤組成物および表面保護粘着フィルムに関する。   The present invention relates to an adhesive composition and a surface protective adhesive film.

従来、打ち抜き刃型を用いて表面保護フィルムが貼り付けられた状態の光学フィルムの長尺状のシートを打ち抜くことで、光学部品を製造することが提案されている。   Conventionally, it has been proposed to produce an optical component by punching a long sheet of an optical film in a state where a surface protection film is attached using a punching blade mold.

特開2007−187781号公報JP 2007-187781 A

光学デバイス、金属板、塗装した金属板、樹脂板、ガラス板等、種々の部材(以下、「被着体」と称する)の表面を保護するために、フィルム状の基材の一方面に粘着剤層が積層されてなる表面保護粘着フィルム(一般に、プロテクトテープ、マスキングテープ、または表面保護シートなどと称される場合もある。)が用いられることがある。なお、表面保護粘着フィルムを被着体から剥がす時は、表面保護粘着フィルムの端部をつかんで引っ張ることで表面保護粘着フィルムは被着体から剥がされる。
被着体上に表面保護粘着フィルムが貼り付けられた積層体に対して上述の打ち抜きが行われた場合、打ち抜きによって得られた積層片の端部では、打ち抜き刃型で押されることで、表面保護粘着シートと部材とが強固に接着される。その結果、端部を被着体から剥がすことが困難となることがある。
光学部材には、プリズムシートや拡散フィルムなどのように、表面が凹凸形状になっているものがある。特に、このような凹凸を有する部材に対して表面保護粘着シートが貼り付けられるときは、打ち抜きによって、凹凸内に表面保護粘着シートの粘着剤が入り込み、特に端部の引き剥がしが困難となる。
本発明の課題は、被着体と表面保護粘着フィルムとの積層体を打ち抜いて得られた打ち抜き片であっても、表面保護粘着フィルムの端部をつかんで引っ張ることにより表面保護粘着フィルムを被着体から容易に剥がすことができる表面保護粘着フィルムを提供することである。
In order to protect the surface of various members such as optical devices, metal plates, painted metal plates, resin plates, glass plates, etc. (hereinafter referred to as “adhered bodies”), it adheres to one side of a film-like substrate. A surface protective adhesive film (in general, sometimes referred to as a protective tape, a masking tape, or a surface protective sheet) in which an agent layer is laminated may be used. When the surface protective adhesive film is peeled off from the adherend, the surface protective adhesive film is peeled off from the adherend by grasping and pulling the end of the surface protective adhesive film.
When the above-mentioned punching is performed on the laminate in which the surface protective adhesive film is adhered on the adherend, the end of the laminated piece obtained by punching is pressed with a punching blade mold, The protective adhesive sheet and the member are firmly bonded. As a result, it may be difficult to remove the end from the adherend.
Some optical members have an uneven surface, such as a prism sheet or a diffusion film. In particular, when a surface protective adhesive sheet is attached to a member having such irregularities, the adhesive of the surface protective adhesive sheet enters the irregularities by punching, and it is particularly difficult to peel off the edges.
The problem of the present invention is that even if a punched piece obtained by punching a laminate of an adherend and a surface protective adhesive film is used, the surface protective adhesive film is covered by grasping and pulling the end of the surface protective adhesive film. An object of the present invention is to provide a surface protective adhesive film that can be easily peeled off from a body.

本発明の粘着剤組成物は、
重合体(ii):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは1以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)で表される構造を有する共重合体(II)またはその水素添加物
を含有し、
又は、
重合体(i):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体(I)またはその水素添加物と、
前記重合体(ii)と、を含有し、
前記重合体(i)および前記重合体(ii)の全体の芳香族アルケニル化合物単位含有率(St(A+B))は、30〜50重量%であり、
前記重合体(i)および前記重合体(ii)にそれぞれ含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比(A:B)が5:95〜25:75の範囲内であり、
さらに、
イミン系化合物及び脂肪酸アミドの少なくとも一方を含有する。
重合体ブロックA:
芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロック
重合体ブロックB:
共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロック
The pressure-sensitive adhesive composition of the present invention is
Polymer (ii): Including the following polymer block A and the following polymer block B, the general formula A-B-A (the symbols in the formula are as defined above) or the general formula (A-B) x A copolymer (II) having a structure represented by -Y (wherein x represents an integer of 1 or more, Y represents a coupling agent residue, and other symbols are as defined above), Containing its hydrogenated product,
Or
Polymer (i): comprising the following polymer block A and the following polymer block B, the general formula [AB] n (wherein A is the polymer block A, B is the polymer block B, n is A copolymer (I) having a structure represented by the formula (1) or a hydrogenated product thereof:
Containing the polymer (ii),
The overall aromatic alkenyl compound unit content (St (A + B)) of the polymer (i) and the polymer (ii) is 30 to 50% by weight,
The weight ratio (A: B) of the total amount of the polymer block A and the total amount of the polymer block B contained in each of the polymer (i) and the polymer (ii) is in the range of 5:95 to 25:75. And
further,
Contains at least one of an imine compound and a fatty acid amide.
Polymer block A:
Polymer block having a series of aromatic alkenyl compound units and mainly consisting of aromatic alkenyl compound units Polymer block B:
An aromatic alkenyl-conjugated diene copolymer block containing a conjugated diene unit and an aromatic alkenyl compound unit at random, wherein the aromatic alkenyl compound unit content (St (b)) is 10 to 35% by weight. Combined block

本発明の表面保護粘着フィルムによれば、被着体と表面保護粘着フィルムとの積層体を打ち抜いて得られた打ち抜き片であっても、表面保護粘着フィルムの端部をつかんで引っ張ることにより表面保護粘着フィルムを被着体から容易に剥がすことができる。   According to the surface protective pressure-sensitive adhesive film of the present invention, even a punched piece obtained by punching a laminate of an adherend and a surface protective pressure-sensitive adhesive film is obtained by grasping and pulling the edge of the surface protective pressure-sensitive adhesive film. The protective adhesive film can be easily peeled off from the adherend.

本発明の一態様の表面保護粘着フィルムが適用されるプリズムシートの斜視図である。It is a perspective view of the prism sheet to which the surface protection adhesive film of one mode of the present invention is applied. 本発明の一実施形態の表面保護粘着フィルムがプリズムシートに貼付された積層体の構造を示す断面図である。It is sectional drawing which shows the structure of the laminated body by which the surface protection adhesive film of one Embodiment of this invention was affixed on the prism sheet.

<本明細書中の記号の定義>
本明細書において数値範囲を表すために用いられる記号「〜」は、特に記載の無い限り、当該数値範囲がその両端の数値を含むことを意図して用いられる。
本明細書において、用語「芳香族アルケニル化合物単位含有率」等において用いられる重合体の繰り返し単位の「含有率」とは、繰り返し単位が由来するモノマーに換算した重量比、すなわち、前記重合体を形成するための全モノマーの重量に対する、前記繰り返し単位が由来するモノマーの重量の比(重量%)、すなわち重合体の芳香族アルケニル化合物含量[alkenyl aromatic compound content]を意味する。ここで、「前記重合体を形成するための全モノマーの重量」は、前記重合体の重量に近似する。また、同様に、本明細書において、重合体ブロックの繰り返し単位の「含有率」とは、繰り返し単位が由来するモノマーに換算した重量比、すなわち、前記重合体ブロックを形成するための全モノマーの重量に対する、前記繰り返し単位が由来するモノマーの重量の比(重量%)を意味する。ここで、「前記重合体ブロックを形成するための全モノマーの重量」は、前記重合体ブロックの重量に近似する。
本明細書において、「ビニル結合の含有率」は、赤外吸収スペクトル法を用い、モレロ法により算出した1,2−ビニル結合および3,4−ビニル結合の総含有率を意味する。
<Definition of symbols in this specification>
The symbol “˜” used to represent a numerical range in this specification is used with the intention that the numerical range includes the numerical values at both ends unless otherwise specified.
In the present specification, the “content” of the repeating unit of the polymer used in the term “aromatic alkenyl compound unit content” or the like means the weight ratio in terms of the monomer from which the repeating unit is derived, that is, the polymer. The ratio (wt%) of the weight of the monomer from which the repeating unit is derived to the weight of all monomers to be formed, that is, the alkenyl aromatic compound content of the polymer. Here, the “weight of all monomers for forming the polymer” approximates the weight of the polymer. Similarly, in the present specification, the “content ratio” of the repeating unit of the polymer block is the weight ratio converted to the monomer from which the repeating unit is derived, that is, the total monomer for forming the polymer block. It means the ratio (% by weight) of the weight of the monomer from which the repeating unit is derived to the weight. Here, the “weight of all monomers for forming the polymer block” approximates the weight of the polymer block.
In the present specification, the “vinyl bond content” means the total content of 1,2-vinyl bonds and 3,4-vinyl bonds calculated by the Morero method using an infrared absorption spectrum method.

<粘着剤組成物>
本発明の粘着剤組成物は、下記重合体(ii)を含有する。粘着剤組成物は、下記重合体(i)をさらに含有してもよい。本明細書中、「重合体(i)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体(I)またはその水素添加物である。
本明細書中、「重合体(ii)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは2以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)
で表される構造を有する共重合体(II)またはその水素添加物である。
なお、本明細書中、前記重合体(i)と前記重合体(ii)とからなる組成物を、単に「共重合体組成物」と称する場合がある。
<Adhesive composition>
The pressure-sensitive adhesive composition of the present invention contains the following polymer (ii). The pressure-sensitive adhesive composition may further contain the following polymer (i). In the present specification, the “polymer (i)” includes the following polymer block A and the following polymer block B, and is represented by the general formula [AB] n (wherein A represents the polymer block A and B represents The polymer block B is a copolymer (I) having a structure represented by n represents an integer of 1 to 3) or a hydrogenated product thereof.
In the present specification, the “polymer (ii)” includes the following polymer block A and the following polymer block B, and is represented by the general formula A-B-A (the symbols in the formula are as defined above) or General formula (AB) xY (wherein x represents an integer of 2 or more, Y represents a coupling agent residue, and other symbols are as defined above).
Or a hydrogenated product thereof.
In the present specification, a composition comprising the polymer (i) and the polymer (ii) may be simply referred to as a “copolymer composition”.

本発明の粘着剤組成物において、前記重合体(i)および前記重合体(ii)の全体の芳香族アルケニル化合物単位含有率は、30〜50重量%であり、
前記重合体(i)と前記重合体(ii)に含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比が5:95〜25:75の範囲内である。
In the pressure-sensitive adhesive composition of the present invention, the total aromatic alkenyl compound unit content of the polymer (i) and the polymer (ii) is 30 to 50% by weight,
The weight ratio of the total amount of the polymer block A and the total amount of the polymer block B contained in the polymer (i) and the polymer (ii) is in the range of 5:95 to 25:75.

本明細書中、「重合体ブロックA」は、芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロックである。   In the present specification, the “polymer block A” is a polymer block in which aromatic alkenyl compound units are continuous and mainly composed of aromatic alkenyl compound units.

本明細書中、「重合体ブロックB」は、共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロックである。
粘着剤組成物は、イミン系化合物及び脂肪酸アミドの少なくとも一方を含有する。これによって、表面保護粘着フィルムとして充分な粘着力が得られると共に、表面保護粘着フィルムの端部を被着体から剥がし易くなる。すなわち、表面保護粘着フィルムを被着体から剥がす時に表面保護粘着フィルムの端部が被着体から容易に剥がせるようになるため、引き剥がす際に端部がつかみやすくなり、表面保護粘着フィルムを被着体から剥がすことができる端部を探しあてる必要が無く、直ちに引き剥がすことができる。したがって、打ち抜きによって表面保護粘着フィルムと被着体とが強く圧着されたとしても、表面保護粘着フィルムの端部が被着体と強く接着してしまうことで被着体から表面保護粘着フィルムが剥がしにくくなるという現象の発生を抑えることができる。
イミン系化合物の含有量は、前記重合体(i)および前記重合体(ii)の合計重量100重量部に対して、0.2重量部以上であることが好ましく、1.5重量部以下であることが好ましい。
イミン系化合物としては、例えば、ポリエチレンイミン、オクタデシルイソシアネート変性ポリエチレンイミン等が挙げられる。市販品としては、例えば、日本触媒社製の「エポミン20」等が挙げられる。
脂肪酸アミドの含有量は、前記重合体(i)および前記重合体(ii)の合計重量100重量部に対して、0.15重量部以上であることが好ましく、3.5重量部以下であることが好ましい。
脂肪酸アミドとしては、例えば、エチレンビスステアリン酸アミド、メチレンビスステアリン酸アミド、およびヘキサメチレンビスステアリン酸アミド等の飽和脂肪酸脂肪族ビスアミド;ならびにm−キシリレンビスステアリン酸アミド、およびN−N’−ジステアリルイソフタル酸アミド等の飽和脂肪酸芳香族ビスアミドが好ましい。飽和脂肪酸脂肪族ビスアミドのなかでは、エチレンビスステアリン酸アミドがより好ましい。また、飽和脂肪酸芳香族ビスアミドのなかでは、m−キシリレンビスステアリン酸アミドがより好ましい。これらの飽和脂肪酸ビスアミドは単独で用いてよく、2種以上を組み合わせて用いてもよい。
イミン系化合物及び/又は脂肪酸アミドの含有量が少なすぎると表面保護粘着フィルムの端部が被着体から剥がしづらくなる。また、イミン系化合物及び/又は脂肪酸アミドの含有量が多すぎると表面保護粘着フィルムの被着体への粘着力の安定性が低下することがあったり、粘着剤に含まれる一部の成分が被着体に付着し被着体を汚染したりすることがある。
In the present specification, the “polymer block B” is an aromatic alkenyl-conjugated diene copolymer block in which a conjugated diene unit and an aromatic alkenyl compound unit are randomly included, and the aromatic alkenyl compound unit content (St (B)) is a polymer block of 10 to 35% by weight.
The pressure-sensitive adhesive composition contains at least one of an imine compound and a fatty acid amide. Thereby, sufficient adhesive force as a surface protective adhesive film can be obtained, and the end of the surface protective adhesive film can be easily peeled off from the adherend. That is, when the surface protective adhesive film is peeled off from the adherend, the end of the surface protective adhesive film can be easily peeled off from the adherend. It is not necessary to find an end that can be peeled off from the adherend, and can be peeled off immediately. Therefore, even if the surface protective adhesive film and the adherend are strongly pressed by punching, the end portion of the surface protective adhesive film adheres strongly to the adherend, so that the surface protective adhesive film is peeled off from the adherend. Occurrence of the phenomenon of becoming difficult can be suppressed.
The content of the imine compound is preferably 0.2 parts by weight or more with respect to 100 parts by weight of the total weight of the polymer (i) and the polymer (ii), and 1.5 parts by weight or less. Preferably there is.
Examples of the imine compound include polyethyleneimine and octadecyl isocyanate-modified polyethyleneimine. Examples of commercially available products include “Epomin 20” manufactured by Nippon Shokubai Co., Ltd.
The content of the fatty acid amide is preferably 0.15 parts by weight or more and 3.5 parts by weight or less with respect to 100 parts by weight of the total weight of the polymer (i) and the polymer (ii). It is preferable.
Examples of fatty acid amides include saturated fatty acid aliphatic bisamides such as ethylene bis stearamide, methylene bis stearamide, and hexamethylene bis stearamide; and m-xylylene bis stearamide, and NN′— Saturated fatty acid aromatic bisamides such as distearyl isophthalic acid amide are preferred. Among the saturated fatty acid aliphatic bisamides, ethylene bis stearamide is more preferable. Of the saturated fatty acid aromatic bisamides, m-xylylene bisstearic acid amide is more preferred. These saturated fatty acid bisamides may be used alone or in combination of two or more.
If the content of the imine compound and / or fatty acid amide is too small, the end portion of the surface protective adhesive film is difficult to peel off from the adherend. Moreover, when there is too much content of an imine type compound and / or fatty acid amide, the stability of the adhesive force to the adherend of the surface protective adhesive film may decrease, or some components contained in the adhesive It may adhere to the adherend and contaminate the adherend.

<重合体ブロックA>
上述のように、「重合体ブロックA」は、芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロックである。
<Polymer block A>
As described above, the “polymer block A” is a polymer block in which aromatic alkenyl compound units are continuous and mainly composed of aromatic alkenyl compound units.

「芳香族アルケニル化合物単位」とは、芳香族アルケニル化合物に由来する繰り返し単位である。「芳香族アルケニル化合物」としては、例えば、スチレン、tert−ブチルスチレン、α−メチルスチレン、p−メチルスチレン、p−エチルスチレン、ジビニルベンゼン、1,1−ジフェニルエチレン、ビニルナフタレン、ビニルアントラセン、N,N−ジェチル−p−アミノエチルスチレンおよびビニルピリジン等を挙げることができる。中でも、原料が工業的に入手し易いという理由から、「芳香族アルケニル化合物単位」はスチレン単位であることが好ましい。   The “aromatic alkenyl compound unit” is a repeating unit derived from an aromatic alkenyl compound. Examples of the “aromatic alkenyl compound” include styrene, tert-butylstyrene, α-methylstyrene, p-methylstyrene, p-ethylstyrene, divinylbenzene, 1,1-diphenylethylene, vinylnaphthalene, vinylanthracene, N , N-Jetyl-p-aminoethylstyrene, vinylpyridine and the like. Among them, the “aromatic alkenyl compound unit” is preferably a styrene unit because the raw materials are easily industrially available.

「重合体ブロックA」は、芳香族アルケニル化合物単位を主たる繰り返し単位として構成されている必要がある。具体的には、その芳香族アルケニル化合物単位含有率は、80重量%以上である。芳香族アルケニル化合物単位含有率を80重量%以上と高くすることにより、粘着剤組成物の熱可塑性を向上させることができ、粘着剤組成物のリサイクルがより容易になるという利点がある。20重量%未満の範囲で含まれていてもよい芳香族アルケニル化合物単位以外の繰り返し単位としては、芳香族アルケニル化合物と共重合可能な化合物に由来する繰り返し単位、例えば、共役ジエン化合物や(メタ)アクリル酸エステル化合物に由来する繰り返し単位を挙げることができる。中でも、1,3−ブタジエン、イソプレンが、芳香族アルケニル化合物との共重合性が高いという理由から好ましい。   The “polymer block A” needs to be composed of an aromatic alkenyl compound unit as a main repeating unit. Specifically, the aromatic alkenyl compound unit content is 80% by weight or more. By making the aromatic alkenyl compound unit content as high as 80% by weight or more, there is an advantage that the thermoplasticity of the pressure-sensitive adhesive composition can be improved and recycling of the pressure-sensitive adhesive composition becomes easier. The repeating unit other than the aromatic alkenyl compound unit that may be contained in an amount of less than 20% by weight includes a repeating unit derived from a compound copolymerizable with the aromatic alkenyl compound, such as a conjugated diene compound or (meth). Mention may be made of repeating units derived from acrylic ester compounds. Of these, 1,3-butadiene and isoprene are preferred because of their high copolymerizability with aromatic alkenyl compounds.

<重合体ブロックB>
上述のように、「重合体ブロックB」は、共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロックである。
<Polymer block B>
As described above, the “polymer block B” is an aromatic alkenyl-conjugated diene copolymer block in which conjugated diene units and aromatic alkenyl compound units are randomly included, and the aromatic alkenyl compound unit content (St (B)) is a polymer block of 10 to 35% by weight.

「重合体ブロックB」を構成する「共役ジエン化合物単位」とは、共役ジエン化合物に由来する繰り返し単位である。「共役ジエン化合物」としては、例えば、1,3−ブタジエン、イソプレン、2,3−ジメチル−1,3−ブタジエン、1,3−ペンタジエン、2−メチル−1,3−オクタジエン、1,3−ヘキサジエン、1,3−シクロヘキサジエン、4,5−ジエチルー1,3−オクタジエン、3−ブチル−1,3−オクタジエン、ミルセンおよびクロロプレン等を挙げることができる。中でも、重合反応性が高く、原料が工業的に入手し易いという理由から、「共役ジエン化合物単位」は1,3−ブタジエン単位およびイソプレン単位の群から選択される少なくとも1種の繰り返し単位であることが好ましい。   The “conjugated diene compound unit” constituting the “polymer block B” is a repeating unit derived from a conjugated diene compound. Examples of the “conjugated diene compound” include 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 2-methyl-1,3-octadiene, 1,3- Examples include hexadiene, 1,3-cyclohexadiene, 4,5-diethyl-1,3-octadiene, 3-butyl-1,3-octadiene, myrcene, and chloroprene. Among them, the “conjugated diene compound unit” is at least one repeating unit selected from the group of 1,3-butadiene units and isoprene units because of high polymerization reactivity and easy availability of raw materials industrially. It is preferable.

「重合体ブロックB」は、共役ジエン化合物単位を主たる繰り返し単位として構成されている必要がある。本発明の効果を発揮させる観点から、共役ジエン化合物単位含有率が65〜90重量%の範囲内であることが好ましい。   The “polymer block B” needs to be composed of a conjugated diene compound unit as a main repeating unit. From the viewpoint of exerting the effects of the present invention, the conjugated diene compound unit content is preferably in the range of 65 to 90% by weight.

また、「重合体ブロックB」は、本発明の効果を得る観点から、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%の範囲内である必要があり、13〜33重量%の範囲内であることが好ましく、16〜30重量%の範囲内であることがより好ましい。芳香族アルケニル化合物単位含有率が10重量%未満では、展開性が重く、ハンドリング性が悪くなることがある。一方、35重量%を超えると、粘着剤組成物の柔軟性が劣り、表面保護粘着フィルムに重要な、十分な粘着力を確保できないことがある。
なお、「重合体ブロックB」は、本発明の効果を妨げない範囲において、共役ジエン化合物単位、および芳香族アルケニル化合物単位以外の繰り返し単位も含んでいてもよい。
Further, from the viewpoint of obtaining the effects of the present invention, the “polymer block B” needs to have an aromatic alkenyl compound unit content (St (b)) in the range of 10 to 35% by weight, and 13 to 33. It is preferably in the range of wt%, more preferably in the range of 16-30 wt%. When the aromatic alkenyl compound unit content is less than 10% by weight, the developability is heavy and the handling property may be deteriorated. On the other hand, when it exceeds 35 wt%, the flexibility of the pressure-sensitive adhesive composition is inferior, and sufficient adhesive force important for the surface protective pressure-sensitive adhesive film may not be ensured.
The “polymer block B” may also contain a repeating unit other than the conjugated diene compound unit and the aromatic alkenyl compound unit as long as the effects of the present invention are not hindered.

また、「重合体ブロックB」は、本発明の効果を発揮させる観点から、ビニル結合含有率が50〜90%の範囲内であることが好ましく、60〜80%の範囲内であることがより好ましい。また、ビニル結合含有率を50%以上とすることにより、タックと粘着力のバランスに優れた粘着剤組成物を構成することができるという利点がある。   The “polymer block B” preferably has a vinyl bond content in the range of 50 to 90% and more preferably in the range of 60 to 80% from the viewpoint of exerting the effects of the present invention. preferable. Moreover, there exists an advantage that the adhesive composition excellent in the balance of tack | tuck and adhesive force can be comprised by making a vinyl bond content rate into 50% or more.

<共重合体(I)>
「共重合体(I)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体である。
<Copolymer (I)>
The “copolymer (I)” includes the following polymer block A and the following polymer block B, and is represented by the general formula [AB] n (wherein A is the polymer block A and B is the polymer block B). , N represents an integer of 1 to 3.).

「n」が1〜3の整数を表すことから、明らかなように、「式[A−B]nで表される構造」としては、例えば、A−B、A−B−A−B、およびA−B−A−B−A−Bで表されるの構造が挙げられる。これらのブロック共重合体においては、AおよびBは、それぞれ繰り返しにおいて同一であってもよく、異なっていてもよい。   As “n” represents an integer of 1 to 3, as is clear, examples of the “structure represented by the formula [A-B] n” include AB, ABAB, And a structure represented by A-B-A-B-A-B. In these block copolymers, A and B may be the same or different in repetition.

[A−B]nで示される構造において、重合体ブロックBの効果を確実に発揮させる観点から、末端の重合体ブロックBは共重合体全体の2重量%以上を占めていることが好ましい。なお、一部の共重合体(I)の末端が−Aの構造を有していても、末端の重合体ブロックAの含有率が共重合体(I)全体の2重量%未満である場合には、末端が重合体ブロックBであるのと同様の効果を発揮させることができる。すなわち、前記構造は実質的に末端が重合体ブロックBであるとみなすことができる。   In the structure represented by [A-B] n, it is preferable that the terminal polymer block B occupies 2% by weight or more of the entire copolymer from the viewpoint of reliably exhibiting the effect of the polymer block B. Even when the terminal of some of the copolymers (I) has a structure of -A, the content of the terminal polymer block A is less than 2% by weight of the entire copolymer (I). Can exhibit the same effect as the terminal being the polymer block B. That is, the structure can be regarded as having a polymer block B at the end.

nは1〜3の整数であることが必要である。nをこの範囲内とすることにより、工業的
な生産性が良好となる。なお、粘着力および材料強度を向上させるという観点から、nが1〜2であることがより好ましく、1であることが特に好ましい。すなわち、「一般式[A−B]nで示される構造を有する共重合体」としては、一般式A−Bで示される構造を有するブロック共重合体が特に好ましい。
n needs to be an integer of 1 to 3. Industrial productivity becomes favorable by making n into this range. In addition, from the viewpoint of improving adhesive strength and material strength, n is more preferably 1 to 2, and particularly preferably 1. That is, as the “copolymer having a structure represented by the general formula [AB] n”, a block copolymer having a structure represented by the general formula AB is particularly preferable.

共重合体(I)またはその水素添加物(重合体(i))は、芳香族アルケニル化合物単位含有率が30〜50重量の範囲内であることが好ましく、33〜45重量%であることがより好ましい。芳香族アルケニル化合物単位含有率をこの範囲内とすることにより、適度な保持力と、被着体表面の凹凸への追随性を兼ね備え、かつ展開性に優れた粘着剤組成物を構成することが可能となる。   The copolymer (I) or its hydrogenated product (polymer (i)) preferably has an aromatic alkenyl compound unit content in the range of 30 to 50% by weight, and is preferably 33 to 45% by weight. More preferred. By setting the aromatic alkenyl compound unit content in this range, it is possible to constitute a pressure-sensitive adhesive composition having an appropriate holding power and followability to the unevenness of the adherend surface, and having excellent spreadability. It becomes possible.

重合体(i)の分子量については特に制限はないが、重量平均分子量が3万〜50万であることが好ましく、8万〜30万であることが更に好ましく、10万〜20万であることが特に好ましい。重量平均分子量を3万〜50万の範囲とすることで、重合体(i)、ひいては重合体(i)と共重合体(II)またはその水素添加物(重合体(ii))とからなる共重合体組成物の工業的な生産を容易なものとすることができる。重量平均分子量が3万未満であると、ポリマーを脱溶媒、乾燥させる工程において製造設備等にポリマーが付着してしまい、重合体(i)の工業的生産が困難となる場合がある。一方、重量平均分子量が50万以上であると、溶剤への溶解性や熱溶融性が悪くなり、粘着体への加工が困難になる場合がある。   The molecular weight of the polymer (i) is not particularly limited, but the weight average molecular weight is preferably 30,000 to 500,000, more preferably 80,000 to 300,000, and 100,000 to 200,000. Is particularly preferred. By setting the weight average molecular weight in the range of 30,000 to 500,000, the polymer (i), and thus the polymer (i) and the copolymer (II) or a hydrogenated product thereof (polymer (ii)) are formed. Industrial production of the copolymer composition can be facilitated. When the weight average molecular weight is less than 30,000, the polymer adheres to the production equipment or the like in the step of removing the solvent and drying the polymer, and industrial production of the polymer (i) may be difficult. On the other hand, when the weight average molecular weight is 500,000 or more, the solubility in a solvent and the heat melting property are deteriorated, and it may be difficult to process the pressure-sensitive adhesive body.

共重合体(I)の水素添加物は、優れた耐熱性および耐候性が得られることから
、共役ジエンモノマーに由来する二重結合が80%以上、好ましくは90%以上、より好ましくは95%以上、水素添加により不飽和結合が飽和結合に水素添加された水素添加物であることが好ましい。
。なお、本明細書中、水素添加の比率(水素添加率)は、四塩化炭素を溶媒として用い、270MHz、H−NMRスペクトルから算出した水素添加率を意味する。
重合体(i)は、単独(1種)であってもよく、2種以上の組み合わせであってもよい。
Since the hydrogenated copolymer (I) has excellent heat resistance and weather resistance, the double bond derived from the conjugated diene monomer is 80% or more, preferably 90% or more, more preferably 95%. As described above, a hydrogenated product in which an unsaturated bond is hydrogenated to a saturated bond by hydrogenation is preferable.
. In the present specification, the ratio of hydrogenation (hydrogenation rate) means a hydrogenation rate calculated from a 270 MHz, 1 H-NMR spectrum using carbon tetrachloride as a solvent.
The polymer (i) may be a single type (one type) or a combination of two or more types.

<共重合体(II)>
「共重合体(II)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは2以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)
で表される構造を有する共重合体である。
<Copolymer (II)>
The “copolymer (II)” includes the following polymer block A and the following polymer block B, and is represented by the general formula ABA (the symbols in the formula are as defined above) or the general formula (A -B) x-Y (wherein x represents an integer of 2 or more, Y represents a coupling agent residue, and other symbols are as defined above).
It is a copolymer which has a structure represented by these.

前記一般式から明らかなように、共重合体(II)は、その全ての分子末端に重合体ブロックAを有する。
末端の重合体ブロックAは共重合体(II)全体の2重量%以上を占めていることが好ましい。重合体ブロックAの効果を確実に発揮させるためである。なお、一部の共重合体(II)の末端が−Bの構造を有していても、末端の重合体ブロックBの含有率が共重合体(II)全体の2重量%未満である場合には、末端が重合体ブロックAであるのと同様の効果を発揮させることができる。すなわち、前記構造は実質的に末端が重合体ブロックAであるとみなすことができる。
As is apparent from the above general formula, the copolymer (II) has a polymer block A at all molecular terminals.
The terminal polymer block A preferably accounts for 2% by weight or more of the entire copolymer (II). This is to ensure that the effect of the polymer block A is exhibited. Even if the terminal of some of the copolymers (II) has a structure of -B, the content of the terminal polymer block B is less than 2% by weight of the entire copolymer (II). Can exhibit the same effect as that of the polymer block A at the end. That is, the structure can be regarded as having the polymer block A at the end.

一般式(A−B)x−Y(式中、xは2以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)で表される構造を有する共重合体は、言い換えれば、共重合体(I)がYによってカップリングした構造を有する。従って、(A−B)x−Yの場合、同じ反応釜で、(I)、(II)の混合物を合成することが出来るため、工業的な観点から、(A−B)x−Yの方が好ましい。xが3以上である場合、当該共重合体は、いわゆる星形重合体である。xは、当該共重合体製造時における副反応を抑制し、当該共重合体の物性を制御する観点からは、好ましくは2〜4である。   A structure represented by the general formula (AB) xY (wherein x represents an integer of 2 or more, Y represents a coupling agent residue, and other symbols are as defined above). In other words, the copolymer having has a structure in which the copolymer (I) is coupled by Y. Therefore, in the case of (AB) x-Y, since the mixture of (I) and (II) can be synthesized in the same reaction kettle, from an industrial point of view, (AB) xY Is preferred. When x is 3 or more, the copolymer is a so-called star polymer. x is preferably 2 to 4 from the viewpoint of suppressing side reactions during the production of the copolymer and controlling the physical properties of the copolymer.

また、共重合体(II)またはその水素添加物(重合体(ii))も重合体(i)と同様の理由から、芳香族アルケニル化合物単位含有率が30〜50重量の範囲内であることが好ましく、33〜45重量%であることがより好ましい。   The copolymer (II) or its hydrogenated product (polymer (ii)) also has an aromatic alkenyl compound unit content in the range of 30 to 50 weights for the same reason as the polymer (i). Is preferable, and it is more preferable that it is 33 to 45 weight%.

重合体(ii)は、優れた耐熱性および耐候性が得られることから、共役ジエンモノマーに由来する二重結合が80%以上、好ましくは90%以上、より好ましくは95%以上、水素添加により不飽和結合が飽和結合に水素添加された水素添加物であることが好ましい。   Since the polymer (ii) has excellent heat resistance and weather resistance, the double bond derived from the conjugated diene monomer is 80% or more, preferably 90% or more, more preferably 95% or more. It is preferable that the unsaturated bond is a hydrogenated product obtained by hydrogenating the saturated bond.

重合体(ii)の分子量については特に制限はないが、重量平均分子量が5万〜50万であることが好ましく、5万〜30万であることがより好ましい。重量平均分子量を5万〜50万の範囲とすることで、重合体(ii)、ひいては重合体(i)と重合体(ii)とからなる共重合体組成物の工業的な生産を容易なものとすることができる。重量平均分子量が3万未満であると、ポリマーを脱溶媒、乾燥させる工程において製造設備等にポリマーが付着してしまい、共重合体(II)またはその水素添加物の工業的生産が困難となる場合がある。一方、重量平均分子量が50万以上であると、溶剤への溶解性や熱溶融性が悪くなり、粘着体への加工が困難になる場合がある。
重合体(ii)は、単独(1種)であってもよく、2種以上の組み合わせであってもよい。
The molecular weight of the polymer (ii) is not particularly limited, but the weight average molecular weight is preferably 50,000 to 500,000, and more preferably 50,000 to 300,000. By making the weight average molecular weight in the range of 50,000 to 500,000, industrial production of the polymer (ii), and thus the copolymer composition comprising the polymer (i) and the polymer (ii) can be facilitated. Can be. When the weight average molecular weight is less than 30,000, the polymer adheres to the production equipment in the process of removing the solvent and drying the polymer, making it difficult to industrially produce the copolymer (II) or its hydrogenated product. There is a case. On the other hand, when the weight average molecular weight is 500,000 or more, the solubility in a solvent and the heat melting property are deteriorated, and it may be difficult to process the pressure-sensitive adhesive body.
The polymer (ii) may be a single type (one type) or a combination of two or more types.

<共重合体組成物>
上述のように、本発明の粘着剤組成物は、重合体(ii)を構成成分として含有するか、または重合体(i)と重合体(ii)とからなる共重合体組成物を構成成分として含有する。この共重合体組成物において、重合体(i)と重合体(ii)との重量比は、90:10〜0:100の範囲内であることが好ましい。重合体(i)を含ませることにより、被着体の表面から粘着剤層が浮き上がり、フィルムが剥離してしまう不具合(浮き)を有効に防止することができるという好ましい効果を発揮させることができる。一方、重合体(i)と重合体(ii)との総量100重量部中、重合体(ii)を10重量部以上含ませることにより、被着体の表面からフィルムを剥離させる際に、被着体の表面に粘着剤が残存して被着体の表面を汚染してしまう不具合(糊残り)を有効に防止することができるという好ましい効果を発揮させることができる。
粘着剤層の浮きや糊残りをより確実に防止するという観点から、重合体(i)と重合体(ii)との重量比は50:50〜15:85の範囲内であることが好ましい。
<Copolymer composition>
As described above, the pressure-sensitive adhesive composition of the present invention contains the polymer (ii) as a constituent component or a copolymer composition comprising the polymer (i) and the polymer (ii) as a constituent component. Contained as. In this copolymer composition, the weight ratio of the polymer (i) and the polymer (ii) is preferably in the range of 90:10 to 0: 100. By including the polymer (i), it is possible to exert a preferable effect that it is possible to effectively prevent a problem (floating) in which the pressure-sensitive adhesive layer is lifted from the surface of the adherend and the film is peeled off. . On the other hand, by including 10 parts by weight or more of the polymer (ii) in 100 parts by weight of the total amount of the polymer (i) and the polymer (ii), the film is peeled off from the surface of the adherend. It is possible to exert a preferable effect that it is possible to effectively prevent a problem (glue residue) that the adhesive remains on the surface of the adherend and contaminates the surface of the adherend.
From the viewpoint of more reliably preventing the pressure-sensitive adhesive layer from being lifted and remaining glue, the weight ratio of the polymer (i) to the polymer (ii) is preferably in the range of 50:50 to 15:85.

本発明の効果を奏する観点から、前記重合体(i)と前記重合体(ii)に含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比が5:95〜25:75の範囲内であることが必要である。また、重合体ブロックAと重合体ブロックBとの総量100重量部中、重合体ブロックAを5重量部以上含ませることにより、形成される粘着剤層に適度な保持力を付与することが可能となるという好ましい効果を発揮させることができる。一方、重合体ブロックAと重合体ブロックBとの総量100重量部中、重合体ブロックBを75重量部以上含ませることにより、形成される粘着剤層が被着体表面の凹凸に対して良好な追随性を示すため、被着体表面を確実に保護することが可能となるという好ましい効果を発揮させることができる。重合体ブロックAの総量と重合体ブロックBの総量との重量比は5:95〜25:75の範囲内であることが好ましく、7:93〜23:77の範囲内であることが更に好ましく、10:90〜21:79の範囲内であることが特に好ましい。   From the viewpoint of achieving the effect of the present invention, the weight ratio of the total amount of the polymer block A and the total amount of the polymer block B contained in the polymer (i) and the polymer (ii) is 5:95 to 25:75. It is necessary to be within the range. In addition, by containing 5 parts by weight or more of the polymer block A in 100 parts by weight of the total amount of the polymer block A and the polymer block B, it is possible to impart an appropriate holding force to the formed pressure-sensitive adhesive layer. The preferable effect of becoming can be exhibited. On the other hand, by including 75 parts by weight or more of the polymer block B in 100 parts by weight of the total amount of the polymer block A and the polymer block B, the pressure-sensitive adhesive layer to be formed is good against unevenness on the surface of the adherend. Therefore, it is possible to exert a preferable effect that the surface of the adherend can be surely protected. The weight ratio of the total amount of the polymer block A and the total amount of the polymer block B is preferably in the range of 5:95 to 25:75, and more preferably in the range of 7:93 to 23:77. A range of 10:90 to 21:79 is particularly preferable.

<表面保護粘着フィルム>
本発明の表面保護粘着フィルムは、基材層と、前記で説明した本発明の粘着剤組成物からなる粘着剤層と、を有する。
好ましくは、当該粘着剤層は、当該基材層の一方の表面上に積層されている。
<Surface protective adhesive film>
The surface-protective pressure-sensitive adhesive film of the present invention has a base material layer and a pressure-sensitive adhesive layer made of the pressure-sensitive adhesive composition of the present invention described above.
Preferably, the pressure-sensitive adhesive layer is laminated on one surface of the base material layer.

<基材層>
当該基材層として好ましくは、ポリオレフィン基材層である。
当該「ポリオレフィン」としては、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖低密度ポリエチレン、エチレン−α−オレフィン共重合体、エチレン−エチルアクリレート共重合体、エチレン−酢酸ビニル共重合体、エチレン−メチルアクリレート共重合体、エチレン−n−ブチルアクリレート共重合体、およびポリプロピレン(ホモポリマー、ランダムコポリマー、ブロックコポリマー)等が挙げられる。
これらは単独または2種以上を組み合わせて用いることができる。また、「ポリオレフィン」は、置換基を有するポリオレフィンであってもよく、ポリオレフィン以外の樹脂が添加されていてもよい。さらに、表面保護粘着フィルムの製造過程で生じた、ポリオレフィン基材層の端材や表面保護粘着フィルムの端材が添加されていてもよい。
基材層は、単層でもよいし、組成の異なる2種以上の多層構造を有している層であってもよい。
基材層は、表面保護粘着フィルムの用途等によって、その厚さを適宜調整することができる。通常、10〜100μm程度の厚さに設定することが適している。
<Base material layer>
The base material layer is preferably a polyolefin base material layer.
Examples of the “polyolefin” include low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, ethylene-α-olefin copolymer, ethylene-ethyl acrylate copolymer, ethylene-vinyl acetate copolymer. Examples thereof include a copolymer, an ethylene-methyl acrylate copolymer, an ethylene-n-butyl acrylate copolymer, and polypropylene (homopolymer, random copolymer, block copolymer).
These can be used alone or in combination of two or more. The “polyolefin” may be a polyolefin having a substituent, and a resin other than the polyolefin may be added. Furthermore, the end material of the polyolefin base material layer and the end material of the surface protection adhesive film which were produced in the manufacturing process of the surface protection adhesive film may be added.
The base material layer may be a single layer or a layer having two or more multilayer structures having different compositions.
The thickness of the base material layer can be appropriately adjusted depending on the use of the surface protective adhesive film. Usually, it is suitable to set the thickness to about 10 to 100 μm.

<粘着剤層>
前記粘着剤層は、本発明の粘着剤組成物からなる。当該粘着剤組成物は、前記重合体(ii)又は前記重合体(ii)および前記重合体(i)に加えて、必要に応じて、粘着付与剤、スチレン系ブロック相補強剤、軟化剤、酸化防止剤、光安定剤、紫外線吸収剤、充填剤、顔料、粘着昂進防止剤、オレフィン系樹脂、シリコーン系ポリマー、液状アクリル系共重合体、リン酸エステル系化合物等の公知の添加剤を適宜含有してもよい。
<Adhesive layer>
The said adhesive layer consists of an adhesive composition of this invention. In addition to the polymer (ii) or the polymer (ii) and the polymer (i), the pressure-sensitive adhesive composition includes a tackifier, a styrene block phase reinforcing agent, a softening agent, if necessary. Known additives such as antioxidants, light stabilizers, UV absorbers, fillers, pigments, adhesion promoters, olefin resins, silicone polymers, liquid acrylic copolymers, phosphate ester compounds, etc. are used as appropriate. You may contain.

本発明で用いられる粘着付与剤としては、例えば、脂肪族系共重合体、芳香族系共重合体、脂肪族・芳香族系共重合体や脂環式系共重合体等の石油系樹脂、クマロン−インデン系樹脂、テルぺン系樹脂、テルぺン−フェノール系樹脂、重合ロジン等のロジン系樹脂、(アルキル)フェノール系樹脂、キシレン系樹脂またはこれらの水添物などの、一般に粘着剤に使用されるものを特に制限なく使用することができる。粘着付与剤の軟化点が、90〜140℃のものを用いることがより好ましい。これらの粘着付与剤は、単独で用いてもよく、2種以上を併用してもよい。なお、剥離性および耐候性などを高めるに、水添系の粘着付与剤を用いることがより好ましい。また、オレフィン樹脂とのブレンド物として市販されている粘着付与剤を用いてもよい。   Examples of the tackifier used in the present invention include petroleum resins such as aliphatic copolymers, aromatic copolymers, aliphatic / aromatic copolymers and alicyclic copolymers, Generally adhesives such as coumarone-indene resin, terpene resin, terpene-phenol resin, polymerized rosin resin such as rosin resin, (alkyl) phenol resin, xylene resin or hydrogenated products thereof What is used for can be used without a restriction | limiting in particular. It is more preferable to use a tackifier having a softening point of 90 to 140 ° C. These tackifiers may be used alone or in combination of two or more. In order to improve peelability and weather resistance, it is more preferable to use a hydrogenated tackifier. Moreover, you may use the tackifier marketed as a blend with an olefin resin.

本発明での粘着付与剤とは、芳香族アルケニルブロック共重合体中の共役ジエン系またはその水素添加されたソフトセグメントであるゴム層に対して相溶し、粘着力をコントロールできるものを意味する。
なお、「相溶」とは、共重合体組成物に粘着付与剤を配合することにより得られる配合物のtanδピーク温度が、共重合体組成物のtanδピーク温度とは異なる値になる状態のことをいう。なお、本明細書中、「tanδピーク温度」とは、tanδの最大となる温度を意味する。
The tackifier in the present invention means a compound that is compatible with a rubber layer that is a conjugated diene system or a hydrogenated soft segment thereof in an aromatic alkenyl block copolymer and can control the adhesive force. .
“Compatible” means that the tan δ peak temperature of a blend obtained by blending a tackifier with the copolymer composition is different from the tan δ peak temperature of the copolymer composition. That means. In the present specification, “tan δ peak temperature” means a temperature at which tan δ is maximized.

スチレン系ブロック相補強剤は、粘着剤層の粘着昂進を抑制するために用いられる。スチレン系ブロック相補強剤は、芳香族アルケニルブロック共重合体が形成する海島構造の島相を補強する剤であり、芳香族アルケニルブロック共重合体からなるドメインに相溶する性質を有する。
本発明で用いられるスチレン系ブロック相補強剤としては、例えば、モノマー単位として、スチレンおよびα−メチルスチレン、p−メチルスチレン、p−クロロスチレン、クロロメチルスチレン、tert−ブチルスチレン、p−エチルスチレン、ジビニルベンゼン等のスチレン系化合物が挙げられる。これらは、単独または2種以上を組み合わせて用いることができる。つまり、スチレン系ブロック相補強剤は、これらモノマーを重合することによって得ることができる。2種以上のモノマーからなる共重合体の場合は、ブロック共重合体であってもよいし、ランダム共重合体であってもよい。なかでも、スチレン系ブロック相補強剤は、100℃程度以上の軟化点を有するものが好ましく、150℃以上がより好ましい。具体的には、イーストマンケミカル社製、商品名「ENDEX155」(軟化点155℃)、「ENDEX160」(軟化点160℃)等が好適に使用される。
当該スチレン系ブロック相補強剤の使用量は、芳香族アルケニルブロック共重合体100重量部に対して、40重量部以下が好ましく、30重量部以下がより好ましい。また、スチレン系ブロック相補強剤の使用量は、好ましくは1重量部以上である。
The styrenic block phase reinforcing agent is used to suppress the adhesion progress of the adhesive layer. The styrenic block phase reinforcing agent is an agent that reinforces the island phase of the sea-island structure formed by the aromatic alkenyl block copolymer, and has a property of being compatible with the domain made of the aromatic alkenyl block copolymer.
Examples of the styrenic block phase reinforcing agent used in the present invention include styrene and α-methylstyrene, p-methylstyrene, p-chlorostyrene, chloromethylstyrene, tert-butylstyrene, and p-ethylstyrene as monomer units. And styrenic compounds such as divinylbenzene. These can be used alone or in combination of two or more. That is, the styrenic block phase reinforcing agent can be obtained by polymerizing these monomers. In the case of a copolymer composed of two or more types of monomers, it may be a block copolymer or a random copolymer. Among them, the styrenic block phase reinforcing agent preferably has a softening point of about 100 ° C. or higher, and more preferably 150 ° C. or higher. Specifically, trade names “ENDEX 155” (softening point 155 ° C.), “ENDEX 160” (softening point 160 ° C.) manufactured by Eastman Chemical Co., Ltd. are preferably used.
The amount of the styrenic block phase reinforcing agent used is preferably 40 parts by weight or less, more preferably 30 parts by weight or less, based on 100 parts by weight of the aromatic alkenyl block copolymer. The amount of the styrenic block phase reinforcing agent used is preferably 1 part by weight or more.

軟化剤は、通例、粘着力の向上に有効である。軟化剤としては、例えば、低分子量のジエン系ポリマー、ポリイソブチレン、水添ポリイソプレン、水添ポリブタジエン、パラフィン系プロセスオイル、ナフテン系プロセスオイル、芳香族系プロセスオイル、ひまし油、トール油、天然油、液体ポリイソブチレン樹脂、ポリブテン、液状のロジン系樹脂またはこれらの水添物などの一般的に粘着剤に使用されるものを特に制限なく使用することができる。これらの軟化剤は、単独で用いてもよく、2種以上を併用してもよい。
具体的な市販品としては、荒川化学社製、商品名「スーパーエステルL」、「スーパーエステルA18」、出光興産社製、商品名「ダイアナプロセスオイル」等が好適に使用される。
Softeners are usually effective in improving adhesive strength. Examples of the softener include low molecular weight diene polymer, polyisobutylene, hydrogenated polyisoprene, hydrogenated polybutadiene, paraffinic process oil, naphthenic process oil, aromatic process oil, castor oil, tall oil, natural oil, Those generally used for pressure-sensitive adhesives such as liquid polyisobutylene resin, polybutene, liquid rosin resin, or hydrogenated products thereof can be used without particular limitation. These softeners may be used alone or in combination of two or more.
As specific commercial products, trade names “Super Ester L”, “Super Ester A18”, Idemitsu Kosan Co., Ltd., trade name “Diana Process Oil”, etc., are preferably used.

酸化防止剤としては、特に限定されず、例えば、フェノール系(モノフェノール系、ビスフェノール系、高分子型フェノール系)、硫黄系、リン系等の通常使用されるものが挙げられる。
光安定化剤としては、ヒンダードアミン系化合物が挙げられる。
紫外線吸収剤としては、特に限定されず、例えば、サリチル酸系、ベンゾフェノン系、ベンゾトリアゾール系、シアノアクリレート系等が挙げられる。
The antioxidant is not particularly limited, and examples thereof include commonly used ones such as phenolic (monophenolic, bisphenolic, and polymeric phenolic), sulfur, and phosphorus.
Examples of the light stabilizer include hindered amine compounds.
The ultraviolet absorber is not particularly limited, and examples thereof include salicylic acid series, benzophenone series, benzotriazole series, and cyanoacrylate series.

充填剤としては、例えば、炭酸カルシウム、炭酸マグネシウム、シリカ、酸化亜鉛、酸化チタン等が挙げられる。
粘着昂進防止剤としては、大豆油変性アルキド樹脂(例えば、荒川化学工業社製、商品名「アラキード251」等)、トール油変性アルキド樹脂(例えば、荒川化学工業社製、商品名「アラキード6300」等)などが挙げられる。
これらの添加剤は、単独で使用してもよいし、2種以上を併用してもよい。
Examples of the filler include calcium carbonate, magnesium carbonate, silica, zinc oxide, and titanium oxide.
Examples of the anti-adhesion progressing agent include soybean oil-modified alkyd resin (for example, trade name “Arachid 251” manufactured by Arakawa Chemical Industries, Ltd.), tall oil-modified alkyd resin (for example, product name “Arachid 6300” manufactured by Arakawa Chemical Industries, Ltd.). Etc.).
These additives may be used alone or in combination of two or more.

粘着剤層の厚さは特に制限されないが、例えば、通常0.5〜50μm程度、好ましくは1〜40μm、さらに好ましくは2〜30μmである。   Although the thickness in particular of an adhesive layer is not restrict | limited, For example, it is about 0.5-50 micrometers normally, Preferably it is 1-40 micrometers, More preferably, it is 2-30 micrometers.

ここで、粘着付与剤としては、前記で例示したものなどを用いることができる。
粘着付与剤は、表面保護粘着フィルムを被着体から剥離する際の糊残りを防止できる量で使用することが適している。例えば、プリズムシート用の表面保護粘着フィルムとして使用する場合には、粘着剤組成物における粘着付与剤の含有量は、ゴム系樹脂成分[前記重合体(ii)、または前記重合体(i)および前記重合体(ii)(以下、これらをまとめて、芳香族アルケニルブロック共重合体と称する場合がある。)]100重量部に対し、好ましくは20重量部以上であり、より好ましくは20〜50重量部であり、さらに好ましくは25〜40重量部である。
粘着剤付与剤の含有量が20重量部以上であることで、帯電防止処理が施されている光学フィルムに対して、十分な初期粘着力を得ることができる。また、粘着剤付与剤の含有量が50重量部以下であることで、糊残りの発生が抑制される。
Here, as the tackifier, those exemplified above can be used.
It is suitable that the tackifier is used in an amount capable of preventing adhesive residue when the surface protective adhesive film is peeled off from the adherend. For example, when used as a surface protective pressure-sensitive adhesive film for a prism sheet, the content of the tackifier in the pressure-sensitive adhesive composition is the rubber-based resin component [the polymer (ii) or the polymer (i) and The polymer (ii) (hereinafter, these may be collectively referred to as an aromatic alkenyl block copolymer)] is preferably 20 parts by weight or more, more preferably 20 to 50 parts per 100 parts by weight. Parts by weight, more preferably 25 to 40 parts by weight.
When the content of the pressure-sensitive adhesive imparting agent is 20 parts by weight or more, sufficient initial pressure-sensitive adhesive strength can be obtained for an optical film that has been subjected to antistatic treatment. Moreover, generation | occurrence | production of the adhesive residue is suppressed because content of an adhesive provision agent is 50 weight part or less.

軟化剤は、表面保護粘着フィルムを被着体から剥離する際の糊残りを抑制できる量で使用することが好ましい。例えば、プリズムシート用の表面保護粘着フィルムとして使用する場合には、粘着剤組成物における軟化剤の含有量は、芳香族アルケニルブロック共重合体100重量部に対し、2〜10重量が好ましく、より好ましくは3〜8重量部である。
軟化剤の含有量が2重量部以上であることで、帯電防止処理が施されている光学フィルムに対しても、十分な初期粘着力が得られる。10重量部以下であることで、展開力が重くならず、糊残りの発生が抑制される。
表面保護粘着フィルムは、粘着剤層中に、前記重合体(ii)、または前記重合体(i)および前記重合体(ii)に加えて、特定の割合で粘着付与剤と軟化剤とを含有することにより、特に帯電防止処理が施されている光学フィルムに対して、初期粘着力を確保しつつ、展開性に優れ、被着体に対する糊残りを抑制することができる。
The softening agent is preferably used in an amount that can suppress the adhesive residue when the surface protective adhesive film is peeled off from the adherend. For example, when used as a surface protective pressure-sensitive adhesive film for a prism sheet, the content of the softener in the pressure-sensitive adhesive composition is preferably 2 to 10 weights with respect to 100 parts by weight of the aromatic alkenyl block copolymer. Preferably it is 3-8 weight part.
When the content of the softening agent is 2 parts by weight or more, sufficient initial adhesive force can be obtained even for an optical film that has been subjected to antistatic treatment. By being 10 parts by weight or less, the deployment force is not increased, and the occurrence of adhesive residue is suppressed.
The surface protective adhesive film contains a tackifier and a softener in a specific ratio in addition to the polymer (ii) or the polymer (i) and the polymer (ii) in the adhesive layer. By doing so, it is possible to suppress the adhesive residue on the adherend with excellent developability while ensuring the initial adhesive force, particularly for the optical film that has been subjected to antistatic treatment.

<シート積層体>
上述の表面保護粘着フィルムは、シート積層体に適用可能である。
シート積層体とは、表面保護粘着フィルムと、表面保護粘着フィルムが貼り付けられた他のシートと、を備える。他のシートとしては、プリズムシート等の光学フィルムが用いられる。シート積層体において、表面保護粘着フィルムが貼り付けられる他のシートは、シート表面に帯電防止処理が施されていてもよい。
<Sheet Laminate>
The above-mentioned surface protective adhesive film can be applied to a sheet laminate.
The sheet laminate includes a surface protective adhesive film and another sheet on which the surface protective adhesive film is attached. As the other sheet, an optical film such as a prism sheet is used. In the sheet laminate, other sheets to which the surface protective adhesive film is attached may have an antistatic treatment applied to the sheet surface.

「帯電防止処理が施された」とは、帯電防止剤を含有することを包含する。帯電防止剤は特に限定されず、公知のものを使用することができる。例えば、アシロイルアミドプロピルジメチルヒドロキシエチルアンモニウムナイトレート、アシロイルアミドプロピルトリメチルアンモニウムサルフェート、セチルモルホリニウムメトサルフェートのような陽イオン系界面活性剤や、直鎖アルキルリン酸カリウム塩、ポリオキシエチレンアルキルリン酸カリウム塩、アルカンスルフォン酸塩のような陰イオン系界面活性剤、N,N−ビス(ヒドロキシエチル)−N−アルキルアミン、その脂肪酸エステル誘導体、多価アルコール脂肪酸部分エステル類のような非イオン系界面活性剤などを使用することができる。これらの帯電防止剤の配合比は、所望とする特性に合わせて適宜決められる。例えば、他のシートがその表面にコーティング層を有する場合、つまり表面保護粘着フィルムの粘着剤層がコーティング層に接着される場合、コーティング層の主成分であるバインダー樹脂100重量部あたりの帯電防止剤の含有量は、通常0.1〜10重量部程度である。   “Antistatic treatment has been applied” includes containing an antistatic agent. An antistatic agent is not specifically limited, A well-known thing can be used. For example, cationic surfactants such as acyloylamidopropyldimethylhydroxyethylammonium nitrate, acyloylamidopropyltrimethylammonium sulfate, cetylmorpholinium methosulfate, linear alkyl potassium phosphate, polyoxyethylene alkyl Nonionic surfactants such as potassium phosphate, anionic surfactant such as alkane sulfonate, N, N-bis (hydroxyethyl) -N-alkylamine, fatty acid ester derivatives thereof, polyhydric alcohol fatty acid partial esters An ionic surfactant or the like can be used. The blending ratio of these antistatic agents is appropriately determined according to desired characteristics. For example, when another sheet has a coating layer on its surface, that is, when the adhesive layer of the surface protective adhesive film is adhered to the coating layer, the antistatic agent per 100 parts by weight of the binder resin that is the main component of the coating layer The content of is usually about 0.1 to 10 parts by weight.

シート積層体において、複数の表面保護粘着フィルムと他のシートとが交互に積層されていてもよい。特に、シート積層体は、表面保護粘着フィルムが他のシートに貼り付けられた状態で巻かれた、巻回体であってもよい。   In the sheet laminate, a plurality of surface protective adhesive films and other sheets may be alternately laminated. In particular, the sheet laminate may be a wound body wound with the surface protective adhesive film attached to another sheet.

本発明の表面保護粘着フィルムが適用されるプリズムシートのレンズ部は、実質的に3角柱からなるプリズム形状を有する。本明細書中、このようなプリズム形状のレンズ部を有する面をプリズム面と称する。より具体的には、図1に示すように、プリズムシート1は、平坦なシート部2の一方面に複数本の三角柱状のレンズ部3が一体化された構造を有する。レンズ部3は、実質的に三角柱の形状を有する。そして、三角柱の各稜線が平行となるように、複数のレンズ部3が密接して並設されている。このプリズム形状のレンズ部3の外表面が本発明の表面保護粘着フィルムにより保護される。   The lens portion of the prism sheet to which the surface protective adhesive film of the present invention is applied has a prism shape substantially consisting of a triangular prism. In the present specification, a surface having such a prism-shaped lens portion is referred to as a prism surface. More specifically, as shown in FIG. 1, the prism sheet 1 has a structure in which a plurality of triangular prism-shaped lens portions 3 are integrated on one surface of a flat sheet portion 2. The lens unit 3 has a substantially triangular prism shape. A plurality of lens portions 3 are closely arranged in parallel so that the ridge lines of the triangular prism are parallel to each other. The outer surface of the prism-shaped lens portion 3 is protected by the surface protective adhesive film of the present invention.

例えば、図2に断面図で示すように、プリズムシート1のレンズ部3が設けられている部分に、第1の表面保護粘着フィルム4(本発明の表面保護粘着フィルム)が貼付される。第1の表面保護粘着フィルム4は、基材層5と、基材層5の一方面に設けられた粘着剤層6とを有し、粘着剤層6側から、プリズムシート1の上記複数のレンズ部3が設けられている側に貼付される。従って、本発明の表面保護粘着フィルムは、三角柱状のレンズ部3の複数の頂部3aに接するように貼付される。また、この三角柱のレンズ部3の横断面形状は三角形であるが、この三角形は、好ましくはシートに固定されている側面を底辺とした二等辺三角形である。   For example, as shown in a cross-sectional view in FIG. 2, the first surface protective adhesive film 4 (surface protective adhesive film of the present invention) is attached to the portion of the prism sheet 1 where the lens portion 3 is provided. The first surface protective pressure-sensitive adhesive film 4 has a base material layer 5 and a pressure-sensitive adhesive layer 6 provided on one surface of the base material layer 5, and the plurality of prism sheets 1 from the pressure-sensitive adhesive layer 6 side. It is affixed to the side where the lens unit 3 is provided. Therefore, the surface protective adhesive film of the present invention is stuck so as to be in contact with the plurality of apexes 3 a of the triangular prism-shaped lens unit 3. Further, the cross-sectional shape of the lens portion 3 of this triangular prism is a triangle, but this triangle is preferably an isosceles triangle with the side fixed to the sheet as the base.

一方、プリズムシート1の、レンズ部3が設けられている側とは反対側の平坦な面には、所望により、第2の表面保護粘着フィルム7が貼付される。   On the other hand, a second surface protective adhesive film 7 is attached to the flat surface of the prism sheet 1 opposite to the side on which the lens portion 3 is provided, if desired.

なお、3角柱のプリズム形状における側面とは、3角柱の長さ方向に延びる3つの側面をいうものとする。   In addition, the side surface in the prism shape of a triangular prism shall mean the three side surfaces extended in the length direction of a triangular prism.

本発明の表面保護粘着フィルムが適用される好適なプリズムシートにおいては、実質的に3角柱の複数のプリズムにおいて、隣り合うプリズムの距離、すなわち、プリズムのピッチは10〜1000μm程度であることが好ましく、より好ましくは10〜500μmであり、さらに好ましくは10〜60μmであり、本発明の表面保護粘着フィルムは微細なプリズムピッチを持つ被着体に対して適している。
また、シート積層体は、打ち抜きによって成形されていてもよい。つまり、表面保護粘着フィルム側又は被着体である他のシート側から積層体に打ち抜き刃を押し付けることで、積層体を所望の形状(例えば長尺状)に打ち抜いて、所望の形状及び大きさの積層体(便宜上、打ち抜かれた後の積層体を「積層片」と称する)を得ることができる。こうして得られた積層片では、表面保護粘着フィルムの端部が被着体に強く接着する。被着体がプリズムシート等の凹凸を有するシートである場合は、その凹凸内に表面保護粘着フィルムの粘着剤層が入り込み、表面保護粘着フィルムと被着体とがさらに強固に接着される。
しかしながら、本実施形態の表面保護粘着フィルムによれば、被着体に表面保護粘着フィルムの端部が強固に接着することなく被着体から容易に剥離することができる。その結果、作業者は、剥離された端部をつかんで引っ張ることにより、表面保護粘着フィルム全体を被着体から剥がすことができる。
In a suitable prism sheet to which the surface protective adhesive film of the present invention is applied, it is preferable that the distance between adjacent prisms, that is, the pitch of the prisms, is approximately 10 to 1000 μm. More preferably, it is 10-500 micrometers, More preferably, it is 10-60 micrometers, The surface protection adhesive film of this invention is suitable with respect to the adherend which has a fine prism pitch.
Moreover, the sheet | seat laminated body may be shape | molded by punching. That is, by pressing a punching blade against the laminate from the surface protective adhesive film side or the other sheet side that is an adherend, the laminate is punched into a desired shape (for example, a long shape), and the desired shape and size are obtained. (For convenience, the laminated body after being punched is referred to as “laminated piece”). In the laminated piece thus obtained, the end portion of the surface protective adhesive film strongly adheres to the adherend. When the adherend is a sheet having irregularities such as a prism sheet, the pressure-sensitive adhesive layer of the surface protective adhesive film enters the irregularities, and the surface protective adhesive film and the adherend are more firmly bonded.
However, according to the surface protective pressure-sensitive adhesive film of this embodiment, the end portion of the surface protective pressure-sensitive adhesive film can be easily peeled off from the adherend without firmly adhering to the adherend. As a result, the operator can peel the entire surface protective adhesive film from the adherend by grasping and pulling the peeled end.

<製造方法>
本発明の粘着剤組成物は、例えば、共重合体(I)および共重合体(II)をそれぞれブロック重合により合成し、これらを所定の質量比でブレンドした後に、所望により水素添加を行って、共重合体(I)またはその水素添加物、および共重合体(I)またはその水素添加物の混合物を得、および所望により配合される添加剤を慣用の方法で混合することによって製造される。
<Manufacturing method>
In the pressure-sensitive adhesive composition of the present invention, for example, copolymer (I) and copolymer (II) are synthesized by block polymerization, blended at a predetermined mass ratio, and then hydrogenated as desired. , Copolymer (I) or a hydrogenated product thereof, and a mixture of copolymer (I) or the hydrogenated product thereof, and an additive to be blended if desired is mixed by a conventional method .

水素添加触媒としては、元素周期表Ib、IVb、Vb、VIb、VIIb、VIII族金属のいずれかを含む化合物を用いることができる。例えば、Ti、V、Co、Ni、Zr、Ru、Rh、Pd、Hf、Re、Pt原子を含む化合物を挙げることができ、より具体的には、Ti、Zr、Hf、Co、Ni、Rh、Ruなどのメタロセン系化合物、pd、Ni、Pt、Rh、Ruなどの金属をカーボン、シリカ、アルミナ、ケイソウ土、塩基性活性炭などの担体に担持させた担持型不均一系触媒を挙げることができる。   As the hydrogenation catalyst, a compound containing any one of Group Ib, IVb, Vb, VIb, VIIb, and Group VIII metals can be used. Examples thereof include compounds containing Ti, V, Co, Ni, Zr, Ru, Rh, Pd, Hf, Re, and Pt atoms, and more specifically, Ti, Zr, Hf, Co, Ni, Rh. And metallocene compounds such as Ru, and supported heterogeneous catalysts in which metals such as pd, Ni, Pt, Rh and Ru are supported on a support such as carbon, silica, alumina, diatomaceous earth, and basic activated carbon. it can.

なお、メタロセン系化合物の具体例としては、シクロペンタジェニル環(Cp環)またはCp環上の水素をアルキル基で置換した配位子を二つ有するKaminsky(カミンスキー)触媒、ansa(アンサ)型メタロセン触媒、非架橋ハーフメタロセン触媒、架橋ハーフメタロセン触媒等を挙げることができる。   Specific examples of the metallocene compounds include a Kaminsky catalyst having two ligands in which hydrogen on the cyclopentagenyl ring (Cp ring) or Cp ring is substituted with an alkyl group, and ansa. Examples thereof include a type metallocene catalyst, a non-crosslinked half metallocene catalyst, and a crosslinked half metallocene catalyst.

具体的な例を挙げると、特開平1−275605号公報、特開平5−271326号公報、特開平5−271325号公報、特開平5−222115号公報、特開平11−292924号公報、特開2000−37632号公報、特開昭59−133203号公報、特開昭63−5401号公報、特開昭62−218403号公報、特開平7−90017号公報、特公昭43−19960号公報、特公昭47−40473号公報に記載の触媒を挙げることができる。これら各種の触媒は1種のみを単独で用いてもよいし、2種以上を併用してもよい。   Specific examples include JP-A-1-275605, JP-A-5-271326, JP-A-5-271325, JP-A-5-222115, JP-A-11-292924, and JP-A-11-292924. JP 2000-37632 A, JP 59-133203 A, JP 63-5401 A, JP 62-218403 A, JP 7-90017 A, JP 43-19960 A, Mention may be made of the catalysts described in JP-B 47-40473. These various catalysts may be used alone or in combination of two or more.

別法として、共重合体(II)が前記一般式(A−B)x−Y(式中の記号は前記と同意義を表す。)で表される構造を有する場合、本発明の粘着剤組成物は、以下のような方法(カップリング法)によって、製造してもよい。カップリング法は、共重合体(I)またはその水素添加物(重合体(i))と共重合体(II)またはその水素添加物(重合体(ii))を1ポットで合成することができるため製造工程が簡素であり、製造コストが低廉で、カップリング剤の種類や量により、重合体(i)と重合体(ii)との比率を制御することができる等の点において好ましい。   Alternatively, when the copolymer (II) has a structure represented by the general formula (AB) xY (wherein the symbols are as defined above), the pressure-sensitive adhesive of the present invention. The composition may be produced by the following method (coupling method). In the coupling method, copolymer (I) or a hydrogenated product thereof (polymer (i)) and copolymer (II) or a hydrogenated product thereof (polymer (ii)) can be synthesized in one pot. Therefore, the production process is simple, the production cost is low, and the ratio of the polymer (i) to the polymer (ii) can be controlled by the kind and amount of the coupling agent.

カップリング法は、
第1工程:[A−B]の構造を有する共重合体をブロック重合により合成する工程と、
第2工程:前記[A−B]の構造を有する共重合体の一部を、カップリング剤Y−Z(但し、「Y」はカップリング剤残基、「Z」は脱離基、「X」は2以上の整数を示す。)によりカップリングさせ、{[A−B]−Y}の構造を有する共重合体を合成する工程と、
水素添加物を得る場合には、更に、
第3工程:前記[A−B]の構造を有する共重合体及び前記{[A−B]−Y}の構造を有する共重合体に水素添加することにより、それぞれ水素化された共重合体(I)と共重合体(II)とからなる共重合体組成物を得る工程と
を備える。
The coupling method is
1st process: The process which synthesize | combines the copolymer which has a structure of [AB] by block polymerization,
Second step: A part of the copolymer having the structure of [AB] is converted into a coupling agent YZ x (where “Y” is a coupling agent residue, “Z” is a leaving group, “X” represents an integer of 2 or more.), And a step of synthesizing a copolymer having a structure of {[AB] x —Y}
When obtaining a hydrogenated product,
Third step: Hydrogenation of the copolymer having the structure [AB] and the copolymer having the structure {[AB] x -Y}, respectively, by hydrogenation And a step of obtaining a copolymer composition comprising the combination (I) and the copolymer (II).

「カップリング剤」としては、例えば、メチルジクロロシラン、ジメチルジクロロシラン、メチルトリクロロシラン、ブチルトリクロロシラン、テトラクロロシラン、ジブロモエタン、テトラクロロ錫、ブチルトリクロロ錫、テトラクロロゲルマニウム、ビス(トリクロロシリル)エタン等のハロゲン化合物;エポキシ化大豆油等のエポキシ化合物;アジピン酸ジエチル、アジピン酸ジメチル、ジメチルテレフタル酸、ジエチルテレフタル酸等のカルボニル化合物、ジビニルベンゼン等のポリビニル化合物;ポリイソシアネート;等を挙げることができる。中でも、工業的に入手し易く、反応性も高いという理由から、メチルジクロロシラン、ジメチルジクロロシラン、メチルトリクロロシラン、テトラクロロシランが好ましい。   Examples of the “coupling agent” include methyldichlorosilane, dimethyldichlorosilane, methyltrichlorosilane, butyltrichlorosilane, tetrachlorosilane, dibromoethane, tetrachlorotin, butyltrichlorotin, tetrachlorogermanium, bis (trichlorosilyl) ethane. Halogen compounds such as epoxidized soybean oil; carbonyl compounds such as diethyl adipate, dimethyl adipate, dimethyl terephthalic acid and diethyl terephthalic acid; polyvinyl compounds such as divinylbenzene; polyisocyanates; . Of these, methyldichlorosilane, dimethyldichlorosilane, methyltrichlorosilane, and tetrachlorosilane are preferred because they are easily industrially available and have high reactivity.

本発明の表面保護粘着フィルムは、例えば、押出成形によって基材シート(基材層)を製造した後、前記粘着剤組成物を溶融または溶解させた液体を基材シートに塗布または噴霧する方法、あるいは、インフレーション法により得られた基材シートと粘着シートを貼り合わせる方法、あるいは多層マニホールドを備えたTダイを用いて基材原料と前記粘着剤組成物を共押出する方法により製造できる。なかでも、基材層と粘着剤層が密着した多層シートが得られるので共押出により製造する方法が好ましい。なお、本発明の粘着剤組成物を溶融または溶解させた液体もまた、本発明の粘着剤組成物に包含される。   The surface protective pressure-sensitive adhesive film of the present invention is, for example, a method of applying or spraying a liquid obtained by melting or dissolving the pressure-sensitive adhesive composition on a base sheet after producing a base sheet (base layer) by extrusion molding, Or it can manufacture by the method of sticking the base material sheet | seat and adhesive sheet which were obtained by the inflation method, or the method of coextruding a base material and the said adhesive composition using T die provided with the multilayer manifold. Especially, since the multilayer sheet | seat with which the base material layer and the adhesive layer contact | adhered is obtained, the method of manufacturing by coextrusion is preferable. A liquid obtained by melting or dissolving the pressure-sensitive adhesive composition of the present invention is also included in the pressure-sensitive adhesive composition of the present invention.

<適用>
本発明の粘着剤組成物は、表面保護粘着フィルムの粘着剤層に好ましく適用される。また、表面保護粘着フィルムは、光学板、プリズムシート、および拡散フィルム等の凹凸のある被着体にも好適に用いることができるが、これに限定されるものではなく、例えば、表面が平滑なシートの表面保護にも使用することができる。
被着体となるシートを構成する材料としては、特に限定されないが、透光性を有する樹脂、例えばアクリル系樹脂、ポリカーボネート等が挙げられる。
<Application>
The pressure-sensitive adhesive composition of the present invention is preferably applied to the pressure-sensitive adhesive layer of the surface protective pressure-sensitive adhesive film. Further, the surface protective adhesive film can be suitably used for uneven adherends such as an optical plate, a prism sheet, and a diffusion film, but is not limited thereto, and for example, has a smooth surface. It can also be used to protect the surface of the sheet.
Although it does not specifically limit as a material which comprises the sheet | seat used as a to-be-adhered body, Resin which has translucency, for example, acrylic resin, a polycarbonate, etc. are mentioned.

以下、本発明の表面保護粘着フィルムを、実施例に基づいて詳細に説明するが、本発明は、以下の実施例に限定されるものではない。   Hereinafter, although the surface protection adhesive film of this invention is demonstrated in detail based on an Example, this invention is not limited to a following example.

(共重合体組成物の合成)
重合体ブロックA
窒素置換された反応容器に、脱気・脱水されたシクロヘキサン500質量部、スチレン20質量部及びテトラヒドロフラン5質量部を仕込み、重合開始温度の40℃にてn−ブチルリチウム0.13質量部を添加して、昇温重合を行った。
重合体ブロックB
重合体Aの重合転化率が略100%に達した後、反応液を15℃に冷却し、次いで、1,3−ブタジエン70質量部およびスチレン10質量部を加え、更に昇温重合を行った。
(Synthesis of copolymer composition)
Polymer block A
A nitrogen-substituted reaction vessel is charged with 500 parts by mass of degassed / dehydrated cyclohexane, 20 parts by mass of styrene and 5 parts by mass of tetrahydrofuran, and 0.13 parts by mass of n-butyllithium is added at a polymerization start temperature of 40 ° C. Then, temperature rising polymerization was performed.
Polymer block B
After the polymerization conversion rate of the polymer A reached approximately 100%, the reaction solution was cooled to 15 ° C., and then 70 parts by mass of 1,3-butadiene and 10 parts by mass of styrene were added, followed by further temperature rising polymerization. .

重合転化率がほぼ100%に達した後、カップリング剤としてメチルジクロロシラン0.06質量部を加え、カップリング反応を行った。カップリング反応が完結した後、水素ガスを0.4MPa−Gaugeの圧力で供給しながら10分間放置した。一部取り出したポリマーは、ビニル含有率64%、重量平均分子量約11万、カップリング率60%であった。   After the polymerization conversion rate reached almost 100%, 0.06 parts by mass of methyldichlorosilane was added as a coupling agent to carry out a coupling reaction. After the coupling reaction was completed, it was left for 10 minutes while supplying hydrogen gas at a pressure of 0.4 MPa-Gauge. A partially extracted polymer had a vinyl content of 64%, a weight average molecular weight of about 110,000, and a coupling rate of 60%.

その後、反応容器内に、ジエチルアルミニウムクロライド0.03質量部及びビス(シクロペンタジエニル)チタニウムフルフリルオキシクロライド0.06質量部を加え、撹拌した。水素ガス供給圧0.7MPa−Gauge、反応温度80℃で水素添加反応を開始し、水素の吸収が終了した時点で、反応溶液を常温、常圧に戻し、反応容器から抜き出すことにより、重合体(i)と重合体(ii)からなる共重合体組成物を得た。
共重合体組成物の特性を表1に示す。
Thereafter, 0.03 parts by mass of diethylaluminum chloride and 0.06 parts by mass of bis (cyclopentadienyl) titanium furfuryloxychloride were added to the reaction vessel and stirred. The hydrogenation reaction was started at a hydrogen gas supply pressure of 0.7 MPa-Gauge and a reaction temperature of 80 ° C., and when the hydrogen absorption was completed, the reaction solution was returned to room temperature and normal pressure, and the polymer was removed from the reaction vessel. A copolymer composition comprising (i) and polymer (ii) was obtained.
The properties of the copolymer composition are shown in Table 1.

Figure 2012117013
Figure 2012117013

なお、「St(A+B)」、「St(B)」、「St(A)」、および「St(b)」は、それぞれ次のように定義される数値を表す。当該定義において、「全重合体」とは、重合体(i)および重合体(ii)の全体を意味する。
「St(A+B)」は、全重合体の芳香族アルケニル化合物単位含有率であり、次式で表される数値を意味する。なお、これは、下記「St(B)」と下記「St(A)」との和に等しい。
式:
St(A+B)=(全重合体中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(B)」は、次式で表される数値を意味する。
式:
St(B)=(全重合体ブロックB中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(A)」は、次式で表される数値を意味する。
式:
St(A)=(全重合体ブロックA中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(b)」は、重合体ブロックBの芳香族アルケニル化合物単位含有率であり、次式で表される数値を意味する。
式:
St(b)=(全重合体ブロックB中の芳香族アルケニル化合物単位重量)/(全重合体ブロックB中の全単量体単位重量)×100(重量%)
また、表1中、「A:B」は、重合体ブロックAの総量と重合体ブロックBの総量との重量比を表す。
また、表1中、「(i):(ii)」は、重合体(i)と重合体(ii)の重量比を表す。
また、表1中、「共役ジエン含有率」は、重合体ブロックBの共役ジエン単位含有率を表す。
また、表1中、「ビニル結合含有率」は、重合体ブロックBのビニル結合の含有率を表す。
Note that “St (A + B)”, “St (B)”, “St (A)”, and “St (b)” represent numerical values defined as follows. In the definition, “total polymer” means the whole of the polymer (i) and the polymer (ii).
“St (A + B)” is the aromatic alkenyl compound unit content of the whole polymer, and means a numerical value represented by the following formula. This is equal to the sum of the following “St (B)” and the following “St (A)”.
formula:
St (A + B) = (aromatic alkenyl compound unit weight in all polymers) / (total monomer unit weight in all polymers) × 100 (% by weight)
“St (B)” means a numerical value represented by the following equation.
formula:
St (B) = (aromatic alkenyl compound unit weight in all polymer blocks B) / (total monomer unit weight in all polymers) × 100 (% by weight)
“St (A)” means a numerical value represented by the following formula.
formula:
St (A) = (aromatic alkenyl compound unit weight in all polymer blocks A) / (total monomer unit weight in all polymers) × 100 (% by weight)
“St (b)” is the aromatic alkenyl compound unit content of the polymer block B, and means a numerical value represented by the following formula.
formula:
St (b) = (aromatic alkenyl compound unit weight in all polymer blocks B) / (total monomer unit weight in all polymer blocks B) × 100 (% by weight)
In Table 1, “A: B” represents a weight ratio between the total amount of the polymer block A and the total amount of the polymer block B.
In Table 1, “(i) :( ii)” represents the weight ratio of the polymer (i) to the polymer (ii).
Further, in Table 1, “conjugated diene content” represents the conjugated diene unit content of the polymer block B.
In Table 1, “Vinyl bond content” represents the vinyl bond content of the polymer block B.

(実施例1〜6、比較例1〜5)
100重量部の共重合体組成物に、粘着付与剤として20重量部の「アルコンP100」(荒川化学工業社製)と、スチレン系ブロック相補強剤として20重量部の「ENDEX155」(イーストマンケミカル社製)と、表2に示す量のポリエチレンイミン(「エポミンRP20」、日本触媒社製)及びエチレンビスステアリン酸アミド(「アルフローHF50」、日油社製)と、を添加することで、粘着剤組成物を得た。
(Examples 1-6, Comparative Examples 1-5)
To 100 parts by weight of the copolymer composition, 20 parts by weight of “Arcon P100” (manufactured by Arakawa Chemical Industries) as a tackifier and 20 parts by weight of “ENDEX 155” (Eastman Chemical) as a styrenic block phase reinforcing agent By adding polyethyleneimine (“Epomin RP20”, manufactured by Nippon Shokubai Co., Ltd.) and ethylenebisstearic acid amide (“Alflow HF50”, manufactured by NOF Corporation) in the amounts shown in Table 2. An agent composition was obtained.

基材にはポリプロピレン(「J715M」、プライムポリマー社製)を用い、Tダイ法により基材と各粘着剤組成物を共押出成形することで、34μmの厚みの基材層と6μmの厚みの粘着剤層とが積層一体化された、実施例1〜6および比較例1〜5の表面保護粘着フィルムを成形した。   Polypropylene ("J715M", manufactured by Prime Polymer Co., Ltd.) is used as the base material, and the base material and each pressure-sensitive adhesive composition are coextruded by the T-die method, so that the base material layer with a thickness of 34 μm and the thickness of 6 μm are The surface protective adhesive films of Examples 1 to 6 and Comparative Examples 1 to 5 in which the adhesive layer was laminated and integrated were molded.

凹凸を有するプリズムシート(「BEF3」、住友3M社製)に表面保護粘着フィルムを貼り付けることで、積層体を得た。   A laminate was obtained by attaching a surface protective adhesive film to a prism sheet having irregularities (“BEF3”, manufactured by Sumitomo 3M).

(評価)
表面保護粘着フィルムについて、「とっかかり」及び「汚染性」を評価した。結果を表2に示す。
(Evaluation)
The surface protective adhesive film was evaluated for “sticking” and “contamination”. The results are shown in Table 2.

Figure 2012117013
Figure 2012117013

<判定基準>
とっかかり(表面保護フィルムの端部をつかんで引っ張り被着体から剥がす際の表面保護フィルムの端部の剥がしやすさ)
正方形の打ち抜き刃によって、表面保護粘着フィルム側から積層体を打ち抜くことで、正方形の積層片を得た。積層片を3つ用意してそれぞれの積層片について次の試験を行った。積層片の一辺から表面保護粘着フィルムを親指を使ってつかみ引き剥がすことを5回試みた。なお、表面保護フィルムをつかむ場所は毎回変えた。用意した3つの積層片のうち5回とも表面保護粘着フィルムを引き剥がすことに成功した積層片の数(成功した数)によって、以下のように評価した。
◎(優): 成功した数 3
○(良): 成功した数 2
×(不良): 成功した数 1またはゼロ
汚染性(被着体への粘着剤の一部の成分の付着(糊残り))
積層片を3つ用意してそれぞれの積層片について次の試験を行った。積層片を80℃で3日間養生した後、表面保護フィルムを剥がした。次いでバックライトで照らしたプリズムシートの凹凸面(プリズム面)を目視により観察し糊残りの有無を評価した。

◎(優):3つの積層片の全てについて表面に糊残りが観察されなかった
○(良):2つの積層片には糊残りが観察されなかったが1つの積層片には表面に糊残りが観察された
×(不良):3つの積層片のいずれについても表面に糊残りが観察された
<Criteria>
Sticking (easy to peel off the edge of the surface protection film when grasping the edge of the surface protection film and pulling it off the adherend)
A square laminate was obtained by punching the laminate from the surface protective adhesive film side with a square punching blade. Three laminated pieces were prepared, and the following test was performed on each laminated piece. Five attempts were made to grasp and peel the surface protective adhesive film from one side of the laminate using a thumb. In addition, the place where a surface protection film is grabbed was changed every time. It evaluated as follows by the number (successful number) of the laminated | multilayer piece which succeeded in peeling off the surface protection adhesive film 5 times among the three laminated pieces prepared.
◎ (Excellent): Successful number 3
○ (Good): Successful number 2
X (defect): Successful number 1 or zero contamination (adhesion of some components of the adhesive to the adherend (adhesive residue))
Three laminated pieces were prepared, and the following test was performed on each laminated piece. After the laminated piece was cured at 80 ° C. for 3 days, the surface protective film was peeled off. Subsequently, the uneven surface (prism surface) of the prism sheet illuminated with the backlight was visually observed to evaluate the presence or absence of adhesive residue.

◎ (excellent): No adhesive residue was observed on the surface of all three laminated pieces. ○ (good): No adhesive residue was observed on the two laminated pieces, but no adhesive residue was observed on the surface of one laminated piece. X (defect): Adhesive residue was observed on the surface of any of the three laminated pieces.

本発明の粘着剤組成物は、プリズムシート、拡散フィルム等の表面保護粘着フィルムの粘着剤層に好適に用いられる。本発明の表面保護粘着フィルムは、プリズムシート、拡散フィルム等の表面保護に好適に用いられる。   The pressure-sensitive adhesive composition of the present invention is suitably used for a pressure-sensitive adhesive layer of a surface protective pressure-sensitive adhesive film such as a prism sheet or a diffusion film. The surface protective adhesive film of the present invention is suitably used for surface protection of prism sheets, diffusion films and the like.

1 プリズムシート
2 シート部
3 レンズ部(プリズム)
3a レンズ部の頂部(プリズム頂角)
4 第1の表面保護粘着フィルム
5 基材層
6 粘着剤層
7 第2の表面保護粘着フィルム
1 Prism sheet 2 Sheet part 3 Lens part (prism)
3a Top of lens part (prism apex angle)
4 First surface protective adhesive film 5 Base material layer 6 Adhesive layer 7 Second surface protective adhesive film

Claims (5)

重合体(ii):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは1以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)で表される構造を有する共重合体(II)またはその水素添加物
を含有し、
又は、
重合体(i):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体(I)またはその水素添加物と、
前記重合体(ii)と、を含有し、
前記重合体(i)および前記重合体(ii)の全体の芳香族アルケニル化合物単位含有率(St(A+B))は、30〜50重量%であり、
前記重合体(i)および前記重合体(ii)にそれぞれ含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比(A:B)が5:95〜25:75の範囲内であり、
さらに、
イミン系化合物及び脂肪酸アミドの少なくとも一方を含有することを特徴とする粘着剤組成物。
重合体ブロックA:
芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロック
重合体ブロックB:
共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロック
Polymer (ii): Including the following polymer block A and the following polymer block B, the general formula A-B-A (the symbols in the formula are as defined above) or the general formula (A-B) x A copolymer (II) having a structure represented by -Y (wherein x represents an integer of 1 or more, Y represents a coupling agent residue, and other symbols are as defined above), Containing its hydrogenated product,
Or
Polymer (i): comprising the following polymer block A and the following polymer block B, the general formula [AB] n (wherein A is the polymer block A, B is the polymer block B, n is A copolymer (I) having a structure represented by the formula (1) or a hydrogenated product thereof:
Containing the polymer (ii),
The overall aromatic alkenyl compound unit content (St (A + B)) of the polymer (i) and the polymer (ii) is 30 to 50% by weight,
The weight ratio (A: B) of the total amount of the polymer block A and the total amount of the polymer block B contained in each of the polymer (i) and the polymer (ii) is in the range of 5:95 to 25:75. And
further,
A pressure-sensitive adhesive composition comprising at least one of an imine compound and a fatty acid amide.
Polymer block A:
Polymer block having a series of aromatic alkenyl compound units and mainly consisting of aromatic alkenyl compound units Polymer block B:
An aromatic alkenyl-conjugated diene copolymer block containing a conjugated diene unit and an aromatic alkenyl compound unit at random, wherein the aromatic alkenyl compound unit content (St (b)) is 10 to 35% by weight. Combined block
前記重合体(i)および前記重合体(ii)の合計重量100重量部に対して、前記イミン系化合物の含有量は0.2〜1.5重量部である、
請求項1に記載の粘着剤組成物。
The content of the imine compound is 0.2 to 1.5 parts by weight with respect to 100 parts by weight of the total weight of the polymer (i) and the polymer (ii).
The pressure-sensitive adhesive composition according to claim 1.
前記脂肪酸アミドの含有量は0.15〜3.5重量部である、
請求項1又は2に記載の粘着剤組成物。
The content of the fatty acid amide is 0.15 to 3.5 parts by weight,
The pressure-sensitive adhesive composition according to claim 1 or 2.
基材層と、請求項1〜3のいずれか1項に記載の粘着剤組成物からなる粘着剤層と、を有する表面保護粘着フィルム。   The surface protection adhesive film which has a base material layer and the adhesive layer which consists of an adhesive composition of any one of Claims 1-3. 前記基材層はポリオレフィン基材層であり、
前記粘着剤組成物は、粘着付与剤およびスチレン系ブロック相補強剤を更に含有し、
前記重合体(i)、前記重合体(ii)およびスチレン系ブロック相補強剤中の芳香族アルケニル化合物単位重量の、前記粘着剤層の重量に対する割合(芳香族アルケニル化合物単位含有率)は、20〜50重量%である、
請求項4に記載の表面保護粘着フィルム。
The substrate layer is a polyolefin substrate layer;
The pressure-sensitive adhesive composition further contains a tackifier and a styrenic block phase reinforcing agent,
The ratio of the weight of the aromatic alkenyl compound unit in the polymer (i), the polymer (ii) and the styrenic block phase reinforcing agent to the weight of the pressure-sensitive adhesive layer (aromatic alkenyl compound unit content) is 20 ~ 50% by weight,
The surface protective adhesive film according to claim 4.
JP2010270497A 2010-12-03 2010-12-03 Adhesive composition and surface protection adhesive film Pending JP2012117013A (en)